BfiCKQKXϊB OP THE DSVHΪTICH

The present invention relates to consolidation and densif ication of metal alloy powders. The field of the invention comprises production of metal parts from powders to achieve essentially full density, i.e., 98-100% of theoretical -density. The prior art approaches to such production are troubled by high capital and operating costs of high temperature and/or high pressure production equipment, and problems of grain growth during production.

In m-any applications of sintered powder metallurgy (PM) parts, essentially full density is required to meet require¬ ments for fatigue strength, ductility, ultimate tensile strength, impact strength, corrosion resistance and hardness which are typically exhibited by cast, forged or wrought parts. Such fully dense PM parts heretofore have been made using powder metallurgy methods involving high temperature vacuum sintering which is considered expensive and difficult to control. Generally, vacuum sintering yields a wide uncon- trolled distribution of sintered densities between 94 and 98.5 percent of theoretical. Another approach which has been used

with the alloys Ti-6A1- ₄ V, Monel, M-2, 4600, 4650, 316 , Stellite 21 and Stellite 6 comprises processing to full densi¬ ty by first pressing suitably prepared alloy metal powders and sintering them to a condition of closed porosity, usually about 92 percent of theoretical density, followed by hot isostatic pressing ("HIP") at 15,000 psi and temperatures 100 to; 3_00°C below the sintering temperatures for closed porosity. With this method, the problems of achieving full densi¬ ty- were essentially solved. However, the cost of high pres- D. sure- HIP equipment was a major deterrent to using this method irr production.

Processes, and equipment, per se, for sintering, die pressing and/or isostatic pressing, per se and in hybrid combinations are well known for consolidation and densifica- 5 tiorr of powder compacts to over 95% of theoretical density. Ther compact so treated may be a simple geometric form, such as a- cube, or a complex shaped part.

It is the object of the invention to provide technical and economical feasibility for metal alloy parts PM production 0 through, a modified form of sintering described herein over¬ coming the above problems.

SUMMARY OF THE INVENTION

The invention comprises low-pressure assisted sintering of a metal alloy powder compact with low pressure. The cost 5 of the pressure vessel and associated compressors and control valves are considerably less under such processing than for high pressure HIP equipment and operating costs for gas will be substantially less at low pressure. The .ability to apply the Law pressure almost instantaneously is a considerable advantage in many ways. In pressure assisted sintering (PAS) , the pressure is applied immediately (or the equ ..lent of

immediately, i.e., recreating the condition of pre-hold after a long time hold) after sintering a pressed compact to closed porosity (75 to 80% of theoretical density). In this process the applied processing pressure for pressure-assisted sin- tering, is an order of magnitude less than would be required in conventional HIP and the temperature during the pressure assist stage is 100 to 300 °C below the sintering temperature, (for a first state of sintering to closed porosity under vacuum or a single atmosphere of reacitive gas) i.e., at a temperature equal or nearly equal to the sinter temperature within minus 20% to plus 10%, preferrably within minus 10% to plus 5%. Densification to 98 - 99% of theoretical density of the metal is achieved via pressure assistance of the sin¬ tering, at pressures between 1,000 and 3 ,000 psi. The powder mixture can be preformed as an alloy or comprise a mixture of metal alloy elemental components. Master alloy portions can also be included.

A closed porosity is established in the initial long sintering step and collapsed during the follow-on, short, pressure assisted step. The two steps together comprise -about 40 - 70% of the time needed for conventional sintering. In use of the invention for some metals a temperature spike may be induced during the pressure assistance portion of the sintering (preferrably early in such portion, during the rise from ambient to 2000 psi) to weaken the body, so that applied pressure collapses remaining voids; this tends to reduce the needed time of pressure assistance. Inert gas pressure is applied (with or without the temperature spike) in the range of 1,000 to 3,000 psi for a period of time sufficient to allow complete densification. The pressure is preferrably applied at or near the sintering temperature immediately following the attainment of closed porosity. But interruptions are toler-

able if cool down and very rapid re-heat can be achieved.

Both the initial sintering without pressure and follow- on pressure sintering steps should be carried out in the same pressure-furnace with the two stages immediately concurrent. Alternatively, the process can be carried out in two stages in two separate systems.

The compressive yield strength of the material sur¬ rounding residual voids is substantially reduced to below the applied pressure and densification occurs quickly thereby avoiding excessive grain growth. The temperature spike when used to overcome resistance and/or to shorten the necessary pressure assist stage may last for a duration of seconds to minutes.

