POLYCRYSTALLINE POROUS AL203 - BODIES ON THE BASIS OF MOLTEN ALUMINUM OXIDE COMPRISING AN INCREASED TOUGHNESS AND USE THEREOF
Document Type and Number:
WIPO Patent Application WO/2015/049273
Kind Code:
A1
Abstract:
The present invention relates to temperature-treated polycrystalline porous Al2O3 bodies comprising an amount of α aluminum oxide of more than 97% by weight, an amount of other oxide alloying components of a total of less than 3% by weight, a macroporosity of between 5 and 30 % by volume, wherein the Al2O3 bodies are composed of a plurality of AI2O3 primary crystals comprising a crystallite size of between 20 and 100 μm.

Inventors:
KUNZ REINER (DE)
MÖHMEL STEFFEN (AT)
Application Number:
PCT/EP2014/071017
Publication Date:
April 09, 2015
Filing Date:
October 01, 2014
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
CT FOR ABRASIVES AND REFRACTORIES REASEARCH AND DEV C A R R D GMBH (AT)
International Classes:
B24D3/00; C01F7/02; C01F7/027; C04B35/10; C04B35/101; C04B35/105; C04B35/107; C04B35/109; C04B35/111; C04B35/119; C04B35/653; C04B38/00; C09K3/14
Domestic Patent References:
WO2012041421A12012-04-05
WO2012041421A12012-04-05
Foreign References:
US20040049990A12004-03-18
EP1339809B12007-03-21
US4157898A1979-06-12
EP1339809B12007-03-21
US4157898A1979-06-12
EP1595081B12007-10-03
EP0152068B11991-03-20
EP0725045A11996-08-07
Other References:
See also references of EP 3052269A1
Attorney, Agent or Firm:
MARGUE, Robert, Germain (Theatinerstrasse 3, Munich, DE)
Download PDF:
Claims:
CLAIMS

1. Polycrystalline porous A1203 bodies of molten aluminum oxide comprising an amount of a aluminum oxide of more than 97% by weight and an amount of other oxide alloying components of a total of less than 3% by weight, wherein the Al203 bodies comprise a plurality of Al203 primary crystals having a crystallite size of between 20 and 100 pm and exhibit a macroporosity comprising a pore volume of between 5 and 30% by volume, an average diameter of the pores of between 20 and 60 μπι and a maximum pore diameter in the range of approx. 100 μτη,

characterized in that,

at the boundaries of the primary crystals, the

polycrystalline Al203 bodies comprise concentrations of individual Ti02 comprising extrinsic phases, wherein the extrinsic phases have a diameter of less than 7 μτη and are distributed individually in a punctiform manner or in lines along the primary crystal boundaries.

2. The Α120 bodies according to claim 1,

characterized in that

the extrinsic phases have a diameter of less than 5 pm,

3. The Al203 bodies according to claim 1 or 2 ,

characterized in that

the extrinsic phases comprise beside Ti02 other oxide alloying components selected from the group consisting of Cr203 , Fe203, MgO, Na20, NiO, ZnO, CoO, Zr02, Si02, Mn02 or oxides of rare earths .

4. The Al203 bodies according to one of claims 1 to 3,

characterized in that the amount of other oxide alloying components is less than 1% by weight .

The AI2O3 bodies according to one of claims 1 to 4, characterized in that

the Al203 bodies are abrasive grains, which are treated and sized into defined grit sizes.

The Al203 bodies according to claim 5,

characterized in that

the abrasive grains have a bulk density of less than 1.75 g/cm3, preferably less than 1.70 g/cm3 , and more preferably less than 1.65 g/cm3, in the grit sizes F24 F80 according to FEPA.

Description:
POLYCRYSTALLINE POROUS AL203 - BODIES ON THE BASIS OF MOLTEN ALUMINUM OXIDE COMPRISING AN INCREASED TOUGHNESS AND USE THEREOF

The present invention relates to polycrystalline porous Al 2 0 3 bodies on the basis of molten aluminum oxide, to a method for the production and use thereof, in particular in abrasives.

