Title:
SEMICONDUCTIVE CROSSLINKABLE POLYMER COMPOSITION
Document Type and Number:
WIPO Patent Application WO/2006/131263
Kind Code:
A1
Abstract:
The present invention relates to a crosslinkable polymer composition which is useful for the preparation of semiconductive layers of electric cables, the polymer composition comprising (a) an unsaturated polyolefm having at least 0.15 vinyl groups/ 1000 carbon atoms and (b) carbon black.

Inventors:
JAEGER KARL-MICHAEL (SE)
JOHANSSON KENNETH (SE)
Application Number:
PCT/EP2006/005245
Publication Date:
December 14, 2006
Filing Date:
June 01, 2006
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
BOREALIS TECH OY (FI)
JAEGER KARL-MICHAEL (SE)
JOHANSSON KENNETH (SE)
International Classes:
C08K3/04; C08F210/02; C08F210/18; H01B1/24; H01B7/00
Domestic Patent References:
WO1997045465A11997-12-04
Foreign References:
US6376595B12002-04-23
EP1188788A12002-03-20
US5539075A1996-07-23
EP1041580A12000-10-04
Attorney, Agent or Firm:
KADOR & PARTNER (München, DE)
Download PDF:
Claims:
-Claims
1. A semiconductive crosslinkable polymer composition comprising (a) an unsaturated polyolefin having at least 0.15 vinyl groups/ 1000 carbon atoms, and (b) carbon black.
2. The polymer composition according to claim 1, wherein the unsaturated polyolefin has at least 0.30 vinyl groups/1000 carbon atoms.
3. The polymer composition according to claim 1 or claim 2 having a volume resistivity of less than 500000 Ohm * cm, measured at 900C.
4. The polymer composition according to one of the preceding claims, wherein the unsaturated polyolefin is prepared by polymerizing an olefin monomer and at least one polyunsaturated comonomer.
5. The polymer composition according to claim 4, wherein at least one polyunsaturated comonomer is a diene.
6. The polymer composition according to claim 5, wherein the diene is selected from 1,7octadiene, 1,9decadiene, 1,13tetradecadiene, 7 methyll,6octadiene, or mixtures thereof.
7. The polymer composition according to one of the claims 4 to 6, wherein the olefin monomer is ethylene.
8. The polymer composition according to claim 7, wherein the unsaturated polyethylene is produced by high pressure radical polymerization. .
9. The polymer composition according to one of the preceding claims, containing 1045 wt% carbon black, based on the weight of the semi conductive crosslinkable polymer composition.
10. The polymer composition according to one of the preceding claims, further comprising at least one crosslinking agent.
11. The polymer composition according to claim 10, wherein the crosslinking agent is a peroxide which is present in an amount of less than 1.0 wt%, based on the weight of the semiconductive crosslink able polymer composition.
12. A semiconductive crosslinked polymer composition, obtainable by treatment of the semiconductive crosslinkable polymer composition according to one of the claims 1 to 11 under crosslinking conditions.
13. The polymer composition according to claim 12, having a volume resistivity of less than 500000 Ohm * cm, measured at 900C.
14. The polymer composition according to claim 12 or 13, having a hot set value, measured according to IEC 81121, of less than 300%.
15. A process for preparing a multilayered article, comprising the steps of: (a) providing the semiconductive crosslinkable polymer composi tion according to one of the claims 1 to 9, and (b) applying the semiconductive, cosslinkable polymer composition onto a substrate by extrusion.
16. The process according to claim 15, wherein a crosslinking agent is added to the semiconductive crosslinkable polymer composition.
17. The process according to claim 16, wherein the crosslinking agent is added during and/or after application of the semiconductive crosslinkable polymer composition onto the substrate, and the addition is effected by migration from an external reservoir containing the crosslinking agent.
18. The process according to claim 17, wherein the external reservoir is another layer also applied onto the substrate and containing the crosslinking agent.
19. The process according to claim 17 or 18, wherein extrusion of the semiconductive crosslinkable polymer composition is effected without the presence of a crosslinking agent.
20. The process according to one of the claims 16 to 19, wherein the semiconductive crosslinkable polymer composition is treated under crosslinking conditions.
21. The process according to claim 20, wherein the semiconductive crosslinked polymer composition has a hot set value, measured ac cording to IEC 81 121, of less than 300%.
22. The process according to one of the claims 15 to 21, wherein the multilayered article is a power cable.
23. A crosslinkable multilayered article, wherein at least one layer thereof comprises the crosslinkable semiconductive polymer compo sition according to one of the claims 1 to 11.
24. A crosslinked multilayered article, obtainable from the crosslinkable multilayered article according to claim 23 by treatment under crosslinking conditions.
25. The article according to claim 24, which is a power cable.
26. The article according to claim 24 or 25, wherein the crosslinked semiconductive polymer composition within at least one layer satisfies the following relationship: VR • CB • HS/1000000 < 2500 wherein VR: volume resistivity in Ohm • cm, measured at 900C CB: weight percentage carbon black, based on the total weight of the crosslinked semiconductive polymer composition within the layer; HS: hot set value in % measured according to IEC 81 121.
27. The article according to claim 25 or 26, wherein the power cable has an inner semiconductive layer which is obtained from the crosslink able semiconductive polymer composition according to one of the claims 1 to 11 by treatment under crosslinking conditions.
Description:
Semiconductive crosslinkable polymer composition

The present invention relates to crosslinkable polymer compositions which are useful for the preparation of semiconductive layers of electric cables.

