This invention concerns new cyclotrisiloxanes, new hyperbranched or linear siloxane polymers, and their preparation.

BACKGROUND OF THE INVENTION The publications and other materials used herein to illuminate the background of the invention, and in particular, cases to provide additional details respecting the practice, are incorporated by reference.

Organosilicon dendritic and hyperbranched polymers are well known. The dendrimer core is usually prepared from tetraallyl-or-vinylsilane, which is then derivatized by hydrosilylation reaction (1,2). On the other hand, hyperbranched polycarbosilanes are commonly prepared from vinyltris (dimethylsiloxy) silane via hydrosilylation reactions. Typically, 8-10 mol-% starting material cyclizes in a side reaction (3). See Scheme 1.

There are few examples of hyperbranched or dendritic polysiloxanes, eg. polymers, whose backbone consist only of-SiRR'-O-linkages. Probably the most significant paper is by Uchicda et al. (4) which describes a multistep pathway for highly regular third generation dendritic polysiloxanes with molecular weight of about 15,000 g/mol. See Scheme 2.

Rebrov (5) used a different approach. He let MeSiCl3 react with three equivalents of NaOSiMe (OEt) 2. Ethoxy groups were then converted quantitatively into chlorines by reaction with thionyl chloride. Treatment of the resulting product again with NaOSiMe (OEt) 2, followed by conversion of the Si-OEt into Si-Cl groups repeatedly

gave a fourth generation polymer in >75% yield. See Scheme 3.

Morikowa (6) utilized easily cleavageable Si-Ph bond in his synthesis. The core was prepared from a compound having three Si-phenyl groups which were converted into Si-Br by treatment of Br2. Reaction with HNMe2 gave Si-N functionalities, which in turn could be reacted with silanols bearing Si-phenyl groups. This cycle was repeated two times to give a 3rd generation dendrimer in 32% yield, with a molecular weight of about 4,800 g/mol. See Scheme 4. Scheme 1 H _S'E---S'--Si- y I//*-Si-O-S-H-9 Po"sr s-0-Sil. I 1 10 0 put 0 -Si--Si- H I p-Si-H 10,/18-10 mol-% /\-/S,-H Scheme 2 Hfo-,'4H (o-Si)-w . 1/I o-sH Mesm, t ! (H ! O-i0-S -si-04si-o+s- -Si-O-Si-QSr-- . ( s)''t. (o- i-s Hsosr--t cr-s- i (o-so-s- (o-IH (O-S§itH Çl (O-S H20 Pd/C ,-HCI SI-H terminated dendrimer. I 'eOH tst eneratlon HO Si-Os- (o--oH I Scheme 3 Scheme 4

OBJECTS AND SUMMARY OF THE INVENTION The aim of this invention is to provide convenient methods for the preparation of hyperbranched siloxane polymers by anionic polymerization of a cyclotrisiloxane having the functional group Si-OH, and for the preparation of linear siloxane polymers by cationic or anionic polymerization of a cyclotrisiloxane having a vinyl terminal functional group. A further object of this invention is to provide novel cyclotrisiloxanes useful for the preparation of the aforementioned polymers.

Thus, according to one aspect, this invention concerns a novel cyclotrisiloxane of the formula (I) wherein Y is OSi (R) 2H, OSi (R) 20H, or O-Si (R) 2-OSi (R) 2-CH=CH2, and the R substituents can be the same or different, any R substituent being selected from the group consisting of phenyl, an unsubstituted or substituted alkyl of 1 to 6 carbon atoms, wherein the optional substituent is a phenyl or one or more fluoro atoms, provided that the alpha or beta position of the alkyl chain cannot be fluorosubstituted.

According to another aspect, the invention concerns a method for the preparation of a hyperbranched siloxane polymer, wherein a compound of formula (II)

wherein Y is OH or OSi (R) 20H, and the R substituents can be the same or different, any R substituent being selected from the group consisting of phenyl, an unsubstituted or substituted alkyl of 1 to 6 carbon atoms, wherein the optional substituent is a phenyl or one or more fluoro atoms, provided that the alpha or beta position of the alkyl chain cannot be fluorosubstituted is subjected to anionic polymerization, in bulk or in a suitable solvent, e. g. THF, to give a hyperbranched polymer, which has the formula (IIIal, Ea2, Ea3) or (nibl, IIIb2, IIIIb3) IIlal IIIa2 IIIs3 IIIb1 IIIb2 IIIb3

