Photocurable compositions are cured by exposure to radiation, usually ultraviolet radiation, and include for example, lacquers which may be applied to wood, metal or similar substrates by suitable techniques such as roll coating or curtain coating. They may also be formulated as inks, for example to be applied by techniques such as letterpress, offset lithography, rotogravure printing, silk screen printing, inkjet or flexographic printing. Printing, depending on the particular printing technique, is applicable to a wide range of substrates which include paper, board, glass, plastics materials or metals. Other application areas will include adhesives, powder coatings, circuit boards and microelectronic products, sterolithography, composites, optical fibres and liquid crystals.

Initiation of polymerisation in a monomer or prepolymer may be effected in a number of ways.

One such way is by irradiation, for example with ultraviolet radiation, in which case it is normally necessary that the polymerisable composition should contain an initiator, commonly referred to as a "photoinitiator", or alternatively by an electron beam. There are two main types of curing chemistry which can be used in this process; free radical and cationic. Although cationic curing has many advantages, its disadvantages, particularly with regard to the photoinitiators used, leads it to be used only in a minority of applications. Most frequently used cationic initiators are either organic iodonium or sulphonium salts.

Briefly, the mechanism by which a sulphonium cationic initiator acts when irradiated is that it forms an excited state which then breaks down to release a radical cation. This radical cation reacts with the solvent, or another hydrogen atom donor, generating a protonic acid. The active species is the protonic acid. However, amongst the breakdown products of sulphonium salts are aromatic sulphides, such as diphenyl sulphide, which are malodorous and can be a health hazard, and lower aromatic hydrocarbons, such as benzene, which are potentially carcinogenic. Many of the commonly used iodonium salts break down to give volatile species such as benzene, toluene or isobutyl benzene.

This places severe restrictions upon the applications for which such cationic photoinitiators can be used. For example, they cannot be used in printing inks on packaging intended for food and, in some cases, cannot be used at all where the packaging is to be handled by the consumer. Indeed, as the industry becomes ever more conscious of health matters, it is increasingly difficult to use such compounds at all.

However, this, although important, is not the only constraint upon the choice of compound to be used as a cationic photoinitiator. Even without consideration of the health issues, the cleavage products of the known cationic photoinitiators are malodorous, and it is highly desirable that unpleasant odours should be minimised. This leads to a desire that the cleavage products should be relatively non-volatile and non-odorous. The cationic photoinitiators must, of course, also be sufficiently stable, both as isolated compounds and when in the uncured coating formulation. They must also be soluble in or miscible with other components of the uncured coating formulation.

Finally, they should be able to absorb radiation over a suitable and sufficiently wide range of wave lengths, ideally without the use of a sensitiser.

What is more, the nature of the cationic photoinitiator can have a major impact on the properties of the cured coating. The cationic photoinitiator should produce a coating which is fully cured, hard and resistant to common solvents and abuse.

Finally, there are a number of practical problems associated with the manufacture of the compounds used as cationic photoinitiators, including the necessity that they should be relatively easy and inexpensive to manufacture.

Thus, it would be desirable to provide a cationic photoinitiator which does not generate malodorous or toxic by-products upon radiation cure, particularly diphenyl sulphide and benzene, and which possesses the following properties: good solubility, good cure performance, good adhesion to substrates and reasonable cost.

Not surprisingly, complying with all of these, often conflicting, requirements is not easy, and we are not aware of any completely satisfactory commercial solution available until now.

However, we have now discovered a series of new compounds, including thioxanthone derivatives, many of which have the advantages of good solubility in the coating composition combined with excellent cure. These compounds have a biphenylyl or phenoxy-or benzyl-substituted phenyl group attached to the thioxanthone or analogous ring. In addition, the potential by-products of these new compounds would be thioxanthone derivatives typical of those used widely in free-radical curing inks for food packaging, and biphenyl, which is itself an approved antioxidant food additive in Europe.

Compounds of this general type are covered in general terms inUS 4 161 478, although these lack the solubility of the compounds of the present invention, and the US Patent does not specifically disclose such compounds. Indeed, the US Patent is silent on the nature of the ring system attached to the thioxanthone or analogous ring system, although we have found that the nature of this ring system is highly important to the achievement of good solubility and cure. Also, a biphenyl-substituted dibenzothiophene compound is disclosed by Sato et al. [Phosphorus, Sulfur, and Silicon, 1994, Vol 95-96, pp 447-448], but no use is suggested for the resulting compounds. Similarly, a biphenyl- substituted thianthrene is disclosed by Kim and Kim (J. Heterocyclic Chem. , 1998, Vol 35, pages 235-247), but this has only been prepared as a salt with a perchlorate anion, and no use is suggested for the compound other than in further synthetic chemistry.

Thus, the present invention consists in compounds of formula (I) :

in which: RI represents a direct bond, an oxygen atom, a group >CH2, a sulphur atom, a group >C=O, a group- (CH2) 2- or a group of formula-N-Ra, where Ra represents a hydrogen atom or an alkyl group having from 1 to 12 carbon atoms; R4, R5, R6 and R7 are individually the same or different and each represents a hydrogen atom or a group or atom selected from substituents a, defined below, provided that, when R1 represents a group >C=O, then at least one of R4, R5, R6 and R7 represents a substituent a; R8, R9, R10 and Rl l are individually the same or different and each represents a hydrogen atom, a hydroxy group, or an alkyl group having from 1 to 4 carbon atoms; or R9 and RI I are joined to form a fused ring system with the benzene rings to which they are attached; R12 represents a direct bond, an oxygen atom or a methylene group; said substituents a are: an alkyl group having from 1 to 20 carbon atoms, an alkoxy group having from 1 to 20 carbon atoms, an alkenyl group having from 2 to 20 carbon atoms, a halogen atom, a nitrile group, a hydroxyl group, an aryl group having from 6 to 10 carbon atoms, an aralkyl group having from 7 to 13 carbon atoms, an aryloxy group having from 6 to 10 carbon atoms, an aralkyloxy group having from 7 to 13 carbon atoms, an arylalkenyl group having from 8 to 12 carbon atoms, a cycloalkyl group having from 3 to 8 carbon atoms, a carboxy group, a carboxyalkoxy group having from 2 to 7 carbon atoms, an alkoxycarbonyl group having from 2 to 7 carbon atoms, an aryloxycarbonyl group having from 7 to 13 carbon atoms, an alkylcarbonyloxy group having from 2

to 7 carbon atoms, an alkanesulphonyl group having from 1 to 6 carbon atoms, an arenesulphonyl group having from 6 to 10 carbon atoms, an alkanoyl group having from 1 to 6 carbon atoms or an arylcarbonyl group having from 7 to 11 carbon atoms; and X'represents an anion, provided X'does not represent an alkoxy, hydroxyalkoxy or aryloxy group when RI represents a direct bond; and esters thereof.

These compounds are useful as photoinitiators for use in energy, e. g. UV, curable coating compositions, including varnishes, lacquers and printing inks, most especially printng inks.

The compounds of the present invention may, as described above, be used as cationic photoinitiators for radiation-curable coating compositions. Thus, the present invention also provides an energy-curable composition comprising: (a) a polymerisable monomer, prepolymer or oligomer, especially a material which undergoes acid-catalysed ring opening polymerisation, e. g. an epoxide (oxirane) or oxetane, or an ethylenically unsaturated material, such as vinyl or propenyl ethers and (b) a cationic photoinitiator which is a compound of formula (I), as defined above, or an ester thereof.

The invention still further provides a process for preparing a cured polymeric composition by exposing a composition of the present invention to curing energy, preferably ultraviolet radiation.

In the compounds of the present invention, we prefer those compounds of formula (I) in which RI represents a group >C=O, a sulphur atom or a direct bond, and especially those in which represents a group >C=O.

More preferred are those compounds of formula (I) in which the residue of formula (A): is a residue of substituted or unsubstituted thianthrene, dibenzothiophene, thioxanthone, thioxanthene, phenoxathiin or phenothiazine, especially those in which said residue is a substituted thioxanthone.

