Title:
POLYMERIZATION CATALYSTS
Document Type and Number:
WIPO Patent Application WO/2018/064038
Kind Code:
A1
Abstract:
Embodiments of the present disclosure directed towards polymerization catalysts having improved ethylene enchainment and/or improved catalyst productivity. As an example, the present disclosure provides a polymerization catalyst of Formula (I), wherein each of R1 to R12 is independently a C1 to C20 alkyl, aryl or aralkyl group, or a hydrogen, wherein at least one of R4 to R7 is not a hydrogen, wherein M is a Group 4 metal, and wherein, each X is independently a halide, C1 to C20 alkyl, aralkyl or hydrogen

Inventors:
KUHLMAN ROGER L (US)
MCDOUGAL MAHSA (US)
BROONER RACHEL E M (US)
YONKEY MATTHEW M (US)
Application Number:
PCT/US2017/053439
Publication Date:
April 05, 2018
Filing Date:
September 26, 2017
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
UNIVATION TECH LLC (US)
International Classes:
C08F210/16; C08F4/6592
Domestic Patent References:
WO2005105864A12005-11-10
WO2009155471A22009-12-23
WO1999060033A11999-11-25
WO1999047598A11999-09-23
WO1999048605A11999-09-30
WO1999050311A11999-10-07
WO2000012565A12000-03-09
WO2000013792A12000-03-16
Foreign References:
US20040249096A12004-12-09
US5965477A1999-10-12
EP0511665B11998-07-22
US6034187A2000-03-07
EP0767184B11999-08-18
US5972510A1999-10-26
US20060173123A12006-08-03
Other References:
TANJA PIEL ET AL: "Effect of Metallocene Structures on their Performance in Ethene Polymerisation", MACROMOLECULAR CHEMISTRY AND PHYSICS., vol. 208, no. 8, 19 April 2007 (2007-04-19), DE, pages 851 - 861, XP055442864, ISSN: 1022-1352, DOI: 10.1002/macp.200600595
ALEXEY N. RYABOV ET AL: "Palladium-Catalyzed Cross-Coupling Reactions of Bromo-Substituted Group 4 Metallocenes", ORGANOMETALLICS, vol. 28, no. 13, 13 July 2009 (2009-07-13), US, pages 3614 - 3617, XP055442866, ISSN: 0276-7333, DOI: 10.1021/om900353m
VIRVE A. KARTTUNEN ET AL: "Influence of the Ligand Structure of Hafnocene Polymerization Catalysts: A Theoretical Study on Ethene Insertion and Chain Propagation", ORGANOMETALLICS, vol. 27, no. 14, 1 July 2008 (2008-07-01), US, pages 3390 - 3398, XP055378319, ISSN: 0276-7333, DOI: 10.1021/om800050d
SCHUMANN H ET AL: "Synthesis, characterization, and catalytic properties of bis[alkylindenyl]-, bis[alkenylindenyl]- and [alkenylindenyl(cyclopentadienyl)]zirconium dichloride complexes", JOURNAL OF ORGANOMETALLIC CHEMIS, ELSEVIER-SEQUOIA S.A. LAUSANNE, CH, vol. 636, no. 1-2, 25 November 2001 (2001-11-25), pages 31 - 40, XP004311755, ISSN: 0022-328X, DOI: 10.1016/S0022-328X(01)00834-8
"HAWLEY'S CONDENSED CHEMICAL DICTIONARY", 1997, JOHN WILEY & SONS, INC.
"Polypropylene Handbook", 1996, HANSER PUBLISHERS, pages: 76 - 78
Attorney, Agent or Firm:
KOTRBA, Kory J. (US)
Download PDF:
Claims:
What is claimed:

1. A polymerization catalyst, the polymerization catalyst comprising a metallocene catalyst of Formula I:

(Formula I)

wherein each of R to R 2 is independently a Ci to C2o alkyl, aryl or aralkyl group, a hydrogen, wherein at least one of R4 to R7 is not a hydrogen, wherein M is a Group 4 metal, and wherein, each X is independently a halide, Ci to C20 alkyl, aralkyl or hydrogen.

2. The polymerization catalyst of claim 1 , wherein each of R9, R 0, R and R 2 of Formula I is a hydrogen.

3. The polymerization catalyst of claim 1 , wherein each of R1 , R2, and R3 of Formula I is a hydrogen.

4. The polymerization catalyst of claim 1 , wherein R5 and R6 of Formula I together form a cycloalkyl group.

5. The polymerization catalyst of claim 4, wherein the cycloalkyl group further comprises cyclohexyl-1 , 1 ,4,4-tetramethyl.

6. The polymerization catalyst of claim 4, wherein the R8 of Formula I is a d to C2o alkyl.

7. The polymerization catalyst of claim 6, wherein R of Formula I further comprises a Ci to C3 alkyl. 6 The polymerization catalyst of claim 1 , wherein each of R7 and R4 of Formula I is independently a Ci to C2o alkyl.

7. The polymerization catalyst of claim 6, wherein each of R , R2 R3 of Formula I is a hydrogen.

8. The polymerization catalyst of claim 6, wherein each of R5 and R6 of Formula I is a hydrogen

9. The polymerization catalyst of claim 1 , wherein M of Formula I further comprises titanium, zirconium or hafnium.

10. A polyethylene composition comprising polyethylene formed in a single reactor via a polymerization catalyst comprising a metallocene catalyst having improved ethylene enchainment of the formula:

(Formula I)

wherein each of R to R 2 is independently a Ci to C2o alkyl, aryl or aralkyl group, or a hydrogen, wherein at least one of R4 to R7 is not a hydrogen, wherein M is a Group 4 metal, and wherein, each X is independently a halide, Ci to C20 alkyl, aralkyl or hydrogen.

11. The polyethylene composition of claim 10, wherein the polyethylene has a weight average molecular weight from 5,000 to 250,000 grams/mole (g/mol).

12. The polyethylene composition of claim 1 1 , wherein the polyethylene having the improved ethylene enchainment has a melt temperature of from 90 degrees Celsius to 136134 degrees Celsius.

13. A method of producing polyethylene having improved ethylene enchainment, the method comprising:

polymerizing ethylene in a reactor in presence of a polymerization catalyst to form the polyethylene, wherein the polymerization catalyst comprises a metallocene catalyst of Formula I:

(Formula I)

wherein each of R to R 2 is independently a Ci to C2o alkyl, aryl or aralkyl group, or a hydrogen, wherein at least one of R4 to R7 is not a hydrogen, wherein M is a Group 4 metal, and wherein, each X is independently a halide, Ci to C20 alkyl, aralkyl or hydrogen.

Description:
POLYMERIZATION CATALYSTS

Field of Disclosure

[0001] Embodiments of the present disclosure are directed towards

polymerization catalysts, more specifically, embodiments are directed towards polymerization catalysts with improved ethylene enchainment and yet that retain a desired degree of activity.

Background

[0002] Polymers may be utilized for a number of products including films and pipes, among other. Polymers can be formed by reacting one or more types of monomer in a polymerization reaction. There is continued focus in the industry on developing new and improved materials and/or processes that may be utilized to form polymers.

[0003] Ethylene alpha-olefin (polyethylene) copolymers are typically produced in a low pressure reactor, utilizing, for example, solution, slurry, or gas phase polymerization processes. Polymerization takes place in the presence of catalyst systems such as those employing, for example, a Ziegler-Natta catalyst, a chromium based catalyst, a

metallocene catalyst, or combinations thereof.

[0004] A number of catalyst compositions containing single site catalysts, e.g., metallocene, catalysts have been used to prepare polyethylene copolymers, producing relatively homogeneous copolymers at good polymerization rates. In contrast to traditional Ziegler-Natta catalyst compositions, single site catalyst compositions, such as metallocene catalysts, are catalytic compounds in which each catalyst molecule contains one or only a few polymerization sites. Single site catalysts may produce polyethylene copolymers that have a narrow molecular weight distribution. Although there are single site catalysts that can produce broader molecular weight distributions, polymers produced by these catalysts often show a narrowing of the molecular weight distribution (MWD) as the reaction temperature is increased, for example, to increase production rates. Further, a single site catalyst will often incorporate an amount of comonomer into the molecules of the polyethylene copolymer. [0005] It is generally known in the art that a polyolefin's MWD affects different product attributes. Polymers having a broad molecular weight distribution may have improved physical and/or mechanical properties, such as stiffness, toughness, processibility, and environmental stress crack resistance (ESCR), among others.

[0006] To achieve these properties, bimodal polymers have become increasingly important in the polyolefin industry, with a variety of manufacturers offering products of this type. Bimodal polymers generally refer to polymers produced using two or more different catalyst types or two or more different reactor environments, such that the resultant polymers have a bimodal molecular weight distribution typically including a low molecular weight component and a high molecular weight component (having a comparatively high molecular weight and/or range of molecular weights than the low molecular weight component). Whereas older technology relied on two-reactor systems to generate such material, advances in catalyst design and supporting technology have allowed for the development of single reactor bimetallic catalyst systems capable of producing bimodal high density polyethylene (HDPE). These systems are attractive both from a cost perspective and ease of use.

[0007] Control of these properties is obtained for the most part by the choice of the catalyst system. Thus, the catalyst design is important for producing polymers that are attractive from a commercial standpoint. Because of the improved physical properties of polymers with the broad molecular distributions needed for commercially desirable products, there exists a need for controlled techniques and/or materials for forming polyethylene copolymers having a desirable molecular weight distribution and/or having a desired distribution of comonomer between a high molecular weight polyethylene component and a low molecular weight polyethylene component of a bimodal polyethylene composition.

Brief description of drawings

[0008] Figure 1 is a schematic of a gas-phase reactor system, showing the addition of a polymerization catalyst, in accordance with embodiments described herein.

Summary

[0009] The present disclosure provides a new polymerization catalyst of Formula

I:

Formula I

[0010] where each of to R 2 is independently a Ci to C 20 alkyl, aryl or aralkyl group, or a hydrogen, where at least one of R 4 to R 7 is not a hydrogen, where M is titanium, zirconium or hafnium, and where each X is independently a halide, Ci to C 20 alkyl, aralkyl or hydrogen. It is noted that any of the adjacent R-groups may combine to form a ring, as described herein.

[0011] The present disclosure provides polyethylene composition comprising polyethylene formed in a single reactor via a polymerization catalyst comprising a new metallocene catalyst of the Formula I, as described above.

[0012] The present disclosure provides methods of producing polyethylene, the method comprising polymerizing ethylene in a reactor in presence of a polymerization catalyst to form the polyethylene, where the polymerization catalyst comprises a new metallocene catalyst of Formula I, as described above.

[0013] The above summary of the present disclosure is not intended to describe each disclosed embodiment or every implementation of the present disclosure. The description that follows more particularly exemplifies illustrative embodiments. In several places throughout the application, guidance is provided through lists of examples, which examples can be used in various combinations. In each instance, the recited list serves only as a representative group and should not be interpreted as an exclusive list.

Detailed Description

[0014] Polymerization catalysts, polyethylene compositions formed via polymerization catalysts, and methods of producing polyethylene employing

polymerization catalysts are described herein. In general, the present techniques are directed to the new metallocene catalysts of Formula I that improves polymerization economics and gives desirable polymer properties. For instance, the polymerization catalyst including the new metallocene of Formula I can be employed in a single reactor to form a polyethylene having desirable properties. Similarly, bimodal polymerization catalyst systems including the new zirconocene catalyst of Formula I can be employed in a single reactor to form a bimodal polyethylene composition having desirable properties such as a desirable (e.g., broad) molecular weight distribution and/or having improved ethylene enchainment (e.g. , as evidenced by melt temperature).

[0015] Catalyst Compounds

[0016] Zirconocene Catalyst Compounds

[0017] Zirconocene catalysts are a type of a metallocene catalyst. Metallocene catalyst compounds can include "half sandwich" and/or "full sandwich" compounds having one or more Cp ligands (e.g. , cyclopentadienyl and ligands isolobal to cyclopentadienyl) bound to at least one Group 3 to Group 12 metal atom, and one or more leaving groups bound to the at least one metal atom. As used herein, all reference to the Periodic Table of the Elements and groups thereof is to the NEW NOTATION published in HAWLEY'S CONDENSED CHEMICAL DICTIONARY, Thirteenth Edition, John Wiley & Sons, Inc. , (1997) (reproduced there with permission from l UPAC), unless reference is made to the Previous lU PAC form noted with Roman numerals (also appearing in the same), or unless otherwise noted.

[0018] The Cp ligands are one or more rings or ring systems, at least a portion of which includes ττ-bonded systems, such as cycloalkadienyl ligands and heterocyclic analogues. The rings or ring systems typically include atoms selected from the group consisting of Groups 13 to 16 atoms, and, in a particular exemplary embodiment, the atoms that make up the Cp ligands are selected from the group consisting of carbon, nitrogen, oxygen, silicon, sulfur, phosphorous, germanium, boron, aluminum, and combinations thereof, where carbon makes up at least 50 % of the ring members. In a more particular exemplary embodiment, the Cp ligands are selected from the group consisting of substituted and unsubstituted cyclopentadienyl ligands and ligands isolobal to cyclopentadienyl, non-limiting examples of which include cyclopentadienyl, indenyl, fluorenyl and other structures. Further non-limiting examples of such ligands include cyclopentadienyl, cyclopentaphenanthreneyl, indenyl, benzindenyl, fluorenyl, octahydrofluorenyl, cyclooctatetraenyl, cyclopentacyclododecene, phenanthrindenyl, 3,4- benzofluorenyl, 9-phenylfluorenyl, 8-H-cyclopent[a]acenaphthylenyl, 7-H- dibenzofluorenyl, indeno[1 ,2-9]anthrene, thiophenoindenyl, thiophenofluorenyl, hydrogenated versions thereof (e.g., 4,5,6,7-tetrahydroindenyl, or "H 4 Ind"), substituted versions thereof (as discussed and described in more detail below), and heterocyclic versions thereof.

[0019] The metal atom "M" of the metallocene catalyst compound can be selected from the group consisting of Groups 3 through 12 atoms and lanthanide Group atoms in one exemplary embodiment; and selected from the group consisting of Groups 3 through 10 atoms in a more particular exemplary embodiment, and selected from the group consisting of Sc, Ti, Zr, Hf, V, Nb, Ta, Mn, Re, Fe, Ru, Os, Co, Rh, Ir, and Ni in yet a more particular exemplary embodiment; and selected from the group consisting of Groups 4, 5, and 6 atoms in yet a more particular exemplary embodiment, and Ti, Zr, Hf atoms in yet a more particular exemplary embodiment, and Hf in yet a more particular exemplary embodiment. The oxidation state of the metal atom "M" can range from 0 to +7 in one exemplary embodiment; and in a more particular exemplary embodiment, can be +1 , +2, +3, +4, or +5; and in yet a more particular exemplary embodiment can be +2, +3 or +4. The groups bound to the metal atom "M" are such that the compounds described below in the formulas and structures are electrically neutral, unless otherwise indicated. The Cp ligand forms at least one chemical bond with the metal atom M to form the "metallocene catalyst compound." The Cp ligands are distinct from the leaving groups bound to the catalyst compound in that they are not highly susceptible to substitution/abstraction reactions

[0020] As used herein, the phrase "catalyst system" or "bimodal catalyst system" includes at least one "catalyst component" and at least one "activator", both of which are described further herein. The catalyst system may also include other components, such as supports, etc., and is not limited to the catalyst component and/or activator alone or in combination. The catalyst system may include any number of catalyst components in any combination as described herein, as well as any activator in any combination as described herein.

[0021] As used herein, the phrase "catalyst compound" includes any compound that, once appropriately activated, is capable of catalyzing the polymerization or oligomerization of olefins.

[0022] As used herein, the phrase "leaving group" refers to one or more chemical moieties bound to the metal center of the catalyst component that can be abstracted from the catalyst component by an activator, thus producing the species active towards olefin polymerization or oligomerization. [0023] As used herein, a "hydrocarbyl" includes aliphatic, cyclic, olefinic, acetylenic and aromatic radicals (i.e., hydrocarbon radicals) comprising hydrogen and carbon that are deficient by one hydrogen. A "hydrocarbylene" is deficient by two hydrogens.

[0024] As used herein, an "alkyl" includes linear, branched and cyclic paraffin radicals that are deficient by one hydrogen. Thus, for example, a— CH3 group ("methyl") and a CH3CH2— group ("ethyl") are examples of alkyls.

[0025] As used herein, an "alkenyl" includes linear, branched and cyclic olefin radicals that are deficient by one hydrogen; alkynyl radicals include linear, branched and cyclic acetylene radicals deficient by one hydrogen radical.

[0026] As used herein, "aryl" groups include phenyl, naphthyl, pyridyl and other radicals whose molecules have the ring structure characteristic of benzene,

naphthylene, phenanthrene, anthracene, etc. It is understood that an "aryl' group can be a C6 to C20 aryl group. For example, a C6H5 - aromatic structure is an "phenyl", a C6H4 2- aromatic structure is an "phenylene". An "arylalkyl" group is an alkyl group having an aryl group pendant therefrom. It is understood that an "aralkyl" group can be a C7 to C20 aralkyl group. An "alkylaryl" is an aryl group having one or more alkyl groups pendant therefrom.

[0027] As used herein, an "alkyiene" includes linear, branched and cyclic hydrocarbon radicals deficient by two hydrogens. Thus,— CH 2 — ("methylene") and— CH 2 CH 2 — ("ethylene") are examples of alkyiene groups. Other groups deficient by two hydrogen radicals include "arylene" and "alkenylene".

[0028] As used herein, the phrase "heteroatom" includes any atom other than carbon and hydrogen that can be bound to carbon, and in one embodiment is selected from the group consisting of B, Al, Si, Ge, N, P, O, and S. A "heteroatom-containing group" is a hydrocarbon radical that contains a heteroatom and may contain one or more of the same or different heteroatoms, and from 1 to 3 heteroatoms in a particular embodiment. Non-limiting examples of heteroatom-containing groups include radicals of imines, amines, oxides, phosphines, ethers, ketones, oxoazo!ines heterocyclics, oxazoiines, thioethers, and the like.

[0029] As used herein, an "alkylcarboxyiate", "arylcarboxyiate", and

"alkylaryicarboxylate" is an alkyl, aryl, and alkylaryl, respectively, that possesses a carboxyl group in any position. Examples include CH 3 C(0)0 ~ , etc.

[0030] As used herein, an aralkyl group is defined to be a substituted aryl group. [0031] As used herein, the term "substituted" means that the group following that term possesses at least one moiety in place of one or more hydrogens in any position, the moieties selected from such groups as halogen radicals (esp., CI, F, Br), hydroxyl groups, carbonyl groups, carboxyl groups, amine groups, phosphine groups, alkoxy groups, phenyl groups, naphthyi groups, Ci to C 20 alkyl groups, C 2 to Ci 0 alkenyl groups, and combinations thereof. Examples of substituted alkyls and aryls includes, but are not limited to, acyl radicals, a!ky!amino radicals, alkoxy radicals, aryloxy radicals, alkylthio radicals, dialkylamino radicals, alkoxycarbonyl radicals, aryioxycarbonyl radicals, carbomoyl radicals, alkyl- and dialkyl-carbamoyl radicals, acyloxy radicals, acylamino radicals, aryiamino radicals, and combinations thereof.

[0032] Embodiments of the present disclosure include a new polymerization catalyst of the Formula I:

(Formula I)

[0033] wherein each of R to R 2 is independently a Ci to C 2 o alkyl, aryl or aralkyl group, or a hydrogen, wherein at least one of R 4 to R 7 is not a hydrogen, wherein M is a Group 4 metal, and wherein, each X is independently a halide, Ci to C 2 o alkyl, aralkyl or hydrogen. In various embodiments, each of R 9 , R 10, and Rn , and R 12 of Formula I can be a hydrogen. Further, in Formula I (and in Formulas I I, III, IV, V, IV, VI, VII, VIII, IX, and X) it is understood that the 'bottom' Cp ligand (i.e., "CP1" as referenced in Table 1) includes R 8 - R 2 while the 'top" Cp Ligand (i.e., "CP2") includes R - R 3 as shown in Figure 1.

[0034] In various embodiments, each of R 9 , R 0 , R and R 2 of Formula I can be a hydrogen. For instance, in some embodiments, the polymerization catalyst of Formula I can further comprise a zirconocene catalyst of:

(Formula V);

(Formula VI);

(Formula VII);

(Formula VIII);

(Formula IX);

(Formula X)

[0035] That is, in various embodiments, the polymerization catalyst of Formula I can comprise a polymerization catalyst of the Formula V, VI, VII, VIII, IX, X or a combination thereof. However, the disclosure is not so limited. Rather, various components of Formula V, VI, VII, VIII, IX, X, can be added, removed, and/or altered. For example, while Formula V, VI, VII, VIII, IX, X each illustrate M as being a zirconium atom is understood that X can be varied, for instance, to be a different compound selected from the group consisting of Groups 3 through 12 atoms and lanthanide Group atoms, among other possibilities. As illustrated in Formulas V, VI, VII, VIII, IX, and X, in various embodiments each of R 1 , R 2 , and R 3 can be a hydrogen.

[0036] In some embodiments adjacent R-groups may combine to form a ring.

For example, R 5 and R 6 of Formula I can together form a cycloalkyl group such as a cyclohexyl-1 , 1 ,4,4-tetramethyl, among other possible combinations of adjacent R to R 2 of Formula I and/or other possible types of rings.

[0037] In some embodiments, each of R 7 and R 4 can independently be a Ci to

C 2 o alkyl. For instance, R 8 is a Ci to C 20 alkyl and/or a Ci to C 3 alkyl, among other possibilities.

[0038] In some embodiments, each of R , R 2 R 3 of Formula I is a hydrogen.

Similarly, in some embodiment, each of R 5 and R 6 of Formula I is a hydrogen. As mentioned, "M" of the metallocene catalyst of Formula I can, in some embodiments be titanium, zirconium or hafnium. [0039] As mentioned, in various embodiments, the polymerization catalyst of

Formula I can be included in a bimodal polymerization catalyst system further including a non-metallocene catalyst.

[0040] Non-metallocene olefin polymerization catalyst Compounds

[0041] The non-metallocene olefin polymerization catalyst may be a Group 15 metal-containing catalyst compound. That is, the bimodal polymerization catalyst system can include one or more Group 15 metal-containing catalyst compounds. As used herein, these are termed non-metallocene olefin polymerization catalyst compounds. The Group 15 metal-containing compound generally includes a Group 3 to 14 metal atom, a Group 3 to 7, or a Group 4 to 6 metal atom. In many embodiments, the Group 15 metal-containing compound includes a Group 4 metal atom bound to at least one leaving group and also bound to at least two Group 15 atoms, at least one of which is also bound to a Group 15 or 16 atom through another group.

[0042] In one or more embodiments, at least one of the Group 15 atoms is also bound to a Group 15 or 16 atom through another group which may be a C1 to C20 hydrocarbon group, a heteroatom containing group, silicon, germanium, tin, lead, or phosphorus, where the Group 15 or 16 atom may also be bound to nothing or a hydrogen, a Group 14 atom containing group, a halogen, or a heteroatom containing group, and where each of the two Group 15 atoms are also bound to a cyclic group and can optionally be bound to hydrogen, a halogen, a heteroatom or a hydrocarbyl group, or a heteroatom containing group.