The process conditions of the invention avoid excessive grain growth, while enabling full densification of metal al¬ loys produced to complex forms at low cost.

Other objects, features, and advantages will be ap¬ parent from the following detailed description of preferred embodiments taken in conjunction with the accompanying drawing in which:

BRIEF DESCKIPTIUN OP THE DRAWING

FIG.1 is a flow chart of powder processing in accor¬ dance with the invention; and

FIG. 2 is an illustration of what would be a typical product density time diagram realized through (A) conventional sintering, (B) pressure assisted sintering; and (C) the latter with a temperature spike.

DETAUaED DESCRIPTION OF PREFERRED EHBCDIMENT

In accordance with preferred embodiments of the inven- tion, powders of metal alloy are prepared by size selection,

pouring into a mold and pressing to form a compact of 75- 80% theoretical density as shown at blocks 10 - 12 (FIG. 1) . The compact is sintered at (e.g., for stainless steel) 1350 de¬ grees C in a vacuum or reactive gas furnace to produce a densified compact (93-95% of theoretical density, as indicated in block 14)

The compact can be contained in a sealed cannister within the sinter furnace or alternatively made self suppor¬ ting as an initial pressed compact. After the initial sin¬ tering stage, the pressurization can be applied in a separate chamber with a rapid transfer of the compact or in the origi¬ nal sinter chamber. The chamber is pressurized to 1000 - 3000 psi (step 16) and the compact is maintained at a temperature just under the original sinter heating temperature. The com- pact is maintained at such pressure and temperature for an hour and then returned to ambient pressure and temperature (step 17) by gradual pressure release and non-forced cooling in an inert gas atmosphere. Alternatively, a moderate amount of post pressure sinter (i.e., very slow cooling) can be applied for some alloys. This HIP step has the effect of increasing density to over 98% of theoretical, depending on the alloy so treated.

The step 10 of powder preparation may involve produc¬ tion of fine, non-crystalline or micro-crystalline forms of the powder , via metal atomization or the like to yield con¬ trolled, a fine particle size of the powder below 44 microns (-325 Mesh) , preferrably below 10 microns. The block 12 compaction can be, e.g., at 60 tons per square inch, in a mold. Sintering provides 93 - 95% densification and full densification is provided in the following pressure assisted sinter treatment. Block 18 indicates the temperature spike optimally induced during the pressure assisted portion of the

sinter cycle to assure collapse of voids. Essentially, the temperature during the latter step is about 100 - 200° C below the first step sinter temperature except for the temperature spike which may be back to the sinter temperature but which is held only for a short time (e.g., 5 - 10 minutes) to avoid significant grain growth.

FIG. 2 shows the density (in % of theoretical) vs. time (hours) profile for an alloy with curve A showing the actual showing the increase which would occur in conventional sinter processing and B and C representing the densiy-time profiles achieved for sintering with pressure applied at time T (curve B) -and application of pressure and a temperature spike (curve C) .

The metal alloys treatable through the invention in- elude steels (stainless and low carbon) , super-alloys and other nichel base alloys, rare-earth-base alloys (e.g., samarium- neodynium, samarium-cobalt) , aluminum or copper base alloys, titanium (e.g., Ti-6H-4V) and other refractory metal base alloys. The resultant compacts can be intermediate blanks of simple geometric forms or essentially finished pieces, e.g., tool cutting edge, airfoil, turbine blade, of complex form — and in either case achieved at net or near net dimensions and surface finish.

EXAMPLES (I) Several alloys (1. Ti-6A1-4V; 2. M-2 tool steel; S.

Stellite 21; 6.98 5m - 1.1 Nd/rare earths -0.9 Co) were sin¬ tered for two hours and then HIP processed for an hour to achieve densities after the first two hours and third hour as shown in Table 1. The work was done at separate times (with a three year interval) between groups of tests. It is apparent in retrospect that a precursor of the present invention is implicit in the data. The 1000 - 2000 psi (2K psi) processing

runs 1-1, 1-5, 1-8, 2-1, 2-4, 3-1, 3-4, 5-1, 5-4, 6-4 is benefici-al compared to 15000 - 30000 psi of other runs, e.g., 1-2, 1-3, 2-2, 2-3 , etc.

