Title:
PROCESS TO PRODUCE AN ACYLATED VINYLAMINE-CONTAINING POLYMER AND ITS APPLICATION AS A PAPERMAKING ADDITIVE
Document Type and Number:
WIPO Patent Application WO/2012/142425
Kind Code:
A1
Abstract:
A process for producing an acylated vinylamine-containing polymer is disclosed. The acylated vinylamine-containing polymer is produced by reacting a vinylamine-containing polymer with at one acylating agent.

Inventors:
GU QU-MING (US)
MCKAY JONATHAN M (US)
Application Number:
PCT/US2012/033544
Publication Date:
October 18, 2012
Filing Date:
April 13, 2012
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
HERCULES INC (US)
GU QU-MING (US)
MCKAY JONATHAN M (US)
International Classes:
C08F8/10; D21H17/54; C08F26/02
Foreign References:
US20090043051A12009-02-12
US6797785B12004-09-28
US2721140A1955-10-18
US4421602A1983-12-20
US6159340A2000-12-12
US6616807B12003-09-09
US6797785B12004-09-28
US5961782A1999-10-05
US4275002A1981-06-23
US4774285A1988-09-27
US5630907A1997-05-20
EP0251182A11988-01-07
US20090314446A12009-12-24
US5292441A1994-03-08
US5994449A1999-11-30
US7902312B22011-03-08
US20090043051A12009-02-12
US20100193148A12010-08-05
US20090031444A12009-01-29
Other References:
D. D. REYNOLDS ET AL, JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, vol. 69, no. 4, 19 April 1947 (1947-04-19), pages 911 - 915, XP055029673, ISSN: 0002-7863, DOI: 10.1021/ja01196a052
SHIER W T ET AL: "Polycations as prostaglandin sythesis inducers. II. structure-activity relationships", PROSTAGLANDINS, BUTTERWORTH, STONEHAM, MA, US, vol. 31, no. 6, 1 June 1986 (1986-06-01), pages 1145 - 1157, XP023447593, ISSN: 0090-6980, [retrieved on 19860601], DOI: 10.1016/0090-6980(86)90216-9
Attorney, Agent or Firm:
ROSSI, Joanne, Mary Fobare (Wilmington, DE, US)
Download PDF:
Claims:
A process for producing acylated vinylamine-containing polymer comprising the steps of a. obtaining an aqueous solution comprising at least one vinylamine-containing polymer, and

b. reacting the vinylamine-containing polymer with at least one acylating agent, wherein the acylating agent is selected from the group consisting of acyl anhydride, acyl halide and mixtures thereof.

The process of claim 1 wherein at least one vinylamine-containing polymer is selected from the groups consisting of partially or completely hydrolyzed poly(N-vinylformamide), copolymers of N-vinylformamide and vinylamine, copolymers of vinylamine and amidine, copolymers of N- vinylacetamide and vinylamine, terpoiymers of N-vinylformamide, vinylamine and amidine, teipolymers of N-vinylformamide, vinylamine and vinylamine methyl chloride quaternary ammonium salts, terpolymers of N-vinylformamide, vinylamine and vinyl alcohol, terpolymers of N-vinylformamide, vinylamine and vinyl acetate, terpolymers of N-vinylformamide, vinylamine and acrylamide, teipolymers of N-vinylformamide, vinylamine and aciylate, terpolymers of N- vinylformaniide, vinylamine, and diallyldimethyl ammonium chloride, terpolymers of N- vinylformamide, vinylamine, and vinyl trimethoxysilane, modified vinylamine-containing polymers, or mixtures thereof.

The process of claim 1 wherein the vinylamine-containing polymer comprises partially or completely hydrolyzed poly(N-vinylforrnamide).

The process of any of claim 1 - 3 wherein the acylated vinylamine-containing polymer has a molecular weight in the range of from about 5,000 to about 2,000,000 Daltons.

A process to produce an acylated poly(vinylamine) comprising the steps of:

a. conducting free radical polymerization of N-vinylformamide in aqueous solution, b. conducting alkaline hydrolysis to form a poly (vinylamine), and

c. reacting the polyvinylamine with at least one acylating agent,

wherein the acylating agent is selected from the group consisting of acyl anhydride, acyl halide and mixtures thereof.

The process of claim 5 wherein the polyvinylamine is selected from the group consisting of partially or completely hydrolyzed poly(N-vinylformamide); copolymers of N-vinylformamide and vinylamine, copolymers of vinylamine and amidine; terpolymers of N-vinylformamide, vinylamine and amidine; and mixtures thereof.

The process of any of claims 1 - 6 wherein the acylating agent comprises acyl anhydride.

The process of any of claims 1 - 7 wherein the acylating agent comprises acyl halide.

The process of any of claims 1 - 6 wherein the acylating agent is selected from the group consisting of acetic anhydride, propionic anhydride, butyric anhydride, heptanoic anhydride, anhydride, benzoic anhydride, phenylacetic anhydride, crotonic anhydride, chloroacetic anhydride, dichloroacetic anhydride and trifloroacetic anhydride, heptanoyl anhydride, an acyl halide and mixtures thereof.

10. The process of any of claims 1 - 6 wherein the acylating agent comprises acetic anhydride.

11. The process of any of claims 1 - 6 wherein the acylating agent comprises propionic anliydride.

12. The process of any of claims 1 - 6 and 9 wherein the acylating agent is selected from the group consisting of an acyl chloride, acyl bromide, acetyl chloride, propionyl chloride, butyiyl chloride, benzoyl chloride, phenylacetyl chloride, crotonyl chloride, chloroacetyl chloride and mixtures thereof.

13. The process of any of claims 1 - 6 wherein the acylating agent comprises acetyl chloride

14. The process of any of claims 1 - 6 wherein the acylating agent comprises propionyl chloride.

15. The process of claim any of claims 1 - 14 wherein the polyvinylamine and the acylating agent are reacted for a period of between 0.1 and 4 hours.

16. The process of any of claims 1 - 15 wherein the polyvinylamine and the acylating agent are reacted at a pH of between 7 and 11.

17. The process of any of claims 1 - 16 wherein the polyvinylamine and the acylating agent are

reacted at a temperature of between 24-50 °C.

Description:
PROCESS TO PRODUCE AN ACYLATED VINYLAMINE-CONTAINING POLYMER AND ITS APPLICATION AS A PAPERMAKING ADDITIVE

FIELD OF THE INVENTION

[0001] This invention relates to the process of preparing acylated vinylamine-containing polymers through acylation of primary and secondary amines of the vinylamine-containing polymers using an acylating agent such as an acyl anhydride or an acyl chloride. In particular, the present invention relates to the process of preparing acylated poly( inylamine) derivatives using acetic anhydride or propionic anhydride. Furthermore, the invention relates to uses of the acylated poly(vinylamine) derivatives as diy strength additives, wet strength additives, retention aids, drainage aids, and pitch and stickies control agents in papermaking applications.

