The polymerisation of diallyamines using free radical initiation is known, for example from Solomon et al. , J.

Macromol. Sci. - Rev Macromol. Chem. c15 (1) 143-164 (1976).

Free radical initiation of polymerisation requires quite extreme reaction conditions which can be generated only in production plants etc. It is not suitable for situations where in situ polymerisation is required.

Other cyclpolymerisation reactions are discussed by C. D.

McLean et al. , J. Macromol. Sci. -Chem., A10 (5), pp857-873 (1976). Yet further reactions are described in WO 97/16504, W097/16472 where such reactions are used in a specialised way in the production of liquid crystal compounds.

The applicants have found that a broad range of compounds with at least two appropriately positioned multiple bonds and in particular double bonds may be activated by the presence of an electron withdrawing group, in particular where the electron withdrawing group is at a position which is alpha, beta or gamma to one or both of the double bonds to make them readily polymerisable under the influence of inter alia radiation. The term treadily polymerisable" means that the compounds will undergo polymerisation under moderate conditions of temperature and pressure (for example at room temperature and atmospheric pressure) in the presence of radiation and an initiator, in a period of less than 24 hours.

Polymeric compounds obtained therefrom include cyclic rings.

These have many advantageous properties. In particular, the invention can be used to generate products such as adhesives (see copending British Patent application No 9816169. 8), coatings, network polymers or conducting polymers (see copending British Patent Application No. 9816171. 0) depending upon the other aspects of the structure of the starting materials.

In its broadest aspect, the invention provides a method for producing a polymeric material, said method comprising subjecting a starting material which includes two double bonds which are activated so that they will take part in a polymerisation reaction and wherein the double bonds are sufficiently close together to ensure that cyclopolymerisation will preferentially occur ; to suitable conditions under which said polymerisation reaction will occur, provided that the starting material is other than triallyamine hydrochloride.

Specifically, the invention provides a method for producing a polymeric material, said method comprising subjecting a starting material which comprises a group of sub-formula (I) where Rl is CRa where Ra is hydrogen of alkyl, and R6 is a bond, or R1 and R6 together form an electron withdrawing group ; R2 and R3 are independently selected from (CR7R8) nt or a group CR9R10, CR7R8CR9R10 or CR9RllCR7RI where n is 0,1 or 2, R7 and R8 are independently selected from hydrogen or alkyl, and either one of R9 or R1° is hydrogen and the other is an electron withdrawing group, or R9 and R1° together form an electron withdrawing group, and

R4 and Rsare independently selected from CH or CR1l where R is an electron withdrawing group ; the dotted lines indicate the presence or absence of a bond, and X1 is a group CX2X3 where the dotted line bond to which it is attached is absent and a group CX2 where the dotted line bond to which it is attached is present, Y1 ils a group CY2Y3 where the dotted line bond to which it is attached is absent and a group Cy2 where the dotted line bond to which it is attached is present, and X2, X3, y2 and Y3 are independently selected from hydrogen and fluorine ; provided that at least one of (a) R1 and R6 or (b) R2 and R3 or (c) R4 and Rs includes an electron withdrawing group which is able to activate a cyclopolymerisation reaction ; to suitable conditions under which a cyclopolymerisation reaction will occur, subject to the following further provisos : (i) that the starting material is other than triallyamine hydrochloride ; (ii) that when R1 and R6 together form the sole electron withdrawing group and Ru ils a group N'R12 (Zm-) 1/., where R12 is hydrogen or hydrocarbyl, Z is an anion of charge m and R6 is a bond, said conditions are subjecting the compound to radiation in the substantial absence of a solvent or sulphur dioxide gas ; and (iii) that where R1 and R6 together form the sole electron withdrawing group and Rlis CH and R6 is OC(O), then the compound does not further contain a mesogenic group, or contains at least one further group of sub-formula (I).

As used herein, the expression"in the substantial absence of solvent"means that there is either no solvent present or there is insufficient solvent present to completely dissolve the reagents, although a small amount of a diluent may be present to allow the reagents to flow.

Conditions under which polymerisation will occur include the influence of radiation or an electron beam, or in the presence of a chemical initiator. Radiation or electron beam

induced polymerisation is suitably effected in the substantial absence of a solvent.

In particular Xl and Y are groups CX X and CY Y respectively and the dotted lines represent an absence of a bond. Thus preferred compounds are those of sub-formula (IA) where Rl, R2, R3, R4, R5, R6, Xz, X3, Yz and Y3 are as defined above.

One or more such starting materials may be polymerised together. When more than one starting material is used, a copolymer will result.

When the dotted bonds in sub formula (I) are present, the resulting polymer will comprise polyacetylene chains. This can lead to a conjugated system and consequently a conducting polymer.

Suitably there are no more than five atoms in between or linking the double bonds in the starting material so that when the cyclopolymerisation takes place, for example as illustrated hereinafter in Figure 1, the size of the rings formed does not exceed 7. Preferably, there are from 3 to 5 atoms in between the double bonds.

Suitably the starting material is one which will cyclopolymerise in the sort of conditions used in polymer production. This may comprise the application of radiation such as uv or thermal radiation, where necessary in the presence of a photoinitiator, by the application of other sorts of initiator such as chemical initiators, or by initiation using an electron beam. The expression chemical initiator"as used herein refers to compounds which can initiate polymerisation such as free radical initiators and ion initiators such as cationic or anionic initiators as are understood in the art.

Preferably, the starting materials polymerise under the influence of ultraviolet or thermal radiation, preferably ultraviolet radiation. Cyclopolymerisation may take place either spontaneously or in the presence of a suitable initiator. Examples of suitable initiators include 2,2'- azobisisobutyronitrile (AIBN), aromatic ketones such as benzophenones in particular acetophenone ; chlorinated acetophenones such as di- or tri-chloroacetophenone ; dialkoxyacetophenones such as dimethoxyacetophenones (sold under the Trade name MIrgacure 651")i dialkylhydroxyacetophenones such as dimethylhydroxyacetophenone (sold under the Trade name "Darocure 1173") ; substituted dialkylhydroxyacetophenone alkyl ethers such compounds of formula where RY is alkyl and in particular 2,2-dimethylethyl, Rx is hydroxy or halogen such as chloro, and RP and Rq are independently selected from alkyl or halogen such as chloro (examples of which are sold under the Trade names"Darocure 1116" and nTrigonal Pl")i 1-benzoylcyclohexanol-2 (sold under the Trade name"Irgacure 184") ; benzoin or derivatives such as benzoin acetate, benzoin alkyl ethers in particular benzoin butyl ether, dialkoxybenzoins such as dimethoxybenzoin or deoxybenzoin ; dibenzyl ketone ; acyloxime esters such as methyl or ethyl esters of acyloxime (sold under the trade name"Quantaqure PDO") ; acylphosphine oxides, acylphosphonates such as dialkylacylphosphonate, ketosulphides for example of formula

where R is alkyi and Ar is an aryl group ; dibenzoyl disulphides such as 4, 4'-dialkylbenzoyldisulphide ; diphenyldithiocarbonate; benzophenone; 4,4'-bis(N,N- dialkylamino) benzophenone ; fluorenone ; thioxanthone ; benzil ; or a compound of formula where Ar is an aryl group such as phenyl and R is alkyi such as methyl (sold under the trade name"Speedcure BMDS ").

As used herein, the term"alkyl"refers to straight or branched chain alkyl groups, suitably containing up to 20 and preferably up to 6 carbon atoms. The term"alkenyl"and "alkynyl"refer to unsaturated straight or branched chains which include for example from 2-20 carbon atoms, for example from 2 to 6 carbon atoms. Chains may include one or more double or triple bonds respectively. In addition, the term "aryl" refers to aromatic groups such as phenyl or naphthyl.

The term"hydrocarbyl"refers to any structure comprising carbon and hydrogen atoms. For example, these may be alkyl, alkenyl, alkynyl, aryl such as phenyl or napthyl, arylalkyl, cycloalkyl, cycloalkenyl or cycloalkynyl. Suitably they will contain up to 20 and preferably up to 10 carbon atoms.

The term"heterocylyl"includes aromatic or non-aromatic rings, for example containing from 4 to 20, suitably from 5 to 10 ring atoms, at least one of which is a heteroatom such as oxygen, sulphur or nitrogen. Examples of such groups

include furyl, thienyl, pyrrolyl, pyrrolidinyl, imidazolyl, triazolyl, thiazolyl, tetrazolyl, oxazolyl, isoxazolyl, pyrazolyl, pyridyl, pyrimidinyl, pyrazinyl, pyridazinyl, triazinyl, quinolinyl, iosquinolinyl, quinoxalinyl, benzthiazolyl, benzoxazolyl, benzothienyl or benzofuryl.

The term"functional group"refers to reactive groups such as halo, cyano, nitro, oxo, C(O)nRa, ORa, S(O)tRa, NRbRC, OC(O)NRbRc, C(O)NRbRc, OC(O)NRbRC, NR7C(O)nR6, NRªCONRbRc, - C=NORa, -N=CRbRC, S(O)tNRbRC, C(S)nRat C(S)ORa, C(S)NRbRC or - NRbS(O)tRa where Ra, Rb and R° are independently selected from hydrogen or optionally substituted hydrocarbyl, or Rb and R' together form an optionally substituted ring which optionally contains further heteroatoms such as S(O)s, oxygen and nitrogen, n is an integer of 1 or 2, t is 0 or an integer of 1-3. In particular the functional groups are groups such as halo, cyano, nitro, oxo, C(O)nRª, ORª, S(O)tRª, NRbRc, b C C (O ) NRbRC OC (O ) NRbRC, -NR7C(O)nR, NR CONR R, <BR> bRc C NORa -N=CRbRC, S(O)tNRbR , , or NR S(O)tR Ra, Rb and RC, n and t are as defined above.

The term"heteroatom"as used herein refers to non-carbon atoms such as oxygen, nitrogen or sulphur atoms. Where the nitrogen atoms are present, they will generally be present as part of an amino residue so that they will be substituted for example by hydrogen or alkyl.

The term"amide"is generally understood to refer to a group of formula C (O) NRaRb where Ra and Rb are hydrogen or an optionally substituted hydrocarbyl group. Similarly, the term"sulphonamide"will refer to a group of formula S ( O ) 2NRaRb, AS described above, suitable starting materials for use in the method of the invention will comprise a group of sub- formula (I)

where X1, X2, yland y2 are independently selected from hydrogen or fluorine, R1 is CRa where Ra is hydrogen or alkyl, and R6is a bond, or R1 and R6 together form an electron withdrawing group ; R² and R³ are independently selected from (CR7R8)n, or a group CR9R10, -(CR7R8CR9R10)- or -(CR9R10C R7R3)- where n is 0, 1 or 2 R and R8 are independently selected from hydrogen or alkyl, and either one of R9 or Rl° is hydrogen and the other is an electron withdrawing group, or R9 and R1° together form an electron withdrawing group, and R4 and Rsare independently selected from CH or CR1l where R is an electron withdrawing group ; provided that at least one of (a) R1 and R6 or (b) R2 and R3 or (c) R4 and R5 includes an electron withdrawing group.

The nature of the electron withdrawing group or groups used in any particular case will depend upon its position in relation to the double bond it is required to activate, as well as the nature of any other functional groups within the compound.

In a preferred embodiment, R¹ and R6 form an electron withdrawing group. For example, R¹ is a heteroatom or a substituted heteroatom which has electron withdrawing properties, for example a group N+R¹²(Zm-)1/m, S(O)pR¹³, B, P (O) qR" or Si(R15) where R12 R13 R14 and R15 are independently selected from hydrogen or hydrocarbyl, Z is an anion of charge m, p is 0,1 or 2, and q is 1 ; and R6 is a bond : or R' is a group CH and R6 is a group -C(O)O- or -OC(O)-. Most preferably, R1 is a group N+R¹²(Zm-)1/m, S (O) pR t Bt ( )q 15 R12 R13 R14 and R15 are independently selected from hydrogen or alkyl in particular C13 alkyl, and Z is an

anion, preferably a halide. In particular R1 is a group N+R12 (Z"-) lim, and R6 is a bond.

The nature of the anion Z will affect the properties of the final polymer and in particular, its conductivity, porosity and water permability. Suitable anions for the Z group include halide ions such as fluoride, chloride, bromide or iodide, borides such as boron tetrafluoride ; carboxylic acid esters such as those of formula R14C (O) O~ where R"is an optionally substituted hydrocarbyl group group such as haloalkyl, in particular trifluoromethyl ; and other cationic groups such as mesylate and tosylate. In general, the water permeability of the ultimate polymer will vary as follows : PF6- < BF4- < CF3SO3- < CF3COO- < N03- < S04 2- < I- < Br- < Cl- Other factors which affect the water permeability of the polymer is the nature of any group to which the group of sub- formula (I) is attached. When this contains for example perhaloalkyl substituents such as perfluoroalkyl, it will be largely water impermeable as compared to polymers which have alkylene bridging groups optionally interposed with say oxygen. Examples of such groups are given below.

