Title:
PROCESS FOR REFINING SILVER BULLION WITH GOLD SEPARATION
Document Type and Number:
WIPO Patent Application WO/2001/055462
Kind Code:
A1
Abstract:
The present invention concerns a process for refining silver bullion, i.e. raw silver containing generally more than 90 % silver besides Se, Pb, Au, Cu and platinum group metals (PGM) as main impurities. The process comprises the steps of: optionally removing Se as gaseous SeO2 from the molten metallic phase by injecting air, which is preferably O¿2? enriched, into the metallic phase at a preferred bath temperature of 1000-1100 °C; optionally slagging off the Pb by contacting the molten metallic phase with a silica and borax based flux at a preferred bath temperature of 1000-1150 °C; granulating the molten metallic phase in water, thereby forming Ag rich granules; leaching the Ag rich granules with HNO¿3? at a temperature above 50 °C, preferably in an O¿2? enriched atmosphere, followed by filtration, thereby separating an Au bearing residue from an Ag rich liquor; heating the Ag rich liquor, thereby evaporating H¿2?O and forming an AgNO¿3? bearing melt; maintaining the AgNO¿3? bearing melt at a temperature of 220-350 °C for at least 15 minutes, thereby forming a mixture of a purified AgNO¿3? and of a denitration residue containing essentially all the PGM as oxides; separating the purified AgNO¿3? from the denitration residue. By this process, the many drawbacks of the classical electrolytic refining of silver are avoided.

