Title:
RECOVERY OF METAL, ESPACIALLY SILVER, FROM METAL CHLORIDES BY HYDROGEN REDUCTION
Document Type and Number:
WIPO Patent Application WO/2009/076684
Kind Code:
A2
Abstract:
A method of recovering silver from a silver chloride mixture in which hydrogen gas is passed through the mixture to produce a metal chloride hydride which is then heated to dissociate the metal and to release hydrogen chloride gas.

Inventors:
MOSTERT PHILIPPUS JACOBUS (ZA)
Application Number:
PCT/ZA2008/000124
Publication Date:
June 18, 2009
Filing Date:
December 09, 2008
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
RAND REFINERY LTD (ZA)
PRIOR ENGINEERING SERVICES AG (CH)
MOSTERT PHILIPPUS JACOBUS (ZA)
International Classes:
C22B5/12; C22B11/02; C22B11/06
Domestic Patent References:
WO2005102569A12005-11-03
Foreign References:
RU2265673C12005-12-10
US3586497A1971-06-22
DE1592499A11972-05-18
Other References:
DATABASE EPODOC [Online] EUROPEAN PATENT OFFICE, THE HAGUE, NL; XP002531312 & RU 2005 128024 A (OOO NPF GERO OOO NPF GERO [RU]) 20 March 2007 (2007-03-20)
Attorney, Agent or Firm:
MCCALLUM, RADEMEYER & FREIMOND (7 June Avenue Maclyn HouseBordeaux, 2125 Randburg, ZA)
Download PDF:
Claims:

CLAIMS

1. A method of recovering metal from a particulate mixture which contains a metal chloride which includes the steps of:

(a) controlling the temperature of the particulate mixture,

(b) passing a gas which contains hydrogen through the particulate mixture for a predetermined time period to produce a metal chloride hydride, and

(c) raising the temperature of the particulate mixture to cause the metal chloride hydride to dissociate into the metal and to release hydrogen chloride gas.

2. A method according to claim 1 which includes an initial step of drying the mixture at a temperature of up to 100 0 C in an atmosphere of the hydrogen- containing gas.

3. A method according to claim 2 wherein the drying is to a dryness of < 0,1% H 2 O.

4. A method according to claim 3 which includes the step, after drying, of comminuting lumps of a salt of the metal before carrying out step (b).

5. A method according to claim 1 which includes the step of forming a plurality of gas passages in the particulate mixture to achieve distribution of the hydrogen- containing gas through the mixture during step (b).

6. A method according to claim 1 wherein the predetermined time period is at least four hours long and the temperature of the particulate material is from 70 0 C to 8O 0 C.

7. A method according to claim 1 wherein, in step (a), the controlled temperature is from 7O 0 C to 80°C.

8. A method according to claim 1 wherein, in step (c), the temperature is raised to at least 400°C.

9. A method according to claim 8 wherein the temperature is thereafter raised to at least 600 0 C.

10. A method according to claim 1 wherein, in step (c), the hydrogen chloride gas is collected in water.

1 1. A method according to claim 1 wherein the hydrogen-containing gas is H 2 /N 2 of 50% / 50% by volume.

12. A method according to claim 1 wherein the metal is at least one of silver, gold and copper.

13. A method according to claim 1 which is carried out at atmospheric pressure.

Description:

REDUCTION OF METAL CHLORIDE

BACKGROUND OF THE INVENTION

[0001] This invention relates to a method of recovering a metal from a metal chloride.

[0002] The invention is described hereinafter with particular reference to the recovery of silver from silver chloride. This application is however exemplary only and, where applicable, the principles of the invention can be used for the recovery of other metals such as gold and copper from their chlorides.

[0003] The miller process has been used in the refining of precious metals for a substantial period. Impurities contained in gold bullion are typically silver and base metals such as copper and nickel. Most of the impurities are removed for example by volatilization or are contained in the miller slag in the form of metal chlorides.