[0043] The Group 15-containing metal compounds can be described more particularly with structures (IX) or (X):

where M is a Group 3 to 12 transition metal or a Group 13 or 14 main group metal, a Group 4, 5, or 6 metal. In many embodiments, M is a Group 4 metal, such as zirconium, titanium, or hafnium. Each X is independently a leaving group, such as an anionic leaving group. The leaving group may include a hydrogen, a hydrocarbyl group, a heteroatom, a halogen, or an alkyi; y is 0 or 1 (when y is 0 group L' is absent). The term 'n' is the oxidation state of M. In various embodiments, n is +3, +4, or +5. In many embodiments, n is +4. The term 'm' represents the formal charge of the YZL or the YZL' ligand, and is 0, -1 , -2 or -3 in various embodiments. In many embodiments, m is -2. L is a Group 15 or 16 element, such as nitrogen or oxygen; L' is a Group 15 or 16 element or Group 14 containing group, such as carbon, silicon or germanium. Y is a Group 15 element, such as nitrogen or phosphorus. In many embodiments, Y is nitrogen. Z is a Group 15 element, such as nitrogen or phosphorus. In many embodiments, Z is nitrogen. R and R 2 are, independently, a Ci to C 20 hydrocarbon group, a heteroatom containing group having up to twenty carbon atoms, silicon, germanium, tin, lead, or phosphorus. In many embodiments, R and R 2 are a C 2 to C 20 alkyi, aryl or aralkyi group, such as a linear, branched or cyclic C 2 to C 20 alkyi group, or a C 2 to C 6 hydrocarbon group. R and R 2 may also be interconnected to each other. R 3 may be absent or may be a hydrocarbon group, a hydrogen, a halogen, a heteroatom containing group. In many embodiments, R 3 is absent, for example, if L is an oxygen, or a hydrogen, or a linear, cyclic, or branched alkyi group having 1 to 20 carbon atoms. R 4 and R 5 are independently an alkyi group, an aryl group, substituted aryl group, a cyclic alkyi group, a substituted cyclic alkyi group, a cyclic aralkyi group, a substituted cyclic aralkyi group, or multiple ring system, often having up to 20 carbon atoms. In many embodiments, R 4 and R 5 have between 3 and 10 carbon atoms, or are a Ci to C 20 hydrocarbon group, a Ci to C 20 aryl group or a Ci to C 20 aralkyi group, or a heteroatom containing group. R 4 and R 5 may be interconnected to each other. R 6 and R 7 are independently absent, hydrogen, an alkyi group, halogen, heteroatom, or a hydrocarbyl group, such as a linear, cyclic or branched alkyi group having 1 to 20 carbon atoms. In many embodiments, R 6 and R 7 are absent. R * may be absent, or may be a hydrogen, a Group 14 atom containing group, a halogen, or a heteroatom containing group.

[0044] By "formal charge of the YZL or YZL' ligand," it is meant the charge of the entire ligand absent the metal and the leaving groups X. By "R and R 2 may also be interconnected" it is meant that R and R 2 may be directly bound to each other or may be bound to each other through other groups. By "R 4 and R 5 may also be

interconnected" it is meant that R 4 and R 5 may be directly bound to each other or may be bound to each other through other groups.

[0045] In one or more embodiments, R 4 and R 5 are independently a group represented by the following structure (XI).

when R 4 and R 5 are independently an alkyl group, an aryl group, substituted aryl group, a cyclic alkyl group, a substituted cyclic alkyl group, a cyclic aralkyl group, a substituted cyclic aralkyl group, or multiple ring system, often having up to 20 carbon atoms. In many embodiments, R 4 and R 5 have between 3 and 10 carbon atoms, or are a Ci to C 2 o hydrocarbon group, a Ci to C 20 aryl group or a Ci to C 20 aralkyl group, or a heteroatom containing group. R 4 and R 5 may be interconnected to each other, R 8 to R 2 are each independently hydrogen, a Ci to C 40 alkyl group, a halide, a heteroatom, a heteroatom containing group containing up to 40 carbon atoms. In many embodiments, R 8 to R 2 are a Ci to C 20 linear or branched alkyl group, such as a methyl, ethyl, propyl, or butyl group. Any two of the R groups may form a cyclic group and/or a heterocyclic group. The cyclic groups may be aromatic. In one embodiment R 9 , R 0 and R 2 are independently a methyl, ethyl, propyl, or butyl group (including all isomers). In another embodiment, R 9 , R 0 and R 2 are methyl groups, and R 8 and R are hydrogen.

[0046] In one or more embodiments, R 4 and R 5 are both a group represented by the following structure (XI I) .

When R 4 and R 5 follow structure (XII), M is a Group 4 metal, such as zirconium, titanium, or hafnium. In many embodiments, M is zirconium. Each of L, Y, and Z may be a nitrogen. Each of R and R 2 may be -CH 2 -CH 2 -. R 3 may be hydrogen, and R 6 and R 7 may be absent.

[0047] Catalyst Forms

[0048] The bimodal polymerization catalyst system may include a catalyst component in a slurry, which may have an initial catalyst compound, and an added solution catalyst component that is added to the slurry. Generally, a non-metallocene olefin polymerization catalyst will be supported in the initial slurry, depending on solubility. However, in some embodiments, the initial catalyst component slurry may have no catalysts but may have an activator or support. In this case, two or more solution catalysts may be added to the slurry to cause each to be supported.

[0049] Any number of combinations of catalyst components may be used in embodiments. For example, the catalyst component slurry can include an activator and a support, or a supported activator. Further, the slurry can include a catalyst compound in addition to the activator and the support. As noted, the catalyst compound in the slurry may be supported.

[0050] The slurry may include one or more activators and supports, and one more catalyst compounds. For example, the slurry may include two or more activators (such as alumoxane and a modified alumoxane) and a catalyst compound, or the slurry may include a supported activator and more than one catalyst compounds. In one embodiment, the slurry includes a support, an activator, and two catalyst compounds. In another embodiment the slurry includes a support, an activator and two different catalyst compounds, which may be added to the slurry separately or in combination. The slurry, containing silica and alumoxane, may be contacted with a catalyst compound, allowed to react, and thereafter the slurry is contacted with another catalyst compound, for example, in a trim system. [0051] The molar ratio of metal in the activator to metal in the catalyst compound in the slurry may be 1000:1 to 0.5: 1 , 300: 1 to 1 :1 , or 150: 1 to 1 : 1. The slurry can include a support material which may be any inert particulate carrier material known in the art, including, but not limited to, silica, fumed silica, alumina, clay, talc or other support materials such as disclosed above. In one embodiment, the slurry contains silica and an activator, such as methyl aluminoxane ("MAO"), modified methyl aluminoxane

("MMAO"), as discussed further below.

[0052] One or more diluents or carriers can be used to facilitate the combination of any two or more components of the catalyst system in the slurry or in the trim catalyst solution. For example, the single site catalyst compound and the activator can be combined together in the presence of toluene or another non-reactive hydrocarbon or hydrocarbon mixture to provide the catalyst mixture. In addition to toluene, other suitable diluents can include, but are not limited to, ethylbenzene, xylene, pentane, hexane, heptane, octane, other hydrocarbons, or any combination thereof. The support, either dry or mixed with toluene can then be added to the catalyst mixture or the catalyst/activator mixture can be added to the support.

[0053] The catalyst is not limited to a slurry arrangement, as a mixed catalyst system may be made on a support and dried. The dried catalyst system can then be fed to the reactor through a dry feed system.

[0054] Support

[0055] As used herein, the terms "support" and "carrier" are used interchangeably and refer to any support material, including a porous support material, such as talc, inorganic oxides, and inorganic chlorides. The one or more single site catalyst compounds of the slurry can be supported on the same or separate supports together with the activator, or the activator can be used in an unsupported form, or can be deposited on a support different from the single site catalyst compounds, or any combination thereof. This may be accomplished by any technique commonly used in the art. There are various other methods in the art for supporting a single site catalyst compound. The single site catalyst compounds of the slurry can be spray dried. The support used with the single site catalyst compound can be functionalized, or at least one substituent or leaving group is selected. The support material may be any of the conventional support materials.

[0056] Preferably the supported material is a porous support material, for example, talc, an inorganic oxide, or an inorganic chloride. Other support materials include resinous support materials (e.g., polystyrene), functionalized or crosslinked organic supports, such as polystyrene divinyl benzene polyolefins or polymeric compounds, zeolites, clays, or any other organic or inorganic support material and the like, or mixtures thereof.

[0057] Preferred support materials are inorganic oxides that include those Group

2, 3, 4, 5, 13 or 14 metal oxides. The preferred supports include silica, fumed silica, alumina (WO 99/60033), silica-alumina and mixtures thereof. Other useful supports include magnesia, titania, zirconia, magnesium chloride (U.S. Patent No.5, 965, 477), montmorillonite (European Patent EP-BI 0 5 11 665), phyllosilicate, zeolites, talc, clays (U.S. Patent No. 6,034, 187) and the like. Also, combinations of these support materials may be used, for example, silica-chromium, silica- alumina, silica-titania and the like. Additional support materials may include those porous acrylic polymers described in EP 0 767 184 Bl.

[0058] Other support materials include nanocomposites as described in PCT

WO 99/47598, aerogels as described in WO 99/48605, spherulites as described in U.S. Patent No. 5,972,510 and polymeric beads as described in WO 99/5031 1. An example of a suitable support is fumed silica available under the trade name Cabosil™ TS- 610, or other TS- or TG-series supports, available from Cabot Corporation. Fumed silica is typically a silica with particles 7 to 30 nanometers in size that has been treated with dimethylsilyldichloride such that a majority of the surface hydroxyl groups are capped.

[0059] It is typically preferred that the support material, preferably an inorganic oxide, has a surface area in the range of from about 10 to about 700 m /g, pore volume in the range of from about 0.1 to about 4.0 cc/g and average particle size in the range of from about 5 to about 500 μηι. More preferably, the surface area of the support material is in the range of from about 50 to about 500 m /g, pore volume of from about 0.5 to about 3.5 cc/g and average particle size of from about 10 to about 200 μηι. Most preferably the surface area of the support material is in the range is from about 100 to about 400 m /g, pore volume from about 0.8 to about 3.0 cc/g and average particle size is from about 5 to about 100 μηι. The average pore size of the carrier typically has pore size in the range of from 10 to IOOOA, preferably 50 to about 500A, and most preferably 75 to about 350A.

[0060] The support materials may be treated chemically, for example with a fluoride compound as described in WO 00/12565. Other supported activators are described in for example WO 00/13792 that refers to supported boron containing solid acid complex.

[0061] In a method of forming a supported catalyst composition component, the amount of liquid in which the activator is present is in an amount that is less than four times the pore volume of the support material, more preferably less than three times, even more preferably less than two times; preferred ranges being from 1.1 times to 3.5 times range and most preferably in the 1.2 to 3 times range. In an alternative embodiment, the amount of liquid in which the activator is present is from one to less than one times the pore volume of the support material utilized in forming the supported activator. Procedures for measuring the total pore volume of a porous support are well known in the art

[0062] Activator

[0063] As used herein, the term "activator" may refer to any compound or combination of compounds, supported, or unsupported, which can activate a single site catalyst compound or component, such as by creating a cationic species of the catalyst component. For example, this can include the abstraction of at least one leaving group (the "X" group in the single site catalyst compounds described herein) from the metal center of the single site catalyst compound/component. The activator may also be referred to as a "co-catalyst".

