Open-Chain Alkoxyamines and their Corresponding Nitroxides for Controlled Low Temperature Radical Polymerization The present invention relates to open chain alkoxyamine compounds, a polymerizable composition comprising a) at least one ethylenically unsaturated monomer and b) at least one open chain alkoxyamine compound. Further aspects of the present invention are a process for polymerizing ethylenically unsaturated monomers, and the use of open chain alkoxyamine compounds for controlled polymerization. The intermediate N-oxyl derivatives, a composition of the N-oxyl derivatives with ethylenically unsaturated monomers and a free radical initiator X, as well as a process and their use for polymerization are also subjects of the present invention.

The compounds of the present invention provide polymeric resin products having low polydispersity. The polymerization process proceeds with enhanced monomer to polymer conversion efficiency at low temperatures. In particular, this invention relates to stable free radical-mediated polymerization processes which provide homopolymers, random copolymers, block copolymers, multiblock copolymers, graft copolymers and the like, at enhanced rates of polymerization and enhanced monomer to polymer conversions at low temperatures.

The polymerization processes and resin products of the present invention are useful in many applications, including a variety of specialty applications, such as for the preparation of block copolymers which are useful as compatibitizing agents for polymer blends, or dispersing agents for coating systems or for the preparation of narrow molecular weight resins or oligomers for use in coating technologies and thermoplastic films or as toner resins and liquid immersion development ink resins or ink additives used for electrophotographic imaging processes.

There are numerous documents in the literature describing the controlled radical polymerization of ethylenically unsaturated monomers using alkoxyamines or nitroxides.

US-A-4 581 429 to Solomon et al., issued April 8,1986, discloses a free radical polymeriza- tion process which controls the growth of polymer chains to produce short chain or oligo- meric homopolymers and copolymers, including block and graft copolymers. The process employs an initiator having the formula (in part) R'R"N-O-X, where X is a free radical species capable of polymerizing unsaturated monomers. The reactions typically have low conversion rates. Specifically mentioned radical R'R"N-O groups are derived from 1,1, 3,3 tetraethylisoindoline, 1,1, 3,3 tetrapropylisoindoline, 2,2, 6,6 tetramethylpiperidine, 2,2, 5,5 tetramethylpyrrolidine or di-t-butylamine. However, the suggested compounds do not fulfill all requirements. Particularly the polymerization of acrylates does not proceed fast enough and/or the monomer to polymer conversion is not as high as desired.

Recently other attempts to develop new polymerization regulators have been published. WO 98/4408 and WO 98/30601 disclose heterocyclic compounds suitable for controlled polymerization processes. WO 98/13392 discloses open chain alkoxyamines which are derived from NO gas or from nitroso compounds.

WO 00/07981 discloses a variety of open chain alkoxyamine compounds, which have no or at most only one electron withdrawing group at the C-atom in 0-position to the nitrogen atom.

These compounds are stable at low temperature and decompose readily at elevated temperature.

Surprisingly, it has now been found that higher alkyl and phenyl substitution patterns at the carbon atom in a position to the nitrogen atom lead to initiators/regulators, which allow controlled radical polymerization at a temperature of 100° C or below. Due to the higher steric hindrance around the nitrogen atom, compared to prior art compounds, high conversions are achievable even at temperatures as low as 100°C. This makes the compounds particularly useful for controlled radical polymerization processes under aqueous conditions at ambient pressure. So far there exists no regulator/initiator which would allow efficient radical polymerization under such conditions, Polymerization of monomers with the instant compounds results in a polymer or copolymer of narrow polydispersity and high monomer to polymer conversion even at temperatures below 100° C. High conversions are achieved even in short reaction times.

One subject of the invention is a compound of formula la, lb, or Ic wherein Y is O or NR, ol and Rlol is H or Cl-C, 8alkyl or R7 and/or R8 and Rio, together with the nitrogen atom to which they are bound form a 5 or 6 membered heterocyclic ring; Ri, R2 and R3 independently are benzyl, C1-C18alkyl, C2-C18alkenyl which are unsubstituted or substituted by OH or a by group-O-C (O)-R102 ; or C2-C18alkyl which is interrupted by at least one O atom or a group NR102 wherein R102 is hydrogen, C1-C18alkyl or C6-C10aryl ; or R, and R2 together with the carbon atom to which they are bound form a C5-C12cycloalkyl group; or in formula la R3 and R4 together with the carbon atom to which they are bound form a C5-C12cycloalkyl group ; R4 is C2-C, 2alkyl ; Rs and R6 are independently H, C1-C18alkyl, C2-C18alkenyl, benzyl, C5-C12cycloalkyl or phenyl ; R7 and R8 independently are H, C1-C18alkyl, C2-C18alkenyl, C5-C12cycloalkyl or a group -C(O)-(C1-C18)alkyl, -C(O)-O-(C1-C18)alkyl, -C(O)-O-phenyl, -C(O)-C(O)-OH, -C(O)-C(O)-NH- i (C,-C, 8alkyl),-C (S)-S-(C,-C, 8) alkyl, °@,-SiRaRbRC wherein Ra, Rb, Rc independently are C1-C18alkyl or R7 and R8 are the following group wherein R103, R104 and R105 independently are H, C1-C8alkyl, C1- C8alkoxy, C1-C8alkylthio, -O-C(O)-(C1-C8)alkyl, -O-C(O)-(C6-C10)aryl, nitro, cyano or halogen ; Rg, R10, R11, R12, R13 and R14 independently are H, OH, C1-C8alkoxy, C1-C8alkyl, SH, Cl- C8alkylthio, -O-C(O)-(C1-C8)alkyl, -O-C(O)-(C6-C10)aryl, nitro, cyano, halogen or a group NR106R107 wherein Rice and R107 independently are hydrogen, C1-C18alkyl or C6-C10aryl or together with the nitrogen atom to which they are bound form a 5 or 6 membered heterocyclic ring; and X is selected from the group consisting of H H3C -CH2-aryl alkyl (C1-C18) Claryl,-CH2-CH2-aryls alkyl (C1-C 8) taryl (C5- C6cycloalkyl) 2CCN, (C1-C12alkyl)2CCN, -CH2CH=CH2, (C1-C12)alkyl-CR20-C(O)-(C1-C12)alkyl, (C1-12)alkyl-CR20-C(O)-(C6-C10)aryl, (C1-12)alkyl-CR20-C(O)-O-R21, (C1-C12)alkyl-CR20- C (O)-phenoxy, (C1-12)alkyl-CR20-C(O)-N-di(C1-C12)alkyl, (C1-12)alkyl-CR20-CO-NH(C1- C, Z) alkyl, (C,-C, 2) alkyl-CR20-CO-NH2,-CH2CH=CH-CH3,-CH2-C (CH3) =CH2,-CH2-CH=CH- cH ri phenyl,-CH c"CH, 3-cyclohexenyl, 3-cyclopentenyl, 0 O R20 is hydrogen or C,-C, 2alkyl ; R2, is C1-C18alkyl or C2-C, 8alkyl which is interrupted by at least one O atom or a group NR102 wherein R102 is hydrogen, C,-C,aalkyl or C6-C, oaryl ; the alkyl groups are unsubstituted or substituted with one or more-OH,-COOH,-O (C1- C8alkyl), NR106R107 or -COR20 groups wherein R20, Rice and R, 07 have the meanings as defined above; the aryl groups are phenyl or naphthyl which are unsubstituted or substituted with C,- C,2alkyl, halogen, C,-C, 2alkoxy, C,-C, 2alkylthio, C,-C, 2alkylcarbonyl, glycidyloxy, OH, SH, - COOH or-COO (C,-C, 2) alkyl.

The alkyl radicals in the various substituents may be linear or branched. Examples of alkyl containing 1 to 18 carbon atoms are methyl, ethyl, propyl, isopropyl, butyl, 2-butyl, isobutyl, t- butyl, pentyl, 2-pentyl, hexyl, heptyl, octyl, 2-ethylhexyl, t-octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, hexadecyl and octadecyl.

Alkenyl with 2 to 18 carbon atoms is a linear or branched radical as for example vinyl, pro- penyl, 2-butenyl, 3-butenyl, isobutenyl, n-2, 4-pentadienyl, 3-methyl-2-butenyl, n-2-octenyl, n- 2-dodecenyl, iso-dodecenyl, oleyl, n-2-octadecenyl oder n-4-octadecenyl.

Preferred is alkenyl with 3 bis 12, particularly preferred with 3 to 6 carbon atoms.

5 or 6 membered heterocyclic rings are for example piperidine or pyrolidine.

Examples for hydroxy substituted alkyl are hydroxy propyl, hydroxy butyl or hydroxy hexyl.

C2-C, 8alkyl interrupted by at least one O atom is for example-CH2-CH2-O-CH2-CH3,-CH2- CH2-O-CH3-or-CH2-CH2-O-CH2-CH2-CH2-O-CH2-CH3-. It is preferably derived from polyethlene glycol. A general description is-((CH2) a-O) b-H/CH3, wherein a is a number from 1 to 6 and b is a number from 2 to 10.

C2-Ciga) 8alkyl interrupted by at least one NR5 group may be generally described as- ( (CH2) a- NR5) b-H/CH3, wherein a, b and R5 are as defined above.

C6-C, o aryl is for example phenyl or naphthyl, but also comprised are C,-C4alkyl substituted phenyl, C,-C4alkoxy substituted phenyl, hydroxy, halogen or nitro substituted phenyl.

Examples for alkyl substituted phenyl are ethylbenzene, toluene, xylene and its isomers, mesitylene or isopropylbenzene. Halogen substituted phenyl is for example dichlorobenzene or bromotoluene.

C5-C, 2cycloalkyl is typically cyclopentyl, methylcyclopentyl, dimethylcyclopentyl, cyclohexyl, methylcyclohexyl or trimethylcyclohexyl.

Alkoxy substituents are typically methoxy, ethoxy, propoxy or butoxy and their corresponding isomers.

The alkythio substituents may be derived from the corresponding alkoxy substituents already mentioned.

Halogen is fluoro, chloro, bromo or iodo.

Preferably X is selected from the group consisting of-CH2-phenyl, CH3CH-phenyl, (CH3) 2C- phenyl, (C5-C6cycloalkyl)2CCN, (CH3)2CCN, CH=CH2, (C,-C8alkyl) CR2o-C (O)-phenyl, (C,-C8) alkyl-CR20-C (O)- (C,-C8) alkoxy, (C,-Cg) alkyl- CR20-C (O)-(C,-C8) alkyl, (C,-C8) alkyl-CR20-C (O)-N-di (C,-C8) alkyl, (C,-C8) alkyl-CR20-C (O)- NH (C,-C8) alkyl and (C,-C8) alkyl-CR20-C (O)-NH2, wherein R20 is hydrogen or (C,-C8) alkyl.

More preferably X is selected from the group consisting of-CH2-phenyl, CH3CH-phenyl, (CH3) 2C-phenyl, (C5-C6cycloalkyl) 2CCN, (CH3) 2CCN, CH3CH-CH=CH2, (C1-C4alkyl)CR20-C(O)-phenyl, (C1-C4)alkyl-CR20-C(O)-(C1-C4)alkoxy, (C1- C4) alkyl-CR2o-C (O)- (C,-C4) alkyl, (C,-C4) alkyl-CR2o-C (O)-N-di (C,-C4) alkyl, (C,-C4) alkyl-CR2o- C (O)-NH (C1-C4) alkyl and (C,-C4) alkyl-CR20-C (O)-NH2, wherein R20 is hydrogen or (C,-C4) alkyl.

Preferably in the compounds of formula la, Ib and Ic Y is O and in formula la R4 is C2-C6alkyl or R3 and R4 together with the carbon atom to which they are bound form a 5 to 7 membered cycloalkyl ring.

A preferred subgenus of compounds is wherein Ri, R2 and R3 are C,-C5alkyl ; or in formula la R3 and R4 together with the carbon atom to which they are bound form a CS-C6cycloalkyl group; or R4 is C2-C6alkyl ; R5 and R6 are H; R7 and R8 independently are H, C1-C18alkyl, alkyl, benzyl, C5-C2cycloalkyl or a group -C(O)-(C1-C18)alkyl, -C(O)-O-(C1-C18)alkyl, -C(O)-C(O)-OH, -C(S)-S-(C1-C18)alkyl, - SiRaRbRc wherein Ra, Rb, Rc independently are C,-C, 8alkyl or R7 and R8 are R105 the following group 10464C 0 wherein R103, R104 and R105 independently are H, C,- C8alkoxy, C1-C8alkylthio, -O-C (O)-(C,-C8) alkyl, nitro, cyano, halogen, C1-C8alkyl ; Rg, Rio and R"independently are H, C1-C8-alkoxy, C1-C8alkylthio, -O-C(O)-(C1-C8)alkyl, nitro, cyano, halogen or Cl-alkyl ; and X is as defined above.

More preferred is a compound of formula lb or Ic.

A particularly preferred subgenus is a compound of formula lb wherein Y is O ; R, and R2 are C,-C5alkyl, or together with the carbon atom to which they are bound form a C5-C7cycloalkyl group ; R3 is methyl, ethyl or propyl ; R5 and R6 are H; R7 and R8 independently are H, C1-C18alkyl, allyl, benzyl, C5-C12cycloalkyl or a group -C(O)-(C1-C18)alkyl, -C(O)-O-(C1-C18)alkyl, -C(O)-C(O)-OH, -C(S)-S-(C1-C18)alkyl, -SiRaRbRc wherein Ra, Rb, Rc independently are C1-C18alkyl or R7 and R8 are R105 the following group 0 R103 D ''103 wherein R103, R104 and R105 independently are H, C,- C8alkoxy, C1-C8alkylthio, -O-C(O)-(C1-C8)alkyl, nitro, cyano, halogen, Cl-alkyl ; Rg, Rio and R"independently are H, C1-C8alkoxy, C,-C8alkylthio,-O-C (O)-(C,-C8) alkyl, nitro, cyano, halogen or Cl-alkyl ; and X is selected from the group consisting of H C H 3 -CH2-aryl alkY§ (C1-C18) Y aryl,-CH2-CH2-aryl, aikYl (C1-C18) tarYl, (C5- C6cycloalkyl) 2CCN, (C1-C12alkyl)2CCN, -CH2CH=CH2, (C1-C12)alkyl-CR20-C(O)-(C1-C12)alkyl, (C1-C12)alkyl-CR20-C(O)-(C6-C10)aryl, (C1-C12)alkyl-CR20-C(O)-O-R21, (C1-C12)alkyl-CR20- C (O)-phenoxy, (C1-C12)alkyl-CR20-C(O)-N-di(C1-C12)alkyl, (C1-C12)alkyl-CR20-CO-NH(C1- C, 2) alkyl, (C,-C, ) alkyl-CR2o-CO-NH2,-CH2CH=CH-CH3,-CH2-C (CH3) =CH2,-CH2-CH=CH- phenyl,-CH-c"CH, 3-cyclohexenyl, 3-cyclopentenyl, 2 O R20 is hydrogen or C,-C, 2alkyl ; R2, is C1-C18alkyl or C2-C, 8alkyl which is interrupted by at least one O atom or a group NR102 wherein R102 is hydrogen, C1-C18alkyl or C6-C, 0aryl ; the alkyl groups are unsubstituted or substituted with one or more-OH,-COOH,-O (C,- C8alkyl), NR106R107 or -COR20 groups wherein R20, Rice and R107 have the meanings as defined above; the aryl groups are phenyl or naphthyl which are unsubstituted or substituted with C1- C, 2alkyl, halogen, C,-C, 2alkoxy, C,-C, 2alkylcarbonyl, glycidyloxy, OH, -COOH or-COO (C,- C12)alkyl.

A further subject of the invention is a polymerizable composition, comprising a) at least one ethylenically unsaturated monomer or oligomer, and b) a compound according to formula (la) (lb) or (Ic).

Yet another subject of the invention is a process for preparing an oligomer, a cooligomer, a polymer or a copolymer (block or random) by free radical polymerization of at least one ethylenically unsaturated monomer or oligomer, which comprises (co) polymerizing the monomer or monomers/oligomers in the presence of an initiator compound of formula (la), (lb) or (Ic) under reaction conditions capable of effecting scission of the O-X bond to form two free radicals, the radical eX being capable of initiating polymerization.

Preferably the scission of the O-X bond is effected by ultrasonic treatment, heating or exposure to electromagnetic radiation, ranging from y to microwaves.

More preferably the scission of the O-X bond is effected by heating and takes place at a temperature of between 50°C and 160°C, in particular between 60°C and 120°C and most preferred between 80°C and 100°C.

Preferably the compound of formula la, lb or Ic is present in an amount of from 0.001 mol-% to 20 mol-%, more preferably of from 0.002 mol-% to 10 mol-% and most preferably of from 0.005 mol-% to 5 mol-% based on the monomer or monomer mixture.

When monomer mixtures are used the average molecular weight is taken as basis.

Definitions and preferences for the compounds are mentioned above, they apply also for the composition and process.

Preferably the ethylenically unsaturated monomer is selected from the group consisting of ethylene, propylene, n-butylene, i-butylene, styrene, substituted styrene, conjugated dienes, acrolein, vinyl acetate, vinylpyrrolidone, vinylimidazole, maleic anhydride, (alkyl) acrylic acidanhydrides, (alkyl) acrylic acid salts, (alkyl) acrylic esters, (alkyl) acrylonitriles, (alkyl) acrylamides, vinyl halides or vinylidene halides.

Preferably the ethylenically unsaturated monomer is a compound of formula CH2=C (Ra)- (C=Z)-Rb, wherein Ra is hydrogen or C,-C4alkyl, Rb is NH2, O- (Me+), glycidyl, unsubstituted C,-C, Salkoxy, C2-C, ooalkoxy interrupted by at least one N and/or O atom, or hydroxy-substituted Ci-Ciaatkoxy, unsubstituted C,-C, 8alkylamino, di (Cl-C, 8alkyl) amino, hydroxy-substituted C,-C, 8alkylamino or hydroxy-substituted di (C,-C, 8alkyl) amino,-O-CH2- CH2-N (CH3) 2 or-O-CH2-CH2-N+H (CH3) 2 An' ; An-is a anion of a monovalent organic or inorganic acid; Me is a monovalent metal atom or the ammonium ion.

Z is oxygen or sulfur.

Examples of acids from which the anion An-is derived are C,-C,2carboxylic acids, organic sulfonic acids such as CF3SO3H or CH3SO3H, mineralic acids such as HCI, HBr or HI, oxo acids such as HC104 or complex acids such as HPF6 or HBF4.

Examples for Ra as C2-C, ooalkoxy interrupted by at least one O atom are of formula wherein Rc is C,-C25alkyl, phenyl or phenyl substituted by C,- C, 8alkyl, Rd is hydrogen or methyl and v is a number from 1 to 50. These monomers are for example derived from non ionic surfactants by acylation of the corresponding alkoxylated alcohols or phenols. The repeating units may be derived from ethylene oxide, propylene oxide or mixtures of both.

Further examples of suitable acrylate or methacrylate monomers are given below. and Ra have the meaning as defined above and Re is methyl or benzyl. An is preferably Cl-, Br or O3S-CH3.

Further acrylate monomers are Examples for suitable monomers other than acrylates are Preferably Ra is hydrogen or methyl, Rb is NH2, gycidyl, unsubstituted or with hydroxy substituted C,-C4alkoxy, unsubstituted C1-C4alkylamino, di (C1-C4alkyl) amino, hydroxy- substituted C1-C4alkylamino or hydroxy-substituted di (C,-C4alkyl) amino; and Z is oxygen.

More preferred the ethylenically unsaturated monomer is an acrylic acid ester, acrylamide, acrylnitrile, methacrylic acid ester, methacrylamide, methacrylnitrile.

Acrylic acid esters and methacrylic acid esters are typically C,-C, 8alkyl esters.

Most preferred is n-butylacrylate, tert-butylacrylate, methylacrylate, ethylacrylate, propylacrylate, hexylacrylate and hydroxyethylacrylate.

After the polymerization step is completed the reaction mixture may be cooled down to a temperature below 60° C, preferably to room temperature. The polymer may be stored at this temperature without further reactions occuring.

The process may be carried out in the presence of an organic solvent or in the presence of water or in mixtures of organic solvents and water. Additional cosolvents or surfactants, such as glycols or ammonium salts of fatty acids, may be present. Other suitable cosolvens are described hereinafter.

When acrylic or methacrylic monomers are polymerized, the process is preferably carried out in the presence of an organic solvent. The concentration of the monomer in the organic solvent may influence polymerization rate and final conversion. The concentration may, for example, vary from 5% to 80% by weight, based on the solvent. It is not necessary that the whole amount of monomer is present at the beginning of the polymerization. It is also possible to add further monomer after the polymerization reaction has already started.

As already mentioned the present compounds are particularly useful for aqueous polymerizations, since they allow efficient conversions at temperatures at or below 100°C.

If organic solvents are used, suitable solvents or mixtures of solvents are typically pure alkanes (hexane, heptane, octane, isooctane), aromatic hydrocarbons (benzene, toluene, xylene), halogenated hydrocarbons (chlorobenzene), alkanols (methanol, ethanol, ethylene glycol, ethylene glycol monomethyl ether), esters (ethyl acetate, propyl, butyl or hexyl acetate) and ethers (diethyl ether, dibutyl ether, ethylene glycol dimethyl ether), or mixtures thereof.

