Title:
SILK COATED FABRICS AND PRODUCTS AND METHODS OF PREPARING THE SAME
Document Type and Number:
WIPO Patent Application WO/2019/067745
Kind Code:
A1
Abstract:
Silk coated and/or infused performance materials, apparel, and methods of preparing the same are disclosed herein. In some embodiments, silk performance apparel includes textiles, fabrics, consumer products, and other materials that are coated with aqueous solutions of pure silk fibroin-based protein fragments having low, medium, and/or high molecular weight in various ratios.

Inventors:
ALTMAN GREGORY (US)
MORTARINO ENRICO (US)
JOHNSON SARA (US)
UFRET MARIA (US)
KRIKORIAN MARKRETE (US)
LACOUTURE REBECCA (US)
Application Number:
PCT/US2018/053163
Publication Date:
April 04, 2019
Filing Date:
September 27, 2018
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
SILK INC (US)
International Classes:
C09D189/00; C07K14/435; D01F4/02; D06M15/15
Domestic Patent References:
WO2017011679A12017-01-19
WO2014145002A22014-09-18
WO2015061079A12015-04-30
WO2004073644A22004-09-02
WO2011069643A22011-06-16
Foreign References:
US20110111031A12011-05-12
US20160222579A12016-08-04
US7115388B22006-10-03
US20160263228A12016-09-15
Other References:
See also references of EP 3688018A4
Attorney, Agent or Firm:
GHIDU, Victor, P. et al. (US)
Download PDF:
Claims:
CLAIMS

1. A material comprising one or more fibers comprising a protein, wherein a substantial portion of fibers are coated with silk fibroin-based protein fragments.

2. The material of claim 1, wherein the material comprises one or more of a woven material, a non-woven material, a knit material, and a crochet material.

3. The material of claim 1, wherein the material comprises fabric, thread, yarn, fiber, or a combination thereof.

4. The material of any one of claims 1-3, wherein the material comprises keratin.

5. The material of any one of claims 1-4, wherein the material comprises one or more of natural wool, synthetic wool, alpaca fleece, alpaca wool, lama fleece, lama wool, cashmere, sheep fleece, sheep wool, mohair wool, camel hair, or angora wool.

6. The material of any one of claims 1-5, wherein the silk fibroin-based protein fragments comprise one or more of low molecular weight silk fibroin-based protein fragments, medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments.

7. The material of any one of claims 1-6, wherein the silk fibroin-based protein fragments have an average molecular weight from about 1 kDa to about 350 kDa.

8. The material of any one of claims 1-7, wherein the silk fibroin-based protein fragments have a polydispersity from about 1.5 to about 3.0.

9. A method of making a silk fibroin coated material, comprising:

preparing a silk fibroin solution comprising low molecular weight silk fibroin- based protein fragments; coating a surface of the material with the silk fibroin solution; and drying the surface of the material that has been coated with the silk fibroin solution to provide the silk fibroin coated material.

10. A method of improving hand in a material, comprising:

preparing a silk fibroin solution comprising low molecular weight silk fibroin- based protein fragments;

coating a surface of the material with the silk fibroin solution; and

drying the surface of the material that has been coated with the silk fibroin solution; wherein the resulting coated material has an improved hand compared to the uncoated material.

11. A method of improving hand retention on laundering in a material, comprising: preparing a silk fibroin solution comprising low molecular weight silk fibroin- based protein fragments;

coating a surface of the material with the silk fibroin solution; and

drying the surface of the material that has been coated with the silk fibroin solution; wherein upon laundering, the coated material retains a substantial portion of its initial hand prior to laundering.

12. A method of improving size and/or shape retention on laundering in a material, comprising:

preparing a silk fibroin solution comprising low molecular weight silk fibroin- based protein fragments;

coating a surface of the material with the silk fibroin solution; and

drying the surface of the material that has been coated with the silk fibroin solution; wherein upon laundering, the coated material substantially retains its initial size and/or shape prior to laundering.

13. A method of improving pilling resistance in a material, comprising: preparing a silk fibroin solution comprising low molecular weight silk fibroin- based protein fragments;

coating a surface of the material with the silk fibroin solution; and

drying the surface of the material that has been coated with the silk fibroin solution; wherein the coated material has an improved pilling resistance compared to a similar material which was not so coated.

14. A method of improving water repellency in a material, comprising:

preparing a silk fibroin solution comprising low molecular weight silk fibroin- based protein fragments;

coating a surface of the material with the silk fibroin solution; and

drying the surface of the material that has been coated with the silk fibroin solution; wherein the coated material has an improved water repellency compared to a similar material which was not so coated.

15. The method of any one of claims 9-14, further comprising an additional treatment step.

16. The method of claim 15, wherein the additional treatment step is a pre-treatment step, a post treatment step, or a final treatment step.

17. The method of claim 15, wherein the additional treatment step comprises an acidic treatment or an alcohol treatment. 18. The method of any one of claims 9-17, wherein the silk fibroin solution further comprises medium molecular weight silk fibroin-based protein fragments.

19. The method of claim 18, wherein the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 90: 10, about 80:20, about 75:25, about 70:30, about 66:34, about 60:40, about 50:50, about 40:60, about 34:66, about 30:70, about 25:75, about 20:80, or about 10:90.

20. The method of claim 18, wherein the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 3 : 1.

21. The method of any one of claims 9-17, wherein the silk fibroin solution further comprises high molecular weight silk fibroin-based protein fragments.

22. The method of any one of claims 9-17, wherein the silk fibroin solution further comprises medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments. 23. The method of any one of claims 9-22, wherein drying the surface of the material comprises heating the surface of the material without substantially modifying silk fibroin coating performance.

24. The method of any one of claims 9-23, wherein the silk fibroin solution comprises silk fibroin-based protein fragments at less than about 0.001% by volume (v/v).

25. The method of any one of claims 9-23, wherein the silk fibroin solution comprises silk fibroin-based protein fragments at less than about 0.1% by volume (v/v). 26. The method of any one of claims 9-23, wherein the silk fibroin solution comprises silk fibroin-based protein fragments at less than about 1% by volume (v/v).

27. The method of any one of claims 9-23, wherein the silk fibroin solution comprises silk fibroin-based protein fragments at less than about 2.5% by volume (v/v).

28. The method of any one of claims 9-23, wherein the silk fibroin solution comprises silk fibroin-based protein fragments at less than about 5% by volume (v/v).

29. The method of any one of claims 9-23, wherein the silk fibroin solution comprises silk fibroin-based protein fragments at about 0.5% by v/v, w/w, or w/v.

30. The method of any one of claims 9-29, wherein the silk fibroin solution comprises a Bransted acid. 31. The method of any one of claims 9-30, wherein the silk fibroin solution comprises one or more of citric acid and acetic acid.

32. The method of any one of claims 9-31, wherein the material comprises one or more of a woven material, a non-woven material, a knit material, and a crochet material.

33. The method of any one of claims 9-32, wherein the material comprises fabric, thread, yarn, fiber, or a combination thereof.

34. The method of any one of claims 9-32, wherein the material comprises keratin.

35. The method of claim 34, wherein the material comprises one or more of natural wool, synthetic wool, alpaca fleece, alpaca wool, lama fleece, lama wool, cashmere, sheep fleece, sheep wool, mohair wool, camel hair, angora wool. 36. A method of making a silk fibroin coated material, comprising:

preparing a silk fibroin solution comprising low molecular weight silk fibroin- based protein fragments;

coating a surface of a synthetic material with the silk fibroin solution; and drying the surface of the synthetic material that has been coated with the silk fibroin solution to provide the silk fibroin coated material.

37. The method of claim 36, wherein the silk fibroin solution further comprises medium molecular weight silk fibroin-based protein fragments.

38. The method of claim 36, wherein the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 90: 10, about 80:20, about 75:25, about 70:30, about 66:34, about 60:40, about 50:50, about 40:60, about 34:66, about 30:70, about 25:75, about 20:80, or about 10:90. 39. The method of claim 38, wherein the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 3 : 1.

40. The method of claim 36, wherein the silk fibroin solution further comprises high molecular weight silk fibroin-based protein fragments.

41. The method of claim 36, wherein the silk fibroin solution further comprises medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments.

42. The method of any one of claims 36 to 41, wherein drying the surface of the material comprises heating the surface of the material without substantially modifying silk fibroin coating performance. 43. The method of any one of claims 36 to 42, wherein the silk fibroin solution comprises silk fibroin-based protein fragments between 0.01% and 1% volume (v/v).

44. The method of any one of claims 36 to 42, wherein the silk fibroin solution comprises silk fibroin-based protein fragments at about 0.25% by volume (v/v).

45. The method of any one of claims 36 to 44, wherein the polydispersity of the silk fibroin-based protein fragments is between 1.5 and 3.

46. The method of any one of claims 36 to 45, wherein the silk fibroin solution further comprises a Bransted acid.

47. The method of any one of claims 36 to 45, wherein the silk fibroin solution further comprises one or more of citric acid and acetic acid. 48. The method of any one of claims 36 to 47, wherein the silk fibroin solution has an acidic pH.

49. The method of any one of claims 36 to 48, wherein the silk fibroin solution has a pH between 4 and 5.

50. The method of any one of claims 36 to 49, further comprising coating the material with a silicone solution.

51. The method of claim 50, wherein the silicone solution has an acidic pH.

52. The method of any one of claims 36 to 51, wherein the silk fibroin solution coating precedes the silicone solution coating.

53. The method of any one of claims 36 to 52, wherein the synthetic material comprises one or more of a woven material, a non-woven material, a knit material, and a crochet material.

54. The method of any one of claims 36 to 53, wherein the synthetic material comprises fabric, thread, yarn, or a combination thereof.

55. The method of any one of claims 36 to 54, wherein the synthetic material comprises one or more of polyester, polyamide, polyaramid, polytetrafluoroethylene, polyethylene, polypropylene, polyurethane, silicone, mixtures of polyurethane and polyethyleneglycol, ultrahigh molecular weight polyethylene, high-performance polyethylene, nylon, and LYCRA.

56. A method of improving hand in a synthetic material, comprising:

coating a surface of the synthetic material with a silk fibroin solution comprising low molecular weight silk fibroin-based protein fragments;

drying the synthetic material; and

coating a surface of the synthetic material with a silicone solution;

wherein the resulting coated material has an improved hand compared to the uncoated material.

57. A method of improving hand retention on laundering in a synthetic material, comprising:

coating a surface of the synthetic material with a silk fibroin solution comprising low molecular weight silk fibroin-based protein fragments;

drying the synthetic material; and

coating a surface of the synthetic material with a silicone solution;

wherein upon laundering, the coated synthetic material retains at least about 80% of its initial hand prior to laundering.

58. A method of improving the water drop absorption time of a synthetic material, comprising:

coating a surface of the synthetic material with a silk fibroin solution comprising low molecular weight silk fibroin-based protein fragments;

drying the synthetic material; and

coating a surface of the synthetic material with a silicone solution;

wherein the resulting coated synthetic material has an improved water drop absorption time compared to the uncoated material.

59. A method of improving the abrasion resistance of a synthetic material, comprising: coating a surface of the synthetic material with a silk fibroin solution comprising low molecular weight silk fibroin-based protein fragments;

drying the synthetic material; and

coating a surface of the synthetic material with a silicone solution;

wherein the resulting coated synthetic material has an improved abrasion resistance compared to the uncoated material. 60. The method of any one of claims 56 to 59, wherein the silk fibroin solution further comprises medium molecular weight silk fibroin-based protein fragments.

61. The method of claim 60, wherein the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 90: 10, about 80:20, about 75:25, about 70:30, about 66:34, about 60:40, about 50:50, about 40:60, about 34:66, about 30:70, about 25:75, about 20:80, or about 10:90.

62. The method of claim 60, wherein the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 3 : 1.

63. The method of any one of claims 56 to 59, wherein the silk fibroin solution further comprises high molecular weight silk fibroin-based protein fragments.

64. The method of any one of claims 56 to 59, wherein the silk fibroin solution further comprises medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments.

65. The method of any one of claims 56 to 64, wherein drying the surface of the material comprises heating the surface of the material without substantially modifying silk fibroin coating performance. 66. The method of any one of claims 56 to 65, wherein the silk fibroin solution comprises silk fibroin-based protein fragments between 0.01% and 1% volume (v/v).

67. The method of any one of claims 56 to 65, wherein the silk fibroin solution comprises silk fibroin-based protein fragments at about 0.25% by volume (v/v).

68. The method of any one of claims 56 to 67, wherein the polydispersity of the silk fibroin-based protein fragments is between 1.5 and 3.

69. The method of any one of claims 56 to 68, wherein the silk fibroin solution further comprises a Bransted acid.

70. The method of any one of claims 56 to 68, wherein the silk fibroin solution further comprises one or more of citric acid and acetic acid. 71. The method of any one of claims 56 to 68, wherein the silk fibroin solution has an acidic pH.

72. The method of any one of claims 56 to 71, wherein the silk fibroin solution has a pH between 4 and 5.

73. The method of any one of claims 56 to 72, wherein the silicone solution has an acidic pH.

74. The method of any one of claims 56 to 73, wherein the silk fibroin solution coating precedes the silicone solution coating.

75. The method of any one of claims 56 to 74, wherein the material comprises one or more of a woven material, a non- woven material, a knit material, and a crochet material.

76. The method of any one of claims 56 to 75, wherein the material comprises fabric, thread, yarn, or a combination thereof.

77. The method of any one of claims 56 to 76, wherein the material comprises one or more of polyester, polyamide, polyaramid, polytetrafluoroethylene, polyethylene, polypropylene, polyurethane, silicone, mixtures of polyurethane and polyethyleneglycol, ultrahigh molecular weight polyethylene, high-performance polyethylene, nylon, and LYCRA.

78. A method of making a silk fibroin coated material, comprising:

preparing a silk fibroin solution comprising low molecular weight silk fibroin- based protein fragments;

coating a surface of the material with the silk fibroin solution; and

drying the surface of the material that has been coated with the silk fibroin solution to provide the silk fibroin coated material. 79. The method of claim 78, wherein the silk fibroin solution further comprises medium molecular weight silk fibroin-based protein fragments.

80. The method of claim 79, wherein the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 90: 10, about 80:20, about 75:25, about 70:30, about 66:34, about 60:40, about 50:50, about 40:60, about 34:66, about 30:70, about 25:75, about 20:80, or about 10:90.

81. The method of claim 79, wherein the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 3 : 1.

82. The method of claim 78, wherein the silk fibroin solution further comprises high molecular weight silk fibroin-based protein fragments. 83. The method of claim 78, wherein the silk fibroin solution further comprises medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments.

84. The method of any of claims 78 to 83, wherein drying the surface of the material comprises heating the surface of the material without substantially modifying silk fibroin coating performance.

85. The method of any of claims 78 to 84, wherein the silk fibroin solution comprises silk fibroin-based protein fragments at less than about 0.001% by volume (v/v).

86. The method of any of claims 78 to 84, wherein the silk fibroin solution comprises silk fibroin-based protein fragments at less than about 0.1% by volume (v/v).

87. The method of any of claims 78 to 84, wherein the silk fibroin solution comprises silk fibroin-based protein fragments at less than about 1% by volume (v/v).

88. The method of any of claims 78 to 84, wherein the silk fibroin solution comprises silk fibroin-based protein fragments at less than about 2.5% by volume (v/v). 89. The method of any of claims 78 to 84, wherein the silk fibroin solution comprises silk fibroin-based protein fragments at less than about 5% by volume (v/v).

90. The method of any one of claims 78 to 89, wherein the step of preparing the silk fibroin solution comprises adding a chemical fabric softener to the solution.

91. The method of any one of claims 78 to 90, wherein the silk fibroin solution comprises a Bransted acid.

92. The method of any one of claims 78 to 91, wherein the silk fibroin solution comprises one or more of citric acid and acetic acid.

93. The method of any one of claims 78 to 92, wherein the step of coating a surface of the material comprises one or more of a roller application process, a saturation and removal process, and a topical application process.

94. The method of any one of claims 78 to 93, wherein the step of coating a surface of the material comprises one or more of a bath coating process, a kiss rolling process, spray coating, and a two-sided rolling process. 95. The method of any one of claims 78 to 94, wherein the step of coating a surface of the material comprises coating one surface of the material.

96. The method of any one of claims 78 to 95, wherein the step of coating a surface of the material comprises coating two surfaces of the material.

97. The method of any one of claims 78 to 96, further comprising the step of dyeing the surface of the material.

98. The method of claim 97, wherein the step of dyeing the surface of the material occurs prior to coating a surface of the material with the silk fibroin solution.

99. The method of claim 97, wherein the step of dyeing the surface of the material occurs after coating a surface of the material with the silk fibroin solution. 100. The method of any one of claims 78 to 99, wherein the material comprises one or more of a woven material, a non- woven material, a knit material, and a crochet material.

101. The method of any one of claims 78 to 100, wherein the material comprises fabric, thread, yarn, or a combination thereof. 102. The method of any one of claims 78 to 101, wherein the material comprises one or more of polyester, polyamide, polyaramid, polytetrafluoroethylene, polyethylene, polypropylene, polyurethane, silicone, mixtures of polyurethane and polyethyleneglycol, ultrahigh molecular weight polyethylene, high-performance polyethylene, nylon, and LYCRA.

103. The method of any of claims 78 to 102, wherein the silk fibroin solution further comprises a chemical agent.

104. The method of claim 103, wherein the chemical agent is selected from the group consisting of silicone, an antimicrobial agent, an antifungal agent, a softener, a water repellant agent, an oil repellant agent, a dye, a flame retardant, a fabric softener, a pH adjusting agent, an anticrocking agent, an antipilling agent, and an antifelting agent.

105. The method of claim 103, wherein the chemical agent is selected to modify one or more of a first property and second property of the silk fibroin coated material.

106. The method of claim 105, wherein the first property comprises one or more of an antimicrobial property, antiodor property, a water repellant property, an oil repellant property, a flame retardant property, a coloring property, a fabric softening property, a stain repellant property, a pH adjusting property, an anticrocking property, an antipilling property, and an antifelting property.

107. The method of claim 105 or 106, wherein the second property comprises one or more of wetting time, absorption rate, spreading speed, accumulative one-way transport, and overall moisture management capability. A silk-coated article as described herein. 109. A silk composition as described herein.

Description:
SILK COATED FABRICS AND PRODUCTS AND

METHODS OF PREPARING THE SAME

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Patent Application

No. 62/564,228, filed on September 27, 2017, U.S. Provisional Patent Application No. 62/564,233, filed on September 27, 2017, U.S. Provisional Patent Application No. 62/564,239, filed on September 27, 2017, and U.S. Provisional Patent Application No. 62/597,898, filed on December 12, 2017, which are hereby incorporated by reference in their entirety.

FIELD OF THE INVENTION

In some embodiments, the invention relates to silk-coated performance materials, apparel, and products for use in home and automotive applications, such as fabrics coated with pure silk fibroin-based proteins or protein fragments thereof.

BACKGROUND OF THE INVENTION

Silk is a natural polymer produced by a variety of insects and spiders, and comprises a filament core protein, silk fibroin, and a glue-like coating consisting of a non-filamentous protein, sericin. Silk fibers are light weight, breathable, and hypoallergenic. Silk is comfortable when worn next to the skin and insulates very well; keeping the wearer warm in cold temperatures and is cooler than many other fabrics in warm temperatures.

SUMMARY OF THE INVENTION

In an embodiment, a method is provided for coating a material with silk fibroin that may include silk-based proteins or fragments thereof to provide a silk fibroin coated material, wherein the silk fibroin coated upon the silk fibroin coated material may be heat resistant to a selected temperature. In some embodiments, the method may include preparing a silk fibroin solution that may include a concentration of one or more of low molecular weight silk fibroin, medium molecular weight silk fibroin, and high molecular weight silk fibroin at less than about 1% by volume (v/v), or less than about 0.1% by volume (v/v), or less than about 0.01% by volume (v/v), or less than about 0.001% by volume (v/v). In some embodiments, the method may include, coating a surface of the material with the silk fibroin solution. In some embodiments, the method may include drying the surface of the material that has been coated with the silk fibroin solution to provide the silk fibroin coated material, wherein drying the surface of the material comprises heating the surface of the material without substantially decreasing silk fibroin coating performance.

In an embodiment, a method is provided for coating a textile with a silk fibroin solution that may include silk-based proteins or fragments thereof to provide a silk fibroin coated article, wherein the silk fibroin coated upon the silk fibroin coated article may be heat resistant to a selected temperature. In some embodiments, the method may include preparing the silk fibroin solution with one or more of low molecular weight silk fibroin, medium molecular weight silk fibroin, and high molecular weight silk fibroin. In some embodiments, the method may include acidically adjusting the pH of the silk fibroin solution with an acidic agent. In some embodiments, the method may include coating a surface of the textile with the silk fibroin solution. In some embodiments, the method may include drying the surface of the textile that has been coated with the silk fibroin solution to provide the silk fibroin coated article, wherein drying the surface of the textile comprises heating the surface of the textile without substantially decreasing silk fibroin coating performance.

In some embodiments, a method is provided for manufacturing a silk fibroin coated textile that may include selected fabric properties. In some embodiments, the method may include admixing silk-based proteins or fragments thereof with one or more chemical agents to provide a coating solution, wherein the one or more chemical agents may be selected to modify one or more of a first selected property and second selected property of the silk fibroin coated textile. In some embodiments, the method may include providing the coating solution to a textile to be coated with one or more of a bath coating process, a kiss rolling process, a spray process, and a two-sided rolling process. In some embodiments, the method may include removing excess coating solution from the silk fibroin coated textile. In some embodiments, the method may include heating the silk fibroin coated textile to modify a third selected property of the silk fibroin coated textile. In some embodiments, the first selected property may include one or more of an antimicrobial property, an antiodor property, a water repellant property, an oil repellant property, a flame retardant property, a coloring property, a fabric softening property, a stain repellant property, a pH adjusting property, an anticrocking property, an antipilling property, and an antifelting property. In some embodiments, the second selected property may include one or more of wetting time, absorption rate, spreading speed, accumulative one-way transport, drying rate, and overall moisture management capability. In some embodiments, the third selected property may include one or more of fabric hand, fabric stretch, fabric recovery, fabric stretch and recovery, and drapability.

In an embodiment, a selected property of the SFS coated articles that may be enhanced as compared to non-coated articles may include one or more of dimensional stability to laundering, dimensional stability to dry cleaning, appearance after laundering, appearance after dry cleaning, colorfastness to laundering, colorfastness to dry cleaning, colorfastness to non-chlorine bleach, seam torque/spirality (on knits), colorfastness to crocking, colorfastness to rubbing, colorfastness to water, colorfastness to light, colorfastness to perspiration, colorfastness to chlorinated pool water, colorfastness to sea water, tensile strength, seam slippage, tearing strength, seam breaking strength, abrasion resistance, pilling resistance, stretch recovery, bursting strength, colorfastness to die transfer in storage (labels), colorfastness to ozone, pile retention, bowing and skewing, colorfastness to saliva, snagging resistance, wrinkle resistance (e.g., appearance of apparel, retention of creases in fabrics, smooth appearance of fabrics), water repellency, water resistance, stain repellant (e.g., water repellency, oil repellency, water/alcohol repellency), vertical wicking, water absorption, dry rate, soil release, air permeability, wicking, antimicrobial properties, ultraviolet protection, resistance to torque, malodor resistant, biocompatibility, wetting time, absorption rate, spreading speed, accumulative one-way transport, flame retardant properties, coloring properties, fabric softening properties, a pH adjusting property, an antifelting property, and overall moisture management capability.

In an embodiment, the silk fibroin coated materials of the invention may be coated with one or more of low molecular weight silk, medium molecular weight silk, and high molecular weight silk to provide resulting coated materials having enhanced hydrophobic or hydrophilic properties.

In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yam, or a fabric, may be coated with compositions including one or more of low molecular weight silk, medium molecular weight silk, and high molecular weight silk, to provide resulting coated materials having enhanced hydrophobic or hydrophilic properties. In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yam, or a fabric, may be coated with compositions including low molecular weight silk and medium molecular weight silk. In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yarn, or a fabric, may be coated with compositions including low molecular weight silk and high molecular weight silk. In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yarn, or a fabric, may be coated with compositions including medium molecular weight silk and high molecular weight silk. In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yarn, or a fabric, may be coated with compositions including low molecular weight silk, medium molecular weight silk, and high molecular weight silk.

In and embodiment, materials coated by silk fibroin coatings described herein may include one or more of textiles, woven materials, non-woven materials, knit materials, crochet materials, and leather materials.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having an average number of amino acid residues of about 1 to 400 residues, or 1 to 300 residues, or 1 to 200 residues, or 1 to 100 residues, or 1 to 50 residues, or 5 to 25 residues, or 10 to 20 residues.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, and wherein the article is a fabric.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01% (w/w) to about 10% (w/w) sericin. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the silk based proteins or protein fragments thereof have an average weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof have a polydispersity of between about 1.5 and about 3.0, and wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yarn is selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is natural fiber or yam selected from the group consisting of cotton, silk, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is synthetic fiber or yam selected from the group consisting of polyester, nylon, poly ester- polyurethane copolymer, acrylic polymer or copolymer, rayon, i.e., semi-synthetic fiber made of modified cellulose, and combinations thereof. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the fabric exhibits an improved property, wherein the improved property is an accumulative one-way moisture transport index selected from the group consisting of greater than 40%, greater than 60%, greater than 80%, greater than 100%, greater than 120%, greater than 140%, greater than 160%, and greater than 180%. In an embodiment, the foregoing improved property is determined after a period of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the fabric exhibits an improved property, wherein the improved property is an accumulative one way transport capability increase relative to uncoated fabric selected from the group consisting of 1.2 fold, 1.5 fold, 2.0 fold, 3.0 fold, 4.0 fold, 5.0 fold, and 10 fold. In an embodiment, the foregoing improved property is determined after a period of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the fabric exhibits an improved property, wherein the improved property is an overall moisture management capability selected from the group consisting of greater than 0.05, greater than 0.10, greater than 0.15, greater than 0.20, greater than 0.25, greater than 0.30, greater than 0.35, greater than 0.40, greater than 0.50, greater than 0.60, greater than 0.70, and greater than 0.80. In an embodiment, the foregoing improved property is determined after a period of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric exhibits substantially no increase in microbial growth after a number of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the fabric exhibits substantially no increase in microbial growth after a number of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles, and wherein the microbial growth is microbial growth of a microbe selected from the group consisting of Staphylococcus aureus, Klebsiella pneumoniae, and combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the fabric exhibits substantially no increase in microbial growth after a number of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles, wherein the microbial growth is microbial growth of a microbe selected from the group consisting of Staphylococcus aureus, Klebsiella pneumoniae, and combinations thereof, wherein the microbial growth is reduced by a percentage selected from the group consisting of 50%, 100%, 500%, 1000%, 2000%, and 3000% compared to an uncoated fabric.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the coating is applied to the fabric at the fiber level prior to forming the fabric.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the coating is applied to the fabric at the fabric level. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is applied to the fabric at the fabric level, and wherein the fabric is bath coated.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is applied to the fabric at the fabric level, and wherein the fabric is spray coated.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is applied to the fabric at the fabric level, and wherein the fabric is coated with a stencil.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is applied to the fabric at the fabric level, wherein the coating is applied to at least one side of the fabric using a method selected from the group consisting of a bath coating process, a spray coating process, a stencil process, a silk-foam based process, and a roller-based process.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, and wherein the coating has a thickness of about one nanolayer.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, and wherein the coating has a thickness selected from the group consisting of about 5 nm, about 10 nm, about 15 nm, about 20 nm, about 25 nm, about 50 nm, about 100 nm, about 200 nm, about 500 nm, about 1 μηι, about 5 μηι, about 10 μηι, and about 20 μηι.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the coating is adsorbed on the fabric.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the coating is attached to the fabric through chemical, enzymatic, thermal, or irradiative cross-linking.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is applied to the fabric at the fabric level, and wherein the hand of the coated fabric is improved relative to an uncoated fabric.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is applied to the fabric at the fabric level, and wherein the hand of the coated fabric is improved relative to an uncoated fabric, wherein the hand of the coated fabric that is improved is selected from the group consisting of softness, crispness, dryness, silkiness, and combinations thereof.

According to aspects illustrated herein, an aqueous solution of pure silk fibroin- based protein fragments of the present disclosure is available for application to a product, including, but not limited to, apparel, padding, shoes, gloves, luggage, furs, jewelry and bags, or for directly spraying on the body of a consumer, to impart desired properties to the product.

Silk performance apparel and methods of preparing the same are disclosed herein. According to aspects illustrated herein, the present disclosure relates to apparel configured to be worn or carried on the body, that is at least partially surface treated with a solution of pure silk fibroin-based protein fragments of the present disclosure so as to result in a silk coating on the product. In some embodiments, the solutions of silk fibroin-based proteins or fragments thereof may be aqueous solutions, organic solutions, or emulsions. In an embodiment, the product is manufactured from a textile material. In an embodiment, the product is manufactured from a non-textile material. In an embodiment, desired additives can be added to an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure so as to result in a silk coating having desired additives.

In an embodiment, a textile comprising a silk coating of the present disclosure is sold to a consumer. In an embodiment, a textile of the present disclosure is used in constructing action sportswear apparel. In an embodiment, a textile of the present disclosure is used in constructing fitness apparel. In an embodiment, a textile of the present disclosure is used in constructing performance apparel. In an embodiment, a textile of the present disclosure is used in constructing golf apparel. In an embodiment, a textile of the present disclosure is used in constructing lingerie. In an embodiment, a silk coating of the present disclosure is positioned on the underlining of action sportswear/apparel. In an embodiment, a silk coating of the present disclosure is positioned on the shell, the lining, or the interlining of action sportswear/apparel. In an embodiment, action sportswear/apparel is partially made from a silk coated textile of the present disclosure and partially made from an uncoated textile. In an embodiment, action sportswear/apparel partially made from a silk coated textile and partially made from an uncoated textile combines an uncoated inert synthetic material with a silk coated inert synthetic material. Examples of inert synthetic material include, but are not limited to, polyester, polyamide, polyaramid, polytetrafiuoroethylene, polyethylene, polypropylene, polyurethane, silicone, mixtures of polyurethane and polyethyleneglycol, ultrahigh molecular weight polyethylene, high-performance polyethylene, nylon, LYCRA (polyester-polyurethane copolymer, also known as SPANDEX and elastomer), and mixtures thereof. In an embodiment, action sportswear/apparel partially made from a silk coated textile and partially made from an uncoated textile combines an elastomeric material at least partially covered with a silk coating of the present disclosure. In an embodiment, the percentage of silk to elastomeric material can be varied to achieve desired shrink or wrinkle resistant properties and desired moisture content against the skin surface. In an embodiment, a silk coating of the present disclosure is positioned on an internal layer of a shoe (textile or non-textile based). In an embodiment, a silk coating of the present disclosure positioned on an internal layer of a shoe helps maintain optimal feet microenvironment, such as temperature and humidity while reducing any excessive perspiration.

In an embodiment, a silk coating of the present disclosure is visible. In an embodiment, a silk coating of the present disclosure is transparent. In an embodiment, a silk coating of the present disclosure positioned on action sportswear/apparel helps control skin temperature of a person wearing the apparel. In an embodiment, a silk coating of the present disclosure positioned on action sportswear/apparel helps control fluid transfer away from the skin of a person wearing the apparel. In an embodiment, a silk coating of the present disclosure positioned on action sportswear/apparel has a soft feel against the skin decreasing abrasions from fabric on the skin. In an embodiment, a silk coating of the present disclosure positioned on a textile has properties that confer at least one of wrinkle resistance, shrinkage resistance, or machine washability to the textile. In an embodiment, a silk coated textile of the present disclosure is 100% machine washable and dry cleanable. In an embodiment, a silk coated textile of the present disclosure is 100% waterproof. In an embodiment, a silk coated textile of the present disclosure is wrinkle resistant. In an embodiment, a silk coated textile of the present disclosure is shrink resistant. In an embodiment, a silk coated fabric improves the health of the skin. In an embodiment, healthy skin can be determined by visibly seeing an even skin tone. In an embodiment, healthy skin can be determined by visibly seeing a smooth, glowing complexion. In an embodiment, a silk coated fabric decreases irritation of the skin. In an embodiment, a decrease in irritation of the skin can result in a decrease in skin bumps or sores. In an embodiment, a decrease in irritation of the skin can result in a decrease in scaly or red skin. In an embodiment, a decrease in irritation of the skin can result in a decrease in itchiness or burning. In an embodiment, a silk coated fabric decreases inflammation of the skin, in an embodiment, a silk coated textile of the present disclosure has the qualities of being waterproof, breathable, and elastic and possess a number of other qualities which are highly desirable in action sportswear. In an embodiment, a silk coated textile of the present disclosure manufactured from a silk fabric of the present disclosure further includes LYCRA brand spandex fibers (polyester-polyurethane copolymer). In an embodiment, a textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is a breathable fabric. In an embodiment, a textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is a water-resistant fabric. In an embodiment, a textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is a shrink-resistant fabric. In an embodiment, a textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is a machine-washable fabric. In an embodiment, a textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is a wrinkle resistant fabric. In an embodiment, textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure provides moisture and vitamins to the skin.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an accumulative one-way transport index of greater than 140. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an accumulative one-way transport index of greater than 120. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an accumulative one-way transport index of greater than 100. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an accumulative one-way transport index of greater than 80.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an overall moisture management capability of greater than 0.4. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an overall moisture management capability of greater than 0.35. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an overall moisture management capability of greater than 0.3. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has an overall moisture management capability of greater than 0.25.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a wetting time of at least 3 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a wetting time of at least 2.5 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a wetting time of at least 2 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a wetting time of at least 1.5 seconds.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a top absorption time of at least 50 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a top absorption time of at least 40 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a top absorption time of at least 30 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a top absorption time of at least 29 seconds, 28 seconds, 27 seconds, 26 seconds, 25 seconds, 24 seconds, 23 seconds, 22 seconds, 21 seconds, 20 seconds, 19 seconds, 18 seconds, 17 seconds, 16 seconds, 15 seconds, 14 seconds, 13 seconds, 12 seconds, 1 1 seconds, 10 seconds, 9 seconds, 8 seconds, 7 seconds, 6 seconds, 5 seconds, 4 seconds, 3 seconds, 2 seconds, or 1 second.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a bottom absorption time of at least 80 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a bottom absorption time of at least 70 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a bottom absorption time of at least 60 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a bottom absorption time of at least 50 seconds. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a bottom absorption time of at least 40 seconds.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a spreading speed of at least 1.6 mm/second. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a spreading speed of at least 1.4 mm/second. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a spreading speed of at least 1.2 mm/second. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a spreading speed of at least 1.0 mm/second. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure has a spreading speed of at least 0.8 mm/second.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 2000% microbial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 1000% microbial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 500% microbial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 400% microbial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 300% microbial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 200% microbial growth over 24 hours. In some embodiments, as described herein, the reduction in microbial growth may be measured and provided after one or more wash cycles in non-chlorine bleach. In some embodiments, solutions that include silk fibroin-based protein fragments may include an additional chemical agent, as described herein, that may provide antimicrobial, antifungal, and/or antibacterial properties.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 2000% bacterial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 1000% bacterial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 500% bacterial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 400% bacterial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 300% bacterial growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 200% bacterial growth over 24 hours.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 2000% fungal growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 1000% fungal growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 500% fungal growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 400% fungal growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 300% fungal growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 200% fungal growth over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 2000% growth of Staphylococcus aureus over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 1000% growth of Staphylococcus aureus over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 500% growth of Staphylococcus aureus over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 400% growth of Staphylococcus aureus over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 300% growth of Staphylococcus aureus over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 200% growth of Staphylococcus aureus over 24 hours.

In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 2000% growth of Klebsiella pneumoniae over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 1000% growth of Klebsiella pneumoniae over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 500% growth of Klebsiella pneumoniae over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 400% growth of Klebsiella pneumoniae over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 300% growth of Klebsiella pneumoniae over 24 hours. In an embodiment, the textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure shows less than 200% growth of Klebsiella pneumoniae over 24 hours. In an embodiment, an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is used to coat a textile. In an embodiment, the concentration of silk in the solution ranges from about 0.001% to about 20.0%. In an embodiment, the concentration of silk in the solution ranges from about 0.01 % to about 15.0%. In an embodiment, the concentration of silk in the solution ranges from about 0.5% to about 10.0%. In an embodiment, the concentration of silk in the solution ranges from about 1.0% to about 5.0%. In an embodiment, an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is applied directly to a fabric. Alternatively, silk microsphere and any additives may be used for coating a fabric. In an embodiment, additives can be added to an aqueous solution of pure silk fibroin- based protein fragments of the present disclosure before coating (e.g., alcohols) to further enhance material properties. In an embodiment, a silk coating of the present disclosure can have a pattern to optimize properties of the silk on the fabric. In an embodiment, a coating is applied to a fabric under tension and/or lax to vary penetration in to the fabric.

In an embodiment, a silk coating of the present disclosure can be applied at the yam level, followed by creation of a fabric once the yam is coated. In an embodiment, an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure can be spun into fibers to make a silk fabric and/or silk fabric blend with other materials known in the apparel industry.

In an embodiment, a method for silk coating a fabric includes immersion of the fabric in any of the aqueous solutions of pure silk fibroin-based protein fragments of the present disclosure. In an embodiment, a method for silk coating a fabric includes spraying. In an embodiment, a method for silk coating a fabric includes chemical vapor deposition. In an embodiment, a method for silk coating a fabric includes electrochemical coating. In an embodiment, a method for silk coating a fabric includes knife coating to spread any of the aqueous solutions of pure silk fibroin- based protein fragments of the present disclosure onto the fabric. The coated fabric may then be air dried, dried under heat/air flow, or cross-linked to the fabric surface. In an embodiment, a drying process includes curing with additives and/or ambient condition.

According to aspects illustrated herein, methods for preparing aqueous solutions of pure silk fibroin-based protein fragments are disclosed. In an embodiment, at least one pure silk fibroin-based protein fragment (SPF) mixture solution having a specific average weight average molecular weight (MW) range and polydispersity is created. In an embodiment, at least SPF mixture solution having a MW range between about 6 kDa and 17 kDa and a polydispersity range between about 1.5 and about 3.0 is created. In an embodiment, at least one SPF mixture solution having a MW between about 17 kDa and 39 kDa and a polydispersity range between about 1.5 and about 3.0 is created. In an embodiment, at least one SPF mixture solution having a MW range between about 39 kDa and 80 kDa and a polydispersity range between about 1.5 and about 3.0 is created.

In one embodiment, the invention relates to a material including one or more fibers including a protein, wherein a substantial portion of fibers are coated with silk fibroin-based protein fragments. In some embodiments, the material includes one or more of a woven material, a non-woven material, a knit material, and a crochet material. In some embodiments, the material includes fabric, thread, yarn, fiber, or a combination thereof. In some embodiments, the material includes wool. In some embodiments, the material includes cashmere. In some embodiments, the wool includes one or more of natural wool, synthetic wool, alpaca fleece, alpaca wool, lama fleece, lama wool, cashmere, sheep fleece, sheep wool, mohair wool, camel hair, or angora wool. In some embodiments, the silk fibroin-based protein fragments include one or more of low molecular weight silk fibroin-based protein fragments, medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments. In some embodiments, the silk fibroin-based protein fragments have an average molecular weight from about 1 kDa to about 350 kDa. In some embodiments, the silk fibroin-based protein fragments have a polydispersity from about 1.0 to about 5.0.

In one embodiment, the invention relates to coating a material including one or more proteinaceous fibers, wherein a substantial portion of the proteinaceous fibers are coated with silk fibroin-based protein fragments. In some embodiments, the proteinaceous fibers include keratin. In some embodiments, the proteinaceous fibers include hair. In some embodiments, the proteinaceous fibers include human hair or animal hair. In some embodiments, the silk fibroin-based protein fragments include one or more of low molecular weight silk fibroin-based protein fragments, medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments. In some embodiments, the silk fibroin-based protein fragments have an average molecular weight from about 1 kDa to about 350 kDa. In some embodiments, the silk fibroin-based protein fragments have a polydispersity from about 1.0 to about 5.0.

In one embodiment, the invention relates to a method of making a silk fibroin coated material, the method including preparing a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, coating a surface of the material with the silk fibroin solution, and drying the surface of the material that has been coated with the silk fibroin solution to provide the silk fibroin coated material. In one embodiment, the invention relates to a method of improving hand in a material, the method including preparing a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, coating a surface of the material with the silk fibroin solution, and drying the surface of the material that has been coated with the silk fibroin solution, wherein the resulting coated material has an improved hand compared to the uncoated material. In one embodiment, the invention relates to a method of improving hand retention on laundering in a material, the method including preparing a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, coating a surface of the material with the silk fibroin solution, and drying the surface of the material that has been coated with the silk fibroin solution, wherein upon laundering, the coated material retains a substantial portion of its initial hand prior to laundering. In one embodiment, the invention relates to a method of improving size and/or shape retention on laundering in a material, the method including preparing a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, coating a surface of the material with the silk fibroin solution, and drying the surface of the material that has been coated with the silk fibroin solution, wherein upon laundering, the coated material substantially retains its initial size and/or shape prior to laundering. In one embodiment, the invention relates to a method of improving pilling resistance in a material, the method including preparing a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, coating a surface of the material with the silk fibroin solution, and drying the surface of the material that has been coated with the silk fibroin solution, wherein the coated material has an improved pilling resistance compared to a similar material which was not so coated. In one embodiment, the invention relates to a method of improving water repellency in a material, the method including preparing a silk fibroin solution comprising low molecular weight silk fibroin-based protein fragments, coating a surface of the material with the silk fibroin solution, and drying the surface of the material that has been coated with the silk fibroin solution, wherein the coated material has an improved water repellency compared to a similar material which was not so coated. In some embodiments, the methods further include an additional treatment step. In some embodiments, the additional treatment step is a pre-treatment step (e.g., preparation of an article surface before treatment or coating), a post treatment step, or a final treatment step. In some embodiments, the additional treatment step comprises an acidic treatment or an alcohol treatment. In some embodiments, the silk fibroin solution further includes medium molecular weight silk fibroin-based protein fragments. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 90: 10, about 80:20, about 75 :25, about 70:30, about 66:34, about 60:40, about 50:50, about 40:60, about 34:66, about 30:70, about 25 :75, about 20: 80, or about 10:90. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 3 : 1. In some embodiments, the silk fibroin solution further includes high molecular weight silk fibroin-based protein fragments. In some embodiments, the silk fibroin solution further includes medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments. In some embodiments, drying the surface of the material includes heating the surface of the material without substantially modifying silk fibroin coating performance. In some embodiments, the silk fibroin solution includes silk fibroin-based protein fragments at less than about 0.001% by volume (v/v), less than about 0.1% v/v, less than about 1% v/v, less than about 2.5% v/v, or less than about 5% v/v. In some embodiments, the silk fibroin solution includes silk fibroin-based protein fragments at about 0.5% by v/v, weight/weight (w/w), or weight/volume (w/v). In some embodiments, the silk fibroin solution includes a Bronsted acid. In some embodiments, the silk fibroin solution includes one or more of citric acid and acetic acid. In some embodiments, the material includes one or more of a woven material, a non-woven material, a knit material, and a crochet material. In some embodiments, the material includes fabric, thread, yarn, fiber, or a combination thereof. In some embodiments, the material includes wool. In some embodiments, the material includes cashmere. In some embodiments, the wool includes one or more of natural wool, synthetic wool, alpaca fleece, alpaca wool, lama fleece, lama wool, cashmere, sheep fleece, sheep wool, mohair wool, camel hair, angora wool.

According to aspects illustrated herein, there is disclosed a composition that includes pure silk fibroin-based protein fragments that are substantially devoid of sericin, wherein the composition has an average weight average molecular weight ranging from about 6 kDa to about 17 kDa, wherein the composition has a polydispersity of between about 1.5 and about 3.0, wherein the composition is substantially homogenous, wherein the composition includes between 0 ppm and about 500 ppm of inorganic residuals, and wherein the composition includes between 0 ppm and about 500 ppm of organic residuals. In an embodiment, the pure silk fibroin-based protein fragments have between about 10 ppm and about 300 ppm of lithium bromide residuals and between about 10 ppm and about 100 ppm of sodium carbonate residuals. In an embodiment, the lithium bromide residuals are measurable using a high- performance liquid chromatography lithium bromide assay, and the sodium carbonate residuals are measurable using a high-performance liquid chromatography sodium carbonate assay. In an embodiment, the composition further includes less than 10% water. In an embodiment, the composition is in the form of a solution. In an embodiment, the composition includes from about 0.01 wt % to about 30.0 wt % pure silk fibroin-based protein fragments. In some embodiments, the pure silk fibroin-based protein fragments are stable in the solution for at least 30 days. In some embodiments, the pure silk fibroin-based protein fragments are stable in the solution for at least 30 days at about 0 °C, about 1 °C, about 2 °C, about 3 °C, about 4 °C, about 5 °C, about 6 °C, about 7 °C, about 8 °C, about 9 °C, about 10 °C, about 11 °C, about 12 °C, about 13 °C, about 14 °C, about 15 °C, about 16 °C, about 17 °C, about 18 °C, about 19 °C, about 20 °C, about 21 °C, about 22 °C, about 23 °C, about 24 °C, or about 25 °C. In some embodiments, the pure silk fibroin-based protein fragments are stable in the solution for at least 30 days at room temperature. In an embodiment, the term "stable" refers to the absence of spontaneous or gradual gelation, with no visible change in the color or turbidity of the solution. In an embodiment, the term "stable" refers to no aggregation of fragments and therefore no increase in molecular weight over time. In an embodiment, the composition is in the form of an aqueous solution. In an embodiment, the composition is in the form of an organic solution. The composition may be provided in a sealed container. In some embodiments, the composition further includes one or more molecules selected from the group consisting of therapeutic agents, growth factors, antioxidants, proteins, vitamins, carbohydrates, polymers, nucleic acids, salts, acids, bases, biomolecules, glycosamino glycans, polysaccharides, extracellular matrix molecules, metals, metal ion, metal oxide, synthetic molecules, polyanhydrides, cells, fatty acids, fragrance, minerals, plants, plant extracts, preservatives and essential oils. In an embodiment, the added molecule or molecules are stable (i.e., retain activity over time) within the composition and can be released at a desired rate. In an embodiment, the one or more molecules is vitamin C or a derivative thereof. In an embodiment, the composition further includes an alpha hydroxy acid selected from the group consisting of gly colic acid, lactic acid, tartaric acid and citric acid. In an embodiment, the composition further includes hyaluronic acid or its salt form at a concentration of about 0.5% to about 10.0%. In an embodiment, the composition further includes at least one of zinc oxide or titanium dioxide. In an embodiment, the pure silk fibroin-based protein fragments in the composition are hypoallergenic. In an embodiment, the pure silk fibroin-based protein fragments are biocompatible, non-sensitizing, and non-immunogenic.

According to aspects illustrated herein, there is disclosed a composition that includes pure silk fibroin-based protein fragments that are substantially devoid of sericin, wherein the composition has an average weight average molecular weight ranging from about 17 kDa to about 39 kDa, wherein the composition has a polydispersity of between about 1.5 and about 3.0, wherein the composition is substantially homogenous, wherein the composition includes between 0 ppm and about 500 ppm of inorganic residuals, and wherein the composition includes between 0 ppm and about 500 ppm of organic residuals. In an embodiment, the pure silk fibroin-based protein fragments have between about 10 ppm and about 300 ppm of lithium bromide residuals and between about 10 ppm and about 100 ppm of sodium carbonate residuals. In an embodiment, the lithium bromide residuals are measurable using a high- performance liquid chromatography lithium bromide assay, and the sodium carbonate residuals are measurable using a high-performance liquid chromatography sodium carbonate assay. In an embodiment, the composition further includes less than 10% water. In an embodiment, the composition is in the form of a solution. In an embodiment, the composition includes from about 0.01 wt % to about 30.0 wt % pure silk fibroin-based protein fragments. The pure silk fibroin-based protein fragments are stable in the solution for at least 30 days. In an embodiment, the term "stable" refers to the absence of spontaneous or gradual gelation, with no visible change in the color or turbidity of the solution. In an embodiment, the term "stable" refers to no aggregation of fragments and therefore no increase in molecular weight over time. In an embodiment, the composition is in the form of an aqueous solution. In an embodiment, the composition is in the form of an organic solution. The composition may be provided in a sealed container. In some embodiments, the composition further includes one or more molecules selected from the group consisting of therapeutic agents, growth factors, antioxidants, proteins, vitamins, carbohydrates, polymers, nucleic acids, salts, acids, bases, biomolecules, glycosamino glycans, polysaccharides, extracellular matrix molecules, metals, metal ion, metal oxide, synthetic molecules, polyanhydrides, cells, fatty acids, fragrance, minerals, plants, plant extracts, preservatives and essential oils. In an embodiment, the added molecule or molecules are stable (i.e., retain activity over time) within the composition and can be released at a desired rate. In an embodiment, the one or more molecules is vitamin C or a derivative thereof. In an embodiment, the composition further includes an alpha hydroxy acid selected from the group consisting of glycolic acid, lactic acid, tartaric acid and citric acid. In an embodiment, the composition further includes hyaluronic acid or its salt form at a concentration of about 0.5% to about 10.0%. In an embodiment, the composition further includes at least one of zinc oxide or titanium dioxide. In an embodiment, the pure silk fibroin-based protein fragments in the composition are hypoallergenic. In an embodiment, the pure silk fibroin-based protein fragments are biocompatible, non-sensitizing, and non- immunogenic.

According to aspects illustrated herein, there is disclosed a composition that includes pure silk fibroin-based protein fragments that are substantially devoid of sericin, wherein the composition has an average weight average molecular weight ranging from about 39 kDa to about 80 kDa, wherein the composition has a polydispersity of between about 1.5 and about 3.0, wherein the composition is substantially homogenous, wherein the composition includes between 0 ppm and about 500 ppm of inorganic residuals, and wherein the composition includes between 0 ppm and about 500 ppm of organic residuals. In an embodiment, the pure silk fibroin-based protein fragments have between about 10 ppm and about 300 ppm of lithium bromide residuals and between about 10 ppm and about 100 ppm of sodium carbonate residuals. In an embodiment, the lithium bromide residuals are measurable using a high- performance liquid chromatography lithium bromide assay, and the sodium carbonate residuals are measurable using a high-performance liquid chromatography sodium carbonate assay. In an embodiment, the composition further includes less than 10% water. In an embodiment, the composition is in the form of a solution. In an embodiment, the composition includes from about 0.01 wt % to about 30.0 wt % pure silk fibroin-based protein fragments. The pure silk fibroin-based protein fragments are stable in the solution for at least 30 days. In an embodiment, the term "stable" refers to the absence of spontaneous or gradual gelation, with no visible change in the color or turbidity of the solution. In an embodiment, the term "stable" refers to no aggregation of fragments and therefore no increase in molecular weight over time. In an embodiment, the composition is in the form of an aqueous solution. In an embodiment, the composition is in the form of an organic solution. The composition may be provided in a sealed container. In some embodiments, the composition further includes one or more molecules selected from the group consisting of therapeutic agents, growth factors, antioxidants, proteins, vitamins, carbohydrates, polymers, nucleic acids, salts, acids, bases, biomolecules, glycosamino glycans, polysaccharides, extracellular matrix molecules, metals, metal ion, metal oxide, synthetic molecules, polyanhydrides, cells, fatty acids, fragrance, minerals, plants, plant extracts, preservatives and essential oils. In an embodiment, the added molecule or molecules are stable (i.e., retain activity over time) within the composition and can be released at a desired rate. In an embodiment, the one or more molecules is vitamin C or a derivative thereof. In an embodiment, the composition further includes an alpha hydroxy acid selected from the group consisting of glycolic acid, lactic acid, tartaric acid and citric acid. In an embodiment, the composition further includes hyaluronic acid or its salt form at a concentration of about 0.5% to about 10.0%. In an embodiment, the composition further includes at least one of zinc oxide or titanium dioxide. In an embodiment, the pure silk fibroin-based protein fragments in the composition are hypoallergenic. In an embodiment, the pure silk fibroin-based protein fragments are biocompatible, non-sensitizing, and non- immunogenic.

According to aspects illustrated herein, there is disclosed a gel that includes pure silk fibroin-based protein fragments substantially devoid of sericin and comprising: an average weight average molecular weight ranging from about 17 kDa to about 39 kDa; and a polydispersity of between about 1.5 and about 3.0; and water from about 20 wt.% to about 99.9 wt.%, wherein the gel includes between 0 ppm and 500 ppm of inorganic residuals, and wherein the gel includes between 0 ppm and 500 ppm of organic residuals. In an embodiment, the gel includes between about 1.0% and about 50.0% crystalline protein domains. In an embodiment, the gel includes from about 0.1 wt.% to about 6.0 wt.% of pure silk fibroin-based protein fragments. In an embodiment, the gel has a pH from about 1.0 to about 7.0. In an embodiment, the gel further includes from about 0.5 wt.% to about 20.0 wt.% of vitamin C or a derivative thereof. In an embodiment, the vitamin C or a derivative thereof remains stable within the gel for a period of from about 5 days to about 5 years. In an embodiment, the vitamin C or a derivative thereof is stable within the gel so as to result in release of the vitamin C in a biologically active form. In an embodiment, the gel further includes an additive selected from the group consisting of vitamin E, rosemary oil, rose oil, lemon juice, lemon grass oil and caffeine. In an embodiment, the gel is packaged in an airtight container. In an embodiment, the pure silk fibroin-based protein fragments are hypoallergenic. In an embodiment, the gel has less than 10 colony forming units per milliliter.