[0064] For example, the activator can include a Lewis acid or a non-coordinating ionic activator or ionizing activator, or any other compound including Lewis bases, aluminum alkyls, and/or conventional-type co-catalysts. In addition to

methylaluminoxane ("MAO") and modified methylaluminoxane ("MMAO") mentioned above, illustrative activators can include, but are not limited to, aluminoxane or modified aluminoxane, and/or ionizing compounds, neutral or ionic, such as tri (n- butyl)ammonium tetrakis(pentafluorophenyl)boron, a trisperfluorophenyl boron metalloid precursor, a trisperfluoronaphthyl boron metalloid precursor, or any combinations thereof.

[0065] Aluminoxanes can be described as oligomeric aluminum compounds having -AI(R)-0- subunits, where R is an alkyl group. Examples of aluminoxanes include, but are not limited to MAO, MMAO, ethylaluminoxane, isobutylaluminoxane, or a combination thereof. Aluminoxanes can be produced by the hydrolysis of the respective trialkylaluminum compound. MMAO can be produced by the hydrolysis of

trimethylaluminum and a higher trialkylaluminum, such as triisobutylaluminum. MMAOs are generally more soluble in aliphatic solvents and more stable during storage. There are a variety of methods for preparing aluminoxane and modified aluminoxanes.

[0066] As noted above, one or more organo-aluminum compounds such as one or more alkylaluminum compounds can be used in conjunction with the aluminoxanes. For example, alkylaluminum species that may be used are diethylaluminum ethoxide, diethylaluminum chloride, and/or diisobutylaluminum hydride. Examples of

trialkylaluminum compounds include, but are not limited to, trimethylaluminum, triethylaluminum ("TEAL"), triisobutylaluminum ("TiBAI"), tri-n-hexylaluminum, tri-n- octylaluminum, tripropylaluminum, tributylaluminum, and the like.

[0067] Catalyst Component Solution

[0068] The catalyst component solution may include only a catalyst compound, such as a zirconocene, or may include an activator in addition to the catalyst compound. The catalyst solution used in the trim process can be prepared by dissolving the catalyst compound and optional activators in a liquid solvent. The liquid solvent may be an alkane, such as a C5 to C30 alkane, or a C5 to C10 alkane. Cyclic alkanes such as cyclohexane and aromatic compounds such as toluene may also be used. In addition, mineral oil may be used as a solvent. The solution employed should be liquid under the feed conditions to the polymerization reactor, and relatively inert. In one embodiment, the liquid utilized in the catalyst compound solution is different from the diluent used in the catalyst component slurry. In another embodiment, the liquid utilized in the catalyst compound solution is the same as the diluent used in the catalyst component solution.

[0069] If the catalyst solution includes both activator and catalyst compound, the ratio of metal in the activator to metal in the catalyst compound in the solution may be 1000: 1 to 0.5: 1 , 300:1 to 1 :1 , or 150: 1 to 1 :1. In various embodiments, the activator and catalyst compound are present in the solution at up to about 90 wt. %, at up to about 50 wt. %, at up to about 20 wt. %, up to about 10 wt. %, at up to about 5 wt. %, at less than 1 wt. %, or between 100 ppm and 1 wt. %, based upon the weight of the solvent and the activator or catalyst compound.

[0070] The catalyst component solution can comprise any one of the soluble catalyst compounds described in the catalyst section herein. As the catalyst is dissolved in the solution, a higher solubility is desirable. Accordingly, the catalyst compound in the catalyst component solution may often include a metallocene, which may have higher solubility than other catalysts. [0071] In the polymerization process, described below, any of the above described catalyst component containing solutions may be combined with any of the catalyst component containing slurry/slurries described above. In addition, more than one catalyst component solution may be utilized.

[0072] Continuity Additive/Static Control Agent

[0073] In gas-phase polyethylene production processes, it may be desirable to use one or more static control agents to aid in regulating static levels in the reactor. As used herein, a static control agent is a chemical composition which, when introduced into a fluidized bed reactor, may influence or drive the static charge (negatively, positively, or to zero) in the fluidized bed. The specific static control agent used may depend upon the nature of the static charge, and the choice of static control agent may vary dependent upon the polymer being produced and the single site catalyst compounds being used.

[0074] Control agents such as aluminum stearate may be employed. The static control agent used may be selected for its ability to receive the static charge in the fluidized bed without adversely affecting productivity. Other suitable static control agents may also include aluminum distearate, ethoxlated amines, and anti-static compositions such as those provided by Innospec Inc. under the trade name OCTASTAT. For example, OCTASTAT 2000 is a mixture of a polysulfone copolymer, a polymeric polyamine, and oil-soluble sulfonic acid.

[0075] The aforementioned control agents and other control agents may be employed either alone or in combination as a control agent. For example, the carboxylate metal salt may be combined with an amine containing control agent (e.g., a carboxylate metal salt with any family member belonging to the KEMAMINE® (available from Crompton Corporation) or ATMER® (available from ICI Americas Inc.) family of products).

[0076] Other useful continuity additives include ethyleneimine additives useful in embodiments disclosed herein may include polyethyleneimines having the following general formula:

- (CH 2 - CH 2 - NH) n - , in which n may be from about 10 to about 10,000. The polyethyleneimines may be linear, branched, or hyperbranched (e.g., forming dendritic or arborescent polymer structures). They can be a homopolymer or copolymer of ethyleneimine or mixtures thereof (referred to as polyethyleneimine(s) hereafter).

Although linear polymers represented by the chemical formula -[CH2-CH2-NH]- may be used as the polyethyleneimine, materials having primary, secondary, and tertiary branches can also be used. Commercial polyethyleneimine can be a compound having branches of the ethyleneimine polymer.

[0077] Suitable polyethyleneimines are commercially available from BASF

Corporation under the trade name Lupasol. These compounds can be prepared as a wide range of molecular weights and product activities. Examples of commercial polyethyleneimines sold by BASF suitable for use in the present invention include, but are not limited to, Lupasol FG and Lupasol WF.

[0078] Another useful continuity additive can include a mixture of aluminum distearate and an ethoxylated amine-type compound, e.g., IRGASTAT AS-990, available from Huntsman (formerly Ciba Specialty Chemicals). The mixture of aluminum distearate and ethoxylated amine type compound can be slurried in mineral oil e.g., Hydrobrite 380. For example, the mixture of aluminum distearate and an ethoxylated amine type compound can be slurried in mineral oil to have total slurry concentration of ranging from about 5 wt. % to about 50 wt. % or about 10 wt. % to about 40 wt. %, or about 15 wt. % to about 30 wt. %. Other static control agents and additives are applicable.

[0079] The continuity additive(s) or static control agent(s) may be added to the reactor in an amount ranging from 0.05 to 200 ppm, based on the weight of all feeds to the reactor, excluding recycle. In some embodiments, the continuity additive may be added in an amount ranging from 2 to 100 ppm, or in an amount ranging from 4 to 50 ppm.

[0080] Gas Phase Polymerization Reactor

[0081] Figure 1 is a schematic of a gas-phase reactor system, showing the addition of a polymerization catalyst system. The catalyst component slurry (e.g., slurry including a catalyst of Working Example 1 , Working Example, 2, Working Example, 3, Working Example 4, Working Example 5, and/or Working Example 6) such as those of preferably a mineral oil slurry including at least one support and at least one activator, at least one supported activator, and optional catalyst compounds (e.g., an optional non- metallocene catalyst) may be placed in a vessel or catalyst pot (cat pot) 102. In one embodiment, the cat pot 102 is an agitated holding tank designed to keep the solids concentration homogenous. A catalyst component solution, prepared by mixing a solvent and at least one catalyst compound (e.g., an optional non-metallocene catalyst and/or a zirconocene catalyst) and/or activator, is placed in another vessel, which can be termed a trim pot 104. The catalyst component slurry can then be combined in-line with the catalyst component solution to form a final catalyst composition. A nucleating agent such as silica, alumina, fumed silica or any other particulate matter may be added to the slurry and/or the solution in-line or in the vessels 102 or 104. Similarly, additional activators or catalyst compounds may be added in-line. For example, a second catalyst slurry that includes a different catalyst may be introduced from a second cat pot. The two catalyst slurries may be used as the catalyst system with or without the addition of a solution catalyst from the trim pot.

[0082] The catalyst component slurry and solution can be mixed in-line. For example, the solution and slurry may be mixed by utilizing a static mixer 108 or an agitating vessel (not shown). The mixing of the catalyst component slurry and the catalyst component solution should be long enough to allow the catalyst compound in the catalyst component solution to disperse in the catalyst component slurry such that the catalyst component, originally in the solution, migrates to the supported activator originally present in the slurry. The combination forms a uniform dispersion of catalyst compounds on the supported activator forming the catalyst composition. The length of time that the slurry and the solution are contacted is typically up to about 220 minutes, such as about 1 to about 60 minutes, about 5 to about 40 minutes, or about 10 to about 30 minutes.

[0083] In an embodiment, an aluminum alkyl, an ethoxylated aluminum alkyl, an aluminoxane, an anti-static agent or a borate activator, such as a C1 to C15 alkyl aluminum (for example tri-isobutyl aluminum, trimethyl aluminum or the like), a C1 to C15 ethoxylated alkyl aluminum or methyl aluminoxane, ethyl aluminoxane,

isobutylaluminoxane, modified aluminoxane or the like are added to the mixture of the slurry and the solution in line. The alkyls, antistatic agents, borate activators and/or aluminoxanes may be added from an alkyl vessel 1 10 directly to the combination of the solution and the slurry, or may be added via an additional alkane (such as isopentane, hexane, heptane, and or octane) carrier stream, for example, from a hydrocarbon vessel 112. The additional alkyls, antistatic agents, borate activators and/or aluminoxanes may be present at up to about 500 ppm, at about 1 to about 300 ppm, at 10 to about 300 ppm, or at about 10 to about 100 ppm. Carrier streams that may be used include isopentane and or hexane, among others. The carrier may be added to the mixture of the slurry and the solution, typically at a rate of about 0.5 to about 60 Ibs/hr (27 kg/hr). Likewise, a carrier gas 114, such as nitrogen, argon, ethane, propane, and the like, may be added in-line to the mixture of the slurry and the solution. Typically, the carrier gas may be added at the rate of about 1 to about 100 Ib/hr (0.4 to 45 kg/hr), or about 1 to about 50 Ib/hr (5 to 23 kg/hr), or about 1 to about 25 Ib/hr (0.4 to 1 1 kg/hr).

[0084] In another embodiment, a liquid carrier stream is introduced into the combination of the solution and slurry that is moving in a downward direction. The mixture of the solution, the slurry and the liquid carrier stream may pass through a mixer or length of tube for mixing before being contacted with a gaseous carrier stream.

[0085] Similarly, a comonomer 116, such as hexene, another alpha-olefin, or diolefin, may be added in-line to the mixture of the slurry and the solution. The slurry/solution mixture is then passed through an injection tube 120 to a reactor 122. In some embodiments, the injection tube may aerosolize the slurry/solution mixture. Any number of suitable tubing sizes and configurations may be used to aerosolize and/or inject the slurry/solution mixture.

[0086] In one embodiment, a gas stream 126, such as cycle gas, or re-cycle gas

124, monomer, nitrogen, or other materials is introduced into a support tube 128 that surrounds the injection tube 120. To assist in proper formation of particles in the reactor 122, a nucleating agent such as fumed silica, can be added directly into the reactor 122.

