10/126,830 filed concurrently herewith, entitled A PROCESS FOR CONVERTING HEAVY FISCHER-TROPSCH WAXY FEEDS BLENDED WITH A WASTE PLASTIC FEED STREAM INTO HIGH VI LUBE OILS.

BACKGROUND OF THE INVENTION [0002] Field of the Invention [0003] The present invention relates to a method for transforming waste polymeric materials into useful products and more particularly to an improved process for manufacturing lubricating oils from waste plastics and Fischer-Tropsch waxes.

Description of Related Art [0004] There is a steadily increasing demand for technology capable of converting discarded and waste plastic materials into useful products. This is due in large measure to public concerns over potential environmental damage caused by the presence of these waste materials. According to a recent report from the Office of Solid Waste, about 62% of plastic packaging in the United States is made of polyethylene, the preferred feed for processing waste plastics. Plastics waste is the fastest growing waste product, with about 18 million tons per year in 1995 compared to only four million tons per year in 1970, and this amount is growing by approximately 10% per year. Transforming plastic waste material and particularly polyethylene into useful products presents a unique opportunity to address a growing environmental problem.

[0005] Because of environmental concerns, the specifications for fuels, lubricants and other petroleum products have become more stringent. This in turn has lead to a greater demand for lighter and cleaner petroleum feedstocks with the result that supplies of these feedstocks have been dwindling. In response to this, the production of synthetic lubricating oils from Fischer-Tropsch synthesized hydrocarbons has received increased attention, particularly in view of the relatively large amounts of natural gas increased attention, particularly in view of the relatively large amounts of natural gas reserves and the desire to convert these into more valuable products such as paraffinic lubricating oils. Accordingly, it would be advantageous to devise an economical process which converts waste plastic such as polyethylene into high viscosity index (VI) lube oils.

[0006] Processes are known which convert waste plastic into hydrocarbon lubricants.

For example, U. S. Patent No. 3,845, 157 discloses cracking of waste or virgin polyolefins to form gaseous products such as ethylene/olefin copolymers which are further processed to produce synthetic hydrocarbon lubricants. U. S. Patent No.

4,642, 401 discloses the production of liquid hydrocarbons by heating pulverized polyolefin waste at temperatures of 150-500°C and pressures of 20-300 bars. U. S.

Patent No. 5,849, 964 discloses a process in which waste plastic materials are depolymerized into a volatile phase and a liquid phase. The volatile phase is separated into a gaseous phase and a condensate. The liquid phase, the condensate and the gaseous phase are refined into liquid fuel components using standard refining techniques. U. S. Patent No. 6,143, 940 discloses a procedure for converting waste plastics into heavy wax compositions. U. S. Patent No. 6,150, 577 discloses a process of converting waste plastics into lubricating oils. EP0620264 discloses a process for producing lubricating oils from waste or virgin polyolefins by thermally cracking the waste in a fluidized bed to form a waxy product, optionally using a hydrotreatment, then catalytically isomerizing and fractionating to recover a lubricating oil.

[0007] One drawback to any process which converts plastic waste into useful products is the fact that, as with any recycle feed, the quality and consistency of the starting material is an important factor in obtaining quality end products. Recycled waste plastic not only is quite variable in consistency but its quality varies from one extreme to the other due to the many grades and types of plastics on the market.

Another key factor is the importance of having a constant and continuous supply to make the process economical particularly when using off-specification waste obtained from polyolefin processing plants (so-called"virgin"polyolefin). A process which economically and efficiently converts plastic waste into high VI lube oils while maintaining control over the quality and quantity of the waste plastic supply and insuring the quality of the end products would be highly desirable.

[0008] Therefore, an object of the present invention is to provide an economic and efficient process for converting plastic waste into high VI lube oils.

[0009] Another object of the invention is to improve the quality of waste plastic pyrolysis feeds and the quality of the end product.

[0010] Still another objective of the invention is to develop an improved process which pyrolyzes plastic waste in combination with Fischer-Tropsch waxy feeds to upgrade the quality of the resultant products.

[0011] These and other objects of the present invention will become apparent to the skilled artisan upon a review of the following description, the claims appended thereto and the Figures of the drawings.

