or the radicals R2 and R3 together form a ring system, R4 is hydrogen or a C,-C40 radical, R5 is a C,-C40 radical, and Z is a divalent group CR8R9-CR'0R", where R", R9, R'° and R"are identical or diffe- rent and are each hydrogen or a C,-C40 radical.

The present invention further relates to biscyclopentadienyl ligand systems having such a substi- tution pattern, catalyst systems comprising at least one of the organometallic transition metal compounds of the present invention, a process for preparing polyolefins by polymerization or co- polymerization of at least one olefin in the presence of one of the catalyst systems of the present invention and the use of the biscyclopentadienyl ligand systems of the present invention for pre- paring organometallic transition metal compounds.

Research and development on the use of organometallic transition metal compounds, in particular metallocenes, as catalyst components for the polymerization and copolymerization of olefins with the aim of preparing tailored polyolefins has been carried out intensively in universities and in industry during the past 15 years.

Now, both polyolefins based on ethylene and prepared by means of metallocene catalyst systems and, in particular, polyolefins based on propylene and prepared by means of metallocene catalyst systems represent a dynamically growing market segment.

Variation of the substitution pattern on the ligand systems of ansa-metallocenes alters the steric circumstances around the active center and also its electronic structure. This makes it possible to influence, for example, the polymerization behavior of the catalyst constituents and also finally the properties of the polymers, e. g. isotacticity, chain length or molar mass and also the macroscopic materials properties of these polymers.

In the polymerization of olefins, in particular propylene, the catalyst system which usually compri- ses at least one organometallic transition metal compound and a catalyst component such as an aluminoxane, a strong Lewis acid or an ionic compound is generally used in supported form in order to avoid formation of deposits in the reactor.

EP 0 629 631 describes C2-symmetric 2,4, 7-substituted ansa-metallocenes. It is demonstrated that the melting point of polypropylene prepared by means of such metallocenes is reduced com- pared to polypropylene which has been prepared using a corresponding C2-symmetrically 2,4- substituted ansa-metallocene. A significant influence of the substituents in the 7 position on the molecular weight of the polypropylenes was not observed.

WO 02/18397 describes an effective process for preparing highly substituted alkyl-bridged metal- locenes. However, the catalysts prepared using the metallocenes mentioned there give polypro- pylenes which do not have sufficiently high melting points.

It is an object of the present invention to find alkyl-bridged metallocenes which, when used as constituents of supported catalyst systems, are able to produce polypropylenes having a melting point higher than that of polypropylenes produced using known alkyl-bridged metallocenes. In addition, for economic reasons, the activity of the metallocenes to be discovered should not be inferior to that of the known metallocenes.

We have found that this object is achieved by the organometallic transition metal compounds of the formula (I) mentioned at the outset.

M1 is an element of group 3,4, 5 or 6 of the Periodic Table of the Elements or the lanthanides, for example titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum or tungsten, preferably titanium, zirconium, hafnium, particularly preferably zirconium and hafnium, and very particularly preferably zirconium.

The radicals X are identical or different, preferably identical, and are each halogen, for example fluorine, chlorine, bromine, iodine, preferably chlorine, hydrogen, C,-Czo-, preferably C,-C4-alkyl, C2-C20-, preferably C2-C4-alkenyl, C6-C22-, preferably C6-C, o-aryl, an alkylaryl or arylalkyl group having from 1 to 10, preferably from 1 to 4, carbon atoms in the alkyl part and from 6 to 22, pre- ferably from 6 to 10, carbon atoms in the aryl part,-OR or-NRRR, preferably-OR, where two radicals X may also be joined to one another, preferably two radicals-ORs which form, in particu- lar, a substituted or unsubstituted 1,1'-di-2-phenoxide radical. Two radicals X can also form a substituted or unsubstituted diene ligand, in particular a 1,3-diene ligand. The radicals R and R7 are each C,-C, o-, preferably C,-C4-alkyl, C6-C, 5-, preferably C6-C, o-aryl, alkylaryl, arylalkyl, fluo- roalkyl or fluoroaryl each having from 1 to 10, preferably from 1 to 4, carbon atoms in the alkyl radical and from 6 to 22, preferably from 6 to 10, carbon atoms in the aryl radical.

The index n is a natural number from 1 to 4 which corresponds to the oxidation number of M' minus 2, and is preferably 2 for the elements of group 4 of the Periodic Table of the Elements.

The radical R'is hydrogen or a Cacao radical. R'is preferably a cyclic, branched or unbranched C,-C20-, preferably C,-C8-alkyl radical, a C2-C20-, preferably C2-C8-alkenyl radical, an arylalkyl

radical having from 1 to 10, preferably from 1 to 4, carbon atoms in the alkyl part and from 6 to 22, preferably from 6 to 10, carbon atoms in the aryl part or a C2-C40-, preferably C4-C24 heteroaro- matic radical, particularly selected from the group consisting of substituted or unsubstituted thienyl radicals or of substituted or unsubstituted furyl radicals. Examples of particularly preferred radicals R1 are hydrogen, methyl, ethyl, n-propyl, isopropyl, n-butyl, i-butyl, s-butyl, t-butyl, n-pentyl, cyclo- pentyl, n-hexyl, cyclohexyl, n-heptyl, n-octyl, 2- (5-methyl) thienyl, 2- (5-methyl) furyl, benzyl and 2- phenylethyl, in particular methyl, ethyl or isopropyl.

The radical R2 is a substituted or unsubstituted C6-C40-aryl radical or C2-C40-heteroaromatic radi- cal containing at least one heteroatom selected from the group consisting of O, N, S and P. The radical R2 is preferably an unsubstituted or alkyl-substituted C6-C4o-aryl radical having from 1 to 10, preferably from 1 to 4, carbon atoms in the alkyl part and from 6 to 22, preferably from 6 to 10, carbon atoms in the aryl part, with the radicals also being able to be halogenated. Examples of preferred radicals R2 are phenyl, 2-toll, 3-toll, 4-toll, 2, 3-dimethylphenyl, 2, 4-dimethylphenyl, 2, 5-dimethylphenyl, 2, 6-dimethylphenyl, 3, 4-dimethylphenyl, 3, 5-dimethylphenyl, 3,5-di (tert-butyl)- phenyl, 2,4, 6-trimethylphenyl, 2,3, 4-trimethylphenyl, 1-naphthyl, 2-naphthyl, phenanthryl, p- isopropylphenyl, p-tert-butylphenyl, p-s-butylphenyl, p-cyclohexylphenyl and p-trimethylsilylphenyl.

The radical R3 is hydrogen or a Cl-C40 radical. R3 is preferably hydrogen or a cyclic, branched or unbranched Cl-C20-, preferably C1-C10-alkyl radical, a Cz-C2O-, preferably C2-C8-alkenyl radical, an arylalkyl radical having from 1 to 10, preferably from 1 to 4, carbon atoms in the alkyl part and from 6 to 22, preferably from 6 to 10, carbon atoms in the aryl part. Examples of particularly pre- ferred radicals R3 are hydrogen, methyl, ethyl, n-propyl, isopropyl, n-butyl, i-butyl, s-butyl, t-butyl, n-pentyl, cyclopentyl, n-hexyl, cyclohexyl, n-heptyl, n-octyl, benzyl or 2-phenylethyl, in particular hydrogen, methyl, ethyl or isopropyl.

The radicals R2 and R3 may also together form a ring system which can be either monocyclic or polycyclic. The radicals R2 and R3 preferably together form a substituted or unsubstituted, in parti- cular unsubstituted, 1, 3-butadiene-1, 4-diyl group.

The radical R4 is hydrogen or a Cl-C40 radical. R4 is preferably hydrogen or a cyclic, branched or unbranched Cl-C20-, preferably C1-C10-alkyl radical, a C2-C20-, preferably C2-CB-alkenyl radical, an arylalkyl radical having from 1 to 10, preferably from 1 to 4, carbon atoms in the alkyl part and from 6 to 22, preferably from 6 to 10, carbon atoms in the aryl part. Examples of particularly pre- ferred radicals R4 are hydrogen, methyl, ethyl, n-propyl, isopropyl, n-butyl, i-butyl, s-butyl, t-butyl, n-pentyl, cyclopentyl, n-hexyl, cyclohexyl, n-heptyl, n-octyl, benzyl and 2-phenylethyl, in particular hydrogen, methyl, ethyl or isopropyl.