Most preferably, the combination of R1 and R6 forms an amide group, where Rlis a nitrogen atom and R6 is a carbonyl group.

In a further preferred embodiment, R1 and R6 together form a sulphonamide group where Rlis a nitrogen atom and R6 is an S (O) 2 group.

Alternatively, where the activation is effected by electron withdrawing groups at a position indicated by R2 or R3, suitable electron withdrawing groups R9 and R10 include nitrile, trifluoromethyl, acyl such as acetyl or nitro, or preferably R9 and R10 together with the carbon atom to which they are attached form a carbonyl group.

Where R1lis an electron withdrawing group, it is suitably acyl such as acetyl, nitrile or nitro.

Preferably X1, X2, yl and y2 are all hydrogen.

Suitable groups Rainclude hydrogen or methyl, in particular hydrogen.

A preferred group of the compounds for use in the method of the invention is a compound of structure (II) and in particular a compound of formula (IIA) where X\X,X\Y\Y,Y\R\R,R\R",RFand the dotted bonds are as defined in relation to formula (I) above, r is an integer of 1 or more, and R16 is a bridging group, an optionally substituted hydrocarbyl group, a perhaloalkyl group or an amide, of valency r.

Where in the compound of formula (II) and (IIA), r is 1, compounds can be readily polymerised to form a variety of polymer types depending upon the nature of the group R16 and examples of groups which are commonly found in polymer technology is included below in Table 1. Some may be able to act, for example, as radiation curable adhesives as described in copending British Patent application No 9816169. 8.

However, other applications for such polymers obtained using the process of the invention may be found.

Monomers of this type may be represented as structure (III) here X1 x2 yl y2 R1 R2, R3, R4, Rs and R6 are as defined in relation to formula (I) above, R16 is an optionally substituted hydrocarbyl group, a perhaloalkyl group or an amide.

Preferably in the compounds of formula (III), as above, R1 and R6 form an electron withdrawing group. Suitably then R2 and R3 are groups (CR'R8) n and R'and R5 are CH groups.

Suitably, in the case of adhesives, R16 comprises a hydrocarbyl group, optionally substituted by a functional group. Preferably R'includes an unsaturated moiety, such as an aryl or alkenyl group, or a carbonyl substituent.

A class of compounds of formula (III) are those of formula (IV) where R16 is as defined above, and is in particular an optionally substituted alkyl, alkenyl, alkynyl or aryl group, wherein the optional substituents may be selected from halogen, hydroxy, carboxy or salts thereof or acyloxy. These compounds may be used in the monomer form as adhesive compositions. However, pre-formed polymers obtained by

polymerisation of these monomers form an aspect of the present invention.

Alternatively, R16 in formula (IV) may comprise a perhaloalkyl group, for example of from 1 to 3 carbon atoms such as a perhalomethyl group, in particular perfluoromethyl.

Another group for R16 in formula (IV) is a dialkenyl substituted amide, for example of sub formula (V) where R18 and R19 are selected from groups defined above for R2 and R3 in relation to formula (I), and are preferably -CH2- or - CHZCH2- groups ; and R20 and R21are selected from groups defined above as R3 and R'in relation to formula (I) and are preferably -CH- groups. Such groups would further activate the double bonds and give rise to the possibility of forming cross-linked polymer networks.

Another class of compound of formula (II) is represented by radiation curable compounds of formula (VI) where Z and m are as defined above, R22 and R23 are independently selected from hydrogen and hydrocarbyl, such as alkyl and alkenyl, in particular prop-2-enyl or hydroxyethyl.

The invention may also be applied to other sorts of polymers, for example, where in the compounds of formula (II), r is

greater than one, polymerisation can result is polymer networks. Particular examples are compounds of formula (II) as defined above, where R is a bridging group and r is an integer of 2 or more, for example from 2 to 8 and preferably from 2 -4.

On polymerisation of these such compounds, networks are formed whose properties may be selected depending upon the precise nature of the R16 group, the amount of chain terminator present and the polymerisation conditions employed. Polymerisation will occur in accordance with the general scheme set out in Figure 1 hereinafter.

Suitably r is an integer of from 2 to 6, preferably from 2 to 4. The polymers produced can be useful in a number of different applications including the production of network polymers and those used in thermal management. Such applications are described and claimed in copending British Patent application No. 9816171. 0.

Thermal management is the control of optical properties of materials across solar and thermal wavebands (-0. 7- 12microns). This control of transmitted, reflected and absorbed radiation gives the potential to design systems that can selectively perform different tasks at different wavelengths. For example use of silver coatings by the glazing industry to limit solar transmission (material transparent at visible wavelengths but reflective across the solar) and thus prevent'greenhouse'heating. Other example could be solar water heaters where the material is transparent at NIR wavelengths but reflective at longer wavelengths. Benefits of thermal management could be in reduced air conditioning/heating costs.

The properties of the polymer obtained in this way will depend upon a variety of factors but will depend very largely on the nature of the group R16

Suitably R16will comprise a bridging groups for example as is known in polymer, paint or coating chemistry. These may include straight or branched chain alkyl groups, optionally substituted or interposed with functional groups or siloxane groups such as alkyl siloxanes. Suitable bridging groups include those found in polyethylenes, polypropylenes, nylons, as listed in Table 1.

Table 1 Polymer type Repeat Unit of Bridging Group Polyethylene CH2 Polystyrene CH2CH(C6H5) where the phenyl ring is optionally substituted PolyisobutyleneCH2CH(CH(CH3)2) Polyisoprene CH2CH(CH3) Polytetrafluoroethylene CH2(CF2)xCH2 PolyvinylidenefluorideCHz(CFzCHz)x polyethyleneoxide (OCH2CH (CH3)) xO NylonCH2(NHCOCH2)xCH2 PeptideCH2(NHCOCHR)xCHz Polyurethanes-NH-CO-0- Polyesters-RC(0)OR'- where R and R'are organic groups such as hydrocarbyl Polysiloxanes e.g. -SiO2-, -R2SiO- or -R2Si203- where R is an organic group such as hydrocarbyl Polyacrylates-CH2C(COOH)H- Polyureas-NHCONH- Polythioureas -NH-C(S)-NH- The length of the bridging group will affect the properties of the polymeric material derived from this. This can be used to design polymers with properties which are best suited to the application. For instance when the bridging group comprises relatively long chains, (for example with in excess

of 6 repeat units, for example from 6-20 repeat units), the polymer will have pliable plastic properties. Alternatively, when the bridging group is relatively short, (e. g. less than 6 repeat units) the material will be more brittle.

Another method for producing particular properties arises from the possibility of producing copolymers where another monomeric compound, for example one which is not of formula (I), is mixed with the compound of formula (I) prior to polymerisation. Such monomers are known in the art.

Composites may also be produced by polymerising compounds of formula (I) in the presence of other moieties such as graphite, ethers such as crown ethers or thioethers, phthalocyanines, bipyridyls or liquid crystal compounds, all of which will produce composite polymers with modified properties.

Examples of possible bridging groups R16 where r is 2 are groups of sub-formula (VII) ~Zl~ (Ql). ~ (Z2~Q2) b-Z 3~ (VII) where a and b are independently selected from 0,1 or 2, Zlt z2 and Z3 are independently selected from a bond, an optionally substituted linear or branched alkyl or alkene chain wherein optionally one or more non-adjacent carbon atoms is replaced with a heteroatom or an amide group, Q1and Q2 are independently selected from an optionally substituted carbocylic or heterocyclic ring which optionally contains bridging alkyl groups.

Suitable carbocyclic rings for Qland Q2include cycloalkyl groups for example from 1 to 20 carbon atoms. Bridged carbocylic ring structures include 1,4-bicyclo[2.2.2] octane, decalin, bicyclo [2. 2. 1] heptane, cubane, diadamantane, adamantane. Suitable heterocyclic rings include any of the above where one or more non adjacent carbon atoms are

replaced by a heteroatom such as oxygen, sulphur or nitrogen (including amino or substituted amino), or a carboxyl or an amide group. Suitable optional substitutents for the groups Q1and Q2 include one or more groups selected from alkyl, alkenyl, alkynyl, aryl, aralkyl such as benzyl, or functional groups as defined above. Substitutents for the groups Q1 and Q2 are oxo and halogen in particular fluorine and chlorine.

Suitable optional substituents for the alkyl and alkene groups z1, z2 and Z3 include aryl, aralkyl and functional groups as defined above. Particular substituents include halogen such as fluorine and chlorine, and oxo.

Other sorts of bridging groups R16 include electrically conducting chains, for instance, electrically conducting unsaturated chains such as alkenes or chains incorporating aromatic or heterocyclic rings. For instance, the group R16 may comprise a tetra substituted conducting unit such as a tertathiafulvalene. Thus an example of such a is a compound of formula (VIII) where R23, R29, R30 and R31are each groups of sub-formula (IX)

where R1, R2, R3, R4, Rs and R6 are as defined in relation to formula (I) above and R24, R25, R26 and R27 are independently selected from groups of sub-formula (II) as given above. In ti lar R24 R25 R26and R27 are alkyl groups.

Polymerisation of compounds of formula (III) will give cross- linked networks where the cross-linking occurs through the double bonded units. This will lead to a very stable material with robust physical properties. Once again, varying the length of the spacer groups R24, R25, R26and R27 will lead to materials with designer properties. For instance when R24 Rzs RZS and RZ'are relatively long chains, the polymer will have pliable plastic properties.

Alternatively, when the chains R24, R25, R26and R27 are relatively short, the material will be more brittle.

Where R1and R6 together form a group -N+R7Z-, varying the counter ion Z-can also be used to adjust the physical properties of the polymer, such as water retention, porosity or conductivity. Suitably substituted materials will exhibit conducting properties, making them suitable as organic semiconductors for example for use as interconnects for IC chips etc.

Alternatively, a bridging group R16may comprise a tetra or octa substituted non-linear optic unit such as an optionally substituted porphyrin or phthalocyanine wherein the optional substitutents include hydrocarbyl groups as well as groups of sub formula (I). An example of such a porphyin compound is a compound of formula (X)

where R24, R25, R26, R27, R28, R29, R30 and R³¹ are as defined in relation to formula (III) above and R, R, R and R are each independently selected from hydrogen or hydrocarbyl groups ; and the compound optionally contains a metal ion within the macrocyclic heterocyclic unit.

An alternative phthalocyanine compound is a compound of formula (XA)

where RS° through to R65 are independently selected from hydrocarbyl in particular C1l2alkyl, a group OR68 where R68 is hydrocarbyl in particular butyl, halogen in particular chlorine or a group where R and R28 are as defined in relation to formula (III) above, provided that at least two of R to R65 are R -R groups, and R66 and R are either hydrogen or together comprise a metal ion such as a copper ion.

Preferably in formula (XA), R , R , R , R , R , R , R and R are halogen and R, R, R, R, R, R, R and R65 are independently C1l2alkyl, C1l2 alkoxy or a group R29-RZg.

Polymerisation of a compound of formula (X) or (XA) in accordance with the scheme of Figure 1, for example by photopolymerisation will provide a cross linked network polymer where the cross linking occurs through the diene units for example as either quaternery ammonium salts or amides depending upon the particular nature of the groups R' and R6 present in the R28, R29, R30and R31units. Again this can produce a very stable network or elastomeric material with robust physical properties. In addition to conductivity, these polymers will be capable of exhibiting third order polarisabilities and be suitable for applications which employ the Kerr effect. These properties can be affected or moderated when metals or metal ions are inserted into the macrocyclic heterocyclic unit. Suitable metal ions include sodium, potassium, lithium, copper, zinc or iron ions.

Yet a further possibility for the bridging group R16is a polysiloxane network polymer where R16comprises a straight or branched siloxane chain of valency r or a cyclic polysiloxane unit.

Thus compounds of structure (XI) where R24, R25, R28 and R29 are as defined above in relation to l (VII) R32 R33 R34 are R35, are selected from hydrocarbyl such as alkyl and in particular methyl, and each R36 or R37 group is independently selected from hydrocarbyl or a group of formula R26-R30 where R26 and R30 are as defined above in relation to formula (VII), and u is 0 or an integer of 1 or more, for example of from 1 to 20 ; and (XII) where R24 R2s R26 R27 R28, R29, R30 and R31 are as defined above in relation to formula (VII) and R32, R33, R34 and R3s are as defined above in relation to formula (XI). Although formula (XII) has been illustrated with four siloxane units in the ring, it will be appreciated that there may be other numbers of such units in the cyclic ring, for example from 3 to 8, preferably from 3 to 6 siloxane units.

In the above structures (XI) and (XII), it will be appreciated that -Si- may be replaced by B or B- ; or -Si-O- is replaced by -B-N (R") - where R39is a hydrocarbyl group such as those defined above in relation to group R32 in formula (XI) or a group -R24-R28 as defined in relation to formula (XII) above.

Upon polymerisation, compounds of formula (XI) and (XII) or variants thereof, will form a cross-linked network where the cross-linking occurs through the groups R28, R29, R30 and R3 as illustrated in Figure 1. Such polymers may exhibit properties similar to those of conventional siloxanes.