[0004] Normally the principal component of miller slag is AgCI with a lesser amount of CU 2 CI 2 . Minor amounts of Pb, Zn and Fe chlorides and sodium chloride also occur. AgCI production is also common in other precious metal refining operations used in the industry. However due to the limited, arduous, expensive and inefficient techniques which are available to convert AgCI to metallic silver, the presence of AgCI is normally regarded as undesirable.

[0005] Various techniques have been used to reduce AgCI to a metallic form. These include the following:

AgCI in powder form, is reduced by placing the AgCI between iron plates, adding an aqueous acid solution to the AgCI and then steam heating the mixture for two to three days to produce a silver product. Extensive washing of the silver product is required before further refining takes place;

zinc dust is added to a silver chloride slurry in an acidified environment. The zinc powder is however expensive and, again, extensive washing is required before melting of the target metal can take place;

silver chloride is reduced using soda ash, soda ash plus borax or by the addition of carbon; and

a technique described in US patent 4,388,109 wherein silver chloride is mixed with sodium carbonate and heated to a temperature in excess of 500 0 C to produce elemental silver and sodium chloride. Extensive washing is required before melting takes place.

[0006] It is an object of the present invention to provide an improved method for the recovery of silver wherein the metal chloride is directly reduced to metal using hydrogen gas and which is carried out at atmospheric or at a low pressure. A further object of the invention is to allow for the recovery of the hydrochloric acid gas which is evolved during the reduction process.

SUMMARY OF INVENTION {

[0007] The invention provides a method of recovering metal from a particulate mixture which contains a metal chloride which includes the steps of: (a) controlling the temperature of the particulate mixture,

(b) passing a gas which contains hydrogen through the particulate mixture for a predetermined time period to produce a metal chloride hydride, and

(c) raising the temperature of the particulate mixture to cause the metal chloride hydride to dissociate into the metal and to release hydrogen chloride gas.

[0008] The method may be preceded by a step of drying the mixture at a temperature of up to 100 0 C in an atmosphere of the hydrogen-containing gas.

[0009] The method is preferably carried out at atmospheric pressure or at a pressure which does not differ substantially from atmospheric pressure.

[0010] The metal chloride mixture is preferably dried to a dryness of less than 0,1 % H 2 O. The drying process can lead to the production of lumps of the metal salt. If so these are comminuted using any suitable technique to produce a typical sand-sized dried product before carrying out step (b).

[0011] The heating and reduction steps are carried out in a crucible. The particulate mixture may form a mixed metal chloride bed in the crucible and, to ensure an even hydrogen gas distribution throughout the bed, gas distribution holes or passages may be formed into the bed.

[0012] In step (b) the predetermined time period may be at least four hours long. The temperature of the bed, during this phase, may be controlled to be between 70 0 C and 80 0 C. In step (c) the temperature may be raised, preferably incrementally, initially to about 400 0 C and thereafter to at least 600°C. Dissociation of the metal chloride hydride starts and as the temperature is increased to about 270 0 C the dissociation proceeds rapidly, releasing HCI. The HCI gas which is soluble in water, is collected in a scrubber using a water collection system.

[0013] The hydrogen-containing gas preferably comprises H 2 /N2 of 50% / 50% by volume mixture.

BRIEF DESCRIPTION OF THE DRAWING

The invention is further described by way of example with reference to the accompanying diagram which illustrates the method of the invention.

DESCRIPTION OF PREFERRED EMBODIMENT

[0014] The accompanying drawing illustrates the application of the method of the invention. A slag mixture 10, produced in a precious metal refining process and containing mixed metal chlorides, typically including in excess of 90% AgCI, is subjected to a drying step 12. The mixture is dried at a temperature of up to 100 0 C using suitable control equipment 14, known in the art, in an atmosphere of H 2 /N 2 (16) of 50% / 50% by volume to a dryness of less than 0,1 % H 2 O. Any lumps of the metal salts which may form during the drying process are broken down in a comminution stage 18 to produce a sand-sized dried product 20 which is then charged into a crucible (not shown) in which the drying was carried out. The particulate mixture 20 forms a mixed metal chloride bed in the crucible. Passages or holes (not shown) are formed in the bed to ensure that an even hydrogen gas distribution can take place throughout the bed.