Abrasive grains on the basis of molten aluminum oxide, which is often also referred to in the literature as corundum, have been known for a long time and still belong to the most commonly used materials for machining surfaces today . Due to the plurality of the different materials, such as, e.g., wood, steel, stainless steel, plastics, stone, ceramics, among others, which are to be machined, types of corundum or special corundum, respectively, which match the respective applications and the physical characteristics of which were optimized for the corresponding case, were developed in the past .

For that purpose , diff rent processes can be chosen, wherein the corundum is either doped with other oxides and/or the production process is varied, so as to change in particular the physical characteristics of the abrasive grain, and/or to also subject the resulting abrasive grain to a post- treacment , so as to obtain special characteristics or so as to intensify them.

WO 2012/041421 discloses polycrystalline A1 2 0 3 bodies, which are produced by melting luminum oxide in an electric arc furnace and by subsequently pouring off the liquid melt . The pouring flow is thereby cooled down quickly, for the purpose of which the liquid melt is poured into a gap between two water-cooled rollers, for example, which rotate in opposite direction. To increase the cool-down speed, fine-particle aluminum oxide particles are additionally added to the pouring flow.

The solid material obtained in this manner is subsequently comminuted and treated to abrasive grit size by means of screening. Abrasive grains, which have a closed macroporosity and which are composed of individual primary crystals, which are connected to one another and which comprise a crystallite size of between 20 pm and 100 pm, are obtained in this manner. Such abrasive grains comprising a defined porosity and a defined crystalline structure have advantages, in particular for use in grinding discs.

EP - B- 1 339 809 describes a method for producing a compact dense abrasive grain on the basis of alumina comprising an increased toughness as well as the use thereof in abrasives. The finished abrasive grit is thereby subjected to a thermal post-treatment of between 800 and 1500°C.

Thermal post-treatments are also known from US-A-4 157 898.. Ti0 2 -containing corundum is annealed under oxidizing

conditions, wherein titanium suboxide, which is formed from the Ti0 2 during the melt, which is carried out under reducing conditions, is oxidized at the grain surface and titanium- aluminum compounds are formed, which comprise quadrivalent titanium and which effect a blue coloration of the surface of the abrasive grains .

In both of the latter cases, finished abrasive grains, which are composed so as to be compact and dense, are thermally post-treated, so as to increase the grain toughness thereof. In the case of certain grinding operations, the increase of the grain toughness correlates with an increase of the grinding performance .

In addition to the abrasive grains, which are composed so as to be compact and dense and which consist of very few large or individual crystallites, a number of abrasive grains, which are composed so as to be microcrystalline or

polycrystalline and which are composed, of a plurality of smaller crystallites and which have a high toughness based on the crystalline structure or the structure thereof alone, have been developed in particular in recent times . For instance , EP-B-l 595 081 describes the production of alumina zirconia , wherein zirconium oxide is melted together with aluminum oxide and the liquid melt is then cooled down as quickly as possible, so as to prevent a segregation of the components when cooling down, so that Zr0 2 and Al 2 0 3 are present in the product so as to be distributed homogenously next to one another in a microcrystalline structure -

Similar tough materials , which are also composed so as to be microcrystalline , can also be obtained via a chemical or ceramic process , respectively, wherein fine-particle fused alumina or a corresponding raw material, from which Al 2 0 3 results during the production process , is processed to form a green body, which is then sintered at temperatures of between 1200 and 1600°C. Microcrystalline sintered corundum, for example, is the subject matter of EP-B-0 152 068 or of EP--A-- 0 725 045.

In the past , a thermal post-treatment of this

microcrystalline or polycrystalline corundum has been avoided, because experience showed that the crystalline structure , which is responsible for the toughness, sustains damage in response to a thermal post - treatment due to crystal growth or, as in the case of the alumina zirconia, also due to modification transformations .

Successful thermal post-treatments are thus currently only known for compact and dense types of corundum consisting of a few large or single crystallites .

Due to the enormous range of the different materials ,

surfaces and shapes , which are to be machined, as well as due to the different demands on the machining process itself, not only the types of corundum, which are specified above in an exemplary manner, are preferably used, but there is

furthermore also still a need to better adapt abrasive grains to certain grinding operations or to special materials , so as to thus further improve the removal rate or the surface quality when machining the materials .

