Opacifying Polymer Particles

This invention relates to improved opacifying polymer particles; a process for making the improved polymer particles and compositions, in particular coatings, comprising the polymer particles.

Pigments are ubiquitous components in many compositions such as plastic components in the form of structural elements for example window frames; and coatings, such as architectural, automotive and marine coatings, in fact wherever colour or white is required. Of the pigments, titanium dioxide is probably the single most common pigment in commercial use.

In the field of architectural paints consumers prefer white or pastel colours to deep colours. This is especially so on large areas such as walls and floors. Being mainly white, such colours contain very high levels of titanium dioxide. Unfortunately, this pigment has one of the highest carbon footprints of all the components in the paint. It is therefore important that it is used as efficiently as possible.

It is known that as the level of titanium dioxide in a paint increases, the efficiency per gram added decreases due to destructive interference between closely adjacent titanium dioxide particles. In addition flocculation of the titanium dioxide during the drying process can exacerbate the problem. Thus controlling the spacing of the titanium dioxide particles in a composition is critical to achieve maximum opacity per gram of the pigment added. This is especially important in coating compositions which start as liquids and dry to a solid film. Pigment particles can flocculate during the drying process.

In known coating compositions the spacing between titanium dioxide or other particles can be affected by a variety of factors including the pigment volume concentration (PVC), the choice of fillers and extenders. However, it is difficult to reliably control this spacing by simply varying these parameters. This is particularly so at high PVC.

US Patent Application Publication No. 2006/0009546 (Brown) discloses a method for forming an opacifying particle comprising: providing, optionally in aqueous dispersion, a pigment particle of from 0.005 to 5 πι average diameter and an index of refraction of at least 1.8; attaching a first polymer to the surface of said pigment particle via a silane residue; and, substantially encapsulating said pigment particle having said attached first polymer with a second polymer, wherein said encapsulating is optionally effected by emulsion polymerizing at least one ethylenically unsaturated monomer in the presence of said pigment particle having said attached first polymer.

European Patent Application Publication No. 2 161 304 A2 (Rohm & Haas) describes an opacifying pigment encapsulated in polymer which includes: a pigment particle having an average particle diameter of from 0.005 to 5 microns and an index of refraction of at least 1.8; an aminophosphorus acid-functional first polymer having been used to disperse the pigment particle in an aqueous medium; and, a second polymer that at least partially encapsulates the dispersed pigment particle. US Patent Application Publication No. 2006/0222851 (Miyabayashi et al.) describes encapsulation of a core material having a surface charge with a plurality of coating layers using a process comprising: (1) adding ionic polymerizable surfactant A and/or ionic monomer, each having a charge opposite to the surface charge of the core material, to an aqueous dispersion of the core material having the charge on the surface thereof, followed by mixing; then, (2) adding ionic polymerizable surfactant B followed by mixing, emulsification and addition of a polymerization initiator thereto to conduct polymerization in water, thus forming the first coating layer; subsequently, (3) adding ionic polymerizable surfactant C and/or an ionic monomer, each having a charge opposite to the surface charge of the first coating layer to an aqueous dispersion of coated matter having the first coating layer, followed by mixing; and, thereafter, (4) adding ionic polymerizable surfactant D, followed by mixing, emulsification and addition of polymerization initiator to conduct polymerization in water, thus forming the second coating layer.

International application W02011/066608 discloses a macro controlled Reversible Addition- Fragmentation chain Transfer (or RAFT) process used to polymerise monomers to form a first polymer from the surface of a pigment in water, where said first polymer uniformly encapsulates the pigment and stabilises the pigment particles to form stable aqueous dispersion in water. Onto the particles of the dispersion are polymerised further monomers to produce a base swellable polymer and onto this are polymerised still more monomers to produce extensible polymer.

The first polymer, base swellable polymer and extendable polymer are polymerised using a RAFT process and consequently a linear block copolymer is formed, attached to the pigment particle. The three regions mentioned are covalently linked; the first polymer is covalently linked to the base swellable polymer and the base swellable polymer is covalently linked to the extensible polymer. Of course this differs from sequential emulsion polymerisation, where the different emulsion polymers are not covalently linked but rather are simply in physical contact at the boundaries. Raising the pH of the swellable polymer under suitable conditions should cause the swellable polymer to swell and the extensible polymer also to swell (to accommodate the increased volume). On drying, the base swellable polymer loses water and the pigment finds itself in an air void. Scattering and thus opacity is improved in such circumstances because the amount destructive interference is reduced. Furthermore, the presence of voids in the particles increases the overall refractive index difference between the binder medium and the pigment.

RAFT agents have the general formula (SHZJCfSPlnR ¹ )

where each X is independently a polymerised residue of an ethylenically unsaturated monomer, n is an integer from 0 to 100, R ¹ and Z are groups independently selected such that the agent can function as a RAFT agent in the polymerisation of the selected one or more ethylenically unsaturated monomers.

Unfortunately, RAFT type polymerisation is a complex, expensive and slow process. In fact the process is so slow that typical cycle times, the time taken from start to finish, can be 24 hours. This is unacceptably long for an industrial process and it is economically unviable.