SUMMARY OF THE INVENTION [0012] The objects and advantages of the invention are attained by a process which includes the steps of : [0013] passing a waste and/or virgin polyolefin into a heating unit maintained at a temperature below the decomposition point of the polyolefin to provide a molten feed; [0014] continuously passing the molten feed through a flow-through pyrolysis reactor maintained at a temperature sufficient to depolymerize at least a portion of the polyolefin and at an absolute pressure of at least one bar to produce a pyrolyzed effluent; [0015] passing at least a portion of the effluent from the pyrolysis reactor to a catalytic isomerization dewaxing unit; [0016] fractionating the product from the isomerization dewaxing unit; and [0017] recovering a lubricating oil base stock.

[0018] In a separate embodiment, at least a portion of the pyrolyzed effluent of step (b) is passed to a hydrotreating unit to remove a significant portion of any nitrogen- containing, sulfur-containing and/or oxygenated contaminants. At least a portion of the effluent from the hydrotreating unit is passed to the catalytic isomerization dewaxing unit of step (c).

[0019] The process of the invention provides several advantages over previously known techniques. The use of a heating unit enables the practitioner to provide a continuous supply of liquified, heated feedstock readily available for pumping to the pyrolysis reactor. Advantageously, the feedstock is blanketed with inert gas thereby minimizing the formation of oxygenated compounds which could cause downstream catalyst deactivation and could lower the quality of the end products. Continuously passing the polyolefin feed through the pyrolysis reactor allows the practitioner to maintain a low residence time in the reactor which contributes to overall efficiency and economy since a larger volume of feed can be processed. It also enables one to use smaller capacity reactors which likewise provides an economical benefit. Although a hydrotreatment is preferred in the process of the invention to eliminate virtually all nitrogen, sulfur, and oxygen-containing contaminants, such is not necessary if an inert gas has been used to blanket the feed in the heating unit since it has been observed that lube oil stocks lighter in color are obtained by using an inert gas to minimize formation of oxygenated compounds. The use of an intermediate pore size molecule sieve SAPO in the isomerization dewaxing unit minimizes the cracking associated with other known dewaxing techniques.

BRIEF DESCRIPTION OF THE DRAWINGS [0020] Fig. 1 is a schematic flow diagram of one embodiment of the invention.

[0021] Fig. 2 is a schematic flow diagram of a second embodiment of the invention which pyrolyzes a blend of a waxy Fischer-Tropsch fraction and waste polymer.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS [0022] With reference to Fig. 1, the first step in the process of the invention involves feeding a plastic material (10) to a heating unit (20). The feed can be a waste plastic, preferably a polyolefin. Suitable plastic waste includes high density and low density polyethylene, polypropylene, EPDM and the like. Typically, the feed is initially prepared by grinding the waste material to a suitable size, removing extraneous material such as metals, etc. , and transporting the solids to the heating unit. Alternatively, the solids may be dissolved or dispersed in a suitable solvent and the liquid fed to the heater.

[0023] The feed to the heater may also be composed of virgin plastics, e. g., polyolefins which are scrap materials recovered from polyolefin processing during fabrication or other manufacturing techniques. Mixtures of polymer waste and virgin material may be employed, depending upon available supplies. The quality and quantity of the feed can have an impact on the quality of the end products. Recycled waste plastic is quite variable in consistency and its quality varies widely due to the many grades and types of plastics on the market. It is also important to have a constant and continuous supply to make the process economical. With these factors in mind, it is a preferred embodiment of the invention to admix waste and/or virgin plastic with waxy hydrocarbon fractions obtained from a Fischer-Tropsch process. Reference is made to the aforementioned related case, Serial No. 10/126,830, for a detailed disclosure of procedures for converting waste polymer/Fischer-Tropsch wax blends into high VI lube oils. The entire disclosure of said application is incorporated herein.

[0024] One important aspect of the present invention is the use of a heating unit (20) which functions to melt the plastics feed and maintain the liquefied material at a temperature low enough to avoid cracking or any other thermal decomposition.

