BACKGROUND OF THE INVENTION

This invention relates to the preparation of inorganic-oxometalate anion pillared clay compositions having the hydrotalcite type layered double hydroxide crystal structure and more particularly, anionic magnesium-aluminum and zinc-aluminum hydrotalcite clays containing large inorganic polyoxometalate anions (POMs) with Keggin-type structures intercalated between positively charged layers of metal hydroxides.

In recent years inorganic materials such as pillared smectite clays have been extensively used as catalytic materials in varying applications. These materials comprise negatively charged metal silicate sheets intercalated or pillared with hydrated cations. See Pinnavaia T. J., Science, 220, 365 (1983) for a review on these clays. The techniques for the intercalation of these clays are well-established and wide variety cf cations may be incorporated into clays such as montmorillonite. Through the changes in the size of the pillar used to separate the sheets in the clay structure, the pore size of the pillared clay may be tailored to a particular application. Porous clay materials with high surface area have been prepared using organic or organometaliic cations, metal chelates, polyoxometalate cations and transition metal halide clusters. Synthesis of several such systems has been disclosed in several patent literatures including the ones by Pinnavaia et. al., in U.S. Patent Nos. 4,665,045; 4,665,044 and 4,621 ,070.

Polyoxometalate anions are another class of pillars that are suitable for lamellar solids. POMs containing early transition metals form water soluble anions with the general formula [M _m O _y p- (isopolyanions) and [XxMmOy ^* (x<m) (heteropolyanions). M is usually molybdenum or tungsten, less frequently vanadium, niobium or tantalum, or mixtures of these elements, in their highest oxidation states. For general review on polyoxometalate anions see, Pope, M. P., Heteropoly and Isopoly Oxometalates, Springer-Verlag, New York, (1983). POMs forms a structurally distinct class of complexes based predominantly, although not exclusively, upon quasi-octahedral-coordinated metal atoms (M0 ₆ ).

The simplest POMs have the hexametalate structure MβO-ig, where the oxygen atoms are in closed-packed arrangement with six MOQ octahedra (Figure 1A). Some of the isopoly anions include [NbeO ig] ⁸ ", [TaeO-ig] ⁸ ', [MoβOig] ^2* etc. The decavanadate anion V10O28 ⁶ " has a related structure (Figure 1 B). Similarly, seven edge-shared octahedra form the Anderson-type structures (Figure 1C) such as in [M02O24] ⁶ ".

The most extensively studied POM compounds are those with Keggin- type structures (Figure 2). At least two isomers of the Keggin structure are known and Fig 2A represents the cc-form. The structure has overall T^ symmetry and is based on a central XO4 tetrahedron surrounded by twelve MOδ octahedra arranged in four groups of three edge shared octahedra, M3O13. These groups ("M3 triplets") are linked by several corners to each other and to the central XO4 tetrahedron. Most of these types of Keggin ions are either molybdates or tungstates with the general formula [XMi2θ4θ] ^π" where M is Mo or W. For M=W, anions with X=H. B, Al, Ga(lll), Si, Ge(IV), P(V). As(V), V(V), Cr(lll), Fe(III), Co(III), Co(ll), Cu(ll), Cu(l), or Zn have been reported. Similarly for M=Mo anions with X= Si, Ge(IV), P(V), As(V), V(V), Ti(V), Zr(IV), In (III) is known. The second isomer has the β-Keggin structure, where one of the edge-shared M3O13 triplets of the α-structure rotated by 60° around the C3 axis, thereby reduction of overall symmetry of the anion from T<j to C3 _V (Figure 2B). This structure is known for several tungstates (X=B, Si, Ge, H2) and molybdates (X= Si, Ge, P, As).

Another class of POM are known in which a single MC-6 octahedron is deficient (Figure 2C). These are known as lacunary (defect) Keggin POM anions and has the general structures such as [XWι ιθ3g] ^n* (represents as

XMn) where X=P, As, Si, Ge, B, Al, Ga, Fe(lll), Co(lll), Co(ll), Zn, H ₂ , Sb(lll), Bi(lll); or [XMoι ιC-39] ^π - where X= P, As, Si, Ge. These anions are stable in aqueous solutions and can be isolated in pure forms. Removal of a trigonal group of three adjacent MOβ octahedra from the Keggin structure derive an another class of lacunary structures, which lead to XM9 structure (Figure 2D).

The anion [PW9O34] ⁹ - represents one such example. The POM [P2W18O62] ^6" consists of two PWg lacunary units fused into a cluster of virtual D3 symmetry

(Figure 2E). This unit is now known as the Dawsoπ structure, and has two types of W atoms , six "polar" and twelve "equatorial". Removal of one MOε octahedra from this Dawson structure results in [X2W17O61] ¹⁰ " type lacunary anions.

There are several other POMs which are closely related to Keggin type structure. For example, the anion PV14O42 ^9* has a "bicapped Keggin" structure. In this POM twelve vanadium atoms form the usual Keggin structure and the remaining two V atoms occupy the pits on the Keggin molecule where a C4 axis is passing, forming trigonal bipyramidal caps (Figure 2F). The POM anion NaP5VV ^" 3θι ι o ^14" has an approximate Dsr, symmetry and consists of a cyclic assembly of five PW6O22 units, each derived from the Keggin anion, [PW12O40] ^3" , by removal of two sets of three corner-shared WOβ octahedra which leads to the PWβ moeity of the P2W18 (Dawson) anion. The sodium ion is located within the polyanion on the five fold axis and is 1.25 A above the pseudomirror plane that contain the five phosphorous atoms.