However, in the case of compounds of formula (XI) and (XII), they may be coated onto surfaces and polymerised in situ, for example using radiation curing.

Further examples of compounds of formula (III) include compounds of formula (XIII) where R,R",R,R,R,R,R° and R31 are as defined above in relation to formula (VIII).

The methodology of the invention may also be applied to the production of liquid crystal polymers. In this case, the monomeric units will include a mesogenic group as is understood in the art.

For example, suitable polymers may be obtained by the polymerisation of compounds of formula (III) where R17 comprises a group of sub formula (XIV) R33-Z6- R24 (XIV) where R24 is as defined above, Z6is selected from O, S, single covalent bond, COO, OCO ; and R33represents any mesogenic group ; Compounds of this type are novel and form the subject of a copending patent application of the applicants.

Compounds of formula (II) are suitably prepared by conventional methods, for example by reacting a compound of formula (XV) where X1, ylt y2, R2, R3, R4, Rs and the dotted bonds are as defined in relation to formula (II), R¹' is a group R¹ as defined in formula II or a precursor thereof, and R40 is hydrogen or hydroxy, with a compound of formula (XVI) R16- [R6-Z4]r (XVI) where R6, R16 and r are as defined in relation to formula (II) and Z4 is a leaving group, and thereafter if necessary, converting a precursor group R¹' to a group R1.

Where a compound of formula (IIA) is produced, the compound of formula (XV) will be of formula (XVA)

where R", R, R, R, R, R, x, x, Y and Y3 are as defined above.

Suitable leaving groups Z4 include halogen in particular bromo, mesylate or tosylate. The reaction is suitably effected in an organic solvent such as tetrahydrofuran, dichloromethane, toluene, an alcohol such as methanol or ethanol, or a ketone such as butanone and at elevated temperatures for example near the boiling point of the solvent.

Preferably the reaction is effected in the presence of a base such as potassium carbonate.

When the group R1 is a precursor of the group R1, it may be converted to the corresponding R'group using conventional techniques. For example R'may be a nitrogen atom, which may be converted to a group NRl2(Zm-) l/m where R12, Z and m are as defined above, by reaction with an appropriate salt under conventional conditions. Examples of this are illustrated hereinafter.

Compounds of formulae (XV) and (XVI) are either known compounds or they can be prepared from known compounds by conventional methods.

During the polymerisation process, the compounds link together by way of the multiple bond, in particular the diene group as illustrated in Figure 1. Where the compounds used include more than one diene grouping, for example compounds of formula (II) where R is 2 or more, they will tend to become cross linked to form a network or three dimensional structure. The degree of cross linking can be controlled by carrying out the polymerisation in the presence of cross-

linkers, where for example r is greater than 2, for example 4, or diluents. The latter will suitably comprise a compound of formula (XVI) whereX\X,Y\Y,R,R,R,R",R,R%R and r are as defined in relation to formula (II).

The method of the invention can be used in the preparation of homopolymers or copolymers where they are mixed with other monomeric units, which may themselves be of a similar basic structure, for example of formula (II) or otherwise.

A general scheme illustrating the sort of polymerisation process which may occur using a polyethylene type bridging group is illustrated in Figure 2.

Using the method of the invention, it is possible to take a suitable organic system that has optimal or optimised properties for use in certain applications, e. g. high yield strength, large hyperpolarisability, high pyroelectric coefficient, high conductivity etc, and to structurally modify the system so that it is possible to polymerise it.

If functional groups are incorporated that will polymerise, it will become possible to create a three dimensional network or plastic that will have properties associated with the parent organic system.

The advantages of the compounds of the invention is that they allow for the possibility that they can be applied in the form of a paint and caused to polymerise in situ. Thus this allows for ease of processing. Further, by providing for the construction of networks as a result of the cross linking, the resultant polymer can be mechanically strong and durable.

The versatility of the systems of the invention mean that it is possible to build in anisotropy which would improve directional physical properties, e. g. NLO, mechanical yield strength etc. Both amorphous or ordered systems can be prepared depending upon the particular polymerisation conditions used.

Copolymerisation is also possible and this can be used advantageously to affect physical properties of the polymer obtained.

Polymers obtained using the method of the invention maybe particularly suitable for the production of adhesive coatings, and multilayer coatings as well as binders. It is possible to manipulate the low molar mass coating before polymerisation is carried out, e. g., poling etc.

Films of polymeric material can be prepared as illustrated hereinafter. Thus material with the properties of for example, polyethylene films can be produced using radiation curing techniques if required.

Polymer coatings prepared as described herein have useful water-proofing, corrosion resistance and general dust and dirt protective properties, in particular where they include halogenated and particularly fluorinated bridging groups.

Thus they may be used in the production of fabrics such as clothing, electrical components or devices, mechanical components as well as building materials which require this feature. In addition, coatings of this type may produce anti-icing features which are useful, particularly where these materials are exposed to harsh external conditions.

Products treated in this way also exhibit strong pearling qualities and this assists in the rapid shedding of condensate. Thus surfaces remain relatively free of such condensates.

Such surfaces can be achieved on at least part of the internal surfaces of a structure containing interconnecting interstitial spaces, such as fibrous or granular material.

The present invention provides a product selected from a fabric, an electrical component or device, a mechanical component, or a construction or building material, having deposited thereon a polymeric coating derived from a monomer of formula (I) as defined above.

Suitable electrical components include small electrical components such as resistors, capacitors, condensers, circuit breakers, switches and connectors, as well as small assemblies of these, for example circuit boards on which these and/or other components are mounted. Electrical devices include conductors, such as HT leads for example, those used in automobile engines, and cables such as external or underground power cables. Such cables may be pre-coated with plastics of another insulating material.

Plastics coatings in accordance with the invention may be applied to electrical wiring. In particular, monomers of formula (I) which mimic polypropylene would be useful in this context.

Mechanical components include housings, bearings, shafts, gears, wheels, gaskets, filter housing, engines, gearboxes, transmission, steering or suspension components.

Building materials include wood, brick, concrete slabs or other pre-formed concrete structures, building blocks, stone, slates or insulation materials where there is a possibility that corrosion, weathering or water penetration is likely to cause problems.

Polymer coatings formed in accordance with the invention may be useful in electronic components which have a polymeric coating as resistance layers. The nature of the bridging group R16 will affect the resistance of the polymer layer.

optionally the bridging groups in the monomers may be aromatic or heteroaromatic, i. e. it may include one or more unsaturated carbon rings, optionally containing heteroatoms such as nitrogen, oxygen or sulphur, which give the surface formed additional resistance to etching by plasma etch processes as used in the semiconductor integrated circuit industry.

If necessary, the coating may be discontinuous, for example, patterned by etching, optionally after masking certain areas, so as to provide the desired electronic properties.

Techniques for achieving this are well known, and include for example, irradiation with high energy radiation such as electron beams, X-rays-or deep ultraviolet rays.

The irradiation breaks the bonds in the polymer and exposed areas can then be dissolved in a developer liquid.

Optionally, the coating may consist of a mixture of a monomer and a chemical designed to enhance its sensitivity to radiation exposure during the patterning process, such as quinione diazide or anthraquinone.

Suitable electronic components include printed circuit boards, semiconductor elements, optical devices, videodiscs, compact discs, floppy discs and the like.

The invention will now be particularly described by way of example with reference to the accompanying diagrammatic drawings in which : Figure 1 illustrates the polymerisation in accordance with the method of the invention ; and Figure 2 shows a general scheme whereby cross-linking to form network polymers may occur.

Example 1 Diallylamine (6.45g, 0.66mol), 1,10-dibromodecane (10.0g, 0.033mol) and potassium carbonate 9. 70g, 0. 66mol) were placed in ethanol (60cm³) and the mixture was refluxed for 10 hours.

The solids were removed by filtration and the solvent removed in vacuo to leave a yellow oil. The oil was purified by column chromatography using silica gel and ethyl acetate to leave, after removal of solvent in vacuo, 9. 80g, 89% of yellow oil.

HNMR (CDCl3) 6: 1.15-1.30 (m, 12H), 1. 35-1. 45 (m, 4H), 2. 40 (t, 4H), 3. 10 (d, 8H), 5. 05-5. 20 (m, 8H), 5. 30-5. 55 (m, 4H).

Ir vmax (thin film) : 2920,2850, 2800,1640, 1460,1440, 1350,1250, 1150,1110, 990, 915cm~l

Step 2 The monomer from step 1 above (4.0g) was treated with 3M aqueous methanolic trifluoroacetic acid to pH 1. 0. The organic phase was extracted with dichloromethane (100cm³) and washed with brine (60cm³) and water (60cm³) and then dried over MgSO4. Removal of solvent left a yellow oil. 6. 4g, 95%.

¹HNMR (CDCl3) #: 1.30(m, 12H), 1. 65 (quin, 4H), 3. 0 (quin, 4H), 3. 72 (s, 8H), 5. 60 (m, 8H), 5. 90 (m, 4H), 10. 10 (s, 2H).

Ir vmax (KCl disc): 2934,2861, 1780,1669, 1428, 1169. 3 (s), 994.5, 950.8, 798,722, 706, 617crn1

Step 3 The monomer from step 2 above (0. 2g) and Irgacure 184 (5mg) were dissolved in dry dichloromethane (2cm3) and the solution was spread evenly on a 18 x 25 cm glass plate. The solvent was evaporated off to leave a thin film. It was then irradiated with a Philips UVA sunlamp (75w) for 10 minutes.

The resultant cross-linked polymer was removed as strips (scalpel), washed in dichloromethane (50 cm3) and thoroughly dried. Yield O. lg, 50%.

Ir vmax (KC1 disc) : 2940,2864, 1780,1650, 1428,1170, 995, 951,799, 743,722, 620cm~1

Example 2 Step 1 The monomer obtained in Example 1 step 1 (5. 0g) was treated with a 3M aqueous methanolic solution of hexafluorophosphoric acid (3.0m) to pHl. The PF6- salt was extracted using dichloromethane (2 x 100cm³) and the combined extracts were dried over MgSO4. Removal of solvent left a yellow oil.

9. 16g, 96%.

Ir vmax (KCl disc): 3508,3199, 2931,2859, 2663,1691, 1648, 1469,1427, 1290,1142, 1049,996, 953, 842.6(s), 737cm-1.

1HNMR (CDCL3) 8 : 1. 25 (s, br, 12H), 1. 65 (s, br, 4H), 2. 95 (s, br, 4H), 3. 65 (s, br, 8H), 5. 60 (m, 8H), 5. 90 (m, 4H), 9. 75 (s, br, 2H)

Step 2 The monomer from step 1 (0. 2g) was dissolved with Irgacure 184 (5mg) in dry dichloromethane (l.Ocm3) and the solution spread evenly on a 2 x 4 sX' sheet of aluminium. The solvent was removed by warming and the film was irradiated with the Philips UVA (75w) u/v lamp for 10 minutes to form a cross- linked polymeric coating.

Ir vmax : 3434,2937, 2859,2717, 1674,1467, 1297,1140, 843 (s) (P-F), 558cm~ Example 3 Step 1

The monomer from Example 1 step 1 (l. Og) was treated with 3M aqueous methanolic hydrochloric acid to pH 1. 0 (universal indicator paper). The organic phase was extracted with dichloromethane (lOOcm3) and washed with brine (60cm³) then water (60cm³) and dried over MgSO4. Removal of solvent left a heavy yellow oil. 1. 2g, 96%.

Ir vmax (KC1. Disc) : 2929,2855, 2632,2536, 1645,1456, 1426,1362, 1222,997, 948cm~l HNMR (DMSO) 8 : 1. 25 (m, 10H), 1. 67 (m, 4H), 2. 89 (m, 4H), 3. 66 (s, 8H), 5. 42-5. 53 (m, 8H), 5. 96-6. 01 (m, 4H), 11. 20 (s, 2H).

Step 2 The diallylamine salt obtained in step 1 above (l. Og, 0. 0025mol) and Irgacure 184 (25. 3mg, 0. 000124mol) were dissolved in dry dichloromethane (2 cm³) and the solution spread on an 18 x 25 cm2 glass plate. The solvent was allowed to evaporate and the remaining clear film was irradiated for approximately 3 minutes under a Philips UVA (75w) sunlamp. The resultant cross-linked polymer was removed

from the glass plate, washed in dichloromethane and. Yield 0. 75g, 75%.

Ir vmax (KC1 disc) : 2800-2200 (broad), 1620 (w), 1455 (s), 1050(w), 1000(w), 950(w), 720(w) cm-1 Example 4 Step 1 The monomer obtained as described in Example 1 step 1 (3. 0g, 0. 0094mol) and methyl iodide (2. 60g, 0. 22mol) in dry dichloromethane (30cm³) were refluxed together for 7 hours.

The solvent and residual methyl iodide were removed in vacuo and the orange residue re-dissolved in dry dichloromethane (lOOcm3). The orange solution was washed in brine (50cm³) and dried over MgS04. Removal of solvent gave an orange oil which formed a soft solid on standing. Yield 4. 95g, 89%.

HNMR (DMSO) 8 : 1. 27 (m, 12H), 1. 69 (m, 4H), 2. 99 (6H), 3. 10- 3. 20 (m, 4H), 3. 95 (d, 8H), 5. 55-5. 75 (m, 8H), 5. 95-6. 18 (m, 4H).

Ir vmax (KC1 disc) : 3081,2925, 2854,2361, 1689,1641, 1470, 1424,1371, 1302,1246, 994,943, 894,868, 724,668.

Step 1A In an alternative preparation of the compound of step 1 above, the monomer obtained as described in Example 1 step 1 above (lO.Og, 0.030mol) and methyl iodide (9. 23g, 0. 065mol) in a mixture of tetrahydrofuran (lOOcm3) and dichloromethane (20cm3) were stirred together. After 0. 5 hour the solution began to become turbid and the turbidity increased as time progressed. The solvent was removed in vacuo and the white solid residue was suspended in 40/60 petrol (100 cm3) and stirred for 1 hour. Filtration and thorough drying in vacuo gave 17. 79g, 96% of a white, soft solid.

HNMR (CDCl2) 6: 1.20-1.40(s, 12H), 1. 80 (s, 4H), 3. 20 (s, 6H), 3. 40 (m, 4H), 4. 15 (m, 8H), 5. 65-5. 86 (m, 8H), 5. 95-6. 10 (m, 4H) Ir vmax (KC1 disc) : 3080,3050, 2930,2860, 1640,1470, 1440, 1425,1370, 1300,995, 945 cm- Step 2 The monomer from step 1 above (0. 7g, 0. 00114mol) and Irgacure 184 (23. 2mg, 0. 00014mol) were dissolved in dry dichloromethane (3cm3). The monomer/photoinitiator mixture was spread evenly on an 18 x 25cm3glass plate and the

solvent left to evaporate in air to leave a clear, light yellow film. The film was irradiated with a Philips UVA (75w) sunlamp for 15 minutes. Examination showed that the monomer had polymerised to form a hard, cross-linked polymer.

The polymer was removed as strips of clear film and placed in dry dichloromethane (lOOcm3) and the mixture stirred for 15 minutes. The film strips were removed by filtration and dried in vacuo.

Ir vmax (KC1 disc) : 2923,2852, 1680 (w), 1613, 1461 (s), 950(s), 726cm~l.

A similar reaction using l.Og(0.0016mol) of the monomer obtained in step 1A above and 16. 3g (0. 00008mol) Irgacure 184 produced 0. 84g (84%) of cross-linked polymer.

Ir vmax (KC1 disc) : 3480 (H20), 2920,2860, 1640 (w), 1460, 1000,955 cW 1 Example 5 Step 1

3, 6, 9-Trioxaundecandioic Acid (4. 4g, 0. 0179 mol), 1, 4- pentadien-3-ol (3. 0g, 0. 0357 mol), 1, 3- dicyclohexylcarbodiimide (7. 63g, 0. 037 mol) and 4- dimethylaminopyridine (250 mg) were stirred together in dry dichloromethane (100 cm³) for 48 hours at room temperature.

The 1, 3-dicyclohexylurea was removed by filtration and the solvent removed in vacuo to leave an oil. Purification using silica gel and ethyl acetate - 40 : 60 petrol (1 : 1) as eluent followed by removal of solvent and thorough drying gave 6. 4g, 91% of colourless, clear oil.

Ir vmax (thin film) : 2920,2860, 1750,1635, 1420,1380, 1350,1270, 1250,1195, 1150,1120, 990,935, 880,850, 730, 690,580 cml HNMR (CDCl3) 6: 3.65-3.80(m, 8H), 4. 15 (s, 4H), 5. 25-5. 50 (m, 10H), 5. 75-5. 95 (m, 4H).

Step 2 The monomer from Example 5 step 1(1.5g, 0.0042mol) and Irgacure 184 (43mg) were dissolved in dry dichloromethane (2

ml) and the solution was spread evenly on an 18 x 25 cm plate glass sheet. The solvent was allowed to dry in air then the remaining polymer/photoinitiator film was irradiated beneath a Philips UVA (70w) U/V sunlamp for 2 hours. The resultant cross-linked polymer was scraped (scalpel) from the plate and suspended in dry dichloromethane (20ml) and the suspension was stirred for approximately 15 minutes. The polymer was recovered by filtration and the retained solid washed with dry dichloromethane (2 x 10 cm3) and then dried thoroughly to leave 0. 6g 40% of clear film polymeric material.

Ir vmax (thin film) : 2920,2860, 1740,1630, 1450,1380, 1275,1200, 1145,1120, 850 cm~ Example 6 Step 1 3, 6, 9-Trioxaundecandioic acid (5. 33g, 0. 024 mol), 1, 5- Hexadien-3-ol (5. 0g, 0. 051 mol), 1, 3-dicyclohexylcarbodiimide (10. 5g, 0. 051 mol) and 4-dimethylaminopyridine (250mg) were stirred together in dry dichloromethane (50 cm3) at room temperature for 6 hours. The 1, 3-dicyclohexylurea was removed by filtration and the solvent removed in vacuo to

leave a yellow oil which was purified by column chromatography using silica gel/ethyl acetate. Yield 8. Og, 87%.

HNMR (CDCl3) 6: 2.4(t, 4H), 3. 65 (m, 8H), 4. 20 (s, 4H), 5. 05- 5. 45 (m, 10H), 5. 65-5. 90 (m, 4H) Ir vmax (thin film) : 2920,2860, 1760,1640, 1425,1200, 1150,1120, 990,920 cm-1 Step 2 The monomer from step 1 above (1. 6g, 0. 0042mol) and Irgacure 184 (43mg, 5 mol%) were dissolved in dry dichloromethane (2 ml) and the solution was spread evenly on an 18 x 25 cm plate glass sheet. The solvent was allowed to dry in air then the remaining polymer/photoinitiator film was irradiated beneath a Philips UVA (70w) U/V sunlamp for 2 hours. The resultant cross-linked polymer was scraped (scalpel) from the plate land suspended in dry dichloromethane (20ml) and the suspension was stirred for approximately 15 minutes. The polymer was recovered by filtration and the retained solid washed with dry dichloromethane (2 x 10 cm3) and then dried

thoroughly to leave a clear film polymeric material. Yield 1. 34g, 87%.

Ir vmax (thin film) : AWH/11 : 2920,2860, 1740 (S), 1635,1450, 1430,1380, 1280,1200, 1145,1120, 990,925, 850 CM-1 Example 7 Step 1 3, 6, 9-Trioxaundecanoic acid (5. 0g, 0. 026 mol), diallylamine (5. 10g, 0. 055 mol), 1, 3-Dicyclohexylcarbodiimide (11. 35g, 0. 055 mol) and 4-dimethylaminopyridine (0. 5g) were stirred together in dry dichloromethane (lOOcm3) for 6 hours. The resultant 1, 3-dicyclohexylurea was removed by filtration and the solvent removed in vacuo to give a yellow oil. Column chromatography using ethyl acetate - petrol 40/60 (1 : 1) followed by removal of solvent in vacuo and thorough drying gave the product as a yellow oil. (Yield 8.0g, 94%) Ir vmax (thin film) : 2930,2860, 1660 (s), 1530,1470, 1450, 1420,1350, 1280,1230, 1195, 1115 (s), 995,930, 755 cm~1

¹HNMR (CDCl3) #: 3.70(m, 8H), 3. 90 (m, 4H), 4. 0 (m, 4H), 4. 25 (s, 4H), 5. 10-5. 25 (m, 8H), 5. 75-5. 90 (m, 4H) Step 2 Monomer from step 1 above (l.Og, 0.00263mol) and 5 mol% Irgacure 184 (27mg, 0. 00013mol) were dissolved in dry dichloromethane (3cm³) and the solution spread over an 18 x 25 cm glass plate. The solvent was allowed to evaporate to leave a thin clear film. The film was then irradiated with a Philips UVA sunlamp (75w) for approximately 5 minutes to form a hard polymeric cross-linked coating. The coating was removed and washed in dry dichloromethane and then thoroughly dried (Yield 0. 73g, 73%) Ir vmax (KC1 disc) : 2920,2860, 1640 (s), 1530,1450, 1240, 1115(s), 730cm~1

Example 8 Step 1 3, 6, 9-Trioxaundecandioic acid (2. 64g, 0. 012 mol), 1, 1- diallylethanol (3. 0g, 0. 023 mol), 1, 3- dicyclohexylcarbodiimide (5. 16g, 0. 025 mol) and 4- dimethylaminopyridine (150mg) were dissolved in dry dichloromethane (100 cm³) and the solution stirred for 18h at room temperature. 1, 3-Dicyclohexylurea was removed by filtration and the solvent removed in vacuo to leave a yellow oil. Column chromatography using silica gel and ethyl acetate gave, after removal of solvent in vacuo, a clear oil, 4.9g, 94%.

¹HNMR (CDCl3) #: 1.45 (s, 8H), 2. 50-2. 70 (m, A : B, 8H), 3. 70 (s, 6H), 4. 05 (s, 4H), 5. 05-5. 15 (m, 8H), 5. 70-5. 90 (m, 4H) Ir vmax (thin film) : 2920,2870, 1750,1450, 1380,1210, 1150,1120, 740,700 cm~1 Step 2

The monomer from Step 1 above (l. Og, 0. 0023 mol) and Irgacure 184 (5 mol % ; 23. 5mg, 0. 00012 mol) were dissolved in dry dichloromethane (3 cm3) and the solution spread over a 18 x 25 cm glass plate. The solvent was allowed to evaporate to leave a thin clear film. The film was them irradiated with a Philips UVA sunlamp (75 w) to form a hard cross-linked polymer coating. The coating was removed and washed in dry dichloromethane and then dried thoroughly. Yield 0. 78g, 78%.

Ir vmax (KC1 disc) : 2940,2880, 1750,1450, 1380,1205, 1145,1120, 1030,960 cm~1

Example 9 Step 1 The diacid shown above (2. 5g, 0. 0114 mol), 1, 5-hexadien-3-ol (1. 34g, 0. 024 mol), 1, 3-dicyclohexylcarbodiimide (206. 33) (5.16g, 0.025 mol) and 4-dimethylaminopyridine (200mg) were placed in dry dichloromethane (lOOcm3) and the solution stirred for 18 hours at room temperature. 1, 3- dicyclohexylurea was removed by filtration and the solvent removed in vacuo to leave a yellow oil. Column chromatography using silica gel with ethyl acetate gave a clear oil, 2. 84g, 66%.

¹HNMR (CDCl3) #: 1.20(quin, 2H), 1. 65 (m 4H), 2. 40 (t, 4H), 3. 60 (d, 4H), 4. 20 (s, 4H), 5. 05-5. 45 (m, 10H), 5. 65-5. 90 (m, 4H).

Ir vmax (thin film) : 2920,2860, 1750,1700, 1510,1430, 1240,1200, 1140,1030, 990,920, 760cm-1

Step 2 Monomer from step 1 above (0. 7g, 0. 001894 mol) and Irgacure 184 (37. 6mg, 0. 0000184 mol) were dissolved in dry dichloromethane (3cm3) and the solution was spread on an 18 x 25 cm3 glass plate. The solvent was allowed to evaporate to leave a clear film. This was irradiated with a Philips UVA (75w) sunlamp for 2 hours until the film hardened. The film was removed and placed in dry dichloromethane (50cm3) and stirred for 1 hour. The cross-linked polymer was removed by filtration and washed with dry dichloromethane (2 x 50 cm3) and dried thoroughly to leave a creamy coloured polymeric solid. Yield 0. 35g, 50%.

Ir vmax (KC1 disc) : 2940,2860, 1750 (s), 1450,1285, 1205, 1130, 1030cm1

Example 10 Step 1 Polyethylene glycol 600 diacid (12.0g, 0.020 mol), diallylamine (4. 67g, 0. 048 mol), 1, 3- dicyclohexylcarbodiimide (10. 6g, 0. 048 mol) and 4- dimethylaminopyridine (600mg) were placed in dichloromethane (100 cm³) and the mixture stirred for 24 hours at room temperature. The 1, 3-dicyclohexylurea was removed by filtration and the solvent removed in vacuo to leave a yellow oil. Column chromatography (silica gel/ethyl acetate) followed by removal of solvent in vacuo gave a pale yellow oil. 13.90g, 92%.

¹HNMR (CDCl3) #: 3.60(m, 48H), 3. 90 (d, 4H), 4. 0 (d, 4H), 4. 20 (s, 4H), 5. 15 (m, 8H), 5. 75 (m, 4H) Ir vmax (thin film) : 3016,2922, 1662 (s), 1470,1353, 1219, 1114,931, 756,666 cml

Step 2 Monomer from Step 1 (l. Og) and Irgacure (1. 5mg) were dissolved in dry dichloromethane (3 cm3) and thoroughly mixed. The solution was spread evenly on an 18 x 25 cm glass plate and the solvent allowed to evaporate to leave a thin film of monomer. The film was irradiated with the Philips UVA (75w) sunlamp for 30 minutes to form a soft, permeable to water, cross-linked polymer film.

