POLYETHYLENE COMPOSITIONS AND ARTICLES MADE THEREFROM

INVENTORS: Dongming Li, Ching-Tai Lue, Adriana S. Silva, Matthew W. Holtcamp, David F. Sanders, Laughlin G. McCullough, Matthew S. Bedoya, and Subramaniam Kuppuswamy

CROSS REFERENCE TO RELATED APPLICATIONS

[0001] This application claims the benefit to Serial No. 62/575,818, filed October 23, 2017, and Serial No. 62/579,537, filed October 31, 2017, the disclosures of which are hereby incorporated by reference in their entireties.

FIELD OF THE INVENTION

[0002] The present disclosure relates to polyethylene (PE) compositions made from mixed metallocene catalyst systems and articles, such as films, made therefrom.

BACKGROUND OF THE INVENTION

[0003] Olefin polymerization catalysts are of great use in industry to produce polyolefin polymers and these polymers have revolutionized virtually every aspect of the modern world. Hence, there is strong interest in finding new catalyst systems to use in polymerization processes that increase the commercial usefulness of the catalyst systems and allow the production of polyolefin polymers having improved properties or a new combination of properties.

[0004] In particular, much effort has been placed in understanding how the comonomer is distributed along the polymer carbon chain or simply polymer chain of a polyolefin polymer. For example, the composition distribution of an ethylene alpha-olefin copolymer refers to the distribution of comonomer (short chain branches) among the molecules that comprise the polyethylene polymer. When the amount of short chain branches varies among the polymer carbon chain, the polymer or resin is said to have a Broad Composition Distribution (BCD). When the amount of comonomer per about 1000 carbons is similar among the polyethylene molecules of different polymer chain lengths or molecular weights, the composition distribution is said to be "narrow" or have a Narrow Composition Distribution (NCD).

[0005] The composition distribution is known to influence the properties of copolymers, for example, extractables content, environmental stress crack resistance, heat sealing, dart drop impact resistance, and tear resistance or strength. The composition distribution of a polyolefin may be readily measured by methods known in the art, for example, Temperature Raising

Elution Fractionation (TREF) or Crystallization Analysis Fractionation (CRYSTAF). See, for example, U.S. Patent No. 8,378,043, Col. 3 and Col. 4. [0006] Ethylene alpha-olefin copolymers may be produced in a low pressure reactor, utilizing, for example, solution, slurry, and/or gas phase polymerization processes. Polymerization takes place in the presence of activated catalyst systems such as those employing a Ziegler-Natta catalyst, a chromium based catalyst, a vanadium catalyst, a metallocene catalyst, a mixed catalyst (i.e., two or more different catalysts co-supported on the same carrier such as a bimodal catalyst), other advanced catalysts, or combinations thereof. In general, these catalysts when used in a catalyst system all produce a variety of polymer chains in a polyolefin polymer composition that vary in molecular weight and comonomer incorporation. In some cases, this variation becomes a "signature" to the catalyst itself.

[0007] For example, it is generally known in the art that a polyolefin's composition distribution is largely dictated by the type of catalyst used. For example, Broad Composition Distribution or BCD refers to polymers in which the length of the molecules would be substantially the same but the amount of the comonomer would vary along the length, for example, for an ethylene-hexene copolymer, hexene distribution varies from low to high while the molecular weight is roughly the same or the Polydispersity Index (PDI) is narrow.

[0008] Polymers made with Zeigler Natta catalysts are considered to be "conventional" in which the composition distribution is broad but the high molecular weight fractions are higher density (i.e., less comonomer) than the lower molecular weight fraction (high comonomer).

[0009] In contrast, metallocene catalysts typically produce a polyolefin polymer composition with an NCD. A metallocene catalyst is generally a metal complex of a transitional metal, typically, a Group 4 metal, and one or more cyclopentadienyl (Cp) ligands or rings. As stated above, NCD generally refers to the comonomer being evenly distributed or not vary much along the polymer chain. An illustration is provided below.

[0010] More recently, a third distribution has been described for a polyolefin polymer composition having a Broad Orthogonal Composition Distribution (BOCD) in which the comonomer is incorporated predominantly in the high molecular weight chains. A substituted hafnocene catalyst has been noted to produce this type of distribution. See, for example, U.S. Patent Nos. 6,242,545, 6,248,845, 6,528,597, 6,936,675, 6,956,088, 7,172,816, 7,179,876, 7,381,783, 8,247,065, 8,378,043, 8,476,392; U.S. Patent Application Publication No. 2015/0291748; and Serial No. 62/461,104, filed February 20, 2017, entitled Supported Catalyst Systems and Processes for Use Thereof. An illustration is provided below. This distribution has been noted for its improved physical properties, for example, ease in fabrication of end-use articles as well as stiffness and toughness in multiple applications such as films that can be measured by dart drop impact resistance and tear resistance or strength.

BOCD

[0011] As taught by U.S. Patent No. 8,378,043, BOCD refers to incorporating the comonomer predominantly in the high molecular weight chains. The distribution of the short chain branches can be measured, for example, using Temperature Raising Elution Fractionation (TREF) in connection with a Light Scattering (LS) detector to determine the weight average molecular weight of the molecules eluted from the TREF column at a given temperature. The combination of TREF and LS (TREF-LS) yields information about the breadth of the composition distribution and whether the comonomer content increases, decreases, or is uniform across the chains of different molecular weights.

[0012] In another patent, U.S. Patent No. 9,290,593 ('593 Patent) teaches that the term "BOCD" is a novel terminology that is currently developed and relates to a polymer structure. The term "BOCD structure" means a structure in which the content of the comonomer such as alpha olefins is mainly high at a high molecular weight main chain, that is, a novel structure in which the content of a short chain branching (SCB) is increased as moving toward the high molecular weight. The '593 Patent also teaches a BOCD Index. The BOCD Index may be defined by the following equation:

BOCD Index = (Content of SCB at the high molecular weight side

- Content of SCB at the low molecular weight side) / (Content of

SCB at the low molecular weight side)

wherein the "Content of SCB at the high molecular weight side" means the content of the SCB (the number of branches/1000 carbon atoms) included in a polymer chain having a molecular weight of Mw of the poly olefin or more and 1.3 ^χ Mw or less, and the "Content of SCB at the low molecular weight side" means the content of the SCB (the number of branches/1000 carbon atoms) included in a polymer chain having a molecular weight of 0.7 ^χ Mw of the polyolefin or more and less than Mw. The BOCD Index defined by equation above may be in the range of 1 to 5, preferably 2 to 4, more preferably 2 to 3.5. See, also, FIG. 1 and FIG. 2 of the '593 Patent (characterizing BOCD polymer structures using GPC-FTIR data).

[0013] BOCD behavior in a polymer composition has been associated with a good balance of mechanical and optical properties and has been an important goal in the development of new polymer products. For example, Linear Low Density Polyethylene (LLDPE) film applications and products strive for a good balance of stiffness, toughness, optical properties (e.g., haze and gloss) and processability. For some LLDPE film applications, sealing performance is also important. Sealing performance is affected mainly by density, it improves as density gets lower, but density has the opposite effect on stiffness. Therefore, to achieve a balanced performance, there is usually a trade-off between stiffness and sealing performance. Thus, to improve sealing performance while maintaining good stiffness remains a challenge. Past efforts have shown that namely molecular weight distribution and comonomer distribution interdependence (MWD x CD) has a strong effect on sealing performance, with narrow CD resin by metallocene catalyst outperforming broad CD resin by conventional catalysts. Other background references include U.S. Patent Application Publication No. 2009/0156764 and U.S. Patent Nos. 7,119,153, 7,547,754, 7,572,875, 7,625,982, 8,383,754, 8,691,715, 8,722,567, 8,846,841, 8,940,842, 9,006,367, 9,096,745, 9,115,229, 9,181,369, 9,181,370, 9,217,049, 9,334,350, and 9,447,265.

[0014] Thus, there is a need for polyethylene compositions that can exhibit, for example, BCD or BOCD behavior to produce LLDPE film products or other useful articles with a good balance of one or more of high stiffness, toughness and sealing performance, as well as good optical properties (e.g., haze and gloss).

SUMMARY OF THE INVENTION

[0015] In a class of embodiments, the invention provides for a polyethylene composition comprising at least 65 wt% ethylene derived units and from 0 to 35 wt% of C3-C12 olefin comonomer derived units, based upon the total weight of the polyethylene composition; wherein the polyethylene composition has:

a) an RCI,m of 100 kg/mol or greater;

and one or both of:

b) a Twi-Tw2 value of from -16 to -38°C; and

c) an Mwi/Mw2 value of at least 0.9;

and one or more of the following:

d) a density of from 0.890 g/cm ³ to 0.940 g/cm ³ ; e) a melt index (MI) of from 0.1 g/10 min to 30 g/10 min;

f) a melt index ratio (I21/I2) of from 10 to 90;

g) an Mw/Mn of from 2 to 12;

h) an Mz/Mw of from 2.5 to 5.0;

i) an Mz/Mn of from 10 to 40; and

j) a g'(vis) of 0.900 or greater.

[0016] In another class of embodiments, the invention provides for articles made from the polyethylene composition and processes for making the same.

BRIEF DESCRIPTION OF THE DRAWINGS

[0017] FIG. 1 is an ¾ NMR olefinic analysis of an exemplary bimodal polyethylene from gas phase ethylene/hexene polymerization using supported mixed catalyst: rac/meso Me2Si(3- (CH3)3SiCH2Cp)2HfMe2: rac, meso-(l-MeInd)2ZrMe2 Mixed Catalyst 1 : additive: Irganox™ 1010.

[0018] FIG. 2 is a graph of weight percent as a function of temperature of CFC data, demonstrating the calculation of T _w i and T _W 2 for various polymers.

[0019] FIG. 3 is a graph of weight average molecular weight as a function of temperature of CFC data, demonstrating the calculation of M _w i and M _W 2 for various polymers.

[0020] FIG. 4 is a plot of compositional presentation plotting (M _w i/M _W 2) values as a function of (Twi - Tw2) values.

[0021] FIG. 5 is a plot of average film modulus versus resin density for various inventive and comparative examples.

DETAILED DESCRIPTION

[0022] Before the present compounds, components, compositions, and/or methods are disclosed and described, it is to be understood that unless otherwise indicated this invention is not limited to specific compounds, components, compositions, reactants, reaction conditions, ligands, metallocene structures, catalyst structures, or the like, as such may vary, unless otherwise specified. It is also to be understood that the terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting.

[0023] In several classes of embodiments of the invention, the present disclosure is directed to catalyst systems and their use in polymerization processes to produce polyolefin polymers such as polyethylene polymers and polypropylene polymers. In another class of embodiments, the present disclosure is directed to polymerization processes to produce polyolefin polymers from catalyst systems comprising the product of the combination of one or more olefin polymerization catalysts, at least one activator, and at least one support.

[0024] In particular, the present disclosure is directed to a polymerization process to produce a polyethylene polymer, the process comprising contacting a catalyst system comprising the product of the combination of one or more metallocene catalysts, at least one activator, and at least one support, with ethylene and one or more C3-C10 alpha-olefin comonomers under polymerizable conditions.

Definitions

[0025] For purposes of this invention and the claims hereto, the numbering scheme for the Periodic Table Groups is according to the new notation of the IUPAC Periodic Table of Elements.

[0026] As used herein, "olefin polymerization catalyst(s) refers to any catalyst, typically an organometallic complex or compound that is capable of coordination polymerization addition where successive monomers are added in a monomer chain at the organometallic active center.

[0027] The terms "substituent," "radical," "group," and "moiety" may be used interchangeably.

[0028] As used herein, and unless otherwise specified, the term "Cn" means hydrocarbon(s) having n carbon atom(s) per molecule, wherein n is a positive integer.

[0029] As used herein, and unless otherwise specified, the term "hydrocarbon" means a class of compounds containing hydrogen bound to carbon, and encompasses (i) saturated hydrocarbon compounds, (ii) unsaturated hydrocarbon compounds, and (iii) mixtures of hydrocarbon compounds (saturated and/or unsaturated), including mixtures of hydrocarbon compounds having different values of n.

[0030] The terms "hydrocarbyl radical," "hydrocarbyl," "hydrocarbyl group," "alkyl radical," and "alkyl" are used interchangeably throughout this document. Likewise, the terms "group," "radical," and "substituent," are also used interchangeably in this document. For purposes of this disclosure, "hydrocarbyl radical" is defined to be C1-C100 radicals, that may be linear, branched, or cyclic, and when cyclic, aromatic or non-aromatic. Examples of such radicals include, but are not limited to, methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert-butyl, pentyl, iso-amyl, hexyl, octyl cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cyclooctyl, and the like including their substituted analogues. Substituted hydrocarbyl radicals are radicals in which at least one hydrogen atom of the hydrocarbyl radical has been substituted with at least one heteroatom or heteroatom containing group, such as halogen (such as Br, CI, F or I) or at least one functional group such as NR*2, OR*, SeR*, TeR*, PR*2, AsR*2, SbR* ₂ , SR*, BR* ₂ , SiR* ₃ , GeR* ₃ , SnR* ₃ , PbR* ₃ , and the like, or where at least one heteroatom has been inserted within a hydrocarbyl ring.

[0031] As used herein, and unless otherwise specified, the term "alkyl" refers to a saturated hydrocarbon radical having from 1 to 12 carbon atoms (i.e. , C1-C12 alkyl), particularly from 1 to 8 carbon atoms (i.e. , Ci-Ce alkyl), particularly from 1 to 6 carbon atoms (i.e. , Ci-Ce alkyl), and particularly from 1 to 4 carbon atoms (i.e., C1-C4 alkyl). Examples of alkyl groups include, but are not limited to, methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, decyl, and so forth. The alkyl group may be linear, branched or cyclic. "Alkyl" is intended to embrace all structural isomeric forms of an alkyl group. For example, as used herein, propyl encompasses both n-propyl and isopropyl; butyl encompasses n-butyl, sec-butyl, isobutyl and tert-butyl and so forth. As used herein, "Ci alkyl" refers to methyl (-CH ₃ ), "C2 alkyl" refers to ethyl (- CH ₂ CH ₃ ), "C ₃ alkyl" refers to propyl (-CH ₂ CH ₂ CH ₃ ) and "C ₄ alkyl" refers to butyl (e.g. , - CH ₂ CH ₂ CH ₂ CH ₃ ,-(CH ₃ )CHCH ₂ CH ₃ , -CH ₂ CH(CH ₃ ) ₂ , etc.). Further, as used herein, "Me" refers to methyl, and "Et" refers to ethyl, "i-Pr" refers to isopropyl, "t-Bu" refers to tert-butyl, and "Np" refers to neopentyl.

[0032] As used herein, and unless otherwise specified, the term "alkylene" refers to a divalent alkyl moiety containing 1 to 12 carbon atoms (i.e., Ci-Ci ₂ alkylene) in length and meaning the alkylene moiety is attached to the rest of the molecule at both ends of the alkyl unit. For example, alkylenes include, but are not limited to, -CH ₂ -, -CH ₂ CH ₂ - - CH(CH ₃ )CH ₂ - -CH ₂ CH ₂ CH ₂ - etc. The alkylene group may be linear or branched.

[0033] As used herein, and unless otherwise specified, the term "alkenyl" refers to an unsaturated hydrocarbon radical having from 2 to 12 carbon atoms (i.e., C ₂ -Ci ₂ alkenyl), particularly from 2 to 8 carbon atoms (i.e. , C ₂ -Cs alkenyl), particularly from 2 to 6 carbon atoms (i.e. , d-Ce alkenyl), and having one or more (e.g., 2, 3, etc.,) carbon-carbon double bonds. The alkenyl group may be linear, branched or cyclic. Examples of alkenyls include, but are not limited to ethenyl (vinyl), 2-propenyl, 3-propenyl, 1 ,4-pentadienyl, 1,4-butadienyl, 1-butenyl, 2-butenyl and 3-butenyl. "Alkenyl" is intended to embrace all structural isomeric forms of an alkenyl. For example, butenyl encompasses 1,4-butadienyl, 1-butenyl, 2-butenyl and 3-butenyl, etc.

[0034] As used herein, and unless otherwise specified, the term "alkenylene" refers to a divalent alkenyl moiety containing 2 to about 12 carbon atoms (i.e. , C ₂ -Ci ₂ alkenylene) in length and meaning that the alkylene moiety is attached to the rest of the molecule at both ends of the alkyl unit. For example, alkenylenes include, but are not limited to, -CH=CH-,- CH=CHCH ₂ - -CH=CH=CH- -CH ₂ CH ₂ CH=CHCH ₂ -, etc. The alkenylene group may be linear or branched.

[0035] As used herein, and unless otherwise specified, the term "alkynyl" refers to an unsaturated hydrocarbon radical having from 2 to 12 carbon atoms (i.e. , C ₂ -Ci ₂ alkynyl), particularly from 2 to 8 carbon atoms (i.e. , C ₂ -Cs alkynyl), particularly from 2 to 6 carbon atoms (i. e. , d-Ce alkynyl), and having one or more (e.g. , 2, 3, etc.) carbon-carbon triple bonds. The alkynyl group may be linear, branched or cyclic. Examples of alkynyls include, but are not limited to ethynyl, 1-propynyl, 2-butynyl, and 1,3-butadiynyl. "Alkynyl" is intended to embrace all structural isomeric forms of an alkynyl. For example, butynyl encompasses 2- butynyl, and 1,3-butadiynyl and propynyl encompasses 1-propynyl and 2-propynyl (propargyl).

[0036] As used herein, and unless otherwise specified, the term "alkynylene" refers to a divalent alkynyl moiety containing 2 to about 12 carbon atoms (i.e. , C ₂ -Ci ₂ alkenylene) in length and meaning that the alkylene moiety is attached to the rest of the molecule at both ends of the alkyl unit. For example, alkenylenes include, but are not limited to, -C≡C-, C≡CCH ₂ - -C≡CCH ₂ C≡C- -CH ₂ CH ₂ C≡CCH ₂ -. The alkynylene group may be linear or branched.

[0037] As used herein, and unless otherwise specified, the term "alkoxy" refers to ~0~ alkyl containing from 1 to about 10 carbon atoms. The alkoxy may be straight-chain or branched-chain. Non-limiting examples include methoxy, ethoxy, propoxy, butoxy, isobutoxy, tert-butoxy, pentoxy, and hexoxy. "Ci alkoxy" refers to methoxy, "C ₂ alkoxy" refers to ethoxy, "C3 alkoxy" refers to propoxy and "C4 alkoxy" refers to butoxy. Further, as used herein, "OMe" refers to methoxy and "OEt" refers to ethoxy.

