ARTICLES MADE FROM THE POLYMER

Field of Invention

The instant invention relates to a polyolefin polymerization process, semi-crystalline ethylene -based polymer made therefrom, and articles made from the polymer.

Background of the Invention

Metallocene-catalyzed polymers have been commercial for several years, and are used in many end-use applications, such as packaging, personal hygiene, automotive, flooring, adhesives, fibers, nonwovens, films, sheets, and fabrics.

Polymerization processes utilizing metallocene catalysts, including constrained geometry catalysts (CGC), to make polyolefin elastomers (POE) and/or polyolefin plastomers (POP) under reaction conditions that give high catalyst efficiency frequently become unstable. Modified methylalumoxane (MMA03A), an impurity scavenger, is usually added in a fixed ratio to the CGC catalyst, and therefore, only a very small amount of MMA03A is added under high efficiency, i.e. low catalyst level, conditions. Therefore, any variation in impurity levels in the feed during the polymerization process may cause a loss of reaction.

POE and POP polymerization processes exhibiting stability and/or efficiency over a range of feed impurity would be desirable.

Summary of the Invention

The instant invention is a polyolefin polymerization process, semi-crystalline ethylene -based polymer made therefrom, and articles made from the polymer.

In one embodiment, the instant invention provides a polymerization process comprising: (A) polymerizing ethylene and optionally one or more a-olefms in the presence of a catalyst to form a semi-crystalline ethylene-based polymer in at least one reactor; the catalyst comprising an organometallic catalyst thereby forming an ethylene-based polymer composition in the at least one reactor, wherein the catalyst is a metal complex of a polyvalent aryloxyether corresponding to the formula:

where M ³ is Ti, Hf or Zr, preferably Zr; Ar ⁴ is independently in each occurrence a substituted C9- ₂₀ aryl group, wherein the substituents, independently in each occurrence, are selected from the group consisting of alkyl; cycloalkyl; and aryl groups; and halo-, trihydrocarbylsilyl- and halohydrocarbyl- substituted derivatives thereof, with the proviso that at least one substituent lacks co-planarity with the aryl group to which it is attached; T ⁴ is independently in each occurrence a C ₂ - ₂₀ alkylene, cycloalkylene or cycloalkenylene group, or an inertly substituted derivative thereof; R ²¹ is independently in each occurrence hydrogen, halo, hydrocarbyl, trihydrocarbylsilyl, trihydrocarbylsilylhydrocarbyl, alkoxy or di(hydrocarbyl)amino group of up to 50 atoms not counting hydrogen; R ³ is independently in each occurrence hydrogen, halo, hydrocarbyl, trihydrocarbylsilyl, trihydrocarbylsilylhydrocarbyl, alkoxy or amino of up to 50 atoms not counting hydrogen, or two R ³ groups on the same arylene ring together or an R ³ and an R ²¹ group on the same or different arylene ring together form a divalent ligand group attached to the arylene group in two positions or join two different arylene rings together; and R ^D is independently in each occurrence halo or a hydrocarbyl or trihydrocarbylsilyl group of up to 20 atoms not counting hydrogen, or 2 R ^D groups together are a hydrocarbylene, hydrocarbadiyl, diene, or poly(hydrocarbyl)silylene group; wherein step (A) is conducted in the presence of from 5 to 20 mmol/m ³ triethylaluminum; and wherein step (A) is conducted in the presence of one or both of the following conditions: (i) from greater than 0: 1 to 65 : 1 molar ratio of triethylaluminum to the catalyst; and (ii) from 0.1 :0 to 5 : 1 molar ratio of triethylaluminum to modified methylalumoxane.

Brief Description of the Drawings

For the purpose of illustrating the invention, there is shown in the drawings a form that is exemplary; it being understood, however, that this invention is not limited to the precise

arrangements and instrumentalities shown. Fig. 1 is a graph illustrating reactor instability with polymerization in the presence of MMAO only; and

Fig. 2 is a graph illustrating reactor stability with polymerization in the presence of MMAO in combination with 10 mmol/m3 of TEA.

Detailed Description of the Invention

The instant invention is a polyolefm polymerization process, semi-crystalline ethylene -based polymer made therefrom, and articles made from the polymer.

The polymerization process according to the present invention comprises: (A) polymerizing ethylene and optionally one or more α-olefms in the presence of a catalyst to form a semi-crystalline ethylene-based polymer in at least one reactor; the catalyst comprising an organometallic catalyst thereby forming an ethylene-based polymer composition in the at least one reactor, wherein the catalyst is a metal complex of a olyvalent aryloxyether corresponding to the formula:

where M ³ is Ti, Hf or Zr, preferably Zr; Ar ⁴ is independently in each occurrence a substituted C9-20 aryl group, wherein the substituents, independently in each occurrence, are selected from the group consisting of alkyl; cycloalkyl; and aryl groups; and halo-, trihydrocarbylsilyl- and halohydrocarbyl- substituted derivatives thereof, with the proviso that at least one substituent lacks co-planarity with the aryl group to which it is attached; T ⁴ is independently in each occurrence a C2-20 alkylene, cycloalkylene or cycloalkenylene group, or an inertly substituted derivative thereof; R ²¹ is independently in each occurrence hydrogen, halo, hydrocarbyl, trihydrocarbylsilyl,

trihydrocarbylsilylhydrocarbyl, alkoxy or di(hydrocarbyl)amino group of up to 50 atoms not counting hydrogen; R ³ is independently in each occurrence hydrogen, halo, hydrocarbyl, trihydrocarbylsilyl, trihydrocarbylsilylhydrocarbyl, alkoxy or amino of up to 50 atoms not counting hydrogen, or two R ³ groups on the same arylene ring together or an R ³ and an R ²¹ group on the same or different arylene ring together form a divalent ligand group attached to the arylene group in two positions or join two different arylene rings together; and R is independently in each occurrence halo or a hydrocarbyl or trihydrocarbylsilyl group of up to 20 atoms not counting hydrogen, or 2 R ^D groups together are a hydrocarbylene, hydrocarbadiyl, diene, or poly(hydrocarbyl)silylene group; wherein step (A) is conducted in the presence of from 5 to 20 mmol/m ³ triethylaluminum; and wherein step (A) is conducted in the presence of one or both of the following conditions: (i) from greater than 0: 1 to 65 : 1 molar ratio of triethylaluminum to the catalyst; and (ii) from 0.1 :0 to 5 : 1 molar ratio of triethylaluminum to modified methylalumoxane.

Such polyvalent aryloxyether metal complexes and their synthesis are described in WO 2007/136496 or WO 2007/136497, using the synthesis procedures disclosed in US-A-2004/0010103. Among the preferred polyvalent aryloxyether metal complexes are those disclosed as example 1 in WO 2007/136496 and as example A10 in WO 2007/136497. Suitable cocatalysts and

polymerization conditions for use of the preferred polyvalent aryloxyether metal complexes are also disclosed in WO 2007/136496 or WO 2007/136497.

As used in the present invention, modified methylaluminoxane and triethylaluminum are used solely as impurity scavengers.

A solution-phase polymerization process may be used in certain embodiments of the inventive process. Typically, such a process occurs in a well-mixed reactor such as a loop reactor or a sphere reactor at temperature from about 130 to about 300 °C, preferably from about 150 to about 200 °C, and at pressures from about 30 to about 1000 psi, preferably from about 30 to about 750 psi. The residence time in such a process is typically from about 2 to about 20 minutes, preferably from about 10 to about 20 minutes. Ethylene, solvent, catalyst, and one or more comonomers are fed continuously to the reactor. Exemplary solvents include, but are not limited to, isoparaffins. For example, such solvents are commercially available under the name ISOPAR E from ExxonMobil Chemical Co., Houston, Texas. The resultant mixture of ethylene-based polymer and solvent is then removed from the reactor and the polymer is isolated. Solvent is typically recovered via a solvent recovery unit, that is, heat exchangers and vapor liquid separator drum, and is recycled back into the polymerization system. In yet other embodiments of the inventive process, the process may proceed in any suitable reactor system, such as slurry polymerization system.

All individual values and subranges from 5 to 20 mmol/m ³ triethylaluminum are included herein and disclosed herein; for example, the amount of triethylaluminum present in step (A) can be from a lower limit of 5, 8, 11, 14, 17 or 19 mmol/m ³ to an upper limit of 6, 9, 12, 15, 18 or 20 mmol/m ³ . For example, the amount of triethylaluminum present in step (A) may be in the range of from 5 to 20 mmol/m ³ , or in the alternative, the amount of triethylaluminum present in step (A) may be in the range of from 10 to 20 mmol/m ³ , or in the alternative, the amount of triethylaluminum present in step (A) may be in the range of from 5 to 10 mmol/m ³ , or in the alternative, the amount of triethylaluminum present in step (A) may be in the range of from 8 to 18 mmol/m ³ , or in the alternative, the amount of triethylaluminum present in step (A) may be in the range of from 9 to 14 mmol/m ³ .

In an alternative embodiment, the instant invention provides a process, in accordance with any of the preceding embodiments, except that step (A) is conducted in the presence of only one of the following conditions: (i) from greater than 0: 1 to 65: 1 molar ratio of triethylaluminum to the catalyst; and (ii) from 0.1 :0 to 5:1 molar ratio of triethylauminum to modified methylalumoxane.