wherein the substituents R are as defined above and where each Z in Eal-a3 is one of the groups IIIal-a3, and each Z in IIIbl-b3 is one of the groups Ebl-b3, or Z is an endcapping group. Said endcapping group, which can be the same or different, can be hydrogen obtained by neutralization, or a radical derived from a halosilane or a halosiloxane, e. g. chlorosilane or chlorosiloxane, wherein said halosilane or halosiloxane can bear functional or non-functional groups. As examples of said functional or non-functional group can be mentioned hydrogen, vinyl, the substituent R as defined before, amino, alkoxy or polyalkylene oxide. The endcapping of the polymer can also be carried out by using a mixture of different compounds. By proper choice of endcapping group the surface of the polymer can be modified in desired ways.

According to a further aspect, the invention concerns a method for the preparation of a linear siloxane polymer, wherein a compound of the formula (IV) wherein Y is O-Si (R) 2-OSi (R) 2-CH=CH2, and the R substituents can be the same or different, any R substituent being selected from the group consisting of phenyl, an unsubstituted or substituted alkyl of 1 to 6 carbon atoms, wherein the optional substituent is a phenyl or one or more fluoro atoms, provided that the alpha or beta position of the alkyl chain cannot be fluorosubstituted,

is subjected to cationic or anionic polymerization to give a linear polymer, which has the formula (V) wherein the substituents R are the same as in compound (IV) and m is 3 to 9000.

The invention also concerns the novel hyperbranched or linear siloxane polymers.

DETAILED DESCRIPTION OF THE INVENTION According to a preferred embodiment, each R-substituent in the cyclotrisiloxane of formula (I) is the same and is an alkyl of 1 to 4 carbon atoms. Most preferably, each R-substituent is methyl.

The anionic polymerization of the Si-OH functionalized cyclotrisiloxane (compound (II)) can be carried out in the presence of a lithium containing base, for example an alkyl lithium such as n-butyl lithium or triphenylmethyl lithium, or lithium diisopropyl amide. The polymerization can be carried out in bulk or in a suitable solvent. As an example of a suitable solvent can be mentioned THF Alternatively, the anionic polymerization can be carried out by subjecting the Si-OH functionalized cyclotrisiloxane to a catalytic amount of superbase such as a phosphazene. A particularly useful superbase is phosphazene base P4-t-Bu [1-tert-

Butyl-4, 4,4-tris (dimethylamino)-2, 2-bis [tris (dimethylamino)-phosphoranyliden- amino]-2A5, 4A5-catenadi (phosphazene)].

The preparation of linear siloxane polymers can be carried out by cationic polymerization initiated by an acid such as trifluoromethane sulfonic acid (triflic acid) or by anionic polymerization initiated by bases such as dilithium diphenylsilanolate or dilithium tetramethylsiloxanediolate.

The invention will be described more in detail in the Experimental section in the following non-limiting examples.

Experimental : Spectroscopic Analysis IH, 13C and 29Si NMR spectra were obtained on a Bruker AMX-500 MHz spectrometer operating in the FT mode.'H NMR spectra were run on 5 % w/v chloroform-d solutions. Forty percent w/v solutions in acetone-d6 were used to obtain 29Si and 13C NMR spectra. 13C NMR spectra were obtained with broad band proton decoupling. An inverse gate decoupling pulse sequence with a 60 sec delay was used to acquire 29Si NMR spectra. Tetramethylsilane (TMS) was used as an internal standard for'H, 13 C and 29Si NMR spectra.

IR spectra of neat films on NaCI plates were recorded on a Perkin Elmer Spectrum 2000 FT-IR spectrometer. GPC analysis of the molecular weight distribution of the polymers was performed on a Waters system equipped with a refractive index detector. Two 7.8 mm x 300 mm Styragel columns packed with < 5 p. divinylbenzene cross-linked polystyrene HR4 and HR2 in series were used for the analysis. The eluting solvent was toluene at a flow rate of 0.3 mL/min. The retention times were calibrated against known monodisperse polystyrene standards. TGA of

the polymers was measured on a Shimadzu TGA-50 instrument. The temperature program was 4 °C/min from 25 to 850 °C.