It is thus the task of the present invention to provide a corundum abrasive grain, which has a characteristic profile, which is optimized for certain grinding operations and which thus allows for a further optimization of the abrasive produced therefrom and of the grinding results .

It is also the task of the present invention to provide a method for producing a corresponding corundum abrasive grain .

The problem is solved by providing polycrystalline porous

Al 2 0 3 bodies on the basis of molten aluminum o ide comprising an amount of a aluminum oxide of more than 97% by weight and a amount of other oxide alloying components of a total of less than 3% by weight .

The Al 2 0 3 bodies are comprised of a plurality of Al 2 0 3 primary crystals comprising a crystallite size of between 20 and 100 μπι and exhibit a macroporosity comprising a pore volume of between 5 and 30 % by volume, an average diameter of the pores of between 20 and 60 pm, and a maximum pore diameter in the range of appro . 100 urn. At the boundaries of the primary crystals , the polycrystalline A1 2 0 3 bodies exhibit

concentrations of individual extrinsic phases , which are distributed individually in a punctiform manner or also in lines along the primary crystal boundaries . The extrinsic phases have a diameter of less than 7 um, preferably less than 5 pm .

In a preferred embodiment of the present invention , the extrinsic phases comprise Ti0 2 and/or other oxide alloying components selected from the group consisting of Cr 2 0 3 , Pe 2 0 3 , MgO, Na 2 0, NiO, ZnO, CoO, Zr0 2 , Si0 2 , Mn0 2 or oxides of rare earths .

The above -described polycrystalline Al 2 C¾ bodies are obtained by means of a thermal post - treatment of polycrystalline Al 2 0 3 bodies comprising small quantities of Ti0 2 and/or of other oxide alloying components , as can be produced according to WO 2012/041421, for example .

The production of the abrasive grains according to the invention on the basis of polycrystalline A1 2 0 3 bodies comprises a sequence of process steps , starting with the melting of a mixture of at least 97% by weight of aluminum oxide and at most 3% by weight of other oxide alloying components in an electric arc furnace . After completely melting the mixture , the liquid melt is poured off at a constant pouring rate of less than 80 kg/min . When pouring, fine aluminum oxide particles are added to the pouring strea . The cool- down of the melt is accelerated in this manner . The complete cool -down of the melt then takes place by pouring the melt into a narrow gap between metal plates, via cooled rollers, which rotate in opposite direction, or also by pouring off onto cooling plates. After the cool-down, polycrystalline Al 2 0 3 bodies are present in the form of coarse pieces or plates, which are then comminuted and are

subsequently screened to a defined abrasive grit size. The essential step for the invention is the subsequent tempering of the abrasive grains, which are obtained in this manner, for 5 - 60 minutes at a temperature of between 1000 and

1400°C. Preferably, the thermal post- treatment takes place for 15 minutes at 1250 °C in a rotary kiln.

As result of the tests, which were carried out in the context of the present invention, it was found that the previous comminuting and screening of the finished abrasive grit prior to the tempering has a significant impact on the quality of the abrasive grain according to the invention . It was thus found that even though a tempering of the coarse pieces, which were obtained after the cool-down, and a subsequent comminuting also results in an improvement of the

characteristics of the abrasive grain, but that said

improvement is by far not as dramatic as in the reverse

order . The shape of the abrasive grain, which is obtained after comminuting, is cubic and blocky, wherein, due to the macroporosity of the base A1 2 0 3 bodies, the finished abrasive grit, however, exhibits a relatively low bulk density, which is less than 1.75 g/cm 3 , preferably less than 1.70 g/cm 3 , and more preferably less than 1.65 g/cm 3 , for the grit sizes F24 - F80 according to FEPA.

Surprisingly, it was now found that an enormous increase of the grain toughness can be obtained by means of a thermal post-treatment even in the case of polycrystalline porous

Al 2 0 3 bodies , in spite of the crystalline structure thereof and the porosity thereof, when the base products encompass small quantities of extrinsic oxides as alloying components. This effect is particularly remarkable and pronounced in the presence of small quantities of T±0 2 .