Prior art attempts using conventional free radical polymerisation, as described in W02011/066608, have proved unsuccessful, producing defective particles including having non-uniform shell polymer.

What is required is a simple and efficient process for making such particles.

Surprisingly, we have now found that we can make hollow polymer particles containing pigment particles therein using a non-RAFT emulsion polymerisation process using free radical polymerisation. The technique is much faster and simpler than the RAFT prior art method previously disclosed.

Accordingly, there is provided an aqueous dispersion of pigmented opacifying polymer particles, the particles comprising:

i. an inorganic core comprising dispersed inorganic pigment particle and a dispersant ii. a first layer of base-swellable polymer comprising acid groups encapsulating the core iii. a second layer of non-base-swellable polymer encapsulating the first layer

wherein the dispersant comprises or consists of hydroxyl moieties; and carboxyl groups derived from itaconic acid

Preferably, the aqueous dispersion of the invention comprises an intermediate polymer layer between the pigment and the base swellable polymer layer and which is free of an intermediate polymer layer between the base swellable polymer layer and the non-base swellable polymer layer.

Preferably, the monomers of step v. used to form the intermediate polymer comprise acid functional monomers and more preferably, the acid functional monomer is free of carboxyl moieties; even more preferably the monomer comprises sodium styrene sulphonate. This ensures that the pigment dispersion is stable (that is, it does not flocculate or become shear unstable) at the low pH necessary for step ii.. By low pH in this context we mean less than pH 4 and more preferably between pH 2 and 4. Preferably, the intermediate polymer comprises from 5 to 30wt% of sodium styrene sulphonate. Preferably the amount of the intermediate polymer required to ensure that the pigment dispersion is stable at the low pH is at least 7.5wt% based on the weight of the pigment.

The presence of an intermediate polymer layer between the pigment and the first layer of base swellable polymer normally ensures the necessary stability, at least to low pH. In such circumstances, a second intermediate polymer layer between the base swellable polymer and the non-base swellable polymer, is not required. However, forming such a polymer can be advantageous for other reasons.

Dispersants comprising itaconic acid and hydroxyl moieties are stable in the conditions prevailing during the polymerisation stages of the process of preparing the particles. Furthermore, the long term storage stability of the dispersion of opacifying polymer particles is improved over prior art dispersants. By stable we mean that the dispersant and the pigment dispersion comprising it do not flocculate during polymerisation. Optionally, intermediate polymer layers of acid value from 0 to lOOmg KOH/g non volatile (non vol) polymer are present between the core and the first layer of base swellable polymer and/or between the first layer of base-swellable polymer and the second layer of non-base swellable polymer.

Preferably, the the polymer layers are free of RAFT agents.

Preferably, the polymer layers are free of agents containing thiocarbonylthio moieties.

Suitable inorganic pigment particles for use in the present invention include barium sulphate, calcium carbonate, zinc sulfide, lithopone, metal oxides including zinc oxide, antimony oxide, zirconium oxide, chromium oxide, iron oxide, lead oxide, and forms of titanium dioxide such as anatase and rutile. Preferably, the inorganic pigment particles are titanium dioxide particles, in particular particles selected from rutile titanium dioxide and anatase titanium dioxide.

In another aspect of the invention there is provided a composition, preferably a coating composition, comprising the aqueous dispersion of the invention. In another aspect of the invention there is provided a method of preparing the aqueous dispersion of opacifying polymer particles of the invention, the particles containing inorganic pigment particles therein, comprising the steps of:

i. dispersing inorganic pigment in aqueous medium using a dispersant, of acid value at least

65mg KOH/g of dispersant,

wherein the dispersant comprises or consists of carboxyl acid moieties of differing pKa derived from itaconic acid, and hydroxyl groups and

the pH during dispersion is greater than the pKa of the carboxyl moiety having the lower pKa

and also at least 0.25 pH units above or below the iso-electric point of the pigment, to form a stable aqueous dispersion of the pigment in the aqueous medium.

ii. adjusting the pH of the pigment dispersion to below the pKa of the acid moiety

comprising the base swellable polymer of step iii. whilst satisfying the pH criteria of step i.

iii. forming a first layer of a base swellable polymer on the pigment particles by polymerising monomers comprising acid groups

iv. forming a second layer of non-base swellable polymer

v. optionally polymerising further monomers to form intermediate polymer layers having acid value between 0 and 65mg KOH/g polymer between the pigment and the first layer and/or between the first and second layer

vi. at least partially neutralising the first polymer, using a base, at a temperature above the effective Tg of the second layer of non-swellable polymer whereby the first layer of polymer is caused to swell; and,

vii. cooling the dispersion to a temperature below the effective Tg of the second layer.

Itaconic acid (l-propene-2, 3 dicarboxylic acid) comprises two carboxyl moieties of different pKa, specifically at 3.85 and 5.45 respectively. The lower pKa acid moiety ionises more readily and it is the pKa of this carboxyl that is to be taken into account for the purposes of the present invention.