The structures of heteropoly and isopoly oxometalates are not confined to the structure-types described above. There are several other variations. For example, the paratungstate anion [H2W12O42] ¹⁰ " has a different arrangement of its twelve MOβ octahedra than in a typical Keggin-type anion. Here, MOε octahedra are arranged in four groups of three edge-shared octahedra to form a central cavity. It has been suggested that the two protons are attached to the oxygen atoms inside the cavity and help stabilize the somewhat open structure by hydrogen-bonding (Figure 1 D). Anionic POM compounds have been extensively used as heterogeneous catalysts for a broad variety of reactions. Examples include: oxidation of propylene and isobutylene to acrylic and methacrylic acids, ammoxidation of acrylonitrile; oxidation of aromatic hydrocarbons; olefin polymerization and epoxidation, and hydrodesulfurization. Thus negatively charged polyoxometalates would present a wider range of thermally stable, catalytically active pillars, provided a suitable host clay material is utilized.

Layered double hydroxides (LDHs), which are also referred to as anionic clays, represent a potentially important class of lamellar ionic solids for forming pillared derivatives with anionic POMs. These clays-have positively charged layers of metal hydroxides between which are located anions and some water molecules. Most common LDHs are based on double hydroxides of such main group metals as Mg, and Al and transition metals such as Ni, Co, Cr, Zn and Fe etc. These clays have structures similar to brucite (Mg(OH)2) in which the magnesium ions are octahedrally surrounded by hydroxyl groups with the resulting octahedra sharing edges to form infinite sheets. In the LDHs , some of the magnesium is isomorphously replaced by a trivalent ion, say Al ³⁺ . The

Mg ²⁺ , Al ³⁺ , OH ^* layers are then positively charged necessitating charge balancing by insertion of anions between the layers. One such clay is hydrotalcite in which the the carbonate ion is the interstitial anion, and has the idealized unit cell formula [Mg6Al2(OH)i6.Cθ3.4H2θ. However, the ratio of Mg/Ai in hydrotalcite can vary between 1.7 and 4 and various other divalent and trivalent ions may be substituted for Mg and Al.

The preparation of LDHs is described in many prior art publications, particular reference being made to following review journal articles by S. L. Suib et. al., in Solid State Ionics, 26 (1988), 77 and W. T. Reichel in CHEMITECH, 58 (1986). An important aspect of the synthesis of these materials, which is particularly relevant to this disclosure, is the variation of the nature of the interstitial anion. The preparation of hydrotalcite-like materials with anions other than carbonate in pure form requires special procedures, because LDH incorporates carbonate in preference to other anions. Most of the time the smaller anions are introduced to the LDH structure via the precipitation method by using the desired anion solutions instead of carbonate. In this manner the carbonate anion in the hydrotalcite can be varied in synthesis by a large number of smaller anions such as NO3", Cl", OH% SO4 ² - etc. However, in these methods the synthesis has to be carried out in an anaerobic condition to prevent carbonate contamination from the atmospheric carbon dioxide. Miyata et. al. in U. S. Pat. Nos. 3,796,792, 3,879,523, and 3,879,525 describes hydrotalcite-like derivatives with anionic substitution including the smaller transition metal anions like Crθ4 -, M0O4 ² -, and M02O7 ² -.

The incorporation of larger anions in to LDH galleries, such as transition metal polyoxoanions, is not easy. This requires ion-exchange techniques subsequent to the LDH synthesis. The work by Miata et al., in Clays and Clay Minerals, 31 , 305 (1983) indicated that the order of ion exchange capability of the gallery anions in hydrotalcite-like derivatives to be OH ^* <F"<CI ^* <Br< θ3-<l ^_ and for divalent anions, Cθ3 ² -<Sθ4 ^2_ . Monovalent anions can be easily replaced by di- or poly-valent anions. Using this strategy, Pinnavaia and

Kwon in J. Am. Chem. Soc, 110, 3653 (1988) have demonstrated the pillaring of several polyoxometales including V10O28 ^6* into the hydrotalcite structure containing Zn and Al metal ions in the layers. This pillared hydrotalcite-like material catalyzes the photooxidation of isopropanol to acetone. U. S. Pat. No. 4,454,244 by Woltermann discloses the preparation of several polyoxometalate-LDH reaction products. However, no XRD or analytical

data were given to support his assumption that the POMs were intercalated into the galleries of a crystalline LDH host. During the course of this work, we reproduced some of the synthetic procedures disclosed by Wolterman and found the products to be largely amorphous and impure (see the description of the invention below).