In addition to Ti0 2 , small portions of additional oxide alloying components selected from the group consisting of Cr 2 0 3 , Fe 2 0 3 , MgO, Na 2 0 , NiO, ZnO, CoO, Zr0 2 , Si0 2 , Mn0 2 and/or oxides of rare earths can also be present in the

polycrystalline Al 2 C 3 bodies according to the invention, wherein the sum of the additional alloying components is less than 3% by weight, preferably < 1% by weight. A positive effect, which, however, is not very pronounced, can also be observed when the extrinsic phases do not include Ti0 2 .

The character of the present invention is additionally illustrated by means of REM images, which are enclosed to the description as Figures 1 to 6.

Figure 1 shows a scanning electron micrograph of a polished section of a polycrystalline abrasive grain

according to the invention in 1000- fold

magnification,

Figure 2 shows a scanning electron micrograph of a polished section of a polycrystalline abrasive grain

according to the invention in 2000-fold

magnification.

Figure 3 shows a scanning electron micrograph of a polished section of a comparative example in 1000-fold magnification. Figure 4 shows a scanning electron micrograph of a polished section of a comparative example in 1000 -fold magnification,

Figure 5 shows a scanning electron micrograph of

polycrystalline abrasive grains in 100-fold

magnification,

Figure 6 shows a scanning electron micrograph of compact

dense monocrystalline abrasive grains in 150- fold magnification,

The boundaries 3 of the primary crystals 1 can be identified in Figures 1 and 2 as dark border areas, which surround the individual primary crystals 1. The crystal boundaries are additionally highlighted by means of the increasingly

appearing individual light extrinsic phases 2 which comprise in the present case more than 88% by weight of Ti0 2 (example 4) , An EDX analysis of the extrinsic phases 2 thus resulted in a composition of 88.6% by weight of Ti0 2 , 0.7% by weight of Na 2 0, 0.1% by weight of MgO, 0.1% by weight of Si0 2 and 10.5% by weight of Al 2 0 3 . For the primary crystals 1» 99.5% by weight of Al 2 0 3 , 0.3% by weight of Si0 2 and in each case 0.1% by weight of CaO and Ti0 2 were analyzed. For the phase boundaries 3, 5.6% by weight of Na 2 0, 93.4% by weight of

Al 2 0 3 , 0.2% by weight of Si0 2 and 0.8% by weight of Ti0 2 were found. The black areas, which can be identified in the image, are pores 4, which form along the primary crystalline

boundaries. Figure 2 shows a polished section of an abrasive grain in 2000-fold magnification, in the case of which in particular the Ti0 2 -containing extrinsic phases 2, which are lined up along the crystallite boundary 3, can be seen. Figures 3 and 4 show a section through a base grain prior to the thermal treatment. Compared to the thermally post-treated grain according to the invention illustrated in Figures 1 or 2, it can be seen, that the quantity of the titanium- containing extrinsic phases 2 is considerably lower, the separations are coarser, and the shape of the separations is more platelet- like . It is thus assumed that the high

temperature of the thermal post-treatment leads to diffusion processes, which leads to an increased separation and to a finer punctiform distribution of the extrinsic phases 2 , It also appears that the temperature treatment or the diffusion effects , respectively, lead to a decrease of the thickness of the phase boundaries 3 -

The polycrystalline composition of the abrasive grains according to the invention, which are comprised of Al 2 0 3 primary crystals having a size of 20 - 100 ym and which are connected to one another , can be seen in Figure 5 in 100 -fold magnification . The fissured surface of the abrasive grains explains the good embedding thereof in a binding agent matrix of an abrasive and the good grinding performance resulting therefrom.

A conventional dense compact abrasive grain, which is composed so as to be monocrystalline and which has a

relatively smooth surface , can be seen in Figure 6 in a 150 - fold magnification as significant contrast to Figure 5, so that the abrasive grain exhibits indeed high grain strength, but it is only poorly embedded in the binding agent matrix.

To evaluate the quality of abrasive grains , it is essential to carry out grinding tests. Grinding tests are relative extensive and time-intensive . In the abrasive industry, it is thus common to evaluate the quality of abrasive grains in advance by means of mechanical characteristics, which can be accessed more easily and which serve as indications for the later behavior in the grinding test . In the context of the present works, the grain toughness of the abrasive grains was determined via the micro grain decomposition by milling in a ball mill.

