The present invention relates to a process for the manufacturing of decorative surface elements with a surface structure matching the decor of the upper surface.

Products coated with simulated versions of materials such as wood and marble are frequent today. They are foremost used where a less expensive material is desired, but also where resistance towards abrasion, indentation and different chemicals and moisture is required. As an example of such products floors, floor beadings, table tops, work tops and wall panels can be mentioned.

As an example of an existing product can be mentioned the thermosetting laminate which mostly consists of a number of base sheets with a decor sheet placed closest to the surface. The decor sheet can be provided with a desired decor or pattern.

Frequently used patterns usually represent the image of different kinds of wood or minerals such as marble or granite. The surface of the laminate can, at the laminating procedure, be provided with a structure, which will make the decor more realistic. Press plates with structure or structure foils are here frequently used during the pressing of the laminate. A negative reproduction of the structure in the press plate or the foil will be embossed into the laminate surface during the laminating procedure.

The structure suitably represents features characteristic for the pattern the decor represents. The structure can be made coarse to simulate for example rough planed stone, or smooth with randomly placed pits and micro cracks to simulate polished marble. When the surface of wood is simulated the surface is provided with randomly placed thin oblong indentations which imitate pores.

It has for a long time been a great need to be able to manufacture simulated materials where a lacquer is used as a top coat on a decor. The only way, so far, to achieve a surface structure in lacquer is casting or abrasive moulding which both are time consuming and expensive processes.

The invention relates to a process for the manufacture of a decorative surface element. The element comprises a base layer, a decor and a wear layer of a UV or electron beam curing lacquer.

The design of the decor can be achieved by utilising the process steps below; i) A segmentation pattern is selected, the segmentation comprising at least two decor segments on each surface element. The shape, as seen from above, of the surface element is hereby selected from the group; triangular, quadratic, rectangular, heptagonal, pentagonal and octagonal while the shape of the segments is selected from the group triangular, quadratic, rectangular, heptagonal, pentagonal, octagonal, circular, elliptical, perturbed and irregular. ii) A segment decor is then selected for each segment. The segment decor is selected from the group; digitised and simulated depiction of different kinds of wood, minerals and stone, different kinds of fabric, art work and fantasy based decor. iii) Each selection is made on a terminal where the selections emanates from a data base and that the selection is visualised via the terminal.

The decor is preferably achieved by digitisation of an actual archetype or by partly or completely being created in a digital media. The digitised decor is preferably stored digitally in order to be used as a control function and original, together with control programs and selection parameters, when printing the decor.

The dimensions of the surface to be covered by surface elements is suitably entered into the terminal and support programs calculates an installation pattern.

The installation pattern calculation is suitably also used for printing an assembly instruction. In order to visualise the selection the installation pattern calculation is possibly used for printing a miniaturised copy of the calculated installation with the selected pattern and decor. The dimensions of the surface to be covered by surface elements is suitably entered into the terminal and that that support programs further calculates decor and segmentation pattern matching between the surface elements.

The selections is preferably also used, together with support programs for controlling further steps in the manufacturing procedure selected from the group; identification marking, positioning marking, packaging, lacquering, surface embossing, storing and delivery logistics.

An algorithm is suitably used for guiding the positioning of the decor segments and segmentation pattern so that a decor segment from one surface element may continue on an adjoining surface element. The control program is suitably used, together with decor data and selection parameters, for applying matching identification on the surface elements.

It is also possible to manufacture a designed larger surface with decor segments larger than a surface element by utilising the process as described below; i) A selected main decor is entered via a terminal, the selected decor emanating from a group consisting of; an archetype digitised via digital camera or scanner and a digitised decor from a database. ii) The dimensions of the surface to be covered by surface elements and the desired dimension of the decor is then entered into the terminal. Support programs are used for calculating the segmentation of the main decor to cover more than one surface element. iii) The result of the selections and calculations is finally visualised via the terminal.

The digitised main decor is stored digitally in order to be used as a control function and original, together with control programs and selection parameters, when printing the decor.

It is, in order to enhance the decorative effect of some decor possible to select a surrounding decor. A decor effect in the border between the main decor and the surrounding decor is suitably also selected, the selection being made from the group ; fading, sharp edge, sharp edge with shadow effect, jagged edge, jagged edge with shadow and surrounding inlay of other decor.

The surrounding decor is preferably processed as follows; i) A segmentation pattern for the surrounding decor is selected. The segmentation comprising at least two decor segments on each surface element. The shape, as seen from above, of the surface element is preferably selected from the group; triangular, quadratic, rectangular, heptagonal, pentagonal and octagonal. The shape of the surface elements with surrounding decor and the shape of the surface elements which, of course, is selected so that they can be joined with each other. The shape of the segments is selected from the group triangular, quadratic, rectangular, heptagonal, pentagonal, octagonal, circular, elliptical, perturbed and irregular. ii) A segment decor is then selected for each segment. The segment decor is selected from the group; digitised and simulated depiction of different kinds of wood, minerals and stone, different kinds of fabric, art work and fantasy based decor. iii) Each selection is made on a terminal where the selections emanates from a data base. The selection is visualised via the terminal.