Recently, in U. S. Pat. No. 4,774,212 by Drezdon, the preparation of several Mg/AI hydrotalcite-like materials with gallery height about 12 A containing transition metal polyoxoanions such as V10O26 ⁶ ". M07O24 ^6" and W7O24 ⁶ " with Anderson type structures (Figure 1 ), is disclosed. We disclose here processes for preparing Mg/AI and Zn/AI LDHs intercalated with transition metal containing large POM anions. The products isolated were pure and gave well-defined XRD peaks corresponding to uniformly crystalline layered double hydroxide products. The basal spacings of these materials agreed with POM-intercalated structures. The replacement of smaller anions, in hydrotalcite-like LDHs with much larger POMs, particularly with POMs with Keggin type structures, produce structures with increased gallery spacings of 14 A or more. Such materials should exhibit intracrystalline microporosity accessible for the adsorption or diffusion of molecules into the structure from the outside. The accessibility of the intracrystalline structure to guest molecules should provide new opportunities for molecular seiving of gas mixtures and for heterogeneous catalysis.

SUMMARY OF INVENTION

This invention describes the synthesis of uniformly crystalline polyoxometalates intercalated layered double hydroxide compositions interlayered by polyoxometalate anions and having the formula [Mι-χ ^ll M _x ^lll (OH)2] A _x /n ⁿ ".yH2θ and X-ray basal spacing values > 14 A, wherein, M" is a divalent metal and M'" is a trivalent metal, A is an anionic polyoxometalate of charge n , x range between 0.12 to 0.8, and y is a positive number.

Other objects and advantages of this invention will be apparent from the following detailed description and the drawings .

IN THE DRAWINGS Figures 1A to ID are perspective views showing the structures of some common POMs and in particular: lA the structure of [Mg0i9] ⁿ ~; IB structure of Vτ _. oO28 ⁶ ~- ^lc structure of an Anderson type anion; ID structure of

_ ^H 2 ^W 12°42- ¹⁰ ~- ^Tne positions of the protons are marked by open circles.

Figures 2A to 2F are perspective views showing Keggin and related structures and in particular isomers of the Keggin structure: 2A alpha-isomer; 2B beta-isomer, where one M3OJ.3 group (shown unshaded) has been rotated by- - 60°; 2C a lacunary structure derived from alpha-Keggin structure 2A by removal of one MOg octahedron to result XMτ_ι structure; 2D a lacunary structure derived from alpha-Keggin structure 2A by removal of three adjacent MOg octahedra to result XM9 structure; 2E alpha-[P2Wi8θ62_ ⁶ ~- the Dawson structure; 2F structure of [PV14O42l ^9- based on alpha-Keggin structure with two additional vanadium atoms occupying trans-related VO5 trigonal bipyramids. Figures 3A to 3C are graphs showing x-ray diffraction patterns for oriented film samples of

3A Zn2Al-N03LDH and Zn2 l-LDH intercalated with 3B Keggin ion alpha-SiV3 9θ4θ ~ 3 V ₁₀ O ₂₈ ^6" . Figures 4A and 4B are graphs showing ^" x-ray diffraction patterns for oriented film samples of Zn2Al-LDH intercalated by 2A. Lacunary Keggin ion BCuCII) ]_]_039 ⁷ ~ 2B POM anion NaP5W3oOno ¹⁴ ~.

Figures 5A to 5C are graphs showing x-ray diffraction patterns for oriented film samples of Mg3Al-LDH containing intercalated 5A 0H~

5B H ₂ W ₁₂ O40 ⁶ - Figures 6A to 6D show x-ray diffraction patterns for film samples of 6A Zn2Al- 03 LDH and the POM-LDH reaction products formed by the reaction of the LDH with 6B

Vlθθ28 ^6- - ^β C PWι ₂ θ4o ³ ~; and 6D SiV ₃ W9θ4 ₀ ^7- intercalates prepared according to the methods _^ .described in U.S. Patent No. 4,454,244.

DESCRIPTION OF THE INVENTION

In certain embodiments described in this invention we describe the preparation of POM-intercalated crystalline Zn/AI-LDH compounds of the formula [Zn2AI(OH)6_Aι _/n ⁿ ".yH ₂ θ, where A is a POM anion of negative charge n, and y is a positive number. The incorporation of the guest POM anions into the Zn/AI LDH was carried out using LDHs of the type Zn2AI(0H)6X, [ abbreviated as Zn ₂ AI-X] where X" = Cl" or NO3-- and NO ₃ - is the preferred anion. The polyoxometalate anions selected contained at least one transition metal and possessed preferably a Keggin or lacunary Keggin-type structure or other POM anions with structures related to Keggin ions. The anion X in Zn ₂ AI-X is readily exchangeable with POM to give the desired POM intercalated Zn2AI-LDH.

The precursor LDHs Zn2Al(0H)6CI or Zn2AI(0H)6NO3 were prepared using the induced precipitation method. Accordingly, a 0.1 M Al ³⁺ solution containing the desired anion (Cl- or NO3-) was added to 1 M NaOH until a pH of

7 was achieved. This white-slurry [AI(OH)3J was then treated with a 0.3M Zn ²⁺ solution while maintaining the pH of the slurry between 6-7, and more preferably between 6.0-6.2. It is desirable to maintain the pH between 6-6.5 in this step to eliminate the formation of undesired products. The resultant slurry was then digested, preferably between 60-100°C, for a period of 18 h to a day to obtain a good crystalline material. This crystallization process for the LDH - chloride or nitrate is important for the subsequent synthesis of well-crystalized pillared POM derivatives from these materials. Shorter durations of digestion resulted in amorphous materials, but extended digestions, for example, through a period of week, increased the crystallinity of the final products. All of the manipulations were carried out under an atmosphere of nitrogen gas and the solvents were degassed prior to the use to avoid possible contamination of CO3 ² - from atmospheric CO ₂ . An oriented film sample of the Zn2AI-N03 LDH reaction product showed a well-defined X-ray powder patterns corresponding to the LDH structure (Figure 3A). Chemical analysis revealed that the Zn/AI ratio of this material to be 2. These Cl" and NO3" precursor Zn2AI-LDHs were stored as aqueous slurries for the subsequent anion exchange reactions with POM anions as discussed below.