Suitable temperatures range from about 150°C to about 350°C, preferably about 200°C to about 350°C, such that the feed is maintained below the temperature at which significant decomposition or depolymerization can occur. Preferably, an inert gas such as nitrogen or argon blankets the heating unit to avoid any significant oxidation of the feed components. Oxidation could give oxygenated impurities which might lead to catalyst poisoning downstream. Avoiding oxidation also would lead to products which are lighter in color. The heating unit also functions as a"holding"vessel which maintains a constant supply of feed for the flow-through pyrolysis reactor.

[0025] The molten feed is then continuously forwarded to a pyrolysis unit (30).

Typically, a flow-through pyrolysis reactor is employed. The temperature in the reactor normally is maintained between about 450°C and about 700°C, preferably between about 500°C and about 650°C, at pressures of less than about 15 bar, preferably in the range of about 1 bar to about 15 bar, and feed rates ranging from about 0.5 to about 5 hr-1 LHSV. One important advantage of the invention is the fact that the contact time for the molten feed is relatively short, ranging from as low as about 15 minutes to about an hour or more if necessary. This enables the practitioner to use smaller capacity reactors which lowers production costs. Conducting the pyrolysis at atmospheric pressures. Pyrolyzing conditions are variable and can easily be adjusted depending upon the time judged desirable to achieve optimum cracking and depolymerization of the feed materials and the type of product desired (e. g. , bright stock, neutral oil, etc. ). (The feed may be combined with a lower viscosity liquid, e. g. a diesel or a diesel cut from a fractionator in the process, to lower viscosity and make the feed easier to pump, as well as to help bring in heat to melt the plastic.) [0026] Preferably, the pyrolyzed effluent is pumped to a hydrotreating (HT) unit (40) to remove nitrogen, sulfur and any oxygen-containing compounds which could contaminate the products and poison downstream catalysts. Typical hydrotreating conditions which are employed to remove contaminants while avoiding cracking include temperatures ranging from about 190°C to about 340°C, pressures ranging from about 400 psig to about 3000 psig, space velocities (LHSV) in the range of about 0.1 hr- I to about 20 ho 1, and hydrogen recycle rates ranging from about 400 to about 15,000 SCF/B. Hydrotreating catalysts include those conventionally used in hydrotreating units. Reference is made to the following U. S. patents for a list of suitable catalysts and hydrotreating conditions: Patent Nos. 3,852, 207; 4,157, 294; 4,921, 594; 3,904, 513; 4,673, 487, the disclosures of which are incorporated herein in their entirety.

[0027] The pyrolysis effluent, which normally is very waxy, may be pumped directly to an isomerization dewaxing unit (50) (IDW). Since the heavier waxes are difficult to treat in the IDW unit and since the pyrolysis effluent typically contains a broad boiling point range of materials, the effluent may be forwarded to a separation or distillation unit (not shown). The heavy paraffins are thereupon removed and used directly as hydrocarbon waxes. The lighter olefins (i. e. , those boiling below about 650°F) and the gaseous olefins recovered directly from the pyrolysis unit can be forwarded to an oligomerization unit for conversion into lube oil products, normally those boiling in the neutral oil range. Techniques are well known in the art for oligomerizing lower molecular weight alpha-olefins into higher molecular weight hydrocarbons which can be converted into useful fuels, lubricants, etc.

[0028] During oligomerization, an olefinic feedstock is contacted with a oligomerization catalyst in a oligomerization zone. Fluid-bed reactors, catalytic distillation reactors, and fixed bed reactors, such as that found in an MTBE or TAME plant, are suitably used as oligomerization reaction zones. Conditions for this reaction in the oligomerization zone are between room temperature and 400°F, preferably between 90 and 275°F, from 0.1 to 3 LHSV, and from 0 to 500 psig, preferably between 50 and 150 psig. Oligomerization catalysts for can be virtually any acidic material including zeolites, clays, resins, BF3 complexes, HF, H2SO4, AIC13, ionic liquids (preferably acidic ionic liquids), superacids, etc. The preferred catalyst includes a Group VIII metal on an inorganic oxide support, more preferably a Group VIII metal on a zeolite support. Zeolites are preferred because of their resistance to fouling and ease of regeneration. The most preferred catalyst is nickel on ZSM-5. Catalysts and conditions for the oligomerization of olefins are well known, and disclosed, for example, in U. S. Patent Nos. 4,053, 534; 4,482, 752; 5,105, 049 and 5, 118,902, the disclosures of which are incorporated herein by reference for all purposes.