BACKGROUND OF THE INVENTION

[0002] Poly(vinylamine) has been used in many industrial and pharmaceutical applications. In the papermaking industry, poly(vinylamine) products have been used as diy and wet strength additives to improve paper and paperboard strength and as retention/drainage aids to improve paper productivity. U.S. Patent No. 2,721,140 originally disclosed the use of poly(vinylamine) molecules as papermaking additives to improve paper wet strength. U.S. Patent No. 4,421,602 disclosed the partially hydrolyzed polymer of poly(N-vinylformamide) for improving flocculation, fines retention and pulp drainage in papermaking. U.S. Patent No. 6,159,340 described the use of the partially hydrolyzed poly(vinylamine) products as diy and wet strength additives for paperboard. U.S. Patent Nos. 6,616,807 and 6,797,785 described a variety of poly(vinylamine) derivatives as drainage aids, flocculants, and retention aids for papermaking. U.S. Patent No. 5,961,782 disclosed the use of poly(vinylamine) to make crosslinkable creping adhesives.

[0003] Poly(vinylamine) is a linear cationic polymer with minimal branching and it contains one amine functional group for eveiy two carbon units. A partially hydrolyzed poly(vinylamine) may contain primary amine, amide and amidine functionalities. Poly(vinylamine) is typically made by solution, free-radical polymerization of N-vinylformamide monomer, followed by base- or acid- catalyzed hydrolysis. U.S. Patent No. 4,275,002 disclosed a process of preparing poly(vinylamine) using N-vinylacetamide monomer through free-radical olymerization followed by hydrolysis using a mineral acid. U.S. Patent No. 4,774,285 described the preparation of copolymer of N-vinylformamide and vinyl alcohol. U.S. Patent No. 5,630,907 disclosed the copolymer of vinylamine and acrylic acid. U.S. Patent No. 6,797,785 disclosed the preparation of the copolymers of vinylamine with diallyldimethylammonium chloride and vinylamine with acrylamide via reverse emulsion polymerization, and the uses as flocculants and coagulants for papermaking. EP 0251 182 described the use of copolymers of vinylamine and aciylonitrile for papermaking as drainage aids, retention aids, and wet end additives to increase paper strength.

[0004] U.S. Patent Application No. 20090314446 described a method of preparing low amidine content poly (vinylamine) and the usage of such polymer to increase papermaking retention and drainage rate and enhance paper dry strength, and other applications.

[0005] The amine functionalities, either primary amine or amidine, of oly (vinylamine) can react with a variety of compounds having reactive functional groups. Post-polymerization chemical modification of poly(viny!amine) with a compound having functional groups is an alternative approach to produce poly(vinylamine) derivatives with altered or improved chemical, physical and application properties. U.S. Patent No. 5,292,441 described the use of quaternized poly(vinylamine)s as flocculants for wastewater clarification, where the quaternized poly(vinylamine) was obtained via the reaction of oly (vinylamine) with an alkylating agent, such as methyl chloride, dimethyl sulfate, or benzyl chloride. U.S. Patent No. 5,994,449 described a resin composition as a reaction product of epihalohydrin with the mixture of a poly(vinylamine-co-vinyl alcohol) and poly(aminoamide), and the use of the resin as creping adhesives.

[0006] More recently, U.S Patent No. 7,902,312 disclosed various Michael addition adducts of poly(vinylamine), and the uses of these modified poly(vinylamine) as dry strength additives and/or retention/drainage aids for papermaking. U.S. Patent Application Nos. 20090043051 and

20100193148 described numerous modified poly(vinylamine) products prepared by alkylation, acylation and condensation reactions of the poly(vinylamine) with a variety of amine-reactive compounds. In these two patent applications, the amine groups of vinylamine-containing polymers are substituted with cationic, anionic, hydrophobic and hydrophilic functional groups, or the combination of those functional groups. The uses of those modified poly(vinylamine) products are also described for papermaking as dry strength additives, retention and drainage aids, as well as pitch and stickies control agents in the applications.

[0007] As mentioned in the prior art, a poly(vinylamine) derivative can also be prepared using N- vinylacetamide monomer through free-radical solution polymerization followed by hydrolysis of the acetamide functional group to liberate a free amine group on the polymer backbone and release acetic acid. The disadvantage of the prior art is that it requires a monomer that is expensive and

commercially unavailable for industrial production, Additionally, poly(N-vinyIacetamide) is more stable than poly(N-vinylformamide) in water and thereby more resistant to hydrolysis.

[0008] The present invention is directed to a new process of producing acylated

poly(vinylamine), particularly acetylated poly(vinylamine), using a readily available acylating agent, e.g., acyl anhydrides, or acyl chlorides, preferably acetic anhydride, propionic anhydride, acetyl chloride and propionyl chloride. Acyiation of a oly(vinylamine) by acetic anhydride or propionic anhydride or acetyl chloride can be completed with high reaction efficiency and without by-products except acetic acid, propionic acid or chloride, respectively.

BRIEF DESCRIPTION OF THE INVENTION

[0009] The present invention provides a process for producing acylated vinylamine-containing polymers which comprises a step of reacting an acylating reagent with the vinylamine-containing polymer. Particularly, the process of the present invention provides a process of making an acylated poly(vinylamine) by reacting an acyl anhydride or acyl chloride with a poly(vinyiamine)

homopolymer.

[0010] Acetic anhydride or propionic anhydride can be reacted with poly(vinyiamine) at a desired ratio of the acyl anhydride to the amine content of the pofy(vmylamme) to produce an acylated poly(vinyJamine) polymer. The product has different chemical, physical and application pro erties as compared to an unmodi ied poly(vinylamine). In the case of poly(vinylamine) homopolymer, the primary amines of poly(vinylamine) are converted to amide bonds through acyiation reaction. When acetic anhydride is used, the acetamide functional group is formed on the backbone of the poly(vinyiamine). Unlike the formamide functional groups in a partially hydrolyzed poly(N-vinylforrnarnide) that predominantly exist as cyclized amidine, the acetamide groups in the polymer react much slower with the adjacent primary amine to form the corresponding amidine functionality.

[0011] In the process of the present invention, the vinylamine-containing polymer is preferably dissolved in water in an amount in the range of 2 to 50 weight %, preferably in an amount in the range of 5 to 40 weight %, and most preferably in an amount in the range of 8 to 20 weight % based on the total weight of the olymer solution.

[0012] The molar ratio of the acylating agent to the amine content of the vinylamine-containing polymer is 1 to 200 mole %, preferably from 5 to about 100 mole %, and most preferably from about 15 to 50 mole %.

[0013] The process is preferably carried out at a reaction temperature from about 24 °C to about 80 °C, more preferably from about 30 °C to about 50 °C, and most preferably from about 35 °C to about 40 °C, The process is carried out in a pH range of from about pH 5 to about 12.5; preferably from about pH 6 to about 12; more preferably from about 7 to about 1 1, and most preferably from about 8 to about 10. [0014] The process is preferably carried out for a period of from about 0.1 to about 4 hours, more preferably from about 0.5 to about 3 hours, and most preferably from about 1 to about 2 hours.

[0015] The molecular weight of the vinylamine-containing polymers used in the present invention is in the range of from 2,000 to 2,000,000 Daltons, preferably from 4,000 to 1,000,000 Daltons, more preferably from 10,000 to 1,000,000 Daltons, and most preferably in the range of from 50,000 to 500,000 Daltons. Accordingly, the acylated vinylamine-containing polymers of the present invention have a molecular weight range of from 3,000 to 2,000,000 Daltons, preferably from 5,000 to 1,000,000 Daltons, more preferably from 12,000 to 1,000,000 Daltons, and most preferably in the range of from 50,000 to 500,000 Daltons.