Electric cables, in particular electric power cables for medium and high voltages, are made of a plurality of polymer layers extruded around the electric conductor. The electric conductor is usually coated first with an inner semiconducting layer, followed by an insulating layer, then an outer semiconducting layer. To these layers, further layers may be added, such as water-barrier layer and a sheath layer.

Normally, the insulating layer and the semiconducting layer are made of ethylene homo- and/or copolymers which are preferably crosslinked. Nowadays, low density polyethylene, crosslinked by adding peroxide compounds, is the predominant cable-insulating material. The inner semiconducting layer normally comprises an ethylene copolymer, such as an ethylene-ethylacrylate copolymer or an ethylene-butylacrylate copolymer. Outer semiconducting layers can be strippable or non-strippable. Normally, a strippable semiconducting layer comprises an ethylene copolymer in combination with an acrylonitrile-butadiene rubber and sufficient carbon black to make the composition semiconducting. A non-strippable outer semiconducting layer may comprise an ethylene-butylacrylate copolymer together with an amount of carbon black sufficient to make the composition semiconducting.

The amount of carbon black added to make the polymeric material semi- conductive does not only affect electrical properties but also a number of other properties like compounding behavior relavant for the manufacturing of the semiconductive material and extrusion behavior as well as formation of scorch of the final product.

. -

For compounding, the surface area of carbon black particles has to be wetted by the polymeric melt to result in a homogeneous blend. However, since carbon black particles usually have a large specific surface area, even a small reduction in carbon black content facilitates the compounding in terms of compounding rate and consistency (i.e. obtaining consistently a good quality).

There is also a relationship between the amount of carbon black and the rheological properties of the resultant polymeric material. As a general rule, viscosity at a given shear rate increases with increasing carbon black content. Furthermore, increasing viscosity with decreasing shear rate/shear stress is typical for polymers having a high content of filler particles. In dies of complex geometry, there may exist regions of low shear forces. Thus, in these regions, the viscosity is very high and, if exceeding a certain limit, the melt does not pass these regions at a sufficiently high rate. As explained above, insulating and semi-conductive layers are preferably made of crosslinked polyethylene, wherein crosslinking is initiated in a vulcanizing tube by crosslinking agents such as peroxides. However, if a significant amount of peroxide already decomposes in the extruder, thereby initiating premature crosslinking, this will result in so-called "scorch", i.e. formation of inhomogeneity, gel-like areas, surface-unevenness of the extruded polymer etc. To suppress the formation of scorch as much as possible, it is desired to minimize residence time of the polymeric melt including the peroxide within the above mentioned regions of low shear forces. Again, with regard to reduction of scorch, less carbon black would be favored.

In EP-A-0929606, the formation of scorch was reduced by blending a si- lane-containing polyethylene with carbon black having a surface area of 30-80 m 2 /g.

. -

In EP-A-1125306, the amount of carbon black was reduced by providing a specific non-uniform ethylene-alkyl(meth)acrylate.

On the other hand, for providing semiconductive cable layers, the amount of carbon black must be sufficiently high. Thus, simply reducing the carbon black content of existing polymer compositions might improve compounding and extrusion behavior but inevitably results in material of high volume resistivity which is not appropriate for semiconductive polymers to be used in power cables.

To improve resistance to thermal and mechanical stress, polymers extruded onto a cable conductor are preferably crosslinked. For crosslinking, the cable is passed through a vulcanization tube, where the cable is heated to activate the crosslinking agent, e.g. peroxides, and initiate crosslinking. To increase production rate, the cable is preferably passed through the vulcanization tube at high line speed. However, at high line speed, the degree of crosslinking might be too low for sufficiently improving thermal and mechanical properties. Thus, to improve production rate, it is desired to have a high crosslinking efficiency, i.e. a high degree of crosslinking obtained within a short period of time. However, any increase of crosslinking efficiency (e.g. by increasing the peroxide content) should not be at the ex- pense of other relevant properties such as compounding, scorch behavior and volume resistivity.

Furthermore, as explained above, if a significant amount of peroxide already decomposes in the extruder, this will result in so-called scorch. Therefore, to suppress the formation of scorch as much as possible, the amount of peroxide needed to sufficiently crosslink the semiconductive material is preferably reduced. However, with too low amounts of peroxide, the degree of crosslinking might be too low for sufficiently improving thermal and mechanical properties. Thus, to improve extrusion behaviour in

_ _

terms of scorch formation, it is desired to have a high crosslinking efficiency, i.e. a high degree of crosslinking obtained with a low amount of peroxide. Optimally, no peroxide is present within the semiconductive material during the extrusion step. However, any decrease of crosslinking agent should not be at the expense of other relevant properties such as compounding behavior, cable production rate and volume resistivity.

Considering the problems mentioned above, it is an object of the present invention to provide a semiconductive polymer composition wherein the amount of carbon black and/or the amount of peroxide can be reduced without adversely affecting semi-conducting properties. Furthermore, there should be a good balance between crosslinking efficiency, suppression of scorch and reduction of volume resistivity.

This object is solved by providing a semi-conductive crosslinkable polymer composition comprising

(a) an unsaturated polyolefin having at least 0.15 vinyl groups/1000 carbon atoms, and

(b) carbon black.

The content of unsaturation, generated by incorporating vinyl groups within the polyolefin component, enables to accomplish improved crosslinking properties. In a preferred embodiment, the number of vinyl groups is at least 0.20/1000 carbon atoms. In other preferred embodiments, it is at least 0.25, at least 0.30, at least 0.35, at least 0.40, at least 0.45, at least 0.55 or at least 0.60 vinyl groups/ 1000 carbon atoms.