[0029] As indicated above, if a hydrotreating step has been utilized, the product stream therefrom is continuously forwarded to the IDW unit (50). Alternatively, the hydrotreatment effluent may be pumped to a separation unit (not shown) to remove heavy wax materials before sending to the IDW unit. The heavy wax fraction normally boils above 1000°F and is recovered and used as a high grade heavy wax.

[0030] The IDW unit (50) preferably is operated under the conditions described in U. S. Patent No. 5, 135, 638, the entire contents of which are incorporated herein.

Preferably, the catalyst employed contains a intermediate pore size molecular sieve such as SAPO-11, SAPO-31, SAPO-41 or SM-3. Reference to suitable isomerization dewaxing conditions may also be found in U. S. Patent 5,246, 566; and U. S. Patent 5,282, 958, the disclosures all of which are incorporated herein in their entirety. Typical reaction conditions in the IDW unit include temperatures ranging from about 200°C to about 475°C, pressures ranging from about 15 psig to about 3000 psig, a liquid hourly space velocity (LHSV) ranging from about 0.1 hr-1 to about 20 hr-1, preferably between about 0.2 hr-1 to about 10 hr~ and a hydrogen recycle between about 500 to about 30,000 SCF/B, preferably between about 1000 to about 20,000 SCF/B. As is known in the art, isomerization catalytic dewaxing converts n-paraffins into iso-paraffins, thereby reducing the pour point of the resultant oils to form a high VI lube oil at a much higher yield.

[0031] At least a portion of the product obtained from the IDW unit is a low pour point lubricating oil stock and can be used as such. Normally, the IDW effluent is forwarded to a distillation unit (60) to separate the effluent into various oil fractions, including a neutral lube oil (62) and a bright stock (63). An amount of diesel (61) is also generally produced. A neutral oil is a refined mineral base oil lubricant with a boiling range above 500°F and below 1000°F. A bright stock is a lubricating oil hydrocarbon in which about 50 wt% boils over 1000°F.

[0032] A preferred embodiment of the invention as illustrated in Fig. 2 involves blending a heavy wax fraction (27) from a Fischer-Tropsch (Fischer-Tropsch) synthesis with the waste or virgin plastic feed 10. The blending can be done before the feed is sent to the heating unit (20) or the heavy wax fraction can be added to the molten stream being pumped to the pyrolysis unit (30). Typical blends comprise a mixture of 5-95 wt% of a Fischer-Tropsch wax fraction and 95-5 wt% of waste and/or virgin polymer. As shown in Fig. 2, a Fischer-Tropsch waxy feed (15) is forwarded to a separator (25), where a 650°F-fraction (29) recovered for use as a fuel or a fuel blend, and a 650°F-1050°F fraction (28) sent to hydrotreating. The bottoms fraction (27) is circulated to the heater (20) where it is blended with a waste feed (10) The melted stream is continuously pumped to the pyrolysis reactor (30). The pyrolysis effluent is forwarded to fractionator (35). A 390°F-fraction (38) is recovered for use as a fuel or a fuel blending stock. The lighter 390-650°F fraction (37) is sent to an oligomerization reactor (45) and the 650°F.-1050°F. middle fraction (39) forwarded to a hydrotreatment unit (40) and then to an IDW unit (50). At least a portion of heavy fraction (36) is sent to hydrotreatment unit (40) and then to IDW unit (50). A portion of heavy fraction may optionally be recycled to the pyrolysis reactor (30). Effluent from unit (50) is processed in fractionator (60) to recover diesel (61), and lube oil (62). Effluent (46) from oligomerization reactor is separated in fractionator (35). A portion of stream (37) may be withdrawn (41) to remove excess unconverted paraffins from the feed to the oligomerization unit. Alternatively, a 390-650°F fraction may be removed from (46) using a separate fractionator for the oligomerization unit (separation not shown).