[0016] The acylated vinylamine-containing polymers of the present invention can be used in papermaking as dry strength additives to improve paper and paperboard dry strength, to accelerate drainage of the pulp fiber and to increase the retention of fines and fillers by the pulp fibers in the papermaking process.

[0017] The acylated vinylamine-containing polymers of the present invention, when added to the wet end of a paper machine on an equal active polymer basis, provided improved dry strength properties to paperboard products relative to the paperboard products made with unmodified vinylamine-containing polymers. More specifically, acetylated poly(vinylamine) products of the present invention were more effective at the treatment level from 0.01 weight % to about 0.5 weight % based on the weight of the dry pulp relative to the unmodified poly(vinylamine). The products also provided good drainage and retention properties to the pulp fiber.

DESCRIPTION OF THE INVENTION

[0018] The present invention is directed to the process for producing acylated vinylamine- containing polymers by reacting at least one acylating reagent with vinylamine-containing polymers wherein the acylating agent is selected from the group consisting of acyl anhydride, acyl halide and mixtures thereof.

[0019] The invention provides for a process for producing acylated vinylamine-containing polymer having the steps of a)obtaining an aqueous solution comprising at least one vinylamine- containing polymer, and b) reacting the vinylamine-containing polymer with at least one acylating agent. The preferred acylating agents include acyl anhydride, acyl halide and mixtures thereof.

[0020] The process of the present invention is a process that provides advantages over the existing processes for the preparation of acylated vinylamine-containing polymers, This process of the present invention utilizes inexpensive and commercially-available acylating agents to modify a widely available vinylamine-containing polymer to produce acylated vinylamine-containing polymers. This differs from the prior art, which uses an expensive and commercially unavailable monomer that contains the same acyl group to make the polymer via polymerization. The reason that

poly(vinylamine) is widely available is because the monomer, N-vinylformamide, is relatively inexpensive and commercially available and that the hydrolysis of the formamide group is much faster than other amide groups that could be used in process. In addition, the process of the present invention produces the acylated vinylamine-containing polymers with a desired level of acyl substitution by applying an appropriate amount of the acylating agent, while in the prior art, it is more difficult to control the ratio via hydrolysis of the acylated vinylamine-containing polymers under the harsh treatment conditions.

[0021] The process of the present invention provides a simplified process of preparing acylated vinylamine-containing polymers with high purity. The process has no side reactions and generates no by-product except the related carboxylic acid when an acyl anhydride is used,

[0022] The process of the present invention produces an acylated vinylamine-containing polymer comprising the general formulae (I).

wherein R is preferably an alkyl or aryl group, more preferably -CH 3 , -CH 2 CH 3 or -(¾€¾(¾, and most preferably -CH 3 .

[0023] Specifically, the process of the present invention provides an acylated vinylamine- containing polymer by reacting at least one acylating agent with primary and/or secondary amines of the vinylamine-containing polymer to form a stable amide functional group on the polymer backbone.

[0024] In one embodiment of the invention provides a process to produce an acylated poly(vinylamine) comprising the steps of conducting free radical polymerization of N- vinylformamide in an aqueous solution, subsequently conducting alkaline hydrolysis to form a polyfvinylamine), and reacting the polyvinylamine with an acylating agent .

[0025] The acylating agents used in the present invention include acyl anhydride and acyl halides. For purposes of this invention acyl anhydrides do not include cyclic anhydrides. The acylating agent used in the present invention include, but are not limited to, anhydrides such as acetic anhydride, propionic anhydride, butyric anhydride, heptanoic anhydride, anhydride, benzoic anhydride, phenylacetic anhydride, crotonic anhydride, chloroacetic anhydride, dichloroacetic anhydride and trifloroacetic anhydride; and carboxylic acid chlorides or bromides such as, acetyl chloride, propionyl chloride, butyrl chloride, heptanoyl anhydride, benzoyl chloride, phenylacetyl chloride, crotonyl chloride, chloroacetyl chloride, or mixtures thereof.

[0026] More preferably, the acylating agents used in the present invention include, but are not limited to, acetic anhydride, propionic anhydride, acetyl chloride, propionyl chloride, chloroacetyl anhydride, or mixtures thereof.

[0027] The vinylamine containing polymer used in the present invention include, but are not limited to, partially or completely hydrolyzed poly(N-vinyiformamide); copolymers of N- vinylformamide and vinylamine; copolymers of vinylamine and amidine; copolymers of N- vinylacetamide and vinylamine; terpolymers of N-vinylformamide, vinylamine and amidine;

terpolymers of N-vinylformamide, vinylamine and vinylamine methyl chloride quaternary ammonium salts; terpolymers of N-vinyl ormamide, vinylamine and vinyl alcohol; terpolymers of N- vinylformamide, vinylamine and vinyl acetate; terpolymers of N-vinylformamide, vinylamine and acrylamide; terpolymers of N-vinylformamide, vinylamine and acrylate; terpolymers of N- vinylformamide, vinylamine, and diallyldimethyl ammonium chloride; terpolymers of N- vinylformamide, vinylamine, and vinyl trimethoxysilane; or mixtures thereof.

[0028] The vinylamine containing polymers used in the present invention also include alkylated vinylamine-containing polymers produced by reacting a vinylamine-containing polymer with alkylating agents. The alkylating agents containing an amine- eactive functional group include, bu are not limited to, methyl chloride, ethyl chloride, propyl chloride, butyl chloride, benzyl chloride, phenylethyl chloride, allyl chloride, 2-(diethylamino)ethyl chloride, 2-(dimethyiamino)ethyl chloride, 3-chloro-2-hydi xypropyltrimethylammonium chloride, 3-chloro-2-hydroxypropyl-lauryl- dimethyiammoniuni chloride, 3-chloro-2-hydroxypropyl-cocoalkyl-dimethylammonium chloride, 3- chloro-2-hydroxypropyl-stearyl-dimethylammonium chloride, (4-chloroobutyl)trimethylammonium chloride, (6-chloiOhexyl)trimethylarnmonium chloride, (8-chlorooctyl)trimethyJammonium chloride, (glycidylpropyl)trimethylammonium chloride, butyl glycidyl ether, 2-erhylhexyl glycidyl ether, hexadecyl glycidyl ether, C12/C14 glycidyl ethers, chloroacetamide, salts of chloroacetic acid or bromoacetic acid, or mixtures thereof.

[0029] The vinylamine containing polymers used in the present invention also include aldehyde- reacted vinylamine-containing polymers produced by reacting a vinylamine-containing polymer with aldehyde-containing compounds. The aldehyde-containing compounds include, but are not limited to, acetaldehyde, propionaldehyde, butylaldehyde, glyoxai, monosaccharide or oligosaccharide that has an aldehyde reducing end (e.g., glucose, maltose, lactose, maltodextrin, corn syrup, enzymatically hydrolyzed starch or guars, chemically hydrolyzed starch or guars, or mixtures thereof).

[0030] The vinylamine containing polymers used in the present invention also include amphoteric vinylamine-containing polymers produced by reacting a vinylamine-containing polymer with a cyclic anhydride through a ring opening reaction of the cyclic anhydride. The cyclic anhydrides include, but are not limited to, succinic anhydride, maleic anhydride, glutaric anhydride, 3- methylglutaric anhydride, 2,2-dimethylsuccinic anhydride, cyclic alkyl carboxylic anhydrides, cyclic alkenyl carboxylic anhydrides, alkenyl succinic anhydride (ASA), phthaHc anhydride or mixtures thereof.