In another aspect of the invention the dispersion of opacifying polymer particles is provided as a dry powder by drying the dispersion using suitable drying means. Suitable means include spray drying or freeze drying. In this form the particles may be used in compositions which are free of volatile materials. In another aspect of the invention, there is provided a coating composition comprising the aqueous dispersion or the dried opacifying polymer particles of the invention.

Tg denotes the glass transition temperature of a polymer. The Tg of a copolymer can be calculated using the Fox equation where 1/Tg =Wi/Tgi+W2/Tg2+W3/Tg3+.... where Tgi, Tg2, Tg3... are the glass transition temperatures of the homopolymers of the component monomers in ² K and Wi, W2, W3... are the weight fractions present.

Polymers can be softened by the use of plasticisers. Such plasticisers effectively reduce the Tg of the polymer. Coalescing solvents are plasticisers and encourage film formation of coatings comprising polymer particles by softening at least the outer regions of the polymer particles to the extent that the merge to form a continuous or semi-continuous film. Some polymers may also be plasticised by monomers. The extent to which a plasticizer, coalescing solvent and/or monomer reduces the calculated Fox Tg of a particular polymer may be calculated according to equation 1: Equation 1

Where: Tg _p and Tg _s is the glass transition temperature of the polymer and the solvent respectively; Tg _e ff is the effective glass transition temperature of the polymer in the presence of the plasticizer; V _p and V _s are the volume fractions of the polymer and the solvent respectively; a is a factor accounting for small changes in plasticising efficiency and is assumed to be 1 for the purposes of this invention. Pigment Dispersant

The dispersant preferably has a weight average molecular weight (Mw) of at least 1000 Daltons, more preferably from 1000 to 100000 Daltons, more preferably from 1500 to 50000 Daltons. The dispersant may be linear or non-linear polymers including comb, block and star types.

Preferably, the acid value of the dispersant is at least lOOmg KOH/g dispersant, more preferably from 100 to 450mg KOH/g dispersant, even more preferably from 150 to 400 mg KOH/g dispersant.

Preferably, the hydroxyl value of the dispersant is from 50 to 400mg KOH/g dispersant, more preferably 100 to 250mg KOH/g dispersant. The hydroxyl group may be introduced into the dispersant through ethylenically unsaturated monomers containing hydroxyl groups. Suitable such monomers include hydroxy ethyl acrylate, hydroxy ethyl methacrylate and hydroxy isopropyl methacrylate. In addition it is preferable that the pigment dispersant contains additional moieties that adsorb to the surface of the pigment or the surface treatment on the pigment. In the case of titanium dioxide used in surface coatings, this is often surface treated with alumina, silica and zirconia. Moieties that adsorb to these are desirable. Suitable moieties include amines - including heterocyclics such as morpholine.

The dispersant may be made using any polymerisation method including free radical addition polymerisation, condensation polymerisation, and controlled radical polymerisation (CRP) including RAFT polymerisation, macromolecular design by interchange of xanthate polymerisation (MADIX), nitroxide mediated polymerisation (NMP) and atom transfer radical polymerisation fATRP).

The dispersant is preferably made in a good solvent for the dispersant so that a solution of dispersant in solvent is formed. Suitable solvents include water compatible organic solvents, aqueous mixtures containing less than 50wt% of organic solvent; or water. More preferably, aqueous mixtures are used.

Preferably, the pigment dispersants are used at from 0.1 to 4, more preferably from 1 to 2wt% based on the weight of titanium dioxide. The amount of pigment dispersant required will vary, mainly in accordance with the particle size and the density of the particular pigment.

Architecture of the Opacifying Polymer Particles

The dispersion of opacifying polymer particles of the invention comprise a particle of titanium dioxide encapsulated by a layer of base swellable polymer, the base swellable polymer encapsulated by a non-base-swellable, non-film-forming polymer.

Optionally, a third layer of film forming polymer is formed onto the second layer of non-base swellable, non-film forming polymer.

This has the unique advantage of providing the pigment in a form that also film forms. The dispersed inorganic pigment particles suitable for use in the invention preferably have a mean particle diameter of from 75 to 300nm, more preferably from 100 to 300nm, even more preferably from 150 to 300nm and most preferably from 200 to 300nm. When the inorganic pigment particles used are titanium dioxide, the mean particle size of the titanium dioxide particles are preferably from 75 to 150nm in diameter.

The amount of base swellable polymer should increase the radius of the opacifying polymer particles by about from 2 to 20nm before swelling and the layer of non-base-swellable, non-film- forming polymer, should increase the radius by about a further 15 tol50nm, preferably 30 to 75nm before swelling.

On adding base to the aqueous dispersion the base swellable layer swells with water. Sufficient base should be added to swell the base swellable layer so that the radius increases to from 10 to 200nm.

Of course, in order for the base-swellable polymer layer to swell, the non-base-swellable polymer must itself be extensible during the swelling step. On drying, the dispersion of the invention naturally loses water. The water swelling the base- swellable polymer migrates through the particle and escapes to the atmosphere leaving an air- filled void in which sits the particle of titanium dioxide.

Figure 1 shows an idealised structure of an opacifying particle comprising the invention where (1) is a pigment particle, (2) is a layer of base-swellable polymer in its unswollen state and (3) is the layer of non-base-swellable polymer.