[0033] The invention will now be illustrated by the following examples which are intended to be merely exemplary and in no manner limiting.

Example 1 [0034] High density polyethylene (HDPE), obtained from Chevron Chemical Company, was mixed 50/50 by weight with a 550-700 °F hydrocracked diesel. This was put into a 7.5 gallon stainless steel feed pot with a stirrer, and heated under 10 psi nitrogen to 500 °F to melt the plastic and lower the viscosity of the plastic/diesel feed to a point at which it could then be easily pumped. The feed was then pumped upflow, using a gear pump, through a stainless steel reactor containing steel bars to lower the reactor volume to 140 cc. Reactor conditions included a temperature of 975 °F, atmospheric pressure, and a residence time of approximately one hour. Products were collected and analyzed.

[0035] Table I shows the yields and inspections from the pyrolysis run. The yield of 725 °F+ product, with an endpoint of about 1100 °F, suitable for lubricating base oil, was 51.4 wt% based on plastic in the feed. The liquid bottoms collected from that run were then isomerized over a Pt/SAPO-11 catalyst at 500 psig, 600 °F, 0.65 LHSV, and 5 MSCF/bbl H2 (followed by a Pd/Si02-Al203 hydrofinishing catalyst at 450 °F and 1.3 LHSV) to produce a-37 °C pour point 5.4 cSt oil of 156 VI (Table II). The overall 725 °F+ yield, based on plastic to the pyrolyzer, was 21.3 wt%.

Example 2 [0036] Example 1 was repeated, except the plastic was 96 wt% HDPE and 4 wt% waste polyethylene terephthalate. An online stripper separated most of the 600 °F minus product from the higher boiling bottoms product. Pyrolysis yields are given in Table III, showing a 725 °F+ yield, based on plastic, of 42.4 wt%. Table IV gives yields and inspections for isomerization of the pyrolysis bottoms over the same Pt/SAPO-11 catalyst as in Example 1, and the same run conditions except for an isomerization temperature of 675 °F. This gave a-13 °C pour point 4.9 cSt oil of 160 VI. The overall 725 °F+ yield, based on plastic to the pyrolyzer, was 25.3 wt%. Since the pyrolysis overhead gas and liquid were highly olefinic, oligomerization of these olefins could produce additional low pour point lube base oil.

Example 3 [0037] A portion of the pyrolysis bottoms made in Example 2 was hydrotreated over a Ni-W/Si02-A1203 catalyst at 600 °F, 1.5 LHSV, 1950 psig, and 5 MSCF/bbl H2 to reduce heteroatom content in the feed. At these conditions, cracking of the feed was very low. The hydrotreated feed was then isomerized over the same Pt/SAPO-11 catalyst as in Example I, and the same conditions, except for an isomerization temperature of 670 °F and pressure of 1950 psig. This gave a-34°C pour point 3.0 cSt oil of 131 VI (Table V). The overall 725 °F+ yield, based on plastic to the pyrolyzer, was 17.2 wt%. It is believed the yield and VI would have been higher had the oil been run to a higher pour point, and distilled to the same viscosity as in Example 2.

Example 4 [0038] The pyrolysis run of Example 1 was repeated (Table VI) at the same conditions, but this time on a feed composed of a 50/50 mixture by weight of low density polyethylene (LDPE), obtained from Chevron Chemical Company, and a hydrotreated Fischer-Tropsch wax, obtained from Moore & Munger (Table VII).

Yields are given in Table VI, showing a 725 °F+ yield of 57.5 wt%. The yield for a broader lube feed, 650 °F+, was 66.0 wt%. While there was considerable 1000 °F+ in the feed to the pyrolyzer, there was little 1000 °F+ in the product, which is believed here to be advantageous for low cloud point. The pyrolysis bottoms were then isomerized over the same Pt/SAPO-11 catalyst as in Example 1, and at the same conditions, except for an isomerization temperature of 687 °F, to give a-22 °C pour point 4.4 cSt oil of 154 VI (Table VIII). The overall 725 °F+ yield, based on feed to the pyrolyzer, was 34.8 wt%. For overall 650 °F+, the yield was 43.7 wt%. Adding the potential lube from oligomerizing the lighter olefinic product from the pyrolyzer would increase these yields still further.