In one alternative embodiment, step (A) is conducted solely in the presence of (i) from greater than 0: 1 to 65 : 1 molar ratio of triethylaluminum to the catalyst. In yet another alternative embodiment, step (A) is conducted solely in the presence of (ii) from 0.1 :0 to 5 : 1 molar ratio of triethylauminum to modified methylalumoxane.

In an alternative embodiment, the instant invention provides a process, in accordance with any of the preceding embodiments, except that step (A) is conducted in the presence of both of the following conditions: (i) from greater than 0: 1 to 65: 1 molar ratio of triethylaluminum to the catalyst; and (ii) from 0.1 :0 to 5:1 molar ratio of triethylauminum to modified methylalumoxane.

In those embodiments in which step (A) is conducted in the presence of from greater than 0: 1 to 65 : 1 molar ratio of triethylaluminum to the catalyst, all individual values and subranges from 0: 1 to 65 : 1 molar ratio of triethylaluminum to the catalyst are included herein and disclosed herein; for example, the molar ratio of triethylaluminum to the catalyst can be from a lower limit of 0.1 :1, 10:1 , 20: 1, 30: 1, 40: 1, 50: 1, or 60: 1 to an upper limit of 5 :1, 151, 25 :1, 35: 1, 45: 1, 55: 1, or 65 :1. For example, the molar ratio of triethylaluminum to the catalyst may be in the range of from 0.1 : 1 to 65 : 1 , or in the alternative, the molar ratio of triethylaluminum to the catalyst may be in the range of from 10: 1 to 50: 1, or in the alternative, the molar ratio of triethylaluminum to the catalyst may be in the range of from 0.05 : 1 to 25 : 1 , or in the alternative, the molar ratio of triethylaluminum to the catalyst may be in the range of from 40: 1 to 65 : 1 , or in the alternative, the molar ratio of

triethylaluminum to the catalyst may be in the range of from 1 : 1 to 30 : 1. In those embodiments in which step (A) is conducted in the presence of from 0.1 :0 to 5 : 1 molar ratio of triethylaluminum to modified methylalumoxane, all individual values and subranges from 0.1 :0 to 5 : 1 molar ratio of triethylaluminum to modified methylalumoxane are included herein and disclosed herein; for example, the molar ratio of triethylaluminum to modified methylalumoxane can be from a lower limit of 0.1 : 1, 0.5: 1, 1.1 : 1, 2:1 , 3.2: 1, 4.5: 1, or 4.9: 1 to an upper limit of 0.2: 1, 0.8:1, 1.5: 1, 2.2: 1, 3.5: 1, 4.7: 1 or 5: 1. For example, the molar ratio of triethylaluminum to modified methylalumoxane may be in the range of from 0.1 :0 to 5 : 1 , or in the alternative, the molar ratio of triethylaluminum to modified methylalumoxane may be in the range of 0.1 :0 to 5 : 1 , or in the alternative, the molar ratio of triethylaluminum to modified methylalumoxane may be in the range of from 0:5 to 4.5: 1, or in the alternative, the molar ratio of triethylaluminum to modified

methylalumoxane may be in the range of from 3.2: 1 to 5: 1, or in the alternative, the molar ratio of triethylaluminum to modified methylalumoxane may be in the range of from 0.1 : 1 to 2.8: 1.

In one embodiment, the instant invention provides a process, in accordance with any of the preceding embodiments, except that step (A) is conducted in the absence of any modified

methylalumoxane and only in the presence of triethylaluminum.

In an alternative embodiment, the instant invention provides a process, in accordance with any of the preceding embodiments, except that the catalyst exhibits a catalyst efficiency from 300 to 15000 kg polymer/g active catalyst metal.

In an alternative embodiment, the instant invention provides a process, in accordance with any of the preceding embodiments, except that the molar ratio of triethylaluminum to modified methylalumoxane is from 1 : 1 to 2: 1.

In an alternative embodiment, the instant invention provides a process, in accordance with any of the preceding embodiments, except that step (A) is conducted in the presence of

bis(hydrogenated tallow alkyl)methyl, tetrakis(pentafluorophenyl)borate(l-) amine, wherein the molar ratio of bis(hydrogenated tallow alkyl)methyl, tetrakis(pentafluorophenyl)borate(l-) amine to metal complex of polyvalent aryloxy ether is from 0.1 to 10. All individual values and subranges from 0.1 to 10 are included herein and disclosed herein; for example, the molar ratio of

bis(hydrogenated tallow alkyl)methyl, tetrakis(pentafluorophenyl)borate(l-) amine to metal complex of polyvalent aryloxy ether can be from a lower limit of 0.1, 1, 2, 3, 4, 5, 6, 7, 8, or 9 to an upper limit of 0.5, 1.2, 2.3, 3.4, 4.5, 5.6, 6.7, 7.8, 8.9 or 10. For example, the molar ratio of