Ir vmax (thin film) : 3438,2946, 2371,1703, 1648 (s), 1544, 1510,1457, 1352, 1099 (vs), 953,856, 727,551 cm~1

Example 11 Step 1 Diallylamine (9. 72g, 0. 1 mol), Sebacic acid (lO.OOg, 0.0050 mol), 1, 3-dicyclohexylcarbodiimide (22. 70g. 0. 11 mol) and 4- dimethylaminopyridine (0. 450g) were stirred together in dry dichloromethane (lOOcm3) for 6 hours. The resultant 1, 3- dicyclohexylurea was removed by filtration and the solvent removed in vacuo to give a yellow oil. Column chromatography using ethyl acetate - petrol 40/60 (1 : 1) followed by removal of solvent in vacuo and thorough drying gave the product as a yellow oil. 15. 90g, 90%.

Ir vmax (thin film) : 2920,2850, 1690 (w), 1640 (s), 1520, 1460,1410, 1220,990, 920, 730cm~1 HNMR (CDCl3) 6: 1.10-1.45 (m, 6H), 1. 50-2. 00 (m, 6H), 2. 40 (t, 4H), 3. 90 (d, 4H), 4. 0 (d, 4H), 5. 05-5. 20 (m, 8H), 5. 20- 5. 90 (m, 4H)

Step 2 Monomer from Step 1 (l. OOg, 0. 0028 mol) and Irgacure 184 (28. 3 mg, 0. 000139 mol) were dissolved in dry dichloromethane (3cm3) and the solution spread over a 18 x 25 cm glass plate.

The solvent was allowed to evaporate to leave a thin clear film. The film was then irradiated with a Philips UVA sunlamp (75w) for approximately 5 minutes to form a hard polymeric cross-linked coating. The coating was removed and washed in dry dichloromethane and then thoroughly dried.

Yield 0. 80 g, 80%.

Ir vmax KC1 disc) : 2920,2860, 1640,1530, 1450, 1230 (w), 1340 (w), 1230 (w), 1000 (w), 930 (w).

Example 12 Step 1 Eicosanedioic acid (5. 0g, 0. 0146 mol), diallylamine (3. 12g, 0. 032 mol), 1, 3-dicyclohexylcarbodiimide (6. 60g, 0. 032 mol) and 4-dimethylaminopyridine (200mg) were dissolved in dichloromethane/tetrahydrofuran mixture (1 : 1) (100 cm3) and the mixture stirred at room temperature for 72 hours. 1, 3- Dicyclohexylurea was removed by filtration and the solvent removed in vacuo to leave a yellow oil. Column chromatography using silica gel/ethyl acetate followed by removal of solvent in vacuo and thorough drying gave a pale yellow oil. 6. 35g, 87%.

¹HNMR (CDCl3) #: 1.20(s, br, 28H), 1. 60 (m, 4H), 1. 80 (m, 4H), 3. 90 (d, 4H), 4. 0 (d, 4H), 5. 10 (m, 8H), 5. 75 (m, 4H).

Ir vmax (thin film) : 3006,2927, 2854,1643, 1530,1466, 1415,1217, 1084,992, 925,893, 756,666 cm~1.

Step 2 Monomer from Step 1 (0. 25g) and Irgacure 184 (5mg) were dissolved in dry dichloromethane (1.0 cm3) and the solution was heated (water bath) to ensure even distribution of photoinitiator. The solution was spread evenly on a 4 x 2" piece of aluminium foil and the solvent was allowed to evaporate off to leave a thin film of monomer/photoinitiator.

This was irradiated with a Philips UVA (75w) sunlamp for 30 minutes until a hard cross-linked polymer was formed. To test for hydrophobicity, the foil + polymer was subjected to running water for 30 minutes. After this time the polymer laminate was not adversely affected, i. e. no loss of adhesion to the foil.

Ir vmax (KC1 disc) : 2924,2851, 1648,1534, 1452,1227, 721 -1

Example 13 Step 1 Diallylamine (12. 90g, 0. 132 mol), 1, 2-dibromoethane (12. 40g, 0. 066 mol) and potassium carbonate (18. 80g, 0. 132 mol) were refluxed in ethanol (lOOcm3) for 24 hours. Solids were removed by filtration and solvents removed in vacuo to leave a yellow oil. The oil was purified by column chromatography (silica gel/ethyl acetate) to leave a pale yellow oil.

13. 40, 92%.

¹HNMR (CDCl3) #: 2.55(s, 4H), 3. 10 (d, 8H), 5. 10 (m, 8H), 5. 80 (m, 4H) Ir vmax (thin film) : 3082,3012, 2983,2927, 2806,1645, 1447,1420, 1355,1262, 1109,997, 919,559 cm~ Step 2

Monomer from Step 1 (5.0g) was treated with an aqueous methanolic solution of hexafluorophosphonic acid 60% solution in H20 (3.Om) to pHl. The PF6- salt was extracted using dichloromethane (2 x lOOcm3) and the combined extracts were dried over MgSO4. Removal of solvent left a yellow oil.

8. 0g, 96%.

¹HNMR (CDCl3) #: 3.60(d, 2H), 3. 75 (d, 2H), 3. 80 (s, 8H), 5. 55 (m, 8H), 5. 90 (m, 4H), 9. 80 (s, br, 2H) Ir vmax (thin film) : 3428,2986, 2634,1460, 1426,1294, 1246,1142, 1053,977, 953,842, 740 cm~1 The product may then be polymerised, for example as described in Example 1 Step 3 above.

Example 14 Step 1 Diallylamine (1. 41g, 0. 0145 mol), perfluoro-1, 10- decanedicarboxylic acid (2. 5g, 0. 0073 mol), 1, 3- dicyclohexylcarbodiimide (3. 20g, 0. 0155 mol) and 4- dimethylaminopyridine (0. 5g) were stirred together in dry dichloromethane (60 cm3) for 6 hours. The solvent was removed in vacuo to leave a white solid which was purified using column chromatography (ethyl acetate-petrol 40/60 1 : 1) and dried thoroughly to give 2. 96g, 79% of clear oil.

SHNMR (CDCl3) 6: 3.90(d, 4H), 4. 00 (d, 4H), 5. 10-5. 25 (m, 8H), 5. 70-5. 81 (m, 4H) Ir vmax (thin film) : 2933,2857, 1692, 1645. 5, 1611. 4, 1576, 1454,1419, 1377,1350, 1219,1151, 1081,992, 932,892, 735, 657,556.

Step 2 Monomer from Step 1 (l. Og, 0. 0019 mol) was dissolved in dry dichloromethane (3 cm3) and Irgacure 184 (20mg, 0. 000095 mol) and the resultant solution spread evenly over an 18 x 25 cm glass plate. The solvent was allowed to evaporate off to leave a clear liquid layer of monomer/photoinitiator. The plate was placed under a Philips UVA (75w) sunlamp for approximately 15 minutes. The resultant clear film was removed (powdery) and dried after stirring for 30 minutes in dry dichloromethane (100 cm3) to leave 0. 79g, 79% of white powder.

Ir vmax (thin film) : 2936,2859, 1691,1624, 1576,1455, 1372,1218, 1151,1079, 892,729, 654,555 cm~1

Example 15 Step 1 Sebacic acid (2. 0g, 0. 0099 mol), 1,4-pentan-3-ol (1.7g, 0.02 mol), 1, 3-dicyclohexylcarbodiimide (4. 52g, 0. 022 mol) and 4- dimethylaminopyridine (200g) in dry dichloromethane (60 cm3) were stirred together for 18 hours. The 1, 3-dicyclohexylurea was removed by filtration and solvent removed to leave clear oil. This was dissolved in 40/60 petrol (lOOcm3) and washed in water then dried over MgS04. Removal of solvent left a clear, colourless oil which tlc (dichloromethane) (developing in iodine) showed as a single spot. The oil was thoroughly dried in vacuo to leave 2. 49g, 75% of clear oil.

HNMR (CDCl3) 6: 1.30(s, 8H), 1. 60 (t, 4H), 2. 35 (t, 4H), 5. 15- 5. 35 (m, 8H), 5. 65-5. 95 (m, 6H) Ir vmax (thin film) : 2920,2860, 1730,1640, 1510,1460, 1410,1365, 1240,1165, 1095,985, 930 cm~1

Step 2 Monomer from Step 1 (l. Og, 0. 003 mol) and Irgacure 184 (31mg, 0. 00015 mol) were dissolved in dry dichloromethane (2 ml) and the solution was spread evenly on an 18 x 25 cm plate glass sheet. The solvent was allowed to dry in air then the remaining polymer/photoinitiator film was irradiated beneath a Philips UVA (75w) sunlamp for 2 hours. The resultant cross-linked polymer was scraped (scalpel) from the plate and suspended in dry dichloromethane (20 ml) and the suspension was stirred for approximately 15 minutes. The polymer was recovered by filtration and the retained solid washed with dry dichloromethane (2 x 10 cm3) and then dried thoroughly to leave 0. 85 of clear film polymeric material.

Yield 0. 85g, 85% Ir vmax (thin film) : 2920,2860, 1725,1520, 1450,1365, 1240,1170, 1090, 985cm~1

Example 16 Step 1 Diallylamine (12. 70g, 0. 134 mol), 1, 12-dibromododecane (20. Og, 0. 061 mol) and potassium carbonate (18. 50g, 0. 134 mol) in ethanol (lOOcm3) were refluxed together for 18 hours. The solids were removed by filtration and the solvent removed in vacuo to leave a yellow oil. The oil was passed through a silica gel column using ethyl acetate as the eluent. Removal of solvent in vacuo gave a pale yellow oil which was thoroughly dried. Yield 17. 4g, 79%.

¹HNMR (CDCl3) #: 1.20(m, 16H), 1. 45 (t, 4H), 2. 40 (t, 4H), 3. 10 (d, 8H), 5. 05-5. 15 (m, 8H), 5. 80 (m, 4H) Ir vmax (thin film) : 3080,3020, 2920,2860, 2800,1645, 1470,1420, 1355,1260, 1155,1115, 1090,1000, 920,725 cm~

Step 2 The diamine from step 1 (10. 00g, 0. 028 mol) and methyl iodide (8. 52g, 0. 060 mol) in a mixture of tetrahydrofuran (lOOcm3) and dichloromethane (20cm3) were stirred together. After 0. 5 hours the solution began to become turbid and the turbidity increased as time progressed. The solvent was removed in vacuo and the white solid residue was suspended in 40/60 petrol (100 cm³) and stirred for 1 hour. Filtration and thorough drying in vacuo gave 17. 40g, 97% of white, soft solid.

HNMR (CD2C12) 6: 1.15-1.40(m, 16H), 1. 80 (s, br, 4H), 3. 20 (s, 6H), 3. 30-3. 45 (m, 4H), 4. 15 (d, 8H), 5. 65-5. 90 (m, 8H), 5. 95- 6. 15 (m, 4H) Ir vmax (thin film) : 2920,2860, 1690,1640, 1470,1370, 1300,1250, 1000,945 cm~1 This material could be polymerised as described in previous examples.

Example 17 Step 1 Diallylamine (8. 80g, 0. 0090 mol), 3, 6-dioxaoctandioic acid (8.00g, 0.0448 mol) were mixed together as shown in Example 15 Step 1. The mixture was stirred in dichloromethane for 24 hours. The crude product was recovered and purified via silica gel/ethyl acetate to leave a clear oil. Yield 13. 43g, 89%.

HNMR (CDCl3) #: 3.70(s, 4H), 3. 80 (d, 4H), 3. 95 (d, 4H), 4. 20 (s, 4H), 5. 20 (m, 8H), 5. 60 (m, 4H) Ir vmax (thin film) : 3080,2940, 2860,1650, 1530,1470, 1420,1350, 1280,1235, 1120,995, 930,860, 815 cm-1

Step 2 Irgacure 184 (5mg) as placed in Monomer from Step 1 (0. 2g) and heated to form a clear solution. It was then stirred to ensure complete mixing of photoinitiator then placed on a 1. 5yin2 piece of copper (ex DRA) and spread evenly using 100 Lm K bar. It was then irradiated for 1 hour beneath a Philips UVA sunlamp and allowed to stand for 24 hours.

Ir vmax (thin film) : 2940,2860, 1640 (strong), 1460,1345, 1125,730 cml

Example 18 Step 1 Meso-butan-1,2,3,4-tetracarboxylic acid (20. Og, 0. 0428 mol), diallylamine (39. Og, 0. 20 mol), 1, 3- dicyclohexylcarbodiimide (82. 50g, 0. 20 mol) and 4- dimethylaminopyridine (2. Omg were dissolved in dichloromethane/tetrahydrofuran (1 : 1) mixture (200 cm3) and the mixture was stirred at room temperature for 120 hours.

1, 3-dicyclohexylurea was removed by filtration and the solvent removed in vacuo to leave a yellow oil. Column chromatography (silica gel/ethyl acetate) followed by removal of solvent in vacuo gave a heavy pale yellow oil which solidified on standing. 42.3g, 89%.