Where R4, R5, R6 or R7 represents an alkyl group having from 1 to 20, preferably from 1 to 10, more preferably from 1 to 6 and most preferably from 1 to 3, carbon atoms, this may be a straight or branched chain group, and examples of such groups include the methyl, ethyl, propyl, isopropyl, butyl, isobutyl, t-butyl, pentyl, isopentyl, neopentyl, 2-methylbutyl, 1-ethylpropyl, 4-methylpentyl, 3- methylpentyl, 2-methylpentyl, l-methylpentyl, 3, 3-dimethylbutyl, 2, 2-dimethylbutyl, 1, 1- dimethylbutyl, 1,2-dimethylbutyl, 1, 3-dimethylbutyl, 2,3-dimethylbutyl, 2-ethylbutyl, hexyl, isohexyl,

heptyl, octyl, nonyl, decyl, dodecyl, tridecyl, pentadecyl, octadecyl, nonadecyl and icosyl groups, but preferably the methyl, ethyl, propyl, isopropyl and t-butyl groups, and most preferably the ethyl or isopropyl group. Ra may be any of the groups having from 1 to 12 carbon atoms exemplified above, especially those having from 1 to 6 carbon atoms, and preferably the methyl group.

Where R4, R5, R6 or R7 represents an alkoxy group having from 1 to 20, preferably from 1 to 10, more preferably from 1 to 6 and most preferably from 1 to 3, carbon atoms, this may be a straight or branched chain group, and examples of such groups include the methoxy, ethoxy, propoxy, isopropoxy, butoxy, isobutoxy, t-butoxy, pentyloxy, isopentyloxy, neopentyloxy, 2-methylbutoxy, 1- ethylpropoxy, 4-methylpentyloxy, 3-methylpentyloxy, 2-methylpentyloxy, 1-methylpentyloxy, 3,3- dimethylbutoxy, 2,2-dimethylbutoxy, 1,1-dimethylbutoxy, 1,2-dimethylbutoxy, 1,3-dimethylbutoxy, 2,3-dimethylbutoxy, 2-ethylbutoxy, hexyloxy, isohexyloxy, heptyloxy, 2-ethylhexyloxy, octyloxy, nonyloxy, decyloxy, dodecyloxy, tridecyloxy, pentadecyloxy, octadecyloxy, nonadecyloxy and icosyloxy groups, but preferably the methoxy, ethoxy, t-butoxy and 2-ethylhexyloxy groups, and most preferably the 2-ethylhexyloxy group.

Where R4, R5, R6 or R7 represents an alkenyl group having from 2 to 20, preferably from 2 to 10, more preferably from 2 to 6 and most preferably from 2 to 4, carbon atoms, this may be a straight or branched chain group, and examples of such groups include the vinyl, 1-propenyl, allyl, isopropenyl, methallyl, butenyl, pentenyl, hexenyl, heptenyl, octenyl, nonenyl, decenyl, dodecenyl, tridecenyl, pentadecenyl, octadecenyl, nonadecenyl and icosenyl groups, but preferably the allyl, methallyl and butenyl groups, and most preferably the allyl group.

Where R4, R5, R6 or R7 represents a halogen atom, this may be, for example, a fluorine, chlorine, bromine or iodine atom, preferably a chlorine atom.

Where R4, R5, R6 or R7 represents an aryl group, this has from 6 to 10 carbon atoms in one or more aromatic carbocyclic rings (which, if there are more than one, may be fused together). Such a group may be substituted or unsubstituted, and, if substituted, the substituent (s) is preferably an alkyl or alkoxy group (as defined above), or an alkoxycarbonyl group (as defined below). Preferred aryl groups are the phenyl and naphthyl (1-or 2-) groups, the phenyl group being most preferred.

Where R4, R5, R6 or R7 represents an aryloxy group, this may be any of the aryl groups above bonded to an oxygen atom, and examples include the phenoxy and naphthyloxy groups.

Where R4, R5, R6 or R7 represents an aralkyl group, this is an alkyl group having from I to 4 carbon atoms which is substituted by one or two aryl groups as defined and exemplified above.

Examples of such aralkyl groups include the benzyl, a-phenylethyl, (3-phenylethyl, 3-phenylpropyl, 4- phenylbutyl, diphenylmethyl, 1-naphthylmethyl and 2-naphthylmethyl groups, of which the benzyl group is preferred.

Where R4, R5, R6 or R7 represents an aralkyloxy group, this may be any of the aralkyl groups above bonded to an oxygen atom, and examples include the benzyloxy, a-phenylethoxy, ß- phenylethoxy, 3-phenylpropoxy, 4-phenylbutoxy, diphenylmethoxy, 1-naphthylmethoxy and 2- naphthylmethoxy groups, of which the benzyloxy group is preferred.

Where R4, R5, R6 or R7 represents an arylalkenyl group having from 8 to 12 carbon atoms, the aryl and alkenyl parts of this group may be as defined and exemplified above for the respective component parts. Specific examples of such groups are the styryl and cinnamyl groups.

Where R4, R5, R6 or R7 represents a cycloalkyl group having from 3 to 8 carbon atoms, this may be, for example, the cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl or cyclooctyl group.

Where R4, R5, R6 or R7 represents a carboxyalkoxy group, this may be any of the alkoxy groups having from 1 to 6 carbon atoms described above which is substituted by a carboxy group.

Preferred examples include the carboxymethoxy, 2-carboxyethoxy and 4-carboxybutoxy groups, of which the carboxymethoxy group is preferred.

Where R4, R5, R6 or R7 represents an alkoxycarbonyl group, this has from 1 to 6 carbon atoms in the alkoxy part, and thus a total of from 2 to 7 carbon atoms. It may be a straight or branched chain group, and examples of such groups include the methoxycarbonyl, ethoxycarbonyl, propoxycarbonyl, isopropoxycarbonyl, butoxycarbonyl, isobutoxycarbonyl, t-butoxycarbonyl, pentyloxycarbonyl, isopentyloxycarbonyl, neopentyloxycarbonyl, 2-methylbutoxycarbonyl, I- ethylpropoxycarbonyl, 4-methylpentyloxycarbonyl, 3-methylpentyloxycarbonyl, 2- methylpentyloxycarbonyl, 1-methylpentyloxycarbonyl, 3, 3-dimethylbutoxycarbonyl, 2,2- dimethylbutoxycarbonyl, 1, 1-dimethylbutoxycarbonyl, 1, 2-dimethylbutoxycarbonyl, 1,3- dimethylbutoxycarbonyl, 2, 3-dimethylbutoxycarbonyl, 2-ethylbutoxycarbonyl, hexyloxycarbonyl and isohexyloxycarbonyl groups, but preferably the methoxycarbonyl, ethoxycarbonyl and t- butoxycarbonyl groups, and most preferably the methoxycarbonyl or ethoxycarbonyl group.

Where R4, R5, R6 or R7 represents an aryloxycarbonyl group having from 7 to 13 carbon atoms, the aryl part of this may be any of the aryl groups defined and exemplified above. Specific examples of such groups include the phenoxycarbonyl and naphthyloxycarbonyl groups.

Where R4, R5, R6 or R7 represents an alkylcarbonyloxy group having from 2 to 7 carbon atoms, this may be any of the alkoxycarbonyl groups defined and exemplified above bonded to an oxygen atom.

Where R4, R5, R6 or R7 represents an alkanesulphonyl group, this has from 1 to 6 carbon atoms and is a straight or branched chain group. Examples of such groups include the methanesulphonyl, ethanesulphonyl, propanesulphonyl, isopropanesulphonyl, butanesulphonyl,

isobutanesulphonyl, t-butanesulphonyl, pentanesulphonyl and hexanesulphonyl groups, of which the methanesulphonyl group is preferred.

Where R4, R5, R6 or R7 represents an arenesulphonyl group, the aryl part may be as defined and exemplified above, and examples include the benzenesulphonyl andp-toluenesulphonyl groups.