[0031] The vinylamine containing polymers used in the present invention also include Michael adducts of vinylamine-containing polymers produced by reacting a vinylamine-containing polymer with the compounds that have an α,β-unsaturated bond conjugated to an electron withdrawing group. Such compounds include, but are not limited to, acrylamide, methacrylamide, i-butyl acrylamide, N- alkylacrylamide, N-alkyJmethacrylamide, N-[3-(propyl)trimethylammonium chloridejacrylamide, N- [3-(propyl)trimethyIammonium chloridejmethacrylarnide, methyl aery late, alkyl acrylate, methyl mefhacrylate, alkyl mefhacrylate, aryl acrylate, aryl mefhacrylates, [2-(methacryloyloxy)ethyl]- trimethylammonium chloride, N-P-tdimethylaminoipiOpylJacrylamide, N-[3- (dimethylamino)propyl]methaciylamide, N-ethylacrylamide, 2-hydroxyethyl acrylate, acrylonitrile, vinylpyridine, l-vinyl-2-pyrrolidinone, or mixtures thereof.

[0032] More preferably, the vinylamine containing polymer used in the present invention include, but are not limited to, partially or completely hydrolyzed poly(N-vinyIformamide);

copolymers of vinylamine and amidine; terpolymers of N-vinylformamide, vinylamine and amidine; terpolymers of N-vinylformamide, vinylamine and acrylate; terpolymers of N-vinylformamide, vinylamine, and diallyldimethyl ammonium chloride; terpolymers of N-vinylformamide, vinylamine and vinyl alcohol; alkylated vinylamine-containing polymers wherein the alkylating agent is allyl chloride, or alkyl glycidyl ether; monosaccharide- or oligosaccharides-reacted vinylamine-containing polymers; or Michael adducts of a vinylamine-containing polymer,

[0033] Active polymer in the solution of a vinylamine-containing polymer of the present invention represents the total weight as a percentage in the solution of all the monomers, acylating agents and other amine-reactive compounds used for making the acylated vinylamine-containing polymer on dry basis. For example, Ν-vinylformamide is the monomer precursor for

poly( vinylamine) and has molecular weight of about 71.1. As an example, a 100 g poly (vinylamine) solution containing a polymer originally made with 7.11 g of N-vinylformamide has 7.1 1 % active polymer. As an example, a 100 g acetylated poly(vinylamine) solution containing a polymer made from 10 g of N-vinylformamide and 4 g of acetic anhydride then will have 14 % active polymer.

[0034] The amine content of a vinyiamine-containing polymer is the amount of vinylamine in the polymer in a certain amount of the product calculated on a molar basis. It can be calculated by multiplying the weight percentage polymer active in solution times the weight percent of N- vinylformamide in the active polymer (based on starting material) times the weight of the product, divided by the molecular weight of N-vinylformamide (MW= 71.08). for a homopolymer the weight percent of n-vinylformamide is 100%. For example, using 100 grams of a 15% active polymer solution of a homopolymer the calculation would be (0.15 actives) (100 gm)/71.08. For example, using 100 grams of a 15% active polymer solution of a 50:50 copolymer the calculation would be (0.15 actives)(0.5 portion of vinyl formamide in polymer)(100 gm)/71.08. The active polymer of a vinyiamine-containing polymer product is defined as the total weight in percentage in the product of all the monomers, modifying agents and other amine-reactive compounds used for making the vinyiamine-containing polymer on dry basis, Commercially vinyiamine-containing polymers commonly use N-vinylformamide as a starting monomer. If a different starting monomer is used to produce the vinyiamine-containing polymer then a similar calculation can be done using the molecular weight of the starting monomer in place of the molecular weight of the N-vinylformamide (71.08).

[0035] In the present invention, the molar ratio of the acylating agent to the amine content of the vinyiamine-containing polymer may be approximately equal. However, the reaction may be carried out in stoichiometric imbalance. Depending on the desired level of acylation, the molar ratio of an acylating agent to the amine content of the vinyiamine-containing polymer is 1 to 200 mole %, preferably from 5 to about 100 mole %, most preferably from about 15 to 50 mole %. Efficiency of the acylating reaction varies with types of the acylating agents and the reaction conditions. When the reaction efficiency is less than 50%, 200 mole % or more of the acylating agent vs. the amine content of the vinyi mine-containing polymer may be needed. The reaction efficiency of acetic anhydride or propionic anhydride with a poly(vinylamine) is around 70-98% while the reaction efficiency of acetyl chloride with the same poly(vinylamine) is in the range of 40-80%.

[0036] The molecular weight of a vinyiamine-containing polymer has little effect on acylation efficiency. Not wishing to be bound by theory, the molecular weight of the acylated vinyiamine- containing polymers of the present invention is important for its use as a papermaking additive for strength improvement of paper products. If the molecular weight is too low, the vinyiamine- containing polymer may have poor retention on pulp fiber. If the molecular weight is too high, it may tend to flocculate the pulp, which may reduce effectiveness of the polymer as a strength additive. The molecular weight (M w ) of the vinyiamine-containing polymers used in the present invention is in the range of from 2,000 to 2,000,000 Daltons, preferably from 4,000 to 1 ,000,000 Daltons, more preferably from 10,000 to 1,000,000 Daltons, most preferably in the range of from 50,000 to 500,000 Daltons.

[0037] Accordingly, the acylated vinylamine-containing polymers of the present invention have a molecular weight ranged from 3,000 to 2,000,000 Daltons, preferably from 5,000 to 1 ,000,000 Daltons, more preferably from 12,000 to 1,000,000 Daltons, most preferably in the range of from 50,000 to 500,000 Daltons.

[0038] In the process of the present invention, the weight percentage of the vinylamine- containing polymer in water and the molecular weight of the polymer govern the solution viscosity property. The higher molecular weight of the vinylamine-containing polymer, the higher the viscosity the aqueous polymer solution would be at equal weight percentage of the vinylamine-containing polymer, and thus the more dilute the polymer solution must be in order to be easily pumpable or prevent gelation. High solution viscosity may revent a homogenous reaction between the acylating agent and the vinylamine-containing polymer due to inefficient mass transfer. The vinylamine- containing polymer used in the present invention is dissolved in water in an amount in the range of from 2 to 50 weight % based on the total weight of the polymer solution, preferably in an amount in the range of from 5 to 40 weight %, and most preferably in an amount in the range of from 8 to 20 weight %. Preferably the weight percentage of a partially or completely hydrolyzed poly(N- vinylformamide) is in the range of 8-20 % in water.

[0039] Preferably, the vinylamine-containing polymer used in the present invention is dissolved in water in the absence of an organic solvent. However, the vinylamine-containing polymer used in the present process may also be dissolved in a mixture of water with one or more water-miscible organic solvents. Examples of the water miscible solvents include, but not limited to, ethanol, ethylene glycol, glycerol ethanol, isopropranol, formic acid, acetic acid and their sodium or potassium salts.