[0015] The gas 16 is then passed through the bed for a minimum of four hours at a temperature which is controlled by the apparatus 14 of between 7O 0 C and 8O 0 C. During this time the hydrogen gas reacts with the metal chloride salts to form corresponding metal chloride hydrides.

[0016] After the four hour treatment phase the temperature of the bed inside the crucible is raised, using the equipment 14, preferably incrementally, to a temperature of 600 0 C to 700 0 C. Dissociation of the metal chloride hydrides starts and as the temperature is increased to about 27O 0 C the dissociation proceeds rapidly, releasing HCI gas (24). This gas, which is soluble in water, is collected in a gas scrubber 26 using an appropriate water collection system as liquid hydrochloric acid 28 which is then available for industrial use or commercial disposal.

[0017] Metal 30 produced in the aforementioned process can then be further refined in a step 32 before disposing thereof.

[0018] Without being bound by the following explanation the applicant believes that AgCI forms ionic crystals with defects of the Schottky or Frenkel type which yield an enthalpy and entropy for the formation of a dominant defect pair. It is difficult to quantify the contribution from each parameter due to the intrinsic region of temperature and the defect concentration which exists in the bulk of the crystal formation. In respect of the total free energy of the complete pair one component of the defect cannot be created without creating the other charge compensating component. This system may result in pair formation free energy. Hence the enthalpy and entropy may be further resolved into the formation of the enthalpies and entropies of individual defect points of a particular crystal structure.

[0019] These effects result in superionic conductivity which provides a facility to incorporate atoms of hydrogen into the crystal structure due to local surcharges of electrons replacing flexible silver atoms by protons which are temporarily bonded. This bonding mechanism only occurs at temperatures below 15O 0 C.

[0020] The preceding theoretical explanation which is specuiatively advanced does however offer an explanation of the effect of working at the different temperatures. Thus, at a temperature below 15O 0 C and preferably in the region of from 70°C to 8O 0 C, the mixed metal chlorides, of which the major component is silver chloride, are able to load hydrogen atoms onto the charged surfaces of the crystals and, by subsequently raising the temperature to about 27O 0 C, the dissociation of the hydrided metal chlorides commences with the evolution of HCI gas. When the temperature is further raised initially to about 400 0 C and thereafter to about 700 0 C the molecular system which is formed is completely dissociated.

[0021] During the collapse of the crystal structure the hydrogen atoms are located sufficiently close to the chlorine atoms within the crystal system and this, together with a greater chemical affinity of chlorine atoms for hydrogen atoms, as opposed to the affinity of the chlorine atoms for the existing silver atoms, results in the formation of the more stable HCI molecule, above 15O 0 C, which is liberated as HCI gas.

[0022] The combination of these process steps results in the hydrogen reduction of silver chloride, to silver metal, with the liberation of HCI gas which readily dissolves in water to produce a hydrochloric acid solution which is available for industrial use. If all of the hydrochloric acid gas which is evolved is collected then the process is pollution free.

LABORATORY PILOT PLANT TEST RESULTS

THERMAL GRAVIMETRIC ANALYSIS (TGA) RESULTS OF THE PROCESS

[0023] Five TGA tests were done on a sample of granulated miller slag from which the copper chloride had been leached usinq the method described by G Stanley;

"The extractive metallurgy of gold in South Africa" SAIMM Publication - 1987 Pages 630 to 633.