Where R4, R5, R6 or R7 represents an alkanoyl group having from 1 to 6 carbon atoms, and preferably from 1 to 4 carbon atoms, this may be a straight or branched chain group, and examples include the formyl, acetyl, propionyl, butyryl, isobutyryl, pivaloyl, valeryl, isovaleryl, and hexanoyl groups, of which the acetyl group is most preferred; Where R4, R5, R6 or R7 represents an arylcarbonyl group, the aryl part has from 6 to 10, more preferably 6 or 10, and most preferably 6, ring carbon atoms and is a carbocyclic group, which is unsubstituted or has from 1 to 5, preferably from 1 to 3 substituents, as defined and exemplified above. The preferred groups are the benzoyl and naphthoyl groups.

We particularly prefer those compounds of formula (I) in which R4, R5, R6 and R7 are individually the same or different and each represents a hydrogen atom, an alkyl group having from 1 to 10 carbon atoms, an alkoxy group having from 1 to 10 carbon atoms, a halogen atom, or a cycloalkyl group having from 3 to 8 carbon atoms, more especially those in which two or three of R4, R5, R6 and R7 represent hydrogen atoms, and most preferably those in which one or two of R4, R5, R6 and R7 represents an ethyl or isopropyl group. The most preferred compounds are those in which one or two of R4, R5, R6 and R7 represent ethyl groups or in which one of R4, R5, R6 and R7 represents an isopropyl group and the others represent hydrogen atoms.

Where R8, R9, RIO or Rll represents an alkyl group, this may be a straight or branched chain alkyl group having from 1 to 4 carbon atoms, and examples include the methyl, ethyl, propyl, isopropyl, butyl, isobutyl and t-butyl groups, of which the methyl group is preferred.

We prefer those compounds of formula (I) in which two, three or four of R8, R9, R10 and R I I represent hydrogen atoms, and especially those in which all of R8, R9, RIO and Rll represent hydrogen atoms.

When R9 and Rll, together with the benzene rings to which they are attached, form a fused ring system, this may be, for example, a biphenylene, fluorene or phenanthrene system, preferably fluorene.

R12 may be a direct bond (so that the two groups joined by R12 together form a biphenylyl group), an oxygen atom (so that the two groups joined by R12 together form a phenoxyphenyl group), or a methylene group (so that the two groups joined by R12 together form a benzylphenyl group).

X represents an anion. In general, there is no particular limitation on the nature of the anion to be used. However, where the compounds of the present invention are to be used as photoinitiators, the anion should be non-nucleophilic, or essentially non-nucleophilic, as is well known in the art. It should also be relatively bulky. If the compounds are not to be used as photoinitiators, the anion need not meet these requirements. For example, in some cases, it may be desirable not to store the compound in the form of the salt which is ultimately to be used. In that case, it may be preferable to form another salt, and then convert the compound to the desired salt at or close to the point of use. In such a case, it is not necessary that the anion should be non-nucleophilic.

Examples of non-nucleophilic anions are well known to those skilled in the art, and include anions of formula Mon where M represents a phosphorus, boron, antimony, arsenic, chlorine or carbon atom, Z represents a halogen atom except where M represents a halogen atom, an oxygen atom or a sulphite group, and n is an integer dependent upon the valence of M and Z. Preferred examples of such groups include the PF6, SbF6, AsF6-, BF4, B (C6F5) 4, RaB (Ph) 3 (where Ra represents an alkyl group having from 1 to 6 carbon atoms and Ph represents a phenyl group), RbS03- (where Rb represents an alkyl or haloalkyl group having from 1 to 6 carbon atoms or an aryl group), C104 and ArSO3 (where Ar represents an aryl group) groups, of which the PF6, SbF6, AsF6-, CF3SO3 and BF4 groups are preferred and the PF6 group is most preferred.

Where the compounds of the present invention contain a carboxy group, i. e. where R4, R5, R6 or R7 represents a carboxy or carboxyalkoxy group, the resulting compounds may form esters, and these esters also form a part of the present invention. There is no particular limitation on the nature of the ester, other than those constraints well known to those skilled in the art, and preferred examples of esters include the alkyl esters, particularly those having from 1 to 12 carbon atoms, such as those containing the C 1-C 12 alkyl groups, and those derived from a polyalkylene glycol ether ester (especially the C 1-C4 alkyl ethers), such as esters containing groups of formula: - [OR13] xOR14 where Rl3 represents an alkylene group having from 1 to 8 carbon atoms, R14 represents an alkyl group having from 1 to 4 carbon atoms, and x is a number from 2 to 20, preferably from 5 to 10.

More preferred are groups of formula: -[OCH2CHR15] XoRl4 where R14 and x are as defined above and R15 represents an alkyl group having from 1 to 4 carbon atoms.

Where R8, R9, RIO or R1l represents a hydroxy group, the resulting compounds may also form esters with acids. Examples of such esters are given in"Protective Groups in Organic Synthesis"by T. W. Greene and P. G. M. Wuts, Second Edition, 1991, published by John Wiley & Sons, Inc.

Any combination of the preferred substituent groups and atoms listed above in respect of Rl, R4, R5, R6, R7, R8, R9, RIO, RI 1, RI 2, is also envisaged by the present invention.

Particularly preferred compounds of the present invention having an especially good combination of good cure and good solubility in coating compositions are those compounds of formula (I) in which: R4, R5, R6 and R7 are individually the same or different and each represents a hydrogen atom or an alkyl group having from 1 to 4 carbon atoms; R12 represents a direct bond; and R8, R9, R10 and R I I represent hydrogen atoms.

The compounds of the present invention may be prepared by reacting a sulphoxide corresponding to ring system (A) with the compound corresponding to the biphenylyl, phenoxyphenyl or benzylphenyl ring system in the presence of an acid, as shown in the following scheme:

In the above formulae, RI, R4, R5, R6, R7, R8, R9, RIO and RI 1 are as defined above, and Y' represents an anion, which will normally be derived from the reaction. Where any one or more of R8, R9, RIO, or RI I represents a hydroxy group, this is preferably protected, since it otherwise may react with the acid used in the reaction. The nature of the protecting group used is not critical to the invention, and any protecting group known in the art for use in compounds ofthis type may equally be used here. Examples of suitable protecting groups are described in"Protective Groups in Organic Synthesis"by T. W. Greene and P. G. M. Wuts, Second Edition, 1991, published by John Wiley & Sons, Inc.

The reaction is normally and preferably effected in a solvent, the nature of which is not critical, provided that it has no adverse effect on the reagents or on the reaction and provided that it can dissolve the reagents, at least to some extent. A suitable solvent is acetic acid.

The reaction is also preferably effected in the presence of a strong acid. Preferred is a combination of concentrated sulphuric acid and acetic anhydride.

A suitable reaction temperature is preferably below 15°C.

The sulphoxide of formula (II) may be prepared by well known methods.

Using the reaction scheme above, it is possible to obtain yields in excess of 90% in each reaction step, which assists the economics of the process.

In general, the anion Y-will not be the anion C which it is desired to incorporate in the final product. If so, then the desired anion may be introduced by an anion exchange reaction, as is well known in the field of synthetic chemistry.

Where a protected hydroxy group represented by R8, R9, RIO, or RI I is present, the protecting group may, if desired, be removed by methods well known to those skilled in the art, as described in"Protective Groups in Organic Synthesis"above.

The compounds of the invention may then be separated from the reaction mixture by well known techniques and, if desired, further purified.

The composition of the present invention may be formulated as a printing ink, varnish, adhesive or any other coating composition which is intended to be cured by irradiation, whether by ultraviolet or electron beam. Such compositions will normally contain at least a polymerisable monomer, prepolymer or oligomer, and the cationic photoinitiator of the present invention, but may also include other components well known to those skilled in the art, for example, reactive diluents and, in the case of printing inks, a pigment.

A wide variety of monomers and prepolymers may be subjected to cationic photoinitiation using the compounds of the present invention as photoinitiators, and the nature of the monomers and prepolymers is not critical to the present invention. Such monomers and prepolymers typically contain cationically polymerisable groups, and general examples of such compounds include the

epoxides, oxetanes, other cyclic ethers, vinyl compounds (such as vinyl and propenyl ethers, styrene and its derivatives and unsaturated polyesters), unsaturated hydrocarbons, lactones and, in the case of hybrid systems, acrylates and methacrylates.