Figure 2 shows the same structure as in Figure 1 at basic pH with the base-swellable polymer (2) swollen with water.

Base Swellable Polymer

The role of the base swellable layer is to react with a base once it has been at least partially overcoated with a rigid outer shell to form a hydrophilic ionomeric layer. This layer causes surrounding water to be drawn in by osmosis and to swell the polymer. The base swellable polymer is preferably derived from one or more monomers selected from the group consisting of methacrylic acid, acrylic acid crotonic acid, maleic acid or maleic anhydride, itaconic acid, cinnamic acid, fumaric acid and beta carboxy ethyl acrylate.

This base swellable polymer layer should preferably contain sufficient acid monomer to give an acid value of from 100 to 450 mg KOH/g of polymer more preferably 130 to 260 mg KOH/g of polymer. This corresponds to from about 15 to 70 wt% and 20 to 40 wt% of methacrylic acid calculated on the total weight of base-swellable polymer.

The base-swellable-polymer layer can also contain non-polymerisable acid if desired. Suitable non-polymerisable acid monomers include Ce - C12 aliphatic moncarboxylic acids and aromatic acids such as benzoic acid. The base-swellable-polymer layer may optionally be crosslinked with a multifunctional unsaturated monomer such as divinyl benzene, diallyl methacrylate, ethylene glycol dimethacrylate, butane diol dimethacrylate or allyl methacrylate. Preferably, from 0.1 to 5 wt. %, based on the weight of base swellable polymer, of said multifunctional unsaturated monomer is used, more preferably from 0.1 to 1.0 wt % is used. Allyl methacrylate is particularly preferred as a crosslinker as it promotes grafting between the different polymer layers.

The Fox Tg of the base-swellable-polymer layer is preferably from 0 to 170°C, and more preferably from 20 to 150°C. The thickness of the base-swellable-layer is from 2 to 20 nm unswollen, and from 10 to 200 nm swollen. By thickness is meant as measured by the increase in radius of the particle.

Non-Base-Swellable Polymer The non-base swellable polymer must fulfil two roles. Firstly, during the neutralisation step of the base-swellable polymer it must expand, without rupturing, in order to accommodate the increased volume - thus, it must be chosen to have an effective Tg below the temperature used during the neutralisation step. Secondly, during drying and loss of water, the non-base-swellable polymer must be rigid enough to prevent collapse of the void. The polymer should preferably have a high modulus. Preferably the non-base-swellable polymer is non-film forming at ambient temperature. Non- film forming polymers have a Tg _eff above ambient temperature. A good guide to modulus is the glass transition temperature, Tg. Generally, as Tg increases, modulus also increases and we have found this can be used as a useful guide to determine the Tg of the polymer which resists collapse and film formation.

Preferably, the Fox Tg of the non-base-swellable polymer is at least 60°C, more preferably from 90 to l40°C.

Furthermore, the polymer is preferably not significantly plasticised by water as this will cause it to soften and deform, especially as the paint dries. Preferably it is hydrophobic as this reduces water plasticisation and it has the added benefit that it improves water resistance of coatings containing the opacifying polymer particles of the present invention. More preferably the solubility of the monomers making up the non-base-swellable polymer should be less than 2g/100g water at 20°C.

Suitable monomers to make the non-base-swellable polymer include styrene, alpha methyl styrene (as a monomer in a copolymer), tert-butyl styrene, vinyl toluene, methyl methacrylate, acrylonitrile, methacrylonitrile and copolymers of these with lower Tg monomers.

Preferably the polymer contains 90-100% styrene monomer. It may also contain from 0 to 20% acidic moieties, more preferably from 0 to 10%. These are especially beneficial because it helps the non-base-swellable layer adhere to the base-swellable polymer layer. The presence of the acid moieties also helps with the swelling stage by helping to facilitate passage of the neutralising base through the rigid outer shell during the neutralisation step.

The acid value of the non-base-swellable polymer layer is preferably less than 130, more preferably less than 100 even more preferably less than 65mg KOH/g non vol. polymer.

The thickness (i.e. the radius) of the non-base-swellable polymer layer is preferably from 15 to 150nm, more preferably from 30 to 75nm. Of course the thickness of the non-base-swellable polymer reduces as the base-swellable polymer swells because it has a greater area to encapsulate. Optional Intermediate Polymer Layer

The optional intermediate polymer layer is not base-swellable.

Preferably the acid value of the optional intermediate polymer layer is from 0.1 to 65.0mg KOH/g of polymer, more preferably from 10 to 65mg KOH/g of polymer. The presence of some acid functional monomers is thought to help the passage of base, especially inorganic base such as NaOH, through the intermediate layer. Suitable acid functional monomers are as hereinbefore described in relation to the base swellable polymer layer. Additionally, monomers comprising strong acid moieties such as sulphonate and phosphate can be used. Suitable examples include sodium styrene sulphonate.

The Fox Tg of the intermediate polymer layer is preferably between 30 and 100°C and more preferably between 50 and 90°C.

