PHASE CHANGE THERMAL CONTROL MATERIALS, METHOD AND APPARATUSES
Document Type and Number:
WIPO Patent Application WO/1994/002257
Kind Code:
A2
Abstract:
A highly flexible composite material (21) having a flexible matrix (B) containing a phase change thermal storage material (20). The composite material can be made to heat or cool the body or to act as a thermal buffer to protect the wearer from changing environmental conditions. The composite (21) may also include an external thermal insulation layer (A) and/or an internal thermal control layer (C) to regulate the rate of heat exchange between the composite (21) and the skin of the wearer. Other embodiments of the PCM composite (21) also provide 1) a path for evaporation or direct absorption of perspiration from the skin of the wearer for improved comfort and thermal control, 2) heat conductive pathways within the material for thermal equalization, 3) surface treatments for improved absorption or rejection of heat by the material, and 4) means for quickly regenerating the thermal storage capacity for reuse of the material. Applications of the composite materials (21) are also described which take advantage of the composite\'s thermal characteristics. The examples described include a diver\'s wet suit, ski boot liners, thermal socks, gloves and a face mask for cold weather activities, and a metabolic heating or cooling blanket useful for treating hypothermia or fever patients in a medical setting and therapeutic heating or cooling orthopedic joint supports.

Inventors:
BUCKLEY THERESA M (US)
Application Number:
PCT/US1993/006638
Publication Date:
February 03, 1994
Filing Date:
July 13, 1993
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
BUCKLEY THERESA M (US)
International Classes:
A41D13/005; A41D31/00; A61B19/00; A61F7/02; B05D7/24; B32B5/18; B32B5/22; B32B5/32; B32B7/027; B63C11/04; C08K5/00; C09K5/06; F28D20/02; A61F7/03; (IPC1-7): B05D/
Foreign References:
US4756958A1988-07-12
US4894931A1990-01-23
Download PDF:
Claims:
I claim:
1. A flexible composite material, comprising a flexible matrix material (21) containing a thermal storage material (20) capable of storing thermal energy as the latent heat of the phase change of the thermal storage material (20).
2. A composite material comprising a layer of matrix material (21) containing a thermal storage material (20) disbursed therein, said thermal storage material (20) capable of storing thermal energy as the latent heat of the phase change of the thermal storage material (20).
3. A material for metabolic cooling and for insulation of a user in an environment having an ambient temperature which is below a comfortable skin temperature, said material comprising: a layer of material including a phase change material having a phase transition temperature of between the ambient temperature of the environment and about 100 degrees Fahrenheit, for placement in thermal contact with the skin of the user to provide a thermal environment at a temperature above said ambient environmental temperature for an extended period of time, and to provide a heat sink to absorb metabolic heat, said absorbed metabolic heat acting to recharge said phase change material.
4. The material of claim 3 wherein said layer of material is a composite material having a matrix material and said phase change material being dispersed in said matrix material.
5. A method of providing metabolic cooling and for insulation of a user in an environment having an ambient temperature which is below a comfoπable skin temperature, said method comprising: covering the user with a layer of material including a phase change material having a phase transition temperature of between the ambient temperature of the environment and about 100 degrees Fahrenheit, for placement in thermal contact with the skin of the user to provide a thermal environment at a temperature for an extended period of time, and to provide a heat sink to absorb metabolic heat, said absorbed metabolic heat acting to recharge said phase change material.
6. The method of claim 5 wherein said layer of material is a composite material having a matrix material and said phase change material being dispersed in said matrix material.
7. The composite material of claim 1, 2 or 4 fuπher comprising: at least one additional layer bonded to said matrix material, said at least one additional layer being formed from a material selected from the group consisting of a thermally conductive material, a thermaUy insulative material, a thermal absoφtion material, a material substantially identical to said matrix material, polytetrafluoroethylene, and ceUulose acetate.
8. The composite material of claim 1, 2 or 4, wherein said matrix material (21) is selected from the group consisting of a flexible polymer, a flexible polymer foam, and elastomeric materials including natural rubber and synthetic rubber in either a foamed or un-foamed state.
9. The composite material of claims 1, 2 or 4, wherein said thermal storage material (20) is disbursed in said matrix material by either encapsulating the thermal storage material (20) in an impermeable material, or absorbing the thermal storage material (20) in a superabsorbent material selected from the group consisting of crosslinked polyethylene oxide, polyacrylate, and carboxy- methyl-ceUulose.
10. The composite material of claims 1, 2 or 4, where in said thermal storage material (20) is a material selected from the group consisting of Glycerol, Acetic Acid, Polyethylene Glycol 600, Camphene, Oxasoline Wax, d-Lactic Acid, formic acid, acrylic acid, p-Xylene, capryUc acid, Jojoba Wax, Cotton Seed Oil, Coconut Oil, Almond Oil, Beechnut Oil, Black Mustard Oil,Candlenut Oil, Castor Oil, Com Oil, Cotton Seed Stearin, Esparto, Poppy Seed Oil, Rape Seed (Canola) OU, Pumpkin Seed Oil, Soy Bean Oil, Sunflower Oil, Walnut Oil, White Mustard Seed Oil, Beeswax, NH4Cl«Na2Sθ4*10H2θ, NaCl»NH4Cl»2NaSθ4*20H2θ, NaCl»Na2*Sθ4,10H2θ, n-tetradecane, n-pentadecane, n-hexadecane, n-heptadecane, n- octadecane* n-nanodecane, n-eicosane, n-heneicosane, n-decosane, n-tricosane,Trimethlyolethane, Neopentyl Glycol, lithium chloride, Phase Change Material, calcium chloride hydrate, 1-decanol octadecane, C-16 to C-22 alkyl hydroc, natural rubber, polychloropropene, Witco 45A, Witco K-61, Witco K-51, Witco 85010-1, pentaerythritol, polyhydric alcohols, acrylate and methacrylate polymers , CaBr2»6H2θ/NaCl, Na2SO4.10H2O/NaCl, CaCl2»6H2θ, Na2SO4» 10H2O, CaBr2»6H2θ, Na2HPO4» 12H2O, Parafin Wax, Xylene, Banana Oil, OUve OU,Anise Oil, Atherosperma Mosechatum, Bay Oil, Bergamot Oil, Bergamot Florence Oil, Birch Bark Oil, Cejeput OU, Calamus Oil, Caraway Oil, Cascarilla Oil, Cassia Oil, Cedar Oil, Cedrat OU, Citronella OU, Clove Oil, Coriander Oil, Cubebs Oil, Dill Oil, Elder Oil, Eucalyptus Oil, Indian Geranium OU, Lavender Oil, Lemon Oil, Lemon Grass Oil, Melaleuea Oil, Mint Oil, Myrtle Oil, Myrrh Oil, NeroU Oil, Nutmeg Oil, Orange Peel Oil, Parsley Oil, Patchouli Oil, Peppermint OU,Petit Grain Oil, Rose Oil, Rosemary Oil, Rosewood Oil, Santalwood Oil, Thyme Oil, Tuφentine Oil, Verbena Oil, Wintergreen Oil, Wormwood Oil, Gallium Alloy, Sodium, and Naphthol.
11. A process for making a thermal storage material comprising the step of making a layer of matrix material having dispersed therein a thermal storage material (20) capable of storing thermal energy as the latent heat of the phase change of the thermal storage material (20).
12. The process of claim 11, wherein said matrix material is a polymer.
13. The process of claim 11, wherein said matrix material is a flexible polymer.
14. The material of claim 1, 2, 3, 4, 8, 9 or 10, wherein said material is fashioned into a garment selected from the group consisting of a wetsuit, a boot, a blanket, a facial mask, a hat, a gater, an ear muff, a Uner, a shoe insert, a shoe insole, a seating article, a jacket, trousers, a thermal undergarment and biking shorts.
15. The material of claim 1, 2, 3, 4, 8, 9 or 10, wherein said material is fashioned into an article selected from the group consisting of a blanket, a bed, a mattress, and a comforter.
16. A thermal building material comprising a matrix material containing a thermal storage material disbursed therein, said thermal storage material capable of storing thermal energy as the latent heat of the phase change of the thermal storage material.
17. A thermal window comprising a matrix material containing a thermal storage material disbursed therein, said thermal storage material capable of storing thermal energy as the latent heat of the phase change of the thermal storage material.
18. The material of claim 1 or 2, wherein said material is fashioned into an article selected from the group consisting of a bed, a mattress, a subroof, a window drape, a window blind, a windscreen blind, a beverage container, and a food chest.
Description:
PHASE CHANGE THERMAL CONTROL MATERIALS,

METHOD AND APPARATUSES

FIELD OF THE INVENTION This invention relates to a flexible composite material containing a phase change material for thermal storage and to garments and other articles made from the composite material.