The radical Rs is a C1-C40 radical. R5 is preferably a cyclic, branched or unbranched, preferably unbranched, C,-C20-, preferably C,-C, o-alkyl radical, a C2-C20-, preferably C2-C8-alkenyl radical,

an arylalkyl radical having from 1 to 10, preferably from 1 to 4, carbon atoms in the alkyl part and from 6 to 22, preferably from 6 to 10, carbon atoms in the aryl part. Examples of particularly pre- ferred radicals Rs are methyl, ethyl, n-propyl, n-butyl, n-pentyl, n-hexyl, n-heptyl, n-octyl, benzyl and 2-phenylethyl, in particular methyl or ethyl, very particularly preferably methyl.

The radicals R', R2, R3, R4 and Rs may, according to the present invention, also contain functional groups without changing the polymerization properties of the novel organometallic transition metal compounds of the formula (I), as long as these functional groups are chemically inert under the polymerization conditions.

Z is a divalent group CR8R9-CR'0R", where Re, R9, R'° and R"are identical or different and are each hydrogen or a C1-C40 radical. R8, R9, R'° and R"are preferably each hydrogen, a trimethyl- silyl group, a C1-C1o-, preferably C1-C3-alkyl group, a C1-C10-fluoroalkyl group, a C6-C10-fluoroaryl group, a C6-C, o-aryl group, a C8-C40-arylalkenyl group, a C7-C4o-arylalkyl group or a C7-C40- alkylaryl group. Two adjacent radicals together with the atoms connecting them may also form a saturated or unsaturated ring having from 4 to 15 carbon atoms. The radicals R8, R9, R'° and R" are particularly preferably hydrogen.

Particularly preferred embodiments of Z are the bridges: ethylidene, 1-methylethylidene, 1, 1-dimethylethylidene, 1, 2-dimethylethylidene, 1,1, 2,2- tetramethylethylidene, in particular ethylidene.

Furthermore, according to the present invention, the substituents are, unless restricted further, defined as follows : The term"C,-C40 radicals used in the present context refers to C,-C40-alkyl radicals, C1-C10- fluoroalkyl radicals, C1-C12-alkoxy radicals, C6-C40-aryl radicals, C2-C40-heteroaromatic radicals, C6-C10-fluoroaryl radicals, C6-C10-aryloxy radicals, C3-C, 8-trialkylsilyl radicals, C2-C20-alkenyl radi- cals, C2-C20-alkinyl radicals, C7-C40-arylalkyl radicals or C8-C40-arylalkenyl radicals.

The term"alkyl"as used in the present context encompasses linear or singly or multiply branched saturated hydrocarbons which may also be cyclic. Preference is given to a C,-C, 8-alkyl such as methyl, ethyl, n-propyl, n-butyl, n-pentyl, n-hexyl, n-heptyl, n-octyl, n-nonyl, n-decyl, cyclopentyl or cyclohexyl, isopropyl, isobutyl, isopentyl, isohexyl, sec-butyl or tert-butyl.

The term"alkenyl"as used in the present context encompasses linear or singly or multiply bran- ched hydrocarbons having at least one C-C double bond. In the case of a plurality of C-C double bonds, these may be cumulated or may alternate.

The term"aryl"as used in the present context refers to aromatic and, possibly fused, polyaromatic hydrocarbon substituents which may be unsubstituted or monosubstituted or polysubstituted by linear or branched C,-C, 8-alkyl, C,-C, e-alkoxy, C2-C, o-alkenyl or C3-C15-alkylalkenyl. Preferred examples of substituted and unsubstituted aryl radicals are, in particular, phenyl, 4-methylphenyl, 4-ethylphenyl, 4-propylphenyl, 4-isopropylphenyl, 4-tert-butylphenyl, 4-methoxyphenyl, 1-naphthyl, 9-anthryl, 9-phenanthryl, 3, 5-dimethylphenyl, 3, 5-di-tert-butylphenyl and 4- trifluoromethylphenyl.

The term"heteroaromatic radicals used in the present context refers to aromatic hydrocarbon substituents in which one or more carbon atoms are replaced by nitrogen, phosphorus, oxygen or sulfur atoms or combinations thereof. These may, like the aryl radicals, be unsubstituted or mono- substituted or polysubstituted by linear or branched C1-C18-alkyl, C2-C10-alkenyl or C3-Crs- alkylalkenyl. Preferred examples are thienyl, furyl, pyrrolyl, pyridyl, pyrazolyl, imidazolyl, oxazolyl, thiazolyl, pyrimidinyl, pyrazinyl and the like, and also derivatives thereof which are substituted by methyl, ethyl, propyl, isopropyl and ter-butyl radicals.

The term"alkylalkenyl"as used in the present context encompasses linear or singly or multiply branched hydrocarbons having one or more C-C double bonds which are isolated, so that the substituent has both alkyl and alkenyl sections.

The term"arylalkyl"as used in the present context refers to aryl-containing substituents whose aryl radical is linked to the appropriate part of the molecule via an alkyl chain. Preferred examples are benzyl, substituted benzyl, phenethyl, substituted phenethyl and the like.

The terms fluoroalkyl and fluoroaryl indicate that at least one hydrogen atom, preferably a plurality of and at most all hydrogen atoms, of the respective substituent are replaced by fluorine atoms.

Examples of fluorine-containing substituents which are preferred according to the present inventi- on are trifluoromethyl, 2,2, 2-trifluoroethyl, pentafluorophenyl, 4-trifluoromethylphenyl, 4-perfluoro- tert-butylphenyl and the like.

Preference is given to organometallic transition metal compounds of the formula (I) in which M'is an element of group 4 of the Periodic Table of the Elements, n is 2, R'is C,-C, o-alkyl, R3 is hydrogen or a C,-C, o-alkyl radical,

R4 is hydrogen or a C,-C, o-alkyl radical, Rs is a C1-C10-alkyl radical, Z is CH2-CH2 and the other variables are as defined in formula (I).

M'is preferably zirconium or hafnium, particularly preferably zirconium.

The radical R'is a C,-C, o-alkyl radical, in particular a C,-C4-alkyl radical, very particularly pre- ferably a methyl radical.

The radical R3 is hydrogen or a C,-C, o-alkyl radical, in particular hydrogen or a C,-C4-alkyl radical, very particularly preferably hydrogen or a methyl radical.

The radical R4 is hydrogen or a C,-C, o-alkyl radical, in particular hydrogen or a C,-C4-alkyl radical, very particularly preferably hydrogen or a methyl radical.

The radical Rs is a C,-C, o-alkyl radical, in particular a C,-C4-alkyl radical, very particularly pre- ferably a methyl radical.