Tg of the polymer was determined by DSC on a Perkin-Elmer DSC-7. The temperature program for the analysis we begun at-150 °C. The temperature was increased at a rate of 10 °C/min. Light scattering CPS/MALLS was performed with a Wyatt Dawn-DSP MALLS detector, which is inserted between the GPC columns and R410 RI detector. Data were analyzed with a Wyatt Astra system. THF was used as the eluant.

All reactions were conducted in flame dried glassware under an atmosphere of argon.

EXAMPLE 1 Preparation of 1-dimethylsiloxy-1, 3,3y5, 5-pentamethylcyclotrisiloxane a) 1,1-Dichloro-1,3,3-trimethyldisiloxane 1,3-Dihydridotetramethyldisiloxane (57 g, 0.42 mol) and methyltrichlorosilane, (96 g, 0.64 mol) were placed into 200 mL rb flask equipped with a Teflon covered magnetic stirbar and sealed with a rubber septum. The catalyst solution pL) was injected into flask at room temperature (RT). No reaction occurred. Dry HCl gas was slowly bubbled into solution. Excess pressure was relieved through a syringe needle which was attached to a drying tube which was filled with Drierite.

An exothermic reaction occurred. The contents of the flask warmed to about 35 °C in 10 minutes. Addition of gaseous HC1 gas was continued for 2 h. The reaction mixture was distilled through a 50 cm vacuum jacketed column which was packed with stainless steel saddles. A fraction, 33.6 g (42 % yield), bp 116°C, was

collected. lH NMR 8 : 0.32 (d, 6H, J = 3 Hz), 0.84 (s, 3H), 4.77 (septet, 1H, J = 3 Hz); '3C NMR 8 :-0.17,5.97 ; 29Si NMR 5 :-17.10 (1Si), 0.94 (1Si). IR v: 2966,2151, 1414,1258, 1088,904,797 cni 1. b) Tetramethyldisiloxane-1, 3-diol The compound was prepared by the controlled hydrolysis of dimethyldichlorosilane (5). c) 1-Dimethylsiloxy-1,3,3,5,5-pentamethylcyclotrisiloxane 1, 1-Dichloro-1, 3,3-trimethyldisiloxane (25. 0 g, 0.13 mol) in 30 mL Et2O and tetramethyldisiloxane-1, 3-diol (22.0 g, 0.13 mol) in 30 mL Et2O were added dropwise to a solution of Et3N (28.0 g, 0.28 mol) and 170 mL Et20 over one hour at RT. After stirring for 2 h, the reaction mixture was filtered and washed with water, dilute H3PO4 solution and saturated NaHC03. It was dried over anhydrous MgSO4, filtered and the volatiles were removed by evaporation under reduced pressure.

Fractional distillation through a 10 cm vacuum jacketed column gave a fraction, 26.9 g (72 % yield), bp 81 °C (40 mm Hg).'H NMR 8 : 0.09 (s, 3H), 0.12 (s, 6H), 0.14 (s, 6H), 0.20 (d, 6H, J = 3 Hz), 4.75 (sept., 1H, J = 3 Hz). 13CNMR # :-3.11, 0.52,0.72,0.82.29Si NMR 8 :-56.20 (1Si),-8. 50 (2Si),-5. 72 (1Si). IR v: 2966, 2907, 2133,1406,1260,1089,1020,907,862,810,770,624 cm~'.

EXAMPLE 2 1-(Hydroxydimethylsiloxy)-1,3,3,5,5-pentamethylcyclotrisilox ane A homogenous solution was formed from 1-dimethylsiloxy-1, 3,3,5,5- pentamethylcyclotrisiloxane obtained in Example 1 (20.0 g, 70 mmol), 250 mL

dioxane and 30 mL distilled water. Palladium catalyst (10 % Pd/C, 0.5 g) was added to the solution in three aliquots at RT, and the system was allowed to react for 12 h. No more H2 evolved when small amount of additional catalyst was added.

After filtration and removal of volatiles by evaporation, fractional distillation gave a fraction, 19.6 g (66 mmol, 93 % yield), bp 52 °C (0.1 mm Hg).'H NMR 8 : 0.10 (6H), 0.11 (3H), 0.12 (6H), 0.15 (6H), 5.15 (lI-). 13C NMR 8 :-2. 81,0.34,0.78, 0.85.29Si NMR 8 :-57.63 (1Si),-12. 45 (1Si),-8. 32 (2Si). IR v: 3339 (br), 2966,2907, 1411,1262,1092,1023,880,867,809,764,624 cai 1.