In the present invention, it might be preferred to keep the number of vinyl groups within a certain range to improve balance between properties like crosslinking efficiency, scorch and electrical conductivity. Preferably, the

. .

number of vinyl groups is from 0.35 to 3, even more preferably from 0.40 to 1/1000 carbon atoms.

Preferred unsaturated polyolefins of the present invention may have densities higher than 0.860, 0.880, 0.900, 0.910, 0.915, 0.917, or 0.920 g/cm 3 .

The polyolefin can be unimodal or multimodal, e.g. bimodal.

Preferably, the unsaturated polyolefin has a melt flow rate MFR 2 .i6/i90°c of 0.1 to 50 g/10 min, more preferably 0.3 to 20 g/10 min, even more preferably 1.0 to 15 g/10 min, and most preferably 2.0 to 10 g/10 min.

Preferably, the unsaturated polyolefin is prepared by copolymerising at least one olefin monomer with at least one polyunsaturated comonomer. In a preferred embodiment, the polyunsaturated comonomer consists of a straight carbon chain with at least 8 carbon atoms and at least 4 carbon atoms between the non-conjugated double bonds, of which at least one is terminal.

Ethylene and propylene are preferred olefin monomers. Most preferably, ethylene is used as the olefin monomer. As a comonomer, a diene compound is preferred, e.g. 1,7-octadiene, 1,9-decadiene, 1,11-dodecadiene, 1,13-tetradecadiene, or mixtures thereof. Furthermore, dienes like 7- methyl-l,6-octadiene, 9-methyl-l,8-decadiene, or mixtures thereof can be mentioned. Unsaturated polyethylene of low density is preferred, e.g. unsaturated polyethylene having a density within the range of 0.915 to 0.939 g/cm 3 . In a preferred embodiment, the unsaturated polyethylene contains at least 50 wt-% ethylene monomer units. In other preferred embodiments, the unsaturated polyethylene contains at least 60 wt-%, at least 70 wt-%, at least 80 wt-% or at least 85 wt-% ethylene monomer units.

_ _

If the unsaturated polyolefin is an unsaturated polyethylene, its melt flow rate MFR 2. i 6/ i 9 o ° c is preferably 0.1 to 50 g/10 min, more preferably 0.3 to 20 g/10 min, even more preferably 1.0 to 15 g/10 min.

Siloxanes having the following formula:

CH 2 =CH-[Si(CH 3 ) 2 -O] n -Si(CH 3 ) 2 -CH=CH 2 , wherein n=l or higher

can also be used as a polyunsaturated comonomer. As an example, divinyl- siloxanes, e.g. α,ω-divinylsiloxane, can be mentioned.

In addition to the polyunsaturated comonomer, further comonomers can optionally be used. Such optional comonomers are selected from C 3 -C 2O alpha-olefins such as propylene, 1-butene, 1-hexene and 1-nonene, polar comonomers such as acrylic acid, methacrylic acid, acrylates, methacry- lates or acetates.

As an example, the crosslinkable polymer composition may contain polar comonomer units, such as 1-50 wt.-%, 3-25 wt.-% and 5-20 wt.-% polar comonomer units per gram of unsaturated polyolefin.

Still more preferably, the polar unsaturated polyolefin comprises a copolymer of ethylene with Ci to C 4 acrylates, such as methyl, ethyl, propyl, butyl acrylates or vinyl acetates.

The unsaturated polyolefin can be produced by any conventional polymeri- sation process. Preferably, it is produced by radical polymerisation, such as high pressure radical polymerisation. High pressure polymerisation can be effected in a tubular reactor or an autoclave reactor. Preferably, it is a tubular reactor. In general, the pressure can be within the range of 1200-3500 bars and the temperature can be within the range of 150°C-350°C. Further details about high pressure radical polymerisation are given in WO93/08222, which is herewith incorporated by reference. However, the

_ _

unsaturated polyolefin can also be prepared by other types of polymerisation, such as coordination polymerisation, e.g. in a low pressure process, with Ziegler-Natta, chromium, single site/dual site, metallocene (for example transition metal catalysts), non-metallocenes (for example late transi- tion metals). The transition and late transition metal compounds are found in groups 3-10 in the periodic table (IUPAC 1989). These catalysts can be used in the supported and non-supported mode, i.e. with and without carrier.

According to the present invention, the semiconductive crosslinkable polymer composition further comprises carbon black.

The semiconductive properties result from the carbon black added to the unsaturated polyolefin. Thus, the amount of carbon black is at least such that a semiconducting composition is obtained. Depending on the desired use and conductivity of the composition, the amount of carbon black can vary. Preferably, the crosslinking polymer composition comprises 15-50 wt% carbon black, based on the weight of the semiconductive crosslinkable composition. In other preferred embodiments, the amount of carbon black is 10-45 wt.-%, 20-45 wt%, 30-45 wt%, 35-45 wt% or 36-41 wt%, based on the weight of the semiconductive crosslinkable composition.

Any carbon black can be used which is electrically conductive. Examples of suitable carbon blacks include furnace blacks and acetylene blacks.

Suitable furnace blacks may have a primary particle size less than 29nm measured according to ASTM D-3849. Many suitable furnace blacks of this category are characterized by an iodine number between 60 and 300mg/g according to ASTM D-1510 and an oil absorption number between 50 and 200 ml/100g.

_ _

Suitable furnace blacks may have a primary particle size of greater than 28nm measured according to ASTM D-3849. Many suitable furnace blacks of this category are characterized by an iodine number between 30 and 200mg/g according to ASTM D- 1510 and an oil absorption number be- tween 80 and 300 ml/100g.

Other suitable carbon blacks can be made by any other process or be further treated.