Illustrative examples of novel organometallic transition metal compounds of the formula (I), which do not, however, restrict the invention, are: 1, 2-ethanediylbis (2, 7-dimethyl-4,5-benzindenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4-phenylindenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 7-trimethyl-4-phenylindenyl) zirconium dichloride, 1, 2-ethanediylbis (2,6, 7-trimethyl-4-phenylindenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl-4-phenylindenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyi-7-methyl-4-phenylindenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 7-dimethyl-4-phenylindenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-6, 7-dimethyl-4-phenylindenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 6, 7-trimethyl-4-phenylindenyl) zirconium dichloride, 1, 2-ethanediylbis(2-n-butyl-7-methyl-4-phenylindenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 7-dimethyl-4-phenylindenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-6, 7-dimethyl-4-phenylindenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 6, 7-trimethyl-4-phenylindenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-7-methyl-4-phenylindenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 7-dimethyl-4-phenylindenyl) zirconium dichloride,

1, 2-ethanediylbis (2-isopropyl-6, 7-dimethyl-4-phenylindenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 6, 7-trimethyl-4-phenylindenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4- (2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 5, 7-trimethyl-4- (2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,6, 7-trimethyl-4- (2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl-4- (2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-7-methyl-4- (2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 7-dimethyl-4- (2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-6, 7-dimethyl4-(2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 6, 7-trimethyl-4- (2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-7-methyl-4- (2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 7-dimethyl-4- (2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-6, 7-dimethyl-4- (2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 6, 7-trimethyl-4- (2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-7-methyl-4- (2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 7-dimethyl-4- (2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-6, 7-dimethyl-4- (2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 6, 7-trimethyl-4- (2-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4- (3-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 7-trimethyl-4- (3-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,6, 7-trimethyl-4- (3-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl-4- (3-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-7-methyl-4- (3-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 7-dimethyl-4- (3-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-6, 7-dimethyl-4- (3-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 6, 7-trimethyl-4-(3-tolyl)indenyl)zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-7-methyl-4- (3-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 7-dimethyl-4- (3-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-6, 7-dimethyl-4- (3-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 6, 7-trimethyl-4- (3-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-7-methyl-4- (3-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 7-dimethyl-4- (3-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-6, 7-dimethyl-4- (3-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 6, 7-trimethyl-4- (3-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4- (4-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 7-trimethyl-4- (4-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,6, 7-trimethyl-4- (4-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl-4- (4-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-7-methyl-4- (4-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 7-dimethyl-4- (4-tolyl) indenyl) zirconium dichloride,

1, 2-ethanediylbis (2-ethyl-6, 7-dimethyl-4- (4-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 6, 7-trimethyl-4- (4-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-7-methyl4- (4-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 7-dimethyl-4- (4-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-6, 7-dimethyl-4- (4-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 6, 7-trimethyl-4- (4-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-7-methyl-4- (4-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 7-dimethyl-4- (4-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-6, 7-dimethyl-4- (4-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 6, 7-trimethyl-4- (4-tolyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 7-trimethyl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,6, 7-trimethyl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-7-methyl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 7-dimethyl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-6, 7-dimethyl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 6, 7-trimethyl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-7-methyl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 7-dimethyl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-6, 7-dimethyl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 6, 7-trimethyl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-7-meth. yl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 7-dimethyl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-6, 7-dimethyl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 6, 7-trimethyl-4- (3, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 7-trimethyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,6, 7-trimethyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-7-methyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 7-dimethyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-6, 7-dimethyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 6, 7-trimethyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-7-methyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 7-dimethyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-6, 7-dimethyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 6, 7-trimethyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethane (2-isopropyl-7-methyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 7-dimethyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichloride,

1, 2-ethanediylbis (2-isopropyl-6, 7-dimethyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 6, 7-trimethyl-4- (3, 5-di-tert-butylphenyl) indenyl) zirconium dichlori- de, 1, 2-ethanediylbis (2, 7-dimethyl-4- (p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 7-trimethyl-4- (p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,6, 7-trimethyl-4- (p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl4-(p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-7-methyl-4- (p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 7-dimethyl-4- (p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-6, 7-dimethyl-4- (p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 6, 7-trimethyl-4- (p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-7-methyl-4- (p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 7-dimethyl4-(p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-6, 7-dimethyl-4- (p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 6, 7-trimethyl-4- (p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethane (2-isopropyl-7-methyl-4- (p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 7-dimethyl-4- (p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-6, 7-dimethyl-4- (p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 6, 7-trimethyl-4- (p-tert-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4- (2, 3-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 7-trimethyl-4- (2, 4-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,6, 7-trimethyl-4- (2, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 5,6, 7-tetramethyl4-(2, 6-dimethylphenyi) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-7-methyl-4- (3, 4-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 7-dimethyl-4- (2, 3-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-6, 7-dimethyl-4- (2, 4-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 6, 7-trimethyl-4- (2, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-7-methyl4-(2, 6-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 7-dimethyl-4- (3, 4-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-6, 7-dimethyl-4- (2, 3-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 6, 7-trimethyl-4- (2, 4-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-7-methyl-4- (2, 5-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 7-dimethyl-4- (2, 6-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-6, 7-dimethyl-4- (3, 4-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 6, 7-trimethyl-4- (2, 3-dimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4- (1-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 7-trimethyl-4- (1-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,6, 7-trimethyl-4- (1-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl-4- (1-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-7-methyl-4- (1-naphthyl) indenyl) zirconium dichloride,

1, 2-ethanediylbis (2-ethyl-5, 7-dimethyl-4- (1-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-6, 7-dimethyl-4- (1-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 6, 7-trimethyl-4- (1-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis(2-n-butyl-7-methyl-4-(1-naphthyl)indenyl)zir conium dichloride, 1, 2-ethanediylbis(2-n-butyl-5,7-dimethyl-4-(1-naphthyl)indenyl )zirconium dichloride, 1, 2-ethanediylbis(2-n-butyl-6,7-dimethyl-4-(1-naphthyl)indenyl )zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 6, 7-trimethyl-4- (1-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-7-methyl-4-(1-naphthyl)indenyl)zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 7-dimethyl-4- (1-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-6, 7-dimethyl-4- (1-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 6, 7-trimethyl-4-(1-naphthyl)indenyl)zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4- (2-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl-4- (2-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-7-methyl-4- (2-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 6, 7-trimethyl-4- (2-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-7-methyl-4- (2-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 6, 7-trimethyl-4-(2-naphthyl)indenyl)zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-7-methyl4-(2-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 6, 7-trimethyl-4- (2-naphthyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4- (9-phenanthryl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl-4- (9-phenanthryl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-7-methyl-4- (9-phenanthryl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 6, 7-trimethyl4-(9-phenanthryl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-7-methyl-4- (9-phenanthryl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 6, 7-trimethyl-4-(9-phenanthryl)indenyl)zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-7-methyl-4- (9-phenanthryl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 6, 7-trimethyl-4- (9-phenanthryl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4- (p-trimethylsilylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl-4-(p-trimethylsilylphenyl)indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-7-methyl-4- (p-trimethylsilylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 6, 7-trimethyl-4-(p-trimethylsilylphenyl)indenyl)zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-7-methyl-4- (p-trimethylsilylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-n-butyl-5, 6, 7-trimethyl-4- (p-trimethylsilylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-7-methyl-4- (p-trimethylsilylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 6, 7-trimethyl4-(p-trimethylsilylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4- (3, 5-diphenylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl-4- (3, 5-diphenylphenyl) indenyl) zirconium dichloride, 1, 2-ethane (2-ethyl-7-methyl-4- (3, 5-diphenylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-ethyl-5, 6, 7-trimethyl-4- (3, 5-diphenylphenyl) indenyl) zirconium dichloride, 1, 2-ethane (2-n-butyl-7-methyl-4- (3, 5-diphenylphenyl) indenyl) zirconium dichloride,

1, 2-ethanediylbis (2-n-butyl-5, 6, 7-trimethyl-4- (3, 5-diphenylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-7-methyl-4- (3, 5-diphenylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2-isopropyl-5, 6, 7-trimethyl-4- (3, 5-diphenylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4- (2, 3, 4-trimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl-4- (2, 3, 4-trimethylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4- (p-sec-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl-4- (p-sec-butylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4- (p-cyclohexylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl-4- (p-cyclohexylphenyi) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2, 7-dimethyl-4- (p-isopropylphenyl) indenyl) zirconium dichloride, 1, 2-ethanediylbis (2,5, 6, 7-tetramethyl-4- (p-isopropylphenyl) indenyl) zirconium dichloride.

1, 2-ethanediylbis (2- (2- (5-methyl) thienyl)-7-methyl-4- (3, 5-diphenylphenyl) indenyl) zirconium dichlo- ride, 1, 2-ethanediylbis (2- (2- (5-methyl) furyl)-7-methyl-4- (p-tert-butylphenyl) indenyl) zirconium dichloride, In the homopolymerization of a-olefins, in particular polypropylene, the novel organometallic tran- sition metal compounds of the formula (I) give homopolymers, in particular isotactic polypropyle- ne, having a melting point higher than that of homopolymers prepared using the previously known metallocenes having a related substitution pattern.

The novel organometallic transition metal compounds of the formula (I) can be prepared by me- thods as described in WO 02/18397. In these methods, the organometallic transition metal com- pounds of the formula (I) are usually obtained as a mixture of diastereomers, with the racemic isomer giving highly isotactic polypropylene while the corresponding, undesired diastereomer, viz. the meso form, usually gives atactic polypropylene. The terms"meso"and"racemic"in the con- text of metallocenes are known and are defined, for example, in Rheingold et al. Organometallics 11 (1992), pages 1869-1876.

The organometallic transition metal compounds of the formula (I) can also be used as a mixture of diastereomers for the preparation of catalysts.

The invention further provides a biscyclopentadienyl ligand system of the formula (II)

or its double bond isomers, where the variables R', R2, R3, R4, R5 and Z are as defined in formula (I).

The double bond isomers of the compound of the formula (II) result from a formal shift of one of the double bonds in the two five-membered rings.

Particular preference is given to a biscyclopentadienyl ligand system of the formula (II) or its dou- ble bond isomer where R1 is C1-C10-alkyl, R3 is hydrogen or a C1-C10-alkyl radical, R4 is hydrogen or a C1-C10-alkyl radical, R 5 is a C1-C10-alkyl radical, Z is CH2-CH2 and R2 is as defined in formula (I).

The substitution pattern of the biscyclopentadienyl ligand systems of the formula (II) is decisive for the particular polymerization properties of the organometallic transition metal compounds in which these biscyclopentadienyl ligand systems are present.

The invention further provides for the use of a biscyclopentadienyl ligand system of the formula (II) for preparing an organometallic transition metal compound, preferably for preparing an orga- nometallic transition metal compound containing an element of group 4 of the Periodic Table of the Elements, in particular zirconium.

The present invention therefore also provides a process for preparing an organometallic transition metal compound, which comprises reacting a biscyclopentadienyl ligand system of the formula (II) or a bisanion prepared therefrom with a transition metal compound. The usual procedure is firstly to doubly deprotonate a ligand system of the formula (II) by means of a base such as n- butyllithium and subsequently to react the product with a suitable transition metal source, for ex- ample zirconium tetrachloride. As an alternative, the uncharged biscyclopentadienyl ligand system of the formula (II) can also be reacted directly with a suitable transition metal source having stron- gly basic ligands, for example tetrakis (dimethylamino) zirconium.

The novel organometallic transition metal compounds of the formula (I) are highly active constitu- ents of catalysts for the polymerization of olefins, particularly in the presence of suitable cocata- lysts.

The present invention therefore also provides a catalyst system comprising at least one organo- metallic transition metal compound of the formula (I) and at least one cocatalyst.

The catalyst and the novel organometallic transition metal compound of the formula (I) together form a polymerization-active catalyst system in which the catalyst serves as cation-forming compound.

Suitable cation-forming compounds which are able to react with an organometallic transition metal compound according to the present invention to convert it into a cationic compound are, for ex- ample, compounds such as an aluminoxane, a strong uncharged Lewis acid, an ionic compound having a Lewis-acid cation or an ionic compound containing a Bronsted acid as cation. In the case of metallocene complexes as organometallic transition metal compound, the cation-forming com- pounds are frequently also referred to as compounds capable of forming metallocenium ions.

As aluminoxanes, it is possible to use, for example, the compounds described in WO 00/31090.

Particularly useful compounds of this type are open-chain or cyclic aluminoxane compounds of the formula (III) or (IV)

(111) (IV) where R'2 is a C,-C4-alkyl group, preferably a methyl or ethyl group, and m is an integer from 5 to 30, preferably from 10 to 25.

These oligomeric aluminoxane compounds are usually prepared by reacting a solution of trial- kylaluminum with water. In general, the oligomeric aluminoxane compounds obtained in this way are in the form of mixtures of both linear and cyclic chain molecules of different lengths, so that m is to be regarded as a mean. The aluminoxane compounds can also be present in admixture with other metal alkyls, preferably aluminum alkyls.

Furthermore, modified aluminoxanes in which some of the hydrocarbon radicals or hydrogen atoms have been replaced by alkoxy, aryloxy, siloxy or amide groups can also be used in place of the aluminoxane compounds of the formula (III) or (IV).

It has been found to be advantageous to use the novel organometallic transition metal compound of the formula (I) and the aluminoxane compounds in such amounts that the atomic ratio of alumi- num from the aluminoxane compounds to the transition metal from the organometallic transition metal compound is in the range from 10: 1 to 1000: 1, preferably in the range from 20: 1 to 500: 1 and in particular in the range from 30: 1 to 400: 1.

As strong, uncharged Lewis acids, preference is given to compounds of the formula (V) M2X'X2X3 (V) where M2 is an element of group 13 of the Periodic Table of the Elements, in particular B, Al or Ga, preferably B,

X1,X2 and X3 are each independently of one another hydrogen, C-C : 0-alkyl, C6-C, 5-aryl, alkylaryl, arylalkyl, haloalkyl or haloaryl each having from 1 to 10 carbon atoms in the alkyl radical and from 6 to 20 carbon atoms in the aryl radical or fluorine, chlorine, bromine or iodine, in particular haloaryl, preferably pentafluorophenyl.

Further examples of strong, uncharged Lewis acids are mentioned in WO 00/31090.

Particular preference is given to compounds of the formula (V) in which X', X2 and X3 are identi- cal, preferably tris (pentafluorophenyl) borane.

Strong uncharged Lewis acids which are suitable as cation-forming compounds also include the reaction products from the reaction of a boronic acid with two equivalents of a trialkylaluminum or the reaction products from the reaction of a trialkylaluminum with two equivalents of an acidic fluorinated, in particular perfluorinated, carbon compound such as pentafluorophenol or bis (pentafluorophenyl) borinic acid.

Suitable ionic compounds having Lewis-acid cations include salt-like compounds of the cation of the formula (VI) [(Ya+)Q1Q2...Qz]d+ (VI) where Y is an element of groups 1 to 16 of the Periodic Table of the Elements, Q1 to Qz is a singly negatively charged group such as C-C28-alkyl, C6-C5-aryl, alkylaryl, arylalkyl, haloalkyl, haloaryl each having from 6 to 20 carbon atoms in the aryl radical and from 1 to 28 carbon atoms in the alkyl radical, C3-C, o-cycloalkyl which may bear Cl-Cio-alkyl groups as substituents, halogen, C,-C28-alkoxy, C6-C, 5-aryloxy, silyl or mercaptyl groups, a is an integer from 1 to 6 and z is an integer from 0 to 5, and d corresponds to the difference a-z, but d is greater than or equal to 1.

Particularly useful cations of this type are carbonium cations, oxonium cations and sulfonium ca- tions and also cationic transition metal complexes. Particular mention may be made of the triphe-

nylmethyl cation, the silver cation and the 1, 1'-dimethylferrocenyl cation. They preferably have noncoordinating counterions, in particular boron compounds as are also mentioned in WO 91/09882, preferably tetrakis (pentafluorophenyl) borate.

Salts having noncoordinating anions can also be prepared by combining a boron or aluminum compound, e. g. an aluminum alkyl, with a second compound which can react to link two or more boron or aluminum atoms, e. g. water, and a third compound which forms an ionizing ionic com- pound with the boron or aluminum compound, e. g. triphenylchloromethane. In addition, a fourth compound which likewise reacts with the boron or aluminum compound, e. g. pentafluorophenol, may be added.

Ionic compounds containing Brönsted acids as cations likewise preferably have noncoordinating counterions. As Bronsted acid, particular preference is given to protonated amine or aniline deri- vatives. Preferred cations are N, N-dimethylanilinium, N, N-dimethylcyclohexylammonium and N, N- dimethylbenzylammonium and also derivatives of the latter two.

