Title:
PRESS HARDENED STEEL WITH EXTREMELY HIGH STRENGTH
Document Type and Number:
WIPO Patent Application WO/2018/160462
Kind Code:
A9
Abstract:
Press hardened steels exhibit increased strength in the press hardened steel parts without a corresponding decrease in elongation. Substitutional elements are included in the steel composition to increase the strength of martensite through a combination of substitutional solute strengthening and a reduction in softening that results from autotempering. Softening as a result of autotempering is minimized by suppression of the martensite start (Ms) temperature through the alloying. As a result of the increased hardenability in the proposed compositions that results from various additions of manganese, chromium, molybdenum, and niobium, the steel compositions permit a boron-free press hardening steel.

Inventors:
PAVLINA ERIK (US)
Application Number:
PCT/US2018/019483
Publication Date:
October 04, 2018
Filing Date:
February 23, 2018
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
AK STEEL PROPERTIES INC (US)
International Classes:
C22C38/02; B21D22/02; B32B15/01; C21D6/00; C21D8/02; C22C38/04; C22C38/12; C22C38/22; C22C38/24; C22C38/26; C22C38/32; C22C38/38; C23C2/06; C23C2/12; C23C2/40
Attorney, Agent or Firm:
SCHOEN, Ann, G. et al. (US)
Download PDF:
Claims:
What is Claimed is:

1. A press hardenable steel comprising, by weight percent, 0.01 to 0.5 % carbon, 2.0 to 8.0 % manganese, 0.1 to 0.5% silicon, 0.0 to 6.0 % molybdenum, 0.0 to 6.0 % chromium, 0.0 to 0.1 % niobium, 0.0 to 0.15% vanadium, and 0.0 to 0.005% boron.

2. The press hardenable steel of claim 1 further comprising 0.1 to 0.35% carbon.

3. The press hardenable steel of claim 1 further comprising greater than 3.0 % to 8% manganese.

4. The press hardenable steel of claim 1 further comprising 2.0 to 5.0% manganese.

5. The press hardenable steel of claim 1 further comprising 0.1 to 2.0%

molybdenum.

6. The press hardenable steel of claim 1 further comprising 2.0 to 6.0% chromium.

7. The press hardenable steel of claim 1 further comprising 0.01 to 0.1 % niobium.

8. The press hardenable steel of claim 1 further comprising 0.01 to 0.15% vanadium.

9. The press hardenable steel of claim 1 having two outer surfaces, and further

comprising an aluminum-based coating or a zinc-based coating applied to at least one outer surface.

10. A press hardenable steel comprising, by weight percent, 0.01 to 0.5 % carbon, 2.0 to 8.0 % manganese, 0.1 to 0.5% silicon, and at least one of 0.1 to 6.0 % molybdenum, 0.2 to 6.0 % chromium, 0.01 to 0.1% niobium, and 0.01 to 0.15% vanadium.

1 1. A press hardenable steel comprising, by weight percent, 0.01 to 0.5 % carbon, 2.0 to 8.0 % manganese, 0.1 to 0.5% silicon, and wherein the Ms temperature is less than 365°C.

12. The press hardenable steel of claim 11 , wherein the press hardenable steel can be fully austenitized at a PMT of less than 850°C.

13. The press hardenable steel of claim 12, wherein the press hardenable steel has, after press hardening or hot stamping, an ultimate tensile strength of at least 1480 MPa and a total elongation of at least 6%.

Description:
PRESS HARDENED STEEL WITH EXTREMELY HIGH STRENGTH

Erik James Pavlina PRIORITY

[0001] This application claims priority to U. S. Provisional Application Serial

Nos. 62/465,523, filed March 1, 2017, entitled "Press Hardened Steel with Extremely High Strength and Method for Production," the disclosure of which is incorporated by reference herein.

BACKGROUND

[0002] The present application relates to an improvement in press hardened steels, hot press forming steels, hot stamping steels, or any other steel that is heated to an austenitization temperature, and formed and quenched in a stamping die to achieve desired mechanical properties in the final part. In this application, they will all be referred to as "press hardened steels."

[0003] Press hardened steels are primarily used as structural members in automobiles where high strength, low weight, and improved intrusion resistance is desired by automobile manufacturers.

[0004] Conventional press hardened steels, such as 22MnB5 steel, are alloyed with boron for increased hardenability. The strength of press hardened steels can easily be increased by increasing the carbon content of the steel however high levels of carbon reduce weldability and reduce the elongation to fracture (also called total elongation) of the steel.

