OPEN METAL ORGANIC FRAMEWORKS WITH EXCEPTIONAL SURFACE AREA AND HIGH GAS STORAGE CAPACITY

CROSS REFERENCE TO RELATED APPLICATIONS

[ 0001 ] This application claims priority under 35 U.S.C. § 119 from Provisional Application Serial No. 61/246,065, filed September 25, 2009, the disclosure of which is incorporated herein by reference.

TECHNICAL FIELD

[ 0002 ] The disclosure provides organic frameworks for gas separation and storage.

BACKGROUND

[ 0003 ] One of the challenges in the field of porous materials is to implement high storage capacity. Such materials are quite important because of the environmental concern in the earth. From the discovery of metal-organic frameworks (MOFs), researchers have sought and developed frameworks with reported high surface area materials whose apparent surface areas approach 6000 square meter per gram.

SUMMARY

[ 0004 ] The disclosure provides a metal-organic framework (MOF) comprising a plurality of metal clusters, each metal cluster comprising one or more metal ions; and a plurality of at least one first multidentate aromatic tritopic linking ligand that connects adjacent metal clusters, the plurality of multidentate linking ligands having a sufficient number of accessible sites for atomic or molecular adsorption such that the surface area of the metal-organic framework is greater than about 5500 m ² /g. In one embodiment, the metal-organic framework further comprises at least one second linking ligand different than the first linking ligand. In yet another embodiment, the metal cluster comprises 3 or more metal ions. In one embodiment, the plurality of multidentate linking ligands have a sufficient number of accessible sites for atomic or molecular adsorption that the surface area is greater than 6,000 m ² /g. In another embodiment, the plurality of multidentate linking ligands have a sufficient number of accessible sites for atomic or molecular adsorption that the surface area is greater than about 6,500 m ² /g. In one embodiment, the plurality of multidentate linking ligands have a sufficient number of accessible sites for atomic or molecular adsorption that the surface area is greater than about 10,000 m ² /g. In yet another embodiment, each ligand of the plurality of multidentate ligand includes 2 or more carboxylates. In one embodiment, the metal ion is selected from the group consisting of Li ⁺ , Na ⁺ , Rb ⁺ , Mg ²⁺ , Ca ²⁺ , Sr ²⁺ , Ba ²⁺ , Sc ³⁺ , Ti ⁴⁺ , Zr ⁴⁺ , Ta ³⁺ , Cr ³⁺ , Mo ³⁺ , W ³⁺ , Mn ³⁺ , Fe ³⁺ , Fe ²⁺ , Ru ³⁺ , Ru ²⁺ , Os ³⁺ , Os ²⁺ , Co ³⁺ , Co ²⁺ , Ni ²⁺ , Ni ⁺ , Pd ²⁺ , Pd ⁺ , Pt ²⁺ , Pt ⁺ , Cu ²⁺ , Cu ⁺ , Au ⁺ , Zn ²⁺ , Al ³⁺ , Ga ³⁺ , In ³⁺ , Si ⁴⁺ , Si ²⁺ , Ge ⁴⁺ , Ge ²⁺ , Sn ⁴⁺ , Sn ²⁺ , Bi ⁵⁺ , Bi ³⁺ , Cd ²⁺ , Mn ²⁺ , Tb ³⁺ , Gd ³⁺ , Ce ³⁺ , La ³⁺ , Cr ⁴⁺ and combinations thereof. In yet another embodiment, the first linking ligand comprises the structure of formula I:

Formula I

wherein R1-R15 are each individually selected from: alkyl, aryl, alkoxy, akenes, alkynes, phenyl, substitutions of the foregoing, sulfur-containing groups (e.g., thioalkoxy), silicon- containing groups, nitrogen-containing groups (e.g., amides), oxygen-containing groups (e.g., ketones, and aldehydes), halogen, nitro, amino , cyano, boron-containing groups, phosphorous-containing groups, carboxylic acids, or esters, H, NH ₂ , CN, OH, =0, =S, CI, I, F,

wherein X=l, 2, or 3; wherein R16, R17 and R18 may or may not be present, if present

R16, R17 and R18 are selected from an alkyl or cycloalkyl group, comprising 1 to 20 carbon atoms, an aryl group comprising 1 to 5 phenyl rings, an alkyl or aryl amine comprising alkyl or cycloalkyl groups having from 1 to 20 carbon atoms or aryl groups comprising 1 to 5 phenyl rings, or -C≡C-. In certain embodiments, the R group is imine functionalized to promote chelating of a post-synthesis metal. In yet another embodiment, the first linking ligand comprises the structure of Formula II:

Formula II

wherein R1-R15 are each individually selected from: alkyl, aryl, alkoxy, akenes, alkynes, phenyl, substitutions of the foregoing, sulfur-containing groups (e.g., thioalkoxy), silicon- containing groups, nitrogen-containing groups (e.g., amides), oxygen-containing groups (e.g., ketones, and aldehydes), halogen, nitro, amino , cyano, boron-containing groups, phosphorous-containing groups, carboxylic acids, or esters, H, NH ₂ , CN, OH, =0, =S, CI, I, F,

wherein X=l, 2, or 3. In one embodiment, the first linking ligand comprises the structure of Formula III:

Formula III

4,4',4"-(benzene-1,3,5-triyl-tris(ethyne-2, l-diyl))tribenzoate (BTE) In another embodiment, the first linking ligand comprises the structure of Formula IV:

Formula IV

wherein R1-R15 are each individually selected from: alkyl, aryl, alkoxy, akenes, alkynes, phenyl, substitutions of the foregoing, sulfur-containing groups (e.g., thioalkoxy), silicon- containing groups, nitrogen-containing groups (e.g., amides), oxygen-containing groups (e.g., ketones, and aldehydes), halogen, nitro, amino , cyano, boron-containing groups, phosphorous-containing groups, carboxylic acids, or esters, H, NH ₂ , CN, OH, =0, =S, CI, I, F,

wherein X=l, 2, or 3. In yet another embodiment, the first linking ligand comprises the structure of Formula V:

Formula V

4,4',4"-(benzene-l,3,5-triyl-tris(benzene-4,l-diyl))tribenzo ate (BBC) In other embodiments, comprising a second linking ligand, second linking ligand comprises a structure of Formula VI or VII:

Formula VI Formula VII wherein R1-R8 are each individually selected from: alkyl, aryl, alkoxy, akenes, alkynes, phenyl, substitutions of the foregoing, sulfur-containing groups (e.g., thioalkoxy), silicon- containing groups, nitrogen-containing groups (e.g., amides), oxygen-containing groups (e.g., ketones, and aldehydes), halogen, nitro, amino , cyano, boron-containing groups, phosphorous-containing groups, carboxylic acids, or esters, H, NH ₂ , CN, OH, =0, =S, CI, I, F,

wherein X=l, 2, or 3. In further embodiments, the second linking ligand comprises the structure of Formula VIII and IX:

Formula VIII Formula IX

(2-6-naphthalenedicarboxylate) biphenyl-4,4' di-

( DC) carboxylate (BPCD)

In some embodiments, wherein the first linking ligand comprises the structure of Formula I lacking R16, R17 and R18 the second linking ligand comprises a structure of Formula VI, VII, VIII or IX.

[ 0005 ] The disclosure also provides a method of forming a metal-organic framework (MOF), the method comprising: combining a solution comprising a solvent and metal ions selected from the group consisting Group 1 through 16 metals including actinides, and lanthanides, and combinations thereof with at least a first multidentate linking ligand comprising the general formula of I-V such that the surface area of the metal-organic framework is greater than 5500 m ² /g.

[ 0006] The disclosure also provides methods of gas storage and separation comprising contacting a MOF of the disclosure with a fluid wherein an analyte in the fluid interacts and is absorbed into the MOF.

[ 0007 ] The details of one or more embodiments of the invention are set forth in the accompanying drawings and the description below. Other features, objects, and advantages of the invention will be apparent from the description and drawings, and from the claims.

DESCRIPTION OF DRAWINGS

[ 0008 ] Figure 1A-H shows connectivity of pyr and qom (6,3)-coordinated nets. For pyr (A), pairs of pyr nets can naturally interpenetrate (B). In contrast, qom is not self-dual (C to E); the connectivity of the net of the dual tiling for qom (D) is very different from the original (C). Crystal structures of MOF- 177 (F), MOF- 180 (G), and MOF-200 (H) are found in qom net (C). The ball is placed in the structure for clarity and to indicate space in the cage. Zn, tetrahedral; O; and C atoms are depicted. Hydrogen atoms are omitted for clarity.

[ 0009 ] Figure 2A-D shows crystal structures of MOF-205 (A) and MOF-210 (B). The balls are placed in the structure for clarity and to indicate space in the cage. Atom are the same as in Fig. 1. Tiling of (C) ith-d and (D) toz nets.

[ 0010 ] Figure 3A-D shows gas uptake results. (A) Low-pressure 2 isotherms of MOF-5, -177, -200, -205, and -210 at 77 K. Simulated isotherms of MOF-200 and -210 were overlaid. P/Po, relative pressure. High-pressure H ₂ isotherms were measured at 77 K (B), and (C) CH ₄ and (D) CO2 isotherms were measured at 298 K of the same MOFs.

[ 0011 ] Figure 4A-B are selected electron density maps calculated by WinGX FOURIER MAP with F ₀ coefficients. Sections at (A) z = 0.25 are displayed by WinGX CONTOUR with a contouring level of 0.15 e A ³ . Black contours are for positive, and blue for negative contours. A model structure is also displayed with a unit cell content of z = 0 ~ 0.25 in (B).

[ 0012 ] Figure 5 shows a fragment structure of MOF- 180 displayed by ORTEP. Selected atoms in the asymmetric unit are labeled. A benzene ring (C27 ~ C32) is disordered over two sites at general positions while a ZruO unit is disordered at a special position, d. According to these disorders, the carboxylate oxygen atoms, 05 and 06 are also disordered over two sites. Thermal ellipsoids for Zn atoms are displayed with 20% probability. Hydrogen atoms are not shown for simplicity.

[ 0013 ] Figure 6 is an ORTEP drawing (20% probability) of a fragment in MOF-200 is displayed with selected atomic labels. Two BBC and two Zn ₄ 0 moieties lie at Wyckoff positions, a, c, d, and h. A Zn ₄ 0 moiety at h has two μ-Η ₂ 08 and two dangling H20 which are displayed as pink ellipsoids. The other ZruO moiety at d is disordered over two sites, which gives two sets of half-occupied Zn atoms denoted with blue and green ellipsoids, respectively.

[ 0014 ] Figure 7 is an ORTEP drawing (50% probability) of a fragment in MOF-205 is displayed with selected atomic labels. The labeled atoms constitute an asymmetric unit. A tripodal ligand, BTB sits on a special position having site symmetry of 32 (Wyckoff position, e at the center of BTB). The central oxo anion, 01 is also located at a special position (Wyckoff d position, 4 ml site symmetry). The linear linker, NDC is disordered over two sites due to the crystallographic site symmetry, mm2 (Wyckoff position, h .

Hydrogen atoms are omitted for simplicity. Six points of extension for the inorganic SBU are composed of two NDC carboxylate C atoms (C8 and C8') and the others belonging to four BTB linkers.