[0038] As used herein, and unless otherwise specified, the term "aromatic" refers to unsaturated cyclic hydrocarbons having a delocalized conjugated π system and having from 5 to 20 carbon atoms (aromatic Cs-C ₂ o hydrocarbon), particularly from 5 to 12 carbon atoms (aromatic C5-Ci ₂ hydrocarbon), and particularly from 5 to 10 carbon atoms (aromatic C5-C hydrocarbon). Exemplary aromatics include, but are not limited to benzene, toluene, xylenes, mesitylene, ethylbenzenes, cumene, naphthalene, methylnaphthalene, dimethylnaphthalenes, ethylnaphthalenes, acenaphthalene, anthracene, phenanthrene, tetraphene, naphthacene, benzanthracenes, fiuoranthrene, pyrene, chrysene, triphenylene, and the like, and combinations thereof.

[0039] Unless otherwise indicated, where isomers of a named alkyl, alkenyl, alkoxy, or aryl group exist (e.g., n-butyl, iso-butyl, sec-butyl, and tert-butyl) reference to one member of the group (e.g., n-butyl) shall expressly disclose the remaining isomers (e.g., iso-butyl, sec- butyl, and tert-butyl) in the family. Likewise, reference to an alkyl, alkenyl, alkoxide, or aryl group without specifying a particular isomer (e.g., butyl) expressly discloses all isomers (e.g., n-butyl, iso-butyl, sec-butyl, and tert-butyl).

[0040] As used herein, the term "hydroxyl" refers to an -OH group.

[0041] As used herein, "oxygenate" refers to a saturated, unsaturated, or poly cyclic cyclized hydrocarbon radical containing from 1 to 40 carbon atoms and further containing one or more oxygen heteroatoms.

[0042] As used herein, "aluminum alkyl adducts" refers to the reaction product of aluminum alkyls and/or alumoxanes with quenching agents, such as water and/or methanol.

[0043] An "olefin," alternatively referred to as "alkene," is a linear, branched, or cyclic compound of carbon and hydrogen having at least one double bond. For purposes of this specification and the claims appended thereto, when a polymer or copolymer is referred to as comprising an olefin, the olefin present in such polymer or copolymer is the polymerized form of the olefin. For example, when a copolymer is said to have an "ethylene" content of 35 wt% to 55 wt%, it is understood that the mer unit in the copolymer is derived from ethylene in the polymerization reaction and said derived units are present at 35 wt% to 55 wt%, based upon the weight of the copolymer.

[0044] A "polymer" has two or more of the same or different mer units. A "homopolymer" is a polymer having mer units that are the same. A "copolymer" is a polymer having two or more mer units that are distinct or different from each other. A "terpolymer" is a polymer having three mer units that are distinct or different from each other. "Distinct" or "different" as used to refer to mer units indicates that the mer units differ from each other by at least one atom or are different isomerically. Accordingly, the definition of copolymer, as used herein, includes terpolymers and the like. An "ethylene polymer" or "ethylene copolymer" is a polymer or copolymer comprising at least 50 mol% ethylene derived units, a "propylene polymer" or "propylene copolymer" is a polymer or copolymer comprising at least 50 mol% propylene derived units, and so on. [0045] "Polymerizable conditions" refer those conditions including a skilled artisan's selection of temperature, pressure, reactant concentrations, optional solvent diluents, reactant mixing/addition parameters, and other conditions within at least one polymerization reactor that are conducive to the reaction of one or more olefin monomers when contacted with an activated olefin polymerization catalyst to produce the desired polyolefin polymer through typically coordination polymerization.

[0046] The term "continuous" means a system that operates without interruption or cessation. For example a continuous process to produce a polymer would be one where the reactants are continually introduced into one or more reactors and polymer product is continually withdrawn.

[0047] A "catalyst composition" or "catalyst system" is the combination of at least one catalyst compound, a support material, an optional activator, and an optional co-activator. For the purposes of this invention and the claims thereto, when catalyst systems or compositions are described as comprising neutral stable forms of the components, it is well understood by one of ordinary skill in the art, that the ionic form of the component is the form that reacts with the monomers to produce polymers. When it is used to describe such after activation, it means the support, the activated complex, and the activator or other charge-balancing moiety. The transition metal compound may be neutral as in a precatalyst, or a charged species with a counter ion as in an activated catalyst system.

[0048] Coordination polymerization is an addition polymerization in which successive monomers are added to or at an organometallic active center to create and/or grow a polymer chain.

[0049] The terms "cocatalyst" and "activator" are used herein interchangeably and are defined to be any compound which can activate any one of the catalyst compounds herein by converting the neutral catalyst compound to a catalytically active catalyst compound cation.

[0050] The term "contact product" or "the product of the combination of is used herein to describe compositions wherein the components are contacted together in any order, in any manner, and for any length of time. For example, the components can be contacted by blending or mixing. Further, contacting of any component can occur in the presence or absence of any other component of the compositions described herein. Combining additional materials or components can be done by any suitable method. Further, the term "contact product" includes mixtures, blends, solutions, slurries, reaction products, and the like, or combinations thereof. Although "contact product" can include reaction products, it is not required for the respective components to react with one another or react in the manner as theorized. Similarly, the term "contacting" is used herein to refer to materials which may be blended, mixed, slurried, dissolved, reacted, treated, or otherwise contacted in some other manner.

[0051] "BOCD" refers to a Broad Orthogonal Composition Distribution in which the comonomer of a copolymer is incorporated predominantly in the high molecular weight chains or species of a poly olefin polymer or composition. The distribution of the short chain branches can be measured, for example, using Temperature Raising Elution Fractionation (TREF) in connection with a Light Scattering (LS) detector to determine the weight average molecular weight of the molecules eluted from the TREF column at a given temperature. The combination of TREF and LS (TREF-LS) yields information about the breadth of the composition distribution and whether the comonomer content increases, decreases, or is uniform across the chains of different molecular weights of polymer chains. BOCD has been described, for example, in U. S. Patent Nos. 8,378,043, Col. 3, line 34, bridging Col. 4, line 19, and 8,476,392, line 43, bridging Col. 16, line 54.

[0052] The breadth of the composition distribution is characterized by the T75- T25 value, wherein T25 is the temperature at which 25% of the eluted polymer is obtained and T75 is the temperature at which 75% of the eluted polymer is obtained in a TREF experiment as described herein. The composition distribution is further characterized by the Fso value, which is the fraction of polymer that elutes below 80°C in a TREF-LS experiment as described herein. A higher Fso value indicates a higher fraction of comonomer in the polymer molecule. An orthogonal composition distribution is defined by a M60/M90 value that is greater than 1 , wherein Μβο is the molecular weight of the polymer fraction that elutes at 60°C in a TREF-LS experiment and M90 is the molecular weight of the polymer fraction that elutes at 90°C in a TREF-LS experiment as described herein.

[0053] In a class of embodiments, the polymers as described herein may have a BOCD characterized in that the T75-T25 value is 1 or greater, 2.0 or greater, 2.5 or greater, 4.0 or greater, 5.0 or greater, 7.0 or greater, 10.0 or greater, 11.5 or greater, 15.0 or greater, 17.5 or greater, 20.0 or greater, 25.0 or greater, 30.0 or greater, 35.0 or greater, 40.0 or greater, or 45.0 or greater, wherein T25 is the temperature at which 25% of the eluted polymer is obtained and T75 is the temperature at which 75% of the eluted polymer is obtained in a TREF experiment as described herein.

[0054] The polymers as described herein may further have a BOCD characterized in that M60/M90 value is 1.5 or greater, 2.0 or greater, 2.25 or greater, 2.50 or greater, 3.0 or greater, 3.5 or greater, 4.0 or greater, 4.5 or greater, or 5.0 or greater, wherein Μβο is the molecular weight of the polymer fraction that elutes at 60°C in a TREF-LS experiment and M90 is the molecular weight of the polymer fraction that elutes at 90°C in a TREF-LS experiment as described herein.

[0055] Additionally, the polymers as described herein may further have a BOCD characterized in that Fso value is 1% or greater, 2% or greater, 3% or greater, 4% or greater, 5% or greater, 6% or greater, 7% or greater, 10% or greater, 11% or greater, 12% or greater, or 15% or greater, wherein Fso is the fraction of polymer that elutes below 80°C.

Olefin Polymerization Catalysts

Metallocene Catalysts

[0056] In a class of embodiments, the catalyst system may be a mixed metallocene catalyst system (i.e., comprising more than one catalyst) and comprise two or more catalysts described below such as a catalyst represented b the formula (A):

where:

M is Hf or Zr;

each R ¹ , R ² , and R ⁴ is independently hydrogen, alkoxide, or a Ci to C40 substituted or unsubstituted hydrocarbyl group (preferably a Ci to C20 substituted or unsubstituted hydrocarbyl group);

R ³ is independently hydrogen, alkoxide or a Ci to C40 substituted or unsubstituted hydrocarbyl group (preferably a Ci to C20 substituted or unsubstituted hydrocarbyl group), or is -R ²⁰ -SiR'3 or -R ²⁰ -CR'3 where R ²⁰ is hydrogen, or a Ci to C4 hydrocarbyl, and each R is independently a Ci to C20 substituted or unsubstituted hydrocarbyl, provided that at least one R' is not H; each R ⁷ , R ⁸ , and R ¹⁰ is independently hydrogen, alkoxide or a Ci to C40 substituted or unsubstituted hydrocarbyl group (preferably a Ci to C20 substituted or unsubstituted hydrocarbyl group);

R ⁹ is -R ²⁰ -SiR'3 or -R ²⁰ -CR'3 where R ²⁰ is hydrogen or a Ci to C4 hydrocarbyl (preferably R ²⁰ is CH2), and each R' is independently a Ci to C20 substituted or unsubstituted hydrocarbyl, (preferably R' is alkyl, such as Me, or aryl, such as phenyl), provided that at least one R' is not H, alternately 2 R are not H, alternately 3 R are not H;

T is a bridging group, such as CR ²¹ R ²² , where R ²¹ and R ²² are independently hydrogen, halogen, or a C1-C20 containing hydrocarbyl group (for example, linear hydrocarbyl group), substituted hydrocarbyl group, and optionally R ²¹ and R ²² join to form a substituted or unsubstituted, saturated, partially unsaturated or aromatic, cyclic or polycyclic substituent, optionally R ²¹ and R ²² are the same or different; and

each X is, independently, a univalent anionic ligand, or two X are j oined and bound to the metal atom to form a metallocycle ring, or two X are joined to form a chelating ligand, a diene ligand, or an alkylidene ligand (preferably halogen or C I to C12 alkyl or aryl, such as CI, Me, Et, Ph).

[0057] In a preferred embodiment of the invention, M is Hf, alternately M is Zr.

[0058] In a preferred embodiment of the invention, each R ¹ , R ² , and R ⁴ is independently hydrogen, or a substituted Ci to C12 hydrocarbyl group or an unsubstituted Ci to C12 hydrocarbyl group, preferably hydrogen, methyl, ethyl, propyl, butyl, pentyl, hexyl, or an isomer thereof.

[0059] In a preferred embodiment of the invention, each R ³ is independently hydrogen, or a substituted Ci to C12 hydrocarbyl group or an unsubstituted Ci to C12 hydrocarbyl group, preferably hydrogen, methyl, ethyl, propyl, butyl, pentyl, hexyl, or an isomer thereof or R ³ is - R ²⁰ -SiR'3 or -R ²⁰ -CR'3 where R ²⁰ is a Ci to C4 hydrocarbyl (preferably methyl, ethyl, propyl, butyl), and R is a Ci to C20 substituted or unsubstituted hydrocarbyl, preferably a substituted Ci to C12 hydrocarbyl group or an unsubstituted Ci to C12 hydrocarbyl group, preferably methyl, ethyl, propyl, butyl, pentyl, hexyl, or an isomer thereof.

[0060] In a preferred embodiment of the invention, each R ⁷ , R ⁸ , and R ¹⁰ is independently hydrogen, or a substituted Ci to C12 hydrocarbyl group or an unsubstituted Ci to C12 hydrocarbyl group, preferably hydrogen, methyl, ethyl, propyl, butyl, pentyl, hexyl, or an isomer thereof.

[0061] In a preferred embodiment of the invention, R ⁹ , is -R ²⁰ -SiR'3 or -R ²⁰ -CR'3 where R ²⁰ is a Ci to C4 hydrocarbyl (preferably methyl, ethyl, propyl, butyl), and R is a Ci to C20 substituted or unsubstituted hydrocarbyl, preferably a substituted Ci to C12 hydrocarbyl group or an unsubstituted Ci to C12 hydrocarbyl group, preferably methyl, ethyl, propyl, butyl, pentyl, hexyl, or an isomer thereof.

[0062] Alternately, R ⁹ and optionally R ³ are, independently, -R ²⁰ -CMe3, or -R ²⁰ -SiMe3 where R ²⁰ is a Ci to C4 hydrocarbyl (preferably methyl, ethyl, propyl, butyl), preferably -CH2- CMe ₃ , or -CH ₂ -SiMe ₃ .

[0063] Alternately, each X may be, independently, a halide, a hydride, an alkyl group, an alkenyl group or an arylalkyl group.

[0064] Alternately, each X is, independently, selected from the group consisting of hydrocarbyl radicals having from 1 to 20 carbon atoms, aryls, hydrides, amides, alkoxides, sulfides, phosphides, halides, dienes, amines, phosphines, ethers, and a combination thereof (two X's may form a part of a fused ring or a ring system), preferably each X is independently selected from halides, aryls and Ci to C5 alkyl groups, preferably each X is a phenyl, methyl, ethyl, propyl, butyl, pentyl, bromo, or chloro group.

[0065] Preferably, T is a bridging group containing at least one Group 13, 14, 15, or 16 element, in particular boron or a Group 14, 15 or 16 element. Examples of suitable bridging groups include P(=S)R, P(=Se)R, P(=0)R, R2C, R ₂ Si, R ₂ Ge, R2CCR2, R2CCR2CR2, R2CCR2CR2CR2, RC=CR, RC=CRCR ₂ , R ₂ CCR=CRCR2, RC=CRCR=CR, RC=CRCR ₂ CR2, R ₂ CSiR'2, R ₂ SiSiR'2, R ₂ SiOSiR'2, R2CSiR ₂ CR2, R2SiCR ₂ SiR2, RC=CRSiR ₂ , R ₂ CGeR2, R ₂ GeGeR2, R2CGeR ₂ CR2, R2GeCR ₂ GeR2, R ₂ SiGeR2, RC=CRGeR ₂ , RB, R2C-BR, R2C-BR-CR2, R2C-O-CR2, R2CR2C-O-CR2CR2, R' ₂ C- O-CR2CR2, R ₂ C-0-CR=CR, R2C-S-CR2, R2CR2C-S-CR2CR2, R2C-S-CR2CR2, R ₂ C-S-CR=CR, R ₂ C-Se-CR'2, R'2CR2C-Se-CR2CR2, R2C-Se-CR ₂ CR2, R ₂ C-Se- CR=CR, R ₂ C-N=CR, R2C-NR-CR2, R2C-NR-CR2CR2, R ₂ C-NR-CR=CR, R2CR2C- NR-CR2CR2, R ₂ C-P=CR, R2C-PR-CR2, O, S, Se, Te, NR, PR, AsR, SbR, O-O, S-S, RN-NR, RP-PR, O-S, O-NR, O-PR, S-NR, S-PR, and RN-PR, where R is hydrogen or a C1-C20 containing hydrocarbyl, substituted hydrocarbyl, halocarbyl, substituted halocarbyl, silylcarbyl or germylcarbyl substituent and optionally two or more adjacent R' may join to form a substituted or unsubstituted, saturated, partially unsaturated or aromatic, cyclic or poly cyclic substituent. Preferred examples for the bridging group T include CH2, CH2CH2, SiMe2, SiPh2, SiMePh, Si(CH ₂ ) ₃ , Si(CH ₂ ) ₄ , O, S, NPh, PPh, NMe, PMe, NEt, NPr, NBu, PEt, PPr, Me ₂ SiOSiMe ₂ , and PBu. [0066] In a preferred embodiment of the invention in any embodiment of any formula described herein, T is represented by the formula R¾J or (R¾J)2, where J is C, Si, or Ge, and each R ^a is, independently, hydrogen, halogen, Ci to C20 hydrocarbyl (such as methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, or dodecyl) or a Ci to C20 substituted hydrocarbyl, and two R ^a can form a cyclic structure including aromatic, partially saturated, or saturated cyclic or fused ring system. Preferably, T is a bridging group comprising carbon or silica, such as dialkylsilyl, preferably T is selected from CH2, CH2CH2, C(CH3)2, SiMe ₂ , SiPh ₂ , SiMePh, silylcyclobutyl (Si(CH ₂ ) ₃ ), (Ph) ₂ C, (p-(Et) ₃ SiPh) ₂ C, Me2SiOSiMe ₂ , and cyclopentasilylene (Si(CH2)4).

[0067] In a preferred embodiment of the invention, the molar ratio of rac to meso in the catalyst compound is from 1 : 1 to 100: 1, preferably 5: 1 to 90: 1, preferably 7: 1 to 80: 1, preferably 5: 1 or greater, or 7: 1 or greater, or 20: 1 or greater, or 30: 1 or greater, or 50: 1 or greater. In an embodiment of the invention, the catalyst comprises greater than 55 mol% of the racemic isomer, or greater than 60 mol% of the racemic isomer, or greater than 65 mol% of the racemic isomer, or greater than 70 mol% of the racemic isomer, or greater than 75 mol% of the racemic isomer, or greater than 80 mol% of the racemic isomer, or greater than 85 mol% of the racemic isomer, or greater than 90 mol% of the racemic isomer, or greater than 92 mol% of the racemic isomer, or greater than 95 mol% of the racemic isomer, or greater than 97 mol% of the racemic isomer, based on the total amount of the racemic and meso isomer, if any, formed. In a particular embodiment of the invention, the metallocene transition metal compound formed consists essentially of the racemic isomer.

