POUR-IN-PLACE POLYURETHANE INSULATION FOAM COMPOSITION COMPRISING HALOGENATED OLEFINS

BACKGROUND

CROSS-REFERENCE TO RELATED APPLICATION

[0001] This application claims the benefit of U.S. Provisional Patent

Application Serial Number 62/558,439, filed September 14, 2017, the entire disclosure of which is incorporated herein by reference

Field

[0002] The present disclosure relates generally to a polyurethane foam composition comprising halogenated olefins.

Background

[0003] Polyurethane insulation foams (e.g., rigid polyurethane insulation foams) are widely used in the refrigeration and construction industries as it offers good insulation performance at low densities. These foams have conventionally been prepared by reacting an isocyanate compound with an isocyanate reactive compound in presence of a suitable blowing agent. With regard to blowing agents, chlorofluorocarbons ("CFCs") and hydrochlorofluorocarbons ("HCFCs"), such as CFC-11 and HCFC-141b, have been widely used because they have been shown to produce closed-cell foams having acceptable thermal insulation and dimensional stability properties. However, in spite of these advantages, CFCs and HCFCs have fallen into disfavor as they may contribute to the depletion of ozone in the earth's atmosphere and to the greenhouse effect. Accordingly, the use of CFCs and HCFCs has been severely restricted.

[0004] More recently, saturated hydrofluorocarbons ("HFCs") and hydrocarbons ("HCs") have been used in polyurethane insulation foams since these compounds have a zero to near zero ozone depletion potential. Examples of HFC's and HC's include HFC-365mfc, HFC-245fa, cyclopentane, n-pentane, and iso-pentane. Like CFCs and HCFCs, these compounds have their own shortcomings. The global warming potential of HFCs has been considered relatively high and questions have been raised with regard to their viability as a long term solution. While the global warming potential of HCs has been considered low, these compounds can be highly flammable and some are deemed to be volatile organic compounds (" VOCs").

[0005] Accordingly, there remains a need to develop a polyurethane insulation foam composition using blowing agents having at least some of the following characteristics: (i) zero to near zero ozone depletion properties; (ii) zero to near zero global warming potential; (iii) not deemed to be VOCs; and (iv) not overly cost prohibitive to deploy in a safe manner. Additionally, the foams made from such compositions should also retain the superior insulation properties and low densities for which closed-cell rigid polyurethane foams are known.

DETAILED DESCRIPTION

[0006] As used herein, unless otherwise expressly specified, all numbers such as those expressing values, ranges, amounts or percentages may be read as if prefaced by the word "about", even if the term does not expressly appear. Plural encompasses singular and vice versa.

[0007] As used herein, "plurality" means two or more while the term "number" means one or an integer greater than one.

[0008] As used herein, "includes" and like terms means "including without limitation."

[0009] When referring to any numerical range of values, such ranges are understood to include each and every number and/or fraction between the stated range minimum and maximum. For example, a range of "1 to 10" is intended to include all sub-ranges between (and including) the recited minimum value of 1 and the recited maximum value of 10, that is, having a minimum value equal to or greater than 1 and a maximum value of equal to or less than 10.

[0010] As used herein, "molecular weight" means weight average molecular weight (M _w ) as determined by Gel Permeation Chromatography.

[0011] Unless otherwise stated herein, reference to any compounds shall also include any isomers (e.g., stereoisomers) of such compounds.

Polyurethane Insulation Foam Composition

[0012] It is well understood that foam formation from a polyurethane foam composition typically involves multiple reactions. The choice of the compositions' components, such as catalyst and other ingredients, are dictated in part by the intended application (e.g., spray application, pour-in place application) or end use (e.g., insulation foam). In general, there may be three reactions that occur during the formation of a foam product from a polyurethane foam composition. The first reaction is often referred to as the gelling reaction. The gelling reaction involves the formation of a urethane compound as an isocyanate compound reacts with a polyol compound. The second reaction is referred to as the blowing reaction. The blowing reaction involves the formation of a urea compound and the release of carbon dioxide as an isocyanate compound reacts with water. The third reaction is referred to as the trimer reaction. The trimer reaction involves the formation of an isocyanurate compound as an isocyanate compound reacts with another isocyanate compound in the presence of a trimerization catalyst. Because the use of the trimerization catalyst is optional, the trimer reaction does not always occur in the formation of a polyurethane foam product. The aforementioned reactions take place at different rates and are dependent on a variety of variables such as temperature, catalyst level, catalyst type and other factors as well (e.g., the presence of either primary or secondary hydroxyl groups in the polyols used). However, to produce high-quality foam, the rates of the competing gelling, blowing, and trimer reactions must be properly balanced to meet a given application/use while also ensuring that the internal cells of the polyurethane foam product do not collapse prior to or during the formation of the polyurethane foam product (e.g., during a polyurethane composition's foam rise phase). Additionally, the rates of the competing gelling, blowing, and trimer reactions must be properly balanced to ensure that the proper gel time, end of rise time, and cream time are being obtained from the polyurethane composition for a given application.

[0013] For example, in a spray foam application the formulator must tailor the polyurethane composition in a manner that would avoid any dripping or draining from the polyurethane composition after the composition has been sprayed onto a substrate (e.g., a wall or ceiling). This can be accomplished by using water and a strong blowing catalyst in the polyurethane composition to generate carbon dioxide ("C0 ₂ "). Ideally, a fine froth (which is caused by the generation of C0 ₂ ) would form within couple of seconds of spraying the polyurethane composition onto the substrate thereby preventing any dripping or draining issues. Another factor a formulator must consider in connection with spray foam applications is a polyurethane composition's tack free time. For example, if a polyurethane composition has a short tack free time, then it could lead to frequent clogging of an applicator's spray equipment. Alternatively, if a polyurethane composition has a long tack free time, then it could lead to deformation of the foam when an applicator's body inadvertently touches the foam after it has been applied onto a substrate. Furthermore, if a polyurethane composition's gel time is too slow, then the foam that begins to form on a substrate (e.g., a wall) might begin to sag as the components of the composition react.

[0014] For a pour-in-place application (e.g., foams used in a refrigerator, water heater, or wall panel) the presence of water and a strong blowing catalyst in a polyurethane composition is required in order to resist void formation during the formation of the foam product. Voids can develop within the internal cell structure of a foam product as it forms due to air being introduced into the forming foam via liquid flow in the mold before the onset of gelling. Another factor a formulator must consider in connection with pour-in-place applications is a polyurethane composition's gel time. For example, if a polyurethane composition has a short gel time, then this can lead to the mold that is being filled with the polyurethane composition not being fully filled with the composition. Alternatively, if a polyurethane composition has a long gel time, then this can lead to long demold times for the final foam product.

[0015] While most tertiary amine catalysts used in a polyurethane composition will drive all three reactions described above to some extent, the catalyst used in a polyurethane composition and the amount that it is used in such composition is often selected based on which reaction or reactions the formulator would like to favor/facilitate. For instance, if the formulator wishes to favor the gelling reaction, then the formulator would select catalysts that favor the gelling reaction (e.g., N- ethylmorpholine) over other catalyst that do not favor such reaction (e.g., N,N,N',N",N"-pentam ethyl di ethyl enetriamine). On the other hand, if the formulator wishes to favor the blowing reaction over the gelling reaction, then the formulator would select a catalyst that would favor the blowing reaction (e.g., N,N,N',N",N"- pentam ethyl di ethyl en etri amine) .

