| 1. | A polymer having an exomethylene group in the repeating unit selected from the group consisting of i ■ and where R, R1 = alkyl group (C = 15) , phenyl group, or H. |
| 2. | A copolymer having the repeating unit [(CH2CH2)X CH, (CH2CH2CH2C)y] . |
| 3. | A copolymer having the repeating unit AB where A is derived from an αolefin and B is derived from an exomethylene substituted cyclic organic compound. |
| 4. | The copolymer of Claim 3 where A is derived from the group consisting of ethylene, propylene, and styrene. |
| 5. | The copolymer of Claim 3 where B is derived from the group consisting of a) X^ϊ, "c) SUBSTITUTE SH I and where R, R1 = alkyl group (c = 15), phenyl group, or H SUBSTITUTE SHEET. |
AND POLYMERS THEREFROM
Background of the Invention This is a continuation-in-part of Application Serial No. 962,390, Filed October 16, 1992. This application relates to catalysts and more particularly to homogeneous catalysts for use in polymerization via the ring opening of strained ring systems, and the polymers formed with such catalysts. In the presence of Ziegler-Natta catalysts, methylenecyclobutane A can be polymerized into a polymer consisting of a mixture of micro-structure units B and C, through a ring-opening mechanism and a simple vinyl type insertion mechanism, respectively.
A B ' C
Micro-structure B is particularly interesting m that it not only represents the thermodynamically unstable form of the synthetic rubber poly(isoprene) , but when incorporated into copolymers with simple olefins, it can impart useful functionalities. Although it has been shown that several Ziegler-Natta catalysts, including AlEt 2 Cl-Cr(acac) 3 -TiCl 4 ARA, can selectively produce a polymer with structure B dominating, the activity of these catalysts appears extremely sluggish. More importantly, the mechanism of the ring-opening process which was earlier proposed to involve the oxidative addition of the ring C-C bond seems unlikely with the early transition metals where the required oxidation states may not necessarily be available.
Summary of the Invention Therefore, an object of the subject invention
.5 .UBSTITUTE Sttfct:
is a novel catalyst for polymerizations having a high activity. A further object of the subject invention is a polymer formed from a catalytic olefin polymerization process which operates via a ring-opening mechanism. A still further object of the subject invention is a polymer formed through the use of a catalyst -by which electrophilic metallocene cations catalyze the facile regioselective ring-opening homopolymerization of exo-methylene substituted cyclic organic compounds and the copolymerization of such compounds with α-olefins such as ethylene, propylene and styrene via a β-alkyl shift mechanism. Catalysts having RB(C 6 F 5 ) 3 " , B(C 6 F 5 ) 4 - or methylalumoxane derivatives as the charge-compensating anion, especially Cp 2 ZrMe + MeB (C 6 F 5 ) 3 " (Cp = η 5 - l ,2-Me 2 C 5 H 3 ) , can catalyze the ring-opening polymerization of methylenecyclobutane to form the iso-rubber micro-structure B with not only very high selectivity, but also great efficiency. Such catalysts also catalyze the co-polymerization of simple olefins with exo- methylene cyclic organic monomers, such as methylenecyclobutane. Polyolefins of the structure [CH 2 CH 2 CH 2 C(CH 2 )] n and ( [CH 2 CHR] x [CH 2 CH 2 CH 2 C(CH 2 ) ] y ) n can thus be prepared where R = an alkyl or aryl group. The probable mechanism of the methylenecyclobutane polymerization is shown in the Reaction Sequence I.
SUBSTITUTE SHEET
The key step is a heretofore unrecognized ring opening polymerization via a β-alkyl shift. Such a polymerization process should be applicable to the polymerization of a variety of strained ring monomers having exocyclic unsaturation.