[0068] Amounts of rac and meso isomers are determined by proton NMR. ¾ NMR data are collected at 23°C in a 5 mm probe using a 400 MHz Bruker spectrometer with deuterated methylene chloride. (Note that some of the examples herein may use deuterated benzene, but for purposes of the claims, methylene chloride shall be used.) Data is recorded using a maximum pulse width of 45°, 5 seconds between pulses and signal averaging 16 transients. The spectrum is normalized to protonated methylene chloride in the deuterated methylene chloride, which is expected to show a peak at 5.32 ppm.

[0069] Catalyst compounds that are particularly useful in this invention include one or more of: rac/meso Me2Si(Me3SiCH2Cp)2HfMe2; racMe2Si(Me3SiCH2Cp)2HfMe2; rac/meso Ph2Si(Me3SiCH2Cp)2HfMe ₂ ; rac/meso (CH2)3Si(Me ₃ SiCH ₂ Cp)2HfMe2; rac/meso (CH2)4Si(Me ₃ SiCH2Cp)2HfMe ₂ ; rac/meso (C6F ₅ )2Si(Me ₃ SiCH2Cp)2HfMe2; rac/meso (CH2)3Si(Me ₃ SiCH2Cp)2ZrMe2; rac/meso Me2Ge(Me3SiCH ₂ Cp)2HfMe2; rac/meso Me ₂ Si(Me2PhSiCH2Cp)2HfMe ₂ ; rac/meso Ph ₂ Si(Me2PhSiCH ₂ Cp)2HfMe2;

Me2Si(Me4Cp)(Me2PhSiCH2Cp)HfMe ₂ ; rac/meso (CH2)3Si(Me2PhSiCH ₂ Cp)2HfMe2; rac/meso (CH ₂ )4Si(Me2PhSiCH ₂ Cp)2HfMe2; rac/meso (C6F5)2Si(Me2PhSiCH ₂ Cp)2HfMe2; rac/meso Me2Ge(Me2PhSiCH2Cp)2HfMe2; rac/meso Me2Si(MePh2SiCH2Cp)2HfMe2; rac/meso Ph2Si(MePh2SiCH2Cp)2HfMe2; rac/meso Me2Si(MePh2SiCH2Cp)2ZrMe2; rac/meso

(CH2)3Si(MePh2SiCH2Cp)2HfMe ₂ ; rac/meso (CH ₂ )4Si(MePh2SiCH2Cp)2HfMe ₂ ; rac/meso

(C6F5)2Si(MePh2SiCH2Cp)2HfMe ₂ ; , rac/meso Me2Ge(MePh2SiCH2Cp)2HfMe ₂ ; rac/meso

Me2Si(Ph3SiCH2Cp)2HfMe ₂ ; rac/meso Ph2Si(Ph3SiCH ₂ Cp)2HfMe ₂ ; rac/meso

Me2Si(Ph ₃ SiCH ₂ Cp)2ZrMe2; rac/meso (CH2)3Si(Ph3SiCH ₂ Cp)2HfMe ₂ ; rac/meso

(CH2)4Si(Ph ₃ SiCH2Cp)2HfMe ₂ ; rac/meso (C6F5)2Si(Ph3SiCH ₂ Cp)2HfMe ₂ ; rac/meso

Me2Ge(Ph3SiCH2Cp)2HfMe ₂ ; rac/meso Me2Si(Cy3SiCH ₂ Cp)2HfMe2; racMe2Si(Cy3SiCH2Cp)2HfMe ₂ ; rac/meso Ph2Si(Cy3SiCH ₂ Cp)2HfMe ₂ ; rac/meso

Me2Si(Cy3SiCH2Cp)2ZrMe2; rac/meso (CH2)3Si(Cy3SiCH ₂ Cp)2HfMe ₂ ; rac/meso

(CH2)4Si(Cy3SiCH ₂ Cp)2HfMe ₂ ; rac/meso (C6F ₅ )2Si(Cy3SiCH2Cp)2HfMe ₂ ; rac/meso

Me2Ge(Cy3SiCH2Cp)2HfMe2; rac/meso Me2Si(Cy2MeSiCH2Cp)2HfMe ₂ ; rac/meso

Ph2Si(Cy2MeSiCH2Cp)2HfMe ₂ ; Me2Si(Me4Cp)(Cy2MeSiCH2Cp)HfMe ₂ ; rac/meso

(CH2)3Si(Cy2MeSiCH2Cp)2HfMe ₂ ; rac/meso (CH2)4Si(Cy2MeSiCH2Cp)2HfMe ₂ ; rac/meso

(C6F5)2Si(Cy2MeSiCH ₂ Cp)2HfMe2 ; rac/meso Me2Ge(Cy2MeSiCH2Cp)2HfMe ₂ ; rac/meso

Me2Si(CyMe2SiCH ₂ Cp)2HfMe2; rac/meso Ph2Si(CyMe2SiCH2Cp)2HfMe ₂ ; rac/meso

(CH2)3Si(CyMe2SiCH2Cp)2HfMe ₂ ; rac/meso (CH ₂ )4Si(CyMe2SiCH2Cp)2HfMe ₂ ; rac/meso

(C6F ₅ )2Si(CyMe2SiCH ₂ Cp)2HfMe2 ; rac/meso Me2Ge(CyMe2SiCH2Cp)2HfMe ₂ ; rac/meso

Me2Si(Cy2PhSiCH2Cp)2HfMe ₂ ; rac/meso Ph ₂ Si(Cy2PhSiCH2Cp)2HfMe ₂ ; rac/meso

(CH ₂ )3Si(Cy2PhSiCH2Cp)2HfMe ₂ ; rac/meso (CH ₂ )4Si(Cy2PhSiCH2Cp)2HfMe ₂ ; rac/meso

(C6F ₅ )2Si(Cy2PhSiCH2Cp)2HfMe ₂ ; rac/meso Me2Ge(Cy2PhSiCH2Cp)2HfMe ₂ ; rac/meso

Me2Si(CyPh2SiCH2Cp)2HfMe ₂ ; rac/meso Ph ₂ Si(CyPh2SiCH2Cp)2HfMe ₂ ; rac/meso

(CH2)3Si(CyPh ₂ SiCH ₂ Cp)2HfMe2; rac/meso (CH2)4Si(CyPh ₂ SiCH ₂ Cp)2HfMe2; rac/meso

(C6F ₅ )2Si(CyPh2SiCH2Cp)2HfMe ₂ ; and rac/meso Me2Ge(CyPh2SiCH ₂ Cp)2HfMe2.

[0070] In a preferred embodiment in any of the processes described herein, one catalyst compound is used, e.g., the catalyst compounds are not different. For purposes of this invention, one catalyst compound is considered different from another if they differ by at least one atom. For example, "bisindenyl zirconium dichloride" is different from "(indenyl)(2- methylindenyl) zirconium dichloride" which is different from "(indenyl)(2-methylindenyl) hafnium dichloride." Catalyst compounds that differ only by isomer are considered the same for purposes if this invention, e.g., rac-dimethylsilylbis(2-methyl 4-phenylindenyl)hafnium dimethyl is considered to be the same as meso-dimethylsilylbis(2-methyl 4- phenylindenyl)hafnium dimethyl.

[0071] Other useful olefin polymerization catalysts include metallocene catalyst compounds represented by the formula (B):

TyCp _m M ⁶ GnX ⁵ q (B),

wherein each Cp is, independently, a cyclopentadienyl group (such as cyclopentadiene, indene or fluorene) which may be substituted or unsubstituted, M ⁶ is a Group 4 transition metal, for example, titanium, zirconium, hafnium, G is a heteroatom group represented by the formula JR*z where J is N, P, O or S, and R* is a Ci to C20 hydrocarbyl group and z is 1 or 2, T is a bridging group, and y is 0 or 1, X ⁵ is a leaving group (such as a halide, a hydride, an alkyl group, an alkenyl group or an arylalkyl group), and m=l or 2, n=0, 1, 2 or 3, q=0, 1, 2 or 3, and the sum of m+n+q is equal to the oxidation state of the transition metal. See, for example, WO 2016/094843.

[0072] In an embodiment, each Cp is a cyclopentadiene, indene or fluorene, which may be substituted or unsubstituted, and each M ⁶ is titanium, zirconium, or hafnium, and each X ⁵ is, independently, a halide, a hydride, an alkyl group, an alkenyl group or an arylalkyl group. In any of the embodiments described herein, y may be 1, m may be one, n may be 1, J may be N, and R* may be methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, cyclooctyl, cyclododecyl, decyl, undecyl, dodecyl, adamantyl or an isomer thereof.

[0073] In yet another embodiment, the one or more olefin polymerization catalysts may comprise one or more metallocene catalysts of: bis(tetrahydroindenyl)Hf Me2; bis(l-butyl,3- methylcyclopentadienyl)ZrCl2; bis-(n-butylcyclopentadienyl)ZrCl2; (dimethylsilyl)20 bis(indenyl)ZrCl2; dimethylsilyl(3-(3-methylbutyl)cyclopentadienyl)(2,3,4,5- tetramethylcyclopentadienyl)ZrCl2; dimethylsilylbis(tetrahydroindenyl)ZrCl2; dimethylsilyl- (3-phenyl-indenyl)(tetramethylcyclopentadienyl)ZrCl2; dimethylsilyl(3- neopentylcyclopentadienyl)(tetramethylcyclopentadienyl)HfCl2 ; tetramethyldisilylene bis(4- (3,5-di-tert-butylphenyl)-indenyl)ZrCl2; cyclopentadienyl(l ,3- diphenylcyclopentadienyl)ZrCl2; bis(cyclopentadienyl)zirconium dichloride; bis(pentaniethylcyclopentadienyl)zirconium dichloride; bis(pentamethylcyclopeiUadienyl)zirconium dimethyl; is(pentarnethylcyclopentadienyl)hafnium dichloride; bis(pentamethylcyclopentadienyl)zircoiiiuni dimethyl; bis(l-methyl-3-n- butylcydopentadienyi)zireoniuni dichloride; bis(l-methyl-3-n- butylcydopentadienyf)zirconiuni dimethyl; bis(l-meth l-3-n-butylc clopentadien l)hafnium dichloride; bis(l -methyl-3-n-butylcyclopentadienyl)zirconium dimethyl; bis(indenyl)zirconium dichloride; bis(indenyl)zirconium dimethyl; bis(tetrahydro-l- indenyl)zirconium dichloride; hisitetrahy dro- 1 -indenyi)zirconium dimethyl; dimethylsily3bis(tetrahydroindenyl)zirconium dichloride; dimethylsilylbis(tetrahydromdenyl)zirconium dimethyl; dimethylsilylbis(indenyl)zircomum dichloride; dimethyisiiyl(bisindenyl)zirconium dimethyl; dimethylsilyibis(cyclopentadienyl)zirconium dichloride; or di metbylsi3ylbis(cy clopentadienyl)zirconi urn dimethyl .

[0074] In another embodiment, the one or more olefin polymerization catalyst compounds may comprise a first metallocene catalyst and a second metallocene catalyst independently selected from the group consisting of: SiMe2(Me4Cp)(cCi2N)TiMe2 and bis(l-Bu,3-Me-Cp) ZrCh; SiMe ₂ (Me4Cp)(cCi2N)TiMe2 and (SiMe ₂ ) bis(indenyl)ZrCl ₂ ; SiMe ₂ (Me4Cp)(cCi2N)TiMe2 and (SiMe ₂ ) ₂ 0 bis(indenyl)ZrCl ₂ ; SiMe ₂ (Me4Cp)(cCi2N)TiMe2 and (SiMe ₂ )20 bis(indenyl)ZrMe ₂ ; SiMe ₂ (Me4Cp)(cCi ₂ N)TiMe2 andSiMe ₂ (3- neopentylCp)((Me ₄ Cp)HfCl2; SiMe ₂ (Me4Cp)(cCi2N)TiMe2 and SiMe ₂ (3- neopentylcy clopentadienyl)(Me4Cp)HfMe2; SiMe2(Me4Cp)(l -adamantylamido)TiMe2 and bis(l-Bu,3-MeCp)ZrCh; and SiMe2(Me4Cp)(l-t-butylamido)TiMe2 and bis(l-Bu,3- MeCp)ZrCl ₂ .

[0075] In a class of embodiments, the one or more metallocene catalysts may comprise (4- propyl, 1 ,2-dimethylcy clopentadienyl)(cy clopentadienyl)hafhium dichloride;

(tetramethylcyclopentadienyl)(propylcyclopentadienyl)hafn ium dimethyl;

(tetramethylcyclopentadienyl)(propylcyclopentadienyl)zirc onium dimethyl; (3,4-dipropyl,l,2- dimethylcyclopentadienyl)(cyclopentadienyl)hafnium dimethyl;

(propylcyclopentadienyl)(methyl cyclopentadienyl)hafnium dimethyl;

(propylcyclopentadienyl)(cyclopentadienyl)hafhium dimethyl;

(tetramethylcyclopentadienyl)(benzylcyclopentadienyl)zirc onium dimethyl; silacyclopentyl(tetramethylcyclopentadienyl)(cyclopentadieny l)zirconium dichloride; dimethylsilyl(tetramethylcyclopentadienyl)(3-(l-hexenyl)cycl opentadienyl)zirconium dichloride; or dimethylsilyl(tetramethylcyclopentadienyl)(3- trimethylsilylmethylcyclopentadienyl)hafnium dimethyl. [0076] In another class of embodiments, the one or more metallocene catalysts may comprise bis(cyclopentadienyl)zirconium dichloride, bis(cyclopentadienyl)zirconium dimethyl, bis(n-butylcyclopentadienyl)zirconium dichloride, bis(n- butylcyclopentadienyl)zirconium dimethyl, bis(pentamethylcyclopentadienyl)zirconium dichloride, bis(pentamethylcyclopentadienyl) dimethyl, bis(pentamethylcyclopentadienyl)hafhium dichloride, bis(pentamethylcyclopentadienyl)zirconium dimethyl, bis(l-methyl-3-n- butylcyclopentadienyl)zirconium dichloride, bis(l-methyl-3-n- butylcyclopentadienyl)zirconium dimethyl, bis(l-methyl-3- phenylcyclopentadienyl)zirconium dichloride, bis(l-methyl-3- phenylcyclopentadienyl)zirconium dimethyl, bis(l-methyl-3-n- butylcyclopentadienyl)hafnium dichloride, bis(l-methyl-3-n- butylcyclopentadienyl)zirconium dimethyl, bis(indenyl)zirconium dichloride, bis(indenyl)zirconium dimethyl bis(tetrahy dro- 1 -indenyl)zirconium dichloride, bis(tetrahydro-l-indenyl)zirconium dimethyl, (n-propyl cyclopentadienyl)(pentamethyl cyclopentadienyl)zirconium dichloride, (n-propyl cyclopentadienyl)(pentamethyl cyclopentadienyl)zirconium dimethyl, rac/meso-(l-ethylindenyl)zirconium dichloride, rac/meso-(l-ethylindenyl)zirconium dimethyl, rac/meso-(l-methylindenyl)zirconium dichloride, rac/meso-(l-methylindenyl)zirconium dimethyl, rac/meso-(l- propylindenyl)zirconium dichloride, rac/meso-(l-propylindenyl)zirconium dimethyl, rac/meso-(l-butylindenyl)zirconium dichloride, rac/meso-(l-butylindenyl)zirconium dimethyl, meso-(lethylindenyl) zirconium dichloride, meso-(lethylindenyl) zirconium dimethyl, (l-methylindenyl)(pentamethyl cyclopentadienyl) zirconium dichloride, (1- methylindenyl)(pentamethyl cyclopentadienyl) zirconium dimethyl, or combinations thereof.

[0077] In yet another class of embodiments, the one or more metallocene catalyst may comprise rac/meso-(l-ethylindenyl)zirconium dichloride, rac/meso-(l-ethylindenyl)zirconium dimethyl, rac/meso-(l-methylindenyl)zirconium dichloride, rac/meso-(l- methylindenyl)zirconium dimethyl, rac/meso-(l-propylindenyl)zirconium dichloride, rac/meso-(l-propylindenyl)zirconium dimethyl, rac/meso-(l-butylindenyl)zirconium dichloride, rac/meso-(l-butylindenyl)zirconium dimethyl, meso-(lethylindenyl) zirconium dichloride, meso-(lethylindenyl) zirconium dimethyl, (l-methylindenyl)(pentamethyl cyclopentadienyl) zirconium dichloride, (l-methylindenyl)(pentamethyl cyclopentadienyl) zirconium dimethyl, or combinations thereof. [0078] One or more of the metallocene catalyst as described above or below may be used in a mixed catalyst system also known as a dual catalyst system comprising, for example, two or three metallocene catalysts or any of the catalysts described herein or known in the art to be useful for olefin polymerization. They may co-supported, that is disposed on the same support material, optionally and in addition to, injected into the reactor(s) separately (with or without a support) or in different combinations and proportions together to "trim" or adjust the polymer product properties according to its target specification. This approach is very useful in controlling polymer product properties and insuring uniformity in high volume production of poly olefin polymers.

[0079] For example, catalyst combinations such as rac-ethylene-bis(indenyl) zirconium di chloride and diphenylmethylidene{η ⁵ -[3-(penten-4-yl)cyclopentadien-l-ylidene] } [η ⁵ -(2,7- di-tert-butylfluoren-9-ylidene)]zirconium dichloride, and the other catalysts disclosed in U.S. Patent No. 9,181,370, may be used in a catalyst system or a mixed catalyst system, sometimes also referred to as a dual catalyst system if only two catalysts are used. In another example, Me ₂ Si(H4lnd) ₂ ZrCl ₂ and (Me ₅ Cp)PrCpZrCl ₂ , and (Cp)IndZrCl ₂ and meso-0(Me ₂ SiInd) ₂ ZrCl ₂ may be utilized in a mixed catalyst system and the other catalysts disclosed in U.S. Patent No. 6,828,394. In yet another example, the catalysts represented by "MTE-A" and "MTE-B" as disclosed in U.S. Patent No. 9,181,369, may be used in a mixed catalyst system.