[0024] TGA test conditions were:

Amount of sample - 20 - 30 mg

Gas flow - 100 ml/min

Gas composition - H 2 /N 2 = 1/1

Heating/temperature profile From 30° to 400 0 C @ 5°C/min

Isotherm STFP @ 400 0 C - 120 mins

Reaction - AgCI + Y 2 H 2 → Ag + HCI

Theoretical weight loss - AgCI to Ag = 24,76%

Weight Loss - % % of 24.76%

TEST 1 After 25 mins - 1.11% (Reduction Efficiency)

After 45 mins - 0.94% After 190 mins - 24.0% 96.9%

TEST 2 After 45 mins - 0.52%

After 190 mins - 21.90% 88.4%

TEST 3 After 35 mins - 0.72%

After 120 mins - 22.60% 91.3%

TEST 4 After 25 mins - 0.94%

After 45 mins - 0.96% After 120 mins - 23.9% 96.5%

TEST 5 After 25 mins - 1.16%

After 45 mins - 1.87% After 190 mins - 24.4% 98.5%

[0025] While the analyses indicate that the process could be highly efficient in reducing AgCI to Ag metal, the hydhding temperature range could not be accurately defined using TGA, due to the theoretical weight gain of only 0.7% on a very small

sample of AgCI (i.e. a 0.00021 gram weight gain on a 0.03 gram sample). Also, as AgCI is hygroscopic, moisture loss made weight gain measurements extremely difficult.

[0026] An optimum hydriding temperature is below 150°C and appears to be greater than 30 0 C; possibly between 70 0 C and 100°C. This optimum hydriding temperature is considered to be important and must be accurately controlled, over an adequate period of time and with sufficient hydrogen available, to ensure complete hydriding of the AgCI. Decomposition of the hydride formed, in turn, only requires an adequate temperature increase over a sufficient period of time.

PILOT PLANT TEST RESULTS

[0027] In order to assess the effect of scale-up from the very small sample size (0.03 gram sample weight) used for the TGA tests, Calcimat Pilot Plant tests were completed using a much larger test sample weight of AgCI of about 500 grams.

Calcimat test work conditions, at atmospheric pressure, were:

Amount of sample - 507 grams

Gas Flow - 0.25l/min

- Gas Composition - H 2 /N 2 = 50/50% (vol/vol)

Specific Heating/temperature profile - 86/277/480 0 C

Process time - 135 min/174 min/239 min

Outcome weight analysis - 252.5 grams

Temperature was estimated inside the bed with a tolerance of app.5°C.

CALCIMAT PILOT PLANT TEST ANALYSES

AqCI TOTAL Ag Au Cu TOTAL

% % % %

Feed 59.5 54. 6 0.81 6.5

Lower Reactor Bed 54.5 52. 9 0.79 6.7

Upper Reactor Bed 54.7 55. 2 0.89 6.7

Product Trace 69. 5 0.7 6.7

Product Melt -- 9900.. 33 11..8844 77..55 99.64

[0028] From these tests it can be concluded that practically 100% reduction of AgCI to metallic silver was achieved. Only a trace of AgCI could be detected in the final melt product. The sum of the metal, Ag + Au + Cu, totalled 99.64%, indicating the complete reduction of all metal chlorides to their metallic forms.

[0029] 40.7% of the HCI was liberated, the remaining portion being entrapped within the Collapsed sinter product. However, this entrapped HCI is released upon melting.

[0030] In the test work which was done to prove the viability of the method of the invention the test samples were dried and comminuted. These steps might not always be necessary in order to obtain a reduction efficiency in excess of 99%. For example if copper chloride has previously been removed by leaching a very porous silver chloride product is left and this may have a sufficiently large surface area to enable the comminution step to be dispensed with.

[0031] Another factor is that when the product is heated to 400 0 C there is complete dissociation of the hydride to silver metal and HCI. This is borne out by the TGA tests in which practically 100% reduction was achieved.

[0032] In the large scale test the temperature was raised to 400 0 C, or 600°C. In this case the elimination of the HCI was not complete, as in the TGA tests, although elimination of the HCI was completed upon subsequent melting.

[0033] As the melting point of AgCI is 455°C it is possible that, in the larger scale tests, the bed melted before all the HCI could be expelled. However if sufficient time is provided with the temperature at 400 0 C all the HCI will be expelled and consequently the temperature of 455 0 C should not be exceeded before the step of expelling the HCI is completed.

[0034] Thus the two process steps of hydriding and dissociating must be fully completed, at the preferred temperatures of about 80 0 C and 400 0 C respectively, to obtain maximum HCI release and maximum reduction.