POLYMER, SEMICON DUCTOR COM POSITION COMPRISING POLYMER, AN D M ETHOD FOR MANUFACTURING FILM USING

SEMICON DUCTOR COM POSITION BACKGROUN D OF THE INVENTION

TECHNICAL FIELD

[0001] The present invention relates to a polymer

comprising certain structural units and a semiconductor composition comprising the polymer. Further, the present invention also relates to methods for

manufacturing a film and a device, using the

semiconductor composition. BACKGROUN D ART

[0002] In the process of manufacturing devices such as semiconductors, fine processing by lithog raphy

technology using a photoresist has been generally performed . The fine processing process comprises the processes of: forming a thin resist layer on a

semiconductor substrate such as a silicon wafer, covering the layer with a mask pattern corresponding to a desired device pattern, irrad iating the layer with an active light such as ultraviolet rad iation throug h the mask pattern, developing the exposed layer to obtain a photoresist pattern, and etching the substrate using the obtained photoresist pattern as a protective film, whereby a fine unevenness corresponding to the above-described pattern is formed .

[0003] In these photolithography processes, there causes a problem that d imensional accuracy of the photoresist pattern is lowered due to the influence of standing wave resulting from reflection of the light from the substrate and the influence of irregular reflection of the exposure lig ht resulting from the level difference of the substrate.

Therefore, in order to solve this problem, a method for provid ing a bottom anti-reflective coating has been widely stud ied . The characteristics required for such a bottom anti-reflective coating include having a large absorbance to the radiation used for exposure of the photoresist, preventing irregular reflection and the like to make the cross section of the photoresist after exposure and development perpend icular to the substrate surface, having poor solubility in a solvent contained in the photoresist composition (intermixing hardly occurs), and the like.

[0004] Patent Document 1 discloses an anti-reflective

coating composition comprising a crosslinker. Patent Document 2 d iscloses a composition for forming a fine resist pattern comprising a certain polymer, but it does not disclose whether or not a bottom anti-reflective coating can be formed and whether or not it has characteristics required as a bottom anti-reflective coating .

PRIOR ART DOCUMENTS

PATENT DOCUMENTS

[0005] [Patent Document 1] WO 2011/101737

[Patent Document 2] JP 2014-71424 A

[Patent Document 3] WO 2007/111147

SUMMARY OF THE INVENTION

PROBLEMS TO BE SOLVED BY THE INVENTION

[0006] The present inventors considered that there are one or more problems still need improvements. These include, for example, the followings: reduction of sublimates; appropriate etching resistance; coating properties; filling properties into complicated and fine substrates (for example, substrates having level difference) ; capability of film formation at low

temperature; large absorbance; suitable refractive index; reduction of standing wave; reduction of intermixing with other composition (for example, resist composition) and film; flatness of upper surface of the formed film; high solubility of solute; storage stability; good shape of the formed resist pattern, high yield, and low LWR.

The present invention has been made based on the technical background as described above and provides a novel polymer and a composition comprising the same.

MEANS FOR SOLVING THE PROBLEMS

[0007] The polymer (A) according to the present invention comprises at least one structural unit selected from the group consisting of the following Units (a), (b), (c) and (d):

Unit (a) represented by the formula (a):

(wherein,

R ^al and R ^a2 are each independently H, C1-5 alkyl, C1-5 alkoxy or -COOH,

L ^a is a single bond, C1-5 alkylene, -O- or C1-5 alkoxylene, ma is 0 to 1,

X ^al is H or a C ₁ -5 hydrocarbon group (one or more of -CH ₂ - in the C ₁ -5 hydrocarbon group can be each independently replaced with -NH-, -C( = 0)- and/or -O- and one or more of -CH ₃ in the C ₁ -5 hydrocarbon group can be each independently replaced with -NH ₂ and/or -COOH), Y ^a is N or 0, where when Y ^a is N, pa is an integer of 1 or 2, and when Y ^a is 0, pa is 1,

X ^a2 is H or a C1-5 hyd rocarbon group (one or more of -CH2- in the C1-5 hydrocarbon g roup can be each independently replaced with -NH-, -C( = 0)- and/or -0- and one or more of -CH3 in the C1-5 hydrocarbon g roup can be each independently replaced with -IMH2 and/or -COOH), and when pa is 2, two X ^a2 can be identical or different, where, X ^{a l} and X ^a2 can be bonded and/or two X ^a2 can be bonded when pa is 2, to form a saturated or unsaturated ring) ;

Unit (b) represented by the formula (b) :

(wherein,

R ^bl and R ^b2 are each independently H, C _1-5 alkyl, C _1-5 alkoxy, C _1-5 alkoxyalkyl or -COOH,

mb is 0 to 1,

L ^b is a single bond, C1-5 alkylene, C6-20 arylene, -0- or C1-5 alkoxylene,

Z ^b is a C6-20 aromatic hyd rocarbon or a C7-20 aromatic substituted aliphatic hydrocarbon,

pb is 0 to 4,

qb is 1 to 3,

R ^b3 is H, Ci- ₅ alkyl, C _1-5 alkoxy, C _1-5 alkoxyalkyl or -COOH, and when pb > 1, each R ^b3 can be identical or different, R ^b4 is H or methyl, and when q b > 1, each R ^b4 can be identical or d ifferent, where, Unit (b) has an aryl having at least one fused structure) ;

Unit (c) represented by the formula (c) :

(wherein,

R ^cl and R ^c2 are each independently H, C _1-5 alkyl, C _1-5 alkoxy or -COOH,

me is 0 to 1,

L ^c is a single bond, C1-5 alkylene, -O- or C1-5 alkoxylene, V ^c is a fused aromatic hyd rocarbon or a fused heterocyclic ring, and V ^c has 3 to 6 rings fused,

pc is 0 to 5,

R ^c3 is Ci- ₅ alkyl, C _1-5 alkoxy or -COOH, and when pc > 1, each R ^c3 can be identical or different) ; and

Unit (d) represented by the formula (d) :

(wherein,

R ^{d l} and R ^d2 are each independently H, C _1-5 alkyl, C _1-5 alkoxy or -COOH, md is 0 to 1,

L ^d is a single bond, C1-5 alkylene (one or more of -CH2- in the Ci-5 alkylene can be replaced with -NH-, -C( = 0)- and/or -0- and one or more of -CH3 in the C1-5 alkylene can be replaced with -OH, -IMH2 and/or -COOH), -0- or C1 -5 alkoxylene),

wherein, n _a , n _b , n _c and n _d , which are the numbers of repetition respectively of Units (a), (b), (c) and (d), satisfy the following formulae:

n _a + n _b > 0,

n _c ³ 0, and

n ³ 0.

[0008] The semiconductor composition according to the present invention comprises the above-mentioned polymer (A) and a solvent (B) .

[0009] The method for manufacturing a film accord ing to the present invention comprises the following processes:

(1) applying the semiconductor composition according to the present invention above a substrate; and

(2) heating said semiconductor composition to form a film.

[0010] The method for manufacturing a device according to the present invention comprises the method described above.

EFFECTS OF THE INVENTION

[0011] It is possible to reduce sublimates. It is possible to control the etching resistance. It is possible to obtain a composition having good coating properties. It is possible to satisfactorily filled the composition into complicated and fine substrates (for example, substrates having level d ifference) . It is possible to form a film at low temperature. It is possible to obtain a film having large absorbance. It is possible to obtain a film having suitable refractive index. It is possible to reduce stand ing wave. It is possible to reduce intermixing with other composition (for example, resist composition) and film. It is possible to improve flatness of upper surface of the formed film. It is possible to obtain a composition having high solubility of solute. It is possible to obtain a composition having high storage stability. It is possible to form a resist pattern having a good shape with high yield . It is possible to form a resist pattern having low LWR. DETAILED DESCRIPTION OF THE INVENTION

MODE FOR CARRYING OUT THE INVENTION

[0012] In the present specification, unless otherwise

specifically mentioned, the singular includes the plural and "one" or "that" means "at least one". In the present specification, unless otherwise specifically mentioned, an element of a concept can be expressed by a plurality of species, and when the amount (for example, % by mass or mol%) is described, it means sum of the plurality of species.

"And/or" includes a combination of all elements and also includes single use of the element.

In the present specification, when a numerical range is indicated using "to" or unless otherwise specifically mentioned, it includes both endpoints and units thereof are common. For example, 5 to 25 mol% means 5 mol% or more and 25 mol% or less.

In the present specification, the descriptions such as "Cx-y", "Cx-Cy" and "C _x " mean the number of carbons in a molecule or substituent. For example, Ci-6 alkyl means an alkyl chain having 1 or more and 6 or less carbons (methyl, ethyl, propyl, butyl, pentyl, hexyl etc.) .

In the present specification, when a polymer has plural types of repeating unit, these repeating units copolymerize. Unless otherwise specifically mentioned, these copolymerizations are any of alternating copolymerization, random copolymerization, block copolymerization, graft copolymerization, or a mixture thereof. When polymer or resin is represented by a structural formula, n, m or the like attached next to parentheses indicate the numbers of repetition.

In the present specification, unless otherwise specifically mentioned, Celsius is used as the temperature unit. For example, 20 degrees means 20 degrees

Celsius.

[0013] (A) Polymer

The polymer (A) according to the present invention comprises at least one of structural unit selected from the group consisting of Unit (a), Unit (b), Unit (c) and Unit (d) described below, wherein na, nb, nc and nd, which are the numbers of repetition respectively of Units (a), (b), (c) and (d), satisfy the following formulae:

n _a + n > 0,

n _c ³ 0, and

nd ³ 0;

and preferably n _a > 0.

[0014] Unit (a) is represented by the formula (a).

wherein,

R ^al and R ^a2 are each independently H, C1-5 alkyl, C1-5 alkoxy or -COOH,

L ^a is a single bond, C1-5 alkylene, -O- or C1-5 alkoxylene, ma is 0 to 1,

X ^{a l} is H or a C1-5 hyd rocarbon group (one or more of -CH2- in the C1-5 hydrocarbon g roup can be each independently replaced with -NH-, -C( = 0)- and/or -0- and one or more of -CH3 in the C1-5 hydrocarbon g roup can be each independently replaced with -IMH2 and/or -COOH),

Y ^a is N or 0, where when Y ^a is N, pa is an integer of 1 or 2, and when Y ^a is 0, pa is 1, and

X ^a2 is H or a C _1-5 hyd rocarbon group (one or more of -CH ₂ - in the C _1-5 hydrocarbon g roup can be each independently replaced with -NH-, -C( = 0)- and/or -0- and one or more of -CH ₃ in the C _1-5 hydrocarbon g roup can be each independently replaced with -IMH ₂ and/or -COOH), and when pa is 2, two X ^a2 can be identical or different, where, X ^{a l} and X ^a2 can be bonded and/or two X ^a2 can be bonded when pa is 2, to form a saturated or unsaturated ring .

[0015] Unit (a) to be introduced as a pendant is considered crosslinkable itself. Thereby, when a film is formed using the composition comprising the polymer (A), a crosslinked polymer can be formed even if it comprises no crosslinker.

[0016] R ^{a l} is preferably H, methyl, ethyl, t-butyl or methoxy, more preferably H or methyl, and further preferably H .

R ^a2 is preferably H, methyl, ethyl, t-butyl or methoxy, more preferably H or methyl, and further preferably methyl.

L ^a is preferably a single bond, methylene, ethylene, propylene, -0- or methoxylene, more preferably

methylene or ethylene, and further preferably methylene. ma is preferably 0 or 1, and more preferably 1. It is possible that the polymer (A) has plural types of Unit (a), but in such a case, a non-integer number such as ma = 0.5 can be taken. Hereinafter, the same applies to the numbers in the formula relating to polymer unless otherwise specified as integers.

Y ^a is preferably N, and pa is preferably 2. In other aspect, Y ^a is N and pa is 1. In this case, N and X ^a2 are bonded by a double bond (-N =X ^a2 ) .

The Ci-5 hydrocarbon group of X ^{a l} can be linear or branched . X ^{a l} is preferably H, methyl, ethyl or propyl, and more preferably H .

The Ci- ₅ hydrocarbon group of X ^a2 can be each independently linear or branched . Preferably, X ^a2 is each independently a C _1-5 hydrocarbon g roup (one or more of -CH ₂ - in the C _1-5 hydrocarbon group can be each independently replaced with -NH- and one or more of -CH ₃ in the C _1-5 hydrocarbon g roup can be each independently replaced with -IMH2) .

[0017] Preferably, the formula (a) is represented by the following formula (a-1) .

(a-1) wherein,

R ^{a l} , R ^a2 , L ^a , ma and X ^{a l} are as described above, and X ^a3 and X ^a4 are each independently H or a C1-5 hydrocarbon group (one or more of -CH2- in the C1-5 hyd rocarbon g roup can be each independently replaced with -NH-, -C( = 0)- and/or -O- and one or more of -CH3 in the C1-5

hydrocarbon g roup can be each independently replaced with -NH2 and/or -COOH),

where, X ^{a l} and X ^a3 or X ^a4 can be bonded and/or X ^a3 and X ^a4 can be bonded, to form a saturated or unsaturated ring . The Ci-5 hydrocarbon group of X ^a3 and X ^a4 can be each independently linear or branched . Preferably, X ^a3 and X ^a4 are each independently a C1-5 hydrocarbon g roup (one or more of -CH2- in the C1-5 hydrocarbon g roup can be each independently replaced with -NH- and one or more of -CH3 in the C1-5 hyd rocarbon group can be each independently replaced with -IMH2) .

[0018] Preferably, X ^{a l} and X ^a3 or X ^a4 form no ring . When

X ^a3 and X ^a4 form a ring, it is preferably a 5- to 7-membered ring, wherein one or two atoms constituting the ring are nitrogen atoms and the remaining atoms are carbon atoms.

When X ^a3 and X ^a4 form no ring, X ^a3 and X ^a4 are each independently H, methyl or ethyl, and more preferably H or methyl. In one preferred embod iment, any one of X ^a3 and X ^a4 is methyl.

[0019] Exemplified embodiments of the formula (a-1) are, for example, as shown below.

[0020] Further, the formula (a) can also be a case represented by the formula (a-2) .

wherein, R ^{a l} , R ^a2 , L ^a , ma and X ^{a l} are as described above, and X ^a5 is a Ci-5 hyd rocarbon group (one or more of -CH2- in the C1-5 hydrocarbon g roup can be each independently replaced with -NH-, -C( = 0)- and/or -0- and one or more of -CH3 in the Ci-5 hydrocarbon g roup can be each independently replaced with -IMH2 and/or -COOH),

where, X ^{a l} and X ^a5 can be bonded to form a saturated or unsaturated ring . Preferably, X ^{a l} and X ^a5 form no ring . The Ci-5 hydrocarbon group of X ^a5 can be linear or branched and is preferably branched . Preferably, X ^a5 is a

Ci-4 hydrocarbon g roup, where -CH2- in the C1-4

hydrocarbon group can be replaced with neither -NH-,

-C( = 0)- nor -0- and -CH ₃ in the C _1-4 hyd rocarbon group can be replaced with neither -NH ₂ nor -COOH .

[0021] Exemplified embodiments of the formula (a-2) are, for example, as shown below.

[0022] Further, the formula (a) can also be a case

represented by the formula (a-3) . wherein, R ^al , R ^a2 , L ^a , ma and X ^al are as described above, and X ^a6 is a C1-5 hydrocarbon group (one or more of -CH2- in the C1-5 hydrocarbon group can be each independently replaced with -NH-, -C( = 0)- and/or -O- and one or more of -CH3 in the C1-5 hydrocarbon group can be each independently replaced with -NH2 and/or -COOH), where, X ^al and X ^a6 can be bonded to form a saturated ring or an unsaturated ring.

[0023] X ^a6 is preferably methyl, ethyl, n-propyl, isopropyl and t-butyl, and more preferably methyl and n-propyl.

[0024] Exemplified embodiments of the formula (a-3) are, for example, as shown below.

[0025] Unit (b) is represented by the formula (b) wherein,

R ^bl and R ^b2 are each independently H, C1-5 alkyl, C1-5 alkoxy, C1-5 alkoxyalkyl or -COOH,

mb is 0 to 1,

L ^b is a single bond, C1-5 alkylene, C6-20 arylene, -0- or C1-5 alkoxylene,

Z ^b is a C6-20 aromatic hyd rocarbon or a C7-20 aromatic substituted aliphatic hydrocarbon,

pb is 0 to 4,

qb is 1 to 3,

R ^b3 is H, Ci-5 alkyl, C1-5 alkoxy, C1-5 alkoxyalkyl or -COOH, and when pb > 1, each R ^b3 can be identical or different, and

R ^b4 is H or methyl, and when q b > 1, each R ^b4 can be identical or d ifferent,

where, Unit (b) has an aryl having at least one fused structure. It can also be said that Unit (b) comprises at least one fused cyclic hydrocarbon. Such a fused cyclic hyd rocarbon is preferably naphthyl or anthracene.

[0026] R ^bl is preferably H, methyl, ethyl or t-butyl, and more preferably H .

R ^b2 is preferably H, methyl, ethyl or t-butyl, more preferably H or methyl, and further preferably methyl, mb is preferably 0 or 1, and more preferably 1.

L ^b is preferably a single bond, methylene, ethylene, propylene, naphthylene, anthracenylene, -0-, methoxylene or ethoxylene, more preferably a single bond, methylene or naphthylene, further preferably a single bond or naphthylene, and still more preferably a sing le bond .

R ^b3 is preferably H, methyl, ethyl, propyl, methoxy or methoxymethyl, more preferably H, methyl or

methoxymethyl, further preferably H or methoxymethyl, and still more preferably H . pb is preferably 0 to 3, more preferably 0 to 2, further preferably 0 or 1, and still more preferably 0. When pb = 0, it can also be said that R ^b3 is noumenally H . In order to secure clarity, when pb = 0, it can also be made R ^b3 ¹ H .

R ^b4 is preferably H . qb is preferably 1 to 2, more preferably 1 or 2, and further preferably 1.

[0027] By having Unit (b), the film formed from the polymer

(A) is considered to have a suitable refractive index (n) . For this reason, the polymer (A) having Unit (b) is useful for the resist underlayer forming composition and further useful for the bottom anti-reflective coating forming composition. In addition, it is also useful for top anti-reflective coating forming composition.

[0028] In addition, the following structure is an example of

Unit (b) . In the above formula (b), this is a case where:

R ^bl and R ^b2 are H, mb is 1,

L ^b and Z ^b have the following structures, respectively,

Pb is 4, q b is 2,

R ^b3 is all -CH2-O-CH3, and

R ^b4 is all H . [0029] Zb is preferably a benzene ring, a naphthalene ring, an anthracene ring, a diphenylmethyl, diphenylethyl or a phenylnaphthylmethyl, and more preferably a

naphthalene ring.

Unit (b) can also be represented by the following formula (b-1).

wherein,

R ^bl , R ^b2 , mb, L ^b , pb, qb, R ^b3 and R ^b4 are each

independently as described above.

[0030] Exemplified embodiments of the formula (b-1) are, for example, as shown below. [0031] As the formula (b-1), the followings are more preferable.

[0032] Unit (c) is represented by the formula (c) . wherein,

R ^cl and R ^c2 are each independently H, C1-5 alkyl, C1-5 alkoxy or -COOH,

me is 0 to 1,

L ^c is a sing le bond, C1 -5 alkylene, -0- or C1-5 alkoxylene,

V ^c is a fused aromatic hyd rocarbon or a fused heterocyclic ring, and V ^c has 3 to 6 rings fused,

pc is 0 to 5, and

R ^c3 is Ci-5 alkyl, C1-5 alkoxy or -COOH, and when pc > 1, each R ^c3 can be identical or different.

[0033] R ^cl is preferably H, methyl or ethyl, and more

preferably H .

R ^c2 is preferably H, methyl or ethyl, more preferably H or methyl, and further preferably methyl.

L ^c is preferably a single bond, methylene, ethylene, propylene, -0- or methoxylene, more preferably a single bond or methylene, and further preferably methylene me is preferably 0 or 1, and more preferably 1.

R ^c3 is preferably H, methyl or ethyl, more preferably H or methyl, and further preferably H .

pc is preferably 0, 1, 2, 3, 4 or 5, more preferably 0, 1 or 2, further preferably 0 or 1, and still more preferably 0. When pc = 0, it can also be said that R ^c3 is noumenally H . In order to secure clarity, when pc = 0, it can also be made R ^c3 ¹ H .

[0034] By having Unit (c), the film formed from the polymer

(A) is considered to have a suitable absorption parameter (k) and/or refractive index (n) . For example, it is considered that (k) value and/or (n) value can be increased . For this reason, the polymer (A) having Unit

(c) is useful for the resist underlayer forming composition and further useful for the bottom anti-reflective coating forming composition. In add ition, it is also useful for top anti-reflective coating forming composition.

[0035] Vc is preferably anthracene derivatives,

phenanthrene derivatives or xanthene derivatives, more preferably anthracene derivatives or phenanthrene derivatives, and further preferably anthracene derivatives.

[0036] Preferably, the formula (c) is represented by the following formula (c-1) or (c-2) .

wherein,

R ^cl , R ^c2 , R ^c3 , L ^c and me are each independently as described above.

One carbon in anthracene, which falls under Vc, can be replaced with oxygen, and an aspect in which it is not replaced is more preferable.

wherein,

R ^cl , R ^c2 , R ^c3 , L ^c and me are each independently as described above.

One carbon in phenanthrene can be replaced with oxygen, and an aspect in which it is not replaced is more preferable. R ^c3 is Ci-5 alkyl, C1-5 alkoxy or -COOH, and when pc" is 2, 3, 4 or 5, each R ^c3 can be identical or different. Two R ^c3 can form a saturated or unsaturated ring .

[0037] Exemplified embodiments of the formula (c-1) are, for example, as shown below.

[0038] Exemplified embodiments of the formula (c-2) are, for example, as shown below. [0039] Exemplified embodiments of formula (c) other than the above exemplified embodiments are, for example, as shown below.

[0040] Unit (d) is represented by the formula (d) .

wherein,

R ^{d l} and R ^d2 are each independently H, C1-5 alkyl, C1-5 alkoxy or -COOH,

md is 0 to 1, and

L ^d is a single bond, C1-5 alkylene (one or more of -CH2- in the Ci-5 alkylene can be replaced with -NH-, -C( = 0)- and/or -0- and one or more of -CH3 in the C1-5 alkylene can be replaced with -OH, -IMH ₂ and/or -COOH), -0- or C _1-5 alkoxylene.

[0041] R ^{d l} is preferably H, methyl, ethyl, t-butyl or methoxy, more preferably H or methyl, and further preferably H .

R ^d2 is preferably H, methyl, ethyl, t-butyl or methoxy, more preferably H or methyl, and further preferably methyl.

md is preferably 0 or 1, and more preferably 1.

L ^d is preferably C _1-5 alkylene (one or more of -CH ₂ in the Ci- ₅ alkylene can be replaced with -C( = 0)- and one or more of -CH ₃ in the C _1-5 alkylene can be replaced with -OH and/or -COOH), more preferably C _1-4 alkylene (one or more of -CH ₂ in the C _1-4 alkylene is -C( = 0) and one or more of -CH ₃ in the C _1-4 alkylene can be replaced with -OH and/or -COOH), and further preferably C _1-4 alkylene (one

-CH2- in the C _1-4 alkylene can be replaced with -C( = 0)- and one -CH ₃ in the C _1-4 alkylene can be replaced with -OH and/or -COOH) .

[0042] By having Unit (d), the film formed from the polymer

(A) is considered to have a suitable absorption parameter

(k), refractive index (n) and/or a fast etching rate.

Further, the unit (d) can also function as a crosslinking site during film formation and can contribute to film formation and crosslinkability. For this reason, the polymer (A) having Unit (d) is useful for the resist underlayer forming composition and further useful for the bottom

anti-reflective coating forming composition. In add ition, it is also useful for top anti-reflective coating forming composition.

[0043] Exemplified embodiments of the formu la (d) are, for example, as shown below.

[0044] In the polymer (A), n _a , n _b , n _c and n _d , which are the numbers of repetition respectively of Units (a), (b), (c) and (d), satisfy the following formulae:

n _a + n _b > 0,

n _c ³ 0, and

rid ³ 0.

[0045] n _a / (n _a + nb + n _c + nd) is preferably 2 to 80%, more preferably 5 to 50%, further preferably 10 to 50%, and still more preferably 20 to 40%.

nb / (n _a + nb + n _c + nd) is preferably 10 to 90%, more preferably 20 to 80%, further preferably 30 to 80%, and still more preferably 25 to 60%.

n _c / (n _a + nb + n _c + nd) is preferably 3 to 80%, more preferably 5 to 40%, further preferably 5 to 50%, and still more preferably 8 to 20%.

nd / (n _a + nb + n _c + nd) is preferably 0 to 80%, more preferably 0 to 40%, further preferably 5 to 30%, and still more preferably 10 to 30%.

[0046] Preferably, these satisfy the following formulae:

5% £ n _a / (n _a + nb + n _c + nd) £ 50%,

30% £ nb / (n _a + nb + n _c + nd) £ 80%,

5% £ n _c / (n _a + nb + n _c + nd) £ 40%, and/or 0% £ rid / (n _a + rib + n _c + rid) £ 40%.

[0047] Preferably, the total number (n _t o _t ai) of all repeating units contained in the polymer (A) satisfies the following formula :

80% £ (n _a + nb + n _c + nd) / ntotai £ 100%.

More preferably, it satisfies the following formula :

90% £ (n _a + nb + n _c + nd) / ntotai £ 100%.

Further preferably, it satisfies the following formula :

95% £ (n _a + nb + n _c + nd) / ntotai £ 100%.

It is also a preferable aspect of the present invention that being (n _a + nb + n _c + nd) / ntotai = 100%, that is, no repeating unit other than n _a , n _b , n _c and n _d is contained .

[0048] The mass average molecular weight (hereinafter sometimes referred to as Mw) of the polymer (A) is preferably 1,000 to 50,000, more preferably 3,000 to 40,000, and further preferably 5,000 to 20, 000.

The number average molecular weig ht (hereinafter sometimes referred to as Mn) of the polymer (A) is preferably 1,000 to 50,000, and more preferably 5,000 to 10,000.

In the present invention, Mw and Mn can be measured by gel permeation chromatography (GPC) . In the measurement, it is a suitable example to use a GPC column at 40 degrees Celsius, an elution solvent tetrahydrofuran at 0.6 mL/min and monodisperse polystyrene as a standard .

[0049] The method for synthesizing the polymer (A)

according to the present invention is not particularly limited, but Exemplified embodiments are shown in the synthesis examples described later. It is also possible to combine known synthesis methods with the synthesis examples.

[0050] Semiconductor composition >

The semiconductor composition according to the present invention (hereinafter sometimes referred to as the composition) comprises a polymer (A) and a solvent (B) .

Here, in the present invention, the semiconductor composition means a composition to be used in a semiconductor manufacturing process, and more preferably to be used in a lithography process. The semiconductor composition according to the present invention is preferably a composition for manufacturing semiconductor. The semiconductor composition

according to the present invention can be one that is removed in the semiconductor manufacturing process not to finally remain in the semiconductor. The

semiconductor composition is preferably a resist underlayer composition, more preferably a bottom anti-reflective coating composition. Here, the resist underlayer and the bottom anti-reflective coating are formed above a substrate and below a resist film. The resist underlayer and the bottom anti-reflective coating can be formed in contact with the substrate or the resist film, or can be formed throug h an interlayer.

[0051] The content of the polymer (A) is preferably 1 to

30% by mass, and more preferably 1 to 15% by mass, based on the total mass of the composition.

[0052] (B) Solvent

The solvent used in the composition according to the present invention preferably comprises water, a

hydrocarbon solvent, an ether solvent, an ester solvent, an alcohol solvent or a ketone solvent.

Exemplified embodiments of the solvent include water, n-pentane, i-pentane, n-hexane, i-hexane, n-heptane, i-heptane, 2,2,4-trimethylpentane, n-octane, i-octane, cyclohexane, methylcyclohexane, benzene, toluene, xylene, ethylbenzene, trimethylbenzene, methylethylbenzene, n-propylbenzene, i-propylbenzene, diethylbenzene, i-butylbenzene, triethylbenzene, di-i-propylbenzene, n-amyl naphthalene, trimethyl benzene, methanol, ethanol, n-propanol, i-propanol, n-butanol, i-butanol, sec-butanol, t-butanol, n-pentanol, i-pentanol, 2-methylbutanol, sec-pentanol, t-pentanol, 3-methoxybutanol, n-hexanol, 2-methylpentanol, sec-hexanol, 2-ethylbutanol, sec-heptanol, heptanol-3, n-octanol, 2-ethylhexanol, sec-octanol, n-nonyl alcohol,

2,6-dimethylheptanol-4, n-decanol , sec-undecyl alcohol, trimethyl nonyl alcohol, sec-tetradecyl alcohol,

sec-heptadecyl alcohol, phenol, cyclohexanol,

methylcyclohexanol, 3,3,5-trimethylcyclohexanol, benzyl alcohol, phenylmethyl carbinol, d iacetone alcohol, cresol, ethylene g lycol, propylene glycol, 1,3-butylene glycol, pentaned iol-2,4,2-methylpentanediol-2,4,

hexanediol-2,5, heptaned iol-2,4,2-ethylhexaned iol-l,3, diethylene g lycol, d ipropylene glycol, triethylene glycol, tripropylene glycol, glycerin, acetone, methyl ethyl ketone, methyl n-propyl ketone, methyl n-butyl ketone, d iethyl ketone, methyl i-butyl ketone, methyl n-pentyl ketone, ethyl n-butyl ketone, methyl n-hexyl ketone, di-i-butyl ketone, trimethylnonane, cyclohexanone, cyclopentanone, methylcyclohexanone, 2,4-pentanedione,

acetonylacetone, d iacetone alcohol, acetophenone, fenthion, ethyl ether, i-propyl ether, n-butyl ether, n-hexyl ether, 2-ethylhexyl ether, ethylene oxide, 1,2-propylene oxide, dioxolane, 4-methyl dioxolane, dioxane, dimethyl dioxane, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol d iethyl ether, ethylene g lycol mono-n-butyl ether, ethylene glycol mono-n-hexyl ether, ethylene g lycol monophenyl ether, ethylene g lycol mono-2-ethyl butyl ether, ethylene glycol dibutyl ether, d iethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene g lycol diethyl ether, d iethylene glycol mono-n-butyl ether, diethylene glycol di-n-butyl ether, d iethylene glycol mono-n-hexyl ether, ethoxytriglycol, tetraethylene g lycol di-n-butyl ether, propylene g lycol monomethyl ether

(PGM E), propylene glycol monoethyl ether, propylene glycol monopropyl ether, propylene glycol monobutyl ether, dipropylene glycol monomethyl ether, d ipropylene glycol monoethyl ether, d ipropylene glycol monopropyl ether, dipropylene glycol monobutyl ether, tripropylene glycol monomethyl ether, tetrahydrofuran,

2-methyltetrahyd rofuran; ester solvents such as d iethyl carbonate, methyl acetate, ethyl acetate, y-butyrolactone, g-valerolactone, n-propyl acetate, i-propyl acetate, n-butyl acetate, i-butyl acetate, sec-butyl acetate, n-pentyl acetate, sec-pentyl acetate, 3-methoxybutyl acetate, methylpentyl acetate, 2-ethylbutyl acetate, 2-ethylhexyl acetate, benzyl acetate, cyclohexyl acetate, methyl cyclohexyl acetate, n-nonyl acetate, methyl acetoacetate, ethyl acetoacetate, ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol monomethyl ether acetate, diethylene g lycol monoethyl acetate, diethylene glycol mono-n-butyl ether acetate, propylene g lycol monomethyl ether acetate, propylene g lycol monoethyl ether acetate, propylene g lycol monopropyl ether acetate, propylene glycol monobutyl ether acetate, dipropylene glycol monomethyl ether acetate, dipropylene g lycol monoethyl ether acetate, glycol diacetate, methoxytrig lycol acetate, ethyl propionate, n-butyl propionate, i-amyl propionate, diethyl oxalate, di-n-butyl oxalate, methyl lactate, ethyl lactate (EL), g-butyrolactone, n-butyl lactate, n-amyl lactate, diethyl malonate, d imethyl phthalate, diethyl phthalate, propylene glycol 1-monomethyl ether

2-acetate (PGMEA), propylene glycol monoethyl ether acetate and propylene glycol monopropyl ether acetate;

N-methylformamide, N,N-dimethylformamide,

N,N-diethylformamide, acetamide, N-methylacetamide, N,N-dimethylacetamide, N -methyl prop ionamide,

N-methyl pyrrolidone, d imethyl sulfide, d iethyl sulfide, thiophene, tetrahyd rothiophene, dimethyl sulfoxide, sulfolane, and 1,3-propane sultone. These solvents can be used alone or in combination of two or more.

The solvent (B) is more preferably PGMEA, PGME or a mixture thereof.

[0053] It is one aspect that the solvent (B) contains no water in relation to other layers or films. For example, the amount of water in the entire solvent (B) is preferably 0.1% by mass or less, more preferably 0.01% by mass or less, and further preferably 0.001% by mass or less.

[0054] The content of the solvent (B) is preferably 50 to

99% by mass, more preferably 70 to 98% by mass, and further preferably 80 to 95% by mass based on the total mass of the semiconductor composition. The film thickness after film formation can be controlled by increasing or decreasing the amount of the solvent in the entire composition.

[0055] (C) Crosslinker

The composition according to the present invention can further comprise a crosslinker. In addition, in the present invention, the crosslinker means a compound itself having a crosslinking function. The compound having a crosslinking function is sometimes dissolved or dispersed in a solvent and contained in the composition. Such a solvent is preferably contained in the

semiconductor composition as the solvent (B) or other component.

The crosslinker is useful to increase film formability when forming a film of the composition, to prevent the film from being intermixed with a film (for example, resist film) to be formed on its upper layer, and to eliminate diffusion of low molecular components into the upper layer film.

As is described later in Examples, among the polymer (A) according to the present invention, there are those good in film formation, filling properties and crosslinkability even without containing any crosslinker. Further, it is possible to suppress sublimate (outgas) during film formation, which is useful for avoid ing contamination of the apparatus. For this reason, as one aspect of the present invention, it is preferable that the content of the

crosslinker to be added is less. Therefore, the content of the crosslinker is preferably 0 to 5% by mass, more preferably 0 to 1% by mass, and further preferably 0% by mass, based on the total mass of the polymer (A) . The content of the crosslinker can be reduced by introducing a structure, which is capable of crosslinking, in the structure of the polymer (A) .

[0056] As the crosslinker, melamine compounds,

guanamine compounds, glycoluril compounds or urea compounds substituted by at least one g roup selected from a methylol group, an alkoxymethyl g roup, and an acyloxymethyl g roup; epoxy compounds; thioepoxy compounds; isocyanate compounds; azide compounds; and compounds comprising a double bond such as an alkenyl ether group can be referred . Further, compounds comprising a hyd roxy g roup can also be used as the crosslinker.

As the epoxy compounds,

tris(2,3-epoxypropyl)isocyanurate, trimethylolmethane trig lycidyl ether, trimethylolpropane triglycidyl ether, and triethylolethane trig lycidyl ether can be referred . As the melamine compounds, hexamethylolmelamine,

hexamethoxymethylmelamine, compounds derived by methoxymethylation of 1 to 6 methylol groups of

hexamethylolmelamine and mixtures thereof,

hexamethoxyethylmelamine,

hexaacyloxymethylmelamine, compounds derived by acyloxymethylation of 1 to 6 methylol groups of

hexamethylolmelamine or mixtures thereof can be referred . As the guanamine compounds,

tetramethylolguanamine, tetramethoxymethylguanamine, compounds derived by methoxymethylation of 1 to 4 methylol groups of tetramethylolguanamine and mixtures thereof, tetramethoxyethylguanamine, tetraacyloxyguanamine, compounds derived by

acyloxymethylation of 1 to 4 methylol groups of

tetramethylolguanamine and mixtures thereof can be referred . As the glycoluril compounds,

tetramethylolglycoluril, tetramethoxyglycoluril,

tetramethoxymethylglycoluril, compounds derived by methoxymethylation of 1 to 4 methylol groups of

tetramethylolg lycoluril or mixtures thereof, compounds derived by acyloxymethylation of 1 to 4 methylol groups of tetramethylolglycoluril or mixtures thereof can be referred .

As the urea compounds, tetramethylolurea,

tetramethoxymethylurea, compounds derived by

methoxymethylation of 1 to 4 of methylol g roups of tetramethylolurea or mixtures thereof,

tetramethoxyethylurea, and the like can be referred . As the compounds containing an alkenyl ether group, ethylene g lycol divinyl ether, triethylene glycol d ivinyl ether, 1,2-propanediol divinyl ether, 1,4-butanediol divinyl ether, tetramethylene glycol divinyl ether, neopentyl glycol divinyl ether, trimethylolpropane trivinyl ether, hexanediol divinyl ether, 1,4-cyclohexanediol divinyl ether, pentaerythritol trivinyl ether, pentaerythritol tetravinyl ether, sorbitol tetravinyl ether, sorbitol pentavinyl ether, trimethylolpropane trivinyl ether, and the like can be referred .

[0057] As the other crosslinker, those represented by the following formula can be referred .

wherein, L ³ is a direct bond, substituted or unsubstituted C1-3 alkyl, and R ²⁰ is hydrogen or methyl. L ³ is preferably a d irect bond or methyl, and more preferably a direct bond . The substituent of the C1-3 alkyl is preferably hydrogen, methyl, C6- 10 aryl, or any one of the following two formulae, and more preferably methyl or any one of the following two formulae.

[0058] Exemplified embodiments of the crosslinker

represented by the above formula are as shown below, but the scope of the present invention is not limited thereto.

[0059] The crosslinking temperature for film formation of the present composition is preferably 50 to 230°C, more preferably 80 to 220°C, and further preferably 80 to

190°C.

[0060] (D) Acid generator

The composition according to the present invention can further comprise an acid generator. In addition, in the present invention, the acid generator means a compound itself having an acid generating function. The compound having an acid generating function is

sometimes dissolved or d ispersed in a solvent and contained in the composition. Such a solvent is preferably contained in the semiconductor composition as the solvent

(B) or other component. The content of the acid generator (D) is preferably 0.01 to 10% by mass, and more preferably 1 to 7% by mass, based on the total mass of the polymer (A) .

[0061] As the acid generator, a thermal acid generator

(TAG) capable of generating a strong acid by heating can be used . The acid generator to be used in the present invention is preferably a compound that generates by heating an acid capable of reacting with the polymer (A) according to the present invention and of propagating crosslinking of the polymer. In a preferred embodiment, the acid to be generated is a strong acid such as sulfonic acid .

Preferably, the thermal acid generator is activated at a temperature exceeding 80°C. Examples of the thermal acid generator include metal-free sulfonium salts and metal-free iodonium salts, for example, triarylsulfonium, dialkylarylsulfonium and diarylalkylsulfonium salts of strong non-nucleophilic acids, and alkylaryliodonium and diaryliodonium salts of strong non-nucleophilic acids; and ammonium, alkylammonium, d ialkylammonium,

trialkylammonium, and tetraalkylammonium salts of strong non-nucleophilic acids. Further, covalent thermal acid generators are also considered as useful add itives, and examples thereof include 2-nitrobenzyl esters of alkyl or aryl sulfonic acids and other sulfonic acid esters which are thermally decomposed to give free sulfonic acid .

Examples thereof include diaryliodonium perfluoroalkyl sulfonates, diaryliodonium

tris(fluoroalkylsulfonyl)methides, d iaryliodonium

bis(fluoroalkylsulfonyl)methides, diaryliodonium

bis(fluoroalkylsulfonyl)imides, and diaryliodonium

quaternary ammonium perfluoroalkyl sulfonates.

Examples of the labile ester include 2-nitrobenzyl tosylate, 2,4-dinitrobenzyl tosylate, 2,6-dinitrobenzyl tosylate, and 4-nitrobenzyl tosylate; benzenesulfonates such as

2-trifluoromethyl -6- nitro benzyl 4-chlorobenzenesulfonate and 2-trifluoromethyl-6-nitrobenzyl

4-nitrobenzenesulfonate; phenolic sulfonate esters such as phenyl 4-methoxybenzenesulfonate; quaternary ammonium tris(fluoroalkylsulfonyl)methides, quaternary alkylammonium bis(fluoroalkylsulfonyl)imides, and alkylammonium salts of organic acids such as

triethylammonium salt of 10-camphorsulfonic acid .

Various aromatic (anthracene, naphthalene or benzene derivative) sulfonic acid amine salts, including those disclosed in U.S. Patent No. 3,474,054, No. 4,200,729, No.

4,251,665 and No. 5, 187,019, can be used as the TAG. The acid generator to be used in the present invention can be two or more compounds.

[0062] (E) Surfactant

The composition according to the present invention can further comprise a surfactant in order to improve coating properties. Here, in the present invention, the surfactant means a compound itself having a surface active action. The compound having a surface active action is sometimes dissolved or d ispersed in a solvent and contained in the composition. Such a solvent is preferably contained in the semiconductor composition as the solvent (B) or other component.

The content of the surfactant (E) is preferably 0.001 to 5% by mass, and more preferably 0.01 to 0.5% by mass, based on the total mass of the polymer (A) .

[0063] As the surfactant (E) that can be used in the present invention, (I) an anionic surfactant, (II) a cationic surfactant or (III) a nonionic surfactant can be referred, and in particular, (I) alkyl sulfonate, alkylbenzene sulfonic acid and alkylbenzene sulfonate, (II) lauryl pyridinium chloride and lauryl methyl ammonium chloride, and (III) polyoxyethylene octyl ether, polyoxyethylene lauryl ether and polyoxy ethylene acetylenic g lycol ether are

preferred .

[0064] (F) Additive The composition according to the present invention can comprise other add itive (F) than (A) to (E) .

The additive (F) is not particularly limited, but the additive is preferably at least one selected from the group consisting of a base generator, a smoothing agent, a monomeric dye, a lower alcohol (Ci- ₆ alcohol), a surface leveling agent, a substrate adhesion agent, an

antifoaming agent and an antiseptic. As in the case of a base generator, for example, wherein it means a

compound itself that generates a base, the additive means a compound itself having its function. The compound is sometimes dissolved or d ispersed in a solvent and contained in the composition. Such a solvent is preferably contained in the semiconductor composition as the solvent (B) or other component.

The content of the add itive (F) is preferably 0 to 10% by mass, and more preferably 0 to 5% by mass, based on the total mass of the polymer (A) . It is a preferable example of the composition according to the present invention that no additive (F) is contained (0% by mass) .

[0065] < Method for manufacturing a film >

The method for manufacturing a film according to the present invention comprises the following processes:

(1) applying the semiconductor composition according to the present invention above a substrate; and

(2) heating said semiconductor composition to form a film.

Flere, the film according to the present invention means a film derived from the semiconductor composition according to the present invention, and is hereinafter sometimes referred to as the film (2) . The film (2) is preferably a resist underlayer, and more preferably a bottom anti-reflective coating .

[0066] hereinafter, one aspect of the manufacturing

method according to the present invention is described . The semiconductor composition according to the present invention is applied above a substrate (for example, a silicon/silicon dioxide-coated substrate, a silicon nitride substrate, a silicon wafer substrate, a glass substrate, an ITO substrate, and the like) by an

appropriate method . Here, in the present invention, the "above" includes the case where a layer is formed immed iately above a substrate and the case where a layer is formed above a substrate via another layer. For example, a planarization film can be formed immed iately above a substrate, and the composition accord ing to the present invention can be applied immed iately above the planarization film. The application method is not particularly limited, and examples thereof include a method using a spinner or a coater. After application, the film accord ing to the present invention is formed by heating . The heating of (2) is performed, for example, by a hot plate. The heating temperature is preferably 100 to 250°C, more preferably 125 to 225°C, and further preferably 150 to 200°C. The temperature here is a temperature of heating atmosphere, for example, that of a heating surface of a hot plate. The heating time is preferably 30 to 300 seconds, and more preferably 45 to 180 seconds. The heating is preferably performed in an air or nitrogen gas atmosphere. By this heating, crosslinking reaction proceeds in the composition.

Therefore, the film (2) is not easily dissolved in the subsequent processes.

The film thickness of the film (2) is preferably 10 to 1,000 nm, more preferably 30 to 500 nm, and further preferably 50 to 100 nm.

[0067] The absorption parameter (k) of the film (2) is

measured by ellipsometric measurement and is a numerical value of 0.01 to 1.0 depending on the exposure wavelength. The refractive index (n) is also optimized and can be a numerical value of 1.3 to 2.0, and preferably 1.5 to 1.9, depending on the exposure wavelength. The values of n and k can be calculated using an ellipsometer such as Woollam WVASE VU-32 (trademark) ellipsometer. The exact values in the optimal range for k and n depend on the exposure wavelength used to expose the resist film coated on the film of (2) and the application method .

[0068] Subsequently, a resist film can be manufactured by the method comprising the following processes:

(3) applying a resist composition above the film (2), and

(4) heating the resist composition to form a resist film.

Although this is described for clarity, the processes (1) and (2) are performed before the process (3) .

Numbers in parentheses indicating processes mean order.

The same applies to the followings.

The resist composition is applied above the film (2) by an appropriate method . The application method is not particularly limited and can be the same as the above application.

The resist composition is not particularly limited, and any positive resist composition, negative resist composition or negative tone development (NTD) resist composition can be used as long as it is sensitive to exposure lig ht for pattern formation. The resist composition to be used in the present invention is preferably a positive resist composition or a negative resist composition, and more preferably a chemically amplified positive resist composition or a chemically amplified negative resist composition. Further, the resist composition preferably comprises an acid generator or a base generator.

After application, a resist film is formed by heating . The heating temperature of (4) is preferably 80 to 250°C, more preferably 80 to 200°C, and further preferably 90 to

180°C. The heating time is preferably 30 to 600 seconds, more preferably 30 to 300 seconds, and further preferably 60 to 180 seconds. The heating is preferably performed in an air or nitrogen gas atmosphere.

The thickness of the resist film varies depending on the exposure wavelength but is preferably 100 to 50,000 nm. When a KrF excimer laser is used for exposure, the film thickness of the resist film is preferably 100 to 5,000 nm, more preferably 100 to 1,000 nm, and further preferably 400 to 600 nm.

[0069] Subsequently, a resist pattern can be manufactured by the method comprising the following processes:

(5) exposing the resist film, and

(6) developing the resist film.

Exposure is performed to the resist film through a predetermined mask. The wavelength of light to be used for exposure is not particularly limited, but it is preferable to expose with lig ht having wavelength of 13.5 to 248 nm. In particular, KrF excimer laser (wavelength : 248 nm), ArF excimer laser (wavelength : 193 nm), extreme ultraviolet light (wavelength : 13.5 nm), or the like can be used, and

KrF excimer laser is preferable. These wavelengths allow a range of ± 1%. After exposure, post exposure bake can be performed as necessary. The post exposure heating temperature is preferably 80 to 150°C, more preferably 100 to 140°C, and the heating time is 0.3 to 5 minutes, preferably 0.5 to 2 minutes.

The exposed resist film is developed using a developer. The developer to be used is preferably a 2.38% by mass tetramethylammonium hydroxide (TMAFI) aqueous solution. The temperature of the developer is preferably 5 to 50°C, more preferably 25 to 40°C, and the development time is preferably 10 to 300 seconds, more preferably 30 to 60 seconds.

Using such a developer, the resist film and/or the film (2) can be easily d issolved and removed at room temperature. Further, to these developers, for example, a surfactant can also be added .

When a positive resist composition is used, the exposed portion of the positive photoresist layer is removed by development to form a resist pattern. The resist pattern can be further made finer, for example, using a shrink material.

[0070] Subsequently, a processed substrate can be

manufactured by the method comprising the following process:

(7) etching with the resist pattern as a mask.

Using the resist pattern as a mask, the film (2) or substrate is preferably etched . At this time, the substrate can be processed by etching the film (2) and substrate at a time, or it is also possible to process in stages, in such a way that after etching the film (2), the substrate is etched using the film (2) as a mask. Etching can be either dry etching or wet etching . Thereby, a gap can be formed in the substrate or a layer on the substrate. After the gap is formed, the resist pattern can be removed by making it contact with water, a mixed solution of water-soluble organic solvent and water, or an alkaline aqueous solution. Further, it is also possible to form a wiring using the formed gap. In addition, the substrate can be processed by a method other than etching .

[0071] Thereafter, if necessary, the substrate is further processed to form a device. For these further processing, known methods can be applied . After forming the device, if necessary, the substrate is cut into chips, which are connected to a lead frame and packaged with resin. In the present invention, this packaged product is referred to as a device.

[0072] Examples

The present invention is described below with reference to examples. In add ition, the aspect of the present invention is not limited only to these examples.

[0073] Synthesis of Polymer 1 In a three-necked flask, 350 g of PGMEA is put, and subsequently 32.79g of MOI-BP (Karenz MOI-BP, Showa Denko), 20g of McFIN (Kawasaki Kasei Chemicals), 6.422g of DYE-M9A (Osaka Shinyaku) and 8.16g of FIPMA (lig ht ester FIOP, Kyoeisha Chemical), which are shown below, are added . These fall under Unit (a), Unit (b), Unit (c) and Unit (d), respectively.

Subsequently, V-601/oil-soluble azo polymerization initiator (Fuji Film Wako Pure Chemical) is added . The three-necked flask is filled with nitrogen, covered, heated while stirring with a stirring bar, and the liquid is reacted at 80°C for 4 hours. Subsequently, 3g of PGME is added and stirred to complete the polymerization. The reaction liquid is returned to a room temperature. The reaction liquid is dropped into l,500g of hexane to precipitate polymer. This is filtered and dried under reduced pressure to obtain Polymer 1.

Polymer 1 (molar ratio, n _a : ri _b : n _c : ri _d = 26 : 49 : 14 : 11) : When measured by GPC (elution solvent: tetrahydrofuran), Mn of polymer 1 is 9,900 and Mw is

22,200.

[0074] Synthesis of Polymers 2 to 11 and Comparative

Polymers 1 and 2

The synthesis is performed in the same manner as in the above-described synthesis example of Polymer 1 except that the molar ratio of Unit (a), Unit (b), Unit (c) and Unit (d) is changed as shown in Table 1. Polymers 2 to 11 and Comparative Polymers 1 and 2 are obtained .

It is capable of visually confirming that Comparative

Polymers 1 and 2 are gelled . Comparative Polymers 1 and 2 are judged to be unsuitable for fine processing and are not subjected to subsequent evaluations.

Mn and Mw of each polymer are measured by GPC (elution solvent tetrahyd rofuran) and they are as shown in

Table 1.

[Table 1]

Table 1

[0075] Preparation of Composition 1

Surfactant (M EGAFACE R-40, DIC) is dissolved in PGMEA so as to be 5% by mass. This is desig nated as the 5% by mass surfactant solution.

As the solvent, 68.4 g of PGMEA and 29.4g of PGM E are mixed . To this, 0.04g of camphorsulfonic acid (Fuji Film Wako Pure Chemical) and 0.018g of triethylamine (Kanto Chemical) are added . These function as a thermal acid generator.

To this, 2g of Polymer 1 and 0.048g of the 5% by mass surfactant solution are added, and stirred and mixed at room temperature for 1 hour. Thereby, Composition 1 is obtained .

When visually observed Composition 1, it is capable of confirming that the solute is dissolved .

[0076] Preparation of Compositions 2 to 11

The preparation is performed in the same manner as the preparation of Composition 1 except that the polymer used is changed as shown in Table 2, and Compositions 2 to 11 are obtained .

When visually observed each composition, it is capable of confirming that the solute is dissolved .

[0077] Preparation of Composition 12

Surfactant (M EGAFACE R-40) is dissolved in PGM EA so as to be 5% by mass. This is designated as the 5% by mass surfactant solution.

As the solvent, 68.4g of PGMEA and 29.4g of PGME are mixed . To this, 0.04g of camphorsulfonic acid and 0.018g of triethylamine are added . These function as a thermal acid generator.

To this, 2g of Polymer 1, 0.6g of the following crosslinker NIKALAC MX-270 (Sanwa Chemical) and 0.048g of the 5% by mass surfactant solution are added, and stirred and mixed at room temperature for 1 hour. Thereby, Composition 12 is obtained .

When visually observed Composition 12, it is capable of confirming that the solute is dissolved .

[0078] Preparation of Compositions 13 and 14

The preparation is performed in the same manner as the preparation of Composition 12 except that the polymer used is changed as shown in Table 2, and Compositions 13 and 14 are obtained .

When visually observed each composition, it is capable of confirming that the solute is dissolved .

[0079] Preparation of Comparative Composition 1

The following P090D polymer is dissolved in PGMEA so as to be 17% by mass. This is desig nated as the P090D polymer solution.

Surfactant (M EGAFACE R-40) is dissolved in PGM EA so as to be 5% by mass. This is designated as the 5% by mass surfactant solution.