[0039] Table VII lists properties of four feed (A = Diesel Diluent: B = Moore & Munger FT Wax: C = hydrotreated heavy (i. e. bottoms) fraction from pyrolyzed HDPE/PET/Diesel: D = hydrotreated heavy (i. e. bottoms) fraction from pyrolyzed LDPE/FT Wax).

Example 5 [0040] A portion of the pyrolysis bottoms from Example 4 was hydrotreated over the Ni-W/Si02-A1203 catalyst as in Example 3. This was then isomerized as in Example 4, except for a isomerization temperature of 640 °F. This gave a-15 °C pour point 3.8 cSt oil with a 150 VI (Table IX). The overall 725 °F+ yield, based on feed to the pyrolyzer, was 31.2 wt%. For overall 650 °F+, the yield was 39.7 wt%.

Example 6 [0041] HDPE beads were admixed with diesel oil to form a 50/50 by weight feed.

The feed was pumped to a heating unit maintained at a temperature of 500°F. The feed was blanketed with nitrogen to minimize oxidation. The heated feed was then continuously pumped upward through a pyrolysis reactor equipped with preheat bars to maintain a reaction temperature of 1025°F and atmospheric pressure. Residence time for the feed was 1 hour. The pyrolyzed product was stripped at a temperature of about 550°F with the overhead and bottoms liquids collected separately. The bottoms, which were quite light in color, were forwarded to an IDW unit. Isomerization dewaxing was performed under the following conditions: 675°F, 0.5 LHSV, 1950 psig, and 3.6 MSCF/BBL of once-through H2. The product from the IDW unit was fractionated.

Analysis of the yield and composition thereof is set forth in Table X.