Detailed Description of the Invention Facile β-alkyl transpositions are a distinctive feature of electrophilic d°f n hydrocarbyl chemistry (e.g., equation (II)) and
M' R M—R II II
represent an important chain transfer channel in certain olefin polymerization processes. In principle, such transpositions might also provide an unusual pathway to functionalized polyolefins by coupling olefin insertion and strained monomer ring-opening sequences (equation (III) ) .
In the presence of conventional heterogeneous Ziegler- Natta catalysts, methylenecyclobutane A undergoes a sluggish reaction to afford polymers having ring-opening or mixed ring-opening/insertion-derived microstructures (B,C) . The ring-opened structures were ascribed to oxidative addition at the C3-C4/C4-C5 junctures of A. As stated above, the subject invention involves electrophilic zirconocene cations, which catalyze the facile, regioselective ring-opening homopolymerization of exo-methylene cyclic organic compounds and copolymerization with ethylene via a β-alkyl shift mechanism.
SUBSTITUTE SHcfc
The exo-methylene cyclic organic compounds generally may be represented by the formula:
where R 1 , R 11 , R m and R IV are organic fragments which may include O, N, S or P. Preferably, the monomer is methylenecyclobutane . In general, reaction of the catalyst Cp n MR + 3.n B(C 6 H 5 ) 3 R' ~ , where Cp is a cyclopentadienyl containing ligand where n = 1 or 2 , M = Ti, Zr, or Hf, and R, R' is an alkyl (C = 1-5) , hydride, or aryl , with A proceeds rapidly in toluene solution to yield, after work-up, polymethylenecyclobutane (PMCB, Table I) . Examples of viable catalysts are (C 5 H S ) 2 ZrMe + MeB (C 6 F 5 ) 3 " and (1, 2 Me 2 C 5 H 3 ) 2 ZrMe + MeB(C 6 F 5 ) 3 -, or (C 5 H 5 ) 2 ZrR 2 and methylalumoxane, (R=alkyl, aryl, hydride, halide or alkoxide. Other nonpolar solvents, both aliphatic (C=l- 12) and aromatic (C=6-20) as well as others may be used. X H and 13 C NMR spectra reveal that the polymer microstructure is almost exclusively B { >_ 95%; minor traces of C may be present) , indicating that the present polymerization is highly selective for the ring-opening pathway. The length of reaction time/extent of conversion appears to have no detectable effect on selectivity (Table I, entries 1, 2) . However, lower reaction temperatures appear to slightly favor microstructure C (Table I, entry 3 by l NMR) . NMR analysis also indicates allylic end groups in all of those PMCB samples, consistent with chain transfer via β- H elimination. The present PMCB samples are soluble in aromatic solvents, but insoluble in CHCI 3 or acetone. Copolymerization of A with α-olefins such as ethylene can be readily effected by stirring A neat or in
SUBSTITUTE SHEET
toluene solution with 1 under 1.0 atm of ethylene (Table I, entries 4-6) . X H and 13 C NMR spectroscopy indicates
that the derived copolymers have ring-opened microstructure C exclusively and that the x and y CH 2 proportions [ (CH 2 -CH 2 ) x (CH 2 -CH 2 -CH 2 -C-) y ] n can be controlled via the reaction stoichiometry.
Table 1. Polymerization of Methylenecyclobutane and Copolymerization with Ethylene Using (1,2-Me 2 C 6 H 3 ),ZrMe " MeB(C 6 F 6 ) 3 ' as a Catalyst
Entry Catalyst Methylene Ethylene Solvent Temp Reaction Yield of Methylene M,.(M n ) :
Amount cyclobutaπe Pressure (mL) ( C) Time (h) Polymer cyclobutane x1000
(umol) Amount (1 atm) (g) :ethylene D (mmol)
7.33 27.0 20 16
7.33 27.0 20
7.33 23.8 -30 20 7.33 23.8 1.0 None 20 0.17
7.33 8.3 1.0 Toluene 20 0.17 (15) 7.57 1.2 1.0 Toluene 20 0.12 0.60 ca.0.002 n.a.
^Monomer conversion by 'H NMR.
"Ratio of methylenecyclobutane and ethylene incorporated into the copolymer as determined by 'H NMR.
: By GPC versus polystyrene.
Various functionalized polymers are possible through the use of the catalyst of the subject invention, which results in a ring-opening Ziegler polymerization. Examples of the possible polymers are set forth in Table 2. The recurring exomethylene group is a signature group in the resulting polymer and is a focal point for additional functionalization or crosslinking.
SUBSTITUTE SHEET
Table 2
Monomer Polymer
(R, R 1 = alkyl group (C = 1-5) or phenyl group.)
All operations were performed with rigorous exclusion of oxygen and moisture in flamed Schlenk-type glassware in a dual manifold Schlenk line or interfaced to a high vacuum (10 "5 torr) system, or in a nitrogen or argon filled glovebox with a high capacity atmosphere recirculator. Argon, ethylene and propylene were purified by passage through a supported MnO oxygen removal column and a molecular sieve column. Aliphatic hydrocarbon solvents were pretreated with concentrated H 2 S0 4 , KMn0 4 solution, MgS0 4 and Na, 4A molecular sieves. All reaction solvents were distilled from Na/K/benzophenone under nitrogen and were condensed and stored in vacuo in bulbs on the vacuum line containing a small amount of [Ti (η 5 -C 5 Η. 5 ) 2 C1] 2 ZnCl 2 as indicator. Methylenecyclobutane was additionally dried over Na/K.
EXAMPLES
Preparation of Catalyst
SUBSTITUTE SHEET
Synthesis of Cp" 2 ZrMe 3 +Me 3 B (C 6 F 5 ) 3 ' (Cp"=l,2Me 2 C 5 H 3 ) CP" 2 ZrMe 2 (0.116 g, 0.378 mmol) and B(C 6 F 5 ) 3 (0.194 g, 0.379 mmol) are loaded into a 25 mL flask. Benzene (10 mL) was then vacuum transferred into this flask at -78°C. As the mixture was slowly warmed to ambient temperature. A clear solution was first seen but it quickly became cloudy as solids began to precipitate. After stirring for 2.5 h, the mixture was filtered. The light yellow solid was washed once with a small amount of benzene and dried under vacuum. Yield, 65%.
Synthesis of Cp 2 ZrCH 3 + CH 3 B (C 6 F 5 ) 3 " (Cp=77 5 -C 5 H 5 ) Cp 2 ZrMe 2 (0.100 g, 0.398 mmol) and B(C 6 F 5 ) 3 (0.205 g, 0.400 mol) are loaded into a 25 mL flask in the glovebox. Benzene (15 mL) was then vacuum-transferred into this flask at -78°C. The mixture was slowly warmed to room temperature and stirred for 1.5 h. At this time large quantities of solid precipitated. Pentane (10 mL) was vacuum-transferred into the flask and the mixture was filtered after stirring. The light yellow solid was washed once with 5 mL of pentane and dried under vacuum. Yield, 72%. Alternately, Cp 2 ZrMe 2 (0.264 g, 1.052 mmol) and B(C 6 F 5 ) 3 (0.539 g, 1.055 mmol) may be stirred in 20 mL of pentane in a 50 mL flask for 12 h at room temperature. The mixture is filtered and the solid washed once with pentane and dried under vacuum. Yield, 81%.
Example 1 Homo - • polymerization of Methylenecyclobutane . ( l , 2 -Me 2 C 5 H 3 ) 2 ZrMe + MeB ( C 6 F 5 ) 3 " ( 6 mg) was loaded into a 25 mL flask in a glovebox. Toluene (10 mL) and methylenecyclobutane (2.4 mL) were vacuum-transferred into the above flask at -78°C. The flask was backfilled with Ar and the solution stirred at room temperature for 16 h. The reaction was then quenched with methanol . After removing the volatiles under vacuum, the elastomeric polymeric product was washed several times
SUBSTITUTE SHEET
with toluene and dried under vacuum. Yield 1.73 g. The polymer is characterized by 1 H and 13 C NMR spectroscopy. The 1 H NMR also gives an number-averaged molecular weight (M n ) of ca.2,000.
Example 2 Co-polymerization of Methylenecyclobutane with Ethylene. (l,2-Me 2 C s H 3 ) 2 ZrMe + MeB(C 6 F 5 ) 3 -(6 mg) was loaded into a 25 mL flask in a glovebox. Toluene (10 mL) and methylene-cyclobutane (0.70 mL) were vacuum-transferred into the above flask at -78°C. The solution was stirred at room temperature under 1 atm of ethylene for 10 min. The reaction was then quenched with methanol. The white solid product was collected by washing with acetone and drying under vacuum. Yield 0.98 g. NMR (toluene-d 8 , 90°C) : X H : δ (PPM) 4.83, 2.06, 1.65, 1.50, 1.35. 13 C: δ (ppm) 150.2, 149.9, 109.5, 109.3, 36.9, 36.4, 30.16, 28.48, 26.78.
Example 3 Co-polvmerization of Methylenecyclobutane with Ethylene. (C 5 H 5 ) 2 ZrMe + MeB (C 6 F S ) 3 " (25.8 mg) was loaded into a 25 mL flask in the glovebox. Toluene (25 mL) and methylenecyclobutane (0.10 mL) were vacuum-transferred into the above flask at -78°C. The solution was stirred at room temperature under 1 atm of ethylene for 2.0 min. The reaction was then quenched with methanol. The white solid product was collected by washing with acetone and drying under vacuum. Yield 0.68 g.
Example 4 Homo-polvmerization of Exomethylene Cyclobutane Cyclopentane. (l,2-Me 2 C 5 H 3 ) 2 ZrMe + MeB(C 6 F 5 ) 3 -(6 mg) is loaded into a 25 mL flask in a glovebox. Toluene (10 mL) and ' exomethylene cyclobutane cyclopentane (1.0 mL) are vacuum-transferred into the above flask at -78 G C. The flask is backfilled with Ar and the solution stirred at
SUBSTITUTESHEET
room temperature for 10 h. The reaction is then quenched with methanol. After removing the volatiles under vacuum, the elastomeric polymeric product is washed several times with acetone and dried under vacuum. Yield should be about 0.49 g. The polymer is characterized by 1 H and 13 C NMR spectroscopy.
Example 5 Homo-polymerization of Exomethylene Cyclobutane Benzene. (l,2-Me 2 C 5 H 3 ) 2 ZrMe + MeB(C 6 F 5 ) 3 -(6 mg) is loaded into a 25 mL flask in a glovebox. Toluene (10 mL) and exomethylene cyclobutane benzene (1.0 mL) are vacuum- transferred into the above flask at -78°C. The flask is backfilled with Ar and the solution stirred at room temperature for 10 h. The reaction is then quenched with methanol. After removing the volatiles under vacuum, the polymeric product is washed several times with acetone and dried under vacuum. Yield should be about 0.39 g. The polymer is characterized by -U and 13 C NMR spectroscopy .
Example 6 Homo-polymerization of Methyl Exomethycyclobutane . ( l , 2 -Me 2 C 5 H 3 ) 2 ZrMe + MeB (C 6 F 5 ) 3 - ( 6 mg) is loaded into a 25 mL flask in a glovebox. Toluene (10 mL) and methyl exomethylcyclobutane (2.0 mL) are vacuum- transferred into the above flask at -78°C. The flask is backfilled with Ar and the solution stirred at room temperature for 20 h. The reaction is then quenched with methanol. After removing the volatiles under vacuum, the elastomeric polymeric product is washed several times with acetone and dried under vacuum. Yield should be about 1.2 g. The polymer is characterized by 1 H and 13 C NMR spectroscopy.
Example 7 Co-polymerization of Ethylene and Methylenecyclopropane . ( 1 , 2 -Me 2 C 5 H 3 ) 2 ZrMe MeB (C 6 F 5 ) 3 ( 14 mg) was loaded
SUBSTITUTE SHEET
into a 50 mL flask in the glove box. Then 20 mL of toluene and 0.25 mL of liquid methylenecyclopropane were vacuum box. Then 20 mL of toluene and 0.25 mL of liquid methylenecyclopropane were vacuum transferred into it . The solution was stirred under 1 atm of ethylene at room temperature for 5 minutes. It was quenched with methanol. The product was collected by filtration, washed with acetone and dried under vacuum. Yield 0.40 g. It was characterized by H 1 NMR in toluene-d 8 at 110°C.
Example 8 Co-polymerization of ethylene and methylenecyclopropane. (C 5 Me 5 ) 2 ZrMe MeB(C 6 F 5 ) 3 (15 mg) was loaded into a 50 mL flask in the glove-box. Then 15 mL of toluene was vacuum transferred into it. The solution was stirred under a mixture of ethylene and methylenecyclopropane (ratio 1:1 by volume) at room temperature for 20 minutes. It was quenched with methanol. The product was collected by filtration, washed with acetone and dried under vacuum. Yield 0.29 g. It was characterized by H 1 NMR in toluene-D 8 AT 100°c.
Example 9 Co-polymerization of Ethylene and Methylenecyclopropane. (C 5 Me s ) 2 ZrMe MeB(C 6 F s ) 3 (15 mg) was loaded into a 50 mL flask in the glove-box. Then 15 mL of toluene was vacuum transferred into it. The solution was stirred under a mixture of ethylene and methylenecyclopropane (ratio 3:1 by volume) at 60°C for 25 minutes. It was quenched with methanol. The product was collected by filtration, washed with acetone and dried under vacuum. Yield 0.30 g. It was characterized by H 1 NMR in toluene- d 8 at 110°C. With regard to the polymerization mechanism, it seems unlikely, based upon known chemistry, that methylenecyclobutane can support two-electron (or one- electron) oxidative addition-reductive elimination propagation sequences. Furthermore, X H and 13 C NMR analysis of copolymerizations with 13 CH 2 = 13 CH 2 indicates the
SUBSTITUTESHEET
presence of one 13 -CH 2 - unit adjacent to every exo- methylene group, compatible only with a C 2 -C 3 /C 2 -C 5 ring opening. Combined with prior evidence for β-Me shifts in propylene polymerizations at cationic zirconocene centers and β-alkyl shift-based methylenecyclobutane --> 1,4- pentadiene rearrangements at isoelectronic scandocene centers, the pathways of Reaction Sequence I set forth above seem most compatible with the present results. Additionally, kinetic measurements ( [1] =1.57-15.7 mm [A] = 1.05-2.09M) reveal that the homopolymerization of A obeys rate law (IV) , where
- dTAl = kflj A] 1 IV d+
K=4.1 (1) x lO^ ^S "1 at -5.5°C. Thus, the turnover- limiting step under these conditions appears to be olefin insertion rather than cyclobutane ring opening. As a result, it would appear that β-alkyl shift processes represent an efficient propagation pathway for the synthesis of new exo-methylene-functionalized polyolefins. While the invention has been described with reference to a preferred embodiment, it will be understood by those skilled in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the invention. In addition, many modifications may be made to adapt a particular situation or material to the teachings of the invention without departing from the essential scope thereof. Therefore, it is intended that the invention not be limited to the particular embodiment disclosed as the best mode contemplated for carrying out this invention, but that the invention will include all embodiments and equivalents falling within the scope of the appended claims. Various features of the invention are set forth in the following claims.