[0005] Current industrial processing of prior art press hardened steel involves heating a blank (piece of steel sheet) to a temperature greater than the A3 temperature (the austenitization temperature), typically in the range 900-950°C, holding the material at that temperature for a certain duration, placing the austenitized blank into a hot stamping die, forming the blank to the desired shape, and quenching the material in the die to a low temperature such that martensite is formed. The end result is a material with a high ultimate tensile strength and a fully martensitic microstructure.

The as-quenched microstructure of prior art press hardened steel is fully martensitic. Conventional press hardened steels (for example 22MnB5) have ultimate tensile strengths of approximately 1500 MPa with total elongations of approximately 6-8%.

SUMMARY

The steels of the present application solve the problem of low elongation while maintaining, or increasing, strength in press hardened steels by a novel alloying strategy that incorporates transition metal elements that increase the strength of the steel through a combination of substitutional solute strengthening and a reduction in softening that results from autotempering.

DESCRIPTION OF DRAWINGS

Fig. 1. depicts a light optical micrograph of a press hardened steel of alloy 4339-1 after austenitizing at PMT 848 °C for 300 seconds and simulated press hardening

Fig. 2 depicts a light optical micrograph of a press hardened steel of alloy 4339-2 after austenitizing at PMT 816 °C for 300 seconds and simulated press hardening.

Fig. 3 depicts a light optical micrograph of a press hardened steel of alloy 4340-1 after austenitizing at PMT 782 °C for 300 seconds and simulated press hardening. [0011] Fig. 4 depicts a light optical micrograph of a press hardened steel of alloy 4340-2 after austenitizing at PMT 759 °C for 300 seconds and simulated press hardening.

[0012] Fig. 5 depicts a light optical micrograph of a press hardened steel of alloy 4341 -1 after austenitizing at PMT 821 °C for 300 seconds and simulated press hardening.

[0013] Fig. 6 depicts a light optical micrograph of a press hardened steel of alloy 4341 -2 after austenitizing at PMT 836 °C for 300 seconds and simulated press hardening.

[0014] Fig. 7 depicts a light optical micrograph of a press hardened steel of alloy 4342-1 after austenitizing at PMT 821 °C for 300 seconds and simulated press hardening.

[0015] Fig. 8 depicts a light optical micrograph of a press hardened steel of alloy 4342-2 after austenitizing at PMT 841 °C for 300 seconds and simulated press hardening.

DETAILED DESCRIPTION

[0016] The press hardened steels of the present application increase the

strength of press hardened steel parts without a corresponding decrease in elongation. The strength of press hardened steels can easily be increased by increasing the carbon content of the steel, however high levels of carbon reduce weldability and reduce the elongation to fracture of the steel. The present alloys employ a novel alloying strategy that uses substitutional elements to increase the strength of martensite through a combination of substitutional solute strengthening and a reduction in softening that results from autotempering. Softening as a result of autotempering is minimized by suppression of the martensite start (Ms) temperature through alloying. As a result of the increased hardenability in the present compositions that results from various additions of manganese, chromium, molybdenum, niobium, and vanadium, the novel compositions permit a boron-free press hardening steel.

[0017] In addition to iron and other impurities incidental to steelmaking, the embodiments of the present alloys include manganese, silicon, carbon, chromium, molybdenum, niobium, and/or vanadium, all in concentrations sufficient to obtain one or more of the above benefits. In some embodiments, the press hardened steel includes manganese, silicon, carbon, and at least one of chromium, molybdenum, niobium, and/or vanadium, as well as iron and other impurities incidental to steelmaking. The concentrations and effects of these and other alloying elements are summarized below.

[0018] Carbon is added to reduce the martensite start temperature, provide solid solution strengthening, and to increase the hardenability of the steel. Carbon is an austenite stabilizer. In certain embodiments, carbon can be present in concentrations of 0.1 - 0.50 weight %; in other embodiments, carbon can be present in concentrations of 0.1 - 0.35 weight %; and in still other embodiments, carbon can be present in concentrations of about 0.22 - 0.25 weight %.

[0019] Manganese is added to reduce the martensite start temperature, provide solid solution strengthening, and to increase the hardenability of the steel. Manganese is an austenite stabilizer. In certain embodiments, manganese can be present in concentrations of 2.0 - 8.0 weight %; in other embodiments, manganese can be present in concentrations of 2.0 - 5.0 weight %; in still other embodiments, manganese can be present in concentrations of greater than 3.0 weight % - 8.0 weight %; and in still other embodiments, manganese can be present in concentrations of greater than 3.0 weight % -5.0 weight %. [0020] Silicon is added to provide solid solution strengthening. Silicon is a ferrite stabilizer. In certain embodiments, silicon can be present in concentrations of 0.1 - 0.5 weight %; in other embodiments, silicon can be present in concentrations of 0.2 - 0.3 weight %.