Preferred ionic compounds as cation-forming compounds are, in particular, N, N-dimethylanilinium tetrakis (pentafluorophenyl) borate, N, N-dimethylcyclohexylammonium tetra- kis (pentafluorophenyl) borate or N, N-dimethylbenzylammonium tetrakis (pentafluorophenyl) borate.

It is also possible for two or more borate anions to be joined to one another, as in the dianion [(C6F5) 2B-C6F4-B (C6Fs) 2] 2-, or the borate anion can be bound to the surface of a support particle via a bridge having a suitable functional group.

Further suitable cation-forming compounds are listed in WO 00/31090.

The amount'of strong, uncharged Lewis acids, ionic compounds having Lewis-acid cations or ionic compounds containing Bronsted acids as cations is usually from 0.1 to 20 equivalents, pre- ferably from 1 to 10 equivalents, per equivalent of the novel organometallic transition metal com- pound of the formula (I).

Further cation-forming compounds include boron-aluminum compounds such as di [bis (pentafluorophenyl) boroxy] methylalane. Boron-aluminum compounds of this type are disclo- sed, for example, in WO 99/06414.

It is also possible to use mixtures of all the abovementioned cation-forming compounds. Preferred mixtures comprise aluminoxanes, in particular methylaluminoxane, and an ionic compound, in particular one containing the tetrakis (pentafluorophenyl) borate anion, and/or a strong uncharged Lewis acid, in particular tris (pentafluorophenyl) borane.

Preference is given to using both the novel organometallic transition metal compound of the for- mula (I) and the cation-forming compounds in a solvent, preferably an aromatic hydrocarbon ha- ving from 6 to 20 carbon atoms, in particular xylenes and toluene.

The catalyst may further comprise a metal compound of the formula (VII) Mus (R13)r(R14)s(R15)t (VII) where M3 is an alkali metal, an alkaline earth metal or a metal of group 13 of the Periodic Ta- ble, i. e. boron, aluminum, gallium, indium or thallium, R'3 is hydrogen, C-C, o-alkyl, C6-C, 5-aryl, alkylaryl or arylalkyl each having from 1 to 10 carbon atoms in the alkyl part and from 6 to 20 carbon atoms in the aryl part, R'4 and R'5 are identical or different and are each hydrogen, halogen, C1-C10-alkyl, C6-C15-aryl, alkylaryl, arylalkyl or alkoxy each having from 1 to 10 carbon atoms in the alkyl radi- cal and from 6 to 20 carbon atoms in the aryl radical, is an integer from 1 to 3, and s and t are integers from 0 to 2, where the sum r+s+t corresponds to the valence of M3, with the metal compound of the formula (VII) usually not being identical to the cation-forming compound. It is also possible to use mixtures of various metal compounds of the formula (VII).

Among the metal compounds of the formula (VII), preference is given to those in which M3 is lithium, magnesium or aluminum and R'4 and R'5 are each C,-C, 0-alkyl.

Particularly preferred metal compounds of the formula (VII) are n-butyllithium, n-butyl-n- octylmagnesium, n-butyl-n-heptylmagnesium, tri-n-hexylaluminum, triisobutylaluminum, triethyl- luminum and trimethylaluminum and mixtures thereof.

If a metal compound of the formula (VII) is used, it is preferably present in the catalyst in such an amount that the molar ratio of M3 from formula (VII) to transition metal M1 from the novel organo- metallic transition metal compound of the formula (I) is from 800: 1 to 1: 1, in particular from 200: 1 to 2: 1.

Particular preference is given to a catalyst system comprising a novel organometallic transition metal compound of the formula (I) and at least one catalyst as cation-forming compound and further comprising a support.

To obtain such a supported catalyst system, the unsupported catalyst system can be reacted with a support. The order in which the support, the organometallic transition metal compound accor- ding to the invention and the catalyst are combined is in principle immaterial. The organometal- lic transition metal compound of the invention and the catalyst can be immobilized indepen- dently of one another or simultaneously. After the individual process steps, the solid can be washed with suitable inert solvents such as aliphatic or aromatic hydrocarbons.

As support, preference is given to using finely divided supports which can be any organic or inor- ganic, inert solids. In particular, the support can be a porous solid such as talc, a sheet silicate, an inorganic oxide or a finely divided polymer powder (e. g. polyolefin).

Suitable inorganic oxides may be found among the oxides of the elements of groups 2,3, 4,5, 13, 14,15 and 16 of the Periodic Table of the Elements. Examples of oxides preferred as supports include silicon dioxide, aluminum oxide and mixed oxides of the elements calcium, aluminum, silicon, magnesium and titanium and also corresponding oxide mixtures. Further inorganic oxides which can be used alone or in combination with the abovementioned preferred oxidic supports are, for example, MgO, Zur02, TiO2 or B203. A preferred mixed oxide is, for example, calcined hy- drotalcite.

The support materials used preferably have a specific surface area in the range from 10 to 1000 m2/g, a pore volume in the range from 0.1 to 5 ml/g and a mean particle size of from 1 to 500 um.

Preference is given to supports having a specific surface area in the range from 50 to 500 m2/g, a pore volume in the range from 0.5 to 3.5 ml/g and a mean particle size in the range from 5 to 350 urn. Particular preference is given to supports having a specific surface area in the range from 200 to 400 m2/g, a pore volume in the range from 0.8 to 3.0 ml/g and a mean particle size of from 10 to 100 urn.

The inorganic support can be subjected to a thermal treatment, e. g. to remove adsorbed water.

Such a drying treatment is generally carried out at from 80 to 300°C, preferably from 100 to 200°C, with drying at from 100 to 200°C preferably being carried out under reduced pressure and/or under a blanket of inert gas (e. g. nitrogen), or the inorganic support can be calcined at

from 200 to 1000°C to generate, if appropriate, the desired structure of the solid and/or the desi- red OH concentration on the surface. The support can also be treated chemically using customary desiccants such as metal alkyls, preferably aluminum alkyls, chlorosilanes or SiC14 or else me- thylaluminoxane. Suitable treatment methods are described, for example, in WO 00/31090.

The inorganic support material can also be chemically modified. For example, treatment of silica gel with (NH4) 2SiF6 leads to fluorination of the silica gel surface and treatment of silica gels with silanes containing nitrogen-, fluorine-or sulfur-containing groups leads to correspondingly modi- fied silica gel surfaces.

Organic support materials such as finely divided polyolefin powders (e. g. polyethylene, polypro- pylene or polystyrene) can also be used and should preferably likewise be freed of adhering moisture, solvent residues or other impurities by appropriate purification and drying operations prior to use. It is also possible to use functionalized polymer supports, e. g. supports based on polystyrenes, via whose functional groups, for example ammonium or hydroxy groups, at least one of the catalyst components can be immobilized.

In a preferred embodiment of the preparation of the supported catalyst system, at least one of the novel organometallic transition metal compounds of the formula (I) is brought into contact with at least one catalyst as cation-forming compound in a suitable solvent, preferably giving a soluble reaction product, an adduct or a mixture.

The preparation obtained in this way is then mixed with the dehydrated or passivated support material, the solvent is removed and the resulting supported organometallic transition metal com- pound catalyst system is dried to ensure that all or most of the solvent is removed from the pores of the support material. The supported catalyst is obtained as a free-flowing powder. Examples of the industrial implementation of the above process are described in WO 96/00243, WO 98/40419 or WO 00/05277.

In a further preferred embodiment, the cation-forming compound is firstly applied to the support component and this supported cation-forming compound is subsequently brought into contact with the organometallic transition metal compound of the present invention.

Catalyst systems of importance therefore likewise include combinations obtained by combining the following components: 1 st component: at least one defined boron or aluminum compound, 2nd component: at least one uncharged compound which possesses at least one acidic hydro- gen atom, 3rd component: at least one support, preferably an inorganic oxidic support,

and optionally as 4th component: a base, preferably an organic nitrogen-containing base, for example an amine, an aniline derivative or a nitrogen heterocycle.

The boron or aluminum compound used in the preparation of these supported cocatalysts are preferably compounds of the formula (VIII) where R16 are identical or different and are each hydrogen, halogen, C-C20-alkyl, C,-C20- haloalkyl, C,-C, o-alkoxy, C6-C20-aryl, C6-C2o-haloaryl, C6-C2o-aryloxy, C7-C4o-arylalkyl, C7-C4o-haloarylalkyl, C7-C4o-alkylaryl, C7-C4o-haloalkylaryl or an OSiR173 group, whe- re R17 are identical or different and are each hydrogen, halogen, C1-C20-alkyl, C1-C20- haloalkyl, C,-C, o-alkoxy, C6-C20-aryl, C6-Czo-haloaryl, C6-C2o-aryloxy, C7-C4o-arylalkyl, C7-C40-haloarylalkyl, C7-C40-alkylaryl, C7-C40-haloalkylaryl, preferably hydrogen, C,- CB-alkyl or C7-C20-arylalkyl, and M4 is boron or aluminum, preferably aluminum.

Particularly preferred compounds of the formula (VIII) are trimethylaluminum, triethylaluminum and triisobutylaluminum.

The uncharged compounds which have at least one acidic hydrogen atom and can react with compounds of the formula (VIII) are preferably compounds of the formula (IX), (X) or (XI), where R18 are identical or different and are each hydrogen, halogen, a boron-free C-C40 group such as C1-C20-alkyl, C1-C20-haloalkyl, C1-C10-alkoxy, C6-C20-aryl, C6-C20-haloaryl, C6-C2o-aryloxy, C7-C40-arylalkyl, C7-C4o-haloarylalkyl, C7-C4o-alkylaryl, C7-C40- haloalkylaryl, an Si (R2°) 3 group or a CH (SiR2°3) 2 group, where

R20 is a boron-free Ci-C40 group such as C,-Czo-alkyl, C,-C20-haloalkyl, C,-C, o-alkoxy, C6-C2o-aryl, C6-Czo-haloaryl, C6-C2o-aryloxy, C7-C4o-arylalkyl, C7-C4o-haloarylalkyl, C7- C40-alkylaryl, C7-C40-haloalkylaryl, and R'9 is a divalent C1-C40 group such as C1-C20-alkylene, C,-C20-haloalkylene, C6-C20- arylen, C6-C20-haloarylene, C7-C40-arylalkylene, C7C-40-haloarylalkylene, C7-C40- alkylarylene, C7-C4o-haloalkylarylene, D is an element of group 16 of the Periodic Table of the Elements or an NR 21 group, where R21 is hydrogen or a C1-C20-hydrocarbon radical such as C,-C20-alkyl or C6- C20-aryl, preferably oxygen, and h is 1 or 2.

Suitable compounds of the formula (IX) are water, alcohols, phenol derivatives, thiophenol deriva- tives or aniline derivatives, with halogenated and especially perfluorinated alcohols and phenols being of particular importance. Examples of particularly useful compounds are pentafluorophenol, 1,1-bis (pentafluorophenyl) methanol and 4-hydroxy-2, 2', 3,3', 4,4', 5,5', 6, 6'-nonafluorobiphenyl.

Suitable compounds of the formula (X) include boronic acids and borinic acids, in particular bori- nic acids bearing perfluorinated aryl radicals, for example (C6F5) 2BOH.

Suitable compounds of the formula (XI) include dihydroxy compounds in which the divalent car- bon-containing group is preferably halogenated, in particular perfluorinated. An example of such a compound is 4,4'-dihydroxy-2, 2', 3,3', 5,5', 6, 6'-octafluorobiphenyl hydrate.

Examples of combinations of compounds of the formula (VIII) with compounds of the formula (IX) or (XI) are trimethylaluminum/pentafluorophenol, trimethylaluminum/1- bis (pentafluorophenyl)methanol, trimethylaluminum/4-hydroxy-2, 2', 3,3', 4,4', 5,5', 6,6'- nonafluorobiphenyl, triethylaluminum/pentafluorophenol and triisobutyl- aluminum/pentafluorophenol and triethylaluminum/4,4'-dihydroxy-2, 2', 3,3', 5, 5', 6,6'- octafluorobiphenyl hydrate, with, for example, reaction products of the following type being able to be formed.

Examples of reaction products from the reaction of at least one compound of the formula (VIII) with at least one compound of the formula (X) are: The order in which the components are combined is in principle immaterial.

If desired, the reaction products from the reaction of at least one compound of the formula (VIIl) with at least one compound of the formula (IX), (X) or (XI) and optionally the organic nitrogen base are additionally combined with an organometallic compound of the formula (III), (IV), (V) and/or (VII) in order to then form the supported catalyst system on being combined with the support.

In a preferred embodiment, the 1st component, e. g. compounds of the formula (VIII), and the 2nd component, e. g. compounds of the formula (IX), (X) or (XI), and also a support as 3rd component and a base as 4th component are combined separately and subsequently reacted with one another, with the reaction preferably taking place in an inert solvent or suspension medium. The supported catalyst formed can be freed of the inert solvent or suspension medium before it is reacted with the novel organometallic transition metal compound of the formula (I) and, if desired, a metal compound of the formula (VII) to form the catalyst system.

It is also possible firstly to prepolymerize the catalyst solid with a-olefins, preferably linear C2-C, O- 1-alkenes, and in particular ethylene or propylene, and then to use the resulting prepolymerized catalyst solid in the actual polymerization. The mass ratio of catalyst solid used in the prepolyme- rization to monomer polymerized onto it is usually in the range from 1: 0.1 to 1: 200.

Furthermore, a small amount of an olefin, preferably a a-olefin, for example vinylcyclohexane, styrene or phenyldimethylvinylsilane, as modifying component, an antistatic or a suitable inert compound such as a wax or oil can be added as additive during or after the preparation of the supported catalyst system. The molar ratio of additives to organometallic transition metal com- pound according to the present invention is usually from 1: 1000 to 1000: 1, preferably from 1: 5 to 20: 1.

The present invention also provides a process for preparing polyolefins by polymerization, i. e. homopolymerization or copolymerization, of at least one olefin in the presence of a catalyst sy- stem comprising at least one of the novel organometallic transition metal compounds of the for- mula (I).

In general, the catalyst system is used together with a further metal compound of the formula (VII), which may be different from the metal compound or compounds of the formula (Vil) used in the preparation of the catalyst system, for the polymerization or copolymerization of olefins. The further metal compound is generally added to the monomer or the suspension medium and ser- ves to free the monomer of substances which can adversely affect the catalyst activity. It is also possible for one or more additional cation-forming compounds to be added to the catalyst system in the polymerization process.

The olefins can be functionalized, olefinic unsaturated compounds such as esters or amide deri- vatives of acrylic or methacrylic acid, for example acrylates, methacrylates or acrylonitrile, or be nonpolar olefinic compounds, including aryl-substituted a-olefins.

Preference is given to polymerizing olefins of the formula Rm-CH=CH=R", where Rm and R"are identical or different and are each hydrogen or a carbon-containing radical having from 1 to 20 carbon atoms, in particular from 1 to 10 carbon atoms, or Rm and Rn together with the atoms con- necting them can form one or more rings.

Examples of such olefins are 1-olefins having from 2 to 40, preferably from 2 to 10, carbon atoms, e. g. ethylene, propylene, 1-butene, 1-pentene, 1-hexene, 1-heptene, 1-octene, 1-decene or 4- methyl-1-pentene or unsubstituted or substituted vinylaromatic compounds such as styrene and styrene derivatives, or dienes such as 1,3-butadiene, 1,4-hexadiene, 1,7-octadiene, 5-ethylidene- 2-norbornene, norbornadiene, ethylnorbornadiene or cyclic olefins such as norbornene, tetracy- clododecene or methyinorbornene.