[0087] When a metallocene catalyst or other similar catalyst is used in the gas phase reactor, oxygen or fluorobenzene can be added to the reactor 122 directly or to the gas stream 126 to control the polymerization rate. Thus, when the zirconocene catalyst (which is sensitive to oxygen or fluorobenzene) is used in combination with another catalyst (that is not sensitive to oxygen) in a gas phase reactor, oxygen can be used to modify the zirconocene polymerization rate relative to the polymerization rate of the other catalyst. The addition of water or carbon dioxide to gas phase polymerization reactors, for example, may be applicable for similar purposes. In one embodiment, the contact temperature of the slurry and the solution is in the range of from 0 °C to about 80 °C, from about 0 °C to about 60 °C, from about 10 °C, to about 50 °C, and from about 20 °C to about 40 °C.

[0088] The examples above are not limiting, as additional solutions and slurries may be included. For example, a slurry can be combined with two or more solutions having the same or different catalyst compounds and or activators. Likewise, the solution may be combined with two or more slurries each having the same or different supports, and the same or different catalyst compounds and or activators. Similarly, two or more slurries combined with two or more solutions, preferably in-line, where the slurries each comprise the same or different supports and may comprise the same or different catalyst compounds and or activators and the solutions comprise the same or different catalyst compounds and or activators. For example, the slurry may contain a supported activator and two different catalyst compounds, and two solutions, each containing one of the catalysts in the slurry, are each independently combined, in-line, with the slurry.

[0089] Use of Catalyst Composition to Control Product Properties

[0090] As described in embodiments herein, appropriate selection of the catalysts and ratios may be used to adjust the MWD, short chain branch distribution (SCBD), and long-chain branch distribution (LCBD) of the polymer, for example, to provide a polymer with a broad orthogonal composition distribution (BOCD). The MWD, SCBD, and LCBDs would be controlled by combining catalysts with the appropriate weight average molecular weight (Mw), comonomer incorporation, and long chain branching (LCB) formation under the conditions of the polymerization. For instance, in various embodiments the weight average molecular weight of the low molecular weight polyethylene component can be from 5,000 to 35,000 grams/mole (g/mol) and/or the weight average molecular weight of the high molecular weight polyethylene component is from 400,000 to 700,000 g/mol. However, other values are possible depending upon an intended application, etc. For instance, in some embodiments, the polyethylene (comprised of the high and/or low molecular weight polyethylene) can have a weight average molecular weight from 5,000 to 250,000 g/mol.

[0091] Employing multiple pre-catalysts that are co-supported on a single support mixed with an activator, such as a silica methylaluminoxane (SMAO), can provide a cost advantage by making the product in one reactor instead of multiple reactors. Further, using a single support also facilitates intimate mixing of the polymers and offers improved operability relative to preparing a mixture of polymers of different Mw and density independently from multiple catalysts in a single reactor. As used herein, a pre-catalyst is a catalyst compound prior to exposure to activator.

[0092] The density of a polyethylene copolymer provides an indication of the incorporation of comonomer into a polymer, with lower densities indicating higher incorporation. The difference in the densities of the low molecular weight (LMW) component and the high molecular weight (HMW) component can be greater than about 0.02, or greater than about 0.04, with the HMW component having a lower density than the LMW component. These factors can be adjusted by controlling the molecular weight distribution (MWD) and SCBD, which, in turn, can be adjusted by changing the relative amount of the two pre-catalysts on the support. This may be adjusted during the formation of the pre-catalysts, for example, by supporting two catalysts on a single support. In some embodiments, the relative amounts of the pre-catalysts can be adjusted by adding one of the components to a polymerization catalyst and/or a catalyst mixture such as a bimodal polymerization catalyst system en-route to the reactor in a process termed "trim". Feedback of polymer property data can be used to control the amount of catalyst addition. Metallocenes (MCNs) such as zirconocenes are known to trim well with other catalysts.

[0093] The properties of the product polymer may be controlled by adjusting the timing, temperature, concentrations, and sequence of the mixing of the solution, the slurry and any optional added materials (nucleating agents, catalyst compounds, activators, etc.) described above. The MWD, melt index, relative amount of polymer produced by each catalyst, and other properties of the polymer produced may also be changed by manipulating process parameters. Any number of process parameters may be adjusted, including manipulating hydrogen concentration in the polymerization system, changing the amount of a first catalyst in the polymerization system, and/or changing the amount of the second catalyst in the polymerization system. Other process parameters that can be adjusted include changing the relative ratio of the catalyst in the polymerization process (and optionally adjusting their individual feed rates to maintain a steady or constant polymer production rate). The concentrations of reactants in the reactor 122 can be adjusted by changing the amount of liquid or gas that is withdrawn or purged from the process, changing the amount and/or composition of a recovered liquid and/or recovered gas returned to the polymerization process, where the recovered liquid or recovered gas can be recovered from polymer discharged from the polymerization process. Further concentration parameters that can be adjusted include changing the polymerization temperature, changing the ethylene partial pressure in the polymerization process, changing the ethylene to comonomer ratio in the polymerization process, changing the activator to transition metal ratio in the activation sequence. Time dependent parameters may be adjusted, such as changing the relative feed rates of the slurry or solution, changing the mixing time, the temperature and or degree of mixing of the slurry and the solution in-line, adding different types of activator compounds to the polymerization process, and adding oxygen or fluorobenzene or other catalyst poison to the polymerization process. Any combinations of these adjustments may be used to control the properties of the final polymer product.

[0094] In one embodiment, the MWD of the polymer product is measured at regular intervals and one of the above process parameters, such as temperature, catalyst compound feed rate, the ratios of the two or more catalysts to each other, the ratio of comonomer to monomer, the monomer partial pressure, and or hydrogen concentration, is altered to bring the composition to the desired level, if necessary. The MWD may be measured by size exclusion chromatography (SEC), e.g., gel permeation chromatography (GPC), among other techniques.

[0095] In one embodiment, a polymer product property is measured in-line and in response the ratio of the catalysts being combined is altered. In one embodiment, the molar ratio of the catalyst compound in the catalyst component slurry to the catalyst compound in the catalyst component solution, after the slurry and solution have been mixed to form the final catalyst composition, is 500:1 to 1 :500, or 100:1 to 1 : 100, or 50:1 to 1 :50 or 40: 1 to 1 :10. In another embodiment, the molar ratio of a non-metallocene catalyst compound in the slurry to a zirconocene catalyst compound in the solution, after the slurry and solution have been mixed to form the catalyst composition, is 500: 1 , 100: 1 , 50: 1 , 10:1 , or 5: 1. The product property measured can include the dynamic shear viscosity, flow index, melt index, density, MWD, comonomer content, and combinations thereof. In another embodiment, when the ratio of the catalyst compounds is altered, the introduction rate of the catalyst composition to the reactor, or other process parameters, is altered to maintain a desired production rate.

[0096] Polymerization Process

[0097] The polymerization catalysts of Formula V-X and bimodal polymerization catalyst systems including the polymerization catalyst of Formula V-X can be used to polymerize one or more olefins to provide one or more polymer products therefrom. Any suitable polymerization process can be used, including, but not limited to, high pressure, solution, slurry, and/or gas phase polymerization processes. In embodiments that use other techniques besides gas phase polymerization, modifications to a catalyst addition system that are similar to those discussed with respect to Fig. 1 can be used. For example, a trim system may be used to feed catalyst to a loop slurry reactor for polyethylene copolymer production.

[0098] The terms "polyethylene" and "polyethylene copolymer" refer to a polymer having at least 50 wt. % ethylene-derived units. In various embodiments, the polyethylene can have at least 70 wt. % ethylene-derived units, at least 80 wt. % ethylene-derived units, at least 90 wt. % ethylene-derived units, or at least 95 wt. % ethylene-derived units. The polyethylene polymers described herein are generally copolymer, but may also include terpolymers, having one or more other monomeric units. As described herein, a polyethylene can include, for example, at least one or more other olefins or comonomers. Suitable comonomers can contain 3 to 16 carbon atoms, from 3 to 12 carbon atoms, from 4 to 10 carbon atoms, and from 4 to 8 carbon atoms. Examples of comonomers include, but are not limited to, propylene, 1-butene, 1- pentene, 1-hexene, 1-heptene, 1-octene, 4-methylpent-1-ene, 1-decene, 1-dodecene, 1- hexadecene, and the like.

[0099] Referring again to Fig. 1 , the fluidized bed reactor 122 can include a reaction zone 132 and a velocity reduction zone 134. The reaction zone 132 can include a bed 136 that includes growing polymer particles, formed polymer particles and a minor amount of catalyst particles fluidized by the continuous flow of the gaseous monomer and diluent to remove heat of polymerization through the reaction zone. Optionally, some of the re-circulated gases 124 can be cooled and compressed to form liquids that increase the heat removal capacity of the circulating gas stream when readmitted to the reaction zone. A suitable rate of gas flow can be readily determined by experimentation. Make-up of gaseous monomer to the circulating gas stream can be at a rate equal to the rate at which particulate polymer product and monomer associated therewith is withdrawn from the reactor and the composition of the gas passing through the reactor can be adjusted to maintain an essentially steady state gaseous composition within the reaction zone. The gas leaving the reaction zone 132 can be passed to the velocity reduction zone 134 where entrained particles are removed, for example, by slowing and falling back to the reaction zone 132. If desired, finer entrained particles and dust can be removed in a separation system such as a cyclone and/or fines filter. The gas 124 can be passed through a heat exchanger 140 where at least a portion of the heat of polymerization can be removed. The gas can then be compressed in a compressor 142 and returned to the reaction zone 132. Additional reactor details and means for operating the reactor 122 are applicable.

[00100] The reactor temperature of the fluid bed process can be greater than about 30°C, about 40°C, about 50°C, about 90°C, about 100°C, about 110°C, about 120°C, about 150°C, or higher. In general, the reactor temperature is operated at the highest feasible temperature taking into account the sintering temperature of the polymer product within the reactor. Thus, the upper temperature limit in one embodiment is the melting temperature of the polyethylene copolymer produced in the reactor. For instance, in some embodiments the polyethylene having the improved ethylene enchainment can a melt temperature of from 90 to 136 degrees Celsius or from 90 to 134 degrees Celsius, among other possibilities. However, higher temperatures may result in narrower MWDs, which can be improved by the addition of other co-catalysts, as described herein.

[00101] Hydrogen gas can be used in olefin polymerization to control the final properties of the polyolefin, such as described in the "Polypropylene Handbook," at pages 76-78 (Hanser Publishers, 1996). Using certain catalyst systems, increasing concentrations (partial pressures) of hydrogen can increase the flow index (Fl), or melt index (Ml) of the polyethylene copolymer generated. The flow index can thus be influenced by the hydrogen concentration. The amount of hydrogen in the

polymerization can be expressed as a mole ratio relative to the total polymerizable monomer, for example, ethylene, or a blend of ethylene and hexene or propylene.