GOVERNMENT RIGHTS

This invention is related to invention disclosures made by the inventor at NASA - Lyndon B. Johnson Space Center, Houston, Texas. The United States government may have certain rights to use this invention.

BACKGROUND OF THE INVENTION

The use of phase change materials or PCM\'s for thermal storage has long been known. In many materials much more heat can be stored as latent heat of phase change than as sensible heat. One of the earliest known applications of this principle is the use of ice as a thermal storage medium for perishable foods. Some of the phase transitions that involve significant amounts of latent heat are solid-to-liquid or liquid-to-gas phase changes or, in certain materials, solid-to-solid phase changes. Another subgroup of PCM\'s uses reversible exothermic reactions, such as hydration-dehydration or solution-precipitation reactions, for heat storage. The latent heat of phase change can be used for heating or cooling depending on whether the phase change is exothermic or endothermic. In most materials, the phase changes are reversible so that the latent heat storage can be used for either heating or cooling depending on the temperature conditions. PCM\'s have recently been applied to personal heating and cooling devices. U.S. patent 4,856,294 to Scaringe et al. describes a Micro-Climate Control Vest which contains a PCM with a solid-to-liquid phase change between 60 and 90°F as a cooling medium. The vest may also have an optional second PCM layer of ice and an optional outer insulation layer. Because of the inherent rigidity of the PCM in its solid state, the inner liner which contains the PCM is divided into individual compartments separated by vertical seams that provide folding points in the vest. This provides very limited flexibility in the vest, making it impractical for use during intense physical activity where the rigidity would be a hindrance.

U.S. patent 4,894,931 to Senee et al. describes a Heating Device for warrning body parts, such as the soles of the feet. The device uses a battery powered electric heater and a PCM salt. The PCM salt serves as a heat storage medium and as a temperature regulator for the resistance heater since it can absorb a lot of heat without rising above its melt temperature. This device is described as having a rigid base, which along with the inherent rigidity of the solid PCM salt, would make it unusable for applications where flexibility is important.

U.S. patent 4,572,158 to Fiedler and 4,077,390 to Stanley et al. both describe heating pads for wa__iiing body parts that use a supercooled PCM salt solution for heat storage. The PCM can be dissolved by placing the pad in boiling water. Once the PCM is liquefied, it can be cooled

to room temperature without solidifying. A trigger is used to activate the PCM, causing an exothermic crystallization which releases heat at about 135°F. The device is sold with a cloth or neoprene cover to prevent burns when it is placed against the skin. These heating pads are made in small sizes for spot heating parts of the body. Because the solid PCM salt is very rigid, the pad cannot be used for heating large areas of the body where the rigidity would be a hindrance to movement.

U.S. patent 4,756,958 to Bryant et al. describes a fiber with enhanced thermal storage properties and fabrics made therefrom. The fiber described contains microcapsules of PCM ranging from 1-10 microns in size. While these fibers provide the sought after flexibility, they do not contain enough PCM to have sufficient thermal mass to be of practical use in heating or cooling.

U.S. patent 4,851,291 to Vigo et al. describes another method of making fibers with thermal storage properties by filling the core of a hollow fiber with a PCM or absorbing a PCM onto the surface of a non-hollow fiber. The PCM\'s described include cross-linked polyethylene glycol and plastic crystals that have a solid-to-solid crystalline phase change. These fibers can also can be made very flexible, but their geometry does not allow absorption of enough PCM into the containment material to be of practical use in heating or cooling.

SUMMARY OF THE INVENTION From the preceding discussion it can be seen that the prior art, in all of its attempts, has failed to provide a flexible composite material with thermal storage properties that at the same time provides: 1) sufficient thermal mass for heating or cooling large areas of the body, and 2) enough flexibility to be fashioned into garments or other articles suitable for wear during vigorous physical activity where rigidity would be a hindrance to movement. With this in mind, the objective of the present invention is to provide a highly flexible composite material that contains a high thermal rxiass of a phase change thermal storage material. In various embodiments, the composite material can be made to heat or cool the body or to act as a thermal buffer to protect the wearer from changing environmental conditions. To help with this objective, the material may also include an external thermal insulation layer and/or an internal thermal control layer to regulate the rate of heat exchange between the composite and the skin of the wearer. Another important objective is to provide a flexible thermal storage composite material that can easily be fashioned into garments or other articles, such as blankets, that can be worn for their thermal properties.

Other secondary objectives of the invention are to provide a flexible thermal storage composite material that also provides 1) a path for evaporation or direct absorption of perspiration from the skin of the wearer for improved comfort and thermal control, 2) heat conductive pathways within the material for thermal equalization, 3) surface treatments for improved absorption or rejection of heat by the material, and 4) means for quickly regenerating the thermal storage capacity for reuse of the material.

In keeping with these objectives, the simplest embodiment of the present invention provides a composite material that has a phase change material incorporated into a flexible matrix material. In a second embodiment, the composite also includes an external thermal insulation layer and an internal thermal control layer to modify the surface temperature experienced by the skin of the wearer. Other embodiments feature moisture wicking components or other components that add different thermal properties to the composite. In each embodiment, the PCM may be chosen to provide heating, cooling or environmental buffering.

Exemplary applications of the composite materials are also described which take advantage of the composite\'s thermal characteristics. The examples described include a diver\'s wet suit, ski boot liners, mermal socks, gloves and a face mask for cold weather activities, and a metabolic heating or cooling blanket useful for treating hypothermia or fever patients in a medical setting.

BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 shows a cross section of a flexible PCM composite. Figure 2 shows a cross section of a multilayer flexible PCM composite having an insulating outer layer and a ermal control inner layer.

Figure 3 shows a laminated construction for a multilayer PCM composite. Figure 4 shows a monolithic construction for a multilayer PCM composite. Figure 5 shows a PCM composite with a semipermeable membrane for moisture control. Figure 6 shows a PCM composite with wicking elements for moisture transport.

Figure 7 shows a PCM composite with a thermal conduction layer. Figure 8 shows a PCM composite containing thermally conductive fibers. Figure 9 shows a PCM composite with an aerogel insulation layer and a solar absorption surface. Figure 10 shows a multilayer PCM composite using three PCM\'s with different transition temperatures.

Figure 11 shows a PCM composite using two PCM\'s with different transition temperatures randomly distributed throughout the composite.

Figure 12 shows a PCM composite having an electrical resistance heater for regenerating the PCM thermal storage. Figure 13 shows a diver\'s wet suit made with the flexible PCM composite.

Figure 14 shows a ski boot liner made with the flexible PCM composite. Figure 15 shows a glove made with the flexible PCM composite. Figure 16 shows a cross section of prior art traditional wet or dry suit. Figure 17 shows a cross section of a phase change material thermal capacitor wet or dry suit Figure 18 shows a cross section of prior art traditional ski boot.

Figure 19 shows a cross section of a phase change material thermal capacitor boot. Figure 20 shows a cross section of a phase change thermal storage window. Figure 21 shows a cross section of a phase change thermal storage window cover.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Figure 1 shows a flexible composite material with a PCM 20 distributed within a flexible matrix material 21. The flexible matrix material 21 is preferably a flexible polymer or a polymer foam, either open cell or closed cell. The PCM 20 can be one of several possible materials capable of absorbing or releasing heat as the latent heat of phase change. The thermal characteristics of the composite can be tailored by the choice of the PCM and the matrix material, as well as the ratio of the concentration between the two materials chosen. The actual choice of the PCM depends on the intended application of the composite material and on the desired characteristics. The criteria for choosing a PCM are discussed more fully in a separate section below. If a solid-solid phase transition PCM is chosen, the PCM may be added directly to the matrix material in the form of pellets or particles as it is being formed. If a solid-liquid phase transition PCM is chosen, the PCM should be encapsulated. The PCM can be in microcapsules or in larger capsules or a mixture of sizes. There are two reasons why it is preferable to encapsulate the PCM in the composite: first, to prevent it from migrating when it is in the liquid state and, second, so that the PCM does not form one solid inflexible mass as it cools. If a solid polymer matrix is used, then the matrix material can also serve as the encapsulant. If an open or closed cell polymer foam is used as the matrix, the PCM should be encapsulated within a polymer or other nonporous material before being added to the foam. Another method of preventing the liquid PCM from migrating within the composite is to absorb it into a material that holds the PCM captive, such as particles or fibers of polyacrylic or carboxy-methyl-cellulose, before adding them to the matrix. Other methods of preventing pcm from migrating are to mix the pcm with a third substance to create a paste or other form to ease incorporation into a matrix

Examples of the structure in figure 1 have been successfully made using a mixture of coconut oil and rice oil as the PCM and latex as the encapsulant and matrix material. Figure 2 shows a multilayer flexible composite material containing a PCM layer. The composite may be made by laminating diverse materials together or it may be made of a single matrix material with the PCM concentrated within one layer of the composite.