[0016] In addition to tertiary amine catalysts, a polyurethane composition can also comprise a halogenated olefin ("FIFO") blowing agent. The use of some FIFOs, however, can result in the loss of reactivity of certain reactive components in a composition comprising a tertiary amine catalyst due to an unintended adverse reaction between the UFO compound and the tertiary amine catalyst. As will be explained in greater detail below, the aforementioned loss of reactivity can then lead to other issues in the final foam product due in part to the reaction products (e.g., halogenated ions and amine salts) of the HFO compound and tertiary amine catalyst used in the polyurethane composition.

[0017] The potential of the HFO compound and tertiary amine reacting with one another is not only problematic in a one component polyurethane system but it is equally problematic in cases where the polyurethane insulation foam composition is provided as a two component system. A typical two component polyurethane system is comprised of an "A-Side" and "B-Side." The A-Side, which is also known as the iso- side, comprises an isocyanate compound and, optionally, other compounds that do not react with the isocyanate compound. The B-Side, which is also known as the polyol- side, comprises an isocyanate reactive compound and, optionally, water, catalyst, blowing agents, foam-stabilizing surfactants, and other additive compounds. If the HFO and tertiary amine compounds are both placed in the B-Side, then there is a high probability that those two compounds will begin reacting prior to the B-Side being mixed with the A-Side thereby creating the halogenated ion and amine salt reaction products mentioned above.

[0018] The halogenated ions and amine salt reaction products can have a negative impact on the polyurethane composition in several ways. For instance, the amine salts can precipitate out of the B-Side making the B-Side turbid. Additionally, the halogenated ions can decompose silicone based surfactants that are widely used in various polyurethane compositions. The depletion/degradation of the silicone based surfactant typically leads to a foam product having lower insulative properties because the foam product will not only have a higher overall density but it will also have a larger and more open internal cell structure which adversely affects the foam's insulative properties.

[0019] The polyurethane insulation foam composition of the present disclosure solves the issues mentioned above by providing a polyurethane foam composition comprising blowing agents, which are not deemed to be VOCs, having zero to near zero ozone depletion properties and zero to near zero global warming potential. Moreover, the polyurethane insulation foam composition of the present disclosure also eliminates or reduces the unintended reaction between HFO compounds and tertiary amine catalysts present in the composition thereby extending not only the shelf-life of the composition but also allowing for the production of a foam product having consistent insulative properties and internal cell structures.

[0020] The polyurethane insulation foam composition disclosed herein comprises: (i) an isocyanate compound; (ii) an isocyanate reactive compound; (iii) water; (iv) a heterocyclic amine compound comprising the structure of Formula (I) (shown below); (v) a hydrophilic carboxylic acid compound having the structure of Formula (II) (shown below); (vi) a halogenated olefin compound; and (vii) optionally, other additives. In certain embodiments, the polyurethane insulation foam composition disclosed herein has a CT REACTIVE SHIFT (defined in the Examples below) less than or equal to 30 (e.g., less than or equal to 25 or 20 or 15 or 10 or 5 or 1 or 0) and a GT REACTIVE SHIFT (defined below in the Examples) less than or equal to 40 (e.g., less than or equal to 30 or 20 or 15 or 10 or 5 or 1 or 0). In certain embodiments, the polyurethane insulation foam composition is a spray polyurethane insulation foam composition (e.g., a spray polyurethane insulation foam composition such as a closed cell spray polyurethane insulation foam composition). As used herein, a polyurethane insulation foam product shall be deemed to be a "closed cell" foam if the closed cell content of such foam is greater than 70% (e.g., 80% or 85%) as measured by ASTM D6226-15. In other embodiments, the polyurethane insulation foam composition is a pour-in-place polyurethane insulation foam composition such as a closed cell pour-in-play polyurethane foam insulation composition. In some embodiments, the polyurethane foam product that is formed from the compositions disclosed herein has a R-value greater than or equal to 6 per inch (e.g., greater than or equal to 8, 10, or 12)

Component (i): Isocyanate Compound

[0021] The polyurethane insulation foam composition disclosed herein comprises one or more isocyanate compounds. In some embodiments, the isocyanate compound is a polyisocyanate compound. Suitable polyisocyanate compounds that may be used include aliphatic, araliphatic, and/or aromatic polyisocyanates. The isocyanate compounds typically have the structure R-(NCO) _x where x is at least 2 and R comprises an aromatic, aliphatic, or combined aromatic/aliphatic group. Non- limiting examples of suitable polyisocyanates include diphenylmethane diisocyanate ("MDI") type isocyanates (e.g., 2,4'-, 2,2'-, 4,4'-MDI or mixtures thereof), mixtures of MDI and oligomers thereof (e.g., polymeric MDI or "crude" MDI), and the reaction products of polyisocyanates with components containing isocyanate-reactive hydrogen atoms (e.g., polymeric polyisocyanates or prepolymers). Accordingly, suitable isocyante compounds that may be usesd include SUPRASEC ^® D R isocyanate, SUPRASEC ^® 2185 isocyanate, RUB ESTATE ^® M isocyanate, and

RUBINATE ^® 1840 isocyanate, or combinations thereof. As used herein,

SUPRASEC ^® and RUBINATE ^® isocyanates are all available from Huntsman

International LLC.

[0022] Other examples of suitable isocyanate compounds also include tolylene diisocyanate ("TDI") (e.g., 2,4 TDI, 2,6 TDI, or combinations thereof), hexamethylene diisocyanate ("HMDI" or "HDI"), isophorone diisocyanate ('ΊΡϋΓ'), butylene diisocyanate, trimethylhexamethylene diisocyanate,

di(isocyanatocyclohexyl)methane (e.g. 4,4'-diisocyanatodicyclohexylmethane), isocyanatomethyl-l,8-octane diisocyanate, tetramethylxylene diisocyanate

("TMXDI"), 1,5-naphtalenediisocyanate (" DI"), p-phenylenediisocyanate ("PPDI"), 1,4-cyclohexanediisocyanate ("CDI"), tolidine diisocyanate ("TODI"), or

combinations thereof. Modified polyisocyanates containing isocyanurate,

carbodiimide or uretonimine groups may also be employed as Component (i).

[0023] Blocked polyisocyanates can also be used as Component (i) provided that the reaction product has a deblocking temperature below the temperature at which Component (i) will be reacted with Component (ii). Suitable blocked polyisocyanates can include the reaction product of: (a) a phenol or an oxime compound and a polyisocyanate, or (b) a polyisocyanate with an acid compound such as benzyl chloride, hydrochloric acid, thionyl chloride or combinations. In certain embodiments, the polyisocyanate may be blocked with the aforementioned compounds prior to introduction into the reactive ingredients/components used to in the composition disclosed herein.

[0024] Mixtures of isocyanates, for example, a mixture of TDI isomers (e.g., mixtures of 2,4- and 2,6-TDI isomers) or mixtures of di- and higher polyisocyanates produced by phosgenation of aniline/formaldehyde condensates may also be used as Component (i).

[0025] In some embodiments, the isocyanate compound is liquid at room temperature. A mixture of isocyanate compounds may be produced in accordance with any technique known in the art. The isomer content of the diphenyl-methane diisocyanate may be brought within the required ranges, if necessary, by techniques that are well known in the art. For example, one technique for changing isomer content is to add monomeric MDI (e.g., 2,4-MDI) to a mixture of MDI containing an amount of polymeric MDI (e.g., MDI comprising 30% to 80% w/w 4,4'-MDI and the remainder of the MDI comprising MDI oligomers and MDI homologues) that is higher than desired.