Micro Grain, Decomposition, (MKZ)

To measure the micro grain decomposition, 10 g of corundum

(of a corresponding grit size) is milled in a ball mill, which is filled with 12 steel balls (diameter 15 mm, weight 330-332 g) at 188 revolutions per minute for a predetermined period of time. The milled grain is subsequently screened in a screening machine (Haver BCcker EHL 200) for 5 minutes via a corresponding fine sieve, which is 2 classes finer than the bottom sieve, which is defined for the corresponding grit size, and the fine portion is balanced out. The MKZ value follows from: sieve pass -through

MKZ (%) = x 100

total weight

In Table 1 below, several selected types of corundum are characterized, the micro grain decomposition of which, in addition to the bulk density, are then summarized in Table 2 and are compared to the abrasive grains according to the invention. Corundum from Treibacher Schleifmittel GmbH is used for the tests. For comparison, blocky and dense fused aluminum oxides (Fig. 6) , which are melted in a batch process, were also used in addition to polycrystalline corundum. The temperature treatment for the polycrystalline corundum was carried out for 15 minutes at 1250 °C in a rotary- kiln.

Table 1

Table 2

For the blocky and dense fused corundum (example 1 and 2} » the low MKZ values show a high toughness and grain strength, which is considerably higher for the alloyed corundum

(example 2} than for the white fused aluminum oxide (example 1) . In the case of the same chemical composition as in

example 2, the MKZ value for the polycrystalline porous corundum (example 3) is considerably higher. In response to corresponding applications, this material nonetheless shows very good grinding performance, which in particular also results from the fact that, due to its porous composition, the abrasive grain can be embedded very well in the abrasive (grinding belt or grinding disc) , wherein the binding agent penetrates into the outer open pores of the abrasive grain and the abrasive grain is anchored in the abrasive .

After a temperature treatment at 1250°C, the same grain shows a decrease of the MKZ value or an increase of the grain toughness, respectively, by approx . 32% . Completely new application possibilities follow from this for the abrasive grain according to the invention, because the porous

polycrystalline structure is now paired with relatively high grain toughness and the advantages of the good embedding can thus be combined with high grain strength.

It is known that the MKZ values are a function of the grain size. Further measurements were thus carried out with finer grit sizes . In the case of examples 5 - 8, it also became apparent for grit sizes F60 and F8C that enormous increases of the grain toughness are obtained by means of a thermal post-treatment . A grain toughness increase of appro . 24% is thus measured for grit size F60 (examples 5 and 6 ) , while even an increase by approx . 44% can be observed for grit size F80.

Ball Mill Grain Decomposition, (KMKZ)

The ball mill grain decomposition is a similar method for measuring the grain strength. Because of the larger sample quantities this method is more exact and less fault-prone. 100 g of corundum (of a corresponding grit size) are milled in a ball mill, which is filled with 8 big 35 mm diameter and 40 to 45 small. 14.7 mm diameter steel balls at 83 revolutions per minute for a predetermined period of time. After

separating the steel balls, the milled grain is subsequently- screened in a Ro ap screening machine for 5 minutes via a corresponding fine sieve, which is 2 classes finer than the bottom sieve, which is defined for the corresponding grit size , and the fine portion is balanced out . The K KZ value follows from: sieve pass-through

x 100

total weight

In the present case unalloyed polycrystailine corundum was compared with Ti0 2 alloyed polycrystailine corundum . The chemical compositions of both types of corundum are

summarized in table 1A

Table 1A

Example Type of Corundum Chemical

Composition

9, 13, 17 unalloyed Al 2 0 3 99.71 (comparison) polycrystall ine corundum Fe 2 0 3 0.04