Inventors:
VANHOUTTE DIRK (BE)
BROUWER SYBOLT (BE)
Application Number:
PCT/EP2001/000613
Publication Date:
August 02, 2001
Filing Date:
January 17, 2001
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
UNION MINIERE SA (BE)
VANHOUTTE DIRK (BE)
BROUWER SYBOLT (BE)
International Classes:
C22B9/05; C01B21/48; C01G5/00; C22B3/04; C22B3/06; C22B3/20; C22B3/44; C22B11/00; C22B11/02; (IPC1-7): C22B11/00; C01G5/00
Foreign References:
DE406320C1924-11-17
DE406430C1924-11-21
DE646087C1937-06-10
GB1396270A1975-06-04
US5000928A1991-03-19
US4857107A1989-08-15
DE947741C1956-08-23
Other References:
PATENT ABSTRACTS OF JAPAN vol. 010, no. 094 (C - 338) 11 April 1986 (1986-04-11)
DATABASE WPI Section Ch Week 200018, Derwent World Patents Index; Class M25, AN 2000-203923, XP002168653
Attorney, Agent or Firm:
Umicore (Att. A. Pilate Kasteelstraat 7 Olen, BE)
Download PDF:
Claims:
Claims
1. 1. Process for refining impure silver bullion containing metals fror. the group consisting of Pb, Se, Cu, Au and PGM as impurities, comprising the steps of leaching the silver bullion with HN03 at a temperature above 50 OC, preferably in an Oz enriched atmosphere, followed by filtration, thereby separating an Au bearing residue from an Ag rich liquor; heating the Ag rich liquor, thereby evaporating H20 and forming an AgN03 bearing melt; maintaining the AgN03 bearing melt at a temperature of 220350 C for at least 15 minutes, thereby forming a mixture of a purified AgN03 and of a denitration residue containing essentially all the PGM as oxides; separating the purified AgN03 from the denitration residue, either by filtrating the mixture at a temperature above 220 °C, thereby obtaining purified molten AgN03 ; or by reacting the mixture with water, followed by filtration, thereby obtaining a purified AgNO3 solution. *& 2.
2. Process for refining impure silver bullion according to claim 1, whereby the leaching step is preceded by the following steps: heating the silver bullion, thereby forming a molten metallic phase; granulating the molten metallic phase in water, thereby forming Ag rich granules; and the leaching step is performed on the Ag rich granules.*& 3.
3. Process according to claim 2, whereby Se is removed as gaseous Set2 from the molten metallic phase by injecting air, which is preferably Oz enriched, into the metallic phase at a temperature of 100012<0 OC, and preferably of 10001100 °C.*& 4.
4. Process according to claims 2 or 3, whereby the molten metallic phase is contacted with an acidic flux at a temperature of 10001300 °C, and preferably of 10001150 °C, and Pb is slagged off.*& 5.
5. Process according to claims 1 to 4, whereby the AgN03 bearing melt is maintained at a temperature of 300350 °C for at least 15 minutes, thereby forming a mixture of a purified AgN03 and of a denitration residue containing essentially all the Cu and PGM as oxides.*& 6.
6. Process according to claims 1 to 5, whereby the purified molten AgNO3 is further processed to elemental Ag, comprising the steps of decomposing the purified molten AgNO3 at a temperature above 400 °C into purified Ag and NOx ; scrubbing the NOX with H2O in an oxidizing atmosphere, thereby forming HN03, which is optionally recycled to the leaching step.*& 7.
7. Process according to claims 1 to 5, whereby the purified AgNO3 solution is further processed to elemental Ag, comprising the steps of either hydrolyzing the purified AgN03 solution with NaOH or KOH, thereby forming an Ag2O precipitate, which is separated by filtration; decomposing the Ag2O at a temperature above 300 °C into elemental Ag and 02 ; or reacting the purified AgN03 solution with HC1, thereby forming AgCl and HN03, which are separated by filtration, the HN03 being optionally recycled to the leaching step, transforming the AgCl to elemental Ag and NaCl by either reacting the AgCl with an NaOH solution in presence of a reducing agent, or by heating the AgCl with a soda flux above 1000 °C. Abstract Process for refining silver bullion The present invention concerns a process for refining silver bullion, i. e. raw silver containing generally more than 90 % silver besides Se, Pb, Au, Cu and platinum group metals (PGM) as main impurities. The process comprises the steps of: optionally removing Se as gaseous Se02 from the molten metallic phase by injecting air, which is preferably 02 enriched, into the metallic phase at a preferred bath temperature of 10001100 °C ; optionally slagging off the Pb by contacting the molten metallic phase with a silica and borax based flux at a preferred bath temperature of 10001150 °C ; granulating the molten metallic phase in water, thereby forming Ag rich granules; leaching the Ag rich granules with HN03 at a temperature above 50 °C, preferably in an 02 enriched atmosphere, followed by filtration, thereby separating an Au bearing residue from an Ag rich liquor; heating the Ag rich liquor, thereby evaporating H20 and forming an AgN03 bearing melt; maintaining the AgN03 bearing melt at a temperature of 220350 °C for at least 15 minutes, thereby forming a mixture of a purified AgN03 and of a denitration residue containing essentially all the PGM as oxides; separating the purified AgN03 from the denitration residue. By this process, the many drawbacks of the classical electrolytic refining of silver are avoided.
Description:
Process for refining silver bullion The present invention concerns a process for refining silver bullion.

Silver bullion is a raw silver alloy originating amongst others from lead-silver smelting, containing generally more than 90 % silver besides Se, Pb, Au, Cu and platinum group metals (PGM) as main impurities. Silver bullion is normally available as large castings.

The present state of technology for refining silver bullion alloy is electrolytic refining: after casting anodes, the alloy is electrorefined in an AgN03-HN03 electrolyte. The following output streams are hereby produced: -purified Ag obtained as dendrites deposited on a stainless steel cathode sheet, -anode slime, containing Au and PGM, which is collected in fabric bags surrounding the anode; -a bleed on the AgN03-HN03 electrolyte.

The electrolyte bleed is necessary to prevent the accumulation of impurities which anodically dissolve completely as nitrates, such as Pb and Cu, or partially, such as Pd.

A first method for bleed treatment is the retrieval of the dissolved Ag by cementation with a less noble metal. The impurities such as Pb and Cu remain in the nitrate bearing bleed solution.

A second method for bleed-treatment is by denitration, also referred to as the black melt process in Ullmann's Encyclopedia of Industrial Chemistry, 1993, vol. A24, p. 134. In this case, the water is evaporated from the electrolyte, and the anhydrous nitrate melt is heated to at least 170 °C. The nitrates of PGM decompose to insoluble oxides. Cu nitrate decomposes partially, to an extent determined by the temperature of the melt. After reaction with water, the oxides are separated from the AgN03 bearing solution. However, if an excess of Pb and Cu has to be removed from the electrolyte, at least part of the bleed must be treated according to the first method. Here again,

the Ag has to be retrieved by cementation, producing an impure Pb bearing nitrate solution.