The aqueous polymerization reactions can be supplemented with a water-miscible or hydrophilic solvent to help ensure that the reaction mixture remains a homogeneous single phase throughout the monomer conversion. Any water-soluble or water-miscible solvent may be used, as long as the aqueous solvent medium is effective in providing a solvent system which prevents precipitation or phase separation of the reactants or polymer products until after all polymerization reactions have been completed. Exemplary cosolvens useful in the present invention may be selected from the group consisting of aliphatic alcohols, glycols, ethers, glycol ethers, pyrrolidines, N-alkyl pyrrolidinones, N-alkyl pyrrolidones, polyethylene glycols, polypropylene glycols, amides, carboxylic acids and salts thereof, esters, organosulfides, sulfoxides, sulfones, alcohol derivatives, hydroxyether derivatives such as butyl carbitol or cellosolve, amino alcohols, ketones, and the like, as well as derivatives thereof and mixtures thereof. Specific examples include methanol, ethanol, propanol, dioxane, ethylene glycol, propylene glycol, diethylene glycol, glycerol, dipropylene glycol, tetrahydrofuran, and other water-soluble or water-miscible materials, and mixtures thereof. When mixtures of water and water-soluble or water-miscible organic liquids are selected as the aqueous reaction media, the water to solvent weight ratio is typically in the range of about 100: 0 to about 10: 90.

The process is particularly useful for the preparation of block copolymers.

Block copolymers are, for example, block copolymers of polystyrene and polyacrylate (e. g., poly (styrene-co-acrylate) or poly (styrene-co-acrylate-co-styrene). They are useful as adhesives or as compatibilizers for polymer blends or as polymer toughening agents.

Poly (methylmethacrylate-co-acrylate) diblock copolymers or poly (methylacrylate-co-acrylate- co-methacrylate) triblock copolymers) are useful as dispersing agents for coating systeme, as coating additives (e. g. rheological agents, compatibilizers, reactive diluents) or as resin component in coatings (e. g. high solid paints). Block copolymers of styrene, (meth) acrylates and/or acrylonitrile are useful as modifiers for plastics, elastomers and adhesives.

Furthermore, block copolymers of this invention, wherein the blocks alternate between polar monomers and non-polar monomers, are useful in many applications as amphiphilic surfactants or dispersants for preparing highly uniform polymer blends.

The (co) polymers of the present invention may have a number average molecular weight from 1 000 to 400 000 g/mol, preferably from 2 000 to 250 000 g/mol and, more preferably, from 2 000 to 200 000 g/mol. The number average molecular weight may be determined by size exclusion chromatography (SEC), matrix assisted laser desorption/ionization mass spectrometry (MALDI-MS) or, if the initiator carries a group which can be easily distinguished from the monomer (s), by NMR spectroscopy or other conventional methods.

The polymers or copolymers of the present invention have preferably a polydispersity of from 1.1 to 2, more preferably of from 1.1 to 1.8 and most preferably from 1.1 to 1.6.

Thus, the present invention also encompasses in the synthesis novel block, multi-block, star, gradient, random, hyperbranched and dendritic copolymers, as well as graft copolymers.

The polymers prepared by the present invention are useful for following applications : adhesives, detergents, dispersants, emulsifiers, surfactants, defoamers, adhesion promoters, corrosion inhibitors, viscosity improvers, lubricants, rheology modifiers, thickeners, crosslinkers, paper treatment, water treatment, electronic materials, paints, coatings, photo- graphy, ink materials, imaging materials, superabsorbants, cosmetics, hair products, preser- vatives, biocide materials or modifiers for asphalt, leather, textiles, ceramics and wood.

Alternatively controlled free radical polymerization may be carried out using the nitroxyl precursors of the corresponding alkoxyamines together with a source of free radicals.

Consequently a further subject of the invention is a polymerizable composition, comprising a) at least one ethylenically unsaturated monomer or oligomer, and b) a compound according to formula (Ila) (Ilb) or (Ilc) wherein Y is O or NRIO, and R101 is H or C1-C18alkyl or R7 and/or R8 and Rlol together with the nitrogen atom to which they are bound form a 5 or 6 membered heterocyclic ring; Ri, R2 and R3 independently are benzyl, C1-C18alkyl, C2-C18alkenyl which are unsubstituted or substituted by OH or a by group-O-C (O)-R102 ; or C2-C, 8alkyl which is interrupted by at least one O atom or a group NR102 wherein R102 is hydrogen, C1-C18alkyl or C6-C10aryl ; or R, and R2 together with the carbon atom to which they are bound form a C5-C12cycloalkyl group; or in formula la R3 and R4 together with the carbon atom to which they are bound form a C5-C12cycloalkyl group ; R4 is C2-C12alkyl ; R5 and R6 are independently H, C1-C18alkyl, C2-C18alkenyl, benzyl, C5-C12cycloalkyl or phenyl ; R7 and R8 independently are H, C1-C18alkyl, C2-C18alkenyl, C5-C12cycloalkyl or a group -C(O)-(C1-C18)alkyl, -C(O)-O(C1-C18)alkyl, -C(O)-O-phenyl, -C(O)-C(O)-OH, -C(O)-C(O)-NH- I (C1-C18alkyl),-C (S)-S-(C1-C18) alkyl, °4 ?,.-SiRaRbRc wherein Ra Rb, Rc independently are C1-C18alkyl or R7 and RB are the following group wherein R103, R104 and R105 independently are H, C1-C8alkyl, Ci- C8alkoxy, C1-C8alkylthio, -O-C(O)-(C1-C8)alkyl, -O-C(O)-(C6-C10)aryl, nitro, cyano or halogen ; Rg, R10, R11, R12, R13 and R14 independently are H, OH, C1-C8alkoxy, C1-C8alkyl, SH, C,- C8alkylthio, -O-C (O)-(C,-C8) alkyl,-O-C (O)-(C6-C10) aryl, nitro, cyano, halogen or a group NR, 06R107 wherein Rice and R107 independently are hydrogen, C,-C, 8alkyl or Cg-C, oaryl or together with the nitrogen atom to which they are bound form a 5 or 6 membered heterocyclic ring; and c) a source of free radicals capable of initiating polymerization of ethylenically unsaturated monomers.

Also subject of the invention is a process for preparing an oligomer, a cooligomer, a polymer or a copolymer (block or random) by free radical polymerization of at least one ethylenically unsaturated monomer/oligomer, which comprises subjecting the above composition to heat or actinic radiation.

For example the polymerization is carried out by applying heat and takes place at a temperature of between 50°C and 160°C, in particular between 60°C and 120°C and most preferred between 80°C and 100°C.

The free radical initiator of component c) is preferably a bis-azo compound, a peroxide perester or a hydroperoxide.

Specific preferred radical sources are 2, 2'-azobisisobutyronitrile, 2,2'-azobis (2-methyl- butyronitrile), 2,2'-azobis (2, 4-dimethylvaleronitrile), 2,2'-azobis (4-methoxy-2, 4-dimethylvale- ronitrile), 1,1'-azobis (1-cyclohexanecarbonitrile), 2,2'-azobis (isobutyramide) dihydrate, 2- phenylazo-2, 4-dimethyl-4-methoxyvaleronitrile, dimethyl-2, 2'-azobisisobutyrate, 2- (carbamoylazo) isobutyronitrile, 2,2'-azobis (2,4, 4-trimethylpentane), 2,2'-azobis (2- methylpropane), 2,2'-azobis (N, N'-dimethyleneisobutyramidine), free base or hydrochloride, 2,2'-azobis (2-amidinopropane), free base or hydrochloride, 2,2'-azobis {2-methyl-N- [1, 1- bis (hydroxymethyl) ethyl] propionamide} or 2,2'-azobis {2-methyl-N- [1, 1-bis (hydroxymethyl)-2- hydroxyethyl] propionamide; acetyl cyclohexane sulphonyl peroxide, diisopropyl peroxy dicarbonate, t-amyl perneodecanoate, t-butyl perneodecanoate, t-butyl perpivalate, t- amylperpivalate, bis (2, 4-dichlorobenzoyl) peroxide, diisononanoyl peroxide, didecanoyl peroxide, dioctanoyl peroxide, dilauroyl peroxide, bis (2-methylbenzoyl) peroxide, disuccinic acid peroxide, diacetyl peroxide, dibenzoyl peroxide, t-butyl per 2-ethylhexanoate, bis- (4- chlorobenzoyl)-peroxide, t-butyl perisobutyrate, t-butyl permaleinate, 1,1-bis (t- butylperoxy) 3,5, 5-trimethylcyclohexane, 1,1-bis (t-butylperoxy) cyclohexane, t-butyl peroxy isopropyl carbonate, t-butyl perisononaoate, 2, 5-dimethylhexane 2,5-dibenzoate, t-butyl peracetate, t-amyl perbenzoate, t-butyl perbenzoate, 2,2-bis (t-butylperoxy) butane, 2,2 bis (t-butylperoxy) propane, dicumyl peroxide, 2, 5-dimethylhexane-2, 5-di-t-butylperoxide, 3-t- butylperoxy 3-phenylphthalide, di-t-amyl peroxide, a, a'-bis (t-butylperoxy isopropyl) benzene, 3,5-bis (t-butylperoxy) 3, 5-dimethyl 1, 2-dioxolane, di-t-butyl peroxide, 2, 5-dimethylhexyne-2, 5- di-t-butylperoxide, 3,3, 6,6, 9, 9-hexamethyl 1,2, 4,5-tetraoxa cyclononane, p-menthane hydroperoxide, pinane hydroperoxide, diisopropylbenzene mono-a-hydroperoxide, cumene hydroperoxide or t-butyl hydroperoxide.

Azo initiators and peroxides are most preferred.

Preferably the nitroxyl radical, component b), is present in an amount of from 0.001 mol-% to 20 mol-%, more preferably of from 0.002 mol-% to 10 mol-% and most preferably of from 0.005 mol-% to 5 mol-% based on the monomer or monomer mixture.

Preferably the free radical initiator, component c), is present in an amount of from 0.001 mol- % to 20 mol-%, more preferably of from 0.002 mol-% to 10 mol-% and most preferably of from 0.005 mol-% to 5 mol-%, based on the monomer or monomer mixture.

The molar ratio of free radical initiator to stable free nitroxyl radical is preferably from 20: 1 to 1: 2, more preferably from 10: 1 to 1: 2.

The compounds of formula Ilb are novel and therefore also subject of the present invention wherein Y is O or NR, o, and Rlol is H or C1-C18alkyl or R7 and Rlol together with the nitrogen atom to which they are bound form a 5 or 6 membered heterocyclic ring; Ri, R2 and R3 independently are benzyl, C1-C18alkyl, C2-C18alkenyl which are unsubstituted or substituted by OH or a group-0-C (O)-R102 ; or C2-C18alkyl which is interrupted by at least one O atom or a group NR102 wherein R102 is hydrogen, C1-C18alkyl or C6-C10aryl ; or R, and R2 together with the carbon atom to which they are bound form a C5-C12cycloalkyl group; R5 and R6 are independently H, C1-C18alkyl, C2-C18alkenyl, benzyl, c5-C12cycloalkyl or phenyl ; R7 and R8 independently are H, C1-C18alkyl, C2-C18alkenyl, C5-C12cycloalkyl or a group -C(O)-(C1-C18)alkyl, -C(O)-O-(C1-C18)alkyl, -C(O)-O-phenyl, -C(O)-C(O)-OH, -C(O)-C(O)-NH- i (C1-C18alkyl),-C (S)-S-(C1-C, 8) alkyl, °9S,-SiRaRbRC wherein Ra, Rb, Rc independently are C,-C, 8alkyl or R7 and RB are one of the following groups wherein R103, R104 and R105 independently are H, C1-C8alkyl, C1- C8alkoxy, C1-C8alkylthio, -O-C(O)-(C1-C8)alkyl, -O-C(O)-(C6-C10)aryl, nitro, cyano or halogen ; Rg, Rio and R11 independently are H, OH, Ci-Cgatkoxy, C,-C8alkyl, SH, C1-C8alkylthio, -O-C(O)-(C1-C8)alkyl, -O-C(O)-(C6-C10)aryl, nitro, cyano, halogen or a group NR106R107 wherein Rice and R, 07 independently are hydrogen, C1-C18alkyl or C6-C10aryl or together with the nitrogen atom to which they are bound form a 5 or 6 membered heterocyclic ring.

Prefered is a compound of formula Ilb wherein Y is O ; Ri and R2 are-CH3, or together with the carbon atom to which they are bound form a C5- C7cycloalkyl group; R3 is methyl, ethyl or propyl ; R5 and R6 are H; R7 and R8 independently are H, C1-C18alkyl, allyl, benzyl, C5-C12cycloalkyl or a group -C(O)-(C1-C18)alkyl, -C(O)-O-(C1-C18)alkyl, -C(O)-C(O)-OH, $-C(S)-S-(C1-C18)alkyl, -SiRaRbRC wherein Ra, Rb, Re independently are C1-C18alkyl or R7 and R8 are one of the following groups wherein R103, R104 and R, os independently are H, C,-C8alkoxy, C1-C8alkylthio, -O-C (O)-(C1-C8) alkyl, nitro, cyano, halogen, Ci-Cgatky) ; and Rg, Rio and R11 independently are H, C,-Caalkoxy, C,-C8alkylthio,-O-C (O)- (C,-C8) alkyl, nitro, cyano, halogen or C1-C8alkyl.

Further subjects of the invention are the use of a compound of formula la, Ib, or Ic for the polymerization of ethylenically unsaturated monomers; the use of a compound of formula IIa, llb or llc together with a source of free radicals for the polymerization of ethylenically unsaturated monomers and a polymer or copolymer obtainable by one of the above mentioned polymerization processes.

The definitions and preferences given for the alkoxyamine compounds apply also for the nitroxyl compounds, their composition with ethylenically unsaturated monomers and the polymerization process therewith.

Open chain alkoxyamines and nitroxides are prepared via two general routes.

A) Oxidation of 3,3, 5,5-tetrasubstituted morpholin-2-ones by peracetic acid, followed by alkylation of the resulting N-oxyls (CuBr, t-BuOOH, ethylbenzene ; or CuCl, pentamethylethylenetriamine, 1-phenethylbromide) and reductive ring cleavage (LiAIH4).

B) Ring opening of 3,3, 5,5-tetrasubstituted morpholin-2-ones (NaOH), followed by dialkylation of the resulting hydroxy carboxylate salts (NaH, alkylhalide), reduction of the ester group (LiAIH4), acetylation (acetylchloride, pyridine), oxidation to the N-oxyl (peracetic acid) and alkylation of the N-oxyl (CuCI, pentamethylethylenetriamine, 1- phenethylbromide).

3,3, 5,5-Tetrasubstituted morpholin-2-ones and 3,3, 5,5-tetrasubstituted morpholin-2-one N- oxyls are well known compounds in the literature. Their preparation is described e. g. in WO 98/44008, WO 01/23435, J. T. Lai, Synthesis 1984,122 and S. D. Rychnovsky et al., J. Org.

Chem. 1998,63, 6363.

The following examples illustrate the invention.

A) Examples for the preparation of alkoxyamines The alkoxyamines may for example be prepared from morpholinone alkoxyamines as described above. The prepared morpholinone-alkoxyamine precursors are shown in Table 1 Table 1: Morpholinone-alkoxyamines No Structure No Structure O O O O -N N 101 N 0 4N N I I u u Reference compound as example for the general preparation O O O O uT I u 103 70 104 4N 4N I I / No Structure No Structure 4N 4NO 0 105 o6 106 1 1 u 0 i 0 0 0 0 107 N /108 N / 1 1b 4N 4N PO I I 109 N ci I I u Example A1 reference for the general preparation : 3, 3,5, 5-Tetramethyl-4- (1-phenyl- ethoxy)-morpholin-2-one 101 To a solution of 87.8 g (0.51 mol) 3,3, 5, 5-tetramethyl-morpholin-2-one-N-oxyl (prepared according to J. T. Lai, Synthesis 1984,122) in ethylbenzene (1275 ml) and water (64 ml) is added 0.88 g (6.1 mmol) of CuBr and 1.97 g (6.1 mmol) of tetrabutylammoniumbromide at ambient temperature. The red suspension is vigorously stirred and heated to 40 °C. At this temperature 150.7 ml (1.10 mol) of a 70% aqueous tert-butylhydroperoxyde solution is added over a period of 20 min. The internal temperature rises during the addition and is kept below 65 °C by cooling with a water-bath. After complete addition, the emulsion is stirred at 50 °C for 30 min, then cooled in an ice-bath and a solution of 137 g Na2SO3 in water (1000 ml) is added. The phases are separated, the organic layer is washed with water (2x500 ml) and brine (250 ml), dried over Na2SO4, filtered and concentrated under reduced pressure. The residue is recrystallized from hexane to yield 104.8 g (74 %) of the title compound as a white solid.

'H-NMR (400 MHz, CDCl3), 8 (ppm): 7.37-7. 28 m (5H), 4.76-4. 64 2q (1H), 4.09-3. 87 m (2H), 1. 65, 1.62, 1.35, 1.29, 1.22, 1.06, 0.85, 0.69 8s (12H), 1.48, 1. 44 2d (3H).

Example A2: 3, 3-Diethyl-5. 5-dimethyl-4- (1-phenyl-ethoxy)-morpholin-2-one 102 The compound is prepared in analogy to example A1 from 3, 3-diethyl-5,5-dimethyl- morpholin-2-one-N-oxyl in a yield of 100 % (crude) as yellow liquid.

'H-NMR (400 MHz, CDCI3), 8 (ppm): 7.36-7. 25 m (5H), 4.73-4. 65 m (1H), 4.04-3. 77 m (2H), 2.22-1. 68 m (3H), 1.50-1. 46 m (3H), 1.40-0. 67 m (13H).

Example A3: 5, 5-Dimethyl-4- (1-phenvl-ethoxy)-3, 3-dipropyl-morpholin-2-one 103 The compound is prepared in analogy to example A1 from 5, 5-dimethyl-3, 3-dipropyl- morpholin-2-one-N-oxyl in a yield of 100 % (crude) as slightly yellow liquid.

'H-NMR (400 MHz, CDCl3), 8 (ppm): 7.36-7. 26 (5H), 4.73-4. 64 m (1H), 4.02-3. 76 m (2H), 2.12-1. 36 m (7H), 1.29-0. 60 m (16 H).

Example A4: 3,5,5-Trimethyl-3-pentyl-4-(1-phenyl-ethoxy)-morpholin-2-one 104 The compound is prepared in analogy to example A1 from 3,5, 5-trimethyl-3-pentyl- morpholin-2-one-N-oxyl in a yield of 100 % (crude) as yellow liquid.

'H-NMR (400 MHz, CDCl3), # (ppm): 7.34-7. 25 m (5H), 4.73-4. 62 m (1H), 4.03, 3.92, 3.82, 3.70 4d (2H), 1.89-0. 61 m (21 H).

Example A5: 2, 2-Dimethvl-1-(1-phenvl-ethoxv)-4-oxa-1-aza-spiror5. 5lundecan-5-one 105 The compound is prepared in analogy to example A1 from 2, 2-Dimethyl-4-oxa-1-aza- spiro [5. 5] undecan-5-one-N-oxyl in a yield of 81 % after crystallization as white solid.

M. p.: 98-102 °C.

Example A6 : 2. 2-Dimethvl-1- (1-phenvl-ethoxy)-4-oxa-1-aza-spiror5. 61dodecan-5-one 106 The compound is prepared in analogy to example A1 from 2, 2-Dimethyl-4-oxa-1-aza- spiro [5.6] dodecan-5-one-N-oxyl in a yield of 89 % after crystallization as white solid.

M. p.: 88-90 °C.

Example A7: 3, 5z5-Trimethvl-3-phenvl-4-(1-phenvl-ethoxv)-morPholin-2-one 107 To 18.3 g (78 mmol) 3,5, 5-trimethyl-3-phenyl-morpholin-2-one-N-oxyl (prepared according to S. D. Rychnovsky et al., J. Org. Chem. 1998,63, 6363), 12.0 g (117 mmol) CuCl and 25.0 ml (117 mmol) pentamethyl-diethlenetriamine, toluene (150 ml) is added. The green suspension is stirred and a solution of 11.0 ml (78 mmol) of 1-phenylethylbromide in toluene (50 ml) is slowly added during a period of 2 h. After complete addition, the suspension is stirred for 20 h, then filtered over Hyflo, washed with 1M HCI solution (2x 70 ml), water (70 ml) and brine (70 ml), dried over Na2SO4, filtered and concentrated under reduced pressure. 25.7 g (97 %) of the title compound is obtained as a slightly yellow resin.

'H-NMR (400 MHz, CDCl3), 8 (ppm): 7.70 d (1H), 7.54 d (1H), 7.39-7. 20 m (7H), 4.57, 4.51 2q (1H), 4.13, 3.93, 3.89, 3.70 4d (2H), 1.93, 1.66, 1.37, 1.36, 1.20, 0.62 6s (9H), 1.51, 1.27 2d (3H).

Example A8: 3-Ethyl-5. 5-dimethyl-3-phenvl-4- (1-phenyl-ethoxy)-morpholin-2-one 108 The compound is prepared in analogy to example A7 from 3-ethyl-5, 5-dimethyl-3-phenyl- morpholin-2-one-N-oxyl in a yield of 95 % as yellow liquid.

'H-NMR (400 MHz, Ceci3), 8 (ppm): 7.70-7. 16 m (10H), 5.24-5. 08,4. 85-4.80 2m (1H), 3.99- 3.50 m (2H), 2.45-0. 57 m (14H).

Example A9: 3-(4-Chloro-phenyl)-3,5,5-trimethyl-4-(1-phenyl-ethoxy)-morp holin-2-one 109 The compound is prepared in analogy to example A7 from 3,5, 5-trimethyl-3- (4-chloro) phenyl- morpholin-2-one-N-oxyl in a yield of 78 % as yellow resin.

'H-NMR (400 MHz, CDCl3), 8 (ppm): 7.64 d (1H), 7.41-7. 18 m (8H), 4.55-4. 45 m (1H), 4.16, 3.98, 3.89, 3.74 4d (2H), 1.93, 1.68 2s (3H), 1.47, 1.25 2d (3H), 1.37, 1.36 2s (3H), 1.20, 0.68 2s (3H).

The prepared alkoxyamine-diols according to formula la and lb are shown in table 2. They are prepared starting from the compounds 101 to 109.

Table 2: Alkoxyamine-diols according to formula (la) and (Ib), No Structure No Structure 201 N 202 HO OH g u reference : not within the scope of the invention HO 203 HO OH 204 0n g : 3) u O 205 HO \ I 206 , 4q Nq O OH OH OH I OH No Structure No Structure 207 208 Lit I I JE cl I I ) T I zu Example A10: 2-[(2-Hydroxy-1,1-dimethyl-ethyl)-(1-phenyl-ethoxy)-amino]-2 -methyl- propan-1-ol 201 To a suspension of 2.93 g (75 mmol) LiAIH4 in THF (100 ml) is slowly added at 0-10 °C a solution of 13.9 g (50 mmol) of compound 101 in THF (50 ml). After complete addition, the suspension is heated to reflux and kept at this temperature for 5 h. The mixture is cooled in an ice-bath and saturated NH4CI-solution (25 ml) is added carefully. EtOAc (500 ml) and water (100 ml) is added, the phases separated and the organic layer washed with water (100 ml) and brine (100 ml), dried over Na2SO4, filtered and concentrated under reduced pressure to yield 13. 2 g (94 %) of the title compound as a white solid.

M. p. : 79-$l OC.

Example A11 : 2-Ethyl-2-f (2-hydroxv-1, 1-dimethyl-ethyl)- (1-phenvl-ethoxy)-aminol- butanol 202 The compound is prepared in analogy to example A10 from compound 102 in a yield of 73 % after crystallization as white solid.

M. p.: 65-69 °C.

Example A12: 2-r (2-Hydroxy-1, 1-dimethyl-ethyl)-(1-phenyl-ethoxy)-amino]-2-propyl- pentan-1-ol 203 The compound is prepared in analogy to example A10 from compound 103 in a yield of 83 % after crystallization as white solid. M. p.: 88-92 °C.

Example A13: 2-f (2-Hydroxy-1, 1-dimethyl-ethyl)- (1-phenyl-ethoxy)-aminol-2-methyl- heptan-1-ol 204 The compound is prepared in analogy to example A10 from compound 104 in a yield of 71 % as yellow resin.

'H-NMR (400 MHz, CDCl3), 8 (ppm): 7.39-7. 26 m (5H), 4.83-4. 75 m (1H), 3.79-2. 50 m (6H), 1.85-0. 83 m (22H).

Example A14: 2-f (1-Hydroxymethyl-cyclohexyl)- (1-phenyl-ethoxy)-aminol-2-methyl- propan-1-ol 205 The compound is prepared in analogy to example A10 from compound 105 in a yield of 77 % after crystallization as white solid.

M. p.: 84-86 °C.

Example A15: 2-f (1-Hydroxymethyl-cycloheptyl)- (1-phenvl-ethoxy)-aminol-2-methyl- propan-1-ol 206 The compound is prepared in analogy to example A10 from compound 106 in a yield of 67 % after crystallization as white solid.

M. p.: 68-72 °C.

Example A16: 2-[(2-Hydroxy-1,1-dimethyl-ethyl)-(1-phenyl-ethoxy)-amino]-2 -phenyl- propan-1-ol 207 The compound is prepared in analogy to example A10 from compound 107 in a yield of 89 % as yellow resin.

'H-NMR (400 MHz, CDCI3), 8 (ppm): 7.54-7. 17 m (10 H), 5.07, 5.00 2q (1H), 4.02-2. 15 m (6H), 1.78, 1.67, 1.25, 1.03, 0.64, 0.56 6s (9H), 1.70, 1.62 2d (3H).

Example A17: 2-r (2-Hydroxy-1, 1-dimethyl-ethyl)- (1-phenvl-ethoxy)-aminol-2-phenyl- butanol 208 The compound is prepared in analogy to example A10 from compound 108 in a yield of 71 % after crystallization as white solid.

M. p.: 94-104 OC.

Example A18: 2-(4-Chloro-phenyl)-2-[(2-hydroxy-1,1-dimethyl-ethyl)-(1-phe nyl-ethoxy)- aminol-propan-1-ol 209 The compound is prepared in analogy to example A10 from compound 109 in a yield of 84 % as yellow resin.

MS (DEP (CI)) : MH+ = 378 The prepared unsymmetrically substituted open chain alkoxyamine derivatives are shown in table 3 together with their amine and nitroxide precursors.

Table 3: No Structure No Structure 301', ? 302 , 9 ON O ON 0 H H No Structure No Structure 303 0--1 0 304 0- Q 0 O-L, 0-IN O-'O O : O 305 0 306 N-< 0 0 H N O I I/ 307 308 A Ç O', Olk N 0 OH N / Example A19: Acetic acid 2- (2-benzvloxv-1, 1-dimethvl-ethVlamino)-2-phenvl-propyl ester 301 The amine 301 is prepared according to the following scheme: O OH /1) NaH, BnBr CHCI3, NaOH 2) LiAIH4 /O - J. + t 2L) AiH JL. J o NH I/- HON ONa H 0 3) AcCI, pyridine ON O 0 ' N H A To a suspension of 183.8 g (2.0 mol) 2-amino-2-methylpropanol, 239 ml (2.0 mol) acetophenone, and 123.7 g (3.0 mol) NaOH in 1,2-dimethoxyethane (500 ml) is slowly added 80.9 ml (1.0 mol) chloroform at 0-5 °C (ice-bath) over a period of 4.5 h. After complete addition, the temperature is raised slowly to ambient temperature and the brown suspension stirred overnight. Water (1 L) is added (exothermic), then tert-butylmethylether (1 L). Stirring is continued for 1 h, then the mixture transferred into a separation funnel, water and tert- butylmethylether added until the phases separate. The aqueous phase is evaporated to dryness and further dried under high vacuum to yield 151 g of a brown solid. The solid is suspended in CH2CI2 (500 ml), stirred for 30 min, then filtered and dried to yield 79.9 g (31 %) of the sodium salt A as beige solid.

To a suspension of 73.6 g (300 mmol) of the sodium salt A is added at room temperature 24.0 g (600 mmol) of a ca. 60% sodium hydride dispersion in oil. After stirring for 1 h 75.9 ml (660 mmol) benzylbromide is slowly added (exothermic, internal temperature is kept below 40 °C by cooling in a water-bath). After complete addition the mixture is stirred for 1 h, another 25.0 ml (217 mmol) benzylbromide are added, stirring continued for 1 h, another 15.0 ml (130 mmol) benzylbromide added, and stirring continued for another 2.5 h. The reaction mixture is carefully hydrolyzed, toluene (500 ml) is added and washed with water (2x250 ml) and brine (250 ml), dried (Na2SO4), filtered and evaporated. Side products are removed by distillation (0.1 mbar, 170 °C bath temperature) to yield 92.4 g (74%) of the dibenzylated compound as a brown liquid. A solution of 30.0 g (71.8 mmol) of this in THF (15 ml) is slowly added to a suspension of LiAIH4 in THF (150 ml), maintaining the internal temperature below 20 °C by cooling (ice-bath). After complete addition, the reaction mixture is heated to reflux for 2.5 h, then cooled to 0 °C (ice-bath) and carefully hydrolyzed. EtOAc (250 ml) is added, the organic phase washed with water (2x100 ml), the aqueous phases extracted with EtOAc (250 ml), the combined organic phases washed with brine (100 ml), dried (Na2SO4), filtered and evaporated. Benzylalcohol is removed by distillation (0.1 mbar, 140 °C bath temperature) to yield 22.5 g (71.8 mmol ; 100%) of the reduced compound as a brown liquid. This is dissolved in CH2CI2 (100 ml), 7.0 ml (86.1 mmol) pyridine added, then 6.10 ml (86.1 mmol) of acetylchloride slowly added (exothermic, temperature is kept below 30 °C by cooling in a water bath). After complete addition, the solution is stirred at ambient temperature for 16 h, washed with 1M K2CO3 solution (100 ml) and brine (100 ml), dried (Na2SO4), filtered and evaporated to yield 26.35 g (103 %) compound 301 as brown liquid.

'H-NMR (400 MHz, CDC13), 8 (ppm): 7.56-7. 54 d (2H), 7.35-7. 20 m (8H), 4.46 s (2H), 3.98 s (2H), 3.20 d (1H), 3.08 d (1 H), 2.19 br s (1 H), 1.96 s (3H), 1.63 s (3H), 0.90 s (3H), 0.89 s (3H).

Example A20: Acetic acid 2- (2-benzvloxy-1. 1-dimethyl-ethylamino)-2-phenvl-butyl ester 302 The compound is prepared in analogy to example A19 using propiophenone instead of acetophenone. Colorless liquid.

'H-NMR (400 MHz, CDC13), 8 (ppm): 7.45 m (2H), 7.35-7. 20 m (8H), 4.58-4. 47 m (4H), 3.08 s (2H), 2.04 s (3H), 1.85-1. 76 m (2H), 0.92 s (3H), 0.81 s (3H), 0. 62 t (3H).

Example A21: Acetic acid 2- (2-benzvloxv-1, 1-dimethyl-ethylamino)-2-phenvi-propyl ester-N-oxyl 303 To a solution of 26.4 g (71.8 mmol) of 301 in toluene (70 ml) is added at the same time a 30% aq. NaOH solution (30 ml) and 23.2 ml (140 mmol) of a 40% solution of peracetic acid in acetic acid (exothermic, internal temperature is kept below 20 °C by cooling in an ice- bath). After complete addition, the emulsion is stirred at ambient temperature for 1.5 h, filtered over hyflo, the organic phase washed with 20% aq. Na2SO3 solution (2x50 ml), water (50 ml) and brine (50 ml), dried (Na2SO4), filtered and evaporated. The residue is purified by flash chromatography over silicagel (hexane/EtOAc 5: 1) to give 10.9 g (41 %) of the title compound as orange solid.

M. p.: 42-49 °C. MS (DEP (CI)) : MH+ = 371.

Example A22: Acetic acid 2- (2-benzyloxv-1, 1-dimethvl-ethylamino)-2-phenyl-butyl ester-N-oxyl 304 The compound is prepared in analogy to example A21 from compound 302 in a yield of 83% as brown liquid.

MS (DEP (CI)) : MH+ = 385.

Example A23: Acetic acid 2-f (2-benzvloxv-1. 1-dimethyl-ethyl)- (1-phenyl-ethoxy)- aminol-2-phenyl-propyl ester 305 The compound is prepared in analogy to example A7 from compound 303 in a yield of 48% as yellowish liquid.

'H-NMR (400 MHz, Ceci3), 8 (ppm): 7.56-7. 13 m (15H), 4.97/4. 93 2q (1H), 4.50, 4.47, 4.29, 4.02, 3.67, 3.55, 3.43, 3.16, 2.94, 2.62 10d (5H), 4.03 s (1H), 1.79, 1.74 2s (3H), 1.61-1. 53 2d + s (4.5H), 1.43, 1.22, 1.05, 0.81, 0.61 5s (7.5 H).