[0080] In another class of embodiments, the following catalysts may be used in a mixed catalyst system: phenyl-3-butenylmethylidene^ ⁵ -cyclopentadienyl)^ ⁵ -9,2-7-di-tert- butylfluorenyl)zirconium dichloride, bis(indenyl)zirconium dichloride, diphenylmethylidene{η ⁵ -[3-(penten-4-yl)cyclopentadien-l-ylidene] } [η ⁵ -(2,7-di-tert- butylfluoren-9-ylidene)]hafnium dichloride, [r| ⁵ -l-(propen-2-yl)indenyl][r| ⁵ -n- butylcyclopentadienyl]zirconium dichloride, rac-ethylene-bis(indenyl)zirconium dichloride, diphenylmethylidene{η ⁵ -[3-(penten-4-yl)cyclopentadien-l-ylidene] } [η ⁵ -(2,7-di-tert- butylfluoren-9-ylidene)]zirconium dichloride, and the other catalysts disclosed in U.S. Patent No. 9,006,367, or any of the catalysts disclosed in U.S. Patent No. 9,217,049, such as those represented by the following:

-21- Activators

[0081] The catalyst compositions may be combined with activators in any manner in the art including by supporting them for use in slurry or gas phase polymerization. Activators are generally compounds that can activate any one of the catalyst compounds described above by converting the neutral metal compound to a catalytically active metal compound cation. Non- limiting activators, for example, include alumoxanes, aluminum alkyls, ionizing activators, which may be neutral or ionic, and conventional-type cocatalysts. Preferred activators typically include alumoxane compounds, modified alumoxane compounds, and ionizing anion precursor compounds that abstract a reactive, σ-bound, metal ligand making the metal compound cationic and providing a charge-balancing non-coordinating or weakly coordinating anion.

Alumoxane Activators

[0082] Alumoxane activators are utilized as activators in the catalyst compositions described herein. Alumoxanes are generally oligomeric compounds containing -A^R^-O- sub-units, where R ¹ is an alkyl group. Examples of alumoxanes include methylalumoxane (MAO), modified methylalumoxane (MMAO), ethylalumoxane and isobutylalumoxane. Alkylalumoxanes and modified alkylalumoxanes are suitable as catalyst activators, particularly when the abstractable ligand is an alkyl, halide, alkoxide or amide. Mixtures of different alumoxanes and modified alumoxanes may also be used. It may be preferable to use a visually clear methylalumoxane. A cloudy or gelled alumoxane can be filtered to produce a clear solution or clear alumoxane can be decanted from the cloudy solution. A useful alumoxane is a modified methyl alumoxane (MMAO) cocatalyst type 3A (commercially available from Akzo Chemicals, Inc. under the trade name Modified Methylalumoxane type 3A, covered under patent number U.S. Patent No. 5,041,584).

[0083] When the activator is an alumoxane (modified or unmodified), some embodiments select the maximum amount of activator typically at up to a 5000-fold molar excess Al/M over the catalyst compound (per metal catalytic site). The minimum activator-to-catalyst-compound is a 1 : 1 molar ratio. Alternate preferred ranges include from 1 : 1 to 500: 1 , alternately from 1 : 1 to 200: 1, alternately from 1 : 1 to 100: 1, or alternately from 1 : 1 to 50: 1.

[0084] In class of embodiments, little or no alumoxane is used in the polymerization processes described herein. Preferably, alumoxane is present at zero mol%, alternatively, the alumoxane is present at a molar ratio of aluminum to catalyst compound transition metal less than 500: 1, preferably less than 300: 1, preferably less than 100: 1, and preferably less than 1 : 1. [0085] In another class of embodiments, the at least one activator comprises aluminum and the aluminum to transition metal, for example, hafnium or zirconium, ratio is at least 150 to 1 ; the at least one activator comprises aluminum and the aluminum to transition metal, for example, hafnium or zirconium, ratio is at least 250 to 1 ; or the at least one activator comprises aluminum and the aluminum to transition metal, for example, hafnium or zirconium, ratio is at least 1,000 to 1.

Ionizing/Non Coordinating Anion Activators

[0086] The term "non-coordinating anion" (NCA) means an anion which either does not coordinate to a cation or which is only weakly coordinated to a cation thereby remaining sufficiently labile to be displaced by a neutral Lewis base. "Compatible" non-coordinating anions are those which are not degraded to neutrality when the initially formed complex decomposes. Further, the anion will not transfer an anionic substituent or fragment to the cation so as to cause it to form a neutral transition metal compound and a neutral by-product from the anion. Non-coordinating anions useful in accordance with this invention are those that are compatible, stabilize the transition metal cation in the sense of balancing its ionic charge at + 1 , and yet retain sufficient lability to permit displacement during polymerization. Ionizing activators useful herein typically comprise an NCA, particularly a compatible NCA.

[0087] It is within the scope of this invention to use an ionizing activator, neutral or ionic, such as tri (n-butyl) ammonium tetrakis (pentafluorophenyl) borate, a tris perfluorophenyl boron metalloid precursor or a tris perfluoronaphthyl boron metalloid precursor, polyhalogenated heteroborane anions (WO 98/43983), boric acid (US 5,942,459), or combination thereof. It is also within the scope of this invention to use neutral or ionic activators alone or in combination with alumoxane or modified alumoxane activators.

[0088] For descriptions of useful activators please see US 8,658,556 and US 6,21 1, 105.

[0089] Preferred activators include N,N-dimethylanilinium tetrakis(perfluoronaphthyl)borate, N,N-dimethylanilinium tetrakis(perfluorobiphenyl)borate, N,N-dimethylanilinium tetrakis(perfluorophenyl)borate, N,N-dimethylanilinium tetrakis(3,5- bis(trifluoromethyl)phenyl)borate, triphenylcarbenium tetrakis(perfluoronaphthyl)borate, triphenylcarbenium tetrakis(perfluorobiphenyl)borate, triphenylcarbenium tetrakis(3,5- bis(trifluoromethyl)phenyl)borate, triphenylcarbenium tetrakis(perfluorophenyl)borate, [Me ₃ NH+] [B(C ₆ F ₅ ) ₄ -]; l -(4-(tris(pentafluorophenyl)borate)-2,3,5,6- tetrafluorophenyl)pyrrolidinium; and tetrakis(pentafluorophenyl)borate, 4-

(tris(pentafluorophenyl)borate)-2,3,5,6-tetrafluoropyridi ne. [0090] In a preferred embodiment, the activator comprises a triaryl carbonium (such as triphenylcarbenium tetraphenylborate, triphenylcarbenium tetrakis(pentafluorophenyl)borate, triphenylcarbenium tetrakis-(2,3,4,6-tetrafluorophenyl)borate, triphenylcarbenium tetrakis(perfluoronaphthyl)borate, triphenylcarbenium tetrakis(perfluorobiphenyl)borate, triphenylcarbenium tetrakis(3,5-bis(trifluoromethyl)phenyl)borate).

[0091] In another embodiment, the activator comprises one or more of trialkylammonium tetrakis(pentafluorophenyl)borate, N,N-dialkylanilinium tetrakis(pentafluorophenyl)borate, N,N-dimethyl-(2,4,6-trimethylanilinium) tetrakis(pentafluorophenyl)borate, trialkylammonium tetrakis-(2,3,4,6-tetrafluorophenyl) borate, N,N-dialkylanilinium tetrakis- (2,3,4,6-tetrafluorophenyl)borate, trialkylammonium tetrakis(perfluoronaphthyl)borate, N,N- dialkylanilinium tetrakis(perfluoronaphthyl)borate, trialkylammonium tetrakis(perfluorobiphenyl)borate, N,N-dialkylanilinium tetrakis(perfluorobiphenyl)borate, trialkylammonium tetrakis(3,5-bis(trifluoromethyl)phenyl)borate, N,N-dialkylanilinium tetrakis(3,5-bis(trifluoromethyl)phenyl)borate, N,N-dialkyl-(2,4,6-trimethylanilinium) tetrakis(3,5-bis(trifluoromethyl)phenyl)borate, di-(i-propyl)ammonium tetrakis(pentafluorophenyl)borate, (where alkyl is methyl, ethyl, propyl, n-butyl, sec-butyl, or t-butyl).

[0092] The typical activator-to-catalyst ratio, e.g., all NCA activators-to-catalyst ratio is about a 1 : 1 molar ratio. Alternate preferred ranges include from 0.1 : 1 to 100: 1 , alternately from 0.5 : 1 to 200: 1 , alternately from 1 : 1 to 500: 1 alternately from 1 : 1 to 1000: 1. A particularly useful range is from 0.5 : 1 to 10: 1, preferably 1 : 1 to 5: 1.

Support Materials

[0093] The catalyst composition may optionally comprise at least one "support" or sometimes also referred to as a "carrier". The terms may be interchangeable unless otherwise distinguished. Suitable supports, include but are not limited to silica, alumina, silica-alumina, zirconia, titania, silica-alumina, cerium oxide, magnesium oxide, or combinations thereof. The catalyst may optionally comprise a support or be disposed on at least one support. Suitable supports, include but are not limited to, active and inactive materials, synthetic or naturally occurring zeolites, as well as inorganic materials such as clays and/or oxides such as silica, alumina, zirconia, titania, silica-alumina, cerium oxide, magnesium oxide, or combinations thereof. In particular, the support may be silica-alumina, alumina and/or a zeolite, particularly alumina. Silica-alumina may be either naturally occurring or in the form of gelatinous precipitates or gels including mixtures of silica and metal oxides. [0094] In class of embodiments, the at least one support may comprise an organosilica material. The organosilica material supports may be a polymer formed of at least one monomer. In certain embodiments, the organosilica material may be a polymer formed of multiple distinct monomers. Methods and materials for producing the organosilica materials as well as a characterization description may be found in, for example, WO 2016/094770 and WO 2016 094774.

Scavengers. Chain Transfer Agents and/or Co-Activators

[0095] Scavengers, chain transfer agents, or co-activators may also be used. Aluminum alkyl compounds which may be utilized as scavengers or co-activators include, for example, one or more of those represented by the formula AIR3, where each R is, independently, a Ci- C8 aliphatic radical, preferably methyl, ethyl, propyl, butyl, pentyl, hexyl octyl or an isomer thereof), especially trimethylaluminum, triethylaluminum, triisobutylaluminum, tri-n- hexylaluminum, tri-n-octylaluminum or mixtures thereof.

[0096] Useful chain transfer agents that may also be used herein are typically a compound represented by the formula A1R ²⁰ 3, ZnR ²⁰ 2 (where each R ²⁰ is, independently, a Ci-Ce aliphatic radical, preferably methyl, ethyl, propyl, butyl, pentyl, hexyl octyl or an isomer thereof) or a combination thereof, such as diethyl zinc, trimethylaluminum, triisobutylaluminum, trioctylaluminum, or a combination thereof.

Polymerization Processes

[0097] In embodiments herein, the invention relates to polymerization processes where monomer (such as propylene and or ethylene), and optionally comonomer, are contacted with a catalyst system comprising at least one activator, at least one support and at least one catalyst, such as a metallocene compound, as described above. The support, catalyst compound, and activator may be combined in any order, and are combined typically prior to contacting with the monomers.

[0098] Monomers useful herein include substituted or unsubstituted C2 to C40 alpha olefins, preferably C2 to C20 alpha olefins, preferably C2 to C12 alpha olefins, preferably ethylene, propylene, butene, pentene, hexene, heptene, octene, nonene, decene, undecene, dodecene and isomers thereof.

[0099] In an embodiment of the invention, the monomer comprises propylene and an optional comonomers comprising one or more ethylene or C4 to C40 olefins, preferably C4 to C20 olefins, or preferably Ce to C12 olefins. The C4 to C40 olefin monomers may be linear, branched, or cyclic. The C4 to C40 cyclic olefins may be strained or unstrained, monocyclic or poly cyclic, and may optionally include heteroatoms and/or one or more functional groups.

[00100] In another embodiment of the invention, the monomer comprises ethylene and optional comonomers comprising one or more C3 to C40 olefins, preferably C4 to C20 olefins, or preferably Ce to C12 olefins. The C3 to C40 olefin monomers may be linear, branched, or cyclic. The C3 to C40 cyclic olefins may be strained or unstrained, monocyclic or poly cyclic, and may optionally include heteroatoms and/or one or more functional groups.

[00101] Exemplary C2 to C40 olefin monomers and optional comonomers include ethylene, propylene, butene, pentene, hexene, heptene, octene, nonene, decene, undecene, dodecene, norbomene, norbomadiene, dicyclopentadiene, cyclopentene, cycloheptene, cyclooctene, cyclooctadiene, cyclododecene, 7-oxanorbornene, 7-oxanorbornadiene, substituted derivatives thereof, and isomers thereof, preferably hexene, heptene, octene, nonene, decene, dodecene, cyclooctene, 1,5-cyclooctadiene, l-hydroxy-4-cyclooctene, l-acetoxy-4-cyclooctene, 5- methylcyclopentene, cyclopentene, dicyclopentadiene, norbomene, norbomadiene, and their respective homologs and derivatives, preferably norbomene, norbomadiene, and dicyclopentadiene.

[00102] In a preferred embodiment one or more dienes are present in the polymer produced herein at up to 10 wt%, preferably at 0.00001 to 1.0 wt%, preferably 0.002 to 0.5 wt%, even more preferably 0.003 to 0.2 wt%, based upon the total weight of the composition. In some embodiments 500 ppm or less of diene is added to the polymerization, preferably 400 ppm or less, preferably or 300 ppm or less. In other embodiments at least 50 ppm of diene is added to the polymerization, or 100 ppm or more, or 150 ppm or more.

[00103] Diolefin monomers useful in this invention include any hydrocarbon structure, preferably C4 to C30, having at least two unsaturated bonds, wherein at least two of the unsaturated bonds are readily incorporated into a polymer by either a stereospecific or a non- stereospecific catalyst(s). It is further preferred that the diolefin monomers be selected from alpha, omega-diene monomers (i.e., di -vinyl monomers). More preferably, the diolefin monomers are linear di-vinyl monomers, most preferably those containing from 4 to 30 carbon atoms. Examples of preferred dienes include butadiene, pentadiene, hexadiene, heptadiene, octadiene, nonadiene, decadiene, undecadiene, dodecadiene, tridecadiene, tetradecadiene, pentadecadiene, hexadecadiene, heptadecadiene, octadecadiene, nonadecadiene, icosadiene, heneicosadiene, docosadiene, tricosadiene, tetracosadiene, pentacosadiene, hexacosadiene, heptacosadiene, octacosadiene, nonacosadiene, triacontadiene, particularly preferred dienes include 1,6-heptadiene, 1,7-octadiene, 1,8-nonadiene, 1,9-decadiene, 1,10-undecadiene, 1,11- dodecadiene, 1,12-tridecadiene, 1,13-tetradecadiene, and low molecular weight poly butadienes (Mw less than 1000 g/mol). Preferred cyclic dienes include cyclopentadiene, vinylnorbornene, norbomadiene, ethylidene norbornene, divinylbenzene, dicyclopentadiene or higher ring containing diolefins with or without substituents at various ring positions.

[00104] Polymerization processes according to the present disclosure can be carried out in any manner known in the art. Any suspension, slurry, high pressure tubular or autoclave process, or gas phase polymerization process known in the art can be used under polymerizable conditions. Such processes can be run in a batch, semi-batch, or continuous mode. Heterogeneous polymerization processes (such as gas phase and slurry phase processes) are useful. A heterogeneous process is defined to be a process where the catalyst system is not soluble in the reaction media. Alternatively, in other embodiments, the polymerization process is not homogeneous.

[00105] A homogeneous polymerization process is defined to be a process where preferably at least 90 wt% of the product is soluble in the reaction media. Alternatively, the polymerization process is not a bulk process is particularly preferred. In a class of embodiments, a bulk process is defined to be a process where monomer concentration in all feeds to the reactor is preferably 70 vol% or more. Alternatively, no solvent or diluent is present or added in the reaction medium, (except for the small amounts used as the carrier for the catalyst system or other additives, or amounts typically found with the monomer; e.g., propane in propylene). In another embodiment, the process is a slurry process. As used herein the term "slurry polymerization process" means a polymerization process where a supported catalyst is employed and monomers are polymerized on the supported catalyst particles. At least 95 wt% of polymer products derived from the supported catalyst are in granular form as solid particles (not dissolved in the diluent).

[00106] Suitable diluents/solvents for polymerization include non-coordinating, inert liquids. Examples include straight and branched-chain hydrocarbons, such as isobutane, butane, pentane, isopentane, hexanes, isohexane, heptane, octane, dodecane, and mixtures thereof; cyclic and alicyclic hydrocarbons, such as cyclohexane, cycloheptane, methylcyclohexane, methylcycloheptane, and mixtures thereof, such as can be found commercially (Isopar™); perhalogenated hydrocarbons, such as perfluorinated C4-10 alkanes, chlorobenzene, and aromatic and alkylsubstituted aromatic compounds, such as benzene, toluene, mesitylene, and xylene. Suitable solvents also include liquid olefins which may act as monomers or comonomers including ethylene, propylene, 1-butene, 1-hexene, 1-pentene, 3- methyl-l-pentene, 4-methyl- 1-pentene, 1-octene, 1-decene, and mixtures thereof. In a preferred embodiment, aliphatic hydrocarbon solvents are used as the solvent, such as isobutane, butane, pentane, isopentane, hexanes, isohexane, heptane, octane, dodecane, and mixtures thereof; cyclic and alicyclic hydrocarbons, such as cyclohexane, cycloheptane, methylcyclohexane, methylcycloheptane, and mixtures thereof. In another embodiment, the solvent is not aromatic, preferably aromatics are present in the solvent at less than 1 wt%, preferably less than 0.5 wt%, preferably less than 0 wt% based upon the weight of the solvents.

[00107] In a preferred embodiment, the feed concentration of the monomers and comonomers for the polymerization is 60 vol% solvent or less, preferably 40 vol% or less, or preferably 20 vol% or less, based on the total volume of the feedstream. Preferably the polymerization is run in a bulk process.

[00108] Preferred polymerizations can be run at any temperature and/or pressure suitable to obtain the desired ethylene polymers and as described above. Typical pressures include pressures in the range of from about 0.35 MPa to about 10 MPa, preferably from about 0.45 MPa to about 6 MPa, or preferably from about 0.5 MPa to about 4 MPa in some embodiments.

[00109] In some embodiments, hydrogen is present in the polymerization reactor at a partial pressure of 0.001 to 50 psig (0.007 to 345 kPa), preferably from 0.01 to 25 psig (0.07 to 172 kPa), more preferably 0.1 to 10 psig (0.7 to 70 kPa).