[ 0015 ] Figure 8A-F are selected electron density maps calculated by WinGX FOURIER MAP with F ₀ coefficients. Sections at (a) y = 0.011, and (c) z = 0.137 are displayed by WinGX CONTOUR with a contouring level of 0.40 e A ³ . Black contours are for positive, and blue for negative contours. Structural models at (b) y = 0. ~ 0.03 and (d) z = 0.12 ~ 0.14 are also displayed for comparison with the electron density map. A three- dimensional electron density map in (e) and its corresponding structure in (f) show also BPDC linkers are participating in building MOF-210 framework; the packing range is 0.22 ~ 1.00 for x, -0.02 ~ 0.80 for y, and 0.05 ~ 0.22 for z. The electron density map was drawn by MCE2005.

[ 0016] Figure 9 is an ORTEP drawing of the asymmetric unit for MOF-210.

Thermal ellipsoids are displayed with 20% probability.

[ 0017 ] Figure 10 is a comparison of the experimental PXRD patterns of MOF-180: (Top) MOF-180 as-prepared and simulated pattern (bottom) from a modeling structure.

[ 0018 ] Figure 11 is a comparison of the experimental PXRD patterns of MOF-200: as-prepared (middle line), evacuated after activated (top line), and simulated pattern (bottom line) from single-crystal X-ray data.

[ 0019 ] Figure 12 is a comparison of the XRD patterns of MOF-205; as-prepared (middle line), activated (top line) and simulated (bottom line) from single-crystal X-ray data.

[ 0020 ] Figure 13 is a comparison of the XRD patterns of MOF-210; as-prepared (middle line), activated (top line) and simulated (bottom line) from single-crystal X-ray data.

[ 0021 ] Figure 14 is a ^-NMR spectrum for as-prepared MOF-180 after digesting in DCl/DMSO-i/6 solution. The integration value of 26.8 at peaks 1 to 3 is attributed to 15 aromatic protons of H ₃ BTE. Comparing to the integration of BTE, 7.4 DMF (peaks 4 to 6, 51.7 H) and 7.8 NMP (peaks 7 to 10, 70.1 H) were also observed. From the molar ratio, the empirical formula has been estimated to be Zn40(BTE)2-(DMF)i4 _. s(NMP)i5.6. [ 0022 ] Figure 15 is a ^-NMR spectrum for as-prepared MOF-200 after digesting in DCl/DMSO-ί/ή solution. The integration value of 26.8 at peaks 1 to 3 is attributed to 27 aromatic protons of H3BBC. Comparing to the integration of BBC, 14.7 DEF (peaks 4 to 6, 160.6 H) and 16.6 NMP (peaks 7 to 10, 148.8 H) were also observed. From the molar ratio, the empirical formula has been estimated to be Zn ₄ 0(BBC) ₂ (H ₂ 0)3-(DEF)29. ₄ (NMP)33. ₂ .

[ 0023 ] Figure 16 is a ^-NMR spectrum for as-prepared MOF-205 after digesting in DCl/DMSO-ί/ή solution. The integration value of 25.8 at peaks 1 to 4 is attributed to 26 aromatic protons, which corresponds to 20 and 6 H of 4/3 H3BTB and 1 H2NDC, respectively. Comparing to the integration of BTB/NDC, 26.4 DMF (peaks 5 to 7, 183.3 H) and 1.7 EtOH (8.69 H) were also observed. From the molar ratio, the empirical formula has been estimated to be Zn40(BTB) ₄ /3(NDC)-(DMF)26.4(EtOH) ₁ .7.

[ 0024 ] Figure 17 is a ^-NMR spectrum for guest- free MOF-205 after digesting in DCl/DMSO-<¾ solution. From the integration of peaks 1 and 3 (3.906 H), integration for H ₃ BTB (peak 4, aromatic proton only) is estimated to be 19.98 when the integration of peak 2 is 2 H. Based on the ratio of the integration of the peaks (19.98:5.906 = 4/3 BTB:NDC), the empirical formula has been estimated to be Zn ₄ 0(BTB) ₄ /3(NDC).

[ 0025 ] Figure 18 is a ^-NMR spectrum for as-prepared MOF-210 after digesting in DCl/DMSO-ί/ή solution. The integration value 28.3 at peaks 1 to 5 is attributed to 28 aromatic protons, which corresponds to 20 and 8 H of 4/3 H3BTE and 1 H ₂ BPDC, respectively. Comparing to the integration of BTE/NDC, 25.7 DMF (peaks 6 to 8, 180 H) and 24.6 NMP (peaks 9 to 11, 221 H) were also observed. From the molar ratio, the empirical formula has been estimated to be Zn ₄ 0(BTE) ₄ /3(BPDC)-(DMF)25.7 (NMP) ₂₄ .6- [ 0026] Figure 19 is a ^-NMR spectrum for guest-free MOF-210 after digesting in DCl/DMSO-<¾ solution. Based on the ratio of the integration of the peaks (20.1 :8.2 = 4/3

BTE:BPDC), the empirical formula has been estimated to be Zn ₄ 0(BTE) ₄ /3(BPDC).

[ 0027 ] Figure 20 is a TGA trace for as-prepared MOF-180.

[ 0028 ] Figure 21 is a TGA trace for as-prepared MOF-200.

[ 0029 ] Figure 22 is a TGA trace for as-prepared MOF-205.

[ 0030 ] Figure 23 is a TGA trace for as-prepared MOF-210.

[ 0031 ] Figure 24 shows a cluster used for deriving partial charges on MOF-200 atoms. [ 0032 ] Figure 25 shows a cluster used for deriving partial charges on MOF-210 atoms.

[ 0033 ] Figure 26 shows simulated 2 isotherm for MOF-200 (+). Experimental data were overlaid (circles).

[ 0034 ] Figure 27 shows simulated 2 isotherm for MOF-210 (+). Experimental data were overlaid (circles).

[ 0035 ] Figure 28 shows V(P ₀ - P) vs. P/P ₀ for simulated MOF-200 isotherm (top). Only the range below P/Po = 0.14 satisfies the first consistency criterion for applying the BET theory. (Bottom) Plot of the linear region for the BET equation.

[ 0036] Figure 29 shows V(P ₀ - P) vs. P/P ₀ for simulated MOF-210 isotherm (top). Only the range below P/Po = 0.27 satisfies the first consistency criterion for applying the BET theory. (Bottom) Plot of the linear region for the BET equation.

[ 0037 ] Figure 30 shows V(P ₀ - P) vs. P/P ₀ for MOF-200 (top). Only the range below P/Po = 0.14 satisfies the first consistency criterion for applying the BET theory. (Bottom) Plot of the linear region for the BET equation.

[ 0038 ] Figure 31 shows V(P ₀ - P) vs. P/P ₀ for MOF-205. Only the range below P/P ₀ = 0.09 satisfies the first consistency criterion for applying the BET theory. (Bottom) Plot of the linear region for the BET equation.

[ 0039 ] Figure 32 shows V(P ₀ - P) vs. P/P ₀ for MOF-210 (top). Only the range below P/Po = 0.27 satisfies the first consistency criterion for applying the BET theory. (Bottom) Plot of the linear region for the BET equation.

[ 0040 ] Figure 33 is a 2 isotherms of independently prepared MOF-200.

[ 0041 ] Figure 34 is a high-pressure H ₂ isotherms plot for MOF-200 measured at 77 K. Lines represent surface excess and total uptakes, and filled and open symbols represent adsorption and desorption branches.

[ 0042 ] Figure 35 shows a high-pressure H ₂ isotherms plot for MOF-205 measured at 77 K. All symbols are the same as in Fig. 34.

[ 0043 ] Figure 36 shows a high-pressure H ₂ isotherms plot for MOF-210 measured at 77 K. All symbols are the same as in Fig. 34.

[ 0044 ] Figure 37 shows a high-pressure CH ₄ isotherms for MOF-200 measured at 298 K. All symbols are the same as in Fig. 34. [ 0045 ] Figure 38 shows a high-pressure CH ₄ isotherms plot for MOF-205 measured at 298 K. All symbols are the same as in Fig. 34.

[ 0046] Figure 39 shows a high-pressure CH ₄ isotherms plot for MOF-210 measured at 298 K. All symbols are the same as in Fig. 34.

[ 0047 ] Figure 40 shows a high-pressure CO ₂ isotherms plot for MOF-200 measured at 298 K. All symbols are the same as in Fig. 34.

[ 0048 ] Figure 41 shows a high-pressure CO ₂ isotherms plot for MOF-205 measured at 298 K. All symbols are the same as in Fig. 34.

[ 0049 ] Figure 42 shows a high-pressure CO ₂ isotherms for MOF-210 measured at 298 K. All symbols are the same as in Fig. 34.

DETAILED DESCRIPTION

[ 0050 ] As used herein and in the appended claims, the singular forms "a," "and," and "the" include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to "a framework" includes a plurality of such frameworks and reference to "the metal" includes reference to one or more metals and equivalents thereof known to those skilled in the art, and so forth.

[ 0051 ] Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood to one of ordinary skill in the art to which this disclosure belongs. Although any methods and reagents similar or equivalent to those described herein can be used in the practice of the disclosed methods and compositions, the exemplary methods and materials are now described.

[ 0052 ] Also, the use of "or" means "and/or" unless stated otherwise. Similarly, "comprise," "comprises," "comprising" "include," "includes," and "including" are interchangeable and not intended to be limiting.

[ 0053 ] It is to be further understood that where descriptions of various embodiments use the term "comprising," those skilled in the art would understand that in some specific instances, an embodiment can be alternatively described using language "consisting essentially of or "consisting of."

[ 0054 ] All publications mentioned herein are incorporated herein by reference in full for the purpose of describing and disclosing the methodologies, which are described in the publications, which might be used in connection with the description herein. The publications discussed above and throughout the text are provided solely for their disclosure prior to the filing date of the present application. Nothing herein is to be construed as an admission that the inventors are not entitled to antedate such disclosure by virtue of prior disclosure.

[ 0055 ] Recently metal-organic frameworks (MOFs) have merged as an important class of porous materials for their well-characterized structures in terms of atomic connectivity and chemical composition. First example of the rigid framework is MOF-2 (Zn(BDC), BDC = 1 ,4-benzenedicarboxylate) having square channels. The isotherm shape, typical Type I without hysteresis, demonstrates the existence of microporous structures even after removal of guest species. Within a decade from this discovery, researchers have been exploring high surface area MOFs, whose apparent surface areas exceed 5000 m ² g ^-1 . The apparent surface area of MOFs can be estimated by use of the free volume ( f _ree ) and density of MOFs ( MOF). Since the pore volume of MOF per gram is described as f _ree [%] / 100 CIMOF [g cm ^-3 ], weight of 2 adsorbed in the pore should be calculated, assuming that adsorbed 2 behaves as a liquid in the micropore and its density (fi?LN ₂ ) is 0.806 g cm ^-3 . Assuming that a cross sectional area of 2 molecule is 16.2 A ² , Langmuir surface area for 1 mole of 2 is theoretically 97524 m ² . By combining two relationships, one can obtain followin simple equation. where MW is molecular weight of N ₂ . This equation implies that one can deliver highly porous MOFs whose apparent surface areas reach 10000 m ² g ^-1 , if V&ee and duo _? are 90% and 0.25 g cm ^-3 , respectively. Although it appears that the apparent surface area may not be equal to a real accessible surface based on simulation calculations, the pursuit of highly porous crystalline materials is still one of the biggest challenges in the field of material science.

[ 0056] The disclosure provides two strategies and resulting compositions that have allowed the realization of crystalline materials with high storage space; (i) isoreticular expansion of the framework and (ii) insertion of secondary organic link for the framework reinforcement. The disclosure demonstrates the methodology and provides, as examples, three MOFs whose porosity is maintained even after complete guest removal. The maximum nitrogen uptake capacities at 77 Kelvin in these exemplary frameworks, named

MOF-200, 205 and 210, are 2340, 1410 and 2330 cubic centimeter per gram, respectively. These apparent surface areas of 10400, 6170, and 10400 square meter per gram can be derived from a cross sectional area of nitrogen (16.2 square angstrom per molecule), which have never been observed in crystalline materials yet.