¹HNMR (CDCl3) #: 2.90(m, 4H), 3. 50 (m, 2H), 3. 80 (m, 16H), 5. 20 (m, 16H), 5. 70 (m, 8H) Ir vmax (thin film) : 3323,3086, 2935,2861, 1650,1545, 1416,1363, 1228,1135, 994,925, 556 cm~1

Step 2 Monomer from Step 1 (l. Og) was dissolved in dry dichloromethane (3cm3). The Irgacure 184 (lOmg) was added to the solution, heated and mixed to ensure homogenicity. It was then spread evenly on an 18 x 25 cm glass plate and the solvent allowed to evaporate off to leave a thin, clear film.

This was irradiated with a Philips UVA sunlamp for 30 minutes to form a hard cross-linked polymer film. This was removed (scalpel), washed in dichloromethane and dried. Yield 0. 64g, 64%.

Ir vmax (thin film) : 3424,2936, 2374,2346, 1705, 1644 (s), 1524, 1436 (s), 1222,1138, 992,924, 561 cm~1

Example 19 Step 1 Polyethylene glycol 600 diacid (6. 0g, 0. 010 mol), 1, 4- pentadiene-3-ol (2. 0g, 0. 024 mol), 1, 3- Dicyclohexylcarbodiimide (206. 33) (4. 95g, 0. 024 mol) and 4- dimethylaminopyridine (300mg) were stirred together in dry dichloromethane (50ml) for 72h. The resultant 1, 3- Dicyclohexyl-urea was removed by filtration and removal of solvent left a clear oil. Column chromatography using silica gel and dichloromethane - 40/60 petrol (1 : 1) followed by dichloromethane-methanol (1 : 3) gave, after removal of solvent, a colourless, clear oil. 6. 73g, 85%.

HNMR (CDCl3) 6: 3.55-3.80 (m, 48H), 4. 15 (s, 4H), 5. 25-5. 50 (m, 10H), 5. 75-5. 95 (m, 4H) Ir vmax (thin film) : 2860,1745, 1635,1450, 1345,1250, 1195,1140, 1115,990, 940,750 cml

Step 2 Monomer from Step 1 (1. 6og, 0. 0021 mol) and Irgacure 184 (21mg, 0. 000105 mol) were dissolved in dry dichloromethane (3cm3) and the solution was spread over a 18 x 25cm glass plate. The solvent was allowed to evaporate to leave a thin, clear film. The. film was then irradiated with a Philips UVA sunlamp (75w) to form a hard cross-linked polymer coating.

The coating was removed and washed in dry dichloromethane and dried thoroughly.

Yield 1. 10 g, 67% Ir vmax (KC1 disc) : 2920,2860, 1745,1680, 1640,1450, 1345, 1280, 1250, 1200, 1140, 1110, 950, 850 Cmi.

Example 20 copolymer The Monomer of Example 12 Step 1(0.5g) and the monomer of Example 11 Step 1, were dissolved with the Irgacure 184 (20mg) in dichloromethane (5 cm3) and the solution was spread evenly on an 18 x 25cm glass plate. The solvent was evaporated off and the residual film irradiated with the Philips UVA (75w) sunlamp for 1 hour. The resultant cross- linked copolymeric film was removed in strips (scalpel) and washed in dichloromethane, then thoroughly dried. The resultant film was soft, stretchy but of low tensile strength.

Ir vmax (thin film) : 3431,2931, 2858, 1649 (s), 1453,720 cm Example 21 copolymer

The monomer of Example 11 Step 2 (0. 5g) and monomer B above (0. 5g) (prepared by analgous methods to those described above) were dissolved in dry dichloromethane (5 cm3). The Irgacure 184 (20mg) was added and the mixture warmed (water bath) until the photoinitiator had dissolved. The solution was spread evenly on an 18 x 25 cm glass plate and the solvent allowed to evaporate. The two monomers phase separated to give an even pimpled'effect. Attempts to mix the two monomers using dichloromethane and mechanical mixing resulted, after evaporation of solvent, in the same pimpled effect. The monomers were irradiated with the Philips UVA (75w) sunlamp for 1 hour to form a phase-separated cross- linked solid polymeric pimpled'film but unstable due to the discontinuity of polymerisation at each phase boundary.

Ir vmax (thin film) : 3421 (s), 2939 (s9), 1642 (s), 1456,1167, 577 cm Example 22 copolymer The monomer of Example 11 step 1 (0. 5g) and the monomer of Example 3 Step 2 (0. 5g), were dissolved with the Irgacure 184 (20mg) in dichloromethane (5 cm3) and the solution was evenly spread on an 18 x 25 cm glass plate. The solvent was evaporated off to leave a residual clear film which was irradiated with the Philips UVA (75w) sunlamp for 1 hour.

The resultant cross-linked copolymer was removed in strips

(scalpel) and washed in dichloromethane (50 cm³) then thoroughly dried.

Ir vmax (thin film) : 3448 (s), 2931,2855, 1629 (s), 1534, 1452, 1230, 731 cl-1.

Example 23 Other polymerisable monomers were produced as follows : Example 23a The monomer illustrated (5.0g) above was treated with a 50% aqueous solution of fluoroboric acid to pH 1. 0 (universal indicator paper). The organic phase was extracted using dichloromethane (2 x 75 cm³) and then dried over MgSO4.

Removal of solvent in vacuo gave a heavy pale yellow oil.

7. 40g, 97%.

¹HNMR (CDCl3) #: 1.20(s, br, 12H), 1. 65 (s, br, 4H), 3. 05 (quin, 4H), 3. 75 (t, 8H), 5. 55 (m, 8H), 5. 90 (m, 4H), 7. 15 (s, br, 2H) Ir vmax (thin film) : 3410 (br), 2930,2857, 2649,1707, 1646, 1460,1428, 1056. 8 (very strong), 952,763 cm-1

Example 23b Using the procedure described in Example 23a, sebacic acid (10. 06g, 0. 050 mol), 1,5-Hexadiene-3-ol (9.80g, 0.1 mol), 1, 3-dicyclohexylcarbodiimide (22. 70g, 0. 11 mol) and 4- dimethylaminopyridine (450 mg) were mixed together to give the desired product Yield : 15. 6g, 87% ¹HNMR (CDCl3) #: 1.30(s, 10H), 1.60(t, 8H), 2. 35 (s, 2H), 5. 05- 5. 45 (m, 10H), 5. 65-5. 90 (m, 4H).

Ir vmax (thin film) : 2920,2860, 1730,1640, 1510,1460, 1410,1365, 1235,1160, 1095 cm-1 Example 24 Diallylamine (lO.Og, 0.103 mol), allyl bromide (25. 41g, 0. 21 mol) and potassium carbonate (20 g) were refluxed in ethanol.

Solids were removed by filtration and the solvents were removed in vacuo to leave a yellow oil.

This compound could be used as a u. v curable adhesive.

Example 25 1-Bromooctane (15.0g, 0.078 mol), diallylamine (8. 26g, 0. 085 mol) and potassium carbonate (11. 75g, 0. 085 mol) were refluxed in ethanol (lOOcm3) for 18 hours. Solids were removed by filtration and the solvents were removed in vacuo to leave a yellow oil. Column chromatography (silica gel/dichloromethane) followed by removal of solvent in vacuo and thorough drying gave 12. 9g, 79% of light yellow oil.

¹HNMR (CDCl3) #: 0.85(t, 3H), 1. 80 (s, br, 10H), 1. 45 (s, br, 2H), 2. 40 (5, 2H), 3. 15 (d, 4H), 5. 10 (m, 4H), 5. 85 (m, 2H).

Ir vmax (thin film) : 3082,2932, 2860,2806, 2355 (w), 1751 (w), 1709 (w), 1644 (m), 1463,1419, 1379,1262, 1083,996, 919,613 cm~ Example 26

Benzoic acid (20. Og, 0. 164 mol) was placed in thionyl chloride (23. 80g, 0. 20 mol) and the mixture heated to approximately 80 °C with stirring for 3 hours. Excess thionyl chloride was removed in vacuo and the residue cooled to approximately - 5°C in a salt/ice bath. Diallylamine (19. 50g, 0. 20 mol) in dry dichloromethane (20 cm3) was added dropwise with much evolution of HC1 gas. After complete addition, the resultant brown solution was allowed to rise to room temperature and left stirring for one hour. It was then washed with 3N HC1 (150 cm3), saturated K2C03 solution (150 cm3) and brine (150 cm3), then finally dried over MgS04.

Removal of solvent gave a brown oil which was passed through a silica gel column using ethyl acetate as the eluent.

Removal of solvent in vacuo gave a yellow oil. 27. 10g, 82%.

HNMR (CDCl3) 6: 3.90(s, br, 2H), 4. 10 (s, br, 2H), 5. 20 (m, 4H), 5. 70 (s, br, 1H), 5. 85 (s, br, 1H), 7. 40 (m, 5H) Ir vmax (thin film) : 3087,1640, 1498,1456, 1413,1262, 1120,991, 928,788, 703 cm Example 27 Heptanoyl chloride (25. Og, 0. 168 mol) was placed in dry dichloromethane (100 cm3) and the solution cooled to -5 °C in a salt-ice bath. Diallylamine (17. 5g, 0. 18 mol) in dry dichloromethane (25 cm3) was added dropwise with much evolution of HCl gas. The resultant solution was allowed to

rise to room temperature then poured into 3N HC1 (300 cm³) and stirred vigorously for ten minutes. The organic layer was removed by separation and to the aqueous layer was added ammonium chloride. This was then re-extracted with dichloromethane (2 x 100 cm3) and the three organic extracts combined and dried over MgS04. Removal of solvent in vacuo left a brown oil (one spot on tlc - silica gel/ethyl acetate) which was passed through a silica gel column using ethyl acetate as the eluent. Removal of solvent in vacuo gave a yellow oil. 32.0g, 91%.

HNMR (CDCl3) 6: O.90(t, 3H), 1. 35 (m, 6H), 1. 65 (quin, 2H), 2. 35 (t, 2H), 3. 90 (m, 2H), 4. 0 (m, 2H), 5. 15 (m, 4H), 5. 75 (m, 2H).

Ir vmax (thin film) : 2933,2861, 2338,1722, 1655,1563, 1466,1415, 1227,1114, 995,923 cm-1 Example 28 Oxalyl Chloride (25. Og, 0, 197 mol) was placed in dry dichloromethane (150 cm³) and cooled to -5 °C and stirred.

The diallylamine (48. 6g, 0. 50 mol) in dry dichloromethane (50 cm³) was slowly added dropwise (much HC1 evolved !) keeping temperature below 20 °C. After addition the solution was stirred at room temperature for thirty minutes and then

washed with 3N HC1 (100 cm3), saturated K2CO3 (100 CM3), brine (100 cm3), and finally dried over MgSO4. Removal of solvent left a brown oil (one spot by tlc, silica gel/EtOAc). The oil was passed through a silica gel column using ethyl acetate as the eluent. Removal of solvent left a yellow oil.

42. 50g, 87%.

¹HNMR (CDCl3) #: 3.85(m, 4H), 4. 0 (m, 4H), 5. 15 (m, 8H), 5. 80 (m, 4H) Ir vmax (thin film) : 3088,2991, 1654,1488, 1413,1285, 1215,1128, 996,930, 783,720 cm-1 Example 29 Acryloyl chloride (25. Og, 0. 28 mol) was placed in dry dichloromethane (150 cm3) and cooled to -5 °C in a salt/ice bath and stirred. The diallylamine (29. 15g, 0. 30 mol) in dry dichloromethane (50 cm3) was added dropwise over ~lh* and the resultant solution allowed to rise to room temperature and stirred for 30 minutes. The solution was treated with 3N HC1 (100 cm3) saturated K2CO3 solution (100 cm³) and brine (100 cm³) then dried over MgSO4. Removal of solvent gave a brown oil. The oil was passed through a silica gel column using ethyl acetate as eluent. Removal of solvent gave a yellow oil 37. Ig 89%.

* evolution of HC1 Ir vmax (thin film) : 2988, (1726), 1657,1618, 1470,1443, 1226,1196, 1077,989, 926,795 cml HNMR (CDCl3) 6: 3.95 (d, 2H), 4. 05 (d, 2H), 5. 15 (m, 4H), 5. 65 (m, 1H), 5. 75 (m, 2H), 6. 90 (m, 2H) Example 30 Malonic acid (16. 23g, 0. 156 mol), diallylamine (31.1g, 0.320 mol) and 1, 3-dicyclohexylcarbodiimide (66. Og, 0. 320 mol) were placed in dry dichloromethane and the mixture stirred for 18 hours at room temperature. The copious quantity of 1, 3- dicyclohexyl-urea was removed by filtration (Whatman No. 1 filter paper) and the organic filtrate washed with 3N HC1 (150 cm3), then saturated potassium carbonate followed by water (150 cm3). The solution was dried over MgSO4 and removal of solvent gave a brown oil. The oil was passed through a silica gel column using ethyl acetate as eluent.

Further decoloration was achieved using charcoal and dichloromethane/40/60 petrol (1 : 1) as solvent. Filtration and removal of solvent in vacuo gave a yellow/brown oil.