Both methods thus necessitate a rather elaborate treatment of the bleed whereby nitrate solutions are produced. Their further treatment leads to the discharge of nitrates.

This disadvantage is further exacerbated when higher levels of Pb, Cu or Pd are present in the Ag bullion: a higher amount of impurities has indeed to be evacuated by bleeding a correspondingly larger quantity of electrolyte.

Also, more than approximately 2 % Pd in the raw silver leads to problems as Pd then gets embedded in the refined Ag deposit.

Both the electrolytic refining process and the anode slime treatment are inherently slow. Consequently, metals have a long residence time and the inventory of the refining plant is high as are the ensuing financial costs.

The present invention aims at resolving the above mentioned disadvantages. Moreover, the new process produces Ag with a higher purity than the state of the art process.

The invention discloses a process for refining silver bullion. The process comprises the steps of -leaching the silver bull-ion with HN03 at a temperature above 50 °C, preferably in an 02 enriched atmosphere, followed by filtration, thereby separating an Au bearing residue from an Ag rich liquor; -heating the Ag rich liquor, thereby evaporating H20 and forming an AgNO3 bearing melt; -maintaining the AgN03 bearing melt at a temperature of 220-350 °C for at least 15 minutes, thereby forming a mixture of a purified AgNO3 and of a denitration residue containing essentially all the PGM as oxides; -separating the purified AgN03 from the denitration residue, either by

-filtrating the mixture at a temperature above 220 °C, thereby obtaining a purified molten AgNO3 ; or by -reacting the mixture with water, followed by filtration, thereby obtaining a purified AgNO3 solution.

The leaching operation can be greatly accelerated and thus rendered more economical if performed on granules instead of on large castings. To this end the leaching step can be preceded by the following steps: -heating the silver bullion, thereby forming a bath with a molten metallic phase; -granulating the molten metallic phase in water, thereby forming Ag rich granules; and the leaching step is performed on the Ag rich granules.

It is useful to take advantage of the above melting operation, which is needed for the granulation, to remove Se and Pb from the molten metallic phase. Se can be completely removed as gaseous Se02 from the molten metallic phase by injecting air, which is preferably Oz enriched, into the metallic phase at a temperature of 1000-1250 °C, or preferably of 1000-1100 °C. Pb can be removed from the molten metallic phase by contacting this phase with an acidic flux at a temperature of 1000-1300 °C, or preferably of 1000-1150 °C, whereby Pb is slagged off. In this way, the quantities of Se and Pb to be treated in the following steps of the process are decreased substantially. Se and Pb. can be-removed in either order.

Cu can be completely removed by increasing the temperature during the denitration of the AgNO3 bearing melt to 300-350 °C, thereby forming a mixture of a purified AgNO3 and of a denitration residue containing essentially all the Cu and PGM as oxides; When purified dry AgNO3 is obtained in the process as described above, it can be commercialized as such. It also can be further processed to metallic Ag. To this end, the purified AgN03 is decomposed at a temperature above 400 °C into elemental Ag and nitrogen oxides (NOX)

which are scrubbed with H20 in an oxidizing atmosphere, thereby forming HNO3, which is optionally recycled to the leaching step.

When the purified AgN03 solution is obtained in the process as described above, it can be commercialized as such. It also can be further processed to metallic Ag.

A first method is to hydrolyze the purified AgN03 solution with NaOH or KOH, thereby forming an Ag2O precipitate, which is separated by filtration and to decompose the Ag2O at a temperature above 300 °C into elemental Ag and °2- A second method is to react the purified AgN03 solution with HC1, thereby forming AgCl and HN03, which are separated by filtration, the HN03 being optionally recycled to the leaching step. The AgCl is then transformed to elemental Ag and NaCl either by reacting the AgCl with an NaOH solution in presence of a reducing agent, or by heating the AgCl with a soda flux above 1000 °C.