[0040] The process of the present invention is preferably carried out at a reaction temperature from about 10 °C to about 80 °C, preferably from about 20 °C to about 50 °C more preferably from about 24 °C to about 50 °C, and most preferably from about 35 °C to about 40 °C. When the temperature of the acylation reaction is too high, the acylating agent, e.g., acetic anhydride or acetyl chloride, may undergo hydrolysis in water before it reacts with the vinylamine-containing polymer.

[0041] One vinylamine-containing polymer is poly(vinylamine) that has typically been made by free radical polymerization of N-vinylformamide monomer followed by a base-hydrolysis by which the primary amine is deprotected and formic acid is liberated. A partially hydrolyzed poly(N- vinylformamide) contains N-vinylformamide, amidine and vinylamine units. These completely and partially hydrolyzed poly(N-vinylformamide) polymers may be directly acylated by the process of the present invention after the polymer solution is adjusted to a proper pH using an acid. The acids used for pH adjustment include, but are not limited to, hydrochloric acid, sulfuric acid, acetic acid and formic acid, or mixtures thereof. However, it should be noted that sulfuric acid may cause precipitation of the acylated vinylamine-containing polymers depending on the degree of the acyiation, and that the most preferable acids are hydrochloric acid, acetic acid and formic acid.

[0042] The process of the present invention is carried out at pH in the range of from pH 5 to about 12.5; preferably carried out in the range of from about pH 6 to about 12; more preferably in the range of from about 7 to about 1 1, and most preferably in the range of from about 8 to about 10. At pH 1 1 or above, an acylating agent, such as acetic anhydride, may be hydrolyzed in water faster than its reaction with the vinylamine-containing polymer. A partially or completely hydrolyzed poly(N- vinylformamide) may not be fully protonated at acidic pH (pH 4,0 or less), due to cationic charge repulsion; therefore, it may still have free primary available for the acyiation reaction under acidic condition at pH less than 4. The reaction pH of the process may be controlled by gradually adding an alkali, such as sodium hydroxide solution, to neutralize the carboxylic acid or halide ion liberated during the acyiation reaction.

[0043] The process of the present invention is preferably carried out from about 0.1 to about 4 hours, more preferably from about 0.5 to about 3 hours, and most preferably from about 1 to about 2 hours. The reaction is usually fast for acylating a vinylamine-containing polymer by an acyl anhydride in water, but it is much faster when an acyl halide is the acylating agent.

[0044] In addition to primary amine moieties, partially hydrolyzed poly(N-vinylformamide) and vinylamine copolymers of the present invention typically comprise randomly distributed amidine functional groups. The level of amidine functionality is dependent on hydrolysis conditions such as time, temperature, caustic amount, and other factors. As a result, acyiation of a partially hydrolyzed poly(N-vinylformamide) by the present invention with an acylating agent, such as acetic anhydride, may also occur on the nitrogen atoms of the amidine functional groups, resulting in randomly distributed monomer units of acylated amidine.

[0045] The process of the present invention can provide acetyiated poly(vinylamine) derivatives by reacting acetic anhydride with poly(vinylamine) homopolymer at a certain ratio of acetic anhydride to the amine content of poly (vinylamine). The acetyiated poly(vinylamine) derivatives have different chemical, physical and application properties vs. the unmodified poly (vinylamine). The acetyiated oly(vinylamine) derivatives of the present invention have a lower Brookfield viscosity than that of the unmodified poly(vinylamine) when compared on an equal active basis. The acetyiated poly(vinylamine) derivatives, when used as papermaking additives on equal polymer active weight basis, provided improved dry strength property relative to poly (vinylamine) to the paper and paperboard products made using a paper machine. The acetylated poly(vinylamine) products were effective at the treatment level from 0.01 weight % to about 0.5 weight % based on the dry pulp. The products also gave good drainage and retention properties to the pulp fiber.

[0046] According to U.S. Patent Application No. 2009031444, amidine functionality can adversely affect pa ermaking retention and drainage and dry strength enhancing performances and low amidine content poly(vinylamine) is preferred. The Ή-NMR and 13 C-NMR spectral analyses of the acetylated poly(vinylamine) indicated that acetamide functionality exists as the main functional group in the polymer with a very small amount of the acetamide cyclized to form amidine functionality during the process and storage. Apparently, the acetamide group of the acetylated poly(vinylamine) reacts much slower than the formamide group to form the corres onded amidine. The formamide group on a partially hydrolyzed poly(N-vinylformamide), or a formylated

polyvinylamine), reacts quickly with the adjacent primary amine to form amidine functionality. At an equal level of acylation, an acetylated poIy(vinylamine) would contain less amidine functionality and more primary amine group than that of a partially hydrolyzed poly(N-vinylformamide). Without wishing to be bound by theoiy, it is believed that decreased amidine content when acetyl groups are present, relative to higher amidine content when formamide are present, results in the observed improved performance.

[0047] The acylated vinylamine-containing polymers of the present invention can be used as dry strength additives for paper and paperboard products to accelerate drainage of the pulp fiber and to increase the retention of fines and fillers by the pulp fibers during the papermaking process.

[0048] The acylated polymers of the present invention can be also used in a combination with other compositions in order to improve the properties of the polymers. The compositions that may be used in combination with the acylated vinylamine-containing polymers of the present invention can be a cationic, or an anionic, or an amphoteric, or a nomonic synthetic, or a natural polymer. For example, the acylated vinylamine-containing polymers of the present invention can be used together with a cationic starch or an amphoteric starch to improve the strength properties of paper products. The acylated vinylamine-containing polymers of the present invention can also be used in combination with an anionic polymer, such as a polyacrylic acid, a copolymer of acrylamide and acrylic acid, or a carboxyl methyl cellulose; a cationic polymer such as a crosslinked polyamidoamine, a

polydiallyldimethylammonium chloride, or a polya ine; to form a polyelectrolyte complex to improve the strength properties of paper products. The acylated vinylamine-containing polymers of the present invention can also be used in combination with polymeric aldehyde-functional compounds, such as glyoxalated polyacrylamides, aldehyde celluloses and aldehyde functional polysaccharides. Individual compositions or any combination of different compositions may be applied together with the acylated vinylamine-containing polymers of the present invention, or may be applied sequentially before or after the application of the polymers of the present invention.

Individual compositions may be blended together with the acylated vinylamine-containing polymers of the present invention to form a blended composition prior to use.

[0049] The embodiments of the invention are defined in the following Examples. It should be understood that these Examples are given by way of illustration only. Thus various modifications of the present invention in addition to those shown and described herein will be apparent to those skilled in the art from the foregoing description. Although the invention has been described with reference to particular means, materials and embodiments, it is to be understood that the invention is not limited to the particulars disclosed, and extends to all equivalents within the scope of the appended claims.

EXAMPLES

[0050] Size exclusion chromatography (SEC) was used to measure molecular weight. The analysis was accomplished using gel permeation columns (CATSEC 4000 + 1000 + 300 + 100) and Waters 515 series chromatographic equipment with a mixture of 1 % NaNO 3 /0.1 % trifluoroacetic acid in 50:50 H 2 0:C¾CN as the mobile phase. The flow rate was 1.0 mL/min. The detector was a Hewlett Packard 1047 A differential refractometer. Column temperature was set at 40 °C and the detector temperature was at 35 °C. The number average (Mn) and weight average molecular weight (Mw) of the polymers were calculated relative to the commercially available narrow molecular weight standard poly(2 -vinyl pyridine).

[0051] The charge densities (Miitek) of the ionized polymers in the present invention were measured at pH 7.0 using a colloid titration method. Charge density (meq/g) is the amount of cationic charge per unit weight, in milliequivalents per gram of product solids. The polymer sample is titrated with potassium polyvinyl sulfate (PVSK) to a 0 mV potential with an autotitrator (Brinkmann Titrino) at a fixed titration rate (0.1 mL/dose, 5 sec) and a Miitek particle charge detector (Model PCD 03, BTG, Muetek Analytic Inc., 2141 Kingston Ct., Marietta, GA, USA) is used for end point detection.

[0052] Brookfie!d viscosity (BV) was measured using a DV-II Viscometer (Brookfield Viscosity Lab, Middleboro, MA). A selected spindle (number 2) was attached to the instrument, which was set for a speed of 30 RPM. The reaction solution is prepared at a specific solid content. The Brookfield viscosity spindle was carefully inserted into the solution so as not to trap any air bubbles and then rotated at the above-mentioned speed for 3 minutes at 24 °C. The units are in centtpoises (cps).

[0053] In all the following examples, a high pH solution of poly(vitiylamine) homopolymer was used unless otherwise stated. This polyfvinylamine) solution was obtained after completing the steps of free radical polymerization of N-vinylformamide and base-hydrolysis but prior to the neutralization with hydrochloric acid. This poly(vinylamine) product has 14.9 % active polymer with pH around 11.5 - 12.5.

EXAMPLE 1 - Preparation of Acetylated (24.7 mol %) Poly(vinyIamine) at a Controlled pH

[0054] A poly(viny!amine) solution (14.9 % active polymer, 322.7 g) in a 1L reaction flask was neutralized to pH 9.0 using 36.5 % HCl, Acetic anhydride (Aldrich Chemical Co., 16.9 g, 24.7 mol % based on the amine content of the poly(vmyIarnine)) was added over 10 minutes with stirring at a temperature in the range of from 30 °C to 40 °C while the pH was maintained at 9.0 using a NaOH solution. The resulting mixture was stirred at a temperature in the range of from 30 °C to 40 °C for 30 minutes and the pH was kept at 9.0 using a NaOH solution. After no further change in the reaction pH, the reactant was cooled to room temperature and the pH was adjusted to 7.5 using 36.5 % HCl to give the final clear solution product with total solids of 25.5 % and the active polymer of 14.2 % as calculated. The charge density was measured to be 6.74 meq / g at pH 7.0. The product is a transparent solution with a Brookfield viscosity of 1429 cps. SEC: M w : 316,000; M w M n : 4.25.

EXAMPLE 2 - Preparation of Acetylated (24.6 mol %) Poly(vinylamine) Without pH Control

[0055] A poly(vinylamine) solution (14.9 % active polymer, 600.0 g) in a 2-L reaction flask was neutralized to pH 10.0 using 36.5 % HCl. Acetic anhydride (Aldrich Chemical Co., 31.3 g, 24.4 mol % based on the amine content of the poly(vinylamine)) was added over 10 minutes with stirring at a temperature in the range of from 30 °C to 40 °C. For this example, the theoretical amine content of t e PVAm is 14.9% x 600/71.08= 1.258 mole; acetic anhydride is 31.3/102.09=0.307 mole; therefore the mole percentage is 0.307/1.258 = 24.4 mol %. The resulting mixture was stirred at a temperature in the range of from 30 °C to 40 °C for 30 minutes and the pH decreased to 8.0. After no further decrease in the reaction pH, the reactant was cooled down without further pH adjustment to give the final product with total solids of 27.0 % and the active polymer of 14.7 % as calculated. The charge density measured to be 6.82 meq / g at pH 7.0. The product is a transparent solution and Brookfield viscosity was 1692 cps. SEC: M w : 322,000; M /M n : 4.39.

EXAMPLES 3 through 15

[0056] Examples 3 to Example 15 were prepared as described in Example 2 except that different mol % of acetic anhydride were used in acetylation and that the reaction started at different pH, All the solution products were transparent in appearance. Table I. Preparation of Acetyiated PoIy(vinylaniine) with Different mol % of Acetic

Anhydride

EXAMPLES 16 through 18

[0057] Examples 16 to example 17 were prepared as described in Example 1 except the acetylation was conducted at different temperatures. All the solution products were transparent in appearance.

Table IL Pre aration of Acet iated Pol vin lamine at Different Tem erature

[0058] The relative acylation efficiency can be estimated by determining the amount of acetic acid produced during the reactions for a series of reactions that are conducted with the same mol % of acetic anhydride vs. polyfvinylamine). The efficiency was calculated based on the amount of NaOH that is consumed to maintain the reaction pH at 10.0. The actual reaction efficiency should be higher as the reaction pH shifted to acidic when the primary amine groups of poly(vinylamine) are acetyiated, which may result in more NaOH consumed to maintain the reaction pH,

[0059] As shown in Table II, under these acetylation conditions, the acetylation efficiency was much higher at a lower temperature (20-28 °C) at 92 % than that at a higher temperature (70-75 °C) at 61 %.

EXAMPLE 19 - Preparation of Acetyiated (26 mol %) Polyfvinylamine) Using Hercobond® 6363

Γ00601 A ιΐΓ ί Ιν νίηνΙ ί ι ί ηίηρΛ cnlutinti TTpivnlinvu-liiii :ι_ι_ ΐ - from Ashland Incorporated, 1 1.7 % active polymer, 165 g, pH 8.0) in a 1L reaction flask was adjusted to pH 10.5 using a NaOH solution. Acetic anhydride (Aldrich Chemical Co., 7.2 g, 26 mol % based on the amine content of the poly(vinylamine)) was added over 10 minutes at 30 °C with agitation. The resulting mixture was stirred at 40 °C for 30 minutes. After no further change in the pH, the solution was cooled to room temperature and the pH was adjusted to 7.5 using 36.5 % HC1 to give the final clear solution product with total solids of 23.9% and total active polymer of 12.5%. The charge density was measured to be 6.65 meq / g at pH 7.0. The product is a transparent solution with a Brookfield viscosity of 1168 cps. SEC: M w : 15,000; M w M„: 4.33. The reaction efficiency was calculated to be 89.5% using the titration method.

EXAMPLE 20 - Succinic Anhydride Acylated (3 mol %) - Acetylated (26 mol %) Poly(vinylamine)

[0061] A poly(vinylamine) solution (14.9 % active polymer, 145 g) in a 1-L reaction flask was neutralized to pH 11.0 using 36.5 % HC1. Acetic anhydride (Aldrich Chemical Co., 8.1 g, 26 mol % based on the amine content of the poly(vinylamine)) was added to the solution with stirring over 10 minutes followed by addition of succinic anhydride (Aldrich Chemical Co., 1.0 g, 3 mol % based on the amine content of the poly(vinylamine)) over 2 minutes at 30 °C - 40 °C. The resulting mixture was stirred at a temperature in the range of from 24 °C to 40 °C for 30 minutes. After no further decrease in pH, the solution pH was adjusted to 8.0 using 36.5% HC1 to give the final clear solution product with total solids of 27.9 % and total active polymer of 15.1 %. The charge density was measured 6.42 meq / g at pH 7.0. The product is a transparent solution with a Brookfield viscosity of 1828 cps; SEC: M w 10,000; M v /M n : 3.07.