As the solvent, 68.4g of PGMEA and 29.4g of PGME are mixed . To this, 0.04g of camphorsulfonic acid and 0.018g of triethylamine are added . These function as a thermal acid generator. To this, 3.2 g of the following VPS-2515 (poly(hydroxystyrene/styrene) copolymer),

4.6g of the P090D polymer solution, 0.6g of a crosslinker (TMOM-BP) and 0.048 g of the 5% by mass surfactant solution are added, and stirred and mixed at room temperature for 1 hour. Thereby, Comparative

Composition 1 is obtained . Hereinafter, for simplification, when VPS-2515 and P090D are polymer components, they are described as VPS + P090D.

When visually observed Comparative Composition 1, it is capable of confirming that the solute is dissolved .

(P090D polymer, TOHO Chemical ; a : b : c: d = 35.7 : 35.7 : 17.9 : 10.7; molecular weig ht: 4,000 to 8,000)

(VPS-2515, N ippon Soda; molecular weig ht: 3,300 to 4,300)

(TMOM-BP, Honshu Chemical Industry)

[0080] Preparation of Comparative Composition 2

The P090D polymer is dissolved in PGMEA so as to be 17% by mass. This is desig nated as the P090D polymer solution.

Surfactant (M EGAFACE R-40) is dissolved in PGM EA so as to be 5% by mass. This is designated as the 5% by mass surfactant solution.

As the solvent, 68.4g of PGMEA and 29.4g of PGME are mixed . To this, 0.04g of camphorsulfonic acid and 0.018g of triethylamine are added . These function as a thermal acid generator.

To this, 3.2g of poly(hydroxystyrene/styrene) copolymer (VPS-2515), 4.6g of the P090D polymer solution, and 0.048g of the 5% by mass surfactant solution are added, and stirred and mixed at room temperature for 1 hour. Thereby, Comparative

Composition 2 is obtained .

When visually observed Comparative Composition 1, it is capable of confirming that the solute is dissolved .

[0081] Evaluation of film formation

Using a coater/developer, Mark 8 (manufactured by Tokyo Electron Ltd .), each composition is spin-coated on a Si bare wafer. The wafer is baked in an air at 180°C for 60 seconds to form a film.

By this process, if a film is formed from the composition, the film formation is evaluated as A, and if no film is formed, the film formation is evaluated as B. The evaluation results are shown in Table 2.

When measured with LambdaAce VM- 1210

(SCREEN), the film thickness is 45 nm.

[0082] Evaluation of uniformity

Uniformity of the film formed by the above film formation is evaluated . The evaluation criteria are as described below. The evaluation results are shown in Table 2.

A: Through visual observation, it is confirmed uniformly applied .

B: Through visual observation, presence of spots is confirmed .

In addition, the film formed using Composition 1 has a difference between the maximum value and the minimum value of 2 nm or less when the film thickness is measured at 21 points on a straight line.

[Table 2] Table 2

[0083] Evaluation of optical constants

Optical constants of the film formed by the above film formation are evaluated . Reflected light is measured with Ellipsometer M2000-D (J .A. Woollam) and

wavelength of 248 nm. Thereby, optical constants n value and k value are obtained . The evaluation results are shown in Table 3.

It is capable of confirming that the film formed from Composition 1 has sufficient characteristics as an antireflection film.

[0084] Evaluation of filling properties

Each composition is spin-coated on a silicon substrate with level d ifference (line space ratio : 1 : 2, pitch width : 48 nm (L16 nm/S32 nm), depth : 100 nm), and a section of the substrate is observed with SEM and filling properties is evaluated . The evaluation criteria are as described below. The evaluation results are shown in Table 3.

A: In the SEM photograph, no voids are observed in the level difference where the composition is filled .

B: In the SEM photograph, some voids exist in a part of the level difference where the composition is filled .

[0085] Evaluation of crosslinkability

The film thickness of the film formed by the above film formation is designated as the initial film thickness. The wafer is immersed in a PGMEA/PGME solution (AZ

EBR7030, Merck Performance Materials, hereinafter referred to as MPM) for 60 seconds, then spin-dried, and the film thickness is measured again. When the decrease width of the film thickness is less than 2 nm compared with the initial film thickness, it is evaluated that the

crosslinking is sufficient. In the case of sufficient crosslinking, the baking temperature at the film formation is lowered sequentially to 170°C, 160°C and 150°C, and the same experiment and evaluation are performed until the film thickness decreased to 2 nm or more (insufficient crosslinking) . Throug h this, confirmation of

crosslinkability is conducted . Conditions of the baking temperature immediately before crosslinking becomes insufficient (temperature at which crosslinking is sufficient) are shown in the table.

When the film of 10 nm or more is dissolved by the PGM EA/PGME solution, it is evaluated as B.

The evaluation results are shown in Table 3.

[0086] Formation of resist pattern

A resist composition (AZ DX3200P, MPM) is spin-coated on the film formed by the above film

formation, and baked at 90°C for 60 seconds. Thereby, a resist film having film thickness of 580 nm is formed .

This wafer is exposed with PFA-3000 EX-5 (Canon) under the conditions of wavelength : 248 nm, mask size =

200 nm, and line: space = 1 : 1. The exposed wafer is subjected to post-exposure baking treatment at 120°C for 90 seconds, and developed using a 2.38% by mass TMAFI aqueous solution for 60 seconds. The resultant is rinsed with water and spin-dried . Thereby, a resist pattern is formed . [0087] Evaluation of standing wave

The resist pattern formed above is observed with a scanning electron microscope and the state of stand ing wave is evaluated . The evaluation criteria are as follows. The evaluation results are shown in Table 3.

A: A reduction of the stand ing wave is observed . The resist wall surface is hard ly waved .

B: A reduction of the stand ing wave is observed . The resist wall surface is slightly waved .

C: A reduction of stand ing wave is not indicated .

[Table 3]

Table 3

[0088] Evaluation of sublimate

The test and evaluation according to the measuring method of the sublimate in thermally set film using the

QCM sensor described in W02007/111147 (Patent Document 3) are performed .

Composition 1 is applied on a silicon wafer substrate having a diameter of 4 inches with a spin coater at 2,500 rpm for 60 seconds. The film thickness is measured to be

78 nm.

The above wafer is set in a sublimate measuring device integrated with a hot plate, which is adjusted to 205°C, and baked for 60 seconds, and the sublimate is collected and determined the quantity using a QCM sensor (TH-Q100 and Sensor SEN-9E-H 10, TAMADEVICE) .

Measurement is performed by raising the

temperature of the hot plate to 180°C, setting the pump flow rate to lm ³ /s and leaving the sublimate for aging for the first 60 seconds. Immediately after that, the wafer coated with the film is quickly put on the hot plate from the slide aperture (measuring object is installed), and the sublimate from the time point of 60 seconds to that of 120 seconds (for 60 seconds) is collected .

A nozzle with a diameter of 2 mm is attached to the flow attachment (detection part) connecting the QCM sensor and the collection funnel part, and the distance between the sensor and the nozzle is kept at 0.5 mm.

Further, a QCM sensor, for which an electrode made of a compound containing silicon and aluminum is used and which has a crystal resonator with a diameter (sensor diameter) of 14 mm, a crystal resonator surface electrode diameter of 5 mm and a resonance frequency of 9 MHz, is used .

Evaluation criteria are as follows.

A: Sublimated amount < 0.1 ng

B : Sublimated amount ³ 0.1 ng, £ 0.5 ng

C: Sublimated amount > 0.5 ng

Also for each composition described in Table 4, tests and evaluations are performed in the same way as those described above. The results are shown in Table 4.

[Table 4] Table 4

[0089] When a film is formed from Compositions 1 to 9 made of Polymers 1 to 9, it is confirmed that the generation of sublimate is small. Using these compositions, contamination of the apparatus can be prevented, and it is considered good in the manufacturing process.