The thickness of the optional intermediate polymer layer is 5 to 50 nm before swelling of the base swellable polymer layer, more preferably 10 to 30 nm. Without being bound by this, it is thought that the optional intermediate polymer layer at least partially or preferably fully encapsulates the base swellable polymer layer in order to make it easier for the far less polar rigid outer shell to overcoat the base swellable polymer in a more uniform manner. Figure 3 shows an idealised structure of an opacifying particle comprising the invention where (1) is a pigment particle, (2) is a layer of base-swellable polymer in its unswollen state, (3) is the layer of non-base-swellable polymer and (4) and (5) are intermediate layers.

Swelling Stage

The base swellable polymer layer is swollen by raising the pH using, for example, either volatile bases, including ammonia or amine, or non-volatile bases, for example alkali metal hydroxides such as sodium hydroxide. Of course, the polymer is not actually swollen by base but rather by the aqueous medium or water comprising the continuous phase of the dispersion. Following addition of the base, the neutralised acid moieties on the polymer become hydrophilic and the aqueous phase or water is drawn in by osmosis creating the driving force for swelling.

In order for the water ingress to proceed unhindered, the non-base-swellable non-film-forming polymer must be extensible during the neutralisation stage. It is necessary that the addition of the base is carried out at a temperature above the effective glass transition temperature of the non-base-swellable non-film-forming polymer in order to accommodate the increase in volumes accompanying the water ingress without rupturing. An aqueous medium comprises at least 50wt% of water, the remainder comprising organic solvents, preferably water compatible solvents.

In the absence of a plasticising material for the polymer, the effective Tg is the same as the Fox Tg. Where a plasticiser is present the effective Fox Tg is lower than the Fox Tg.

Preferably, the addition of base is at a temperature at least 5°C, more preferably from 5 to 20°C above the effective Tg of the polymer.

For example where the base swellable layer is overcoated with an intermediate polymer layer of Tg less than the process temperature, the base can be added to the dispersion at elevated temperature (>Tg of the intermediate layer) and after the swelling is complete and the pH has dropped, a rigid hydrophobic layer of polymer is polymerised on top of this. Alternatively, the addition and polymerisation of the monomer can occur whilst the swelling is occurring.. Alternatively, a rigid hydrophobic layer of polymer can be polymerised directly onto the base swellable polymer layer, followed by plasticising this polymer layer with monomer (in order to reduce its effective Tg). This can be achieved by (a) stopping the addition of initiator, (b) optionally adding a free radical inhibitor (e.g. monomethyl ether hydroquinone, MEHQ), (c) using a non-homopolymerisable monomer, or (d) using a monomer with a ceiling temperature below the operating temperature (e.g. alpha methyl styrene). The base is then added to the dispersion at elevated temperature as before and after the swelling is complete and the pH has dropped, the polymerisation is continued (e.g. by adding further initiator and monomer) and a rigid hydrophobic layer of polymer is polymerised on top of this. Of course, a plasticising solvent can be also be used but is far less preferable as, since, depending on its boiling point, it may well contribute to VOC. Polymerisation method

The polymerisation steps of the present invention are carried out using a sequential emulsion polymerisation process in the presence of inorganic pigment particles, preferably titanium dioxide, dispersed in aqueous medium, preferably water.

By sequential is meant that monomer mixtures of different composition are polymerised one after the other. In the simplest example of such a method, particles may be made having a first polymer or core region differing in composition from a second or shell polymer region. Of course, the particles may have more than two polymer regions.

Preferably, the polymers are made using unconstrained free radical polymerisation methods, more preferably using free radical emulsion polymerisation methods. Even more preferably free radical initiators are used.

The monomers are preferably emulsified in water and surfactant and fed into the reactor vessel over a period of from 1 to 6 hours, preferably from 1 to 3 hours. Consecutively, the free radical initiator is fed into the reactor. It is advantageous to have a delay between the various monomer feeds. In the non-RAFT type polymerisation used in this invention, the growing chains are very short-lived. The delay, therefore, ensures that any growing chains of the previous polymerisation terminate and stop growing before the next monomer mixture is polymerised. Preferably the titanium dioxide pigment particles are dispersed in water in the form of primary particles (i.e. with the minimum level of agglomerates). More preferably, the dispersed pigment has a mean particle diameter of from 150 to 300nm, even more preferably from 200 to 300nm and most preferably from 225 to 275nm as measured by dynamic light scattering. The polymerisation is carried out in the absence of RAFT chain transfer agents, preferably in the absence of all types of controlled radical polymerisation.

Processing Conditions

It is preferable to run the polymerisation under conditions that encourage control of the morphology, e.g. low free monomer levels and levels of surfactant that are adequate for giving stability but not so high as to cause nucleation and stabilisation of non pigmented latex particles. As a corollary to this, it may be useful to make adjustments to lower the pH of the dispersion of inorganic pigment particles formed after step i) of the process - for instance, by the addition thereto of an acid such as hydrochloric acid - and allow for pH equilibration before the polymerization of the base swellable polymer.

The invention will now be illustrated by the following examples, in which the abbreviations used are defined below.