EXAMPLE 21 - Maltodextrin Coupled (0.6 moi %) - Acetylated (20 mol %) Poly(vinylamine)

[0062] A poly(vinylamine) solution (14.9 % active polymer, 141 g) in a 1-L reaction flask was neutralized to pH 1 1.0 using 36.5 % HCl. A maltodextrin (Maltrin M100, Grain Processing Corp., 3.0 g, 0.6 mol % based on the amine content of the poly(vinylamine)) dissolved in 30 g water was added to the solution with stirring over 10 minutes at 40 °C. The resulting mixture was stirred at 40 °C for 10 minutes, and then acetic anhydride (Aldrich Chemical Co., 6.0 g, 20 mol % based on the amine content of the poly(vinylamine)) was added over 10 minutes with stirring. The resulting mixture was stirred at a temperature in the range of from 24 °C to 40 °C for 30 minutes to give the final product at pH 8.0 with total active polymer of 14.1%. The charge density was measured 6.28 meq / g at pH 7.0. The product is a transparent solution with a Brookfield viscosity of 1548 cps. SEC: M w : 352,000; Μ„7Μ η : 3.38.

EXAMPLE 22 - Lactose coupled (1.2 mol %) - Acetylated (20 mol %) Poly(vinylamine)

[0063] A poly(vinylamine) solution (14.9 % active polymer, 180 g) in a 1-L reaction flask was T/US2012/033544 neutralized to pH 11.0 using 36.5 % HCl. Lactose (Aldrich Chemical Co., 1.5 g, 1.2 mol % based on the amine content of the poly(vinylamine)) dissolved in 10 g water was added to the solution with stirring over 10 minutes at 40 °C. The resulting mixture was stirred at 40 °C for 10 minutes, and then acetic anhydride (Aldrich Chemical Co., 7.7 g, 20 mol % based on the amine content of the poly(vinylamine)) was added over 10 minutes with stirring. The resulting mixture was stirred at a temperature in the range of from 24 °C to 40 °C for 30 minutes to give the final product at pH 8.0 with total active polymer of 10.0%. The product is a transparent solution with a Brookfield viscosity of 218 cps.

EXAMPLE 23 - Preparation of Propionylated (20 mol %) Poly(vinylamine)

[0064] A poly(vinylamine) solution (14.9 % active polymer, 130.0 g) in a 1 -L reaction flask was neutralized to pH 10.0 using 36.5 % HCl. Propionic anhydride (Aldrich Chemical Co., 7.2 g, 20 mol % based on the amine content of the poly(vinylamine)) was added over 10 minutes with stirring at a temperature in the range of from 30 °C to 40 °C. The resulting mixture was stirred at a temperature in the range of from 30 °C to 40 °C for 30 minutes. The pH was adjusted to 7.4 using 36.5% HCl to give the final product with total solids of 21.4% and total active polymer of 11.8%. The product was a little bit hazy and Brookfield viscosity was 1020 cps.

EXAMPLE 24 - Preparation of Acetylated (38 mol %) Poly(vinylamine) Using Acetyl Chloride

[0065] A poly(vinylamine) solution (14.9 % active polymer, 133.0 g) in a 1L reaction flask was neutralized to pH 9.0 using 36.5 % HCl. Acetyl chloride (Aldrich Chemical Co., 8.3 g, 38 mol % based on the amine content of the poly(vinylamine)) was added dropwise over 20 minutes with stirring at a temperature in the range of from 23 °C to 30 °C. The reaction was vigorous and immediate. The resulting mixture was stirred at a temperature in the range of from 23 °C to 35 °C for 30 minutes to give the final product at pH 6.7 with total solids of 24.0 % and total active polymer of 13.1 %. The product is a transparent solution with a Brookfield viscosity of 1120 cps.

EXAMPLE 25 - Allyl Chloride alkylated (10 mol %) - Acetylated (17 mol %) Poly(vinylamine)

[0066] To a poly(vinylamme) solution (14,9 % active polymer, 149 g) in a 1-L reaction flask at pH 12.1 was added allyl chloride (Aldrich Chemical Co., 2.5 g, 10 mol % based on the amine content of the poly(vinylamine)) over 5 minutes at 60 °C. The resulting mixture was stirred at 60 °C for 2 hours, and then cooled to 40 °C while the pH was adjusted to 11.0 using 36.5% HCl. Acetic anhydride (Aldrich Chemical Co., 5.4 g, 17 mol % based on the amine content of the poly(vinylamine)) was added over 10 minutes with stirring. The resulting mixture was stiired at a temperature in the range of from 24 °C to 40 °C for 50 minutes. The pH was adjusted to 8.0 using 36.5% HCl to give the final nroduct with total active nolvmer of 14.0 %. The solution product was hazy and Brookfield viscosity was 1252 cps. SEC: M w : 308,000; M w M n : 4.71.

EXAMPLE 26 - Chloroacetamide Alkylated (3.4 mol %) - Acetylated (22.6 mol %) Poly(vinylamine)

[0067] To a poly(vinylamine) solution (14.9 % active polymer, 150 g) in a 1-L reaction flask at pH 12.1 was added chloroacetamide (Aldrich Chemical Co., 1.0 g, 3.4 mol % based on the amine content of the poly(vinylamine)) over 5 minutes at 40 °C. The resulting mixture was stirred at 40 °C for 30 minutes, and then cooled to 30 °C while the pH was adjusted to 11.0 using 36.5% HCl. Acetic anhydride (Aldrich Chemical Co., 7.25 g, 22.6 mol % based on the amine content of the

poly(vinylamine)) was added over 10 minutes with stirring. The result ing mixture was stirred at a temperature in the range of from 24 °C to 40 °C for 40 minutes. The pH was adjusted to 7.75 using 36.5% HCl to give the final product with total active polymer of 13.4 %. The product is a transparent solution with a Brookfield viscosity of 1756 cps. SEC: M w : 318,000; M ¾ 7M n : 4.55.

EXAMPLE 27 - (3-AciyiamidopiOpyl)trimethylammonium Chloride Alkylated (20 mol %) - Acetylated (10 mol %) Poly(vinylamine)

[0068] A poly(vinylamine) solution (Hercobond® 6363 paper performance additive, available from Ashland Incorporated, 1 1.7 % active polymer, 250 g, pH 8.0) in a IL reaction flask was adjusted to pH 1 1.5 using a 50% NaOH solution (16.9 g). (3-aciylamidopropyl)-trimethylammonium chloride (APTAC, 60% solution in water, available from Ashland Incorporated, 21 ,27 g, 20 mol % based on the amine content of the poly(vinylamine)) was added to the poly(vinylamine) solution, which was subsequently heated to 70 °C. The solution was stirred with heating for 3 hours at 70 °C, and was then cooled to 50 °C. Acetic anhydride (Aldrich Chemical Co., 6.30 g, 10 mol % based on the amine content of the poly(vinylamine)) was added and the solution was stirred at 50 °C for 3 hours longer. The solution was cooled down and the pH was adjusted to 8.3 using 36.5 % HCl to give the final clear solution product with total solids of 26.9% and total active polymer of 15.5%. The charge density was measured to be 7.97 meq / g at pH 7.0. The product is a transparent solution with a Brookfield viscosity of 1 166 cps. SEC: Mw: 350,000; Mw/Mn: 3.83.