[00102] The amount of hydrogen used in the polymerization process can be an amount necessary to achieve the desired flow index of the final polyolefin polymer. For example, the mole ratio of hydrogen to total monomer (H2: monomer) can be greater than about 0.0001 , greater than about 0.0005, or greater than about 0.001. Further, the mole ratio of hydrogen to total monomer (H2: monomer) can be less than about 10, less than about 5, less than about 3, and less than about 0.10. A desirable range for the mole ratio of hydrogen to monomer can include any combination of any upper mole ratio limit with any lower mole ratio limit described herein. Expressed another way, the amount of hydrogen in the reactor at any time can range to up to about 5,000 ppm, up to about 4,000 ppm in another embodiment, up to about 3,000 ppm, or between about 50 ppm and 5,000 ppm, or between about 50 ppm and 2,000 ppm in another embodiment. The amount of hydrogen in the reactor can range from a low of about 1 ppm, about 50 ppm, or about 100 ppm to a high of about 400 ppm, about 800 ppm, about 1 ,000 ppm, about 1 ,500 ppm, or about 2,000 ppm, based on weight. Further, the ratio of hydrogen to total monomer (H2:monomer) can be about 0.00001 : 1 to about 2: 1 , about 0.005: 1 to about 1.5: 1 , or about 0.0001 : 1 to about 1 : 1. The one or more reactor pressures in a gas phase process (either single stage or two or more stages) can vary from 690 kPa (100 psig) to 3,448 kPa (500 psig), in the range from 1 ,379 kPa (200 psig) to 2,759 kPa (400 psig), or in the range from 1 ,724 kPa (250 psig) to 2,414 kPa (350 psig). [00103] The gas phase reactor can be capable of producing from about 10 kg of polymer per hour (25 Ibs/hr) to about 90,900 kg/hr (200,000 Ibs/hr), or greater, and greater than about 455 kg/hr (1 ,000 Ibs/hr), greater than about 4,540 kg/hr (10,000 Ibs/hr), greater than about 11 ,300 kg/hr (25,000 Ibs/hr), greater than about 15,900 kg/hr (35,000 Ibs/hr), and greater than about 22,700 kg/hr (50,000 Ibs/hr), and from about 29,000 kg/hr (65,000 Ibs/hr) to about 45,500 kg/hr (100,000 Ibs/hr).

[00104] As noted, a slurry polymerization process can also be used in

embodiments. A slurry polymerization process generally uses pressures in the range of from about 101 kPa (1 atmosphere) to about 5,070 kPa (50 atmospheres) or greater, and temperatures in the range of from about 0°C to about 120°C, and more particularly from about 30°C to about 100°C. In a slurry polymerization, a suspension of solid, particulate polymer can be formed in a liquid polymerization diluent medium to which ethylene, comonomers, and hydrogen along with catalyst can be added. The

suspension including diluent can be intermittently or continuously removed from the reactor where the volatile components are separated from the polymer and recycled, optionally after a distillation, to the reactor. The liquid diluent employed in the

polymerization medium can be an alkane having from 3 to 7 carbon atoms, such as, for example, a branched alkane. The medium employed should be liquid under the conditions of polymerization and relatively inert. When a propane medium is used the process should be operated above the reaction diluent critical temperature and pressure. In one embodiment, a hexane, isopentane, or isobutane medium can be employed. The slurry can be circulated in a continuous loop system.

[00105] A number of tests can be used to compare resins from different sources, catalyst systems, and manufacturers. Such tests can include melt index, high load melt index, melt index ratio, density, dies swell, environmental stress crack resistance, and many others. Results of tests runs on resins made in embodiments described herein are presented in the examples section.

[00106] As used herein, Mn is number average molecular weight, Mw is weight average molecular weight, and Mz is z average molecular weight, wt% is weight percent, and mol% is mole percent.

[00107] Mw, Mn and Mw/Mn are determined by using a High Temperature Gel Permeation Chromatography (Polymer Laboratories), equipped with a differential refractive index detector (DRI). Three Polymer Laboratories PLgel 10μηι Mixed-B columns are used. The nominal flow rate is 1.0 mL/min, and the nominal injection volume is 300 μΙ_. The various transfer lines, columns, and differential refractometer (the DRI detector) are contained in an oven maintained at 160°C. Solvent for the experiment is prepared by dissolving 6 grams of butylated hydroxytoluene as an antioxidant in 4 liters of Aldrich reagent grade 1 , 2, 4 trichlorobenzene (TCB). The TCB mixture is then filtered through a 0.1 μηι Teflon filter. The TCB is then degassed with an online degasser before entering the GPC instrument. Polymer solutions are prepared by placing dry polymer in glass vials, adding the desired amount of TCB, then heating the mixture at 160 °C with continuous shaking for about 2 hours. All quantities are measured gravimetrically. The injection concentration is from 0.5 to 2.0 mg/ml, with lower concentrations being used for higher molecular weight samples. Prior to running each sample the DRI detector is purged. Flow rate in the apparatus is then increased to 1.0 ml/minute, and the DRI is allowed to stabilize for 8 hours before injecting the first sample. The molecular weight is determined by combining universal calibration relationship with the column calibration which is performed with a series of

monodispersed polystyrene (PS) standards. The MW is calculated at each elution volume with following equation:

where the variables with subscript "X" stand for the test sample while those with subscript "PS" stand for PS. In this method, a ps = 0.67 and K ps = 0.000175 while a x and K x ate obtained from published literature. Specifically, a/K = 0.695/0.000579 for PE and 0.705/0.0002288 for PP.

[00108] The concentration, c, at each point in the chromatogram is calculated from the baseline-subtracted DRI signal, I QRI, using the following equation:

c = K DRl'DRI /(dn/dc)

where K^py is a constant determined by calibrating the DRI, and (dn/dc) is the refractive index increment for the system. Specifically, dn/dc = 0.109 for polyethylene.

[00109] The mass recovery is calculated from the ratio of the integrated area of the concentration chromatography over elution volume and the injection mass which is equal to the pre-determined concentration multiplied by injection loop volume.

[00110] All molecular weights are reported in g/mol unless otherwise noted. In event of conflict between the GPC-DRI procedure and the "Rapid GPC," the GPC-DRI procedure immediately above shall be used. Further details regarding methods of determining Mw, Mn, MWD are described in US 2006/0173123 page 24-25, paragraphs [0334] to [0341].

[0011 1] Catalyst productivity (i.e., Cat Prod) (grams polymer/gram catalyst-hour) can be determined as a ratio of an amount of polymer produce to an amount of catalyst added to the reactor.

[00112] Melt temperature (i.e., Tm) can be determined via Differential Scanning Calorimetry according to ASTM D 3418-08. For instance, using a scan rate of 10° C./min on a sample of 10 mg and using the second heating cycle.

[00113] The product polyethylene can have a melt index ratio (MIR or 121/12) ranging from about 10 to less than about 300, or, in many embodiments, from about 15 to about 150. Flow index (Fl, HLMI, or 121 can be measured in accordance with ASTM D1238 (190°C, 21.6 kg). The melt index (Ml, I2) can be measured in accordance with ASTM D1238 (at 190°C, 2.16 kg weight). The melt index (Ml, I5) can be measured in accordance with ASTM D1238 (190°C, 5 kg). Another melt index (Ml, 121) can be measured in accordance with ASTM D1238 (190°C, 21.6 kg).

[00114] Density can be determined in accordance with ASTM D-792. Density is expressed as grams per cubic centimeter (g/cm3) unless otherwise noted. The polyethylene can have a density ranging from a low of about 0.89 g/cm3, about 0.90 g/cm3, or about 0.91 g/cm3 to a high of about 0.95 g/cm3, about 0.96 g/cm3, or about 0.97 g/cm3. The polyethylene can have a bulk density, measured in accordance with ASTM D1895 method B, of from about 0.25 g/cm3 to about 0.5 g/cm3. For example, the bulk density of the polyethylene can range from a low of about 0.30 g/cm3, about 0.32 g/cm3, or about 0.33 g/cm3 to a high of about 0.40 g/cm3, about 0.44 g/cm3, or about 0.48 g/cm3. In some embodiments, the bimodal polyethylene composition can have a density of 0.940 gram/cubic centimeters or more.

[00115] The polyethylene (e.g., a HDPE) can be suitable for such articles as films, fibers, nonwoven and/or woven fabrics, extruded articles, and/or molded articles.

Examples of films include blown or cast films formed in single layer extrusion, coextrusion, or lamination useful as shrink film, cling film, stretch film, sealing films, oriented films, snack packaging, heavy duty bags, grocery sacks, baked and frozen food packaging, medical packaging, industrial liners, membranes, etc. in food-contact and non-food contact applications, agricultural films and sheets. Examples of fibers include melt spinning, solution spinning and melt blown fiber operations for use in woven or non- woven form to make filters, diaper fabrics, hygiene products, medical garments, geotextiles, etc. Examples of extruded articles include tubing, medical tubing, wire and cable coatings, pipe, geomembranes, and pond liners. Examples of molded articles include single and multi-layered constructions by injection molding or rotation molding or blow molding processes in the form of bottles, tanks, large hollow articles, rigid food containers and toys, etc.

[00116] All numerical values are "about" or "approximately" the indicated value, and take into account experimental error and variations that would be expected by a person having ordinary skill in the art. Further, various terms have been defined above. To the extent a term used in a claim is not defined above, it should be given the broadest definition persons in the pertinent art have given that term as reflected in at least one printed publication or issued patent. All patents, test procedures, and other documents cited in this application are fully incorporated by reference to the extent such disclosure is not inconsistent with this application and for all jurisdictions in which such incorporation is permitted.

[00117] While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention can be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow.

[00118] EXAMPLES

[00119] Sample Catalyst Preparation

[00120] The polymerization catalyst used in the Comparative Examples and Examples summarized in Table 1 below were made by a process identical to or similar to the following sample catalyst preparation process.

[00121] Comparative Example 1 : Preparation of Spray Dried Polymerization Catalysts:

[00122] Comparative Example 1 : The metallocene compound representative of Formula I is purchased from Boulder Scientific Company.

[00123] A comparative polymerization catalyst system is prepared by slurrying 5.30 g of treated fumed silica (Cabosil TS-610) in 125 g of toluene, followed by addition of a 10 % solution (44 g) by weight of MAO in toluene. Next, the catalyst compound of Formula I is added and the mixture is stirred for 30-60 minutes. The resulting mixture of Formula I (below) is introduced into an atomizing device, producing droplets that are then contacted with a hot nitrogen gas stream to evaporate the liquid and form a powder. The powder is separated from the gas mixture in a cyclone separator and discharged into a container. The spray drier temperature is set at 165 °C and the outlet temperature at 60-70 °C. The product collected is a fine powder. Catalyst compound loadings are kept at a constant 50 umol/g, corresponding to a AI:Zr ratio of about 100. The spray dried product of Comparative Example 1 is then used as a polymerization catalyst using the equipment and under conditions described herein.

[00124] (Formula I)

[00125] Comparative Example 2: A comparative polymerization catalyst is prepared similar to Comparative Example 1 but with a catalyst compound of Formula II. A metallocene compound representative of Formula II is prepared by the following procedure:

[00126] Indene (15.0 ml_) is dissolved in hexane (200 ml_) and BuLi (88.4 ml_,

1.6M in hexanes) is added slowly. After stirring overnight, the white precipitate is collected by filtration, washed with hexane, and dried in vacuo to yield 15.25g of indenyllithium. Indenyllithium (0.485 g) is slurried in ether (150 ml_) and

(nPrCp)ZrCI 3 (DME) (1.569 g) is added. After stirring three hours, the reaction mixture is filtered and solvents removed from the filtrate in vacuo. Dichloromethane (40 ml_) is added, the mixture filtered and then solvent removed from the filtrate in vacuo to yield the product as a yellow solid (1.431 g). The spray dried product of Comparative Example 2 is then used as a polymerization catalyst using the equipment and under conditions described herein.