Layer A, on the exterior surface of the composite, is a thermal insulation layer to reduce the heat exchange between the PCM and the environment and to protect the wearer from harsh exterior temperatures. The ideal material for this layer in most applications is a flexible polymer foam.

Layer B is the layer which contains the PCM. It may be a matrix material with the PCM distributed within it, as in Figure 1, or other structures may be used to hold the PCM in place.

Layer C, on the interior surface of the composite, is a thermal control layer, whose function is to regulate the rate of heat exchange between the PCM and the skin of the wearer and thereby keep the skin contact surface at a comfortable temperature. If the PCM transition temperature is within the comfort range for skin contact, then layer C might be a simple barrier layer to contain the PCM. If the PCM transition temperature is outside the comfprt range, either too hot or too cold, then layer C should be a thermally insulating material, such as plastic foam to reduce heat exchange. In most applications, it is preferable to have layer C thinner than layer A so

that the PCM will have better thermal coupling with the wearer\'s skin than with the external environment. The thermal control layer can also be used to increase the rate of heat exchange. For this purpose, layer C can be made to include fibers or films of thermally conductive material to provide a thermally conductive pathway between the PCM and the skin of the wearer. Figure 3 shows one embodiment of the multilayer flexible composite constructed by laminating layers of different materials together. Layer A is a layer of closed cell neoprene foam that acts as thermal insulation. Layer B includes an inner web of perforated neoprene foam. The webbing serves as the matrix which contains the PCM and lends structure to the composite. The

PCM 20 is preferably in peletized form so that the rigidity of the PCM in its solid form does not adversely affect the flexibility of the composite. Layer C is a thin layer of closed cell neoprene foam. Layers A, B, and C are bonded together to make the composite material.

Figure 4 shows an embodiment of the multilayer flexible composite that is made as a monolithic structure without laminations. The matrix material is preferably a flexible polymer or a polymer foam. One method of manufacturing the composite is by casting it in large sheets or as preshaped parts. Any castable material can be used as the matrix in this method. Satisfactory materials used for prototypes of this embodiment include latex, silicone, polyurethane, polyurethane foam, and other natural and synthetic rubbers.

Other materials suitable for use as matrices are: ABS, SAN, acetal, acrylic, alkyd, allyl, amino, cellulosic, epoxy, fluoroplastics, liquid-crystal polymers, nylon, phenolic, polyamide, polyimide, polycarbonate, polyester, polyetheretherketone, polyetherimide, polyolefins, polypheylene ether, polypheylene sulfide, polystyrene, polyurethane, polyvinyl chloride, suirone polymers, laminated plastics, structural foam, nitrile rubber, butyl rubber, viton, mylar, thermoplastic elastomers, thermoplastic rubbers, ethylene vinal acetate, polyureas, kevlar, aramide, aromatic polyamides, fluorinated hydrocarbons, and parylene.

The suggested process for producing the monolithic composite is as follows: Layer A of the matrix material 21 is cast to the desired thickness in a mold or on a very flat surface. Layer A is allowed to partially, but not fully, vulcanize. Layer B of the matrix material containing a high concentration of granulated or encapsulated PCM 20 is cast over layer A and smoothed to the desired thickness. Layer B is also allowed to partially vulcanize. Layer C of the matrix material is cast over layer B and smoothed to the desired thickness. The entire composite is then allowed to fully vulcanize. Because successive layers of the matrix material are added before the previous layers are fully vulcanized, bonding between the layers is as strong as the matrix material itself. There are no weak points that could cause delamination of the composite. Optionally, outer or inner linings of fabric or other materials may be added to the composite at the beginning or the end of the process. In some embodiments, this fabric layer may constitute the entirety of the outer or inner layer.

The described process is given by way of example only. Those skilled in the art of polymer fabrication will, no doubt, be able to devise other processes or variations on the described

process to arrive at the same result. For instance, a thermal storage composite could also be made by one of the following processes:

1. Dispersing an absorbent, super absorbent, etc, into an open cell matrix then adding the pcm to the matrix. As the absorbent now swells, it will tend to lock the absorbed pcm into the open cell matrix.

2. Injecting the pcm into a cavity or gel material. For example, new synthetic skins have been developed that permit injection of antibiotics or other substances.

3. Creating a flexible embodiment containing the phase change material via vulcanization to form factice from unsaturated vegetable oils such as rung oil and Unseed oil ("Chemical Reactions

During Vulcanization," E.A. Hauser and M.C. SZE). The oils forming the factice then become the phase change material.

4. Supersaturation of a pcm salt solution, absorption of this solution into an open cell matrix or foam then subsequent evaporation of the solvent. 5. Incorporation of micro encapsulated, macro encapsulated, etc. pcm into a froth such as the polyurethane froths used to created foam backings on carpet (ICI Polvurethane\'s Handbook, D. Sparrow).

6. Use of macro encapsulation and pharmaceutical hard, soft, gel, etc. drug encapsulating techniques to contain the pcm prior to incorporation into the matrix (Micro capsule Processes and Technology. A. Kondo).

4. Absorption, adsorption, etc. of the pcm onto a membrane bound with the absorbing, adsorbing, etc. material.

5. Absorption of natural fats and oils into unvulcanized natural rubber, rubber, silicones, etc. or other natural and synthetic polymers that absorb the pcm of interest. 6. The use of molding, vacuum forming and thermoforming techniques for macro encapsulation of a continuum of pcm particles during the formation of a laminate.

7. Deposition of micro encapsulated pcm onto thin films. An example of this form of carrying micro capsules is given in Polymers for Engineering Applications by R. Seymour.

8. Forming aggregates with granules or encapsulated pcms by dispersing the particles into a gel, or other flexible bonding material to form an aggregate.

9. Forming jellies of pern\'s using pectin, gelatin (proteins), then dispersing these jellies within sealed matrices.

10. Creating a rubber, rubber gels or other gels as described by S.S. Kistler in "Coherent Expanded Aerogels," however, a pcm is used in the solvent step. 11. Selective absorption of embodiment of the pcm into cellular (natural and synthetic) membranes or matrices. Techniques might include dialysis, and the use of absorbents, adsorbents, etc. within the membrane for containment of the pcm upon its entry into the cellular space. Techniques may also include Graham\'s method of cell fixation whereby liquids in gelatinous tissues are sequentially replaced with other liquids, miscible in the first, such that the

final replacement liquid is a paraffin. In this intended application, the process is designed so that the final liquid is chosen to be the pcm itself. (Graham, "On the properties of Silicic Acid and other Analogous Colloidal Substances," The journal of the Chemical Society, 1864). Graham\'s same process forms the foundation for the formation of alcogels, aerogels, etc. as described in S.S. Kistler\'s "Coherent Expanded Aerogels and Jellies," Nature, 1931 wherein the aerogel process is stopped at the stage that contains the desired cm formation.

12. Inco orating the step of macro encapsulating the pcm into a higher melting point, semi-stable form such as a paraffin prior to incorporation into a matrix.

13. Spraying a sheet of coating over a dispersion of pcm to bond the pcm to another layer in the composite.

14. Ivlixing the pcm with a third substance to create a paste in order to stabilize it while in a liquid state during lamination.

For some applications of the PCM composite it will be desirable to incorporate a moisture transpoπ mechanism into the composite to transport perspiration, condensation, or other moisture away from the skin of the wearer. Figure 5 shows a PCM composite with one possible moisture transport mechanism. The composite is made with an open cell foam or other porous material as the matrix material 23 so that it is permeable to moisture. The PCM is distributed within the matrix as pellets or capsules. The skin surface of the composite is lined with a semipermeable membrane 22 which is permeable to water vapor, but impermeable to liquid water. One possible material for this semipermeable membrane is expanded polytetrafluoroethylene which is available under the trade name Gσre-Tex® from W. L. Gore and Co. Another semipermeable membrane material usable in this application is cellulose acetate. The membrane allows water vapor from perspiration to diffuse through the composite while preventing liquid water from entering the open cell matrix. If desired, another layer of semipermeable membrane may also be laminated to the exterior surface of the composite. One embodiment of this has been made using particles or capsules of PCM bonded between two Gore-Tex® membranes using an adhesive to form a porous matrix.