According to aspects illustrated herein, there is disclosed a method for preparing an aqueous solution of pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from about 6 kDa to about 17 kDa, the method including the steps of: degumming a silk source by adding the silk source to a boiling (100 °C) aqueous solution of sodium carbonate for a treatment time of between about 30 minutes to about 60 minutes; removing sericin from the solution to produce a silk fibroin extract comprising non-detectable levels of sericin; draining the solution from the silk fibroin extract; dissolving the silk fibroin extract in a solution of lithium bromide having a starting temperature upon placement of the silk fibroin extract in the lithium bromide solution that ranges from about 60 °C to about 140 °C; maintaining the solution of silk fibroin-lithium bromide in an oven having a temperature of about 140 °C for a period of at least 1 hour; removing the lithium bromide from the silk fibroin extract; and producing an aqueous solution of silk protein fragments, the aqueous solution comprising: fragments having an average weight average molecular weight ranging from about 6 kDa to about 17 kDa, and wherein the aqueous solution of pure silk fibroin-based protein fragments comprises a polydispersity of between about 1.5 and about 3.0. In an embodiment, the method includes the step of drying the silk fibroin extract prior to the dissolving step. In an embodiment, the amount of lithium bromide residuals in the aqueous solution can be measured using a high-performance liquid chromatography lithium bromide assay. In an embodiment, the amount of sodium carbonate residuals in the aqueous solution can be measured using a high-performance liquid chromatography sodium carbonate assay. In an embodiment, the method includes the step of adding a therapeutic agent to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method includes the step of adding a molecule selected from one of an antioxidant or an enzyme to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method includes the step of adding a vitamin to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the vitamin is selected from one of vitamin C or a derivative thereof. In an embodiment, the method further includes the step of adding an alpha hydroxy acid to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the alpha hydroxy acid is selected from the group consisting of gly colic acid, lactic acid, tartaric acid and citric acid. In an embodiment, the method further includes the step of adding hyaluronic acid at a concentration of about 0.5% to about 10.0% to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method further includes the step of adding at least one of zinc oxide or titanium dioxide to the aqueous solution of pure silk fibroin-based protein fragments.

According to aspects illustrated herein, there is disclosed a method for preparing an aqueous solution of pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from about 17 kDa to about 39 kDa, the method including the steps of: adding a silk source to a boiling (100 °C) aqueous solution of sodium carbonate for a treatment time of between about 30 minutes to about 60 minutes so as to result in degumming; removing sericin from the solution to produce a silk fibroin extract comprising non-detectable levels of sericin; draining the solution from the silk fibroin extract; dissolving the silk fibroin extract in a solution of lithium bromide having a starting temperature upon placement of the silk fibroin extract in the lithium bromide solution that ranges from about 80 °C to about 140 °C; maintaining the solution of silk fibroin-lithium bromide in a dry oven having a temperature in the range between about 60 °C to about 100 °C for a period of at least 1 hour; removing the lithium bromide from the silk fibroin extract; and producing an aqueous solution of pure silk fibroin-based protein fragments, wherein the aqueous solution of pure silk fibroin-based protein fragments comprises lithium bromide residuals of between about 10 ppm and about 300 ppm, wherein the aqueous solution of silk protein fragments comprises sodium carbonate residuals of between about 10 ppm and about 100 ppm, wherein the aqueous solution of pure silk fibroin-based protein fragments comprises fragments having an average weight average molecular weight ranging from about 17 kDa to about 39 kDa, and wherein the aqueous solution of pure silk fibroin-based protein fragments comprises a polydispersity of between about 1.5 and about 3.0. In an embodiment, the method includes the step of drying the silk fibroin extract prior to the dissolving step. In an embodiment, the amount of lithium bromide residuals in the aqueous solution can be measured using a high-performance liquid chromatography lithium bromide assay. In an embodiment, the amount of sodium carbonate residuals in the aqueous solution can be measured using a high-performance liquid chromatography sodium carbonate assay. In an embodiment, the method includes the step of adding a therapeutic agent to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method includes the step of adding a molecule selected from one of an antioxidant or an enzyme to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method includes the step of adding a vitamin to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the vitamin is selected from one of vitamin C or a derivative thereof. In an embodiment, the method further includes the step of adding an alpha hydroxy acid to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the alpha hydroxy acid is selected from the group consisting of gly colic acid, lactic acid, tartaric acid and citric acid. In an embodiment, the method further includes the step of adding hyaluronic acid at a concentration of about 0.5% to about 10.0% to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method further includes the step of adding at least one of zinc oxide or titanium dioxide to the aqueous solution of pure silk fibroin-based protein fragments.

According to aspects illustrated herein, there is disclosed a method for preparing an aqueous solution of pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from about 39 kDa to about 80 kDa, the method including the steps of: adding a silk source to a boiling (100 °C) aqueous solution of sodium carbonate for a treatment time of about 30 minutes so as to result in degumming; removing sericin from the solution to produce a silk fibroin extract comprising non-detectable levels of sericin; draining the solution from the silk fibroin extract; dissolving the silk fibroin extract in a solution of lithium bromide having a starting temperature upon placement of the silk fibroin extract in the lithium bromide solution that ranges from about 80 °C to about 140 °C; maintaining the solution of silk fibroin-lithium bromide in a dry oven having a temperature in the range between about 60 °C to about 100 °C for a period of at least 1 hour; removing the lithium bromide from the silk fibroin extract; and producing an aqueous solution of pure silk fibroin- based protein fragments, wherein the aqueous solution of pure silk fibroin-based protein fragments comprises lithium bromide residuals of between about 10 ppm and about 300 ppm, sodium carbonate residuals of between about 10 ppm and about 100 ppm, fragments having an average weight average molecular weight ranging from about 40 kDa to about 65 kDa, and wherein the aqueous solution of pure silk fibroin-based protein fragments comprises a polydispersity of between about 1.5 and about 3.0. In an embodiment, the method includes the step of drying the silk fibroin extract prior to the dissolving step. In an embodiment, the amount of lithium bromide residuals in the aqueous solution can be measured using a high-performance liquid chromatography lithium bromide assay. In an embodiment, the amount of sodium carbonate residuals in the aqueous solution can be measured using a high-performance liquid chromatography sodium carbonate assay. In an embodiment, the method includes the step of adding a therapeutic agent to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method includes the step of adding a molecule selected from one of an antioxidant or an enzyme to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method includes the step of adding a vitamin to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the vitamin is selected from one of vitamin C or a derivative thereof. In an embodiment, the method further includes the step of adding an alpha hydroxy acid to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the alpha hydroxy acid is selected from the group consisting of gly colic acid, lactic acid, tartaric acid and citric acid. In an embodiment, the method further includes the step of adding hyaluronic acid at a concentration of about 0.5% to about 10.0% to the aqueous solution of pure silk fibroin-based protein fragments. In an embodiment, the method further includes the step of adding at least one of zinc oxide or titanium dioxide to the aqueous solution of pure silk fibroin-based protein fragments. According to aspects illustrated herein, a method is disclosed for producing silk gels having entrapped molecules or therapeutic agents such as those listed in the following paragraphs. In an embodiment, at least one molecule or therapeutic agent of interest is physically entrapped into a SPF mixture solution of the present disclosure during processing into aqueous gels. An aqueous silk gel of the present disclosure can be used to release at least one molecule or therapeutic agent of interest.

In some embodiments, the w/w ratio between low molecular weight silk and medium molecular weight silk is between about 99: 1 to about 1:99, between about 95:5 to about 5:95, between about 90: 10 to about 10:90, between about 75:25 to about 25:75, between about 65:35 to about 35:65, or between about 55:45 to about 45:55. In some embodiments, the w/w ratio between low molecular weight silk and medium molecular weight silk is between about 99:1 to about 55:45, between about 95:5 to about 45:55, between about 90:10 to about 35:65, between about 75:25 to about 15:85, between about 65:35 to about 10:90, or between about 55:45 to about 1:99. In an embodiment, the w/w ratio between low molecular weight silk and medium molecular weight silk is about 99: 1, about 98:2, about 97:3, about 96:4, about 95:5, about 94:6, about 93:7, about 92:8, about 91:9, about 90:10, about 89:11, about 88:12, about 87:13, about 86:14, about 85:15, about 84:16, about 83:17, about 82:18, about 81:19, about 80:20, about 79:21, about 78:22, about 77:23, about 76:24, about 75:25, about 74:26, about 73:27, about 72:28, about 71:29, about 70:30, about 69:31, about 68:32, about 67:33, about 66:34, about 65:35, about 64:36, about 63:37, about 62:38, about 61:39, about 60:40, about 59:41, about 58:42, about 57:43, about 56:44, about 55:45, about 54:46, about 53:47, about 52:48, about 51:49, about 50:50, about 49:51, about 48:52, about 47:53, about 46:54, about 45:55, about 44:56, about 43:57, about 42:58, about 41:59, about 40:60, about 39:61, about 38:62, about 37:63, about 36:64, about 35:65, about 34:66, about 33:67, about 32:68, about 31:69, about 30:70, about 29:71, about 28:72, about 27:73, about 26:74, about 25:75, about 24:76, about 23:77, about 22:78, about 21:79, about 20:80, about 19:81, about 18:82, about 17:83, about 16:84, about 15:85, about 14:86, about 13:87, about 12:88, about 11:89, about 10:90, about 9:91, about 8:92, about 7:93, about 6:94, about 5:95, about 4:96, about 3:97, about 2:98, or about 1:99. In an embodiment, the w/w ratio between low molecular weight silk and medium molecular weight silk is about 3:1. In an embodiment, the w/w ratio between low molecular weight silk and medium molecular weight silk is about 1:3. In some embodiments, the w/w ratio between low molecular weight silk and high molecular weight silk is between about 99:1 to about 1:99, between about 95:5 to about 5:95, between about 90:10 to about 10:90, between about 75:25 to about 25:75, between about 65:35 to about 35:65, or between about 55:45 to about 45:55. In some embodiments, the w/w ratio between low molecular weight silk and high molecular weight silk is between about 99:1 to about 55:45, between about 95:5 to about 45:55, between about 90:10 to about 35:65, between about 75:25 to about 15:85, between about 65:35 to about 10:90, or between about 55:45 to about 1:99. In an embodiment, the w/w ratio between low molecular weight silk and high molecular weight silk is about 99: 1, about 98:2, about 97:3, about 96:4, about 95:5, about 94:6, about 93:7, about 92:8, about 91:9, about 90:10, about 89:11, about 88:12, about 87:13, about 86:14, about 85:15, about 84:16, about 83:17, about 82:18, about 81:19, about 80:20, about 79:21, about 78:22, about 77:23, about 76:24, about 75:25, about 74:26, about 73:27, about 72:28, about 71:29, about 70:30, about 69:31, about 68:32, about 67:33, about 66:34, about 65:35, about 64:36, about 63:37, about 62:38, about 61:39, about 60:40, about 59:41, about 58:42, about 57:43, about 56:44, about 55:45, about 54:46, about 53:47, about 52:48, about 51:49, about 50:50, about 49:51, about 48:52, about 47:53, about 46:54, about 45:55, about 44:56, about 43:57, about 42:58, about 41:59, about 40:60, about 39:61, about 38:62, about 37:63, about 36:64, about 35:65, about 34:66, about 33:67, about 32:68, about 31:69, about 30:70, about 29:71, about 28:72, about 27:73, about 26:74, about 25:75, about 24:76, about 23:77, about 22:78, about 21:79, about 20:80, about 19:81, about 18:82, about 17:83, about 16:84, about 15:85, about 14:86, about 13:87, about 12:88, about 11:89, about 10:90, about 9:91, about 8:92, about 7:93, about 6:94, about 5:95, about 4:96, about 3:97, about 2:98, or about 1:99. In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yam, or a fabric, may be coated with compositions including medium molecular weight silk and high molecular weight silk. In some embodiments, the w/w ratio between medium molecular weight silk and high molecular weight silk is between about 99:1 to about 1:99, between about 95:5 to about 5:95, between about 90:10 to about 10:90, between about 75:25 to about 25:75, between about 65:35 to about 35:65, or between about 55:45 to about 45:55. In some embodiments, the w/w ratio between medium molecular weight silk and high molecular weight silk is between about 99: 1 to about 55:45, between about 95:5 to about 45:55, between about 90:10 to about 35:65, between about 75:25 to about 15:85, between about 65:35 to about 10:90, or between about 55:45 to about 1 :99. In an embodiment, the w/w ratio between medium molecular weight silk and high molecular weight silk is about 99: 1, about 98:2, about 97:3, about 96:4, about 95:5, about 94:6, about 93:7, about 92:8, about 91 :9, about 90: 10, about 89: 11, about 88: 12, about 87: 13, about 86: 14, about 85: 15, about 84: 16, about 83: 17, about 82: 18, about 81 : 19, about 80:20, about 79:21, about 78:22, about 77:23, about 76:24, about 75:25, about 74:26, about 73:27, about 72:28, about 71 :29, about 70:30, about 69:31, about 68:32, about 67:33, about 66:34, about 65:35, about 64:36, about 63:37, about 62:38, about 61 :39, about 60:40, about 59:41, about 58:42, about 57:43, about 56:44, about 55:45, about 54:46, about 53:47, about 52:48, about 51 :49, about 50:50, about 49:51, about 48:52, about 47:53, about 46:54, about 45:55, about 44:56, about 43:57, about 42:58, about 41 :59, about 40:60, about 39:61, about 38:62, about 37:63, about 36:64, about 35:65, about 34:66, about 33:67, about 32:68, about 31 :69, about 30:70, about 29:71, about 28:72, about 27:73, about 26:74, about 25:75, about 24:76, about 23:77, about 22:78, about 21 :79, about 20:80, about 19:81, about 18:82, about 17:83, about 16:84, about 15:85, about 14:86, about 13:87, about 12:88, about 11 :89, about 10:90, about 9:91, about 8:92, about 7:93, about 6:94, about 5:95, about 4:96, about 3:97, about 2:98, or about 1 :99.

In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yarn, or a fabric, may be coated with compositions including low molecular weight silk, medium molecular weight silk, and high molecular weight silk. In an embodiment, the w/w ratio between low molecular weight silk, medium molecular weight silk, and high molecular weight silk is about 1 : 1 :8, 1 :2:7, 1 :3:6, 1 :4:5, 1 :5:4, 1 :6:3, 1 :7:2, 1 :8: 1, 2: 1 :7, 2:2:6, 2:3:5, 2:4:4, 2:5:3, 2:6:2, 2:7: 1, 3: 1 :6, 3:2:5, 3:3:4, 3:4:3, 3:5:2, 3:6: 1, 4: 1 :5, 4:2:4, 4:3:3, 4:4:2, 4:5: 1, 5: 1 :4, 5:2:3, 5:3:2, 5:4: 1, 6: 1 :3, 6:2:2, 6:3: 1, 7: 1 :2, 7:2: 1, or 8: 1 : 1. In an embodiment, the w/w ratio between low molecular weight silk, medium molecular weight silk, and high molecular weight silk is about 3:0.1 :0.9, 3:0.2:0.8, 3:0.3:0.7, 3:0.4:0.6, 3:0.5:0.5, 3:0.6:0.4, 3:0.7:0.3, 3:0.8:0.2, or 3:0.9:0.1.

According to aspects illustrated herein, pure silk fibroin-based protein fragments from aqueous solutions of the present disclosure can be formed into yarns and fabrics including for example, woven or weaved fabrics, and these fabrics can be used in textiles, as described above. According to aspects illustrated herein, silk fabric manufactured from SPF mixture solutions of the present disclosure are disclosed. In an embodiment, at least one molecule or therapeutic agent of interest is physically entrapped into a SPF mixture solution of the present disclosure. A silk film of the present disclosure can be used to release at least one molecule or therapeutic agent of interest.

In some embodiments, the invention may include an article having a fiber or yam having a coating, wherein the coating may include silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa. In some embodiments, the article may be a fabric. In some embodiments, the silk based proteins or fragments thereof may include silk fibroin-based proteins or protein fragments having about 0.01% (w/w) to about 10% (w/w) sericin.

In some embodiments, the silk based proteins or fragments thereof may be selected from the group consisting of natural silk based proteins or fragments thereof that may be selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof.

In some embodiments, the silk based proteins or fragments thereof may be natural silk based proteins or fragments thereof that may be selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof.

In some embodiments, the natural silk based proteins or fragments may be silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof may be Bombyx mori silk based proteins or fragments thereof.

In some embodiments, the silk based proteins or fragments may include silk and a copolymer.

In some embodiments, the silk based proteins or protein fragments thereof may have an average weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof may have a polydispersity of between about 1.5 and about 3 In some embodiments, the natural silk based proteins or fragments may be silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof may be Bombyx mori silk based proteins or fragments thereof.

In some embodiments, the silk based proteins or fragments may include silk and a copolymer.

In some embodiments, the silk based proteins or protein fragments thereof may have an average weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the silk based proteins or fragments thereof may have a polydispersity of between about 1.0 and about 5.0, and wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days.

In some embodiments, the fiber or yarn may be selected from the group consisting of natural fiber or yam, synthetic fiber or yarn, or combinations thereof.

In some embodiments, the fiber or yarn may be natural fiber or yarn selected from the group consisting of cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof. In some embodiments, the fiber or yarn may be natural fiber or yarn comprising wool, and combinations thereof. In some embodiments, the fiber or yam may be natural fiber or yam comprising cashmere, and combinations thereof.

In some embodiments, the fiber or yarn may be synthetic fiber or yam selected from the group consisting of polyester, nylon, poly ester-poly urethane copolymer, and combinations thereof.

In some embodiments, the fabric may exhibit an improved property, wherein the improved property may be an accumulative one-way moisture transport index selected from the group consisting of greater than 40%, greater than 60%, greater than 80%, greater than 100%, greater than 120%, greater than 140%, greater than 160%, and greater than 180%.

In some embodiments, the fabric may exhibit an improved property, wherein the improved property may be an accumulative one-way transport capability increase relative to uncoated fabric selected from the group consisting of 1.2 fold, 1.5 fold, 2.0 fold, 3.0 fold, 4.0 fold, 5.0 fold, and 10 fold. In some embodiments, the fabric may exhibit an improved property, wherein the improved property may be an overall moisture management capability selected from the group consisting of greater than 0.05, greater than 0.10, greater than 0.15, greater than 0.20, greater than 0.25, greater than 0.30, greater than 0.35, greater than 0.40, greater than 0.50, greater than 0.60, greater than 0.70, and greater than 0.80. In some embodiments, the improved property may be determined after a period of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In some embodiments, the fabric may exhibit substantially no increase in microbial growth after a number of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles. In some embodiments, the microbial growth may be microbial growth of a microbe selected from the group consisting of Staphylococcus aureus, Klebsiella pneumoniae, and combinations thereof. In some embodiments, the microbial growth may be reduced by a percentage selected from the group consisting of 50%, 100%, 500%, 1000%, 2000%, and 3000% compared to an uncoated fabric.

In some embodiments, the coating may be applied to the fabric at the fiber level prior to forming the fabric.

In some embodiments, the coating may be applied to the fabric at the fabric level. In some embodiments, the fabric may be bath coated. In some embodiments, the fabric may be spray coated. In some embodiments, the fabric may be coated with a stencil. In some embodiments, the coating may be applied to at least one side of the fabric using a method selected from the group consisting of a bath coating process, a spray coating process, a stencil process, a silk-foam based process, and a roller-based process.

In some embodiments, the coating may have a thickness of about one nanolayer.

In some embodiments, the coating may have a thickness selected from the group consisting of about 5 nm, about 10 nm, about 15 nm, about 20 nm, about 25 nm, about 50 nm, about 100 nm, about 200 nm, about 500 nm, about 1 μιτι, about 5 μιτι, about 10 μιτι, and about 20 μιτι.

In some embodiments, the coating may be adsorbed on the fabric. In some embodiments, the coating may be attached to the fabric through chemical, enzymatic, thermal, or irradiative cross-linking.

In some embodiments, the hand of the coated fabric may be improved relative to an uncoated fabric.

In some embodiments, the hand of the coated fabric that may be improved may be selected from the group consisting of softness, crispness, dryness, silkiness, and combinations thereof.

In some embodiments, a flame retardation property of the coated fabric may be improved relative to an uncoated fabric.

In some embodiments, a flame retardation property of an uncoated fabric may not be adversely affected by the coating.

In some embodiments, the abrasion resistance may be improved relative to an uncoated fabric.

In an embodiment, the invention may include an article comprising a textile or leather having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, or about 1 kDa to about 350 kDa.

In some embodiments, the silk based proteins or protein fragments thereof have an average weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the silk based proteins or fragments thereof have a polydispersity of between about 1.0 and about 5.0, and wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days.

In some embodiments, at least one property of the article may be improved, wherein the property that may be improved may be selected from the group consisting of color retention, resistance to microbial growth, resistance to bacterial growth, resistance to fungal growth, resistance to the buildup of static electrical charge, resistance to the growth of mildew, transparency of the coating, resistance to fireeze- thaw cycle damage, resistance from abrasion, blocking of ultraviolet (UV) radiation, regulation of the body temperature of a wearer, resistance to tearing, elasticity of the article, rebound dampening, tendency to cause itching in the wearer, thermal insulation of the wearer, wrinkle resistance, stain resistance, stickiness to skin, and flame resistance.

In some embodiments, the article may be a textile used for apparel.

In some embodiments, the article may be fabricated as an item selected from the group consisting of an item of athletic apparel, an item of outdoor gear, a jacket, an overcoat, a shoe, a sneaker, a glove, an umbrella, a chair, a blanket, a towel, a surgical drape, a surgical gown, a laboratory coat, a wound dressing, a sterilization wrap, a surgical face mask, a surgical sleeve, a laboratory sleeve, a retention bandage, a support device, a compression bandage, a shoe cover, and a surgical blanket.

In some embodiments, the article may be a textile used to fabricate an automotive product.

In an embodiment, the invention may include a method of coating a fabric that may include the step of optionally applying a pretreatment selected from the group consisting of a wetting agent, a detergent, a sequestering or dispersing agent, an enzyme, a bleaching agent, an antifoaming agent, an anti-creasing agent, a dye dispersing agent, a dye leveling agent, a dye fixing agent, a dye special resin agent, a dye anti-reducing agent, a pigment dye system anti-migrating agent, a pigment dye system binder, a delave agent, a wrinkle free treatment, a softener, a handle modifier, a waterborne polyurethane dispersion, a finishing resin, an oil or water repellant, a flame retardant, a crosslinker, a thickener for technical finishing, or any combination thereof. In an embodiment, the method may include the step of applying a coating that may include a solution of silk based proteins or fragments thereof that may have an average molecular weight range of about 1 kDa to about 350 kDa, using a process selected from the group consisting of a continuous spray process, a continuous screen or stencil process, a continuous bath process, a batch spray process, a batch screen or stencil process, and a batch bath process. In an embodiment, the method may include the step of drying and optionally curing the coating.

In an embodiment, the silk based proteins or protein fragments thereof may have an average weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the silk based proteins or fragments thereof may have a polydispersity of between about 1.0 and about 5.0, and optionally wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days.

In one embodiment, the invention relates to a method of making a silk fibroin coated material, the method including preparing a silk fibroin solution comprising low molecular weight silk fibroin-based protein fragments, coating a surface of a material with the silk fibroin solution, and drying the surface of the material that has been coated with the silk fibroin solution to provide the silk fibroin coated material. In some embodiments, the silk fibroin solution further includes medium molecular weight silk fibroin-based protein fragments. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 90: 10, about 80:20, about 75 :25, about 70:30, about 66:34, about 60:40, about 50:50, about 40:60, about 34:66, about 30:70, about 25 :75, about 20: 80, or about 10:90. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 3 : 1. In some embodiments, the silk fibroin solution further includes high molecular weight silk fibroin-based protein fragments. In some embodiments, the silk fibroin solution further includes medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments. In some embodiments, drying the surface of the material includes heating the surface of the material without substantially modifying silk fibroin coating performance. In some embodiments, the silk fibroin solution includes silk fibroin-based protein fragments between 0.01 % and 1% volume (v/v). In some embodiments, the silk fibroin solution includes silk fibroin-based protein fragments at about 0.25% by volume (v/v). In some embodiments, the polydispersity of the silk fibroin-based protein fragments is between 1.5 and 3. In some embodiments, the silk fibroin solution further includes a Bronsted acid. In some embodiments, the silk fibroin solution further includes one or more of citric acid and acetic acid. In some embodiments, the silk fibroin solution has an acidic pH. In some embodiments, the silk fibroin solution has a pH between 4 and 5. In some embodiments, the method further includes coating the material with a silicone solution. In some embodiments, the silicone solution has an acidic pH. In some embodiments, the silk fibroin solution coating precedes the silicone solution coating. In some embodiments, the material includes one or more of a woven material, a non-woven material, a knit material, and a crochet material. In some embodiments, the material includes fabric, thread, yarn, or a combination thereof. In some embodiments, the material includes one or more of polyester, polyamide, polyaramid, polytetrafluoroethylene, polyethylene, polypropylene, polyurethane, silicone, mixtures of polyurethane and polyethyleneglycol, ultrahigh molecular weight polyethylene, high-performance polyethylene, nylon, and/or LYCRA.

In one embodiment, the invention relates to a method of improving hand in a material, the method including coating a surface of the material with a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, drying the material, and coating a surface of the material with a silicone solution, wherein the resulting coated material has an improved hand compared to the uncoated material. In one embodiment, the invention relates to a method of improving hand retention on laundering in a material, the method including coating a surface of the material with a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, drying the material, and coating a surface of the material with a silicone solution, wherein upon laundering, the coated material retains at least about 80% of its initial hand prior to laundering. In one embodiment, the invention relates to a method of improving the water drop absorption time of a material, the method including coating a surface of the material with a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, drying the material, and coating a surface of the material with a silicone solution, wherein the resulting coated material has an improved water drop absorption time compared to the uncoated material. In one embodiment, the invention relates to a method of improving the abrasion resistance of a material, the method including coating a surface of the material with a silk fibroin solution including low molecular weight silk fibroin-based protein fragments, drying the material, and coating a surface of the material with a silicone solution, wherein the resulting coated material has an improved abrasion resistance compared to the uncoated material. In some embodiments, the silk fibroin solution further includes medium molecular weight silk fibroin-based protein fragments. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 90: 10, about 80:20, about 75 :25, about 70:30, about 66:34, about 60:40, about 50:50, about 40:60, about 34:66, about 30:70, about 25 :75, about 20: 80, or about 10:90. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 3 : 1. In some embodiments, the silk fibroin solution further includes high molecular weight silk fibroin-based protein fragments. In some embodiments, the silk fibroin solution further includes medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments. In some embodiments, drying the surface of the material includes heating the surface of the material without substantially modifying silk fibroin coating performance. In some embodiments, the silk fibroin solution includes silk fibroin-based protein fragments between 0.01 % and 1 % volume (v/v). In some embodiments, the silk fibroin solution includes silk fibroin-based protein fragments at about 0.25% by volume (v/v). In some embodiments, the polydispersity of the silk fibroin-based protein fragments is between 1.5 and 3. In some embodiments, the silk fibroin solution further includes a Bronsted acid. In some embodiments, the silk fibroin solution further includes one or more of citric acid and acetic acid. In some embodiments, the silk fibroin solution has an acidic pH. In some embodiments, the silk fibroin solution has a pH between 4 and 5. In some embodiments, the silicone solution has an acidic pH. In some embodiments, the silk fibroin solution coating precedes the silicone solution coating. In some embodiments, the material includes one or more of a woven material, a non-woven material, a knit material, and a crochet material. In some embodiments, the material comprises fabric, thread, yarn, or a combination thereof. In some embodiments, the material includes one or more of polyester, polyamide, polyaramid, polytetrafluoroethylene, polyethylene, polypropylene, polyurethane, silicone, mixtures of polyurethane and poly ethylenegly col, ultrahigh molecular weight polyethylene, high-performance polyethylene, nylon, and/or LYCRA.

In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yarn, or a fabric, may be coated with compositions including low molecular weight silk and medium molecular weight silk. In some embodiments, the w/w ratio between low molecular weight silk and medium molecular weight silk is between about 99: 1 to about 1 :99, between about 95 :5 to about 5:95, between about 90: 10 to about 10:90, between about 75:25 to about 25:75, between about 65 :35 to about 35 :65, or between about 55 :45 to about 45:55. In some embodiments, the w/w ratio between low molecular weight silk and medium molecular weight silk is between about 99: 1 to about 55:45, between about 95 :5 to about 45 :55, between about 90: 10 to about 35 :65, between about 75 :25 to about 15 : 85, between about 65 :35 to about 10:90, or between about 55:45 to about 1 :99. In an embodiment, the w/w ratio between low molecular weight silk and medium molecular weight silk is about 99: 1 , about 98:2, about 97: 3, about 96:4, about 95:5, about 94:6, about 93:7, about 92:8, about 91:9, about 90:10, about 89:11, about 88:12, about 87:13, about 86:14, about 85:15, about 84:16, about 83:17, about 82:18, about 81:19, about 80:20, about 79:21, about 78:22, about 77:23, about 76:24, about 75:25, about 74:26, about 73:27, about 72:28, about 71:29, about 70:30, about 69:31, about 68:32, about 67:33, about 66:34, about 65:35, about 64:36, about 63:37, about 62:38, about 61:39, about 60:40, about 59:41, about 58:42, about 57:43, about 56:44, about 55:45, about 54:46, about 53:47, about 52:48, about 51:49, about 50:50, about 49:51, about 48:52, about 47:53, about 46:54, about 45:55, about 44:56, about 43:57, about 42:58, about 41:59, about 40:60, about 39:61, about 38:62, about 37:63, about 36:64, about 35:65, about 34:66, about 33:67, about 32:68, about 31:69, about 30:70, about 29:71, about 28:72, about 27:73, about 26:74, about 25:75, about 24:76, about 23:77, about 22:78, about 21:79, about 20:80, about 19:81, about 18:82, about 17:83, about 16:84, about 15:85, about 14:86, about 13:87, about 12:88, about 11:89, about 10:90, about 9:91, about 8:92, about 7:93, about 6:94, about 5:95, about 4:96, about 3:97, about 2:98, or about 1:99. In an embodiment, the w/w ratio between low molecular weight silk and medium molecular weight silk is about 3:1. In an embodiment, the w/w ratio between low molecular weight silk and medium molecular weight silk is about 1:3.

In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yarn, or a fabric, may be coated with compositions including low molecular weight silk and high molecular weight silk. In some embodiments, the w/w ratio between low molecular weight silk and high molecular weight silk is between about 99:1 to about 1:99, between about 95:5 to about 5:95, between about 90:10 to about 10:90, between about 75:25 to about 25:75, between about 65:35 to about 35:65, or between about 55:45 to about 45:55. In some embodiments, the w/w ratio between low molecular weight silk and high molecular weight silk is between about 99:1 to about 55:45, between about 95:5 to about 45:55, between about 90: 10 to about 35:65, between about 75:25 to about 15:85, between about 65:35 to about 10:90, or between about 55:45 to about 1:99. In an embodiment, the w/w ratio between low molecular weight silk and high molecular weight silk is about 99:1, about 98:2, about 97:3, about 96:4, about 95:5, about 94:6, about 93:7, about 92:8, about 91:9, about 90:10, about 89:11, about 88:12, about 87:13, about 86:14, about 85:15, about 84:16, about 83:17, about 82:18, about 81:19, about 80:20, about 79:21, about 78:22, about 77:23, about 76:24, about 75:25, about 74:26, about 73:27, about 72:28, about 71:29, about 70:30, about 69:31, about 68:32, about 67:33, about 66:34, about 65:35, about 64:36, about 63:37, about 62:38, about 61:39, about 60:40, about 59:41, about 58:42, about 57:43, about 56:44, about 55:45, about 54:46, about 53:47, about 52:48, about 51:49, about 50:50, about 49:51, about 48:52, about 47:53, about 46:54, about 45:55, about 44:56, about 43:57, about 42:58, about 41:59, about 40:60, about 39:61, about 38:62, about 37:63, about 36:64, about 35:65, about 34:66, about 33:67, about 32:68, about 31:69, about 30:70, about 29:71, about 28:72, about 27:73, about 26:74, about 25:75, about 24:76, about 23:77, about 22:78, about 21:79, about 20:80, about 19:81, about 18:82, about 17:83, about 16:84, about 15:85, about 14:86, about 13:87, about 12:88, about 11:89, about 10:90, about 9:91, about 8:92, about 7:93, about 6:94, about 5:95, about 4:96, about 3:97, about 2:98, or about 1:99.

In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yam, or a fabric, may be coated with compositions including medium molecular weight silk and high molecular weight silk. In some embodiments, the w/w ratio between medium molecular weight silk and high molecular weight silk is between about 99:1 to about 1:99, between about 95:5 to about 5:95, between about 90:10 to about 10:90, between about 75:25 to about 25:75, between about 65:35 to about 35:65, or between about 55:45 to about 45:55. In some embodiments, the w/w ratio between medium molecular weight silk and high molecular weight silk is between about 99: 1 to about 55:45, between about 95:5 to about 45:55, between about 90:10 to about 35:65, between about 75:25 to about 15:85, between about 65:35 to about 10:90, or between about 55:45 to about 1:99. In an embodiment, the w/w ratio between medium molecular weight silk and high molecular weight silk is about 99:1, about 98:2, about 97:3, about 96:4, about 95:5, about 94:6, about 93:7, about 92:8, about 91:9, about 90:10, about 89:11, about 88:12, about 87:13, about 86:14, about 85:15, about 84:16, about 83:17, about 82:18, about 81:19, about 80:20, about 79:21, about 78:22, about 77:23, about 76:24, about 75:25, about 74:26, about 73:27, about 72:28, about 71:29, about 70:30, about 69:31, about 68:32, about 67:33, about 66:34, about 65:35, about 64:36, about 63:37, about 62:38, about 61:39, about 60:40, about 59:41, about 58:42, about 57:43, about 56:44, about 55:45, about 54:46, about 53:47, about 52:48, about 51:49, about 50:50, about 49:51, about 48:52, about 47:53, about 46:54, about 45:55, about 44:56, about 43:57, about 42:58, about 41:59, about 40:60, about 39:61, about 38:62, about 37:63, about 36:64, about 35:65, about 34:66, about 33:67, about 32:68, about 31 :69, about 30:70, about 29:71, about 28:72, about 27:73, about 26:74, about 25:75, about 24:76, about 23:77, about 22:78, about 21 :79, about 20:80, about 19:81, about 18:82, about 17:83, about 16:84, about 15:85, about 14:86, about 13:87, about 12:88, about 11 :89, about 10:90, about 9:91, about 8:92, about 7:93, about 6:94, about 5:95, about 4:96, about 3:97, about 2:98, or about 1 :99.

In an embodiment, the silk fibroin coated materials of the invention, for example a fiber, a yarn, or a fabric, may be coated with compositions including low molecular weight silk, medium molecular weight silk, and high molecular weight silk. In an embodiment, the w/w ratio between low molecular weight silk, medium molecular weight silk, and high molecular weight silk is about 1 : 1 :8, 1 :2:7, 1 :3:6, 1 :4:5, 1 :5:4, 1 :6:3, 1 :7:2, 1 :8: 1, 2: 1 :7, 2:2:6, 2:3:5, 2:4:4, 2:5:3, 2:6:2, 2:7: 1, 3: 1 :6, 3:2:5, 3:3:4, 3:4:3, 3:5:2, 3:6: 1, 4: 1 :5, 4:2:4, 4:3:3, 4:4:2, 4:5: 1, 5: 1 :4, 5:2:3, 5:3:2, 5:4: 1, 6: 1 :3, 6:2:2, 6:3: 1, 7: 1 :2, 7:2: 1, or 8: 1 : 1. In an embodiment, the w/w ratio between low molecular weight silk, medium molecular weight silk, and high molecular weight silk is about 3:0.1 :0.9, 3:0.2:0.8, 3:0.3:0.7, 3:0.4:0.6, 3:0.5:0.5, 3:0.6:0.4, 3:0.7:0.3, 3:0.8:0.2, or 3:0.9:0.1.

According to aspects illustrated herein, pure silk fibroin-based protein fragments from aqueous solutions of the present disclosure can be formed into yarns and fabrics including for example, woven or weaved fabrics, and these fabrics can be used in textiles, as described above.

In some embodiments, the fiber or yarn may be selected from the group consisting of synthetic fiber or yarn, or combinations thereof.

In some embodiments, the fabric may exhibit an improved property, wherein the improved property may be an accumulative one-way transport capability increase relative to uncoated fabric selected from the group consisting of 1.2 fold, 1.5 fold, 2.0 fold, 3.0 fold, 4.0 fold, 5.0 fold, and 10 fold.

In some embodiments, the fabric may exhibit an improved property, wherein the improved property may be an overall moisture management capability selected from the group consisting of greater than 0.05, greater than 0.10, greater than 0.15, greater than 0.20, greater than 0.25, greater than 0.30, greater than 0.35, greater than 0.40, greater than 0.50, greater than 0.60, greater than 0.70, and greater than 0.80. In some embodiments, the improved property may be determined after a period of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In some embodiments, the fabric may exhibit substantially no increase in microbial growth after a number of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles. In some embodiments, the microbial growth may be microbial growth of a microbe selected from the group consisting of Staphylococcus aureus, Klebsiella pneumoniae, and combinations thereof. In some embodiments, the microbial growth may be reduced by a percentage selected from the group consisting of 50 %, 100 %, 500 %, 1000 %, 2000 %, and 3000 % compared to an uncoated fabric.

In some embodiments, the coating may be applied to the fabric at the fiber level prior to forming the fabric.

In some embodiments, the coating may be applied to the fabric at the fabric level. In some embodiments, the fabric may be bath coated. In some embodiments, the fabric may be spray coated. In some embodiments, the fabric may be coated with a stencil. In some embodiments, the coating may be applied to at least one side of the fabric using a method selected from the group consisting of a bath coating process, a spray coating process, a stencil process, a silk-foam based process, and a roller-based process.

In some embodiments, the coating may have a thickness of about one nanolayer.

In some embodiments, the coating may have a thickness selected from the group consisting of about 5 nm, about 10 nm, about 15 nm, about 20 nm, about 25 nm, about 50 nm, about 100 nm, about 200 nm, about 500 nm, about 1 μιτι, about 5 μιτι, about 10 μη and about 20 μιτι.

In some embodiments, the coating may be adsorbed on the fabric.

In some embodiments, the coating may be attached to the fabric through chemical, enzymatic, thermal, or irradiative cross-linking.

In some embodiments, the hand of the coated fabric may be improved relative to an uncoated fabric. In some embodiments, the hand of the coated fabric that may be improved may be selected from the group consisting of softness, crispness, dryness, silkiness, and combinations thereof.

In some embodiments, a flame retardation property of the coated fabric may be improved relative to an uncoated fabric.

In some embodiments, a flame retardation property of an uncoated fabric may not be adversely affected by the coating.

In some embodiments, the abrasion resistance may be improved relative to an uncoated fabric.

In an embodiment, the invention may include an article comprising a textile having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa.

In some embodiments, the silk based proteins or protein fragments thereof have an average weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof have a polydispersity of between about 1.5 and about 3.0, or between about 1.0 and about 5.0, and wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days.

In some embodiments, at least one property of the article may be improved, wherein the property that may be improved may be selected from the group consisting of color retention, resistance to microbial growth, resistance to bacterial growth, resistance to fungal growth, resistance to the buildup of static electrical charge, resistance to the growth of mildew, transparency of the coating, resistance to fireeze- thaw cycle damage, resistance from abrasion, blocking of ultraviolet (UV) radiation, regulation of the body temperature of a wearer, resistance to tearing, elasticity of the article, rebound dampening, tendency to cause itching in the wearer, thermal insulation of the wearer, wrinkle resistance, stain resistance, stickiness to skin, and flame resistance. In some embodiments, the article may be a textile used for apparel.

In some embodiments, the article may be fabricated as an item selected from the group consisting of an item of athletic apparel, an item of outdoor gear, a jacket, an overcoat, a shoe, a sneaker, a glove, an umbrella, a chair, a blanket, a towel, a surgical drape, a surgical gown, a laboratory coat, a wound dressing, a sterilization wrap, a surgical face mask, a surgical sleeve, a laboratory sleeve, a retention bandage, a support device, a compression bandage, a shoe cover, and a surgical blanket.

In some embodiments, the article may be a textile, leather, or foam used to fabricate an automotive product.

In some embodiments, the article may be fabricated as an item selected from the group consisting of an upholstery, a foam cushion, a fabric cushion, a floor mat, a vehicle carpet, an automotive trim, a children's car seat, a seat belt, a safety hamess, a headrest, an armrest, a dashboard, a sunvisor, a seat, an interior panel, an airbag, an airbag cover, a wiring harness, or an insulation. In an embodiment, the invention may include a method of coating a fabric that may include the step of optionally applying a pretreatment selected from the group consisting of a wetting agent, a detergent, a sequestering or dispersing agent, an enzyme, a bleaching agent, an antifoaming agent, an anti-creasing agent, a dye dispersing agent, a dye leveling agent, a dye fixing agent, a dye special resin agent, a dye anti-reducing agent, a pigment dye system anti-migrating agent, a pigment dye system binder, a delave agent, a wrinkle free treatment, a softener, a handle modifier, a waterborne polyurethane dispersion, a finishing resin, an oil or water repellant, a flame retardant, a crosslinker, a thickener for technical finishing, or any combination thereof. In an embodiment, the method may include the step of applying a coating that may include a solution of silk based proteins or fragments thereof that may have an average molecular weight range of about 5 kDa to about 144 kDa, or about 1 kDa to about 350 kDa, using a process selected from the group consisting of a continuous spray process, a continuous screen or stencil process, a continuous bath process, a batch spray process, a batch screen or stencil process, and a batch bath process. In an embodiment, the method may include the step of drying and optionally curing the coating.

In an embodiment, the silk based proteins or protein fragments thereof may have an average weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof may have a polydispersity of between about 1.0 and about 5.0, or between about 1.5 and about 3.0, and optionally wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days.

BRIEF DESCRIPTION OF THE DRAWINGS

The presently disclosed embodiments will be further explained with reference to the attached drawings. The drawings shown are not necessarily to scale, with emphasis instead generally being placed upon illustrating the principles of the presently disclosed embodiments.

FIG. 1A is a photograph of wool tubular fabric control sample no. 17056902 after one laundering cycle.

FIG. IB is a photograph of wool tubular fabric control sample no. 17042001 after one laundering cycle.

FIG. 2A is a photograph of silk coated wool tubular fabric sample no. 17051003 after one laundering cycle.

FIG. 2B is a photograph of silk coated wool tubular fabric sample no. 17051001 after one laundering cycle.

FIG. 3 is a photograph of several wool tubular fabric control samples after two laundering cycles.

FIG. 4 is a photograph of several silk coated wool tubular fabric samples after two laundering cycles.

FIG. 5 A is a photograph of wool tubular fabric control sample no. 17042001 after five laundering cycles.

FIG. 5B is a photograph of wool tubular fabric control sample no. 17042002 after five laundering cycles. FIG. 5C is a photograph of wool tubular fabric control sample no. 17050901 after five laundering cycles.

FIG. 5D is a photograph of wool tubular fabric control sample no. 17050902 after five laundering cycles.

FIG. 6A is a photograph of silk coated wool tubular fabric sample no. 17051101 after five laundering cycles.

FIG. 6B is a photograph of silk coated wool tubular fabric sample no. 17051003 after five laundering cycles.

FIG. 6C is a photograph of silk coated wool tubular fabric sample no. 17051001 after five laundering cycles.

FIG. 6D is a photograph of silk coated wool tubular fabric sample no. 17051002 after five laundering cycles.

FIG. 7A - 7C are a series of SEM photographs of citric acid control wool tubular fabric sample no. 17060105 at 500x and lOOOx magnification.

FIG. 8A - 8C are a series of SEM photographs of methanol control wool tubular fabric sample no. 17060106 at 500x and lOOOx magnification.

FIG. 9A - 9C are a series of SEM photographs of citric acid control wool tubular fabric sample no. 17060107 at 500x and lOOOx magnification.

FIG. 10A - IOC are a series of SEM photographs of methanol control wool tubular fabric sample no. 17060108 at 500x and lOOOx magnification.

FIG. 11A - l lC are a series of SEM photographs of citric acid control wool tubular fabric sample no. 17060201 at 500x and lOOOx magnification.

FIG. 12A - 12C are a series of SEM photographs of methanol control wool tubular fabric sample no. 17060202 at 500x and lOOOx magnification.

FIG. 13A - 13C are a series of SEM photographs of citric acid control wool tubular fabric sample no. 17060203 at 500x and lOOOx magnification.

FIG. 14A - 14C are a series of SEM photographs of methanol control wool tubular fabric sample no. 17060204 at 500x and lOOOx magnification. FIG. 15A - 15C are a series of SEM photographs of silk coated wool tubular fabric sample no. 17051001 at 500x and l OOOx magnification.

FIG. 16A - 16C are a series of SEM photographs of silk coated wool tubular fabric sample no. 17051002 at 500x and l OOOx magnification. FIG. 17A - 17C are a series of SEM photographs of silk coated wool tubular fabric sample no. 17051003 at 500x and l OOOx magnification.

FIG. 18A - 18C are a series of SEM photographs of silk coated wool tubular fabric sample no. 17051 101 at 500x and l OOOx magnification.

FIG. 19A - 19C are a series of SEM photographs of wool tubular fabric control sample no. 17042001 at 500x and lOOOx magnification.

FIG. 20A - 20C are a series of SEM photographs of wool tubular fabric control sample no. 17042002 at 500x and lOOOx magnification.

FIG. 21A - 21C are a series of SEM photographs of wool tubular fabric control sample no. 17050901 at 500x and lOOOx magnification. FIG. 22A and 22B are two SEM photographs of wool tubular fabric control sample no. 17050902 at 500x and lOOOx magnification.

FIG. 23 is a chart summarizing dimensional stability to laundering (Woolmark Test Method) of NeW 1 -42.8 with 18.9 micron NS wool samples, including the dimensional stability of a silk coated sample, the dimensional stability of a control sample, the dimensional stability of a citric acid pretreated and silk coated sample, and the dimensional stability of a silk coated and finally treated sample.

FIG. 24 is a chart summarizing dimensional stability to laundering (Woolmark Test Method) of NeW 1 -30 with 21.0 micron NS wool samples, including the dimensional stability of a silk coated sample, the dimensional stability of a control sample, the dimensional stability of a citric acid pretreated and silk coated sample, and the dimensional stability of a silk coated and finally treated sample.

FIG. 25 is a chart summarizing dimensional stability to laundering (Woolmark Test Method) of NeW 2-60 with 18.5 micron SW wool samples, including the dimensional stability of a silk coated sample, the dimensional stability of a control sample, the dimensional stability of a citric acid pretreated and silk coated sample, and the dimensional stability of a silk coated and finally treated sample. FIG. 26 is a chart summarizing dimensional stability to laundering (Woolmark Test Method) of NeW 1-27 with 23.5 micron SW wool samples, including the dimensional stability of a silk coated sample, the dimensional stability of a control sample, the dimensional stability of a citric acid pretreated and silk coated sample, and the dimensional stability of a silk coated and finally treated sample.

FIG. 27 is a chart summarizing dimensional stability to laundering (AATCC Test Method) of NeW 1-42.8 with 18.9 micron NS wool samples, including the dimensional stability of a silk coated sample, the dimensional stability of a control sample, the dimensional stability of a citric acid pretreated and silk coated sample, and the dimensional stability of a silk coated and finally treated sample.

FIG. 28 is a chart summarizing dimensional stability to laundering (AATCC Test Method) of NeW 1-30 with 21.0 micron NS wool samples, including the dimensional stability of a silk coated sample, the dimensional stability of a control sample, the dimensional stability of a citric acid pretreated and silk coated sample, and the dimensional stability of a silk coated and finally treated sample.

FIG. 29 is a chart summarizing dimensional stability to laundering (AATCC Test Method) of NeW 2-60 with 18.5 micron SW wool samples, including the dimensional stability of a silk coated sample, the dimensional stability of a control sample, the dimensional stability of a citric acid pretreated and silk coated sample, and the dimensional stability of a silk coated and finally treated sample.

FIG. 30 is a chart summarizing dimensional stability to laundering (AATCC Test Method) of NeW 1-27 with 23.5 micron SW wool samples, including the dimensional stability of a silk coated sample, the dimensional stability of a control sample, the dimensional stability of a citric acid pretreated and silk coated sample, and the dimensional stability of a silk coated and finally treated sample.

FIG. 31 A to FIG. 3 ID are a series of charts summarizing dimensional stability to laundering (AATCC Test Method 135-2015) of CHA-17101902-T001 (control) and CHA-17101902-T002 (silk coated) cashmere fabric samples, including a chart illustrating the length changes over the course of five washes (FIG. 31 A), a chart illustrating the change in average lengths after each wash over the course of four washes (FIG. 3 IB), a chart illustrating the area dimensional change % through four washes based from the original state lengths (FIG. 31C), and a chart illustrating the area dimensional change % through four washes based from the state lengths after one wash (FIG. 3 ID).

FIG. 32 is a chart illustrating the average water drop absorption times for various silk coated fabric samples before laundering (t=0), and after 10, 25, or 50 laundering cycles.

FIG. 33A is a graph illustrating wetting time with spray coating; FIG. 33B is a graph illustrating wetting time with stencil coating; FIG. 33C is a graph illustrating wetting time with bath coating; FIG. 33D is a graph illustrating wetting time with screen coating.

FIG. 34A is a graph illustrating absorption time with spray coating; FIG. 34B is a graph illustrating absorption time with stencil coating; FIG. 34C is a graph illustrating absorption time with bath coating; FIG. 34D is a graph illustrating absorption time with screen coating.

FIG. 35A is a graph illustrating spreading speed with spray coating; FIG. 35B is a graph illustrating spreading speed with stencil coating; FIG. 35C is a graph illustrating spreading speed with bath coating; FIG. 35D is a graph illustrating spreading speed with screen coating.

FIG. 36A is a graph illustrating accumulative one-way transport index with spray coating; FIG. 36B is a graph illustrating accumulative one-way transport index with stencil coating; FIG. 36C is a graph illustrating accumulative one-way transport index with bath coating; FIG. 36D is a graph illustrating accumulative one-way transport index with screen coating.

FIG. 37A is a graph illustrating overall moisture management capability with spray coating; FIG. 37B is a graph illustrating overall moisture management capability with stencil coating; FIG. 37C is a graph illustrating overall moisture management capability with bath coating; FIG. 37D is a graph illustrating overall moisture management capability with screen coating.

FIG. 38A is a graph illustrating wetting time top; FIG. 38B is a graph illustrating wetting time bottom.

FIG. 39A is a graph illustrating top absorption rate; FIG. 39B is a graph illustrating bottom absorption rate. FIG. 40 A is a graph illustrating top max wetted radius; FIG. 40B is a graph illustrating bottom max wetted radius.

FIG. 41 A is a graph illustrating top spreading speed; FIG. 41B is a graph illustrating bottom spreading speed.

FIG. 42A is a graph illustrating accumulative one-way transport index; FIG.

42B is a graph illustrating overall moisture management capability.

FIG. 43A is a graph illustrating wetting time of non-wicking finished; FIG. 43B is a graph illustrating wetting time of semi-finished before final setting.

FIG. 44A is a graph illustrating absorption time of non-wicking finished; FIG. 44B is a graph illustrating absorption time of semi -finished before final setting.

FIG. 45A is a graph illustrating spreading speed of non-wicking finished; FIG. 45B is a graph illustrating spreading speed of semi-finished before final setting.

FIG. 46A is a graph illustrating accumulative one-way transport index of non- wicking finished; FIG. 46B is a graph illustrating accumulative one way transport index of semi-finished before final setting.

FIG. 47A is a graph illustrating overall moisture management capability of non-wicking finished. FIG. 47B is a graph illustrating overall moisture management capability of semi-finished before final setting.

FIG. 48A is a graph illustrating wetting time with spray coating. FIG. 48B is a graph illustrating wetting time with stencil coating. FIG. 48C is a graph illustrating wetting time with bath coating.

FIG. 49A is a graph illustrating absorption time with spray coating. FIG. 49B is a graph illustrating absorption time with stencil coating. FIG. 49C is a graph illustrating absorption time with bath coating.

FIG. 50A is a graph illustrating spreading speed with spray coating. FIG. 50B is a graph illustrating spreading speed with stencil coating. FIG. 50C is a graph illustrating spreading speed with bath coating.

FIG. 51 A is a graph illustrating accumulative one-way transport index with spray coating. FIG. 5 IB is a graph illustrating accumulative one-way transport index with stencil coating. FIG. 51C is a graph illustrating accumulative one-way transport index with bath coating.

FIG. 52A is a graph illustrating overall moisture management capability with spray coating. FIG. 52B is a graph illustrating overall moisture management capability with stencil coating. FIG. 52C is a graph illustrating overall moisture management capability with bath coating.

FIG. 53 A is a graph illustrating wetting time with 1% SFS. FIG. 53B is a graph illustrating wetting time with 0.1% SFS.

FIG. 54A is a graph illustrating absorption time with 1% SFS. FIG. 54B is a graph illustrating absorption time with 0.1% SFS.

FIG. 55A is a graph illustrating spreading speed with 1% SFS. FIG. 55B is a graph illustrating spreading speed with 0.1% SFS.

FIG. 56A is a graph illustrating accumulative one-way transport index with 1% SFS. FIG. 56B is a graph illustrating accumulative one-way transport index with 0.1% SFS.

FIG. 57A is a graph illustrating overall moisture management capability with 1% SFS. FIG. 57B is a graph illustrating overall moisture management capability with 0.1% SFS.

FIG. 58A is a graph illustrating summary of wetting time top. FIG. 58B is a graph illustrating summary of wetting time bottom.

FIG. 59A is a graph illustrating summary of top absorption rate. FIG. 59B is a graph illustrating summary of bottom absorption rate.

FIG. 60 A is a graph illustrating summary of top max wetted radius. FIG. 60B is a graph illustrating summary of bottom wetted radius.

FIG. 61 A is a graph illustrating summary of top spreading speed. FIG. 61 B is a graph illustrating summary of bottom spreading speed.

FIG. 62A is a graph illustrating summary of accumulative one-way transport index. FIG. 62B is a graph illustrating summary of overall moisture management capability.

FIG. 63 illustrates bacterial growth results. FIG. 64 illustrates bacterial growth results.

FIG. 65 illustrates bacterial growth results.

FIG. 66 illustrates bacterial growth results.

FIG. 67 illustrates bacterial growth results.

FIG. 68 illustrates accumulative one-way transport index versus fabric washing cycles.

FIG. 69 illustrates overall moisture management capability (OMMC) versus fabric washing cycles.

FIG. 70 illustrates wetting time at the top of the fabric versus fabric washing cycles.

FIG. 71 illustrates wetting time at the bottom of the fabric versus fabric washing cycles.

FIG. 72 illustrates absorption rate at the top of the fabric versus fabric washing cycles.

FIG. 73 illustrates absorption rate at the bottom of the fabric versus fabric washing cycles.

FIG. 74 illustrates spreading speed at the top of the fabric versus fabric washing cycles.

FIG. 75 illustrates spreading speed at the bottom of the fabric versus fabric washing cycles.

FIG. 76 illustrates wetted radius at the top of the fabric versus fabric washing cycles.

FIG. 77 illustrates wetted radius at the bottom of the fabric versus fabric washing cycles.

FIG. 78 illustrates percent reduction in growth of Staphylococcus aureus

ATCC 6538 versus fabric washing cycles.

FIG. 79 illustrates percent reduction in growth of Klebisiella pneumoniae ATCC 4354 versus fabric washing cycles. FIG. 80 illustrates a scanning electron microscopy image of fabric sample FAB-01-BATH-B (first view).

FIG. 81 illustrates a scanning electron microscopy image of fabric sample FAB-01-BATH-B (third view).

FIG. 82 illustrates a scanning electron microscopy image of fabric sample

FAB-01-BATH-B (fourth view).

FIG. 83 illustrates a scanning electron microscopy image of fabric sample FAB-01-SPRAY-B (first view).

FIG. 84 illustrates a scanning electron microscopy image of fabric sample FAB-01-SPRAY-B (second view).

FIG. 85 illustrates a scanning electron microscopy image of fabric sample FAB-01-SPRAY-B (fifth view).

FIG. 86 illustrates a scanning electron microscopy image of fabric sample FAB-01-SPRAY-B (sixth view).

FIG. 87 illustrates a scanning electron microscopy image of fabric sample

FAB-01-SPRAY-C (first view).

FIG. 88 illustrates a scanning electron microscopy image of fabric sample FAB-01-SPRAY-C (second view).

FIG. 89 illustrates a scanning electron microscopy image of fabric sample

FAB-01-SPRAY-C (fourth view).

FIG. 90 illustrates a scanning electron microscopy image of fabric sample FAB-01-STEN-C (first view).

FIG. 91 illustrates a scanning electron microscopy image of fabric sample FAB-01-STEN-C (second view).

FIG. 92 illustrates a scanning electron microscopy image of fabric sample FAB-01-STEN-C (seventh view).

FIG. 93 illustrates a scanning electron microscopy image of fabric sample FAB-01-STEN-C (ninth view). FIG. 94 illustrates a scanning electron microscopy image of fabric sample FAB-10-BATH-B (first view).

FIG. 95 illustrates a scanning electron microscopy image of fabric sample FAB-10-BATH-B (second view).

FIG. 96 illustrates a scanning electron microscopy image of fabric sample FAB-10-BATH-B (third view).

FIG. 97 illustrates a scanning electron microscopy image of fabric sample FAB-10-BATH-B (fourth view).

FIG. 98 illustrates a scanning electron microscopy image of fabric sample FAB-10-BATH-B (fifth view).

FIG. 99 illustrates a scanning electron microscopy image of fabric sample FAB-10-BATH-C (first view).

FIG. 100 illustrates a scanning electron microscopy image of fabric sample FAB-10-BATH-C (second view).

FIG. 101 illustrates a scanning electron microscopy image of fabric sample FAB-10-BATH-C (third view).

FIG. 102 illustrates a scanning electron microscopy image of fabric sample FAB-10-BATH-C (fourth view).

FIG. 103 illustrates a scanning electron microscopy image of fabric sample FAB- 10-BATH-C (fifth view).

FIG. 104 illustrates a scanning electron microscopy image of fabric sample FAB-10-BATH-C (sixth view).

FIG. 105 illustrates a scanning electron microscopy image of fabric sample FAB- 10-BATH-C (seventh view).

FIG. 106 illustrates a scanning electron microscopy image of fabric sample FAB-10-SPRAY-B (first view).

FIG. 107 illustrates a scanning electron microscopy image of fabric sample FAB- 10-SPRAY-B (second view). FIG. 108 illustrates a scanning electron microscopy image of fabric sample FAB-10-SPRAY-B (fourth view).

FIG. 109 illustrates a scanning electron microscopy image of fabric sample FAB-10-SPRAY-B (fifth view).

FIG. 110 illustrates a scanning electron microscopy image of fabric sample

FAB-10-SPRAY-B (sixth view).

FIG. I l l illustrates a scanning electron microscopy image of fabric sample FAB-10-SPRAY-B (seventh view).

FIG. 112 illustrates a scanning electron microscopy image of fabric sample FAB-10-SPRAY-C.

FIG. 113 illustrates a scanning electron microscopy image of fabric sample FAB-10-STEN-B (first view).

FIG. 114 illustrates a scanning electron microscopy image of fabric sample FAB-10-STEN-B (third view).

FIG. 115 illustrates a scanning electron microscopy image of fabric sample

FAB-10-STEN-B (fifth view).

FIG. 116 illustrates a scanning electron microscopy image of fabric sample FAB-10-STEN-B (sixth view).

FIG. 117 illustrates a scanning electron microscopy image of fabric sample FAB-10-STEN-B (seventh view).

FIG. 118 illustrates a scanning electron microscopy image of a fabric control sample (first view).

FIG. 119 illustrates a scanning electron microscopy image of a fabric control sample (second view).

FIG. 120 illustrates a scanning electron microscopy image of a fabric control sample (third view).

FIG. 121 shows results from optical profiling measurements on the Mylar Control sample taken at the top, location 1 (shiny side). FIG. 122 shows results from optical profiling measurements on the Mylar Control sample taken at the bottom, location 2 (more matte side).

FIG. 123 shows results from optical profiling measurements on the Melinex Control sample taken at the top, location 1.

FIG. 124 shows results from optical profiling measurements on the Melinex

Control sample taken at the bottom, location 2.

FIG. 125 shows results from optical profiling measurements on sample FIL-10- SPRAY-B-01MYL taken at the top, location 1.

FIG. 126 shows results from optical profiling measurements on sample FIL-10- SPRAY-B-01MYL taken at the bottom, location 2.

FIG. 127 shows results from optical profiling measurements on sample FIL-01- SPRAY-B-01MYL taken at the top, location 1.

FIG. 128 shows results from optical profiling measurements on sample FIL-01- SPRAY-B-01MYL taken at the bottom, location 2.

FIG. 129 shows results from optical profiling measurements on sample FIL-01-

SPRAY-B-007MEL taken the top, location 1.

FIG. 130 shows results from optical profiling measurements on sample FIL-01- SPRAY-B-007MEL taken at the bottom, location 2.

FIG. 131 shows results from optical profiling measurements on sample FIL-01- SPRAY-C-01MYL taken at the top, location 1.

FIG. 132 shows results from optical profiling measurements on sample FIL-01- SPRAY-C-01MYL taken at bottom, location 2

FIG. 133 shows results from optical profiling measurements on sample FIL-01- STEN-B-01MYL taken at the top, location 1.

FIG. 134 shows results from optical profiling measurements on sample FIL-01-

STEN-B-01MYL taken at the bottom, location 2.

FIG. 135 shows results from optical profiling measurements on sample FIL-01- STEN-C-01MYL taken at the top, location 1. FIG. 136 shows results from optical profiling measurements on sample FIL-01- STEN-C-01MYL taken at the bottom, location 2.

FIG. 137 shows results from optical profiling measurements on sample FIL-10- B ATH-B-01 MYL taken at the top, location 1.

FIG. 138 shows results from optical profiling measurements on sample FIL- 10-

B ATH-B-01 MYL taken at the bottom, Location 2.

FIG. 139 shows results from optical profiling measurements on sample FIL-10- BATH-B-007MEL taken at the top, location 1.

FIG. 140 shows results from optical profiling measurements on sample FIL-10- BATH-B-007MEL taken at the bottom, location 2.

FIG. 141 shows results from optical profiling measurements on sample FIL-10- BATH-C-01MYL taken at top, location 1.

FIG. 142 shows results from optical profiling measurements on sample FIL-10- BATH-C-01MYL taken at the bottom, location 2.

FIG. 143 shows results from optical profiling measurements on sample FIL-01-

B ATH-B-01 MYL taken at the top, location 1.

FIG. 144 shows results from optical profiling measurements on sample FIL-01- B ATH-B-01 MYL taken at the bottom, location 2.

FIG. 145 illustrates a scanning electron microscopy image of film sample FIL- 01-SPRAY-B-OlMYL cross-section.

FIG. 146 illustrates a scanning electron microscopy image of film sample FIL- 01-SPRAY-B-OlMYL cross-section.

FIG. 147 illustrates a scanning electron microscopy image of film sample FIL- 01-SPRAY-B-OlMYL cross-section.

FIG. 148 illustrates a scanning electron microscopy image of film sample FIL-

10-BATH-C-OlMYL cross-section.

FIG. 149 illustrates accumulative one-way transport index results for natural fibers.

FIG. 150 illustrates overall moisture management capability for natural fibers. FIG. 151 illustrates flammability test results for a cotton interlock fabric with (16021103) and without (16021101) coating with 1% silk fibroin solution.

FIG. 152 illustrates flammability test results for a cotton interlock fabric with (16021103) and without (16021101) coating with 1% silk fibroin solution.

FIG. 153 illustrates flammability test results for a polyester double knit fabric with (16021104) and without (16021102) coating with 1% silk fibroin solution.

FIG. 154 illustrates flammability test results for a polyester double knit fabric with (16021104) and without (16021102) coating with 1% silk fibroin solution.

FIG. 155 illustrates abrasion test results for a cotton interlock fabric with (16021501) and without (16021101) coating with 1% silk fibroin solution.

FIG. 156 illustrates abrasion test results for a polyester double knit fabric with (16021502) and without (16021102) coating with 1% silk fibroin solution.

FIG. 157 illustrates a scanning electron microscope image of sample 16041301.

FIG. 158 illustrates a scanning electron microscope image of sample 16041301.

FIG. 159 illustrates a scanning electron microscope image of sample 16041301.

FIG. 160 illustrates a scanning electron microscope image of sample 16041302.

FIG. 161 illustrates a scanning electron microscope image of sample 16041302.

FIG. 162 illustrates a scanning electron microscope image of sample 16041302.

FIG. 163 illustrates a scanning electron microscope image of sample 16041303.

FIG. 164 illustrates a scanning electron microscope image of sample 16041303.

FIG. 165 illustrates a scanning electron microscope image of sample 16041303.

FIG. 166 illustrates a scanning electron microscope image of sample 16041303.

FIG. 167 illustrates a scanning electron microscope image of sample 16041304.

FIG. 168 illustrates a scanning electron microscope image of sample 16041304.

FIG. 169 illustrates a scanning electron microscope image of sample 16041304.

FIG. 170 illustrates a scanning electron microscope image of sample 16041305.

FIG. 171 illustrates a scanning electron microscope image of sample 16041305. FIG. 172 illustrates a scanning electron microscope image of sample 16041305. FIG. 173 illustrates a scanning electron microscope image of sample 16041306. FIG. 174 illustrates a scanning electron microscope image of sample 16041306. FIG. 175 illustrates a scanning electron microscope image of sample 16041306. FIG. 176 illustrates a scanning electron microscope image of sample 16041306. FIG. 177 illustrates a scanning electron microscope image of sample 16040803. FIG. 178 illustrates a scanning electron microscope image of sample 16040803. FIG. 179 illustrates a scanning electron microscope image of sample 16040803. FIG. 180 illustrates a scanning electron microscope image of sample 16040808. FIG. 181 illustrates a scanning electron microscope image of sample 16040808. FIG. 182 illustrates a scanning electron microscope image of sample 16040808. FIG. 183 illustrates an exemplary padder roller.

FIG. 184 illustrates an exemplary kiss roller.

FIG. 185 illustrates the process of unrolling an exemplary fabric roller.

FIG. 186 illustrates a square of sample fabric to be coated.

FIG. 187 illustrates an exemplary stainless steel bath.

FIG. 188 illustrates a padder unit having two rollers.

FIG. 189 illustrates a curing frame without fabric provided thereon.

FIG. 190 illustrates a curing frame with fabric provided thereon.

FIG. 191 illustrates an exemplary curing oven.

FIG. 192 illustrates a cooling rack with a curing frame and fabric provided thereon.

FIG. 193 illustrates a table that provides testing results for wetting time, absorption rate, wetted radius, spreading speed, accumulative one-way transport, and overall moisture management capability (OMMC) for sample nos. 16040101, 16040102, 16040103,16040104, 16040105, and 16040106. FIG. 194 illustrates testing results in grades for wetting time, absorption rate, wetted radius, spreading speed, accumulative one-way transport, and OMMC for 16040101, 16040102, 16040103, 16040104, 16040105, and 16040106.

FIG. 195 illustrates testing results for wetting time, absorption rate, wetted radius, spreading speed, accumulative one-way transport, and OMMC for 16040801, 16040802, 16040803, 16040804, 16040805, 16040806, 16040807, and 16040808.

FIG. 196 illustrates testing results in grades for wetting time, absorption rate, wetted radius, spreading speed, accumulative one-way transport, and OMMC for 16040801, 16040802, 16040803, 16040804, 16040805, 16040806, 16040807, and 16040808.

FIG. 197 illustrates testing results for wetting time, absorption rate, wetted radius, spreading speed, accumulative one-way transport, and OMMC for 16041201, 16041202, 16041302, 16041303, 16041203, 16041204, 16041305, 16041306,

16041301, and 16041304.

FIG. 198 illustrates testing results in grades for wetting time, absorption rate, wetted radius, spreading speed, accumulative one-way transport, and OMMC for 16041201, 16041202, 16041302, 16041303, 16041203, 16041204, 16041305, 16041306, 16041301, and 16041304.

FIG. 199 illustrates testing results for wetting time, absorption rate, wetted radius, spreading speed, accumulative one-way transport, and OMMC for 16041301,

16041302, 16041303, 16041304, 16041305, 16041306, 16042001, 16040101, and 16040106.

FIG. 200 illustrates testing results in grades for wetting time, absorption rate, wetted radius, spreading speed, accumulative one-way transport, and OMMC for 16041301, 16041302, 16041303, 16041304, 16041305, 16041306, 16042001, 16040101, and 16040106.

FIG. 201 illustrates a map of Liquid Moisture Management Test results for various coated fabrics described herein

FIG. 202 illustrates drapability coefficient testing results for various SFS coated fabrics. FIG. 203 illustrates drapability coefficient testing results for an SFS coated fabric after mechanical and steam finishing.

FIG. 204 illustrates the results of a solution depletion calculation during coating.

FIG. 205 illustrates samples used in moisture management testing.

FIG. 206 illustrates the results of moisture management testing.

FIG. 207 illustrates samples used in moisture management testing.

FIG. 208 illustrates the results of moisture management testing.

FIG. 209 illustrates samples used in moisture management testing.

FIG. 210 illustrates the results of moisture management testing.

FIG. 211 illustrates samples used in antimicrobial testing.

FIG. 212 illustrates the results of a water drop test on polyester/lycra knitted fabric treated with Ultratex CSP.

FIG. 213 illustrates the results of a water drop test on polyester/lycra knitted fabric treated with Ultratex SI.

FIG. 214 illustrates the results of a water drop test on polyester/lycra knitted fabric treated with Ultratex CSP.

FIG. 215 illustrates the results of a water drop test on polyester/lycra knitted fabric treated with Ultratex SI.

FIG. 216 illustrates the results of a water drop test on polyester/lycra knitted fabric treated with RODI water or tap water.

FIG. 217A illustrates a silk-coated cotton SEM image; scalebar represents 2 μιτι. FIG. 217B illustrates a silk-coated cotton SEM image; scalebar represents 10 μιη.

FIG. 218 illustrates manipulating water absorbency of liquid silk coated fabric. The time needed for a standard water drop to fully absorb into the fabric is recorded, and varies according to the silk treatment.

FIG. 219 illustrates various process parameters for coating fabrics.

FIG. 220 illustrates that liquid silk application significantly reduces pilling on cashmere; the pilling score of each cashmere panel, as measured according to ISO 12945-1 : Score 5 = No change; Score 4 = Slight surface fuzzing and/or partially formed pills; Score 3 = Moderate surface fuzzing and/or moderate pilling, pills of varying size and density partially covering the specimen surface; Score 2 = Distinct surface fuzzing and/or severe pilling, pills of varying size and density covering a large proportion of the specimen; Score 1 = Dense surface fuzzing and/or severe pilling, pills of varying size and density covering the whole of the specimen surface. Silk Formulation A: 0.05% M Silk; pH unadjusted, STI-18050801-T004. Silk Formulation B: 0.25% M Silk; pH 9.25, STI-18050801-T009. Silk Formulation C: 0.25% 3L1M Silk, pH unadjusted, STI- 18050801-T005.

FIG. 221 A (control) and FIG. 22 IB (cashmere treated with silk) illustrate cashmere coating coverage by scanning electron microscopy (SEM); as liquid silk and cashmere bond naturally, SEM demonstrates that liquid silk smooths and refines cashmere fibers.

FIG. 222A (microscopic image) and FIG. 222B (dye intensity chart) illustrate deposition of FITC labeled silk fragments preferentially on cashmere cuticles; cuticle edges are 15-20 microns apart, and exhibit more fluorescence than the cuticle faces. (20x objective; laser power: 12%; gain: 600; gamma: 0.45).

FIG. 223 illustrate silk protein binding and smoothing the "scales" of wool to the core fiber, preventing the "Velcro-like" effect that is responsible for wool's shrinkage and inability to withstand washing; additional data shows wool + liquid silk is water resistant, stable and shrink-resistant following washing while matching or improving pilling.

FIG. 224 illustrates improved washability of wool by area dimensional change on wool tubes finished with liquid silk compared to untreated wool tubes. Liquid silk improves area dimensional change about twofold.

FIG. 225A - 225D illustrates SEM images of silk coated wool.

FIG. 226 illustrates the coating coverage of silk fragments on polyester as shown by scanning electron microscopy (SEM); SEM confirms that after application of liquid silk, coating coverage is similar or greater than other commercial coatings for polyester. FIG. 226 A illustrates polyester unfinished control sample, showing fibers with no coating. FIG. 226B illustrates polyester finished with silk, showing coated layers on the polyester fibers. FIG. 227 illustrates EDS Data on Polyester Related Experiments; polyester fabric was coated in 6% silk (FIG. 227C) and energy-dispersive X-ray spectroscopy (EDS) was used to determine chemical content (FIG. 227 A and FIG. 227B); EDS suggests regions between fibers (FIG. 227B) show nitrogen content due to silk depositions regions.

FIG. 228 illustrates liquid silk coated polyester absorbency; the results indicate that the coated material exceeds commonly accepted industry criteria for absorbency, and outperformed commercial counterparts after 50 laundering cycles.

FIG. 229 illustrates dry rate in polyester samples; in general liquid silk coated polyester dried faster than commercial control before laundering and after multiple laundering cycles; AATCC Test Method 201-1013 Heated Plate Method; higher values indicate faster dry rate (silk + mechanical denotes a second water pass and drying process).

FIG. 230 illustrates vertical wicking and abrasion resistance in polyester samples. FIG. 230A: liquid silk coated polyester demonstrated improved wicking at 5 minutes vs. unfinished fabric after 3 laundering cycles. FIG. 230B: liquid silk improves abrasion resistance of polyester fabrics, and outperformed the commercial standard.

FIG. 231 illustrates pilling resistance in polyester liquid silk coated fabric which outperforms the commercial standard.

FIG. 232A and FIG. 232B illustrates silk-coated Nylon SEM images.

FIG. 233 illustrates fluorescence microscopy images for silk-coated vs. control; FIG. 233A: FITC-Silk Coated Nylon; scale bars represent 107 μιη. FIG. 233B: Uncoated Nylon Control; scale bars represent 53 μιτι. Nylon coated in FITC-Silk showed increased fluorescence due to the FITC-silk coating; 5% enhancement.

FIG. 234 illustrates coating coverage on Nylon: scanning electron microscopy

(SEM) confirms application of liquid silk. FIG. 234A: Nylon unfinished control. FIG. 234B: Nylon with silk finish - coated silk layers also adopt clear surface features.

FIG. 235A illustrates absorbency performance of coated Nylon; liquid silk coated nylon exceeded commonly accepted industry criteria for absorbency, and outperformed commercial counterparts after 50 laundering cycles (AATCC Test Method 79-2013; smaller values indicate faster absorbency, silk + mechanical denotes a second water pass and drying process). FIG. 235B illustrates dry rate performance in coated nylon; liquid silk coated nylon dried faster than commercial control before laundering and after multiple laundering cycles (AATCC Test Method 201-1013 Heated Plate Method; higher values indicate faster dry rate; silk + mechanical denotes a second water pass and drying process).

FIG. 236A illustrates vertical wi eking performance; Nylon liquid silk coated nylon demonstrated improved wi eking at 5 minutes vs. commercial finish after 3 laundering cycles (AATCC Test Method 197 (modified); higher values indicate better wicking; silk + mechanical denotes a second water pass and drying process). FIG. 236B illustrates abrasion resistance performance; Nylon liquid silk coated improves abrasion resistance of nylon; liquid silk coated nylon matched the commercial standard Abrasion Resistance - ASTM Standard D4966-12Esl (accelerated); testing ended when fabric first demonstrated abrasion or broke, whichever happened first; instead of wool, Trizact was used.

FIG. 237 illustrates the Sour Milk Test Experimental Results; liquid silk coated fabrics reduced odor more than both finished and unfinished fabrics.

FIG. 238A and FIG. 238B illustrates Sour Milk Test Experimental Results; liquid silk coated fabrics reduced odor more than both finished and unfinished fabrics.

FIG. 239 illustrates biocompatibility of liquid silk coated fabrics (by the FDA standard test to show compatibility for contact with human skin); liquid silk coated fabrics demonstrated no reactivity; multiple commercial performance fabrics failed biocompatibility testing (0 = No reactivity around or under specimen (passed); 1 = Slight reactivity, some degenerated cell under test article (passed); 2 = Mild reactivity, zone limited to area under the test article (passed); 3 = Moderate reactivity, zone of lysis extending specimen size up to 1 cm (failed); 4 = Severe, zone of lysis extending farther than 1 cm beyond specimen (failed)).

FIGS. 240A - 240D illustrate samples of fabric coated with silk formulations using a nebulizer applicator. FIG. 240 A: low MW silk; FIG. 240B: medium MW silk; FIG. 240C: low MW to medium MW 3: 1 ; FIG. 240D: control. FIGS. 240A - 240D illustrate nebulizers and the silk solutions, and control, respectively.

While the above-identified drawings set forth presently disclosed embodiments, other embodiments are also contemplated, as noted in the discussion. This disclosure presents illustrative embodiments by way of representation and not limitation. Numerous other modifications and embodiments can be devised by those skilled in the art which fall within the scope and spirit of the principles of the presently disclosed embodiments. DETAILED DESCRIPTION OF THE INVENTION

Silk Fibroin-Based Protein Fragments and Solutions Thereof

Provided herein are methods for producing pure and highly scalable silk protein fragment (SPF) mixture solutions that may be used to coat at least a portion of textiles or may be formed into usable fibers for weaving into yam. In some embodiments, SPF mixture solutions may also refer to silk fibroin solutions (SFS), and vice versa. The solutions are generated from raw pure intact silk protein material and processed in order to remove any sericin and achieve the desired weight average molecular weight (MW) and polydispersity of the fragment mixture. Select method parameters may be altered to achieve distinct final silk protein fragment characteristics depending upon the intended use. The resulting final fragment solution is pure silk protein fragments and water with PPM to non-detectable levels of process contaminants. The concentration, size and polydispersity of silk protein fragments in the solution may further be altered depending upon the desired use and performance requirements. In an embodiment, the pure silk fibroin-based protein fragments in the solution are substantially devoid of sericin, have an average weight average molecular weight ranging from about 1 kDa to about 350 kDa, and have a polydispersity ranging from about 1.0 and about 5.0. In an embodiment, the pure silk fibroin-based protein fragments in the solution are substantially devoid of sericin, have an average weight average molecular weight ranging from about 6 kDa to about 17 kDa, and have a polydispersity ranging from about 1.5 and about 3.0, or from about 1.0 and about 5.0. In an embodiment, the pure silk fibroin-based protein fragments in the solution are substantially devoid of sericin, have an average weight average molecular weight ranging from about 17 kDa to about 39 kDa, and have a polydispersity ranging from about 1.5 and about 3.0, or from about 1.0 and about 5.0. In an embodiment, the pure silk fibroin-based protein fragments in the solution are substantially devoid of sericin, have an average weight average molecular weight ranging from about 39 kDa to about 80 kDa, and have a polydispersity ranging from about 1.5 and about 3.0, or from about 1.0 and about 5.0. In an embodiment, the solutions may be used to generate articles, such as silk gels of varying gel and liquid consistencies by varying water content/concentration, or sold as a raw ingredient into the consumer market. As used herein, the term "silk solution" may refer to solutions of silk proteins, including solutions of silk fibroin-based protein fragments. Methods of making silk fibroin-based protein fragments and solutions thereof are described for example in U.S. Patents Nos. 9,187,538, 9,511,012, 9,517,191, 9,522,107, 9,522,108, and 9,545,369.

As used herein, the term "leather" refers to natural leather and synthetic leather. Natural leather includes chrome-tanned leather (e.g., tanned using chromium sulfate and other chromium salts), vegetable-tanned leather (e.g. , tanned using tannins), aldehyde-tanned leather (also known as wet-white leather, e.g. , tanned using glutaraldehyde or oxazolidine compounds), brain-tanned leather, formaldehyde-tanned leather, Chamois leather (e.g. , tanned using cod oils), rose-tanned leather (e.g. , tanned using rose otto oils), synthetic-tanned leather (e.g. , tanned using aromatic polymers), alum-tanned leather, patent leather, Vachetta leather, nubuck leather, and rawhide leather. Natural leather also includes split leather, full-grain leather, top-grain leather, and corrected-grain leather, the properties and preparation of which are known to those of skill in the art.

As used herein, "silk based proteins or fragments thereof includes silk fibroin- based proteins or fragments thereof, natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof. Natural silk based proteins or fragments thereof include spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof. Silkworm based proteins or fragments thereof may include Bombyx mori silk based proteins or fragments thereof. The SPF mixture solutions described herein may include silk based proteins or fragments thereof. Moreover, SFS, as described herein, may be replaced with SPF mixture solutions.

As used herein, "low molecular weight" silk fibroin solutions may include those SFS solutions that include silk fibroin-based protein fragments having a molecular weight in a range of about 5 kDa to 20 kDa. In some embodiments, a target low molecular weight for certain silk fibroin-based protein fragments may be about 11 kDa.

As used herein, "medium molecular weight" silk fibroin solutions may include those SFS solutions that include silk-fibroin based protein fragments having a molecular weight in a range of about 20 kDa to about 55 kDa. In some embodiments, a target medium molecular weight for certain silk fibroin-based protein fragments may be about 40 kDa.

As used herein, "high molecular weight" silk fibroin solutions may include those SFS solutions that include silk-fibroin based protein fragments having a molecular weight that is in a range of about 55 kDa to about 150 kDa. In some embodiments, a target high molecular weight for certain silk fibroin-based protein fragments may be about 100 kDa to about 145 kDa.

In some embodiments, the molecular weights described herein (e.g., low molecular weight silk, medium molecular weight silk, high molecular weight silk) may be converted to the approximate number of amino acids contained within the respective natural or recombinant proteins, such as natural or recombinant silk proteins, as would be understood by a person having ordinary skill in the art. For example, the average weight of an amino acid may be about 110 daltons (i.e., 1 10 g/mol). Therefore, in some embodiments, dividing the molecular weight of a linear protein by 1 10 daltons may be used to approximate the number of amino acid residues contained therein.

As used herein, the terms "substantially sericin free" or "substantially devoid of sericin" refer to silk fibers in which a majority of the sericin protein has been removed. In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having between about 0.01% (w/w) and about 10.0% (w/w) sericin. In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having between about 0.01% (w/w) and about 9.0% (w/w) sericin. In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having between about 0.01 % (w/w) and about 8.0% (w/w) sericin. In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having between about 0.01 % (w/w) and about 7.0% (w/w) sericin. In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having between about 0.01 % (w/w) and about 6.0% (w/w) sericin. In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having between about 0.01 % (w/w) and about 5.0% (w/w) sericin. In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having between about 0% (w/w) and about 4.0% (w/w) sericin. In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having between about 0.05% (w/w) and about 4.0% (w/w) sericin. In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having between about 0.1% (w/w) and about 4.0% (w/w) sericin. In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having between about 0.5% (w/w) and about 4.0% (w/w) sericin. In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having between about 1.0% (w/w) and about 4.0% (w/w) sericin. In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having between about 1.5% (w/w) and about 4.0% (w/w) sericin. In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having between about 2.0% (w/w) and about 4.0% (w/w) sericin. In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having between about 2.5% (w/w) and about 4.0% (w/w) sericin. In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having a sericin content between about 0.01% (w/w) and about 0.1 % (w/w). In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having a sericin content below about 0.1 % (w/w). In an embodiment, silk fibroin that is substantially devoid of sericin refers to silk fibroin having a sericin content below about 0.05% (w/w). In an embodiment, when a silk source is added to a boiling (100 °C) aqueous solution of sodium carbonate for a treatment time of between about 30 minutes to about 60 minutes, a degumming loss of about 26 wt.% to about 31 wt.% is obtained.

As used herein, the term "substantially homogeneous" may refer to pure silk fibroin-based protein fragments that are distributed in a normal distribution about an identified molecular weight. As used herein, the term "substantially homogeneous" may refer to an even distribution of additive, for example vitamin C, throughout a composition of the present disclosure.

As used herein, the term "substantially free of inorganic residuals" means that the composition exhibits residuals of 0.1 % (w/w) or less. In an embodiment, substantially free of inorganic residuals refers to a composition that exhibits residuals of 0.05% (w/w) or less. In an embodiment, substantially free of inorganic residuals refers to a composition that exhibits residuals of 0.01% (w/w) or less. In an embodiment, the amount of inorganic residuals is between 0 ppm ("non-detectable" or "ND") and 1000 ppm. In an embodiment, the amount of inorganic residuals is ND to about 500 ppm. In an embodiment, the amount of inorganic residuals is ND to about 400 ppm. In an embodiment, the amount of inorganic residuals is ND to about 300 ppm. In an embodiment, the amount of inorganic residuals is ND to about 200 ppm. In an embodiment, the amount of inorganic residuals is ND to about 100 ppm. In an embodiment, the amount of inorganic residuals is between 10 ppm and 1000 ppm.

As used herein, the term "substantially free of organic residuals" means that the composition exhibits residuals of 0.1 % (w/w) or less. In an embodiment, substantially free of organic residuals refers to a composition that exhibits residuals of 0.05% (w/w) or less. In an embodiment, substantially free of organic residuals refers to a composition that exhibits residuals of 0.01 % (w/w) or less. In an embodiment, the amount of organic residuals is between 0 ppm ("non-detectable" or "ND") and 1000 ppm. In an embodiment, the amount of organic residuals is ND to about 500 ppm. In an embodiment, the amount of organic residuals is ND to about 400 ppm. In an embodiment, the amount of organic residuals is ND to about 300 ppm. In an embodiment, the amount of organic residuals is ND to about 200 ppm. In an embodiment, the amount of organic residuals is ND to about 100 ppm. In an embodiment, the amount of organic residuals is between 10 ppm and 1000 ppm.

Compositions of the present disclosure are "biocompatible" or otherwise exhibit "biocompatibility" meaning that the compositions are compatible with living tissue or a living system by not being toxic, injurious, or physiologically reactive and not causing immunological rejection or an inflammatory response. Such biocompatibility can be evidenced by participants topically applying compositions of the present disclosure on their skin for an extended period of time. In an embodiment, the extended period of time is about 3 days. In an embodiment, the extended period of time is about 7 days. In an embodiment, the extended period of time is about 14 days. In an embodiment, the extended period of time is about 21 days. In an embodiment, the extended period of time is about 30 days. In an embodiment, the extended period of time is selected from the group consisting of about 1 month, about 2 months, about 3 months, about 4 months, about 5 months, about 6 months, about 7 months, about 8 months, about 9 months, about 10 months, about 11 months, about 12 months, and indefinitely. For example, in some embodiments, the coatings described herein are biocompatible coatings.

In some embodiments, compositions described herein, which may be biocompatible compositions (e.g., biocompatible coatings that include silk), may be evaluated and comply with International Standard ISO 10993-1, titled the "Biological evaluation of medical devices - Part 1 : Evaluation and testing within a risk management process." In some embodiments, compositions described herein, which may be biocompatible compositions, may be evaluated under ISO 106993-1 for one or more of cytotoxicity, sensitization, hemocompatibility, pyrogenicity, implantation, genotoxicity, carcinogenicity, reproductive and developmental toxicity, and degradation.

In some embodiments, compositions and articles described herein, and methods of preparing the same, include silk coated fabrics and textiles wherein the silk coating is partially dissolved in the fabric or textile. The fabric or textile may be a polymeric material such as those described elsewhere herein. The term "partially dissolved" includes mixing to form a dispersion of, e.g., a portion of a polymeric fabric or textile with a portion of the silk based coating. In some embodiments, the dispersion may be a solid suspension (i.e. , a dispersion comprising domains on the order of 10 nm) or a solid solution (i.e., a molecular dispersion) of silk in the polymeric fabric or textile. In some embodiments, the dispersion may be localized at the surface interface between the silk coating and the polymeric fabric or textile, and may have a depth of 1 nm, 2 nm, 5 nm, 10 nm, 25 nm, 50 nm, 75 nm, 100 nm, or greater than 100 nm, depending on the method of preparation. In some embodiments, the dispersion may be a layer sandwiched between the polymeric fabric or textile and the silk coating. In some embodiments, the dispersion may be prepared by coating silk, including silk fibroin with the characteristics described herein, onto the polymeric fabric or textile, and then performing an additional process to form the dispersion, including heating at a temperature of 100 °C, 125 °C, 150 °C, 175 °C, 200 °C, 225 °C, or 250 °C for a time period selected from the group consisting of 1 minute, 2 minutes, 5 minutes, 10 minutes, 15 minutes, 20 minutes, 30 minutes, 1 hour, 2 hours, 4 hours, 8 hours, 16 hours, or 24 hours. In some embodiments, heating may be performed at or above the glass transition temperature (T ) of silk and/or the polymeric fabric or textile, which may be assessed by methods known in the art. In some embodiments, the dispersion may be formed by coating silk, including silk fibroin with the characteristics described herein, onto the polymeric fabric or textile, and then performing an additional process to impregnate the silk coating into the polymeric fabric or textile, including treatment with an organic solvent. Methods for characterizing the properties of polymers dissolved in one another are well known in the art and include differential scanning calorimetry and surface analysis methods capable of depth profiling, including spectroscopic methods. Compositions of the present disclosure are "hypoallergenic" meaning that they are relatively unlikely to cause an allergic reaction. Such hypoallergenicity can be evidenced by participants topically applying compositions of the present disclosure on their skin for an extended period of time. In an embodiment, the extended period of time is about 3 days. In an embodiment, the extended period of time is about 7 days. In an embodiment, the extended period of time is about 14 days. In an embodiment, the extended period of time is about 21 days. In an embodiment, the extended period of time is about 30 days. In an embodiment, the extended period of time is selected from the group consisting of about 1 month, about 2 months, about 3 months, about 4 months, about 5 months, about 6 months, about 7 months, about 8 months, about 9 months, about 10 months, about 11 months, about 12 months, and indefinitely.

In some embodiments, where aqueous solutions are used to prepare SPF compositions or SPF containing coatings, the aqueous solutions may be prepared with DI water or tap water. As used herein, "tap water" refers to potable water provided by public utilities and water of comparable quality, regardless of the source, without further refinement such as by reverse osmosis, distillation, and/or deionization. Therefore, the use of "DI water," "RODI water," or "water," as set forth herein, may be understood to be interchangeable with "tap water" according to the processes described herein without deleterious effects to such processes.

Textiles and Materials Coated with Silk Fibroin-Based Protein Fragments

As used herein, the term "washable" and "exhibiting washability" means that a silk coated fabric of the present disclosure is capable of being washed without shrinking, fading, or the like.

As used herein, the term "textile" refers to a flexible woven or non-woven material consisting of a network of natural or artificial fibers often referred to as fabric, thread, or yarn. In an embodiment, textiles can be used to fabricate clothing, apparel, shoes, and bags. In an embodiment, textiles can be used to fabricate carpeting, upholstered furnishings, window shades, towels, and coverings for tables, beds, and other flat surfaces. In an embodiment, textiles can be used to fabricate flags, backpacks, tents, nets, handkerchiefs, balloons, kites, sails, and parachutes.

As used herein, the term "hand" refers to the feel of a fabric, which may be further described as the feeling of softness, crispness, dryness, silkiness, and combinations thereof. Fabric hand is also referred to as "drape." A fabric with a hard hand is coarse, rough, and generally less comfortable for the wearer. A fabric with a soft hand is fluid and smooth, such as fine silk, wool, or cashmere, and generally more comfortable for the wearer. Fabric hand can be determined by comparison to collections of fabric samples, or by use of methods such as the Kawabata Evaluation System (KES) or the Fabric Assurance by Simple Testing (FAST) methods. Behera and Hari, Ind. J. Fibre & Textile Res., 1994, 79, 168-71.

As used herein, the term "yam" refers to a single or multi-fiber construct.

As used herein, a "coating" refers to a material, or combination of materials, that form a substantially continuous layer or film on an exterior surface of a substrate, such as a textile. In some embodiments, a portion of the coating may penetrate at least partially into the substrate. In some embodiments, the coating may penetrate at least partially into the interstices of a substrate. In some embodiments, the coating may be infused into a surface of the substrate such that the application of the coating, or coating process, may include infusing (at the melting temperature of the substrate) at least one coating component at least partially into a surface of the substrate. A coating may be applied to a substrate by one or more of the processes described herein.

In embodiments described where the coating may be infused into a surface of the substrate, the coating may be codissolved in a surface of the substrate such that a component of the coating may be intermixed in the surface of the substrate to a depth of at least about 1 nm, or at least about 2 nm, or at least about 3 nm, or at least about 4 nm, or at least about 5 nm, or at least about 6 nm, or at least about 7 nm, or at least about 8 nm, or at least about 9 nm, or at least about 10 nm, or at least about 20 nm, or at least about 30 nm, or at least about 40 nm, or at least about 50 nm, or at least about 60 nm, or at least about 70 nm, or at least about 80 nm, or at least about 90 nm, or at least about 100 nm. In some embodiments, the coating may be infused into a surface of the substrate where the substrate includes one or more polymers including, but not limited to, polyester, polyamide, polyaramid, polytetrafluoroethylene, polyethylene, polypropylene, polyurethane, silicone, mixtures of polyurethane and polyethyleneglycol, ultrahigh molecular weight polyethylene, high-performance polyethylene, nylon, and LYCRA. As used herein, the term "bath coating" encompasses coating a fabric in a batch, immersing a fabric in a bath, and submerging a fabric in a bath. Concepts of bath coating are set forth in U.S. Patent No. 4,521,458, the entirety of which is incorporated by reference.

As used herein, and unless more specifically described, the term "drying" may refer to drying a coated material as described herein at a temperature greater than room temperature (i.e., 20 °C).

In one embodiment, the invention relates to coating a material including one or more proteinaceous fibers, wherein a substantial portion of the proteinaceous fibers are coated with silk fibroin-based protein fragments. In some embodiments, the proteinaceous fibers include keratin. In some embodiments, the proteinaceous fibers include hair. In some embodiments, the proteinaceous fibers include human hair or animal hair. In some embodiments, the silk fibroin-based protein fragments include one or more of low molecular weight silk fibroin-based protein fragments, medium molecular weight silk fibroin-based protein fragments, and high molecular weight silk fibroin-based protein fragments. In some embodiments, the silk fibroin-based protein fragments have an average molecular weight from about 1 kDa to about 350 kDa. In some embodiments, the silk fibroin-based protein fragments have a polydispersity from about 1.0 to about 5.0.

Synthetic leather includes poromeric imitation leathers (e.g. , polyurethane on polyester), vinyl and polyamide felt fibers, polyurethane, polyvinyl chloride, polyethylene (PE), polypropylene (PP), vinyl acetate copolymer (EVA), polyamide, polyester, textile-polymer composite microfibers, corfan, koskin, leatherette, BIOTHANE®, BIRKIBUC®, BIRKO-FLOR®, CLARINO®, ECOLORICA®, KYDEX®, LORICA®, NAUGAHYDE®, REXINE®, VEGETAN®, FABRIKOID®, or combinations thereof.

In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile used for human apparel, including performance and/or athletic apparel. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, and wherein the textile or leather product exhibits improved moisture management properties and/or resistance to microbial growth. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product used for home upholstery. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile or leather product is used for automobile upholstery. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile or leather product is used for aircraft upholstery. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile or leather product is used for upholstery in transportation vehicles for public, commercial, military, or other use, including buses and trains. In an embodiment, the invention provides a textile or leather product coated with silk fibroin- based proteins or fragments thereof, wherein the textile or leather product is used for upholstery of a product that requires a high degree of resistance to wear as compared to normal upholstery.

In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as trim on automobile upholstery. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as a steering wheel. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as a headrest. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as an armrest. In an embodiment, the invention provides a textile or leather product coated with silk fibroin- based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as an automobile floor mat. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as automobile or vehicle carpet. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as automotive trim. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as a children's car seat. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as a seat belt or safety harness. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as a dashboard. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as a seat. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as a seat panel. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as an interior panel. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as an airbag cover. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as an airbag. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as a sunvisor. In an embodiment, the invention provides a textile or leather product coated with silk fibroin-based proteins or fragments thereof, wherein the textile is a textile or leather product fabricated as a wiring harness. In an embodiment, the invention provides a product coated with silk fibroin-based proteins or fragments thereof, wherein the product is a cushion. In an embodiment, the invention provides a product coated with silk fibroin-based proteins or fragments thereof, wherein the product is automotive, aircraft, or other vehicular insulation. The coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the silk based proteins or protein fragments thereof have an average weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof have a polydispersity of between about 1.5 and about 3.0, or about 1.0 and about 5.0, and optionally wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days. The coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa and about 144 kDa, wherein the silk based proteins or protein fragments thereof have an average weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof have a polydispersity of between about 1.5 and about 3.0, and optionally wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days.

In an embodiment, the invention provides an article comprising a textile or leather coated with silk fibroin-based proteins or fragments thereof. In an embodiment, the textile or leather is a textile or leather used in the manufacture of tents, sleeping bags, ponchos, and soft-walled coolers. In an embodiment, the textile or leather is a textile or leather used in the manufacture of athletic equipment. In an embodiment, the textile or leather is a textile or leather used in the manufacture of outdoor gear. In an embodiment, the textile or leather is a textile or leather used in the manufacture of hiking gear, such as harnesses and backpacks. In an embodiment, the textile or leather is a textile or leather used in the manufacture of climbing gear. In an embodiment, the textile or leather is canvass. In an embodiment, the textile or leather is a textile or leather used in the manufacture of a hat. In an embodiment, the textile or leather is a textile or leather used in the manufacture of an umbrella. In an embodiment, the textile or leather is a textile or leather used in the manufacture of a tent. In an embodiment, the textile or leather is a textile or leather used in the manufacture of a baby sleeper, a baby blanket, or a baby pajama. In an embodiment, the textile or leather is a textile or leather used in the manufacture of a glove, such as a driving glove or an athletic glove. In an embodiment, the textile or leather is a textile or leather used in the manufacture of athletic pants, such as sweat pants, jogging pants, yoga pants, or pants for use in competitive sports. In an embodiment, the textile or leather is a textile or leather used in the manufacture of athletic shirts, such as sweat shirts, jogging shirts, yoga shirts, or shirts for use in competitive sports. In an embodiment, the textile or leather is a textile or leather used in the manufacture of beach equipment, such as beach umbrellas, beach chairs, beach blankets, and beach towels. In an embodiment, the textile or leather is a textile or leather used in the manufacture of jackets or overcoats. In an embodiment, the textile or leather is a textile or leather used in the manufacture of medical garments, such as surgical drapes, surgical gowns, surgical sleeves, laboratory sleeves, laboratory coats, wound dressings, sterilization wraps, surgical face masks, retention bandages, support devices, compression bandages, shoe covers, surgical blankets, and the like. The coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa.

In an embodiment, the invention provides an article comprising a textile coated with silk fibroin-based proteins or fragments thereof. In an embodiment, the textile is a textile used in the manufacture of tents, sleeping bags, ponchos, and soft- walled coolers. In an embodiment, the textile is a textile used in the manufacture of athletic equipment. In an embodiment, the textile is a textile used in the manufacture of outdoor gear. In an embodiment, the textile is a textile used in the manufacture of hiking gear, such as harnesses and backpacks. In an embodiment, the textile is a textile used in the manufacture of climbing gear. In an embodiment, the textile is canvass. In an embodiment, the textile is a textile used in the manufacture of a hat. In an embodiment, the textile is a textile used in the manufacture of an umbrella. In an embodiment, the textile is a textile used in the manufacture of a tent. In an embodiment, the textile is a textile used in the manufacture of a baby sleeper, a baby blanket, or a baby pajama. In an embodiment, the textile is a textile used in the manufacture of a glove, such as a driving glove or an athletic glove. In an embodiment, the textile is a textile used in the manufacture of athletic pants, such as sweat pants, jogging pants, yoga pants, or pants for use in competitive sports. In an embodiment, the textile is a textile used in the manufacture of athletic shirts, such as sweat shirts, jogging shirts, yoga shirts, or shirts for use in competitive sports. In an embodiment, the textile is a textile used in the manufacture of beach equipment, such as beach umbrellas, beach chairs, beach blankets, and beach towels. In an embodiment, the textile is a textile used in the manufacture of jackets or overcoats. In an embodiment, the textile is a textile used in the manufacture of medical garments, such as surgical drapes, surgical gowns, surgical sleeves, laboratory sleeves, laboratory coats, wound dressings, sterilization wraps, surgical face masks, retention bandages, support devices, compression bandages, shoe covers, surgical blankets, and the like. The coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the silk based proteins or protein fragments thereof have an average weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof have a polydispersity of between about 1.0 and about 5.0, and optionally wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days.

In an embodiment, the invention provides a shoe coated with silk fibroin-based proteins or fragments thereof. In an embodiment, the invention provides a shoe coated with silk fibroin-based proteins or fragments thereof, wherein the shoe exhibits an improved property relative to an uncoated shoe. In an embodiment, the invention provides a shoe coated with silk fibroin-based proteins or fragments thereof, wherein the shoe exhibits an improved property relative to an uncoated shoe, and wherein the improved property is stain resistance. In an embodiment, the invention provides a shoe coated with silk fibroin-based proteins or fragments thereof, wherein the shoe exhibits an improved property relative to an uncoated shoe, and wherein the shoe is made of natural leather or synthetic leather. The coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or protein fragments thereof have an average weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof have a polydispersity of between about 1.0 and about 5.0, or about 1.5 and about 3.0, and optionally wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, and wherein the article is a textile or leather.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or protein fragments thereof have an average weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof have a poly dispersity of between about 1.0 and about 5.0, or about 1.5 and about 3.0, and wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yarn is selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is natural fiber or yam selected from the group consisting of cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of synthetic fiber or yam, or combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yam, comprising for example wool, synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester-polyurethane copolymer and combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is synthetic fiber or yam selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof, wherein the fiber or yam comprises cashmere, nylon, polyester-polyurethane copolymer, polyester, polyamide, polyaramid, polytetrafluoroethylene, polyethylene, polypropylene, polyurethane, silicone, mixtures of polyurethane and polyethyleneglycol, ultrahigh molecular weight polyethylene, high-performance polyethylene, nylon, and combinations thereof, and/or LYCRA.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the fabric exhibits an improved property, wherein the improved property is an accumulative one-way moisture transport index selected from the group consisting of greater than 40%, greater than 60%, greater than 80%, greater than 100%, greater than 120%, greater than 140%, greater than 160%, and greater than 180%. In an embodiment, the foregoing improved property is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the fabric exhibits an improved property, wherein the improved property is an accumulative one way transport capability increase relative to uncoated fabric selected from the group consisting of 1.2 fold, 1.5 fold, 2.0 fold, 3.0 fold, 4.0 fold, 5.0 fold, and 10 fold. In an embodiment, the foregoing improved property is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the fabric exhibits an improved property, wherein the improved property is an overall moisture management capability selected from the group consisting of greater than 0.05, greater than 0.10, greater than 0.15, greater than 0.20, greater than 0.25, greater than 0.30, greater than 0.35, greater than 0.40, greater than 0.50, greater than 0.60, greater than 0.70, and greater than 0.80. In an embodiment, the foregoing improved property is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the fabric exhibits an improved property, wherein the improved property is dimensional stability. In some embodiments, dimensional stability refers to length stability, width stability, or an overall dimensional stability. In an embodiment, dimensional stability is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, and wherein the fabric exhibits substantially no increase in microbial growth after a number of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the fabric exhibits substantially no increase in microbial growth after a number of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles, and wherein the microbial growth is microbial growth of a microbe selected from the group consisting of Staphylococcus aureus, Klebsiella pneumoniae, and combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the fabric exhibits substantially no increase in microbial growth after a number of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles, wherein the microbial growth is microbial growth of a microbe selected from the group consisting of Staphylococcus aureus, Klebsiella pneumoniae, and combinations thereof, wherein the microbial growth is reduced by a percentage selected from the group consisting of 50 %, 100 %, 500 %, 1000 %, 2000 %, and 3000 % compared to an uncoated fabric.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the fabric exhibits substantially no increase in microbial growth after a number of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles, and wherein the microbial growth is microbial growth of a microbe selected from the group consisting of Staphylococcus aureus, Klebsiella pneumoniae, and combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the fabric exhibits substantially no increase in microbial growth after a number of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles, wherein the microbial growth is microbial growth of a microbe selected from the group consisting of Staphylococcus aureus, Klebsiella pneumoniae, and combinations thereof, wherein the microbial growth is reduced by a percentage selected from the group consisting of 50%, 100%, 500%, 1000%, 2000%, and 3000% compared to an uncoated fabric.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the coating is applied to the fabric at the fiber level prior to forming the fabric.

In some embodiments, the silk coated fibers and/or yams included herein may have enhanced dye and/or color features due to application of dye and/or coloring agent at the liquid silk layer and/or the fabric or yarn layer of the silk coated fibers and/or yams that may make up the articles described herein. In some embodiments, a liquid silk layer of the silk coated fibers and/or yarns included herein may affect, change, increase, decrease, or otherwise modulate the birefringence, reflectivity, and/or refractivity of the silk coated fibers and/or yams as compared to uncoated fibers and/or yams.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the fabric exhibits a change in birefringence compared to an uncoated fabric. In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the fabric exhibits an increase in birefringence compared to an uncoated fabric. In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the fabric exhibits a decrease in birefringence compared to an uncoated fabric. In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the fabric exhibits a modulation of birefringence compared to an uncoated fabric.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the fabric exhibits a change in reflectivity compared to an uncoated fabric. In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the fabric exhibits an increase in reflectivity compared to an uncoated fabric. In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the fabric exhibits a decrease in reflectivity compared to an uncoated fabric. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the fabric exhibits a modulation of reflectivity compared to an uncoated fabric.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the fabric exhibits a change in refractivity compared to an uncoated fabric. In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the fabric exhibits an increase in refractivity compared to an uncoated fabric. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the fabric exhibits a decrease in refractivity compared to an uncoated fabric. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the fabric exhibits a modulation of refractivity compared to an uncoated fabric.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, and wherein the coating is applied to the fabric at the fiber level prior to forming the fabric.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, and wherein the coating is applied to the fabric at the fabric level or garment level (e.g. , after manufacture of a garment from fabrics, leathers, and/or other materials).

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is applied to the fabric at the fabric level or garment level, and wherein the fabric is bath coated.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is applied to the fabric at the fabric level or garment level, and wherein the fabric is spray coated.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is applied to the fabric at the fabric level or garment level, and wherein the fabric is coated with a stencil.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is applied to the fabric at the fabric level or garment level, and wherein the coating is applied to at least one side of the fabric using a method selected from the group consisting of a bath coating process, a spray coating process, a stencil (i.e. , screen) process, a silk-foam based process, a roller-based process, a magnetic roller process, a knife process, a transfer process, a foam process, a lacquering process, and a printing process. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is applied to the fabric at the fabric level, and wherein the coating is applied to both sides of the fabric using a method selected from the group consisting of a bath coating process, a spray coating process, a stencil (i.e. , screen) process, a silk-foam based process, a roller-based process, a magnetic roller process, a knife process, a transfer process, a foam process, a lacquering process, and a printing process.

In any of the foregoing embodiments, the coating may be applied at the fabric garment level by any of the methods disclosed herein to recondition fabrics or garments. For example, such reconditioning using a coating comprising silk based proteins or fragments thereof may be performed as part of washing or cleaning a fabric or garment.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, and wherein the coating has a thickness of about one nanolayer.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, and wherein the coating has a thickness selected from the group consisting of about 5 nm, about 10 nm, about 15 nm, about 20 nm, about 25 nm, about 50 nm, about 100 nm, about 200 nm, about 500 nm, about 1 μιτι, about 5 μιτι, about 10 μιτι, and about 20 μιτι.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the coating is adsorbed on the fabric.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the coating is attached to the fabric through chemical, enzymatic, thermal, or irradiative cross-linking.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is applied to the fabric at the fabric level, and wherein the hand of the coated fabric is improved relative to an uncoated fabric.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is applied to the fabric at the fabric level, and wherein the hand of the coated fabric is improved relative to an uncoated fabric, wherein the hand of the coated fabric that is improved is selected from the group consisting of softness, crispness, dryness, silkiness, and combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is applied to the fabric at the fabric level, and wherein the hand of the coated fabric is improved relative to an uncoated fabric, wherein the hand of the coated fabric that is improved is selected from the group consisting of softness, crispness, dryness, silkiness, and combinations thereof.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is applied to the fabric at the fabric level, and wherein the pilling of the fabric is improved relative to an uncoated fabric. In an embodiment, the silk coating is applied using a bath process, a screen (or stencil) process, a spray process, a silk-foam based process, and a roller based process.

In an embodiment, a fiber or a yam comprises a synthetic fiber or yam (e.g., from animal or plant sources), including polyester, Mylar, cotton, nylon, polyester- polyurethane copolymer, rayon, acetate, aramid (aromatic polyamide), acrylic, ingeo (polylactide), lurex (polyamide-polyester), olefin (polyethylene-polypropylene), and combinations thereof.

In an embodiment, a fiber or a yam comprises a natural fiber or yam (e.g. , from animal or plant sources), including alpaca fiber, alpaca fleece, alpaca wool, lama fiber, lama fleece, lama wool, cotton, cashmere and sheep fiber, sheep fleece, sheep wool, byssus, chiengora, qiviut, yak, rabbit, lambswool, mohair wool, tibetan wool, lopi, camel hair, pashmina, angora wool, spider silk, silkworm silk, abaca fiber, coir fiber, flax fiber, jute fiber, kapok fiber, kenaf fiber, raffia fiber, bamboo fiber, hemp, modal fiber, pina, ramie, sisal, and soy protein fiber. In an embodiment, a fiber or a yam comprises a natural fiber or yam, including wool fiber. In an embodiment, a fiber or a yam comprises a natural fiber or yam, including cashmere fiber. In an embodiment, a fiber or a yam comprises a natural fiber or yam, including silk.

In an embodiment, a fiber or a yam comprises a mineral fiber, also known as mineral wool, mineral cotton, or man-made mineral fiber, including fiberglass, glass, glasswool, stone wool, rock wool, slagwool, glass filaments, asbestos fibers, and ceramic fibers.

In an embodiment, a fiber or a yam may include cashmere fiber or yam component and non-cashmere fiber or yam component. In some embodiments, the non- cashmere fiber or yam component may comprise alpaca fiber, alpaca fleece, alpaca wool, lama fiber, lama fleece, lama wool, cotton, sheep fleece, sheep wool, byssus, chiengora, qiviut, yak, rabbit, lambswool, mohair wool, tibetan wool, lopi, camel hair, pashmina, angora wool, silkworm silk, spider silk, abaca fiber, coir fiber, flax fiber, jute fiber, kapok fiber, kenaf fiber, raffia fiber, bamboo fiber, hemp, modal fiber, pina, ramie, sisal, soy protein fiber, polyester, polyamide, polyaramid, polytetrafluoroethylene, polyethylene, polypropylene, polyurethane, silicone, mixtures of polyurethane and polyethyleneglycol, ultrahigh molecular weight polyethylene, high-performance polyethylene, nylon, LYCRA (polyester-polyurethane copolymer, also known as SPANDEX and elastomer), or a mixture thereof. In some embodiments, the non-cashmere fiber or yarn component may be wool. In some embodiments, the non-cashmere fiber or yarn component may be an inert synthetic material, such as polyester, polyamide, polyaramid, polytetrafluoroethylene, polyethylene, polypropylene, polyurethane, silicone, mixtures of polyurethane and polyethyleneglycol, ultrahigh molecular weight polyethylene, high-performance polyethylene, nylon, LYCRA (polyester-polyurethane copolymer, also known as SPANDEX and elastomer), rayon, or a mixture thereof.

In some embodiments, an article described herein may include a cashmere fiber or yarn component in an amount, by weight of the article (w/w), of greater than 1 %,

2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 1 1 %, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21 %, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31%, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41 %, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49%, 50%, 51 %, 52%, 53%, 54%, 55%, 56%, 57%, 58%, 59%, 60%, 61%, 62%, 63%, 64%, 65%, 66%, 67%, 68%, 69%, 70%, 71 %, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79%, 80%, 81 %, 82%, 83%, 84%, 85%, 86%, 87%, 88%, 89%, 90%, 91%, 92%, 93%, 94%, 95%, 96%, 97%, 98%, or 99%, where the balance of the article, by weight (w/w), is a non-cashmere fiber or yarn component, as described herein. In some embodiments, an article described herein may include a cashmere fiber or yam component in an amount, by weight of the article (w/w), of less than 1 %, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 11 %, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21 %, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31 %, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41 %, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49%, 50%, 51%, 52%, 53%, 54%, 55%, 56%, 57%, 58%, 59%, 60%, 61 %, 62%, 63%, 64%, 65%, 66%, 67%, 68%, 69%, 70%, 71 %, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79%, 80%, 81%, 82%, 83%, 84%, 85%, 86%, 87%, 88%, 89%, 90%, 91 %, 92%, 93%, 94%, 95%, 96%, 97%, 98%, or 99%, where the balance of the article, by weight (w/w), is a non-cashmere fiber or yam component, as described herein. In some embodiments, an article described herein may include a cashmere fiber or yarn component in an amount, by weight of the article (w/w), of about 1 %, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 1 1%, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21 %, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31 %, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41 %, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49%, 50%, 51 %, 52%, 53%, 54%, 55%, 56%, 57%, 58%, 59%, 60%, 61 %, 62%, 63%, 64%, 65%, 66%, 67%, 68%, 69%, 70%, 71 %, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79%, 80%, 81 %, 82%, 83%, 84%, 85%, 86%, 87%, 88%, 89%, 90%, 91%, 92%, 93%, 94%, 95%, 96%, 97%, 98%, or 99%, where the balance of the article, by weight (w/w), is a non-cashmere fiber or yam component, as described herein.

In some embodiments, the cashmere fiber or yam component may be a silk coated cashmere fiber or yam component, where the silk coating may be any silk coating provided herein. In some embodiments, the non-cashmere fiber or yam component may be a silk coated non-cashmere fiber or yam component, where the silk coating may be ay silk coating provided herein.

In some embodiments, an article described herein may include a silk coated cashmere fiber or yam component in an amount, by weight of the article (w/w), of greater than 1%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 11%, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21 %, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31%, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41 %, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49%, 50%, 51 %, 52%, 53%, 54%, 55%, 56%, 57%, 58%, 59%, 60%, 61%, 62%, 63%, 64%, 65%, 66%, 67%, 68%, 69%, 70%, 71 %, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79%, 80%, 81 %, 82%, 83%, 84%, 85%, 86%, 87%, 88%, 89%, 90%, 91%, 92%, 93%, 94%, 95%, 96%, 97%, 98%, or 99%, where the balance of the article, by weight (w/w), is a non-cashmere fiber or yam component, as described herein. In some embodiments, an article described herein may include a silk coated cashmere fiber or yam component in an amount, by weight of the article (w/w), of less than 1 %, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 1 1%, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21 %, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31%, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41 %, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49%, 50%, 51 %, 52%, 53%, 54%, 55%, 56%, 57%, 58%, 59%, 60%, 61%, 62%, 63%, 64%, 65%, 66%, 67%, 68%, 69%, 70%, 71 %, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79%, 80%, 81 %, 82%, 83%, 84%, 85%, 86%, 87%, 88%, 89%, 90%, 91%, 92%, 93%, 94%, 95%, 96%, 97%, 98%, or 99%, where the balance of the article, by weight (w/w), is a non-cashmere fiber or yam component, as described herein. In some embodiments, an article described herein may include a silk coated cashmere fiber or yam component in an amount, by weight of the article (w/w), of about 1%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 11 %, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21 %, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31%, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41%, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49%, 50%, 51 %, 52%, 53%, 54%, 55%, 56%, 57%, 58%, 59%, 60%, 61%, 62%, 63%, 64%, 65%, 66%, 67%, 68%, 69%, 70%, 71%, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79%, 80%, 81 %, 82%, 83%, 84%, 85%, 86%, 87%, 88%, 89%, 90%, 91%, 92%, 93%, 94%, 95%, 96%, 97%, 98%, or 99%, where the balance of the article, by weight (w/w), is a non-cashmere fiber or yam component, as described herein.

In some embodiments, an article described herein may include a silk coated cashmere fiber or yam component in an amount, by weight of the article (w/w), of greater than 1%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 11%, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21 %, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31%, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41 %, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49%, 50%, 51 %, 52%, 53%, 54%, 55%, 56%, 57%, 58%, 59%, 60%, 61%, 62%, 63%, 64%, 65%, 66%, 67%, 68%, 69%, 70%, 71 %, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79%, 80%, 81 %, 82%, 83%, 84%, 85%, 86%, 87%, 88%, 89%, 90%, 91%, 92%, 93%, 94%, 95%, 96%, 97%, 98%, or 99%, where the balance of the article, by weight (w/w), is a silk coated non-cashmere fiber or yam component, as described herein. In some embodiments, an article described herein may include a silk coated cashmere fiber or yam component in an amount, by weight of the article (w/w), of less than 1%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 1 1%, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21%, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31 %, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41%, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49%, 50%, 51%, 52%, 53%, 54%, 55%, 56%, 57%, 58%, 59%, 60%, 61 %, 62%, 63%, 64%, 65%, 66%, 67%, 68%, 69%, 70%, 71%, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79%, 80%, 81%, 82%, 83%, 84%, 85%, 86%, 87%, 88%, 89%, 90%, 91 %, 92%, 93%, 94%, 95%, 96%, 97%, 98%, or 99%, where the balance of the article, by weight (w/w), is a silk coated non-cashmere fiber or yam component, as described herein. In some embodiments, an article described herein may include a silk coated cashmere fiber or yam component in an amount, by weight of the article (w/w), of about 1 %, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 11 %, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21%, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31 %, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41%, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49%, 50%, 51%, 52%, 53%, 54%, 55%, 56%, 57%, 58%, 59%, 60%, 61 %, 62%, 63%, 64%, 65%, 66%, 67%, 68%, 69%, 70%, 71%, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79%, 80%, 81%, 82%, 83%, 84%, 85%, 86%, 87%, 88%, 89%, 90%, 91 %, 92%, 93%, 94%, 95%, 96%, 97%, 98%, or 99%, where the balance of the article, by weight (w/w), is a silk coated non-cashmere fiber or yam component, as described herein.

In some embodiments, an article described herein may include a cashmere fiber or yam component in an amount, by weight of the article (w/w), of greater than 1 %,

2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 1 1 %, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21 %, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31%, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41 %, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49%, 50%, 51 %, 52%, 53%, 54%, 55%, 56%, 57%, 58%, 59%, 60%, 61%, 62%, 63%, 64%, 65%, 66%, 67%, 68%, 69%, 70%, 71 %, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79%, 80%, 81 %, 82%, 83%, 84%, 85%, 86%, 87%, 88%, 89%, 90%, 91%, 92%, 93%, 94%, 95%, 96%, 97%, 98%, or 99%, where the balance of the article, by weight (w/w), is a silk coated non-cashmere fiber or yam component, as described herein. In some embodiments, an article described herein may include a cashmere fiber or yam component in an amount, by weight of the article (w/w), of less than 1%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 1 1%, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21%, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31 %, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41 %, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49%, 50%, 51%, 52%, 53%, 54%, 55%, 56%, 57%, 58%, 59%, 60%, 61 %, 62%, 63%, 64%, 65%, 66%, 67%, 68%, 69%, 70%, 71 %, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79%, 80%, 81%, 82%, 83%, 84%, 85%, 86%, 87%, 88%, 89%, 90%, 91 %, 92%, 93%, 94%, 95%, 96%, 97%, 98%, or 99%, where the balance of the article, by weight (w/w), is a silk coated non-cashmere fiber or yam component, as described herein. In some embodiments, an article described herein may include a cashmere fiber or yam component in an amount, by weight of the article (w/w), of about 1%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 1 1%, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19%, 20%, 21%, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31%, 32%, 33%, 34%, 35%, 36%, 37%, 38%, 39%, 40%, 41 %, 42%, 43%, 44%, 45%, 46%, 47%, 48%, 49%, 50%, 51%, 52%, 53%, 54%, 55%, 56%, 57%, 58%, 59%, 60%, 61 %, 62%, 63%, 64%, 65%, 66%, 67%, 68%, 69%, 70%, 71 %, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79%, 80%, 81%, 82%, 83%, 84%, 85%, 86%, 87%, 88%, 89%, 90%, 91 %, 92%, 93%, 94%, 95%, 96%, 97%, 98%, or 99%, where the balance of the article, by weight (w/w), is a silk coated non-cashmere fiber or yam component, as described herein.

In an embodiment, a water-soluble silk coating may be used as an adhesive or binder for binding particles to fabrics or for binding fabrics. In an embodiment, an article comprises a fabric bound to another fabric using a silk coating. In an embodiment, an article comprises a fabric with particles bound to the fabric using a silk adhesive.

In an embodiment, the coating is applied to an article including a fabric at the yam level. In an embodiment, the coating is applied at the fabric level. In an embodiment, the coating has a thickness selected from the group consisting of about 5 nm, about 10 nm, about 15 nm, about 20 nm, about 25 nm, about 50 nm, about 100 nm, about 200 nm, about 500 nm, about 1 μιτι, about 5 μιτι, about 10 μιτι, and about 20 μηι. In an embodiment, the coating has a thickness range selected from the group consisting of about 5 nm to about 100 nm, about 100 nm to about 200 nm, about 200 nm to about 500 nm, about 1 μιη to about 2 μιτι, about 2 μηι to about 5 μιτι, about 5 μηι to about 10 μιη, and about 10 μηι to about 20 μηι.

In an embodiment, a fiber or a yarn is treated with a polymer, such as polyglycolide (PGA), polyethylene glycols, copolymers of glycolide, glycolide/L- lactide copolymers (PGA/PLLA), glycolide/trimethylene carbonate copolymers (PGA/TMC), polylactides (PLA), stereocopolymers of PLA, poly-L-lactide (PLLA), poly-DL-lactide (PDLLA), L-lactide/DL-lactide copolymers, co-polymers of PLA, lactide/tetramethylglycolide copolymers, lactide/trimethylene carbonate copolymers, lactide/5-valerolactone copolymers, lactide/s-caprolactone copolymers, polydepsipeptides, PLA/polyethylene oxide copolymers, unsymmetrically 3,6- substituted poly-l,4-dioxane-2,5-diones, poly- -hydroxybutyrate (PHBA), ΡΗΒΑ/β- hydroxyvalerate copolymers (PHBA/HVA), poly- -hydroxypropionate (PHP A), poly- p-dioxanone (PDS), poly-5-valerolactone, poly-s-caprolactone, methylmethacrylate-N- vinyl pyrrolidine copolymers, polyesteramides, polyesters of oxalic acid, polydihydropyrans, polyalkyl-2-cyanoacrylates, polyurethanes (PU), polyvinylalcohols (PVA), polypeptides, poly- -malic acid (PMLA), poly- -alkanoic acids, polyvinylalcohol (PVA), polyethyleneoxide (PEO), chitine polymers, polyethylene, polypropylene, polyasetal, polyamides, polyesters, polysulphone, polyether ether ketone, polyethylene terephthalate, polycarbonate, polyaryl ether ketone, and polyether ketone ketone.

In an embodiment, the silk coating surface can be modified silk crystals that range in size from nm to μπι. The criterion for "visibility" is satisfied by any one of the following: a change in the surface character of the textile; the silk coating fills the interstices where the yams intersect; or the silk coating blurs or obscures the weave.

In an embodiment, a silk based protein or fragment solution may be utilized to coat at least a portion of a fabric which can be used to create a textile. In an embodiment, a silk based protein or fragment solution may be weaved into yam that can be used as a fabric in a textile. In an embodiment, a silk based protein or fragment solution may be used to coat a fiber. In an embodiment, the invention provides an article comprising a silk based protein or fragment solution coating at least a portion of a fabric or a textile. In an embodiment, the invention provides an article comprising a silk based protein or fragment solution coating a yarn. In an embodiment, the invention provides an article comprising a silk based protein or fragment solution coating a fiber.

There is disclosed a textile that is at least partially surface treated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure so as to result in a silk coating on the textile. In an embodiment, the silk coating of the present disclosure is available in a spray can and can be sprayed on any textile by a consumer. In an embodiment, a textile comprising a silk coating of the present disclosure is sold to a consumer. In an embodiment, a textile of the present disclosure is used in constructing action sportswear/apparel. In an embodiment, a silk coating of the present disclosure is positioned on the underlining of apparel. In an embodiment, a silk coating of the present disclosure is positioned on the shell, the lining, or the interlining of apparel. In an embodiment, apparel is partially made from a silk coated textile of the present disclosure and partially made from an uncoated textile. In an embodiment, apparel partially made from a silk coated textile and partially made from an uncoated textile combines an uncoated inert synthetic material with a silk coated inert synthetic material. Examples of inert synthetic material include, but are not limited to, polyester, polyamide, polyaramid, polytetrafluoroethylene, polyethylene, polypropylene, polyurethane, silicone, mixtures of polyurethane and polyethyleneglycol, ultrahigh molecular weight polyethylene, high-performance polyethylene, and mixtures thereof. In an embodiment, apparel partially made from a silk coated textile and partially made from an uncoated textile combines an elastomeric material at least partially covered with a silk coating of the present disclosure. In an embodiment, the percentage of silk to elastomeric material can be varied to achieve desired shrink or wrinkle resistant properties.

In an embodiment, a silk coating of the present disclosure is visible. In an embodiment, a silk coating of the present disclosure positioned on apparel helps control skin temperature. In an embodiment, a silk coating of the present disclosure positioned on apparel helps control fluid transfer away from the skin. In an embodiment, a silk coating of the present disclosure positioned on apparel has a soft feel against the skin decreasing abrasions from fabric on skin. In an embodiment, a silk coating of the present disclosure positioned on a textile has properties that confer at least one of wrinkle resistance, shrinkage resistance, or machine washability to the textile. In an embodiment, a silk coated textile of the present disclosure is 100% machine washable and dry cleanable. In an embodiment, a silk coated textile of the present disclosure is 100% waterproof. In an embodiment, a silk coated textile of the present disclosure is wrinkle resistant. In an embodiment, a silk coated textile of the present disclosure is shrink resistant, in an embodiment, a silk coated textile of the present disclosure has the qualities of being waterproof, breathable, and elastic and possess a number of other qualities which are highly desirable in action sportswear. In an embodiment a silk coated textile of the present disclosure manufactured from a silk fabric of the present disclosure further includes LYCRA® brand spandex fibers.

In an embodiment, a textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is a breathable fabric. In an embodiment, a textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is a water-resistant fabric. In an embodiment, a textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is a shrink-resistant fabric. In an embodiment, a textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is a machine-washable fabric. In an embodiment, a textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is a wrinkle resistant fabric. In an embodiment, textile at least partially coated with an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure provides moisture and vitamins to the skin.

In an embodiment, an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is used to coat a textile or leather. In an embodiment, the concentration of silk in the solution ranges from about 0.1% to about 20.0%. In an embodiment, the concentration of silk in the solution ranges from about 0.1% to about 15.0%. In an embodiment, the concentration of silk in the solution ranges from about 0.5% to about 10.0%. In an embodiment, the concentration of silk in the solution ranges from about 1.0% to about 5.0%. In an embodiment, an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure is applied directly to a fabric. Alternatively, silk microsphere and any additives may be used for coating a fabric. In an embodiment, additives can be added to an aqueous solution of pure silk fibroin- based protein fragments of the present disclosure before coating (e.g., alcohols) to further enhance material properties. In an embodiment, a silk coating of the present disclosure can have a pattern to optimize properties of the silk on the fabric. In an embodiment, a coating is applied to a fabric under tension and/or lax to vary penetration in to the fabric.

In an embodiment, a silk coating of the present disclosure can be applied at the yam level, followed by creation of a fabric once the yam is coated. In an embodiment, an aqueous solution of pure silk fibroin-based protein fragments of the present disclosure can be spun into fibers to make a silk fabric and/or silk fabric blend with other materials known in the apparel industry.

Uses of Textiles and Leathers Coated with Silk Fibroin-Based Protein Fragments in Apparel and Garment Applications

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article exhibits an improved color retention property. Without being bound by any specific theory, it is postulated that the coating prevents the article from color degradation by separating the fiber or yarn from air or from detergents during washing. Methods of testing the color retention property of an article are well within the knowledge of one skilled in the art. A specific method of testing of the color retention property of a fabric is described in U. S. Patent No. 5, 142,292, which is incorporated herein by reference in its entirety.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article exhibits an improved color retention property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the article exhibits an improved color retention property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the article exhibits an improved color retention property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the article exhibits an improved color retention property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, wherein the article exhibits an improved color retention property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, wherein the article exhibits an improved color retention property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is natural fiber or yarn selected from the group consisting of cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof, wherein the article exhibits an improved color retention property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester-polyurethane copolymer, and combinations thereof, wherein the article exhibits an improved color retention property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article exhibits an improved color retention property. In an embodiment, the foregoing color retention property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure exhibits an improved color retention property. In an embodiment, the foregoing improved color retention property of the textile is determined after a period of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is resistant to microbial (including bacterial and fungal) growth.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article is resistant to microbial (including bacterial and fungal) growth.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the article is resistant to microbial (including bacterial and fungal) growth.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the article is resistant to microbial (including bacterial and fungal) growth.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the article is resistant to microbial (including bacterial and fungal) growth.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, wherein the article is resistant to microbial (including bacterial and fungal) growth.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, wherein the article is resistant to microbial (including bacterial and fungal) growth.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, wherein the article is resistant to microbial (including bacterial and fungal) growth.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yarn is selected from the group consisting of natural fiber or yam, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is natural fiber or yarn selected from the group consisting of cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof, wherein the article is resistant to microbial (including bacterial and fungal) growth.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yarn is selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester-polyurethane copolymer, cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof, wherein the article is resistant to microbial (including bacterial and fungal) growth. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, or about 1 kDa to about 350 kDa, wherein the fiber or yam is selected from the group consisting of synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is natural fiber or yarn selected from the group consisting of polyester, nylon, polyester-polyurethane copolymer, and combinations thereof, wherein the article is resistant to microbial (including bacterial and fungal) growth.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the article is resistant to microbial (including bacterial and fungal) growth. In an embodiment, the foregoing resistant to microbial (including bacterial and fungal) growth property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure exhibits resistant to microbial (including bacterial and fungal) growth property. In an embodiment, the foregoing resistant to microbial (including bacterial and fungal) growth property of the textile is determined after a period of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is resistant to the buildup of static electrical charge.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article is resistant to the buildup of static electrical charge. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the article is resistant to the buildup of static electrical charge.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the article is resistant to the buildup of static electrical charge.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the article is resistant to the buildup of static electrical charge.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, wherein the article is resistant to the buildup of static electrical charge.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, wherein the article is resistant to the buildup of static electrical charge.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is natural fiber or yarn selected from the group consisting of cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof, wherein the article is resistant to the buildup of static electrical charge.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yarn is selected from the group consisting of natural fiber or yam, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is synthetic fiber or yarn selected from the group consisting of polyester, nylon, polyester- polyurethane copolymer, and combinations thereof, wherein the article is resistant to the buildup of static electrical charge.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yarn is natural fiber or yarn selected from the group consisting of synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester-polyurethane copolymer, and combinations thereof, wherein the article is resistant to the buildup of static electrical charge.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the fiber or yam is selected from the group consisting of cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof, wherein the article is resistant to the buildup of static electrical charge.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the article is resistant to the buildup of static electrical charge. In an embodiment, the foregoing resistant to the buildup of static electrical charge property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure exhibits resistant to the buildup of static electrical charge property. In an embodiment, the foregoing resistant to the buildup of static electrical charge property of the textile is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is mildew resistant.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article is mildew resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the article is mildew resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article is mildew resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the article is mildew resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the article is mildew resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the article is mildew resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, wherein the article is mildew resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, wherein the article is mildew resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is natural fiber or yarn selected from the group consisting of cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof, wherein the article is mildew resistant.

I l l In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yarn is selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester- polyurethane copolymer, and combinations thereof, wherein the article is mildew resistant.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is natural fiber or yam selected from the group consisting of silk, cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, or wherein the fiber or yam is synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester- polyurethane copolymer, rayon, and combinations thereof, wherein the article is mildew resistant.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is a fabric, wherein the article is mildew resistant. In an embodiment, the foregoing mildew resistant property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure exhibits mildew resistant property. In an embodiment, the foregoing mildew resistant property of the textile is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the coating is transparent.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the coating is transparent.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the coating is transparent.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the coating is transparent.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the coating is transparent.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, wherein the coating is transparent.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, wherein the coating is transparent.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is natural fiber or yarn selected from the group consisting of silk, cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof, wherein the coating is transparent.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is natural fiber or yarn selected from the group consisting of natural fiber or yam, silk, cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, or synthetic fiber or yarn, or combinations thereof, wherein the fiber or yam is synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester- polyurethane copolymer, rayon, and combinations thereof, wherein the coating is transparent.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating is transparent. In an embodiment, the foregoing transparent property of the coating is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather comprises a silk coating of the present disclosure, wherein the silk coating is transparent. In an embodiment, the foregoing transparent property of the coating is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is resistant to freeze-thaw cycle damage.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article is resistant to freeze-thaw cycle damage.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the article is resistant to freeze-thaw cycle damage. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the article is resistant to freeze-thaw cycle damage.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the article is resistant to freeze- thaw cycle damage.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, wherein the article is resistant to freeze-thaw cycle damage.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, wherein the article is resistant to freeze-thaw cycle damage.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is natural fiber or yam selected from the group consisting of silk, cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof, wherein the article is resistant to freeze-thaw cycle damage.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester- polyurethane copolymer, rayon, and combinations thereof, wherein the article is resistant to freeze-thaw cycle damage.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article is resistant to freeze-thaw cycle damage. In an embodiment, the foregoing resistant to freeze-thaw cycle damage property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure exhibits resistant to freeze-thaw cycle damage. In an embodiment, the foregoing resistant to freeze-thaw cycle damage property of the textile is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the coating provides protection from abrasion.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating provides protection from abrasion.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the coating provides protection from abrasion.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the coating provides protection from abrasion.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the coating provides protection from abrasion.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, wherein the coating provides protection from abrasion.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, wherein the coating provides protection from abrasion.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is natural fiber or yarn selected from the group consisting of silk, cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof, wherein the coating provides protection from abrasion. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yarn is selected from the group consisting of natural fiber or yam, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is synthetic fiber or yarn selected from the group consisting of polyester, nylon, polyester- polyurethane copolymer, rayon, and combinations thereof, wherein the coating provides protection from abrasion.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the coating provides protection from abrasion. In an embodiment, the foregoing abrasion resistant property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure exhibits abrasion resistant. In an embodiment, the foregoing abrasion resistant property of the textile is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article exhibits the property of blocking ultraviolet (UV) radiation.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article exhibits the property of blocking ultraviolet (UV) radiation.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01% (w/w) to about 10% (w/w) sericin, wherein the article exhibits the property of blocking ultraviolet (UV) radiation.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the article exhibits the property of blocking ultraviolet (UV) radiation.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the article exhibits the property of blocking ultraviolet (UV) radiation.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, wherein the article exhibits the property of blocking ultraviolet (UV) radiation.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, wherein the article exhibits the property of blocking ultraviolet (UV) radiation.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is natural fiber or yarn selected from the group consisting of silk, cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, or synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester-polyurethane copolymer, rayon, and combinations thereof, wherein the article exhibits the property of blocking ultraviolet (UV) radiation.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yarn is selected from the group consisting of natural fiber or yam, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is synthetic fiber or yarn selected from the group consisting of polyester, nylon, polyester- polyurethane copolymer, rayon, and combinations thereof, wherein the article exhibits the property of blocking ultraviolet (UV) radiation.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article exhibits the property of blocking ultraviolet (UV) radiation. In an embodiment, the foregoing UV blocking property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure exhibits UV blocking property. In an embodiment, the foregoing UV blocking property of the textile is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides a garment comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the garment regulates the body temperature of a wearer.

In an embodiment, the invention provides a garment comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the garment regulates the body temperature of a wearer.

In an embodiment, the invention provides a garment comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the garment regulates the body temperature of a wearer.

In an embodiment, the invention provides a garment comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the garment regulates the body temperature of a wearer.

In an embodiment, the invention provides a garment comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the garment regulates the body temperature of a wearer.

In an embodiment, the invention provides a garment comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, wherein the garment regulates the body temperature of a wearer.

In an embodiment, the invention provides a garment comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, wherein the fiber or yam is selected from the group consisting of natural fiber or yarn, synthetic fiber or yam, or combinations thereof, wherein the fiber or yarn is natural fiber or yam selected from the group consisting of silk, cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, or synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester-polyurethane copolymer, rayon, and combinations thereof, wherein the garment regulates the body temperature of a wearer.

In an embodiment, the invention provides a garment comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is natural fiber or yam selected from the group consisting of silk, cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof, wherein the garment regulates the body temperature of a wearer.

In an embodiment, the invention provides a garment comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester- polyurethane copolymer, rayon, and combinations thereof, wherein the garment regulates the body temperature of a wearer.

In an embodiment, the invention provides a garment comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the garment regulates the body temperature of a wearer. In an embodiment, the foregoing temperature regulation property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure exhibits a temperature regulation property. In an embodiment, the foregoing temperature regulation property of the textile is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, and wherein the article is tear resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the article is tear resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, and wherein the article is tear resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, and wherein the article is tear resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, and wherein the article is tear resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, and wherein the article is tear resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, and wherein the article is tear resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is natural fiber or yarn selected from the group consisting of silk, cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof, and wherein the article is tear resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yarn is selected from the group consisting of natural fiber or yam, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is synthetic fiber or yarn selected from the group consisting of polyester, nylon, polyester- polyurethane copolymer, rayon, and combinations thereof, and wherein the article is tear resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the article is tear resistant. In an embodiment, the foregoing tear resistant property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure exhibits a tear resistant property. In an embodiment, the foregoing tear resistant property of the textile is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the elasticity of the article is improved.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the elasticity of the article is reduced.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the elasticity of the article is improved. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the elasticity of the article is improved.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the elasticity of the article is reduced.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article exhibits a rebound dampening property. Without being bound by any specific theory, it is postulated that the coating prevents the article from returning to the original shape or orientation, and results in the rebound dampening property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article exhibits a rebound dampening property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the article exhibits a rebound dampening property. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the article exhibits a rebound dampening property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the article exhibits a rebound dampening property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, wherein the article exhibits a rebound dampening property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, wherein the article exhibits a rebound dampening property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is natural fiber or yarn selected from the group consisting of silk, cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof, wherein the article exhibits a rebound dampening property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yarn is selected from the group consisting of natural fiber or yam, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is synthetic fiber or yarn selected from the group consisting of polyester, nylon, polyester- polyurethane copolymer, rayon, and combinations thereof, wherein the article exhibits a rebound dampening property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article exhibits a rebound dampening property. In an embodiment, the foregoing rebound dampening property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure exhibits a rebound dampening property. In an embodiment, the foregoing rebound dampening property of the textile is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article exhibits an anti-itch property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article exhibits an anti-itch property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the article exhibits an anti-itch property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the article exhibits an anti-itch property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the article exhibits an anti-itch property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, wherein the article exhibits an anti-itch property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, wherein the article exhibits an anti-itch property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is natural fiber or yarn selected from the group consisting of silk, cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof, wherein the article exhibits an anti-itch property. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yarn is selected from the group consisting of natural fiber or yam, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is synthetic fiber or yarn selected from the group consisting of polyester, nylon, polyester- polyurethane copolymer, rayon, and combinations thereof, wherein the article exhibits an anti-itch property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article exhibits an anti-itch property. In an embodiment, the foregoing anti-itch property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure exhibits an anti- itch property. In an embodiment, the foregoing anti-itch property of the textile is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article exhibits an improved insulation/warmth property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article exhibits an improved insulation/warmth property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the article exhibits an improved insulation/warmth property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the article exhibits an improved insulation/warmth property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the article exhibits an improved insulation/warmth property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, wherein the article exhibits an improved insulation/warmth property.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article exhibits an improved insulation/warmth property. In an embodiment, the foregoing improved insulation/warmth property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure exhibits improved an insulation/warmth property. In an embodiment, the foregoing improved insulation/warmth property of the textile is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is wrinkle resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article is wrinkle resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01% (w/w) to about 10% (w/w) sericin, wherein the article is wrinkle resistant. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the article is wrinkle resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the article is wrinkle resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, wherein the article is wrinkle resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, wherein the article is wrinkle resistant.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is natural fiber or yam selected from the group consisting of silk, cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, or synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester-polyurethane copolymer, rayon, and combinations thereof, wherein the article is wrinkle resistant.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester- polyurethane copolymer, rayon, and combinations thereof, wherein the article is wrinkle resistant.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article is wrinkle resistant. In an embodiment, the foregoing wrinkle resistant property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure exhibits wrinkle resistant property. In an embodiment, the foregoing wrinkle resistant property of the textile is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is stain resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article is stain resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the article is stain resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the article is stain resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the article is stain resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, wherein the article is stain resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, wherein the article is stain resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yarn, synthetic fiber or yarn, or combinations thereof, wherein the fiber or yarn is natural fiber or yarn selected from the group consisting of silk, cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, or synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester-polyurethane copolymer, rayon, and combinations thereof, wherein the article is stain resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yarn is selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester- polyurethane copolymer, rayon, and combinations thereof, wherein the article is stain resistant.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article is stain resistant. In an embodiment, the foregoing stain resistant property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure exhibits stain resistant property. In an embodiment, the foregoing stain resistant property of the textile is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is sticky. Without being bound to any specific theory, it is postulated that the coating provides stickiness and maintains stickiness.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article is sticky.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the article is sticky.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article is sticky. In an embodiment, the foregoing sticky property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure exhibits sticky property. In an embodiment, the foregoing sticky property of the textile is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides an article comprising a textile or leather coated with silk fibroin-based proteins or fragments thereof, wherein the article exhibits improved flame resistance relative to an uncoated textile. In an embodiment, the invention provides an article comprising a textile or leather coated with silk fibroin- based proteins or fragments thereof, wherein the article exhibits equal flame resistance relative to an uncoated textile or leather. In an embodiment, the invention provides an article comprising a textile or leather coated with silk fibroin-based proteins or fragments thereof, wherein the article exhibits equal flame resistance relative to an uncoated textile or leather, wherein an alternative textile or leather coating exhibits reduced flame resistance. In an embodiment, the invention provides an article comprising a textile or leather coated with silk fibroin-based proteins or fragments thereof, wherein the article exhibits improved resistance to fire relative to an uncoated textile or leather, wherein the improved resistance to fire is determined by a flammability test. In an embodiment, the flammability test measures afterflame time, afterglow time, char length, and the observation of fabric melting or dripping.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is flame resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the article is flame resistant.

In an embodiment, the invention provides an article comprising a polyester having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is flame resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the article is a fabric, and wherein the article is flame resistant.

In an embodiment, the invention provides an article comprising a polyester having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the article is flame resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof comprise silk fibroin-based proteins or protein fragments having about 0.01 % (w/w) to about 10% (w/w) sericin, wherein the article is flame resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the article is flame resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the article is flame resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof are selected from the group consisting of natural silk based proteins or fragments thereof, recombinant silk based proteins or fragments thereof, and combinations thereof, wherein the silk based proteins or fragments thereof are natural silk based proteins or fragments thereof that are selected from the group consisting of spider silk based proteins or fragments thereof, silkworm silk based proteins or fragments thereof, and combinations thereof, wherein the natural silk based proteins or fragments are silkworm silk based proteins or fragments thereof, and the silkworm silk based proteins or fragments thereof is Bombyx mori silk based proteins or fragments thereof, wherein the article is flame resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the silk based proteins or fragments comprise silk and a copolymer, wherein the article is flame resistant.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is natural fiber or yam selected from the group consisting of silk, cotton, alpaca fleece, alpaca wool, lama fleece, lama wool, cotton, cashmere, sheep fleece, sheep wool, and combinations thereof, wherein the article is flame resistant.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the fiber or yam is selected from the group consisting of natural fiber or yam, synthetic fiber or yam, or combinations thereof, wherein the fiber or yam is synthetic fiber or yam selected from the group consisting of polyester, nylon, polyester- polyurethane copolymer, rayon, and combinations thereof, wherein the article is flame resistant.

In an embodiment, the invention provides an article comprising a fiber or yam having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the article is a fabric, wherein the fabric is flame resistant. In an embodiment, the foregoing flame resistant property of the fabric is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, a textile or leather of the present disclosure is flame resistant. In an embodiment, the foregoing flame resistant property of the textile is determined after a period of machine washing cycles selected from the group consisting of 1 cycle, 2 cycles, 3 cycles, 4 cycles, 5 cycles, 10 cycles, 25 cycles, and 50 cycles.

In an embodiment, the invention provides a leather coated with coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the leather exhibits an property selected from the group consisting of an improved color retention property, improved mildew resistance, improved resistance to freeze-thaw cycle damage, improved resistance to abrasion, improved blocking of ultraviolet (UV) radiation, improved regulation of the body temperature of a wearer, improved tear resistance, improved elasticity, improved rebound dampening, improved anti-itch properties, improved insulation, improved wrinkle resistance, improved stain resistance, and improved stickiness. In an embodiment, the invention provides a leather coated with coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the coating is transparent.

In any of the foregoing embodiments, at least one property of the article is improved, wherein the property that is improved is selected from the group consisting of color retention, resistance to microbial growth, resistance to bacterial growth, resistance to fungal growth, resistance to the buildup of static electrical charge, resistance to the growth of mildew, transparency of the coating, resistance to fireeze- thaw cycle damage, resistance from abrasion, blocking of ultraviolet (UV) radiation, regulation of the body temperature of a wearer, resistance to tearing, elasticity of the article, rebound dampening, tendency to cause itching in the wearer, thermal insulation of the wearer, wrinkle resistance, stain resistance, stickiness to skin, and flame resistance, and wherein the property is improved by an amount relative to an uncoated article selected from the group consisting of at least 5%, at least 10%, at least 15%, at least 20%, at least 25%, at least 30%, at least 35%, at least 40%, at least 45%, at least 50%, at least 55%, at least 60%, at least 65%, at least 70%, at least 75%, at least 80%, at least 85%, at least 90%, at least 95%, at least 100%, at least 125%, at least 150%, at least 200%, at least 300%, at least 400%, and at least 500%.

In any of the foregoing embodiments, the silk based proteins or protein fragments thereof have an average weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof have a poly dispersity of between about 1.0 and about 5.0, or about 1.5 and about 3.0, and optionally wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days. Additional Agents for Use with Textiles Coated with Silk Fibroin-Based Protein Fragments

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is pretreated with a wetting agent. In an embodiment, the wetting agent improves one or more coating properties. Suitable wetting agents are known to those of skill in the art. Exemplary, non-limiting examples of wetting agents from a representative supplier, Lamberti SPA, are given in the following table.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is pretreated with a detergent. In an embodiment, the detergent improves one or more coating properties. Suitable detergents are known to those of skill in the art. Exemplary, non-limiting examples of detergents from a representative supplier, Lamberti SPA, are given in the following table.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is pretreated with a sequestering or dispersing agent. Suitable sequestering or dispersing agents are known to those of skill in the art. Exemplary, non-limiting examples of sequestering or dispersing agents from a representative supplier, Lamberti SPA, are given in the following table.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is pretreated with an enzyme. Suitable enzymes are known to those of skill in the art. Exemplary, non-limiting examples of enzymes from a representative supplier, Lamberti SPA, are given in the following table.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is pretreated with a bleaching agent. Suitable bleaching agents are known to those of skill in the art. Exemplary, non- limiting examples of bleaching agents from a representative supplier, Lamberti SPA, are given in the following table.

Stabilox OTN Highly concentrated stabilizer for alkaline bleaching with cone. hydrogen peroxide. Suitable for a wide variety of processes.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is pretreated with an antifoaming agent. Suitable antifoaming agents are known to those of skill in the art. Exemplary, non-limiting examples of antifoaming agents from a representative supplier, Lamberti SPA, are given in the following table.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is pretreated with an anti- creasing agent. Suitable anti-creasing agents are known to those of skill in the art. Exemplary, non-limiting examples of anti-creasing agents from a representative supplier, Lamberti SPA, are given in the following table.

Lubisol AM Lubricating and anti-creasing agent for rope wet operation on all kind of fibers and machines.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is treated with a dye dispersing agent. Suitable dye dispersing agents are known to those of skill in the art. Exemplary, non-limiting examples of dye dispersing agents from a representative supplier, Lamberti SPA, are given in the following table.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is treated with a dye leveling agent. Suitable dye leveling agents are known to those of skill in the art. Exemplary, non-limiting examples of dye leveling agents from a representative supplier, Lamberti SPA, are given in the following table.

Lamegal A 12 Leveling agent for dyeing on wool, polyamide

and its blends with acid or metal complex dyes.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is treated with a dye fixing agent. Suitable dye fixing agents are known to those of skill in the art. Exemplary, non- limiting examples of dye fixing agents from a representative supplier, Lamberti SPA, are given in the following table.

Lamfix PA/TR Fixing agent to improve the wet fastness of acid

dyes on polyamide fabrics, dyed or printed and polyamide yarns. Retarding agent in dyeing of

Polyamide/cellulosic blends with direct dyes.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is treated with a dye special resin agent. Suitable dye special resin agents are known to those of skill in the art. Exemplary, non-limiting examples of dye special resin agents from a representative supplier, Lamberti SPA, are given in the following table.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is treated with a dye anti- reducing agent. Suitable dye anti-reducing agents are known to those of skill in the art. Exemplary, non-limiting examples of dye anti-reducing agents from a representative supplier, Lamberti SPA, are given in the following table.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is treated with a pigment dye system anti-migrating agent. Suitable pigment dye system anti-migrating agents are known to those of skill in the art. Exemplary, non-limiting examples of pigment dye system anti-migrating agents from a representative supplier, Lamberti SPA, are given in the following table.

Neopat Compound Compound, developed as migration inhibitor for 96/m cone. continuous dyeing process with pigments (pad- dry process).

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is treated with a pigment dye system binder. Suitable pigment dye system binders are known to those of skill in the art. Exemplary, non-limiting examples of pigment dye system binders from a representative supplier, Lamberti SPA, are given in the following table.

Neopat Binder PM/S Concentrated version of a specific binder used to cone. prepare pad-liquor for dyeing with pigments

(pad-dry process).

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is treated with a pigment dye system binder and anti-migrating agent combination. Suitable pigment dye system binder and anti-migrating agent combinations are known to those of skill in the art. Exemplary, non-limiting examples of pigment dye system binder and anti-migrating agent combinations from a representative supplier, Lamberti SPA, are given in the following table.

Neopat Compound Highly concentrated all-in-one product

PK1 specifically developed as migration inhibitor

with specific binder for continuous dyeing

process with pigments (pad-dry process).

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is treated with a delave agent. Suitable delave agents are known to those of skill in the art. Exemplary, non-limiting examples of delave agents from a representative supplier, Lamberti SPA, are given in the following table.

Neopat compound FTN Highly concentrated compound of surfactants

and polymers specifically developed for pigment dyeing and pigment-reactive dyeing process;

especially for medium/dark shades for wash off effect. In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is traditionally finished with a wrinkle free treatment. Suitable wrinkle free treatments are known to those of skill in the art. Exemplary, non-limiting examples of wrinkle free treatments from a representative supplier, Lamberti SPA, are given in the following table.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is traditionally finished with a softener. Suitable softeners are known to those of skill in the art. Exemplary, non- limiting examples of softeners from a representative supplier, Lamberti SPA, are given in the following table.

Texamina HVO Anphoteric softening agent for woven and knitted fabrics of cotton, other cellulosics and blends. Provides a soft, smooth and dry handle. Applied by padding.

Texamina SIL Nonionic silicon dispersion in water. Excellent softening, lubricating and anti-static properties for all fibre types by padding.

Texamina SILK Special cationic softener with silk protein inside. Provides a

"swollen touch" particularly suitable for cellulosic, wool, silk.

Lamfinish LW All-in compound based on special polymeric hydrophilic softeners; by coating, foulard, and exhaustion.

Elastolam E50 General purpose mono-component silicone elastomeric

softener for textile finishing.

Elastolam EC 100 Modified polysiloxane micro-emulsion which gives a

permanent finishing, with extremely soft and silky handle.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is traditionally finished with a handle modifier. Suitable handle modifiers are known to those of skill in the art. Exemplary, non-limiting examples of handle modifiers from a representative supplier, Lamberti SPA, are given in the following table.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is traditionally finished with a waterborne polyurethane (PU) dispersion. Suitable waterbome polyurethane dispersions for traditional finishing are known to those of skill in the art. Exemplary, non-limiting examples of waterborne polyurethane dispersions for traditional finishing from a representative supplier, Lamberti SPA, are given in the following table.

Rolflex NBC Aliphatic waterborne PU dispersion generally used by

padding application as a filling and zero formaldehyde sizing agent. Can be used for outwear and fashion finishing where a full, elastic and non-sticky touch is required.

Rolflex PAD Aliphatic waterborne PU dispersion specifically designed for padding application for outwear, sportswear and fashion applications where a full, elastic and non sticky touch is required. Excellent washing and dry cleaning fastness as well as good bath stability.

Rolflex PN Aliphatic waterborne PU dispersion generally applied by padding application for outerwear and fashion high quality applications where strong, elastic non sticky finishes are required.

Elafix PV 4 Aliphatic blocked isocyanate nano-dispersion used in order to give anti-felting and anti-pilling properties to pure wool fabrics and his blend.

Rolflex SW3 Aliphatic waterborne PU dispersion particularly suggested to be used by padding application for the finishing of outwear, sportswear and fashion where a slippery and elastic touch is required. It is also a good anti-pilling agent. Excellent in wool application.

Rolflex C 86 Aliphatic cationic waterborne PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, fashion where medium-soft and pleasant full touch is required. Fabrics treated with the product can be dyed with a selection of dyes, to get double-color effects of different intensity.

Rolflex CN 29 Aliphatic cationic waterborne PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, fashion where soft and pleasant full touch is required. Fabrics treated with the product can be dyed with a selection of dyes, to get double-color effects of different intensity.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is traditionally finished with a finishing resin. Suitable finishing resins are known to those of skill in the art. Exemplary, non-limiting examples of finishing resins from a representative supplier, Lamberti SPA, are given in the following table. Textol SB 21 Butadienic resin for finishing and binder for textile printing

Appretto PV/CC Vinylacetate water dispersion for rigid stiffening

Amisolo B CMS water dispersion for textile finishing as stiffening agent

Lamovil RP PVOH stabilized solution as stiffening agent

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is technically finished with a waterbome polyurethane dispersion. Suitable waterbome polyurethane dispersions for technical finishing are known to those of skill in the art. Exemplary, non-limiting examples of waterbome polyurethane dispersions for technical finishing from a representative supplier, Lamberti SPA, are given in the following table.

Rolflex BZ 78 Aliphatic waterborned PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, sportswear, fashion and technical articles for industrial applications. The product has an excellent hydrolysis resistance, a very high charge digestion and electrolites stability and an excellent mechanical and tear resistance. Can be also suitable for foam coating and printing application.

Rolflex PU 147 Aliphatic poly ether polyurethane dispersion in water. This product shows good film forming properties at room temperature. It has high fastness to light and ultraviolet radiation and good resistance to water, solvent and chemical agents, as well as mechanical resistance.

Rolflex SG Aliphatic poly ether polyurethane dispersion in water. Due to its thermoplastic properties it is suggested to formulate heat activated adhesives at low temperatures.

Elafix PV 4 Aliphatic blocked isocyanate nano-dispersion used in order to give antifelting and antipilling properties to pure wool fabrics and his blend.

Rolflex C 86 Aliphatic cationic waterborne PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, fashion where medium-soft and pleasant full touch is required. Fabrics treated with the product can be dyed with a selection of dyes, to get double-color effects of different intensity.

Rolflex CN 29 Aliphatic cationic waterborne PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, fashion where soft and pleasant full touch is required. Fabrics treated with the product can be dyed with a selection of dyes, to get double-color effects of different intensity.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is technically finished with an oil or water repellant. Suitable oil or water repellants for technical finishing are known to those of skill in the art. Exemplary, non-limiting examples of oil or water repellants for technical finishing from a representative supplier, Lamberti SPA, are given in the following table.

Lamgard EXT Crosslinker for fluorocarbon resins to improve washing fastness.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is technically finished with a flame retardant. Suitable flame retardants for technical finishing are known to those of skill in the art. Exemplary, non-limiting examples of flame retardants for technical finishing from a representative supplier, Lamberti SPA, are given in the following table.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is technically finished with a crosslinker. Suitable crosslinkers for technical finishing are known to those of skill in the art. Exemplary, non-limiting examples of crosslinkers for technical finishing from a representative supplier, Lamberti SPA, are given in the following table.

In an embodiment, the invention provides an article comprising a fiber or yarn having a coating, wherein the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa, wherein the article is a fabric, and wherein the fabric is technically finished with a thickener for technical finishing. Suitable thickeners for technical finishing are known to those of skill in the art. Exemplary, non-limiting examples of thickeners for technical finishing from a representative supplier, Lamberti SPA, are given in the following table.

In any of the foregoing textile or leather embodiments, the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa. In any of the foregoing textile or leather embodiments, the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 6 kDa to about 17 kDa. In any of the foregoing textile or leather embodiments, the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 17 kDa to about 39 kDa. In any of the foregoing textile or leather embodiments, the coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 39 kDa to about 80 kDa.

In any of the foregoing textile or leather embodiments, the silk based proteins or protein fragments thereof have an average weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof have a polydispersity of between about 1.5 and about 3.0, and optionally wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days.

Other Materials Coated with Silk Fibroin-Based Protein Fragments

In an embodiment, the invention provides a material coated with silk fibroin- based proteins or fragments thereof. The material may be any material suitable for coating, including plastics (e.g., vinyl), foams (e.g. , for use in padding and cushioning), and various natural or synthetic products.

In an embodiment, the invention provides an automobile component coated with silk fibroin-based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa. In an embodiment, the invention provides an automobile component coated with silk fibroin-based proteins or fragments thereof having a weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof have a polydispersity of between about 1.5 and about 3.0, and optionally wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days. In an embodiment, the invention provides an automobile component coated with silk fibroin-based proteins or fragments thereof, wherein the automobile component exhibits an improved property relative to an uncoated automobile component. In an embodiment, the invention provides an automobile component coated with silk fibroin- based proteins or fragments thereof, wherein the automobile component exhibits an improved property relative to an uncoated automobile component, and wherein the automobile component is selected from the group consisting of an upholstery fabric, a headliner, a seat, a headrest, a transmission control, a floor mat, a carpet fabric, a dashboard, a steering wheel, a trim, a wiring harness, an airbag cover, an airbag, a sunvisor, a seat belt, a headrest, an armrest, and a children's car seat. In an embodiment, the invention provides an electrical component insulated with a coating comprising silk fibroin-based proteins or fragments thereof.

In an embodiment, the invention provides a foam coated with silk fibroin-based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa. In an embodiment, the invention provides a foam coated with silk fibroin-based proteins or fragments thereof having a weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof have a polydispersity of between about 1.5 and about 3.0, and optionally wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days. In an embodiment, the invention provides a foam coated with silk fibroin-based proteins or fragments thereof, wherein the foam exhibits an improved property relative to an uncoated foam, and wherein the foam is selected from the group consisting of a polyurethane foam, an ethylene-vinyl acetate copolymer foam, a low density polyethylene foam, a low density polyethylene foam, a high density polyethylene foam, a polypropylene copolymer foam, a linear low density polyethylene foam, a natural rubber foam, a latex foam, and combinations thereof.

In any of the foregoing embodiments, the material coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 5 kDa to about 144 kDa. In any of the foregoing embodiments, the material coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 6 kDa to about 17 kDa. In any of the foregoing embodiments, the material coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 17 kDa to about 39 kDa. In any of the foregoing embodiments, the material coating comprises silk based proteins or fragments thereof having a weight average molecular weight range of about 39 kDa to about 80 kDa.

In any of the foregoing embodiments, the silk based proteins or protein fragments thereof have an average weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof have a polydispersity of between about 1.5 and about 3.0, and wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days.

Processes for Coating Textiles and Leathers with Silk Fibroin-Based Protein Fragments In an embodiment, a method for silk coating a textile, leather, or other material

(such as a foam) includes immersion of the textile, leather, or other material in any of the aqueous solutions of pure silk fibroin-based protein fragments of the present disclosure. In an embodiment, a method for coating a textile, leather, or other material (such as a foam) includes spraying. In an embodiment, a method for coating a textile, leather, or other material (such as a foam) includes chemical vapor deposition. In an embodiment, a method for silk coating a textile, leather, or other material (such as a foam) includes electrochemical coating. In an embodiment, a method for silk coating a textile, leather, or other material (such as a foam) includes knife coating to spread any of the aqueous solutions of pure silk fibroin-based protein fragments of the present disclosure onto the fabric. The coated article may then be air dried, dried under heat/air flow, or cross-linked to the fabric surface. In an embodiment, a drying process includes curing with additives, irradiation (e.g. , using UV light), heat (e.g., microwave or radiofrequency irradiation), and/or drying at ambient condition. In an embodiment, the invention provides a method of coating a textile, leather, or other material (such as a foam) comprising the step of applying a coating, wherein the coating comprises a solution of silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, wherein the coating is applied to at least one side of the textile, leather, or other material using a method selected from the group consisting of a bath coating process, a spray coating process, a stencil (i. e. , screen) process, a silk-foam based process, a roller-based process, a magnetic roller process, a knife process, a transfer process, a foam process, a lacquering process, a supercritical fluid impregnation process, and a printing process.

In an embodiment, the invention provides a method of coating a textile or leather comprising a step selected from the group consisting of providing an unwinding device used to unroll the fabric supply in a roll configuration, providing a feeding system used to control the feed rate of fabric, providing a material compensator used to maintain consistent the fabric tension, providing a coating machine to apply the silk solution (i.e. , silk fibroin-based protein fragments) in different state (liquid or foam) to the fabric, providing a measuring system used to control the amount of silk solution applied, providing a dryer used to cure or dry the silk solution on the fabric, providing a cooling station used to bring the fabric temperature close to room value, providing a steering frame used to guide the fabric to the rewinding device and maintain straight edges, providing a rewinding step used to collect the coated fabric in roll, providing UV irradiation for curing of silk and/or other fabric additives (e.g. , in a chemical cross- linking step), providing radiofrequency (RF) irradiation (e.g., using microwave irradiation) for drying and chemical cross-linking, and combinations thereof. Chemical and enzymatic cross-linking steps suitable for use with the compositions, articles, and methods of the invention include any method known to those of skill in the art, including but not limited to N-hydroxysuccinimide ester crosslinking, imidoester crosslinking, carbodiimide crosslinking, dicyclohexyl carbodiimide crosslinking, maleimide crosslinking, haloacetyl crosslinking, pyridyl disulfide crosslinking, hydrazide crosslinking, alkoxyamine crosslinking, reductive animation crosslink, aryl azide crosslinking, diazirine crosslinking, azide-phosphine crosslinking, transferase crosslinking, hydrolase crosslinking, transglutaminase crosslinking, peptidase crosslinking (e.g., sortase SrtA from Staphylococcus aureus), oxidoreductase crosslinking, tyrosinase crosslinking, laccase crosslinking, peroxidase crosslinking (e.g., horseradish peroxidase), lysyl oxidase crosslinking, and combinations thereof.

In an embodiment, the invention provides a method of coating a textile or leather comprising the step of applying a coating, wherein the coating comprises a solution of silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, and wherein the coating is applied to at least one side of the textile or leather using a supercritical fluid impregnation process. The supercritical fluid impregnation process may use CCh as the supercritical fluid to solubilize and impregnate silk based proteins or fragments thereof into a textile or leather, wherein the supercritical CCh may include optional organic modifiers known in the art (e.g. , methanol) and may further include additional agents described herein, such as dyes.

In an embodiment, the invention provides a method of coating a textile or leather comprising the step of applying a coating, wherein the coating comprises a solution of silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, using a handheld aerosol spray suitable for consumer use or an aerosol spray system suitable for use by a professional cleaner (e.g. , a dry cleaner).

In an embodiment, the invention provides a method of coating a textile or leather comprising the step of applying a coating, wherein the coating comprises a solution of silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, using a home washing machine. In an embodiment, the invention provides a method of coating a fabric comprising the steps of:

(a) applying a pretreatment selected from the group consisting of a wetting agent, a detergent, a sequestering or dispersing agent, an enzyme, a bleaching agent, an antifoaming agent, an anti-creasing agent, a dye dispersing agent, a dye leveling agent, a dye fixing agent, a dye special resin agent, a dye anti-reducing agent, a pigment dye system anti-migrating agent, a pigment dye system binder, a delave agent, a wrinkle free treatment, a softener, a handle modifier, a waterborne polyurethane dispersion, a finishing resin, an oil or water repellant, a flame retardant, a crosslinker, a thickener for technical finishing, or any combination thereof;

(b) applying a coating comprising a solution of silk based proteins or fragments thereof having a weight average molecular weight range of about 1 kDa to about 350 kDa, or about 5 kDa to about 144 kDa, using a spray, screen, or stencil coating process; and

(c) drying and optionally curing the coating.

In any of the foregoing embodiments of methods, the silk based proteins or protein fragments thereof may have an average weight average molecular weight range selected from the group consisting of about 5 to about 10 kDa, about 6 kDa to about 17 kDa, about 17 kDa to about 39 kDa, about 39 kDa to about 80 kDa, about 60 to about 100 kDa, and about 80 kDa to about 144 kDa, wherein the silk based proteins or fragments thereof have a polydispersity of between about 1.0 and about 5.0, or about 1.5 and about 3.0, and optionally wherein the proteins or protein fragments, prior to coating the fabric, do not spontaneously or gradually gelate and do not visibly change in color or turbidity when in a solution for at least 10 days. Additives for Silk Fibroin-Based Protein Fragments and Solutions Thereof

In an embodiment, a solution of the present disclosure is contacted with an additive, such as a therapeutic agent and/or a molecule. In an embodiment, molecules include, but are not limited to, antioxidants and enzymes. In an embodiment, molecules include, but are not limited to, ceramics, ceramic particles, metals, metal particles, polymer particles, aldehydes, luminescent molecules, phosphorescent molecules, fluorescent molecules, inorganic particles, organic particles, selenium, ubiquinone derivatives, thiol-based antioxidants, saccharide-containing antioxidants, polyphenols, botanical extracts, caffeic acid, apigenin, pycnogenol, resveratrol, folic acid, vitamin B12, vitamin B6, vitamin B3, vitamin E, vitamin C and derivatives thereof, vitamin D, vitamin A, astaxathin, Lutein, lycopene, essential fatty acids (omegas 3 and 6), iron, zinc, magnesium, flavonoids (soy, Curcumin, Silymarin, Pycnongeol), growth factors, aloe, hyaluronic acid, extracellular matrix proteins, cells, nucleic acids, biomarkers, biological reagents, zinc oxide, benzoyl peroxide, retinoids, titanium, allergens in a known dose (for sensitization treatment), essential oils including, but not limited to, lemongrass or rosemary oil, and fragrances. Therapeutic agents include, but are not limited to, small molecules, drugs, proteins, peptides and nucleic acids. In an embodiment, a solution of the present disclosure is contacted with an allergen of known quantity prior to forming the article. Allergens include but are not limited to milk, eggs, peanuts, tree nuts, fish, shellfish, soy and wheat. Known doses of allergen loaded within a silk article can be released at a known rate for controlled exposure allergy study, tests and sensitization treatment.

In an embodiment, silk fibroin-based protein fragments and solutions thereof may be combined with other soluble and insoluble additives coated onto textiles and leather as described herein, wherein the silk fibroin-based protein fragments and solutions functions as a binder or a dispersion medium for the additives. Additives described herein and those known of ordinary skill in the art for use with coating textiles and leather may be used. The combinations of silk fibroin-based protein fragments and solutions thereof with other soluble and insoluble additives may exhibit improved properties as described herein. The property that is improved may be selected from the group consisting of color retention, resistance to microbial growth, resistance to bacterial growth, resistance to fungal growth, resistance to the buildup of static electrical charge, resistance to the growth of mildew, transparency of the coating, resistance to freeze-thaw cycle damage, resistance from abrasion, blocking of ultraviolet (UV) radiation, regulation of the body temperature of a wearer, resistance to tearing, elasticity of the article, rebound dampening, tendency to cause itching in the wearer, thermal insulation of the wearer, wrinkle resistance, stain resistance, stickiness to skin, flame resistance, and combinations thereof. For example, silk fibroin-based protein fragments and solutions thereof may be combined with insoluble ceramic particles as a suspension, and subsequently coated onto a textile using any of the methods described herein to provide further thermal insulation for the wearer and/or to provide improved flame resistance, or to provide other improved properties.

In an embodiment, a solution of the present disclosure is used to create an article with microneedles by standard methods known to one in the art for controlled delivery of molecules or therapeutic agents to or through the skin.

Processes for Production of Silk Fibroin-Based Protein Fragments and Solutions Thereof

As used herein, the term "fibroin" includes silkworm fibroin and insect or spider silk protein. In an embodiment, fibroin is obtained from Bombyx mori. In an embodiment, the spider silk protein is selected from the group consisting of swathing silk (Achniform gland silk), egg sac silk (Cylindriform gland silk), egg case silk (Tubuliform silk), non-sticky dragline silk (Ampullate gland silk), attaching thread silk (Pyriform gland silk), sticky silk core fibers (Flagelliform gland silk), and sticky silk outer fibers (Aggregate gland silk).

A silk fragment- water solution of the present disclosure can be sterilized following standard methods in the art not limited to filtration, heat, radiation or e-beam. It is anticipated that the silk protein fragment mixture, because of its shorter protein polymer length, will withstand sterilization better than intact silk protein solutions described in the art. Additionally, silk articles created from the SPF mixtures described herein may be sterilized as appropriate to application.

In an embodiment, the above-described SPF mixture solutions may be utilized to coat at least a portion of a fabric which can be used to create a textile. In an embodiment, the above-described SPF mixture solutions may be weaved into yarn that can be used as a fabric in a textile.

Methods and processes for making silk fibroin-based protein fragments and solutions thereof are generally described by U.S. Patents Nos. 9,187,538, 9,522, 107, 9,517, 191, 9,522,108, 9,51 1 ,012, and 9,545,369, U.S. Patent Application Publications Nos. 20160022559, 20150094269, 20160222579, and 20160281294, and International Patent Application Publications Nos. WO 2015048805 and WO 2016090055, the entirety of each are incorporated herein by reference. Briefly, heat-treated or non-heat- treated silk worm cocoons, silk fibers, silk powder, or spider silk can be used as the silk source. If starting from raw silk cocoons from Bombyx mori, the cocoons can be cut into small pieces. The raw silk is then extracted and rinsed to remove any sericin, which results in substantially sericin free raw silk. In an embodiment, water is heated, and a salt is added, for example a carbonate. The raw silk is added to the boiling water/salt, and submerged for a period of time. In some embodiments, boiling for a longer time results in smaller silk protein fragments. Subsequently, the solution is drained, and excess water/salt is removed from the silk fibroin fibers (e.g., ring out the fibroin extract by hand, spin cycle using a machine, etc.). The resulting silk fibroin extract is rinsed with warm to hot water to remove any remaining adsorbed sericin or contaminate. The resulting silk fibroin extract is a substantially sericin-depleted silk fibroin. In some embodiments, it may be advantageous to agitate, turn or circulate the rinse water to maximize the rinse effect. After rinsing, excess water is removed from the extracted silk fibroin fibers (e.g., ring out fibroin extract by hand or using a machine). Alternatively, methods known to one skilled in the art such as pressure, temperature, or other reagents or combinations thereof may be used for the purpose of sericin extraction. The extracted fibroin fibers are then allowed to dry. Once dry, the extracted silk fibroin is dissolved using a solvent added to the silk fibroin at a temperature between ambient and boiling. In an embodiment, the solvent is a solution of a different salt. Alternatively, the extracted fibroin fibers are not dried but wet and placed in the solvent; solvent concentration can then be varied to achieve similar concentrations as to when adding dried silk to the solvent. Complete dissolution of the extracted fibroin fibers can be achieved by varying the treatment time and temperature along with the concentration of dissolving solvent. To ensure complete dissolution, the silk fibers should be fully immersed within the already heated solvent solution and then maintained at various temperatures. The temperature at which the silk fibroin extract is added to the salt solution (or vice versa) has an effect on the time required to completely dissolve the fibroin and on the resulting molecular weight and polydispersity of the final SPF mixture solution. In addition, agitation during introduction or dissolution may be used to facilitate dissolution at varying temperatures and concentrations. Alternatively, whole cocoons may be placed directly into a solvent, bypassing extraction. This requires subsequent filtration of silk worm particles from the silk and solvent solution and sericin removal using methods know in the art for separating hydrophobic and hydrophilic proteins such as a column separation and/or chromatography, ion exchange, chemical precipitation with salt and/or pH, and or enzymatic digestion and filtration or extraction, all methods are common examples and without limitation for standard protein separation methods. Non-heat treated cocoons with the silkworm removed, may alternatively be placed into a solvent, bypassing extraction. The methods described above may be used for sericin separation, with the advantage that non-heat treated cocoons will contain significantly less worm debris. Dialysis may be used to remove the dissolution solvent from the resulting dissolved fibroin protein fragment solution by dialyzing the solution against a volume of water. Pre-filtration prior to dialysis is helpful to remove any debris (i.e., silk worm remnants) from the silk and salt solution. The result of dissolution at the desired time and temperate filtration is a generally translucent particle-free room temperature shelf- stable silk protein fragment-salt solution. After dialysis, the final silk solution maybe further filtered to remove any remaining debris (i.e., silk worm remnants). Alternatively, Tangential Flow Filtration (TFF), which is a rapid and efficient method for the separation and purification of biomolecules, may be used to remove the solvent from the resulting dissolved fibroin solution. TFF offers a highly pure aqueous silk protein fragment solution and enables scalability of the process in order to produce large volumes of the solution in a controlled and repeatable manner.

Following are non-limiting examples of suitable ranges for various parameters in and for preparation of the silk solutions of the present disclosure. The silk solutions of the present disclosure may include one or more, but not necessarily all, of these parameters and may be prepared using various combinations of ranges of such parameters.

In an embodiment, the percent silk in the solution is less than 30%. In an embodiment, the percent silk in the solution is less than 25%. In an embodiment, the percent silk in the solution is less than 20%. In an embodiment, the percent silk in the solution is less than 19%. In an embodiment, the percent silk in the solution is less than 18%. In an embodiment, the percent silk in the solution is less than 17%. In an embodiment, the percent silk in the solution is less than 16%. In an embodiment, the percent silk in the solution is less than 15%. In an embodiment, the percent silk in the solution is less than 14%. In an embodiment, the percent silk in the solution is less than 13%. In an embodiment, the percent silk in the solution is less than 12%. In an embodiment, the percent silk in the solution is less than 11 %. In an embodiment, the percent silk in the solution is less than 10%. In an embodiment, the percent silk in the solution is less than 9%. In an embodiment, the percent silk in the solution is less than 8%. In an embodiment, the percent silk in the solution is less than 7%. In an embodiment, the percent silk in the solution is less than 6%. In an embodiment, the percent silk in the solution is less than 5%. In an embodiment, the percent silk in the solution is less than 4%. In an embodiment, the percent silk in the solution is less than 3%. In an embodiment, the percent silk in the solution is less than 2%. In an embodiment, the percent silk in the solution is less than 1%. In an embodiment, the percent silk in the solution is less than 0.9%. In an embodiment, the percent silk in the solution is less than 0.8%. In an embodiment, the percent silk in the solution is less than 0.7%. In an embodiment, the percent silk in the solution is less than 0.6%. In an embodiment, the percent silk in the solution is less than 0.5%. In an embodiment, the percent silk in the solution is less than 0.4%. In an embodiment, the percent silk in the solution is less than 0.3%. In an embodiment, the percent silk in the solution is less than 0.2%. In an embodiment, the percent silk in the solution is less than 0.1%. In an embodiment, the percent silk in the solution is greater than 0.1%. In an embodiment, the percent silk in the solution is greater than 0.2%. In an embodiment, the percent silk in the solution is greater than 0.3%. In an embodiment, the percent silk in the solution is greater than 0.4%. In an embodiment, the percent silk in the solution is greater than 0.5%. In an embodiment, the percent silk in the solution is greater than 0.6%. In an embodiment, the percent silk in the solution is greater than 0.7%. In an embodiment, the percent silk in the solution is greater than 0.8%. In an embodiment, the percent silk in the solution is greater than 0.9%. In an embodiment, the percent silk in the solution is greater than 1%. In an embodiment, the percent silk in the solution is greater than 2%. In an embodiment, the percent silk in the solution is greater than 3%. In an embodiment, the percent silk in the solution is greater than 4%. In an embodiment, the percent silk in the solution is greater than 5%. In an embodiment, the percent silk in the solution is greater than 6%. In an embodiment, the percent silk in the solution is greater than 7%. In an embodiment, the percent silk in the solution is greater than 8%. In an embodiment, the percent silk in the solution is greater than 9%. In an embodiment, the percent silk in the solution is greater than 10%. In an embodiment, the percent silk in the solution is greater than 11 %. In an embodiment, the percent silk in the solution is greater than 12%. In an embodiment, the percent silk in the solution is greater than 13%. In an embodiment, the percent silk in the solution is greater than 14%. In an embodiment, the percent silk in the solution is greater than 15%. In an embodiment, the percent silk in the solution is greater than 16%. In an embodiment, the percent silk in the solution is greater than 17%. In an embodiment, the percent silk in the solution is greater than 18%. In an embodiment, the percent silk in the solution is greater than 19%. In an embodiment, the percent silk in the solution is greater than 20%. In an embodiment, the percent silk in the solution is greater than 25%. In an embodiment, the percent silk in the solution is between 0. 1% and 30%. In an embodiment, the percent silk in the solution is between 0. 1 % and 25%. In an embodiment, the percent silk in the solution is between 0. 1% and 20%. In an embodiment, the percent silk in the solution is between 0. 1 % and 15%. In an embodiment, the percent silk in the solution is between 0.1 % and 10%. In an embodiment, the percent silk in the solution is between 0. 1 % and

9%. In an embodiment, the percent silk in the solution is between 0. 1 % and 8^ Ό. In an embodiment, the percent silk in the solution is between OA 0 / x o and 7%. In an embodiment, the percent silk in the solution is between 0. 1 % and 6.5%. In an embodiment, the percent silk in the solution is between OA 0 / x o and 6%. In an embodiment, the percent silk in the solution is between 0. 1 % and 5.5%. In an embodiment, the percent silk in the solution is between OA 0 / x o and 5%. In an embodiment, the percent silk in the solution is between 0. 1 % and 4.5%. In an embodiment, the percent silk in the solution is between OA 0 / x o and 4%. In an embodiment, the percent silk in the solution is between 0. 1 % and 3.5%. In an embodiment, the percent silk in the solution is between OA 0 / x o and 3%. In an embodiment, the percent silk in the solution is between 0. 1 % and 2.5%. In an embodiment, the percent silk in the solution is between 0. 1 % and 2.0%. In an embodiment, the percent silk in the solution is between 0. 1 % and 2.4%. In an embodiment, the percent silk in the solution is between 0.5°/ x o and 5%. In an embodiment, the percent silk in the solution is between 0.5% and 4.5%. In an embodiment, the percent silk in the solution is between 0.5°/ x o and 4%. In an embodiment, the percent silk in the solution is between 0.5% and 3.5%. In an embodiment, the percent silk in the solution is between 0.5°/ x o and 3%. In an embodiment, the percent silk in the solution is between 0.5% and 2.5%. In an embodiment, the percent silk in the solution is between 1 and 4%. In an embodiment, the percent silk in the solution is between 1 and 3.5%. In an embodiment, the percent silk in the solution is between 1 and 3%. In an embodiment, the percent silk in the solution is between 1 and 2.5%. In an embodiment, the percent silk in the solution is between 1 and 2.4%. In an embodiment, the percent silk in the solution is between 1 and 2%. In an embodiment, the percent silk in the solution is between 20% and 30%. In an embodiment, the percent silk in the solution is between 0.1% and 6%. In an embodiment, the percent silk in the solution is between 6% and 10%. In an embodiment, the percent silk in the solution is between 6% and 8%. In an embodiment, the percent silk in the solution is between 6% and 9%. In an embodiment, the percent silk in the solution is between 10% and 20%. In an embodiment, the percent silk in the solution is between 11% and 19%. In an embodiment, the percent silk in the solution is between 12% and 18%. In an embodiment, the percent silk in the solution is between 13% and 17%. In an embodiment, the percent silk in the solution is between 14% and 16%. In an embodiment, the percent silk in the solution is 2.4%. In an embodiment, the percent silk in the solution is 2.0%.

In an embodiment, the percent sericin in the solution is non-detectable to 30%. In an embodiment, the percent sericin in the solution is non-detectable to 5%. In an embodiment, the percent sericin in the solution is 1%. In an embodiment, the percent sericin in the solution is 2%. In an embodiment, the percent sericin in the solution is 3%. In an embodiment, the percent sericin in the solution is 4%. In an embodiment, the percent sericin in the solution is 5%. In an embodiment, the percent sericin in the solution is 10%. In an embodiment, the percent sericin in the solution is 30%.

In an embodiment, the stability of the LiBr-silk fragment solution is 0 to 1 year. In an embodiment, the stability of the LiBr-silk fragment solution is 0 to 2 years. In an embodiment, the stab lity of the LiBr-silk fragment solution is 0 to 3 years. In an embodiment, the stab lity of the LiBr-silk fragment solution is 0 to 4 years. In an embodiment, the stab lity of the LiBr-silk fragment solution is 0 to 5 years. In an embodiment, the stab lity of the LiBr-silk fragment solution is 1 to 2 years. In an embodiment, the stab lity of the LiBr-silk fragment solution is 1 to 3 years. In an embodiment, the stab lity of the LiBr-silk fragment solution is 1 to 4 years. In an embodiment, the stab lity of the LiBr-silk fragment solution is 1 to 5 years. In an embodiment, the stab lity of the LiBr-silk fragment solution is 2 to 3 years. In an embodiment, the stab lity of the LiBr-silk fragment solution is 2 to 4 years. In an embodiment, the stab lity of the LiBr-silk fragment solution is 2 to 5 years. In an embodiment, the stab lity of the LiBr-silk fragment solution is 3 to 4 years. In an embodiment, the stab lity of the LiBr-silk fragment solution is 3 to 5 years. In an embodiment, the stability of the LiBr-silk fragment solution is 4 to 5 years. In an embodiment, the stability of a composition of the present disclosure is 10 days to 6 months. In an embodiment, the stability of a composition of the present disclosure is 6 months to 12 months. In an embodiment, the stability of a composition of the present disclosure is 12 months to 18 months. In an embodiment, the stability of a composition of the present disclosure is 18 months to 24 months. In an embodiment, the stability of a composition of the present disclosure is 24 months to 30 months. In an embodiment, the stability of a composition of the present disclosure is 30 months to 36 months. In an embodiment, the stability of a composition of the present disclosure is 36 months to 48 months. In an embodiment, the stability of a composition of the present disclosure is 48 months to 60 months.

In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 5 kDa to 144 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 6 kDa to 17 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 17 kDa to 39 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin- based protein fragments having an average weight average molecular weight ranging from 39 kDa to 80 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 39 kDa to 144 kDa.

In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight of about 1 kDa to about 350 kDa, or about 1 kDa to about 300 kDa, or about 1 kDa to about 250 kDa, or about 1 kDa to about 200 kDa, or about 1 kDa to about 150 kDa, or about 1 kDa to about 100 kDa, or about 1 kDa to about 50 kDa, or about 1 kDa to about 25 kDa.

In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 1 to 5 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 5 to 10 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 10 to 15 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 15 to 20 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 20 to 25 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 25 to 30 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 30 to 35 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 35 to 40 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 40 to 45 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 45 to 50 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 50 to 55 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 55 to 60 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 60 to 65 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 65 to 70 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 70 to 75 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 75 to 80 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 80 to 85 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 85 to 90 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 90 to 95 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 95 to 100 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 100 to 105 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 105 to 1 10 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 110 to 1 15 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 115 to 120 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 120 to 125 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 125 to 130 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 130 to 135 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 135 to 140 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 140 to 145 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 145 to 150 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 150 to 155 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 155 to 160 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 160 to 165 kDa. I In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 165 to 170 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 170 to 175 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 175 to 180 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 180 to 185 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 185 to 190 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 190 to 195 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 195 to 200 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 200 to 205 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 205 to 210 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 210 to 215 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 215 to 220 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 220 to 225 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 225 to 230 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 230 to 235 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 235 to 240 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 240 to 245 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 245 to 250 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 250 to 255 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 255 to 260 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 260 to 265 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 265 to 270 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 270 to 275 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 275 to 280 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 280 to 285 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 285 to 290 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 290 to 295 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 295 to 300 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 300 to 305 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 305 to 310 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 310 to 315 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 315 to 320 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 320 to 325 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 325 to 330 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 330 to 335 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 35 to 340 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 340 to 345 kDa. In an embodiment, a composition of the present disclosure includes pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from 345 to 350 kDa.

In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 5 kDa to 144 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 6 kDa to 17 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 17 kDa to 39 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 39 kDa to 80 kDa.

In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight of about 1 kDa to about 350 kDa, or about 1 kDa to about 300 kDa, or about 1 kDa to about 250 kDa, or about 1 kDa to about 200 kDa, or about 1 kDa to about 150 kDa, or about 1 kDa to about 100 kDa, or about 1 kDa to about 50 kDa, or about 1 kDa to about 25 kDa.

In an embodiment, a composition of the present disclosure includes silk protein fragments having a weight average molecular weight ranging from 5 kDa to 144 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having a weight average molecular weight ranging from 6 kDa to 17 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having a weight average molecular weight ranging from 17 kDa to 39 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having a weight average molecular weight ranging from 39 kDa to 80 kDa.

In an embodiment, a composition of the present disclosure includes silk protein fragments having a weight average molecular weight of about 1 kDa to about 350 kDa, or about 1 kDa to about 300 kDa, or about 1 kDa to about 250 kDa, or about 1 kDa to about 200 kDa, or about 1 kDa to about 150 kDa, or about 1 kDa to about 100 kDa, or about 1 kDa to about 50 kDa, or about 1 kDa to about 25 kDa.

In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 1 to 5 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 5 to 10 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 10 to 15 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 15 to 20 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 20 to 25 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 25 to 30 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 30 to 35 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 35 to 40 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 40 to 45 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 45 to 50 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 50 to 55 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 55 to 60 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 60 to 65 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 65 to 70 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 70 to 75 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 75 to 80 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 80 to 85 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 85 to 90 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 90 to 95 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 95 to 100 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 100 to 105 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 105 to 1 10 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 1 10 to 1 15 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 1 15 to 120 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 120 to 125 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 125 to 130 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 130 to 135 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 135 to 140 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 140 to 145 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 145 to 150 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 150 to 155 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 155 to 160 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 160 to 165 kDa. I In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 165 to 170 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 170 to 175 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 175 to 180 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 180 to 185 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 185 to 190 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 190 to 195 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 195 to 200 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 200 to 205 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 205 to 210 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 210 to 215 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 215 to 220 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 220 to 225 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 225 to 230 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 230 to 235 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 235 to 240 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 240 to 245 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 245 to 250 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 250 to 255 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 255 to 260 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 260 to 265 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 265 to 270 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 270 to 275 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 275 to 280 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 280 to 285 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 285 to 290 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 290 to 295 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 295 to 300 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 300 to 305 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 305 to 310 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 310 to 315 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 315 to 320 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 320 to 325 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 325 to 330 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 330 to 335 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 35 to 340 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 340 to 345 kDa. In an embodiment, a composition of the present disclosure includes silk protein fragments having an average weight average molecular weight ranging from 345 to 350 kDa.

In an embodiment, a composition of the present disclosure includes silk fibroin- based protein fragments having one or more of low molecular weight, medium molecular weight, and high molecular weight. In an embodiment, a composition of the present disclosure includes silk fibroin-based protein fragments having low molecular weight and silk fibroin-based protein fragments having medium molecular weight. In an embodiment, a composition of the present disclosure includes silk fibroin-based protein fragments having low molecular weight and silk fibroin-based protein fragments having high molecular weight. In an embodiment, a composition of the present disclosure includes silk fibroin-based protein fragments having medium molecular weight and silk fibroin-based protein fragments having high molecular weight. In an embodiment, a composition of the present disclosure includes silk fibroin- based protein fragments having low molecular weight, silk fibroin-based protein fragments having medium molecular weight, and silk fibroin-based protein fragments having high molecular weight.

In an embodiment, a composition of the present disclosure includes silk fibroin- based protein fragments having low molecular weight and silk fibroin-based protein fragments having medium molecular weight. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is between about 99:1 to about 1:99, between about 95:5 to about 5:95, between about 90:10 to about 10:90, between about 75:25 to about 25:75, between about 65:35 to about 35:65, or between about 55:45 to about 45:55. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin- based protein fragments is between about 99:1 to about 55:45, between about 95:5 to about 45:55, between about 90:10 to about 35:65, between about 75:25 to about 15:85, between about 65:35 to about 10:90, or between about 55:45 to about 1:99. In an embodiment, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 99:1, about 98:2, about 97:3, about 96:4, about 95:5, about 94:6, about 93:7, about 92:8, about 91:9, about 90:10, about 89:11, about 88:12, about 87:13, about 86:14, about 85:15, about 84:16, about 83:17, about 82:18, about 81:19, about 80:20, about 79:21, about 78:22, about 77:23, about 76:24, about 75:25, about 74:26, about 73:27, about 72:28, about 71:29, about 70:30, about 69:31, about 68:32, about 67:33, about 66:34, about 65:35, about 64:36, about 63:37, about 62:38, about 61:39, about 60:40, about 59:41, about 58:42, about 57:43, about 56:44, about 55:45, about 54:46, about 53:47, about 52:48, about 51:49, about 50:50, about 49:51, about 48:52, about 47:53, about 46:54, about 45:55, about 44:56, about 43:57, about 42:58, about 41:59, about 40:60, about 39:61, about 38:62, about 37:63, about 36:64, about 35:65, about 34:66, about 33:67, about 32:68, about 31:69, about 30:70, about 29:71, about 28:72, about 27:73, about 26:74, about 25:75, about 24:76, about 23:77, about 22:78, about 21:79, about 20:80, about 19:81, about 18:82, about 17:83, about 16:84, about 15:85, about 14:86, about 13:87, about 12:88, about 11:89, about 10:90, about 9:91, about 8:92, about 7:93, about 6:94, about 5:95, about 4:96, about 3:97, about 2:98, or about 1:99. In an embodiment, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 3: 1. In an embodiment, the w/w ratio between low molecular weight silk fibroin-based protein fragments and medium molecular weight silk fibroin-based protein fragments is about 1:3.

In an embodiment, a composition of the present disclosure includes silk fibroin- based protein fragments having low molecular weight and silk fibroin-based protein fragments having high molecular weight. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and high molecular weight silk fibroin-based protein fragments is between about 99: 1 to about 1:99, between about 95:5 to about 5:95, between about 90:10 to about 10:90, between about 75:25 to about 25:75, between about 65:35 to about 35:65, or between about 55:45 to about 45:55. In some embodiments, the w/w ratio between low molecular weight silk fibroin-based protein fragments and high molecular weight silk fibroin-based protein fragments is between about 99:1 to about 55:45, between about 95:5 to about 45:55, between about 90:10 to about 35:65, between about 75:25 to about 15:85, between about 65:35 to about 10:90, or between about 55:45 to about 1:99. In an embodiment, the w/w ratio between low molecular weight silk fibroin-based protein fragments and high molecular weight silk fibroin-based protein fragments is about 99: 1, about 98:2, about 97:3, about 96:4, about 95:5, about 94:6, about 93:7, about 92:8, about 91:9, about 90:10, about 89:11, about 88:12, about 87:13, about 86:14, about 85:15, about 84:16, about 83:17, about 82:18, about 81:19, about 80:20, about 79:21, about 78:22, about 77:23, about 76:24, about 75:25, about 74:26, about 73:27, about 72:28, about 71:29, about 70:30, about 69:31, about 68:32, about 67:33, about 66:34, about 65:35, about 64:36, about 63:37, about 62:38, about 61:39, about 60:40, about 59:41, about 58:42, about 57:43, about 56:44, about 55:45, about 54:46, about 53:47, about 52:48, about 51:49, about 50:50, about 49:51, about 48:52, about 47:53, about 46:54, about 45:55, about 44:56, about 43:57, about 42:58, about 41:59, about 40:60, about 39:61, about 38:62, about 37:63, about 36:64, about 35:65, about 34:66, about 33:67, about 32:68, about 31:69, about 30:70, about 29:71, about 28:72, about 27:73, about 26:74, about 25:75, about 24:76, about 23:77, about 22:78, about 21:79, about 20:80, about 19:81, about 18:82, about 17:83, about 16:84, about 15:85, about 14:86, about 13:87, about 12:88, about 11:89, about 10:90, about 9:91, about 8:92, about 7:93, about 6:94, about 5:95, about 4:96, about 3:97, about 2:98, or about 1:99.

In an embodiment, a composition of the present disclosure includes silk fibroin- based protein fragments having medium molecular weight and silk fibroin-based protein fragments having high molecular weight. In some embodiments, the w/w ratio between medium molecular weight silk fibroin-based protein fragments and high molecular weight silk fibroin-based protein fragments is between about 99:1 to about 1:99, between about 95:5 to about 5:95, between about 90:10 to about 10:90, between about 75:25 to about 25:75, between about 65:35 to about 35:65, or between about 55:45 to about 45:55. In some embodiments, the w/w ratio between medium molecular weight silk fibroin-based protein fragments and high molecular weight silk fibroin- based protein fragments is between about 99:1 to about 55:45, between about 95:5 to about 45:55, between about 90: 10 to about 35:65, between about 75:25 to about 15:85, between about 65:35 to about 10:90, or between about 55:45 to about 1:99. In an embodiment, the w/w ratio between medium molecular weight silk fibroin-based protein fragments and high molecular weight silk fibroin-based protein fragments is about 99: 1, about 98:2, about 97:3, about 96:4, about 95:5, about 94:6, about 93:7, about 92:8, about 91:9, about 90:10, about 89:11, about 88:12, about 87:13, about 86:14, about 85:15, about 84:16, about 83:17, about 82:18, about 81:19, about 80:20, about 79:21, about 78:22, about 77:23, about 76:24, about 75:25, about 74:26, about 73:27, about 72:28, about 71:29, about 70:30, about 69:31, about 68:32, about 67:33, about 66:34, about 65:35, about 64:36, about 63:37, about 62:38, about 61:39, about 60:40, about 59:41, about 58:42, about 57:43, about 56:44, about 55:45, about 54:46, about 53:47, about 52:48, about 51:49, about 50:50, about 49:51, about 48:52, about 47:53, about 46:54, about 45:55, about 44:56, about 43:57, about 42:58, about 41:59, about 40:60, about 39:61, about 38:62, about 37:63, about 36:64, about 35:65, about 34:66, about 33:67, about 32:68, about 31:69, about 30:70, about 29:71, about 28:72, about 27:73, about 26:74, about 25:75, about 24:76, about 23:77, about 22:78, about 21:79, about 20:80, about 19:81, about 18:82, about 17:83, about 16:84, about 15:85, about 14:86, about 13:87, about 12:88, about 11:89, about 10:90, about 9:91, about 8:92, about 7:93, about 6:94, about 5:95, about 4:96, about 3:97, about 2:98, or about 1:99.

In an embodiment, a composition of the present disclosure includes silk fibroin- based protein fragments having low molecular weight, silk fibroin-based protein fragments having medium molecular weight, and silk fibroin-based protein fragments having high molecular weight. In an embodiment, the w/w ratio between low molecular weight silk fibroin-based protein fragments, medium molecular weight silk fibroin- based protein fragments, and high molecular weight silk fibroin-based protein fragments is about 1:1:8, about 1:2:7, about 1:3:6, about 1:4:5, about 1:5:4, about 1:6:3, about 1:7:2, about 1:8:1, about2:l:7, about2:2:6, about2:3:5, about2:4:4, about2:5:3, about 2:6:2, about 2:7:1, about 3:1:6, about 3:2:5, about 3:3:4, about 3:4:3, about 3:5:2, about3:6:l, about 4:1:5, about 4:2:4, about 4:3:3, about 4:4:2, about 4:5:1, about5:l:4, about 5 :2:3, about 5 :3:2, about 5 :4: l , about 6: l :3, about 6:2:2, about 6:3: l, about 7: l :2, about 7:2: 1, or about 8: 1 : 1. In an embodiment, the w/w ratio between low molecular weight silk fibroin-based protein fragments, medium molecular weight silk fibroin- based protein fragments, and high molecular weight silk fibroin-based protein fragments is about 3:0.1 :0.9, about 3 :0.2:0.8, about 3:0.3 :0.7, about 3 :0.4: 0.6, about 3: 0.5:0.5, about 3 :0.6:0.4, about 3 :0.7:0.3, about 3 :0.8:0.2, or about 3 :0.9:0.1.

In some embodiments, the silk compositions provided herein may be applied as mixtures to an article to be coated or in stepwise processes to form coating layers on the article. For example, a silk composition that includes low molecular weight silk and medium molecular weight silk may be applied to an article to be coated. Alternatively, a low molecular weight silk composition may be applied to an article to be coated, as provided by the processes described herein, and then a medium or high molecular weight silk may then be applied to the article. The low, medium, and high molecular weight silk compositions may be added in any order or any combination (e.g., low/med, low/high, med/high, low/med/high).

In some embodiments, where multiple layers of silk compositions are applied to an article to be coated, they may have at least one layer, or 1 layer to 1 million layers, or 1 layer to 100,000 layers, or 1 layer to 10,000 layers, or 1 layer to 1,000 layers of such silk compositions, wherein the layers may have the same or different thicknesses. For example, in some embodiments, the layers may have a thickness of from about 1 nm to about 1 mm, or about 1 nm to about 1 μιτι, or about 1 nm to about 500 nm, or about 1 nm to about 400 nm, or about 1 nm to about 300 nm, or about 1 nm to about 200 nm, or about 1 nm to about 100 nm, or about 1 nm to about 75 nm, or about 1 nm to about 50 nm, or about 1 nm to about 25 nm, or about 1 nm to about 20 nm, or about 1 nm to about 15 nm, or about 1 nm to about 10 nm, or about 1 nm to about 5 nm.

In an embodiment, a composition of the present disclosure having pure silk fibroin-based protein fragments has a polydispersity ranging from about 1 to about 5.0. In an embodiment, a composition of the present disclosure having pure silk fibroin- based protein fragments has a polydispersity ranging from about 1.5 to about 3.0. In an embodiment, a composition of the present disclosure having pure silk fibroin-based protein fragments has a polydispersity ranging from about 1 to about 1.5. In an embodiment, a composition of the present disclosure having pure silk fibroin-based protein fragments has a polydispersity ranging from about 1.5 to about 2.0. In an embodiment, a composition of the present disclosure having pure silk fibroin-based protein fragments has a polydispersity ranging from about 2.0 to about 2.5. In an embodiment, a composition of the present disclosure having pure silk fibroin-based protein fragments, has a polydispersity ranging from about 2.0 to about 3.0. In an embodiment, a composition of the present disclosure having pure silk fibroin-based protein fragments, has a polydispersity ranging from about 2.5 to about 3.0.

In an embodiment, a composition of the present disclosure having silk protein fragments has a polydispersity ranging from about 1 to about 5.0. In an embodiment, a composition of the present disclosure having silk protein fragments has a polydispersity ranging from about 1.5 to about 3.0. In an embodiment, a composition of the present disclosure having silk protein fragments has a polydispersity ranging from about 1 to about 1.5. In an embodiment, a composition of the present disclosure having silk protein fragments has a polydispersity ranging from about 1.5 to about 2.0. In an embodiment, a composition of the present disclosure having silk protein fragments has a polydispersity ranging from about 2.0 to about 2.5. In an embodiment, a composition of the present disclosure having silk protein fragments, has a polydispersity ranging from about is 2.0 to about 3.0. In an embodiment, a composition of the present disclosure having silk protein fragments, has a polydispersity ranging from about is 2.5 to about 3.0.

In some embodiments the polydispersity of low molecular weight silk protein fragments may be about 1 to about 5.0, or about 1.5 to about 3.0, or about 1 to about 1.5, or about 1.5 to about 2.0, or about 2.0 to about 2.5, or about 2.5 to about 3.0.

In some embodiments the polydispersity of medium molecular weight silk protein fragments may be about 1 to about 5.0, or about 1.5 to about 3.0, or about 1 to about 1.5, or about 1.5 to about 2.0, or about 2.0 to about 2.5, or about 2.5 to about 3.0.

In some embodiments the polydispersity of high molecular weight silk protein fragments may be about 1 to about 5.0, or about 1.5 to about 3.0, or about 1 to about 1.5, or about 1.5 to about 2.0, or about 2.0 to about 2.5, or about 2.5 to about 3.0.

In some embodiments, in compositions described herein having combinations of low, medium, and/or high molecular weight silk protein fragments, such low, medium, and/or high molecular weight silk proteins may have the same or different polydispersities. In an embodiment, a composition of the present disclosure having pure silk fibroin-based protein fragments has non-detectable levels of LiBr residuals. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is between 10 ppm and 1000 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is between 10 ppm and 300 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is less than 25 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is less than 50 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is less than 75 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is less than 100 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is less than 200 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is less than 300 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is less than 400 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is less than 500 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is less than 600 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is less than 700 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is less than 800 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is less than 900 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is less than 1000 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is non-detectable to 500 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is non-detectable to 450 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is non-detectable to 400 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is non-detectable to 350 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is non-detectable to 300 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is non-detectable to 250 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is non- detectable to 200 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is non-detectable to 150 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is non- detectable to 100 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is 100 ppm to 200 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is 200 ppm to 300 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is 300 ppm to 400 ppm. In an embodiment, the amount of the LiBr residuals in a composition of the present disclosure is 400 ppm to 500 ppm.

In an embodiment, a composition of the present disclosure having pure silk fibroin-based protein fragments, has non-detectable levels of Na2C03 residuals. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is less than 100 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is less than 200 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is less than 300 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is less than 400 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is less than 500 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is less than 600 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is less than 700 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is less than 800 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is less than 900 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is less than 1000 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is non-detectable to 500 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is non-detectable to 450 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is non-detectable to 400 ppm. In an embodiment, the amount of the Na2CCb residuals in a composition of the present disclosure is non-detectable to 350 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is non-detectable to 300 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is non-detectable to 250 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is non-detectable to 200 ppm. In an embodiment, the amount of the Na2CCb residuals in a composition of the present disclosure is non-detectable to 150 ppm. In an embodiment, the amount of the Na2CCb residuals in a composition of the present disclosure is non-detectable to 100 ppm. In an embodiment, the amount of the Na2CCb residuals in a composition of the present disclosure is 100 ppm to 200 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is 200 ppm to 300 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is 300 ppm to 400 ppm. In an embodiment, the amount of the Na2C03 residuals in a composition of the present disclosure is 400 ppm to 500 ppm.

In an embodiment, the water solubility of pure silk fibroin-based protein fragments of the present disclosure is 50 to 100%. In an embodiment, the water solubility of pure silk fibroin-based protein fragments of the present disclosure is 60 to 100%. In an embodiment, the water solubility of pure silk fibroin-based protein fragments of the present disclosure is 70 to 100%. In an embodiment, the water solubility of pure silk fibroin-based protein fragments of the present disclosure is 80 to 100%. In an embodiment, the water solubility is 90 to 100%. In an embodiment, the silk fibroin-based fragments of the present disclosure are non-soluble in aqueous solutions.

In an embodiment, the solubility of pure silk fibroin-based protein fragments of the present disclosure in organic solutions is 50 to 100%. In an embodiment, the solubility of pure silk fibroin-based protein fragments of the present disclosure in organic solutions is 60 to 100%. In an embodiment, the solubility of pure silk fibroin- based protein fragments of the present disclosure in organic solutions is 70 to 100%. In an embodiment, the solubility of pure silk fibroin-based protein fragments of the present disclosure in organic solutions is 80 to 100%. In an embodiment, the solubility of pure silk fibroin-based protein fragments of the present disclosure in organic solutions is 90 to 100%. In an embodiment, the silk fibroin-based fragments of the present disclosure are non-soluble in organic solutions.

In an embodiment, the extraction temperature during a method of preparing a composition of the present disclosure is greater than 84 °C. In an embodiment, the extraction temperature during a method of preparing a composition of the present disclosure is less than 100 °C. In an embodiment, the extraction temperature during a method of preparing a composition of the present disclosure is 84 °C to 100 °C. In an embodiment, the extraction temperature during a method of preparing a composition of the present disclosure is 84 °C to 94 °C. In an embodiment, the extraction temperature during a method of preparing a composition of the present disclosure is 94 °C to 100 °C.

Compositions and Processes Including Silk Fibroin-Based Coatings

In an embodiment, the invention may include textiles, such as fibers, yarns, fabrics, or other materials and combinations thereof, that may be coated with an SPF mixture solution (i.e., silk fibroin solution (SFS)) as described herein to produce a coated article. In an embodiment, the coated articles described herein may be treated with additional chemical agents that may enhance the properties of the coated article. In an embodiment, the SFS may include one or more chemical agents that may enhance the properties of the coated article.

In an embodiment, textiles may be flexible materials (woven or non-woven) that include a network of natural and/or man-made fibers, thread, yarn, or a combination thereof. SFS may be applied at any stage of textile processing from individual fibers, to yarn, to fabric, to thread, or a combination thereof.

In an embodiment, fibers may be natural fibers that may include a natural fiber cellulose base, wherein the natural fiber cellulose base may include one or more of: (1) a baste such as flax, hemp, kenaf, jute, linen, and/or ramie; (2) a leaf such as flax, hemp, sisal, abaca, banana, henequen, ramie, sunn, and/or coir; and (3) seed hair such as cotton and/or kapok. In an embodiment, fibers may be natural fibers that may include a natural fiber protein base, wherein the natural fiber protein base may include one or more of: (1) hair such as alpaca, camel, cashmere, llama, mohair, and/or vicuna; (2) wool such as sheep; (3) filament such as silk. In an embodiment, fibers may be natural fibers that may include a natural fiber mineral base, including asbestos. In an embodiment, fibers may be man-made fibers that may include a man-made fiber organic natural polymer base, which may include one or more of: (1) a cellulose base such as bamboo, rayon, lyocell, acetate, and/or triacetate; (2) a protein base such as azlon; (3) an alginate; and (4) rubber. In an embodiment, fibers may be man-made fibers that may include a man- made fiber organic synthetic base, which may include one or more of acrylic, anidex, aramid, fluorocarbon, modacrylic, novoloid, nylon, nytril, olefin, PBI, polycarbonate, polyester, rubber, saran, spandex, vinal vinvon. In an embodiment, fibers may be man- made fibers that may include a man-made fiber inorganic base, which may include one or more of a glass material, metallic material, and carbon material.

In an embodiment, yarn may include natural fibers that may include a natural fiber cellulose base, wherein the natural fiber cellulose base may be from: (1) a baste such as flax, hemp, kenaf, jute, linen, and/or ramie; (2) a leaf such as flax, hemp, sisal, abaca, banana, henequen, ramie, sunn, and/or coir; or (3) seed hair such as cotton and/or kapok. In an embodiment, yam may include natural fibers that may include a natural fiber protein base, wherein the natural fiber protein base may be from: (1) hair such as alpaca, camel, cashmere, llama, mohair, and/or vicuna; (2) wool such as sheep; or (3) filament such as silk. In an embodiment, yarn may include natural fibers that may include a natural fiber mineral base, including asbestos.

In an embodiment, yarn may include man-made fibers that may include a man- made fiber organic natural polymer base, which may include: (1) a cellulose base such as bamboo, rayon, lyocell, acetate, and/or triacetate; (2) a protein base such as azlon; (3) an alginate; or (4) rubber. In an embodiment, yam may include man-made fibers that may include a man-made fiber organic synthetic base, which may include acrylic, anidex, aramid, fluorocarbon, modacrylic, novoloid, nylon, nytril, olefin, PBI, polycarbonate, polyester, rubber, saran, spandex, vinal and/or vinvon. In an embodiment, yarn may include man-made fibers that may include a man-made fiber inorganic base, which may include a glass material, metallic material, carbon material, and/or specialty material.

In an embodiment, fabric may include natural fibers and/or yarn that may include a natural fiber protein base, wherein the natural fiber protein base may be from: (1) hair such as alpaca, camel, cashmere, llama, mohair, and/or vicuna; (2) wool such as sheep; or (3) filament such as silk. In an embodiment, fabric may include natural fibers and/or yarn that may include a natural fiber mineral base, including asbestos.

In an embodiment, fabric may include man-made fibers and/or yarn that may include a man-made fiber organic natural polymer base, which may include: (1) a cellulose base such as bamboo, rayon, lyocell, acetate, and/or triacetate; (2) a protein base such as azlon; (3) an alginate; or (4) rubber. In an embodiment, fabric may include man-made fibers and/or yarn that may include a man-made fiber organic synthetic base, which may include acrylic, anidex, aramid, fluorocarbon, modacrylic, novoloid, nylon, nytril, olefin, PBI, polycarbonate, polyester, rubber, saran, spandex, vinal and/or vinvon. In an embodiment, fabric may include man-made fibers and/or yarn that may include a man-made fiber inorganic base, which may include a glass material, metallic material, carbon material, and/or specialty material.

In an embodiment, textiles may be manufactured via one or more of the following processes weaving processes, knitting processes, and non-woven processes. In an embodiment, weaving processes may include plain weaving, twill weaving, and/or satin weaving. In an embodiment, knitting processes may include weft knitting (e.g., circular, flat bed, and/or full fashioned) and/or warp knitting (e.g., tricot, Raschel, and/or crochet). In an embodiment, non-woven processes may include stable fiber (e.g., dry laid and/or wet laid) and/or continuous filament (e.g., spun laid and/or melt blown).

In some embodiments, SFS may be applied to fibers and/or yarn having a diameter of less than about 100 nm, or less than about 200 nm, or less than about 300 nm, or less than about 400 nm, or less than about 500 nm, or less than about 600 nm, or less than about 700 nm, or less than about 800 nm, or less than about 900 nm, or less than about 1000 nm, or less than about 2 μιτι, or less than about 5 μιτι, or less than about 10 μπι, or less than about 20 μιτι, or less than about 30 μιτι, or less than about 40 μιτι, or less than about 50 μιτι, or less than about 60 μιτι, or less than about 70 μιτι, or less than about 80 μιτι, or less than about 90 μιτι, or less than about 100 μιτι, or less than about 200 μπι, or less than about 300 μιτι, or less than about 400 μιτι, or less than about 500 μιτι, or less than about 600 μιτι, or less than about 700 μιτι, or less than about 800 μιτι, or less than about 900 μιτι, or less than about 1000 μιτι, or less than about 2 mm, or less than about 3 mm, or less than about 4 mm, or less than about 5 mm, 6 mm, or less than about 7 mm, or less than about 8 mm, or less than about 9 mm, or less than about 10 mm, or less than about 20 mm, or less than about 30 mm, or less than about 40 mm, or less than about 50 mm, or less than about 60 mm, or less than about 70 mm, or less than about 80 mm, or less than about 90 mm, or less than about 100 mm, or less than about 200 mm, or less than about 300 mm, or less than about 400 mm, or less than about 500 mm, or less than about 600 mm, or less than about 700 mm, or less than about 800 mm, or less than about 900 mm, or less than about 1000 mm.

In some embodiments, SFS may be applied to fibers and/or yarn having a diameter of greater than about 100 nm, or greater than about 200 nm, or greater than about 300 nm, or greater than about 400 nm, or greater than about 500 nm, or greater than about 600 nm, or greater than about 700 nm, or greater than about 800 nm, or greater than about 900 nm, or greater than about 1000 nm, or greater than about 2 μιτι, or greater than about 5 μιτι, or greater than about 10 μιτι, or greater than about 20 μιτι, or greater than about 30 μιτι, or greater than about 40 μιτι, or greater than about 50 μιτι, or greater than about 60 μιτι, or greater than about 70 μιτι, or greater than about 80 μιτι, or greater than about 90 μιτι, or greater than about 100 μηι, or greater than about 200 μπι, or greater than about 300 μιτι, or greater than about 400 μιτι, or greater than about 500 μπι, or greater than about 600 μιτι, or greater than about 700 μιτι, or greater than about 800 μιτι, or greater than about 900 μιτι, or greater than about 1000 μιτι, or greater than about 2 mm, or greater than about 3 mm, or greater than about 4 mm, or greater than about 5 mm, 6 mm, or greater than about 7 mm, or greater than about 8 mm, or greater than about 9 mm, or greater than about 10 mm, or greater than about 20 mm, or greater than about 30 mm, or greater than about 40 mm, or greater than about 50 mm, or greater than about 60 mm, or greater than about 70 mm, or greater than about 80 mm, or greater than about 90 mm, or greater than about 100 mm, or greater than about 200 mm, or greater than about 300 mm, or greater than about 400 mm, or greater than about 500 mm, or greater than about 600 mm, or greater than about 700 mm, or greater than about 800 mm, or greater than about 900 mm, or greater than about 1000 mm.

In some embodiments, SFS may be applied to fibers and/or yarn having a length of less than about 100 nm, or less than about 200 nm, or less than about 300 nm, or less than about 400 nm, or less than about 500 nm, or less than about 600 nm, or less than about 700 nm, or less than about 800 nm, or less than about 900 nm, or less than about 1000 nm, or less than about 2 μιτι, or less than about 5 μιτι, or less than about 10 μιτι, or less than about 20 μιτι, or less than about 30 μιτι, or less than about 40 μιτι, or less than about 50 μιτι, or less than about 60 μιτι, or less than about 70 μιτι, or less than about 80 μπι, or less than about 90 μιτι, or less than about 100 μιτι, or less than about 200 μιτι, or less than about 300 μιτι, or less than about 400 μιτι, or less than about 500 μιτι, or less than about 600 μιτι, or less than about 700 μιτι, or less than about 800 μιτι, or less than about 900 μιτι, or less than about 1000 μιτι, or less than about 2 mm, or less than about 3 mm, or less than about 4 mm, or less than about 5 mm, 6 mm, or less than about 7 mm, or less than about 8 mm, or less than about 9 mm, or less than about 10 mm, or less than about 20 mm, or less than about 30 mm, or less than about 40 mm, or less than about 50 mm, or less than about 60 mm, or less than about 70 mm, or less than about 80 mm, or less than about 90 mm, or less than about 100 mm, or less than about 200 mm, or less than about 300 mm, or less than about 400 mm, or less than about 500 mm, or less than about 600 mm, or less than about 700 mm, or less than about 800 mm, or less than about 900 mm, or less than about 1000 mm.

In some embodiments, SFS may be applied to fibers and/or yarn having a length of greater than about 100 nm, or greater than about 200 nm, or greater than about 300 nm, or greater than about 400 nm, or greater than about 500 nm, or greater than about 600 nm, or greater than about 700 nm, or greater than about 800 nm, or greater than about 900 nm, or greater than about 1000 nm, or greater than about 2 μιτι, or greater than about 5 μιτι, or greater than about 10 μιτι, or greater than about 20 μιτι, or greater than about 30 μιτι, or greater than about 40 μιτι, or greater than about 50 μιτι, or greater than about 60 μιτι, or greater than about 70 μιτι, or greater than about 80 μιτι, or greater than about 90 μιτι, or greater than about 100 μιτι, or greater than about 200 μιτι, or greater than about 300 μιτι, or greater than about 400 μιτι, or greater than about 500 μιτι, or greater than about 600 μιτι, or greater than about 700 μιτι, or greater than about 800 μιη, or greater than about 900 μιτι, or greater than about 1000 μιτι, or greater than about 2 mm, or greater than about 3 mm, or greater than about 4 mm, or greater than about 5 mm, 6 mm, or greater than about 7 mm, or greater than about 8 mm, or greater than about 9 mm, or greater than about 10 mm, or greater than about 20 mm, or greater than about 30 mm, or greater than about 40 mm, or greater than about 50 mm, or greater than about 60 mm, or greater than about 70 mm, or greater than about 80 mm, or greater than about 90 mm, or greater than about 100 mm, or greater than about 200 mm, or greater than about 300 mm, or greater than about 400 mm, or greater than about 500 mm, or greater than about 600 mm, or greater than about 700 mm, or greater than about 800 mm, or greater than about 900 mm, or greater than about 1000 mm.

In some embodiments, SFS may be applied to fibers and/or yarn having a weight (g/m 2 ) of less than about 1 g/m 2 , or less than about 2 g/m 2 , or less than about 3 g/m 2 , or less than about 4 g/m 2 , or less than about 5 g/m 2 , or less than about 6 g/m 2 , or less than about 7 g/m 2 , or less than about 8 g/m 2 , or less than about 9 g/m 2 , or less than about 10 g/m 2 , or less than about 20 g/m 2 , or less than about 30 g/m 2 , or less than about 40 g/m 2 , or less than about 50 g/m 2 , or less than about 60 g/m 2 , or less than about 70 g/m 2 , or less than about 80 g/m 2 , or less than about 90 g/m 2 , or less than about 100 g/m 2 , or less than about 200 g/m 2 , or less than about 300 g/m 2 , or less than about 400 g/m 2 , or less than about 500 g/m 2 .

In some embodiments, SFS may be applied to fibers and/or yarn having a weight (g/m 2 ) of at greater than about 1 g/m 2 , or greater than about 2 g/m 2 , or greater than about 3 g/m 2 , or greater than about 4 g/m 2 , or greater than about 5 g/m 2 , or greater than about 6 g/m 2 , or greater than about 7 g/m 2 , or greater than about 8 g/m 2 , or greater than about 9 g/m 2 , or greater than about 10 g/m 2 , or greater than about 20 g/m 2 , or greater than about 30 g/m 2 , or greater than about 40 g/m 2 , or greater than about 50 g/m 2 , or greater than about 60 g/m 2 , or greater than about 70 g/m 2 , or greater than about 80 g/m 2 , or greater than about 90 g/m 2 , or greater than about 100 g/m 2 , or greater than about 200 g/m 2 , or greater than about 300 g/m 2 , or greater than about 400 g/m 2 , or greater than about 500 g/m 2 .

In some embodiments, SFS may be applied to fabric having a thickness of less than about 100 nm, or less than about 200 nm, or less than about 300 nm, or less than about 400 nm, or less than about 500 nm, or less than about 600 nm, or less than about 700 nm, or less than about 800 nm, or less than about 900 nm, or less than about 1000 nm, or less than about 2 μιτι, or less than about 5 μιτι, or less than about 10 μιτι, or less than about 20 μιτι, or less than about 30 μιτι, or less than about 40 μιτι, or less than about 50 μπι, or less than about 60 μιτι, or less than about 70 μιτι, or less than about 80 μιτι, or less than about 90 μιτι, or less than about 100 μιτι, or less than about 200 μιτι, or less than about 300 μιτι, or less than about 400 μιτι, or less than about 500 μιτι, or less than about 600 μηι, or less than about 700 μιτι, or less than about 800 μιτι, or less than about 900 μηι, or less than about 1000 μιτι, or less than about 2 mm, or less than about 3 mm, or less than about 4 mm, or less than about 5 mm, 6 mm, or less than about 7 mm, or less than about 8 mm, or less than about 9 mm, or less than about 10 mm.

In some embodiments, SFS may be applied to fabric having a thickness of greater than about 100 nm, or greater than about 200 nm, or greater than about 300 nm, or greater than about 400 nm, or greater than about 500 nm, or greater than about 600 nm, or greater than about 700 nm, or greater than about 800 nm, or greater than about 900 nm, or greater than about 1000 nm, or greater than about 2 μιτι, or greater than about 5 μηι, or greater than about 10 μιτι, or greater than about 20 μιτι, or greater than about 30 μπι, or greater than about 40 μιτι, or greater than about 50 μιτι, or greater than about 60 μπι, or greater than about 70 μιτι, or greater than about 80 μιτι, or greater than about 90 μηι, or greater than about 100 μηι, or greater than about 200 μηι, or greater than about 300 μηι, or greater than about 400 μηι, or greater than about 500 μηι, or greater than about 600 μηι, or greater than about 700 μηι, or greater than about 800 μηι, or greater than about 900 μηι, or greater than about 1000 μηι, or greater than about 2 mm, or greater than about 3 mm, or greater than about 4 mm, or greater than about 5 mm, 6 mm, or greater than about 7 mm, or greater than about 8 mm, or greater than about 9 mm, or greater than about 10 mm.

In some embodiments, SFS may be applied to fabric having a width of less than about 100 nm, or less than about 200 nm, or less than about 300 nm, or less than about 400 nm, or less than about 500 nm, or less than about 600 nm, or less than about 700 nm, or less than about 800 nm, or less than about 900 nm, or less than about 1000 nm, or less than about 2 μιτι, or less than about 5 μιτι, or less than about 10 μιτι, or less than about 20 μηι, or less than about 30 μιτι, or less than about 40 μιτι, or less than about 50 μπι, or less than about 60 μιτι, or less than about 70 μιτι, or less than about 80 μιτι, or less than about 90 μιτι, or less than about 100 μιτι, or less than about 200 μιτι, or less than about 300 μιτι, or less than about 400 μιτι, or less than about 500 μιτι, or less than about 600 μηι, or less than about 700 μιτι, or less than about 800 μιτι, or less than about 900 μηι, or less than about 1000 μιτι, or less than about 2 mm, or less than about 3 mm, or less than about 4 mm, or less than about 5 mm, 6 mm, or less than about 7 mm, or less than about 8 mm, or less than about 9 mm, or less than about 10 mm, or less than about 20 mm, or less than about 30 mm, or less than about 40 mm, or less than about 50 mm, or less than about 60 mm, or less than about 70 mm, or less than about 80 mm, or less than about 90 mm, or less than about 100 mm, or less than about 200 mm, or less than about 300 mm, or less than about 400 mm, or less than about 500 mm, or less than about 600 mm, or less than about 700 mm, or less than about 800 mm, or less than about 900 mm, or less than about 1000 mm, or less than about 2 m, or less than about 3 m, or less than about 4 m, or less than about 5 m.

In some embodiments, SFS may be applied to fabric having a width of greater than about 100 nm, or greater than about 200 nm, or greater than about 300 nm, or greater than about 400 nm, or greater than about 500 nm, or greater than about 600 nm, or greater than about 700 nm, or greater than about 800 nm, or greater than about 900 nm, or greater than about 1000 nm, or greater than about 2 μιτι, or greater than about 5 μιη, or greater than about 10 μιτι, or greater than about 20 μιτι, or greater than about 30 μηι, or greater than about 40 μηι, or greater than about 50 μηι, or greater than about 60 μηι, or greater than about 70 μηι, or greater than about 80 μηι, or greater than about 90 μηι, or greater than about 100 μηι, or greater than about 200 μηι, or greater than about 300 μηι, or greater than about 400 μηι, or greater than about 500 μηι, or greater than about 600 μηι, or greater than about 700 μηι, or greater than about 800 μηι, or greater than about 900 μηι, or greater than about 1000 μηι, or greater than about 2 mm, or greater than about 3 mm, or greater than about 4 mm, or greater than about 5 mm, 6 mm, or greater than about 7 mm, or greater than about 8 mm, or greater than about 9 mm, or greater than about 10 mm, or greater than about 20 mm, or greater than about 30 mm, or greater than about 40 mm, or greater than about 50 mm, or greater than about 60 mm, or greater than about 70 mm, or greater than about 80 mm, or greater than about 90 mm, or greater than about 100 mm, or greater than about 200 mm, or greater than about 300 mm, or greater than about 400 mm, or greater than about 500 mm, or greater than about 600 mm, or greater than about 700 mm, or greater than about 800 mm, or greater than about 900 mm, or greater than about 1000 mm, or greater than about 2 m, or greater than about 3 m, or greater than about 4 m, or greater than about 5 m.

In some embodiments, SFS may be applied to fabric having a length of less than about 100 nm, or less than about 200 nm, or less than about 300 nm, or less than about 400 nm, or less than about 500 nm, or less than about 600 nm, or less than about 700 nm, or less than about 800 nm, or less than about 900 nm, or less than about 1000 nm, or less than about 2 μιτι, or less than about 5 μιτι, or less than about 10 μιτι, or less than about 20 μηι, or less than about 30 μιτι, or less than about 40 μιτι, or less than about 50 μηι, or less than about 60 μιτι, or less than about 70 μιτι, or less than about 80 μιτι, or less than about 90 μιτι, or less than about 100 μιτι, or less than about 200 μιτι, or less than about 300 μιτι, or less than about 400 μιτι, or less than about 500 μιτι, or less than about 600 μηι, or less than about 700 μιτι, or less than about 800 μιτι, or less than about 900 μηι, or less than about 1000 μιτι, or less than about 2 mm, or less than about 3 mm, or less than about 4 mm, or less than about 5 mm, 6 mm, or less than about 7 mm, or less than about 8 mm, or less than about 9 mm, or less than about 10 mm, or less than about 20 mm, or less than about 30 mm, or less than about 40 mm, or less than about 50 mm, or less than about 60 mm, or less than about 70 mm, or less than about 80 mm, or less than about 90 mm, or less than about 100 mm, or less than about 200 mm, or less than about 300 mm, or less than about 400 mm, or less than about 500 mm, or less than about 600 mm, or less than about 700 mm, or less than about 800 mm, or less than about 900 mm, or less than about 1000 mm.

In some embodiments, SFS may be applied to fabric having a length of greater than about 100 nm, or greater than about 200 nm, or greater than about 300 nm, or greater than about 400 nm, or greater than about 500 nm, or greater than about 600 nm, or greater than about 700 nm, or greater than about 800 nm, or greater than about 900 nm, or greater than about 1000 nm, or greater than about 2 μιτι, or greater than about 5 μπι, or greater than about 10 μιτι, or greater than about 20 μιτι, or greater than about 30 μπι, or greater than about 40 μιτι, or greater than about 50 μιτι, or greater than about 60 μπι, or greater than about 70 μιτι, or greater than about 80 μιτι, or greater than about 90 μπι, or greater than about 100 μιτι, or greater than about 200 μιτι, or greater than about 300 μπι, or greater than about 400 μιτι, or greater than about 500 μιτι, or greater than about 600 μηι, or greater than about 700 μιτι, or greater than about 800 μιτι, or greater than about 900 μιτι, or greater than about 1000 μιτι, or greater than about 2 mm, or greater than about 3 mm, or greater than about 4 mm, or greater than about 5 mm, 6 mm, or greater than about 7 mm, or greater than about 8 mm, or greater than about 9 mm, or greater than about 10 mm, or greater than about 20 mm, or greater than about 30 mm, or greater than about 40 mm, or greater than about 50 mm, or greater than about 60 mm, or greater than about 70 mm, or greater than about 80 mm, or greater than about 90 mm, or greater than about 100 mm, or greater than about 200 mm, or greater than about 300 mm, or greater than about 400 mm, or greater than about 500 mm, or greater than about 600 mm, or greater than about 700 mm, or greater than about 800 mm, or greater than about 900 mm, or greater than about 1000 mm.

In some embodiments, SFS may be applied to fabric having a stretch percentage of less than about 1%, or less than about 2%, or less than about 3%, or less than about 4%, or less than about 5%, or less than about 6%, or less than about 7%, or less than about 8%, or less than about 9%, or less than about 10%, or less than about 20%, or less than about 30%, or less than about 40%, or less than about 50%, or less than about 60%, or less than about 70% , or less than about 80%, or less than about 90%, or less than about 100, or less than about 110%, or less than about 120%, or less than about 130%, or less than about 140%, or less than about 150%, or less than about 160%, or less than about 170%, or less than about 180%, or less than about 190%, or less than about 200%. Stretch percentage may be determined for a fabric having an unstretched width and stretching the fabric to a stretched width, then subtracting the unstretched width from the stretched width to yield the net stretched width, then dividing the net stretched width and multiplying the quotient by 100 to find the stretch percentage (%):

(Stretched Width— Unstretched Width)

Stretch Percentage = ;— 1 Ji r , , * 100

Unstretched Width

In some embodiments, SFS may be applied to fabric having a stretch percentage of greater than about 1%, or greater than about 2%, or greater than about 3%, or greater than about 4%, or greater than about 5%, or greater than about 6%, or greater than about 7%, or greater than about 8%, or greater than about 9%, or greater than about 10%, or greater than about 20%, or greater than about 30%, or greater than about 40%, or greater than about 50%, or greater than about 60%, or greater than about 70% , or greater than about 80%, or greater than about 90%, or greater than about 100, or greater than about 110%, or greater than about 120%, or greater than about 130%, or greater than about 140%, or greater than about 150%, or greater than about 160%, or greater than about 170%, or greater than about 180%, or greater than about 190%, or greater than about 200%

In some embodiments, SFS may be applied to fabric having a tensile energy (N/cm 2 ) of less than about 1 cN/cm 2 , or less than about 2 cN/cm 2 , or less than about 3 cN/cm 2 , or less than about 4 cN/cm 2 , or less than about 5 cN/cm 2 , or less than about 5 cN/cm 2 , or less than about 6 cN/cm 2 , or less than about 7 cN/cm 2 , or less than about 8 cN/cm 2 , or less than about 9 cN/cm 2 , or less than about 10 cN/cm 2 , or less than about 20 cN/cm 2 , or less than about 30 cN/cm 2 , or less than about 40 cN/cm 2 , or less than about 50 cN/cm 2 , or less than about 60 cN/cm 2 , or less than about 70 cN/cm 2 , or less than about 80 cN/cm 2 , or less than about 90 cN/cm 2 , or less than about 100 cN/cm 2 , or less than about 2 N/cm 2 , or less than about 3 N/cm 2 , or less than about 4 N/cm 2 , or less than about 5 N/cm 2 , or less than about 6 N/cm 2 , or less than about 7 N/cm 2 , or less than about 8 N/cm 2 , or less than about 9 N/cm 2 , or less than about 10 N/cm 2 , or less than about 20 N/cm 2 , or less than about 30 N/cm 2 , or less than about 40 N/cm 2 , or less than about 50 N/cm 2 , or less than about 60 N/cm 2 , or less than about 70 N/cm 2 , or less than about 80 N/cm 2 , or less than about 90 N/cm 2 , or less than about 100 N/cm 2 , or less than about 150 N/cm 2 , or less than about 200 N/cm 2 .

In some embodiments, SFS may be applied to fabric having a tensile energy (N/cm 2 ) of greater than about 1 cN/cm 2 , or greater than about 2 cN/cm 2 , or greater than about 3 cN/cm 2 , or greater than about 4 cN/cm 2 , or greater than about 5 cN/cm 2 , or greater than about 5 cN/cm 2 , or greater than about 6 cN/cm 2 , or greater than about 7 cN/cm 2 , or greater than about 8 cN/cm 2 , or greater than about 9 cN/cm 2 , or greater than about 10 cN/cm 2 , or greater than about 20 cN/cm 2 , or greater than about 30 cN/cm 2 , or greater than about 40 cN/cm 2 , or greater than about 50 cN/cm 2 , or greater than about 60 cN/cm 2 , or greater than about 70 cN/cm 2 , or greater than about 80 cN/cm 2 , or greater than about 90 cN/cm 2 , or greater than about 100 cN/cm 2 , or greater than about 2 N/cm 2 , or greater than about 3 N/cm 2 , or greater than about 4 N/cm 2 , or greater than about 5 N/cm 2 , or greater than about 6 N/cm 2 , or greater than about 7 N/cm 2 , or greater than about 8 N/cm 2 , or greater than about 9 N/cm 2 , or greater than about 10 N/cm 2 , or greater than about 20 N/cm 2 , or greater than about 30 N/cm 2 , or greater than about 40 N/cm 2 , or greater than about 50 N/cm 2 , or greater than about 60 N/cm 2 , or greater than about 70 N/cm 2 , or greater than about 80 N/cm 2 , or greater than about 90 N/cm 2 , or greater than about 100 N/cm 2 , or greater than about 150 N/cm 2 , or greater than about 200 N/cm 2 .

In some embodiments, SFS may be applied to fabric having a shear rigidity (N/cm-degree) of less than about 1 cN/cm-degree, or less than about 2 cN/cm-degree, or less than about 3 cN/cm-degree, or less than about 4 cN/cm-degree, or less than about 5 cN/cm-degree, or less than about 5 cN/cm-degree, or less than about 6 cN/cm-degree, or less than about 7 cN/cm-degree, or less than about 8 cN/cm-degree, or less than about 9 cN/cm-degree, or less than about 10 cN/cm-degree, or less than about 20 cN/cm- degree, or less than about 30 cN/cm-degree, or less than about 40 cN/cm-degree, or less than about 50 cN/cm-degree, or less than about 60 cN/cm-degree, or less than about 70 cN/cm-degree, or less than about 80 cN/cm-degree, or less than about 90 cN/cm-degree, or less than about 100 cN/cm-degree, or less than about 2 N/cm-degree, or less than about 3 N/cm-degree, or less than about 4 N/cm-degree, or less than about 5 N/cm- degree, or less than about 6 N/cm-degree, or less than about 7 N/cm-degree, or less than about 8 N/cm-degree, or less than about 9 N/cm-degree, or less than about 10 N/cm- degree, or less than about 20 N/cm-degree, or less than about 30 N/cm-degree, or less than about 40 N/cm-degree, or less than about 50 N/cm-degree, or less than about 60 N/cm-degree, or less than about 70 N/cm-degree, or less than about 80 N/cm-degree, or less than about 90 N/cm-degree, or less than about 100 N/cm-degree, or less than about 150 N/cm-degree, or less than about 200 N/cm-degree. In some embodiments, SFS may be applied to fabric having a shear rigidity (N/cm-degree) of greater than about 1 cN/cm-degree, or greater than about 2 cN/cm- degree, or greater than about 3 cN/cm-degree, or greater than about 4 cN/cm-degree, or greater than about 5 cN/cm-degree, or greater than about 5 cN/cm-degree, or greater than about 6 cN/cm-degree, or greater than about 7 cN/cm-degree, or greater than about 8 cN/cm-degree, or greater than about 9 cN/cm-degree, or greater than about 10 cN/cm- degree, or greater than about 20 cN/cm-degree, or greater than about 30 cN/cm-degree, or greater than about 40 cN/cm-degree, or greater than about 50 cN/cm-degree, or greater than about 60 cN/cm-degree, or greater than about 70 cN/cm-degree, or greater than about 80 cN/cm-degree, or greater than about 90 cN/cm-degree, or greater than about 100 cN/cm-degree, or greater than about 2 N/cm-degree, or greater than about 3 N/cm-degree, or greater than about 4 N/cm-degree, or greater than about 5 N/cm- degree, or greater than about 6 N/cm-degree, or greater than about 7 N/cm-degree, or greater than about 8 N/cm-degree, or greater than about 9 N/cm-degree, or greater than about 10 N/cm-degree, or greater than about 20 N/cm-degree, or greater than about 30 N/cm-degree, or greater than about 40 N/cm-degree, or greater than about 50 N/cm- degree, or greater than about 60 N/cm-degree, or greater than about 70 N/cm-degree, or greater than about 80 N/cm-degree, or greater than about 90 N/cm-degree, or greater than about 100 N/cm-degree, or greater than about 150 N/cm-degree, or greater than about 200 N/cm-degree.

In some embodiments, SFS may be applied to fabric having a bending rigidity (N » cm 2 /cm) of less than about 1 cN»cm 2 /cm, or less than about 2 cN»cm 2 /cm, or less than about 3 cN»cm 2 /cm, or less than about 4 cN»cm 2 /cm, or less than about 5 cN»cm 2 /cm, or less than about 5 cN»cm 2 /cm, or less than about 6 cN»cm 2 /cm, or less than about 7 cN»cm 2 /cm, or less than about 8 cN»cm 2 /cm, or less than about 9 cN»cm 2 /cm, or less than about 10 cN»cm 2 /cm, or less than about 20 cN»cm 2 /cm, or less than about 30 cN»cm 2 /cm, or less than about 40 cN»cm 2 /cm, or less than about 50 cN»cm 2 /cm, or less than about 60 cN»cm 2 /cm, or less than about 70 cN»cm 2 /cm, or less than about 80 cN»cm 2 /cm, or less than about 90 cN»cm 2 /cm, or less than about 100 cN»cm 2 /cm, or less than about 2 N»cm 2 /cm, or less than about 3 N»cm 2 /cm, or less than about 4 N»cm 2 /cm, or less than about 5 N»cm 2 /cm, or less than about 6 N»cm 2 /cm, or less than about 7 N»cm 2 /cm, or less than about 8 N»cm 2 /cm, or less than about 9 N»cm 2 /cm, or less than about 10 N»cm 2 /cm, or less than about 20 N»cm 2 /cm, or less than about 30 N»cm 2 /cm, or less than about 40 N»cm 2 /cm, or less than about 50 N»cm 2 /cm, or less than about 60 N»cm 2 /cm, or less than about 70 N»cm 2 /cm, or less than about 80 N»cm 2 /cm, or less than about 90 N»cm 2 /cm, or less than about 100 N»cm 2 /cm, or less than about 150 N»cm 2 /cm, or less than about 200 N»cm 2 /cm.

In some embodiments, SFS may be applied to fabric having a bending rigidity

(N»cm 2 /cm) of greater than about 1 cN»cm 2 /cm, or greater than about 2 cN»cm 2 /cm, or greater than about 3 cN»cm 2 /cm, or greater than about 4 cN»cm 2 /cm, or greater than about 5 cN»cm 2 /cm, or greater than about 5 cN»cm 2 /cm, or greater than about 6 cN»cm 2 /cm, or greater than about 7 cN»cm 2 /cm, or greater than about 8 cN»cm 2 /cm, or greater than about 9 cN»cm 2 /cm, or greater than about 10 cN»cm 2 /cm, or greater than about 20 cN»cm 2 /cm, or greater than about 30 cN»cm 2 /cm, or greater than about 40 cN»cm 2 /cm, or greater than about 50 cN»cm 2 /cm, or greater than about 60 cN»cm 2 /cm, or greater than about 70 cN»cm 2 /cm, or greater than about 80 cN»cm 2 /cm, or greater than about 90 cN»cm 2 /cm, or greater than about 100 cN»cm 2 /cm, or greater than about 2 N»cm 2 /cm, or greater than about 3 N»cm 2 /cm, or greater than about 4 N»cm 2 /cm, or greater than about 5 N»cm 2 /cm, or greater than about 6 N»cm 2 /cm, or greater than about 7 N»cm 2 /cm, or greater than about 8 N»cm 2 /cm, or greater than about 9 N»cm 2 /cm, or greater than about 10 N»cm 2 /cm, or greater than about 20 N»cm 2 /cm, or greater than about 30 N»cm 2 /cm, or greater than about 40 N»cm 2 /cm, or greater than about 50 N»cm 2 /cm, or greater than about 60 N»cm 2 /cm, or greater than about 70 N»cm 2 /cm, or greater than about 80 N»cm 2 /cm, or greater than about 90 N»cm 2 /cm, or greater than about 100 N»cm 2 /cm, or greater than about 150 N»cm 2 /cm, or greater than about 200 N»cm 2 /cm.

In some embodiments, SFS may be applied to fabric having a compression energy (N»cm/cm 2 ) of less than about 1 cN»cm/cm 2 , or less than about 2 cN»cm/cm 2 , or less than about 3 cN»cm/cm 2 , or less than about 4 cN»cm/cm 2 , or less than about 5 c N»cm/cm 2 , or less than about 5 cN»cm/cm 2 , or less than about 6 cN»cm/cm 2 , or less than about 7 cN»cm/cm 2 , or less than about 8 cN»cm/cm 2 , or less than about 9 cN»cm/cm 2 , or less than about 10 cN»cm/cm 2 , or less than about 20 cN»cm/cm 2 , or less than about 30 cN»cm/cm 2 , or less than about 40 cN»cm/cm 2 , or less than about 50 cN»cm/cm 2 , or less than about 60 cN»cm/cm 2 , or less than about 70 cN»cm/cm 2 , or less than about 80 cN»cm/cm 2 , or less than about 90 cN»cm/cm 2 , or less than about 100 cN»cm/cm 2 , or less than about 2 N»cm/cm 2 , or less than about 3 N»cm/cm 2 , or less than about 4 N»cm/cm 2 , or less than about 5 N»cm/cm 2 , or less than about 6 N»cm/cm 2 , or less than about 7 N»cm/cm 2 , or less than about 8 N»cm/cm 2 , or less than about 9 N»cm/cm 2 , or less than about 10 N»cm/cm 2 , or less than about 20 N»cm/cm 2 , or less than about 30 N»cm/cm 2 , or less than about 40 N»cm/cm 2 , or less than about 50 N»cm/cm 2 , or less than about 60 N»cm/cm 2 , or less than about 70 N»cm/cm 2 , or less than about 80 N»cm/cm 2 , or less than about 90 N»cm/cm 2 , or less than about 100 N»cm/cm 2 , or less than about 150 N»crn/cm 2 , or less than about 200 N»cm/cm 2 .

In some embodiments, SFS may be applied to fabric having a compression energy (N»cm/cm 2 ) of greater than about 1 cN»cm/cm 2 , or greater than about 2 cN»cm/cm 2 , or greater than about 3 cN»cm/cm 2 , or greater than about 4 cN»cm/cm 2 , or greater than about 5 cN»cm/cm 2 , or greater than about 5 cN»cm/cm 2 , or greater than about 6 cN»cm/cm 2 , or greater than about 7 cN»cm/cm 2 , or greater than about 8 cN»cm/cm 2 , or greater than about 9 cN»cm/cm 2 , or greater than about 10 cN»cm/cm 2 , or greater than about 20 cN»cm/cm 2 , or greater than about 30 cN»cm/cm 2 , or greater than about 40 cN»cm/cm 2 , or greater than about 50 cN»cm/cm 2 , or greater than about 60 cN»cm/cm 2 , or greater than about 70 cN»cm/cm 2 , or greater than about 80 cN»cm/cm 2 , or greater than about 90 cN»cm/cm 2 , or greater than about 100 cN»cm/cm 2 , or greater than about 2 N»cm/cm 2 , or greater than about 3 N»cm/cm 2 , or greater than about 4 N»cm/cm 2 , or greater than about 5 N»cm/cm 2 , or greater than about 6 N»cm/cm 2 , or greater than about 7 N»cm/cm 2 , or greater than about 8 N»cm/cm 2 , or greater than about 9 N»cm/cm 2 , or greater than about 10 N»cm/cm 2 , or greater than about 20 N»cm/cm 2 , or greater than about 30 N»cm/cm 2 , or greater than about 40 N»cm/cm 2 , or greater than about 50 N»cm/cm 2 , or greater than about 60 N»cm/cm 2 , or greater than about 70 N»cm/cm 2 , or greater than about 80 N»cm/cm 2 , or greater than about 90 N»cm/cm 2 , or greater than about 100 N»cm/cm 2 , or greater than about 150 N»cm/cm 2 , or greater than about 200 N»cm/cm 2 .

In some embodiments, SFS may be applied to fabric having a coefficient of friction of less than about 0.04, or less than about 0.05, or less than about 0.06, or less than about 0.07, or less than about 0.08, or less than about 0.09, or less than about 0.10, or less than about 0.10, or less than about 0.15, or less than about 0.20, or less than about 0.25, or less than about 0.30, or less than about 0.35, or less than about 0.40, or less than about 0.45, or less than about 0.50, or less than about 0.55, or less than about 0.60, or less than about 0.65, or less than about 0.70, or less than about 0.75, or less than about 0.80, or less than about 0.85, or less than about 0.90, or less than about 0.95, or less than about 1.00, or less than about 1.05.

In some embodiments, SFS may be applied to fabric having a coefficient of friction of greater than about 0.04, or greater than about 0.05, or greater than about 0.06, or greater than about 0.07, or greater than about 0.08, or greater than about 0.09, or greater than about 0.10, or greater than about 0.10, or greater than about 0.15, or greater than about 0.20, or greater than about 0.25, or greater than about 0.30, or greater than about 0.35, or greater than about 0.40, or greater than about 0.45, or greater than about 0.50, or greater than about 0.55, or greater than about 0.60, or greater than about 0.65, or greater than about 0.70, or greater than about 0.75, or greater than about 0.80, or greater than about 0.85, or greater than about 0.90, or greater than about 0.95, or greater than about 1.00, or greater than about 1.05.

In some embodiments, chemical finishes may be applied to textiles before or after such textiles are coated with SFS. In an embodiment, chemical finishing may be intended as the application of chemical agents and/or SFS to textiles, including fibers, yam, and fabric, or to garments that are prepared by such fibers, yam, and fabric to modify the original textile's or garment's properties and achieve properties in the textile or garment that would be otherwise absent. With chemical finishes, textiles treated with such chemical finishes may act as surface treatments and/or the treatments may modify the elemental analysis of treated textile base polymers.

In an embodiment, a type of chemical finishing may include the application of certain silk-fibroin based solutions to textiles. For example, SFS may be applied to a fabric after it is dyed, but there are also scenarios that may require the application of SFS during processing, during dyeing, or after a garment is assembled from a selected textile or fabric, thread, or yam. In some embodiments, after its application, SFS may be dried with the use of heat. SFS may then be fixed to the surface of the textile in a processing step called curing.

In some embodiments, SFS may be supplied in a concentrated form suspended in water. In some embodiments, SFS may have a concentration by weight (% w/w or % w/v) or by volume (v/v) of less than about 50%, or less than about 45%, or less than about 40%, or less than about 35%, or less than about 30%, or less than about 25%, or less than about 20%, or less than about 15%, or less than about 10%, or less than about 5%, or less than about 4%, or less than about 3%, or less than about 2%, or less than about 1%, or less than about 0.1%, or less than about 0.01%, or less than about 0.001%, or less than about 0.0001%, or less than about 0.00001%. In some embodiments, SFS may have a concentration by weight (% w/w or % w/v) or by volume (v/v) of greater than about 50%, or greater than about 45%, or greater than about 40%, or greater than about 35%, or greater than about 30%, or greater than about 25%, or greater than about 20%, or greater than about 15%, or greater than about 10%, or greater than about 5%, or greater than about 4%, or greater than about 3%, or greater than about 2%, or greater than about 1%, or greater than about 0.1%, or greater than about 0.01%, or greater than about 0.001%, or greater than about 0.0001%, or greater than about 0.00001%.

In some embodiments, the solution concentration and the wet pick of the material determines the amount of silk fibroin solution (SFS), which may include silk- based proteins or fragments thereof, that may be fixed or otherwise adhered to the textile being coated. The wet pick up may be expressed by the following formula:

. , / ·„, - > weiqht of SFS applied xlOO

wet pick up(%) = .

weight of dry textile material

The total amount of SFS added to the textile material may be expressed by the following formula:

weight of dry SFS coated textile material x 100

SFS added (%) =

weight of dry textile material before coating

Regarding methods for applying SFS to textiles more broadly, SFS may be applied to textiles through a pad or roller application on process, a saturation and removal process, and/or a topical application process. Moreover, the methods of silk application (i.e., SFS application or coating) may include bath coating, kiss rolling, spray coating, and/or two-sided rolling. In some embodiments, the coating processes (e.g., bath coating, kiss rolling, spray coating, two-sided rolling, roller application, saturation and removal application, and/or topical application), drying processes, and curing processes may be varied as described herein to modify one or more selected textile (e.g., fabric) properties of the resulting coated textile wherein such properties include, but are not limited to wetting time, absorption rate, spreading speed, accumulative one-way transport, and/or overall moisture management capability. In some embodiments, the aforementioned selected properties may be enhanced by varying one or more of the coating processes, drying processes, and curing processes as described herein.

In some embodiments, the silk compositions provided herein may be applied in a wet process or a dry process, such as by applying the silk compositions to a wet textile or a dry textile.

In an embodiment, the padder application may be used on dry or wet textile. For example, it may be applied on fabric after the dyeing process. The fabric may be fed into a water bath solution and may reach saturation. The fabric to be coated may then pass through a set of rollers that, based on multiple variables, extract the bath solution in excess to the desired wet pick up %. The variables that affect the wet pick up % are the roller pressure and materials, the fabric composition and construction, and the SFS viscosity. An exemplary padder roller configuration is shown in FIG. 183.

In an embodiment, the padder application on wet textile may be used to reduce the cost of drying the fabric post dyeing. The fabric exiting the pad rollers may maintain a higher weight % than the incoming fabric to maintain a SFS deposit on the fabric; and the SFS solution may need to account for any dilution taking place due to water present on the incoming fabric.

In an embodiment, the saturation and removal application is a low wet pick up method that may, for example, solve some of the issues associated with removing large amounts of water during drying processes. Since fabric may dry in an oven from the outside surface towards the inside, water may move from the inside to the outside resulting in a higher coating concentration on the outside surface. With less water content, migration may be reduced due to a higher viscosity in the solution. However, decreased wet pick up may result in an uneven solution deposit.

In an embodiment, vacuum extraction may be used as a method for low wet pick up. Saturated fabric may be subject to a vacuum that pulls solution out of the fabric and returns it to an application loop. Air jet ejection may be a method for providing low wet pick up. The saturated fabric may be subjected to high pressure steam that removes solution out of the fabric and returns it to an application loop.

In an embodiment, a porous bowl method may be used for low wet pick up.

Solid pad rollers may be substituted with rubber coated fiber rollers. Saturated fabric may be subjected to the pressure of the roller since the porosity of the rollers may allow for more solution to be squeezed from the fabric.

In an embodiment, a transfer padding method may be used for low wet pick up. Saturated fabric may be passed through two continuous dry non-woven fabrics and may be pressed at low pressure. The non-woven fabrics may extract excess solution from the fabric being treated.

In an embodiment, topical application may be used as a low wet pick up method of application that deposits the desired amount of SFS to the fabric without removing any excess material. The methods described above may be used for one-sided coating applications, but there are variations that may allow for two-sided coating.

In an embodiment, kiss rolling may be used as a topical method of application that transfers the SFS from a roller (i.e., a kiss roller) to one side of the fabric. The solution viscosity, roller surface finish, speed of the roller, speed of the fabric, contact angle of the fabric on the roller and properties of the fabric are parameters that control the amount of solution deposited on the fabric. An exemplary kiss roller is depicted in FIG. 184.

In an embodiment, a variation to the kiss roller technique may be the Triatex MA system that uses two moisture content sensors to determine the solution pick up at the kiss roller and adjust the kiss roller controllable variable to maintain consistent the solution deposit onto the fabric.

In an embodiment, a loop transfer application may be used as a topical method of application that transfers the SFS from a saturated loop fabric to the fabric to be coated between low pressure pad rollers. There is a two rollers version that may allow for minimum contact with the fabric and a three rollers version that allows for greater contact with the fabric.

In an embodiment, an engrave roller application may be used as a topical method of application that may transfer a metered amount of SFS onto the fabric. This may be achieved by engraving a pattern on the surface of the roller with precise depth and design that contains a controlled amount of SFS. A blade may be used to remove any solution that is deposited on the surface of the roller in order to maintain a consistent transfer of solution to the fabric to be coated. In an embodiment, rotary screen printing may be used as a topical method of application that may deposit SFS onto the fabric by seeping the solution through a roller screen. The solution may be contained in the screen print roller core at a set level while a blade may be used to remove any excess solution from the interior roller wall, providing a clean surface for the next revolution of the screen printer roller.

In an embodiment, magnetic roller coating may be used as a topical method of application that may deposit SFS from a kiss roller onto the fabric to be coated. The kiss roller is semi-submersed in a bath solution while a magnetic field created in the fabric driving roller determines the amount of pressure applied by the kiss roller, controlling the solution pick up rate.

In an embodiment, spraying may be used as a topical method of application that may transfer SFS onto the fabric by nebulizing the solution. The spray pattern may be controlled by the nozzle pattern, size, and the air flow. Spray application may be used for one side application or also two sided applications.

In an embodiment, foam application may be used a topical method of application that may transfer SFS onto the fabric. Foam may be made by substituting part of the water in the solution with air therefore reducing the amount of water to be applied to the fabric. Foam application may be used for one-sided application or two- sided application where the same foam may be deposited through a squeeze roller or different foam solutions may be provided through transfer rolls or through a slot applicator.

In an embodiment, the application of SFS may take place after a garment is assembled. In an embodiment, the process may take place in a washing and dyeing machine or in a spray booth. For example, a washing and dyeing machine may be similar in shape to a household front loader washing machine, it allows the process to take place at exhaustion post dyeing or with an independent processing cycle. In an embodiment, a spray booth machine may include a manual or a fully automated process. For example, a garment may be held by a mannequin while an operator or an anthropomorphic robot may spray the solution onto the fabric.

In an embodiment, SFS may be a water based solution that, after its application to the textile, may require thermal vaporization to infuse the SFS onto the textile. Thermal vaporization may be applied by heat transfer through radiation with equipment such as infrared or radio frequency dryer.

In an embodiment, thermal vaporization may be applied by convection through heated air circulating in an oven to the required temperature, while the fabric is clamped and is transported by a conveyor. This allows full control on fabric width dimension.

In an embodiment, thermal vaporization may be applied by conduction through contacting the textile with heated cylinder or calendar cylinder. Since the fabric is not clamp there is minimal control on fabric width.

In an embodiment, curing of the SFS on the textile may be completed with the same equipment used for the thermal vaporization in a continuous cycle or in a separate cycle.

In an embodiment, curing time temperature may be dependent the textile polymer content and the binding method of preference for the SFS with the specific polymer. The curing process may not start until the thermal vaporization is completed.

In some embodiments, sensor may be used to monitor SFS deposition on the textile and the drying and curing steps.

In some embodiments, for monitoring the deposition of SFS, a contactless sensor, like the one supplied by Pleva model AF120 based on microwave absorption of water, may be used. Measurement of the material moisture may be based on microwave absorption by water. A semiconductor oscillator transmits microwave energy through the web. The non-absorbed part of the energy may be received on the opposite side by a microwave receiver. The amount of absorption is a measurement of the absolute moisture content. The microwave sensor is capable of detecting and measuring water content from a minimum of 0 up to 2000 g FhO/m 2 .

In some embodiments, for wide fabric processing multiple sensor may be paired side by side, delivering the data analysis to a centralized control system loop capable to add more solution in the area of the fabric that is low.

In some embodiments, another sensor may be used that is based on microwave technology, such as Aqualot by Mahlo. The sensor may evaluate the shift in the resonant frequency of the two standing waves with respect to each other rather than the attenuation of the microwaves by the quantity of water molecules in the measuring gap. In some embodiments, another contactless sensor for SFS may be the IR-3000 by MoistTech based on near infrared sensing technology. The sensor measures the amount of near infrared energy reflected at a given wavelength that is inversely proportional to the quantity of absorbing molecules in the fabric.

In some embodiments, the residual moister at the end of the curing process may be measured to further confirm the drying and curing process. In addition to the above sensor, a contact sensor such as the Textometer RMS by Mahlo may be used for measuring moister through conductivity.

In some embodiments, monitoring the end of the drying process phase may be achieved by measuring the fabric temperature with a contactless temperature sensor. When wet product enters the dryer, it first heats up to the cooling limit temperature. In some embodiments, when the water content drops to residual moisture levels, the product temperature may begin to rise again. The closer the product temperature approaches the circulation air temperature in the dryer, the slower the temperature continues to rise. In some embodiments, at a certain temperature threshold (called the fixing temperature) the temperature necessary for processing, fixing, or condensing is reached.

In some embodiments, to determine the dwell time for a desired product temperature, the surface temperature of the product may be measured without contact at several locations in the dryer using high-temperature resistant infrared pyrometers. Mahlo Permaset VMT is an infrarem Pyrometer that may be assembled in multiple units to monitors temperature through the dryer. Setex is another manufacturer offering fabric temperature sensors for use in dryers and oven like the models WTM VI 1, V21, and V41.

In some embodiments, SFS may be applied to a textile during exhaust dyeing.

In some embodiments, the process may involve loading fabric into a bath, originally known as a batch, and allowing it to come into equilibrium with the solution. Exhaust dyeing may be the ability of the silk fibroin molecules to move from the solution onto the fibers or thread of a textile (substantivity). The substantivity of the silk fibroin may be influenced by temperature or additives, such as salt.

In some embodiments, an exhaust dyeing process may take anywhere from a few minutes to a few hours. When the fabric has been absorbed, or fixed, as much silk fibroin as it can, the bath may be emptied and the fabric may be rinsed to remove any excess solution.

In some embodiments, an important parameter in exhaust dyeing may be what is known as the specific liquor ratio. This describes the ratio of the mass of the fabric to the volume of the SFS bath and determines the amount of silk fibroin deposited on a textile.

In some embodiments, SFS can be applied to a textile during jet dyeing processes. A jet dyeing machine may formed by closed tubular system where the fabric is placed. For transporting the fabric through the tube, a jet of dye liquor is supplied through a venturi. The jet may create turbulence. This may help in SFS penetration along with preventing the fabric from touching the walls of the tube. For example, as the fabric is often exposed to comparatively higher concentrations of liquor within the transport tube, a small SFS bath is needed in the bottom of the vessel. This arrangement may be enough for the smooth movement from rear to front of the vessel.

In some embodiments, SFS may be applied during Paddle dyeing. Paddle dyeing machines may be generally used to many forms of textiles but the method best suits to garments. Heat may be generated through steam injection directly into the coating bath. In an embodiment, a paddle dyeing machine operates through a paddle that circulates both the bath and garments in a perforated central island. It is here that the SFS, water, and steam for heat are added. The overhead paddle machine may be described as a vat with a paddle that has blades of full width. The blades may generally dip a few centimeters into the vat. This action may stir the bath and push garments to be died down, thus keeping them submerged in the dye liquor.

In some embodiments, the processing methods set forth herein may be used to apply SFS to textiles with one or more of the following parameters including, but not limited to, fabric speed, solution viscosity, solution added to fabric, fabric range width, drying temperature, drying time, curing time, fabric tension, padder pressure, padder roller shore hardness, stenter temperature, and common drying and curing temperatures. In an embodiment, the processing method parameters may also include a condensation temperature, which may vary depending upon the chemical recipe used to apply the SFS to the textiles. In an embodiment, the fabric speed for the processes of the invention may be less than about 0.1 m/min, or less than about 0.2 m/min, or less than about 0.3 m/min, or less than about 0.4 m/min, or less than about 0.5 m/min, or less than about 0.6 m/min, or less than about 0.7 m/min, or less than about 0.8 m/min, or less than about 0.9 m/min, or less than about 1 m/min, or less than about 2 m/min, or less than about 3 m/min, or less than about 4 m/min, or less than about 5 m/min, or less than about 6 m/min, or less than about 7 m/min, or less than about 8 m/min, or less than about 9 m/min, or less than about 10 m/min, or less than about 20 m/min, or less than about 30 m/min, or less than about 40 m/min, or less than about 50 m/min, or less than about 60 m/min.

In an embodiment, the fabric speed for the processes of the invention may be greater than about 0.1 m/min, or greater than about 0.2 m/min, or greater than about 0.3 m/min, or greater than about 0.4 m/min, or greater than about 0.5 m/min, or greater than about 0.6 m/min, or greater than about 0.7 m/min, or greater than about 0.8 m/min, or greater than about 0.9 m/min, or greater than about 1 m/min, or greater than about 2 m/min, or greater than about 3 m/min, or greater than about 4 m/min, or greater than about 5 m/min, or greater than about 6 m/min, or greater than about 7 m/min, or greater than about 8 m/min, or greater than about 9 m/min, or greater than about 10 m/min, or greater than about 20 m/min, or greater than about 30 m/min, or greater than about 40 m/min, or greater than about 50 m/min, or greater than about 60 m/min.

In an embodiment, the solution viscosity for the processes of the invention may be less than about 1000 mPas, or less than about 1500 mPas, or less than about 2000 mPas, or less than about 2500, or less than about 3000 mPas, or less than about 4000 mPas, or less than about 4500 mPas, or less than about 5000 mPas, or less than about 5500 mPas, or less than about 6000 mPas, or less than about 6500 mPas, or less than about 7000 mPas, or less than about 7500 mPas, or less than about 8000 mPas, or less than about 8500 mPas, or less than about 9000 mPas, or less than about 9500 mPas, or less than about 10000 mPas, or less than about 10500 mPas, or less than about 11000 mPas, or less than about 11500 mPas, or less than about 12000 mPas.

In an embodiment, the solution viscosity for the processes of the invention may be greater than about 1000 mPas, or greater than about 1500 mPas, or greater than about 2000 mPas, or greater than about 2500, or greater than about 3000 mPas, or greater than about 4000 mPas, or greater than about 4500 mPas, or greater than about 5000 mPas, or greater than about 5500 mPas, or greater than about 6000 mPas, or greater than about 6500 mPas, or greater than about 7000 mPas, or greater than about 7500 mPas, or greater than about 8000 mPas, or greater than about 8500 mPas, or greater than about 9000 mPas, or greater than about 9500 mPas, or greater than about 10000 mPas, or greater than about 10500 mPas, or greater than about 11000 mPas, or greater than about 11500 mPas, or greater than about 12000 mPas.

In an embodiment, the solution may be added to a textile (e.g., fabric) for the processes of the invention in less than about 0.01 g/m 2 , or less than about 0.02 g/m 2 , or less than about 0.03 g/m 2 , or less than about 0.04 g/m 2 , or less than about 0.05 g/m 2 , or less than about 0.06 g/m 2 , or less than about 0.07 g/m 2 , or less than about 0.08 g/m 2 , or less than about 0.09 g/m 2 , or less than about 0.10 g/m 2 , or less than about 0.2 g/m 2 , or less than about 0.3 g/m 2 , or less than about 0.4 g/m 2 , or less than about 0.5 g/m 2 , or less than about 0.6 g/m 2 , or less than about 0.7 g/m 2 , or less than about 0.8 g/m 2 , or less than about 0.9 g/m 2 , or less than about 1 g/m 2 , or less than about 2 g/m 2 , or less than about 3 g/m 2 , or less than about 4 g/m 2 , or less than about 5 g/m 2 , or less than about 6 g/m 2 , or less than about 7 g/m 2 , or less than about 8 g/m 2 , or less than about 9 g/m 2 , or less than about 10 g/m 2 , or less than about 20 g/m 2 , or less than about 30 g/m 2 , or less than about 40 g/m 2 , or less than about 50 g/m 2 , or less than about 60 g/m 2 , or less than about 70 g/m 2 , or less than about 80 g/m 2 , or less than about 90 g/m 2 , or less than about 100 g/m 2 .

In an embodiment, the solution may be added to a textile (e.g., fabric) for the processes of the invention in greater than about 0.01 g/m 2 , or greater than about 0.02 g/m 2 , or greater than about 0.03 g/m 2 , or greater than about 0.04 g/m 2 , or greater than about 0.05 g/m 2 , or greater than about 0.06 g/m 2 , or greater than about 0.07 g/m 2 , or greater than about 0.08 g/m 2 , or greater than about 0.09 g/m 2 , or greater than about 0.10 g/m 2 , or greater than about 0.2 g/m 2 , or greater than about 0.3 g/m 2 , or greater than about 0.4 g/m 2 , or greater than about 0.5 g/m 2 , or greater than about 0.6 g/m 2 , or greater than about 0.7 g/m 2 , or greater than about 0.8 g/m 2 , or greater than about 0.9 g/m 2 , or greater than about 1 g/m 2 , or greater than about 2 g/m 2 , or greater than about 3 g/m 2 , or greater than about 4 g/m 2 , or greater than about 5 g/m 2 , or greater than about 6 g/m 2 , or greater than about 7 g/m 2 , or greater than about 8 g/m 2 , or greater than about 9 g/m 2 , or greater than about 10 g/m 2 , or greater than about 20 g/m 2 , or greater than about 30 g/m 2 , or greater than about 40 g/m 2 , or greater than about 50 g/m 2 , or greater than about 60 g/m 2 , or greater than about 70 g/m 2 , or greater than about 80 g/m 2 , or greater than about 90 g/m 2 , or greater than about 100 g/m 2 .

In an embodiment, the fabric range width for the processes of the invention may be less than about 1 mm, or less than about 2 mm, or less than about 3 mm, or less than about 4 mm, or less than about 5 mm, or less than about 6 mm, or less than about 7 mm, or less than about 8 mm, or less than about 9, or less than about 10 mm, or less than about 20 mm, or less than about 30 mm, or less than about 40 mm, or less than about 50 mm, or less than about 60 mm, or less than about 70 mm, or less than about 80 mm, or less than about 90 mm, or less than about 100 mm, or less than about 200, or less than about 300 mm, or less than about 400 mm, or less than about 500 mm, or less than about 600 mm, or less than about 700 mm, or less than about 800 mm, or less than about 900 mm, or less than about 1000 mm, or less than about 2000 mm, or less than about 2000 mm, or less than about 3000 mm, or less than about 4000 mm, or less than about 5000 mm.

In an embodiment, the fabric range width for the processes of the invention may be greater than about 1 mm, or greater than about 2 mm, or greater than about 3 mm, or greater than about 4 mm, or greater than about 5 mm, or greater than about 6 mm, or greater than about 7 mm, or greater than about 8 mm, or greater than about 9, or greater than about 10 mm, or greater than about 20 mm, or greater than about 30 mm, or greater than about 40 mm, or greater than about 50 mm, or greater than about 60 mm, or greater than about 70 mm, or greater than about 80 mm, or greater than about 90 mm, or greater than about 100 mm, or greater than about 200, or greater than about 300 mm, or greater than about 400 mm, or greater than about 500 mm, or greater than about 600 mm, or greater than about 700 mm, or greater than about 800 mm, or greater than about 900 mm, or greater than about 1000 mm, or greater than about 2000 mm, or greater than about 2000 mm, or greater than about 3000 mm, or greater than about 4000 mm, or greater than about 5000 mm.

In an embodiment, the drying and/or curing temperature for the processes of the invention may be less than about 70 °C, or less than about 75 °C, or less than about 80 °C, or less than about 85 °C, or less than about 90 °C, or less than about 95 °C, or less than about 100 °C, or less than about 110 °C, or less than about 120 °C, or less than about 130 °C, or less than about 140 °C, or less than about 150 °C, or less than about 160 °C, or less than about 170 °C, or less than about 180 °C, or less than about 190 °C, or less than about 200 °C, or less than about 210 °C, or less than about 220 °C, or less than about 230 °C.

In an embodiment, the drying and/or curing temperature for the processes of the invention may be greater than about 70 °C, or greater than about 75 °C, or greater than about 80 °C, or greater than about 85 °C, or greater than about 90 °C, or greater than about 95 °C, or greater than about 100 °C, or greater than about 110 °C, or greater than about 120 °C, or greater than about 130 °C, or greater than about 140 °C, or greater than about 150 °C, or greater than about 160 °C, or greater than about 170 °C, or greater than about 180 °C, or greater than about 190 °C, or greater than about 200 °C, or greater than about 210 °C, or greater than about 220 °C, or greater than about 230 °C.

In an embodiment, the drying time for the processes of the invention may be less than about 10 seconds, or less than about 20 seconds, or less than about 30 seconds, or less than about 40 seconds, or less than about 50 seconds, or less than about 60 seconds, or less than about 2 minutes, or less than about, 3 minutes, or less than about 4 minutes, or less than about 5 minutes, or less than about 6 minutes, or less than about 7 minutes, or less than about 8 minutes, or less than about 9 minutes, or less than about 10 minutes, or less than about 20 minutes, or less than about 30 minutes, or less than about 40 minutes, or less than about 50 minutes, or less than about 60 minutes.

In an embodiment, the drying time for the processes of the invention may be greater than about 10 seconds, or greater than about 20 seconds, or greater than about 30 seconds, or greater than about 40 seconds, or greater than about 50 seconds, or greater than about 60 seconds, or greater than about 2 minutes, or greater than about, 3 minutes, or greater than about 4 minutes, or greater than about 5 minutes, or greater than about 6 minutes, or greater than about 7 minutes, or greater than about 8 minutes, or greater than about 9 minutes, or greater than about 10 minutes, or greater than about 20 minutes, or greater than about 30 minutes, or greater than about 40 minutes, or greater than about 50 minutes, or greater than about 60 minutes.

In an embodiment, the curing time for the processes of the invention may be less than about 1 second, or less than about 2 seconds, or less than about 3 seconds, or less than about 4 seconds, or less than about 5 seconds, or less than about 6 seconds, or less than about 7 seconds, or less than about 8 seconds, or less than about 9 seconds, or less than about 10 seconds, or less than about 20 seconds, or less than about 30 seconds, or less than about 40 seconds, or less than about 50 seconds, or less than about 60 seconds, or less than about 2 minutes, or less than about 3 minutes, or less than about 4 minutes, or less than about 5 minutes, or less than about 6 minutes, or less than about 7 minutes, or less than about 8 minutes, or less than about 9 minutes, or less than about 10 minutes, or less than about 20 minutes, or less than about 30 minutes, or less than about 40 minutes, or less than about 50 minutes, or less than about 60 minutes.

In an embodiment, the curing time for the processes of the invention may be greater than about 1 second, or greater than about 2 seconds, or greater than about 3 seconds, or greater than about 4 seconds, or greater than about 5 seconds, or greater than about 6 seconds, or greater than about 7 seconds, or greater than about 8 seconds, or greater than about 9 seconds, or greater than about 10 seconds, or greater than about 20 seconds, or greater than about 30 seconds, or greater than about 40 seconds, or greater than about 50 seconds, or greater than about 60 seconds, or greater than about 2 minutes, or greater than about 3 minutes, or greater than about 4 minutes, or greater than about 5 minutes, or greater than about 6 minutes, or greater than about 7 minutes, or greater than about 8 minutes, or greater than about 9 minutes, or greater than about 10 minutes, or greater than about 20 minutes, or greater than about 30 minutes, or greater than about 40 minutes, or greater than about 50 minutes, or greater than about 60 minutes.

In an embodiment, the fabric tension for the processes of the invention may be less than about 1 N, or less than about 2 N, or less than about 3 N, or less than about 4 N, or less than about 5 N, or less than about 6 N, or less than about 7 N, or less than about 8 N, or less than about 9 N, or less than about 10 N, or less than about 20 N, or less than about 30 N, or less than about 40 N, or less than about 50 N, or less than about 60 N, or less than about 70 N, or less than about 80 N, or less than about 90 N, or less than about 100 N, or less than about 150 N, or less than about 200 N, or less than about 250 N, or less than about 300 N.

In an embodiment, the fabric tension for the processes of the invention may be greater than about 1 N, or greater than about 2 N, or greater than about 3 N, or greater than about 4 N, or greater than about 5 N, or greater than about 6 N, or greater than about 7 N, or greater than about 8 N, or greater than about 9 N, or greater than about 10 N, or greater than about 20 N, or greater than about 30 N, or greater than about 40 N, or greater than about 50 N, or greater than about 60 N, or greater than about 70 N, or greater than about 80 N, or greater than about 90 N, or greater than about 100 N, or greater than about 150 N, or greater than about 200 N, or greater than about 250 N, or greater than about 300 N.

In an embodiment, the padder pressure for the processes of the invention may be less than about 1 N/mm, or less than about 2 N/mm, or less than about 3 N/mm, or less than about 4 N/mm, or less than about 4 N/mm, or less than about 5 N/mm, or less than about 6 N/mm, or less than about 7 N/mm, or less than about 8 N/mm, or less than about 9 N/mm, or less than about 10 N/mm, or less than about 20 N/mm, or less than about 30 N/mm, or less than about 40 N/mm, or less than about 50 N/mm, or less than about 60 N/mm, or less than about 70 N/mm, or less than about 80 N/mm, or less than about 90 N/mm.

In an embodiment, the padder pressure for the processes of the invention may be greater than about 1 N/mm, or greater than about 2 N/mm, or greater than about 3 N/mm, or greater than about 4 N/mm, or greater than about 4 N/mm, or greater than about 5 N/mm, or greater than about 6 N/mm, or greater than about 7 N/mm, or greater than about 8 N/mm, or greater than about 9 N/mm, or greater than about 10 N/mm, or greater than about 20 N/mm, or greater than about 30 N/mm, or greater than about 40 N/mm, or greater than about 50 N/mm, or greater than about 60 N/mm, or greater than about 70 N/mm, or greater than about 80 N/mm, or greater than about 90 N/mm.

In an embodiment, the padder roller shore hardness for the processes of the invention may be less than about 70 shore A, or less than about 75 shore A, or less than about 80 shore A, or less than about 85 shore A, or less than about 90 shore A, or less than about 95 shore A, or less than about 100 shore A.

In an embodiment, the padder roller shore hardness for the processes of the invention may be greater than about 70 shore A, or greater than about 75 shore A, or greater than about 80 shore A, or greater than about 85 shore A, or greater than about 90 shore A, or greater than about 95 shore A, or greater than about 100 shore A.

In an embodiment, the stenter temperature for the processes of the invention may be less than about 70 °C, or less than about 75 °C, or less than about 80 °C, or less than about 85 °C, or less than about 90 °C, or less than about 95 °C, or less than about 100 °C, or less than about 110 °C, or less than about 120 °C, or less than about 130 °C, or less than about 140 °C, or less than about 150 °C, or less than about 160 °C, or less than about 170 °C, or less than about 180 °C, or less than about 190 °C, or less than about 200 °C, or less than about 210 °C, or less than about 220 °C, or less than about 230 °C.

In an embodiment, the stenter temperature for the processes of the invention may be greater than about 70 °C, or greater than about 75 °C, or greater than about 80 °C, or greater than about 85 °C, or greater than about 90 °C, or greater than about 95 °C, or greater than about 100 °C, or greater than about 110 °C, or greater than about 120 °C, or greater than about 130 °C, or greater than about 140 °C, or greater than about 150 °C, or greater than about 160 °C, or greater than about 170 °C, or greater than about 180 °C, or greater than about 190 °C, or greater than about 200 °C, or greater than about 210 °C, or greater than about 220 °C, or greater than about 230 °C.

In an embodiment, the common drying temperatures for the processes of the invention may be less than about 110 °C, or less than about 115 °C, or less than about 120 °C, or less than about 125 °C, or less than about 130 °C, or less than about 135 °C, or less than about 140 °C, or less than about 145 °C, or less than about 150 °C.

In an embodiment, the common drying temperatures for the processes of the invention may be greater than about 110 °C, or greater than about 115 °C, or greater than about 120 °C, or greater than about 125 °C, or greater than about 130 °C, or greater than about 135 °C, or greater than about 140 °C, or greater than about 145 °C, or greater than about 150 °C.

In some embodiments, a silk fibroin coated material (e.g., fabric) may be heat resistant to a selected temperature where the selected temperature is chosen for drying, curing, and/or heat setting a dye that may be applied to the material (e.g., LYCRA). As used herein, a "heat resistant" may refer to a property of the silk fibroin coating deposited on the material where the silk fibroin coating and/or silk fibroin protein does not exhibit a substantial modification (i.e., "substantially modifying") in silk fibroin coating performance as compared to a control material having a comparable silk fibroin coating that was not subjected to the selected temperature for drying, curing, wash cycling, and/or heat setting purposes. In some embodiments, the selected temperature is the glass transition temperature (Tg) for the material upon which the silk fibroin coating is applied. In some embodiments, the selected temperature is greater than about 65 °C, or greater than about 70 °C, or greater than about 80 °C, or greater than about 90 °C, or greater than about 100 °C, or greater than about 110 °C, or greater than about 120 °C, or greater than about 130 °C, or greater than about 140 °C, or greater than about 150 °C, or greater than about 160 °C, or greater than about 170 °C, or greater than about 180 °C, or greater than about 190 °C, or greater than about 200 °C, or greater than about 210 °C, or greater than about 220 °C. In some embodiments, the selected temperature is less than about 65 °C, or less than about 70 °C, or less than about 80 °C, or less than about 90 °C, or less than about 100 °C, or less than about 110 °C, or less than about 120 °C, or less than about 130 °C, or less than about 140 °C, or less than about 150 °C, or less than about 160 °C, or less than about 170 °C, or less than about 180 °C, or less than about 190 °C, or less than about 200 °C, or less than about 210 °C, or less than about 220 °C.

In an embodiment, "substantially modifying" silk fibroin coating performance may be a decrease in a selected property of silk fibroin coating, such as wetting time, absorption rate, spreading speed, accumulative one-way transport, or overall moisture management capability as compared to a control silk fibroin coating that was not subjected to the selected temperature for drying, curing, wash cycling, and/or heat setting purposes, where such decrease is less than about a 1% decrease, or less than about a 2% decrease, or less than about a 3% decrease, or less than about a 4% decrease, or less than about a 5% decrease, or less than about a 6% decrease, or less than about a 7% decrease, or less than about an 8% decrease, or less than about a 9% decrease, or less than about a 10% decrease, or less than about a 15% decrease, or less than about a 20% decrease, or less than about a 25% decrease, or less than about a 30% decrease, or less than about a 35% decrease, or less than about a 40% decrease, or less than about a 45% decrease, or less than about a 50% decrease, or less than about a 60% decrease, or less than about a 70% decrease, or less than about a 80% decrease, or less than about a 90% decrease, or less than about 100% decrease in wetting time, absorption rate, spreading speed, accumulative one-way transport, or overall moisture management capability as compared to a control silk fibroin coating that was not subjected to the selected temperature for drying, curing, wash cycling, and/or heat setting purposes. In some embodiments, "wash cycling" may refer to at least one wash cycle, or at least two wash cycles, or at least three wash cycles, or at least four wash cycles, or at least five wash cycles. In an embodiment, "substantially modifying" silk fibroin coating performance may be an increase in a selected property of silk fibroin coating, such as wetting time, absorption rate, spreading speed, accumulative one-way transport, or overall moisture management capability as compared to a control silk fibroin coating that was not subjected to the selected temperature for drying, curing, wash cycling, and/or heat setting purposes, where such increase is less than about a 1% increase, or less than about a 2% increase, or less than about a 3% increase, or less than about a 4% increase, or less than about a 5% increase, or less than about a 6% increase, or less than about a 7% increase, or less than about an 8% increase, or less than about a 9% increase, or less than about a 10% increase, or less than about a 15% increase, or less than about a 20% increase, or less than about a 25% increase, or less than about a 30% increase, or less than about a 35% increase, or less than about a 40% increase, or less than about a 45% increase, or less than about a 50% increase, or less than about a 60% increase, or less than about a 70% increase, or less than about a 80% increase, or less than about a 90% increase, or less than about 100% increase in wetting time, absorption rate, spreading speed, accumulative one-way transport, or overall moisture management capability as compared to a control silk fibroin coating that was not subjected to the selected temperature for drying, curing, wash cycling, and/or heat setting purposes. In some embodiments, "wash cycling" may refer to at least one wash cycle, or at least two wash cycles, or at least three wash cycles, or at least four wash cycles, or at least five wash cycles.

In some embodiments, the SFS coated article may be subjected to heat setting in order to set one or more dyes that may be applied to the SFS coated article in order to permanently set the one or more dyes on the SFS coated article. In some embodiments, the SFS coated article may be heat setting resistant, wherein the SFS coating on the SFS coated article may resist a heat setting temperature of greater than about 100 °C, or greater than about 110 °C, or greater than about 120 °C, or greater than about 130 °C, or greater than about 140 °C, or greater than about 150 °C, or greater than about 160 °C, or greater than about 170 °C, or greater than about 180 °C, or greater than about 190 °C, or greater than about 200 °C, or greater than about 210 °C, or greater than about 220 °C. In some embodiments, the selected temperature is less than about 100 °C, or less than about 110 °C, or less than about 120 °C, or less than about 130 °C, or less than about 140 °C, or less than about 150 °C, or less than about 160 °C, or less than about 170 °C, or less than about 180 °C, or less than about 190 °C, or less than about 200 °C, or less than about 210 °C, or less than about 220 °C.

In an embodiment, a material coated by the silk fibroin coating as described herein may partially dissolved or otherwise partially incorporated within a portion of the material after the silk fibroin coated material is subjected to heating and/or curing as described herein. Without being limited to any one theory of the invention, where the silk fibroin coated material is heated to greater than about the glass transition temperature (Tg) for the material that is coated, the silk fibroin coating may become partially dissolved or otherwise partially incorporated within a portion of the material.

In some embodiments, a material coated by the silk fibroin coating as described herein may be sterile or may be sterilized to provide a sterilized silk fibroin coated material. Alternatively, or in addition thereto, the methods described herein may include a sterile SFS prepared from sterile silk fibroin. In some embodiments, the fabric constructions that are compatible with the processes of the invention include woven fabrics, knitted fabrics, and non-woven fabrics.

In some embodiments, the coating partem provided by the processes of the invention include one side coating, two side coating, and/or throughout coating.

In some embodiments, the equipment manufacturers that are capable of producing equipment configured to continuously coat SFS on textiles include, but are not limited to, Aigle, Amba Projex, Bombi, Bruckner, Cavitec, Crosta, Dienes Apparatebau, Eastsign, Europlasma, Fermor, Fontanet, Gaston Systems, Hansa Mixer, Harish, Has Group, Icomatex, Idealtech, Interspare, Isotex, Klieverik, KTP, M P, Mageba, Mahr Feinpruef, Matex, Mathis, Menzel LP, Meyer, Monforts, Morrison Textile, Mtex, Muller Frick, Muratex Textile, Reliant Machinery, Rollmac, Salvade, Sandvik Tps, Santex, Chmitt-Machinen, Schott & Meissner, Sellers, Sicam, Siltex, Starlinger, Swatik Group India, Techfull, TMT Manenti, Unitech Textile Machinery, Weko, Willy, Wumag Texroll, Yamuna, Zappa, and Zimmer Austria.

In some embodiments, the equipment manufactures that are capable of producing equipment configured to dry SFS coated on textiles include, but are not limited to, Alea, Alkan Makina, Anglada, Atac Makina, Bianco, Bruckner, Campen, CHTC, CTMTC, Dilmenler, Elteksmak, Erbatech, Fontanet, Harish, Icomatex, Ilsung, Inspiron, Interspare, Master, Mathis, Monfongs, Monforts, Salvade, Schmitt- Maschinen, Sellers, Sicam, Siltex, Swastik Group India, Tacome, Tubetex, Turbang, Unitech Textile Machinery, and Yamuna.

In some embodiments, SFS may be used in combination with chemical agents. In some embodiments, SFS may include a chemical agent. In some embodiments, a chemical agent may be applied to a textile to be coated prior to providing an SFS coating. In some embodiments, a chemical agent may be applied to a textile after such textile has been coated with an SFS coating. In some embodiments, a chemical agent may be applied to a textile to be coated simultaneously with providing an SFS coating. One or more chemical agents may be applied, as set forth above, and may include a first chemical agent, second chemical agent, third chemical agent, and the like, where the chemical agents may be the same or a combination of two or more of the chemical agents described herein. In some embodiments, chemical agents may provide selected properties to coated textile (e.g., fabric) including, but not limited to, an antimicrobial property, an antiodor property, a water repellant property, an oil repellant property, a coloring property, a flame retardant property, a fabric softening property, a pH adjusting property, an anticrocking property, an antipilling property, and/or an antifelting property. In some embodiments, chemical agents may include, but are not limited to, an antimicrobial agent, acidic agents (e.g., Bronsted acids, citric acid, acetic acid, etc.), a softener, a water repellant agent, an oil repellant agent, a dye, a flame retardant, a fabric softener, a pH adjusting agent (e.g., an acidic agent), an anticrocking agent, an antipilling agent, and/or an antifelting agent. Such chemical agents may include, but are not limited to, softeners (e.g., chemical fabric softeners), acidic agents, antimicrobials, dyes, finishing agents including monomers (e.g., melted polyester), and combinations thereof.

In some embodiments, SFS may be used in combination with a dye. In some embodiments, SFS may include a dye. In some embodiments, a dye may be applied to a fabric, yarn, textile, or garment to be coated prior to providing an SFS coating. In some embodiments, a dye may be applied to a fabric, yarn, textile, or garment after such fabric, yam, textile, or garment has been coated with an SFS coating. In some embodiments, a dye may be applied to a fabric, yarn, textile, or garment to be coated simultaneously with SFS coating the fabric, yarn, textile, or garment.

absorption rate, spreading speed, accumulative one-way transport, flame retardant properties, coloring properties, fabric softening properties, a pH adjusting property, an antifelting property, and overall moisture management capability.

In some embodiments, SFS may be used in an SFS coating, where such coating includes one or more chemical agents (e.g., a silicone). SFS may be provided in such an SFS coating at a concentration by weight (% w/w or % w/v) or by volume (v/v) of less than about 25%, or less than about 20%, or less than about 15%, or less than about 10%, or less than about 9%, or less than about 8%, or less than about 7%, or less than about 6%, or less than about 5%, or less than about 4%, or less than about 3%, or less than about 2%, or less than about 1%, or less than about 0.9%, or less than about 0.8%, or less than about 0.7%, or less than about 0.6%, or less than about 0.5%, or less than about 0.4%, or less than about 0.3%, or less than about 0.2%, or less than about 0.1%, or less than about 0.01%, or less than about 0.001%. In some embodiments, SFS may be provided in such an SFS coating at a concentration by weight (% w/w or % w/v) or by volume (v/v) of greater than about 25%, or greater than about 20%, or greater than about 15%, or greater than about 10%, or greater than about 9%, or greater than about 8% , or greater than about 7%, or greater than about 6%, or greater than about 5%, or greater than about 4%, or greater than about 3%, or greater than about 2%, or greater than about 1%, or greater than about 0.9%, or greater than about 0.8%, or greater than about 0.7%, or greater than about 0.6%, or greater than about 0.5%, or greater than about 0.4%, or greater than about 0.3%, or greater than about 0.2%, or greater than about 0.1%, or greater than about 0.01%, or greater than about 0.001%.

In some embodiments, chemical fabric softeners may include silicones as described herein.

In some embodiments, the chemical agents may include the following, which are supplied by CHT Bezema and are associated with certain selected textile (e.g., fabric) properties, which may be used to strengthen SFS binding on coated surfaces and/or SFS may be used for enhancing the following chemical agents' properties:

ALPAPRINT CLEAR

Silicone printing and coating Component B is mentioned in the technical leaflet Dry handle

Good rubbing fastness

Good washfastness

ALPAPRINT ELASTIC ADD

Silicone printing and coating

Component B is mentioned in the technical leaflet

Good rubbing fastness

Good washfastness

Suited for yardage printing

ALPAPRINT WHITE

Silicone printing and coating

Component B is mentioned in the technical leaflet

Dry handle

Good rubbing fastness

Good washfastness

ALPATEC 30142 A

Textile finishing

Coating

Silicone printing and coating

Component B is mentioned in the technical leaflet

Suitable for narrow ribbon coating

Good rubbing fastness

Good washfastness

ALPATEC 30143 A

Silicone printing and coating

Component B is mentioned in the technical leaflet

Good rubbing fastness

Good washfastness

Suited for yardage printing

ALPATEC 30191 A

Silicone printing and coating

Component B is mentioned in the technical leaflet

Suitable for narrow ribbon coating High transparency

Coating

ALPATEC 30203 A

Silicone printing and coating

Component B is mentioned in the technical leaflet

Suitable for narrow ribbon coating

High transparency

Coating

ALPATEC 3040 LSR KOMP. A

Functional coatings, Silicone printing and coating Component B is mentioned in the technical leaflet High abrasion resistance

High transparency

Coating

ALPATEC 3060 LSR KOMP. A

Functional coatings, Silicone printing and coating

Component B is mentioned in the technical leaflet

High abrasion resistance

High transparency

Coating

ALPATEC 530

Silicone printing and coating

Suitable for narrow ribbon coating

High transparency

Coating

One component system

ALPATEC 540

Silicone printing and coating

Suitable for narrow ribbon coating

High transparency

Coating

One component system

ALPATEC 545

Silicone printing and coating Suitable for narrow ribbon coating

High transparency

Coating

One component system

ALPATEC 550

Silicone printing and coating Suitable for narrow ribbon coating High transparency

Coating

One component system

ALPATEC 730

Silicone printing and coating

Suitable for narrow ribbon coating

Good washfastness

High abrasion resistance

High transparency

ALPATEC 740

Silicone printing and coating

Suitable for narrow ribbon coating Good washfastness

High abrasion resistance

High transparency

ALPATEC 745

Silicone printing and coating Suitable for narrow ribbon coating

Good washfastness

High abrasion resistance

High transparency

ALPATEC 750

Silicone printing and coating

Suitable for narrow ribbon coating

Good washfastness

High abrasion resistance

High transparency ALPATEC BANDAGE A

Silicone printing and coating

Component B is mentioned in the technical leaflet

Suitable for narrow ribbon coating

Coating

Two component system

APYROL BASE2 E

Flame retardants

Liquid

Soft handle

For BS 5852/ 1+2

Suited for paste coating

APYROL FCR-2

Water repellency / oil repellency

Cationic

High effectiveness

Water-based

Liquid

APYROL FFD E

Flame retardants

Liquid

Suited for polyester

Suited for polyamide

Flame inhibiting filler

APYROL FR CONC E

Flame retardants, Functional coatings

Liquid

Suited for polyester

Suited for polyamide

Flame inhibiting filler

APYROL GBO-E

Flame retardants, Functional coatings

Suited for polyester

Black-out coating For DIN 4102/ Bl

Containing halogen

APYROL LV 21

Flame retardants, Functional coatings

For DIN 4102/ Bl

Suited for paste coating

Suited for backcoating of black-out vertical blinds and roller blinds Containing halogen

APYROL PP 31

Flame retardants

Liquid

Free from antimony

Flame inhibiting filler

For BS 5852/ 1+2

APYROL PP 46

Flame retardants

Powder

Free from antimony

Flame inhibiting filler

Suited for paste coating

APYROL PREM E

Flame retardants

Soft handle

For BS 5852/ 1+2

Containing halogen

Semi-permanent

APYROL PREM2 E

Flame retardants

Soft handle

For BS 5852/ 1+2

Containing halogen

Semi-permanent

COLORDUR 005 WHITE

Flock adhesives, Functional coatings. Silicone printing and coating Based on silicone

Dyestuff pigment suspension

COLORDUR 105 LEMON

Flock adhesives, Functional coatings, Silicone printing and coating

Based on silicone

Dyestuff pigment suspension

COLORDUR 115 GOLDEN YELLOW

Flock adhesives, Functional coatings, Silicone printing and coating

Based on silicone

Dyestuff pigment suspension

COLORDUR 185 ORANGE

Flock adhesives, Functional coatings, Silicone printing and coating

Based on silicone

Dyestuff pigment suspension

COLORDUR 215 RED

Flock adhesives, Functional coatings, Silicone printing and coating

Based on silicone

Dyestuff pigment suspension

COLORDUR 225 DARK RED

Flock adhesives, Functional coatings, Silicone printing and coating

Based on silicone

Dyestuff pigment suspension

COLORDUR 285 VIOLET

Flock adhesives, Functional coatings, Silicone printing and coating

Based on silicone

Dyestuff pigment suspension

COLORDUR 305 BLUE

Flock adhesives, Functional coatings, Silicone printing and coating

Based on silicone

Dyestuff pigment suspension

COLORDUR 355 MARINE

Flock adhesives, Functional coatings, Silicone printing and coating

Based on silicone

Dyestuff pigment suspension COLORDUR 405 GREEN

Flock adhesives, Functional coatings, Silicone printing and coating

Based on silicone

Dyestuff pigment suspension

COLORDUR 465 OLIVE GREEN

Flock adhesives, Functional coatings, Silicone printing and coating

Based on silicone

Dyestuff pigment suspension

COLORDUR 705 BLACK

Flock adhesives, Functional coatings, Silicone printing and coating

Based on silicone

Dyestuff pigment suspension

COLORDUR AM ADDITIVE

Flock adhesives, Silicone printing and coating

Based on silicone

Migration prevention

Dyestuff pigment suspension

COLORDUR FL 1015 YELLOW

Flock adhesives, Functional coatings, Silicone printing and coating

Based on silicone

Dyestuff pigment suspension

COLORDUR FL 1815 ORANGE

Flock adhesives, Functional coatings, Silicone printing and coating

Based on silicone

Dyestuff pigment suspension

COLORDUR FL 2415 PINK

Flock adhesives, Functional coatings, Silicone printing and coating

Based on silicone

Dyestuff pigment suspension

COLORDUR FL 4015 GREEN

Flock adhesives, Functional coatings, Silicone printing and coating

Based on silicone

Dyestuff pigment suspension

ECOPERL 1 Water repellency / oil repellency

Washfast

Sprayable

Based on special functionalised polymers/waxes Cationic

ECOPERL ACTIVE

Water repellency / oil repellency

Washfast

Based on special functionalised polymers/waxes Cationic

High effectiveness

LAMETHAN 1 ET 25 BR 160

Functional coatings, Lamination

Washfast

Transparent

25 μηι strong

Film based on polyester urethane

LAMETHAN ADH-1

Functional coatings, Lamination

Breathable

Suited for dry laminating

Good stability to washing at 40 °C

Stable foam adhesive

LAMETHAN ADH-L

Functional coatings, Lamination

Washfast

Transparent

Suited for paste coating

Suited for wet laminating

LAMETHAN ALF-

Functional coatings, Lamination

Adhesive additive for bondings

Suited for dry laminating

Stable foam adhesive Suited for stable foam coating

LAMETHAN LB 15-T BR 152DK

Functional coatings, Lamination

Transparent

15 μηι strong

Breathable

Suited for dry laminating

LAMETHAN LB 25 BR 155

Functional coatings, Lamination

Transparent

25 μηι strong

Suited for dry laminating

Good stability to washing at 40 °C

LAMETHAN LB 25 W BR 152

Lamination

25 μιη strong

Breathable

Suited for dry laminating

Good stability to washing at 40 °C

LAMETHAN TAPE DE 80

Functional coatings, Lamination

Polymer base: polyurethane

Transparent

Good stability to washing at 40 °C

Tape for seam sealing

LAMETHAN TAPE ME 160

Functional coatings, Lamination

Polymer base: polyurethane

Transparent

Good stability' to washing at 40 °C

Tape for seam sealing

LAMETHAN VL-H920 O BR150

Functional coatings, Lamination

Two coats with membrane and PES charmeuse Breathable

Suited for dry laminating

Good stability to washing at 40 °C

LAMETHAN VL-H920 S BR 150

Functional coatings, Lamination

Two coats with membrane and PES charmeuse Breathable

Suited for dry laminating

Good stability to washing at 40 °C

LAMETHAN VL-H920 W BR150

Functional coatings, Lamination

Two coats with membrane and PES charmeuse

Breathable

Suited for dry laminating

Good stability to washing at 40 °C

TUBICOAT A 12 E

Binders, Functional coatings

Anionic

Liquid

Formaldehyde-free

Polymer base: polyacrylate

TUBICOAT A 17

Binders, Functional coatings

Suitable for tablecloth coating

Anionic

Liquid

Self-crosslinking

TUBICOAT A 19

Binders, Functional coatings

Washfast

Anionic

Formaldehyde-free

Good stability to washing

TUBICOAT A 22 Binders, Functional coatings

Washfast

Medium-hard film

Anionic

Liquid

TUBIJET NWA

Ink jet printing preparation TUBICOAT A 23

Binders

Medium-hard film

Anionic

Liquid

Application for varying the handl TUBICOAT A 28

Binders, Functional coatings

Anionic

Liquid

Formaldehyde-free

TUBIJET PUS

Ink jet printing preparation

Film forming

Good stability to washing TUBICOAT A 36

Binders, Functional coatings

Washfast

Anionic

Liquid

Low formaldehyde

TUBICOAT A 37

Binders, Functional coatings Washfast

Suitable for tablecloth coating

Anionic

Liquid TUBICOAT A 41

Binders, Functional coatings

Anionic

Liquid

Self-crosslinking

Good fastnesses

TUBICOAT A 61

Binders, Functional coatings

Suitable for tablecloth coating

Liquid

Non-ionic

Self-crosslinking

TUBICOAT A 94

Binders, Functional coatings

Anionic

Liquid

Self-crosslinking

Good fastnesses

TUBICOAT AIB 20

Fashion coatings

Transparent

Suited for foam coating

Pearl Gloss Finish

TUBICOAT AOS

Foaming auxiliaries

Non-ionic

Foaming

Suited for the fluorocarbon finishing TUBICOAT ASK

Functional coatings, Lamination

Adhesive additive for bondings

Transparent

Suited for paste coating

Suited for dry laminating TUBICOAT B-H

Binders, Functional coatings

Polymer base: Styrene butadiene

Anionic

Liquid

Formaldehyde-free

TUBIJET VDK

Inkjet printing preparation

TUBICOAT B 45

Binders, Functional coatings

Washfast

Polymer base: Styrene butadiene

Anionic

Liquid

TUBICOAT BO-NB

Functional coatings

Medium hard

Suited for black-out coating

Good flexibility at low temperatures Suited for stable foam coating

TUBICOAT BO-W

Functional coatings

Suited for black-out coating

Impermeable for light

Suited for stable foam coating

Water vapour permeable

TUBICOAT BOS

Foaming auxiliaries

Anionic

Foaming

Foam stabilizer

TUBICOAT DW-FI

Functional coatings, Special products Anionic Suited for coating pastes

Suited for stable foam

Foamable

TUBICOAT E 4

Binders

Anionic

Self-crosslinking

Low formaldehyde

Polymer base: polyethylene vinyl acetate TUBICOAT ELC

Functional coatings

Suited for paste coating

Black

Electrically conductive

Soft

TUBICOAT EMULGATOR HF

Functional coatings, Special products

Anionic

Dispersing

Suited for coating pastes

Suited for stable foam

TUBICOAT ENTSCHAUMER N

Defoamers and deaerators

Liquid

Non-ionic

Silicone-free

Suited for coating pastes

TUBICOAT FIX FC

Fixing agents

Cationic

Water-based

Liquid

Formaldehy de-free

TUBICOAT FIX ICB CONC. Fixing agents

Liquid

Non-ionic

Formaldehyde-free

Suited for crosslinking

TUBICOAT FIXIERER AZ

Fixing agents

Liquid

Suited for crosslinking

Based on polyaziridin

Unblocked

TUBICOAT FIXIERER FA

Fixing agents

Anionic

Water-based

Liquid

Low formaldehyde

TUBICOAT FIXIERER H 24

Fixing agents

Anionic

Water-based

Liquid

Formaldehyde-free

TUBICOAT FIXIERER HT

Fixing agents

Water-based

Liquid

Non-ionic

Suited for crosslinking

TUBICOAT FOAMER NY

Foaming auxiliaries

Non-ionic

Foaming

Suited for the fluorocarbon finishing Non-yellowing

TUBICOAT GC PU

Fashion coatings

Washfast

Soft handle

Polymer base: polyurethane Transparent

TUBICOAT GRIP

Functional coatings

Slip resistant

Suited for stable foam coating Soft

TUBICOAT HEC

Thickeners

Powder

Non-ionic

Stable to electrolytes Stable to shear forces TUBICOAT HOP-S

Special products

Anionic

Suited for coating pastes Coating

Adhesion promoter

TUBICOAT HS 8

Binders

Anionic

Liquid

Formaldehy de-free

Hard film

TUBICOAT HWS-1

Functional coatings

Suited for paste coating Water-proof Suited for giant umbrellas and tents

TUBICOAT KL-TOP F

Fashion coatings, Functional coatings

Washfast

Polymer base: polyurethane

Transparent

Suited for paste coating

TUBICOAT KLS-M

Fashion coatings, Functional coatings

Washfast

Soft handle

Polymer base: polyurethane

Breathable

TUBICOAT MAF

Fashion coatings

Washfast

Matrix effect

TUBIJET WET

Ink jet printing preparation

Without impact on Improves the rubbing fastnesses

Soft handle

TUBICOAT MD TC 70

Fashion coatings

Vintage wax

Suited for foam coating

Suited for topcoats

TUBICOAT MEA

Functional coatings

Washfast

Polymer base: polyurethane

Suited for paste coating

Suited for topcoat coatings

TUBICOAT MG-R

Fashion coatings Washfast

Soft handle

Suited for paste coating

Duo Leather Finish

TUBICOAT MOP NEU

Functional coatings. Special products

Washfast

Anionic

Foamable

Finish

TUBICOAT MP-D

Fashion coatings, Functional coatings

Washfast

Soft handle

Medium hard

Breathable

TUBICOAT MP-W

Functional coatings

Washfast

Polymer base: polyurethane

Breathable

Water-proof

TUBICOAT NTC-SG

Functional coatings

Washfast

Transparent

Suited for paste coating

Medium hard

TUBICOAT PERL A22-20

Fashion coatings

Suited for paste coating

Suited for foam coating

Pearl Gloss Finish

TUBICOAT PERL HS-1 Functional coatings

Suited for paste coating

Suited for black-out coating

Suited for pearlescent coating

Suited for topcoat coatings

TUBICOAT PERL PU SOFT

Fashion coatings

Washfast

Scarabaeus effect

Soft handle

Polymer base: polyurethane

TUBICOAT PERL VC CONC.

Fashion coatings, Functional coatings Soft handle

Polymer base: polyurethane

Suited for paste coating

Suited for black-out coating

TUBICOAT PHV

Functional coatings

Medium hard

Suited for three-dimensional dot coating TUBICOAT PSA 1731

Functional coatings, Lamination

Transparent

Suited for paste coating

Suited for dry laminating

Non-breathable

TUBICOAT PU-UV

Binders

Anionic

Liquid

Formaldehyde-free

Good fastnesses

TUBICOAT PU 60 Binders

Anionic

Liquid

Application for varying the handle

Formaldehyde-free

In some embodiments, the chemical agents of the invention may include the following inkjet printing dyes, which are supplied by CHT Bezema and are associated with certain selected textile (e.g., fabric) properties, which may be used in combination with SFS:

BEZAFLUOR BLUE BB

Pigments

High Performance

BEZAFLUOR (fluorescent pigments)

BEZAFLUOR GREEN BT

Pigments

High Performance

BEZAFLUOR (fluorescent pigments)

BEZAFLUOR ORANGE R

Pigments

High Performance

BEZAFLUOR (fluorescent pigments)

BEZAFLUOR PINK BB

Pigments

High Performance

BEZAFLUOR (fluorescent pigments)

BEZAFLUOR RED R

Pigments

High Performance

BEZAFLUOR (fluorescent pigments)

BEZAFLUOR VIOLET BR

Pigments

High Performance

BEZAFLUOR (fluorescent pigments) BEZAFLUOR YELLOW BA

Pigments

High Performance

BEZAFLUOR (fluorescent pigments) BEZAPRINT BLACK BDC

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT BLACK DT

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT BLACK DW

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT BLACK GOT

Pigments

High Performance

BEZAKTIV GOT (GOTS)

BEZAPRINT BLUE BN

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT BLUE BT

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT BLUE GOT

Pigments

High Performance

BEZAKTIV GOT (GOTS)

BEZAPRINT BLUE RR

Pigments Advanced

BEZAPRINT (classic pigments) BEZAPRINT BLUE RT

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT BLUE RTM

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT BLUE TB

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT BORDEAUX K2R

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT BROWN RP

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT BROWN TM

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT CITRON 10G

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT CITRON GOT

Pigments

High Performance

BEZAKTIV GOT (GOTS) BEZAPRINT GREEN 2B

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT GREEN BS

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT GREEN BT

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT GREY BB

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT NAVY GOT

Pigments

High Performance

BEZAKTIV GOT (GOTS) BEZAPRINT NAVY RRM

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT NAVY TR

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT OLIVE GREEN BT

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT ORANGE 2G

Pigments Advanced

BEZAPRINT (classic pigments) BEZAPRINT ORANGE GOT

Pigments

High Performance

BEZAKTIV GOT (GOTS) BEZAPRINT ORANGE GT

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT ORANGE RG

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT PINK BW

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT RED 2BN

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT RED GOT

Pigments

High Performance

BEZAKTIV GOT (GOTS) BEZAPRINT RED KF

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT RED KGC

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT SCARLET GRL

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT SCARLET RR

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT TURQUOISE GT

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT VIOLET FB

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT VIOLET KB

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT VIOLET R

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT VIOLET TN

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT YELLOW 2GN

Pigments

Advanced

BEZAPRINT (classic pigments) BEZAPRINT YELLOW 3GT

Pigments Advanced

BEZAPRINT (classic pigments)

BEZAPRINT YELLOW 4RM

Pigments

Advanced

BEZAPRINT (classic pigments)

BEZAPRINT YELLOW GOT

Pigments

High Performance

BEZAKTIV GOT (GOTS)

BEZAPRINT YELLOW RR

Pigments

Advanced

BEZAPRINT (classic pigments)

In some embodiments, the chemical agents of the invention may include the following, which are supplied by Lamberti SPA and are associated with certain selected textile (e.g., fabric) properties, which may be used to strengthen SFS binding on coated surfaces or SFS may be used for enhancing such chemical agent properties:

Pre treatment;

Waterborne Polyurethanes Dispersions

Rolflex AFP.

Aliphatic poly ether polyurethane dispersion in water. The product has high hydrolysis resistance, good breaking load resistance and excellent tear resistance.

Rolflex ACF.

Aliphatic polycarbonate polyurethane dispersion in water. The product shows good PU and PVC bonding properties, excellent abrasion resistance as well as chemical resistance, included alcohol.

Rolflex V 13.

Aliphatic poly ether/acrylic copolymer polyurethane dispersion in water. The product has good thermoadhesive properties and good adhesion properties on PVC. Rolflex K 80.

Aliphatic poly ether/acrylic copolymer polyurethane dispersion in water. ROLFLEX K 80 is specifically designed as a high performing adhesive for textile lamination. The product has excellent perchloroethylene and water fastness.

Rolflex ABC.

Aliphatic poly ether polyurethane dispersion in water. Particularly, the product presents very high water column, excellent electrolytes resistance, high LOI index, high resistance to multiple bending. Rolflex ADH.

Aliphatic poly ether polyurethane dispersion in water. The product has a very high water column resistance.

Rolflex W4.

Aliphatic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear where a full, soft and non sticky touch is required.

Rolflex ZB7.

Aliphatic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, sportswear, fashion and technical articles for industrial applications. The product has a very high charge digestion properties, electrolites stability and excellent mechanical and tear resistance. TUBICOAT PU 80

Binders, Functional coatings

Washfast

Anionic

Liquid

Can be washed off

TUBICOAT PUH-BI

Binders

Anionic

Liquid

Formaldehyde-free

Hard film

TUBICOAT PUL Functional coatings

Polymer base: polyurethane

Suited for paste coating

Rolflex BZ 78.

Aliphatic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, sportswear, fashion and technical articles for industrial applications. The product has an excellent hydrolysis resistance, a very high charge digestion and electrolites stability and an excellent mechanical and tear resistance. Can be also suitable for foam coating and printing application.

Rolflex PU 147.

Aliphatic poly ether polyurethane dispersion in water. This product shows good film forming properties at room temperature. It has high fastness to light and ultraviolet radiation and good resistance to water, solvent and chemical agents, as well as mechanical resistance.

Rolflex SG.

Aliphatic poly ether polyurethane dispersion in water. Due to its thermoplastic properties it is suggested to formulate heat activated adhesives at low temperatures.

Elafix PV 4.

Aliphatic blocked isocyanate Nano-dispersion used in order to give antifelting and antipilling properties to pure wool fabrics and his blend.

Rolflex C 86.

Aliphatic cationic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, fashion where medium-soft and pleasant full touch is required. Fabrics treated with the product can be dyed with a selection of dyes, to get double-color effects of different intensity. Rolflex CN 29.

Aliphatic cationic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, fashion where soft and pleasant full touch is required. Fabrics treated with the product can be dyed with a selection of dyes, to get double-color effects of different intensity.

Oil and water repellents

Lamgard FT 60.

General purpose fluorocarbon resin for water and oil repellency; by padding application.

Lamgard 48.

High performance fluorocarbon resin for water and oil repellency; by padding application. High rubbing fastness.

Imbitex NRW3

Wetting agent for water-and oil repellent finishing. Lamgard EXT.

Crosslinker for fluorocarbon resins to improve washing fastness. Flame retard ants

Piroflam 712.

Non-permanent flame retardant compound for padding and spray application.

Piroflam ECO.

Alogen free flame retardant compound for back coating application for all kind of fibers.

Piroflam UBC.

Flame retardant compound for back coating application for all kind of fibers.

Crosslinkers

Rolflex BK8.

Aromatic blocked polyisocyanate in water dispersion. It is suggested as a cross-linking agent in coating pastes based of polyurethane resins to improve washing fastness.

Fissativo 05.

Water dispersible aliphatic polyisocyanate suitable as crosslinking agent for acrylic and polyurethane dispersions to improve adhesion and wet and dry scrub resistance.

Resina MEL. Melammine-formaldheyde resin.

Cellofix VLF.

Low formaldehyde melamine resin.

Lambicol CL 60.

Fully neutralized synthetic thickener for pigment printing in oil/water emulsion; medium viscosity type

Viscolam PU cone.

Nonionic polyurethane based thickener with pseudoplastic behavior

Viscolam 115 new.

Acrylic thickener not neutralized

Viscolam PS 202.

Nonionic polyurethane based thickener with newtonian behavior Viscolam 1022.

Nonionic polyurethane based thickener with moderate pseudoplastic behavior.

Dyeing

Dispersing agents

Lamegal BO.

dispersing agent non ionic, suitable for direct, reactive, disperse dyeing and PES stripping

Lamegal DSP.

Dispersing / anti back-staining agent in preparation, dyeing and soaping of dyed and printed materials. Antioligomer agent. Lamegal 619.

Effective low foam dispersing leveling agent for dyeing of PES Lamegal TL5.

Multi-purpose sequestring and dispersing agent for all kind of textile process

Levelling agents

Lamegal A 12.

Leveling agent for dyeing on wool, polyamide and its blends with acid or metalcomplex dyes

Lamfix L. Fixing agent for direct and reactive dyestuffs, containing formal dheyde

Lamfix LU cone.

Formaldehyde free cationic fixing agent for direct and reactive dyes. It does not affect the shade and light fastness.

Lamfix PA/TR.

Fixing agent to improve the wet fastness of acid dyes on polyamide fabrics, dyed or printed and polyamide yarns. Retarding agent in dyeing of Polyamide/cellulosic blends with direct dyes.

Special resins

Denifast TC.

Special resin for cationization of cellulose fibers to obtain special effects ("DENIFAST system" and "DENISOL system").

Cobral DD/50.

Special resin for cationization of cellulose fibers to obtain special effect ("DENIFAST system" and "DENISOL system").

Antireducing agents

Lamberti Redox L2S gra.

Anti-reducing agent in grain form. 100% active content

Lamberti Redox L2S liq.

Anti-reducing agent in liquid form for automatic dosage.

Anticreasing agent

Lubisol AM.

Lubricating and anti creasing agent for rope wet operation on all kind of fibers and machines.

Pigment dye

Antimigrating agent

Neopat Compound 96/m cone.

Compound, developed as migration inhibitor for continuous dyeing process with pigments (pad-dry process).

Binding agent

Neopat Binder PM/S cone.

Concentrated version of a specific binder used to prepare pad- liquor for dyeing with pigments (pad-dry process). All in One agent

Neopat Compound PK1.

High concentrated compound specifically developed as migration inhibitor with specific binder for continuous dyeing process with pigments (pad-dry process)all in one

Delave agent

Neopat compound FTN.

High concentrated compound of surfactants and polymers specifically developed for pigment dyeing and pigment-reactive dyeing process; especially for medium/dark shades for wash off effect

Traditional finishing agents

Wrinkle free treatment

Cellofix ULF cone.

Anti-crease modified gly oxalic resin for finishing of cottons, cellulosics and blend with synthetics fibers.

Poliflex PO 40.

Polyethilenic resin for waxy, full and slippy handle by foulard applications.

Rolflex WF.

Aliphatic waterborned Nano-PU dispersion used as extender for wrinkle free treatments.

Softeners

Texamina C/FPN.

softening agent with a very soft handle particularly recommended for application by exhaustion for all kind of fabrics. Suitable also for cone application.

Texamina C SAL flakes.

100% cationic softening agent in flakes form for all type of fabrics. at room temperature.

Texamina CL LIQ.

Anphoteric softening agent for all types of fabrics. Not yellowing. Texamina HVO. Anphoteric softening agent for woven and knitted fabrics of cotton, other cellulosics and blends. Gives a soft, smooth and dry handle. Applied by padding.

Texamina SIL.

Nonionic silicon dispersion in water. Excellent softening, lubricating and anti-static properties for all fibre types by padding.

Texamina SILK.

Special cationic softener with silk protein inside. Gives a "swollen touch" particularly suitable for cellulosic, wool, silk. Lamfinish LW.

All-in compound based on special polymeric hydrophilic softeners; by coating, foulard, and exhaustion.

Elastolam E50.

General purpose mono-component silicone elastomeric softener for textile finishing.

Elastolam EC 100.

Modified polysiloxane micro-emulsion which gives a permanent finishing, with extremely soft and silky handle.

Handle modifier

Poliflex CSW.

anti-slipping agent.

Poliflex R 75.

Parafine finishing agent to give waxy handle.

Poliflex s.

Compound specifically developed for special writing effects.

Poliflex m.

Compound for special dry-waxy handle.

Lamsoft SW 24.

Compound for special slippy handle specifically developed for coating application.

Lamfinish SLIPPY.

All-in compound to get a slippy touch; by coating.

Lamfinish GUMMY.

All-in compound to get a gummy touch; by coating. Lamfinish OLDRY.

All-in compound to get dry-sandy touch especially suitable for vintage effects; by coating

Waterborne Polyurethanes Dispersions

Rolflex LB 2.

Aliphatic waterbomed PU dispersion particularly suggested for the formulation of textile coatings where bright and rigid top finish is required. It is particularly suitable as a finishing agent for organza touch on silk fabrics, and shiny.

RolflexSuited for three-dimensional dot coating

Slip resistant

TUBICOAT PUS

Binders, Functional coatings

Anionic

Liquid

Formaldehyde-free

Polymer base: polyurethane

TUBICOAT PUW-M

Binders

Medium-hard film

Anionic

Liquid

Formaldehyde-free

TUBICOAT PUW-S

Binders

Anionic

Liquid

Formaldehyde-free

Good stability to washing

TUBICOAT PW 14

Binders, Functional coatings

Anionic

Formaldehyde-free

Heat-sealable Not wetting

TUBICOAT SA-M

Functional coatings

Washfast

Suited for paste coating

Suited for three-dimensional dot coating TUBICOAT SCHAUMER HP

Foaming auxiliaries, Functional coatings

Non-ionic

Foaming

Suited for the fluorocarbon finishing TUBICOAT SF-BASE

Fashion coatings

Washfast

Soft handle

Suited for foam coating

Silk gloss effect

TUBICOAT SHM

Foaming auxiliaries

Anionic

Foam stabilizer

TUBICOAT SI 55

Special products

Pseudo-cationic

Suited for coating pastes

Foamable

Coating

TUBICOAT STABILISATOR RP

Foaming auxiliaries

Anionic

Foam stabilizer

TUBICOAT STC 100

Fashion coatings, Functional coatings

Transparent Breathable

Suited for stable foam coating TUBICOAT STC 150

Fashion coatings, Functional coatings

Washfast

Soft handle

Transparent

Breathable

TUBICOAT STL

Functional coatings

Washfast

Slip resistant

Suited for stable foam coating Soft

TUBICOAT TCT

Fashion coatings, Functional coatings Washfast

Polymer base: polyurethane

Transparent

Suited for paste coating

TUBICOAT V A 10

Binders

Anionic

Liquid

Formaldehy de-free

Hard film

TUBICOAT VCP

Functional coatings

Suited for paste coating

Medium hard

Suited for black-out coating

TUBICOAT VERDICKER 17

Thickeners

Anionic High efficiency

TUBICOAT VERDICKER ASD

Thickeners

Anionic

Quick swelling

Stable to shear forces

Pseudoplastic

TUBICOAT VERDICKER LP

Thickeners

Anionic

Stable to shear forces

Pseudoplastic

Dispersible

TUBICOAT VERDICKER PRA

Thickeners

Anionic

Liquid

Stable to electrolytes

Rheological additive

TUBICOAT WBH 36

Special products

Finish

Application for preventing roller deposit TUBICOAT WBV

Special products

Non-ionic

Finish

Application for preventing roller deposit TUBICOAT WEISS EU

Functional coatings, Special products Suited for coating pastes

Suited for stable foam

Suited for topcoat coatings

Titanium dioxide paste TUBICOAT WLI-LT KONZ

Functional coatings

Washfast

Suited for paste coating

Slip resistant

Soft

TUBICOAT WLI

Fashion coatings, Functional coating Washfast

Scarabaeus effect

Soft handle

Suited for paste coating

TUBICOAT WOT

Fashion coatings

Washfast

Soft handle

Suited for paste coating

Wash-out effect

TUBICOAT WX-TCA 70

Fashion coatings. Functional coating

Vintage wax

Suited for paste coating

Suited for topcoat coatings

TUBICOAT WX BASE

Fashion coatings

Vintage wax

Soft handle

Suited for paste coating

Application in the prime coat TUBICOAT ZP NEU

Water repellency / oil repellency Zircon-paraffine base

Suited for aqueous systems Cationic Foamable

Liquid

TUBIGUARD 21

Water repellency / oil repellency

Washfast

Cationic

High effectiveness

Water-based

TUBIGUARD 25-F

Water repellency / oil repellency

Washfast

Spray able

Cationic

High effectiveness

TUBIGUARD 270

Functional coatings, Water repellency / oil repellency

Washfast

Cationic

High effectiveness

Liquid

TUBIGUARD 30-F

Water repellency / oil repellency

Washfast

Spray able

Cationic

High effectiveness

TUBIGUARD 44 N

Water repellency / oil repellency

Washfast

Spray able

Suited for aqueous systems

Liquid

TUBIGUARD 44N-F

Water repellency / oil repellency Suited for aqueous systems

Non-ionic

Suited for polyester

Foamable

TUBIGUARD 66

Water repellency / oil repellency

Washfast

Spray able

High effectiveness

Liquid

TUBIGUARD 90-F

Water repellency / oil repellency

Washfast

Cationic

High effectiveness

Liquid

TUBIGUARD AN-F

Water repellency / oil repellency

Washfast

Sprayable

Cationic

High effectiveness

TUBIGUARD FA2-F

Water repellency / oil repellency

Sprayable

Cationic

Suited for polyester

Foamable

TUBIGUARD PC3-F

Functional coatings. Water repellency / oil repellency

Washfast

Cationic

Liquid

Paste TUBIGUARD SR 2010-F W

Water repellency / oil repellency

Cationic

High effectiveness

Foamable

Based on C6 fluorocarbon

TUBIGUARD 10-F

Water repellency / oil repellency

Washfast

Spray able

CationicAliphatic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for outwear, luggage, technical articles especially where hard and flexible touch is required, and shiny.

Rolflex PU 879.

Aliphatic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for outwear, luggage, technical articles where a medium-hard and flexible touch is required. Rolflex ALM.

Aliphatic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for outwear, luggage, technical articles where a soft and flexible touch is required. Can be also suitable for printing application.

Rolflex AP.

Aliphatic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for outwear, fashion where a soft and gummy touch is required.

Rolflex W4.

Aliphatic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear where a full, soft and non sticky touch is required.

Rolflex ZB7.

Aliphatic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, sportswear, fashion and technical articles for industrial applications. The product has a very high charge digestion properties, electrolites stability and excellent mechanical and tear resistance. Can be also suitable for foam coating and printing application.

Rolflex BZ 78.

Aliphatic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, sportswear, fashion and technical articles for industrial applications. The product has an excellent hydrolysis resistance, a very high charge digestion and electrolites stability and an excellent mechanical and tear resistance. Can be also suitable for foam coating and printing application.

Rolflex K 110.

Gives to the coated fabric a full, soft, and slightly sticky handle with excellent fastness on all types of fabrics.

Rolflex OP 80.

Aliphatic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for outwear, luggage and fashion finishes where an opaque non writing effect is desired.

Rolflex NBC.

Aliphatic waterbomed PU dispersion generally used by padding application as a filling and zero formaldheyde sizing agent. Can be used for outwear and fashion finishings where a full, elastic and non sticky touch is required.

Rolflex PAD.

Aliphatic waterbomed PU dispersion specifically designed for padding application for outwear, sportswear and fashion applications where a full, elastic and non sticky touch is required. Excellent washing and dry cleaning fastness as well as good bath stability.

Rolflex PN.

Aliphatic waterbomed PU dispersion generally applied by padding application for outerwear and fashion high quality applications where strong, elastic non sticky finishes are required. Elafix PV 4.

Aliphatic blocked isocyanate Nano-dispersion used in order to give antifelting and antipilling properties to pure wool fabrics and his blend.

Rolflex SW3.

Aliphatic waterbomed PU dispersion particularly suggested to be used by padding application for the finishing of outwear, sportswear and fashion where a slippery and elastic touch is required. It is also a good antipilling agent. Excellent in wool application.

Rolflex C 86.

Aliphatic cationic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, fashion where medium-soft and pleasant full touch is required. Fabrics treated with the product can be dyed with a selection of dyes, to get double-color effects of different intensity. Rolflex CN 29.

Aliphatic cationic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, fashion where soft and pleasant full touch is required. Fabrics treated with the product can be dyed with a selection of dyes, to get double-color effects of different intensity.

resins

Textol 110.

Handle modifier with very soft handle for coating finishes Textol RGD.

Water emulsion of acrylic copolymer for textile coating, with very rigid handle.

Textol SB 21.

Butadienic resin for finishing and binder for textile printing Appretto PV/CC.

Vinylacetate water dispersion for rigid stiffening

Amisolo B.

CMS water dispersion for textile finishing as stiffening agent Lamovil RP.

PVOH stabilized solution as stiffening agent

Technical finishing agents

Waterborne Polyurethanes Dispersions

Rolflex AFP.

Aliphatic poly ether polyurethane dispersion in water. The product has high hydrolysis resistance, good breaking load resistance and excellent tear resistance.

Rolflex ACF.

Aliphatic polycarbonate polyurethane dispersion in water. The product shows good PU and PVC bonding properties, excellent abrasion resistance as well as chemical resistance, included alcohol.

Rolflex V 13.

Aliphatic polyether/acrylic copolymer polyurethane dispersion in water. The product has good thermoadhesive properties and good adhesion properties on PVC.

Rolflex K 80.

Aliphatic polyether/acrylic copolymer polyurethane dispersion in water. ROLFLEX K 80 is specifically designed as a high performing adhesive for textile lamination. The product has excellent perchloroethylene and water fastness.

Rolflex ABC.

Aliphatic poly ether polyurethane dispersion in water. Particularly, the product presents very high water column, excellent electrolytes resistance, high LOI index, high resistance to multiple bending. Rolflex ADH.

Aliphatic poly ether polyurethane dispersion in water. The product has a very high water column resistance.

Rolflex W4.

Aliphatic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear where a full, soft and non sticky touch is required.

Rolflex ZB7. Aliphatic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, sportswear, fashion and technical articles for industrial applications. The product has a very high charge digestion properties, electrolites stability and excellent mechanical and tear resistance. Can be also suitable for foam coating and printing application.

Rolflex BZ 78.

Aliphatic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, sportswear, fashion and technical articles for industrial applications. The product has an excellent hydrolysis resistance, a very high charge digestion and electrolites stability and an excellent mechanical and tear resistance. Can be also suitable for foam coating and printing application.

Rolflex PU 147.

Aliphatic poly ether polyurethane dispersion in water. This product shows good film forming properties at room temperature. It has high fastness to light and ultraviolet radiation and good resistance to water, solvent and chemical agents, as well as mechanical resistance.

Rolflex SG.

Aliphatic poly ether polyurethane dispersion in water. Due to its thermoplastic properties it is suggested to formulate heat activated adhesives at low temperatures.

Elafix PV 4.

Aliphatic blocked isocyanate Nano-dispersion used in order to give antifelting and antipilling properties to pure wool fabrics and his blend.

Rolflex C 86.

Aliphatic cationic waterbomed PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, fashion where medium-soft and pleasant full touch is required. Fabrics treated with the product can be dyed with a selection of dyes, to get double-color effects of different intensity. Rolflex CN 29.

Aliphatic cationic waterborned PU dispersion particularly suggested for the formulation of textile coatings for clothing, outwear, fashion where soft and pleasant full touch is required. Fabrics treated with the product can be dyed with a selection of dyes, to get double-color effects of different intensity.

Oil and water repellents

Lamgard FT 60.

General purpose fluorocarbon resin for water and oil repellency; by padding application.

Lamgard 48.

High performance fluorocarbon resin for water and oil repellency; by padding application. High rubbing fastness.

Imbitex NRW3.

Wetting agent for water-and oil repellent finishing. Lamgard EXT.

Crosslinker for fluorocarbon resins to improve washing fastness. Flame retard ants

Piroflam 712.

Non-permanent flame retardant compound for padding and spray application.

Piroflam ECO.

Alogen free flame retardant compound for back coating application for all kind of fibers.

Piroflam UBC.

Flame retardant compound for back coating application for all kind of fibers.

Crosslinkers

Rolflex BK8.

Aromatic blocked polyisocyanate in water dispersion. It is suggested as a cross-linking agent in coating pastes based of polyurethane resins to improve washing fastness.

Fissativo 05. Water dispersible aliphatic polyisocyanate suitable as crosslinking agent for acrylic and polyurethane dispersions to improve adhesion and wet and dry scrub resistance.