Table I Pyrolysis of 50/50 by Weight Plastic/Diesel at 975 °F, Atmospheric Pressure, and 1 Hr Residence Time Plastic = HDPE Yield, Wt% Cl 0. 5 C2= 0.8 C2 0.6 C3= 1.2 C3 0.5 C4= 0.8 C4 0.5 C4-4.9 C5-350 °F 9.6 350-650 °F 56.0 650-725 °F 3.8 725 °F+ 25. 7 725°F+, based on plastic 51.4 Bottoms Wt% of feed 92.0 Gravity, API 42.7 Sulfur, ppm <1.5 Nitrogen, ppm 1.3 Sim. Dist., °F, Wt% ST/5 149/302 10/30 390/506 50 572 70/90 692/955 95/EP 1011/1109 Table II Isomerization Dewaxing of Pyrolyzed Product from HDPE/Diesel at 500 psig, 600 °F, 0.65 LHSV, and 5 MSCF/bbl H2 Yield, Wt% C3 0.8 C4 2.9 C4-3.7 C5-350 °F 25.3 350-650 °F 56.1 650-725 °F 3.3 725 °F+ 11.6 725°F+, based on 725 °F+ to IDW 41.1 Overhead Wt% of Feed 75.9 Sim. Dist., °F, Wt% ST/5 73/194 10/30 243/367 50 448 70/90 520/584 95/EP 605/647 Bottoms Wt% of feed 15.4 Pour Point, °C-37 Cloud Point, °C +9 Viscosity, 40 °C, cSt 25.43 100 °C, cSt 5.416 VI 156 Sim. Dist., °F, Wt% ST/5 621/655 10/30 674/745 50 844 70/90 925/1051 95/EP 1094/1153 Overall Wt% 725 °F+, based on plastic 21.3 Table III Pyrolysis of 50/50 by Weight Plastic/Diesel at 975 °F, Atmospheric Pressure, and 1 Hr Residence Time Plastic = 96 wt% HDPE/4 wt% PET Yield, Wt% Cl 0.2 C2= 0.5 C2 0.4 C3= 0.6 C3 0.4 C4= 0.6 C4 0.2 C4-2.9 C5-350 °F 15.6 350-650 °F 52.7 650-725 °F 7.6 725 °F+ 21.2 725°F+, based on plastic 42.4 Overhead Wt% of Feed 56.2 P+N/Olefins/Aromatics 41.0/56. 0/3.0 Sim. Dist., °F, Wt% ST/5 106/194 10/30 231/382 50 513 70/90 568/621 95/EP 649/784 Bottoms Wt% of feed 39.5 Gravity, API 40.0 Sulfur, ppm 3.6 Nitrogen, ppm 6.1 Sim. Dist., °F, Wt% ST/5 458/525 10/30 555/629 50 732 70/90 821/911 95/EP 944/995 Table IV Isomerization Dewaxing of Pyrolyzed Product from HDPE/PET/Diesel at 500 psig, 675 °F, 0.65 LHSV, and 5 MSCF/bbl H2 (Hydrofinish at 450°F and 1.3 LHSV) Yield, Wt% C3 0.5 C4 1.4 C4-1.9 C5-350 °F 7.4 350-650 °F 46.3 650-725 °F 13.4 725 °F+ 31.0 725°F+, based on 725 °F+ to IDW 68.9 Overhead Wt% of Feed 56.9 Sim. Dist., °F, Wt% ST/5 156/288 10/30 368/538 50 582 70/90 613/650 95/EP 665/694 Bottoms Wt% of feed 38.7 Pour Point, °C-13 Cloud Point, C +6 Viscosity, 40 °C, cSt 21.63 100 °C, cSt 4.920 VI 160 Sim. Dist., °F, Wt% ST/5 655/684 10/30 699/752 50 810 70/90 873/958 95/EP 999/1085 Overall Wt% 725 °F+, based on plastic 25.3 Table V Isomerization Dewaxing of Hydrotreated Pyrolyzed Product from HDPE/PET at 1950 psig, 670 °F, 0.65 LHSV, and 5 MSCF/bbl H2 (Hydrofinish at 450°F and 1.3 LHSV) Yield, Wt% Ci 0.1 C2 0.2 C3 2.7 C4 6.2 C4-9.2 C5-350 °F 22.3 350-650 °F 41.7 650-725 °F 6.0 725 °F+ 20.8 725°F+, based on 725 °F+ to IDW 37.1 Overhead Wt% of Feed 40.3 Sim. Dist., °F, Wt% ST/5 72/152 10/30 193/297 50 395 70/90 505/553 95/EP 569/598 Bottoms Wt% of feed 45.0 Pour Point, °C-34 Cloud Point, °C-3 Viscosity, 40 °C, cSt 10.86 100 °C, cSt 2.967 VI 131 Sim. Dist., °F, Wt% ST/5 510/565 10/30 587/642 50 710 70/90 793/899 95/EP 941/1041 Overall Wt% 725 °F+, based on plastic 17.2 Table VI Pyrolysis of 50/50 by Weight LDPE/FT Wax at 975 °F, Atmospheric Pressure, and 1 Hr Residence Time Yield, Wt% Cl 0.2 C2= 0.6 C2 0.4 C3= 0.9 C3 0.7 C4= 0.9 C4 0.4 C4-4.1 C5-350 °F 9.9 350-650 °F 20.0 650-725 °F 8.5 725 °F+ 57.5 Overhead Wt% of Feed 17.1 P+N/Olefins/Aromatics 22.0/76. 