EXAMPLE 3 1-Dimethylsiloxy-1-phenyl-3, 3,5,5-tetramethylcyclotrisiloxane The preparation was carried out according to the procedure described in Example 1 from 1-phenyl-1, 1-dichloro-3, 3-dimethyldisiloxane (22.0 g, 88 mmol), tetramethyldisiloxane-1, 3-diol (14.56 g, 88 mmol), and Et3N (18.6 g, 184 mmol) in 210 mL diethyl ether. 13.02 g (yield 43%), bp. 86 °C (1 mm Hg).'H NMR 8 : 0.17 (s, 6H), 0.24 (s, 6H), 0.26 (d, 6H, J = 2.5 Hz), 4.82 (sept. 1H, J = 2.5 Hz), 7.42 (m, 3H), 7.65 (m, 2H). 13C NMR 8 : 0.80,0.98,1.23,128.42,130.86,133.73, 134. 30. 9F NMR #: 29Si NMR # :-70.00 (1Si),-7. 27 (2Si),-3.90 (1Si). IR v: 2964, 2133,1431,1261,1133,1084,1021,998,902,851,808,771,699,641 cri '.

EXAMPLE 4 1-(Hydroxydimethylsiloxy)-1-phenyl-3,3,5,5-tetramethylcyclot risiloxane The preparation was carried out according to the procedure described in Example 2 from l-dimethylsiloxy-1-phenyl-3, 3,5,5-tetramethylcyclotrisiloxane from Example 2 (8.34 g, 24 mmol), distilled water (10 mL), catalyzed by 0.4 g 10 % Pd/C. 6.18 g

(yield 71 %), bp. 94°C (0.2 mm Hg.) 1H NMR 8 : 0.13 (s, 6H), 0.16 (s, 6H), 0.23 (s, 6H), 5.37 (s, 1H), 7.41 (m, 3H), 7.67 (m, 2H). 13C NMR 8 : 0.62,0.90,1.10,128.31, 130.72,134.38. 29Si NMR 8 :-71.73 (1Si),-11. 97 (1Si),-7. 35 (2Si). IR v: 3392,2964, 1595,1431,1262,1133,1189,1020,998,879,852,808,745,717,699,64 1,593 <BR> <BR> <BR> cm~'.<BR> <BR> <BR> <BR> <BR> <BR> <BR> <BR> <BR> <P>EXAMPLE 5 3'-Vinyl-1',1',3',3',-tetramethyldisiloxy-1,3,3,5,5-pentamet hylcyclotrisiloxane Vinyldimethylchlorosilane (4.0 g, 33 mmol) in 10 mL Et20 was added dropwise to a solution of 1-dimethylhydroxysiloxyl-1, 3,3,5,5-pentamethylcyclotrisiloxane prepared in Example 2 (4.85 g, 16 mmol), 60 mL Et20 and Et3N (4.0 g, 40 mmol) at RT during 20 min. After 5 h, the reaction was filtered. The filtrate was washed with water, dilute aqueous H3P04 and saturated NaHC03, to remove the triethylammonium chloride, dried over anhydrous MgS04 and filtered. Final product was obtained in 4.91 g (0.13 mol, yield 79 %) by fractional distillation at 50 °C / (0. 15 mm Hg).'H NMR 8 : 0.09 (s, 6H), 0.11 (s, 3H), 0.13 (s, 6H), 0.15 (d, 6H, = 0.5 Hz), 0.17 (s, 6H), 5.76 (dd, 1H, J = 21 and 4 Hz), 5.93 (dd, 1H, J = 15 and 4 Hz), 6.14 (dd, 1H, J = 21 and 15 Hz). ßC NMR 8 :-2. 73,0.36,0.77,0.93,1.07,132.08, 139.69.29Si NMR # :-58.11 (Si),-20. 30 (1Si),-8. 40 (2Si),-3.53 (1Si). IR v: 3052, 2965, 2906,1596,1408,1261,1068,1021,862,839,808,763,710,625 cl''.