Suitable carbon blacks for semiconductive cable layers are preferably characterized by their cleanliness. Therefore, preferred carbon blacks have an ash-content of less than 0.2 wt-% measured according to ASTM- 1506, a 325 mesh sieve residue of less than 30ppm according to ASTM D-1514 and have less than 1 wt-% total sulphur according to ASTM-1619.

Most preferred are extra-clean carbon blacks having an ash-content of less than 0.05 wt-% measured according to ASTM- 1506, a 325 mesh sieve resi- due of less than 15ppm according to ASTM D-1514 and have less than 0.05 wt-% total sulphur according to ASTM- 1619.

Preferably, the semiconductive crosslinkable polymer composition has a volume resistivity, measured at 9O 0 C, of less than 500000 Ohm • cm, more preferably less than 100000 Ohm • cm, even more preferably less than 50000 Ohm • cm. Volume resistivity is in a reciprocal relationship to electrical conductivity, i.e. the lower resistivity, the higher is conductivity.

As discussed above, an unsaturated polyolefin having at least 0.15 vinyl groups/1000 carbon atoms and carbon black are essential components of the semiconductive crosslinkable composition of the present invention. In a preferred embodiment, the crosslinkable semiconductive polymer composition comprises (a) an unsaturated polyolefin having 0.35 to 3.0, even more preferably 0.40 to 1.0 vinyl groups/1000 carbon atoms, prepared by polym-

_ _

erizing ethylene with a diene comonomer, optionally in the presence of a further comonomer like propylene and (b) 30 to 45 wt%, even more preferably 36 to 41 wt% carbon black, based on the weight of the crosslinkable semiconductive polymer composition.

According to a preferred embodiment, the semiconductive crosslinkable polymer composition further comprises a crosslinking agent.

In the context of the present invention, a crosslinking agent is defined to be any compound which can initiate radical polymerisation. A crosslinking agent can be a compound capable of generating radicals when decomposed but also comprises the radicals obtained after decomposition. Preferably, the crosslinking agent contains at least one -O-O- bond or at least one - N=N- bond. More preferably, the cross-linking agent is a peroxide and/or a radical obtained therefrom after thermal decomposition.

The cross-linking agent, e.g. a peroxide, is preferably added in an amount of less than 3.0 wt.-%, more preferably 0.2-2.6 wt.-%, even more preferably 0.3-2.2 wt.-%, based on the weight of the crosslinkable polymer composition. To have a good balance between scorch and crosslinking efficiency, it might be preferred to add the crosslinking agent, in particular a peroxide, in an amount of 0.3 to 1.0 wt%, even more preferably 0.4 to 0.8 wt%, based on the weight of the semiconductive crosslinkable composition.

The cross-linking agent may be added to the semiconductive crosslinkable composition during the compounding step (i.e. when the unstaturated poly- olefin is mixed with the carbon black), or after the compounding step in a separate process, or during the semiconductive crosslinkable composition is extruded, or after the extrusion, e.g. by diffusion of cross-linking radicals from another cable layer into the semiconductive layer.

_

As peroxides used for crosslinking, the following compounds can be mentioned: di-tert-amylperoxide, 2,5-di(tert-butylperoxy)-2,5-dimethyl-3- hexyne, 2,5-di(tert-butylperoxy)-2,5-dimethylhexane, tert-butylcumylper- oxide, di(tert-butyl)peroxide, dicumylperoxide, di(tert-butylperoxy- isopropyl)benzene, butyl-4,4-bis(tert-butylperoxy)valerate, l,l-bis(tert- butylperoxy)-3,3,5-trimethylcyclohexane, tert-butylperoxybenzoate, diben- zoylperoxide.

Preferably, the peroxide is selected from 2,5-di(tert-butylperoxy)-2,5- dimethyl-hexane, di(tert-butylperoxy-isopropyl)benzene, dicumylperoxide, tert-butylcumylperoxide, di(tert-butyl)peroxide, or mixtures thereof. Most preferably, the peroxide is di(tert-butylperoxy-isopropyl)benzene.

The semiconductive crosslinkable polymer composition may comprise further additives. As possible additives, antioxidants, scorch retarders, crosslinking boosters, stabilisers, processing aids, flame retardant addi- tives, acid scavengers, inorganic fillers, voltage stabilizers, additives for improving water tree resistance, or mixtures thereof can be mentioned.

A "scorch retarder" is defined to be a compound that reduces the formation of scorch during extrusion of a polymer composition if compared to the same polymer composition extruded without said compound. Besides scorch retarding properties, the scorch retarder may simultaneously result in further effects like boosting, i.e. enhancing crosslinking performance.

Useful scorch retarders can be selected from 2,4-diphenyl-4-methyl-l-pentene, substituted or unsubstituted diphenylethylene, quinone derivatives, hydro- quinone derivatives, monofunctional vinyl containing esters and ethers, or mixtures thereof. More preferably, the scorch retarder is selected from 2,4- diphenyl-4-methyl-l-pentene, substituted or unsubstituted diphenylethylene, or mixtures thereof. Most preferably, the scorch retarder is 2,4- diphenyl-4-methyl- 1 -pentene.

Preferably, the amount of scorch retarder is within the range of 0.005 to 1.0 wt.-%, more preferably within the range of 0.01 to 0.8 wt.-%, based on the weight of the crosslinkable polyolefin composition. Further preferred ranges are 0.03 to 0.75 wt-%, 0.05 to 0.70 wt-% and 0.10 to 0.50 wt-%, based on the weight of the crosslinkable polyolefin composition.