EXAMPLE 28 - (3-Aciylamtdopropyl)trimethylammonium Chloride Alkylated (10 mol %) - Acetylated (15 mol %) Poly(vinyIamine)

[0069] A poly(vinylamine) solution (Hercobond® 6363 paper performance additive, available from Ashland Incorporated, 11.7 % active polymer, 250 g, pH 8.0) in a IL reaction flask was adjusted to pH ί 1.5 using a 50% NaOH solution (16.5 g). (3-acrylamidopi pyl)-trimethylammonium chloride (APTAC, 60% solution in water, available from Ashland Incorporated, 28.35 g, 10 mol % based on the amine content of the poly(vinylamine)) was added to the oly(vinylamine) solution, which was 12 033544 subsequently heated to 70 °C. The solution was stirred with heating for 3 hours at 70 °C, and was then cooled to 50 °C. Acetic anhydride (Aldrich Chemical Co., 4.20 g, 15 mol % based on the amine content of the poly(vinylamine)) was added and the solution was stirred at 50 °C for 3 hours longer. The solution was cooled down and the pH was adjusted to 8.3 using 36.5 % HCl to give the final clear solution product with total solids of 26.9% and total active polymer of 16.1%. The charge density was measured to be 8.16 meq / g at pH 7,0. The product is a transparent solution with a Brookfield viscosity of 11 16 cps.

EXAMPLE 29 - (3-Aciylamidopropyl)trimerhylammomum Chloride Alkylated (15 mol %) - Acetylated (15 mol %) Poly(vinylamine)

[0070] A poly(vinylamine) solution (Hercobond© 6363 paper performance additive, available from Ashland Incorporated, 1 1.7 % active polymer, 250 g, pH 8.0) in a 3L reaction flask was adjusted to pH 1 1 ,5 using a 50% NaOH solution (17.05 g). (3-acrylamidopropyl)-trimethyIammonium chloride (APTAC, 60% solution in water, available from Ashland Incorporated, 21.27 g, 15 mol % based on the amine content of the polyfvinylamine)) was added to the poly(vinylamine) solution, which was subsequently heated to 70 °C. The solution was stirred with heating for 3 hours at 70 °C, and was then cooled to 50 °C. Acetic anhydride (Aldrich Chemical Co., 4.20 g, 15 mol % based on the amine content of the poly(vinylamine)) was added and the solution was stirred at 50 °C for 3 hours longer. The solution was cooled down and the pH was adjusted to 8.3 using 36.5 % HCl to give the final clear solution product with total solids of 26.2% and total active polymer of 15.0%. The charge density was measured to be 8.64 meq / g at pH 7.0. The product is a transparent solution with a Brookfield viscosity of 1022 cps.

EXAMPLE 30 - Approach B: (3-Aciylamidopropyl)trimethylammonium Chloride Alkylated (20 mol %) - Acetylated (10 mol %) Poly(vinylamine)

[0071] A poly(vinylamine) solution (Hercobond® 6363 paper performance additive, available from Ashland Incorporated, 11.7 % active polymer, 250 g, pH 8.0) in a 1L reaction flask was adjusted to pH 10.1 using a 50% NaOH solution (12.4 g). Acetic anhydride (Aldrich Chemical Co., 4.20 g, 10 mol % based on the amine content of the poly(vinylamine)) was added and the solution was stirred at 50 °C for 3 hours. The solution was treated with 50% NaOH (4.65 g), followed by (3- acrylamidopropyl)trimethylammonium chloride (APTAC, 60% solution in water, available from Ashland Incorporated, 14.18 g, 20 mol % based on the amine content of the poly(vinylamine)). The solution was the heated to 70 °C and stirred for 3 more hours. The solution was cooled to room temperature and the pH was adjusted to 9.1 using 36.5 % HCl to give the final clear solution product with total solids of 27.6% and total active polymer of 14.3%. The charge density was measured to be 8.37 meq / g at pH 7,0. The product is a transparent solution with a Brookfield viscosity of 942 cps. EXAMPLE 31 - Biguanidinylated (5 mol %) - Acetylated (25 mol %) Poly(vinylamine)

[0072] A poly(vinylamine) solution (Hercobond® 6363 paper performance additive, available from Ashland Incorporated, 1 1.7 % active polymer, 250 g, pH 8.0) in a 1L reaction flask was adjusted to pH 10.1 using a 50% NaOH solution (10.8 g). Acetic anhydride (Aldrich Chemical Co., 10.50 g, 25 mol % based on the amine content of the poly(vinylamine)) was added and the solution was stirred at 50 °C for 3 hours. The solution was treated with 50% NaOH (9.00 g), followed by dicyandiamide (Aldrich Chemical Co., 1.75 g, 5 moi % based on the amine content of the poIy(vinylamine)). The solution was the heated to 100 °C and stirred for 3 more hours. The solution was cooled to room temperature and the pH was adjusted to 7.6 using 36.5 % HC1 to give the final clear solution product with total solids of 25.8% and total active polymer of 14.0%. The charge density was measured to be 7.33 meq / g at pH 7.0. The product is a transparent solution with a Brookfield viscosity of 394 cps.

EXAMPLE 32 - Evaluation as Dry Strength Additives in Papermaking Applications

[0073] The diy strength of papers made with the poly(vinylamine) derivatives of the above examples are compared with the dry strength of paper made with a benchmark dry strength resin poly(vinylamine) (Hercobond® 6363 paper performance additive, available from Hercules

Incorporated).

[0074] Linerboard paper is made using a papermaking machine. The paper pulp is a 100 % recycled medium with 50 ppm hardness, 25 ppm alkalinity, 2.5 % GPC D15F and 2000 uS/cm conductivity. The system pH is 7.0 and the pulp freeness is 350-420 CSF with the stock temperature at 52 °C. The basis weight is 100 lbs per 3000 ft 2 . Poly(vinyl amine) derivatives prepared in the above examples are added as dry strength agents to the wet end of the papermaking machine at the level of 0.3 weight % of active polymer versus dry paper pulp. Dry tensile strength, Ring Crush and Mullen Burst are used to measure the dry strength effects.

[0075] The diy strength test results are shown below in Table ΙΠ. Performances of the poly(vinyiamine) derivatives are expressed as a percentage increase over the diy strength of paper made with Poly(vinylamine) (Hercobond® 6363 paper performance additive, available from Hercules Incorporated). Table ΠΙ. Dry Strength Performances of Acylated Poly(vinylamine) versus Poly(vinylamine)

[0076] Table III compares the representative polymers of the present invention with poly(vinylamine) (Hercobond® 6363). All the acylated poly(vinylamine) derivatives evaluated gave improved Mullen Burst relative to the unmodified poly(vinylamine) (Hercobond® 6363) at an equal active basis. All the acylated poly(vitvylamine) derivatives also provided equivalent (within 2%) or better Dry Tensile and Ring Crush compared to the unmodified Hercobond® 6363. For example, the acetylated PVAm (27%) (Example 8) improved Mullen Burst by 10.4 %, Ring Crush by 6.6 % and dty tensile by 7.2% over the benchmark Hercobond® 6363. It should be also noted that all the acylated poly(vinylamine) derivatives cost less to make compared to unmodified poly(vinylamine) on active basis and have improved cost effectiveness relative to Hercobond® 6363,