[0026] Component (i) can comprise 30% to 65% (e.g., 33% to 62% or 35% to

60%) by weight of the polyurethane insulation foam composition based the total weight of the composition.

Component (ii): Isocyanate Reactive Compound

[0027] Any of the known organic compounds containing at least two isocyanate reactive moieties per molecule may be employed as isocyanate reactive compound. For example, polyol compounds or mixtures thereof that are liquid at 25°C, have a molecular weight ranging from 60 to 10,000 (e.g., 300 to 10,000 or less than 5,000), a nominal hydroxyl functionality of at least 2, and a hydroxyl equivalent weight of 30 to 2000 (e.g., 30 to 1,500 or 30 to 800) can be used as Component (ii).

[0028] Examples of suitable polyols that may be used as Component (ii) include polyether polyols, such as those made by addition of alkylene oxides to initiators, containing from 2 to 8 active hydrogen atoms per molecule. In some embodiments, the aforementioned initiators include glycols, glycerol,

trimethylolpropane, triethanolamine, pentaerythritol, sorbitol, sucrose,

ethylenediamine, ethanolamine, diethanolamine, aniline, toluenediamines (e.g., 2,4 and 2,6 toluenediamines), polymethylene polyphenylene polyamines, N- alkylphenylene-diamines, o-chloro-aniline, p-aminoaniline, diaminonaphthalene, or combinations thereof. Suitable alkylene oxides that may be used to form the polyether polyols include ethylene oxide, propylene oxide, and butylene oxide, or combinations thereof.

[0029] Other suitable polyol compounds that may be used as Component (ii) include Mannich polyols having a nominal hydroxyl functionality of at least 2, and having at least one secondary or tertiary amine nitrogen atom per molecule. In some embodiments, Mannich polyols are the condensates of an aromatic compound, an aldehyde, and an alkanol amine. For example, a Mannich condensate may be produced by the condensation of either or both of phenol and an alkylphenol with formaldehyde and one or more of monoethanolamine, diethanolamine, and diisopronolamine. In some embodiments, the Mannich condensates comprise the reaction products of phenol or nonylphenol with formaldehyde and diethanolamine. The Mannich condensates of the present invention may be made by any known process. In some embodiments, the Mannich condensates serve as initiators for alkoxylation. Any alkylene oxide (e.g., those alkylene oxides mentioned above) may be used for alkoxylating one or more Mannich condensates. When polymerization is completed, the Mannich polyol comprises primary hydroxyl groups and/or secondary hydroxyl groups bound to aliphatic carbon atoms.

[0030] In certain embodiments, the polyols that are used are polyether polyols that comprise propylene oxide ("PO"), ethylene oxide ("EO"), or a combination of PO and EO groups or moieties in the polymeric structure of the polyols. These PO and EO units may be arranged randomly or in block sections throughout the polymeric structure. In certain embodiments, the EO content of the polyol ranges from 0 to 100% by weight based on the total weight of the polyol (e.g., 50% to 100%) by weight). In some embodiments, the PO content of the polyol ranges from 100 to 0% by weight based on the total weight of the polyol (e.g., 100%> to 50% by weight). Accordingly, in some embodiments, the EO content of a polyol can range from 99% to 33% by weight of the polyol while the PO content ranges from 1% to 67%) by weight of the polyol. Moreover, in some embodiments, the EO and/or PO units can either be located terminally on the polymeric structure of the polyol or within the interior sections of the polymeric backbone structure of the polyol.

Suitable polyether polyols include poly(oxyethylene oxypropylene) diols and triols obtained by the sequential addition of propylene and ethylene oxides to di-or trifunctional initiators that are known in the art. In certain embodiments, Component (ii) comprises the aforementioned diols or triols or, alternatively, Component (ii) can comprise a mixture of these diols and triols.

[0031] The aforementioned polyether polyols also include the reaction products obtained by the polymerization of ethylene oxide with another cyclic oxide (e.g., propylene oxide) in the presence of polyfunctional initiators such as water and low molecular weight polyols. Suitable low molecular weight polyols include ethylene glycol, propylene glycol, diethylene glycol, dipropylene glycol, cyclohexane dimethanol, resorcinol, bisphenol A, glycerol, trimethylolopropane, 1,2,6-hexantriol, pentaerythritol, or combinations thereof. [0032] Polyester polyols that can be used as Component (ii) include polyesters having a linear polymeric structure and a number average molecular weight (Mn) ranging from about 500 to about 10,000 (e.g., preferably from about 700 to about 5,000 or 700 to about 4,000) and an acid number generally less than 1.3 (e.g., less than 0.8). The molecular weight is determined by assay of the terminal functional groups and is related to the number average molecular weight. The polyester polymers can be produced using techniques known in the art such as: (1) an esterification reaction of one or more glycols with one or more dicarboxylic acids or anhydrides; or (2) a transesterification reaction (i.e. the reaction of one or more glycols with esters of dicarboxylic acids). Mole ratios generally in excess of more than one mole of glycol to acid are preferred so as to obtain linear polymeric chains having terminal hydroxyl groups. Suitable polyester polyols also include various lactones that are typically made from caprolactone and a bifunctional initiator such as di ethylene glycol. The dicarboxylic acids of the desired polyester can be aliphatic, cycloaliphatic, aromatic, or combinations thereof. Suitable dicarboxylic acids which can be used alone or in mixtures generally have a total of from 4 to 15 carbon atoms include succinic, glutaric, adipic, pimelic, suberic, azelaic, sebacic, dodecanedioic, isophthalic, terephthalic, cyclohexane dicarboxylic, or combinations thereof. Anhydrides of the aforementioned dicarboxylic acids (e.g., phthalic anhydride, tetrahydrophthalic anhydride, or combinations thereof) can also be used. In some embodiments, adipic acid is the preferred acid. The glycols used to form suitable polyester polyols can include aliphatic and aromatic glycols having a total of from 2 to 12 carbon atoms. Examples of such glycols include ethylene glycol, 1,2- propanediol, 1,3 -propanediol, 1,3-butanediol, 1,4-butanediol, 1,5-pentanediol, 1,6- hexanediol, 2,2-dimethyl-l,3-propanediol, 1,4-cyclohexanedimethanol, decamethylene glycol, dodecamethylene glycol, or combinations thereof.

[0033] Additional examples of suitable polyols include hydroxyl -terminated polythioethers, polyamides, polyesteramides, polycarbonates, polyacetals, polyolefins, polysiloxanes, and simple glycols such as ethylene glycol, butanediols, diethylene glycol, triethylene glycol, the propylene glycols, dipropylene glycol, tripropylene glycol, and mixtures thereof.

[0034] The active hydrogen-containing material may contain other isocyanate reactive material such as, without limitation, polyamines and polythiols. Suitable polyamines include primary and secondary amine-terminated polyethers, aromatic diamines such as diethyltoluene diamine and the like, aromatic polyamines, and combinations thereof.

[0035] Component (ii) can comprise 20% to 50% (e.g., 23% to 47% or 25% to 45%) by weight of the polyurethane insulation foam composition based the total weight of the composition.