Typical cross-linking boosters may include compounds having an allyl group, e.g. triallylcyanurate, triallylisocyanurate, and di-, tri- or tetra- acrylates.

As antioxidant, sterically hindered or semi-hindered phenols, aromatic amines, aliphatic sterically hindered amines, organic phosphates, thio compounds, polymerized 2,2,4-trimethyl-l,2-dihydroquinoline and mixtures thereof, can be mentioned.

Preferably, the antioxidant is selected from the group of diphenyl amines and diphenyl sulfides. The phenyl substituents of these compounds may be substituted with further groups such as alkyl, alkylaryl, arylalkyl or hydroxy groups.

Preferably, the phenyl groups of diphenyl amines and diphenyl sulfides are substituted with tert.-butyl groups, preferably in meta or para position, which may bear further substituents such as phenyl groups.

More preferred, the antioxidant is selected from the group of 4,4'- bis(l,rdimethylbenzyl)diphenylamine 5 para-oriented styrenated diphenyl- amines, 6,6'-di-tert.-butyl-2,2'-thiodi-p-cresol, tris(2-tert.-butyl-4-thio-(2'- methyl-4'hydroxy-5'-tert.-butyl)phenyl-5-methyl)phenylphosph ite, polymerized 2,2,4-trimethyl-l,2-dihydroquinoline, or derivatives thereof.

Of course, not only one of the above-described antioxidants may be used but also any mixture thereof.

- -

If an antioxidant, optionally a mixture of two or more antioxidants, is used, the added amount can range from 0.005 to 2.5 wt-%, based on the weight of the unsaturated polyolefin. If the unsaturated polyolefin is an unsaturated polyethylene, the antioxidant(s) are preferably added in an amount of 0.005 to 1.0 wt-%, more preferably 0.01 to 0.80 wt-%, even more preferably 0.05 to 0.60 wt-%, based on the weight of the unsaturated polyethylene. If the unsaturated polyolefin is an unsaturated polypropylene, the antioxidant(s) are preferably added in an amount of 0.005 to 2 wt-%, more preferably 0.01 to 1 wt-%, even more preferably 0.05 to 0.5 wt-%, based on the weight of the unsaturated polypropylene.

Further additives may be present in an amount of 0.005 to 3 wt%, more preferably 0.005 to 2 wt%. Flame retardant additives and inorganic fillers can be added in higher amounts.

From the semiconductive crosslinkable polymer composition comprising at least one of the crosslinking agents as defined above, preferably a peroxide, a semiconductive crosslinked polymer composition can be prepared by treatment under crosslinking conditions, e.g. by heat treatment.

Preferably, the semiconductive crosslinked polymer composition has a volume resistivity, measured at 9O 0 C, of less than 500000 Ohm • cm, more preferably less than 100000 Ohm • cm, even more preferably less than 50000 Ohm • cm.

Furthermore, the semiconductive crosslinked polymer composition preferably has a hot set value, measured according to IEC 811-2-1, of less than 300 %, more preferably less than 200 %, and even more preferably less than 100 %. Hot set values are related to the degree of crosslinking. The lower a hot set value, the higher is the degree of crosslinking.

From the semiconductive crosslinkable polymer composition of the present invention, a multi-layered article can be prepared by applying said composition onto a substrate, preferably by extrusion.

To the semiconductive crosslinkable polyolefin composition, a crosslinking agent, preferably a peroxide, can be added.As already explained above, the point in time for adding the crosslinking agent can be varied. As an example, the crosslinking agent may be added to the semiconductive crosslink- able polymer composition when the unsaturated polyolefin is mixed with the carbon black in a compounding step, or after the compounding step in a separate process step. Furthermore, the crosslinking agent may be added during extrusion of the semiconductive crosslinkable polymer composition.

As a further alternative, the crosslinking agent can be added during and/or after application of the semiconductive crosslinkable polymer composition onto the substrate. In this preferred embodiment, the crosslinking agent can be provided in an external reservoir from which it can migrate into the layer comprising the semiconductive crosslinkable composition. In the context of the present invention, an "external reservoir" is a reservoir which is not part of the layer comprising the semiconductive crosslinkable composition. Preferably, the external reservoir is another layer also applied onto the substrate and containing the crosslinking agent. As explained above, the term "crosslinking agent" has to be defined in a broad sense. Thus, the other layer acting as a reservoir may comprise compounds not yet decomposed but may also comprise radicals resulting from decomposition. From the other layer, the crosslinking agent migrates to the layer comprising the semiconductive crosslinkable composition. Thus, since the crosslinking agent is provided from an external reservoir during and/or after having been applied onto the substrate, the semiconductive crosslinkable polymer composition of the present invention can be extruded without crosslinking agent or at least with a very low amount of crosslinking agent.

_ _

In a preferred embodiment, the other layer acting as an external crosslink- ing agent reservoir is provided adjacent to the layer comprising the semi- conductive crosslinkable polymer composition to facilitate migration of the crosslinking agent. If necessary, migration is enhanced by thermal treat- ment of one of these layers or both layers.

When sufficient crosslinking agent has been diffused into the semiconduc- tive crosslinkable composition, said composition can be treated under crosslinking conditions. If peroxides are used, crosslinking can be effected by raising the temperature to at least 160-170 0 C.

Even if the crosslinking agent is added to the semiconductive crosslinkable polymer composition by migration from an external reservoir, it is possible to obtain a semiconductive polymer composition sufficiently crosslinked, as will be further demonstrated below in examples 11-12.

Preferably, crosslinking results in a multilayered article having at least one layer in which the semiconductive crosslinked polymer composition has a hot set value, measured according to IEC 811-2-1, of less than 300 %, more preferably less than 200 %, and even more preferably less than 100 %.