Figure 6 shows another possible embodiment of the composite incorporating a moisture transport mechanism. In this example, the matrix material 24 is a closed cell foam or a solid polymer which is impermeable to moisture. To allow moisture to be transported through the impermeable matrix material, moisture transport elements 25 are added that bridge the composite from the inner surface to the outer surface.

In their simplest form, the moisture transport elements may be nothing more than vents that allow perspiration and water vapor to escape. In their preferred form, they are wicking elements 25 that are made of a moisture absorbent material that conducts moisture from the skin surface to the exterior of the composite. Superabsorbent materials, such as carboxy-methyl-cellulose fibers, may also be used as the wicking element. It is also possible to incorporate dessicants into the composite to absorb moisture.

Another feature that may be added to PCM composite is a thermally conductive material that helps to distribute the heat within the composite. Figure 7 shows a PCM composite that contains a heat equalization layer 26 of thermally conductive material. The layer 26 may be made from a conductive film or a network or mesh of fine wires or heat conductive fibers or a mat of random wires or fibers. The heat equalization layer 26 distributes heat horizontally within the composite material so that hot spots are eliminated and there is an even temperature distribution all over the skin surface.

Figure 8 shows a PCM composite that contains heat conductive fibers or wires 27 distributed throughout the matrix material 21 to distribute heat horizontally and vertically within the composite. The advantage of this is that it makes more effective utilization of the PCM. The improved thermal coupling between the skin surface and the PCM shortens the thermal path for absorption or release of heat from the PCM.

Another effective way to use thermally conductive materials in the PCM composite is to use them for encapsulating the PCM. Thin metal capsules or capsules of another thermally conductive material surrounding the PCM would greatly improve the thermal coupling with the

PCM.

Another method of affecting the thermal coupling between the PCM composite and the skin is to change the contact pressure between the two surfaces. Increasing the contact pressure will increase the rate of heat transfer and decreasing the pressure will lower the rate of heat transfer. One way to accomplish this is by adding an inflatable bladder within the composite material or within a garment containing the composite so that fluid pressure can be used to regulate the contact pressure and therefore the thermal coupling. Another way would be to add elastic straps or hook- and-loop fasteners to increase contact pressure between the PCM composite and the skin.

Another feature to enhance the thermal properties of the PCM composite is the addition of a solar absorption surface to the exterior of the composite material. By absorbing solar radiation and converting it to heat, the solar absorption surface acts to regenerate the PCM in a warming garment In its simplest form this could be the addition of a dark colorant or a dark material to the exterior surface of the composite. In another embodiment, shown in figure 9, a transparent aerogel 28 has been added to the outer surface of the composite to act as a very effective insulation layer and as a window to solar radiation. The solar absorption surface 29 is placed at the interface between the aerogel layer and the PCM-containing layer.

In some applications it may be advantageous to combine two or more PCM\'s having different transition temperatures into the composite material. Figure 10 shows a schematic diagram of a multilayer PCM composite with three PCM layers having different transition temperatures.

This arrangement can be used to overcome one of the drawbacks inherent in some of the prior art PCM applications. Namely, some PCM garments start to lose some of their effectiveness after the PCM near the skin has undergone its phase transition. This is because the thermal path length is longer to the unchanged PCM that is farther from the skin. One solution to this is to add

conductive materials to the composite as previously described. The other solution is to use multiple PCM\'s with different transition temperatures. To understand how this works, please refer to figure 10.

For the sake of discussion let us say that the PCM composite of figure 10 is to be used for a cooling garment. PCM\'s 1, 2, and 3 should be chosen so that they have progressively lower transitions temperatures moving away from the skin surface, that is, Ti > T2 > T3.

If the transition temperatures and the thicknesses of the layers 1 , 2, and 3 are properly chosen, then each layer will be equally effective in cooling the skin of the wearer because the longer thermal path length to the more distant layers will be compensated by the lower transition temperature of the PCM. Thus, the rate of heat absoφtion of the composite will remain relatively constant until all of the PCM has undergone its phase transition.

Mathematically, the heat flux, Q, is proportional to the temperature difference, ΔT=Tsi_ . n- T t ransi t ion * divided by the thermal resistance, R, which is determined by the thermal path length:

O « _ΔJ_ = T sk in-T.

R R; where Ti > T 2 > T3 and R] < R2 < R 3

By the proper choice of Tj, T2, and T $t Qi, Q2, and Q3 can be made approximately equal so the rate of heat absorption of the composite will remain relatively constant until all three layers of PCM are exhausted.

Another way to incorporate multiple PCM\'s into a single composite is to evenly distribute two or more encapsulated PCM\'s 30, 31 throughout the matrix 32 as shown in figure 11. This arrangement can be used when thermal protection is needed at two or more different temperatures. One PCM can be a heating PCM 30 and the other can be a cooling PCM 31 to incoφorate both functions into a single composite.

PHASE CHANGE MATERIALS

As mentioned in the background discussion, a phase change material or PCM is any material capable of storing thermal energy as latent heat of a phase change. There are a great many materials that exhibit this property. Table 1 shows some of the materials useful as PCM\'s. The choice of which PCM to use for thermal storage in the flexible PCM composite of this invention depends principally on two factors: the latent heat of the phase change and the transition temperature. A number of secondary factors may also affect the choice of PCM\'s, such as density, low toxicity and low flammability. In general, the higher its latent heat of phase change is, the better a material will be as a PCM because more thermal energy can be stored in it. The choice of transition temperature depends largely on the intended function of the composite. The PCM\'s can be categorized as heating PCM\'s, cooling PCM\'s and buffering PCM\'s. Heating PCM\'s are materials whose phase transition temperature is above the body\'s normal skin

temperature. When a heating PCM is warmed above its transition temperature and placed in thermal contact with the skin, the temperature gradient will be such that heat flows from the PCM into the body. More extreme heating PCM\'s will also have their transition temperatures above the body\'s core temperature. Cooling PCM\'s are defined as those materials whose phase transition temperatures are below the body\'s normal skin temperature. When a cooling PCM is chilled below its transition temperature and placed in thermal contact with the skin, the temperature gradient will make heat flow from the body into the PCM.

A buffering PCM is a material whose phase transition temperature is slightly below normal skin temperature so that it can serve to absorb or release heat depending on environmental and metabolic conditions. Thus, a buffering PCM could also be classified as a mildly-cooling PCM. A buffering PCM can be effectively used to help a body maintain thermal equilibrium by regulating heat flow from the body. A buffering PCM can also be used to protect a body from rapidly changing or cycling environmental temperatures. This buffering function is most effective when the PCM is at its phase transition temperature and some of the PCM is in its high energy state and some is in its low energy state. Let us say for instance, that a garment is made of a flexible PCM composite using a solid-liquid PCM with a transition temperature of 60°F. The initial condition of the PCM is at 60°F and some of the PCM is solid and some is liquid when the garment is donned. The temperature of the PCM is lower than the wearer\'s skin temperature so there is a temperature gradient that causes heat to flow from the body into the PCM. Instead of heating up the way an insulating garment would, the solid PCM serves as a constant temperature heat sink absorbing heat as it changes to a liquid, not heating up as long as there is solid PCM in the composite.

Now, let us say that the wearer begins a job or a recreational activity that involves entering a cold environment. The outside temperature drops and the PCM begins to give up heat to the surrounding environment. However, because of the stored heat in the liquid PCM which is given up when the PCM turns to a solid, the PCM maintains a constant 60°F as long as some liquid PCM remains. Although the outside environment may drop to arctic temperatures, the skin experiences a constant temperature of 60°F which keeps the wearer comfortable. Next, if the wearer moves into a hot environment with a temperature above body temperature, the temperature gradient is reversed and the PCM begins to absorb heat from the environment. Again, instead of heating up, the garment keeps a constant temperature of 60°F as long as there is solid PCM within the composite to absorb heat. If the wearer had been wearing an insulating garment, he or she would have had to remove the garment to avoid overheating and the dangers of hyperthermia. Thus, a garment made with a buffering PCM within the flexible PCM composite will maintain a comfortable, constant temperature environment for the body despite drastic changes in the external environment.

A buffering PCM can also be used to accommodate large changes in metabolic rate in constant or changing environmental conditions. To illustrate this principle, let us consider the

example of two crosscountry skiers engaged in a biathlon race. Skier 1 is wearing an ordinary insulating garment and skier 2 is wearing a garment made with flexible PCM composite. At the beginning of the race both skiers are warm and comfortable, appropriately dressed for the outdoor conditions. When they start skiing, however, skier 1 starts to heat up because his insulating garment prevents him from rejecting the excess metabolic heat to the environment Skier 1 must either stop and remove some of his insulation or he must endure the overheating, which will cause excessive perspiration and perhaps hyperthermia. Skier 2, on the other hand, maintains his thermal comfort because his PCM garment absorbs the excess metabolic heat without any rise in temperature. After skiing the first leg of the race, both biathletes must stop to shoot at a rifle target.

When their activity level drops so does their metabolism. Skier 1, depending on his insulating garment for warmth, starts to chill, especially if his garment is sweat soaked, thereby losing its insulating value. This chilling can greatly affect the racer\'s marksmanship. Skier 2, however, stays warm as his PCM garment stops absorbing heat and starts releasing heat to maintain a constant comfortable temperature. This thermal cycling continues for the rest of the race, with skier 1 getting the worst of it each time. At the end of the race, skier 1 must quickly don a heavy parka or go indoors to avoid a severe chill, while skier 2 can remain warm and comfortable for some time because of the heat stored up in his PCM garment. Thus a buffering PCM composite can be used to maintain a constant thermal environment for the wearer in spite of temperature changes in the external environment or changes in the wearer\'s metabolic rate.

PCM\'S IN ABSORBENT MATERIALS

As briefly mentioned in the detailed description above, absorbent materials can be used as an alternative to encapsulation to hold the PCM and to keep it from migrating within the composite. Absorbent materials such as open cell polymer foam or cellulose fibers can be used to absorb a PCM while it is in the liquid state. Superabsorbent materials such as crosslinked polyethylene oxide, polyacrylates or carboxy-methyl-cellulose in the form of particles, fibers or films can also be used to absorb certain PCM\'s. The superabsorbents have the advantages that they absorb a higher percentage of their own weight in PCM and that the PCM is held tenaciously within the superaborbent so that it will not migrate even in the liquid state.

Some solid-liquid PCM\'s can be easily absorbed into an absorbent or superabsorbent material when they are in the liquid state. PCM salts can be introduced into an absorbent in solution or as a supersaturated solution, then the solvent can be evaporated to leave the PCM salt behind. Some PCM\'s will not readily absorb into certain absorbent or superabsorbent materials even when they are in the liquid state. This problem can sometimes be overcome by introducing the PCM into the absorbent using a method based on Graham\'s method of cell fixation. In this method, a compatible liquid such as water is first absorbed into the material; the water is then gradually replaced with another liquid like an alcohol that is miscible with the water. Once the alcohol has completely replaced the water, then stronger and stronger solutions of an alcohol

soluable PCM, like a parafin wax or an oil, can be used to replace the alcohol with a high concentration of the PCM. In this way, a PCM can be gradually introduced into a superabsorbent material that normally is only absorbent for water. This is only one simple example of this process, other types of PCM materials can be introduced to absorbent materials with variations on this process using suitable solvents.

PCM composites of the types shown in Figures 1 and 4 can be made by absorbing a PCM into small particles of foam or a superabsorbent material and adding them to the matrix material in place of the pellets or capsules of PCM previously described. Likewise, the laminated composite structure of Figure 3 can be made by replacing the PCM capsules shown with PCM contained in particles of absorbent materials or small blocks of absorbent cut to fit the perforations in layer B. In the multilayer composite structure shown in Figure 2, the entire layer B can be replaced with a layer of absorbent foam or a layer of superabsorbent material.

To avoid having the absorbent layer become inflexible when the PCM solidifies, a combination of different melting point waxes can be used as the PCM. When a combination like this is used the lower melting point wax will keep the mixture flexible until all of the waxes are below their freezing points. Alternately, the layer of PCM-containing absorbent material can be broken up with a flexible network or webbing that provides flexibility to the layer when the PCM is solidified.

Some absorbent and superabsorbent materials swell significantly when they absorb another material. A superabsorbent is generally defined as a material which absorbs more than 20 times its weight of the substance to be absorbed. This property can be used to advantage when making the flexible PCM composite. Particles of the absorbent material by itself can placed into the internal spaces of an open cell foam or a fibrous network and then swelled in place by allowing them to absorb the PCM. The absorbent panicles with the PCM become locked into place inside the matrix when they swell up. The result is a flexible composite material containing the PCM within a foam or fibrous matrix.

Suitable absorbents and super absorbents include cellulose, cotton, open-called foam, silica, polypropylene, carboxymethyl groups, diethylaminoethyl groups, styrene devinylbenzene copolymers with selected functional groups, polyacrylamides and their copolymers, agarose gels, polystyrene, hydroxyapatite, alumina, silicone, celotex (sugar cane fiber), methyl cellulose, carboxymethyl cellulose, poly-N-vinyl-2-pyrrodine and its copolymers, hydrogels, dextran, starch grafted polyacrylate polymers, down, synthetic downs and ethylene oxides. In addition, several absorbant products are available on the market for oil spill recovery. These include Envirobon 403 from Petroleum Environmental Technologies, Nochars A610/A650 bonding agent from Nochar Inc., Elastol (polu-iso-butylene) and Elastasorb from Bεneral Technology, rubberizers and Magic Sorb from Devcon. Obviously that absobent must be matched to the substance to be absorbed. Another embodiment of the invention involves phase change materials that change phase from a liquid to a gaseous state to absorb thermal energy. One example involves absorbing a liquid, such as ethanol or isopropanol, into a superabsorbant material such as ethylene oxide. The

ethylene oxide can be crosslinked to make it structurally stable and/or reinforced with a webbing material. This creates a composite material which has a high percentage of the phase change liquid in the matrix. Such a composite can be used for cooling febrile patients by evaporative cooling as the phase change liquid in the matrix changes from a liquid to a gaseous state to absorb thermal energy. The composite can also be made with a perforated barrier material around the outside to regulate the evaporation rate of the phase change liquid. Alternatively, the composite can be made with an imperveous barrier material on one side to prevent the liquid from contacting the patient\'s skin. The phase change liquid in the matrix can be recharged by soaking the material in the liquid.

This has an important advantage over the traditional method of using alcohol baths for cooling febrile patients in that the cooling effect can be sustained for an extended period of time because of the high percentage of phase change Uquid that can be absorbed into the superabsorbant.

REGENERATING THE FLEXIBLE PCM COMPOSITE

Once all of the PCM in the composite material has been exhausted, that is, all of the PCM has undergone its phase transition, the PCM must be regenerated to its original state before the material can be used again. The simplest way to regenerate the PCM is to place the material in an environment with the correct temperature. A cooling garment may be placed in a refrigerator or freezer or any other cold place to resolidify the melted PCM. A heating garment may be placed in an oven, a steam cabinet, or boiling water to melt the solidified PCM. For a thermal buffering garment, with a moderate transition temperature, the PCM may be regenerated without special equipment. For instance, if a buffering PCM has a transition temperature below normal room temperature, the material can be reheated by simply taking it indoors or into a heated car and allowing the temperature to equilibrate.

Of course, the matrix material and any encapsulant or adhesive used to make the composite must be chosen to withstand the temperature extremes of the regeneration cycle.

To make the regeneration step faster or more convenient, features may be added to the composite to heat or cool the PCM. Figure 12 schematically depicts a flexible PCM composite with an electrical resistance heater 33 to regenerate the PCM in a heating garment. Another way to use electrical energy to regenerate the PCM is with a thermoelectric (Peltier effect) heat pump. This approach has the advantage that it can be used to heat or cool the material, depending on the current flow in the device.

Rather than including these regeneration devices in the PCM composite, it is also possible to make an auxiliary device that serves to regenerate the PCM. For instance, a flexible bag for storing a PCM garment between uses can incoφorate an electrical device for heating or cooling the garment inside. A carrying case or a storage cabinet could also be equipped with regenerating devices such as these.

Chemical means may also be employed to regenerate the PCM or to supplement its effectiveness. An exothermic chemical reaction can be used to heat the PCM composite to regenerate it. Likewise an endothermic chemical reaction can be used to cool the composite. If

such an exothermic or endothermic reaction is thermally coupled to the PCM composite while the user is still wearing it, it can be used to supplement the effectiveness of the PCM in heating or cooling or to extend the operation time of the composite.

Another way to regenerate the PCM in the composite is to place it in thermal contact with another PCM. For instance, a cooling garment can be placed into ice to solidify its melted PCM.

The reason for doing this instead of using ice as the primary PCM is that the temperature of ice is too low for comfoπ in long-term contact with the skin. The PCM in the composite can be chosen so that the transition temperature is within the body\'s comfoπ range.

If a secondary PCM is placed in thermal contact with the composite while the user is wearing it, the primary PCM can be regenerated while it is still in use. Replaceable layers with the secondary PCM can be used to extend the operation time of the composite.

Other ways of facilitating the regeneration of the PCM composite include making it susceptible to efficient forms of heating such as microwave or induction heating. Some PCM\'s, such as polyethylene glycol, are naturally susceptible to microwave heating. Other PCM\'s, for instance most of the PCM salts, cannot be heated with microwaves. For these materials, a susceptor can be added to the PCM or the matrix or the encapsulation material to absorb the microwaves and conveπ their energy to heat which regenerates the PCM.

Likewise, if induction heating is desired, a susceptor material such as stainless steel can be added to the composite in the PCM, the matrix, or the encapsulant to absorb electromagnetic waves and conveπ their energy to heat. One way to control the induction heating and prevent overheating the composite and damaging it, is to choose a susceptor material whose Curie temperature is above the transition temperature of the PCM, but below the safe maximum temperature limit of the composite. When the susceptor reaches its Curie temperature it wiU lose its susceptibility to induction heating until the temperature falls below the Curie point. Thus, the temperature will oscillate around the Curie temperature to quickly and safely heat the composite and regenerate the PCM.

The flexible PCM composite of this invention was designed to provide passive heating and cooUng for garments and other articles. It is also possible to combine the PCM composite with active heating or cooling systems to enhance the effectiveness of both. For instance, a PCM composite inner Uner can be worn under a space suit that has an active environmental control system. Or a heat exchanger can be coupled to the PCM composite for additional heating or cooUng or to regenerate the PCM in use.

The PCM composite would be beneficial to the heating or cooling system. The heat capacity of the PCM composite can be used to reduce peak loads on heating/cooling systems and to maintain the temperature during temporary power outages or disconnections. The temperature stability of the PCM material would also allow the temperature controls of the heating/cooling system to be made less sophisticated because the PCM will protect against overheating or overcooling.

In order to accommodate connection of the PCM composite to an active heating or cooling source, the composite can be made with tubes or passages for a fluid or other heat exchange medium.

THERMAL CONTROL EXAMPLES

Example 1: Thermal Capacitor Diving Suit

The foUowing example of a phase change material thermal capacitor diving suit has been chosen to illustrate the benefits of the present invention. The use of a phase change material thermal capacitor diving suit offers a unique approach to both buffer the individual from extreme environments and simultaneously provide the cooling required to absorb heat generated in the body at a rate that maintains thermal comfoπ and/or prevents hypothermia or hyperthermia. The same thermal design method is applicable to the other embodiments of the invention described elsewhere in the specification.

A simplification of the steady-state heat transfer process in a prior an diving suit is shown in figure 16. Many analytical and experimental algorithms exist, along with computer programs thereof, for determining the allowable rate or quantity of net heat loss from or input to the body to maintain thermal comfoπ and protection from hypothermia and hypenhermia. The former allowable heat loss or gain is refeπed to, herein, as Qcomfor t - For a given environment and expected metabolic rates, one can determine the component, Qeq_il > that summed with the respiratory heat losses, sensible and latent heat losses through the skin for areas not covered by the suit, heat loss from water leakage into the suit, etc. maintains Qcomf within the heat storage bandwidth chosen. It is reaUzed that convective cooling from water leaking into the suit is an important mode of heat exchange and it is important to rrήnimize this mode of heat exchange by sealing the suit as well as possible. The example below is an ideal case to demonstrate the difference between heat loss across the diving suit with and without a phase change layer.

For example purposes only, suppose that the following conditions are true:

T S kin = 90 F T e ι = 43 F

Te2 = 33 F xi = 3/16"

X2 = 3/16" ki = 0.03 B/hr-ft-F k2 = 0.02 B/hr-ft-F h = 150 B/hr-ft 2 -F

A f = 18 ft 2

Cpf = 0.83 B/lbm-F

Qequiι = 625 B/hr

From these givens, one can compute Q 0 ss according to equation [1], below, to be equal to 646 B/hr in a 43 F environment and 815 B/hr in a 33 F environment From the difference between Oj oss and Qequil, one can conservatively estimate a drop in body temperature equal to 0.2 F/hr for 5 the first case and 1.5 F/hr for the latter. Although this is less likely the case, had Qeq U π exceeded Ojoss, a rise in body temperature would occur with a tendency towards overheating.

V-.OSS- σskiπ-T_J [1]

l o The disadvantage of the current practice to strictly use insulation for thermal control is that the thermal resistance is fixed in the diving suit. As explained above, to avoid overheating or chilUng, i.e. thermal discomfoπ, a balance must be achieved between the heat desired to be removed from the body to maintain comfoπ, Qequil, an the actual heat flow out of the suit, Oj 0 ss- Since environmental conditions change constantly and since thermal conditions of the foot are

15 directly Unked to the changing environment through this fixed heat transfer path, no latitude exists to achieve this balance at conditions other than those at the single environment for which a solution exists.

An example of a thermal capacitor diving suit cross section is illustrated in figure 17. For this example, the same diving suit of figure 16 has been used, however, integral to the diving suit

20 is a layer of phase change material, enclosed or encapsulated in an impermeable membrane, that acts as a thermal capacitor. The phase change material can be any paraffin, salt, crystalline, etc. material the undergoes a phase transition at a temperature appropriate to maintain thermal comfoπ and at a temperature compatible with regeneration in an environment consistent with its use. The phase change material layer might be interspersed with highly conductive metallic fibers to

25 improve heat distribution throughout this layer. The capacitor serves two purposes. The first is to maintain thermal equilibrium and, hence, continuous thermal comfoπ. The second is to act as a thermal barrier or buffer to maintain this thermal equilibrium, for extended periods, regardless of changes in the external environment.

The maintenance of thermal equilibrium is accomplished in the following manner. A phase

30 change material is chosen such that, given its melt point and the heat transfer coefficient between the skin and its melt Une, Qequil can be attained according to equation [2], below. Depending upon the relative magnitude of contact conductance between the suit and the skin, this thermal resistance can be added as weU.

Qequil

35

Qequil is rriaintained fairly constant as long as the phase change material is undergoing a phase transition, either from solid to liquid or liquid to solid. This simpUfication has been used to illustrate the buffering effect Time variant analysis offer a more rigorous solution. Several analytical techniques have been developed to describe the change of phase heat transfer process. A rigorous, time variant solution to the pcm heat transfer process is given in "Numerical Simulation of a Latent Heat Exchanger," by J. Sun and C.K. Rush in Advances in Phase Change Heat

Transfer..

The function of the phase change material as a barrier or buffer evolves from the characteristic of a phase change process. As a phase change material undergoes a phase transition, depending upon its initial state, it can either absorb or emit a quantity of heat equal to its latent heat of fusion while stiU maintaining a constant temperature. In such a manner, heat can be lost or gained from either side of this barrier, yet the temperature at this barrier will remain constant. This remains true until all of the phase change material has either solidified or liquefied. After this point, all of the latent capacity of the phase change material has been consumed and a sensible change in temperature results. The phase change material then acts as any other insulation and a gradual and continuous loss or addition of heat and, hence, rise or decline in temperature of the body results.

The result of this phase change material as a capacitor is that, in the ideal sense of continuous coverage, the heat transfer dynamics between the environment and this barrier and the heat transfer dynamics especially designed for thermal comfoπ inside this barrier have been de coupled. The quantities of phase change material required to maintain this de coupling is the mass whose equivalent heat of fusion equals the difference between the average Qι oss and Qequil for the time period and environmental limits considered.

Again refer to the simplification of the steady state heat transfer process description of figure 2. Suppose that the same original lay-up is retained, however, a 1/8" layer of a hypothetical phase change material with a melting point equal to 71 F and a heat of fusion equal to 104 B/lbm has been added to constitute this thermal capacitor. Again, for example purposes only, suppose that the following conditions are true:

hf = 104 B/lbm

T s ink = 71 F Tskin = 90 F T e ι = 43 F T e2 = 33 F xi = 3/16" x2 = l/8" x 3 = 3/16" ki = 0.03 B/hr-ft-F k 2 = 0.02 B/hr-ft-F

k 3 = 0.2 B/hr-ft-F h = 150 B/hr-ft 2 -F

A f = 18 ft2

Cpf = 0.83 B bm-F Qequil = 625 B/hr

From equation [2] it can be shown that the desired Qequil is indeed attained. As Qequil serves to induce a solid to liquid phase transition of the phase change material, the heat flow from the opposite side of this barrier or buffer to the external environment, O OS s» simultaneously serves to induce a liquid to solid phase change. O oss is estimated from equation [3].

Qloss — (Tskin-Te) [3]

For T e 2 = 43 F, Qι oss = 619 B/hr and for T e ι= 33 F, Qι 0S s = 840 B/hr. Regardless of the change in external environment and Qj 0 ss > Qequil w iU De maintained as long as sufficient thermal capacitance of the phase change material is provided. Finally, the quantity of phase change material required to maintain this de coupling with the environment, assuming Te2 = 33F and a 215 B/hr delta between Qequil and Ojoss, is computed by equation [4] to be equivalent to 2 lbm/hr.

- m « a„s_. o s = (Qloss \' r Q—equil) At [4J h f

Since the thermal capacity of this 1/8" layer is 840 B and the de coupling requires 215 B/hr capacitance, continuous thermal equilibrium and comfoπ is maintained for close to four hours (for comparison, this same change of environments for the traditional diving suit resulted in a 1.5 F/hr drop in body core temperature of a 150 Ibm individual). After this point, the wax must be warmed and regenerated to its Uquid state to maintain this same thermal equilibrium. If not, the thermal performance will simply reduce to that of the traditional diving suit where Qι 0S s is defined as in equation [1] with the additional resistance of the phase change material layer.

IntelUgent choices of phase change melt points and lay-ups can be made such that regeneration can be accomplished by exposing the capacitor to a warm beach, to a high solar flux environment or to a room temperature environment. In order to minimize mass, it is desirable to choose the insulation values and thicknesses as well as phase change melt temperatures so that Qequil is achieved while minimizing O 0 ss-An active, yet still simple, alternative procedure for regeneration might be the use of a hand dryer or portable heat source. This same philosophy can be applied to ski boots, work boots, shoes, socks, shoe liners, garment liners, face masks, etc. The lay-up, dimensions, phase change material and propeπies were chosen for illustrative purposes to demonstrate the advantage in a diving suit. Obviously,

variations on this concept are limitless and larger environmental envelopes must be considered as a lay-up and design is optimized.

Example 2: Thermal Capacitor Ski or Spoπ Boot A simpUfication of the heat transfer process in a prior an ski boot is shown in figure 16.

The term, Qequil, refers to the amount of heat generated from the foot such that, if removed, no uncomfortable or medicaUy unsafe net heat storage or loss in the foot results. Hence, thermal comfoπ is maintained. The term, Q oss , refers to the amount of heat lost from the foot, through the boot and to the external environment. When Qequil, or the amount of heat desirable to remove, is less than Qj oss , chilling of the foot occurs and vice versa.

For example purposes only, suppose that the following conditions are true:

Tskin = 83.5 F T e ι = 15 F

T e2 = 5 F xi = 3/16" x 2 = l" ki = 0.035 B/hr-ft-F k2 = 0.05 B/hr-ft-F h = 30 B/hr-ft2-F A f = 0.67 ft2 C p f = 0.83 B/lbm-F Qequil = 19.9 B/hr

From these givens, one can compute Qj oss according to equation [5], below, to be equal to 21.4 B/hr in a 15 F environment and 27.5 B/hr in a 5 F environment. If one assumes no distribution of heat via the bloodstream, local chilling of the foot results and one can conservatively estimate a drop in temperature equal to 2 F/hr for the first case and 10.4 F/hr for the latter. Although this is less likely the case, had Qequil exceeded Qioss, a rise in foot temperature would occur with a tendency towards overheating.

Qoss - (Tskin-Te) [5]

The disadvantage of the current practice to strictly use insulation for thermal control is that the thermal resistance is fixed in the boot. As explained above, to avoid overheating or chilUng, i.e. thermal discomfoπ, a balance must be achieved between the heat generated in the foot, Qequil, and the heat flow out of the foot, Qioss- Since environmental conditions change constantly and

since theπnal conditions of the foot are directly Unked to the changing environment through this fixed heat transfer path, no latitude exists to achieve this balance at conditions other than those at the single environment for which a solution exists.

An example of a thermal capacitor ski boot cross section is illustrated in figure 19. For this example, the same boot of figure 18 has been used, however, integral to the boot is a layer of phase change material, enclosed or encapsulated in an impermeable membrane, that acts as a thermal capacitor. The phase change material can be any paraffin, salt, crystalUne, etc. material the undergoes a phase transition at a temperature appropriate to maintain thermal comfoπ and at a temperature compatible with regeneration in an environment consistent with its use. The phase change material layer might be interspersed with highly conductive metallic fibers to improve heat distribution throughout this layer. The capacitor serves two purposes. The first is to maintain thermal equilibrium and, hence, continuous thermal comfoπ. The second is to act as a theπnal barrier or buffer to maintain this thermal equilibrium, for extended periods, regardless of changes in the external environment. The maintenance of thermal equilibrium is accomplished in the following manner. A phase change material is chosen such that, given its melt point and the heat transfer coefficient between the skin and its melt Une, Qequil can be attained according to equation [6], below.

Qequil ( I skin" -1 sink) 6]

Qequil is maintained fairly constant as long as the phase change material is undergoing a phase transition, either from solid to liquid or liquid to solid.

The function of the phase change material as a barrier or buffer evolves from the characteristic of a phase change process. As a phase change material undergoes a phase transition, depending upon its initial state, it can either absorb or emit a quantity of heat equal to its latent heat of fusion while stiU maintaining a constant temperature. In such a manner, heat can be lost or gained from either side of this barrier, yet the temperature at this barrier will remain constant. This remains true until all of the phase change material has either solidified or liquefied. After this point, all of the latent capacity of the phase change material has been consumed and a sensible change in temperature results. The phase change material then acts as any other insulation and a gradual and continuous loss or addition of heat and, hence, rise or decline in temperature of the foot results.

The result of this phase change material as a capacitor is that the heat transfer dynamics between the environment and this barrier and the heat transfer dynamics especially designed for thermal comfoπ inside this barrier have been de coupled. The quantities of phase change material required to maintain this de coupling is the mass whose equivalent heat of fusion equals the difference between the average Oj 0S s and Qequil for the time period and environmental limits considered.

Again refer to the simplified description of figure 18. Suppose that the same original lay- up is retained, however, a 1/4" layer of a hypothetical phase change material with a melting point equal to

50 F and a heat of fusion equal to 105 B/lbm has been added to constitute this thermal capacitor. Again, for example purposes only, suppose that the following conditions are true:

h f = 105 B/lbm

T S ink = 50 F

T skin = 83.5 F Tei = 15 F

T e2 = 5 F xi = 3/16"

X2 = 3/8"

X3 -. 1/4" X4 = 5/8" ki = 0.035 B/hr-ft-F k 2 = 0.05 B/hr-ft-F k 3 = 0.2 B/hr-ft-F h = 30 B/hr-ft 2 -F A f = 0.67 ft 2

C p f = 0.83 B/lbm-F

Qequil = 19-9 B/hr

From equation [6] it can be shown that the desired Qequil i indeed attained. As Qequil serves to induce a solid to liquid phase transition of the phase change material, the heat flow from the opposite side of this barrier or buffer to the external environment, Qj 0 ss, simultaneously serves to induce a liquid to solid phase change. O oss is estimated from equation [7].

Moss - (Tskin-Te) [7]

For Tei = 15 F, Qι 0S s = 1.4 B/hr and for T e 2= 5 F, Qι oss = 27.5 B/hr. Regardless of the change in external environment and Ojoss, Qequil will be maintained as long as sufficient thermal capacitance of the phase change material is provided. Finally, the quantity of phase change material required to maintain this de coupling with the environment, based on the extreme chosen, is computed by equation [8]. Assuming Te = 15 F and a 7.6 B/hr delta between Qequil and Qioss, this mass is computed to be 0.1 Ibm.

mass = [8] hf

Since the thermal capacity of this 1/4" layer is 63 B, continuous thermal equiUbrium and comfoπ is maintained for up to eight hours (for comparison, this same change of environments for the traditional suit resulted in an increase in the temperature drop of the foot from 2 F/hr to 10

F hr). After this point, the wax must be warmed and regenerated to its Uquid state to maintain this same thermal equiUbrium. If not, the thermal performance will simply reduce to that of the traditional ski boots where Qj oss is defined as in equation [5] with the additional resistance of the phase change material layer. IntelUgent choices of phase change melt points and lay-ups can be made such that regeneration can be accomplished by exposing the capacitor to a room temperature environment.