Typical epoxides which may be used include the cycloaliphatic epoxides (such as those sold under the designations UVR6110 by Union Carbide or UVACURE 1500 by UCB), which are well known to those skilled in the art.

Other epoxy-functional oligomers/monomers which may be used include the glycidyl ethers of polyols [bisphenol A, alkyl diols or poly (alkylene oxides), which be di-, tri-, tetra-or hexa- functional]. Also, epoxides derived by the epoxidation of unsaturated materials may also be used (e. g. epoxidised soybean oil, epoxidised polybutadiene or epoxidised alkenes). Naturally occurring epoxides may also be used, including the crop oil collected from Vernonia galamensis.

As well as epoxides, other reactive monomers/oligomers which may be used include the vinyl ethers of polyols [such as triethylene glycol divinyl ether, 1, 4-cyclohexane methanol divinyl ether and the vinyl ethers of poly (alkylene oxides) ]. Examples of vinyl ether functional prepolymers include the urethane-based products supplied by Allied Signal. Similarly, monomers/oligomers containing propenyl ether groups may be used in place of the corresponding compounds referred to above containing vinyl ether groups.

Similarly, compounds bearing oxetane groups may be used in place of the corresponding compounds referred to above containing epoxide groups. A typical oxetane is that derived from trimethylolpropane (3-ethyl-3-hydroxymethyloxetane).

Other reactive species can include styrene derivatives and cyclic esters (such as lactones and their derivatives).

It is also common to include polyols in ultraviolet cationic curable formulations, which promote the cross-linking by a chain-transfer process. Examples of polyols include the ethoxylated/propoxylated derivatives of, for example, trimethylolpropane, pentaerythritol, di- trimethylolpropane, di-pentaerythritol and sorbitan esters, as well as more conventional poly (ethylene oxide) s and poly (propylene oxide) s. Other polyols well known to those skilled in the art are the polycaprolactone diols, triols and tetraols, such as those supplied by Union Carbide.

Additives which may be used in conjunction with the principal components of the coating formulations of the present invention include stabilisers, plasticisers, pigments, waxes, slip aids, levelling aids, adhesion promoters, surfactants and fillers. Also, compounds which act as sensitisers for the photoinitiator, such as thioxanthone (and derivatives), benzophenone (and derivatives), hydroxyalkylphenones, anthracene (and derivatives), perylene, xanthone, pyrene and anthraquinone, may be included.

The compounds of the present invention may be included as photoinitiators in coating formulations such are well known in the art, and the precise composition of such formulations will

vary depending upon the other components and the intended use, as is well known. However, a typical formulation for an ink coatable by flexography might be: Pigment 8-20% Photoinitiator 2-6% Monomer/prepolymer/oligomer 30-90% Polyol 0-30% Additives 0-10% In order to enhance the solubility of the compounds of the present invention in the curable composition, they may first be dissolved in a suitable solvent, for example propylene carbonate.

The invention is further illustrated by the following non-limiting Examples.

EXAMPLE 1 Preparation of isopropylthioxanthone sulphoxide

10. Og of ITX (isopropylthioxanthone) (0.03937moles) were dissolved in 630ml of a mixture of acetonitrile and water (75% acetonitrile, 25% water). Gentle heating was required to dissolve the isopropylthioxanthone (35°C). 86.34g of Ceric ammonium nitrate (0. 15748moles) were added in one batch. The reaction was followed by thin layer chromatography (TLC). The reaction mixture was then stirred for 1 hour at room temperature. 400ml of water was then added and the mixture was extracted with 1000ml of diethyl ether. The ether layers were combined and dried with magnesium sulphate, and the ether was removed on a rotary evaporator to yield the product.

Product yield 9.92g (93.32%) of a yellow solid.

The product was analysed by HPLC, LC-MS and IR EXAMPLE 2

2.025g (0. 0075moles) of the compound of Example 1, biphenyl (1.604g, 0.01040moles), acetic acid (7ml), dichloromethane (1. 75ml) and acetic anhydride (7ml) were mixed in round bottomed flask.

The temperature of the mixture was reduced to <15°C using a water/ice bath. Concentrated sulphuric acid (2. 6ml) was then added drop wise, making sure the temperature did not exceed 15°C. After the addition was complete, the mixture was stirred for 2 hours, allowing the temperature to increase to room temperature. 100ml of water was then added to the mixture. This was then extracted with - 200m ! (2xl00mt) of dichloromethane. The dichloromethane was then removed on a rotary evaporator. This yielded 7.17g of intermediate product. This was dissolved in a minimum of acetic acid. The solution was then poured into a KPF6 solution (4g in 130ml water). This appeared to yield a viscous liquid. This was extracted with dichloromethane. The dichloromethane layer was then dried with magnesium sulphate, and the solvent was removed on a rotary evaporator to yield the product. A second extraction was also carried out by dissolving the product in dichloromethane and extracting with water, re-drying the dichloromethane and removing the dichloromethane using a rotary evaporator.

Product yield 4.12g (99.5%) of a brown pasty solid.

The product was analysed by HPLC, LC-MS and IR EXAMPLE 3

10. Og (0. 03731moles) of 2,4-diethylthioxanthone (DETX) were dissolved in 630ml of a mixture of acetonitrile and water (75% acetonitrile, 25% water). Gentle heating was required to dissolve the DETX (45°C). 81.79g of Ceric ammonium nitrate (0. 1492moles) were added in one batch. The reaction was followed by TLC. The reaction mixture was stirred for 45minutes. At this stage TLC indicated that the reaction was complete. The reaction mixture was allowed to cool to room temperature and 400ml of water was then added. The mixture was extracted with 1000ml of diethyl ether. The ether layers were combined and dried with magnesium sulphate, and the ether was removed on a rotary evaporator to yield the product. At this stage the product still contained some inorganic residue. The product was therefore re-dissolved in diethyl ether, washed with water and dried with magnesium sulphate. The ether was then removed on a rotary evaporator to yield the product.

Product is a yellow solid, yield not recorded.

The product was analysed by HPLC, LC-MS and IR.

EXAMPLE 4

2. Og (0. 00704moles), DETX sulphoxide from Example 3, biphenyl (1.503g, 0.0098moles), acetic acid (7ml), dichloromethane (1. 75ml) and acetic anhydride (7ml) were mixed in round bottomed flask. The temperature of the mixture was reduced to <15°C using a water/ice bath.

Concentrated sulphuric acid (2. 6ml) was then added drop wise, making sure the temperature did not exceed 15°C. After the addition was complete, the mixture was stirred for 2 hours, allowing the temperature to increase to room temperature. 100ml of water was then added to the mixture. This was then extracted with-200ml (2xlOOml) of dichloromethane. The dichloromethane was then dried with magnesium sulphate, filtered and removed on a rotary evaporator. This yielded-4. 0g of intermediate product. This was dissolved in a minimum of acetic acid. The solution was then poured into a KPF6 solution (2g in 65ml water). This appeared to yield a viscous liquid. This was extracted with dichloromethane. The dichloromethane layer was washed with 3xlOOml water and then dried with magnesium sulphate, and the solvent was removed on a rotary evaporator to yield the product.

Product yield 2.12g (53.2%) of a brown pasty solid.

The product was analysed by HPLC, LC-MS and IR.

EXAMPLE 5 Preparation of 2-isopropylthioxanthone sulphoxide 10. Og (0. 03937moles) of 2-isopropylthioxanthone were dissolved in 630mol of a mixture of acetonitrile and water (75% acetonitrile, 25% water). Gentle heating was required to dissolve the 2- isopropylthioxanthone (35°C). The temperature was then allowed to return to room temperature.

86.336g of Ceric ammonium nitrate (0.15748moles) were added in one batch. The reaction was followed by TLC. The reaction mixture was stirred for 2.5 hours at room temperature. 400mol of water was then added and the mixture was extracted with 1000ml of diethyl ether. The ether layers were combined and dried with magnesium sulphate, and the ether was removed on a rotary evaporator to yield the product. At this stage the product still contained some inorganic residue. The product was therefore re-dissolved in diethyl ether, washed with water and dried with magnesium sulphate.

The ether was then removed on a rotary evaporator to yield the product.

Product yield 5.54g (52.3%) of a yellow solid.

The product was analysed by HPLC, LC-MS and IR EXAMPLE 6

2.025g 2-isopropylthioxanthone sulphoxide (0. 0075moles) from Example 5, biphenyl (1.604g, 0. 01040moles), acetic acid (7ml), dichloromethane (1. 75ml) and acetic anhydride (7moi) were mixed in a round bottomed flask. The temperature of the mixture was reduced to <15°C using a water/ice bath.

Concentrated sulphuric acid (2. 6ml) was then added drop wise, making sure the temperature did not exceed 15°C. After the addition was complete, the mixture was stirred for 2 hours, allowing the temperature to increase to room temperature. 100ml of water was then added to the mixture. This was then extracted with ~200ml (2xlOOml) of dichloromethane. The dichloromethane was then dried with magnesium sulphate, filtered and removed on a rotary evaporator. This yielded 4. Og of intermediate product. This was dissolved in a minimum of acetic acid. The solution was then poured into a KPF6 solution (2g in 65ml water). This appeared to yield a viscous liquid. This was extracted with dichloromethane. The dichloromethane layer was then dried with magnesium sulphate and the solvent was removed on a rotary evaporator to yield the product. There was still an odour of acetic acid. Therefore the product was dissolved in dichloromethane (100ml), and rewashed with 3xlOOml water. The dichloromethane was dried with magnesium sulphate and filtered, and then the dichloromethane was removed on a rotary evaporator to yield the product.

Product yield 2.54g (61.2%) of a brown pasty solid.

The product was analysed by HPLC, LC-MS and IR.

EXAMPLE 7

9. 71g of 2-chlorothioxanthone (0.03937moles) were dissolved in 630ml of a mixture of acetonitrile and water (75% acetonitrile, 25% water). A further 75ml of acetonitrile and heating was required to try to dissolve the 2-chlorothioxanthone (65°C). However, the 2-chlorothioxanthone was still not soluble but the reaction was carried out anyway. 86.336g of Ceric ammonium nitrate (0. 15748moles) were added in one batch. The reaction was followed by TLC. The reaction mixture was stirred for 90mins at 65°C. 400ml of water was then added which crystallised the product. The product was collected by filtration and dried in a vacuum oven.

Product yield 6.96g (67.3%) of a yellow solid.

The product was analysed by HPLC, LC-MS and IR.

EXAMPLE 8

1.97g 2-Chlorothioxanthone sulphoxide (0. 0075moles) from Example 7, biphenyl (1.604g, 0.01040moles), acetic acid (7ml), dichloromethane (1. 75ml) and acetic anhydride (7ml) were mixed in a round bottomed flask. The temperature of the mixture was reduced to <15°C using a water/ice bath.

Concentrated sulphuric acid (2. 6ml) was then added drop wise, making sure the temperature did not exceed 15°C. After the addition was complete, the mixture was stirred for 2 hours, allowing the temperature to increase to room temperature. 100mol of water was then added to the mixture. This was then extracted with-200ml (2xl00ml) of dichloromethane. The dichloromethane was then removed on a rotary evaporator. This yielded 5.39g of intermediate product. This was dissolved in a minimum of acetic acid. The solution was then poured into a KPF6 solution (2. 5g in 75ml water).

This appeared to yield a viscous liquid. This was extracted with dichloromethane. The dichloromethane layer was then dried with magnesium sulphate and the solvent was removed on a rotary evaporator to yield the product.

Product yield 3.42g (83. 71 %) of a brown pasty solid.

The product was analysed by HPLC, LC-MS and IR.

EXAMPLE 9

! 0. 0g (0.0328moles) of 1-chloro-4-propoxythioxanthone (CPTX) were dissolved in 630mol of a mixture of acetonitrile and water (75% acetonitrile, 25% water). Gentle heating was required to dissolve the CPTX (50°C). 71.93g of Ceric ammonium nitrate (0.1312moles) were added in one batch. The reaction was followed by TLC. The reaction mixture was stirred for 1 hour. At this stage TLC indicated that the reaction was complete. The reaction was allowed to cool to room temperature and 400ml of water added. A small amount of precipitate formed. The mixture was extracted with 1000ml of diethyl ether. The ether solution was dried with magnesium sulphate, and the ether was removed on a rotary evaporator to yield the product that was subsequently dried in a vacuum oven.

Product yield 6.74g (72.7%) of a yellow/orange solid.

The product was analysed by HPLC, LC-MS and IR.

EXAMPLE 10

2.4g (0. 0075moles) of CPTX sulphoxide from Example 9, biphenyl (1.6g, 0. 0104moles), acetic acid (7ml), dichloromethane (1. 75ml) and acetic anhydride (7ml) were mixed in a round bottomed flask. The temperature of the mixture was reduced to <15°C using a water/ice bath.

Concentrated sulphuric acid (2. 6ml) was then added drop wise, making sure the temperature did not exceed 15°C. After the addition was complete, the mixture was stirred for 2 hours, allowing the temperature to increase to room temperature. 100moi of water was then added to the mixture. This was then extracted with-200ml (2xlOOml) of dichloromethane. The dichloromethane was then dried with magnesium sulphate and filtered, and the solvent was removed on a rotary evaporator. This yielded-4. 0g of intermediate product. This was dissolved in a minimum of acetic acid. The solution was then poured into a KPF6 solution (2g in 65ml water). A viscous residue was obtained which was extracted into dichloromethane. The dichloromethane layer was washed with water (3xlOOml) and dried with magnesium sulphate, and then the dichloromethane was removed on a rotary evaporator to yield the product. The product is a dark brown viscous material which becomes more crystalline on standing.

Product yield 2.4g (44.3%) of a brown pasty solid.

The product was analysed by HPLC, LC-MS and IR.

EXAMPLE 11

(2.025g, 0.0075moles), 2-isopropylthioxanthone sulphoxide from Example 5, diphenyl ether (1.768g, 0. 01040moles), acetic acid (7ml), dichloromethane (1. 75ml) and acetic anhydride (7ml) were mixed in a round bottomed flask. The temperature of the mixture was reduced to <15°C using a water/ice bath. Concentrated sulphuric acid (2. 6ml) was then added drop wise, making sure the temperature did not exceed 15°C. After the addition was complete, the mixture was stirred for 2 hours, allowing the temperature to increase to room temperature. 100mol of water was then added to the mixture. This was then extracted with-200ml (2x100ml) of dichloromethane. The dichloromethane was then removed on a rotary evaporator. This yielded 6.21g of intermediate product. This was dissolved in a minimum of acetic acid. The solution was then poured into a KPF6 solution (2.6g in 85ml water). This appeared to yield a viscous liquid. This was extracted with dichloromethane. The dichloromethane layer was then dried with magnesium sulphate and the solvent was removed on a rotary evaporator to yield the product.

Product yield 4.23g (99.3%) of an orange pasty solid.

The product was analysed by HPLC, LC-MS and IR.

EXAMPLE 12

(2.025g, 0.0075moles), 2-isopropylthioxanthone sulphoxide from Example 5, 4-methyl biphenyl (1.75g, 0. 01040moles), acetic acid (7ml), dichloromethane (1. 75ml) and acetic anhydride (7ml) were mixed in a round bottomed flask. The temperature of the mixture was reduced to <15°C using a water/ice bath. Concentrated sulphuric acid (2. 6ml) was then added drop wise, making sure the temperature did not exceed 15°C. After the addition was complete, the mixture was stirred for 2 hours, allowing the temperature to increase to room temperature. 100ml of water was then added to the mixture. This was then extracted with-200ml (2x100ml) of dichloromethane. The dichloromethane was then removed on a rotary evaporator. This yielded 5. 21g of intermediate product. This was dissolved in a minimum of acetic acid. The solution was then poured into a KPF6 solution (2. 5g in 75ml water). This appeared to yield a viscous liquid. This was extracted with dichloromethane. The dichloromethane layer was then dried with magnesium sulphate and the was solvent removed on a rotary evaporator to yield the product.

Product yield 2.69g (63.4%) of a brown pasty solid.

The product was analysed by HPLC, LC-MS and IR.

EXAMPLE 13

1. 5g Dibenzothiophene sulphoxide (0. 0075moles), biphenyl (1.604g, 0. 01040moles), acetic acid (7ml), dichloromethane (1. 75ml) and acetic anhydride (7ml) were mixed in a round bottomed flask. The temperature of the mixture was reduced to <15°C using a water/ice bath. Concentrated sulphuric acid (2. 6ml) was then added drop wise, making sure the temperature. did not exceed 15'C.

After the addition was complete, the mixture was stirred for 2 hours, allowing the temperature to increase to room temperature. 100ml of water was then added to the mixture. This was then extracted with-200ml (2xlOOml) of dichloromethane. The dichloromethane was then removed on a rotary evaporator. This yielded 4. 41g of intermediate product. This was dissolved in a minimum of acetic acid. The solution was then poured into a KPF6 solution (2. 5g in 75ml water). The product crystallised from solution and was collected by filtration, washed with water and dried in a vacuum oven.

Product yield 3.04g (84. 1 %) of a light brown solid.

The product was analysed by HPLC, LC-MS and IR.

EXAMPLE 14

Thianthrene sulphoxide (2. 0g, 0. 0086moles), biphenyl (1.86g, 0.012moles), acetic acid (7ml), dichloromethane (1. 75ml) and acetic anhydride (7ml) were mixed in a round bottomed flask. A further 5ml of dichloromethane was added to dissolve the thianthrene sulphoxide. The temperature of the mixture was reduced to <15°C using a water/ice bath. Concentrated sulphuric acid (2. 6ml) was then added drop wise, making sure the temperature did not exceed 15°C. After the addition was complete, the mixture was stirred for 2 hours, allowing the temperature to increase to room temperature. 100ml of water was then added to the mixture. This was then extracted wih-200ml (2xlOOml) of dichloromethane. The dichloromethane was then dried with magnesium sulphate, filtered and removed on a rotary evaporator. This yielded 4. Og of intermediate product. This was dissolved in a minimum of acetic acid. The solution was then poured into a KPF6 solution (2g in 65ml water). The product produced was a solid that was collected by filtration and washed with water.

Finally, the product was dried in a vacuum oven.

Product yield 3.42g (77. 1 %) of a very pale pink solid.

The product was analysed by HPLC, LC-MS and IR.

EXAMPLE 15

2. Og (0.00704moles), 2,4-diethylthioxanthone sulphoxide from Example 3, fluorene (1.63g, 0.0098moles), acetic acid (7ml), dichloromethane (1. 75ml) and acetic anhydride (7ml) were mixed in a round bottomed flask. The temperature of the mixture was reduced to <15°C using a water/ice bath.

Concentrated sulphuric acid (2. 6ml) was then added drop wise, making sure the temperature did not exceed 15°C. After the addition was complete, the mixture was stirred for 2 hours, allowing the temperature to increase to room temperature. 100ml of water was then added to the mixture. This was then extracted with-200ml (2x I OOml) of dichloromethane. The dichloromethane was then dried with magnesium sulphate, filtered and removed on a rotary evaporator. This yielded-4. 0g of intermediate product. This was dissolved in a minimum of acetic acid. The solution was then poured into a KPF6 solution (2g in 65ml water). This appeared to yield a viscous liquid. This was extracted with dichloromethane. The dichloromethane layer was washed with 3xlOOml water and then dried with magnesium sulphate, and the solvent was removed on a rotary evaporator to yield the product Product yield 2. 31 g (53.8%) of a brown solid.

The product was analysed by HPLC, LC-MS and IR EXAMPLE 16

(2.025g, 0.0075moles), 2-isopropylthioxanthone sulphoxide from Example 5,4- hydroxybiphenyl (1.768g, 0.01040moles), acetic acid (7ml), dichloromethane (1. 75ml) and acetic anhydride (7ml) were mixed in a round bottomed flask. The temperature of the mixture was reduced to <15°C using a water/ice bath. Concentrated sulphuric acid (2. 6ml) was then added drop wise, making sure the temperature did not exceed 15°C. After the addition was complete, the mixture was stirred for 2 hours, allowing the temperature to increase to room temperature. 100ml of water was then added to the mixture. This was then extracted with-200ml (2xlOOml) of dichloromethane. The dichloromethane was then removed on a rotary evaporator. This yielded 5. 91g of intermediate product. This was dissolved in a minimum of acetic acid. The solution was then poured into a KPF6 solution (2. 5g in 75ml water). This appeared to yield a viscous liquid. This was extracted with dichloromethane. The dichloromethane layer was then dried with magnesium sulphate and the solvent was removed on a rotary evaporator to yield the product. A second extraction was carried out to purify the product further as there was still a strong odour of acetic acid.

Product is a brown solid, yield not recorded The product was analysed by HPLC, LC-MS and IR. Analysis suggests product is a mixture of hydroxy and acetyl biphenyl derivatives (produced under the conditions of the reaction).

COMPARATIVE EXAMPLE 1

8.35g of Thioxanthone (0. 03937moles) were dissolved in 630moi of a mixture of acetonitrile and water (75% acetonitrile, 25% water). A further 75ml of acetonitrile was added in an unsuccessful attempt to dissolve the thioxanthone. The mixture was heated to 55°C. 86. 336g of Ceric ammonium nitrate (0.15748moles) was added, and the reaction was carried out, followed by thin layer chromatography (TLC). The reaction mixture was stirred for 90mins at 55°C. 400ml of water was then added which, when cooled, resulted in the product crystallising from solution. The ctystals were remove by filtration and then dried in a vacuum oven.

Product yield 7. 23g (80.54%) of a yellow solid.

The product was analysed by HPLC, LC-MS and IR COMPARATIVE EXAMPLE 2

1. 71g (0. 0075moles) of thioxanthone sulphoxide from Comparative Example 1, 1.604g biphenyl (0. 01040moles), acetic acid (7m1), dichloromethane (1. 75ml) and acetic anhydride (7ml) were mixed in a round bottomed flask. The temperature of the mixture was reduced to <15°C using a water/ice bath. Concentrated sulphuric acid (2. 6ml) was then added drop wise, making sure the temperature did not exceed 15°C. After the addition was complete, the mixture was stirred for 2 hours, allowing the temperature to increase to room temperature. 100ml of water was then added to the mixture. This was then extracted with-200ml (2xlOOml) of dichloromethane. The dichloromethane was then removed on a rotary evaporator to give 5.17g of intermediate product. This was dissolved in a minimum of acetic acid. The solution was then poured into a KPF6 solution (2. 5g in 75ml water). The product crystallised from solution and was collected by filtration, washed with water and then dried in a vacuum oven.

Product yield 2.38g (62.2%) of a brown solid.

The product was analysed by HPLC, LC-MS and IR COMPARATIVE EXAMPLE 3 (ATTEMPTED SYNTHESIS)

1. 71g (0.0075moles) of thioxanthone sulphoxide from Comparative Example 1, 0.96g toluene (0. 01040moles), acetic acid (7ml), dichloromethane (1. 75ml) and acetic anhydride (7mol) were mixed in a round bottomed flask. The temperature of the mixture was reduced to <15°C using a water/ice bath. Concentrated sulphuric acid (2. 6ml) was then added drop wise, making sure the temperature did not exceed 15°C. After the addition was complete, the mixture was stirred for 2 hours, allowing the temperature to increase to room temperature. 100ml of water was then added to the mixture. This was then extracted with-200ml (2xlOOml) of dichloromethane. The dichloromethane was then removed on a rotary evaporator to give 1. 51g of intermediate product. This was dissolved in a minimum of acetic acid. The solution was then poured into a KPF6 solution (2g in 65ml water). The product crystallised from solution and was collected by filtration, washed with water and then dried in a vacuum oven.

Product yield 0.48g of a brown solid.

The product was analysed by HPLC, LC-MS and IR and found not to have produced any product. Analysis suggests the isolated product is still the thioxanthone sulphoxide starting material.

COMPARATIVE EXAMPLE 4

Isopropylthioxanthone sulphoxide (2.025g, 0.0075moles) from Comparative Example 1, anisole (1.1232g, 0.01040moles), acetic acid (7ml), dichloromethane (1. 75ml) and acetic anhydride (7ml) were mixed in a round bottomed flask. The temperature of the mixture was reduced to <15°C using a water/ice bath. Concentrated sulphuric acid (2. 6ml) was then added drop wise, making sure the temperature did not exceed 15°C. After the addition was complete, the mixture was stirred for 2 hours, allowing the temperature to increase to room temperature. 100ml of water was then added to the mixture. This was then extracted with-200ml (2x100ml) of dichloromethane. The dichloromethane was then removed on a rotary evaporator. This yielded 10. Og of intermediate product. This was dissolved in a minimum of acetic acid. The solution was then poured into a KPF6 solution (4g in 130ml water). This appeared to yield a viscous liquid. This was extracted with dichloromethane. The dichloromethane layer was then dried with magnesium sulphate, and the solvent was removed on a rotary evaporator to yield the product.

Product yield 2.88g (75.9%) of a brown viscous liquid.

The product was analysed by HPLC, LC-MS and IR COMPARATIVE EXAMPLE 5

Isopropylthioxanthone sulphoxide (2.025g, 0. 0075moles) from Comparative Example 1, toluene (0.9568g, 0. 01040moles), acetic acid (7ml), dichloromethane (1. 75mol) and acetic anhydride (7ml) were mixed in a round bottomed flask. The temperature of the mixture was reduced to <15°C using a water/ice bath. Concentrated sulphuric acid (2. 6ml) was then added drop wise, making sure the temperature did not exceed 15°C. After the addition was complete, the mixture was stirred for 2 hours, allowing the temperature to increase to room temperature. 100ml of water was then added to the mixture. This was then extracted with-200ml (2xlOOml) of dichloromethane. The dichloromethane was then dried with magnesium sulphate and the dichloromethane then removed on a rotary evaporator. This yielded 2.72g of intermediate product. This was dissolved in a minimum of acetic acid. The solution was then poured into a KPF6 solution (2g in 65ml water). This appeared to yield a viscous liquid. This was extracted with dichloromethane. The dichloromethane layer was then dried with magnesium sulphate and the solvent was removed on a rotary evaporator to yield the product.

Product yield 2.28g (62.04%) of a brown viscous liquid.

The product was analysed by HPLC, LC-MS and IR.

EXAMPLE 17 Varnish Formulations.

The following varnish formulations were used in the evaluation experiments. Material Code/Standard Standard Experimental Experimental Description Varnish 1 Varnish 2 Varnish 1 Varnish 2 Uvacure 1500 91. 8 87. 8 95. 8 91. 8 Tegorad 2100 0. 2 0. 2 0. 2 0. 2 Propylene carbonate-4. 0-4. 0 Uvacure 1592* 8. 0 8. 0-- Experimental--4. 0 4.0 Photoinitiator Total 100. 0 100. 0 100. 0 100. 0

Uvacure 1592 is a standard photoinitiator from UCB (supplied as a 50% solution in propylene carbonate.) Uvacure 1500 is a cycloaliphatic epoxide monomer from UCB.

Tegorad 2100 is a wetting aid from TEGO.

Summary of Curing Experiments.

The varnishes were printed onto Leneta opacity charts using a No. 1 K-bar and draw down pad.

The prints were passed through a UV curing rig fitted with a medium pressure mercury arc lamp at 80m/min. The UV lamp power is 280watts/inch.

Standard Varnish formulations 1 & 2, containing the photoinitiator Uvacure 1592 cure with one pass at the UV rig conditions stated above. However, the photoinitiator Uvacure 1592 is only completely soluble with additional propylene carbonate (Standard Varnish formulation 2). Colour on cure is good but there is a very strong diphenyl sulphide odour. Initiator Initiator Soluble. Curing Results Summary Code Description Number of passes to cure Odour Colour of Experimental Experimental film varnish 1 (No varnish 2 (4% propylene propylene carbonate) carbonate) Comparative ITX/Yes >15 9 No Slightly Example 5 Toluene Yellow Comparative ITX/Yes 10 2-3 No Slightly Example 4 Anisole Yellow Example 2 ITX/Yes-1-No Slightly Biphenyl Yellow Comparative TX/No No Slightly Example 2 Biphenyl Yellow Example 8 CTX/No 1-2 1 No Slightly Biphenyl Yellow Example 6 2-ITX/Yes 1 1 No Slightly Biphenyl Yellow Example 4 DETX/Yes No Slightly Biphenyl Yellow Example 13 Dibenzo-No 1-2 1 No None thiophene/ Biphenyl Example 12 2-ITX/4-Yes 2 1 No Slightly Methyl-Yellow biphenyl Example 16 2-ITX/4-Yes >6 2-3 No Slightly Hydroxy-Yellow biphenyl Example 11 2-ITX/Yes 1 1 No Slightly Diphenyl Yellow ether Example 10 CPTX/No >7 No Very Biphenyl Yellow Example 14 Thianthrene Yes 1 1 No None /Biphenyl Example 15 DETX/No 3 2-3 No Slightly Fluorene Yellow

EXAMPLE 18 Evaluation results for Example 6 in UV flexo inks Ink formulation. Ingredient Yellow Yellow Magenta Magenta Cyan Cyan Black Black test Std Test Std Test Std Test Std Pigment 44. 0 44. 0 56. 8 56. 8 54. 0 54. 0 70. 0 70. 0 Concentrate TMPO 39. 6 39. 6 30. 3 30. 3 33. 0 33. 0 22. 0 22. 0 Uvacure 1500 8.4 8.4 4.9 4.9 4.7 4.7 - - Uvacure 1592 8. 0-8. 0-8. 0-8. 0- Example 6-8. 0-8. 0-8. 0-8. 0 (50% solids in Uvacure 1500) Uvacure 1592, a triaryl sulphonium salt photoinitiator from UCB, was supplied at 50% solids in propylene carbonate.

TMPO is trimethylolpropane oxetane from Perstorp Cure and Test conditions The inks were printed on SWH-30, BOPP film from Hoechst, using the Easiproof hand held flexo proofer with anilox tool 41. The prints were cured under a medium pressure mercury arc lamp at a belt speed of 80m/min with a lamp power of 120W/cm.

The inks were assessed for MEK resistance, scratch, thumb twist and adhesion. The MEK resistance was assessed immediately after cure and 3 dayslater. The test ink and the standard were printed side-by-side and alone.

Cure results.

All formulations were found to cure with a single pass under the UV lamp with the conditions described.

Yellow Printing Ink MEK Scratch Thumb Twist Adhesion conditions Immediate 3 Days Side by Std 23 62 # # 100% side Test 10 35 # # 100% Alone Std 6 31 # # 100% Test62477100%

Magenta Printing Ink MEK Scratch Thumb Twist Adhesion conditions Immediate 3 Days Side by Std 32 100% side Test 17 Inferior, As 100% std after 90s Alone Std 6 17 # # 100% Test 2 12 Inferior, As Inferior, as 100% std after 90s std after 30s Cyan Printing Ink MEK Scratch Thumb Twist Adhesion conditions Immediate 3 Days Side by Std 3 na 100 side Test na ; 100 Alone Std 4 na # # 100% (Slow) 0% jerky Test 2 na 100

Black Printing Ink MEK Scratch Thumb Twist Adhesion conditions Immediate 3 Days Side by Std 3 21 # # 0% side Test 1 9 # # 0% Alone Std 4 21 After 30s Slow 100% Jerky 0% Test 2 10 After 30s # Slow 100% Jerky 0%

EXAMPLE 19

24 g sodium hydroxide was refluxed in 400 ml tetrahydrofuran for five minutes. 22.8 g (0.1 mols) hydroxythioxanthone was added and reflux continued for 1 hour, during which time the colour changed to bright red, indicating the formation of the sodium salt of hydroxythioxanthone. 35.1 g (0.21 mols) of ethyl bromoacetate was added and reflux was continued for three hours. After cooling to room temperature, 400 ml of deionised water were added with stirring, and the tetrahydrofuran was distilled out to yield a clear red solution. Reflux was continued for a further 2 hours in order to hydrolyse all the ester intermediate. The solution was then cooled to 50°C and 400 ml 1.0 M aqueous hydrochloric acid was added with stirring, causing the solid product to precipitate out. After refluxing for five minutes to be sure that all the sodium salt was converted to free acid, the solution was cooled to room temperature and stirred for two hours before filtering off the solid, washing with 400 ml deionised water and drying in a vacuum oven at 80 C.