A decor effect in the border between the main decor and the surrounding decor is suitably selected. The selection is preferably made from the group; fading, sharp edge, sharp edge with shadow effect, jagged edge, jagged edge with shadow and surrounding inlay of other decor. Also this selection is made on the terminal.

The dimensions of the surface to be covered by surface elements is suitably entered into the terminal and support programs calculates an installation pattern.

The installation pattern calculation is preferably used for printing an assembly instruction. The installation pattern calculation is according to one embodiment of the invention used for printing a miniaturised copy of the calculated installation with the selected pattern and decor. This print out may serve as an evaluation copy of the design before making decisions regarding the manufacturing.

The dimensions of the surface to be covered by surface elements is entered into the terminal. Support programs further calculates decor and segmentation pattern matching between the surface elements. The selections is preferably used, together with support programs for controlling further steps in the manufacturing procedure selected from the group ; identification marking, positioning marking, packaging, lacquering, surface embossing, storing and delivery logistics. An algorithm is preferably used for guiding the positioning of the decor segments and segmentation pattern so that a decor segment from one surface element may continue on an adjoining surface element. The control program is then preferably used together with decor data and selection parameters for applying matching identification on the surface elements.

The surface elements may be used as floor, wall or ceiling boards. The surface elements are suitably manufactured through the following process; i) A supporting core with a desired format is manufactured and provided with an upper side and a lower side. ii) The upper side of the supporting core is then provided with a decor, by for example printing. The decor is positioned after a predetermined fixing point on the supporting core. iii) The upper side of the supporting core is then provided with a protecting, at least partly translucent, wear layer by for example spray coating, roller coating, curtain coating and immersion coating or by being provided with one or more sheets of a-cellulose impregnated with thermosetting resin or lacquer.

The decor is suitably achieved by digitisation of an actual archetype or by partly or completely being created in a digital media. The digitised decor is stored digitally in order to be used as a control function and original, together with possible control programs, when printing the decor.

The decor may accordingly be obtained by making a high resolution or selected resolution digital picture of the desired decor. This is suitably made by means of a digital camera. The most common decor will of course be different kinds of wood and minerals like marble, as these probably will continue to be preferred surface decoration in home and public environments. It is, however, possible to depict anything that is visible. The digitised version of the decor is then edited to fit the size of the supporting core. It is also possible to rearrange the decor in many different ways, like changing colour tones, contrast, dividing the decor into smaller segments and adding other decorative elements. It is also possible to completely create the decor in a computer equipped for graphic design. It is possible to create a simulated decor so realistic that even a professional will have great problems in visually separating it from genuine material. This makes it possible to make for example floor boards with an almost perfect illusion of a rare kind of wood, like ebony or rose wood and still preserving trees under threat of extermination.

The digital decor is used together with guiding programs to control a printer.

The printer may be of an electrostatic type or an inc-jet type printer. The resolution needed is much depending on the decor that is to be simulated, but resolutions of 10-1500 dots per inch (dpi) is the practical range in which most decor will be printed. Under normal conditions a resolution of 300-600 dpi is sufficient when creating simulations of even very complex decorative patterns and still achieve a result that visually is very difficult to separate form the archetype without close and thorough inspection.

The digitally stored decor can also be used together with support programs when guiding other operations and procedures in the manufacturing process. Such steps in the operation may include procedures like identification marking, packaging, lacquering, surface embossing, storing and delivery logistics as well as assembly instructions.

It is advantageous to manufacture the supporting core in the desired end user format and to provide it with edges suited for joining before applying the decor and wear layer, since the amount of waste thereby is radically reduced. The decor matching tolerances will also be improved further by this procedure.

The main part of the supporting core is suitably constituted by a particle board or a fibre board. It is, however, possible to manufacture the core that at least partly consist of a polymer such as for example polyurethane or a polyolefin such as polyethylene, polypropylene or polybutene. A polymer based core can be achieved by being injection moulded or press moulded and can be given its shape by plastic moulding and does therefore not require any abrasive treatment. A polymer based core may except polymer also contain a filler in the form of a particle or fibre of organic or inorganic material, which besides the use a cost reducing material also will be used to modify the mechanical characteristics of the core. As an example of such suitable fillers can be mentioned; cellulose or wood particles, straw, starch, glass, lime, talcum, stone powder and sand. The mechanical characteristics that may be changed is for example viscosity, thermal coefficient of expansion, elasticity, density, fire resistance, moisture absorption capacity, acoustic properties, thermal conductivity, flexural and shearing strength as well as softening temperature.