The abbreviations below have the following meaning

AMA Allyl Methacrylate

AMPS 2 -Aery lamido-2-Methylpropane Sulfonic Acid DELETE ???

AMS Alpha-Methyl Styrene DELETE ???

BA Butyl Acrylate

BMA Butyl Methacrylate

DI water Deionised water

DMAEMA Dimethylaminoethyl Methacrylate DELETE ???

DVB Di-Vinyl Benzene DELETE ???

HEMA Hydroxyethylmethacrylate

IA Itaconic Acid

MAA Methacrylic Acid

MAM Methacrylamide

MMA Methyl Methacrylate

SSS Styrenesulfonic Acid Sodium salt hydrate

ST Styrene

Example 1

Anionic Dispersant Solution (D-l)

A solution of anionic polymer dispersant was produced according to the process described below and in Table 1, and having a monomer composition MMA:HEMA:IA:MAM of 15:45:36:4 by weight. Table 1. Dispersant Polymer (PI)

Material .

Weight (g)

Solvent (A)

Iso-Propanol 15.17

DI water 5.06 Monomer (B)

Methyl Methacrylate 7.05

Hydroxyethylmethacrylate 20.97

Itaconic Acid 16.68

Metha cry lamide 1 .91

n-Octyl Mercaptan 1 .05

VAZO 67 1 .46

Iso-Propanol 22.58

DI Water 7.75

Initiator (C)

VAZO 67 0.1 1

Iso-Propanol 0.24

DI Water 0.14

Total 100.17

The solvent mixture (A) was loaded to a reaction vessel. 25 % of the mixture (B) was then added and the temperature increased to 65 °C under a blanket of nitrogen.

The mixture was then allowed to exotherm to 82 °C and held for 15 min. The remainder of the mixture (B) was then fed over 2 h at 85 °C. The mixture (C) was then added and the mixture held at reflux temperature (80 to 85 °C) for 2 h.

A Dean Stark was then adapted to the reaction vessel and the Iso-Propanol was distilled off. As described in Table 2, (D) and (E) were then added while stirring at high speed at 75 °C to form the polymer solution (D-l ) at 27.3 wt% solids.

Table 2. Anionic Dispersant Solution D-l

Material Weight (g)

Polymer (PI) 33.50

DI Water (D) 62.50

Ammonia (E) 4.00

Total 100.00

Aqueous dispersion of titanium dioxide MB-1

The anionic dispersant solution, D-l , was used to make an aqueous dispersion of titanium dioxide according to the recipe and method below.

Table 3. Material Weight (g)

D-1 23.01

DI Water 106.24

Tipure R-706 420.75

Total 550.00

23.01 g of the dispersant solution (D-1) were diluted in 106.24 g of water. 420.75 g of Tipure R-706 were then dispersed in the solution obtained using a high speed disperser operating at 1,500 rpm for 20 min.

Aqueous dispersion of opacifying polymer particles

An aqueous dispersion of opacifying polymer particles was made using the titanium dioxide dispersion prepared in Table 3. The method and ingredients used are shown in Table 4.1 and 4.2 Table 4.1. Ti02 dispersion with first polymer layer (ME-1 )

Material Weight (g)

Aqueous charge (A)

MB-1 261.90

Sodium Dodecyl B enzene Sulphonate 1.46

Solids adjust (B)

DI water 258.68

Initiator Catalyst (C)

0.1% Iron II Sulphate aqueous solution 1.12

1% Ethylene Diamine Tetra Acetic Acid aqueous solution 0.08

Initiator Feed (D )

Tert-Butyl Hydroperoxide (70% active) 0.37

DI water 3.27

Reductant Feed (E)

Ascorbic Acid 0.20

DI water 15.04

Optional non-base swellable polymer layer (F)

DI water 5.38

Sodium Dodecyl Benzene Sulphonate 0.64

Butyl Methacrylate 10.93

Methyl Methacrylate 6.25

Styrenesulfonic Acid Sodium salt hydrate 1.93 Total 567.69

The Ti0 ₂ dispersion (A) was charged to a reaction vessel, diluted with DI (B), purged with nitrogen and the temperature raised to 50 °C. The catalyst (C) was then added followed two minutes later by the initiator (D). The reductant (E) and the monomer mixture (F) were then fed in linearly over 30 min at 50 °C.

Table 4.2.

Material Weight (g)

Aqueous charge

ME-1 567.69 Solids Adjust (G)

DI Water 154.89 Initiator Catalyst (H)

0.1% Iron II Sulphate aqueous solution 1.48

1 % Ethyl ene Diamine Tetra Acetic Acid aqueous solution 0.17

Sodium Dodecyl Benzene Sulphonate 4.93

Initiator Feed (I)

Tert-Butyl Hydrop eroxide 1.19

DI Water 1 1.18

Reductant Feed (J)

Sodium Formaldehyde Sulfoxylate 0.42

DI Water 1 1.13

Base swellable layer stage (K)

DI Water 7.08

Sodium Dodecyl Benzene Sulphonate 3.26

Methyl Methacrylate 16.01

Butyl Aery late 16.01

Methacrylic Acid 16.01

Allyl Methacrylate 0.05

Solids Adjust (L)