Example A24: 2-[(2-Benzyloxy-1,1-dimethyl-ethyl)-(1-phenyl-ethoxy)-amino] -2-phenyl- propan-1-ol 306 A solution of 15.3 g (32 mmol) of compound 305 in diethylether (35 ml) is slowly added to a suspension of 1.26 g (32 mmol) LiAIH4 in diethylether (95 ml). The internal temperature is kept below 10 °C by cooling with an ice-bath. After complete addition, stirring is continued at room temperature for 1.5 h. The mixture is cooled to 0 °C and carefully hydrolyzed. The suspension is filtered, the organic phase washed with water (50 ml) and brine (100 ml), dried (Na2SO4), filtrated and evaporated. The residue is purified by flash chromatography over silicagel (hexane/EtOAc 8: 1) to give 5.42 g (40 %) of the title compound as yellowish liquid.

'H-NMR (400 MHz, CDC13), 8 (ppm): 7.62-7. 16 m (15H), 5.09, 5.00 2q (1H), 4.51 AB (1H), 4.05 AB (1 H), 4.04, 3.44, 3.09, 2.94 4dd (3H), 3.60, 2.68 2d (1H), 2.54-2. 51,2. 26-2.20 2m (1 H), 1.77, 1.55, 1.18, 1.05, 0.82, 0.70 6s (9H), 1.66, 1.54 2d (3H).

Example A25: Acetic acid 2-r (2-benzvloxv-1, 1-dimethyl-ethyl)- (1-phenyl-ethoxv)- aminol-2-phenvl-butyl ester 307 The compound is prepared in analogy to example A7 from compound 304 in a yield of 70 % as yellowish liquid.

1H-NMR (400 MHz, CDCl3), 8 (ppm): 7.62-7. 16 m (15H), 4.97-0. 25 m (24H).

Example A26: 2-r (2-Benzvloxv-1, 1-dimethyl-ethyl)- (1-phenvl-ethoxy)-aminol-2-phenyl- butanol 308 The compound is prepared in analogy to example A24 from compound 307 in a yield of 87 % as colorless resin.

'H-NMR (400 MHz, CDCl3), 8 (ppm): 7.562-7. 21 m (15H), 4.97-0. 15 m (21H).

EA: required C = 77.82, H = 8.33, N = 3.13 ; found: C = 77.85, H = 8.61, N = 3.03.

The prepared symmetrically 0-substituted alkoxyamines according to formula la and lb are shown in table 4.

Table 4: No Structure No Structure 401 0 402 s-"° °"s o o o o o. 0 /non I I O O I 403 Wo oq, 9 404 Wo O$3 "0 o o o os, s oA ro ss Zon I-I- O O I 405 Wo oX 406 Wo O$3 1. 0 0 S Ou, vs 0 g I I O O I I 407 Wo O43 408 p o oX vs S 0 tSs 41 t g O I No Structure No Structure 409 -" r""1 r- 0 0 0 0 : : : Zu I Example A27: 0, 0'-Di- (2-Methoxvbenzoyl)-2-Ethyl-2-f (2-hydroxv-1, 1-dimethVl-ethyl)- (1-phenvl-ethoxv)-aminol-butan-1-ol} 401 To a solution of 4.64 g (15 mmol) of compound 202 in CH2CI2 (45 ml) is added 3.60 mi (45 mmol) pyridine. 5.0 ml (36 mmol) 2-methoxybenzoylchloride is slowly added while keeping the internal temperature at ambient temperature by cooling with a water-bath. After complete addition, 0.18 g (1.5 mmol) dimethylaminopyridine is added and the mixture is stirred for 70 h. The resulting yellow suspension is diluted with CH2CI2 (150 ml), the organic layer washed with 1 M HCI (50 ml), water (50 ml) and brine (50 ml), then dried over Na2SO4, filtered and concentrated under reduced pressure. The residue is purified by flash chromatography over silicagel (hexane/EtOAc 3: 1) to give 6.94 g (80 %) of the title compound as yellow resin.

'H-NMR (400 MHz, CDCl3), 6 (ppm): 7.93-7. 88 m (1H), 7.84-7. 79 m (1H), 7.51-7. 41 m (2H), 7.31-7. 23 m (5H), 7.00-6. 90 m (4H), 4.84 m (1H), 4.66-4. 05 6d (3H), 3.91-3. 86 m (7H), 1.94- 1.60 m (4H), 1.58-1. 56 m (3H), 1.52, 1.42, 1.34, 1.24 4s (6H), 1.11, 1.02, 0.93, 0.79 4t (6H). Example A28: O, O'-Di-(Thiophene-2-carbonyl)-{2-ethyl-2-[(2-hydroxy-1,1-dime thyl- ethyl)- (1-phenyl-ethoxy)-aminol-butan-1-ol} 402 The compound is prepared in analogy to example A27 from compound 202 and 2-thiophene- carboxylic acid chloride in a yield of 78 % as yellow resin.

'H-NMR (400 MHz, CDCl3), 8 (ppm): 7.88-7. 72 m (2H), 7.60-7. 51 m (2H), 7.31-7. 24 m (5H), 7.16-7. 05 m (2H), 4.85-4. 79 m (1H), 4.65-3. 72 8d (4H), 1.96-1. 60 m (4H), 1.55 d (3H), 1.51, 1.42, 1.35, 1.18 4s (6H), 1.13, 1.08, 0.95, 0.81 4t (6H).

Example A29: O, O'-Di-(2-Methoxybenzoyl)-{2-[(2-Hydroxy-1,1-dimethyl-ethyl)- (1- phenvl-ethoxy)-aminol-2-propyl-pentan-1-ol} 403 The compound is prepared in analogy to example A27 from compound 203 and 2- methoxybenzoyl chloride in a yield of 87 % as colorless resin.

'H-NMR (400 MHz, CDCI3), 8 (ppm): 7.93-7. 81 m (2H), 7.51-7. 44 m (2H), 7.29-7. 22 m (5H), 7.01-6. 93 m (4H), 4.85-4. 77 m (1H), 4.66-4. 03 m (3H), 3.91-3. 83 m (7H), 1.88-1. 14 m (17H), 0.91-0. 61 m (6H).

Example A30: O, O'-Di-(2-Methylthiobenzoyl)-{2-[(2-Hydroxy-1,1-dimethyl-ethy l)-(1- phenvl-ethoxy)-aminol-2-propyl-pentan-1-ol} 404 The compound is prepared in analogy to example A27 from compound 203 and 2- (methylthio) benzoyl chloride in a yield of 71 % as slightly yellow resin.

'H-NMR (400 MHz, CDCI3), 8 (ppm): 8.18-7. 96 m (2H), 7.52-7. 44 m (2H), 7.30-7. 10 m (9H), 4.82-3. 84 m (5H), 2.46-2. 44 m (6H), 1.84-1. 05 m (17H), 0.93-0. 60 m (6H).

Example A31: O, O'-Di-(2-Methoxybenzoyl)-{2-[(2-Hydroxy-1,1-dimethyl-ethyl)- (1- phenvl-ethoxy)-aminol-2-methyl-heptan-1-ol} 405 The compound is prepared in analogy to example A27 from compound 204 and 2- methoxybenzoyl chloride in a yield of 84 % as slightly yellow resin.

'H-NMR (400 MHz, CDCI3), 8 (ppm): 7.95-7. 80 m (2H), 7.52-7. 42 m (2H), 7.32-7. 20 m (5H), 7.00-6. 90 m (4H), 4.84-4. 82 m (1H), 4.58-3. 86 m (10H), 1.90-0. 80 m (23H).

Example A32: O, O'-Di-(2-Methylthiobenzoyl)-{2-[(1-Hydroxymethyl-cyclohexyl) -(1- phenyl-ethoxy)-aminol-2-methyl-propan-1-ol 406 The compound is prepared in analogy to example A27 from compound 205 and 2- (methylthio) benzoyl chloride in a yield of 87 % as colorless resin.

'H-NMR (400 MHz, CDCl3), 8 (ppm): 8.16-8. 02 m (2H), 7.52-7. 43 m (2H), 7.30-7. 22 m (7H), 7.15-7. 06 m (2H), 4.94-4. 88 m (1H), 4. 76- 3. 95 8d (4H), 2.48-2. 44 m (6H), 2.10-1. 10 m (19H).

Example A33 : O, O'-Di- (2-Methylthiobenzoyll-f2-f (1-Hydroxymethyl-cycloheptyl)- (1- phenvl-ethoxy)-aminol-2-methyl-propan-1-ol} 407 The compound is prepared in analogy to example A27 from compound 206 and 2- (methylthio) benzoyl chloride in a yield of 64 % as colorless resin.

'H-NMR (400 MHz, CDC13), # (ppm): 8.16-7. 95 m (2H), 7.51-7. 42 m (2H), 7.30-7. 25 m (7H), 7.15-7. 00 m (2H), 4.93-4. 86 m (1H), 4.63-3. 76 8d (4H), 2.47-2. 44 m (6H), 2.18-1. 22 m (21H). <BR> <BR> <P>Example A34 : O. O'-Di- (2-Methoxvbenzoyl)-f2-f (2-Hydroxv-1, 1-dimethyl-ethyl)- (1- phenvl-ethoxy)-aminol-2-phenyl-propan-1-ol) 408 The compound is prepared in analogy to example A27 from compound 207 and 2- methoxybenzoyl chloride in a yield of 81 % as colorless resin.

'H-NMR (400 MHz, CDC13), 5 (ppm): 7.91-6. 77 m (18H), 5.18-3. 58 (m, 11H), 1.86-0. 65 m (12H).

Example A35 :. N.- (2-Benzyloxv-1, 1-dimethyl-ethyl)-. N.- (2-benzvloxy-1-methyl-1-phenyl- ethyl)-@ O.- (1-phenvl-ethyl)-hydroxylamine 409 To a solution of 5.0 g (14.6 mmol) of compound 207 in THF (50 ml) is added 1.46 g (36.4 mmol) of a ca. 60% NaH dispersion in oil. The resulting suspension is stirred at ambient temperature for 1 h, then cooled to 0 °C (ice-bath) and 3.60 ml (29.8 mmol) benzylbromide added slowly. The temperature is slowly raised to ambient temperature and the reaction mixture stirred for 46 h, then again cooled to 0 °C and hydrolyzed. Toluene (100 ml) is added, the organic phase washed with water (2x100 ml) and brine (100 ml), dried (Na2SO4), filtrated and evaporated. The residue is purified by flash chromatography over silicagel (hexane/EtOAc 20: 1) to give 2.81 g (37 %) of the title compound as yellow resin.

'H-NMR (400 MHz, CDCl3), 8 (ppm): 7.66-6. 69 m (20H), 4.96, 4.88 2q (1H), 4.56-2. 57 m (9H), 1.74-0. 47 m (12H).

Example A36 :. N.-(2-BenzvloXv-1, 1-dimethyl-ethyl)-. N.-(2-benzYloxy-1-ethvl-l-phen ethyl)-. O.- (1-phenyl-ethyl)-hydroxylamine 410 To a solution of 7.15 g (20 mmol) of compound 208 in toluene 100 ml) is added 2.0 g (50 mmol) of a ca. 60% NaH dispersion in oil at 0 °C. The resulting suspension is stirred at ambient temperature for 1 h, then again cooled to 0 °C (ice-bath) and 5.10 ml (42 mmol) benzylbromide added slowly. The temperature is slowly raised to ambient temperature. After 4 h DMF (50 ml) is slowly added (exothermic!). The reaction mixture is stirred overnight, then again cooled to 0 °C and hydrolyzed. Toluene (100 mi) is added, the organic phase washed with water (2x100 ml) and brine (100 ml), dried (Na2SO4), filtrated and evaporated. The residue is purified by flash chromatography over silicagel (hexane/EtOAc 20: 1) to give 9.4 g (87 %) of the title compound as yellow resin.'H-NMR (400 MHz, CDC13), 8 (ppm): 7.67-6. 70 m (20H), 4.96-4. 70 m (1 H), 4.56-1. 85 m (11 H), 1.53-0. 40 m (12H).

B) Examples for Polymerizations General remarks: Styrene (Merck), methylmethacrylate (MMA, Merck), n-butylacrylate (Merck) and tert- butylbenzene (Aldrich) are distilled over a Vigreux column under vacuum, shortly before being used. Acrylonitrile is used as obtained from Aldrich.

To remove oxygen, the polymerization reaction mixtures are degassed in three consecutive freeze-thaw-cycles and then purged with argon or nitrogen before polymerization. The reaction mixtures are then polymerized under argon/nitrogen atmosphere. The temperatures given are bath-temperatures.

At the start of the polymerization reaction, all starting materials are homogeneously dissolved.

Unreacted monomer is removed from the polymer by heating at a pressure of torr until constant weight is achieved. Conversion is determined by weighing the remaining polymer and subtracting the weight of the initiator. The statistical copolymers (Sty/AN) are precipitated with methanol, dryed at 40°C and 1 torr until constant weight is achieved. Conversion is determined by weighing the residual The styrene/acrylonitrile copolymerization is carried out in a Buchi miniclave drive bmc dr (200 ml glass reactor vessel having following features: reverse bursting disc 10 bar; temperature and pressure control; propeller stirrer (3 arms): torque 75 Ncm; speed 250 rpm (max. ); temperature 250°C (max. ); pressure rating 100 bar (max. ) ; material of closing cap 1.4435 Hastelloy C22; material of bearings PFTE/graphite; stirrer shaft 8 mm.

Characterization of the polymers is carried out by GPC (Gel Permeation Chromatography).

GPC: Is performed using RHEOS 4000 of FLUX INSTRUMENTS. Tetrahydrofuran (THF) is used as a solvent and is pumped at 1 ml/min. Two chromatography columns are put in series: type Plgel 5pm mixed-C of POLYMER INSTRUMENTS, Shropshire, UK. Or by a Hewlett Packart HP 1090 LC (column PSS 1, length 60cm. Elution is done with tetrahydrofurane (THF), rate 1 mUmin, concentration 10 mg polymer in 1 mi THF, Measurements are performed at 40 °C. The columns are calibrated with low polydispersity polystyrenes having Mn from 200 to 2 000 000 Dalton. Detection is carried out using a Rl- and UV-detection. The polydispersity is calculated from Mn (g/mol) and Mw (g/mol) as PD = M ; Mn Polymerization of Styrene: Example B1 : Polymerization with 1 mol% of compound 204 at 100 °C In a 100 ml Schlenck-flask with stopper and magnetic stirrer, are placed 1.47 g (4.35 mmol) of compound 204 and 45.3 g (435 mmol) of styrene and degassed. The clear solution is then stirred at 100 °C for 6 h. The residual monomer is removed under high vacuum at 70 °C.

28.4g (63 %) of the monomer is converted and a slightly yellow foam is obtained.

Mn = 7930, Mw = 10590, PD = 1. 34 Example B2: Polymerization with 1 mol% of compound 205 at 100 °C In a 100 mi Schlenck-flask with stopper and magnetic stirrer, are placed 1.40 g (4.35 mmol) of compound 205 and 45.3 g (435 mmol) of styrene and degassed. The clear solution is then stirred at 100 °C for 6 h. The residual monomer is removed under high vacuum at 70 °C.

21.7g (48 %) of the monomer is converted and a slightly yellow foam is obtained.

Mn=5130, Mw=6180, PD=1. 20 Example B3: Polymerization with 0.1 mol% of compound 205 at 100 °C In a 100 ml Schlenck-flask with stopper and magnetic stirrer, are placed 0.14 g (0.44 mmol) of compound 205 and 45.3 g (435 mmol) of styrene and degassed. The clear solution is then stirred at 100 °C for 6 h. The residual monomer is removed under high vacuum at 70 °C.

12.6g (28 %) of the monomer is converted and a slightly yellow foam is obtained.

Mn = 27350, Mw = 34750, PD = 1. 27 Example B4: Polymerization with 1 mol% of compound 207 at 100 °C In a 100 ml Schlenck-flask with stopper and magnetic stirrer, are placed 1.49 g (4.35 mmol) of compound 207 and 45.3 g (435 mmol) of styrene and degassed. The clear solution is then stirred at 100 °C for 6 h. The residual monomer is removed under high vacuum at 70 °C.

30. 7g (68 %) of the monomer is converted and a slightly yellow foam is obtained.

Mn = 7520, Mw = 9300, PD = 1.24 Example B5: Polymerization with 1 mol% of compound 208 at 100 °C In a 100 ml Schlenck-flask with stopper and magnetic stirrer, are placed 1.56 g (4.35 mmol) of compound 208 and 45.3 g (435 mmol) of styrene and degassed. The clear solution is then stirred at 100 °C for 3 h. The residual monomer is removed under high vacuum at 70 °C.

44.6g (95 %) of the monomer is converted and a slightly yellow foam is obtained.

Mn = 10000, Mw = 16400, PD = 1.63 Example B6: Polymerization with 0.1 mol% of compound 208 at 100 °C In a 100 ml Schlenck-flask with stopper and magnetic stirrer, are placed 0.156 g (0.435 mmol) of compound 208 and 45.3 g (435 mmol) of styrene and degassed. The clear solution is then stirred at 100 °C for 6 h. The residual monomer is removed under high vacuum at 70° C. 17.0 g (37 %) of the monomer is converted and a slightly yellow foam is obtained.

Mn = 46300, Mw = 74000, PD = 1.60 Example B7: Polymerization with 1 mol% of compound 209 at 100 °C In a 100 ml Schlenck-flask with stopper and magnetic stirrer, are placed 1.96 g (4.35 mmol) of compound 209 and 45.3 g (435 mmol) of styrene and degassed. The clear solution is then stirred at 100 °C for 6 h. The residual monomer is removed under high vacuum at 70 °C.

34. 9g (73 %) of the monomer is converted and a slightly yellow foam is obtained.

Mn = 9700, Mw = 12100, PD = 1. 25 Example B8: Polymerization with 1 moi% of compound 306 at 100 °C In a 100 ml Schlenck-flask with stopper and magnetic stirrer 1.89 g (4.35 mmol) of compound 306 and 45.3 g (435 mmol) of styrene are placed and degassed. The clear solution is then stirred at 100 °C for 5 h. The residual monomer is removed under high vacuum at 40 °C.

42.5g (94 %) of the monomer is converted and a slightly yellow foam is obtained.

Mn = 10000, Mw = 11600, PD = 1. 27 Example B9: Polymerization with 1 mol% of compound 307 at 75 °C In a 100 ml Schlenck-flask with stopper and magnetic stirrer, are placed 2.13 g (4.35 mmol) of compound 307 and 45.3 g (435 mmol) of styrene and degassed. The clear solution is then stirred at 75 °C for 6 h. The residual monomer is removed under high vacuum at 40 °C. 19. 3g (38 %) of the monomer is converted and a slightly yellow foam is obtained.

Mn = 3130, Mw = 5010, PD = 1. 60 Example B10: Polymerization with 1 mol% of compound 308 at 85 °C In a 100 ml Schlenck-flask with stopper and magnetic stirrer 1.95 g (4,36 mmol) of compound 308 and 45,45 g (436 mmol) of styrene are placed and degassed. The clear solution is then stirred at 85 °C for 6 h. The residual monomer is removed under high vacuum at 40 °C. 44,5 g (94 %) of the monomer is converted and a slightly yellow foam is obtained.

Mn = 12050, Mw = 14890, PD = 1. 24 Example B11 : Reinitiation of polymer B10 with MMA at 85°C In a 100 ml Schlenck-flask with stopper and magnetic stirrer 2.50 g of polymer B10 (Mn = 12050) and 15.0 g (150 mmol) of MMA are placed and degassed. The clear solution is then stirred at 85°C for 6 h. The residual monomer is removed under high vacuum at 40°C. 2.99g (19.9%) of the monomer is converted and a colorless foam is obtained.

Mn = 46590, Mw = 85150, PD = 1.8 Example B12: Polymerization with 1 mol% of compound 401 at 100 °C In a 100 ml Schlenck-flask with stopper and magnetic stirrer 2.51 g (4.35 mmol) of compound 412 and 45.3 g (435 mmol) of styrene are placed and degassed. The clear solution is then stirred at 100 °C for 6 h. The residual monomer is removed under high vacuum at 70 °C.

22.5g (50 %) of the monomer is converted and a slightly yellow foam is obtained.

Mn = 8610, Mw = 10990, PD = 1. 28 Example B13 : Polymerization with 0.1 mol% of compound 401 at 100 °C In a 100 ml Schlenck-flask with stopper and magnetic stirrer 0.25 g (0.44 mmol) of compound 412 and 45.3 g (435 mmol) of styrene are placed and degassed. The clear solution is then stirred at 100 °C for 6 h. The residual monomer is removed under high vacuum at 70 °C.

19. 3g (43 %) of the monomer is converted and a slightly yellow foam is obtained.

Mn = 42800, Mw = 56400, PD = 1.32 Example B14: Polymerization with 1 mol% of compound 408 at 100 °C In a 100 ml Schlenck-flask with stopper and magnetic stirrer 2.67 g (4.36 mmol) of compound 419 and 45.4 g (436 mmol) of styrene are placed and degassed. The clear solution is then stirred at 100 °C for 6 h. The residual monomer is removed under high vacuum at 70 °C.

24.2g (53 %) of the monomer is converted and a slightly yellow foam is obtained.

Mn = 5520, Mw = 7430, PD = 1.35 Example B15: Polymerization with 1 mol% of compound 208 at 85 °C In a 100 mi Schlenck-flask with stopper and magnetic stirrer 1.56 g (4.35 mmol) of compound 306 and 45.3 g (435 mmol) of styrene are placed and degassed. The clear solution is then stirred at 85 °C for 6 h. The residual monomer is removed under high vacuum at 40 °C. 20.4g (42 %) of the monomer is converted and a slightly yellow foam is obtained.