[0021] Molybdenum is added to provide solid solution strengthening, to

increase the hardenability of the steel, to provide microstructural refinement, and to protect against embrittlement. In certain embodiments, molybdenum can be present in concentrations of 0-2.0 weight %; in other embodiments, molybdenum can be present in concentrations of 0.0-0.6 weight %; in still other embodiments, molybdenum can be present in concentrations of 0.1 - 2.0 weight %; in other embodiments, molybdenum can be present in concentrations of 0.1 - 0.6 weight %; and in yet other embodiments, molybdenum can be present in concentrations of 0.4 - 0.5 weight %.

[0022] Chromium can be added to reduce the martensite start temperature, provide solid solution strengthening, and increase the hardenability of the steel. Chromium is a ferrite stabilizer. In certain embodiments, chromium can be present in concentrations of 0 - 6.0 weight %; in other embodiments, chromium can be present in concentrations of 2.0 - 6.0 weight %; in other embodiments, chromium can be present in concentrations of 0.2 - 6.0 weight %; and in other embodiments chromium can be present in concentrations of 0.2 - 3.0 weight %.

[0023] Niobium can be added to increase strength and improve hardenability of the steel. In some embodiments niobium can also be added to provide improved grain refinement. In certain embodiments, niobium can be present in concentrations of 0 - 0.1 weight %; in other embodiments, niobium can be present in concentrations of 0.01 - 0.1 weight %; and in other embodiments, niobium can be present in concentrations of 0.001 - 0.055 weight %. [0024] Vanadium can be added to increase strength and improve hardenability of the steel. In certain embodiments, vanadium can be present in concentrations of 0 - 0.15 weight %; and in other embodiments, vanadium can be present in concentrations of 0.01 - 0.15 weight %.

[0025] Boron can be added to increase the hardenability of the steel. In certain embodiments, boron can be present in concentrations of 0 - 0.005 weight %.

[0026] The press hardened steels can be processed using conventional steel making, roughing, and finishing processes. For example, the steels can be continuously cast to produce slabs approximately 12-25 cm in thickness. Slabs are then reheated at temperatures of 1200-1320 °C, and hot rolled to a final gauge of >2.5 mm, with the final reduction pass occurring at a temperature of approximately 950 °C. Steels are then coiled at temperatures of 400-675 °C. After cooling, the steel coils may be annealed at temperatures of 600-900 °C for times longer than 1 second, and pickled, prior to cold reduction. One or more intermediate annealing and reduction steps may be required before reaching the desired thickness. Such intermediate annealing utilizes temperatures similar to the first annealing treatment.

[0027] The alloys of the present application can also be coated with an

aluminum-based coating, a zinc-based coating (either galvanized or galvannealed), after cold rolling and before hot stamping. Such coating can be applied to the steel sheet using processes known in the art, including hot dip coating or electrolytic coating. Because of the lower critical temperatures, press hardening of the present alloys after they have been coated is less likely to result in melting of the coating and the detrimental effects associated with such melting. [0028] Example 1

[0029] Table 1 lists steel compositions of the press hardened steel alloys that have been tested.

[0030] Alloys of the composition of Table 1 were prepared using standard steel making processes. All concentrations are in weight %. In addition, a prior art 22MnB5 press hardened steel was also prepared, and its typical composition is also provided.

TABLE 1

[0031] Mechanical properties were assessed after a press hardening simulation in which the steels of Table 1 were austenitized at peak metal temperatures (PMT) that were 25-30 °C above the Ac3 temperature (that is, the temperature at which the ferrite to austenite transformation is complete on heating). Steels were then quenched in flat, water- cooled copper dies. Uniaxial tensile tests at room temperature and quasi-static rates were performed to measure the strength and elongation of the press hardened steels. Table 2 summarizes processing temperatures and mechanical properties of the steels after austenitizing for a specified time. The trial heats exhibited unexpectedly high strengths at low carbon concentrations that are typical of the conventional 22MnB5 press hardening steel.

[0032] Table 2 - Mechanical Properties of Press Hardened Steels After

Austenization for Time and Simulated Press Hardening

4341-2 285 836 1200 1254 1814 7.6

4342-1 294 821 300 1297 1891 7.8

4342-1 294 821 600 1218 1854 7.4

4342-1 294 821 1200 1247 1837 7.5

4342-2 263 841 300 1425 2006 7.3

4342-2 263 841 600 1324 1945 7.4

4342-2 263 841 1200 1352 1914 7.4

22MnB5 410 930 300 1034 1461 8

[0033] While substitutional elements are typically considered to be very weak solute strengtheners in as-quenched martensite, the ultimate tensile strength remarkably increased by approximately 156 MPa per weight percent of manganese addition and by approximately 83 MPa per weight percent of chromium addition. Most surprisingly, there was no

degradation in elongation to fracture (that is, total elongation) relative to the conventional 22MnB5 steel for steels with ultimate tensile strengths up to and exceeding 2000 MPa. Ultimate tensile strengths in excess of 1800 MPa were achieved using several alloying strategies: Mn (4340-1, 4340-2), Mn+Mo+Nb (4341-1), Mn+Mo+Nb+V (4341-2), Mn+Cr (4342-2). For all of these alloys, total elongation was 7-8%.