DI Water 234.84

Initiator Catalyst (M) 0.1% Iron II Sulphate aqueous solution 1.13

1 % Ethylene Diamine Tetra Acetic Acid aqueous solution 0.13

Initiator Feed (N)

Tert-Butyl Hydroperoxide 0.92

DI Water 8.63

Reductant Feed (O)

Sodium Formaldehyde Sulfoxylate 0.32

DI Water 8.46

Optional Intermediate Polymer layer (P)

Methyl Methacry late 33.10

Butyl Acrylate 3.68

Aerosol MA80 0.87

DI Water 8.83

Non film forming outer shell (Q)

Methyl Methacrylate 55.21

Aerosol MA80 1.31

DI Water 13.24

Initiator/Feed (R)

Ammonium Persulphate 0.34

DI Water 19.51

Ammonia addition (S)

Ammonia 45.00

Total 1247.00

ME-1 and Solids Adjust (G) were charged to a reaction vessel. The dispersion was then adjusted to pH 4.1 by addition of hydrochloric acid (1 mol/L) and stirred for 10 min to allow for pH equilibration. After addition of (I), the pH was checked again and readjusted if necessary to 4.1 by addition of hydrochloric acid (1 mol/L). The solution was purged with N ₂ and the temperature adjusted to 50 °C. (J) and (K) were fed in linearly over 30 min, before the solid adjust (L) was added.

The temperature was then kept at 50 °C while adding (M) and (N); (O) and (P) were then fed over 30 min.

The dispersion was then heated up to 90 °C and (Q) and (R) were fed into the vessel.

The mixture was then allowed to cool to room temperature; it was filtered to remove any grit. The filtered dispersion was then stirred at 90 °C and ammonia (S) added over 30 min. The stirring was continued for 4 hours at 90 °C, before the dispersion was allowed to cool and was filtered. Example 2.

As for Example 1 , with the following formulation changes:

Base swellable layer stage (K)

DI Water 7.13 Sodium Dodecyl Benzene Sulphonate 3.29

Methyl Methacrylate 20.78

Butyl Aery late 13.07

Methacrylic Acid 14.53 Allyl Methacrylate 0.05

Optional Intermediate Polymer layer (P)

Styrene 36.78

Aerosol MA80 0.87

DI Water 8.83

Non film forming outer shell (Q)

Styrene 55.21

All other process and formulation steps remaining identical.

Example 3.

As for Example 1 , with the following formulation changes:

Base swellable layer stage (K)

DI Water 7.02

Sodium Dodecyl Benzene Sulphonate 3.24

Methyl Methacrylate 1 1.84

Butyl Acrylate 16.75

Methacrylic Acid 19.06

Allyl Methacrylate 0.05

Non film forming outer shell (Q)

Styrene 54.79

Aerosol MA80 1.30

DI Water 13.14

All other process and formulation steps remaining identical.

Example 4.

As example 2, with the following formulation changes:

Base swellable layer stage (K)

DI Water 7.08

Sodium Dodecyl Benzene Sulphonate 3.26

Methyl Methacrylate 16.01

Butyl Acrylate 16.01 Methacrylic Acid 16.01

Allyl Methacrylate 0.05

All other process and formulation steps remaining identical.

Example 5.

As for example 1, with the following formulation changes:

Non film forming outer shell (Q)

Styrene

Aerosol MA80

DI Water

All other process and formulation steps remaining identical.

Example 6.

As for example 1, with the following formulation changes:

Optional Intermediate Polymer layer (P)

Methyl Methacrylate

Butyl Aery late

Aerosol MA80

DI Water

Non film forming outer shell (Q)

Styrene

Aerosol MA80

DI Water

All other process and formulation steps remaining identical.

Example 7.

As for example 1, but with the following changes:

Material

Aqueous charge (A)

MB-1

Sodium Dodecyl Benzene Sulphonate

Solids adjust (B)

DI water

Initiator Catalyst (C)

0.1% Iron II Sulphate aqueous solution 1.12

1% Ethylene Diamine Tetra Acetic Acid aqueous solution 0.08

Initiator Feed (D )

Tert-Butyl Hydroperoxide (70% active) 0.37 DI water 3.28 Reductant Feed (E)

Sodium Formaldehyde Sulfoxylate 0.20 DI water 15.09

Optional non base swellable polymer layer (F)

DI water 5.40

Sodium Dodecyl Benzene Sulphonate 0.65

Butyl Methacrylate 11.28

Methacrylic Acid 0.39

Methyl Methacrylate 5.98

Styrenesulfonic Acid Sodium salt hydrate 1.96

Solids Adjust (G)

DI Water 155.43 Initiator Catalyst (H)

0.1% Iron II Sulphate aqueous solution 1.48

1 % Ethyl ene Diamin e Tetra Acetic Acid aqueous solution 0.17

Sodium Dodecyl Benzene Sulphonate 4.95

Initiator Feed (I)

Tert-Butyl Hydrop eroxide 1.19

DI Water 11.22

Reductant Feed (J)

Sodium Formaldehyde Sulfoxylate 0.42

DI Water 11.17

Base swellable layer stage (K)