Component (iii): Water

[0036] The polyurethane insulation foam composition disclosed herein comprises water. While water can be considered an isocyanate reactive compound, for purposes of this disclosure water shall be considered a distinct component from Component (ii). In other words, the polyurethane insulation foam composition disclosed herein comprises not only Component (ii) but water as well.

[0037] Any type of purified water can be used as Component (iii) provided that it has been filtered or processed to remove impurities. Suitable types of water include distilled water and water that has been purified via one or more of the following processes: capacitive deionization, reverse osmosis, carbon filtering, microfiltration, ultrafiltration, ultraviolet oxidation, and/or electrodeionization.

[0038] Component (iii) can comprise 0.25% to 2.5% (e.g., 0.4% to 9% or 3% to 8%) by weight of the polyurethane insulation foam composition based on the total weight of the composition.

Component (iv): Heterocyclic Amine Compound & Other Optional Catalysts

[0039] The polyurethane insulation foam composition disclosed herein comprises a one or more heterocyclic amine compounds comprising the structure of Formula (I).

Formula (I):

Rl - [CH2 - CH ₂ - X - ]z - CH2 - CH ₂ - R2 wherein

Rl and R2 are independently a five, six, or seven membered heterocyclic amine comprising carbon, nitrogen, or

combinations thereof;

X is oxygen or N - R3 wherein R3 is a Ci - C ₄ alkyl or C ₂ - C ₄ alkanol or C ₄ - C ₁₂ ether group; and

Z is an integer from 1 to 4.

[0040] Suitable five, six, and/or seven-membered heterocyclic amines of carbon and nitrogen that can be used as Rl and/or R2 include pyrrolidine (e.g., 2,2'- dipyrrolidinyldiethyl ether), pyrrole, imidazolidine, pyrazolidine, imidazole, pyrazole, pipendine, pyridine, piperazine, diazine, azepane, or combinations thereof. In certain embodiments, Rl and/or R2 comprise pyrrolidine, pyrrole, imidazole, piperidine, or combinations thereof. It is noted that in some embodiments, Rl may be the same or different from R2.

[0041] In certain embodiments Formula I can com rise the followin structure:

[0042] In other embodiments Formula I can com rise the followin structure:

[0043] In et other embodiments Formula I can com rise the following structures:

and/or

wherein Xi is C1-C4 alkyl (methyl, ethyl, or propyl group), C2-C4 alkanol (e.g., ethanol or propanol group), C2-C20 alkoxy group (e.g., C4-C6 ether group or diethyl ether group), or combinations thereof.

[0044] In other embodiments, Formula (I) can comprise the following structure:

[0045] In yet other embodiments, Formula (I) can comprise the following structure:

N CH ₂ -CH ₂ -0-CH ₂ -CH ₂ -OH

[0046] While Component (iv) is a catalyst that accelerates the blowing (i.e., the reaction of water with polyisocyanate to generate C0 ₂ ) and gelling (i.e., the reaction of a polyol with polyisocyanate) of the polyurethane foam composition, Component (iv) can be further used in combination with other amine or non-amine catalyst compounds to balance the blow, gel, and trimerization reactions of the polyurethane insulation foam composition to produce a foam product having the desired properties. Therefore, in certain embodiments, Component (iv) may be combined with one or more amine catalyst compounds comprising at least one tertiary amine group and/or one or more non-amine catalyst compounds.

[0047] Suitable amine catalyst compounds comprising at least one tertiary group include bis-(2-dimethylaminoethyl)ether (e.g., JEFFCAT ^® ZF-20 catalyst), Ν,Ν,Ν'- trimethyl-N'-hydroxyethylbisaminoethylether (e.g., JEFFCAT ^® ZF-10 catalyst), N-(3- dimethylaminopropyl)-N,N-diisopropanolamine (e.g., JEFFCAT ^® DPA catalyst), N,N- dimethylethanolamine (e.g., JEFFCAT ^® DMEA catalyst), blends of N,N- dimethylethanolamine aniethylene diamine (e.g., JEFFCAT ^® TD-20 catalyst), N,N- dimethylcyclohexylamine (e.g., JEFFCAT ^® DMCHA catalyst), N- methyldicyclohexylamine (e.g., POLYCAT 12 available from Evonik Industries AG), benzyldimethylamine (e.g., JEFFCAT ^® BDMA catalyst), pentamethyldiethylenetriamine (e.g., JEFFCAT ^® PMDETA catalyst), N,N,N',N",N"- pentamethyldipropylenetriamine (e.g., JEFFCAT ^® ZR-40 catalyst), N,N-bis(3- dimethylaminopropyl)-N-isopropanolamine (e.g, JEFFCAT ^® ZR-50 catalyst), N'-(3- (dimethylamino)propyl-N,N-dimethyl-l,3-propanediamine (e.g., JEFFCAT ^® Z-130 catalyst), 2-(2-dimethylaminoethoxy)ethanol (e.g., JEFFCAT ^® ZR-70 catalyst), Ν,Ν,Ν'-trimethylaminoethyl-ethanolamine (e.g., JEFFCAT ^® Z-110 catalyst; DABCO T), N-ethylmorpholine (e.g, JEFFCAT ^® EM catalyst), N-methylmorpholine (e.g., JEFFCAT ^® MM catalyst), 4-methoxyethylmorpholine, N,N'dimethylpiperzine (e.g, JEFFCAT ^® DMP catalyst), 2,2'dimorpholinodiethylether (e.g., JEFFCAT ^® DMDEE catalyst), l,3,5-tris(3-(dimethylamino)propyl)-hexahydro-s-triazine (e.g., JEFFCAT ^® TR-90 catalyst), 1-Propanamine, 3-(2-(dimethylamino)ethoxy); substituted imidazoles (e.g., 1-methylimidazole, 1,2-dimethlyimidazol (e.g., DABCO 2040 available from Evonik Industries AG and TOYOCAT DM70 available from Tosho Corporation), 1- methyl-2-hydroxyethylimidazole (e.g., N-(3-aminopropyl)imidazole, l-n-butyl-2- methylimidazole, l-iso-butyl-2-methylimidazole, Ν,Ν'-dimethylpiperazines), bis- substituted piperazines (e.g., aminoethylpiperazine, Ν,Ν',Ν'-trimethyl aminoethylpiperazine or bis-(N-methyl piperazine)urea), N-methylpyrrolidines and substituted methylpyrrolidines (e.g., 2-aminoethyl-N-methylpyrrolidine or bis-(N- methylpyrrolidine)ethyl urea), 3-dimethylaminopropylamine, N,N,N",N"- tetramethyldipropylenetriamine, tetramethylguanidine, 1,2-bis-diisopropanol, or combinations thereof. Other examples of amine catalysts include N-alkylmorpholines, N-butylmorpholine and dimoipholinodiethylether, Ν,Ν'-dimethylaminoethanol, N,N- dimethylamino ethoxyethanol, bis-(dimethylaminopropyl)-amino-2-propanol, bis- (dimethylamino)-2-propanol, bis-(N,N-dimethylamino)ethylether, Ν,Ν,Ν'-trimethyl- N'hydroxyethyl-bis-(aminoethyl)ether, Ν,Ν-dimethyl amino ethyl-N' -methyl amino ethanol, tetramethyliminobispropylamine, N,N-dimethyl-p-toluidine, diethyltoluenediamine (Ethacure 100), 3,5-dimethylthio-2,4-toluenediamine (Ethacure 300); poly(oxypropylene)triamine (JEFF AMINE ^® T-5000) reactive acid blocked catalysts (e.g., phenolic acid salt of l,8-diazabicyclo(5,4,0)undecene-7 (POLYCAT SA-1), JEFFCAT ^® LED and JEFFCAT ^® ZF brand catalysts), or combinations thereof. As used herein, JEFFCAT ^® catalysts are all available from Huntsman Petrochemical LLC. In certain embodiments, the polyurethane foam insulation composition does not comprise a guanidine compound.