[0057] The disclosure provides a composition comprising a metal linked to one or more other metals by a linking substructure. The metals are linked to the linking substructure by a linking cluster, typically be a condensation reaction. As depicted herein, most linking clusters are depicted as a carboxylate group at ends of the linking substructure. One of skill in the art will recognize that upon condensation with a metal, the linking cluster will form a bond between the linking substructure and the metal through, for example, an oxygen atom. Other linking clusters will be readily apparent and are described herein.

[0058] The linking substructure used in the methods and compositions of the disclosure comprise compounds that increase the distance between metal atoms while limiting fragility and maintaining stability. By increasing the distance between metals the pores size of a particular MOF is increased. In some embodiments, heterogeneous linking substructures are used.

[0059] As used herein, a "core" refers to a repeating unit or units found in a framework. Such a framework can comprise a homogenous repeating core or a

heterogeneous repeating core structure. A core comprises a transition metal or cluster of transitions metals and a linking substructure. A plurality of cores linked together defines a framework.

[0060] The term "cluster" refers to identifiable associations of 2 or more atoms. Such associations are typically established by some type of bond— ionic, covalent, van der Waals, and the like.

[0061] A "linking cluster" refers to a one or more reactive species capable of condensation comprising an atom capable of forming a bond between a linking moiety substructure and a metal group or between a linking moiety and another linking moiety. Examples of such species are selected from the group consisting of a boron, oxygen, carbon, nitrogen, and phosphorous atom. In some embodiments, the linking cluster may comprise one or more different reactive species capable of forming a link with a bridging oxygen atom. For example, a linking cluster can comprise CO ₂ H, CS ₂ H, NO ₂ , SO ₃ H, Si(OH) ₃ , Ge(OH) ₃ , Sn(OH) ₃ , Si(SH) ₄ , Ge(SH) ₄ , Sn(SH) ₄ , P0 ₃ H, As0 ₃ H, As0 ₄ H, P(SH) ₃ , As(SH) ₃ , CH(RSH) ₂ , C(RSH) ₃ , CH(RNH ₂ ) ₂ , C(R H ₂ ) ₃ , CH(ROH) ₂ , C(ROH) ₃ , CH(RCN) ₂ , C(RCN) ₃ , CH(SH) ₂ , C(SH) ₃ , CH(NH ₂ ) ₂ , C(NH ₂ ) ₃ , CH(OH) ₂ , C(OH) ₃ , CH(CN) ₂ , and C(CN) ₃ , wherein R is an alkyl group having from 1 to 5 carbon atoms, or an aryl group comprising 1 to 2 phenyl rings and CH(SH) ₂ , C(SH) ₃ , CH(NH ₂ ) ₂ , C( H ₂ ) ₃ , CH(OH) ₂ , C(OH) ₃ , CH(CN) ₂ , and C(CN) ₃ . Typically ligands for MOFs contain carboxylic acid functional groups.

[ 0062 ] A "linking moiety" refers to a mono-dentate or polydentate compound that bind a transition metal or a plurality of transition metals, respectively. Generally a linking moiety comprises a substructure of an alkyl or cycloalkyl group, comprising 1 to 20 carbon atoms, an aryl group comprising 1 to 5 phenyl rings, or an alkyl or aryl amine comprising alkyl or cycloalkyl groups having from 1 to 20 carbon atoms or aryl groups comprising 1 to 5 phenyl rings, and in which linking cluster(s) are covalently bound to the substructure. A cycloalkyl or aryl substructure may comprise 1 to 5 rings that comprise either of all carbon or a mixture of carbon with nitrogen, oxygen, sulfur, boron, phosphorus, silicon and/or aluminum atoms making up the ring. Typically the linking moiety will comprise a substructure having one or more carboxylic acid linking clusters covalently attached.

[ 0063 ] As used herein, a line in a chemical formula with an atom on one end and nothing on the other end means that the formula refers to a chemical fragment that is bonded to another entity on the end without an atom attached. Sometimes for emphasis, a wavy line will intersect the line.

[ 0064 ] In one embodiment, a linking moiety substructure for use in the

compositions and methods of the disclosure comprises:

Formula I wherein R1-R15 are each individually selected from: alkyl, aryl, alkoxy, akenes, alkynes, phenyl, substitutions of the foregoing, sulfur-containing groups (e.g., thioalkoxy), silicon- containing groups, nitrogen-containing groups (e.g., amides), oxygen-containing groups (e.g., ketones, and aldehydes), halogen, nitro, amino , cyano, boron-containing groups, phosphorous-containing groups, carboxylic acids, or esters, H, NH ₂ , CN, OH, =0, =S, CI, I, F,

wherein X=l, 2, or 3; wherein R16, R17 and R18 may or may not be present, if present R16, R17 and R18 are selected from an alkyl or cycloalkyl group, comprising 1 to 20 carbon atoms, an aryl group comprising 1 to 5 phenyl rings, an alkyl or aryl amine comprising alkyl or cycloalkyl groups having from 1 to 20 carbon atoms or aryl groups comprising 1 to 5 phenyl rings, or -C=C-. In certain embodiments, the R group is imine functionalized to promote chelating of a post-synthesis metal.

[ 0065 ] In one embodiment, the linking moiety has the general structure of Formula II:

Formula II

wherein R1-R15 are each individually selected from: alkyl, aryl, alkoxy, akenes, alkynes, phenyl, substitutions of the foregoing, sulfur-containing groups (e.g., thioalkoxy), silicon- containing groups, nitrogen-containing groups (e.g., amides), oxygen-containing groups (e.g., ketones, and aldehydes), halogen, nitro, amino , cyano, boron-containing groups, phosphorous-containing groups, carboxylic acids, or esters, H, NH ₂ , CN, OH, =0, =S, CI, I, F,

O—

wherein X=l, 2, or 3.

[ 0066] In another embodiment, the linking moiety has the general structure of Formula III:

Formula III

(benzene-1, 3, 5-triyl-tris (ethyne-2, 1

diyl) ) tribenzoate (BTE) In another embodiment, the linking moiety has the general structure of

Formula IV

wherein R1-R15 are each individually selected from: alkyl, aryl, alkoxy, akenes, alkynes, phenyl, substitutions of the foregoing, sulfur-containing groups (e.g., thioalkoxy), silicon- containing groups, nitrogen-containing groups (e.g., amides), oxygen-containing groups (e.g., ketones, and aldehydes), halogen, nitro, amino , cyano, boron-containing groups, phosphorous-containing groups, carboxylic acids, or esters, H, NH ₂ , CN, OH, =0, =S, CI, I, F,

wherein X=l, 2, or 3.

[ 0068 ] In another embodiment, the linking moiety has the general structure of Formula V:

Formula V

4,4', 4"- (benzene-1, 3, 5-triyl-tris (benzene-4, 1- diyl) ) tribenzoate (BBC)

[ 0069 ] In each of the foregoing the carboxylic acid linking cluster can under condensation with a metal to for a framework. Metal ions that can be used in the synthesis of frameworks of the disclosure include Li ⁺ , Na ⁺ , Rb ⁺ , Mg ²⁺ , Ca ²⁺ , Sr ²⁺ , Ba ²⁺ , Sc ³⁺ , Ti ⁴⁺ , Zr ⁴⁺ , Ta ³⁺ , Cr ³⁺ , Mo ³⁺ , W ³⁺ , Mn ³⁺ , Fe ³⁺ , Fe ²⁺ , Ru ³⁺ , Ru ²⁺ , Os ³⁺ , Os ²⁺ , Co ³⁺ , Co ²⁺ , Ni ²⁺ , Ni ⁺ , Pd ²⁺ , Pd ⁺ , Pt ²⁺ , Pt ⁺ , Cu ²⁺ , Cu ⁺ , Au ⁺ , Zn ²⁺ , Al ³⁺ , Ga ³⁺ , In ³⁺ , Si ⁴⁺ , Si ²⁺ , Ge ⁴⁺ , Ge ²⁺ , Sn ⁴⁺ , Sn ²⁺ , Bi ⁵⁺ , Bi ³⁺ , Cd ²⁺ , Mn ²⁺ , Tb ³⁺ , Gd ³⁺ , Ce ³⁺ , La ³⁺ , Cr ⁴⁺ and combinations thereof, along with corresponding metal salt counteranions.

[ 0070 ] In certain embodiments, the framework comprises heterogeneous linking moieties. In such instances, one linking moiety is selected from Formulas I-V above and a second moiety is selected from a structure having the general formula of VI or VII:

Formula VI Formula VI I

wherein R1-R8 are each individually selected from: alkyl, aryl, alkoxy, akenes, alkynes, phenyl, substitutions of the foregoing, sulfur-containing groups (e.g., thioalkoxy), silicon- containing groups, nitrogen-containing groups (e.g., amides), oxygen-containing groups (e.g., ketones, and aldehydes), halogen, nitro, amino , cyano, boron-containing groups, phosphorous-containing groups, carboxylic acids, or esters, H, NH ₂ , CN, OH, =0, =S, CI, I, F,

wherein X=l, 2, or 3.

[ 0071 ] In one embodiment, the heterogenous linking moieties are selected from a first linking moiety of Formula I-V and a second linking moiety selected from Formula VIII and IX:

Formula VIII Formula IX

(2-6-naphthalenedicarboxylate) biphenyl-4 , 4 ' di-

(NDC) carboxylate (BPCD)

[0072] In one embodiment, a linking moiety comprising formula I lacking R16, R17 and R18 is used as a linking moiety in combination with a second linking moiety having a structure of Formula VI, VII, VIII or IX.

[0073] As mentioned above, the linking moieties can be reacted with a metal, metal salt or ion to form a metal organic framework having a porosity and surface area that exceeds previous MOF porosity and surface area (e.g., MOF-177).

[0074] The preparation of the frameworks of the disclosure can be carried out in either an aqueous or non-aqueous system. The solvent may be polar or non-polar as the case may be. The solvent can comprise the templating agent or the optional ligand containing a monodentate functional group. Examples of non-aqueous solvents include n- alkanes, such as pentane, hexane, benzene, toluene, xylene, chlorobenzene, nitrobenzene, cyanobenzene, aniline, naphthalene, naphthas, n-alcohols such as methanol, ethanol, n- propanol, isopropanol, acetone, 1,3-dichloroethane, methylene chloride, chloroform, carbon tetrachloride, tetrahydrofuran, dimethylformamide, dimethylsulfoxide, N- methylpyrollidone, dimethylacetamide, diethylformamide, thiophene, pyridine, ethanolamine, triethylamine, ethlenediamine, and the like. Those skilled in the art will be readily able to determine an appropriate solvent based on the starting reactants and the choice of solvent is not believed to be crucial in obtaining the materials of the disclosure.

[0075] Templating agents can be used in the methods of the disclosure. Templating agents employed in the disclosure are added to the reaction mixture for the purpose of occupying the pores in the resulting crystalline base frameworks. In some variations of the disclosure, space-filling agents, adsorbed chemical species and guest species increase the surface area of the metal-organic framework. Suitable space-filling agents include, for example, a component selected from the group consisting of: (i) alkyl amines and their corresponding alkyl ammonium salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; (ii) aryl amines and their corresponding aryl ammonium salts having from 1 to 5 phenyl rings; (iii) alkyl phosphonium salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; (iv) aryl phosphonium salts, having from 1 to 5 phenyl rings; (v) alkyl organic acids and their corresponding salts, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; (vi) aryl organic acids and their corresponding salts, having from 1 to 5 phenyl rings; (vii) aliphatic alcohols, containing linear, branched, or cyclic aliphatic groups, having from 1 to 20 carbon atoms; or (viii) aryl alcohols having from 1 to 5 phenyl rings.