33. 70g, 87%.

¹HNMR (CDCl3) #: 3.55(s, 2H), 4. 04 (d, 8H), 5. 15 (m, 8H), 5. 80 (m, 4H).

Ir vmax (thin film) : 2987,2934, 1652,1414, 1310,1223, 1193,1136, 996,922, 852,700, 556 cm~1.

Example 31 Succinic anhydride (50. Og, 0. 5 mol) was placed in a dry dichloromethane (400 cm3) and stirred and cooled to -5 °C in a salt/ice bath. Diallylamine (48. 6g, 0. 5 mol) in dry dichloromethane (100 cm³) was added dropwise over 1 hour keeping the temperature at >20 °C. As addition proceeded, the succinic anhydride, suspended in dichloromethane became less evident until all had reacted to form a pale yellow solution. The solution was washed in 3N HC1 solution (200 cm3), saturated K2CO2 (200 cm³) then water (200 cm³) and finally dried over MgSO4. Removal of solvent left a light yellow oil (of one spot purity on t. l. c.). 95. 46g, 96%.

HNMR (CDCl3) 6: 2.65(m, 4H), 3. 95 (d, 2H), 4. 05 (d, 2H), 5. 15 (m, 4H), 5. 75 (m, 2H) Ir vmax (thin film) : 3088 (br), 1737,1650, 1480,1418, 1233, 1176,995, 928,829, 558 cm~1

Example 32 Diallylamine (17. 0g, 0. 185 mol) and 1, 3- dicyclohexylcarbodiimide (36. 12g, 0. 175 mol) were dissolved in dry dichloromethane (150 cm3) and the solution cooled to 0 °C. Trifluoroacetic acid (20. Og, 0. 175 mol) in dry dichloromethane (50 cm³) was added dropwise over 1 hour and the whole was left stirring at room temperature for 72 hours.

The 1, 3-dicyclohexylurea was removed by filtration and the solvent removed in vacuo to leave a yellow oil. Column chromatography (silica gel - dichloromethane) followed by removal of solvent in vacuo gave a pale yellow oil which crystallised slowly on standing. 26. 67g, 79. 0%.

HNMR (CDCl3) 6: 4.0(d, 4H), 5. 20 (m, 4H), 5. 75 (m, 2H) Ir vmax (thin film) : 2935,2866, 1698,1559, 1454,1348, 1305,1160, 1050,994, 926,895 cm~1

Example 33 Cyanoacetic acid (25. Og, 0. 294 mol) in dry dichloromethane (lOOcm3) was added dropwise to a solution of diallylamine (29. Og, 0. 30 mol) and 1, 3-dicyclohexylcarbodiimide (64. Og, 0. 31 mol) in dry dichloromethane (250cm3). The mixture was left stirring for 15 hours at room temperature. The 1, 3- dicyclohexylurea was removed by filtration and the solvent removed to leave a brown oil. Column chromatography (silica gel - dichloromethane) followed by removal of solvent in vacuo left a light yellow oil. 40. 50g, 84%. <BR> <BR> <BR> <BR> <BR> <BR> <BR> <P>HNMR (CDCl3) b: 3.75(s, 2H), 4.0(d, 2H), 4.10(d, 2H), 5.40(m, 4H), 5. 90 (m, 2H).

Ir vmax (thin film) : 3091,2931, 2261,1674, 1448,1316, 1229,1192, 1139,996, 931, 820cm-1.

Example 34 Acryloyl Chloride (16. 5g, 0. 180 mol) was dissolved in dry dichloromethane (50 cm3) and the solution was cooled to -5 °C in a salt/ice bath and stirred. The allylamine (5. 0g, 0. 087 mol) in dry dichloromethane (25 cm3) was added dropwise over

30 minutes and the resultant solution was allowed to rise to room temperature and stirred for a further 30 minutes. The solution was treated with 3M HC1 (50 cm3), saturated K2CO3 solution (50 cm3) and brine (50 cm3) then dried over MgSO4.

Removal of solvent gave a yellow oil. The oil was passed through a silica gel column using ethyl acetate as the eluent. Removal of solvent gave a yellow oil. 8.90g, 92%.

¹HNMR (CDCl3) #: 3.95(t, 2h), 5. 15 (m, 2h), 5. 60 (m, Ih), 5.85(m, lh), 6.20(m, 2h), 6. 70 (s, br, 1H) Ir vmax (thin film) : 3289,3084, 1664,1628, 1549,1412, 1246,1070, 989, 922,808 cm Example 35 Methane sulphonyl chloride (lO.Og, 0.087 mol), diallyamine (8. 75g, 0. 090 mol) and potassium carbonate (lOg) were placed in sieve-dried butanone (lOOcm3) and the mixture was refluxed with stirring for 3 hours. Thin layer chromatography (ethyl acetate) showed a product spot at -Rf 0. 5 with no evidence of diallyamine remaining. The reaction mixture was filtered (Whatman No. 1 filter paper) and the solvent was removed in vacuo to leave a brown oil. The oil was purified using column chromatography using silica gel and ethyl acetate- petrol 40/60 (1 : 1) as eluent. Removal of solvent in vacuo gave the product as a yellow oil (12. 30g, 80%) Ir vmax (thin film) : 3089,2990, 1331 (s), 1150,1046, 996, 934,793, 733cm~1~

HNMR (CDCl3) 6: 2.90(s,3H), 3.85(d, 4H)m 5.2(m,4H), <BR> 5. 80 (m, 2H).

The compounds of each of Examples 24 -35 above had the properties of a u. v. curable adhesive.

Example 36 Amide A (5. 0g, 0. 023 mol), diethanolamine (2. 40g, 0. 023 mol) and potassium carbonate (3. 45g (0. 025 mol) in ethanol (50 cm3) were stirred together at reflux for 15h. The solids were removed by filtration (Whatman No. 1) and the solvent removed in vacuo to leave a brown oil. Column chromatography (silica gel/ethyl acetate) followed by removal of solvent in vacuo and thorough drying left 4. 8g, 87% as a yellow oil.

Ir vmax (thin film) : 3650-3100,2937, 1646 (S), 1419,1354, 1229,1131, 995,927, 754 cirai 1.

¹HNMR (CDCl3) #: 2.80(t, 2H), 3. 40 (t, 2H), 3. 50 (s, 2H), 3. 90 (d, 2H), 4. 0 (d, 2H), 5. 15 (m, 4H), 5. 85 (m, 2H).

Example 37 Diethanolamine (lO.Og, 0.095 mol), allyl bromide (24. 2g, 0. 20 mol) and potassium carbonate (34. 5g, 0. 25 mol) were placed in ethanol (150 cm³) and the mixture was warmed to 65-70 °C with stirring and kept at this temperature for 15h. Solids were removed by filtration and the solvent removed in vacuo to leave a yellow oil, 21. 7g, 86%.

Ir vmax (thin film) : 3600-3100 (s), 2980,1647, 1457,1366, 1090,955, 754 cm~1.

¹HNMR (CDCl3) #: 3.62(s, 2H), 3. 78 (d, 2H), 3. 98 (s, 2H), 4. 10 (m, 4H), 4. 24 (m, 4H), 5. 24 (m, 4H), 6. 10 (m, 2H).

Example 38 0 Dichloromethane O + H- 0 0 t\ 1°l U Glutaric anhydride (30. Og, 0. 26 mol) was placed in dry dichloromethane (150 cm3) and the mixture cooled (salt/ice

bath) and stirred. Diallylamine (27. 20g, 0. 28 mol) in dry dichloromethane (50 cm3) was added dropwise to form a clear yellow solution which was stirred for a further 30 min. It was then washed with 3N HCl (200 cm3) then brine (200 cm3) and dried over MgS04. Removal of solvent left a yellow oil, 53.7g, 98%.

Ir vmax (thin film) : 2500-3600,1715, 1605,1640, 1480,1410, 1215,995, 920 cm~1.

HNMR (CDCl3) 6: 1.95 (quin, 2H), 2. 45 (m, 4H), 3. 90 (d, 2H), 3. 98 (d, 2H), 5. 15 (m, 4H), 5. 75 (m, 2H), 11. 10 (s, 1H).

Example 39 Bromoacetyl bromide (30. Og, 0. 15 mol) was dissolved in dry dichloromethane (200 cm³) and the solution stirred at room temperature. Diallylamine (14. 50g, 0. 15 mol) in dry dichloromethane (50 cm³) was added dropwise with much evolution of HCl gas, after complete addition the solvent was removed in vacuo to give a brown oil. Column chromatography (silica gel/ethyl acetate) followed by removal of solvent gave a yellow oil, 31. 4g, 97%.

Ir vmax (thin film) : 3513,3087, 2989,2927, 1657,1449, 1343,1257, 1212,1108, 994,922, 728,689, 618, 555 cm-1.

¹HNMR (CDCl3) #: 3.85(s, 2H), 3. 95 (m, 4H), 5. 20 (m, 4H), 5. 80 (m, 2H).

Example 40 Hexafluoroglutaric anhydride (5. 0g, 0. 0225 mol) was dissolved in dry dichloromethane (100 cm³) and the solution was cooled to - -5 °C in a salt/ice bath. Diallylamine (2. 20g, 0. 022 mol) in dry dichloromethane (20 cm³) was added dropwise over 15 minutes and the mixture stirred for 30 minutes at room temperature. Aqueous HC1 (6N) (100 cm3) was added and the mixture stirred for 10 minutes. The organic layer was separated and dried over MgS04. Removal of solvent gave a brown oil, 5.50g, 77%.

Ir vmax (thin film) : 3095,3650-2500, 1786, 1678 (s), 1422, 1244,1164, 1052,993 cm-1.

¹HNMR (CDCl3) #: 3.67(~1H, 4.0(d, 2H), 4. 05 (d, 2H), 5. 25 (m, 4H), 5. 76 (m, 2H), 12. 0 (s, 1H), 5.43(s ~ 1/2H), 5.46(d, ~ 1/2H)

Example 41 Amide A (5. 0g, 0. 0254 mol) and triethanolamine (3. 78, 0. 0254 mol) were dissolved in dry dichloromethane (100 cm³) and stirred at room temperature for 1hr. The solvent was removed in vacuo to leave a pale yellow oil (8. 78g, 100%) which was not purified since both of the starting materials were 98- 100% pure.

¹HNMR (CDCl3) #: 2.55(m, 2H), 2. 60 (m, 2H), 2. 98 (t, 6H), 3. 75 (t, 6H), 3. 95 (m, 4H), 5. 15 (m, 1H), 5. 76 (m, 2H), 6. 32 (s, br, 4H).

Ir vmax (thin film) : 3363 (s), 3156,2936, 1639 (s), 1579 (s), 1409,1249, 1080,1032, 1003,918, 563 cl-1.

Example 42 Amide A (5. 0g, 0. 0254 mol) and tris (hydroxymethyl) aminoethane (3. 08g, 0. 0254 mol) were placed together in dry dichloromethane (100 cm3) and the combination stirred for lh at room temperature. The solvent was removed in vacuo to leave a pale yellow oil which was not further purified since both starting materials were 98-100% pure. Yield 8. 08g, 100%.

¹HNMR (CDCl3) #: 2.40(s, br, 2H), 2. 60 (s, br, 2H), 3. 75 (s, br, 8H), 3. 95 (s, br, 2H), 5. 15 (m, 4H), 5. 70 (m, 2H), 6. 85 (s, br, 6H, -OH1 + NH) Ir vmax (thin film) : 3392,1561, 1463,1407, 1221,1190, 1063,933, 565 cm~1.

Example 43 Glutaric anhydride (3. 68g, 0. 032 mol) was placed in dry dichloromethane (100 cm3) but did not dissolve.

Dipropargylamine (3. 00g, 0. 032 mol) in dry dichloromethane (25 m3) was added slowly dropwise with a rise in temperature due to an exothermic reaction. As addition of the dipropargylamine proceeded, the glutaric anhydride became less evident until a clear yellow reaction mixture was formed. This was left stirring for a further Ih. The solution was washed in (i) dil (lN) (50ml) HC1 solution, (ii) NaHCO3 solution (lN) (50 ml), water (50ml), then dried over MgS04 to leave an orange coloured oil, 6. 38g, 96%.

Ir vmax (thin film) : 3300,2940, 2863,2130, 1730 (s), 1660 (s), 1420,1345, 1211,1040, 956 cm~1.

Example 44 Acid A (5. 0g, 0. 027 mol) and lithium hydroxide (648mg, 0. 027 mol) were dissolved in ethanol-water mixture (20 cm3).

Solvents were removed in vacuo to leave a white solid which was suspended in acetone. Filtration (No. 1 sinter) followed by washing of the retained solid with acetone (50 cm3) and thorough drying gave the lithium salt B 4. 90g, 96%, as a white powder insoluble in most organic solvents.

Ir vmax (KBr Disc) : 3085,3020, 2980,2922, 1643 (s), 1581 (s), 1422,1347, 1279,1256, 1213,1140, 1013,912, 833,808, 721, 622,575 cari'.

