Login| Sign Up| Help| Contact|

Patent Searching and Data


Title:
PARTIALLY FLUORINATED POLYMERS
Document Type and Number:
WIPO Patent Application WO/1997/045464
Kind Code:
A1
Abstract:
Selected partially fluorinated 'alpha','omega'-dienes bearing -CF3 substitution can be free radically (co)polymerized to form polymers in which cyclic structures are present. The polymers are useful for films, coating and molded parts.

Inventors:
YANG ZHEN-YU (US)
Application Number:
PCT/US1997/009121
Publication Date:
December 04, 1997
Filing Date:
May 27, 1997
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
DU PONT (US)
YANG ZHEN YU (US)
International Classes:
C07C17/278; C07C17/361; C07C21/19; C07C67/293; C08F14/18; (IPC1-7): C08F14/18; C07C21/19
Domestic Patent References:
WO1996010047A11996-04-04
Other References:
CHEMICAL ABSTRACTS, vol. 83, no. 21, 24 November 1975, Columbus, Ohio, US; abstract no. 178192, XP002040125
JOURNAL OF POLYMER SCIENCE PART A-2, vol. 7, 1969, pages 601 - 608, XP002040124
Download PDF:
Claims:
CLAIMS
1. What is claimed is: A polymer, comprising, one or more of the repeat units (IA), (IB), or <IQ or one or more of the repeat units (HA), (IIB), or ^C— CH2 F2C ^CH2 — CF. CF2 CF CF3 (πc), or both.
2. The polymer as recited in Claim 1 which comprises one or more of repeat units (IA), (IB) or (IC).
3. The polymer as recited in Claim 1 which comprises one or more of repeat units (IIA) , (UB) or (IIC) .
4. The polymer as recited in Claim 1 which is a copolymer.
5. The polymer as recited in Claim 4 wherein a comonomer is one or more of tetrafluoroethylene, hexafluoropropylene, vinylidene fluoride, perfluoro(methyl vinyl ether), perfluoro(propyl vinyl ether), methyl vinyl ether, propylene, ethylene, chlorotnfluoroethylene, or perfluoro(2,2dimethyll,3 dioxole).
6. The polymer as recited in Claim 4 wherein a comonomer is one or more of tetrafluoroethylene, perfluoro(propyl vinyl ether) or perfluoro (2,2dimethyll,3dioxole).
7. The polymer as recited in Claim 4 wherein a comonomer is tetrafluoroethylene .
8. A compound of the formula CF2 = CFCF2CF(CF3)CH2CH = CH2 or CF2=CFCF(CF3)CF2CH2CH=CH2.
9. The compound as recited in Claim 8 of the formula CF2=CFCF2CF(CF3)CH2CH = CH2.
10. The compound as recited in Claim 8 of the formula CF2 = CFCF(CF3)CF2CH2CH = CH2.
Description:
TITLE PARTIALLY FLUORINATED POLYMERS FIELD OF THE INVENTION This invention concerns polymers made from selected partially fluorinated dienes, in which the repeat units are cycloaliphatic. Also disclosed are novel monomers for making these polymers .

TECHNICAL BACKGROUND Free radical polymerizations which include nonconjugated dienes (and bis vinyl ethers) usually yield polymers which are crosslinked because of the "separate" reaction of each of the double bonds with the free radicals in the reactions. However, it is known that in some instances perfluorinated or partially fluorinated compounds containing two such double bonds do not form crosslinked polymers, but form polymers containing cyclic structures.

U.S. Patents 5,326,917, 5,313,003, 5,260,492, 4,897,457, J. E. Fearn, et al., J. Polym. Sci. A-1, vol. 4, p. 131-140 (1966) and D. W. Brown, et al., J. Polym. Sci. A-2, vol. 7, p. 601-608 (1969) all describe the polymerization of paπially or fully fluorinated compounds containing two double bonds which give polymers having cyclic structures. The instant monomers and polymers are not disclosed therein. D. J. Burton, et al., J. Fluorine Chem., vol. 50, p. 257-264 (1990) describe the synthesis of 1 , 1,2,3, 3-pentafluoro-l ,5-heaxdiene. No homologs are described.

SUMMARY OF THE INVENTION This invention concerns a polymer, comprising, one or more of the repeat units

(IA), (IB), or

H

^C— CH 2

F 2 C ^CH 2

— CF ,CFCF 3

F2 (IQ; or one or more of the repeat units

F

F H / Cς— CF^ F 2 C— C— C— CH 2 H 2 C X CFCF 3

/ \ I

F 3 CFC \ / CH 2 — CH ^ .CF 2

F 2 H 2

(IIA), (UB), or

H

^ Cς-Ctt,

F 2 C CH 7 "

I I

— CF v ^ CF 2 CF

I

CF 3

(no, or both.

This invention also concerns a compound of the formula CF 2 = CFCF 2 CF(CF 3 )CH 2 CH = CH 2 or CF 2 = CFCF(CF 3 )CF 2 CH 2 CH = CH 2 .

DETAILS OF THE INVENTION The compounds CF 2 =CFCF 2 CF(CF 3 )CH 2 CH=CH 2 or CF 2 =CFCF(CF 3 )CF 2 CH 2 CH=CH 2 can be free radically polymerized to polymers containing one or more cyclic structures. When the monomer is CF 2 =CFCF 2 CF(CF 3 )CH 2 CH=CH 2 , a polymer with one or more of the repeat units (IA), (IB), and (IC) is produced. When the monomer is CF 2 =CFCF(CF 3 )CF 2 CH 2 CH=CH 2 , a polymer with one or more of the repeat units (IIA), (IIB) and (IIC) is produced. The synthesis of these two monomers is described in Examples 1-3. These 2 compounds may be separated from their mixture by methods known in the art, such as gas chromatography or liquid phase chromatography.

These monomers may be polymerized by themselves to form homopolymers, or copolymerized with other monomers to form copolymers. By "comprising" in describing these polymers is meant that they contain the above cyclic repeat units, plus any other repeat units from other monomers. Suitable comonomers include fluorinated and unfluorinated compounds such as tetrafluoroethylene, hexafluoropropylene, vinylidene fluoride, perfluoro(methyl vinyl ether), perfluoroφropyl vinyl ether), methyl vinyl ether, propylene, ethylene, chlorotrifluoroethylene, and perfluoro(2,2-dimethyl-l ,3-dioxole). Preferred comonomers are tetrafluoroethylene, perfluoroφropyl vinyl ether) and perfluoro(2,2-dimethyl-l ,3-dioxole), and tetrafluoroethylene is especially preferred.

The homo- and copolymers described herein are useful for films, coatings, and for molded articles. Such items can be made by standard

techniques. Since these polymers are at least partially fluorinated, they have superior chemical resistance, and in many cases superior thermal properties. The polymerizations described herein may be done by methods well known to the artisan, see for instance polymerizations methods described in H. Mark, et al., Ed., Encyclopedia of Polymer Science and Engineering, vol. 16, John Wiley & Sons, New York, 1989, p. 577-648. The polymerizations may be done neat, in aqueous emulsion or suspension, in solution or organic suspension. They may be done in batch, semibatch or continuous operations. A free radical polymerization initiator is used, suitable initiators including peroxides such as perfluoro(propionyl peroxide) (3P), azonitriles such as azobis(isobutylronitrile) (AIBN), and redox initiators such as persulfate-bisulfite. As is well known, the process is run at a temperature at which the initiator generates free radicals.

In the Examples, the following abbreviations are used: AIBN - azobis(isobutyronitrile)

CFC-122 - l ,l,2-trichloro-l,2,2-trifluoroethane DSC - differential scanning calorimetry DMF - N,N-dimethylformamide PDD - perfluoro(2,2-dimethyl-l,3-dioxole) TGA - thermogravimetric analysis

Glass transition temperatures were taken as the beginning of the transition, while melting points were taken as the peak of the melting endotherm. The heating rate for the DSC was 20°C/min.

EXAMPLE 1 Preparation of C1CF 2 C1CFCF 2 CFICF 3 and CF 2 C1CFC1CF(CF 3 )CF 2 I

A mixture of 280 g of CF 2 C1CFC1I and 400 g of CF 3 CF=CF 2 was heated in a autoclave at 200°C for 15 hours. The reaction mixture (367.4 g) was distilled on a 91 cm spinning band column to give 19 g of bp 64 to 98 °C, 99.2 g of CF 2 C1CFC1I, bp 99 to 101 °C, 8.5 g of bp 61°C/5.3 kPa to 75 °C/5.3 kPa and 199 g of CF 2 C1CFC1CF 2 CFICF 3 and

CF 2 C1CFC1CF(CF 3 )CF 2 I in a 94 to 6, bp 75°C/5.3 kPa. ™F NMR for major product: -62.0 to -64.8 (m, 2F), -72.5 (m, -72.9 (m) ( total 3F), -99.6 (m), -101.0 (dm, J = 275 Hz), -105.1 (dm, J = 275 Hz) (total 2F), -125.7 (m), -129.0 (m), (total IF), -138.5 (m), -142.8 (m) (total IF). HRMS: calcd for C 5 F 9 C1 2 I: 427.8278. Found: 427.8272.

P T/U 1

EXAMPLE 2 Preparation of CF 2 ClCFClCFCF 3 CH 2 CHICH 2 OAc and CF 2 ClCFClCF(CF 3 )CF 2 CH 2 CHICH 2 OAc A mixture 20 g of allyl acetate 43 g of a mixture CF 2 C1CFC1CF 2 CFICF 3 and CF 2 C1CFC1CF(CF 3 )CF 2 I in a 94 to 6, 1.5 g of copper powder and 60 mL of hexane was stirred at 72°C overnight. After removal of solids, the filtrate was evaporated to give 63.2 g of residue, which was distilled to give 26.7 g of 1 to 1 adducts, bp 80°C/12 Pa. IR: 1752 (s), 1229 (s), 1169 (s), 1047 (s). HRMS: calcd for CιoH 8 O 2 F 9 Cl2-I: 400.9756. Found: 400.9705. EXAMPLE 3

Preparation of CF 2 =CFCF 2 CF(CF 3 )CH 2 CH=CH 2 and CF 2 =CFCF(CF 3 )CF 2 CH 2 CH=CH 2 To a stirred solution of 9.0 g of Zn and 30 mL of DMF was slowly added 24 g of 1 to 1 adducts of Example 2 at 80°C. After the resulting mixture was stirred at 80°C for 5 hours, volatiles were distilled out and collected in a -78°C receiver at 1.3 kPa. The distillate was washed with water, NaCl solution and dried over MgSO 4 and redistilled to give 9.8 g of product, bp 102-103 °C.

19 F NMR: -91.0 (ddt, J = 53.8 Hz, J = 38.0 Hz, J = 5.9 Hz, IF), -75.6 (m, 3F), -106.2 (ddtd, J = 116.0 Hz, J = 53.8 Hz, J = 27.4 Hz, J = 5.8 Hz, IF), -113.5 (dm, J = 27.4 Hz, 2F), -180.9 (m, IF), -186.2 (dm, J = 116.0 Hz, IF). *H NMR: 5.80 (m, 1H), 5.30 (m, 2H), 2.85 (m, 2H). IR: 3043 (w), 1789.0 (s), 1652 (w), 1366 (s), 1316 (s), 1221 (s), 1193 (s). HRMS: calcd for QH5F9: 272.0247. Found: 272.0239.

EXAMPLE 4 Homopolvmerization of a mixture of 94 to 6 ratio of

CF 2 =CFCF 2 CF(CF 3 )CH 2 CH=CH 2 and CF 2 =CFCF(CF 3 )CF 2 CH 2 CH=CH 2 initiated bv bis(perfluoropropionyl) peroxide A 25 mL glass ampul fitted with a Teflon ® coated stir bar was charged with 0.01 mL of 5% of bis(perfluoropropionyl) peroxide in 1 , 1 ,2-trichloro- trifluoroethane and 0.71 g of the title compounds. The ampul was sealed and cooled in a liquid nitrogen bath. After being evacuated and purged with N 2 alternately six times, contents of the sealed ampul were stirred at 40 °C for 4 hours. The white heterogeneous mixture was filtered and washed with ethyl acetate and dried under vacuum at 100°C to give 0.50 g of polymer. The IR spectrum of this polymer showed no absorption at around 1790 and 1650 cm" 1 which could be attributed to double bonds in the polymer. This polymer was insoluble in acetone, ethyl acetate, DMF and hexafluorobenzene. The polymer had a glass transition temperature of 130°C, and no melting point by DSC (second heat). By TGA the polymer showed a 10% weight loss

temperature of about 430°C in nitrogen and 400°C in air, respectively, when heated at 20°C/minute.

EXAMPLE 5 Homopolvmerization of a mixture of 94 to 6 ratio of CF 2 =CFCF 2 CF(CF 3 )CH 2 CH = CH 2 and CF 2 =CFCF(CF 3 )CF 2 CH 2 CH=CH 2 initiated by initiated by AIBN A glass ampul fitted with a Teflon ® coated stir bar was charged with 7 mg of AIBN, 0.72 g of the title compound. The ampul was sealed and cooled in a liquid nitrogen bath. After being evacuated and purged with N 2 alternately six times, contents of the sealed ampul were stirred at 75 °C for 48 hours. The white heterogeneous solution were filtered and washed with CFC113 and dried under vacuum at 110°C to give 0.35 g of polymer.