[00127] (Formula II)

[00128] Comparative Example 3: A polymerization catalyst is prepared similar to Comparative Example 1 but with a catalyst compound of Formula III. A metallocene compound representative of Formula III is prepared by the following procedure: 2-Methylindene (2.43 g, 18.6 mmol) is dissolved in hexanes (50 mL) in a 100 mL glass jar equipped with a stir bar. To this stirred solution is added a solution of n-butyllithium in hexanes (1.6 M, 12.8 mL, 21 mmol) slowly at room temperature. The reaction is allowed to stir at room temperature for five hours, and the resultant white precipitate is collected by vacuum filtration, washed with hexanes, and dried under vacuum to yield 2- methylindenyllithium as a white solid (2.50 g, 98.4%). A 20 mL glass jar equipped with a stir bar is charged with a solution of 2-methylindenyllithium (0.321 g, 2.36 mmol) in diethyl ether (12 mL). ("PrCp)ZrCI 3 - DME (0.930 g, 2.36 mmol) is added, resulting in immediate formation of a bright yellow solution and precipitate. The mixture is stirred for three days then filtered, and the filtrate is concentrated under vacuum. The resultant yellow solids are triturated with hexanes and dried under vacuum to give ("PrCpJ^-Me- lnd)ZrCI 2 as a bright yellow solid product.

[00129] The spray dried product of Comparative Example 3 is then used as a polymerization catalyst using the equipment and under conditions described herein.

Pr

[00130] (Formula III)

[00131] Comparative Example 4 (CE 4: A polymerization catalyst is prepared similar to Comparative Example 1 but with the new catalyst compound of Formula IV. A metallocene compound representative of Formula IV is prepared by the following procedure:

[00132] Indene (15.0 mL) is dissolved in hexane (200 mL) and BuLi (88.4 mL,

1.6M in hexanes) is added slowly. After stirring overnight, the white precipitate is collected by filtration, washed with hexane, and dried in vacuo to yield 15.25g of indenyllithium.

[00133] Indenyllithium (6.64 g) is slurried in ether (70 mL) and cooled to -40 °C. lodomethane (4.1 mL) is added, and the reaction stirred overnight as it warms to room temp. Volatiles are removed in vacuo, and hexane (100 mL) is added to the residue. After filtering, butyllithium (35.7 mL, 1.6M in hexanes) is added to the filtrate and the mixture stirred overnight as a white precipitate develops. The white solid is collected by filtration, washed with hexane, and dried to yield 4.932 g of 1-methylindenyllithium. 1- Methylindenyllithium (2.40 g) is dissolved in THF (40 mL) and cooled to -40 °C. Methyl iodide (1.40 mL) is added slowly, and the reaction mixture is allowed to warm to room temperature overnight. Volatiles are removed in vacuo, and ether (100 mL) and water (100 mL) are added. The organic layer is separated, washed with brine (50 mL), dried over MgS0 4 and filtered. Removal of volatiles in vacuo yields 2.255g of a mixture comprising about 93 mol% 1 ,3-dimethylindene, and about 7 mol% 3,3-dimethylindene. The dimethylindene mixture (2.25 g) is dissolved in hexane (40 mL), butyllithium (10.8 mL, 1.6M in hexane) is added, and the reaction mixture stirred for several days. A white solid is collected by filtration, washed with hexane, and dried in vacuo to yield 1.961g of 1 ,3-dimethylindenyllithium. 1 ,3-Dimethylindenyllithium (1.948g) and (PrCp)ZrCI 3 (dme) (4.760g) are combined in ether (90 mL) and stirred for 2.5 hr. Solvents are removed in vacuo to yield a bright yellow solid. After extracting into dichloromethane (150 mL) and filtering, solvents removed from the filtrate in vacuo to yield 4.660g of (PrCp)(1 ,3- Me 2 lnd)ZrCI 2 . The spray dried product of Comparative Example 4 is then used as a polymerization catalyst using the equipment and under conditions described herein.

r

[00134] (Formula IV)

[00135] Working Example 1 (WE 1): A polymerization catalyst is prepared similar to Comparative Example 1 but with the new catalyst compound of Formula V. A new metallocene compound representative of Formula V is prepared by the following procedure:

[00136] 4,7-Dimethylindene is prepared by one of two methods (Method A or Method B).

[00137] Method A. A 500 mL two-necked round bottomed flask equipped with a magnetic stir bar, a powder addition funnel containing aluminum chloride (16.04 g, 120.3 mmol), a nitrogen inlet, and an outlet which purges to a NaOH scrubber is flushed with dry nitrogen gas. The vessel is charged with anhydrous dichloromethane (70 mL) followed by p-xylene (14.91 g, 140.5 mmol) and 3-chloropropionyl chloride (13.35 g, 105.1 mmol) and then cooled using an ice water bath. Aluminum chloride is then added over 90 min via the powder addition funnel, then the vessel is warmed to 10°C and allowed to stir for 2 hr. The bright red reaction mixture is poured onto ice, resulting in a color change from red to yellow. The organic layer is separated and washed three times with water, dried over anhydrous magnesium sulfate, filtered, and condensed under vacuum to form the crude intermediate as a yellow liquid. The intermediate is added into a flask containing sulfuric acid (60 ml_) via syringe over a period of 30 min., and the solution is slowly heated to 65°C and held at this temperature for two hr., resulting in gas evolution and appearance of a dark brown color. The solution is cooled to room temperature, poured over ice, and extracted with diethyl ether (100 ml_). The organic layer is washed with sodium bicarbonate solution and water, dried over anhydrous magnesium sulfate, and condensed under vacuum to afford the crude product as a tan colored solid. Purification by column chromatography (Si0 2 , hexanes:ethyl acetate = 90: 10) gives 4,7-dimethylindan-1-one as a light yellow/tan colored solid (11.82 g, 70.43 %). A 500 ml_ two-necked round bottom flask equipped with a magnetic stir bar, removable cap, and reflux condenser with attached nitrogen inlet is charged with 4,7- dimethylindan-1-one (8.040 g, 50.18 mmol), methanol (150 ml_) and THF (50 ml_). The solution is cooled using an ice bath to an internal temperature of 5°C. To the stirring solution is added sodium borohydride (1.96 g, 51.81 mmol) portion wise via the removable cap over a period of 60 min, allowing gas evolution to cease between each addition. The resulting solution is allowed to warm to room temperature and stir overnight (17 h). The reaction mixture is quenched by the addition of ice, concentrated under vacuum, and extracted with ethyl acetate. The organic layer is separated, dried over anhydrous magnesium sulfate, filtered and concentrated to give 4,7-dimethylindan- 1-ol as a tan solid (7.56 g, 93.3 %). A 1000 ml_ round bottomed flask equipped with a magnetic stir bar and reflux condenser with attached nitrogen inlet is charged with 4,7- dimethylindan-1-ol (8.56 g, 52.8 mmol), toluene (800 ml_), and p-toluene sulfonic acid (p- TSA) (0.188 g, 0.99 mmol). The solution is heated at 45°C, and reaction progress is monitored closely by GC/MS. After 4 hr, molecular sieves are added to the reaction mixture, and heating is continued. After 6 hr, the reaction is quenched with saturated sodium bicarbonate solution. The organic layer is separated, dried over anhydrous magnesium sulfate, filtered and concentrated to afford the crude product as light yellow liquid. Purification by column chromatography (Si0 2 , hexanes) produces 4,7-dimethyl- 1 H-indene as a colorless liquid (5.68 g, 74.7 %). Alternatively, 4,7-dimethyl-1 H-indene is prepared according to the following method: [00138] Method B. A 3-neck round bottom flask is charged with a solution of sodium methoxide in methanol (5 M, 170.5 mL, 852.5 mmol) and cooled to 0 °C degrees. Cyclopentadiene (34.3 mL, 511.5 mmol) that has been freshly cracked and distilled is added over 20 minutes. The reaction mixture is stirred at 0 °C for about 2 hours under a nitrogen atmosphere. 2,5-Hexanedione (40 mL, 340.9 mmol) is added dropwise using an addition funnel over 30 minutes. The reaction is stirred overnight at ambient temperature. The volatiles are removed in vacuo, and water (150 mL) and ether (250 mL) are added. The organic and aqueous layers are separated and the aqueous layer extracted twice with 50 mL of diethyl ether. The organic layer is washed with saturated sodium chloride, dried over magnesium sulfate and the solvent is removed in vacuo. The product is purified by distillation (bp. 65 °C, 0.01 mmHg) to afford 4,7- dimethylindene as a pale yellow oil (35 g, 71 % yield). The remaining synthetic steps may be performed using 4,7-dimethylindene obtained from either of Method A or Method B.

[00139] 4,7-Dimethyl-1 H-indene (5.60 g, 39.4 mmol) is dissolved in hexanes (100 mL) in a 200 mL glass jar equipped with a stir bar. To this stirred solution is added a solution of n-butyllithium in hexanes (2.5 M, 17 mL, 43 mmol) slowly at room

temperature. The reaction is allowed to stir at room temperature 17 hr, and the resultant white precipitate is collected by vacuum filtration, washed with hexanes, and dried under vacuum to yield of 4,7-dimethylindenyllithium as an off-white solid (5.27 g, 90.4 %). A 110 mL glass jar equipped with a stir bar is charged with a solution of 4,7- dimethylindenyllithium (0.683 g, 4.13 mmol) in diethyl ether (80 mL). ("PrCpJZrC DME (1.64 g, 4.16 mmol) is added, resulting in immediate formation of a bright yellow solution and precipitate. The mixture is stirred 18 hours, then diluted with dichloromethane (15 mL) and filtered through a 0.45 ml syringe filter. The filtrate is concentrated under vacuum to give "PrCp)(4,7-Me 2 -lnd)ZrCl 2 as a bright yellow solid (1.53 g, 89.6 %). The spray dried product of Working Example 1 is then used as a polymerization catalyst using the equipment and under conditions described herein.

[00140] (Formula V) [00141] Working Example 2 (WE 2): A polymerization catalyst is prepared similar to Comparative Example 1 but with the catalyst compound of Formula VI. A new metallocene compound representative of Formula VI is prepared by the following procedure: Outside of the glovebox, a 500 mL two-necked round bottomed flask equipped with a magnetic stir bar, a powder addition funnel containing aluminum chloride (26.6 g, 199 mmol), a nitrogen inlet, and an outlet which purges to a NaOH scrubber is flushed with dry nitrogen gas. The vessel is charged with anhydrous o- dichlorobenzene (250 mL) followed by 1 , 1 ,4,4-tetramethyl-1 ,2,3,4-tetrahydronaphthalene (25.00 g, 132.8 mmol) and acryloyl chloride (12.02 g, 132.8 mmol) and then cooled using an ice water bath. Aluminum chloride is added over 30 min via the powder addition funnel, then the vessel is warmed to room temperature. After stirring 1 hr at room temperature, the dark red solution is heated to 70 °C and allowed to react for 6 hours. The solution is then cooled to room temperature and poured over ice (-300 g) containing cone. HCI (15 mL). The biphasic mixture is transferred to a separatory funnel; the layers are separated, and the aqueous layer extracted with dichloromethane (300 mL) then ethyl acetate (300 mL). Combined organic fractions are washed with water (200 mL) and brine (200 mL), dried over anhydrous magnesium sulfate, filtered, and concentrated under vacuum. Reaction solvent is removed by distillation under high vacuum, leaving a viscous, sticky, red residue. Hexane is added, and the resultant yellow precipitate collected by filtrationandchromatographed (Si0 2 , hexanes -> 5% hexanes in EtOAc). then purified further by vacuum sublimation (100 °C, 0.1 torr) to give 5,5,8,8-tetramethyl- 2,3,5,6,7,8-hexahydro-1 H-cyclopenta[b]naphthalen-1-one as a white solid (6.86 g, 21.3 %). A 250 mL round bottom flask equipped with a magnetic stir bar is charged with 5,5,8,8-tetramethyl-2,3,5,6,7,8-hexahydro-1 H-cyclopenta[b]naphthalen-1-one (6.83 g, 28.2 mmol), methanol (45 mL) and THF (90 mL). The solution is cooled using an ice bath, and sodium borohydride (1.6 g, 42 mmol) is added in portions over 15 minutes, allowing gas evolution to cease between each addition. The reaction mixture is warmed to room temperature over 1 hour then concentrated under vacuum. Water (50 mL) and diethyl ether (100 mL) are added, and the layers separated. The organic layer is dried over anhydrous magnesium sulfate, filtered and concentrated to give 5,5,8,8- tetramethyl-2,3,5,6,7,8-hexahydro-1 H-cyclopenta[b]naphthalen-1-ol as a white solid (6.80 g, 98.8 %).