An active, yet stiU simple, alternative procedure for regeneration might be the use of a hand dryer. Thus, the invention offers a simple, reliable solution to the "cold feet" problem, whether it is applied to ski boots, work boots, shoes, socks, liners, etc. The lay-up, dimensions, phase change material and properties were chosen for illustrative purposes to demonstrate the advantage of such a boot Obviously, variations on this concept are limitless and larger environmental envelopes must be considered as a lay-up and design is optimized.

APPLICATIONS OF THE FLEXIBLE PCM COMPOSITE Figure 13 shows a diver\'s exposure suit 34, commonly called a wet suit, made in accordance with the present invention. One of the inherent problems in underwater diving is that water has such a high heat transfer coefficient and a high heat capacity that it draws heat out of the body very quickly. Even in tropical waters most divers have to wear an insulative exposure suit to prevent hypothermia. For some divers, however, an insulative wetsuit is not enough because they do not generate enough body heat to compensate for the heat loss to the surrounding water. In colder waters, even the hardiest divers must resoπ to expensive and complicated drysuits to prevent hypothermia.

Accordingly, this embodiment of the present invention takes the form of a diver\'s wetsuit made with the flexible PCM composite so that it provides the diver with a reservoir of heat to keep warm while diving. By way of example, the wetsuit shown is made of a material analogous to the three layer PCM composite in figures 2 and 4. The prefeπed matrix material is closed cell neoprene foam. There is an insulative outer layer A of the matrix material alone. The middle layer B has a high concentration of PCM as pellets or capsules. There is a thin inner layer C of the matrix material so that there is a good thermal coupling between the PCM and the wearer\'s skin. For mild water temperatures the PCM chosen can be a buffering PCM with a transition temperature between normal skin temperature and the water temperature. The buffering PCM does not reverse the heat flow from the body, but only slows it down to a normal level, so that the person remains warmer in the water longer. The amount of PCM can be chosen so that the

thermal mass is enough to act as a buffer for the duration of a normal dive, which seldom exceeds an hour for recreational divers.

Using a buffering PCM has an added benefit when diving in mild temperatures. When using a standard insulative wetsuit, upon resurfacing, a diver will quickly have to strip off the wetsuit to avoid overheating. A wetsuit with enough insulation to keep a diver warm in the water has much too much insulation for wearing in air. With the buffering PCM, however, when the skin temperature rises, it will start to melt the solidified PCM, regenerating the PCM for the next dive and protecting the wearer from overheating. Thus, the buffering action of the PCM protects the wearer from the extremes of high and low environmental temperatures. The buffering PCM can also be regenerated by taking the wetsuit indoors or putting it in a warm car until the next dive. For diving in cold water or for divers who always have trouble keeping warm, the composite can be made with a heating PCM. The PCM is chosen with a transition temperature above the skin temperature or even above body core temperature. Thus, the heat flow is reversed so that the PCM gives up heat to the body to compensate for the heat loss to the water from exposed skin. If the transition temperature is high enough to be beyond the comfoπ range for skin contact, the inner layer C should be thickened to regulate the heat flow between the PCM and the skin.

It is even conceivable that a wetsuit with a cooling PCM would be useful for the rare occasion when someone would be diving in very warm water such as a hot spring. Another application of the flexible PCM Composite is for cold weather wear. Again, a buffering PCM or a heating PCM can be chosen depending on the temperature extremes and the duration of use. Examples of cold weather wear that can benefit from the use of the flexible PCM composite are hats, socks, gloves, mittens, ski masks, and ski boot liners. Figure 14 shows a cross section of a modem downhill ski boot 36 to which has been added a flexible PCM composite inner Uner 35. The liner may be a permanent part of the boot or it may be made removable so that an already regenerated liner can be slipped into the boot between downhiU runs. This design is equally applicable to crosscountry ski boots, snowmobile boots and winter hiking boots. The flexibiUty of the PCM composite makes it far superior in this application to any of the prior art warming devices that use an inflexible PCM salt for heat storage. Figure 15 shows a glove 37 that has been made with a two layer flexible PCM composite.

Layer A is an outer insulating layer and layer B is the PCM-containing inner layer. The glove can be made with a closed cell polymer foam matrix for underwater use or with a breathable open cell foam for cold weather wear.

Another area of application of the flexible PCM composite is for therapeutic medical products. One example is a therapeutic blanket made of a flexible PCM composite in accordance with the present invention. If made with a cooling PCM having a transition temperature below normal skin temperature, such a blanket could be used for cooling febrile patients in a careful and controlled manner. It would not require frequently repeated applications the way alcohol baths do, and by careful choice of the PCM transition temperature it would avoid the danger of overcooUng

the patient that is inherent with ice packs. Alternatively, a heating PCM can be used to make a blanket that is useful for gently and controllably reheating hypothermia patients.

Another therapeutic medical use of the flexible PCM composite is to incorporate it into elastic wraps or oπhopedic joint supports. Thus hot or cold therapy can be combined with a supporting bandage for joints or muscles. Another medical use envisioned for the flexible PCM composite is to incorporate it into an artificial skin that can be used for protection of wounds from infection while simultaneously applying hot or cold therapy. A nonstick inner surface can be added to the composite for this application so that it does not adhere to the wound.

The flexible PCM composite of the present invention will also find a great many other uses in everyday items. For instance flexible containers can be made using a cooUng PCM to keep perishable foods or other material cold.

PHASE CHANGE THERMAL STORAGE BUILDING MATERIALS

Phase change thermal storage materials can also be used for thermal buffering in other thermal control applications. They can be used, for instance, in building panels, window insulation, temporary shelters, automobiles and environmental spaces for humans, plants and animals. Figure 20 shows an embodiment of a thermal storage window aπangement using phase change thermal storage materials. The window has a first layer of transparent material, such as glass or a transparent plastic enclosing a thermal insulation layer. The thermal insulation layer can be air or vacuum or a highly insulative material such as an aerogel. Behind the thermal insulation layer is a layer containing the phase change thermal storage material (PCM). The PCM layer is preferably transparent or translucent to allow light to pass through. One example of a translucent PCM layer can be made by absorbing glycerine into polyacrylimide, which is a superabsorbant material. Behind the PCM layer is a barrier layer, also preferably transparent. Optionally, the window will also contain a solar absorption/emission control layer next to the PCM layer. The solar control layer is capable of controlling the absoφtion of solar radiation and the emission of infrared radiation by changing the color of the panel. There are several methods for accompUshing this function. One method is to provide a panel with cells of white powder containing a magnetic black powder, such as iron or magnatite. A magnetic or electromagnetic field can be used to draw the magnetic black powder toward or away from the side of the panel facing the exterior. Thus the panel can be made black during the day to increase the absoφtion of solar radiation or it can be made white at night to decrease the emission of the stored thermal energy. Another method of controlling absoφtion or emission of thermal energy is to provide a Uquid crystal panel which can be made to change its tranparency or reflectivity by application of an electric field to the material.

Figure 21 shows another application of phase change thermal storage materials to windows for environmental thermal control. In this embodiment, the window has associated with it a panel of reversible louvers. The louvers are filled with an appropriate phase change thermal storage material. One side of the louvers is made with a highly absoφtive surface, for instance a black

colored surface. The other side of the louvers is made with a low absoφtion/low emissivity surface, for instance a white colored surface. The absoφtion or emissivity of the panel can be controUed by reversing the louvers to present either the black surface or the white surface to the exterior. The louvered PCM panel can be positioned inside a window as illustrated, or the panel can be put between the panes of a double pane window to thermally isolate the panel.

Phase change thermal storage materials can be effective as thermal buffering materials when used in building panels, window insulation or other applications by selecting the PCM with a phase transition temperature between the desired interior temperature of the building or structure and the exterior ambient environmental temperature. The buffering effect can be used to increase the efficiency of either heating or cooling of a structure. For instance, in winter it would be desirable to use the panels with the black side outward during the day and the white side outward at night to increase heating efficiency. In the summer it would be preferable to face the white side outward during the day and the black side outward at night to aid the efficiency of an air conditioning system.

Although the examples given include many specificities, they are intended as illustrative of only one possible embodiment of the invention. Other embodiments and modifications will, no doubt, occur to those skilled in the art. Thus, the examples given should only be inteφreted as illustrations of some of the prefeπed embodiments of the invention, and the full scope of the invention should be determined by the appended claims and their legal equivalents.