bis(hydrogenated tallow alkyl)methyl, tetrakis(pentafluorophenyl)borate(l-) amine to metal complex of polyvalent aryloxy ether may be in the range of from 0.1 to 10, or in the alternative, the molar ratio of bis(hydrogenated tallow alkyl)methyl, tetrakis(pentafluorophenyl)borate(l-) amine to metal complex of polyvalent aryloxy ether may be in the range of from 1.5 to 5, or in the alternative, the molar ratio of bis(hydrogenated tallow alkyl)methyl, tetrakis(pentafluorophenyl)borate(l-) amine to metal complex of polyvalent aryloxy ether may be in the range of from 5 to 10, or in the alternative, the molar ratio of bis(hydrogenated tallow alkyl)methyl, tetrakis(pentafluorophenyl)borate(l-) amine to metal complex of polyvalent aryloxy ether may be in the range of from 3.5 to 7.5, or in the alternative, the molar ratio of bis(hydrogenated tallow alkyl)methyl,

tetrakis(pentafluorophenyl)borate(l-) amine to metal complex of polyvalent aryloxy ether may be in the range of from 0.1 to 3.9.

In an alternative embodiment, the instant invention provides a process, in accordance with any of the preceding embodiments, except that the polymerization process utilizes a first

polymerization reactor and a second polymerization reactor, wherein step (A) is conducted in the second polymerization reactor in the presence of freshly supplied ethylene; and further comprising (B) polymerizing ethylene and optionally one or more α-olefms in the presence of a second catalyst to form a semi-crystalline ethylene-based polymer in the first polymerization reactor. The second catalyst may be selected from any known ethylene polymerization catalyst, including for example, single site catalysts, Ziegler-Natta catalysts and combinations thereof.

In another alternative embodiment, the polymerization process is conducted in only one polymerization reactor.

Known metallocene-catalyzed polymers include both (a) the homogeneous-branched, substantially linear ethylene polymers ("SLEP") which are prepared using constrained geometry catalysts ("CGC Catalyst"), such as disclosed in USP 5,272,236 and USP 5,278,272, and

WO93/08221, as well as the homogeneous linear ethylene polymers ("LEP") which are prepared using other metallocene (called "bis-CP catalysts"). Various grades of SLEPs, having a variety of densities and melt flow rates, are commercially available from The Dow Chemical Company as ENGAGE™ polyolefm elastomers or AFFINITY™ plastomers. Various grades of LEPs are commercially available from ExxonMobil Chemical Company as EXACT™ or EXCEED™ polymers.

One technique for preparing such modified aluminoxane (aka alumoxane) is disclosed in U.S. Patent No. 5,041,584 (Crapo et al). Aluminoxanes can also be made as disclosed in U.S. Patent Nos. 5,542,199 (Lai et al); 4,544,762 (Kaminsky et al); 5,015,749 (Schmidt et al); and 5,041,585 (Deavenport et al).

In an alternative embodiment, the instant invention further provides a semi-crystalline ethylene-based polymer produced by the polymerization process according to any one of the preceding embodiments. Commercial examples of semi-crystalline, CGC-catalysed ethylene-based plastomers or elastomers include AFFINITY™ polyolefm plastomers and ENGAGE™ polyolefm elastomers, both available from The Dow Chemical Company.

In another alternative embodiment, the instant invention further provides an article comprising the semi-crystalline ethylene-based polymer of according to any one of the preceding embodiments.

Examples

The following examples illustrate the present invention but are not intended to limit the scope of the invention.

Inventive Example 1 and Comparative Example 1 were a polymerization process to make an ethylene-octene copolymer pursuant to the reactor conditions shown below. In Comparative Example 1 , only MMA was added with no TEA. In Inventive Example 1 , TEA and MMA were both added to the polymerization process with TEA present at a level of 10 mmol/m ³ in the reactor.

Reactor conditions

Average temperature; 155 °C

Average ethylene concentration: 14.5 kg/m3

Average octene concentration: 145 kg/m3

Average polymer concentration 21.6 wt%

Cocatalys to catalyst molar ratio (B/Zr) 1.8: 1

Al (MMAO) to catalyst molar ratio (Al/Zr) between 15: 1 and 25 : 1

Resulting polymer has the following properties:

Density = 870 kg/m3

Melt index = 0.5 dg/min (controlled by adding hydrogen as chain terminator)

Typical polymer yield

Expressed in amount of polymer per amount of active catalyst metal (in this case Zr) for this product and these conditions is between 4.0 and 12 t/g (typically 9 t/g). Fig. 1 shows the reactor stability, expressed as measured ethylene concentration, for Comparative Example 1. Fig. 2 shows the reactor stability, expressed as measured ethylene concentration, for Inventive Example 1.

The present invention may be embodied in other forms without departing from the spirit and the essential attributes thereof, and, accordingly, reference should be made to the appended claims, rather than to the foregoing specification, as indicating the scope of the invention.