TABLE 1

SUMMARY OF HIP'ING RESULTS TABLES 1- 6 AND COMPARISON TO PREVIOUS WORK

Hot Isostatic % Theoretical

Rum Sintering Pressing Density

Temp Time Temp Pressure Time Sin¬

Material °C Hrs °C KPSI Hrs tered HIP'ed

1-1 TI-6A1-4V 1230 2 1000 2.0 1 92.27 99.41

1-2 T -6A1-4V 1230 2 1000 15.0 1 92.27 99.48

1-3 T -6A1-4V 1230 2 1000 30.0 1 92.27 99.38

1-4 Ti-6A1-4V 1100 2 900 2.0 1 92.30 95.10

1-5 Ti-6A1-4V 1100 2 1000 2.0 1 92.30 99.30

1-6 TΪ-6A1-4V 1120 2 1180 - . _ 1 93.20 99.30

1-7 Ti-6A1-4V 1120 2 1000 2.3 1 93.00 99.10

1-8 Ti-6A1-4V 1120 2 1000 L.3 1 93.00 98.60

2-1 M-2 Tool Sceel 1230 - _>. 1100 2.0 1 93.65 96.57

2-2 M-2 Tool Steel 1230 2 1100 15.0 1 89.89 99.20 2-3 M-2 Tool Steel 1230 2 1100 30.0 1 89.89 99.03

2-4 M-2 Tool Steel 1210 2 1240 1.0 1 94.40 98.50

2-5 M-2 Tool Steel 1210 2 1235 1.0 1 . . . cr> 97.70

3-1 316L Stainless 1370 2 1100 2.0 1 96.17 96.24

3-2 316L Stainless 1370 2 1100 15.0 1 95. ή δ 100.00

3-3 316L Stainless 1370 2 1100 30.0 1 5.όn 99.41

3-4 316L Stainless 1360 2 1350 1.0 1 95.70 98.10

3-5 316L Stainless 1360 2 1350 1.0 1 95.70 97.90

4--1 4650 Alloy Steel 1350 2 1300 2.0 1 95.2J 97.52 4-24650 Alloy Steel 1350 2 1300 15.0 1 94.79 100.00 4-34650 Alloy Steel 1350 2 1300 30.0 1 97.52 99.96 4-44650 Alloy Steel 1370 2 1350 1.0 1 95.3 ^f" > 97.50 4-54650 Alloy Steel 1370 2 1360 1.1 1 95.30 98.40 5-1 Stellite®2l 1350 2 1300 2.0 1 92. I 5-2. Stellice®21 93.23

1350 2 1300 15.0 1 92.57

5-3 Stellite®21 99.83

1350 2 1300 30.0 1 93.1 .J

5-4 Stellite®21 LOO.00

1350 2 1300 2.0 1 92.60 93.30

5-5 Stellite®21 1340 2 1300 2.0 1 92.60 93.00

6-1 Rare Earth Cobalt Magnets* 1 1114400 1 950 15.0 1 97.6 100.00

6-2 Rare Earth Cobalt Magnets 1140 1 950 15.0 1 95.50 100.00

6-3 Rare Earth Cobalt Magnets 1140 1 1120 1.0 1 97.60 98.90

6-4 Rare Earth Cobalt Magnets 1140 1 1120 1.0 1 95.60 99.10

(II) The invention preferably uses compressed time conditions of FIG.2 compared to the extended times of conven¬ tional sintering or the Table I hybrid processes. As an example, for a low temperature sinter alloy (circa 350°C, compared to the steel circa 1200°C processing) an alloy with a recrystallization temperature of 300°C can be heated up to 290°C in a few minutes (1-2) and maintained at such tempera¬ ture for the balance of 50 minutes (First Stage, FIG. 2), then expo-sed at such time to pressure of 1500 psi and temperature spike of 30°C being in effect a 10-20° C spike, because the alloy might cool about 10-20°C from the 290°C temperature as cool pressurizing gas is admitted to the sintering chamber (or heat is lost in transfer of the compact between different First Stage and Second Stage vessels). The then high density of the compact facilitates heat transfer in the compact. In any event the pressure at the increased temperature, exceeds the compressive yield strength of the compact in the region(s) of its porosity. The temperature spike is terminated in five minutes and the pressure at or shortly after the same time. it will now be apparent to those skilled in the art that other embodiments, improvements, details, and uses can be made consistent with the letter and spirit of the foregoing disclosure and within the scope of this patent, which is limited only by the following claims, construed in accordance with the patent law, including the doctrine of equivalents. What is claimed is: