Field of the Invention

The present invention relates to resins for films or coatings having release or peelability characteristics and modified surface tension properties, which makes them suitable for use in release films such as those used to protect adhesive films. It especially relates to so-called release films formed from polyolefin, a polysiloxane, a vinyl silane, and an ultra-high molecular weight silicone polymer.

The invention relates particularly to a multi-layer film comprising the release films formed from polyolefin, a polysiloxane, a vinyl silane, and an ultra- high molecular weight silicone polymer as a layer and a polyolefin forming another layer. The release film of this invention can also be adhered to or coated onto a subweb of paper, aluminum, plastics such as nylon and polyester, or other subwebs suitable for coating. The multi-layer film can be used in liquid-absorbing products, such as feminine hygiene pads, baby diapers and incontinence products.

Background of the Invention

Films containing a polyolefin, a polysiloxane, an organo-peroxide agent and a vinyl silane are known from U.S. Pat. Nos. 4,978,436 and 5, 169,900, both incorporated herein by reference. Such films are useful for their slip, release, peelability or related characteristics, making them suitable for use as peelable coatings on adhesive materials, as removable protective layers for substrates, and as slip layers used in high-speed coating and packaging apparatuses. The patents suggest a nominal film thickness of 25 microns and a gauge uniformity for such films of 25 to 30 microns. While these films perform their functions well, they have the disadvantage of being expensive, particularly in comparison with films made entirely of polyolefin. It has now been found that a thin film, one with thickness of about 1 to about 10 microns, can be made to perform the function of the much thicker films.

In the field of feminine hygiene pads, baby diapers, incontinence products and the like, perforated polyolefin films have long been used as a topsheet. These topsheets typically have tapered capillaries of critical diameters and tapers with a base in the plane of the topsheet and an apex remote from the plane and in contact with an absorbent element. U.S. Pat. No. 3,929,135, incorporated herein by reference, describes such topsheets. The patent discusses the product's ability to allow passage of fluid through the topsheet (away from the user) to the absorbent material, while preventing backflow from the absorbent material to the user.

The most commonly used polyolefin employed in such topsheets is low density polyethylene, which is ideal from a liquid wicking standpoint. With its relatively high surface tension (about 32 dynes/centimeter), liquid drainage through the topsheet is good. On the other hand, as a result of the high surface tension, certain discharge products such as menstrual fluids and feces adhere somewhat to the surface of the film, soiling the surface in contact with the user and occluding perforations with a resultant reduction in fluid transfer.

It has now been found that polyolefin film having a thin surface layer or coating of polysiloxane, with a surface tension of about 23 dynes/centimeter, can provide superior performance in these applications. While the lower surface tension would be expected to cause reduced liquid flow (that is, fluid drainage normally decreases with decreases in surface tension), it has been found that the polysiloxane-coated polyolefin has improved soiling resistance and generally allows for more rapid transfer of liquid through the topsheet to the absorbent material. Summary of the Invention

The present invention provides a silicone-containiπg polyolefin resin that in film-form has superior uniformity and efficacy at surprisingly low thickness. This film comprises (i) a polyolefin, (ϋ) a dimethyl polysiloxane having functional end-groups, (iii) at least one vinyl silane compound, and (iv) ultra-high molecular weight silicone polymer. Additionally, the film is preferably formed using an organic peroxide and an organo-metallic moisture curing agent, the organic peroxide preferably being at a level that not all the vinyl silane grafts to the polyolefin. The invention provides a multi-layer structure comprising (a) a subweb layer, preferably a polyolefin, and (b) a surface layer of the silicone-containing polyolefin film of this invention placed, preferably by coextrusion, on the subweb, the surface layer being a film having a thickness of about 1 to about 10 microns. The silicone-containing polyolefin film preferably is surface treated, for example by corona discharge, to improve its release properties.

The present invention further encompasses the use of the films hereindescribed as release layers, and, when the subweb is a polyolefin, in the aforementioned absorbent products.