In a preferred embodiment, the multi-layered article is a power cable, i.e. the crosslinkable composition is extruded onto a metallic conductor and/or at least one coating layer thereof for the preparation of a power cable.

Preferably, it is the inner semiconductive layer which is prepared from the semiconductive crosslinkable polymer composition by treatment under crosslinking conditions. However, it is also possible to prepare the inner and the outer semiconductive layer from the crosslinkable polymer compo- sition.

Preferably, the crosslinked semiconductive polymer composition, which may be present as a power cable coating layer, satisfies the following relationship:

VR « CB • HS/1000000 < 2500

wherein

VR: volume resistivity in Ohm • cm, measured at 90 0 C, CB: wt% carbon black, based on the total weight of the crosslinked semi-conductive polymer composition, and HS hot set value in %, measured according to IEC 811-2-1.

More preferable, VR • CB • HS/1000000 < 2000, even more preferable < 1000.

VR and HS are determined for a composition extruded as an inner cable layer at a line speed of 2.2 m/min.

According to another preferred embodiment, the crosslinked semiconduc- tive polymer composition satisfies the following relationship:

VR • CB • HS • S/1000000 < 80,

wherein

VR, CB and HS have the same meaning as indicated above and S is the scorch volume in %, measured at 134.5°C. Again, VR and HS are deter- mined for a composition extruded as an inner cable layer at a line speed of 2.2 m/min.

More preferable, VR • CB • HS • S/1000000 S < 50, even more preferable < 30.

_ _

Preferably, the semiconductive crosslinked polymer composition has a volume resistivity, measured at 90 0 C, of less than 500000 Ohm » cm, even more preferably less than 100000 Ohm » cm, and most preferably less than 50000 Ohm » cm.

In the present invention, the use of an unsaturated polyolefin having at least 0.15 vinyl groups/1000 carbon atoms does not only increase crosslinking efficiency and production rate but also enables to reduce carbon black content without adversely affecting volume resistivity. Furthermore, scorch can be suppressed effectively. Thus, even when the amount of carbon black is reduced, there is still a good balance between volume resistivity and scorch behavior. The improved balance enables to obtain a crosslinked semiconductive polymer composition satisfying the relationships mentioned above.

The invention is now further elucidated by making reference to the follow- ing examples.

Examples

Testing methods/measuring methods

a) Determination of the content of double bonds

The procedure for the determination of the number of vinyl groups/1000 C- atoms is based on the ASTM D-3124-72 method. In that method, a detailed description for the determination of vinyliden groups/ 1000 C-atoms is given based on 2,3-dimethyl-l,3-butadiene. This sample preparation procedure has been applied for the determination of vinyl groups/1000 C-atoms in the present invention. However, for the determination of the extinction coefficient for vinyl groups, 1-decene has been used, and the procedure as described in ASTM D-3124 section 9 was followed.

- -

The degree of unsaturation was analyzed by means of IR-spectrometry and given as the number of vinyl bonds.

The pure polymer is pressed at 15O 0 C into a thin film and cooled down to room temperature. The thickness of the film is about 0.8-1.2 mm. The in- frared absorbance of the film is measured by a Perkin-Elmer FT-IR spectrometer Spectro 2000.

The IR absorbance of the vinyl characteristic peak is determined from its peak height over a base line.

The peak is defined by the maximum absorbance in the wave number range from 904-920 cm "1 . The base line is defined through a linear connection between two points. These two points are set at the lowest absorbance in the wave number range from 910-990 cm " ' and from 810-880 cm "1 , respectively.

The concentration of vinyl groups is expressed as the number of vinyl groups per 1000 carbon atoms in a polymer chain. This value is calculated from the infrared absorbance as determined above.

The absorbance A (peak height at 910 cm '! ), is related to the number of vinyl groups according to

vinyl/1000 C-atoms = (14 x A )/ 13.13 x L x D),

L is the thickness (in mm) of the measured polymer film, and D is the density (g/cm 3 ) of the same film.

b) Melt flow rate

The melt flow rate is equivalent to the term "melt index" and is determined according to ISO 1133 and is indicated in g/10 min. Melt flow rate is de- termined at different loadings, such as 2.16 kg (MFR 2 ) used for characteriz-

_ _

ing the base polymer or 21.6 kg (MFR 2 O f° r tne semiconductive composition. Melt flow rate is determined at a temperature of 19O 0 C.

c) Melt pressure/pressure of the inner semiconductive layer during cable extrusion

Cables with three layers have been made using the semiconductive composition as inner and outer layer. The middle insulation layer is formed of low-density polyethylene LDPE (MFR 2 =2 g/10 min) containing 2 wt-% of dicumyl peroxide and 0.2 wt-% of 4,4'-thiobis(2-tert.-butyl-5- methylphenol).

The construction of the cables is 50 mm 2 stranded Al-conductor and 5.5 mm thick insulation. The inner and outer semiconductive layers have a thickness of 0.9 mm and 0.8 mm, respectively. The cable line is a catenary Nokia Mailefer 1+2 system, thus one extrusion head for the inner conducting layer and another for the insulation + outer semiconductive layer. The semiconductive layers have been exruded by a extruder of 45mm diameter and of a 24 length:diameter ration (L/D). The insulation layer has been exruded by a extruder of 60mm diameter and of a 24 L/D. The cables is cross-linked in the vulcanization tube using nitrogen and afterwards cooled in water. Cables were produced at different line speeds, i.e. 1.6, 2.2 and 2.4 m/min.