This polymer was insoluble in acetone, ethyl acetate, DMF and hexafluorobenzene. The polymer had a glass transition temperature of 130°C, and no melting point by DSC (second heat). By TGA the polymer showed a 10% weight loss temperature of about 430°C in nitrogen and 400°C in air, respectively, when heated at 20°C/minute.

EXAMPLE 6 Copolvmerization of a mixture of 94 to 6 ratio of CF 2 =CFCF 2 CF(CF 3 )CH 2 CH=CH 2 and CF 2 =CFCF(CF 3 )CF 2 CH 2 CH=CH 2 with perfluoropropyl vinyl ether (PPVE) A 25 mL glass ampul fitted with a Teflon ® coated stir bar was charged with 0.01 mL of 5% of bis(perfluoropropionyl) peroxide in 1 , 1 ,2-trichlorotri- fluoroethane, 0.71 g of the title compounds and 0.71 g of PPVE. The ampul was sealed and cooled in a liquid nitrogen bath. After being evacuated and purged with N 2 gas six times, contents of the sealed ampul were stirred at 40°C overnight. The white solid was washed with methanol and dried under vacuum at 100°C to give 0.50 g of polymer. The polymer had a glass transition temperature of 131.6 °C and no melting point by DSC (second heat). By TGA the polymer showed a 10% weight loss temperature of about 410°C in nitrogen and 390°C in air, respectively, when heated at 20°C/minute.

EXAMPLE 7 Copolvmerization of a mixture of 94 to 6 ratio of CF 2 =CFCF 2 CF(CF 3 )CH2CH=CH 2 and CF 2 =CFCF(CF 3 )CF 2 CH 2 CH=CH 2 with perfluoro-2.2-dimethyl-1.3-dioxole (PDD)

A 25 mL glass ampul fitted with a Teflon ® coated stir bar was charged with 0.01 mL of 5% of bis(perfluoropropionyl) peroxide in 1,1 ,2-trichlorotri- fluoroethane and 0.65 g of the title compounds and 0.8 g of PDD. The ampul was sealed and cooled in a liquid nitrogen bath. After being evacuated and

purged with N 2 alternately six times, contents of the sealed ampul were stirred at 40 °C overnight. White solids was washed with ethyl acetate and dried under vacuum at 100°C to give 0.86 g of polymer. The polymer had a glass transition temperature of 139.1 °C and no melting point by DSC (second heat). By TGA the polymer showed a 10% weight loss temperature of about 470 °C in air when heated at 20°C/minute.

EXAMPLE 8

Copolvmerization of a mixture of 94 to 6 ratio of

CF 7 =CFCF 2 CF(CF 3 )CH 2 CH=CH 2 and CF 2 =CFCF(CF 3 )CF 7 CH 2 CH=CH 2 with Chlorotrifluoroethylene

A 25 mL glass ampul fitted with a Teflon ® coated stir bar was charged with 0.01 mL of 5% of bis(perfluoropropionyl) peroxide in 1,1,2-trichlorotri- fluoroethane and 0.65 g of the title compounds and 1.0 g of chlorotrifluoro- ethylene. The ampul was sealed and cooled in a liquid nitrogen bath. After being evacuated and purged with N 2 alternately six times, contents of the sealed ampul were stirred at 40°C overnight. White solids was washed with ethyl acetate and dried under vacuum at 100°C to give 0.52 g of polymer. The polymer had a glass transition temperature of 127°C and no melting point by DSC (second heat). By TGA the polymer showed a 10% weight loss temperature of about 385 °C in nitrogen when heated at 20°C/minute.

EXAMPLE 9

Copolvmerization of a mixture of 94 to 6 ratio of

CF 2 =CFCF 2 CF(CF 3 )CH 2 CH=CH 2 and CF 2 =CFCF(CF 3 )CF 2 CH 2 CH=CH 2 with CF 2 =CFOCF 2 CF(CF 3 )OCF 2 CF 2 SQ 2 F (PSEPVE) A 25 mL glass ampul fitted with a Teflon ® coated stir bar was charged with 0.01 mL of 5% of bis(perfluoropropionyl) peroxide in 1 , 1 ,2-trichlorotri- fluoroethane and 0.65 g of the title compounds and 0.85 g of PSEPVE. The ampul was sealed and cooled in a liquid nitrogen bath. After being evacuated and purged with N 2 alternately six times, contents of the sealed ampul were stirred at 40°C overnight. The white solid was washed with ethyl acetate and dried under vacuum at 100°C to give 0.60 g of polymer. The polymer had glass transition temperatures of 127.6°C, 190.3°C and 364°C and no melting point by DSC (second heat). By TGA the polymer showed a 10% weight loss temperature of about 400°C in nitrogen when heated at 20°C/minute.