[00110] In a class of embodiments, the polymerization is performed in the gas phase, preferably, in a fluidized bed gas phase process. Generally, in a fluidized bed gas phase process used for producing polymers, a gaseous stream containing one or more monomers is continuously cycled through a fluidized bed in the presence of a catalyst under reactive conditions. The gaseous stream is withdrawn from the fluidized bed and recycled back into the reactor. Simultaneously, polymer product is withdrawn from the reactor and fresh monomer is added to replace the polymerized monomer. {See, for example, U.S. Patent Nos. 4,543,399; 4,588,790; 5,028,670; 5,317,036; 5,352,749; 5,405,922; 5,436,304; 5,453,471; 5,462,999; 5,616,661; and 5,668,228; all of which are fully incorporated herein by reference.

[00111] In another embodiment of the invention, the polymerization is performed in the slurry phase. A slurry polymerization process generally operates between 1 to about 50 atmosphere pressure range (15 psi to 735 psi, 103 kPa to 5068 kPa) or even greater and temperatures as described above. In a slurry polymerization, a suspension of solid, particulate polymer is formed in a liquid polymerization diluent medium to which monomer and comonomers, along with catalysts, are added. The suspension including diluent is intermittently or continuously removed from the reactor where the volatile components are separated from the polymer and recycled, optionally after a distillation, to the reactor. The liquid diluent employed in the polymerization medium is typically an alkane having from 3 to 7 carbon atoms, preferably a branched alkane. The medium employed should be liquid under the conditions of polymerization and relatively inert. When a propane medium is used, the process is typically operated above the reaction diluent critical temperature and pressure. Often, a hexane or an isobutane medium is employed.

[00112] In an embodiment, a preferred polymerization technique useful in the invention is referred to as a particle form polymerization, or a slurry process where the temperature is kept below the temperature at which the polymer goes into solution. Such technique is known in the art, and described in for instance U. S. Patent No. 3,248, 179. A preferred temperature in the particle form process is within the range of about 85°C to about 1 10°C. Two preferred polymerization methods for the slurry process are those employing a loop reactor and those utilizing a plurality of stirred reactors in series, parallel, or combinations thereof. Non-limiting examples of slurry processes include continuous loop or stirred tank processes. Also, other examples of slurry processes are described in U.S. Patent No. 4,613,484, which is herein fully incorporated by reference.

[00113] In another embodiment, the slurry process is carried out continuously in a loop reactor. The catalyst, as a slurry in isobutane or as a dry free flowing powder, is injected regularly to the reactor loop, which is itself filled with circulating slurry of growing polymer particles in a diluent of isobutane containing monomer and comonomer. Hydrogen, optionally, may be added as a molecular weight control. In one embodiment 500 ppm or less of hydrogen is added, or 400 ppm or less or 300 ppm or less. In other embodiments at least 50 ppm of hydrogen is added, or 100 ppm or more, or 150 ppm or more.

[00114] Reaction heat is removed through the loop wall since much of the reactor is in the form of a double-jacketed pipe. The slurry is allowed to exit the reactor at regular intervals or continuously to a heated low pressure flash vessel, rotary dryer and a nitrogen purge column in sequence for removal of the isobutane diluent and all unreacted monomer and comonomers. The resulting hydrocarbon free powder is then compounded for use in various applications.

[00115] In a preferred embodiment, the catalyst system used in the polymerization comprises no more than one catalyst compound. A "reaction zone" also referred to as a "polymerization zone" is a vessel where polymerization takes place, for example a batch reactor. When multiple reactors are used in either series or parallel configuration, each reactor is considered as a separate polymerization zone. For a multi-stage polymerization in both a batch reactor and a continuous reactor, each polymerization stage is considered as a separate polymerization zone. In a preferred embodiment, the polymerization occurs in one reaction zone.

[00116] Useful reactor types and/or processes for the production of polyolefin polymers include, but are not limited to, UNIPOL™ Gas Phase Reactors (available from Univation Technologies); INEOS™ Gas Phase Reactors and Processes; Continuous Flow Stirred-Tank (CSTR) reactors (solution and slurry); Plug Flow Tubular reactors (solution and slurry); Slurry: (e.g., Slurry Loop (single or double loops)) (available from Chevron Phillips Chemical Company) and (Series Reactors) (available from Mitsui Chemicals)); BORSTAR™ Process and Reactors (slurry combined with gas phase); and Multi-Zone Circulating Reactors (MZCR) such as SPHERIZONE™ Reactors and Process available from Lyondell Basell.

[00117] In several classes of embodiments, the catalyst activity of the polymerization reaction is at least 4,250 g/g*cat or greater, at least 4,750 g/g*cat or greater, at least 5,000 g/g*cat or greater, at least 6,250 g/g*cat or greater, at least 8,500 g/g*cat or greater, at least 9,000 g/g*cat or greater, at least 9,500 g/g*cat or greater, or at least 9,700 g/g*cat or greater. Polyolefin Products

[00118] In an embodiment, the process described herein produces polyethylene compositions including homopolymers and copolymers of one, two, three, four or more d to C40 olefin monomers, for example, C2 to C20 a-olefin monomers.

[00119] For example, the polyethyelene compositions include copolymers of a C2 to C40 olefin and one, two or three or more different C2 to C40 olefins, (where the C2 to C40 olefins are preferably C3 to C20 olefins, preferably are C3 to C12 a-olefin, preferably are propylene, butene, hexene, octene, decene, dodecene, preferably propylene, butene, hexene, octene, or a mixture thereof).

[00120] The polyethylene composition may comprise from 99.0 to about 80.0 wt%, 99.0 to 85.0 wt%, 99.0 to 87.5 wt%, 99.0 to 90.0 wt%, 99.0 to 92.5 wt%, 99.0 to 95.0 wt%, or 99.0 to 97.0 wt%, of polymer units derived from ethylene and about 1.0 to about 20.0 wt%, 1.0 to 15.0 wt%, 0.5 to 12.5 wt%, 1.0 to 10.0 wt%, 1.0 to 7.5 wt%, 1.0 to 5.0 wt%, or 1.0 to 3.0 wt% of polymer units derived from one or more C3 to C20 a-olefin comonomers, preferably C3 to C10 a-olefins, and more preferably C4 to Cs a-olefins, such as hexene and octene. The a-olefin comonomer may be linear or branched, and two or more comonomers may be used, if desired. [00121] Examples of suitable comonomers include propylene, butene, 1-pentene; 1-pentene with one or more methyl, ethyl, or propyl substituents; 1 -hexene; 1 -hexene with one or more methyl, ethyl, or propyl substituents; 1 -heptene; 1-heptene with one or more methyl, ethyl, or propyl substituents; 1 -octene; 1-octene with one or more methyl, ethyl, or propyl substituents; 1-nonene; 1 -nonene with one or more methyl, ethyl, or propyl substituents; ethyl, methyl, or dimethyl-substituted 1-decene; 1 -dodecene; and styrene. Particularly suitable comonomers include 1 -butene, 1 -hexene, and 1 -octene, 1-hexene, and mixtures thereof.

[00122] The polyethylene composition may have a melt index, I2.16, according to the test method listed below, of > about 0.10 g/10 min, e.g., > about 0.15 g/10 min, > about 0.18 g/10 min, > about 0.20 g/10 min, > about 0.22 g/10 min, > about 0.25 g/10 min, > about 0.28 g/10 min, or > about 0.30 g/10 min and, also, a melt index (I2.16)≤ about 3.00 g/10 min, e.g., < about 2.00 g/10 min, < about 1.00 g/10 min, < about 0.70 g/10 min, < about 0.50 g/10 min, < about 0.40 g/10 min, or < about 0.30 g/10 min. Ranges expressly disclosed include, but are not limited to, ranges formed by combinations any of the above-enumerated values, e.g., about 0.10 to about 0.30, about 0.15 to about 0.25, about 0.18 to about 0.22 g/10 min, etc.

[00123] The polyethylene composition may have a high load melt index (HLMI) (I21.6) in accordance with the test method listed below of from 1 to 60 g/10 min, 5 to 40 g/10 min, 15 to 40 g/10 min, or 18 to 39.5 g/10 min.

[00124] The polyethylene composition may have a melt index ratio (MIR) , from 10 to 90, from 20 to 45, from 25 to 60, alternatively, from 30 to 55, alternatively, from 35 to 50, and alternatively, from 40 to 46. MIR is defined as I21.6/I2.16.

[00125] The polyethylene composition may have a density of about 0.890 g/cm ³ , about 0.918 g/cm ³ > about 0.920 g/cm ³ , e.g., > about 0.922 g/cm ³ , > about 0.928 g/cm ³ , > about 0.930 g/cm ³ , > about 0.932 g/cm ³ . Additionally, the polyethylene composition may have a density < about 0.945 g/cm ³ , e.g.,≤ about 0.940 g/cm ³ , < about 0.937 g/cm ³ , < about 0.935 g/cm ³ , < about 0.933 g/cm ³ , or < about 0.930 g/cm ³ . Ranges expressly disclosed include, but are not limited to, ranges formed by combinations any of the above-enumerated values, e.g., about 0.920 to about 0.945 g/cm ³ , 0.920 to 0.930 g/cm ³ , 0.925 to 0.935 g/cm ³ , 0.920 to 0.940 g/cm ³ , etc. Density is determined in accordance with the test method listed below.

[00126] The polyethylene composition may have a molecular weight distribution (MWD, defined as M _w /M _n ) of about 2 to about 12, about 5 to about 10.5 or 11 , about 2.5 to about 5.5, preferably 4.0 to 5.0 and about 4.4 to 5.0. [00127] In a class of embodiments, the polyethylene composition comprises at least 65 wt% ethylene derived units and from 0 to 35 wt% of C3-C12 olefin comonomer derived units, based upon the total weight of the polyethylene composition; wherein the polyethylene composition has:

a) an RCI,m of 100 kg/mol or greater, alternatively, 110 kg/mol or greater, alternatively, 125 kg/mol or greater, alternatively, 150 kg/mol or greater, alternatively, 170 kg/mol or greater, and alternatively, 185 kg/mol or greater;

and one or both of:

b) a Twi-Tw2 value of from -16 to -38°C, alternatively, a Twi-Tw2 value of from -23 to -36°C, and alternatively, a Twi-Tw2 value of from -23 to -33°C; and

c) an Mwi/Mw2 value of at least 0.9, alternatively, an Mwi/Mw2 value of from 0.9 to 4, and alternatively, an Mwi/Mw2 value of from 1.25 to 4;

and one or more of the following:

d) a density of from 0.890 g/cm ³ to 0.940 g/cm ³ ;

e) a melt index (MI) of from 0.1 g/10 min to 30 g/10 min, alternatively, a melt index (MI) of from 0.1 g/10 min to 6 g/10 min;

f) a melt index ratio (I21/I2) of from 10 to 90;

g) an Mw/Mn of from 2 to 12;

h) an Mz/Mw of from 2.5 to 5.0;

i) an Mz/Mn of from 10 to 40; and

j) a g'(vis) of 0.900 or greater, alternatively, 0.930 or greater, alternatively, 0.940 or greater, and alternatively 0.994 or greater.

[00128] In any of the embodiments described herein, the polyethylene composition may be a multimodal polyethylene composition such as a bimodal polyethylene composition. As used herein, "multimodal" means that there are at least two distinguishable peaks in a molecular weight distribution curve (as determined using gel permeation chromatography (GPC) or other recognized analytical technique) of a polyethylene composition. For example, if there are two distinguishable peaks in the molecular weight distribution curve such composition may be referred to as bimodal composition. Typically, if there is only one peak (e.g., monomodal), no obvious valley between the peaks, either one of the peaks is not considered as a distinguishable peak, or both peaks are not considered as distinguishable peaks, then such a composition may be referred to as non-bimodal. For example, in U.S. Patent Nos. 8,846,841 and 8,691,715, figures 1-5 illustrate representative bimodal molecular weight distribution curves. In these figures, there is a valley between the peaks, and the peaks can be separated or deconvoluted. Often, a bimodal molecular weight distribution is characterized as having an identifiable high molecular weight component (or distribution) and an identifiable low molecular weight component (or distribution). In contrast, in U. S. Patent Nos. 8,846,841 and 8,691,715, figures 6-1 1 illustrate representative non-bimodal molecular weight distribution curves. These include unimodal molecular weight distributions as well as distribution curves containing two peaks that cannot be easily distinguished, separated, or deconvoluted.

[00129] In any of the embodiments described herein, the polyethylene composition may have an internal unsaturation as measured by ¾ NMR (see below for the test method) of more than 0.2 total internal unsaturations per thousand carbon atoms, alternatively, more than 0.3 total internal unsaturations per thousand carbon atoms, alternatively, more than 0.32 total internal unsaturations per thousand carbon atoms, alternatively, more than 0.38 total internal unsaturations per thousand carbon atoms, and alternatively, more than 0.4 total internal unsaturations per thousand carbon atoms.

Blends

[00130] In another embodiment, the polymer (preferably the polyethylene or polypropylene) or polyethylene composition produced herein is combined with one or more additional polymers in a blend prior to being formed into a film, molded part, or other article. As used herein, a "blend" may refer to a dry or extruder blend of two or more different polymers, and in-reactor blends, including blends arising from the use of multi or mixed catalyst systems in a single reactor zone, and blends that result from the use of one or more catalysts in one or more reactors under the same or different conditions (e.g., a blend resulting from in series reactors (the same or different) each running under different conditions and/or with different catalysts).

[00131] Useful additional polymers include other polyethylenes, isotactic polypropylene, highly isotactic polypropylene, syndiotactic polypropylene, random copolymer of propylene and ethylene, and/or butene, and/or hexene, polybutene, ethylene vinyl acetate, LDPE, LLDPE, HDPE, ethylene vinyl acetate, ethylene methyl acrylate, copolymers of acrylic acid, polymethylmethacrylate or any other polymers polymerizable by a high-pressure free radical process, polyvinylchloride, polybutene-1, isotactic polybutene, ABS resins, ethylene- propylene rubber (EPR), vulcanized EPR, EPDM, block copolymer, styrenic block copolymers, polyamides, polycarbonates, PET resins, cross linked polyethylene, copolymers of ethylene and vinyl alcohol (EVOH), polymers of aromatic monomers such as polystyrene, poly-1 esters, polyacetal, polyvinylidine fluoride, polyethylene glycols, and/or polyisobutylene.

End Uses

[00132] Any of the foregoing polymers and compositions in combination with optional additives {see, for example, U. S. Patent Application Publication No. 2016/0060430, paragraphs [0082]-[0093]) may be used in a variety of end-use applications. Such end uses may be produced by methods known in the art. End uses include polymer products and products having specific end-uses. Exemplary end uses are films, film-based products, diaper backsheets, housewrap, wire and cable coating compositions, articles formed by molding techniques, e.g., injection or blow molding, extrusion coating, foaming, casting, and combinations thereof. End uses also include products made from films, e.g., bags, packaging, and personal care films, pouches, medical products, such as for example, medical films and intravenous (IV) bags. Films

[00133] Films include monolayer or multilayer films. Films include those film structures and film applications known to those skilled in the art. Specific end use films include, for example, blown films, cast films, stretch films, stretch/cast films, stretch cling films, stretch handwrap films, machine stretch wrap, shrink films, shrink wrap films, green house films, laminates, and laminate films. Exemplary films are prepared by any conventional technique known to those skilled in the art, such as for example, techniques utilized to prepare blown, extruded, and/or cast stretch and/or shrink films (including shrink-on-shrink applications).

[00134] In one embodiment, multilayer films or multiple-layer films may be formed by methods well known in the art. The total thickness of multilayer films may vary based upon the application desired. A total film thickness of about 5-100 μιτι, more typically about 10-50 μιτι, is suitable for most applications. Those skilled in the art will appreciate that the thickness of individual layers for multilayer films may be adjusted based on desired end-use performance, resin or copolymer employed, equipment capability, and other factors. The materials forming each layer may be coextruded through a coextrusion feedblock and die assembly to yield a film with two or more layers adhered together but differing in composition. Coextrusion can be adapted for use in both cast film or blown film processes. Exemplary multilayer films have at least two, at least three, or at least four layers. In one embodiment the multilayer films are composed of five to ten layers.

[00135] To facilitate discussion of different film structures, the following notation is used herein. Each layer of a film is denoted "A" or "B". Where a film includes more than one A layer or more than one B layer, one or more prime symbols (', ", "', etc.) are appended to the A or B symbol to indicate layers of the same type that can be the same or can differ in one or more properties, such as chemical composition, density, melt index, thickness, etc. Finally, the symbols for adjacent layers are separated by a slash (/). Using this notation, a three-layer film having an inner layer disposed between two outer layers would be denoted A/B/A'. Similarly, a five-layer film of alternating layers would be denoted A/B/A'/B'/A". Unless otherwise indicated, the left-to-right or right-to-left order of layers does not matter, nor does the order of prime symbols; e.g., an A/B film is equivalent to a B/A film, and an A/A'/B/A" film is equivalent to an A/B/A'/A" film, for purposes described herein. The relative thickness of each film layer is similarly denoted, with the thickness of each layer relative to a total film thickness of 100 (dimensionless) indicated numerically and separated by slashes; e.g., the relative thickness of an A/B/A film having A and A layers of 10 μιτι each and a B layer of 30 μιτι is denoted as 20/60/20.

[00136] The thickness of each layer of the film, and of the overall film, is not particularly limited, but is determined according to the desired properties of the film. Typical film layers have a thickness of from about 1 to about 1000 μιτι, more typically from about 5 to about 100 μηι, and typical films have an overall thickness of from about 10 to about 100 μιτι.

[00137] In some embodiments, and using the nomenclature described above, the present invention provides for multilayer films with any of the following exemplary structures: (a) two- layer films, such as A/B and B/B'; (b) three-layer films, such as A/B/A', A/ /B, B/A/B' and B/B'/B"; (c) four-layer films, such as A/A7A7B, A/A'/B/A", A/A'/B/B', A/B/A'/B', A/B/B'/A, B/A/A'/B', A/B/B'/B", B/A/B'/B" and B/B'/B"/B"'; (d) five-layer films, such as A/A'/A"/A"'/B, A/A'/A"/B/A", A/A'/B/A"/A", A/A'/A"/B/B', A/A'/B/A"/B', A/A'/B/B'/A", A/B/A'/B'/A", Α/Β/Α7ΑΎΒ, B/A/A'/A"/B', A/A'/B/B'/B", A/B/A'/B'/B", A/B/B'/B"/A, B/A/A'/B'/B", B/A/B'/A'/B", B/A/B'/B"/A, A/B/B'/B"/B"', B/A/BVB7B"', B/B'/A/B"/B"', and B/B'/B"/B"'/B""; and similar structures for films having six, seven, eight, nine, twenty-four, forty-eight, sixty-four, one hundred, or any other number of layers. It should be appreciated that films having still more layers.