0/2.0 Sim. Dist., °F, Wt% ST/5 114/201 10/30 215/307 50 378 70/90 455/550 95/EP 599/692 Bottoms Wt% of feed 76.0 Gravity, API 40.7 Sulfur, ppm <4 Nitrogen, ppm 7.9 Sim. Dist., °F, Wt% ST/5 460/580 10/30 633/757 50 850 70/90 910/979 95/EP 1002/1051 Table VII<BR> Feed Inspections<BR> Feed A B C D<BR> Gravity, °API 38.2 40.5 42.1<BR> Nitrogen, ppm 1.9<BR> Sim. Dist., °F, Wt%<BR> ST/5 505/533 791/856 255/518 118/544<BR> 10/30 553/621 876/942 553/648 598/744<BR> 50 670 995 753 842<BR> 70/90 699/719 1031/1085 840/928 914/985<BR> 95/EP 725/735 1107/1133 964/1023 1011/1068 Table VIII Isomerization Dewaxing of Pyrolyzed Product from 50/50 LDPE/FT Wax at 500 psig, 687 °F, 0.65 LHSV, and 5 MSCF/bbl H2 (Hydrofinish at 450°F and 1.3 LHSV) Yield, Wt% C3 0.5 C4 0.9 C4-1.4 C5-350 °F 8.7 350-650 °F 32.6 650-725 °F 11.5 725 °F+ 45.8 Overhead Wt% of Feed 34.9 Sim. Dist., °F, Wt% ST/5 157/246 10/30 292/430 50 512 70/90 569/611 95/EP 621/641 Bottoms Wt% of feed 60.9 Pour Point, °C-22 Cloud Point, °C-2 Viscosity, 40 °C, cSt 18.70 100 °C, cSt 4.416 VI 154 Sim. Dist., °F, Wt% ST/5 614/646 10/30 668/745 50 819 70/90 885/961 95/EP 991/1088 Overall Wt% 725 °F+, based on feed 34.8 Overall Wt% 650 °F+, based on feed 43.7 Table IX Isomerization Dewaxing of Hydrotreated Pyrolyzed Product from 50/50 LDPE/FT at 500 psig, 640 °F, 0.65 LHSV, and 5 MSCF/bbl H2 (Hydrofinish at 450°F and 1.3 LHSV) Yield, Wt% C2 0.1 C3 0.8 C4 1.7 C4-2.6 C5-350 °F 13.7 350-650 °F 31.7 650-725 °F 11.0 725 °F+ 41.0 Overhead Wt% of Feed 31.9 Sim. Dist., °F, Wt% ST/5 81/190 10/30 238/344 50 438 70/90 508/565 95/EP 586/682 Bottoms Wt% of feed 61.6 Pour Point, °C-15 Cloud Point, °C-2 Viscosity, 40 °C, cSt 15.23 100 °C, cSt 3.829 VI 150 Sim. Dist., °F, Wt% ST/5 564/601 10/30 623/710 50 798 70/90 878/962 95/EP 995/1067 Overall Wt% 725 °F+, based on feed 31.2 Overall Wt% 650 °F+, based on feed 39.7 Table X Isomerization Dewaxing of Pyrolyzed Product from HDPE/Diesel at 675 °F, 1950 psig, 0.5 LHSV, and 3.6 MSCF/bbl H2 (Hydrofinish at 450°F and 1.3 LHSV) C4-0.5 C5,-180°F 2.3 180-300°F 3.7 300-725°F 73.5 725°F+ 20.00 725°F+ Conversion 27.5 wt. % 725°F+ Overhead Wt% of IDW Feed 74.3 St/5 175/287 10/30 361/531 50 601 70/90 661/707 95/EP 720/759 725°F+ Bottoms Wt% of IDW Feed 19.4 Wt% of Plastic Feed to Process 26.7 St/5 686/722 10/30 744/818 50 882 70/90 948/1028 95/EP 1056/1110 Pour Pt, °C-9 Cloud Pt. °C +14 Viscosity, 40°C, cSt 34.35 100°C, cSt 6.891 VI 165 [0042] It is clear from the above that the invention provides an efficient process wherein a waste or virgin polyolefin is heated and continuously processed through a pyrolyzing reactor at low residence times and at atmospheric pressure followed by isomerization dewaxing to produce high yields of lube oil stocks. Shorter residence times mean that smaller reactors can be used. The light olefins from the pyrolysis can be oligomerized to form useful higher molecular weight products. Process conditions in the reactor can be altered to vary the types of products obtained, i. e. , neutral oil and/or bright stock. Waxy Fischer-Tropsch products can be blended with the waste polymer feed to the pyrolysis reactor to maintain quality of the feed and quality of the end products. Catalysts and conditions for performing Fischer-Tropsch reactions are well known to those of skill in the art, and are described, for example, in EP 0 921 184A1, the contents of which are hereby incorporated by reference in their entirety.

[0043] While the invention has been described with preferred embodiments, it is to be understood that variations and modifications may be understood that variations and modifications may be resorted to as will be apparent to those skilled in the art. Such variations and modifications are to be considered within the purview and the scope of the claims appended hereto.