The upper surface, i. e. the surface that is to be provided with decor, is suitably surface treated before the printing. Such surface treatment will then incorporate at least one of the steps, ground coating and sanding. It is also possible to provide the surface with a structure that matches the decor that is to be applied.

The translucent wear layer is suitably constituted by a UV-or electron beam curing lacquer such as an acrylic, epoxy, or maleimide lacquer. The wear layer is suitably applied in several steps with intermediate curing where the last one is a complete curing while the earlier ones are only partial. It will hereby be possible to achieve thick and plane layers. The wear layer suitably includes hard particles with an average particle size in the range 50 nm-150 m. Larger particles, in the range 10 um-150) J. m, preferably in the range 30 pm-150 m, is foremost used to achieve abrasion resistance while the smaller particles, in the range 50 nm-30 pm, preferably 50 nm-10 pm is used for achieving scratch resistance. The smaller particles is hereby used closest to the surface while the larger ones are distributed in the wear layer. The hard particles are suitably constituted of silicon carbide, silicon oxide, a-aluminium oxide and the like. The abrasion resistance is hereby increased substantially. Particles in the range 30 mm-150 mm can for example be sprinkled on still wet lacquer so that they at, least partly, becomes embedded in finished wear layer. It is therefore suitable to apply the wear layer in several steps with intermediate sprinkling stations where particles are added to the surface. The wear layer can hereafter be cured. It is also possible to mix smaller particles, normally particle sizes under 30 pm with a standard lacquer. Larger particles may be added if a gelling agent or the like is present. A lacquer with smaller particles is suitably used as top layer coatings, closer to the upper surface.

The scratch resistance can be improved by sprinkling very small particles in the range 50 nm-1000 nm on the uppermost layer of lacquer. Also these, so called nano-particles, can be mixed with lacquer, which with is applied in a thin layer with a high particle content. These nano-particles may besides silicon carbide, silicon oxide and a-aluminium oxide also be constituted of diamond.

The decor on the surface elements is suitably constituted by a number of decor segments with intermediate borders, which borders, on at least two opposite edges coincides with intended, adjacent surface elements.

Thus, the invention relates to a process for providing the decorative surface elements with a surface structure that in all essential aspects matches the decor.

The decorative surface element also comprises a base layer and a decorative upper surface. The invention is characterised in that a radiation curing lacquer is printed in a predetermined pattern as an uppermost layer on the decorative upper surface.

The radiation curing lacquer is covering only parts of the decorative upper surface. The lacquer is then exposed to radiation whereby it cures whereby a surface structure is achieved. The radiation curing lacquer is preferably cured by UV or electron beam radiation and consists of an acrylic, epoxy or a maleimide lacquer. The radiation curing lacquer is suitably applied in several steps with intermediate curing.

According to one embodiment of the invention the radiation curing lacquer includes hard particles with an average particle size in the range 50nm-150pm.

These hard particles consists of for example silicon oxide, a-aluminium oxide or silicon carbide. The main part of the hard particles preferably consists of for example silicon oxide, a-aluminium oxide or silicon carbide while a smaller amount of the hard particles consist of diamond. The hard particles consisting of diamond is suitably in the average particle size range 50nm-2pm and is placed close to the upper surface of the wear layer.

The radiation curing lacquer is suitably translucent and is applied by means of an ink-jet printer. The radiation curing lacquer may alternatively be semi-translucent. The radiation curing lacquer may according to one alternative include a matting agent which creates a structure enhancing effect in the structure.

According to a preferred embodiment of the invention the decorative upper layer further comprises a decor layer and a wear layer, which wear layer is applied on top of the decor layer whereby the radiation curing lacquer is applied on top of the wear layer. The wear layer suitably comprises UV or electron beam curing lacquer of an acrylic, epoxy or a maleimide lacquer which is cured before the step where the uppermost, structured layer is applied. The wear layer preferably comprises hard particles with an average particle size in the range 50nm-150pm. The hard particles of the wear layer preferably consists of for example silicon oxide, a-aluminium oxide or silicon carbide.

The decorative upper surface comprises a decor layer, which decor layer preferably originates from a digitally stored original. The digitally stored original is then processed in order to achieve a digital structure original whereby a surface structure that in every essential aspect matches the decor is achieved. This digital structure original is used together with control or support programs for guiding the ink-jet printer used for printing the radiation curing lacquer of the uppermost, structured layer.

According to one embodiment of the invention the surface structure is achieved by utilising the following steps; i) The radiation curing lacquer is printed in a predetermined pattern on the decorative upper surface. The radiation curing lacquer is printed so that it covers only parts of the decorative upper surface. The amount of surface covered by the radiation curing lacquer may of course be selected by desire, but it is advantageous to cover the surface to an amount greater than 50%, preferably greater than 75%, in order to achieve an abrasion resistant surface structure. ii) Hard particles with an average particle size in the range 1-150m is then sprinkled on the still sticky printed lacquer to an amount of 5-30 g/m2. iii) The lacquer is then exposed to radiation so that it cures. iv) Possible residual particles are removed by blowing air over the surface v) A layer of UV or electron beam curing lacquer is then applied on the decorative upper surface in one or more steps, so that the particles becomes, at least mainly, embedded in the lacquer.

It is according to the present invention possible to achieve matching structure on even particularly characteristic decor segments such as borderlines between simulated slabs, bars, blocks or the like and also knots, cracks, flaws and grain which is visually simulated in the decor. The structure may be stored as digital data. Said data may be used for guiding automated printers when providing said characteristic decor segments with a suitable surface structure. Said printing process is synchronised via the predetermined fixing point on the surface element.

The process described in the present application, for manufacturing surface elements is very advantageous from a logistic point of view since the number of steps when achieving a new decor is radically reduced. It is, according to the present invention possible to use digitally created or stored data for directly printing the decor on a surface element by using a ink-jet printer or a photo-static printer. The so-called set up time will thereby be very short, whereby even very special customer requirements may be met at a reasonable cost. It is according to the present invention possible to manufacture, for example, a world map with matching surface structure in very large format, stretching over a great number of surface elements without any disrupting deviations in decor and structure matching, to mainly the same cost as bulk produced surface elements. Since the decor and surface structure may be handled digitally all the way to the point of being applied to the surface of the core, set up times will be practically non-existent while at the same time a high degree of automation will be practicable. It is also possible to automatically provide the surface elements with identification and orientation marking which would make the installation of complex decor, like world maps in the example above, much easier. This has so far been impossible.

Surface elements manufactured as described above is suitably used as a floor covering material where the demands on stability and scratch and abrasion resistance is great. It is, according to the present invention, also possible to use the surface elements as wall and ceiling decorative material. It will however not be necessary to apply thick wear layer coatings in the latter cases as direct abrasion seldom occurs on such surfaces.

The invention is described further in connection to an enclosed figure, embodiment examples and schematic process descriptions showing different embodiments of the invention.

Accordingly, the figure shows parts of a surface element 1 which includes an upper decorative layer 2, edges 3 intended for joining, a lower side 4 and a supporting core 5. The process is initiated by manufacturing a supporting core 5 with a desired format and edges 3 intended for joining. The supporting core 5 is further provided with an upper side 1'suited for printing and a lower side 4. The upper side 1'of the supporting core 5 is then provided with a decor 2'by printing, utilising an inc-jet printer. The decor 2'is oriented after a predetermined fixing point on the supporting core 5. The upper side 1'of the supporting core S is provided with a protecting translucent wear layer 2"through curtain coating. The supporting core 5 is constituted by particle board or fibre board. The translucent wear layer 2"is constituted by a UV-curing acrylic lacquer which is applied in several steps with intermediate curing, of which the last one is a complete curing while the earlier ones are only partial curing. The wear layer 2"also includes hard particles of a-aluminium oxide with an average particle size in the range 0, 5pm- 150tm.

The decor side of the surface element I is provided with a surface structure 2"' which enhances the realism of the decor 2'. It possible to simulate the surface structure of, for example, wood block chevron pattern decor.

Process scheme 1. Manufacturing of a supposing core j Moulding edges with joining functionality Possible surface treatment of upper l Digitally stored decor basic data Applying decor on upper /// Applying identity code on lower side /11 Applying base lacquer coating /11 Sprinkling 75 m particles /11 Applying main lacquer coating /11 Partial curing Printing embossing pattern Sprinkling 75 pm particles l, l Partialcuring /i' i Applying top layer with 10 pm particle content l l Partialcuring Possible glazing Completecuring Inspection I Packing A supporting polymer and filler based core is manufactured in the desired format and is provided with an upper side, a lower side and edges provided with joining members, such as tongue and groove. The upper side of the supporting core is then sanded smooth after which a primer is applied. A decor is then applied on the upper side by means of a digital photo-static five colour printer. The colours are magenta, yellow, cyan, white and black. The decor is positioned from a predetermined fixing point in form of a corner of the supporting core, while the decor direction is aligned with the long side edge initiating from the same corner.

The basis for the decor is stored as digital data. This digital data has been achieved by digitising a number of wood grain patterns with a digital camera. A number of rectangular blocks with a fixed width, but of varying length is selected and parted from the digital wood grain pictures. The width of-the rectangular blocks is selected so that three block widths equals the width of a supporting core.

The digital image of the wood blocks are then classified after wood grain pattern and colour so that a number of groups is achieved. The groups are; fair wood with even grain, dark wood with even grain, fair wood with knots and flaws, dark wood with knots and flaws, fair cross-grained wood and finally dark cross-grained wood. Each group contains five different block simulations. An algorithm is feed into a computer which is used for the guiding of the printing operation so that the simulated wood blocks is digitally placed in three longitudinal rows and mixed so that two similar wood blocks never is placed next to each other. The algorithm will also guide the position of the latitudinal borderlines between the simulated wood blocks so that they are unaligned with more than one block width between adjacent rows. It will also guide the latitudinal position of the borderlines so that it either aligns with the shorter edges of the supporting core or is unaligned with more than one block width. Another printer, also guided by the computer, is utilised for printing a running matching number on the lower side short side edges.

The decor will hereby continue longitudinally over the surface elements and a perfect matching is obtained when the surface elements are placed in numerical order.

A basic layer of UV-curing acrylic lacquer is then applied by means of a rollers.

Particles with an average particle size in the range 75 llm is then sprinkled onto the still wet second basic layer which then is cured to a desired viscosity, whereby the main layer of UV-curing acrylic lacquer is applied by roller coating. The lacquer is then cured using UV-light whereby the viscosity of the lacquer increases.

The surface structuring is then initiated by printing the part of the structure that is to form elevations in the finished surface. A UV-curing acrylic lacquer is printed by means of an ink-jet printer in the desired pattern. The pattern is made up by larger areas containing non coated narrow lines of varying length and spots and will cover more than 95% of the total surface of the surface element. The ink-jet printer is controlled by a computer where the digital decor used earlier is processed to receive a digital structure matching the decor in aspects like grain direction and density, flaws, knots and border lines between simulated wood blocks. This processing may be achieved by an automatic process where an algorithm is used as a digital filter or by manual operation during the scanning procedure. It is also possible to scan the actual structure of the archetype. By this procedure a surface structure matching all essential aspects of the decor is achieved.

Particles with an average particle size in the range 75 llm is then sprinkled onto the still wet printed structure layer. The lacquer is then cured using UV-light to a desired viscosity. A top layer of UV-curing acrylic lacquer with an additive in the form of hard particles with an average size of 10 m, is then gently applied by means of a hard roller so that the only particle coated part of the surface absorbs the lacquer. The lacquer is then cured with UV-light to a desired viscosity. It may, in some cases, be advantageous to perform a glazing operation on the top surface in order to make the edges between the main upper surface and the recesses more well defined. This is suitably achieved by pressing a heated roller towards the surface. The surface temperature of the roller is then suitably between 40 and 150°C.

The lacquer is then, if not already completely cured at a prior stage in the process, completely cured with UV-light to desired strength. The finished surface elements may then be inspected by the naked eye or by a digital camera supported by a computer. The surface elements are then packed in batches which are provided with identification markings.

The process above will make it possible to have a completely customer driven manufacturing where even very small quantities may be produced with the same efficiency as bulk manufacturing. Even though only one decor is described in connection to the process scheme above, it becomes clear to anyone skilled in the art, that a decor is changed very easily in the process. All of the important steps of the manufacturing such as printing, structuring, inspection, packaging and identification marking may be controlled and supervised by central processing data. This will make it logistically possible to manufacture customer designed decor. Such a process is exemplified as follows ; The customer utilises a database via Internet or at a local dealer. It is also possible for another operator utilise a database. The database contains samples and/or reduced resolution copies of a great variety of standard decor which can be combined after predetermined parameters.

The parameters may, for example, concern a single surface element where, for example, chevron pattern, diamond pattern and block pattern may be the choices of decor segmentation. It will here be possible to select a set of different simulations to randomly or by selected parameters fill the segments, for example, marble, birch and mahogany. The customer may also add an inlay from a design of his own which is digitised and processed, preferably automatically, to a desired format and resolution.

The parameters may alternatively include decor segments that requires the space of several surface elements, for example a map over the world. The parameters may here further include fading of the larger design to a surrounding decor, surrounding frame of other decor etc.

The customers enters the measurements of the surface that is to be covered by the surface elements. The customer then makes selections from the database and is able to see his selection as a completed surface, either on screen or by printing.

The visualisation program used, is suitably also used for calculating installation pattern and presenting installation instructions with identification numbers on surface elements and where to cut the elements in order to make a perfect match.

The surface elements may also be provided with removable matching lines on the decorative side making matching of decor between adjacent rows easier. The customer or dealer may then confirm his order via electronic mail where the pattern and decor is reduced to a code sequence and the order can be the direct input to the computer guiding the manufacturing process as described above. The customer and/or dealer data follows the manufacturing process all the way to packaging and a fully customer guided manufacturing process is achieved.

Process scheme 2 Manufacturing supporting core Surface treatment Digitally stored decor basic data Application of décor incl. identity code on lower side Roller coating of basic layer with additive of 10 m particles// Partialcuring Printing embossing pattern Sprinkling 75 llm particles /,/ Partial curing i Applying structured coating with additive of 10 Vim particles I I Complete curing / Moulding edges with joining functionality I/ Inspection / / Packing A supporting fibre board based core is manufactured in the desired format and is provided with an upper side, a lower side and edges. The upper side of the supporting core is then sanded smooth after which a white primer is applied. A decor is then applied on the upper side by means of a digital ink-jet four colour printer. The colours are magenta, yellow, cyan and black. The decor is positioned from a predetermined fixing point in form of a corner of the supporting core, while the decor direction is aligned with the long side edge initiating from the same corner.

The basis for the decor is stored as digital data. This digital data has been achieved by digitising a number of wood grain patterns with a digital camera. A number of rectangular blocks with a fixed width, but of varying length are selected and parted from the digital wood grain pictures. The width of the rectangular blocks is selected so that three block widths equals the width of a. finished surface element. The digital image of the wood blocks are then joined digitally to form a rectangular surface of a specified size, for example, 200 x 1200 mm. A selected amount of such combinations of different blocks are designed as described above so that a number of slightly different rectangular surfaces is achieved. The printer, or preferably a set of printers are positioned so that a desired number of rectangular decor surfaces with a specified intermediate distance is printed on the supporting core. The intermediate distance between the rectangular surfaces is the distance needed for parting and moulding of edges. The decor printer or printers are also used for printing fixing points at predetermined positions. Another printer, also guided by the computer, is utilised for printing an identity code on the lower side of each intended finished surface element.

A basic layer of UV-curing acrylic lacquer with an additive of 10% by weight of hard particles of a-cellulosc with an average particle size in the range 10pm is then applied on top of the printed decor by means of rollers. The lacquer is then cured with UV-light to desired viscosity.

The surface structuring is then initiated by printing the part of the structure that is to form elevations in the finished surface. A UV-curing acrylic lacquer is printed by means of an ink-jet printer in the desired pattern. The pattern covers more than 95% of the total surface of the surface element. The ink-jet printer is controlled by a computer where the digital decor used earlier is processed to receive a digital structure matching the decor in aspects like grain direction and density, flaws, knots and border lines between simulated wood blocks. This processing may be achieved by an automatic process where an algorithm is used as a digital filter or by manual operation during the scanning procedure. By this procedure a surface structure matching all essential aspects of the decor is achieved. Particles with an average particle size in the range 75 pm is then sprinkled onto the still wet printed structure layer, which then is cured. Residual particles are removed, whereupon the main layer of UV-curing acrylic lacquer with an additive in the form of hard particles of a-aluminium oxide with an average size of 10 m, is gently applied by means of a hard roller so that only the parts of the surface covered with particles will absorb the lacquer. The lacquer is then completely cured with UV-light to desired strength, whereby the finished surface element is cut into the predetermined formats which are provided with edges with joining functionality are moulded by milling. The cutting and edge moulding process is positioned from fixing point printed close to the decor. The surface elements may then be inspected by the naked eye or by a digital camera supported by a computer. The surface elements are then packed in batches and provided with identification markings.

It is, according to an alternative procedure in the process, possible to cut and mould the edges at an earlier stage in the process. It is suitable to apply and cure a protecting layer of lacquer on top of the printed decor followed by cutting and moulding of the edges. The remaining and main part of the wear layer is then applied as described in connection to process scheme I or 2 above.

The process above will make it possible to have a customer initiated manufacturing where even very small quantities may be produced with the same efficiency as bulk manufacturing. Even though only one decor is described in connection to the process scheme above, it becomes clear anyone skilled in the art, that décor is changed very easily in the process. All of the important steps of the manufacturing such as printing, structuring, inspection, packaging and identification marking may be controlled and supervised by central processing data.

The invention is also described through embodiment examples.

EXAMPLE 1.

A supporting core of medium density fibre board were sanded smooth. A layer of primer lacquer were applied on top of the fibre board. The primer were cured after which a decor was printed on top of the primer.

The build up of a wear layer was then initiated by applying 30g/m2 of UV-curing acrylic lacquer by means of roller coating. 20g/m2 of hard particles made of a-aluminium oxide with an average particle size of 70pm were sprinkled on the still sticky lacquer. The lacquer was then exposed to a predetermined energy amount of UV-light so that it cured only partly and the viscosity was increased.