EXAMPLE 6 Preparation of a linear siloxane polymer by cationic polymerization 3'-Vinyl-l', 1', 3', 3'-tetramethyldisiloxyl-1,3,3,5,5-pentamethylcyclotrisiloxan e from Example 5 (1.0 g, 2. 6 mmol) in 250 µL of 1,1,2-trichlorotrifluoroethane was cooled

to-78 °C and 5 iL trifluoromethane sulfonic acid (triflic acid) was injected into solution. Additional 1,1,2-trichlorotrifluoroethane (3 x 250 p. L) was added when the system became too viscous to permit stirring. The reaction was quenched after 0.5 h by addition of 20 mg, 0.12 mmol hexamethyldisilazane. Polymer was precipitated three times from a mixture of Et20/MeOH, and dried under vacuum for 12 h. In this way, 0.48 g (48 % yield) of polymer was obtained. 4/Mw = 83,900/28,300.'H NMR 8 : 0.08-0.18 (m, 27H), 5.75 (dd, 1H, J = 20.5 and 4 Hz), 5.92 (dd, 1H, J = 15 and 4 Hz), 6.13 (dd, 1H, J = 20.5 and 15 Hz). 13C NMR 8 :-2.04,-2.02,-0.39,1.11, 1.15,1.18,1.20,1.23,1.28,131.96,139.57.29SiNMR5:-67.17,-67.1 1,-21.93,- 21.92,-21.84,-21.76,-21.75,-21.68,-21.04,-3.95,-3.94. IR v: 3053,2964,2906, 1596,1408,1261,1094,1030,956,839,799,756,707,518 cm~'.

EXAMPLE 7 Preparation of a linear siloxane polymer by anionic polymerization a) Initiator Dilithium diphenylsilanolate was prepared by treatment of diphenylsilanediol with n-butyl lithium in THF. Styrene was used as an indicator (8). b) Anionic polymerization Initiator (22 ZL, 10 Amol) was injected to a solution of 3'-vinyl-1', 1', 3', 3'- tetramethyldisiloxyl-1, 3,3,5,5-pentamethylcyclotrisiloxane from Example 5 (1.0 g, 2.6 mmol) in 250 gL THF at RT. Polymerization was carried out for 24 h, after which it was quenched with vinyldimethylchlorosilane (0.1 g, 0.8 mmol). The polymer was precipitated three times with Et20/MeOH and dried in vacuum for 10 h, yielding 0.92 g (92 %) of product. MW/Mn = 29,100/12,400. TGA: Decomposition

begins at 425 °C. At 530 °C, 90 % of material is left. At 655 °C, half of the total weight is lost. Forty five percent residue is left at 850 °C.

EXAMPLE 8 Preparation of a linear siloxane polymer by anionic polymerization using a superbase The superbase (Phosphazene Base P4-t-Bu (1M in n-hexane) (2 pL, 2 pmol) was injected into solution of 3'-vinyl-1', 1', 3', 3'-tetramethyldisiloxyl-1, 3,3,5,5- pentamethylcyclotrisiloxane (1.0 g, 2. 6 mmol) in 2501lL THF at RT. After 0.5 h, reaction was quenched with dimethylvinylchlorosilane (0.1 g, 0.8 mmol). Volatiles were removed by vacuum. Reaction product was low viscous liquid, Mw/Mn = 8700/2100.

EXAMPLE 9 Preparation of a hyperbranched polymer by anionic polymerization The monomer (1-dimethylhydroxysiloxyl-1, 3,3,5,5-pentamethylcyclotrisiloxane), 2.0 g, 6.7 mmol and THF 1.0 mL were cooled to-9 °C and the base (P4-t-Bu) (8 pL, 8 Zmol) was injected. After 4 h, 1 mL THF, Et3N (2 mL, 7.3 mmol) and 1 mL vinyldimethylchlorosilane was added, and stirring was continued for 12 h. Polymer was extracted into hexamethyldisiloxane, washed with aq. NaCl and precipitated three times from THF/MeOH. Yield 2.47 g (96 %), M, ,/Mn = 15400/5900. 1H NMR S : 0.05-0.20 (m, 27H), 5.74 (dd, 0.65H, J = 20.5 and 4.5 Hz), 5.76 (dd, 0.35H, = 20.5 and 4.5 Hz), 5. 91 (dd, 0.65H, J = 14 and 4.5 Hz), 5.92 (dd, 0.35H, J = 14 and 4.5 Hz), 6.13 (dd, 0.65H, J = 20.5 and 14.5 Hz), 6.13 (dd, 0.35H, 20.5 and 14.5 Hz). ßC NMR 8 :-2.79,-2.11,0.25,0.36,0.75-1.23 (m), 131.84,131. 97,139.27,139.49.29Si

NMR 8 :-67.27,067.20,-67.14,-67.06,-66.20,-66.14,-66.06,-22.05,-21 .97,- 21.89,-21.82,-21.80,-21.76,-21.74,-21.11,-8. 55,-4.00,-3.66,-3.64. IR v: 3053, 2964,2906,1596,1408,1261,1093,1028,956,839,799,756,707,519 ci'.