Example 45 Spermidine (5. 0g, 0. 035 mol), allyl bromide (34. Og, 0. 28 mol), potassium carbonate (35. Og) and ethanol (100 cm3)

were refluxed for 6h at 60 °C. The solvent and excess allyl bromide were removed in vacuo to leave a brown oil, 21. Og, 84%.

HNMR (CD30D) 6: 1.95(m, 4H), 2. 55 (quin, 2H), 3. 45 (m, 8H), 4. 0 (d, 8H), 4. 15 (d, 8H), 5. 75 (m, 16H), 6. 20 (m, 8H).

Ir vmax (thin film) : 2934,2458, 1644,1472, 1427,1368, 1246,995, 953, 848,749, 662 cm'\ Example 46 Amidoacid A (lO.Og, 0.047 mol), 3-fluorophenol (5. 27g, 0. 047 mol), dicyclohexylcarbodiimide (9. 70g, 0. 047 mol) and 4- dimethylaminopyridine (0. 50g) were stirred together in dry dichloromethane (150 cm³) for 18h at room temperature. The dicyclohexylurea was removed by filtration (Whatman No. 1 filter paper) and the filtrate washed with 2M KOH solution (100 cm3), then water (100 cm³) and dried over MgSO4. Removal of solvent left a yellow oil which was purified by column chromatography (silica gel) using dichloromethane as the eluent. Removal of solvent left a clear oil, 13.4g, 93.0%.

HNMR (CDCl3) 6: 2.09(t, 2H), 2. 47 (t, 2H), 2. 66 (t, 2H), 3. 88 (d, 2H), 3. 99 (d, 2H), 5. 20 (m, 4H), 5. 78 (m, 2H), 6. 90 (m, 3H), 7.40 (m, 1H).

Example 47 Itaconic anhydride (lO.Og, 0.09 mol) was placed in dry dichloromethane (150 cm3) and the mixture was cooled to -5 °C in a salt/ice bath. The diallylamine (9. 72g, 0. 10 mol) in dry dichloromethane (50 cm3) was added dropwise over 20 minutes, maintaining temperature > 0 °C during addition. The mixture was stirred (during which a clear yellow solution was formed) for 1 hour. The solvent was removed in vacuo to leave a brown oil, 16. 60g, 89%.

Ir vmax (thin film) : 2400-3400, 1717 (s), 1646 (s), 1620 (s), 1419,1220, 995,929, 842, 555 cm-1.

¹HNMR (CDCl3) #: 3.35(s, 2H), 3. 92 (d, 2H), 4. 10 (d, 2H), 5. 2 (m, 4H), 5. 70 (s, 1H), 5. 75 (m, 2H), 6. 35 (s, 1H), 12. 40 (s. v. br, 1H).

Example 48 4-Hydroxybenzoic acid (lO.Og, 0.072 mol) and diallylamine (8. 0g, 0. 082 mol) were dissolved in dichloromethane/tetrahydrofuran mixture (1 : 1) (100 cm3).

Dicyclohexylcarbodiimide (15. 48g, 0. 075 mol) was added slowly and the mixture was stirred for 72 h. The dicyclohexylurea was removed by filtration (Whatman No. 1 filter paper) and solvents removed to leave a brown oil. The oil was dissolved in dry dichloromethane (100 cm3) and the solution washed with 3M HCl solution (100 cm3) and dried over MgSO4. Removal of solvent left a white oily solid. Column chromatography (silica gel/EtOAc) followed by removal of solvent, gave after removal of solvent in vacuo a white powder, 14. 6g, 93%.

Ir vmax (KBr disc) : 3098 (br), 2932,2809, 1640 (w), 1573, 1447,1281, 1241,1174, 1112,988, 936,852, 748,679, 636, 611,575 cl 1.

Example 49 H3C t / (+ H o citraconic anhydride 0 4r-\ I I N-CCH= 7-COOH CH3 HOOC-C=C-C-N Y 1°l n CH3 Citraconic anhydride (20. Og, 0. 178 mol) was dissolved in dry dichloromethane (300 cm3). Diallylamine (19. 4g, 0. 20 mol) in dry dichloromethane (100 cm3) was added slowly dropwise over 45 minutes and stirring was continued for a further lh. The solvent was removed in vacuo to leave a brown oil, 34. 85g, 100%.

Ir vmax (thin film) : 3600-2400, 1695 (s), 1625 (s), 1415,1263, 1200,1091, 997,930, 798,762, 661 crn. <BR> <BR> <BR> <P>1HNMR (CDC13) 8 : 1. 90 (s), 3. 40 (d), 3. 73 (d), 3. 80 (d), 3. 85 (d), <BR> <BR> <BR> <BR> <BR> 3. 92 (d), 4. 95-5. 15 (m), 5. 18 (d), 5. 22 (d), 5. 29 (d), 5. 55- <BR> <BR> <BR> <BR> 5. 92 (complex).

Example 50 Phenylmaleic anhydride (5. 0g, 0. 029 mol) was dissolved in dry dichloromethane (100 cm³) and stirred. Diallylamine (3. 40g, 0. 035 mol) in dry dichloromethane (20 cm³) was added slowly dropwise over 10 minutes and stirring was continued for a further lh. The solvent was removed in vacuo and the residual brown oil thoroughly dried. 7. 30g, 94%. The oil solidified on standing.

Ir vmax (thin film) : 3600-2500, 1625 (s), 1700,1420, 1363, 1200,1091, 997,930, 798,762, 660 cm~1. <BR> <BR> <BR> <BR> <BR> <P>HNMR (CDCl3) 6: 3.60(d, 3.70(d), 4.10(d), 5.0(m), 5.20(m), <BR> <BR> <BR> <BR> 5. 45 (m), 5. 90 (m), 7. 40 (m), 7. 55 (m).

Example 51

Gamma butyrolactone (5. 00g, 0. 06 mol) and diallylamine (5. 83g, 0. 06 mol) were mixed together (no solvent) and heated (60 °C) for 24h. Thin layer chromatography (EtOAc) showed predominantly a new single product spot at - Rf 0. 25.

The reaction mixture was dissolved in dry dichloromethane (100 cm3) and washed with 3N HC1 (50 cm3), 3N K2CO3 solution (50 cm3) and then brine (50 cm3). Finally, the solution was dried over MgSO4. The solvent was removed in vacuo and the residual brown oil purified using column chromatography (silica gel, ethyl acetate) to give after removal of solvent in vacuo, and thorough drying 7. 4g, 70%, of clear oil.

1HNMR (CDCl3) 6: l.90(quin, 2H), 2. 50 (t, 2H), 3. 55 (s, 1H - OH), 3. 66 (t, 2H), 3. 90 (d, 2H), 4. 00 (d, 2H), 5. 15 (m, 4H), 5. 75 (m, 2H).

Ir vmax (thin film) : 3420 (br, s), 3088,2935, 1630 (s), 1417, 1359,1283, 1239,1138, 1063,995, 927 cm~1.

Example 52 6-Chlorohexan-1-ol (lO.Og, 0.073 mol), diallylamine (7. 30g, 0. 075 mol) and potassium carbonate (10. 37g, 0. 075 mol) were placed in ethanol (150 cm3) and refluxed for 48h. The solvent was removed in vacuo to leave a brown oil. The oil was dissolved in dichloromethane (150 cm³) and the solution was washed in brine (100 cm3), then dried over MgS04. The solvent was removed in vacuo and the residual brown oil

purified using column chromatography (silica gel - ethyl acetate). Removal of solvent in vacuo gave a yellow oil, 14.7g, 99%.

¹HNMR (CDCl3) #: 1.40(m, 2H), 1. 50 (quin, 2H), 1. 55 (quin, 2H), 2. 45 (t, 2H), 2. 65 (s, 1H), 3. 10 (d, complex, 4H), 3. 55 (t, 2H), 3. 65 (quartet, 2H), 5. 10 (m, 4H), 5. 80 (m, 2H).

Ir vmax (thin film) : 3369 (s), 2964,2934, 1517,1459, 1374, 1300,1243, 1106,1047, 1018,826, 770 cl-1.

Example 53 Amide A (lO.Og, 0.055 mol) was dissolved in dry dichloromethane (100 cm³) the mixture was cooled in an ice bath. Acryloyl chloride (4. 95g, 0. 055 mol) in dry dichloromethane (20 cm3) was added dropwise over 30 minutes and the mixture was allowed to rise to room temperature. It was left stirring for 4h. Thin layer chromatography (EtOAc) showed a new spot at ~Rf 0.6. The solvent was removed in vacuo and the product purified using column chromatography (EtOAc - 40/60 petrol 1 : 1). Removal of solvent in vacuo gave a yellow oil 11. 48g, 89%.

Ir vmax (thin film) : 2986, 1728 (s), 1645 (1), 1414,1276, 1196,1058, 992,929, 813,669 cl-1.

¹HNMR (CDCl3) #: 2.10(m, 2H), 2. 45 (m, 2H), 3. 90 (d, 2H), 4. 0 (d, 2H), 4. 2 (t, 2H), 5. 20 (m, 2H), 5. 75 (m, 4H), 5. 80 (m, 1H), 6. 15 (m, 1H), 6. 45 (d, 1H).

Example 54 11 + F- C) CI KsCOa/Butanone r Benzyl chloroformate (lO.Og, 0.059 mol), diallylamine (5. 85g, 0. 060 mol), potassium carbonate (lO.Og) in sieve dried butanone (100 cm³) were stirred together at - reflux temperature for 3h. Thin layer chromatography (ethyl aetate) showed a new spot at - Rf 0. 5 and no evidence of diallylamine. The reaction mixture was filtered (Whatman No.

1 filter paper) and solvent removed in vacuo to leave a brown oil. The oil was purified using column chromatography (silica gel with ethyl acetate as eluent). Removal of solvent in vacuo left a clear yellow oil, 10. 34g, 77%.

Ir vmax (thin film) : 2987, 1708 (s), 1460,1415, 1368,1294, 1243,1153, 1096,995, 926,769, 699 cm~1.

¹HNMR (CDCl3) #: 3.85(d, 4H), 5. 11 (m, 4H), 5. 14 (s, 2H), 5. 75 (m, 2H). 7. 30 (m, 5H).

Example 55 3-aminopropyltrimethoxysilane (lO. Og, 0. 056 mol), 4- diallylamidobutyric Acid (11. 8g, 0. 056 mol), dicyclohexylcarbodiimide (11. 55g, 0. 056 mol) and 4- dimethylaminopyridine (0. 5g) were stirred at room temperature in dry dichloromethane for 72h. The dicyclohexylurea was removed by filtration (Whatman No. 1 filter paper) and solvent removed to leave a yellow oil. The oil was passed through a short column of neutral aluminium followed by ethyl acetate (500 cm3). Removal of solvent left a clear colourless oil 16.8g, 80%.

Ir vmax (thin film) : 3314,2940, 2120, 1650 (s), 1547,1417, 1229,1086, 994,927, 808,754, 666 cm~1.

¹HNMR (CDCl3) #: 0.65(t, 2H), 1.95(quin, 2H), 2. 25 (t, 2H), 2. 40 (t, 2H), 3. 20 (quin, 2H), 3. 55 (s, 9H), 3. 90 (d, 2H), 4. 0 (d, 2H), 5. 10 (m, 4H), 5. 75 (m, 2H), 6. 5 (d, 2H).

Example 56 1,4-Pentadien-3-ol (5.0g, 0.060 mol) and acryloyl chloride (5. 43g, 0. 060 mol) were dissolved in dry acetone. Potassium carbonate (lOg) was added and the mixture was stirred at reflux for 15h. The solids were removed by filtration (Whatman No. 1 filter paper) and the solvent removed in vacuo to leave a yellow oil. Chromatography using flash silica gel with ethyl acetate as the eluent gave, after thorough drying in vacuo, etc. 6. 43g, 78% of pale yellow oil.

Ir vmax (thin film) : 2935, 1736 (s), 1653,1618, 1411,1186, 1090,989, 931,810 cml.

¹HNMR (CDCl3) #: 5.10-5.45(m, 5H), 5. 70-5. 95 (m, 3H), 6. 20 (m, 1H), 6. 45 (m, 1H).

Example 57 Triallylamine (20. Og) was dissolved in methanol and stirred at room temperature. 6N hexafluorophosphoric acid in methanol (from 65% solution in H20) was added to pH 2. 0 and the pink solution was left stirring for 15 minutes. The solvents (MeOH and H20) were removed in vacuo to leave a pink coloured oil. The oil was re-dissolved in dry dichloromethane and the solution was dried over MgSO4. It was then filtered (Whatman No. 1 filter paper +'Hyflo"). Removal of solvent in vacuo gave a clear, pink coloured oil, 35. 4g, 85%.

Ir vmax (thin film) : 2997,2543, 1459,1429, 1289,1244, 1143,1056, 997,953, 841 (s), 756,661 cm~1.

¹HNMR (CDCl3) #: 3.65(s, 6H), 5. 55 (m, 6H), 6. 0 (m, 3H), 10. 55 (s, br, 1H).