Another 30g/m2 of UV-curing acrylic lacquer was then roller coated onto the already applied layer after which another 20g/m2 of a-aluminium oxide particles with an average particle size of 7011m were sprinkled on the still sticky second coating. The lacquer was then exposed to a predetermined energy amount of UV-light so that it cured only partly and the viscosity was increased. Three layers of UV-curing acrylic lacquer was then applied by roller coating with intermediate partial curing as a above. Each of the three layers had a surface weight of 20g/m2.

The hard particles were completely embedded in the lacquer after the three layers were applied and a plane upper wear layer surface was achieved.

A structuring and top coating procedure was then initiated. A layer of UV-curing acrylic lacquer was printed by means of an ink-jet printer in a predetermined pattern on top of the previous, partly cured, layers. Narrow parts of the surface were left non-coated. 20g/m2 of a-aluminium oxide particles were sprinkled on the still wet partial coating after which the lacquer was cured with UV-curing lacquer. Residual particles were then removed resulting in a surface which partially was free from particles. A top coating procedure was then initiated by applying a topcoat lacquer which contained 10% by weight of hard particles of a-aluminium oxide with an average particle size of 1 0llm by means of gentle roller coating with a hard roller so that only the parts of the surface covered with particles were coated. The first layer was applied to a surface weight of I og/M2.

The topcoat lacquer was then exposed to a predetermined energy amount of UV-light so that it cured only partly and the viscosity was increased. Further layers of the topcoat lacquer was then applied and partly cured as described above.

All layers were then exposed to a predetermined energy amount of UV-light so that it cured completely.

The wear layer was then tested for abrasion resistance according to ISO 4586/2-88, where an IP value of 8200 turns was obtained. An IP value of 8200 turns is fully sufficient for floor covering materials with medium to heavy traffic like hotel lobbies, hallways and the like.

EXAMPLE 2.

A supporting core of medium density fibre board were sanded smooth. A layer of primer lacquer were applied on top of the fibre board. The primer were cured after which a decor was printed on top of the primer.

The build up of a wear layer was then initiated by applying 30g/m2 of UV-curing acrylic lacquer by means of roller coating. 20g/m2 of hard particles made of a-aluminium oxide with an average particle size of 701lm were sprinkled on the still sticky lacquer. The lacquer was then exposed to a predetermined energy amount of UV-light so that it cured only partly and the viscosity was increased.

Another 30g/m2 of UV-curing acrylic lacquer was then roller coated onto the already applied layer after which another 20g/m2 of a-aluminium oxide particles with an average particle size of 70pm were sprinkled on the still sticky second coating. The lacquer was then exposed to a predetermined energy amount of UV-light so that it cured only partly and the viscosity was increased. Three layers of UV-curing acrylic lacquer was then applied by roller coating with intermediate curing as a above. Each of the three layers had a surface weight of 20g/m2. The hard particles were completely embedded in the lacquer after the three layers were applied and a plane upper wear layer surface was achieved. Also the uppermost of the three layers of lacquer was cured to a desired viscosity.

A second decor layer was then printed on top of the wear layer. The second decor layer, which was identical to the first decor closest to the core, was oriented and positioned so that it completely matched the first decor.

A top coating procedure was then initiated. A layer of UV-curing acrylic topcoat lacquer was applied by means of a roller coater on top of the second decor layer.

The topcoat lacquer contained 10% by weight of hard particles of a-aluminium oxide with an average particle size of 10pm. The topcoat layer was applied to a surface weight of lOg/m2. The topcoat lacquer was then exposed to a predetermined energy amount of UV-light so that it cured and the viscosity was increased.

The build up of a structured upper wear layer was then initiated by applying 10g/m2 of UV-curing acrylic lacquer by means of roller coating. The surface structuring was then initiated by printing the part of the structure forming the elevated parts of the finished surface. A UV-curing acrylic lacquer with a content of silicone polymer was printed by means of an ink-jet printer in the desired pattern. The pattern covered around 95% of the total surface of the surface element. 20g/m2 of hard particles made of a-aluminium oxide with an average particle size of 70pm were then sprinkled on the still sticky lacquer. The lacquer was then exposed to a predetermined energy amount of UV-light so that it cured only partly and the viscosity was increased. Residual particles were then removed by blowing an air stream over the surface. A top coating procedure was then initiated by applying a topcoat lacquer which contained 10% by weight of hard particles of a-aluminium oxide with an average particle size of 10pm by means of gentle roller coating with a hard roller so that only the parts of the surface covered with particles were coated. The first topcoat layer was applied to a surface weight of lOg/m=. The topcoat lacquer was then exposed to a predetermined energy amount of UV-light so that it cured and the viscosity was increased. Further layers of the topcoat lacquer was then applied and cured as described above. All layers were then exposed to a predetermined energy amount of UV-light so that it cured completely.