[0048] Other amine catalysts which may be used polyurethane composition disclosed herein may be found in Appendix D in "Dow Polyurethanes Flexible Foams" by Herrington et al. at pages D.1-D.23 (1997), which is incorporated herein by reference. Further examples may be found in " JEFFCAT ^® Amine Catalysts for the Polyurethane Industry" version JCT-0910 which is incorporated herein by reference.

[0049] The non-amine catalyst compound, like Component (iv) and/or the amine catalyst compounds described above, is a compound that catalyzes the reaction between Component (i) with Components (ii) and/or (iii). Suitable non-amine catalyst compound that can be used include organo-metallic compounds (e.g., organic salts of transition metals such as titanium, iron, nickel), post-transition metals (e.g., zinc, tin and bismuth), alkali metals (e.g., lithium, sodium and potassium), alkaline earth metals (e.g., magnesium and calcium), or combinations thereof. Other suitable non-amine catalyst compounds include ferric chloride, ferric acetylacetonate, zinc salts of carboxylic acids, zinc 2-ethylhexanoate, stannous chloride, stannic chloride, tin salts of carboxylic acids, dialkyl tin salts of carboxylic acids, tin (II) 2-ethylhexanoate, dibutyltin dilaurate (e.g., DABCO T-12 available from Evonik Industries AG), dimethyltin dimercaptide (e.g., FOMREZ UL-22 available from Momentive Performance Materials Inc.), bismuth (III) carboxylate salts (e.g., bismuth(2- ethylhexanote)), bismuth neodecanoate (DABCO MB-20 available from Evonik Industries AG), bismuth pivalate, bismuth-based catalysts (e.g., the compounds identified in US Patent Pub. No. 016/020888), 1, 1', 1",1"'-(1,2- ethanediyldinitrilo)tetrakis[2-propanol] neodecanoate complexes (e.g., BICAT 8840 available from Shepherd Chemicals Co.), 2,2',2",2"'-(l,2- ethanediyldinitrilo)tetrakis[ethanol] neodecanoate complexes (e.g., BICAT 8842 available from Shepherd Chemicals Co.), K-KAT XC-C227 bismuth salt (available from King Industries), sodium acetate, sodium N-(2-hydroxy-5-nonylphenol)methyl- N— methylglycinate (JEFFCAT ^® TR52), bismuth(2-ethylhexanote), or combinations thereof.

[0050] Suitable trimerization catalysts that may be used in combination with the catalysts listed above (i.e., Component (iv) and/or the non-amine catalyst compounds) include potassium salts of carboxylic acids (e.g., potassium acetate, potassium pivlate, potassium octoate, potassium triethylacetate, potassium neoheptanoate, potassium neooctanoate), quaternary ammonium carboxylates (e.g., (2- hydroxypropyl)trimethylammonium 2-ethylhexanoate ("TMR"), (2- hydroxypropyl)trimethylammonium formate ("TMR-2"), tetramethylammonium pivalate, tetramethylammonium triethylacetate, TOYOCAT TRX (available from Tosoh, Corp)), or combinations thereof.

[0051] Component (iv) can comprise 0.5% to 4% (e.g., 0.7% to 3.7% or 0.5% to 3.5%) by weight of the polyurethane insulation foam composition based on the total weight of the composition. If used in combination with other amine or non-amine catalysts, then such catalysts (i.e., not the compounds used as Component (iv)) can comprise 0% to 4% (e.g., 0.2% to 3.7% or 0.5% to 3.5%) by weight of the polyurethane insulation foam composition based on the total weight of the composition.

[0052] While the amount of catalyst depends on the reactivity requirements of the application, including geographic and seasonal requirements, the weight ratio of: (1) the heterocyclic tertiary amine catalyst of Formula (I) to (2) the amine catalyst containing at least one amine group and/or the non-amine catalyst is at least 1 :5 (e.g., at least 1 :2, at least 1 : 1, at least 2: 1, or at least 5: 1).

Component (v): Hydrophilic Carboxylic Acid Compound

[0053] The polyurethane insulation foam composition disclosed herein comprises a one or more hydrophilic carboxylic acid compounds comprising the structure of Formula (II) that serves as a blowing agent for the polyurethane foam composition.

Formula (II):

wherein

R' is a divalent Ci - Cio aliphatic hydrocarbon moiety, n and m are both integers and wherein when n = 0 then m > 2 and wherein when n > 1 then m > 1.

[0054] The divalent Ci - Cio aliphatic hydrocarbon moiety can comprise a linear/branched aliphatic moiety comprising 1 to 10 carbon atoms. Suitable examples of such Ci - Cio aliphatic hydrocarbon moieties include methylene, ethylene, n- propylene, iso-propylene, n-butylene, isobutylene, n-amylene, n-decylene, 2- ethylhexylene, or combinations thereof. While the aforementioned Ci - Cio aliphatic hydrocarbon moieties do comprise two available substitution sites, it is contemplated that additional hydrogens on the hydrocarbon could be replaced with further carboxyl and/or hydroxyl groups.

[0055] Suitable compounds that can be used as Component (v) include hydroxyl- carboxylic acid, di-carboxylic acid, malonic acid, glutaric acid, maleic acid, glycolic acid, lactic acid, 2-hydroxybutyric acid, citric acid, AGS acid, or combinations thereof. AGS acid is a mixture of dicarboxylic acids (i.e., adipic acid, glutaric acid, and succinic acid) that is obtained as a by-product of the oxidation of cyclohexanol and/or cyclohexanone in the adipic acid manufacturing process. Suitable AGS acid that may be used as Component (v) include RHODIACID AGS (available from Solvay S.A.), DIBASIC ACID (available from Invista S.a.r.l), "FLEXATRAC-AGS-200 (available from Ascend Performance Materials LLC), and Gglutaric acid, technical grade (AGS) (available from Lanxess A.G.). It should be noted that hydrocarbon mono-carboxylic acids are not suitable for use as Component (v).

[0056] As used herein, a carboxylic acid shall be deemed hydrophilic when 25 gm or more (e.g., 40 gm or more or 60 gm or more) of the carboxylic acid is soluble per 100 gm of water at 25°C.

[0057] It should be noted that a hydrophobic acid would not be suitable for use as Component (v) because a hydrophobic acid would lack the aforementioned properties that are exhibited by the hydrophilic carboxylic acid compound described above. Moreover, hydrophilic mono-acids (e.g., acetic acid and butyric acid) are also not suitable for use as Component (v) despite having a solubility of > lOOgm of water at 25°C.

[0058] Component (v) can comprise 0.1% to 4% (e.g., 0.15% to 3.5% or 0.2% to 3%) by weight of the polyurethane insulation foam composition based on the total weight of the composition.

Component (vi): Halogenated Olefin Compound

[0059] The polyurethane insulation foam composition disclosed herein comprises a one or more halogenated olefin ("HFOs") compounds that serves as a blowing agent for the polyurethane foam composition.