DI Water 7.10

Sodium Dodecyl Benzene Sulphonate 3.27

Methyl Methacrylate 20.70

Butyl Acrylate 13.02

Methacrylic Acid 14.47

Allyl Methacrylate 0.05

Solids Adjust (L)

DI Water 235.66 Initiator Catalyst (M)

0.1% Iron II Sulphate aqueous solution 1.14

1 % Ethylene Diamine Tetra Acetic Acid aqueous solution 0.13

Initiator Feed (N)

Tert-Butyl Hydroperoxide 0.92

DI Water 8.66

Reductant Feed (O)

Sodium Formaldehyde Sulfoxylate 0.32

DI Water 8.49 Optional intermediate Polymer layer (P)

Methyl Methacylate 33.21

Butyl Aery late 3.69

Aerosol MA80 0.87

DI water 8.86

Non film forming outer shell (Q)

Styrene 55.40

Aerosol MA80 1.31

DI water 13.29

Initiator/Feed (R)

Ammonium Persulphate 0.34

DI Water 19.58

Ammonia (S)

Ammonia 40.81

Total 1246.98

All process steps remain unchanged.

Example 8.

Same as example 1, but with the following formulation changes:

Optional non base swellable polymer layer (F)

DI water 5.42

Sodium Dodecyl Benzene Sulphonate 0.65

Butyl Acrylate 4.18

Methyl Methacrylate 13.54

Styrenesulfonic Acid Sodium salt hydrate 1.97

Base swellable layer stage (K)

DI Water 7.13

Sodium Dodecyl Benzene Sulphonate 3.29

Methyl Methacrylate 20.78

Butyl Acrylate 13.07

Methacrylic Acid 14.53

Allyl Methacrylate 0.05

Non film forming outer shell (Q)

Styrene 55.61 10

Aerosol MA80 1.32

DI Water 13.34

Ammonia addition (S)

Ammonia 36.17

15

All other formulation and process steps remaining unchanged. Example 9.

Same as example 5, with the following formulation changes.

Optional non base swellable polymer layer (F)

DI water 5.38

Sodium Dodecyl Benzene Sulphonate 0.64

Styrene 0.39

Butyl Methacrylate 10.93

Methyl Methacrylate 6.69

Styrenesulfonic Acid Sodium salt hydrate 1.93

All other formulation and process steps remaining unchanged.

Spreading rates

The spreading rate to achieve a contrast ratio of 95% and 98% was evaluated by converting examples 1-3, 5-7 and 9 of the dispersion to model paints according to the formulations shown in Table A

Table A

Example 1 2 3 5 6 7 9

wt (g) wt (g) wt (g) wt (g) wt (g) wt (g) wt (g)

Opacifier

dispersion

of example 46.72 50.01 49.19 32.85 47.26 44.66 48.90 indicated

above

Film

forming

35.50 34.30 33.03 33.57 32.83 33.94 33.64 latex

VA:BA

Thickener 1.50 1.50 1.49 1.48 1.51 1.51 1.50

Water 15.98 13.89 15.99 31.79 18.10 19.59 15.66

AMP 95 0.30 0.30 0.30 0.30 0.30 0.30 0.30

Total 100.00 100.00 100.00 100.00 100.00 100.00 100.00

Table B shows the recipes of two standard paints at PVC 9 and 10% .

Table B

The T1O2 and clay slurry recipes as used in Standard A and B are shown below

Ti0 ₂ slurry ASP 170 slurry wt% wt%

Water 22.80 34.30

Biocide (25% solids) 0.11

Dispersant (45% solids)

0.30 0.35 (Polyacrylic acid)

Antifoam

AMP 95

Biocide (22% solids) 0.23

Antifoam (60% solids) 0.19

Ti0 ₂ 76.48

Hydrous Clay 65.00

Total 100.00 100.00 The spreading rates are shown in Table C

Table C

As can be seen, at 95% contrast ratio all of the examples containing opacifying particle of the invention have better opacity, as evidenced by the increased spreading rates, compared to standard A and B at PVC of 9 and 10%, even though the inventive compositions are at PVC significantly lower than these. Even at 98% contrast ratio all examples of the invention have a better spreading rate than the standard A at PVC of 9%.

Effect of intermediate polymer on pH stability of a pigment dispersion

Onto the pigment dispersion, MB-1 (as described in Table 3) was polymerised various intermediate polymer comprising sodium styrene sulphonate.

The resulting dispersions were allowed to cool and hydrochloric acid was added, whilst stirring, to reduce the pH. The minimum pH reached before flocculation was noted.

Replacing sodium styrene sulphonate monomer with methacrylic acid monomer in the intermediate polymer resulted in flocculation on addition of hydrochloric acid. Example intermediate polymer ² SSS content of Minimum pH reached /wt% intermediate polymer before flocculation

/wt%

1 9.6 10.0 3.78

2 13.0 15.0 3.53

3 9.6 20.0 1.40

4 6.0 20.0 3.05

5 6.0 15.0 Flocculated at pH 4.3

6 9.6 10.0 3.05 wt% based on pigment

SS = sodium styrene sulphonate