Detailed Description of the Invention

As used herein, the following terms have the meanings given below.

"Polyolefin", whether used in layer (a) or layer (b) of the film of the present invention, means homopolymers and copolymers of unsaturated hydrocarbons having 2 - 20 carbon atoms. They can be made by processes well

known in the art, including metallocene processes. In particular, the polymers are homopolymers of ethylene or propylene or copolymers of ethylene with one or more alpha-olefin hydrocarbons having 3 - 10 carbon atoms, especially propylene, butene- 1 , hexene- 1 and octene- 1 and styrene. Suitable alpha-olefins also include dienes, that is, monomers with more than 1 site of unsaturation, especially 1,3 butadiene, 1,5 hexadiene and norbornadiene. In particularly preferred embodiments, the Polyolefins are copolymers of ethylene with a hydrocarbon alpha-olefin having from 4 - 8 carbon atoms and having a density in the range of about 0.850 to about 0.970 grams per cubic centimeter (g/cm^) and especially in the range of 0.920 to 0.930 g/cm Preferably, the polymers have a melt index (MI) in the range of 0.05 to 120 dg/min, especially 0.1 to 75 dg/min and in particular 1 to 10 dg/min. (as measured per ASTM D-1238, condition E).

Mixtures and blends of the Polyolefins may be used. In general, the polymers are of the type that may be extruded in the form of film. The Polyolefin may contain additives, for example antioxidants and other stabilizers, anti-block and slip agents and the like. The Polyolefin may also contain fillers, e.g., talc, mica, calcium carbonate, and the like and/or pigments such as titanium dioxide. In addition, the Polyolefin may contain modifying polymers, e.g., rubber-like modifying polymers such as ethylene propylene/diene, styrene butadiene styrene, and other elastomers. It is to be understood that any additive must not cause undue adverse effects on the release and/or surface tension properties of the film.

In alternative embodiments, direct copolymers or blends of copolymers of ethylene and a polar monomer, e.g., α,β-ethylenically-unsaturated C ₃ - Cs carboxylic acid ("ethylene-acid copolymers"), or ester thereof, or an ethylenically unsaturated ester of a carboxylic acid may be employed as the Polyolefins or may be blended with the Polyolefins. By "direct copolymer", it is meant that the copolymer is made by polymerization of monomers together at the same time, as distinct from a "graft copolymer" where a monomer is attached or polymerized onto an existing polymer chain. Preparation of the direct ethylene-acid copolymers is described in U.S. Pat. No. 4,351,931.

The ethylene-acid copolymers can be E/X/Υ copolymers where E is ethylene; X is a modifying comonomer and Y is the α,β-ethylenically-unsaturated C3- Ce carboxylic acid, particularly acrylic or methacrylic acid, or ester thereof. Preferably, however, the ethylene-acid copolymer is a dipolymer (no modifying comonomer). The preferred acid moieties are methacrylic acid and acrylic acid. . Suitable modifying comonomers (X) are selected from alkyl acrylate and alkyl

methacrylate, the alkyl groups having from 1 - 12 carbon atoms, which, when present, may be up to 30 (preferably up to 25, most preferably μp to 15) wt.% of the ethylene-acid copolymer. X may also be vinyl acetate or carbon monoxide.

A wide range of percent acid moiety in the ethylene-acid copolymer may be used. The acid moiety may be present in a range of about 1 to 30 weight percent of the acid copolymer, preferably in a range of about 5 to 25, alternatively about 10 to about 20. The ethylene-acid copolymers with high levels of acid are difficult to prepare in continuous polymerizers because of monomer-polymer phase separation. This difficulty can be avoided however by use of "cosolvent technology" as described in U.S. Pat. No. 5,028,674 or by employing somewhat higher pressures than those at which copolymers with lower acid can be prepared.

Examples of such copolymers include ethylene/acrylic acid copolymers, ethylene/methacrylic acid copolymers, ethylene/itaconic acid copolymers, ethylene/alkyl acrylate copolymers and ethylene/alkyl methacrylate copolymers especially where the alkyl group is methyl, ethyl, propyl or butyl, and ethylene vinyl acetate copolymers.

Specific other copolymers include ethylene/alkyl acrylate/acrylic acid, ethylene/alkyl acrylate/methacrylic acid, ethylene/alkyl acrylate/maleic anhydride, and ethylene alkyl methacrylate/maleic anhydride, wherein the alkyl group can have 1-10 carbon atoms, preferably n-butyl, iso butyl, or methyl, ethylene/vinyl acetate/methacrylic acid, ethylene/vinyl acetate/maleic anhydride, ethylene vinyl acetate/carbon monoxide, ethylene/alkyl acrylate/carbon monoxide, ethylene/alkyl methacrylate/carbon monoxide, ethylene/carbon monoxide/acrylic acid, ethylene/vinyl tri-alkoxy silane, ethylene/vinyl acetate tri-alkoxy silane, ethylene/alkyl acrylate/vinyl tri-alkoxy silane, ethylene/vinyl acetate/glycidyl methacrylate, ethylene/glycidyl methacrylate, ethylene/alkyl acrylate/glycidyl methacrylate and ethylene/alkyl methacrylate/glycidyl methacrylate where the alkyl or alkoxy group can have 1-10 carbon atoms.

In the alternate embodiments, ionomeric copolymers may be employed as the Polyolefins or may be blended therewith. These ionomers are derived from direct copolymers of ethylene and ethylene-acid copolymers by neutralization with metal ions. Methods of preparing such ionomers are well known and are described in U.S. Pat. No. 3,264,272. The ethylene-acid copolymers are partially neutralized (15 to 75 percent) with metal cations, particularly monovalent and/or bivalent metal cations. Preferably about 25 to about 60 of the acid is neutralized. Preferred metal cations include lithium, sodium, and zinc, or a combination of such cations. Zinc is most preferred.

Further, graft copolymers or blends of graft copolymers of polyolefins may be used as the Polyolefin, either by themselves or blended with the Polyolefins, ethylene/polar-monomer direct copolymers, or inomeric copolymers. These graft copolymers are made by means well known in the art with one or more graft monomers. The graft monomers can be selected from the group consisting of ethylenically unsaturated acidic monomers and their derivatives including acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid, crotonic acid, 5- norbornene-2,3-dicarboxylic acid, maleic anhydride, monosodium maleate, disodium maleate, itaconic anhydride, citraconic anhydride, monomethyl fumarate and monomethyl maleate. Also, the graft monomers can be selected from ethylenically unsaturated monomers containing amino or hydroxy functional groups including vinyl pyridines, vinyl silanes, 4-vinyI pyridine, vinyltriethoxysilane, and hydroxy ethyl methacrylate. The graft monomers can also include styrene and glycidyl methacrylate. The grafting monomers, and mixtures thereof, can be present in the graft polymer in an amount of about 0.05 to about 5 weight percent. Preferred polyolefins for grafting include polyethylene, polypropylene, ethylene propylene diene terpolymer and copolymers of ethylene with vinyl acetate, carbon monoxide, or ethylenically unsaturated carboxylic acids or esters thereof. "Polysiloxane" means a dimethyl polysiloxane having functional end groups. The preferred functional end group is a hydroxyl group. Such dimethyl polysiloxanes are commercially available, for example as silanol-terminated dimethyl polysiloxane from Huls America Inc., U.S.A. under the trade name OHEB. However, dimethyl polysiloxanes having other terminal groups that are reactable with vinyl silanes, especially when grafted onto polyolefins, may be used, e.g., polysiloxanes with amine, epoxy, methoxy groups or the like. In addition, the Polysiloxane may be a moisture-crosslinkable polysiloxane, in which event the amount of vinyl silane used in the manufacture of the release film may be lowered. In preferred embodiments, the dimethyl polysiloxane is of the formula: Me

HO - (SiO)π - H

I

Me where Me = methyl and n is the range of 100 to 100,000.