EXAMPLE 10 Preparation of a hyperbranched polymer from 1-hydroxy-1, 3,3,5,5,- pentamethylcyclotrisiloxane, phenyldimethylsiloxy terminated THF (0.3 mL) and Phosphazene Base P4-t-Bu Solution (10 pL, Fluka Chemie AG) were placed into a test tube equipped with a Teflon covered magnetic stirbar and sealed with a rubber septum. It was cooled down to-15 °C and pentamethyl- cyclotrisiloxane-1-ol (1.70 g, 7. 57 mmol) was added slowly over a 30 min period.

The system was allowed to react at-15 °C for 5 hours followed by 4 days at RT after which Et3N (1.5 mL, 10.8 mmol), phenyldimethylchlorosilane (1.5 mL, 9.07 mmol), and 3 mL THF were added to end cap the polymer. After 24 hours, the solution was filtered and the ammonium salt discarded. The volatiles were evaporated under vacuum and the polymer was precipitated three times from Et2O/MeOH. Yield 1.72 g, (63.3 %). MWlMn = 32,020/11,320 (GPC), Mw/Mn = 62,980/13,240 (Light Scattering). Tg =-98 °C, Tm =-56 °C.'H NMR 8 : (m, 15.8H), 0.37 (m, 5.2H), 7.29 (s, 2.6H), 7.56 (s, 0.9M, 7.59 (s, 0. 8H). 13C NMR 8 :- 2.01 (m), 0.80 (m), 1.20 (m), 127.97,129.57,129.60,133.21,133.27,133.29,139.41, 139.44,139.64,139. 68. 29Si NMR 8 :-67.78,-67.34,-67.25,-66.29,-65.86,-65.79,- 21.73,-21.58,-21.53,-21.37,-21.34,-20.53,-8.29,-8.15,-2.25,- 2.12,-1.76,-1.62.

IR v: 3091,3072,3053,3025,3012,2963,2905,1592,1488,1429,1412,1261, 1120,1090,1027,999,857,831,800,755,726,699,668 cai'. TGA: 95 % left at 437 °C. 50 % left at 576 °C. After 600 °C, 25 % residue remains.

It will be appreciated that the methods of the present invention can be incorporated in the form of a variety of embodiments, only a few of which are disclosed herein. It will be apparent for the specialist in the field that other embodiments exist and do not depart from the spirit of the invention. Thus, the described embodiments are illustrative and should not be construed as restrictive.

REFERENCES 1. Rebrov, E. A; Vasilenko, N. G; Muzafarov, A. M; et al; Polym. Preprints, (1998) 39 (1), 479,481,581.

2. Kazakova, V; Myakushev, V; Strelkova, T; Muzafarov, A;. Preprints, (1998) 39 (1), 483.

3. Herzig, C; Deubzer, B; Polym Preprints, (1998) 39 (1), 477.

4. Uchida, H; Kabe, Y; Yoshino, K; Kawamata, A; Tsumuraya, T; Masamune, S; J.

Am. Chem. Soc. (1990) 112, 7077.

5. Rebrov, E. A; Muzafarov, A. M; Papkov, V. S; Zhdanov, A. A; Dokl. Akad Nauk.

SSSR, (1989). 309 (2), 367.

6. Morikawa, A; Kakimoto, M; Imai, Y; Macromolecules, (1991) 24 (12), 3469.

7. Harris, G. I., J. Chez Soc. (1963), 5978.

8. Battjes, K.; Kuo, C-M.; Miller, R. L.; Saam, J. C. Macromolecules (1995), 28, 790.

9. Masatoshi, A.; Sato, S. Jpn. Patent JP 61,167,694 [86,167,694], (1986), CA 106: P 102 803 p, (1987).