Title:
RADIO-OPAQUE 3D PRINTING INK
Document Type and Number:
WIPO Patent Application WO/2017/096378
Kind Code:
A1
Abstract:
A 3D printing ink comprising a radio-opaque additive and a polymer ink and a method for 3D printing of anatomic replicas using the 3D printing ink are described. The radio-opaque additive is bismuth neodecanoate, and the amount of bismuth neodecanoate in the printing ink may range from about 6% to about 20% by weight. The polymer ink may be transparent or opaque. X-rays of anatomic replicas created with the 3D printing ink appear very similar to x-rays of organic hard tissues, thereby enhancing procedural training for health care professionals.

Inventors:
BUCHANAN STEPHEN L (US)
Application Number:
PCT/US2016/064973
Publication Date:
June 08, 2017
Filing Date:
December 05, 2016
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
BUCHANAN STEPHEN L (US)
International Classes:
C09D11/10; B29C67/00; C09D11/38; G09B23/28
Domestic Patent References:
WO2016019078A12016-02-04
Foreign References:
EP2526901A12012-11-28
EP1837043A22007-09-26
US20110275159A12011-11-10
US201314017225A
Attorney, Agent or Firm:
ROSSLER, Paul E. (US)
Download PDF:
Claims:
WHAT IS CLAIMED

1. A 3D printing ink comprising a radio-opaque additive and a polymer ink.

2. A 3D printing ink according to claim 1, wherein the radio-opaque additive is bismuth neodecanoate.

3. A 3D printing ink according to claim 2, wherein the 3D printing ink contains bismuth neodecanoate in a range of about 6% to about 20% by weight.

4. A 3D printing ink according to claim 2, wherein the 3D printing ink contains about 12% bismuth neodecanoate by weight.

5. A 3D printing ink according to claim 1, wherein the polymer ink is transparent or opaque.

6. A method for 3D printing of an anatomic replica using a 3D printing ink comprising a radio-opaque additive and a polymer ink.

7. A method according to claim 6, wherein the radio-opaque additive is bismuth neodecanoate.

8. A method according to claim 7, wherein the 3D printing ink contains bismuth neodecanoate in a range of about 6% to about 20% by weight.

Description:
RADIO-OPAQUE 3D PRINTING INK

BACKGROUND OF THE INVENTION

This invention relates to inks for use in 3D printers and, more specifically, radio- opaque 3D printing inks.

In the new world of 3D printing seemingly everything is possible. However, like the internet of 20 years ago, the applications of this technology are being worked out day by day to address the specifics of each imagined use. This patent application describes an innovation that furthers the ability to authentically reproduce human anatomy in printed training replicas for health care professionals.

All surgical skills to date have required neophyte surgeons to practice on human patients with oversight from trained colleague preceptors. There are two significant deficits in this method of procedural training. First, the process inescapably involves learning by failures as well as successful clinical outcomes, many times with serious consequences to the patients who have been used in this teaching environment. Second is the severe limitation of a one-on-one requirement to transfer these procedural skills, making it exorbitantly expensive as well as exclusive in the numbers of professionals who are able to acquire these skills.

The advent of multi-ink 3D printers offers an elegant solution to these worldwide problems— the possibility of replicating human anatomy in ways that can authentically mimic the procedural experiences surgeons require to become competent in their fields. Such replicas are advantageous because they reduce patient mortality and morbidity usually attendant to procedural training by taking humans out of the learning process every procedural clinician must go through to achieve competence in their given field of expertise. At the same time, the replicas allow the training of a much larger number of clinicians, thereby reducing the costs and increasing the availability of medical and dental procedures.

{ As an example, dentistry, specifically endodontics, has been served through the replication of external and internal tooth anatomy— see e.g. U.S. Patent Application No. 14/017,225, Anatomic Apparatus and Training System for Remote and Interactive Hands-On Procedural Training for Dentists, hereby incorporated by reference herein— by way of 3D printing. 3D printing is uniquely capable of reproducing the nuances of root canal morphology, a process that injection molding cannot adequately accomplish as there is no way to recreate the microscopic and often tortuous anatomy inside of human and animal teeth.

However, as closely as 3D printing with ultraviolet ("UV")-cured polymers is able to reproduce hard tissue anatomy, before now these anatomic replicas have had very different properties than human hard tissue in their radio-opacity. While clinicians can gain skills by directly viewing the action of instruments and filling materials within root canal spaces, the final connection of that experience to real life clinical situations has been hampered by the nearly radio-lucent nature of the polymer inks used in their printing. There is a need for anatomic replicas that mimic organic hard tissue when subject to X-ray imaging.