The term melt pressure refers to the pressure of the molten semiconductive composition measured at the tip of the extruder screw during production of the cables.

d) Volume resistivity

The volume resisitivity of the semiconductive material is measured on crosslinked polyethylene cables according to ISO 3915 (1981).

Cable specimens having a length of 13.5 cm are conditioned at 1 atm and 60 ± 2°C for 5 ± 0.5 hours before measurement. The resistance of the outer semiconductive layer is measured using a four-terminal system using metal wires pressed against the semiconductive layer. To measure the resistance of the inner semiconductive layer, it is necessary to cut the cable in two halves, removing the metallic conductor. The resistance between the conductive silver paste applied onto the specimen ends is then used to determine the volume resistivity of the inner semiconductive layer. The measurements were carried out at room temperature and 90 0 C.

The same procedure is used to determine the volume resistivity of compositions that have not yet been crosslinked.

e) Scorch

A laboratory extruder is used with a specifically designed die for the evaluation of scorch in the die. A die with a relatively long channel (about 25 mm in diameter and about 80 mm long) and a high residence time is used to promote scorch.

The test can be carried out at a range of selected temperatures and uses a constant output of about 1 kg/h. The material is run continuously for at least 5 hours. After the test, the hot sample in the die is taken out. The amount of scorch is measured in the sample by examining 0.2-0.3 mm cross sections taken from 6 different position. The volume of scorch in the 6 cross sections is measured by the use of a microscope. The mean value of the 6 cross sections is reported. Further information about the measurement of scorch volume can be found in EP 1 188 788 Al under the headline "Scorch (BTM 22527)".

f) Hot set

Specimen having been cut from the inner semi-conductive layers of the cables described above. Hot set has been measured according to IEC 811-2-1. Hot set values are related to the degree of crosslinking, i.e. the higher a hot set value, the lower the degree of crosslinking.

g) Shear rate/shear stress/shear viscosity

Shear rate, shear stress and shear viscosity were determined in a Rosand capillary rheometer having a piston diameter of 15 mm, a die length of 20 mm, a die diameter of 1 mm and a die inlet angle of 180°. The preheating time was 10 minutes and the measurement temperature was 130 0 C.

Examples 1 to 10

6 semiconductive polymer compositions A-F according to the present invention were prepared. Furthermore, 4 comparative compositions Ref. 1 to Ref. 4 were prepared. All the compositions are based on ethylene buty- lacrylate copolymer with similar butylacrylate content and MFR (table 1). However, for compositions A-F, an increased amount of double bonds was introduced into the polyethylene by effecting polymerization of ethylene with 1,7-octadiene as a polyunsaturated comonomer. Each polymerization reaction was carried out in a high pressure tubular reactor at a pressure of 2000-2500 bar and a temperature of 200-300 0 C.

In Table 1, the relationship between the amount of unsaturation, indicated by the number of vinyl groups per 1000 carbon atoms, and the amount of 1,7-octadiene is shown. In these runs, octadiene was added to the reactor and after having reached a stable octadiene concentration, samples were taken and analyzed. The results are compared to an ethylene butylacrylate copolymer made under the same conditions but without adding 1,7- octadiene .

Table 1: Relationship between a diene comonomer and vinyl groups

The results of Table 1 clearly indicate that the number of vinyl groups in- creases with increasing amounts of octadiene comonomer.

To all polymer compositions A-F and Ref. 1 to Ref. 4, a peroxide di(tert- butylperoxy-isopropyl)benzene) was added as a crosslinking agent. Furthermore, to obtain a semiconductive material, carbon black was added. The resultant semiconductive compositions are then extruded onto a cable, either as an inner semiconductive layer directly applied onto the cable conductor or as an outer semiconductive layer applied onto an insulation layer. Subsequently, the cable is guided through a vulcanization tube where the cable is heated to activate the peroxide and crosslink the polymer. Cables are run at different line speeds (i.e. from 1.6 to 2.4 m/min) which means that the residence time in the vulcanization tube is shorter with increasing line speed.

A summary of the semiconductive polymer compositions A-F and Ref. 1 to Ref. 4 is given in Table 2. Also provided are values for melt pressure within the extruder, volume resistivity of the inner and outer semi- conductive layer as a function of line speed, hot set, which is an indication for the degree of crosslinking, and formation of scorch.

Table 2: Summary of semi-conductive compositions

Table 2 continued

- -

The results of Table 2 clearly indicate that in compositions according to the invention a sufficient electrical conductivity can be obtained with a reduced amount of carbon black. Furthermore, a good balance between improved electrical properties, high crosslinking efficiency and reduction of scorch results from the composition according to the invention.

Comparing compositions A and B with Ref. 1, it is clearly indicated that the increased number of vinyl groups enables to lower the amount of peroxide and reduce the formation of scorch. Although the amount of peroxide in compositions A and B is significantly lower than in Ref. 1, the degree of crosslinking at high line speed of 2.2 m/min (i.e. higher production rate) is even increasing, as indicated by the hot set values. The higher a hot set value, the lower the degree of crosslinking.

Furthermore, although the amount and type of carbon black is the same in all samples, volume resistivity in compositions A and B is significantly im- proved.

As explained above, the formation of scorch causes a number of problems like adhesion of the polymer gel to the surface of the equipment. However, the present invention enables to obtain a composition of sufficiently high electrical conductivity with reduced amount of peroxide, thereby also re- ducing the scorch. Thus, if the production rate is limited by the formation of scorch and the burden of cleaning, the invention enables to have longer cable runs until scorch occurs.

Comparing composition C and Ref. 1, these compositions only differ in the amount of double bonds, indicated by the number of vinyl groups, whereas the amount of carbon black and peroxide, respectively, remains unchanged.