Anion exchange reactions were carried out by adding an aqueous hot suspension of [Zn2AI(OH)6]X.zH2θ (X = C and NO3-) into an aqueous solution containing POM anions under anaerobic conditions. Preferably, a stoichiometric

excess of the anion pillaring material over the hydrotalcite-type clay is used, for example, about 1 to about 2 molar excess, although a stoichiometric amount can also be used. The exchange reaction depends on the temperature and the pH of the solution. When the exchange reaction was carried out at ambient temperatures, the products obtained showed incomplete exchange. Zn2AI- LDHs are amphoteric and stable only within the pH range of 5.8 to 10. Moreover, most POMs are unstable or undergo hydrolysis at high basic conditions. Therefore, exchange reactions were carried out under slight acidic conditions at a pH in the range of about 6 to 4. Aqueous hot suspensions of [Zn2AI(OH)6]Nθ3.2H2θ were found to undergo complete intercalative ion exchange reactions with aqueous solutions of POM anions such as 0 H2W12O40 _. 6-, α-[SiV3Wgθ40]7-, BV(IV)Wι ι θ4θ7-. SiFe(III)(SO3)Wi i O397-, with Keggin structure. These intercalated products were crystallographically well-ordered phases. For example X-ray diffraction patterns for oriented film samples of the Zπ2AI[α-SiV3Wgθ4θ7-] reaction product show at least six orders of 001 harmonics corresponding to a basal spacing of 14.5 A (Figure 3A). If the thickness of the LDH layer is taken to be 4.8 A, then the gallery height-is 9.7 A, in accordance with the expected size of the Keggin ion. Similarly, POM anions such as PM02W9O397-, BCo(ll)Wι -| θ397-, BCu(!l)Wι ι θ397-, SiW-j i θ398-, BW1 1 O399-, PW9O349-, with lacunary

(defect) Keggin structure can be intercalated in Zn2AI-LDH structure to give pure products with basal spacings around 14 A. Furthermore, robust POMs with fused Keggin-type structures such as H2W12O42I O- (Figure 1 D), PV14O429- (Figure 2E), NaP5W3oOn o14- also readily undergo intercalation to give pure crystalline products.

ThlTanϊons with lower charge, for example a charge less than 7-, such as [PW12O40] ³ " and [SiW-]2θ4o] ^4" show no ion exchange whereas, intermediate anions show partial intercalation (eg. [PCuWn θ3g(H2θ)] ⁵ -). Partial intercalation also was observed with several POMs with 6- charge such as BV(v)Wι ι0 ₄ o ⁶ -, BCo(m)W ₁₁ θ3 ₉ 6- and PV3W9O40 ⁶ -. X-ray diffraction patterns of these materials showed the presence of small amounts of non-intercalated starting material Zn2AI-Nθ3, along with intercalated product. However, as described above, the anion α-[H2Wi2θ4θ] ⁶ ", showed complete intercalation. These observations can be explained considering the guest anion size and host layer charge density. If one assumes a triangular arrangement of Keggin ions with a 9.8 A diameter in the LDH galleries, then the area needed to

accommodate each ion is 83 A ² . Since the area per unit layer charge for [Zn2AI(OH)6 _. Nθ ₃ .2H2θ is 16.6 A ² , Keggin ions with a charge less than 5- such as [PW ₁₂ O40] ³ " and [SiWi ₂ θ4θ] ^4* , is spatially incapable of balancing the host layer charge and making their intercalation in the LDH structure impossible. It is also apparent that the stacking symmetry of these Keggin ions plays a role in the intercalation reactions. The oxygen frame work of the POM anions with the α-Keggin structure define a polyhedral form with Td symmetry. Thus, there are two plausible orientations for α-isomers of Keggin structure in the LDH galleries. One orientation suggests the C3 axis is orthogonal to the layers, and the other orientation the C ₂ axis is orthogonal. The C ₃ orthogonal orientation of the α-isomer allow the hydroxyl groups in LDH to undergo H-bonding to six oxygens of the upper M3 triad and to three terminal oxygens on the opposing side of the POM. Conversely, the C2 orthogonal orientation permits 12 H- bonding interactions to 8 terminal and 4 bridging POM oxygen atoms. Thus, larger number of H-bonds should favor the C ₂ orthogonal orientation.