[00142] A 1000 mL round bottomed flask equipped with a magnetic stir bar is charged with 5,5,8,8-tetramethyl-2,3,5,6,7,8-hexahydro-1 H-cyclopenta[b]naphthalen-1-ol (6.80 g, 27.8 mmol), toluene (500 mL), and p-toluenesulfonic acid (0.188 g, 0.99 mmol). The solution is held at 60 °C for 3.5 hours then cooled and quenched with saturated sodium bicarbonate solution. The organic layer is separated, dried over anhydrous magnesium sulfate, filtered and concentrated to afford the crude product as yellow oily solid. The solid is recrystallized from chloroform (25 mL) and methanol (10 ml) to give 5,5,8,8-tetramethyl-5,6,7,8-tetrahydro-1 H-cyclopenta[b]naphthalene as a white solid. Additional product is isolated from the mother liquor by column chromatography (Si0 2 , hexanes) (combined yield 4.19 g, 66.4 %).

[00143] 5,5,8,8-tetramethyl-5,6,7,8-tetrahydro-1 H-cyclopenta[b]naphthalene) (2.87 g, 12.7 mmol) is dissolved in hexanes (50 mL) in a 1 10 mL glass jar equipped with a stir bar. To this stirred solution is added a solution of n-butyllithium in hexanes (1.6 M, 8.7 mL, 14 mmol) slowly at room temperature. The reaction is allowed to stir at room temperature 24 hr, and the resultant white precipitate is collected by vacuum filtration, washed with hexanes, and dried under vacuum to yield the lithium 5,5,8,8-tetramethyl- 5,6,7,8-tetrahydro-1 H-cyclopenta[b]naphthalenide as a white solid (2.62 g, 88.8 %).

[00144] A 30 mL glass vial equipped with a stir bar is charged with a solution of lithium 5,5,8,8-tetramethyl-5,6,7,8-tetrahydro-1 H-cyclopenta[b]naphthalenide (0.500 g, 2.15 mmol) in diethyl ether (10 mL). ("PrCp)ZrCI 3 (0.850 g, 2.15 mmol) is added, resulting in formation of a precipitate. The mixture is stirred 3 days, , then filtered through a 0.2 m syringe filter. The filtrate is concentrated under vacuum. The resultant yellow solids are recrystallized from dichloromethane and hexane to give ("PrCp){5,5,8,8- tetramethyl-5,6,7,8-tetrahydro-1 H-cyclopenta[b]naphthalenide}ZrCI 2 as a bright yellow solid (0.703 g, 66.1 %). The spray dried product of Working Example 2 is then used as a polymerization catalyst using the equipment and under conditions described herein.

[00145]

[00146] (Formula VI)

[00147] Working Example 3 (WE 3): A polymerization catalyst is prepared similar to Comparative Example 1 but with the catalyst of Formula VII. A new metallocene compound representative of Formula VII is prepared by the following procedure: 4,7-Dimethylindenylithium is prepared as described in Working Example 1. A 200 mL glass jar equipped with a stir bar is charged with a solution of 4,7-dimethylindenylithium (0.800 g, 5.33 mmol) in diethyl ether (100 mL). (MeCp)ZrCI 3 DME (1.95 g, 5.34 mmol) is added, resulting in immediate formation of a bright yellow solution and precipitate. The mixture is stirred 17 hours, then diluted with dichloromethane (20 mL) and filtered through a 0.45 μηι syringe filter. The filtrate is concentrated under vacuum, and the resultant yellow solid suspended in hexane (100 mL) and collected by vacuum filtration. The crude residue is recrystallized first from diethyl ether (20 mL) and dichloromethane (10 mL), and then from toluene (40 mL) and hexanes (10 mL). The crystals are collected and dried under vacuum to give (MeCp)(4,7-Me 2 -lnd)ZrCI 2 as a bright yellow solid (0.471 g, 23.1 %). The spray dried product of Working Example 3 is then used as a

polymerization catalyst using the equipment and under conditions described herein.

[00148] (Formula VII)

[00149] Working Example (WE 4): A polymerization catalyst is prepared similar to Comparative Example 1 but with the catalyst of Formula VIII. A new metallocene compound representative of Formula VIII is prepared by the following procedure:

[00150] 4,7-dimethylindenylithium is prepared as described in Working Example 1. A 200 mL glass jar equipped with a stir bar is charged with a solution of 4,7- dimethylindenylithium (2.33 g, 15.5 mmol) in diethyl ether (100 mL). CpZrCI 3 DME (5.50 g, 15.6 mmol) and additional diethyl ether (20 mL) are added, resulting in formation of a precipitate. The mixture is stirred 17 hours, then diluted with dichloromethane (40 mL) and filtered. The filtrate is concentrated under vacuum, and the resultant yellow solid was dissolved in dichloromethane (80 mL) and filtered. Concentration of the filtrate under vacuum gives (Cp)(4,7-Me 2 -lnd)ZrCI 2 as a bright yellow solid (3.72 g, 65.1 %). The spray dried product of Working Example 4 is then used as a polymerization catalyst using the equipment and under conditions described herein.

[00151] (Formula VIII)

[00152] Working Example 5 (WE 5): A polymerization catalyst is prepared similar to Comparative Example 1 but with the new catalyst of Formula IX. A metallocene compound representative of Formula VII is prepared by the following procedure:

[00153] Lithium 5,5,8,8-tetramethyl-5,6,7,8-tetrahydro-1 H

cyclopenta[b]naphthalenide is prepared as described in Working Example 2. A 30 mL glass vial equipped with a stir bar is charged with a solution of lithium 5,5,8,8- tetramethyl-5,6,7,8-tetrahydro-1 H-cyclopenta[b]naphthalenide (0.650 g, 2.80 mmol) in diethyl ether (15 mL). (MeCp)ZrCI 3 (0.774 g, 2.80 mmol) is added, resulting in formation of a precipitate, then DME (5 mL) is added, and the color is observed to change from orange to yellow. The mixture is stirred for 24 hours then filtered through a 0.2 μηι syringe filter. The filtrate is concentrated under vacuum. The resultant yellow solids are recrystallized from dichloromethane at room temperature by slow mixing of a hexane layer. The product is collected, washed with hexane, and dried under vacuum to give (MeCp){5,5,8,8-tetramethyl-5,6,7,8-tetrahydro-1 H-cyclopenta[b]naphthalenide})ZrCI 2 as a bright yellow solid (0.80 g, 61 %). The spray dried product of Working Example 5 is then used as a polymerization catalyst using the equipment and under conditions described herein.

[00154] (Formula IX)

[00155] Working Example 6 (WE 6): A polymerization catalyst is prepared similar to Comparative Example 1 but with the new catalyst of Formula X. A metallocene compound representative of Formula X is prepared by the following procedure: Lithium 5,5,8,8-tetramethyl-5,6,7,8-tetrahydro-1 H-cyclopenta[b]naphthalenide is prepared as described in Example 6. [00156] A 30 ml_ glass vial equipped with a stir bar is charged with a solution of lithium 5,5,8,8-tetramethyl-5,6,7,8-tetrahydro-1 H-cyclopenta[b]naphthalenide (0.670 g, 2.88 mmol) in diethyl ether (15 ml_). CpZrCI 3 (0.758 g, 2.88 mmol) is added, resulting in immediate formation of an orange solution and precipitate, then DME is added (5 ml_), resulting in a color change from orange to yellow. The mixture is stirred 24 hours then filtered through a 0.2 μηι syringe filter. The filtrate is concentrated under vacuum, and the residual solids are triturated with hexane (10 ml_) and dried under vacuum to give (Cp){5,5,8,8-tetramethyl-5,6,7,8-tetrahydro-1 H-cyclopenta[b]naphthalenide})ZrCI 2 as a bright yellow solid (0.80 g, 61 %). The spray dried product of Working Example 6 is then used as a polymerization catalyst using the equipment and under conditions described herein.

[00157] (Formula X)

[00158] Polymerization Process for CE 1 , 2, 3, 4 and WE 1 , 2, 3, 4, 5, 6.

[00159] The gas phase reactor employed is a 2 liter, stainless steel autoclave equipped with a mechanical agitator. For the experimental runs, the reactor is first dried for 1 hour, charged with 400 g of NaCI and dried by heating at 105 °C under nitrogen for 30 minutes. After baking out the reactor, 5 g of SMAO (silica supported

methylalumoxane) was introduced as a scavenger under nitrogen pressure. After adding SMAO, the reactor is sealed and components are stirred. The reactor is charged with hydrogen sufficient to produce a concentration of 1500 ppm at the reaction conditions, and hexene to produce a ratio of hexene to ethylene of 0.004 at reaction conditions. The reactor is pressurized with ethylene (total pressure = 220 psi). Once the system reaches a steady state, the catalyst is charged into the reactor to start polymerization. The reactor temperature is brought to 100 °C and maintained at this temperature throughout the experiment run. The polymerization is carried out for 60 minutes then the reactor is cooled, vented and opened. The resulting product mixture is washed with water, methanol and dried. The activity (grams polymer/gram catalyst-hour) can be determined as a ratio of polymer yield to the amount of catalyst added to the reactor.

[00160] TABLE 1- Data for CE 1 , 2, 3, 4 and WE 1 , 2, 3, 4, 5, 6. Cat

CP1 CP2 I2 Mn Mw Tm (C °)

Prod

CE

PrCp Me4Cp 6692 117 10,725 28,447 132.1

1

CE

PrCp Ind 7838 143 5,810 20,468 130.7

2

CE

PrCp 2-Melnd 5909 367 3,838 20,725 128.1

3

CE 1 ,3-

PrCp 5510 184 5,016 25,683 130.4

4 Me2lnd

WE 4,7-

PrCp 18395 857 6,943 22,767 131.1

1 Me2lnd

WE Me4-

PrCp 9006 857 6,764 20,614 133.6

2 566lnd

WE 4,7-

MeCp 33961 55 — — 130.1

3 Me2lnd

WE 4,7- 4 Cp 32166 198 — — 130.6

Me2lnd

WE Me4-

MeCp 4275 198 — — 132.7

5 566lnd

WE Me4-

Cp 3493 161 — — 131.8

6 566lnd

[00161] As shown in Table 1 with regard to Working Examples 1-6, surprisingly, it has been found that both high ethylene enchainment (as evidenced by melt temperature) and high catalyst productivity can be obtained for metallocenes that have less than five total substituents on the cyclopentadienyl rings, by incorporating substituents in positions more remote from the metal center. Not wishing to be bound by theory, the more remote substituents may sterically hinder the approach of oolefin comonomers without significantly slowing the approach of ethylene.

[00162] The effects of remote substituent patterns are illustrated by the results in Table 1 with respect to Working Examples 1-6. That is, including alkyl (e.g.., methyl) or other substituents on the five-membered ring of the indenyl substituent may adversely affect catalyst productivity, and in fact, lends no enhancement of ethylene enchainment or even decreases it. For example, Comparative Example 3 is deficient in productivity and/or ethylene enchainment when compared to each of Working Examples 1-6. In contrast, substituents at more remote positions such as in Working Examples 1-6 display enhanced polymerization activity or ethylene enchainment or both. For instance, Working Examples 3 and 4 have particularly high productivities when compared to each of Comparative Examples 1-4.