[ 0076] Crystallization can be carried out by leaving the solution at room temperature or in isothermal oven for up to 300 °C; adding a diluted base to the solution to initiate the crystallization; diffusing a diluted base into the solution to initiate the crystallization; and/or transferring the solution to a closed vessel and heating to a predetermined temperature.

[ 0077 ] For example, in certain embodiments, a ZruCX C^-containing compound such as Zn ₄ 0(0 ₂ CR)6, wherein R can be alkyl, aryl, or - (Ri)(R ₂ ), wherein Ri and R ₂ can be -H or any alkyl group can be reacted with a linking moiety of Formula I-V to form a metal organic framework comprising a surface area of about 10,400 m ² /g and a pore volume of about 3.59 cm ³ /g and an RCSR code of qom and a crystal density of between about 0.20 and 0.39 g/cm ³ . As described more fully below, these MOFs can be utilized for gas storage and separation or they may be further functionalize (using post synthesis reactions) to obtain yet further structures useful in gas separation, storage, sensing and catalysis.

[ 0078 ] In another embodiment, a Zn ₄ 0(C0 ₂ )6-containing compound such as Zn ₄ 0(0 ₂ CR)6, wherein R can be alkyl, aryl, or -N(R ₁ )(R ₂ ), wherein Ri and R ₂ can be -H or any alkyl group can be reacted with heterogenous linking moieties wherein a first linking moiety comprises a Formula I-IV or V and a second linking moiety comprises Formula VI- VIII or IX to form a metal organic framework comprising a surface area of between about 6, 100 and about 10,400 m ² /g, a pore volume of about 2.1 to 3.6 cm ³ /g, an RCSR code of ith-d or toz and a crystal density of between about 0.20 and 0.39 g/cm ³ . As described more fully below, these MOFs can be utilized for gas storage and separation or they may be further functionalize (using post synthesis reactions) to obtain yet further structures useful in gas separation, storage, sensing and catalysis.

[ 0079 ] Scheme 1 , below, provides examples of certain MOFs generated by the methods of the disclosure utilizing a metal and a linking moiety selected from formula I-IX or combinations thereof.

[ 0080 ] For example, the MOFs generated by Scheme I above having the characteristics set forth in Table I:

[ 0081 ] As described herein and above, the linking moieties may be tailored to comprise a reactive side group for post framework synthesis and reaction. All the aforementioned organic links that possess appropriate reactive functionalities can be chemically transformed by a suitable reactant post framework synthesis to further functionalize the pores. By modifying the organic links within the framework post- synthetically, access to functional groups that were previously inaccessible or accessible only through great difficulty and/or cost is possible and facile. Post framework reactants include all known organic transformations and their respective reactants; rings of 1-20 carbons with functional groups including atoms such as N, S, O and all metals that may chelate to and added functional group or a combination of previously existing an newly added functional groups. All reactions that result in tethering an organometallic complex to the framework for use, for example, as a heterogenous catalysts are contempalted.

[ 0082 ] Examples of post framework reactants include, but are not limited to, heterocyclic compounds. In one embodiment, the post framework reactant can be a saturated or unsaturated heterocycle. The term "heterocycle" used alone or as a suffix or prefix, refers to a ring-containing structure or molecule having one or more multivalent heteroatoms, independently selected from N, O and S, as a part of the ring structure and including at least 3 and up to about 20 atoms in the ring(s). Heterocycle may be saturated or unsaturated, containing one or more double bonds, and heterocycle may contain more than one ring. When a heterocycle contains more than one ring, the rings may be fused or unfused. Fused rings generally refer to at least two rings share two atoms therebetween. Heterocycle may have aromatic character or may not have aromatic character. The terms "heterocyclic group", "heterocyclic moiety", "heterocyclic", or "heterocyclo" used alone or as a suffix or prefix, refers to a radical derived from a heterocycle by removing one or more hydrogens therefrom. The term "heterocyclyl" used alone or as a suffix or prefix, refers a monovalent radical derived from a heterocycle by removing one hydrogen therefrom. The term "heteroaryl" used alone or as a suffix or prefix, refers to a heterocyclyl having aromatic character. Heterocycle includes, for example, monocyclic heterocycles such as: aziridine, oxirane, thiirane, azetidine, oxetane, thietane, pyrrolidine, pyrroline,

imidazolidine, pyrazolidine, pyrazoline, dioxolane, sulfolane 2,3 -dihydrofuran, 2,5- dihydrofuran tetrahydrofuran, thiophane, piperidine, 1,2,3,6-tetrahydro-pyridine, piperazine, morpholine, thiomorpholine, pyran, thiopyran, 2,3-dihydropyran, tetrahydropyran, 1,4- dihydropyridine, 1,4-dioxane, 1,3-dioxane, dioxane, homopiperidine, 2,3,4,7-tetrahydro-1H- azepine homopiperazine, 1,3-dioxepane, 4,7-dihydro-1,3-dioxepin, and hexamethylene oxide. For example, heteroc cles useful in the methods of the disclosure include:

[ 0083 ] In addition, heterocycle includes aromatic heterocycles (heteroaryl groups), for example, pyridine, pyrazine, pyrimidine, pyridazine, thiophene, furan, furazan, pyrrole, imidazole, thiazole, oxazole, pyrazole, isothiazole, isoxazole, 1,2,3-triazole, tetrazole, 1,2,3- thiadiazole, 1,2,3-oxadiazole, 1,2,4-triazole, 1,2,4-thiadiazole, 1,2,4-oxadiazole, 1,3,4- triazole, 1,3,4-thiadiazole, and 1,3,4-oxadiazole.

[ 0084 ] Additionally, heterocycle encompass poly cyclic heterocycles, for example, indole, indoline, isoindoline, quinoline, tetrahydroquinoline, isoquinoline,

tetrahydroisoquinoline, 1,4-benzodioxan, coumarin, dihydrocoumarin, benzofuran, 2,3- dihydrobenzofuran, isobenzofuran, chromene, chroman, isochroman, xanthene,

phenoxathiin, thianthrene, indolizine, isoindole, indazole, purine, phthalazine,

naphthyridine, quinoxaline, quinazoline, cinnoline, pteridine, phenanthridine, perimidine, phenanthroline, phenazine, phenothiazine, phenoxazine, 1,2-benzisoxazole,

benzothiophene, benzoxazole, benzthiazole, benzimidazole, benztriazole, thioxanthine, carbazole, carboline, acridine, pyrolizidine, and quinolizidine. [0085] In addition to the poly cyclic heterocycles described above, heterocycle includes polycyclic heterocycles wherein the ring fusion between two or more rings includes more than one bond common to both rings and more than two atoms common to both rings. Examples of such bridged heterocycles include quinuclidine,

diazabicyclo[2.2.1]heptane and 7-oxabicyclo[2.2.1]heptane.

[0086] The ultrahigh surface areas exhibited by the MOFs described herein (e.g., MOF-180, MOF-200, -205 and -210 are near the ultimate limit for solid materials. To appreciate this, it is useful to note that all these compounds have a volume specific surface area in the range of 1000 to 2000 m ² /cm ³ = 1 x 10 ⁹ to 2 x 10 ⁹ m ^_1 , and for a cube of edge d the external surface area/volume is 6d ² /d ³ = 61 d. Thus, for a monodisperse powder of cubic nanoparticles to have external surface that is equal to that of these MOFs the cube edge would have to be only 3 to 6 nm, which is a size far too small to practically realize in stable dry powders and therefore impossible to access the full surface area of such particles.

[0087] Natural gas is an important fuel gas and it is used extensively as a basic raw material in the petrochemical and other chemical process industries. The composition of natural gas varies widely from field to field. Many natural gas reservoirs contain relatively low percentages of hydrocarbons (less than 40%, for example) and high percentages of acid gases, principally carbon dioxide, but also hydrogen sulfide, carbonyl sulfide, carbon disulfide and various mercaptans. Removal of acid gases from natural gas produced in remote locations is desirable to provide conditioned or sweet, dry natural gas either for delivery to a pipeline, natural gas liquids recovery, helium recovery, conversion to liquefied natural gas (LNG), or for subsequent nitrogen rejection. C0 ₂ is corrosive in the presence of water, and it can form dry ice, hydrates and can cause freeze-up problems in pipelines and in cryogenic equipment often used in processing natural gas. Also, by not contributing to the heating value, CO ₂ merely adds to the cost of gas transmission.

[0088] An important aspect of any natural gas treating process is economics. Natural gas is typically treated in high volumes, making even slight differences in capital and operating costs of the treating unit significant factors in the selection of process technology. Some natural gas resources are now uneconomical to produce because of processing costs. There is a continuing need for improved natural gas treating processes that have high reliability and represent simplicity of operation. [ 0089 ] In addition, removal of carbon dioxide from the flue exhaust of power plants, currently a major source of anthropogenic carbon dioxide, is commonly accomplished by chilling and pressurizing the exhaust or by passing the fumes through a fluidized bed of aqueous amine solution, both of which are costly and inefficient. Other methods based on chemisorption of carbon dioxide on oxide surfaces or adsorption within porous silicates, carbon, and membranes have been pursued as means for carbon dioxide uptake. However, in order for an effective adsorption medium to have long term viability in carbon dioxide removal it should combine two features: (i) a periodic structure for which carbon dioxide uptake and release is fully reversible, and (ii) a flexibility with which chemical

functionalization and molecular level fine-tuning can be achieved for optimized uptake capacities.

[ 0090 ] A number of processes for the recovery or removal of carbon dioxide from gas steams have been proposed and practiced on a commercial scale. The processes vary widely, but generally involve some form of solvent absorption, adsorption on a porous adsorbent, distillation, or diffusion through a semipermeable membrane.

[ 0091 ] Accordingly, the MOFs of the disclosure can be used for gas separation, storage, chemical separation and storage, catalysis and as sensors. The disclosure accordingly provides devices for the sorptive uptake of a chemical species. The device includes a sorbent comprising a framework provided herein or obtained by the methods of the disclosure. The uptake can be reversible or non-reversible. In some embodiments, the sorbent is included in discrete sorptive particles. The sorptive particles may be embedded into or fixed to a solid or liquid- and/or gas-permeable three-dimensional support. The MOFs of the disclosure comprise exception porosity for the reversible uptake or storage of liquids or gases and wherein the sorptive particles can reversibly adsorb or absorb the liquid or gas.

[ 0092 ] In some embodiments, a device provided herein comprises a storage unit for the storage of chemical species such as ammonia, carbon dioxide, carbon monoxide, hydrogen, amines, methane, oxygen, argon, nitrogen, argon, organic dyes, polycyclic organic molecules, and combinations thereof.

[ 0093 ] Also provided are methods for the sorptive uptake of a chemical species. The method includes contacting the chemical species with a sorbent that comprises a framework provided herein. The uptake of the chemical species may include storage of the chemical species. In some embodiments, the chemical species is stored under conditions suitable for use as an energy source.

[ 0094 ] Also provided are methods for the sorptive uptake of a chemical species which includes contacting the chemical species with a device provided described herein.

[ 0095 ] The following examples are intended to illustrate but not limit the disclosure. While they are typical of those that might be used, other procedures known to those skilled in the art may alternatively be used.

EXAMPLES

[ 0096] In the pursuit of MOFs with ultrahigh porosity, the octahedral Zn ₄ 0(C0 ₂ )6 has been used as a building unit in producing structures exhibiting exceptional porosity (Scheme 1). Joining such units by 4,4',4"-benzene-1,3,5-triyl-tribenzoate (BTB) and/or 1,4- benzenedicarboxylate (BDC) linkers produces MOF-5, UMCM-2, and MOF-177, which heretofore showed the highest BET surface area and pore volume among MOFs (Table 1).

[ 0097 ] The disclosure expanded the links and use various combination of links to develop porosity that extendd the porosity of known MOFs.

[ 0098 ] The disclosure expanded the porosity of the MOFs using links comrpising 4,4',4"-[benzene-1,3,5-triyl-tris(ethyne-2, l-diyl)]tribenzoate (BTE) and 4,4',4"-[benzene- 1,3,5-triyl-tris(benzene-4, l-diyl)] tribenzoate (BBC) to give MOF-180 and MOF-200, respectively, and used mixed 4,4',4"-benzene-1,3,5-triyl-tribenzoate (BTB)/2,6- naphthalenedicarboxylate (NDC) and BTE/biphenyl-4,4'-dicarboxylate (BPDC) links to obtain MOF-205 and 210 (Scheme 1 and Table 1).

[ 0099 ] Derivative of aromatic tritopic linkers were used to extend MOF- 177. The derivative comprises extended "arms" from the central aromatic ring extending the pores size (Fig. 1). The resulting framework in which alternating octahedral Zn ₄ 0(C0 ₂ )6 and triangular BTE and BBC units produce one of the most porous structures yet reported.

[ 00100 ] An isoreticular non- interpenetrating expansion of MOF- 177was targeted by using BTE or BBC to make the highly porous materials MOF-180 and -200 (Fig. 1, G and H). The unit cell volumes of MOF-180 and -200 are respectively 1.9 and 2.6 times greater than that of MOF-177, with void volumes of 89 and 90% of the crystal volume (Table 1). The cage sizes for MOF-180 and -200 are 15 by 23 and 18 by 28 A, respectively, which is on the border of micropores and mesopores.

[ 00101 ] The bulk density for MOF-200 is 0.22 g cnf ³ , implying that the qom net is advantageous to reduce the dead space and increase the gas storage capacity per unit volume in a closed tank. This density is the lowest for MOF structures, and of any other crystals at room temperature except for those of the least dense covalent organic frameworks.

[ 00102 ] On the basis of the effective use of the qom net for the successful synthesis of the non-interpenetrating MOF- 180 and MOF-200, the development of other MOFs of nets without self-dual tilings were attempted by mixing organic links of mixed connectivity. Both tritopic H ₃ BTB and ditopic H ₂ NDC were used in a reaction with Zn ions to produce Zn ₄ 0(C0 ₂ ) ₆ units and make MOF-205 (Fig. 2A).

[ 00103 ] The MOF-205 structure belongs to a cubic space group Pm 3n and consists of one type of Zii40(C0 ₂ )6 octahedral unit whose vertices are connected to four BTB and two NDC links. The topology of MOF-205 (ith-d) is of considerable intrinsic interest; all the rings of the underlying net are 5 -rings, and it forms a face transitive tiling of dodecahedra [5 ¹² ] and tetrahedral [5 ⁴ ] in the ratio 1 :3 (Fig. 2C). The dual structure (ith) is an edge-transitive net with tetrahedral and icosahedral vertices and very different from the original net.

[ 00104 ] Attempts at isoreticular expansion of MOF-205 by use of the linkers BTE and BPDC produced a different but related material (termed MOF-210) (Fig. 2B). MOF- 210 was prepared from a solvothermal reaction ofH ₃ BTE,H ₂ BPDC, and zinc(II) nitrate hexahydrate. Rather than the 12-face tile of ith-d, the new topology has 30-face tiles, and the full tiling consists of [4 ⁶ .5 ²⁴ ], [4 ³ .5 ⁶ ], and [5 ⁴ ] in the ratio 1 :2:3 (Fig. 2D). The difference in the link length ratio (for example, 0.76 for MOF-210 and 0.79 for UMCM-2) may be important. The dimension of the largest cage in MOF-210 is 26.9 by 48.3 A, which comprises 18 Zn ₄ 0 units with 14 BTE and 6 BPDC links. The estimated bulk density (void space) is 0.25 g cnf ³ (89%), which is almost the same as that for MOF-180.

[ 00105 ] Considering the bulk density and void space calculated from the crystal structure analyses, MOF-200 and -210 are promising candidates to realize ultrahigh surface area. Before gas adsorption measurements, grand canonical Monte Carlo (GCMC) simulations were performed to calculate nitrogen adsorption isotherms. Predicted isotherms (Fig. 3A) show unusual steps attributed to the micropore filling at P/P ₀ = 0.12 and 0.26 (for MOF-200 and -210, respectively), and total nitrogen uptakes in MOF-200 and -210 reaching 2650 and 2300 cm ³ g ^_1 , respectively. The BET and Langmuir surface areas determined from these calculated isotherms are respectively 6260 and 12,040 for MOF-200 and 6580 and 10,450 m ² g ¹ for MOF-210; these are much higher than values reported previously for other porous crystals.

[ 00106] To assess the architectural stability and porosity of these low-density MOFs, and to confirm the calculations, nitrogen adsorption isotherms were measured on the guest free samples of MOF-200, -205, and -210. Preliminary trials revealed that the solvent exchange followed by pore evacuation under vacuum was not effective to activate MOF- 200 and -210 without losing the porosity. Thus, these crystals were fully exchanged with liquid CO2, they were kept under supercritical CO2 atmosphere, and then their pores were bled of CO2 in order to yield activated samples. Successful guest removal was confirmed by powder x-ray diffraction measurements and elemental analyses. As shown in Fig. 3A, all MOF samples show distinctive steps (P/P ₀ = 0.14, 0.09, and 0.27 for MOF-200, -205, and - 210, respectively), and the profiles for MOF-200 and -210 are nearly the same as the predicted isotherms. The maximum nitrogen uptake capacities at 77 K in MOF-200, -205, and -210 are 2340, 1410, and 2330 cm ³ g ^_1 , respectively.

[ 00107 ] These uptake values in MOF-200 and -210 are well beyond those observed for other crystalline porous solids. Further, the measured values are near the values predicted on the basis of the structure, indicating that these materials are well activated. Because of the successful sample activation, extremely high BET (and Langmuir) surface areas were obtained: 4530 (10,400), 4460 (6, 170), and 6240 (10,400) m ² g ^_1 for MOF-200, - 205, and -210, respectively. The BET surface area of MOF-210 is the highest reported for crystalline materials. It has recently been shown that the BET method applied to nitrogen adsorption isotherms provides physically meaningful values for the surface areas of MOFs.

[ 00108 ] Given the exceptional properties of such materials, it is expected that MOFs with ultrahigh surface area would exhibit exceptional gas storage capacity. Accordingly, this series of MOFs was subjected to high-pressure hydrogen (77 K) and methane (298 K) adsorption so as to examine their potential utility in the storage of gaseous fuels (Fig. 3, B and C, and table 13). In hydrogen isotherms, these MOFs reach saturation uptakes, and the saturation pressure increases with an increase in the cavity size. The surface excess hydrogen uptake in MOF-210 (86 mg g ^_1 ) is higher than those in MOF-5, MOF- 177, UMCM-2, and NOTT-112). The total uptake that a material can store is more relevant to the practicability of using H2 as a fuel, but it cannot be measured experimentally. Therefore, this value was estimated using the pore volume and the density of hydrogen at 77 K. The calculated gravimetric hydrogen density in MOF-210 (176 mg g ^_1 ) exceeds that of typical alternative fuels (methanol and ethanol) and hydrocarbons (pentane and hexane). MOF-200 and -205 also show large total hydrogen uptake (163 and 123 mg respectively); again, these values are higher than MOF-177.

[ 00109 ] Methane uptake was measured at 298 K and up to 80 bar (Fig. 3C); under the present experimental conditions, all isotherms were not saturated. Although the excess methane uptake in MOF-200, -205, and -210 (234, 258, and 264 mg g ^_1 at 80 bar, respectively) were smaller than that in PCN-14 (253 mg g-1 at 290 K and 35 bar, respectively), the calculated total uptakes (446, 394, and 476 mg g ^_1 for MOF-200, -205, and -210, respectively) were more than 50% greater than those of PCN-14. Moreover, the corresponding volumetric methane densities in the present MOFs are respectively 2, 3, and 2.5 times greater than volumetric bulk density (grams per liter) of methane at the same temperature and pressure (table 13). Because the isotherms are nearly linear up to 80 bar, these materials can deliver most of the sorbed methane in the pressure range between 10 to 200 bar.

[ 00110 ] Large storage volumes should also be desirable for short-term CO ₂ storage. High-pressure CO ₂ isotherms for all three MOFs were collected and are presented in Fig. 3D. These MOFs show sigmoidal isotherms, and the pressure for the steep rise reflects the pore size of the MOFs. An isotherm for MOF-205 is saturated at a pressure of 37 bar, whereas the saturation pressure for MOF- 200 and -210 are ~50 bar. In contrast to hydrogen and methane uptakes, the amounts of excess CO ₂ uptake are directly related to the total pore volume. The CO ₂ uptake value of 2400 mg g ^_1 in both MOF-200 and -210 exceeds those of any other porous material, such as MOF-177 and MIL-lOlc(Cr) (1470 and 1760 mg g ^_1 , respectively).

[ 00111 ] Chemicals used in this work: 2,6-Naphthalendicarboxylic acid (H ₂ NDC), biphenyl-4,4'-dicarboxylic acid (H ₂ BPDC), zinc(II) nitrate hexahydrate (Zn(N0 ₃ ) ₂ -6H ₂ 0), and anhydrous acetone were purchased from Sigma-Aldrich Co. and N,N- dimethylformamide (DMF) and l-methyl-2- pyrrolidinone (NMP) were purchased from Fisher Scientific International Inc. Zinc(II) nitrate tetrahydrate (Zn( 0 ₃ ) ₂ -4H ₂ 0) was purchased from EM Science. Pyridine was purchased from Daejung Chemicals & Metals Co., Ltd. All starting materials except for Ν,Ν-diethylformamide (DEF, BASF) were used without further purifications. DEF was treated by addition of charcoal carbon (ca. 0.5 g, Acros, CAS No.: 7440-44-0) into 1 L and stirred 12 h at room temperature. The black suspension solution was filtered through a silica-gel column (ca. 350 g, Silica gel 60, 230- 400 mesh, EMD Chemicals) to remove carbon powder. l,3,5-Tris(4'-carboxyphenyl- )benzene (H ₃ BTB) was prepared according to published procedures.

[ 00112 ] Syntheses of organic linkers:

[ 00113 ] A. 4,4',4"-(Benzene-1,3 ,5-triyltris(ethyne-2, l-diyl))tribenzoic acid (H ₃ BTE) Trimethyl 4,4',4"-(benzene-l,3,5-triyltris(ethyne-2, l-diyl))tribenzoate. A mixture of methyl 4-iodobenzoate (2.29 g, 8.75 mmol), Pd(PPh ₃ ) ₂ Cl ₂ (154 mg, 0.22 mmol) and Cul (209 mg, 1.10 mmol) in Et ₃ (30 mL) was added to 1,3,5- triethynylbenzene (365 mg, 2.43 mmol) in Et ₃ (10 mL). The mixture was stirred for 20 h at room temperature under argon atmosphere. The solution was evaporated and the residue was dissolved in CH2CI2. The organic layer was washed by brine, dried over MgS04, filtered and concentrated.

Purification of the crude product by flash column chromatography on silica gel (CH2CI2) provided trimethyl 4,4',4"-(benzene-l,3,5-triyltris(ethyne-2,l-diyl))tribenzoat e as a pale yellow powder (788 mg, 59%): mp 177 °C;な-NMR (CDC1 ₃ , 400 MHz) δ 8.05 (d, 6H, J = 8.4 Hz), 7.70 (s, 3H), 7.60 (d, 6H, J = 8.4 Hz), 3.94 (s, 9H); ¹³ C-NMR (CDC1 ₃ , 100 MHz) δ

166.5, 134.6, 131.6, 130.0 129.6, 127.3, 123.8, 90.3, 90.0, 52.3; FT-IR (KBr, 4000-400 cm- ^x ) 3428 (br), 2951 (w), 2372 (w), 1724 (s), 1604 (S), 1435 (m), 1403 (w), 1274 (s), 1175 (m), 1105 (s), 1017 (w), 857 (w), 768 (s).

[ 00114 ] 4,4',4"-(Benzene-1,3,5-triyltris(ethyne-2,l-diyl))tribenzoic acid. A mixture of trimethyl 4,4',4"-(benzene-l,3,5-triyltris(ethyne-2, l-diyl))tribenzoate (773 mg, 1.40 mmol), LiOH-H ₂ 0 (881 mg, 21.0 mmol), tetrahydrofuran (THF, 25 mL) and water (5 mL) was stirred for 16 h at room temperature. The reaction mixture was concentrated. The residue was acidified with cold 3 M HCl (1 M = 1 mol dm ^-3 ) and cooled in an ice bath. The precipitate was filtered and washed with cold 3 M HCl. The ivory solid was dried. The dried solid was taken up in THF and filtered to remove insoluble inorganic salt. The solution was dried over MgS0 ₄ , filtered concentrated and dried under vacuum to give an ivory solid (693 mg, 97%): mp 352 °C;な-NMR (DMSO-d6, 400 MHz) δ 8.01 (d, 6H, J = 8.0 Hz), 7.88 (s, 3H), 7.72 (d, 6H, J = 8.0 Hz); ¹³ C-NMR (DMSO-d6, 100 MHz) δ 166.6, 134.5, 131.8, 131.0

129.6, 126.0, 123.4, 90.3, 89.8; FT-IR (KBr, 4000-400 cm ^-1 ) 3428 (br), 2994 (br), 2658 (w), 2534 (w), 2376 (w), 1687 (s), 1604 (s), 1518 (s), 1312 (s), 1277 (s), 1173 (w), 1105 (w), 856 (m), 768 (s); MALDI-TOF MS (m/z) [M]+ 510.0935 (found), 510.1103 (calcd. for

[ 00115 ] B. 4,4',4"-(Benzene-l,3,5-triyl-tris(benzene-4, l-diyl))tribenzoic acid (H3BBC) Trimethyl 4,4',4"-(benzene-l,3,5-triyl-tris(benzene-4, l-diyl))tribenzoate.

Anhydrous 1,2-dimethoxyethane (150 mL) was placed in a two-neck 250-mL round bottom flask equipped with a magnetic stirring bar and a reflux condenser under nitrogen atmosphere. 4-Methoxycarbonylphenylboronic acid (2.98 g, 16.6 mmol), CsF (5.03 g, 33.1 mmol), Pd(PPh ₃ ) ₄ (574 mg, 0.50 mmol), and 1,3 ,5-tris(4-bromo-phenyl) benzene (2.00 g, 3.68 mmol) were added to the flask, and the reaction mixture was refluxed for 48 h under nitrogen atmosphere. The solution was cooled to room temperature and evaporated under vacuum. The residue was dissolved in CHCl ₃ , washed with water and dried over MgS0 ₄ . The solvent was evaporated under vacuum. Further purification was achieved by dissolving the product in 50 mL of diethyl ether and the solution was heated for 20 min and placed in the refrigerator for 1 h. The white product was collected by filtration and dried in vacuum overnight (2.1 g, 80%): mp 218 °C;な-NMR (CDC1 ₃ , 400 MHz) δ 8.17 (d, 6H, J = 8.0Hz), 7.93 (s, 3H), 7.86 (d, 6H, J = 8.4Hz), 7.80 (d, 6H, J = 8.4Hz), 7.77 (d, 6H, J = 8.4Hz), 3.90 (s, 9H); ¹³ C-NMR (CDCI ₃ , 100 MHz) δ 167.4, 145.4, 142.3, 141.1, 139.7, 130.6, 129.5, 128.3, 128.2, 127.4, 125.6, 52.6; FT-IR (KBr, 4000-400 cm ^-1 ) 3428 (br), 2947 (w), 1932 (w), 1719 (s), 1607 (m), 1434 (m), 1277 (s), 1180 (m), 1110 (s), 1004 (m), 824 (s), 772 (s).

[ 00116] 4,4',4"-(Benzene-1,3,5-triyl-tris(benzene-4,l-diyl))tribenzo ic acid.

Trimethyl 4,4',4"-(benzene-1,3 ,5-triyl-tris(benzene-4, l-diyl))tribenzoate (2.00 g, 2.82 mmol), 2.2 g of NaOH, THF, water, and methanol (200, 80, and 50 mL, respectively) were mixed in a 1 L round bottom flask equipped with a magnetic stirring bar, and the mixture was stirred for 2 days at room temperature. The solution was evaporated under vacuum. The residue was acidified with 3 M C1 . The white solid was collected by filtration, washed with methylene chloride and methanol and dried in vacuum overnight (1.80 g, 96%): mp 326 °C; ^X H-NMR (DMSO-d6, 400 MHz) δ 13.07 (br, 3H) 8.07 (d, 6H, J = 8.0Hz), 8.06 (s, 3H), 8.05 (d, 6H, J = 8.0Hz), 7.91 (d, 6H, J = 7.6Hz), 7.89 (d, 6H, J = 7.2Hz); ¹³ C-NMR (DMSO-d6, 100 MHz) δ 168.0, 144.6, 141.9, 140.7, 139.2, 130.9, 130.6, 128.8, 128.4, 127.6, 125.3; FT-IR (KBr, 4000-400 cm ^-1 ) 3448 (br), 3029 (br), 2661 (w), 2536 (w), 1925 (w), 1686 (s), 1606 (s), 1419 (m), 1276 (m), 1177 (m), 1118 (m), 1003 (m), 824 (s), 773 (s); MALDI-TOF MS (m/z) [M]+ 666.2976 (found), 666.2042 (calcd. for C ₄₅ H ₃ o0 ₆ ). [ 00117 ] Analytical techniques: Single-crystal X-ray diffraction data for MOF-200 were collected at 100 K using a Bruker Platium 200 diffractometer with synchrotron radiation (λ =0.77490 A) at Beamline 11.3.1 at the Advanced Light Source (ALS),

Lawrence Berkeley National Laboratory. Single-crystal X-ray diffraction data for MOF-205 and MOF-210 were collected at 100 K using synchrotron radiation (λ = 0.90000 A (MOF- 205), and 1.10000 A (MOF-210), respectively) at beamlines 4A HFMX, and 6B MX-I. The diffraction data for MOF-180 were collected at 258 K on a Bruker APEX CCD

diffractometer with CuKa (λ = 1.54178 A).

[ 00118 ] Powder X-ray diffraction data were collected using a Bruker D8 Discover Θ- 2Θ diffractometer in reflectance Bragg-Brentano geometry at 40 kV, 40 mA (1,600 W) for CuKal radiation (λ = 1.5406 A). TGA was carried out using a TA Q500 and a Scinco TGA- S1000 thermal analysis system. Fourier transform infrared spectra (FT-IR) of samples prepared as KBr pellets were measured using a Nicolet FT-IR Impact 400 system and a JASCO FT/IR-4000 spectrophotometer.

[ 00119 ] Synthesis and characterization of MOFs:

[ 00120 ] MOF-180. A solid mixture of H ₃ BTE (7.5 mg, 0.015 mmol) and

Zn(N0 ₃ ) ₂ -6H ₂ 0 (75 mg, 0.25 mmol) was dissolved in a mixture of DMF/NMP (2.0/2.0 mL) in an 8-mL glass vial. The clear reaction solution was heated in an isotherm oven at 85 °C for 96 h resulting in colorless polyhedral crystals, which were isolated by washing with a mixture of DMF and NMP (3 x 4 mL) and dried in air. Yield: 5.2 mg, 27% based on 1 mol of H3BTE. Elemental microanalysis for Ζη ₄ 0(ΒΤΕ)2(Η2θ)3Ή20≡ C66t½Oi ₄ Zn ₄ , calculated (%): C, 60.49; H, 2.46; N, 0.00. Found (%): C, 60.98; H, 2.54; N, 0.06. FT-IR (KBr, 4000-400 cm-1): 3422 (br, w), 1604 (s), 1534 (s), 1413 (vs), 1176 (w), 1016 (w), 875 (w), 859 (m), 779 (s), 743 (w), 698 (w), 677 (w), 609 (w), 523 (w), 446 (w), 405 (w).

[ 00121 ] MOF-200. A solid mixture of H3BBC (22.0 mg, 0.033 mmol) and

Zn(N0 ₃ ) ₂ -6H ₂ 0 (98.2 mg, 0.33 mmol) was dissolved in a mixture of DEF/NMP (4.0/4.0 mL) in a 20-mL glass vial. The clear reaction solution was heated in an isotherm oven at 85 °C for 24 h resulting in colorless trigonal prismatic crystals, which were isolated by washing with a mixture of DEF and NMP (3 x 4 mL) and dried in air. Yield: 30 mg, 29% based on 1 mol of H ₃ BBC. Elemental microanalysis for Zn ₄ 0(BBC) ₂ (H ₂ 0)3-Fl ₂ 0≡ C ₉ oH ₆₂ Oi7Zn ₄ , calculated (%): C, 64.46; H, 3.73; N, 0.00. Found (%): C, 64.42; H, 3.57; N, 0.00. FT-IR (KBr, 4000-400 cm-1): 1928 (w), 1800 (w), 1709 (m), 1612 (vs), 1566 (s), 1525 (s), 1408 (vs), 1184 (m), 1108 (w), 1006 (m), 869 (w), 828 (s), 787 (s), 706 (w), 655 (m), 558 (w), 512 (w).

[ 00122 ] MOF-200 (large scale synthesis). A solid mixture of H ₃ BBC (200 mg, 0.30 mmol) and Zn( 03)2-6H20 (950 mg, 3.19 mmol) was dissolved in a mixture of DEF/NMP (80/80 mL) in a 500-mL Nalgene® high-density polyethylene (HDPE) container. Reaction solution was sonicated for 1 h prior to heating, and then placed in an isothermal oven at 82 °C for 48 h to give the crystals of MOF-200 (150 - 170 mg, 44 - 50% yield based on 1 mol of H ₃ BBC).

[ 00123 ] MOF-205. A solid mixture of H ₃ BTB (12.8 mg, 0.029 mmol), and H ₂ NDC (10.5 mg, 0.049 mmol), and Ζη(Ν0 ₃ ) ₂ ·6Η ₂ 0 (42.5 mg, 0.14 mmol) was dissolved in a mixture of DMF/EtOH (3.0/0.3 mL) in a 4-mL vial. The vial was capped and heated in an isothermal oven at 95 °C for 24 h to give colorless truncated-octahedral crystals. The reaction mixture was allowed to cool naturally to room temperature and the crystals were washed with DMF and dried in air. Yield: 21 mg, 68% based on 1 mol of H3BTB.

Elemental microanalysis for MOF-205, Zn40(BTB)4/3(NDC)≡ C ₄₈ H ₂₆ 0 ₁₃ Zn ₄ , calculated (%): C, 53.78; H, 2.48; N, 0.00. Found (%): C, 53.58; H, 2.29; N, < 0.1. FT-IR (KBr, 4000- 400 cm ^-1 ): 3335 (s, br), 1584 (vs), 1541 (vs), 1406 (vs), 1186 (m), 1141 (w), 1108 (w), 1015 (w), 921 (w), 854 (m), 779 (vs), 704 (m), 672 (w), 560 (w), 475 (m), 457 (m), 442 (m), 419 (w).

[ 00124 ] MOF-210. A solid mixture of H ₃ BTE (8.3 mg, 0.016 mmol), H ₂ BPDC (15.7 mg, 0.065 mmol), and Zn( 03)2'6H20 (42.5 mg, 0.14 mmol) was dissolved in a mixture of DMF/NMP (5.0/5.0 mL) in a 20-mL vial. The vial was capped and heated in an isothermal oven at 95 °C for 72 h to give colorless polyhedral crystals. The reaction mixture was allowed to cool naturally to room temperature and the crystals were washed with DMF and dried in air. Yield: 13 mg, 68% based on 1 mol of H3BTE. Elemental microanalysis for MOF-210, Zn ₄ 0(BTE) _4/3 (BPDC)≡ C ₅₈ H ₂₈ O ₁₃ n ₄ , calculated based on framework only (%): C, 53.78; H, 2.48; N, 0.00. Found (%): C, 53.58; H, 2.29; N, < 0.1. FT-IR (KBr, 4000-400 cm ^-1 ): 3338 (s, br), 2206 (w), 1934 (w), 1654 (w), 1604 (vs), 1579 (vs), 1533 (vs), 1407 (vs), 1175 (m), 1098 (w), 1015 (w), 960 (w), 859 (m), 770 (s), 744 (w), 699 (w), 679 (w), 607 (w), 526 (w), 471 (w), 456 (m), 439 (m), 419 (m).

[ 00125 ] Single Crystal X-ray Diffraction Analyses. [ 00126] MOF-180. A colorless polyhedral crystal was sealed in a capillary, and its diffraction data set was collected at 258 K on a Bruker APEX CCD diffractometer with CuKa radiation (λ = 1.54178 A). Bruker SMART program was used for data collection, and SAINT was used for cell refinement, and reduction. Absorption correction was applied using SADABS. XPREP suggested a trigonal space group, P 3 lc (No. 163) with a CFOM of 7.99. Since the space group is the same as MOF-177 (Zn ₄ 0(BTB) ₂ ), it is expected that the atomic connectivity of MOF-180 is also similar with that of MOF-177 (the qom net). Due to the weak diffraction intensities and low resolution (2.23A), only the Zn ions could be found. However, this resolution was sufficient for dissolving the Zn- · - Zn separation in a Zn ₄ 0 unit (about 3.2 A) although it was not for other bonds involving light atoms such as CO and CC as well as ZnO bonds (~ 2.0 A). In more detail, direct methods by XS in SHELX-TL software package suggested two unique Zn atoms (Znl and Zn2) belonging to one of two independent Zn ₄ 0 units in the asymmetric unit. The symmetry generated Zn atoms formed a tetrahedral arrangement with inter-atomic distances of about 3.4 A. The third Zn atom examination on the electron density maps by WinGX (S13) indicated that a moiety of large electron densities was present around a special position (0.3333, 0.6667, 0.2500), which was ascribed to the other Zr^O unit showing a disorder over two sites. Two oxygen atoms (OIC and 02C) were generated at the centers of the two Zn40 moieties; O IC and 02C sit on Wyckoff positions h and d, respectively. All the Zn atoms were refined anisotropically with application of restrains on interatomic distances and thermal parameters (DFIX and ISOR instructions in XL). Because of the very low and diffuse residual electron densities, it was not possible to identify the C and O atoms of the organic linkers. However, it was clear that noticeable electron densities were joining Zn ₄ 0 moieties and they corresponded to the BTE linkers (Fig. 4). Therefore, using the geometric information of a qom net, a model structure was built by incorporation of a BTE fragment into the crystal lattice using Materials Studio. The final structural model was obtained by Materials Studio Forcite calculations; both the positions of ZruO units and the unit cell parameters were not optimized. Due to the disordered one of two Zn ₄ 0 units, the bond geometry involving Zn and O atoms were deviated significantly from the ideal values, and therefore, the disordered Zn sites were finally adjusted manually using Materials Studio Visualizer. A part of the extended structure is in Fig. 5, and crystal and refinement data are given in Table 2. Crystallographic data for MOFS 180 has been deposited into the Cambridge

Crystallographic Data Centre under deposition number CCDC 775690.

[ 00127 ] Table 2. Crystal data and structure refinement for MOF- 180. The marked (*) results are based on Zn ₄ 0 moieties only.

[ 00128 ] MOF-200. Intensity data were collected at Beamline 11.3.1 at the Advanced Light Source (ALS), Lawrence Berkeley National Laboratory through the SCrALS (Service Crystallography at Advanced Light Source) program. The diffraction data set from a colorless trigonal prismatic crystal sealed in a capillary was collected at 100 K on a Bruker Platinum 200 diffractometer with synchrotron radiation (λ = 0.77490 A). Bruker APEX-2 program was used for data collection, and SAINT was used for cell refinement, and reduction. Absorption correction was applied using SADABS. Crystal structure was solved using SHELX-TL software package with a trigonal space group, P 3 lc (No. 163). An initial model for MOF-200 was obtained by direct methods using XS, and improved by subsequent refinements using XL. Direct methods using a default TREF instruction in XS produced four Zn atoms and many electron density peaks that were difficult to extract ligand. Among four Zn atoms, two Zn atoms, Zn3 and Zn4 showed a statistical disorder over two sites. After fixing their site occupancy factors, and removing all other non-Zn atoms, phase expansion using a TEXP instruction with 2347 E0 > 1.5 was conducted to obtain an improved framework structure. There were three independent BBC links in the asymmetric unit. One lies at a general position and other two at special positions (Wyckoff positions, a and c, respectively) as shown in Fig. 6). Two independent Zn ₄ 0 units were also found at special positions (Wyckoff positions, d and h, respectively). While a Zn40 unit at an h position is ordered, the other one at a d position was disordered over two sites. The latter case required one of three carboxylate groups in the ordered BBC to be present over two positions with a half occupancy. One of the benzene rings of the BBC was also statistically disordered over two sites. Due to tendencies of dynamic disorder of all BBC links, restraints by AFIX, SADI and FLAT instructions were applied to maintain ideal geometry of their aromatic rings. For C43 and C44 atoms, EADP instructions were applied to avoid eccentric thermal ellipsoids. All hydrogen except for coordinating water molecules were placed in calculated positions and refined by applying a riding model. Without including solvent molecules, the refinement converged to Rl = 0.1924, and wR2 = 0.4783 for 12,945 reflections of I > 2σ(Ι). The large volume fraction of disordered solvents was calculated by PALTON SOLV CALC to 88444.1 A3 which corresponds to 89.2 % of the unit cell volume. PALTON SQUEEZE routine calculated that 10711 electrons per unit cell were attributed to the disordered solvents. With a modified reflection data excluding the solvent contribution, the final refinement process converged to Rl = 0.0686, wR2 =0.1855 (I > 2σ(Ι)). A part of the extended structure is in Fig. 6, and crystal and refinement data are given in Table 3. Crystallographic data for MOF-200 has been deposited into the Cambridge Crystallographic Data Centre under deposition number CCDC 775691.

[ 00129 ] Table 3. Crystal data and structure refinement for MOF-200.

[ 00130 ] MOF-205. The diffraction data set from a colorless truncated octahedral crystal measuring 0.30 x 0.30 x 0.30 mm ³ mounted was collected at 100 K on a ADSC Quantum 210 CCD diffractometer with synchrotron radiation (λ = 0.90000 A) at

Macromolecular Crystallography Wiggler Beamline 4A HFMX, Pohang Accelerator Laboratory (PAL), Pohang, Korea. ADSC Quantum-210 ADX program (Ver. 1.96) was used for data collection. HKL2000 (Ver. 0.98.699) (SI 8) was used for cell refinement, reduction, and absorption correction. Crystal structure was solved using SHELX-TL software package with a cubic space group, Pm3 n (No. 223). An initial model for MOF-205 was obtained by direct methods using XS, and improved by subsequent refinements using XL. Most non- hydrogen atoms in the framework were easily identified except for a disordered 2,6- naphthalenedicarboxylate (NDC) around a special position (Wyckoff position, h). Before resolving the disorder, other atoms were refined anisotropically to suppress noisy electron densities. As the molecular symmetry of NDC (C2h point group or m/2 if NDC is flat) is lower than the site symmetry (mm2) in the lattice, geometric restraints with DFIX were applied to prevent severe distortion of the naphthalene moiety. In NDC, two terminal carboxylate groups are parallel, but their C atoms not aligned in the same line. This required also a disordered model for the carboxylate. However, further resolution was not been applied, and instead, we have prepared an ordered carboxylate model for simplicity. As it is, the C8 and 03 atoms in the carboxylate have elongated ellipsoids normal to a

crystallographic 2-fold rotation axis as shown in Fig. 7. All phenyl groups were refined with restrained models by applying DFIX and FLAT instructions. Hydrogen atoms were placed in calculated positions and refined by applying a riding model. As usually observed in highly porous and symmetric MOF structures, it was very difficult to find occluded solvent molecules from diffuse electron densities. Without including solvent molecules, the refinement converged to Rl = 0.1271, and wR2 = 0.3973 for 4,318 reflections of I > 2σ(Ι). The large volume fraction of disordered solvent was calculated by PALTON SOLV CALC) to 23281.0 A3 which corresponds to 83.3% of the unit cell volume. PALTON SQUEEZE routine calculated that 4551 electrons per unit cell were attributed to the disordered solvents. With a modified reflection data excluding the solvent contribution, the final refinement process converged to Rl = 0.0516, wR2 = 0.1579 (I > 2σ(Ι)). A part of the extended structure is displayed in Fig. 7, and crystal and refinement data are given in Table 4. Crystallographic data for MOF-205 has been deposited into the Cambridge

Crystallographic Data Centre under deposition number CCDC 775692.

[ 00131 ] Table 4. Crystal data and structure refinement for MOF-205.

[ 00132 ] MOF-210. The diffraction data set from a fragment cut from a twinned crystal measuring 0.35 x 0.30 x 0.25 mm ³ mounted was collected at 100 K with synchrotron radiation (λ = 1.10000 A) on a 6B MX-I ADSC Quantum-210 detector with a silicon (111) doublecrystal monochromator at the Pohang Accelerator Laboratory, Korea. The ADSC Quantum-210 ADX program (Ver. 1.96) was used for data collection, and HKL2000 (Ver. 0.98.699) was used for cell refinement, reduction, and absorption correction. Although we mounted more than twenty crystals, the best data has only a low resolution of 1.9 A, a combinational approach using X-ray crystallography and a structural modeling has been applied to build the structure of MOF-210 similarly to the case of MOF-180. The Zn atoms were found with a trigonal space group, R3 (No. 148), by direct methods using XS in the SHEX-TL program package. Three sets of tetrahedrally-arranged Zn4 clusters were identified and refined anisotropically. The central oxygen atoms were introduced in the center of four Zn atoms per each Zn4 unit. With bond distance restraints using SADI instructions, the geometries of Zn ₄ 0 clusters were maintained during refinements. Three central oxygen atoms were also refined anisotropically. At this stage, some oxygen atoms coordinated to Zn atoms were shown in the difference Fourier map. However, incorporation of those atoms could not contribute for the expansion of the structural model. The Rl value was converged to 0.4698 for 9129 observed reflections (I > 2σ(Ι)) among 14547 unique reflections. The BTE and BPDC organic linkers were inserted based on both electron density-map analyses and with consideration on the ZruO · ZruO distances (Fig. 8). Four independent Zn ₄ 0 clusters in an asymmetric unit require four BTE and three BPDC links which could be generated using a Materials Studio modeling program. The structural model was finally optimized by the geometry optimization using Materials Studio Forcite routine with fixing both ZruO positions and unit cell parameters. The final coordinates were generated in a SHELX ins-file, and further refinements were tried to investigate whether the model would give reduced R-values. However, the refinement processes diverged due to distortion of organic moieties; therefore, refinements with a 'DMAP 0 0' instruction were performed to generate a CIF-file. PLATON ADSYMM indicated the presence of pseudo- symmetry and suggested R3 c (No. 167) with 88% probability. In fact, the structure could be also solved with R3 c, which gave the same framework connectivity as that for the lower space group, R 3. However, PLATON ADSYMM EXACT calculation supports R3, and there were many reflections that violated systematic absence conditions in R3 c; 224 reflections (average I, 90.0; average Ι/σ(Ι), 20.9) violated a reflection condition for the c- glide plane in R3 c. A part of the extended structure is shown in Fig. 9, and crystal and refinement data are shown in Table 5. Crystallographic data for MOF-205 has been deposited into the Cambridge Crystallographic Data Centre under deposition number CCDC 775693.

[ 00133 ] Table 5. Crystal data and structure refinement for MOF-210. The marked (*) results are based on Zn ₄ 0 moieties only.

[ 00134 ] Thermal Gravimetric Analyses.

[ 00135 ] MOF-180 and 200 samples were heated at a constant rate of 5 °C mm ^-1 up to 700 °C on a TA Instruments Q-500 series thermal gravimetric analyzer in ambient atmosphere. MOF-205 and 210 samples were heated at a constant rate of 5 °C mm ^-1 up to 700 °C in ambient atmosphere on a Scinco TGA-S1000 apparatus. When the samples contain guest molecules, two distinguishable weight losses were observed before the final plateau. The first large decrease in weight % is due to the evaporation of occluded guest molecules. The weight loss probably due to the framework destruction was observed at between 300 to 500 °C. In the case of mixed link MOFs, there were small shoulder traces in the TGA curve because of the difference in the decomposition temperature of the links. The estimation on the guest contents based on the TAG analysis was in good agreement with the results obtained by the ^- MR experiments. [ 00136] Grand Canonical Monte Carlo Simulations & Geometric Area

Calculations.

[ 00137 ] Atomistic grand canonical Monte Carlo (GCMC) simulations were performed to obtain nitrogen isotherms in MOF-200 and MOF-210. Prior to GCMC simulations density functional theory (DFT) calculations were performed for each MOF to derive partial charges of the MOF atoms which are needed to calculate the electrostatic interaction energy between atoms during the GCMC simulations.

[ 00138 ] DFT calculations. DFT calculations were performed on clusters isolated from the unit cells of MOF-200 and MOF-210, with the atomic coordinates taken from the experimental crystallographic data. These clusters included building units (e.g. metal-oxide corner and the linker) representative of their respective unit cells. Details of structure and atom types on MOF-200 and MOF-210 clusters are shown in Figs. 24 and 25, respectively. All DFT calculations were performed with the Gaussian 03 software using the PBEPBE level of theory and the 6-31G* basis set, and partial atomic charges were extracted using the ChelpG method by fitting them to reproduce the electrostatic potential generated by the DFT calculations. Resulting partial charges for MOF-200 and MOF-210 are given in Tables 6 and 7, respectively.

[ 00139 ] Grand canonical Monte Carlo (GCMC) simulations and Interaction potential. The interaction energy between the atoms was computed through the Lennard- Jones (LJ) and Coulomb potentials

where i and j are interacting atoms, and ri _j is the distance between atoms i and j. ei _j and Oij are the LJ well depth and diameter, respectively, q; and c are the partial charges of the interacting atoms, and εο is the dielectric constant. LJ parameters between different types of sites were calculated using the Lorentz-Berthelot mixing rules.

[ 00140 ] MOF models. LJ parameters for MOF-200 and MOF-210 atoms were taken from the DREIDING force field. Partial charges for MOF atoms were derived from DFT calculations as explained above. Table 8 shows the LJ parameters for all atom types found in MOF-200 and MOF-210.

[ 00141 ] Table 6: Partial atomic charges for MOF-200 atoms.

.42 ] Table 7: Partial atomic charges for MOF-210 atoms.

[ 00143 ] Table 8 : LJ paramaters for MOF-200 and MOF-210 atoms.

[ 00144 ] Nitrogen Model. Nitrogen molecule was modeled using the TraPPE force field. This force field was originally fit to reproduce the vapor-liquid coexistence curve of nitrogen. In this force field nitrogen molecule is a rigid structure where the N-N bond length is fixed at its experimental value of 1.10 A. This model also reproduces the experimental gas-phase quadrupole moment of nitrogen by placing partial charges on N atoms and on a point located at the center of mass (COM) of the nitrogen molecule. Table 9 shows the LJ parameters and partial charges for nitrogen.

[ 00145 ] Table 9. LJ parameters and partial charges for the sites in the nitrogen molecule.

[ 00146] General GCMC simulation settings. All GCMC simulations included a 10000 cycle equilibration period followed by a 10000 cycle production run. A cycle consists of n Monte Carlo steps; where n is equal to the number of molecules (which fluctuates during a GCMC simulation). All simulations included random insertion/deletion, translation and rotation moves of nitrogen molecules with equal probabilities. MOF atoms were held fixed at their crystallographic positions. An LJ cutoff distance of 12.5 A was used for all simulations. The Ewald sum technique was used to compute the electrostatic interactions. One unit cell of MOF-200 or MOF- 210 (Rhombohedral representation) was used for the simulations. Nitrogen isotherms were simulated at 77 K up to 0.9 bar. Fugacities needed to run the GCMC simulations were calculated using the Peng-Robinson equation of state. All simulated adsorption data reported in this work are the excess quantities, as it is the proper quantity for comparison with experimental data as explained elsewhere.

[ 00147 ] Table 10. Simulated surface areas and pore volume of MOFs.

[ 00148 ] Geometric surface area calculations. Geometric surface areas of the MOFs listed in Table 1 were calculated by rolling a sphere probe over the framework atoms as explained in the work of Duren et al. The probe diameter was equal to the van der Waals diameter of nitrogen, which is 3.72 A. The diameters of the framework atoms were also set to their van der Waals diameters (Table 11) which were calculated by multiplying their Lennard- Jones well depth diameters, σ, by 21/6. The σ values of all framework atoms were taken from the DREIDING force field except for the Cu and Cr atoms, which were taken from the Universal Force Field (UFF).

[ 00149 ] Table 11. Van der Waals diameters of the framework atoms of MOFs listed in Table 1.

[ 00150 ] Gas Adsorption Analyses. As -synthesized sample of MOF-205 were immersed in dichloromethane for 3 days; during the exchange the dichloromethane was refreshed three times. The resulting dichloromethane-exchanged sample of MOF-205 was transferred as a suspension to a quartz cell and the solvent was decanted. The wet sample was then evacuated (10 ^~3 Torr) at room temperature for 10 h then at 100 °C for 12 h.

[ 00151 ] As -synthesized samples of MOF-200 and 210 were immersed in DEF and dichloromethane for 3 days, respectively, during which the activation solvent was decanted and freshly replenished three times. Obtained samples were immersed in acetone for 12 h, during which the activation solvent was replenished more than five times. The sample was evacuated with supercritical CO2 in a Tousimis Samdri PVT-3D critical point dryer. Briefly, the acetone-containing sample was placed in the chamber and acetone was completely exchanged with liquid CO2. After that the chamber containing the sample and liquid CO2 was heated up around 40 °C and kept under the supercritical condition (typically 1300 psi) for 1 h. The CO2 was slowly vented (ca. 1 h) from the chamber at around 40 °C, yielding porous material.

[ 00152 ] Low-pressure gas adsorption measurements. Low-pressure gas adsorption experiments (up to 760 torr) were carried out on a Quantachrome AUTOSORB-1 automatic volumetric instrument. Ultrahigh-purity-grade 2 and He gases were used in all adsorption measurements. The N2 (77 K) isotherms were measured using a liquid nitrogen bath (77 K). [ 00153 ] BET surface area of MOFs. A BET surface area was obtained by using the data points on the adsorption branch of the 2 isotherm. The BET surface area for MOF- 200, 205, and 210 were calculated to be 4530, 4460, and 6240 m ² g ^-1 , respectively.

[ 00154 ] Table 12. Porosity data of highly porous MOFs. ND, no data.

[ 00155 ] High-pressure gas adsorption measurements. High-pressure gas adsorption isotherms for MOF-205 were gravimetrically recorded on a GHP-300 gravimetric high-pressure analyzer from VTI Corporation (currently TA Instruments). To obtain the excess adsorption isotherm, all data points were corrected for buoyancy and the thermal gradient that arises between the balance and the sample bucket. For MOF-200 and 210 equilibrium gas adsorption isotherms were measured using the static volumetric method in an HPA-100 from the VTI Corporation (currently Particulate Systems). Ultra-high-purity grade H ₂ , CH ₄ , He (99.999% purity), and C0 ₂ gases (99.995% purity) were used throughout the high-pressure adsorption experiments. When H ₂ gas was used, water and other condensable impurities were removed with a liquid nitrogen trap.

[ 00156] Estimation of total gas uptake. Although the surface excess mass is a useful concept, from the viewpoint of gas storage, the total amount that a material can store is more relevant. However, at high temperatures and pressures (i.e., above the critical point of gases), the density profile of the adsorbed phase becomes more diffused and, therefore, it is not possible to distinguish between the adsorbed and bulk phases with the present techniques. In this situation the surface excess is the only experimentally accessible quantity, and there is not a reliable method to estimate the absolute adsorbed amount with high accuracy, although many efforts have been devoted to resolve this issue. Therefore, the absolute amount of hydrogen adsorbed was estimated using a simple equation: (total uptake) = (excess uptake) + (bulk density of gas) x (pore volume).

[ 00157 ] Needless to say, the volumetric gas uptake (e.g., g L ^-1 unit) is also influenced by the packing factor of the crystalline materials. The packing density is influenced by both shape and size of the materials and usually is below unity, although these numbers for MOFs are not available here. Indeed, the volumetric uptake should be 10-25% smaller compared to the data in Table 13, if the packing density is 0.7.

[ 00158 ] Table 13. Summary of high-pressure adsorption measurements for MOFs. ND, no data; NA, not applicable.

[ 00159 ] A number of embodiments of the invention have been described.

Nevertheless, it will be understood that various modifications may be made without departing from the spirit and scope of the invention. Accordingly, other embodiments are within the scope of the following claims.