Accordingly, intercalation of β-isomers of Keggin type POM was slow and incomplete. For example, β-[SiV3Wgθ ₄ o] ⁷ " POM anion which has a C _3V oxygen framework symmetry, undergoes partial intercalation in Zn ₂ AI-LDHs. As discussed earlier, in the β-Keggin structure, one of the edge-shared M3O ₁ 3 triplets of the α-structure is rotated by 60° around the C ₃ axis (Figure 2B). Thus once the β-isomer is intercalated inside the LDH galleries with orientation similar to that of α-isomer, it's preferred orientation is a one with C ₃ axis inclined. In this orientation β-Keggin ion is capable of mimicking only half the H- bonding interaction encountered for a C ₂ orthogonal orientation of α-isomer. One face of the POM experiences guest-host interactions equivalent to those found for the C3 orthogonal orientation of α, but the H-bonding pattern on the opposite face of the POM is completely disrupted. As a result POM anions such as β-SiV3Wgθ ₄ o ^7* , with β-Keggin type structures undergo only partial intercalation. The anions that posses structures other than Keggin- or lacunary Keggin- type also can be intercalated using this procedure. For example intercalation of smaller POM anions with Anderson type structures such as V1 ₀ O ₂₈ ⁶ " ive crystalline products with basal spacing of about 12 A (Figure 3C).

In this invention we also describe the preparation of POM-intercalated, hydrotalcite-like Mg/AI LDH compounds of formula

[Mg6Al (OH)i6_(A ⁿ -)2 _/ n-yH ₂ θ, where A is the anion of negative charge n and y

is a positive number. The advantage of the method that we disclose here is the ability to begin with hydrotalcite, a readily accessible Mg/AI-LDH carbonate, and then to convert this material to a pillared derivative containing large POM anions. Hydrotalcites with different Mg/AI ratios are easy to make and their syntheses are widely known in the art. In addition, hydrotalcite is commercially available. Hydrotalcite used in this invention was prepared by the addition of stoichiometric amounts of mixed magnesium and aluminum nitrates as an aqueous solution to a solution of stoichiometric amounts of sodium hydroxide and carbonate at about 25-30°C, with vigorous stirring over a several-hour period, producing a slurry. This slurry was then heated for about 18 hours at about 60 -75°C in order to allow crystallization. After filtering the solids, and thorough washing and drying, the dry solids were recovered. This procedure is readily adaptable to variations in the Mg/AI ratio, although a Mg/AI ratio of 3:1 was used in this invention. The hydrotalcite was then calcined to remove all of CO3- anions from the structure. This heat treatment is a very important part of this synthesis and may be carried out between 400-550°C, preferably at 500°C, in air, or preferably, an inert gas stream or even under vacuum. This heat treatment resulted in the formation of an amorphous magnesium-aluminum oxide solid solution Although the conversion was complete in about three hours, the calcination was carried out for about 10-12 hours to ensure the removal of all carbonate anions from the hydrotalcite structure. Upon being -slurried in degassed-deionized water under an inert atmosphere, this calcined product undergoes hydrolysis to reform the LDH structure with OH- ions in the gallery. The product isolated showed well defined X-ray diffraction patterns corresponding to the LDH structure with a basal spacings of 7.8 A (Figure 5A). Chemical analysis confirmed the hydrotalcite hydroxide structure. The calcining temperature of hydrotalcite is very critical to obtain the pure "reactive" LDH-OH form. At or below 400°C, the hydrotalcite decomposition process is slow and incomplete and results in residual CO3 ² - anions. Above 600°C, the resulting metal oxide mixture begins to sinter and lose its ability to reform the LDH structure in aqueous solutions.

The [Mg ₃ AI(OH)8]OH.yH ₂ 0 (referred to as [Mg ₃ AI]-OH) prepared in this manner was found to be reactive towards anion exchange reactions. The. anion exchange reactions were carried out under anaerobic conditions by adding an aqueous suspension of [Mg3AI]-OH to a vigorously stirred aqueous solution

containing the desired gallery anion. Preferably, a stoichiometric excess of the POM anion is used, for example about a 1 to about 2 moiar excess. The mode of addition is important at this stage. The -addition of POM solutions to a [Mg3AI]- OH slurry results in mixed products containing several crystalline phases. The mixed phases are presumed to result from the hydrolysis reaction of the POM and LDH. Adding the [Mg3AI]-OH slurry drop-wise into the POM solution prevents hydrolysis, as well as the need for controlling the pH of the solutions. The resulting suspensions were stirred for about 30 min. at ambient temperatures (25-30°C), although the anion exchange reactions were completed within minutes. The POM-intercalated LDHs were recovered by filtration, washed with water, and dried in air at 120°C.

The gallery OH- ions in the Mg3AI-OH LDH can easily be exchanged by a wide variety of anions, such as Crθ4 ^2* , Sθ4 ^2* -- CO3 ² - etc or larger anions such as V10O28 ⁶ ". W7O2 ⁶ - or much larger POM anions with Keggin-type structures such as H2Wi2θ4o ^6* , BVW10O40 ⁷ -, SiV3Wgθ4o ^7_ _, etc., or lacunary structures such as SiWι ιθ39 ⁸ ', BC0W11O39 ⁷ -, BCuW^Osg ⁷ - _, etc. In general, the isolated products have the idealized formula where A is the POM anion of negative charge n. The products isolated were pure and showed X-ray diffraction peaks corresponding to crystalline phases with well-defined basal spacings (Table 1 ). For example, [Mg6Al2(OH)i6][H2Wi2θ4o]ι/3.zH ₂ 0, where the gallery anions are H2W12O40 ⁶ -, showed a basal spacing of 14.8 A with well defined 001 reflections (Figure 5B). The basal spacing corresponded to gallery height of about 10 A and with a LDH layer thickness of about 4.8 A.