"Organic Peroxides", which serve as grafting agents in the present invention, are known in the art and include di-tertiary alkyl peroxides, especially dicumyl peroxide, which is available under the trade name LUPEROX® 500, and 2,5-dimethyl-2,5-di(t-butylperoxy) hexane, or Lupersol® 101. Other organic peroxides include acetylenic diperoxy compounds especially 2,5-dimethyl-2,5-di(t- butylperoxy) hexyne-3, which is available under the trade names LUPERSOL® 130, . Other organic peroxides include peroxyesters, preferably t-amyl peroxypivalate and t-butyl peroxypivalate, peroxydicarbonates, preferably di(sec- butyl)peroxydicarbonate, and acylperoxides, preferably dibenzoyl peroxide . The grafting agent serves to graft a portion of the vinyl silane onto the polyolefin. Absence of grafted vinyl silane may adversely affect properties of the films, especially the processability of the compositions that form the films.

"Vinyl Silane Compounds" are known in the art and include vinyl trimethoxy silane, vinyl triethoxy silane, vinyl triacetoxy silane, trisbutanoxime vinyl silane, divinyl tetramethoxy disiloxane, hexamethyl bisdimethyiaminoxy cyclotetrasiloxane and the like. Mixtures of such silanes may be used.

"Organo-metallic Moisture Curing Agents" are known in the art, and for use in the present invention, will typically be organo-tin or organo-titanium compounds. The preferred cross-linking agent is dibutyl tin dilaurate. Compositions containing vinyl silane, organic peroxide and cross-linking agent are available under the trade name SILCAT®R, which is believed to contain vinyl trimethoxy silane, dicumyl peroxide and dibutyl tin dilaurate.

"UHMW Silicone Polymer" means an ultrahigh molecular weight silicone polymer with a molecular weight range from about 250,000 to about 1 million. The UHMW Silicone Polymer will have a viscosity in the range of about 10 million to about 50 million centistokes. It may preferably be used in the form of a masterbatch in a polyolefin carrier resin, typically about 25 to about 50 weight % UHMW Silicone Polymer in a suitable polyolefin carrier resin such as LDPE or PP. Alternatively, the UHMW Silicone Polymer may be made "in situ" by crosslinking vinyl silane with Polysiloxane.

"Tie Layer" means an extrudable adhesive layer well known in the art selected for its capability to bond a core layer to outer layers. Examples of such adhesive, tie layer polymer are based on either polyethylene or ethylene vinyl acetate copolymers. Ethylene-based and propylene-based homopolymers and copolymers, modified to enhance adhesion, are marketed by E. I. du Pont de Nemours and Company under the tradename, BYNEL®. They are typically modified with carboxyl groups such as anhydride.

The silicone-containing resin or film mad therefrom of the present invention comprises

1. polyolefin homopolymer or copolymer of unsaturated hydrocarbons having 2 - 20 carbon atoms, particularly homopoiymers of ethylene or propylene or copolymers of ethylene with alpha-olefin hydrocarbons having 3 - 10 carbon atoms, especially butene-1 and octene-1,

2. dimethyl polysiloxane having functional end groups, preferably a hydroxyl end group, the polysiloxane preferably being of the formula,

Me

HO - (SiO)n - H

Me where Me = methyl and n is the range of 100 to 100,000, 3. vinyl silane compound, preferably one selected from the group consisting of vinyl trimethoxy silane, vinyl triethoxy silane, vinyl triacetoxy silane, trisbutanoxime vinyl silane, divinyl tetramethoxy disiloxane, and hexamethyl bisdimethyiaminoxy cyclotetrasiloxane and mixtures thereof, and

4. ultra-high molecular weight silicone polymer having a molecular weight range from about 250,000 to about 1 million, preferably having a viscosity in the range of about 10 million to about 50 million centistokes, plus optionally

5. organic peroxide grafting agent, preferably one selected from the group consisting of di-tertiary alkyl peroxides, especially dicumyl peroxide and 2,5- dimethyl-2,5-di(t-butylperoxy) hexane; acetylenic diperoxy compounds, especially 2,5-dimethyl-2,5-di(t-butylperoxy) hexyne-3; peroxyesters, especially t-amyl peroxypivalate and t-butyl peroxyprivalate; peroxydicarbonates, especially di(sec-butyl) peroxydicarbonate; and acylperoxides, especially dibenzoyl peroxide to graft a portion of the vinyl silane onto the polyolefin, and

6. organo-metallic moisture curing agent, preferably an organo-tin compound, more preferably dibutyl tin dilaurate, or an organo-titanium compound.

Preferably, the silicone-containing resin or film made therefrom comprises, based on total weight of polymer components,

1. about 85 to about 98.89% (preferably about 91.0 to about 95.9%) polyolefin homo or copolymer,

2. about 1 to about 10% (preferably about 3 to about 7%) dimethyl polysiloxane having functional end groups,

3. about 0.01 to about 1.0% (preferably about 0.01 to about 0.5%) vinyl silane compound, and 4. about 0.1 to about 5% (preferably about 0.25 to about 3%) ultra-high molecular weight silicone polymer, plus

5. about 1 to about 100 parts per million (preferably about 5 to about 75 parts per million), based on weight of total polymer, of organic peroxide grafting agent, and 6. about 1 to about 100 parts per million (preferably about 3 to about 50 parts per million), based on weight of total polymer, of organo-metallic moisture curing agent.

Preferably, the amount of organic peroxide is sufficiently low that not all of the vinyl silane compound grafts to the polyolefin under grafting conditions. Expressed in an alternative way, conditions (i.e. process parameters and feed rates) are chosen such that only a portion of the vinyl silane is grafted to the polyolefin leaving some free vinyl silane after grafting.

Polyolefins used preferably are copolymers of ethylene with a hydrocarbon alpha-olefin having from 4 - 8 carbon atoms and having a density in the range of about 0.850 to about 0.970 grams per cubic centimeter (g/cm.3) and especially in the range of 0.920 to 0.930 g/cm Preferably, the polymers have a melt index (MI) in the range of 0.05 to 120 dg/min, especially 0.1 to 75 dg/min and in particular in the range of 1 to 10 dg/min. (as measured per ASTM D-1238, condition E). The present invention is a multi-layer structure which comprises a subweb as layer (a) and the silicone-containing polyolefin film or this invention as layer (b) placed on the subweb. Layer (a) will typically have a thickness of about 10 to about 100 microns (micrometers), preferably from about 15 to about 25 microns. Layer (b) will typically have a thickness of about 1 to about 10 microns, preferably from about 2 to about 6 microns. Particularly, if it is desired to prevent migration of silicone through layer (a), layer (b) preferably should have lower thickness, say about 1 to about 3 microns.

Layer (a), the subweb, may be any subweb known in the art suitable for coating or being laminated to the silicone-containing polymer of layer (b). In particular, the subweb may be paper particularly kraft paper, non-wovens, metal foil such as steel or aluminum, plastics such as nylon and polyesters particularly

polyethylene terephthalate, or other subwebs suitable for coating. Preferably, the subweb is a Polyolefin, particularly the same Polyolefin used in the film of layer (b). The multi-layer film wherein the subweb is Polyolefin can be used in liquid- absorbing products, such as feminine hygiene pads, baby diapers and incontinence products.

The silicone-containing polyolefin film of this invention preferably is surface treated, preferably by a corona discharge. The corona discharge is applied after formation of the film, preferably shortly after formation of the film, e.g., prior to the film being wound up, and prior to the film being subjected to significant amounts of moisture. In preferred embodiments, the corona discharge is formed between two elongated electrodes, using techniques that are known to those skilled in the art, at a sufficient level to improve the release properties of the film. The film is passed between the electrodes while the corona discharge is formed between the electrodes. Subjecting the silicone-containing polyolefin film to a corona discharge results in a release film having superior release characteristics compared with film that has not been so treated. The film may conveniently be treated at the speeds at which film is extruded from an extruder in the manufacture thereof. Other techniques for chemically activating the surface of the film, such as flame treatment and plasma discharge, may be used in place of corona discharge. Such techniques and the associated equipment are known to those skilled in the art.

The corona-discharge treated films of the present invention may be used in a variety of end-uses. For example, the film may be in the form of a film that is peelable from another substrate. Such films usually require that the layer of adhesive material be readily removed from the release film and then the layer be adhered to another substrate. In addition, multi-layer films wherein layer (a) is a Polyolefin may be perforated using known techniques and employed in the aforementioned feminine hygiene pads, baby diapers and incontinence products.

Processes for the manufacture of films of the type described above are known, including blowing, casting and extruding. Optionally, films can be monaxially or biaxially oriented using methods known in the art to improve properties and reduce thickness. Multi-layer films preferably are made by coextrusion of layer (a) and layer (b). In such coextrusions, using polyolefin as an example of layer (a), this first polyolefin is fed to one extruder to form layer (a), and a second polyolefin, dimethyl polysiloxane, vinyl silane compound, ultra-high molecular weight silicone polymer, organic peroxide grafting agent and organo- metallic moisture curing agent is fed in a suitable manner to a second extruder to

form layer (b). The second extruder should be capable of forming a uniform mixture of such components and of extruding a uniform mixture in the form of a molten web so as to form a uniform film, which may be in the form of a sheet or a coating on layer (a). The process should be operated in the absence of excessive moisture prior to the extrusion of the composition from the extruder, to reduce premature cross-linking reactions of the vinyl silane.

In circumstances where the silicone-containing polyolefin will not effectively adhere to the substrate desired for layer (a), layer (b) may be coextruded with a tie layer between layer (a) and layer (b). The components that form the layer (b) may be fed to the extruder in a number of ways. For instance, all components may be fed to the hopper of the extruder, using suitable carrier materials where appropriate, as is described in greater detail below. In alternative procedures, some of the components may be fed through the hopper of the extruder and the remainder fed directly into the extruder. For example, the polyolefin may be fed to the hopper and heated in the extruder until in a molten condition. Subsequently, the remaining ingredients may be introduced into the extruder by means of suitable feed ports on the extruder. For instance, the remaining ingredients may be fed into a cavity transfer mixer located in the extruder after the barrel of the extruder containing the extruder screw and prior to the extrusion die or other orifice through which the polymer is extruded. Cavity transfer mixers are known and are used for admixing of two or more materials in an extruder immediately prior to extrusion. Alternatively, the remaining ingredients may be introduced into the extruder through a gear pump, which is also known for the introduction of ingredients into an extruder. As a further example, a composition of polyolefin, dimethyl polysiloxane, and vinyl silane compound, plus organic peroxide grafting agent and organo-metallic moisture curing agent if used, may be melt-blended as one component in a twin- screw extruder, and allowed to age (cure) for a sufficient time prior to pellet (dry blending) or melt blending with a melt-blended composition of polyolefin and dimethyl polysiloxane, as well as with the ultra-high molecular weight silicone polymer , all of which in combination form the composition of layer (b) to be extruded. This final composition for layer (b) can be extruded using a single-screw extruder.

In addition, the aforementioned composition for forming layer (b) may be blended with any polyolefin compatible with polyolefin used to make layer (b), for example low density polyethylene (LDPE), without adversely effecting the properties of the resulting film. Such blending can range from 0.1 parts to 1.5

parts LDPE to 1 part layer (b) composition. Other additives as defined above may also be added.

A suitable procedure for extruding a film according to the present invention is as follows: a first polyolefin is fed to a first extruder; and simultaneously, a second modified polyolefin is fed to a second extruder through the hopper of the extruder. The modified polyolefin in the second extruder is preferably a blend of two or more compositions, which in combination form the composition to be extruded, and is heated in the extruder to form molten polymer. Thus, for the modified polyolefin in the second extruder, a composition of polyolefin, dimethyl polysiloxane, and vinyl silane compound, plus organic peroxide grafting agent and organo-metallic moisture curing agent if used, may be melt-blended as one component in a twin-screw extruder and allowed to cure for a sufficient amount of time prior to dry blending or melt blending with a composition of polyolefin and dimethyl polysiloxane, as well as with the ultra-high molecular weight silicone polymer. This final blend can be extruded into film using a single- screw extruder. It is important that the introduction of the components of the composition and the mixing capabilities of the apparatus being used be such that a uniform mixture be formed in the extruder and extruded therefrom.

If the components are fed in part directly into the extruder, e.g., using a cavity transfer mixer, then higher levels of, for example, dimethyl polysiloxane may be used at levels up to about 15%, which may be advantageous to the properties of the product that is obtained.

Examples

The invention is illustrated through the following examples, wherein: • Component A is polydimethyl siloxane, silanol terminated, 1000 centistokes (cSt)

• Component B is SILFIN® 6, a proprietary mixture of vinyl trimethoxy silane, organic peroxide and organic tin curing accelerator. SILFIN® 6 is made by Hϋls. • Component C is vinyl triethoxy silane.

• Component D is UHMW Silicone Polymer with a viscosity in the range of 10 to 50 million centistokes as a 25 % masterbatch in LDPE.

Example 1

A two-layer film was made by a blown-film process using a 200 mm diameter die and a blow-up ratio of 2.1 : 1 and a film line speed of about 14

meters/minute. Employing two 50 mm extruders, layer (a), a 23 micron thick film of a 5 MI LDPE, was extruded at 180 - 190°C at an extruder RPM of 40, and layer (b), a 5 micron film formed from a dry pellet blend of 50% 5 MI LDPE + 50% (10 MI LLDPE + 6 % component A + 160 ppm component B and 240 ppm component C) by melt-blending in the extruder, was extruded at 160 - 170°C at an extruder RPM of 8. The film was corona treated on the layer (b) side.

The resulting film had film thickness variations of +/- 15%. Surface tension on the 5 micron side of the film was 25 dynes/cm, but silicone was found to have also migrated through layer (a) of the film to the opposite side. The film was tested using a modified TAPPI UM502 test wherein the film (surface of layer (b)) was placed on the adhesive tape of a commercial sanitary napkin and heat-aged for 20 hours at 70°C. The film release force from the adhesive was about 50 grams/inch. The adhesive release force from a stainless steel plate (after the film was peeled off the adhesive tape) was 50 - 60 grams inch. Silicon was found to have migrated from the film surface into the adhesive.

Example 2

A two-layer blown film construction was made on the same equipment and under the same conditions as Example 1. Layer (a) was a 23 micron film of a 5 MI LDPE. Layer (b) was a 2 micron film formed from of a blend of: 70 % (10 MI LLDPE + 6 % component A + 160 ppm component B + 240 ppm component C), 25 % 5 MI LDPE, and 5 % component D. The film was corona treated on layer (b) side at the same level of discharge as in Example 1. This film extruded stabily. The resulting film thickness variations were +/- 5%. Surface tension on the 2 micron side was found to be 25 dynes cm. No silicone was found to have migrated through layer (a) of the film. Using the same adhesive test as in Example 1, the film release force from the adhesive was about the same as in Example 1 (50 grams/inch). The release force of the adhesive from the stainless steel plate (after the film was peeled off the adhesive tape), however, was about 150 - 200 grams/inch, indicating significant reduction of silicone migration into the adhesive.