[0060] The halogenated olefin compound used as Component (vi) comprises at least one haloalkene (e.g, fluoroalkene or chlorofluoroalkene) comprising from 3 to 4 carbon atoms and at least one carbon-carbon double bond. Suitable compounds that may be used as Component (vi) include hydrohaloolefins such as trifluoropropenes, tetrafluoropropenes (e.g., tetrafluoropropene (1234)), pentafluoropropenes (e.g., pentafluoropropene (1225)), chlorotrifloropropenes (e.g., chlorotrifloropropene (1233)), chlorodifluoropropenes, chlorotrifluoropropenes, chlorotetrafluoropropenes, hexafluorobutenes (e.g., hexafluorobutene (1336)), or combinations thereof. In certain embodiments, the tetrafluoropropene, pentafluoropropene, and/or chlorotrifloropropene compounds used as Component (vi) has no more than one fluorine or chlorine substituent connected to the terminal carbon atom of the unsaturated carbon chain (e.g., 1,3,3,3-tetrafluoropropene (1234ze); 1,1,3,3- tetrafluoropropene, 1,2,3,3,3-pentafluoropropene (1225ye), 1,1, 1-trifluoropropene, 1,2,3,3,3-pentafluoropropene, 1, 1,1,3,3-pentafluoropropene (1225zc), 1,1,2,3,3- pentafluoropropene (1225yc), (Z)-l, l, l,2,3-pentafluoropropene (1225yez), 1-chloro- 3,3,3-trifluoropropene (1233zd), l, l, l,4,4,4-hexafluorobut-2-ene (1336mzzm), or combinations thereof).

[0061] Other blowing agents that may be used in combination with the HFOs described above include air, nitrogen, carbon dioxide, hydrofluorocarbons ("HFCs"), alkanes, alkenes, mono-carboxylic acid salts, ketones, ethers, or combinations thereof. Suitable HFCs include 1, 1-difluoroethane (HFC-152a), 1, 1, 1,2-tetrafluoroethane (HFC-134a), pentafluoroethane (HFC-125), 1, 1, 1,3,3-pentafluoropropane (HFC- 245fa), 1, 1, 1,3,3-pentaflurobutane (HFC-365mfc), or combinations thereof. Suitable alkanes and alkenes include n-butane, n-pentane, isopentane, cyclopentane, 1-pentene, or combinations thereof. Suitable mono-carboxylic acid salts include methyl formate, ethyl formate, methyl acetate, or combinations thereof. Suitable ketones and ethers include acetone, dimethyl ether, or combinations thereof.

[0062] Component (vi) can comprise 2% to 10% (e.g., 2.5% to 9% or 3% to 8%) by weight of the polyurethane insulation foam composition based on the total weight of the composition.

Component (vii): Other Auxiliary Agents and Additives

[0063] The polyurethane insulation foam composition disclosed herein can comprise various auxiliary agents and additives that are known in the art of isocyanate-based insulation foam technology. Suitable additives include surfactant, fire retardants, smoke suppressants, cross-linking agents, viscosity reducer, infra-red pacifiers, cell- size reducing compounds, pigments, fillers, reinforcements, mold release agents, antioxidants, dyes, pigments, antistatic agents, biocide agents, or combinations thereof.

[0064] Examples of suitable flame retardants that may be used in the polyurethane insulation foam composition disclosed herein include organo-phosphorous compounds (e.g., organic phosphates, phosphites, phosphonates, polyphosphates, polyphosphites, polyphosphonates), ammonium polyphosphates (e.g., triethyl phosphate, diethy ethyl phosphonate, and tris(2-chloropropyl)-phosphate); and halogenated fire retardants (e.g., tetrabromophthalate esters and chlorinated parrafins).

[0065] Examples of other suitable auxiliary agents and additives that may be used in the polyurethane insulation foam composition disclosed herein include triethanolamine and glycerol cross linking agents; propylene carbonate and l-methyl-2-pyrrolidinone viscosity reducers; carbon black, titanium dioxide, and metal flake infra-red opacifiers; inert, insoluble fluorinated compounds, and perfluorinated cell-size reducing compounds; calcium carbonate fillers; glass fibers and/or ground up foam waste reinforcing agents; zinc stearate mold release agents; butylated hydroxy toluene antioxidants; azo-/diazo dyestuff and phthalocyanines pigments.

[0066] In certain embodiments, the surfactants used in the foam composition of the present disclosure can comprise one or more silicone or non-silicone based surfactants. These surfactants are typically used to control the size of the cells that form as the foam composition reacts to form the polyurethane foam product thereby allowing for the control of the internal cell structure of the foam product. In certain embodiments, a foam comprising a uniform set of small sized cells (e.g., < 300μπι) is desired because the foam will exhibit outstanding physical properties (e.g., compressive strength and thermal conductivity properties). Additionally, the aforementioned surfactants will also assist in the stabilization of the internal cells thereby ensuring that the cells do not collapse as the composition reacts to form the polyurethane foam product.

[0067] Suitable silicone surfactants that can be used in the polyurethane insulation foam composition disclosed herein include polyorganosiloxane polyether copolymers and polysiloxane polyoxyalkylene block co-polymers (e.g., Momentive's L-5345, L- 5440, L-6100, L-6642, L-6900, L-6942, L-6884, L-6972 and Evonik Industries AG's DC-193, DC5357, Si3102, Si3103, Tegostab 8490; 8496, 8536; 84205; 84210; 84501; 84701, 84715). Others silicone surfactants that can be used also are disclosed in U.S. Patent No. 8,906,974 and U.S. Patent Publication No. US 2016/0311961.

[0068] Non-silicone surfactants that can be used in the polyurethane insulation foam composition disclosed herein include non-ionic, anionic, cationic, ampholytic, semi- polar, zwitterionic organic surfactants. Suitable non-ionic surfactants include phenol alkoxylates and alkylphenol alkoxylates (e.g., ethoxylated phenol and ethoxylated nonylphenol, respectively). Other useful non-silicone non-ionic surfactants include LK- 443 (available from Evonik Industries AG) and VORASURF 504 (available from Dow Chemicals).

[0069] Component (vii) can comprise 0.5% to 10% (e.g., 0.8% to 9% or 1% to 8%) by weight of the polyurethane insulation foam composition based the total weight of the composition.

Processing [0070] A polyurethane insulation foam product (e.g., a closed-cell polyurethane insulation foam product) may be made from the polyurethane insulation foam composition disclosed herein via a one component, two component, or multi- component (i.e., greater than two component) system. As used herein, a polyurethane foam product shall be deemed to be a "closed cell" foam if the closed cell content of such foam is greater than 70% (e.g., 80% or 85%) as measured by ASTM D6226-15. Moreover, in certain embodiments, the polyurethane insulation foam product of the present disclosure would exhibit a thermal conductivity value (K-value) ranging from 0.10 to 0.16 Btu-in/hr.ft ^2o F (e.g., 0.11 to 0.15 Btu-in/hr.ft ^2o F or 0.12 to 0.14 16 Btu- in/hr.ft ^2o F) as measured by ASTM C518-17 at average plate temperature of 75°F. In a two component system, the B-Side of the polyurethane insulation foam composition, which is typically in a liquid state, is mixed with the A-Side of the composition thereby activating polymerization of the reaction system. As will be understood by one skilled in the art, Component (i) of the polyurethane insulation foam composition disclosed herein will be in the A-Side of a two component system while Component (ii) will be in the B-Side. However, it is noted that Components (iv), (v), (vi), and (vii) can be added to one or both of the A-Side and B-Side. In other words, Components (iv) - (vii) can be combined with one or both of Components (i) and (ii) simply based on the chemical and physical compatibility of the those compounds with Components (i) and (ii).