The [Mg3AI]-OH LDH prepared according to this invention undergoes swelling in the presence of various alcohols, ethers, polyalcohols and polyethers which results in an increase in gallery height. For example, suspending the LDH-OH in 1 :2 (v/v) H2θ:giycerol and flash drying at 190°C for ten minutes affords a product containing a mixture of two expanded phases with basal spacings of 14.2 A and 9.4 A. These phases result from glycerol-swollen derivatives containing a multilayer and monolayer of glycerol, respectively.

Further drying at 190°C for 1.5 hr resulted in the conversion of the multilayer glycerol solvate to the monolayer form. These results unequivocally demonstrate that glycerol swells the hydroxide interlayers of the LDH.

We have utilized the swelling behavior of [Mg3AI]-OH LDH to disclose a jelrϊeral-and exceptionally convenient route to introduce POM anions into the

LDH galleries. Our approach, as disclosed in this patent, utilizes a swelling

agent and the swellable [Mg3AI]-OH LDH precursor to enhance the accessibility of the intercrystaliine gallery surfaces of the LDH for topotactic reaction. LDH intercalation compounds interlayered by POM anions are readily prepared by the ion exchange reaction of [Mg3AI]-OH and POM. The [Mg3AI]-OH LDH is 5 slurried in glycerol: water preferably in 2:1 (v/v) ratio, and this solution is added dropwise to an aqueous solution containing the POM anion. This solution could contain much higher or lower amounts of glycerol with glycerol water ratio in the range 1 :1 to 4:1 (v/v). A stoichiometric excess of the POM anion over the hydrotalcite-like clay is used, for example about 1 to about 2 molar excess. The 1 0 resulting slurry is stirred at 25°C for a period of about 1 hr. After filtering the solids, and thorough washing and drying at 120°C, the POM-intercalated Mg/AI LDHs are recovered. The isolated product contained well-ordered crystalline POM intercalated-LDH phases and XRD patterns similar to the products discussed earlier (Figure 5B and 5C).

1 5 This process of incorporating large POM anions into hydrotalcite structure has several novel features. Most importantly, the anion exchange reactions do not require controlled pH conditions, and the methods are convenient and fast. Furthermore, all the products prepared according to this invention afford pure and completely intercalated crystalline products with basal

2 0 spacings of 14 A or higher with high surface area values (Table 1 ). Although not discussed here, all the materials were further characterized by NMR, IR and other techniques. The types of POMs that can be intercalated are not limited to the ones described in this invention. The processes described could be adapted for the intercalation of any suitable POM anion. _2-5 The preparation of materials prepared by the reaction of polyoxometalate anion with Zn/AI and Mg/AI-LDH has been disclosed in U.S. Pat. No. 4,774,212 by Drezdon. In this latter work pillaring by relatively small POMs with Anderson type structures such as V10O28 ⁶ ". Mθ7θ24 ^6- and W7O24 ⁶ - were disclosed. In the preparation of these materials, controlled acidic conditions and LDH precursors

3 0 intercalated by dicarboxylate anions were used. Hydrotalcite-like materials were first interlayered by dicarboxylate anions to obtain organic anion derivatives with basal spacings about 14 A. These dicarboxylate anion pillared LDHs were then treated with vanadates, molybdates or tungstates at controlled acidic pH conditions to intercalate V10O26 ⁶ ". M07O24 ^6' and W7O24 ^6" anions 3 5 (Figure 1 ), with basal spacings of about 12 A. By following the teachings of our disclosure we can also intercalate these smaller ions into LDH structures

(Figure 3C) . The emphasis of our invention was the synthesis of POM-intercalated LDHs that result in higher basal spacings of 14 A or more. The polyoxometalates selected have Keggin- type structures or related ones. A second patent, U.S. Patent No. 4,454,244 by Wolterman, also has claimed the preparation of several POM-LDH reaction products. The POMs used by Wolterman were mostly non-Keggin type anions such as V10O ₂ 8 ⁶ ". Mθ ₂ θ7 ^6_ , Ta6θιβ(OH) ⁷ - etc. His starting materials were either the nitrates or chlorides of Zn/AI or Mg/AI-LDHs. These solid LDHs were slurried in solutions containing POM anions to obtain POM-containing products. However, no XRD or analytical data were given in the patent to support the presence of a pillared crystalline phase. The pillaring of a layered solid by a gallery ion requires that the product be crystalline with the host structure still intact following insertion of the guest. Depending on pH, however, the reaction of a LDH and a POM can lead to hydrolysis products that are amorphous non-pillared phases and to diffusely crystalline impurities. Thus, we have made several attempts as described below to characterize some of Wolterman's materials by following the teachings of his patent.

Following the conditions given in U.S. Patent No. 4,454,244, we have found the reaction products to be largely X-ray amorphous and impure. For example, the yellow product said to be V _{1 (} )θ ₂₈ ⁶ " intercalated into a Zn ₂ AI-LDH was found to be X-ray amorphous as judged by the absence of distinct Bragg reflections. The X-ray diffraction pattern for this product is shown in Figure 6B. The diffuse reflection near 10-11 A are coincident with the reflections for poorly formed Mg or Al salts of the POM; they are not characteristic of a pillared LDH-

V10O28 ^6" . In contrast, the V10O28 ⁶ " intercalated Zn2AI-LDH prepared according to our teachlrϊgs as disclosed in this patent was an analytically pure, crystalline layered material. The XRD of the [Zn ₂ AI(OH)6 _. (V ₁₀ θ28)ι _/ 6-xH ₂ θ product synthesized according to our teachings showed four orders of 00! harmonics corresponding to a basal spacing of 11.9 A (Figure 3C). This basal spacings corresponded to gallery heights of 7.1 A (three oxygen planes) and to a ₁ 0O ₂ 8 ⁶ " orientation in which the C ₂ axis is parallel to the host layers.

U.S. Patent No, 4,454,244 further claimed the intercalation of four

Keggin-type POM anions. These included, PM012O ₄ 0 ³ -, PW12O ₄ Q ³ -, PM06V6O40 ⁵ - and PM06W6O ₄ 0 ⁵ -. We believe that one of these anions, namely

PM06V6O ₄ 0 ⁵ ' is not known to the public. The known P, Mo, V containing

Keggin-type POMs include PM011VO40 ^4' . PM010V2O40 ^5" . and PM09V3O40 ^6" . but not PMθ ₆ V6θ ₄ o ^5* . Moreover, a POM that contained six V, six Mo and one P, if it existed, should have an overall anion charge of minus 9, i.e., PM06V6O40 ⁹ ". Our attempts to intercalate a Keggin-type polyoxometalate according to Wolterman's method also resulted in an X-ray amorphous materials. For example the reaction of, [PW1 ₂ O ₄ 0] ³ - with Zn2AI-N03 according to procedures given in example 5 of U.S. Patent 4,454,244 resulted in a material that was largely X-ray amorphous (Figure 6C). Furthermore, the reaction of Zn ₂ AI-Nθ3 and the Keggin ion α-SiV3Wgθ4o ^7- , resulted in a product which showed diffuse scattering features (Figure 6D) that were different from those observed for an authentic sample of pillared [Zn2AI(OH)6_(SiV3W9θ ₄ o) _1/ 7.XH2O which we discussed earlier (cf., Figure 3B). The diffuse XRD peaks in Figure 6C and 6D were consistent with those observed for the Mg ²⁺ or Al ³⁺ salts of the POM.

We have also found that the products prepared according to Wolterman's teachings were not only amorphous and impure, but also exhibited physical properties different from an authentic, crystalline pillared LDH-POM. For example, the N ₂ BET surface area of 155 m ² /g was observed for the crystalline α-SiV3Wgθ ₄ o ⁷ ' intercalated LDH prepared according to our teachings, when out gassing was done at 150°C under vacuum. However a much lower surface area of 47 m ² /g was observed under analogous conditions for the amorphous material prepared according to Wolterman's method.

The above observations clearly demonstrate that the POM intercalated LDH materials we disclose here have compositions and properties different from the ones resulting from the work of Drezdon (U.S. Patent No. 4,774,212) and the work of Wolterman (U.S. Patent No. 4,454,244). We have presented in this disclosure, evidence to prove that our materials contain Keggin ions intercalated between LDH layers with retention of crystallinity. We believe that the Keggin-anion products claimed in U.S. Patent No. 4,454,244 were amorphous and impure M" and M -POM salts outside the composition of matter represented by our materials.

On the basis of the known catalytic properties of POMs and hydrotalcites, the POM-intercalated hydrotalcites of this invention may be useful as catalysts for many industrially important processes including the oxidation of methane, sulfur oxides, nitrogen oxides etc., most likely at temperatures in the range of from 100-1000°C.

The following examples will serve to illustrate certain embodiments of the herein disclosed invention. These examples should not, however, be construed as the limiting scope of the novel invention as there are many variations which may be made thereon without departing from the theme of the disclosed invention.

EXAMPLE 1

The preparation of [Zn2AI(OH) ₆ ]X.zH2θ (X = NO3, Cl) is described in this example.

All the manipulations were carried out under a N2 atmosphere, and the water used as a solvent was pre-boiled for about 2 hours under N2 before using.

To a 200-ml solution of 0.1 M AI(N03)3.9H ₂ 0 was added a 1.0 M solution of NaOH until the pH of the solution was 7. The white slurry was stirred for one hour, and a 200-ml solution of 0.3M Zn(N03)2 was added drop-wise. The pH of the mixture was maintained at about 6.0, by adding NaOH. The resulting slurry was boiled for 24h under a nitrogen atmosphere. (Boiling this suspension for one week produced products with high crystallinity.) The product, [Zn2AI(OH)6]Nθ3.zH2θ, was washed several times with water by centrifugation, and stored as an aqueous slurry. A portion of the slurry was dried in air. The X- ray diffraction powder pattern of the dried solid corresponds in to a LDH structure with a basal spacing value of 8.9 A. By employing a similar method,

^~ the Cl" derivative, [Zn2AI(OH)6]Cl.zH2θ, can be prepared using AICI3 and MgCl2 as starting materials.

EXAMPLE 2

The general preparation of poiyoxometalate-intercalated Zn/AI LDH materials is described in this example.

A boiling solution containing about a 5 mequiv. portion of a Zn2AI-X (X = NO3, or Cl) LDH slurry, prepared by the method in Example 1 , was added drop- wise to a stirred aqueous solution containing about 7.5 mequiv. of the desired polyoxometalate anion. After the additions were complete, the pH of the resultant slurries were adjusted to about 6 by adding dilute HNO3 acid. The slurries were stirred for about 1 h and the solid products were isolated and

washed thoroughly with water by centrifugation. The X-ray powder diffraction patterns of the dried solids correspond to hydrotalcite-like layered structures, with polyoxometalate anions in the gallery (Figures 3B, 3C, 4A and 4B). The basal spacings are given in Table 1. Chemical analyses conformed to the structure Zn2AI(OH ) 6[ PO M ⁿ -]ι/ _n .YH2θ, where POM .represent the polyoxometalate with a negative charge of n. The N2 BET surface area for selected products outgassed at 150°C were also determined (Table 1 ).

EXAMPLE 3

The preparation of a hydrotalcite-like [Mg3AI]-C03 LDH is described in this example.

A solution of 12.8 g Mg(N0 ₃ ) ₂ .6H ₂ 0 and 9.4 g AI(N0 ₃ ) ₃ .9H2θ in 100 ml deionized water was added to a solution containing 14 ml 50% (w/w) NaOH and 5 g Na2C03 (anhydr.) in 200 ml distilled water. The addition was carried out very slowly over a period of 90 min. with vigorous stirring. The resulting heavy slurry was heated at 65*5 ⁰ 0 for 18 hours with good mixing. The mixture was then cooled to room temperature, and the precipitate was separated by centrifugation. The solid was washed several times with deionized water until the washings were free of salts and then dried in air. The X-ray diffraction pattern of the dried solid was indexed to hydrotalcite and the basal spacing was found to be 7.78 A. Chemical analysis show the Mg/AI ratio to be 3.2, very near the value expected for hydrotalcite with an idealized formula unit of [Mg ₃ AI(OH)8](Cθ3)o.5.2H2θ.

EXAMPLE 4

The preparation from hydrotalcite of a [Mg3AI]-OH LDH is described in this example. A sample of synthetic hydrotalcite, prepared according to Example 3, was calcined at 500°C for about 12 hours under a stream of N2 gas. A 5-gram portion of this sample was pulverized and suspended in 200 ml of hot (65°C) degassed deionized water to form a white slurry. The resulting slurry was then stirred vigorously at 65°C for one hour under an atmosphere of nitrogen, to form the hydroxide derivative [Mg3AI(OH)8]OH.xH2θ. The resulting slurry was cooled to room temperature and the volume was adjusted to 250 ml with deionized

water. The suspention was stored under N2. The X-ray diffraction powder pattern of the dried solid sample corresponds to the hydrotalcite-like layered structure (Figure 5A). The basal spacing was found to be 7.81 A.

EXAMPLE 5

This example describe a general method for the preparation of polyoxometalate-intercaiated Mg/AI-LDHs.

A 25-mequiv. portion of the [Mg3AI]-OH LDH slurry prepared according to Example 4 was added drop-wise to a stirred aqueous solutions containing about 40 mequiv. of the desired polyoxometalate anion under an atmosphere of nitrogen. The resulting slurry was stirred at ambient temperature for about 15 min. and the solid product was isolated and washed thoroughly with water by centrifugation. The X-ray diffraction powder pattern of oriented film samples of the isolated products correspond to a hydrotalcite-like structure with intercalated polyoxometalates. The basal spacing are given in Table 1. Elemental analyses of the dried products revealed the ratio of POM to Al equivalents to be around 1.1 as expected for [Mg ₃ AI(OH) ₈ ][POM ^π -] / _n .xH2θ, where POM is the polyoxometalate of negative charge n. The N2 BET surface area for selected products outgassed at 150°C were also determined (Table 1).

EXAMPLE 6

This example describes a second general method for preparing polyoxometalate-intercaiated Mg/AI-LDHs.

A 25-mequiv. portion of the [Mg3AI]-OH LDH slurry prepared according to Example 4 was diluted with two volumes of glycerol to obtain a slurry of LDH in 2:1 (v/v) glycerol .-water. This slurry was then added drop-wise to stirred aqueous solutions containing about 40 mequiv. of polyoxometalate anion under an atmosphere of nitrogen. The resulting slurry was stirred at ambient temperatures for about 45 min. and the solid product was isolated and washed thoroughly with water by centrifugation. The X-ray diffraction powder patterns of the oriented film samples of the isolated products corresponded to a hydrotalcite-like structure with intercalated polyoxometalates (Figure 5B and . 5C). The basal spacings are given in Table 1. The observed basal spacings were greater than 14 A, which corresponded to POM-intercalated products,

since the LDH layer thickness is about 5 A and POM height is about 9 A. Elemental analyses of the dried products revealed ratio of POM to Al equivalents to be around 1.1 , as expected for [Mg3AI(OH)8][POM ⁿ -]ι _/n .xH ₂ θ, where POM is the polyoxometalate of negative charge n. The N2 BET surface area for selected products outgassed at 150°C were also determined (Table 1).

TABLE 1. Basal Spacings and Surface Areas of Polyoxometalate Pillared Layered Double Hydroxides of the Type [Mι- _x ^ll M _x ^l "(OH) ₂ ]A _x/ n ^π -.YH2θ

It is intended that the foregoing description be only illustrative of the present invention and that the present invention be limited only by the hereinafter appended claims.