[0034] Fig. 1-8 are light optical micrographs after austenitizing for 300

seconds and simulated press hardening of the steels in accordance with the parameters of Table 2. These figures show a primarily martensitic structure with increasing grain refinement as one moves from Fig. 1 through Fig. 8, in part because of smaller starting austenite grain structure resulting from the lower austenitization temperature and/or because of the refinement resulting from the additional alloying.

[0035] Example 2

[0036] Mechanical properties were assessed after a press hardening simulation in which samples of the steel alloy 4340-2 was austenitized at varying temperatures and time. The samples were then quenched in flat, water- cooled copper dies. Uniaxial tensile tests at room temperature and quasi-static rates were performed to measure the strength and elongation of the press hardened steels. Table 3 summarizes processing temperatures and mechanical properties of the samples after austenitizing for a specified time. The trial samples showed the benefit of the lower austenization temperature made possible by the present press hardened alloys. As shown in Table 3, the higher austenization temperature resulted in lower yield strength and tensile strength. Additionally, the ultimate tensile strength obtained at the lowest austenitization temperature still exceeds 1900 MPa after austenitizing for 1200 seconds prior to press hardening, which demonstrates beneficial robustness to the process window for this alloy.

Table 3 - Mechanical Properties of Alloy 4340-2 After Austenization for Time and Simulated Press Hardening

[0038] Example 3:

[0039] A press hardenable steel comprising by total weight percentage of the steel:

[0040] (a) from 0.1 % to 0.5 %, preferably from 0.1 % to 0.35%, more

preferably from 0.22 - 0.25%, Carbon;

[0041] (b) from 2.0% to 8.0 %, preferably from greater than 3.0% to 8 %;

more preferably from 2.0 to 5.0 %, and more preferably from greater than 3.0% to 5.0%, Manganese; and

[0042] (c) from 0.1 % to 0.5 %, preferably from 0.2% to 0.3%, Silicon; [0043] wherein said steel is substantially fully austenitized prior to forming and quenching in a hot stamping die.

[0044] Example 4

[0045] A press hardenable steel of Example 4 or any one of the following

Examples, further comprising from 0.0% to 6.0 %, preferably from 0.0% to 2.0%, more preferably 0.1% to 6.0%, more preferably 0.1% to 2.0%, more preferably 0.1 % to 0.6%, and more preferably 0.4% to 0.5%), Molybdenum.

[0046] Example 5

[0047] A press hardenable steel of either one of Examples 3 and 4, or any one of the following Examples, further comprising from 0% to 6.0%, preferably 0.2% to 6.0%, more preferably 2.0% to 6.0%, and more preferably 0.2% to 3.0%, Chromium.

[0048] Example 6

[0049] A press hardenable steel of any one of Examples 3 through 5, or any one of the following Examples, further comprising from 0.0% to 0.1 %, preferably 0.01 % to 0.1 %, more preferably 0.001 to 0.055% Niobium.

[0050] Example 7

[0051] A press hardenable steel of any one Examples 3 through 6, or any one of the following Examples, further comprising from 0.0% to 0.15%, preferably 0.01% to 0.15%, Vanadium.

[0052] Example 8

[0053] A press hardenable steel of any Examples 3 through 7, or any one of the following Examples, further comprising from 0% to 0.005 % Boron. [0054] Example 9

[0055] A press hardenable steel of any of Examples 3 through 8, or any one of the following Examples, wherein the M s temperature is less than 365°C.

[0056] Example 10

[0057] A press hardenable steel of any of Examples 3 through 9, or any one of the following Examples, wherein the PMT for austenization is less than 850°C.

[0058] Example 11

[0059] A press hardenable steel of any one of Examples 3 through 10, or any one of the following Examples, wherein the press hardenable steel has, after press hardening or hot stamping, an ultimate tensile strength of at least 1480 MPa and a total elongation of at least 6%.

[0060] Example 12

[0061] A press hardenable steel of any one of Examples 3 through 11 , wherein the press hardenable steel is coated with an aluminum-based coating or a zinc-based coating (either galvanized or galvannealed), after cold rolling and before hot stamping.