The claimed process is well suited to refine raw silver, especially when high levels of Pb, Au, Cu and Pd are present. No nitrates are discharged in the environment. Au and PGM are readily separated and recovered from the Ag stream. The inventory of precious metals is thus much lower than with electrolytic refining.

The mandatory and the preferred working conditions of the new process are explained hereunder.- When Se is not removed before the molten metallic phase is granulated in water, it will concentrate in the Au bearing residue during the leaching of Ag with HN03. This will considerably complicate the refining of Au from the Au bearing residue.

During Se removal, the bath temperature should not exceed ec.

The higher the temperature, the lower the rate of Se removal. A temperature of up to 1100 °C is therefore preferred. The bath should in any case remain above 1000 °C, i. e. well above the melting point

of the raw silver. It is advisable to remove any slag from the surface of the metallic bath to enhance the volatilization rate of Se02.

During Pb removal, the bath temperature should not exceed 1300 °C.

With respect to refractory wear, a temperature of up to 1150 °C is preferred. The flux used for slagging off the Pb should be of the acidic type. An acidic flux is a flux comprising phoshates, silicates or borates as essential components. A flux consisting of Si02 and Na2B407. 5aq in a weight ratio between 15: 85 and 20: 80 is recommended.

When leaching the Ag rich granules with HN03, a minimum temperature of 50 °C is needed. At a lower temperature, there is a risk for the leaching reaction to slow down or even to stop temporarily, and then to resume violently. Such unstable behavior is to be avoided for obvious safety reasons. Furthermore, it is recommended to raise the temperature gradually to at least 70 °C during leaching to obtain a residue which is as rich as possible in Au.

Preferably, the amount and concentration of HN03 are chosen so as to obtain an AgN03 solution with approximately 1000 g/1 of Ag and a free HN03 concentration of 1.5 M. In this way, the volume of AgN03 solution to be processed is kept low, while crystallization of AgNO3 is avoided as long as the solution is kept above 45 °C.

During leaching, it is preferred to maintain an 02 enriched atmosphere above the reaction mixture. To this end, the vessel might be of the closed type or of the pressurized type. An oxidizing atmosphere is indeed helpful to recycle NOX, which are a byproduct of the leaching reaction, to HN03 in situ. The reactions are: 2NO + 02-> 2NO2 and d 3NO2 + H20-> 2HNO + NO.

A high O2 partial pressure is useful to enhance the reaction rates.

The purpose of the next operation is to separate the Cu, PGM, and the residual Pb from the Ag rich liquor. A heat treatment is applied whereby most impurities nitrate, i. e. their nitrate decomposes to

oxide, forming an insoluble residue. In this step, the temperature of the AgN03 bearing melt should be kept between 220 and 350 °C. A hold time of at least 15 minutes is needed to ensure a sufficient denitration level.

However, when Cu has to be removed down to 10 ppm or less as referenced to Ag, a higher minimal denitration temperature of 300 °C has to be maintained to fully decompose Cu nitrates.

There are two methods to separate the mixture of the purified AgN03 and the denitration residue.

The first method is the filtration of the mixture as a melt. The filtration has to be performed at a temperature of at least 220 °C so as to stay well above the solidification temperature of AgN03.

Purified molten AgNO3 is obtained.

The second method is to first react the mixture with water and then to filtrate the obtained slurry. For similar reasons as for those explained above for the HN03 leaching, the amount of water with which the mixture is reacted is determined so as to obtain a purified AgN03 solution with preferably about 1000 g/l of Ag.

Purified AgN03 or AgN03 solutions can be commercialized as such.

However, if elemental Ag is needed, then the above process should be supplemented with a process for the transformation of purified AgN03 to Ag metal. To this end, any of the two methods described hereunder can be applied.

In a first method, the purified AgN03 is injected in a furnace where it is decomposed at a temperature above 400 °C. The decomposition products are elementary Ag and NOX. A scrubber converts the NOX to HN03 which can be reused in the leaching step. Any Ag compound present in the flue dust is also converted to AgNO3 in the scrubber. The decomposition can be performed below or above the melting point of Ag. The latter case lends itself more easily to continuous processing of AgN03.

The above method will normally be applied directly on the purified molten AgNO3 ; it is however also applicable to the purified AgNO3 solutions in which case water is evaporated first.

A second method starts from the purified AgN03 solution. In a first step, an insoluble Ag compound such as Ag2O is precipitated, e. g. by hydrolysis of the AgNO3 solution with KOH, or, preferably, with NaOH.

In the latter case, the byproduct of the hydrolysis is an NaN03 solution. This NaN03 solution is relatively pure and can be transformed into solid NaN03 by a known drying or crystallization process. For example, by using fluid bed drying, granules of NaN03 are obtained which are similar in appearance and in composition to commercially available prills.

The Ag2O is optionally washed and is then thermally decomposed to Ag and 02 at a temperature of at least 300 °C. Sponge-like elemental Ag is obtained, which is re-melted and cast into ingots or granulated.

If Pb has been removed to a large extent from the molten metallic silver bullion phase before leaching the Ag with HN03, then any traces of Pb which are still present in the sponge-like elemental Ag can be removed by natural volatilization during the re-melting and casting of Ag, or by absorption of Pb in a relatively small amount of silica- borax based flux. However, if Pb has not been removed from the molten metallic phase before the leaching step, then it can be removed from the molten Ag by blowing air, or by absorption in a relatively large amount of silica-borax based flux.

An alternative to the precipitation of Ag2O is the precipitation of a halide of Ag such as AgCl. This is done by reacting the purified AgNO3 solution with HC1 according to the reaction: AgNO3 + HC1-> AgCl + HN03.

Thereafter, two different reaction schemes are available to obtain elemental Ag. According to a first scheme, AgCl is transformed to metallic Ag by melting with a soda flux: 2AgCl + Na2CO3-> 2Ag + 2NaCl + CO2 + 1/202.

According to a second scheme, an aqueous AgCl suspension is formed which is then reduced with H2 to metallic Ag under addition of NaOH.

The reaction is: AgCl + NaOH + 1/2H2-> Ag + NaCl + H2O.

Both alternatives lead to the formation of NaCl, whether as an aqueous solution or as a solid, which normally can be discharged without harm.

Each essential step of the invention is further illustrated with an example.

Example 1 250 kg of silver bullion is melted and brought at a temperature of 1050 °C. 550 1/hr air enriched with 220 1/hr O2 is blown through the molten bath. Any slag which is formed during blowing is removed well before the slag completely covers the bath surface.

After 90 minutes of blowing, 10 kg flux consisting of 83 wt% Na2B407. and 17 wt% Si02 is added and contacted for 20 minutes with the bath while maintaining the injection of 550 1/hr air and 220 1/hr O2. After 20 minutes, the molten slag is drawn off. The addition of flux and the removal of molten slag after 20 minutes is repeated 2 more times while maintaining the same gas injection. The molten metal is then granulated in water at 50 °C.

The composition of silver bullion and of the obtained Ag rich granules is reported-in Table 1-. This process proves to be capable to remove Pb and Se to below 15 ppm and 4 ppm respectively. Because traces of Pb and Se remaining in the Ag are also partially removed in the next operations of the process, a refined Ag containing typically 2 ppm Pb and <1 ppm Se can be expected.

Table 1: Removal of Pb and Se from the silver bullion (all concentrations in ppm) Pb Se Silverbullion 578 52 Ag rich granules <15 <4

Example 2 To 1 kg of Ag rich granules with a mean diameter of 4 mm, an amount of 0.9 1 of 60 % HN03 solution is added at a flow rate of 0.45 1/h in a water cooled jacket reactor. During addition of the acid, the temperature of the mixture is maintained at 60 °C. Pure °2 is injected into the suspension at a flow rate of 40 g/h. An overpressure of 50 kPa in maintained. After addition of HNO3, the temperature is raised to 80 °C. Then, for 0.5 h, 02 continues to be injected at a flow rate of 40 g/hr. The obtained mixture of Au bearing residue and of Ag rich liquor is separated by filtration. The residue is washed with 50 ml water and dried.

The compositions are shown in Table 2. It appears that the Au bearing residue has a very high Au content and that this residue tends to capture residual Se present in the Ag rich granules. No significant amount of Au is left in the Ag rich liquor.

Table 2: Separation of Au Ag Au Pt Pd Pb Se Ag rich granules matrix 1.4 % 1539 4811 12 ppm 5 ppm ppm ppm Au bearing residue 7300 98.9 % 1000 476 ppm <100 147 ppmppm ppm ppm Ag rich liquor 1000 <0.2 1.7 g/l 6.8 g/l <0.1 <0.01 g/l mg/l g/l g/l Example 3 This example illustrates the effect of the denitration of the Ag rich liquor. In this case, the denitration residue is separated from the purified molten AgNO3 by hot filtration.

270 kg of silver bullion is purified as described in Example 1. The obtained Ag rich granules are then leached under conditions as described in Example 2. The Ag rich liquor, at a concentration of 1000 g/1 Ag, is first evaporated and then further heated to a melt at 350 °C for 2 h. Partial denitration of Pb and substantially complete

denitration of Cu and PGM occurs at this temperature and the oxides of these metals form an insoluble denitration residue. Thereafter, the mixture of molten AgN03 and precipitated oxides is transferred to a pressure leaf filter equipped with a layered sintered stainless steel mesh with an absolute filter rating of 5 um. The mixture is filtrated under a differential pressure of 6 bars, at a temperature of 280 °C.

Table 3 shows the compositions. It is clear that the purified molten AgN03 is substantially free from PGM, Pb and Cu. These impurities are concentrated in the denitration residue.

Table 3: Removal of PGM, Pb and Cu after denitration by filtration of AgN03 in the molten B,,. |Ag |Pt |Pd |Pb |Cu Ag rich granules matrix 1410 ppm 5175 ppm 32 ppm 3500 ppm Ag rich liquor1000 g/1 1.3 g/l 5.1 g/l 0.03 g/l 3.5 g/l Purified molten AgN03 matrix <0. 3 ppm 1. 6 ppm 9 ppm <1 ppm Example 4 This example illustrates the effect of the denitration of the Ag rich liquor. In this case the denitration residue is separated from the purified AgN03 by aqueous filtration.

270 kg of silver bullion is purified as described in Example 1. The obtained Ag rich granules are then leached under conditions as described in Example 2. The Ag rich liquor, at a concentration of 1090 g/1 Ag, is first evaporated and then further heated to a melt at 350 °C for 1 h. Partial denitration of Pb and substantially complete denitration of Cu and PGM occurs at this temperature and the oxides of these metals form an insoluble denitration residue. Thereafter the mixture of molten AgN03 and precipitated oxides is transferred at a controlled rate of 30 kg per minute to an agitated vessel containing 160 1 of water. During the transfer of the mixture, cooling water is circulated through the vessel jacket limiting the temperature to 80 °C. After settling of the oxides, the clear fraction of the solution is drawn off from the vessel and filtrated through a cartridge filter

with an absolute rating of 5 um. The settled slurry is filtrated separately on a pressure leaf filter with a woven multi-filament filter medium. Both filtrates are combined, forming the purified AgN03 solution.

Table 4 shows the compositions. It is clear that the purified AgN03 solution is substantially free from PGM, Pb and Cu. These impurities are concentrated in the denitration residue.

Table 4: Removal of PGM, Pb and Cu after denitration by filtration of AgN03 in aqueous solution Ag Pt Pd Pb Cu Ag rich granules matrix 570 ppm 5100 ppm 15 ppm 2370 ppm Ag rich liquor 1090 g/l 0.6 g/l 5.5 g/l 0.02 g/l 2.6 g/l Purified AgNO3 1000 g/1 <0.4 mg/1 0.2 mg/1 4.4 mg/1 3 mg/1 solution Example 5 Table 5 illustrates the typical level of purity obtained by the process according to the invention compared to the level obtained by a state of the art electrorefining process.

Table 5: Comparison of the purity of elemental Ag (all concentrations in ppm) Process Au Pt Pd Pb Cu Electrorefining <30 <3 <30 <10 <30 According to the <2 <2 <3 <10 <10 invention