The catalyst system of the present invention is particularly preferably used for homopolymerizing propylene or ethylene or copolymerizing ethylene with C3-C8-a-olefins such as propylene, 1- butene, 1-pentene, 1-hexene and/or 1-octene and/or cyclic olefins such as norbornene and/or dienes having from 4 to 20 carbon atoms, e. g. 1,4-hexadiene, norbornadiene, ethylidene- norbornene or ethylnorbornadiene or, particularly preferably, copolymerizing propylene with ethy- lene and/or 1-butene. Examples of copolymers obtained in this way are propylene-ethylene, pro- pylene-1-butene, ethylene-1-butene, ethylene-1-hexene and ethylene-1-octene copolymers, and ethylene-propylene-ethylidenenorbornene and ethylene-propylene-1, 4-hexadiene terpolymers.

The polymerization can be carried out in a known manner in bulk, in suspension, in the gas phase or in a supercritical medium in the customary reactors used for the polymerization of olefins. It can

be carried out batchwise or preferably continuously in one or more stages. Solution processes, suspension processes, stirred gas-phase processes or gas-phase fluidized-bed processes are all possible. As solvent or suspension medium, it is possible to use inert hydrocarbons, for example isobutane, or else the monomers themselves.

The polymerization can be carried out at from-60 to 300°C and pressures in the range from 0.5 to 3000 bar. Preference is given to temperatures in the range from 50 to 200°C, in particular from 60 to 100°C and pressures in the range from 5 to 100 bar, in particular from 15 to 70 bar. The mean residence times are usually from 0.5 to 5 hours, preferably from 0.5 to 3 hours. Hydrogen can be used in the polymerization as molar mass regulator and/or to increase the activity. It is also possi- ble to use customary additives such as antistatics. The catalyst system of the present invention can be used directly for the polymerization, i. e. it is introduced in pure form into the polymerization system, or it is admixed with inert components such as paraffins, oils or waxes in order to improve the meterability.

The novel organometallic transition metal compounds of the formula (I) and the catalyst systems in which they are present are especially useful for preparing propylene homopolymers having high melting points.

The polymers prepared by the process of the present invention are, in particular, suitable for pro- ducing strong, hard and stiff shaped bodies such as fibers, filaments, injection-molded parts, films, sheets or large hollow bodies (e. g. pipes).

The invention is illustrated by the following examples which do not, however, restrict the invention.

Examples General The preparation and handling of the organometallic compounds and their use as catalyst compo- nents were carried out in the absence of air and moisture under argon (Schlenk technique or glove box). All solvents required were purged with argon and dried over molecular sieves before use.

Determination of the melting point: The melting point Tm was determined by means of DSC measurement in accordance with ISO standard 3146 in a first heating phase at a heating rate of 20°C per minute to 200°C, a dynamic crystallization at a cooling rate of 20°C per minute to 25°C and a second heating phase at a hea- ting rate of 20°C per minute to 200°C once again. The melting point was then the temperature at which the curves of the enthalpy versus the temperature measured in the second heating phase displayed a maximum.

Gel permeation chromatography: Gel permeation chromatography (GPC) was carried out at 145°C in 1,2, 4-trichlorobenzene using a Waters 150C GPC apparatus. The data were evaluated using the software Win-GPC from HS- Entwicklungsgesellschaft fur wissenschaftliche Hard-und Software mbH, Ober-Hilbersheim. The columns were calibrated by means of polypropylene standards having molar masses of from 100 to 10'g/mol. The mass average (Mw) and number average (Mn) of the molar masses of the poly- mers were determined. The Q value is the ratio of mass average (Mw) to number average (Mn).

Example 1 Preparation of 1, 2-ethanediylbis (2, 7-dimethyl-4- (4'-tert-butylphenyl) indenyl) zirconium dichloride (1) a) Preparation of 2-chloro-5-methylpropiophenone (1a) 43.8 g (329 mmol) of aluminum chloride and 34.66 g (274 mmol) of 4-chlorotoluene were placed in a reaction vessel and admixed with 26.6 g (287 mmol) of propionyl chloride. Moderate HCI gas evolution occurred. The reaction mixture was stirred at 50°C for four hours and was subsequently poured into a mixture of 350 ml of ice water and 35 ml of concentrated hydrochloric acid. The aqueous phase was extracted twice with 200 ml each time of methylene chloride. The combined organic phases were washed with 200 ml of water, 200 ml of NaHCO3 solution and NaCI solution and dried over MgS04. Removal of the solvent and drying in an oil pump vacuum gave 47.06 g of (1 a).

'H-NMR (400 MHz, CDC13) : 7.60-7. 10 (m, 3H, arom-H), 2.94 (m, 2H, CH2-H), 2.32 (s, 3H, CH3), 1.18 (t, 3H, Chus). b) Preparation of 2-chloro-5-methylmethacrylophenone (1b) 47.0 g (257 mmol) of 2-chloro-7-methylpropiophenone (1a) and 21.2 ml (765 mmol) of aqueous formaldehyde solution were placed in a reaction vessel and a solution of 10.3 g (257 mmol) of NaOH in 515 ml of water was added over a period of 30 minutes. The reaction mixture was stirred vigorously at 40°C for two hours. The phases were subsequently separated and the aqueous phase was extracted twice with 200 ml of methylene chloride. The combined organic phases were washed with 200 ml of dilute hydrochloric acid and subsequently dried over MgS04. Removal of the solvent and drying in an oil pump vacuum gave 47.37 g of (1b).

'H-NMR (400 MHz, CDC13) : 7.39-7. 05 (m, 3H, arom-H), 5.97 ; 5.57 (dd, 2H, CH2-H), 2.31 (s, 3H, CH3), 2.02 (s, 3H, CH3). c) Preparation of 7-chloro-2, 4-methyl-1-indanone (1c) 349 g of concentrated sulfuric acid were placed in a reaction vessel at 65°C and 47.3 g (243 mmol) of 2-chloro-5-methylmethacrylophenone (1 b) were added dropwise over a period of two hours, the mixture was stirred at 65°C for another 30 minutes and was then cooled to room tem- perature. The reaction mixture was poured into 800 g of ice water. The brownish green suspensi- on formed was extracted three times with 300 ml each time of diethyl ether. The combined orga- nic phases were washed with 300 ml of NaHCO3 solution, 300 ml of water and 300 ml of satura- ted NaCI solution and subsequently dried over MgS04. Removal of the solvent and drying in an oil pump vacuum gave 39.29 g of (1c).

'H-NMR (400 MHz, CDC13) : 7.50-7. 00 (m, 2H, arom-H), 3. 32, 3.21 (dd, 2H, CH2-H), 2.70 (m, 1H, CH-H), 2.28 (s, 3H, CH3), 1.30 (d, 3H, CH3). d) Preparation of 2, 4-dimethyl-7- (4'-tert-butylphenyl)-1-indanone (1d) 13.4 g (68.8 mmol) of 7-chloro-2, 4-dimethyl-1-indanone (1c), 14.71 g (82.6 mmol) of 4-tert- butylphenylboronic acid, 16.05 g (151 mmol) of sodium carbonate, 188 ml of ethylene glycol and 30.7 ml of water were placed in a reaction vessel under a protective gas atmosphere and the mixture was heated to 80°C. While stirring vigorously, a freshly prepared catalyst solution compri- sing 77 mg (0.343 mmol) of palladium acetate and 1.7 ml (1.01 mmol) of an aqueous TPPTS solution (0.6 molar) in 25 ml of water was added to the reaction components and the reaction mixture was refluxed for 3 hours until the reaction was complete. After cooling to room tempera- ture, the ethylene glycol phase was extracted three times with a total of 900 ml of toluene. The combined toluene phases were washed twice with a total of 250 ml of sodium chloride solution

and dried over 150 g of sodium sulfate. Removal of the solvent and drying of the residue and subsequent distillation in an oil pump vacuum gave 18.59 g of (1d).

'H-NMR (400 MHz, CDC13) : 7.39-7. 19 (m, 6H, arom-H), 3.30 (dd, 1 H, CH2-H), 2.68 (m, 1H, CH- H), 2.60 (dd, 1 H, CH2-H), 2.35 (s, 3H, CH3), 1.34 (s, 9H, tert-butyl-H), 1.27 (d, 3H, CH3). e) Preparation of 2, 7-dimethyl-4- (4'-tert-butylphenyl) indene (1e) 2.09 g (55.3 mmol) of sodium borohydride and 18.59 g (55.3 mmol) of 2, 4-dimethyl-7- (4'-tert- butylphenyl)-1-indanone (1d) together with 51 ml of toluene were placed in a reaction vessel. At 50°C, 9.8 ml of methanol were slowly added and the reaction mixture was stirred at 50°C for 3 hours. After cooling to room temperature, 35 ml of 2N sulfuric acid were added and the mixture was stirred for 30 minutes. After phase separation, the organic phase was washed twice with a total of 60 ml of 2N sulfuric acid, most of the solvent was removed and the residue was taken up in 200 ml of toluene and admixed with 0.2 g of p-toluenesulfonic acid. Water was distilled off from this reaction mixture with the aid of a water separator by refluxing for 1.5 hours until the reaction was complete. The reaction mixture was washed once with 100 ml of saturated sodium hydrogen carbonate solution and dried over magnesium sulfate. After removal of the solvent, the residue was dried in an oil pump vacuum. This gave 16.8 g of the desired product (1e).

'H-NMR (400 MHz, CDCI3) : 7.50-6. 97 (m, 6H, arom-H), 6.70 (s, 1 H, olefin-H), 3.24 (s, 2H, CH2- H), 2.35 (s, 3H, CH3), 2.15 (s, 3H, CH3), 1.36 (s, 9H, tert-butyl-H).

Preparation of 1,2-bis (2, 7-dimethyl-4- (4'-tert-butylphenyl)-1-indenyl) ethane (1f) 5.4 g (19.54 mmol, 92%-pure by GC) of 2, 7-dimethyl-4- (4'-tert-butylphenyl) indene (1e) together with 25 mi of tetrahydrofuran (THF) were placed in a reaction vessel and admixed at 0°C with 7.8 ml of an n-butyllithium solution (2.5 M in toluene), resulting in the temperature rising to 10°C. The reaction mixture was stirred at room temperature for one hour and was subsequently added dropwise to a solution of 3.0 g (9.3 mmol) of 1,2-bis (trifluoromethylsulfonyloxy) ethane in 3.5 ml of THF at-40°C. The reaction mixture obtained was stirred at-20°C for one hour and was subse- quently stirred overnight at room temperature. The solvent was then removed under reduced pressure and the residue was taken up in 100 ml of toluene. The organic phase was washed firstly with 50 ml of a 2N sodium hydroxide solution and then four times with 50 mi each time of water. The organic phase was dried over sodium sulfate and the solvent was removed under re- duced pressure. This gave 7.4 g of crude product which was purified by column chromatography on silica gel, giving a clean fraction of the product (1f) in a yield of 1.9 g.

GC-MS M+=578

g) Preparation of 1, 2-ethanediylbis (2, 7-dimethyl-4- (4'-tert-butylphenyl) indenyl) zirconium dichloride (1) 1. 8 g (3.1 mmol) of ligand (1f) together with 18 ml of diethyl ether were placed in a reaction vessel and admixed at 0°C with 4.2 ml of a solution of tert-butyllithium in pentane (1.5 M in pentane). A further 10 ml of diethyl ether were added to the yellow suspension formed and the suspension was stirred overnight at room temperature. At 0°C, 1.10 g (3.42 mmol) of zirconium tetrachloride- dimethoxyethane complex were added. After warming to room temperature, 10 ml of diethyl ether were added and the reaction mixture was stirred at room temperature for 8 hours. The solvent was removed completely under reduced pressure and the residue, viz. 2.5 g of crude complex, was admixed with 150 ml of toluene at 80°C. After filtration through a layer of Celite, the toluene solution was evaporated to about 8 ml and admixed with 5 ml of n-heptane. A solid precipitated at - 30°C and this was filtered off, analyzed by NMR and then discarded. The filtrate was once again evaporated completely, dissolved in 30 ml of toluene/5 mi of heptane at 100°C and an insoluble residue was filtered off once again. The clear filtrate was evaporated to about 15 ml, admixed with 10 ml of heptane and stored at-30°C for one day. The crystals which had precipitated were filte- red off via a G3 frit, washed with 1 mi of heptane and dried under reduced pressure. This gave 0.2 g of the complex (1).

'H-NMR (400 MHz, Ceci3) : 1.30, 1.32 (18H, t-Bu-H), 2.19 (6H, Me-H), 2.34 (6H, Me-H), 3. 7, 4.1 (2 x 4H), 6.6 (2H), 6.9-7. 8 (12H, aromat. H) Example 2 0.206 mmol of 1,2-Et (2, 7-Me2-4- ! Bu-Ph)-1-lnd) 2ZrCI2 (1) from example 1 were added at room temperature to 4.33 mmol of MAO (30% strength by weight solution in toluene, manufactured by Albemarle). The solution was allowed to stand overnight at room temperature and was subse- quently diluted with 10.9 ml of toluene. The diluted solution was carefully added to 10 g of silica (Sylopol 948 calcined at 600°C, manufactured by Grace). Particular attention was paid to ensu- ring that the colored solution was distributed uniformly over the support material. After 10 minutes, most of the solvent was removed from the catalyst suspension in an oil pump vacuum. The free- flowing catalyst powder obtained was dried in an oil pump vacuum until the volatiles content of the catalyst solid had been reduced to below 5% by weight.

Comparative example A Example 2 was repeated, but 1,2-Et (2-Me-4- (p-'Bu-Ph)-1-ind) 2ZrCI2 was used in place of the me- tallocene from example 1 for preparing the catalyst in this experiment.

Comparative example B Example 2 was repeated, but 1,2-Et (2,4, 7-Me3-1-ind) 2ZrCI2 was used in place of the metallocene from example 1 for preparing the catalyst in this experiment.

Example 3 Homopolymerization of propene The homopolymerization was carried out in a 51 reactor charged with 31 of liquid propene. The reactor had been made inert by means of nitrogen before being charged. 2.4 ml of a 20% strength by weight solution of triethylaluminum in Exsol (from Witco) were added to the propene in the reactor and the mixture was stirred at 30°C for 15 minutes. A suspension of 500 mg of the cata- lyst prepared in example 2 in 20 ml of Exsol was introduced into the reactor. The reactor tempe- rature was increased to 65°C and the reactor was maintained at this temperature for 60 minutes.

The polymerization was stopped by venting the reactor. The polymer was dried overnight under reduced pressure. The results of the polymerization and the results of the analysis of the polymer are shown in the table below.

Comparative example C Homopolymerization of propene The homopolymerization was carried out in a 2 I reactor charged with 1. 51 of liquid propene. The reactor had been made inert by means of nitrogen before being charged. 1.7 ml of a 20% strength by weight solution of triethylaluminum in Exsol (from Witco) were introduced into the reactor and the mixture was stirred at 30°C for 15 minutes. A suspension of 600 mg of the catalyst prepared in comparative example A in 20 ml of Exsol was introduced into the reactor. The reactor tempe- rature was increased to 65°C and the reactor was maintained at this temperature for 60 minutes.

The polymerization was stopped by venting the reactor. The polymer was dried overnight under reduced pressure.

Comparative example D Homopolymerization of propene The polymerization of comparative example C was repeated, but 930 mg of the catalyst prepared in comparative example B were used as catalyst in this experiment.

Table Polymerization results and results of the analysis of the polymers

Activity Mw Mw/Mn Tm [kg/g*h] [g/mol] [°C] Example 3 0.82 335 900 3. 0 156. 4 Comparative example C 0. 40 315 100 4. 2 153. 7 Comparative example D 0. 27 400 000 2. 7 153. 9 Units and abbreviations: melting point (Tm) : °C ; weight average molar mass (Mw) : glmol ; polydis- persity: Q=Mw/Mn ; activity: mass of polymer/ (mass of catalyst * polymerization time in hours)