Field of Invention

The invention relates to a neural electrode. It relates in particular to such an elec- trode which is able to withstand high mechanical forces, and to a method of fabrication of the same.

Cross References to related Documents

Schuettler, M., Stiess, S., King, B., Suaning, G.J.: "Fabrication of Implantable Microelectrode Arrays by Laser-Cutting of Silicone Rubber and Platinum Foil". Journal of Neural Engineering, No. 2, p. 121-128 (2005). Schuettler, M., Pfau, D., Ordonez, J.S., Henle, C, Woias, P., Stieglitz, T.: "Stretchable Tracks for Laser-Machined Neural Electrode Arrays", Proceedings of the IEEE Engineering in Medicine and Biology Conference, pp. 1612-1615, (2009). Suaning, G. J., Schuettler, M., Ordonez, J. S., Lovell, N. H.: "Fabrication of Multi-Layer, High Density Micro-Electrode Arrays for Neural Stimulation and Bio-Signal Recording", Proceedings of the IEEE Neural Engineering Conference, pp. 5-8 (2007). Background of the Invention

The established and published [Schuettler 2005] process of fabricating neural electrodes based on metalized elastomer is improved in order to allow a better mechanical stability of the electrode arrays.

Objects of the Invention The current fabrication process utilizes a laser for cutting metal foil in order to generate electrically conducting tracks and contact pads. These tracks and pads are embedded into a silicone elastomer. Since the silicone is very elastic, it cannot protect the delicate metal tracks against strain and other mechanical load as applied, e.g. during implantation surgery.

Summary of the Invention

Currently, there is no fabrication process for silicone-based implantable neural electrode, which employs an additional layer which function is to set the mechanical properties of the neural electrode and to protect the metal structures.

The current layering (elastomer-metal-elastomer) will be extended by at least one additional layer of high tensile strength polymer. This polymer acts as mechanical protection, e.g. strain relieve in order to minimize the force reaching the delicate metal tracks.

It is safer to handle the electrode structure. The risk of damaging the metal tracks during and after implantation are dramatically reduced. Also, if required, the polymer layer can be shaped in a way to locally strengthen (or stiffen) the electrode array, allowing the designer of the electrode to define anisotropic mechani- cal properties (e.g. very high Young's modulus in direction longitudinal to the metal tracks, low Young's modulus in lateral direction).

Brief description of the drawings

A potential fabrication process, which can be applied for fabricating polymer- reinforced silicone-based neural electrodes is shown in Figure 1. Generating anisotropic mechanical properties in an electrode grid by shaping the polymeric reinforcement embedded in the grid elastomer is shown in Figures 2A- C

Detailed description of the Invention

In the following, several preferred embodiments of the invention are given. Subsequently, the process according to the invention is described. The foil used to obtain reinforcement has multiple perforations. Through these holes, the two adjacent layers of elastomer touch each other and establish a strong mechanical link between each other and the polymer foil by interlocking.

In order to enhance the robustness of the neural electrodes, polymer-reinforcement can be combined with giving the conductive metal tracks the shape of meanders. Meander-shaped electrodes permit stretching to some degree without being damaged [Schuettler 2009].

In order to enhance mechanical flexibility of the polymer reinforced neural elec- trode, the polymer foil can be shaped in a way that it only takes up tensile forces in the direction longitudinal to the metal tracks. In contrast, they cannot take up forces in direction lateral to the tracks and also would not affect the flexibility of the elastomer very much (see figure 2).

The neural electrodes could be fabricated in multiple alternating layers of elas- tomer and laser-patterned metal [Suaning 2007]. Depending on the application, one has to decide which layer is to be used for placing the polymeric reinforcement.

Some applications require the use of more than one layer of reinforcement.

Some applications require the use of polymeric reinforcement that has some additional functionality, like: carrying makers for imaging technology (e.g. radiopaque)

- carrying fluidic channels allowing controlled drug release

carrying printed information on how to implant the array or on design aspects like labeling of electrode contacts, etc.

being (partly) made from degradable material, providing mechanical protection only during implantation and during the curing-in process but providing maximal softness for the delicate neural tissue in the long-term use.

The concept of embedding a polymeric reinforcement in elastomers can be applied but is not restricted to laser-patterning of neural electrodes (as shown in figure 1). It is also applicable to photolithography-based patterning of metal layers and/or elastomers, methods based on electroplating of metal on elastomers and other methods employing metal structures embedded in elastomer.

The potential fabrication process, which can be applied for fabricating polymer- reinforced silicone-based neural electrodes, as shown in Figure 1, requires a me- chanical carrier on which the electrode array is processed, which will be discarded after finishing the fabrication. During the first step, a release layer is deposited onto the carrier in order to prevent the uncured elastomer, which is applied in the second step to permanently bond to the carrier. During the third step, the polymeric reinforcement is laminated to the elastomer. Typically, a thin plastic foil is used as reinforcement. This foil will be embedded in elastomer during the next process step.

In step five, a metal foil is laminated onto the elastomer. In the following step, a laser is used to cut the perimeter of contacts and conductive tracks into the metal foil. All metal not needed (e.g. the metal between two adjacent tracks) is manually removed in step seven. A third layer of elastomer is deposited in process set eight, covering the metal tracks. Electrode sites and contact pads are exposed in an additional laser process and the contour of the electrode array is also cut through all elastomer layers using a laser. In step ten, the fabricated electrode array is removed from the mechanical carrier.

Usually, medical grade silicone rubber is used as elastomer. The metal foil could be made from stainless steel, platinum, or similar material. The polymer reinforcement can be made from Polyethylene, Polypropylene, Parylene C, or others. Figure 2A shows an exemplary design of an electrode according to the invention. More precise, an electrode grid with no forces applied, is shown.

Figure 2B shows how tensile forces (arrows) in longitudinal direction (relative to the metal tracks) are taken up by the reinforcement and do not affect the shape of electrode grid.

According to figure 2C, tensile forces (arrows) in lateral direction (relative to the metal tracks) can affect the shape of the electrode grid without being a risk to the delicate metal tracks.