Product yield 28.12 g (97 %). Product analysed by NMR.

EXAMPLE 20

18.0 g (0.063 mols) carboxymethoxythioxanthone from Example 19 and 19. 6g (0. 056 mols) of polyethylene glycol methyl ether (350 molecular weight) were azeotropically refluxed under nitrogen in 200 ml toluene with 0.6 g p-toluenesulphonic acid monohydrate catalyst. After 10 hours, the solution was cooled to 35 °C and washed twice with 100ml 10% aqueous potassium carbonate solution and 100 ml deionised water before drying over anhydrous magnesium sulphate. The solution was filtered and all solvent was removed on a rotary evaporator to yield an orange oil.

Product yield 25.47 g (73. 6 %). Product analysed by HPLC and IR

EXAMPLE 21

5. Og of the product from Example 20 (0.0080906moles) were dissolved in 129. 5mi of acetonitrile/water (75: 25). 17.74g (0.03236moles) of CAN were added in one batch. The reaction mixture was stirred for 1 hour at room temperature. 82ml of water was then added. The mixture was then extracted with 3x50ml of dichloromethane. The organic extracts were combined and dried with magnesium sulphate and then filtered. The solvent was removed on a rotary evaporator to yield the product.

Product yield 5. 00g (97.5%) of a yellow liquid. The product was analysed by FT-IR and HPLC.

EXAMPLE 22

4. Og of the product from Example 21 (0. 0063091moles), biphenyl (0.972g, 0. 00631 moles) and acetic anhydride (5. 2ml) were mixed in a round bottomed flask. The temperature of the mixture was reduced to approx. 10°C using a water/ice bath. Conc. Sulphuric acid (1.97g) was then added drop- wise making sure that the temperature did not exceed 20°C. The mixture was then added drop-wise to a solution of 1. 37g potassium hexafluoro phosphate (KPF6) in water 8.52g/methanol 10. 1g. 2ml of methanol was also used to wash out the reaction vessel and added to the methanol/water/KPF6 solution. The mixture was then stirred at 35-40°C for 30minutes. The mixture was then cooled to 10°C and stirred for a further 30minutes. No product crystallised. Therefore, 50ml of MEK and 50ml of water were added but separation did not occur. 75ml of DCM were added to extract the product and then a further 30ml of DCM. The DCM extracts were combined and dried with magnesium sulphate.

The DCM was then filtered and finally removed on a rotary evaporator to yield the product.

Product yield 5.94g of a viscous brown liquid/paste. The product was analysed by FT-IR and HPLC.

EXAMPLE 23

5g of the product of Example 5 (0.01852moles), biphenyl (2.852g, 0. 01852moles) and acetic anhydride (15. 12g) were mixed in a round bottomed flask. The temperature of the mixture was reduced to <10°C using a water/ice bath. Concentrated sulphuric acid (5.79g) was then added drop wise, making sure the temperature did not exceed 20°C. After the addition was complete, the mixture was added to a solution of methanol (29. 5g), water (25. 0g) and KSbF6 (5.97g). The mixture was then stirred at 35-40°C for 30 minutes. The mixture was then cooled to <10°C using an ice/water bath and stirring continued for a further 30 minutes. The precipitate was collected by filtration and washed with 50ml of water. The material was then dried in the vacuum oven at 40°C for 4 hours.

Product yield 8.85g (74.34%) of a brown solid. The product was analysed by HPLC and IR.

EXAMPLE 24 Varnish Formulations.

The following varnish formulations were used in the evaluation experiments. Material Standard Experimental Code/Description Varnish Varnish Uvacure 1500 91. 8 95. 8 Tegorad 2100 0. 2 0. 2 Propylene carbonate Uvacure 1592 8. 0 Experimental Photoinitiator-4. 0 Total 100. 0 100. 0

Uvacure 1592 is a standard photoinitiator from UCB (supplied as a 50% solution in propylene carbonate).

Uvacure 1500 is a cycloaliphatic epoxide monomer from UCB.

Tegorad 2100 is a wetting aid from TEGO Summary of Curing Experiments.

The varnishes were printed onto Leneta opacity charts using a No. 0 K-bar and draw down pad.

The prints were passed through a Primarc Maxicure UV curing rig fitted with a medium pressure mercury arc lamp at 80m/min. The UV lamp power is 300 Watts/inch and was run at a half power setting to aid product differentiation. Initiator Code Initiator Soluble No. passes Odour Colour Description to cure Uvacure 1592 Standard With Strong (diphenyl Colourless triarylsulphon difficulty sulphide) ium salt Example 22 PEG350CMT Yes 2 No Slightly X/Biphenyl Yellow PF6 Example 23 2-ITX/Yes I No Slightly Biphenyl Yellow SbF6

These results demonstrate that the experimental photoinitiators of the present invention have cure speed similar to those of one of the best available commercial standard photoinitiators. Solubility and odour on cure are superior to that of the standard photoinitiator.

EXAMPLE 25 GC-MS headspace analysis The following varnish formulations were used in the evaluation experiments. Material Code/Sulphonium salt Iodonium salt Description formulations formulation Uvacure 1500 75 77. 5 TMPO 20. 9 18. 9 Tegorad 2100 0. 1 0. 1 Propylene carbonate 2 Photoinitiator 2 1. 5 Esacure KIP 150-2 The standard photoinitiators used were Uvacure 1592 (triarylsulphonium salt photoinitiator from UCB, supplied as a 50% solution in propylene carbonate) and IGM 440 (diaryliodonium salt photoinitiator from IGM.

Uvacure 1500 is a cycloaliphatic epoxide monomer from UCB.

Tegorad 2100 is a wetting aid from TEGO.

TMPO is a monofunctional oxetane alcohol diluent from Perstorp.

Esacure KIP 150 is a hydroxyalkylphenone photoinitator from Lamberti.

The varnishes were printed onto aluminium foil using a No. 0 K-bar and draw down pad. The prints were passed twice through a Primarc Maxicure UV curing rig fitted with a 300 Watts/inch medium pressure mercury arc lamp at 80m/min. Under these conditions the samples were over-cured, which was desirable in order to maximise the amount of by-product formation. 200cm2 of each sample was placed in a sealed tube and subjected to a standard headspace analysis proceedure where they are heated to 200°C for 10 minutes and then the headspace volume transferred to a gas chromatograph fitted with a mass spectrometer detector via a heated transfer line.

The compounds detected in these analyses are shown below. No attempt was made to quantify individual materials. Note that there were also several peaks common to all samples that derive from the Uvacure 1500. Photoinitiator Materials detected in Head-space proceedure Uvacure 1592 Diphenyl sulphide Several small unidentified peaks * IGM 440 Toluene lodobenzene Several unidentified peaks Example 6 Biphenyl

*Benzene would also be expected from this analysis but was not seen due to the solvent delay used in this standard GC method.

These results demonstrate that for Example 6, the only photoinitiator byproduct detected is biphenyl, which is of limited toxicological concern for food packaging inks as it is itself an approved food additive material. This is in contrast with the undesirable materials released from the 2 standard photoinitiators.