[00138] In any of the embodiments above, one or more A layers can be replaced with a substrate layer, such as glass, plastic, paper, metal, etc., or the entire film can be coated or laminated onto a substrate. Thus, although the discussion herein has focused on multilayer films, the films may also be used as coatings for substrates such as paper, metal, glass, plastic, and other materials capable of accepting a coating. [00139] The films can further be embossed, or produced or processed according to other known film processes. The films can be tailored to specific applications by adjusting the thickness, materials and order of the various layers, as well as the additives in or modifiers applied to each layer.

Stretch Films

[00140] The polymers and compositions as described above may be utilized to prepare stretch films. Stretch films are widely used in a variety of bundling and packaging applications. The term "stretch film" indicates films capable of stretching and applying a bundling force, and includes films stretched at the time of application as well as "pre-stretched" films, i.e., films which are provided in a pre-stretched form for use without additional stretching. Stretch films can be monolayer films or multilayer films, and can include conventional additives, such as cling-enhancing additives such as tackifiers, and non-cling or slip additives, to tailor the slip/cling properties of the film.

Shrink Films

[00141] The polymers and compositions as described above may be utilized to prepare shrink films. Shrink films, also referred to as heat-shrinkable films, are widely used in both industrial and retail bundling and packaging applications. Such films are capable of shrinking upon application of heat to release stress imparted to the film during or subsequent to extrusion. The shrinkage can occur in one direction or in both longitudinal and transverse directions. Conventional shrink films are described, for example, in WO 2004/022646.

[00142] Industrial shrink films are commonly used for bundling articles on pallets. Typical industrial shrink films are formed in a single bubble blown extrusion process to a thickness of about 80 to 200 μιτι, and provide shrinkage in two directions, typically at a machine direction (MD) to transverse direction (TD) ratio of about 60:40.

[00143] Retail films are commonly used for packaging and/or bundling articles for consumer use, such as, for example, in supermarket goods. Such films are typically formed in a single bubble blown extrusion process to a thickness of about 35 to 80, μιτι, with a typical MD:TD shrink ratio of about 80:20.

[00144] Films may be used in "shrink-on-shrink" applications. "Shrink-on-shrink," as used herein, refers to the process of applying an outer shrink wrap layer around one or more items that have already been individually shrink wrapped (herein, the "inner layer" of wrapping). In these processes, it is desired that the films used for wrapping the individual items have a higher melting (or shrinking) point than the film used for the outside layer. When such a configuration is used, it is possible to achieve the desired level of shrinking in the outer layer, while preventing the inner layer from melting, further shrinking, or otherwise distorting during shrinking of the outer layer. Some films described herein have been observed to have a sharp shrinking point when subjected to heat from a heat gun at a high heat setting, which indicates that they may be especially suited for use as the inner layer in a variety of shrink-on-shrink applications.

Greenhouse Films

[00145] The polymers and compositions as described above may be utilized to prepare stretch to prepare greenhouse films. Greenhouse films are generally heat retention films that, depending on climate requirements, retain different amounts of heat. Less demanding heat retention films are used in warmer regions or for spring time applications. More demanding heat retention films are used in the winter months and in colder regions.

Bags

[00146] Bags include those bag structures and bag applications known to those skilled in the art. Exemplary bags include shipping sacks, trash bags and liners, industrial liners, produce bags, and heavy duty bags.

Packaging

[00147] Packaging includes those packaging structures and packaging applications known to those skilled in the art. Exemplary packaging includes flexible packaging, food packaging, e.g., fresh cut produce packaging, frozen food packaging, bundling, packaging and unitizing a variety of products. Applications for such packaging include various foodstuffs, rolls of carpet, liquid containers, and various like goods normally containerized and/or palletized for shipping, storage, and/or display.

Blow Molded Articles

[00148] The polymers and compositions described above may also be used in blow molding processes and applications. Such processes are well known in the art, and involve a process of inflating a hot, hollow thermoplastic preform (or parison) inside a closed mold. In this manner, the shape of the parison conforms to that of the mold cavity, enabling the production of a wide variety of hollow parts and containers.

[00149] In a typical blow molding process, a parison is formed between mold halves and the mold is closed around the parison, sealing one end of the parison and closing the parison around a mandrel at the other end. Air is then blown through the mandrel (or through a needle) to inflate the parison inside the mold. The mold is then cooled and the part formed inside the mold is solidified. Finally, the mold is opened and the molded part is ejected. The process lends itself to any design having a hollow shape, including but not limited to bottles, tanks, toys, household goods, automobile parts, and other hollow containers and/or parts.

[00150] Blow molding processes may include extrusion and/or injection blow molding. Extrusion blow molding is typically suited for the formation of items having a comparatively heavy weight, such as greater than about 12 ounces, including but not limited to food, laundry, or waste containers. Injection blow molding is typically used to achieve accurate and uniform wall thickness, high quality neck finish, and to process polymers that cannot be extruded. Typical injection blow molding applications include, but are not limited to, pharmaceutical, cosmetic, and single serving containers, typically weighing less than 12 ounces.

Injection Molded Articles

[00151] The polymers and compositions described above may also be used in injection molded applications. Injection molding is a process commonly known in the art, and is a process that usually occurs in a cyclical fashion. Cycle times generally range from 10 to 100 seconds and are controlled by the cooling time of the polymer or polymer blend used.

[00152] In a typical injection molding cycle, polymer pellets or powder are fed from a hopper and melted in a reciprocating screw type injection molding machine. The screw in the machine rotates forward, filling a mold with melt and holding the melt under high pressure. As the melt cools in the mold and contracts, the machine adds more melt to the mold to compensate. Once the mold is filled, it is isolated from the injection unit and the melt cools and solidifies. The solidified part is ejected from the mold and the mold is then closed to prepare for the next injection of melt from the injection unit.

[00153] Injection molding processes offer high production rates, good repeatability, minimum scrap losses, and little to no need for finishing of parts. Injection molding is suitable for a wide variety of applications, including containers, household goods, automobile components, electronic parts, and many other solid articles.

Extrusion Coating

[00154] The polymers and compositions described above may be used in extrusion coating processes and applications. Extrusion coating is a plastic fabrication process in which molten polymer is extruded and applied onto a non-plastic support or substrate, such as paper or aluminum in order to obtain a multi-material complex structure. This complex structure typically combines toughness, sealing and resistance properties of the polymer formulation with barrier, stiffness or aesthetics attributes of the non-polymer substrate. In this process, the substrate is typically fed from a roll into a molten polymer as the polymer is extruded from a slot die, which is similar to a cast film process. The resultant structure is cooled, typically with a chill roll or rolls, and would into finished rolls.

[00155] Extrusion coating materials are typically used in food and non-food packaging, pharmaceutical packaging, and manufacturing of goods for the construction (insulation elements) and photographic industries (paper).

Foamed Articles

[00156] The polymers and compositions described above may be used in foamed applications. In an extrusion foaming process, a blowing agent, such as, for example, carbon dioxide, nitrogen, or a compound that decomposes to form carbon dioxide or nitrogen, is injected into a polymer melt by means of a metering unit. The blowing agent is then dissolved in the polymer in an extruder, and pressure is maintained throughout the extruder. A rapid pressure drop rate upon exiting the extruder creates a foamed polymer having a homogenous cell structure. The resulting foamed product is typically light, strong, and suitable for use in a wide range of applications in industries such as packaging, automotive, aerospace, transportation, electric and electronics, and manufacturing.

Wire and Cable Applications

[00157] Also provided are electrical articles and devices including one or more layers formed of or comprising the polymers and compositions described above. Such devices include, for example, electronic cables, computer and computer-related equipment, marine cables, power cables, telecommunications cables or data transmission cables, and combined power/telecommunications cables.

[00158] Electrical devices described herein can be formed by methods well known in the art, such as by one or more extrusion coating steps in a reactor/extruder equipped with a cable die. Such cable extrusion apparatus and processes are well known. In a typical extrusion method, an optionally heated conducting core is pulled through a heated extrusion die, typically a cross-head die, in which a layer of melted polymer composition is applied. Multiple layers can be applied by consecutive extrusion steps in which additional layers are added, or, with the proper type of die, multiple layers can be added simultaneously. The cable can be placed in a moisture curing environment, or allowed to cure under ambient conditions. Test Methods

¾ NMR

[00159] ¾ NMR data was collected at 393K in a 10 mm probe using a Bruker spectrometer with a ¾ frequency of 400 MHz (available from Agilent Technologies, Santa Clara, CA). Data was recorded using a maximum pulse width of 45°C, 5 seconds between pulses and signal averaging 512 transients. Spectral signals were integrated and the number of unsaturation types per 1000 carbons was calculated by multiplying the different groups by 1000 and dividing the result by the total number of carbons. M _n was calculated by dividing the total number of unsaturated species into 14,000, and has units of g/mol.

TREF Method

[00160] Unless otherwise indicated, the TREF-LS data reported herein were measured using an analytical size TREF instrument (Polymerchar, Spain), with a column of the following dimension: inner diameter (ID) 7.8 mm and outer diameter (OD) 9.53 mm and a column length of 150 mm. The column was filled with steel beads. 0.5 mL of a 6.4% (w/v) polymer solution in orthodichlorobenzene (ODCB) containing 6 g BHT/4 L were charged onto the column and cooled from 140°C to 25°C at a constant cooling rate of 1.0°C/min. Subsequently, the ODCB was pumped through the column at a flow rate of 1.0 ml/min and the column temperature was increased at a constant heating rate of 2°C/min to elute the polymer. The polymer concentration in the eluted liquid was detected by means of measuring the absorption at a wavenumber of 2857 crrT ¹ using an infrared detector. The concentration of the ethylene-a- olefin copolymer in the eluted liquid was calculated from the absorption and plotted as a function of temperature. The molecular weight of the ethylene-a-olefin copolymer in the eluted liquid was measured by light scattering using a Minidawn Tristar light scattering detector (Wyatt, Calif , USA). The molecular weight was also plotted as a function of temperature. GPC 4D Procedure: Molecular Weight. Comonomer Composition and Long Chain Branching Determination by GPC-IR Hyphenated with Multiple Detectors

[00161] The distribution and the moments of molecular weight (M _w , M _n , M _w /M _n , etc.), the comonomer content (C2, C3, Ce, etc.) and the branching index (g'vis) are determined by using a high temperature Gel Permeation Chromatography (Polymer Char GPC-IR) equipped with a multiple-channel band-filter based Infrared detector IR5, an 18-angle light scattering detector and a viscometer. Three Agilent PLgel 10-μιτι Mixed-B LS columns are used to provide polymer separation. Aldrich reagent grade 1 ,2,4-trichlorobenzene (TCB) with 300 ppm antioxidant butylated hydroxy toluene (BHT) is used as the mobile phase. The TCB mixture is filtered through a 0.1 μηι Teflon filter and degassed with an online degasser before entering the GPC instrument. The nominal flow rate is 1.0 ml/min and the nominal injection volume is 200 μί. The whole system including transfer lines, columns, and detectors are contained in an oven maintained at 145°C. The polymer sample is weighed and sealed in a standard vial with 80 flow marker (Heptane) added to it. After loading the vial in the autosampler, polymer is automatically dissolved in the instrument with 8 ml added TCB solvent. The polymer is dissolved at 160°C with continuous shaking for about 1 hour for PE samples or 2 hour for PP samples. The TCB densities used in concentration calculation are 1.463 g/ml at about 23°C temperature and 1.284 g/ml at 145°C. The sample solution concentration is from 0.2 to 2.0 mg/ml, with lower concentrations being used for higher molecular weight samples. The concentration (c), at each point in the chromatogram is calculated from the baseline-subtracted IR5 broadband signal intensity {I), using the following equation: c = βΐ, where β is the mass constant. The mass recovery is calculated from the ratio of the integrated area of the concentration chromatography over elution volume and the injection mass which is equal to the pre-determined concentration multiplied by injection loop volume. The conventional molecular weight (IR MW) is determined by combining universal calibration relationship with the column calibration which is performed with a series of monodispersed polystyrene (PS) standards ranging from 700 to 10M gm/mole. The MW at each elution volume is calculated with following equation:

, \og{K _ps IK) a _ps + \ . _t

log = ^ps +— log _ra

a + 1 a + 1

where the variables with subscript "PS" stand for polystyrene while those without a subscript are for the test samples. In this method, aps = 0.67 and KPS = 0.000175 while a and K are for other materials as calculated and published in literature (Sun, T. et al. Macromolecules 2001, 34, 6812), except that for purposes of this invention and claims thereto, a = 0.695 and K = 0.000579 for linear ethylene polymers, a = 0.705 and K = 0.0002288 for linear propylene polymers, a = 0.695 and K = 0.000181 for linear butene polymers, a is 0.695 and K is 0.000579*(l-0.0087*w2b+0.000018*(w2b) ^A 2) for ethylene-butene copolymer where w2b is a bulk weight percent of butene comonomer, a is 0.695 and K is 0.000579*(l-0.0075*w2b) for ethylene-hexene copolymer where w2b is a bulk weight percent of hexene comonomer, and a is 0.695 and K is 0.000579*(l-0.0077*w2b) for ethylene-octene copolymer where w2b is a bulk weight percent of octene comonomer. Concentrations are expressed in g/cm ³ , molecular weight is expressed in g/mole, and intrinsic viscosity (hence K in the Mark- Houwink equation) is expressed in dL/g unless otherwise noted.

[00162] The comonomer composition is determined by the ratio of the IR5 detector intensity corresponding to CH2 and CH3 channel calibrated with a series of PE and PP homo/copolymer standards whose nominal value are predetermined by NMR or FTIR. In particular, this provides the methyls per 1000 total carbons (CH3/IOOOTC) as a function of molecular weight. The short-chain branch (SCB) content per lOOOTC (SCB/IOOOTC) is then computed as a function of molecular weight by applying a chain-end correction to the CH3/IOOOTC function, assuming each chain to be linear and terminated by a methyl group at each end. The wt% comonomer is then obtained from the following expression in which / is 0.3, 0.4, 0.6, 0.8, and so on for C3, C4, C6, C8, and so on co-monomers, respectively:

w2 = / * SCB/IOOOTC.

[00163] The bulk composition of the polymer from the GPC-IR and GPC-4D analyses is obtained by considering the entire signals of the CH3 and CH2 channels between the integration limits of the concentration chromatogram. First, the following ratio is obtained

Area of CH signal within integration limits

Bulk IR ratio = — .

Area of CH ₂ signal within integration limits

[00164] Then the same calibration of the CH3 and CH2 signal ratio, as mentioned previously in obtaining the CH3/1000TC as a function of molecular weight, is applied to obtain the bulk

CH3/1000TC. A bulk methyl chain ends per lOOOTC (bulk CH3end/1000TC) is obtained by weight-averaging the chain-end correction over the molecular-weight range. Then

w2b = f * bulk CH3/1000TC

bulk SCB/IOOOTC = bulk CH3/1000TC - bulk CH3end/1000TC and bulk SCB/IOOOTC is converted to bulk w2 in the same manner as described above.

[00165] The LS detector is the 18-angle Wyatt Technology High Temperature DAWN HELEOSII. The LS molecular weight ( ) at each point in the chromatogram is determined by analyzing the LS output using the Zimm model for static light scattering (Light Scattering from

Polymer Solutions; Huglin, M. B., Ed.; Academic Press, 1972.):

AR ^° (e) ^~ ΜΡ(Θ) ^{+ 2Α} °

[00166] Here, AR(6) is the measured excess Rayleigh scattering intensity at scattering angle Θ, c is the polymer concentration determined from the IR5 analysis, A2 is the second virial coefficient, Ρ(θ) is the form factor for a monodisperse random coil, and Ko is the optical constant for the system: _ 4π ² η ² (dn / dc) ²

° ⁼ λ ⁴ Ν _Α

where NA is Avogadro's number, and (dn/dc) is the refractive index increment for the system. The refractive index, n = 1.500 for TCB at 145°C and λ = 665 nm. For analyzing polyethylene homopolymers, ethylene-hexene copolymers, and ethylene-octene copolymers, dn/dc = 0.1048 ml/mg and A2 = 0.0015; for analyzing ethyl ene-butene copolymers, dn/dc = 0.1048*(1- 0.00126*w2) ml/mg and A2 = 0.0015 where w2 is weight percent butene comonomer.

[00167] A high temperature Agilent (or Viscotek Corporation) viscometer, which has four capillaries arranged in a Wheatstone bridge configuration with two pressure transducers, is used to determine specific viscosity. One transducer measures the total pressure drop across the detector, and the other, positioned between the two sides of the bridge, measures a differential pressure. The specific viscosity, ns, for the solution flowing through the viscometer is calculated from their outputs. The intrinsic viscosity, [η], at each point in the chromatogram is calculated from the equation [η]= ns/c, where c is concentration and is determined from the IR5 broadband channel output. The viscosity MW at each point is calculated as

, where aps is 0.67 and Kp _S is 0.000175.

[00168] The branching index (gVis) is calculated using the output of the GPC-IR5-LS-VIS method as follows. The average intrinsic viscosity, [r|]avg, of the sample is calculated by: m i =

L ' U avg ^ C where the summations are over the chromatographic slices, i, between the integration limits.

₌ fo

The branching index g'vis is defined as ^vis KM ^v , where Mv is the viscosity-average molecular weight based on molecular weights determined by LS analysis and the K and a are for the reference linear polymer, which are, for purposes of this invention and claims thereto, a = 0.695 and K = 0.000579 for linear ethylene polymers, a = 0.705 and K = 0.0002288 for linear propylene polymers, a = 0.695 and K = 0.000181 for linear butene polymers, a is 0.695 and K is 0.000579*(l-0.0087*w2b+0.000018*(w2b) ^A 2) for ethylene-butene copolymer where w2b is a bulk weight percent of butene comonomer, a is 0.695 and K is 0.000579*(1-

0.0075*w2b) for ethylene-hexene copolymer where w2b is a bulk weight percent of hexene comonomer, and a is 0.695 and K is 0.000579*(l-0.0077*w2b) for ethylene-octene copolymer where w2b is a bulk weight percent of octene comonomer. Concentrations are expressed in g/cm ³ , molecular weight is expressed in g/mole, and intrinsic viscosity (hence K in the Mark- Houwink equation) is expressed in dL/g unless otherwise noted. Calculation of the w2b values is as discussed above.

[00169] The reversed-co-monomer index (RCI,m) is computed from %2 (mol% co- monomer C3, C ₄ , Ce, Ce, etc.), as a function of molecular weight, where x2 is obtained from the following expression in which n is the number of carbon atoms in the comonomer (3 for C ₃ , 4 for C ₄ , 6 for Ce, etc.):

200 w2

-100 n-2 w2+n w2 ^'

[00170] Then the molecular-weight distribution, W(z) where z = log ₁₀ M, is modified to W'(z) by setting to 0 the points in W that are less than 5% of the maximum of W; this is to effectively remove points for which the S/N in the composition signal is low. Also, points of W for molecular weights below 2000 gm/mole are set to 0. Then W is renormalized so that

1 = C W'dz,

and a modified weight-average molecular weight (M _w ^r ) is calculated over the effectively reduced range of molecular weights as follows:

M _w ' = S _∞ 10 ^z * W'dz.

[00171] The RCI,m is then computed as

RCI,m = S _∞ x2 (10 ^z - M _w ')W'dz.

[00172] A reversed-co-monomer index (RCI,w) is also defined on the basis of the weight fraction co-monomer signal (w2 /100) and is computed as follows:

RCI,w = _co ^ (10 ^z - M _w ')^'dz.

[00173] In the above definite integrals the limits of integration are the widest possible for the sake of generality; however, in reality the function is only integrated over a finite range for which data is acquired, considering the function in the rest of the non-acquired range to be 0. Also, by the manner in which W is obtained, it is possible that W is a discontinuous function, and the above integrations need to be done piecewise.

[00174] Three co-monomer distribution ratios are also defined on the basis of the % weight (w2) comonomer signal, denoted as CDR-l,w, CDR-2,w, and CDR-3,w, as follows:

w2 (Mz)

CDR-l,w =

w2 (Mw)'

w2 (Mz)

CDR-2,w =

_ (Mw + Mn\'

w2 2 J Mz + Mw

2

CDR-3,w =

Mw + Mn

2

where w2(Mw) is the % weight co-monomer signal corresponding to a molecular weight of Mw, w2(Mz) is the % weight co-monomer signal corresponding to a molecular weight of Mz, w2[(Mw+Mn)/2)] is the % weight co-monomer signal corresponding to a molecular weight of (Mw+Mn)/2, and w2[(Mz+Mw)/2] is the % weight co-monomer signal corresponding to a molecular weight of Mz+Mw/2, where Mw is the weight-average molecular weight, Mn is the number-average molecular weight, and Mz is the z-average molecular weight.

[00175] Accordingly, the co-monomer distribution ratios can be also defined utilizing the % mole co-monomer signal, CDR-l ,m, CDR-2,m, CDR-3,m, as

x2 {Mz)

CDR-l ,m =

x2 (Mw)'

x2 {Mz)

CDR-2,m =—

„ (Mw + Mn\'

x2 { - ₂ J

„ (Mz + Mw\

x ² ( 2 )

CDR-3,m =

„ ( (MMww ++ MMnn\Y'

x2 { - ₂ J

where x2(Mw) is the % mole co-monomer signal corresponding to a molecular weight of Mw, x2(Mz) is the % mole co-monomer signal corresponding to a molecular weight of Mz, x2[(Mw+Mn)/2)] is the % mole co-monomer signal corresponding to a molecular weight of (Mw+Mn)/2, and x2[(Mz+Mw)/2] is the % mole co-monomer signal corresponding to a molecular weight of Mz+Mw/2, where Mw is the weight-average molecular weight, Mn is the number-average molecular weight, and Mz is the z-average molecular weight. Table X depicts the molecular weight characteristics of the polymers made from mixed catalysts 1 and 2. Cross-Fractionation Chromatography (CFC)

[00176] Cross-fractionation chromatography (CFC) analysis was done using a CFC-2 instrument from Polymer Char, S.A., Valencia, Spain. The principles of CFC analysis and a general description of the particular apparatus used are given in the article by Ortin, A. ; Monrabal, B.; Sancho-Tello, 257 J. Macromol. Symp. 13 (2007). In FIG. 1 of the article is an appropriate schematic of the particular apparatus used. Details of the analysis method and features of the apparatus used are as follows.

[00177] The solvent used for preparing the sample solution and for elution was 1,2- Dichlorobenzene (ODCB) which was stabilized by dissolving 2 g of 2,6-bis(l ,l - dimethylethyl)-4-methylphenol (butylated hydroxy toluene) in a 4-L bottle of fresh solvent at ambient temperature. The sample to be analyzed (25-125 mg) was dissolved in the solvent (25 ml metered at ambient temperature) by stirring (200 rpm) at 150°C for 75 min. A small volume (0.5 ml) of the solution was introduced into a TREF column (stainless steel; o.d., 3/8"; length, 15 cm; packing, non-porous stainless steel micro-balls) at 150°C, and the column temperature was stabilized for 30 min at a temperature (120-125°C) approximately 20°C higher than the highest-temperature fraction for which the GPC analysis was included in obtaining the final bivariate distribution. The sample volume was then allowed to crystallize in the column by reducing the temperature to an appropriate low temperature (30, 0, or -15°C) at a cooling rate of 0.2°C/min. The low temperature was held for 10 min before injecting the solvent flow (1 ml/min) into the TREF column to elute the soluble fraction (SF) into the GPC columns (3 x PLgel 10 μπι Mixed-B 300 x 7.5 mm, Agilent Technologies, Inc.); the GPC oven was held at high temperature (140°C). The SF was eluted for 5 min from the TREF column and then the injection valve was put in the "load" position for 40 min to completely elute all of the SF through the GPC columns (standard GPC injections). All subsequent higher- temperature fractions were analyzed using overlapped GPC injections wherein at each temperature step the polymer was allowed to dissolve for at least 16 min and then eluted from the TREF column into the GPC column for 3 min. The IR4 (Polymer Char) infrared detector was used to generate an absorbance signal that is proportional to the concentration of polymer in the eluting flow.

[00178] The universal calibration method was used for determining the molecular weight distribution (MWD) and molecular-weight averages (M _n , M _w , etc.) of eluting polymer fractions. Thirteen narrow molecular- weight distribution polystyrene standards (obtained from Agilent Technologies, Inc.) within the range of 1.5-8200 kg/mol were used to generate a universal calibration curve. Mark-Houwink parameters were obtained from Appendix I of Mori, S.; Barth, H. G. Size Exclusion Chromatography; Springer, 1999. For polystyrene K = 1.38 x 10 ^"4 dl/g and a = 0.7; and for polyethylene K = 5.05 x 10 ^"4 dl/g and a = 0.693 were used. For a polymer fraction, which eluted at a temperature step, that has a weight fraction (wt% recovery) of less than 0.5%, the MWD and the molecular- weight averages were not computed; additionally, such polymer fractions were not included in computing the MWD and the molecular-weight averages of aggregates of fractions. Measuring Twl. Tw2. Mwl and Mw2 from CFC

[00179] A technique has been developed for determining both MWD and SCBD compositional information, using cryogenic cross fractionation (cryo CFC), to compare the polymers. The procedures for the determination of CFC data are discussed in more detail below.

[00180] In the section of "Fraction summary" in the CFC data file, each fraction is listed by its fractionation temperature (Ti) along with its normalized wt% value (Wi), cumulative wt%, i.e., Sum wt. on FIG. 2 and FIG. 3, and various moments of molecular weight averages (including weight average molecular weight, Mwi).

[00181] FIG. 2 and FIG. 3 are plots that graphically illustrate the calculations used to determine the CFC result. Only fractions having MWD data are considered. In both FIG. 2 and FIG. 3, the x- axis represents the elution temperature in centigrade, while the right hand y- axis represents the value of the integral of the weights of polymer that have been eluted up to an elution temperature. The temperature at which 100% of the material has eluted in this example is about 100°C. The closest point at which 50% of the polymer has eluted is determined by the integral, which is used then to divide each of the plots into a l ^st -half and a 2 ^nd -half.

[00182] To calculate values of Twi, Tw2, Mwi and Mw2, the data in "Fraction summary" was divided into two roughly equal halves. Weight averages of Ti and Mwi; for each half were calculated according to the conventional definition of weight average. Fractions which did not have sufficient quantity (i.e., < 0.5 wt%) to be processed for molecular weight averages in the original data file were excluded from the calculation of Twi, Tw2, Mwi and Mw2.

[00183] The first part of the process is illustrated by FIG. 2. From the section of fraction summary in the CFC data file, the fraction whose cumulative wt% (i.e., Sum wt) is closest to 50 is identified (e.g., the fraction at 84°C on FIG. 2). The Fraction summary data is divided into two halves, e.g., Ti <= 84°C as the 1st half and Ti > 84°C as the 2nd half on FIG. 2. Fractions which do not have molecular weight averages reported in the original data file are excluded, e.g., excluding the fractions with Ti between 25°C and 40°C on FIG. 2.

[00184] In FIG. 2, the left hand y-axis represents the wt% of the eluted fraction. Using the procedure above to divide the curves into two halves, these values are used to calculate the weight average elution temperature for each half using the formula shown in Eqn. 1.

∑n wi

Tw = Eqn. 1.

∑Wi [00185] In Eqn. 1, Ti represents the elution temperature for each eluted fraction, and Wi represents the normalized wt% (polymer amount) of each eluted fraction. For the example shown in FIG. 2, this provides a weight average elution temperature of 64.9°C for the first half, and 91.7°C for the second half.

[00186] In FIG. 3, the left hand axis represents the weight average molecular weight (Mwj) of each eluted fraction. These values are used to calculate the weight average molecular weight for each half using the formula shown in Eqn. 2.

∑Mwi Wi „

Mw = Eqn. 2.

∑wi

[00187] In Eqn. 2, Mw; represents the weight average molecular weight of each eluted fraction, and Wj represents the normalized wt% (polymer amount) of each eluted fraction. For the example shown in FIG. 3, this provides a weight average molecular weight of 237,539 g/mole for the first half, and 74,156 g/mole for the second half. The values calculated using the techniques described above may be used to classify the MWDxSCBD for experimental polymers and control polymers.

[00188] FIG. 4 is a semi-log plot of (Mwi Mw ₂ ) vs. (Twi - Tw2) designed to show the important differences in MWD / SCBD combination among inventive examples vs. commercial benchmarks. Such differences are believed to play a key role in determining the trade-off pattern and/or balance of various performance attributes such as stiffness, toughness and processability. In FIG. 4, the bridged hafnocenes (rac/meso- Me2Si((Me3Si)CH2Cp)2HfMe2) are denoted by OMC2918 and the zirconocenes (rac/meso) are denoted by Meind and Etind to reflect the corresponding substituted hydrocarbyl group. Other polymers are described in Table 5.

[00189] In the plot FIG. 3, the x-axis represents the value of the difference between the first and second weight average elution temperatures (Twi - Tw ₂ ). The y-axis in a log scale represents the ratio of the first weight average molecular weight to the second weight average molecular weight (Mwi/Mw ₂ ).

[00190] Various types of polymer composition can be described as below:

Point at X=0/Y=0: An ideal case of absolutely narrow MWD and absolutely narrow SCBD. Practically impossible for X=0 due to the forced division along temperature axis into two halves, as shown in FIG. 2 and FIG. 3.

Line of X=0: An ideal case of broadening MWD while keeping SCBD absolutely narrow. At X=0, no difference in the direction of moving Y values up or down; i.e., broadening MWD while keeping SCBD at absolute narrow. Line of Y=0: A case of broadening SCBD while keeping MWD unchanged and narrow.

Corner with X<0/Y <1 : Products where polymer composition characterized by the combination of Low Mwi/Low Ti (high SCB) molecules with High Mwi/High Ti (low SCB) molecules; exemplified by conventional LLDPE with ZN-catalyst.

Comer with X<0/Y>1 : Products where polymer composition characterized by the combination of Low Mwi/High Ti (low SCB) molecules with High Mwi/Low Ti (high SCB) molecules; exemplified by the so-called BOCD (Broad Orthogonal Composition Distribution) or Reversed Composition Distribution products.

[00191] Additional test methods include the following.

EXAMPLES

[00192] It is to be understood that while the invention has been described in conjunction with the specific embodiments thereof, the foregoing description is intended to illustrate and not limit the scope of the invention. Other aspects, advantages and modifications will be apparent to those skilled in the art to which the invention pertains.

[00193] Therefore, the following examples are put forth so as to provide those skilled in the art with a complete disclosure and description and are not intended to limit the scope of that which the inventors regard as their invention.

[00194] Catalyst systems (i.e., mixed or dual catalyst systems) were prepared using bridged hafnocenes (rac/meso-Me2Si((Me3Si)CH2Cp)2HfMe2) and zirconocenes (rac/meso) as shown below. Upon evaluation and testing to produce LLDPE products, the results revealed high catalyst activity and unique BOCD LLDPE products.

Me = methyl, Eth = ethyl, Ind = indenyl *Dimethyl leaving groups for the zirconocenes were employed although di-chloro versions of the catalyst could have also been employed as the drawing suggests. [00195] All manipulations were performed in an inert N2 purged glove box unless otherwise stated. All anhydrous solvents were purchased from Fisher Chemical and were degassed and dried over molecular sieves prior to use. Deuterated solvents were purchased from Cambridge Isotope Laboratories and dried over molecular sieves prior to use. n-Butyl lithium (2.5 M solution in hexane), dimethylsilyl dichloride (IVtoSiCh) and methylmagnesium bromide (3.0 M solution in diethyl ether) were purchased from Sigma-Aldrich. Hafnium tetrachloride (HfC ) 99+% and (trimethylsilyl)methyl trifluoromethanesulfonate were procured from Strem Chemicals and TCI America, respectively. n-Butyl lithium (2.5 M solution in hexane), iodomethane, indene and methyllithium (1.6 M solution in diethyl ether) were purchased from Sigma-Aldrich, and pentamethylcyclopentadienylzirconium trichloride (Cp*ZrCh) was purchased from Strem Chemical. All chemicals were used as purchased unless otherwise stated. 1-Methylindene and lithium- 1-methylindene were prepared in accordance with the description in Curnow, O. I ; Fern, G. M. J. Organomet. Chem. 2005, 690, 3018-3026.

Synthesis of (Trimethylsilyl) methylcvclopentadiene. (Me3Si)CH2CpH

[00196] (trimethylsilyl)methyl trifluoromethanesulfonate (10.57g, 44.7 mmol) was dissolved in 150 mL of diethyl ether and cooled to -25°C, to this a solid potassium cyclopentadienide (KCp) (4.66g, 44.7 mmol) was slowly added over a period of 5-10 minutes. It was prepared in accordance with the description in Amsharov, K. ; Abdurakhmanova, N.; Stepanow, S. ; Rauschenbach, S.; Jansen, M. ; Kern, K. Angew. Chem. Int. Ed. 2010, 49, 9392- 9396. The resulting mixture was stirred 5 hours at about 23°C. Volatiles from the reaction mixture were carefully removed under dynamic vacuum to avoid evaporating the volatile (trimethylsilyl)methylcyclopentadiene, (Me3Si)CH2CpH. The reaction flask (250 mL round bottom flask) and frit with celite were weighted to calculate yield of the product after extraction. The crude materials were extracted into pentane (3 x 10 mL) and used without any further purification. Based on above mathematical method, the yield is calculated as 5.55 g (81.6%). The ¾ NMR spectrum was recorded for the crude material to ensure the product formation. ¾ NMR (400 MHz, CeDe): δ -0.05 (9H, s, S1-CH3), 1.77 (2Η, d, JHH=1 .2 HZ, Me ₃ Si-CH ₂ ), 2.83 (1Η, sex, JHH=1 .5 HZ, Cp-CH), 5.80-6.49 (4Η, m, Cp-CH) ppm.

Synthesis of Lithium (trimethylsilyl) methylcvclopentadienide. (Me3Si)CH2CpLi

[00197] A hexane solution of n-butyl lithium (14.6 mL, 36.5 mmol) was added drop-wise to a precooled solution (pentane and diethyl ether, 50/50 mL) of (Me3Si)CH2CpH (5.55 g, 36.5 mmol) over a period of 15-20 minutes at -25°C. The resulting mixture was gradually brought to about 23°C and then continuously stirred overnight. Volatiles were removed in vacuo and remaining crude materials were thoroughly washed with pentane. The final materials were dried under vacuum to obtain a colorless crystalline solid of (Me3Si)CH2CpLi in 5.75 g (99.7%) yield. ¾ NMR (400 MHz, THF-c s): δ -0.09 (9H, s, Si-CH ₃ ), 1.84 (2Η, s, Me ₃ Si-CH ₂ ), 5.36 (2Η, t, 1HH=2.6 HZ, Cp-H), 5.47 (2Η, t, 1HH=2.6 HZ, Cp-H) ppm.

Synthesis of Dimethylsilyl-bis((trimethylsilyl) methylcvclopentadiene).

Me ₂ Si((Me ₃ Si)CH ₂ CpH) ₂

[00198] A neat Me ₂ SiCl ₂ (340 mg, 2.6 mmol) was dissolved in 10 mL of THF and cooled to -25°C. A solid lithium (trimethylsilyl) methylcyclopendienide was added to the above mixture and the resulting mixture was stirred overnight at about 23°C to ensure completion of the reaction. Volatiles from the reaction mixture were removed in vacuo and subsequently triturated with pentane to remove trace of THF. The crude materials were extracted into pentane and followed by solvent removal under vacuum afforded a thick yellow viscous oil of Me ₂ Si((Me ₃ Si)CH ₂ CpH) ₂ in 750 mg (80%) yield. ¾ NMR (400 MHz, CeDe): δ -0.15 (6H, bs, SiMe ₂ -CH ₃ ), 0.05 (18Η, s, SiMe ₃ -CH ₃ ), 1.81-1.87 (4Η, m, Me ₃ Si-CH ₂ ), 3.26 (1Η, s, Cp-H), 3.37 (1Η, s, Cp-H), 5.99-6.82 (6Η, m, Cp-H) ppm.