SUMMARY OF THE INVENTION

A 3D printing ink comprising a radio-opaque additive and a polymer ink is described. The radio-opaque additive is bismuth neodecanoate, and the amount of bismuth neodecanoate in the 3D printing ink may range from about 6% to about 20% by weight. The polymer ink may be transparent or opaque. A method for 3D printing of an anatomic replica using the 3D printing ink is also described. X-rays of anatomic replicas created with the 3D printing ink appear very similar to x-rays of organic hard tissues, thereby enhancing procedural training for health care professionals. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

This invention offers 3D printed anatomic replication that appears, when exposed to x-ray imaging, very similar to the x-ray imaging of organic hard tissues. The challenge of creating a radio-opaque 3D printing ink is greater than one would initially imagine as the chemical composition must, at the same time, a) not affect the setting or set properties of the polymer ink, b) not obscure the transparent polymer inks used to print clear procedural training replicas, and c) not clog the microscopic printer jets as they disperse the printing ink to build the 3D anatomic replicas.

A radio-opaque 3D printing ink contains a radio-opaque additive and a polymer ink. The polymer ink is vinyl acetate ink, anilide ink, or any other polymer ink that is known in the art. The polymer ink may be transparent or opaque. The radio-opaque additive is bismuth neodecanoate ("Bi-NDE", CAS 34364-26-6, Bi(CioHi90 2 )3). Bi-NDE is an organo- metallic compound commercially available in liquid form from sources such as Sigma- Aldrich. Bi-NDE, also known as bismuth trineodecanoate and neodecanoic acid bismuth salt, has a refractive index of n20/D 1.479, a boiling point of 300°C, and a density of 1.145 g/mL at 25 °C.

Bi-NDE is an ideal radio-opacifier in polymer inks, preferably UV-cured polymer inks, due to the following properties:

1. Bi-NDE, when added in a range of about 6% to about 20% by weight to a polymer ink such as vinyl acetate ink or anilide ink, does not significantly affect the hardness or heat resistance of the printed replicas;

2. Bi-NDE is a clear, syrup-like solution; and

3. Bi-NDE, while relatively thick in consistency, disburses through the microjet printing block ports of ink-jet printers without inordinately clogging the jets. Table 1 discloses embodiments of a radio-opaque 3D printing ink that has a Bi-NDE content ranging from about 6% to about 20% by weight and by volume.

Table 1 g % wgt. mL % vol.

Bi-NDE 250 6.67 218.34 5.48

Vinyl Acetate 3500 93.33 3763.44 94.52

Total 3750 100.00 3981.78 100.00 g % wgt. mL % vol.

Bi-NDE 500 12.50 436.68 10.40

Vinyl Acetate 3500 87.50 3763.44 89.60

Total 4000 100.00 4200.12 100.00 g % wgt. mL % vol.

Bi-NDE 600 14.63 524.02 12.22

Vinyl Acetate 3500 85.37 3763.44 87.78

Total 4100 100.00 4287.46 100.00 g % wgt. mL % vol.

Bi-NDE 700 16.67 611.35 13.97

Vinyl Acetate 3500 83.33 3763.44 86.03

Total 4200 100.00 4374.79 100.00 g % wgt. mL % vol.

Bi-NDE 800 18.60 698.69 15.66

Vinyl Acetate 3500 81.40 3763.44 84.34

Total 4300 100.00 4462.13 100.00 g % wgt. mL % vol.

Bi-NDE 900 20.45 786.03 17.28

Vinyl Acetate 3500 79.55 3763.44 82.72

Total 4400 100.00 4549.47 100.00 g % wgt. mL % vol.

Bi-NDE 1000 22.22 873.36 18.84

Vinyl Acetate 3500 77.78 3763.44 81.16

Total 4500 100.00 4636.8 100.00 g % wgt. mL % vol.

Bi-NDE 1100 23.91 960.7 20.34

Vinyl Acetate 3500 76.09 3763.44 79.66

Total 4600 100.00 4724.14 100.00

{ Experimentation shows that less than 6% Bi-NDE in the radio-opaque 3D printing ink by weight does not provide sufficient radio-opaque properties for the anatomic replicas to mimic organic hard tissue upon X-ray. Experimentation also shows that more than 20% Bi-NDE in the printing ink causes the jets of the printer to clog too frequently, with cleaning required during each printing cycle. Approximately 12% Bi-NDE by weight seems to strike a good balance between the amount of radio-opacity provided and good printing performance. Ideally, the printer jets should be cleaned about halfway through the printing cycle.

While 3D printing inks containing a radio-opaque additive have been described with a certain degree of particularity, many changes may be made in the composition of the ink and the methods of using it without departing from the spirit and scope of this disclosure. The invention, therefore, is limited only by the scope of the attached claims, including the full range of equivalency to which each element thereof is entitled.