The wear layer was then tested for abrasion resistance according to ISO 4586/2-88, where an IP value of 10300 turns was obtained. An IP value of 10300 turns is fully sufficient for floor covering materials with heavier traffic like airports, railway stations and the like. The second layer of decor and wear layer will add abrasion resistance without having obtained an unwanted hazy effect in the decor.

EXAMPLE 3.

A supporting core of medium density fibre board were sanded smooth. A layer of primer lacquer were applied on top of the fibre board. The primer were cured after which a decor was printed on top of the primer.

The build up of a wear layer was then initiated by applying 30g/m2 of UV-curing acrylic lacquer by means of roller coating. 20g/m2 of hard particles made of a-aluminium oxide with an average particle size of 70pm were sprinkled on the still sticky lacquer. The lacquer was then exposed to a predetermined energy amount of UV-light so that it cured and the viscosity was increased. Three layers of UV-curing acrylic lacquer was then applied by roller coating with intermediate partial curing as a above. Each of the three layers had a surface weight of 20g/m2.

The hard particles were completely embedded in the lacquer after the three layers were applied and a plane upper wear layer surface was achieved.

A structuring and top coating procedure was then initiated. A layer of UV-curing acrylic lacquer was printed by means of an ink-jet printer in a predetermined pattern on top of the previous, partly cured, layers. Narrow parts of the surface were left non-coated. 15g/m2 of a-aluminium oxide particles were sprinkled on the still wet partial coating after which the lacquer was cured with UV-curing lacquer. Residual particles were then removed resulting in a surface which partially was free from particles. A top coating procedure was then initiated by applying a topcoat lacquer which contained 10% by weight of hard particles of a-aluminium oxide with an average particle size of 1 011m by means of gentle roller coating with a hard roller so that only the parts of the surface covered with particles were coated. The first layer was applied to a surface weight of 10g/m2.

The topcoat lacquer was then exposed to a predetermined energy amount of UV-light so that it cured only partly and the viscosity was increased. Further layers of the topcoat lacquer was then applied and partly cured as described above.

All layers were then exposed to a predetermined energy amount of UV-light so that it cured completely.

The wear layer was then tested for abrasion resistance according to ISO 4586/2-88, where an IP value of 4100 turns was obtained. An IP value of 4100 turns is fully sufficient for floor covering materials with medium to heavy traffic like hotel lobbies, hallways and the like.

EXAMPLE 4.

A supporting core of medium density fibre board were sanded smooth. A layer of primer lacquer were applied on top of the fibre board. The primer. were cured after which a decor was printed on top of the primer.

10g/m2 of UV-curing acrylic lacquer which contained 10% by weight of hard particles of a-aluminium oxide with an average particle size of 1 0llm were applied by means of roller coating. The lacquer was then exposed to a predetermined energy amount of UV-light so that it cured and the viscosity was increased.

A structuring and top coating procedure was then initiated. A layer of UV-curing acrylic lacquer was printed by means of an ink-jet printer in a predetermined pattern on top of the previous, partly cured, layers. Narrow parts of the surface were left non-coated. 15g/m2 of a-aluminium oxide particles were sprinkled on the still wet partial coating after which the lacquer was cured with UV-curing lacquer. Residual particles were then removed resulting in a surface which partially was free from particles. A top coating procedure was then initiated by applying a topcoat lacquer which contained 10% by weight of hard particles of a-aluminium oxide with an average particle size of zip by means of gentle roller coating with a hard roller so that only the parts of the surface covered with particles were coated. The first layer was applied to a surface weight of 10g/m2.

The topcoat lacquer was then exposed to a predetermined energy amount of UV-light so that it cured only partly and the viscosity was increased. Further layers of the topcoat lacquer was then applied and partly cured as described above.

All layers were then exposed to a predetermined energy amount of UV-light so that it cured completely.

The wear layer was then tested for abrasion resistance according to ISO 4586/2-88, where an IP value of 1800 turns was obtained. An IP value of 1800 turns could be sufficient foi floor covering materials with light traffic like bedrooms, living rooms and the tike.

The invention is not limited to the embodiments shown as these can be varied in different ways within the scope of the invention. It is for example possible to plane the surface by pressing one or more glazing rollers towards the surface structured wear layer before or after the complete curing stage. The glazing rollers are preferably also heated to a surface temperature above 30°C, preferably in the range 35°C-100°C.

The hard particles added to the lacquer consists of for example silicon oxide, a-aluminium oxide or silicon carbide. According to one embodiment of the invention the main part of the hard particles consists of for example silicon oxide, a-aluminium oxide or silicon carbide while a smaller amount of the hard particles consist of diamond. The hard particles consisting of diamond is then in the average particle size range 50nni-2pm and is placed close to the upper surface of the wear layer.