Synthesis of Lithium dimethylsilyl-bis((trimethylsilyl) methylcvclopentadienide) dimethoxy ethane complex. Me ₂ Si((Me ₃ Si)CH ₂ Cp) ₂ Li ₂ dme

[00199] A hexane solution of n-butyl lithium (1.7 mL, 4.2 mmol, 2.5 M solution) was added drop-wise to a precooled solution of Me ₂ Si((Me ₃ Si)CH ₂ CpH) ₂ (750 mg, 2.1 mmol) in 10 mL of dimethoxyethane over a period of 5-10 minutes at -25°C. The resulting mixture was gradually warmed to about 23°C and then continuously stirred ovemight. Volatiles from the reaction mixture were removed in vacuo, and triturated with pentane to remove DME. The crude materials were thoroughly washed with pentane to remove any soluble impurities, and dried under vacuum to give the colorless crystalline solid of Me ₂ Si((Me ₃ Si)CH ₂ Cp) ₂ Lir dme in 830 mg (93%) yield. ¾ NMR (400 MHz, THF-c¾): δ 0.2 (18H, s, SiMe ₃ -CH ₃ ), 0.93 (6Η, bs, SiMe ₂ -CH ₃ ), 2.26 (4Η, s, Me ₃ Si-CH ₂ ), 2.57 (4Η, s, dme-CH ₂ ), 2.77 (6H, s, dme-OCH ₃ ), 5.94-6.15 (6H, m, Cp-H) ppm.

Synthesis of Rac-meso- dimethylsilyl-bis((trimethylsilyl) methylcvclopentadienide)hafnium dichloride. Me ₂ Si((Me ₃ Si)CH ₂ Cp) ₂ HfCl ₂

[00200] A solid HfC (570 mg, 1.8 mmol) was added to a precooled diethyl ether (20 mL) solution of Me ₂ Si((Me ₃ Si)CH ₂ Cp) ₂ Lirdme (830 mg, 1.8 mmol) at -25°C. The resulting mixture was stirred overnight at about 23°C. Volatiles from the reaction mixture were removed in vacuo, and then extracted into dichloromethane. Solvent removal under vacuum gave a yellow crystalline solid of Me ₂ Si((Me3Si)CH2-Cp) ₂ HfCl2 in 1.02 g (94%) yield. The ¾ NMR spectrum of final material integrated a -1 : 1 ratio of raclmeso isomers. ¾ NMR (400 MHz, CD2CI2): δ -0.05 (18H, s, SiMe ₃ -CH ₃ ), -0.04 (18Η, s, SiMe ₃ -CH ₃ ), -0.64 (3Η, s, SiMe ₂ -CH ₃ , meso), -0.65 (6Η, s, SiMe ₂ -CH ₃ , rac), -0.68 (3Η, s, SiMe ₂ -CH ₃ , meso), 2.08-2.18 (8Η, m, Me ₃ Si-CH ₂ ), 5.14 (2Η, t, 1HH=2.6 HZ, Cp-H), 5.28 (2Η, t, 1HH=2.6 HZ, Cp-H), 5.64 (2Η, t,

Hz, Cp-H), 6.34 (2Η,

Synthesis of Rac-meso- dimethylsilyl-bis((trimethylsilyl) methylcvclopentadienide)hafnium dimethyl. Me2Si((Me ₃ Si)CH ₂ Cp)2HfMe2

[00201] An ethereal solution of MeMgBr (1.12 mL, 3.34 mmol) was added drop wise to a precooled diethyl ether solution of Me2Si((Me ₃ Si)CH2-Cp)2HfCl2 (1.01 g, 1.65 mmol) over a period of 3-5 minutes at -25°C. The resulting mixture was stirred overnight at about 23°C to ensure completion of the reaction. Insoluble materials were filtered through a pad of celite. Volatiles from the filtrate were removed under vacuum, and then the crude materials were extracted into pentane. Solvent removal in vacuo afforded a sticky yellow material of Me ₂ Si((Me ₃ Si)CH ₂ -Cp)2HfMe2 in 660 g (71%) yield. The ¾ NMR spectrum of final material integrated a -1 : 1 ratio of raclmeso isomers. ¾ NMR (400 MHz, CeDe): δ -0.25(3H, s, Hf- CH ₃ , meso), δ -0.24 (6Η, s, Hf-CH ₃ , rac), δ -0.20 (3Η, s, Hf-CH ₃ , meso), 0.03 (18Η, s, SiMe ₃ - CH ₃ ), 0.04 (18Η, s, SiMe ₃ -CH ₃ ), 0.19 (3Η, s, SiMe ₂ -CH ₃ , meso), 0.20 (6Η, s, SiMe ₂ -CH ₃ , rac), 0.22 (3Η, s, SiMe ₂ -CH ₃ , meso), 2.06 (4Η, s, Me ₃ Si-CH ₂ , rac), 2.09 (4Η, d, JHH=3.1 HZ, Me ₃ Si- CH2, meso), 5.03 (2Η, t, JHH=2.2 HZ, Cp-H), 5.10 (2Η, t, JHH=2.2 HZ, Cp-H), 5.34 (2Η, t,

Η, t, JHH=2.6 HZ, Cp-H), 6.26 (2Η, t, JHH=2.6 HZ, Cp-H), 6.31 (2Η,

Synthesis of itoc-ffleso-bisQ-Methyl-indenvDzirconium dimethyl. (!-MeInd)2ZrMe2

[00202] In a 500 mL round bottom flask, a solid ZrC (9.42 g, 40.4 mmol) was slurried with 250 mL of dimethoxy ethane (DME) and cooled to -25°C. A solid lithium- 1 -methyl-indenyl (11.0 g, 80.8 mmol) was added over a period of 5-10 minutes. The orange-yellow reaction mixture was gradually warmed to about 23°C and subsequently heated at 80°C for 1 hour to ensure the formation of bis(l-methyl-indenyl)zirconium di chloride in-situ. While heating resulting mixture, it was clear at first and then byproduct (LiCl) was precipitated out over a course reaction, revealing the product formation. Without any further purification, reaction mixture of bis(l-methyl-indenyl)zirconium dichloride was cooled to -25°C, and to this an ethereal solution of methylmagnesium bromide (27.0 mL, 80.8 mmol, 3.0 M solution in diethyl ether) was added over a period of 10-15 minutes. The resulting mixture was slowly turned pale yellow and then maroon over a course of reaction and continuously stirred overnight at about 23°C. Volatiles were removed in vacuo. The crude materials were then extracted with hexane (50 mL x 5), and solvent removal afforded to the formation of (l-MeInd)2ZrMe2 as an off- white solid in 13.6 g (89%) yield. The ¾ NMR spectrum of final material integrated a -0.8: 1 ratio of rac/meso isomers. ¾ NMR (400 MHz, CeDe): δ -1.33 (3H, s, meso), -0.84 (4.77H, s, rac), -0.34 (3H, s, meso), 2.14 (11.42H. overlapping s), 5.47-5.42 (6.41H, m), 6.95-6.88 (7.34H, m), 7.14-7.06 (3.45H, m), 7.30-7.27(3.35H, m) ppm.

Supported Catalyst Syntheses:

Mixed Catalyst 7 (Rac-meso- dimethylsilyl-bis((trimethylsilyl) methylcvclopentadienide)hafhium dimethyl: rac.meso-(l-MeInd)2ZrMe2. 80:20)

[00203] To a stirred vessel 1400 g of toluene was added along with 925 g of methylaluminoxane (30 wt% in toluene). To this solution 734 g of ES70 silica - 875°C calcined silica was added. The mixture was stirred for three hours at 100°C after which the temperature was reduced and the reaction was allowed to cool to about 23°C. Rac-meso- dimethylsilyl-bis((trimethylsilyl) methylcyclopentadienide)hafnium dimethyl (16.35 g, 32.00 mmol) and bis-ethylindenyl zirconium (IV) dimethyl (3.26 g, 8.00 mmol) were then dissolved in toluene (250 g) and added to the vessel, which was stirred for two more hours. The mixing speed was then reduced and stirred slowly while drying under vacuum for 60 hours, after which 1038 g of a light yellow material was obtained.

Mixed Catalyst 2 (Rac-meso- dimethylsilyl-bis((trimethylsilyl) methylcvclopentadienide)hafnium dimethyl: rac.meso-(l-EthInd)2ZrMe2. 80:20)

[00204] To a stirred vessel 1400 g of toluene was added along with 925 g of methylaluminoxane (30 wt% in toluene). To this solution 734 g of ES70 silica - 875°C calcined silica was added. The mixture was stirred for three hours at 100°C after which the temperature was reduced and the reaction was allowed to cool to about 23°C. Rac-meso- dimethylsilyl-bis((trimethylsilyl) methylcyclopentadienide)hafnium dimethyl (18.1 g, 32.00 mmol) and bis-ethylindenyl zirconium (IV) dimethyl (3.04 g, 8.00 mmol) were then dissolved in toluene (250 g) and added to the vessel, which was stirred for two more hours. The mixing speed was then reduced and stirred slowly while drying under vacuum for 60 hours, after which 1038 g of a light yellow material was obtained. Synthesis of i?ac-/we.s ^, o-bis(l-Ethyl-indenyl)zirconium dimethyl. (l -EtInd)2ZrMe2.

[00205] In a 500 mL round bottom flask, a solid ZrC (9.42 g, 40.4 mmol) was slurried with 250 mL of dimethoxy ethane (DME) and cooled to -25°C. A solid lithium- 1 -ethyl-indenyl (12.13 g, 80.8 mmol) was added over a period of 5-10 minutes, and then the reaction mixture was gradually warmed to about 23°C. The resulting orange-yellow mixture was heated at 80°C for 1 hour to ensure the formation of bis(l-ethyl-indenyl)zirconium dichloride. The mixture was clear at first and then byproduct (LiCl) was precipitated out over a course of reaction, revealing the product formation. Without further purification, the reaction mixture of bis(l - ethyl-indenyl)zirconium dichloride was cooled to -25°C, and to this an ethereal solution of methylmagnesium bromide (27.0 mL, 80.8 mmol, 3.0 M solution in diethyl ether) was added over a period of 10-15 minutes. The resulting mixture was slowly turned to pale yellow and then maroon over a course of reaction and continuously stirred overnight at about 23°C. Volatiles were removed in vacuo. The crude materials were then extracted with hexane (50 mL x 5), and subsequent solvent removal afforded to the formation of (l-EtInd)2ZrMe2 as an off-white solid in 13.0 g (78.9%) yield. The ¾ NMR spectrum of final material integrated a 1 : 1 ratio of rac/meso isomers. ¾ NMR (400 MHz, CeDe): δ -1.38 (3H, s, Zr-CH3, meso), - 0.88 (6Η, s, Zr-CH ₃ , rac), -0.30 (3Η, s, Zr-CH ₃ , meso), 1.10-1.04 (12Η, m, Et-CHs), 2.41 -2.52 (4Η, m, Et-CH ₂ ), 2.67-2.79 (4Η, m, Et-CH ₂ ), 5.46-5.52 (8Η, m, Ind-CH), 6.90-6.96 (8Η, m, Ar-CH), 7.08-7.15 (4Η, m, Ar-CH), 7.28-7.22 (4Η, m, Ar-CH) ppm.

Mixed Catalyst System and Polymerization Process

[00206] The polymerization process was performed in an 18.5 foot tall gas-phase fluidized bed reactor with an 18" diameter straight section. Cycle and feed gases were fed into the reactor body through a perforated distributor plate, and the reactor was controlled at 300 psi and 70 mol% ethylene. Reactor temperature was maintained by heating the cycle gas. The use of different poor comonomer incorporator (zirconocene as described above) catalysts can be used to alter the properties of the resulting polymer. Using mixed catalyst 1 yielded resin with a lower melt index ratio than mixed catalyst system 2. The ratio of poor comonomer incorporator (zirconocene as described above) and good comonomer incorporator (hafhocene as described above) can also be used to tune the product properties. Reaction conditions and product properties may be found in the following tables. Table 1 : Production of Bimodal Polyethylene Using Mixed Catalysts

[00207] Nuclear magnetic resonance measurements of the bimodal polyethylenes reveals some unsaturations, as summarized in Table 2. The labels "Vyl", "Vy2" and "Vy5" refer to proton resonances attributed to the protons on double bonds within the polymer backbone, as shown in the example ¾ NMR of FIG. 1. Table 2: Level of Unsaturation

(internal (I) and terminal (T)) for inventive polyethylenes

Table 3: Gas Phase Polymerization of Ethylene and 1-Hexene

Table 4: Gas Phase Polymerization of Ethylene and 1-Hexene

Table 5: Cross-Fractionation Chromatography

Dowlex™ 2045 polyethylene, Borstar™ FB2230 polyethylene, Evolue™ 3010 polyethylene, Elite™ 5400 polyethylene, and Exceed™ 1018 and Enable™ 2010 polyethylenes are all commercially available and may be obtained from The Dow Chemical Company, the Borealis Group, Prime Polymer Co., Ltd., The Dow Chemical Company, and ExxonMobil Chemical Company, respectively.

Film Production and Evaluation

[00208] Blown film evaluations of the inventive polymers from Table 1 were carried out on the Gloucester line at 60 mil die gap and 2.5 BUR. Further process data is found in Table 6. Film properties at 1.0 mil gauge are summarized below in Table 7 and comparative films in Table 8.

[00209] TDA is the total defect area. It is a measure of defects in a film specimen, and reported as the accumulated area of defects in square millimeters (mm ² ) normalized by the area of film in square meters (m ² ) examined, thus having a unit of (mm ² /m ² ) or "ppm". In the table below, only defects with a dimension above 200 microns are reported.

[00210] TDA is obtained by an Optical Control System (OCS). This system consists of a small extruder (ME20 2800), cast film die, chill roll unit (Model CR-9), a winding system with good film tension control, and an on-line camera system (Model FSA-100) to examine the cast film generated for optical defects. The typical testing condition for the cast film generation is given below:

• Extruder temperature setting (°C): Feed throat/Zone 1/Zone 2/Zone 3/Zone 4/Die:

70/190/200/210/215/215

· Extruder speed: 50 rpm

Chill roll temperature: 30°C

• Chill roll speed: 3.5 m/min

[00211] The system generates a cast film of about 4.9 inch in width and a nominal gauge of 2 mil. Melt temperature varies with materials, and is around 215°C.

[00212] ESO is the Energy specific output, is the extrusion output (lb/hr) in film extrusion normalized by the extruder power (hp) consumption and is a measure of a material's processability.

[00213] FIG. 5 shows the average MD/TD film modulus as a function of resins density for both comparative examples as well as the inventive examples. The equation (Eq-3) below shows the film modulus dependence of comparative examples on its resin density. All the inventive examples exhibited a substantial advantage in film stiffness at a given resin density.

Average Modulus = CI * Density - C2 (Eq-3).

[00214] In a class of embodiments, the film exhibits a relationship between average MD/TD modulus and density satisfying the following equation:

Avg. Modulus > 1.2 * (Cl *Density - C2);

and, in particular as an example,

Average Modulus > 1.2 * (2,065,292 * Density - 1,872,345). Table 6: Production of Films

Table 7: Properties of Films

Peak Force (lbs/mil) 10.06 10.27 9.34 9.82 9.01

Break Energy (in-lbs) 26.15 28.94 25.65 26.73 24.04

Break Energy

25.64 28.94 24.9 26.21 23.34 (in-lbs/mil)

Sealing

Seal Initiation

Temperature at IN force

(°C) 105.5 98.0 99.1 98.0

Seal Temperature at 5N

force (°C) 111.8 106.6 107.4 102.6

Maximum Seal force

(N) 10.3 10.7 10.7 10.4

Hot tack initiation

temperature at IN force

(°C) 103.7 97.4 96.6 97.2

Maximum hot tack force

(N) 9.0 14.2 14.8 12.1

Table 8: Comparative Films

(made under the same conditions as the inventive bPE Films as described above)

TD 6.0 4.9

Tensile Strength (psi)

MD 7515 8222

TD 7726 7343

Elongation @ Break (%)

MD 464 501

TD 638 700

Elmendorf Tear

MD (g) 226 117

TD (g) 429 620

MD (g/mil) 235 113

TD (g/mil) 440 602

Haze (%) >30 10.0

Gloss

MD 31.0 59.0

TD 32.0 60.0

Dart Drop

(g) 617 206

(g/mil) 643 204

Puncture

Peak Force (lbs) 11.04 10.67

Peak Force (lbs/mil) 11.5 11.57

Break Energy (in-lbs) 34.08 28.91

Break Energy (in-lbs/mil) 35.5 28.62

Sealing

Seal Initiation Temperature at IN force (°C) 98.7 105.2

Seal Initiation Temperature at 5N force (°C) 102.8 111.1

Seal force (N) 10.0 11.3

Hot tack initiation temperature at IN force (°C) 98.8 103.7

Hot tack peak force (N) 12.2 7.6

[00215] The phrases, unless otherwise specified, "consists essentially of and "consisting essentially of do not exclude the presence of other steps, elements, or materials, whether or not, specifically mentioned in this specification, so long as such steps, elements, or materials, do not affect the basic and novel characteristics of the invention, additionally, they do not exclude impurities and variances normally associated with the elements and materials used.

[00216] For the sake of brevity, only certain ranges are explicitly disclosed herein.

However, ranges from any lower limit may be combined with any upper limit to recite a range not explicitly recited, as well as, ranges from any lower limit may be combined with any other lower limit to recite a range not explicitly recited, in the same way, ranges from any upper limit may be combined with any other upper limit to recite a range not explicitly recited. Additionally, within a range includes every point or individual value between its end points even though not explicitly recited. Thus, every point or individual value may serve as its own lower or upper limit combined with any other point or individual value or any other lower or upper limit, to recite a range not explicitly recited.

[00217] All priority documents are herein fully incorporated by reference for all jurisdictions in which such incorporation is permitted and to the extent such disclosure is consistent with the description of the present invention. Further, all documents and references cited herein, including testing procedures, publications, patents, j oumal articles, etc. are herein fully incorporated by reference for all jurisdictions in which such incorporation is permitted and to the extent such disclosure is consistent with the description of the present invention.

[00218] While the invention has been described with respect to a number of embodiments and examples, those skilled in the art, having benefit of this disclosure, will appreciate that other embodiments can be devised which do not depart from the scope and spirit of the invention as disclosed herein.