Table 2 clearly indicates a decrease of volume resistivity, in particular at higher line speed, and an increase of the crosslinking degree whereas there

is only a slight increase of scorch. There is still a good balance between conductivity, crosslinking efficiency and scorch.

Thus, if crosslinking speed is the limiting factor for the rate of cable production, the invention allows a faster production rate by using the same amount of peroxide or even less peroxide. Simultaneously, the electrical conductivity is even improved although the amount of carbon black remains unchanged.

In composition D, the amount of carbon black is reduced if compared to Ref. 1. Rheological properties of Composition D and Ref. 1 are summarized in Table 3. As already discussed above, polymers having a high amount of fillers show rapidly increasing viscosity with decreasing shear rate and shear stress. Materials appear to become more "solid-like" as the filler particles are allowed to create a strong network within the polymer melt. This general trend is reflected in Table 3. However, for Ref. 1, the effect is much more pronounced. In particular, at lower shear rate and shear stress, compound D has a lower viscosity, thereby facilitating flow in critical regions of the processing equipment and avoiding stagnancy or blocking.

Table 3: Relationship between shear rate and viscosity

REF l Compound D

Shear rate (/s) Shear stress Shear viscosity Shear stress Shear viscosity (kPa) (Pa.s) (kPa) (Pa.s)

20 203.51 10175 175.35 8768

50 282.67 5653 245.31 4906

100 361.49 3615 316.99 3170

198 457.26 2313 405.68 2051

400 574.18 1435 511.21 1280

600 647.56 1079 580.70 968

801 703.13 878 629.33 787

The results of Table 3 clearly indicate that the invention allows faster and easier incorporation of carbon black during compounding and facilitates extrusion with less risk of stagnant zones and lower melt pressure.

Furthermore, although the carbon black content of composition D has been reduced to improve rheological properties, volume resistivity is not adversely effected. On the contrary, at higher line speed (i.e. higher production rate), volume resistivity of composition D is even improved.

The results for composition F indicate that the amount of carbon black can be even further reduced but still enables to have the good balance between rheological properties, electrical conductivity, crosslinking efficiency and scorch behavior. Furthermore, considering the amount of vinyl groups of composition F, the results of Table 2 demonstrate that an increase of vinyl groups beyond the lower limit of the present invention is necessary to obtain the improved properties.

Examples 11 to 12

These examples show that the semiconductive compound of this invention can be sufficiently crosslinked without adding peroxide directly to the compound, but by a migration of peroxide from the insulation layer to the semiconductive layer. This is of particular interest, because this would mean that no peroxide needs to be present during extruding the semiconductive layer of a cable.

The samples used are sandwich-type plaques (diameter about 8 cm) with one insulation layer (about 4 mm thick) and one semiconductive layer (about 1.3 mm thick). The insulation layer is formed of LDPE (MFR 2 = 2g/10 min) containing 2 wt% of dicumyl peroxide and 0.2 wt% of 4,4'- thiobis(2-tert.-butyl-5-methylphenol), and the semiconductive layer is made of the semiconductive material to be tested.

_ _

The sandwich plaques are produced by means of a heatable laboratory press. Firstly, sheets of the insulation layer and the semiconductive layer are pressed individually at 120 0 C for 10 minutes. Secondly, the sheet of the insulation layer and the sheet of the semiconductive layer are brought to- gether and pressed together at 120 0 C for about 20 minutes. Thirdly, the temperature is increased to 18O 0 C above the activation temperature of the peroxide. The sandwich plaque remains pressed together at 180 0 C for about 30 minutes so that the crosslinking reaction is completed.

Specimen having been cut from the semiconductive layer. Hot set has been measured according to IEC 811-2-1 using a load of 10N/cm 2 .

The semiconductive materials to be tested were: Composition A but without peroxide added and composition REFl but without peroxide added.

The average hot set value of three tests of specimen of Example A without peroxide is 132%. However, when testing the example REF without perox- ide none of the three tests allowed a percent hot set to be determined, because the specimen broke due to insufficient crosslinking. This shows that the semiconductive material of the invention has improved crosslinking properties that enable a sufficient crosslinking by the addition of peroxide through migration from the insulating layer.

Examples 13 to 15

Wafer Boil Test

The wafer boil test is indicative whether the crosslinking degree of the semiconductive layer is sufficient.

The wafer boil test has been performed according to AEIC CS5-94, 10th edition, section G.2, on cross sections of the cables described above. Only

the cables made at highest line speed (2.4 m/min) have been investigated, since these are most critical for the wafer boil test; i.e. least crosslinked.

As described in the standard above, the wafers have been boiled in decahy- dronaphthalene for 5 hours. The wafers have been removed from the sol- vent and examined. A pass/fail results has been given as described in section D.5.1 of the above standard. Accordingly, if the inner semiconductive

* layer dissolves or cracks such that it does not maintain a continuous ring, the test result is "fail".

Compositions A, D and REFl have been subjected to the wafer boil test. However, only compositions A and D according to the present invention passed the test, as indicated in Table 4.

Table 4: Results of wafer boil test

Conclusion from this test:

Although Examples A, D and REFl appear to have a similar crosslinking degree as measured by the hot set test, the semiconductive material of the present invention is clearly superior in the wafer boil test, which also is a measure of the cross-linking degree. This suggests surprisingly that not only the crosslinking efficiency is enhanced by the increased number of vinyl groups but that, furthermore, the crosslinked polymer morphology is altered in a beneficial manner. This may lead also to the improved conductivity of Examples A and D, although they have the same hot set and the same or less amount of carbon black compared to REF 1.