[0071] Regardless of the number of components used in connection with the polyurethane insulation foam composition disclosed herein, the relative proportions of the components may be metered, either by weight or by volume, to provide a ratio of free isocyanate groups to the total of the isocyanate-reactive groups ranging from 0.9 to 5 (e.g., 0.95 to 4 or 1 to 3.5) based on the total isocyanate and isocyanate reactive compounds present in the polyurethane insulation foam composition.

[0072] In certain embodiments, a polyurethane foam product may be made using the polyurethane insulation foam composition and a one-shot, prepolymer, or semi- prepolymer technique together with a mixing method such as impingement mixing. In other embodiments, after mixing, the polyurethane insulation foam composition (while still in a substantially liquid state) may be dispensed into a cavity (i.e., cavity filling), molded, open poured (e.g., process for making slabstock), sprayed, frothed, or laminated with facing materials such as paper, metal, plastics, or wood-board. Such foam products are useful in any insulating surfaces or enclosures such as houses, roofing, buildings, refrigerators, freezers, appliances, piping, and vehicles.

[0073] The preparation of polyurethane foams using the compositions described herein may follow any of the methods well known in the art can be employed (e.g., see Saunders and Frisch, Volumes I and II Polyurethanes Chemistry and technology, 1962, John Wiley and Sons, New York, N.Y.; or Oertel, Polyurethane Handbook 1985, Hanser Publisher, New York; or Randall and Lee, The Polyurethanes Book 2002).

Polyisocyanurate Foam Product

[0074] While the present disclosure has been focused on a polyurethane insulation foam composition and the resulting polyurethane foam product (e.g., a rigid, closed- cell polyurethane insulation foam product), the composition can also be used to form a polyisocyanurate foam product (e.g., a rigid, closed-cell polyisocyanurate foam product) simply by adding one or more trimerization catalysts to the reactive system disclosed herein. Suitable isocyanate trimerization catalysts that may be added to Components (i) - (vii) include those listed above. Accordingly, in some embodiments, the polyurethane insulation foam composition is a polyisocyanurate insulation foam composition. It is noted that the polyisocyanurate insulation foam composition would form a polyisocyanurate foam product that comprises both polyisocyanurate and polyurethane reaction products.

[0075] In certain embodiments, the relative proportions of the components used to form the polyisocyanurate insulation foam composition may be metered, either by weight or by volume, to provide a ratio of free isocyanate groups to the total of the isocyanate-reactive groups in a range of from ranging from 2 to 5 (e.g., 2.25 to 4) based on the total isocyanate and isocyanate reactive compounds present in the polyurethane insulation foam composition.

Modifications

[0076] While specific embodiments of the disclosure have been described in detail, it will be appreciated by those skilled in the art that various modifications and alternatives to those details could be developed in light of the overall teachings of the disclosure. Accordingly, the particular arrangements disclosed are meant to be illustrative only and not limiting as to the scope of the disclosure which is to be given the full breadth of the claims appended and any and all equivalents thereof. Therefore, any of the features and/or elements which are listed above may be combined with one another in any combination and still be within the breadth of this disclosure.

Examples

Components:

[0077] The following compounds are referred to in the examples:

[0078] Polyol 1 : A polyether polyol having an OH value of 360 mg KOH/g initated with sucrose and di ethylene glycol.

[0079] Polyol 2: A polyether polyols having an OH value of 500 mg KOH/g. polymethylene polyphenylene polyamine and di ethylene glycol.

[0080] Polyol 3 : A polyether polyol having an OH value of 35 mg KOH/g initiated with glycerol.

[0081 ] JEFFC AT ^® DMCHA: N, N-dimethylcyclohexylamine catalyst available from Huntsman Petrochemical LLC.

[0082] JEFFCAT ^® ZF-20: Bis-(2-dimethylaminoethyl)ether catalyst available from

Huntsman Petrochemical LLC.

[0083] Catalyst A: 2,2' -dipyrrolidinyl diethyl ether.

[0084] POLYC AT ^® 203 : a reactive amine catalyst available from Evonik Industries AG.

[0085] Glutaric acid: Glutaric acid available from Sigma-Aldrich.

[0086] TEGOSTAB ^® B8491 : A hydrolysis-resitant silicone surfactant available from

Evonik Industries AG.

[0087] HFO-1233zd(E): l-chloro-3,3,3-trifluoropropene available from Honeywell International Inc. as Solstice ^® LB A.

[0088] RUB IN ATE M: Polymeric MDI having an NCO value of 30.5% available from Huntsman International LLC.

Description of the FOAM REACTIVITY TEST:

[0089] A composition's (e.g., the compositions described in Tables 1 and 2) REACTIVE SHIFT (i.e., CT REACTIVE SHIFT as calculated by Formula X, TFT REACTIVE SHIFT as calculated by Formula Y, and EOR REACTIVE SHIFT as calculated by Formula Z) was calculated through the use various data points gathered via the FOAM REACTIVITY TEST. The FOAM REACTIVITY TEST comprises the following steps: (i) equilibrating a composition's A-Side (polyol premix) and B-Side (isocyanate) to 15°C by placing the A- and B-Side in a cooling thermostat (e.g., LAUDA Alpha RA 24 Cooling thermostat) (ii) pouring the contents of the equilibrated A-Side and B-Side into a 32-oz non-waxed paper cup (e.g., Solo H4325-2050) thereby combining the two components; (ii) mixing the combined components for 4 seconds at 2500 rpm using a mechanical mixer (e.g., Caframo BDC3030 stirrer); (iii) allowing the components of the composition to react thereby forming the polyurethane foam product; and (iv) measuring one or more of the composition's CT, TFT, and/or GT (each defined below) during the formation of the polyurethane foam product.

[0090] For purposes of this disclosure, the following terms shall be defined as follows:

[0091] Cream Time ("CT") means the elapsed time between the moment a composition's isocyanate component is mixed with the composition's isocyanate reactive component and the formation of the fine froth or cream in the composition.

[0092] Gel Time ("GT") means the elapsed time between the moment a composition' s isocyanate component is mixed with the composition's isocyanate reactive component and the point at which a distinct cross-linked polymer network is formed. Experimentally, this cross-linked network is considered formed when a 6" wooden tongue depressor is inserted into the forming foam and has a string of polyurethane attached to it as the tongue depressor is pulled out of the forming foam.

[0093] Tack Free Time ("TFT") means the elapsed time between the moment a composition's isocyanate component is mixed with the composition's isocyanate reactive component and the point at which the outer skin of the foam loses its stickiness or adhesive quality. Experimentally, such loss of stickiness is when a 6" wooden tongue depressor (e.g., Puritan 705) is brought into contact with the surface of the reaction mixture and appears non-sticky when it is removed from the surface.

Calculation of REACTIVE SHIFT:

[0094] A composition's CT REACTIVE SHIFT was calculated using Formula X:

Formula X:

CT REACTIVE SHIFT = 100 * [(CT ₃₅ - CT ₀ ) / CT ₀ ] wherein

CT ₃ 5 means a composition's CT as determined using the FOAM REACTIVITY TEST after the composition's B- Side has been aged at 40°C in a closed, pressure-rated, glass container (e.g., ACE GLASS Pressure Bottle (#8648-251)) that was placed in an oven (e.g., VWR 1370GM oven) for 35 days. CTo means a composition's CT as determined using the FOAM REACTIVITY TEST after the composition's B- Side has been aged at 40°C in a closed, pressure-rated, glass container (e.g., ACE GLASS Pressure Bottle (#8648-251)) that was placed in an oven (e.g., VWR 1370GM oven) for 0 days.

[0095] A composition's TFT REACTIVE SHIFT was calculated using Formula Y:

Formula Y:

TFT REACTIVE SHIFT = 100 * [(TFT35 - TFTo) / TFTo] wherein

TFT35 means a composition's TFT as determined using the FOAM REACTIVITY TEST after the composition's B-Side has been aged at 40°C in a closed, pressure-rated, glass container (e.g., ACE GLASS Pressure Bottle (#8648-251)) that was placed in an oven (e.g., VWR 1370GM oven) for 35 days.

TFTo means a composition's TFT as determined using the FOAM REACTIVITY TEST after the composition's B-Side has been aged at 40°C in a closed, pressure-rated, glass container (e.g., ACE GLASS Pressure Bottle (#8648-251)) that was placed in an oven (e.g., VWR 1370GM oven) for 0 days.

[0096] A composition's GT REACTIVE SHIFT was calculated using Formula Z:

Formula Z:

GT REACTIVE SHIFT = 100 * [(GT35 - GTo) / GT ₀ ] wherein

GT35 means a composition's GT as determined using the FOAM REACTIVITY TEST after the composition's B- Side has been aged at 40°C in a closed, pressure-rated, glass container (e.g., ACE GLASS Pressure Bottle (#8648-251)) that was placed in an oven (e.g., VWR 1370GM oven) for 35 days.

GTo means a composition's GT as determined using the FOAM REACTIVITY TEST after the composition's B- Side has been aged at 40°C in a closed, pressure-rated, glass container (e.g., ACE GLASS Pressure Bottle (#8648-251)) that was placed in an oven (e.g., VWR 1370GM oven) for 0 days. [0097] It should be noted that in some embodiments, the temperature used to age a composition's B-side as described above can range from 30°C to 40°C (e.g, 30°C to 55°C).

Overview of Table 1 :

[0098] Table 1 shows various data points for four polyurethane compositions used to make a polyurethane foam product. The B-side for each composition was aged at 40°C in a in an ACE GLASS Pressure Bottle (#8648-251) and placed in a VWR 1370GM oven for the total number of days listed in Table 1. When a particular day was reached (e.g., at Day 21 or 35), the B-side was taken out of the oven and placed in a water bath at 15°C. Once the polyol premix reached bath temperature, visual inspection of the polyol premix was made to assess whether it was clear or cloudy and whether a precipitate (abbreviated as "ppt" in the Table 1) can be seen at the bottom of container.

After the visual inspection, a foam product was made using the steps of the FOAM REACTIVITY TEST (described above) and the composition's REACTIVE SHIFT (i.e., CT REACTIVE SHIFT as calculated by Formula X, TFT REACTIVE SHIFT as calculated by Formula Y, and EOR REACTIVE SHIFT as calculated by Formula Z) was calculated using data points measured during the FOAM REACTIVITY TEST.

[0099] It should be noted that a foam product was made for each day that is represented in the Tables (e.g., Day 0, 21, or 35).

Example 1 :

[00100] Table 1 shows four polyurethane compositions to make a polyurethane foam product. The compositions' components (including the amounts thereof) were chosen to reflect what would typically be used in a pour-in-place insulation foam application (e.g., foams used in refrigerators, insulated doors, freezers, and water heaters). In the compositions shown in Table 1, only the catalyst and acid used were the only parameters changed among the compositions.

Table 1

Foams / Formulations A B C D

Polyol Premix

Polyol 1 49.6 49.6 49.6 49.6 Polyol 2 6.8 6.8 6.8 6.8 Polyol 3 20.8 20.8 20.8 20.8

TEGOSTAB ^® B8491 1.6 1.6 1.6 1.6 JEFFCAT ^® DMCHA 0 0 0.58 0.58 POLYCAT ^® 203 0.90 0.90 0 0

JEFFCAT ^® ZF-20 0.37 0 0 0

Catalyst A 0 0.54 0.55 0.55

Glutaric acid 0 0 0 1.7

Water 1.7 1.7 1.7 1.7

HFO-1233zd[E] 18.2 18.1 18.3 18.1

Total Polyol Premix 100.0 100.0 100.0 101.4

Isocyanate

Rubinate M 140 140 140 142

Isocyanate/ Polyol Premix ratio 1.40 1.40 1.40 1.40

Aging time at 40°C, (days) 0 0 0 0

Foam CT/GT/TFT (sec)* 9/95/165 10/95/164 11/96/157 9/112/192

Free Rise Density, pcf 1.73 1.75 1.76 1.73

Aging time at 40°C, (days) 21 21 21 21

Foam CT/GT/TFT (sec)* 12/134/230 12/125/189 13/117/181 9/112/180

Free Rise Density, pcf 1.81 1.84 1.84 1.75

Aging time at 40°C, (days) 35 35 35 35

Foam CT/GT/TFT (sec)* 24/151/262 14/130/204 15/123/194 9/113/186

Free Rise Density, pcf 1.8 1.79 1.83 1.74

No

Aging time at 40°C, (days) No Data*** Data*** 63 63

No

Foam CT/GT/TFT (sec)* No Data*** Data*** 22/143/218 9/118/185

No

Free Rise Density, pcf No Data*** Data*** 1.91 1.73

CT REACTIVITY SHIFT** 167 40 36 0

GT REACTIVITY SHIFT** 59 27 28 0.9

TFT REACTIVITY SHIFT** 59 34 24 -3

* CT, GT, and TFT are defined above

** Calculated as described above

*** No data collected- see Paragraph [0099] below

[00101] The composition for Foam D is one embodiment of the present disclosure.

Foams A, B and C are simply comparative examples.

[00102] As can be seen in Table 1 , the composition for Foam A used POLYCAT ^® 203

in combination with another widely known strong blowing catalyst. Formulation B used

POLYCAT ^® 203 in combination with Catalyst A. The reactivity of the compositions used for Foams A and B changed significantly as they aged at 40°C. Reactivity data at Day 63 was not collected for those compositions because as there was too much precipitate formed and we were unable to get the compositions to make a foam product.

[00103] The compositions for Foams C and D used JEFFCAT ^® DMCHA in combination with Catalyst A. The composition for Foam D used glutaric acid while the composition for Foam C lacked the acid. When compared to the other compositions, Foam D had better reactivity after aging the polyol premix at 40°C for 35 days and 63 days.

Appearance of Foam Products

[00104] It should also be noted that the foam products made from the compositions for Foam D (which represent an embodiment of the present disclosure) had internal excellent appearance (e.g., uniform internal cell size and free of internal voids) and had fine internal cells with no evidence of cell collapse. In other words, good quality foam product was produced using the compositions disclosed herein irrespective of whether the polyol premix used was fresh or aged.