Mn = 4200, Mw = 5160, PD = 1. 23 Example B16: Polymerization with 1 mol% of compound 208 at 85 °C with additional initiator In a 100 ml Schlenck-flask with stopper and magnetic stirrer are placed 1.56 g (4.35 mmol) of compound 306,0. 105 g (0.435 mmol) of benzoylperoxide, and 45.3 g (435 mmol) of styrene and degassed. The clear solution is then stirred at 85 °C for 6 h. The polymer is dissolved in CH2CI2 (50 ml) and precipitated from 500 mi MeOH. The precipitation is repeated and the resulting white powder dried under high vacuum to yield 34.5 g (72 %) of polymer.

Mn = 6890, Mw = 9070, PD = 1.32 Example B17: Reinitiation of polymer B16 at 85 °C In a 100 ml Schlenck-flask with stopper and magnetic stirrer 2.50 g of polymer B16 (Mn = 6890) and 10.0 g (96 mmol) of styrene are placed and degassed. The clear solution is then stirred at 85 °C for 6 h. The residual monomer is removed under high vacuum at 40 °C. 3.09g (31 %) of the monomer is converted and a colorless foam is obtained.

Mn = 13900, Mw = 23300, PD = 1.67 Example B18 : Polymerization with 0, 25 mol% of compound 410 at 85°C In a 100 ml Schlenck-flask with stopper and magnetic stirrer 0.59 g (1.10 mmol) of compound 410 and 45.3 g (435 mmol) of styrene are placed and degassed. The clear solution is then stirred at 85°C for 6 h. The residual monomer is removed under high vacuum at 40°C. 9.20g (18.9%) of the monomer is converted and a colorless foam is obtained.

Mn = 11590, Mw = 14990, PD = 1.29 Example B19 : Reinitiation of polymer B17 with n-BuA at 85°C In a 100 ml Schlenck-flask with stopper and magnetic stirrer 2.50 g of polymer B17 (Mn = 11590) and 15.0 g (117 mmol) of n-butylacrylate (n-BuA) are placed and degassed. The clear solution is then stirred at 85°C for 6 h. The residual monomer is removed under high vacuum at 40°C. 10.1 g (67.3%) of the monomer is converted and a colorless foam is obtained.

Mn = 146600, Mw = 259600, PD = 1.8 Example B20: Polymerization with 1.0 mol% of compound 410 at 85°C In a 100 ml Schlenck-flask with stopper and magnetic stirrer 2.35 g (4.37 mmol) of compound 410 and 45.3 g (435 mmol) of styrene are placed and degassed. The clear solution is then stirred at 85°C for 6 h. The residual monomer is removed under high vacuum at 40°C.

24.57g (48.9%) of the monomer is converted and a colorless foam is obtained.

Mn = 4340, Mw = 5600, PD = 1.29 Example B21: Reinitiation of polymer B19 with MMA at 85°C In a 100 ml Schlenck-flask with stopper and magnetic stirrer 2.50 g of polymer B19 (Mn = 4340) and 15.0 g (150 mmol) of MMA, are placed and degassed. The clear solution is then stirred at 85°C for 6 h. The residual monomer is removed under high vacuum at 40°C. 5.69g (37.9%) of the monomer is converted and a colorless foam is obtained.

Mn = 14780, Mw = 30510, PD = 2. 1 Polymerization of n-butyl acrylate : Example B22: Polymerization with 1.5 mol% of compound 208 at 120 °C In a 25 mi three neck flask, equipped with thermometer, cooler and magnetic stirrer, 0.418g (1.17 mmol) of compound 208 and 10.0 g (78.0 mmol) of n-butylacrylate are mixed and degassed. The clear solution obtained is heated under argon to 120 °C and polymerization is carried out during 5 h. The remaining monomer is removed by evaporation under high vacuum at 80 °C. 8.0 g (80 %) of the initial monomer have reacted. A clear colorless viscous fluid is obtained.

Mn = 5150, Mw = 8040, PD = 1. 56 Example B23: Polymerization with 1.5 mol% of compound 208 at 100 °C In a 25 mi three neck flask, equipped with thermometer, cooler and magnetic stirrer, 0.418 g (1.17 mmol) of compound 208 and 10.0 g (78 mmol) of n-butylacrylate are mixed and degassed. The clear solution obtained is heated under argon to 100 °C and polymerization is carried out during 20 h. The remaining monomer is removed by evaporation under high vacuum at 50 °C. 9.80 g (98 %) of the initial monomer have reacted. A clear colorless viscous fluid is obtained.

Mn = 5150, Mw = 8540, PD = 1. 66 Example B24: Polymerization with 1.5 mol% of compound 209 at 100 °C In a 25 mi three neck flask, equipped with thermometer, cooler and magnetic stirrer, 0.528 g (1.17 mmol) of compound 209 and 10.0 g (78 mmol) of n-butylacrylate are mixed and degased. The clear solution obtained is heated under argon to 100 °C and polymerization is carried out during 3 h. The remaining monomer is removed by evaporation under high vacuum at 50 °C. 9.41 g (94 %) of the initial monomer have reacted. A clear colorless viscous fluid is obtained.

Mn = 7670, Mw = 14300, PD = 1.87 Example B25: Polymerization with 1.5 mol% of compound 307 at 100 °C In a 25 ml three neck flask, equipped with thermometer, cooler and magnetic stirrer, 0.573 g (1.17 mmol) of compound 307 and 10.0 g (78 mmol) of n-butylacrylate are mixed and degased. The clear solution obtained is heated under argon to 100 °C and polymerization is carried out during 3 h. The remaining monomer is removed by evaporation under high vacuum at 50 °C. 7.22 g (72 %) of the initial monomer have reacted. A clear colorless viscous fluid is obtained.

Mn = 5340, Mw = 9290, PD = 1. 74 Example B26: Reinitiation of polymer B24 at 100 °C In a 25 ml three neck flask, equipped with thermometer, cooler and magnetic stirrer, 2.50 g of poly-butylacrylate B24 and 10 g (96 mmol) of styrene are mixed and degased. The clear solution obtained is heated under argon to 100 °C and polymerization is carried out during 6 h. The remaining monomer is removed by evaporation under high vacuum at 40 °C. 4.88 g (49 %) of the initial monomer have reacted. A clear colorless viscous fluid is obtained.

Mn = 32600, Mw = 51900, PD = 1. 59 Example B27: Polvmerization with 0.25 mol% of compound 410 at 85 °C In a Schlenck-flask 0,59 g (1.1 mmol) of compound 410 and 55.9 g (436 mmol) n-BuA are dissolved in 100 ml tert-butylbenzene and degassed. The clear solution obtained is heated under argon to 85 °C and polymerization is carried out during 6 h. The remaining monomer and the solvent are removed by evaporation under vacuum at 40°C. 31.1 g (55.7%) of the initial monomer have reacted. A clear colorless vicous fluid is obtained.

Mn = 72740, Mw = 133400, PD = 1.8 Example B28: Reinitiation of polymer B27 with MMA at 85°C In a 100 ml Schlenck-flask with stopper and magnetic stirrer 2.50 g of polymer B27 (Mn = 72740) and 15.0 g (150 mmol) of MMA are placed and degassed. The clear solution is then stirred at 85°C for 6 h. The residual monomer is removed under vacuum at 40°C. 11.6 g (77.0%) of the monomer is converted and a colorless solid is obtained.

Mn = 125300, Mw = 207000, PD = 1.7 Statistical copolymers with styrene (sty)/acrylonitrile (AN) Example B29: Polymerization of Sty/AN (3: 1) with 0.25% mol% of compound 410 In the autoclave, equipped with a thermometer and a magnetic stirrer, 75 g (720 mmol) styrene and 25 g (471 mmol) acrylonitrile are mixed and stirred with 500 U/min. After addition of 1.6 g (3.0 mmol) of compound 410 the homogenious solution is cooled in an ice bath and degassed with argon for 30 min. The solution is then heated to 85°C and polymerization is carried out during 6 h. After cooling down to room temperature the statistical polymer is precipitated in methanol and dried in a vacuum oven at 40°C. The polymer is obtained with 42.2 % conversion as a white solid.

Mn = 21630, Mw = 28620, PD = 1.3 Example B30: Polymerization of sty/AN (1: 1) with 0.25% mol% of compound 410 In the autoclave, equipped with a thermometer and a magnetic stirrer, 50 g (480 mmol) styrene and 50 g (942 mmol) acrylonitrile are mixed and stirred with 500 U/min. After addition of 1.9 g (3.5 mmol) of compound 410 the homogenious solution is cooled in an ice bath and degassed with argon for 30 min. The solution is then heated to 85°C and polymerization is carried out during 6 h. After cooling down to room temperature the statistical polymer is precipitated in methanol and dried in a vacuum oven at 40°C. The polymer is obtained with 31.1 % conversion as a white solid.

Mn = 15730 Mw = 21920, PD = 1.4 Example B31: Polymerization of sty/AN (1: 3) with 0.25% mol% of compound 410 In the autoclave, equipped with a thermometer and a magnetic stirrer, 25 g (240 mmol) styrene and 75 g (1414 mmol) acrylonitrile are mixed and stirred with 500 U/min. After addition of 2.2 g (4.1 mmol) of compound 410 the homogenious solution is cooled in an ice bath and degassed with argon for 30 min. The solution is then heated to 85°C and polymerization is carried out during 6 h. After cooling down to room temperature the statistical polymer is precipitated in methanol and dried in a vacuum oven at 40°C. The polymer is obtained with 17.1 % conversion as a white solid.

Mn = 8730, Mw = 11930, PD = 1.4 Example B32: Reinitiation of polymer B29 with styrene at 85°C In a 100 ml Schlenck-flask with stopper and magnetic stirrer 1.25 g of statistical polymer B29 (Mn = 21630) and 7.5 g (72 mmol) of styrene are placed and degassed. The clear solution is then stirred at 85°C for 6 h. The residual monomer is removed under high vacuum at 70°C.

1.11 g (14.8%) of the monomer is converted and a colorless solid is obtained.

Mn = 31120, Mw = 43680, PD = 1.4 Example B33: Reinitiation of polymer B30 with n-BuA at 85°C In a 100 ml Schlenck-flask with stopper and magnetic stirrer 1.25 g of statistical polymer B30 (Mn = 15730) and 7.5 g (58.5 mmol) of n-BuA are placed and degassed. The clear solution is then stirred at 85°C for 6 h. The residual monomer is removed under high vacuum at 40°C.

6.88 g (91.8%) of the monomer is converted and a colorless solid is obtained.

Mn = 207700, Mw = 441100, PD = 2.1 Example B34 : Reinitiation of polymer B31 with MMA at 85°C In a 100 ml Schlenck-flask with stopper and magnetic stirrer 0.51 g of statistical polymer B31 (Mn = 8730) and 3.0 g (30 mmol) of MMA are placed and degassed. The clear solution is then stirred at 85°C for 6 h. The residual monomer is removed under high vacuum at 40°C.

1.93 g (64.3%) of the monomer is converted and a colorless solid is obtained.

Mn = 67350, Mw = 91580, PD = 1.4