Na 2 0 0.21 Si0 2 0.04

10, 14, 18 unalloyed

(comparison) polycrystailine corundum

temperature- treated

11, 15, 19 alloyed corundum

(comparison) polycrystall ine Na 2 0 0.20

Fe 2 0 3 0.04

12, 16, 20 alloyed Ti0 2 0.28 (invention) polycrystailine corundum Cr 2 0 3 0.06

temperature- reated Table 2A

The temperature treatment of the polycrystailine corundum was carried out in a rotary kiln at 1250°C for 15 minutes. The results of the ball mill grain decomposition are summarized in table 2A. It was found out that the untreated

polycrystailine corundum has comparable grain strength irrespective whether it is alloyed or unalloyed. Both types of corundum exhibit an improvement of grain strength after temperature-treatment , whereby the improvement for unalloyed polycrystailine corundum is below 20%, whereas the grain strength of the alloyed polycrystailine corundum increases more than 50%.

Grinding To also verify the positive effect of the MKZ values for the praxis grinding praxis , additional grinding tests were

carried out from the samples 1 to .

For this purpose , cutting discs were produced in the

dimensions 125 x 1.5 x 22.23, which, were then used to cut a stainless steel tube comprising the diameter of 20 mm and a thickness of 2 mm. 3 rough cuts were made initially for conditioning the disc and a total of 20 cuts were

subsequently made with each disc . The grinding performance was determined via the decrease of the disc diameter {disc wear) . The average values were in each case formed from 3 discs in response to the disc wear . The grinding results and the grinding condi ions are summarized in Table 3 below .

Table 3

Grinding machine FEIN WS14

Power 1.2 kW

Speed 8.300 rpm

Cutting rate 20

Workpiece tube 22/2

Material stainless

steel

dimension disc wear after

20 cuts

Abrasi e cutting disc 125 x 1.5

(decrease of the

X 22.23

diameter) abrasive exam le 1 8.4 mm

grain

example 2 4.5 mm

exam le 3 5.4 mm

example 4 3.9 mm In the case of the above- listed grinding conditions,, the cutting disc comprising the compact and dense white fused aluminum oxide shows the highest disc wear, which can be explained with the inferior embedding of the compact grain in the binding agent matrix and in particular with the

relatively low grain toughness. Compared thereto, the cutting disc comprising the tough alloyed corundum wears considerably less (approx. 45%) . The result of the cutting disc comprising polycrystalline porous corundum, which shows a disc wear, which, in spite of the very high MKZ value {example 3 = 23.6), is only slightly lower as compared to the compact and tough grain from example (2) , is surprising and can surely be explained with the good embedding of the porous

polycrystalline grain in the binding agent matrix. By tempering the abrasive grain at 1250°C for 15 minutes, the stability of the cutting disc, based on the decrease of the diameter, can be increased by approx. 30% and thus exceeds the extremely solid compact alloyed corundum.

It is important to note in this context that the above- described grinding test was mainly carried out so as to generally determine the suitability of the Al 2 0 3 bodies according to the invention as abrasive grains and so as to show the performance increase as compared to the untreated abrasive grain. For specific applications and grinding operations, in the case of which the porosity and the relatively high grain toughness of the abrasive grain according to the invention have a particularly positive impact, further performance increases in particular as compared to the compact and dense corundum types, are to be expected. Corresponding results were found for the precision grinding or also for the high-performance grinding with ceramic-bonded abrasive grains. In particular when used in abrasive discs, which should have a defined porosity, the use of the abrasive grains according to the invention leads to improvements as compared to the state of the art, because the desired porosity is now at least partially embodied by the abrasive grain itself, which is associated with the additional advantage that the cooling lubricant can be brought directly into the abrasive contact zone. On the one hand, the cutting ability of the abrasive disc is improved and the free cutting during the operating process is supported by introducing additional porosity in response to the use of the abrasive grain according to the invention. On the other hand, the embedding of the abrasive grain in the grinding disc is furthermore improved due to the polycrystall ine structure comprising a large, fissured surface, whereby the grinding performance is additionally increased.

In spite of the high macroporosity, the abrasive grain is extremely stable and can also be used for grinding

operations, in the case of which high contact pressures are applied. Even if, due to their composition, the

polycrystalline Al 2 0 3 bodies are predestined in particular for the use in grinding discs, they are also suitable for use as loose abrasive, for use in coated abrasives, for the

production of refractory materials and for use as wear protection materials.