Resina MEL.

Melammine-formaldheyde resin.

Cellofix VLF.

Low formaldehyde melamine resin.

Thickeners

Lambicol CL 60.

Fully neutralized synthetic thickener for pigment printing in oil/water emulsion; medium viscosity type

Viscolam PU cone.

Nonionic polyurethane based thickener with pseudoplastic behavior

Viscolam 115 new.

Acrylic thickener not neutralized

Viscolam PS 202.

Nonionic polyurethane based thickener with newtonian behavior Viscolam 1022.

Nonionic polyurethane based thickener with moderate

pseudoplastic behavior.

In some embodiments, the chemical agent may include one or more of a silicone, an acidic agent, a dyeing agent, a pigment dye, a traditional finishing agent, and a technical finishing agent. The dyeing agent may include one or more of a dispersing agent, a levelling agent, a fixing agent, a special resin, an antireducing agent, and an anticreasing agent. The pigment dye may include one or more of an antimigrating agent, a binding agent, an all in one agent, and a delave agent. The traditional finishing agent may include one or more of a wrinkle free treatment, a softener, a handle modifier, a waterborne polyurethanes dispersion, and other resins. The technical finishing agent may include one or more of a waterborne polyurethanes dispersion, an oil repellant, a water repellant, a crosslinker, and a thickener.

In some embodiments, certain chemical agents of the invention may be provided by one or more of the following chemical suppliers: Adrasa, AcHitex Minerva, Akkim, Archroma, Asutex, Avocet dyes, BCC India, Bozzetto group, CHT, Clearity, Dilube, Dystar, Eksoy, Erca group, Genkim, Giovannelli e Figli, Graf Chemie, Huntsman, KDN Bio, Lamberti, LJ Specialties, Marlateks, Montegauno, Protex, Pulcra Chemicals, Ran Chemicals, Fratelli Ricci, Ronkimya, Sarex, Setas, Silitex, Soko Chimica, Tanatex Chemicals, Zaitex, Zetaesseti, and Z Schimmer.

In some embodiments, the chemical agent may include an acidic agent. Accordingly, in some embodiments, SFS may include an acidic agent. In some embodiments, an acidic agent may be a Bronsted acid. In an embodiment, the acidic agent includes one or more of citric acid and acetic acid. In an embodiment, the acidic agent aids the deposition and coating of SPF mixtures (i.e., SFS coating) on the textile to be coated as compared to the absence of such acidic agent. In an embodiment, the acidic agent improves crystallization of the SPF mixtures at the textile to be coated.

In an embodiment, the acidic agent is added at a concentration by weight (% w/w or % w/v) or by volume (v/v) of greater than about 0.001% , or greater than about 0.002%, or greater than about 0.003%, or greater than about 0.004%, or greater than about 0.005%, or greater than about 0.006%, or greater than about 0.007%, or greater than about 0.008%, or greater than about 0.009%, or greater than about 0.01%, or greater than about 0.02%, or greater than about 0.03%, or greater than about 0.04%, or greater than about 0.05%, or greater than about 0.06%, or greater than about 0.07%, or greater than about 0.08%, or greater than about 0.09%, or greater than about 0.1%, or greater than about 0.2%, or greater than about 0.3%, or greater than about 0.4%, or greater than about 0.5%, or greater than about 0.6%, or greater than about 0.7%, or greater than about 0.8%, or greater than about 0.9%, or greater than about 1.0% or greater than about 2.0%, or greater than about 3.0%, or greater than about 4.0%, or greater than about 5.0%.

In an embodiment, the acidic agent is added at a concentration by weight (% w/w or % w/v) or by volume (v/v) of less than about 0.001% , or less than about 0.002%, or less than about 0.003%, or less than about 0.004%, or less than about 0.005%, or less than about 0.006%, or less than about 0.007%, or less than about 0.008%, or less than about 0.009%, or less than about 0.01%, or less than about 0.02%, or less than about 0.03%, or less than about 0.04%, or less than about 0.05%, or less than about 0.06%, or less than about 0.07%, or less than about 0.08%, or less than about 0.09%, or less than about 0.1%, or less than about 0.2%, or less than about 0.3%, or less than about 0.4%, or less than about 0.5%, or less than about 0.6%, or less than about 0.7%, or less than about 0.8%, or less than about 0.9%, or less than about 1.0% or less than about 2.0%, or less than about 3.0%, or less than about 4.0%, or less than about 5.0%.

In an embodiment, the chemical agent may include silicone. In some embodiments, a SFS may include silicone. In some embodiments, silicone may include a silicone emulsion. The term "silicone," may generally refer to a broad family of synthetic polymers, mixtures of polymers, and/or emulsions thereof, that have a repeating silicon-oxygen backbone including, but not limited to, polysiloxanes. For example, a silicone may include ULTRATEX® CSP, which is a commercially available (Huntsman International LLC) silicone emulsion that may be used as a softening agent and which may also increase fabric resilience, elasticity of knitted fabrics, and fiber lubrication and also improve sewability. A silicone may also include ULTRATEX® CI, which is a commercially available silicone composition (Huntsman International LLC) that may be used as a fabric softening agent. In some embodiments, a silicone may include any silicone species disclosed herein.

Describing the compositions and coatings more broadly, silicone may be used, for example to improve fabric hand, but may also increase the water repellency (or reduce water transport properties) of a fabric coated with silicone. Silicone may be used in combination with SFS to counteract the water repellant (water transport) properties of silicone.

In some embodiments, SFS may include silicone in a concentration by weight (% w/w or % w/v) or by volume (v/v) of less than about 25%, or less than about 20%, or less than about 15%, or less than about 10%, or less than about 9%, or less than about 8%, or less than about 7%, or less than about 6%, or less than about 5%, or less than about 4%, or less than about 3%, or less than about 2%, or less than about 1%, or less than about 0.9%, or less than about 0.8%, or less than about 0.7%, or less than about 0.6%, or less than about 0.5%, or less than about 0.4%, or less than about 0.3%, or less than about 0.2%, or less than about 0.1%, or less than about 0.01%, or less than about 0.001%.

In some embodiments, SFS may include silicone in a concentration by weight

(% w/w or % w/v) or by volume (v/v) of greater than about 25%, or greater than about 20%, or greater than about 15%, or greater than about 10%, or greater than about 9%, or greater than about 8% , or greater than about 7%, or greater than about 6%, or greater than about 5%, or greater than about 4%, or greater than about 3%, or greater than about 2%, or greater than about 1%, or greater than about 0.9%, or greater than about 0.8%, or greater than about 0.7%, or greater than about 0.6%, or greater than about 0.5%, or greater than about 0.4%, or greater than about 0.3%, or greater than about 0.2%, or greater than about 0.1%, or greater than about 0.01%, or greater than about 0.001%.

In some embodiments, SFS may be supplied in a concentrated form suspended in water. In some embodiments, SFS may have a pH of less than about 9, or less than about 8. In some embodiments, SFS may have a concentration by weight (% w/w or % w/v) or by volume (v/v) of less than about 50%, or less than about 45%, or less than about 40%, or less than about 35%, or less than about 30%, or less than about 25%, or less than about 20%, or less than about 15%, or less than about 10%, or less than about 5%, or less than about 4%, or less than about 3%, or less than about 2%, or less than about 1%, or less than about 0.1%, or less than about 0.01%, or less than about 0.001%, or less than about 0.0001%, or less than about 0.00001%. In some embodiments, SFS may have a concentration by weight (% w/w or % w/v) or by volume (v/v) of greater than about 50%, or greater than about 45%, or greater than about 40%, or greater than about 35%, or greater than about 30%, or greater than about 25%, or greater than about 20%, or greater than about 15%, or greater than about 10%, or greater than about 5%, or greater than about 4%, or greater than about 3%, or greater than about 2%, or greater than about 1%, or greater than about 0.1%, or greater than about 0.01%, or greater than about 0.001%, or greater than about 0.0001%, or greater than about 0.00001%.

In some embodiments, SFS may include an acidic agent, and may have a pH of less than about 9, or less than about 8.5, or less than about 8, or less than about 7.5, or less than about 7, or less than about 6.5, or less than about 6, or less than about 5.5, or less than about 5, or less than about 4.5, or less than about 4, or greater than about 3.5, or greater than about 4, or greater than about 4.5, or greater than about 5, or greater than about 5.5, or greater than about 6, or greater than about 6.5, or greater than about 7, or greater than about 7.5, or greater than about 8, or greater than about 8.5.

In some embodiments, an SFS coating may include SFS, as described herein. In some embodiments, SFS may include a silicone and/or an acidic agent. In some embodiments, SFS may include a silicone and an acidic agent. In some embodiments, the SFS may include a silicone, an acidic agent, and/or an additional chemical agent, wherein the additional chemical agent may be one or more of the chemical agents described herein. In some embodiments, SFS may include a silicone emulsion and an acidic agent, such as acetic acid or citric acid.

In some embodiments, the coating processes of the invention may include a finishing step for the resulting coated textiles. In some embodiments, the finishing or final finishing of the textiles (e.g., fabrics) that are coated with SFS under the processes of the invention may include sueding, steaming, brushing, polishing, compacting, raising, tigering, shearing, heatsetting, waxing, air jet, calendaring, pressing, shrinking, treatment with polymerizer, coating, lamination, and/or laser etching. In some embodiments, finishing of the SFS coated textiles may include treatment of the textiles with an AIRO® 24 dryer that may be used for continuous and open-width tumbling treatments of woven, non-woven, and knitted fabrics.

In some embodiments, a coated textile (e.g., a fabric) may be prepared by unrolling a fabric roll (FIG. 185) to prepare a piece of fabric. The perimeter of such fabric may be processed. For example, fabric (FIG. 186) may have dimensions of 35 cm x 35 cm (13.5 inch x 13.5 inch) with a tolerance of +/- 1 cm (+/- 0.4 inch). In some embodiments, every fabric sample may be massed on analytical balance by folding the fabric sample multiple times until it may be contained by a weighing boat on a balance. Each measurement may be recorded. In some embodiments, a coating process may be initiated by preparing a curing oven by setting a selected temperature therein. A padder laboratory unit may be turned on and the speed of said padder unit may be set to a selected velocity and the roller pressure may be adjusted to a selected pressure by operating a cam lever system and locking it in place once the desired pressure is achieved. A silk solution (i.e., SFS) may be poured into a bath (e.g., a stainless steel bath) (FIG. 187). After a fabric sample is submerged in the bath, it may be allowed to reach saturation, and the fabric sample may then be removed from the bath and laid between two rollers of the padder unit (FIG. 188). The fabric sample as it is transported through the rollers it may be squeezed of excessive fluid as determined by the rollers' pressure. The fabric sample may then exit to the opposite side of the rollers. The resulting fabric sample may then be placed on top of the curing frame and may then be gently pushed one edge at a time to engage the fabric edges with frame pins (see FIGS. 189 and 190). The frame may be placed in the drying and curing oven, with the door of said oven secured and kept closed for the drying and curing time (FIG. 191). A timer may be started to alert when the drying and curing time has elapsed. When the timer signals completion of the curing process, the oven door is opened and a temperature sensor (e.g., an IR temperature sensor) may be used to measure the fabric sample surface temperature. The frame bearing the fabric sample may then be removed from the oven and placed on a cooling rack (FIG. 192). The sample fabric may then be removed from the frame and weighed.

In some embodiments, the SFS coated textiles (e.g., fabrics) described herein may meet or exceed requirements established by the following Test Methods:

Test Description Test Method Requirements

Dimensional Stability to AATCC 135 Maximum, Length: -3%, Width: -3% Laundering

Maximum, Length: -3%, Width: -5%, for two way

Stretch Fabrics

Maximum, Length: -5%, Width: -5%, for fourway

Stretch Fabrics

No Growth

Dimensional Stability to AATCC 158 Maximum, Length: -3%, Width: -3% Dry Cleaning

Maximum, Length: -3%, Width: -5%, for two way

Stretch Fabrics

Maximum, Length: -5%, Width: -5%, for fourway

Stretch Fabrics

No Growth

Pilling Resistance ASTM D 3512 Minimum 3.0 Abrasion Resistance ASTM D 4966 No rupture to 10,000 cycles (plain fabrics up to 7.5 oz/yd 2 ; or no rupture to 15,000 cycles (plain fabrics over 7.5 oz/yd 2 )

Tearing Strength ASTM D 1424 Shorts, Pants, Jeans, Jackets, All Plus

Size Styles: 2.5 Lbs Minimum; or Blouse, Skirt Dress, Lining, excluding plus size styles: 1.5 Lbs Minimum; or

Intimate:

<3 oz/yd 2 : Minimum 1.5 lbs 3-6 oz/yd 2 : Minimum 2.0 lbs >6 oz/yd 2 : Minimum 2.5 lbs

Colorfastness to AATCC 61, 2A Color Change: Minimum 4.0

Laundering/Colorfastness Staining: Minimum 3.0

to Washing

Colorfastness to Dry AATCC 132 Color Change: Minimum 4.0 Cleaning Staining: Minimum 3.0

Colorfastness to AATCC 8 All except below - Dry: Minimum

Crocking/ Colorfastness 4.0; Wet: Minimum 3.0; or to Rubbing

Dark Shades (black, red, navy) - Dry: Minimum 4.0; Wet: Minimum 2.5; or

Indigos - Dry: Minimum 3.0; Wet: Minimum 2.0; or

Pigments - Dry: Minimum 3.5; Wet: Minimum 2.5.

Colorfastness to Water AATCC 107 Color Change: Minimum 4.0;

Staining: Minimum 3.0

Colorfastness to AATCC 15 Color Change: Minimum 4.0; Perspiration Staining: Minimum 3

Colorfastness to Light AATCC 16/20 Color Change: Minimum 4.0

AFU

AATCC 16/5

AFU pH Value AATCC 81 4.0 ~ 8.5 or 4.0-7.5 (children < 36 months)

Antimicrobial AATCC 147 Original: 0% Bacterial Growth 20

Washes: 0% Bacterial Growth

Minimum 99.9% Reduction

AATCC 100

Original: Minimum 99.9% Reduction ASTM E 2149 20 Washes: Minimum 80%

Reduction Wicking AATCC 79 1.0 second or less

Water Repellency - Spray AATCC 22 Original: 100 Rating

Test After 3x Washes: Minimum 70

Rating

Water Resistance - Rain AATCC 35 Maximum 1 gram on original and Test after 3 x washes

Dimensional Stability to AATCC 150 Maximum, Length= - 3%, Width= -

Laundering (Yoga 3%

Garment)

Maximum, Length : -3%, Width= - 5% for two-way

Stretch Fabrics

Maximum, Length : -5%, Width= - 5% for four- way

Stretch fabrics

No Distortion Between Components No Growth

Dimensional Stability to AATCC 158 Maximum, Length= -3%, Width= -

Dry Cleaning (Yoga 3%

Garment)

Maximum, Length= -3%, Width= - 5%, for two-way Stretch Fabrics

Maximum, Length= -5%, Width= - 5%, for four-way

Stretch Fabrics

No Distortion Between Components No Growth

Pilling Resistance (Yoga ASM D 3512 Minimum 3.0

Garment)

Colorfastness to AATCC 61. 2A Color Change Minimum 4.0

Laundering/Colorfastness Staining: Minimum 3.0

to Washing (Yoga

Garment)

Colorfastness AATCC 8 General: Dry: Minimum 4.0 ;

Crocking/ Colorfastness Minimum 3.0;

to Rubbing (Yoga

Garment) For Dark Colors (Black, Red, Navy):

Wet: Minimum 2.5

Pigment: Dry: Minimum 3.5 ; Wet: Minimum 2.5

Indigos: Dry: Minimum 3.0; Wet: Minimum 2.0

Colorfastness to Water AATCC 107 Color Change: Minimum 4.0

(Yoga Garment) Staining: Minimum 3.0

Colorfastness to AATCC 15 Color Change: 4.0 or better

Perspiration (Yoga Staining: 3.0 or better

Garment)

Colorfastness to Light AATCC 16, 20 Minimum 4.0, All, Except Silk/ (Yoga Garment) AFU/5 AFU Minimum 4.0, Silk

pH Value (Yoga AATCC 81 Children (>36 months) & Adults: 4.0 Garment) ~ 8.5

Children (< 36 months): 4.0 ~ 7.5

In some embodiments, the SFS coated textiles (e.g., fabrics) described herein may meet requirements established by the foregoing Test Methods. In some embodiments, the SFS coated textiles (e.g., fabrics) described herein may exceed the requirements established by the foregoing Test Methods.

In some embodiments, the SFS coated textiles (e.g., fabrics) may have antiodor activity due to the SFS coating.

In some embodiments, the SFS coated textiles (e.g., fabrics) may have antimicrobial activity (e.g., antifungal and/or antibacterial activity) due to the SFS coating. In an embodiment, antibacterial activity may be determined by the ability of bacteria on the SFS coated textile's surface to be washed away from the SFS coated textile surface following one or more wash cycles, or two or more wash cycles, or three or more wash cycles, or four or more wash cycles, or five or more wash cycles, where the bacteria do not adhere to the surface of the SFS coated textile. In an embodiment, antibacterial activity may be determined by the ability of the SFS coating to reduce the quantity of the bacteria deposited on a surface of the SFS coated textile, wherein the SFS coating may reduce the quantity of the bacteria by greater than about 1%, or greater than about 2%, or greater than about 3%, or greater than about 4%, or greater than about 5%, or greater than about 10%, or greater than about 20%, or greater than about 30%, or greater than about 40%, or greater than about 50%, or greater than about 60%, or greater than about 70%, or greater than about 80%, or greater than about 90%, or greater than about 95%, or greater than about 96%, or greater than about 97%, or greater than about 98%, or greater than about 99%, or by about 100%. In an embodiment, antibacterial activity of the SFS coating on the coated textile may be determined by fluorescent activity (see, e.g., U.S. Patent Nos. 5,089,395 and 5,968,762, the entirety of which are incorporated herein by reference). In an embodiment, antibacterial activity for an SFS coating may be determined by the ability of the SFS coating on a coated textile to break up colonies of bacteria that may be deposited on a surface of the coated textile. In an embodiment, antibacterial activity for an SFS coating may be determined by the ability of the SFS coating on a coated textile to: (a) prevent the formation of a bacterial biofilm on the coated textile; and/or (b) reduce the size of a bacterial biofilm on the coated textile.

In some embodiments, SFS may be coated upon a textile or other material having antimicrobial (e.g., antibacterial and/or antifungal) properties without interfering with such properties or otherwise inhibiting such properties.

In an embodiment, a textile may be coated with SFS to provide an SFS coated article. In some embodiments, the textile may include one or more of polyester, polyamide, polyaramid, polytetrafluoroethylene, polyethylene, polypropylene, polyurethane, silicone, mixtures of polyurethane and poly ethylenegly col, ultrahigh molecular weight polyethylene, high-performance polyethylene, nylon, and LYCRA (polyester-polyurethane copolymer, also known as SPANDEX and elastomer). In some embodiments, the textile may include LYCRA.

In some embodiments, the SFS coated article may have a crocking value of greater than 4 as determined by AATCC 8. In some embodiments, the SFS coated article may have a crocking value of greater than 4 as determined by AATCC 8, wherein the SFS coated article includes one or more of a silicone and an acidic agent. In some embodiments, the SFS coated article may have a crocking value of greater than 4 as determined by AATCC 8, wherein the SFS coated article includes a silicone. In some embodiments, the SFS coated article may have an overall moisture management capability (OMMC) of greater than 0.3. In some embodiments, the SFS coated article may have an overall moisture management capability (OMMC) of greater than 0.3, wherein the SFS coated article includes one or more of a silicone and an acidic agent. In some embodiments, the SFS coated article may have an overall moisture management capability (OMMC) of greater than 0.3, wherein the SFS coated article includes a silicone.

In some embodiments, the SFS coated article may contain no sites for bacterial adhesion. In some embodiments, the SFS coated article may contain no sites for bacterial adhesion after heat treatment. In some embodiments, the SFS coated article may contain no sites for bacterial adhesion following a wash cycle with non- chlorinated bleach. In some embodiments, the SFS coated article may contain no bacteria after washing.

EXAMPLES

The following examples are put forth so as to provide those of ordinary skill in the art with a complete disclosure and description of how to make and use the described embodiments, and are not intended to limit the scope of what the inventors regard as their invention nor are they intended to represent that the experiments below are all or the only experiments performed. Efforts have been made to ensure accuracy with respect to numbers used (e.g., amounts, temperature, etc.) but some experimental errors and deviations should be accounted for. Unless indicated otherwise, parts are parts by weight, molecular weight is weight average molecular weight, temperature is in degrees Centigrade, and pressure is at or near atmospheric.

Materials and Methods

A) Silk Molecular Weight Determination

The following equipment and material are used in determination of Silk Molecular weight: Agilent 1100 with chemstation software ver. 10.01 ; Refractive Index Detector (RID); analytical balance; volumetric flasks (1000 mL, 10 mL and 5 mL); HPLC grade water; ACS grade sodium chloride; ACS grade sodium phosphate dibasic heptahydrate; phosphoric acid; dextran MW Standards-Nominal Molecular Weights of 5 kDa, 11.6 kDa, 23.8 kDa, 48.6 kDa, and 148 kDa; 50 mL PET or polypropylene disposable centrifuge tubes; graduated pipettes; amber glass HPLC vials with Teflon caps; Phenomenex PolySep GFC P-4000 column (size: 7.8 mm x 300 mm).

PROCEDURE:

I) Preparation of 1 L Mobile Phase (0.1 M Sodium Chloride solution in 0.0125 M Sodium phosphate buffer)

Take a 250 mL clean and dry beaker, place it on the balance and tare the weight. Add about 3.3509 g of sodium phosphate dibasic heptahydrate to the beaker. Note down the exact weight of sodium phosphate dibasic weighed. Dissolve the weighed sodium phosphate by adding 100 mL of HPLC water into the beaker. Take care not to spill any of the content of the beaker. Transfer the solution carefully into a clean and dry 1000 mL volumetric flask. Rinse the beaker and transfer the rinse into the volumetric flask. Repeat the rinse 4-5 times. In a separate clean and dry 250 mL beaker weigh exactly about 5.8440 g of sodium chloride. Dissolve the weighed sodium chloride in 50 mL of water and transfer the solution to the sodium phosphate solution in the volumetric flask. Rinse the beaker and transfer the rinse into the volumetric flask. Adjust the pH of the solution to 7.0 ± 0.2 with phosphoric acid. Make up the volume in volumetric flask with HPLC water to 1000 mL and shake it vigorously to homogeneously mix the solution. Filter the solution through 0.45 μηι polyamide membrane filter. Transfer the solution to a clean and dry solvent bottle and label the bottle. The volume of the solution can be varied to the requirement by correspondingly varying the amount of sodium phosphate dibasic heptahydrate and sodium chloride.

II) Preparation of Dextran Molecular Weight Standard solutions

At least five different molecular weight standards are used for each batch of samples that are run so that the expected value of the sample to be tested is bracketed by the value of the standard used. Label six 20 mL scintillation glass vials respective to the molecular weight standards. Weigh accurately about 5 mg of each of dextran molecular weight standards and record the weights. Dissolve the dextran molecular weight standards in 5 mL of mobile phase to make a 1 mg/mL standard solution.

III) Preparation of Sample solutions

When preparing sample solutions, if there are limitations on how much sample is available, the preparations may be scaled as long as the ratios are maintained. Depending on sample type and silk protein content in sample weigh enough sample in a 50 mL disposable centrifuge tube on an analytical balance to make a 1 mg/mL sample solution for analysis. Dissolve the sample in equivalent volume of mobile phase make a 1 mg/mL solution. Tightly cap the tubes and mix the samples (in solution). Leave the sample solution for 30 minutes at room temperature. Gently mix the sample solution again for 1 minute and centrifuge at 4000 RPM for 10 minutes.

IV) HPLC analysis of the samples

Transfer 1.0 mL of all the standards and sample solutions into individual HPLC vials. Inject the molecular weight standards (one injection each) and each sample in duplicate. Analyze all the standards and sample solutions using the following HPLC conditions:

Column Poly Sep GFC P-4000 (7.8 x 300 mm)

Column Temperature 25 °C

Detector Refractive Index Detector (Temperature @ 35 °C)

Injection Volume 25.0

Mobile Phase 0.1 M Sodium Chloride solution in 0.0125 M sodium phosphate buffer

Flow Rate 1.0 mL/min

Run Time 20.0 min

V) Data analysis and calculations - Calculation of Average Molecular Weight using Cirrus Software

Upload the chromatography data files of the standards and the analytical samples into Cirrus SEC data collection and molecular weight analysis software. Calculate the weight average molecular weight (M w ), number average molecular weight (Mn), peak average molecular weight (M p ), and polydispersity for each injection of the sample. Average the results for duplicate injections for each sample (Table 1).

Table 1 : Exemplary Medium and Low Molecular Weight Values, and Polydispersity Values

21 1 19328 41512

("Mid") 19391 41761 2.15

2 19454 42010

22 1 19529 42245

("Mid") 19550 42447 2.17

2 19570 42649

23 1 19732 43015

("Mid") 19678 42706 2.17

2 19624 42396

24 1 19686 42838

("Mid") 19802 42862 2.16

2 19918 42886

25 1 19689 42608

("Mid") 19696 42850 2.18

2 19703 43092

26 1 14303 40498

("Mid") 14923 40640 2.73

2 15543 40782

27 1 14654 38546

("Mid") 14582 38558 2.64

2 14509 38569

28 1 14303 35937

("Mid") 14242 35847 2.52

2 14180 35756

29 1 3318 10508

3427 10939 3.19

("Low") 2 3536 11369

30 1 3616 8340

3647 8450 2.32

("Low") 2 3678 8559

31 1 4709 13104

("Low") 4778 13297 2.78

2 4846 13489

32 1 4237 12232

("Low") 4506 13042 2.89

2 4774 13851

33 1 4696 12754

("Low") 4783 12986 2.71

2 4870 13217

B) Wool Coating

Wool raw material:

Tube A: 100% wool tubular fabric made with NeW 1/42.8 with 18.9 μηι wool fibers (4 inches diameter tubes by 14 inches long supplied by MSC) non superwashed supplied by Kentwool in Greenville SC;

Tube B: 100% wool tubular fabric made with NeW 1/30 with 21.0 μιη Australian wool fibers (4 inches diameter tubes by 14 inches long supplied by MSC) non superwashed supplied by Kentwool in Greenville SC;

Tube C: 100% wool tubular fabric made with NeW 27/1 with 23.0 μιη

Australian wool fibers (4 inches diameter tubes by 14 inches long supplied by MSC) superwashed supplied by Kentwool in Greenville SC; Tube D: 100% wool tubular fabric made with NeW 60/2 with 18.5 μηι Australian wool fibers (4 inches diameter tubes by 14 inches long supplied by MSC) superwashed supplied by Kentwool in Greenville SC.

Equipment:

- Werner Mathis MA0881 padder/coater;

Curing frame 13x13 inches;

Across International oven FO-19140;

Magnetic stirrer hot plate JoanLab SH-2;

Stirrer bar;

- Large tweezers;

- Balance Veritas M314-AI;

Universal plastic PH test strip;

Glassware.

Processes (by number of processing steps):

- 4 steps process: pre-treatment, silk treatment, post treatment, and final treatment;

3 steps process: pre-treatment, silk treatment, and post treatment;

2 steps process: pre-treatment, and silk treatment;

1 step process: silk treatment.

Processing steps and sub-steps:

- Wool tubes A, B, C, and D are massed before any processing (see Table 2 for wool samples cross-reference numbers);

Control samples of each fabric A, B, C, and D are not processed;

A pretreatment bath at 20: 1 ratio liquor to fabric with tap water with 5% citric acid to a pH of 3-4 is maintained at a temperature of 70 °C with a hot plate and is recirculated with a stirrer bar. The silk tube fabrics (N=4) are immersed for 60 minutes;

The wool tube fabrics are removed from the bath and are padded at 50 pressure on the padder and 3 m/min followed by a 10 min drying cycle at 80 °C in the oven;

The dried wool tube fabrics are immersed in the same pretreatment bath after the addition of 0.375% low MW and 0.125% medium MW silk solutions based on the liquor volume resulting in a pH of 4-5 and is maintained at 70 °C with a hot plate for 30 minutes with liquor recirculating through a stirrer bar;

The wool tube fabrics are removed from the bath and are padded at 20 pressure setting and 3 m/min followed by a 10 min drying cycle at 80 °C in the oven; - The dried wool tube fabrics are immersed in a new bath with 20: 1 ratio liquor to fabric with tap water and 0.25% citric acid to a pH of 3-4 at room temperature. The silk tube fabrics are immersed for 3 minutes;

The wool tube fabrics are removed from the bath and are padded at 50 pressure setting and 3 m/min followed by a 10 min drying cycle at 80 °C in the oven; - The dried wool tube fabrics are immersed in a new 100 ml bath with 80% methanol and 20% deionized water at room temperature for 10 minutes;

The wool tube fabrics are removed from the bath and are padded at 50 pressure setting and 3 m/min followed by a 10 min drying cycle at 80 °C in the oven.

Table 2: Wool Samples Cross-reference

1706020

wool tube 17042001 NeW 1/27 with 23.5 micron, 80% methanol 2

1706020

wool tube 17042002 NeW 2/60 with 18.5 micron, 0.2% citric acid 3

1706020

wool tube 17042002 NeW 2/60 with 18.5 micron, 80% methanol 4

3L1M: 3: 1 low MW silk to medium MW silk

C) Synthetic Materials Coating Method

The following equipment and material are used in coating experiments: medium molecular weight silk fragments solution at 6%; low molecular weight silk fragments solution at 6%; citric acid; Ultratex CSP (Huntsman); M Dohmen Domosil RWAF; Ultratex SI (Huntsman); permanent marker; fabric style # 6606D2 nylon/spandex; fabric style # 6608D2B polyester/spandex.

The coating processing includes two separate coating steps. Each coating step may be followed by a drying step.

First Coating Step: the total liquor solution prepared and individual ingredient quantities are prepared. The sequence for mixing includes: loading tap water in a mixing tank; adding citric acid 50% in water, followed by mixing for 2-3 minutes; measuring and confirming that the pH is between 4-5; adding low molecular weight silk solution to the mixing tank, and mixing for 1-2 minutes; adding medium molecular weight silk solution to the mixing tank, and mixing for 1-2 minutes; transferring the liquor to the pad bath; processing the fabric with a pick-up rate of 35-70%, with a drying time as required by the fabric material and construction.

Second Coating Step: the total liquor solution prepared and individual ingredient quantities are prepared. The sequence for mixing includes: loading tap water in the mixing tank; adding citric acid 50% in water, and mixing for 2-3 minutes; measuring and confirming that the pH is between 4-5; adding silicone solution to the liquor, and mixing for 2-3 minutes; transferring the liquor to the pad bath; fabrics processed with the first coating step are processed through the frame; fabric is processed with a pick- up rate of 35-70% with a drying time as required by the fabric material and construction.

Example 1 : Silk coating wool, including a citric acid pretreatment and methanol post treatment - water drop tested and hand evaluated This experiment includes application of silk fibroin solution on wool fabrics after a pretreatment of citric acid and followed by a methanol bath (variables described in Table 3). The application takes place in a sequence of baths and pads application with multiple drying steps.

Table 3: Coating Experimental Variables

0.375% low

Tube C MW + 80%

0.250%

NeW 1/27 0.125% methanol,

citric acid

23 μηι medium 20% di

N/A for 10 min N/A Australian MW 0.200% water for 10

at room

wool citric acid min at room

temp

for 30 min at temp

70 C

Tube D

NeW 2/60

176 (80) for 18.5 μηι N/A N/A N/A N/A

10 min Australian

wool

0.375% low

Tube D MW + 80%

0.250%

NeW 2/60 0.200% 0.125% methanol,

citric acid

18.5 μηι citric acid medium 20% di 176 (80) for for 10 min

Australian for 60 min MW 0.200% water for 10 10 min at room

wool at 70 °C citric acid min at room

temp

for 30 min at temp

70 C

0.375% low

Tube D MW +

0.250%

NeW 2/60 0.200% 0.125%

citric acid

18.5 μηι citric acid medium 176 (80) for for 10 min N/A

Australian for 60 min MW 0.200% 10 min at room

wool at 70 °C citric acid

temp

for 30 min at

70 C

0.375% low

Tube D MW + 80%

NeW 2/60 0.200% 0.125% methanol,

18.5 μηι citric acid medium 20% di 176 (80) for

N/A

Australian for 60 min MW 0.200% water for 10 10 min wool at 70 °C citric acid min at room

for 30 min at temp

70 C

0.3711%

Tube D low m +

NeW 2/60 0.200% 0.125%

18.5 μηι citric acid medium 176 (80) for

N/A N/A

Australian for 60 min MW 0.200% 10 min wool at 70 °C citric acid

for 30 min at

70 C 0.375% low

Tube D MW + 80%

0.250%

NeW 2/60 0.125% methanol,

citric acid

18.5 μηι medium 20% di

N/A for 10 min N/A Australian MW 0.200% water for 10

at room

wool citric acid min at room

temp

for 30 min at temp

70 C

Tube D

NeW 2/60

176 (80) for 18.5 μηι N/A N/A N/A N/A

10 min Australian

wool

Water drop test (Table 4) and hand evaluation (Tables 5 and 6) are used to characterize the fabrics, as follows:

Samples are conditioned at ambient condition for 24 hrs;

A 7 cm diameter round metal hoop is inserted in the wool fabric tube and is placed on the drapability jig. A RODI water drop is dispensed with an eye dropper from approximately 3 cm above the fabric. A video imaging recording capture the time from the water drop contacting the fabric until its full absorption or up to 30 seconds;

- The wool fabric tubes are scored for hand against a non treated control. Scoring are made from more softest to rougher and any additional perceived difference.

Table 4: Water Drop Test

Sample # Description Average test test test

1 2 3

17042105 NeW 2/60 18.5 micron, pre-treatment, silk 30 30 30 30 coating, post treatment, final treatment

17042106 NeW 1/27 23.5 micron pre-treatment, silk 30 30 30 30 coating, post treatment, final treatment

17042107 NeW 2/60 18.5 micron, pre-treatment, silk 30 30 30 30 coating, final treatment

17042108 NeW 1/27 23.5 micron pre-treatment, silk 30 30 30 30 coating, final treatment

17042401 NeW 1/27 23.5 micron silk coating, post 30 30 30 30 treatment, final treatment

17042402 NeW 2/60 18.5 micron, silk coating, post 30 30 30 30 treatment, final treatment

17042404 NeW 2/60 18.5 micron, water only 30 30 30 30

Table 5 : Hand Scores for Softness

Table 6: Hand Scores Identified Perceived Cool/Wet Feeling

Sample #2 Description Score 17042105 NeW 2/60 18.5 micron, pre-treatment, silk coating, post treatment, 5 final treatment

17042102 NeW 2/60 18.5 micron, pre-treatment, silk coating, post treatment 5

17042402 NeW 2/60 18.5 micron, silk coating, post treatment, final 5 treatment

17042107 NeW 2/60 18.5 micron, pre-treatment, silk coating, final treatment 4

17042106 NeW 1/27 23.5 micron pre-treatment, silk coating, post treatment, 1 final treatment

Example 2: Silk coating wool, including a citric acid pretreatment and methanol post treatment - tested for dimensional changes after laundering, perceived hand, and fiber morphology by SEM analysis

Silk fibroin solution is applied on wool fabrics after a pretreatment of citric acid and, followed by a methanol bath (Table 7). The application takes place in a sequence of baths and pads application with multiple drying steps. The samples are tested for dimensional changes after laundering, perceived hand, and fiber morphology with SEM analysis (Tables 8-11).

Table 7: Coating Experimental Variables

Dry /cure

Pre Post Final

Wool type Silk coating temperature treatment treatment treatment

0.375% low

mw + 80%

0.250%

NeW 1/27 0.200% 0.125% methanol,

citric acid

23 μηι citric acid medium mw 20% di 176 (80) for for 10 min

Australian for 60 min 0.200% water for 10 10 min at room

wool at 70 °C citric acid min at room

temp

for 30 min temp

at 70 °C

0.375% low

mw + 80%

0.250%

NeW 2/60 0.200% 0.125% methanol,

citric acid

18.5 μηι citric acid medium mw 20% di 176 (80) for for 10 min

Australian for 60 min 0.200% water for 10 10 min at room

wool at 70 °C citric acid min at room

temp

for 30 min temp

at 70 °C

Samples are conditioned at ambient condition for 24 hrs before a massing post coating. The percentage change is calculated based on the following formula:

mass post coating— mass before coating

Mass change % = ;— x 100 mass before coating

Samples are delivered to the MSC lab for dimensional changes post laundering analysis based on Woolmark Company TM31-May 2000 and AATCC Test Method 135-2015. Samples are tested after t=l and t=4 laundering cycle for the Woolmark test and at t=0 and t=3 for the AATCC test.

After the dimensional analysis test, the wool fabric tubes are scored for hand against a non-treated control. Scoring are made for softness and any additional perceived difference. After the hand test is completed the samples are subjected to SEM analysis.

Table 8: Processing recording and mass percentage change post treatment sample 17051001

17051001

Table 9: Processing recording and mass percentage change post treatment sample 17051002

Table 10: Processing recording and mass percentage change post treatment sample 17051003

Table 11 : Processing recording and mass percentage change

post treatment sample 17051101

The following tables (Tables 12 to 36) include testing data for assessing the dimensional stability to laundering using the Woolmark method (Woolmark test method: Washing of Wool Textile Products - The Woolmark Company TM31-May 2000, incorporated by reference herein in its entirety), and the AATCC method (Dimensional Changes of Fabrics after Home Laundering - AATCC Test Method 135- 2015, incorporated by reference herein in its entirety). Unless specified otherwise, the sample type is knitted fabric, the sample form is tube, and the sample color is greige.

Testing Information: Home Laundered, times using AATCC TM 150 Table II; Laundry Test Conditions: load size = 1.8 kg (4 lbs); Launder Right Side Out; Top Loading Machine Wash (2) Delicate, using 66±1 g 1993 AATCC Standard Reference Detergent WOB; (A)Tumble Dry ii Delicate; Ballast Wash Load Type 3 - 50/50 polyester/cotton bleached plain weave; (-) indicates shrinkage and (+) indicates growth; fabrics were not hand ironed or restored; evaluation conditions: 21 °C (± 2 °C) and 65% RH (± 5% RH). Table 12: Reference TS 131863 / 17051001 Coated

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.0cm 20.1 cm 6.4cm 6.3 cm

After IX wash 17.9cm 17.7cm 6.3cm 6.3 cm shrinkage/ growth -2.1 cm -2.4cm -0.1 cm 0.0cm

Dimensional

-10.5% -11.9% -1.6% 0.0% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.0cm 20.1 cm 6.4cm 6.3 cm

After 2X wash 17.1 cm 17.2cm 6.4cm 6.4cm shrinkage/ growth -2.9 cm -2.9cm 0.0cm 0.1 cm

Dimensional

-14.5% -14.4% 0.0% 1.6% Change

After IX wash 17.9cm 17.7cm 6.3cm 6.3 cm

After 2X wash 17.1 cm 17.2cm 6.4cm 6.4cm shrinkage/ growth -0.8 cm -0.5 cm 0.1 cm 0.1 cm

Dimensional

-4.5% -2.8% 1.6% 1.6% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.0cm 20.1 cm 6.4cm 6.3 cm

After 3X wash 16.2cm 16.6cm 6.2cm 6.3 cm shrinkage/ growth -3.8cm -3.5cm -0.2cm 0.0cm

Dimensional

-19.0% -17.4% -3.1% 0.0% Change

After IX wash 17.9cm 17.7cm 6.3cm 6.3 cm

After 3X wash 16.2cm 16.6cm 6.2cm 6.3 cm shrinkage/ growth -1.7cm -1.1 cm -0.1 cm 0.0cm

Dimensional

-9.5% -6.2% -1.6% 0.0% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.0cm 20.1 cm 6.4cm 6.3 cm

After 4X wash 15.1 cm 15.7cm 6.2cm 6.1 cm shrinkage/ growth -4.9 cm -4.4cm -0.2cm -0.2cm

Dimensional

-24.5% -21.9% -3.1% -3.2% Change

After IX wash 17.9cm 17.7cm 6.3cm 6.3 cm

After 4X wash 15.1 cm 15.7cm 6.2cm 6.1 cm shrinkage/ growth -2.8 cm -2.0cm -0.1 cm -0.2cm Dimensional

-15.6% -11.3% -1.6% -3.2% Change

Table 13: Reference 131864 / 17051002 Coated

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 19.6cm 19.7cm 5.6cm 6.3 cm

After IX wash 17.9cm 18.2cm 5.6cm 6.4cm shrinkage/ growth -1.7cm -1.5cm 0.0 cm 0.1 cm

Dimensional

-8.7% -7.6% 0.0% 1.6% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 19.6cm 19.7cm 5.6cm 6.3 cm

After 2X wash 17.4cm 17.4cm 5.7cm 6.3 cm shrinkage/ growth -2.2cm -2.3 cm 0.1 cm 0.0cm

Dimensional

-11.2% -11.7% 1.8% 0.0% Change

After IX wash 17.9cm 18.2cm 5.6cm 6.4cm

After 2X wash 17.4cm 17.4cm 5.7cm 6.3 cm shrinkage/ growth -0.5 cm -0.8cm 0.1 cm -0.1 cm

Dimensional

-2.8% -4.4% 1.8% -1.6% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 19.6cm 19.7cm 5.6cm 6.3 cm

After 3X wash 16.9cm 16.9cm 5.7cm 6.3 cm shrinkage/ growth -2.7 cm -2.8 cm 0.1 cm 0.0cm

Dimensional

-13.8% -14.2% 1.8% 0.0% Change

After IX wash 17.9cm 18.2cm 5.6cm 6.4cm

After 3X wash 16.9cm 16.9cm 5.7cm 6.3 cm shrinkage/ growth -1.0cm -1.3cm 0.1 cm -0.1 cm

Dimensional

-5.6% -7.1% 1.8% -1.6% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 19.6cm 19.7cm 5.6cm 6.3 cm

After 4X wash 16.7cm 16.5cm 5.7cm 6.2cm shrinkage/ growth -2.9cm -3.2cm 0.1 cm -0.1 cm Dimensional

-14.8% -16.2% 1.8% -1.6% Change

After IX wash 17.9cm 18.2cm 5.6cm 6.4cm

After 4X wash 16.7cm 16.5cm 5.7cm 6.2cm shrinkage/ growth -1.2cm -1.7cm 0.1 cm -0.2cm

Dimensional

-6.7% -9.3% 1.8% -3.1% Change

Table 14: Reference 131865 / 17051003 Coated

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.2cm 20.2 cm 6.2 cm 5.7 cm

After IX wash 18.9cm 19.3 cm 6.2 cm 5.6cm shrinkage/ growth -1.3 cm -0.9 cm 0.0 cm -0.1 cm

Dimensional

-6.4% -4.5% 0.0% -1.8% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.2cm 20.2 cm 6.2 cm 5.7 cm

After 2X wash 19.2cm 19.2 cm 6.1 cm 5.7 cm shrinkage/ growth -1.0cm -1.0cm -0.1 cm 0.0cm

Dimensional

-5.0% -5.0% -1.6% 0.0% Change

After IX wash 18.9cm 19.3 cm 6.2 cm 5.6cm

After 2X wash 19.2cm 19.2 cm 6.1 cm 5.7 cm shrinkage/ growth 0.3 cm -0.1 cm -0.1 cm 0.1 cm

Dimensional

1.6% -0.5% -1.6% 1.8% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.2cm 20.2 cm 6.2 cm 5.7 cm

After 3X wash 18.9cm 19.1 cm 6.0 cm 5.6cm shrinkage/ growth -1.3 cm -1.1 cm -0.2cm -0.1 cm

Dimensional

-6.4% -5.4% -3.2% -1.8% Change

After IX wash 18.9cm 19.3 cm 6.2 cm 5.6cm

After 3X wash 18.9cm 19.1 cm 6.0 cm 5.6cm shrinkage/ growth 0.0 cm -0.2 cm -0.2cm 0.0cm

Dimensional

0.0% -1.0% -3.2% 0.0% Change Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.2cm 20.2 cm 6.2 cm 5.7 cm

After 4X wash 18.9cm 19.4 cm 6.0 cm 5.7 cm shrinkage/ growth -1.3 cm -0.8 cm -0.2cm 0.0cm

Dimensional

-6.4% -4.0% -3.2% 0.0% Change

After IX wash 18.9cm 19.3 cm 6.2 cm 5.6cm

After 4X wash 18.9cm 19.4 cm 6.0 cm 5.7 cm shrinkage/ growth 0.0 cm 0.1 cm -0.2cm 0.1 cm

Dimensional

0.0% 0.5% -3.2% 1.8% Change

Table 15: Reference 131866 / 17051101 Coated

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.1 cm 19.8cm 5.9cm 5.9cm

After IX wash 18.9cm 18.9cm 5.8cm 6.0 cm shrinkage/ growth -1.2cm -0.9cm -0.1 cm 0.1 cm

Dimensional

-6.0% -4.5% -1.7% 1.7% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.1 cm 19.8cm 5.9cm 5.9cm

After 2X wash 18.9cm 18.7cm 5.9cm 5.8cm shrinkage/ growth -1.2cm -1.1 cm 0.0cm -0.1 cm

Dimensional

-6.0% -5.6% 0.0% -1.7% Change

After IX wash 18.9cm 18.9cm 5.8cm 6.0cm

After 2X wash 18.9cm 18.7cm 5.9cm 5.8cm shrinkage/ growth 0.0cm -0.2cm 0.1 cm -0.2cm

Dimensional

0.0% -1.1% 1.7% -3.3% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.1 cm 19.8cm 5.9cm 5.9cm

After 3X wash 18.9cm 18.7cm 5.8cm 5.9cm shrinkage/ growth -1.2cm -1.1 cm -0.1 cm 0.0cm

Dimensional

-6.0% -5.6% -1.7% 0.0% Change

After IX wash 18.9cm 18.9cm 5.8cm 6.0cm

After 3X wash 18.9cm 18.7cm 5.8cm 5.9cm shrinkage/ growth 0.0cm -0.2cm 0.0cm -0.1 cm

Dimensional

0.0% -1.1% 0.0% -1.7% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.1 cm 19.8cm 5.9cm 5.9cm

After 4X wash 18.9cm 18.9cm 5.7cm 5.7cm shrinkage/ growth -1.2cm -0.9cm -0.2cm -0.2cm

Dimensional

-6.0% -4.5% -3.4% -3.4% Change

After IX wash 18.9cm 18.9cm 5.8cm 6.0cm

After 4X wash 18.9cm 18.9cm 5.7cm 5.7cm shrinkage/ growth 0.0cm 0.0 cm -0.1 cm -0.3 cm

Dimensional

0.0% 0.0% -1.7% -5.0% Change

Table 16: Reference 131867 / 17042001 Control

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.2cm 20.4cm 7.5cm 7.0cm

After IX wash 20.0cm 20.4cm 6.5cm 5.8cm shrinkage/ growth -0.2cm 0.0 cm -1.0cm -1.2cm

Dimensional

-1.0% 0.0% -13.3% -17.1% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.2cm 20.4cm 7.5cm 7.0cm

After 2X wash 20.2cm 20.2cm 6.2cm 5.7cm shrinkage/ growth 0.0cm -0.2cm -1.3cm -1.3cm

Dimensional

0.0% -1.0% -17.3% -18.6% Change

After IX wash 20.0cm 20.4cm 6.5cm 5.8cm

After 2X wash 20.2cm 20.2cm 6.2cm 5.7cm shrinkage/ growth 0.2cm -0.2cm -0.3 cm -0.1 cm

Dimensional

1.0% -1.0% -4.6% -1.7% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.2cm 20.4cm 7.5cm 7.0cm

After 3X wash 20.2cm 20.0cm 6.1 cm 5.6cm shrinkage/ growth 0.0cm -0.4cm -1.4cm -1.4cm

Dimensional

0.0% -2.0% -18.7% -20.0% Change After IX wash 20.0cm 20.4cm 6.5cm 5.8cm

After 3X wash 20.2cm 20.0cm 6.1 cm 5.6cm shrinkage/ growth 0.2cm -0.4cm -0.4cm -0.2cm

Dimensional

1.0% -2.0% -6.2% -3.4% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.2cm 20.4cm 7.5cm 7.0cm

After 4X wash 20.1 cm 20.1 cm 6.4cm 5.7cm shrinkage/ growth -0.1 cm -0.3 cm -1.1 cm -1.3cm

Dimensional

-0.5% -1.5% -14.7% -18.6% Change

After IX wash 20.0cm 20.4cm 6.5cm 5.8cm

After 4X wash 20.1 cm 20.1 cm 6.4cm 5.7cm shrinkage/ growth 0.1 cm -0.3 cm -0.1 cm -0.1 cm

Dimensional

0.5% -1.5% -1.5% -1.7% Change

Note: Sample was torqued after wash

Table 17: Reference 131868 / 17042002 Control

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.0cm 19.9cm 7.0cm 6.1 cm

After IX wash 20.9cm 20.7 cm 6.0cm 5.4cm shrinkage/ growth 0.9cm 0.8 cm -1.0cm -0.7cm

Dimensional

4.5% 4.0% -14.3% -11.5% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.0cm 19.9cm 7.0cm 6.1 cm

After 2X wash 21.0cm 21.2cm 5.9cm 5.2cm shrinkage/ growth 1.0cm 1.3cm -1.1 cm -0.9cm

Dimensional

5.0% 6.5% -15.7% -14.8% Change

After IX wash 20.9cm 20.7 cm 6.0cm 5.4cm

After 2X wash 21.0cm 21.2cm 5.9cm 5.2cm shrinkage/ growth 0.1 cm 0.5 cm -0.1 cm -0.2cm

Dimensional

0.5% 2.4% -1.7% -3.7% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.0cm 19.9cm 7.0cm 6.1 cm After 3X wash 21.1 cm 20.7 cm 5.9cm 5.1 cm shrinkage/ growth 1.1 cm 0.8 cm -1.1 cm -1.0cm

Dimensional

5.5% 4.0% -15.7% -16.4% Change

After IX wash 20.9cm 20.7 cm 6.0cm 5.4cm

After 3X wash 21.1 cm 20.7 cm 5.9cm 5.1 cm shrinkage/ growth 0.2cm 0.0 cm -0.1 cm -0.3cm

Dimensional

1.0% 0.0% -1.7% -5.6% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.0cm 19.9cm 7.0cm 6.1 cm

After 4X wash 21.1 cm 20.7 cm 5.9cm 5.4cm shrinkage/ growth 1.1 cm 0.8 cm -1.1 cm -0.7cm

Dimensional

5.5% 4.0% -15.7% -11.5% Change

After IX wash 20.9cm 20.7 cm 6.0cm 5.4cm

After 4X wash 21.1 cm 20.7 cm 5.9cm 5.4cm shrinkage/ growth 0.2cm 0.0 cm -0.1 cm 0.0cm

Dimensional

1.0% 0.0% -1.7% 0.0% Change

Note: Sample was torqued after wash

Table 18: Reference 131869 / 17050901 Control

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.1 cm 20.9cm 6.5 cm 6.2cm

After IX wash 17.5cm 19.9cm 5.9cm 5.4cm shrinkage/ growth -2.6cm -1.0cm -0.6cm -0.8cm

Dimensional

-12.9% -4.8% -9.2% -12.9% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.1 cm 20.9cm 6.5 cm 6.2cm

After 2X wash 18.1 cm 19.7cm 5.5cm 5.4cm shrinkage/ growth -2.0cm -1.2cm -1.0cm -0.8cm

Dimensional

-10.0% -5.7% -15.4% -12.9% Change

After IX wash 17.5cm 19.9cm 5.9cm 5.4cm

After 2X wash 18.1 cm 19.7cm 5.5cm 5.4cm shrinkage/ growth 0.6cm -0.2cm -0.4cm 0.0cm

Dimensional

3.4% -1.0% -6.8% 0.0% Change Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.1 cm 20.9cm 6.5 cm 6.2cm

After 3X wash 17.2cm 18.5cm 5.4cm 5.2cm shrinkage/ growth -2.9cm -2.4 cm -1.1 cm -1.0cm

Dimensional

-14.4% -11.5% -16.9% -16.1% Change

After IX wash 17.5cm 19.9cm 5.9cm 5.4cm

After 3X wash 17.2cm 18.5cm 5.4cm 5.2cm shrinkage/ growth -0.3 cm -1.4cm -0.5cm -0.2cm

Dimensional

-1.7% -7.0% -8.5% -3.7% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.1 cm 20.9cm 6.5 cm 6.2cm

After 4X wash 16.8cm 17.4cm 5.1 cm 5.2cm shrinkage/ growth -3.3cm -3.5cm -1.4cm -1.0cm

Dimensional

-16.4% -16.7% -21.5% -16.1% Change

After IX wash 17.5cm 19.9cm 5.9cm 5.4cm

After 4X wash 16.8cm 17.4cm 5.1 cm 5.2cm shrinkage/ growth -0.7cm -2.5 cm -0.8cm -0.2cm

Dimensional

-4.0% -12.6% -13.6% -3.7% Change

Note: Sample was torqued and wrinkled after wash

Table 19: Reference 131870 / 17050902 Control

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.4cm 20.5 cm 6.5 cm 6.2cm

After IX wash 19.0cm 20.0cm 5.2cm 5.4cm shrinkage/ growth -1.4cm -0.5 cm -1.3cm -0.8cm

Dimensional

-6.9% -2.4% -20.0% -12.9% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.4cm 20.5 cm 6.5 cm 6.2cm

After 2X wash 18.4cm 20.2cm 5.3cm 5.1 cm shrinkage/ growth -2.0cm -0.3 cm -1.2cm -1.1 cm

Dimensional

-9.8% -1.5% -18.5% -17.7% Change

After IX wash 19.0cm 20.0cm 5.2cm 5.4cm After 2X wash 18.4cm 20.2cm 5.3cm 5.1 cm shrinkage/ growth -0.6cm 0.2cm 0.1 cm -0.3cm

Dimensional

-3.2% 1.0% 1.9% -5.6% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.4cm 20.5 cm 6.5 cm 6.2cm

After 3X wash 17.7cm 18.1 cm 5.0cm 5.0cm shrinkage/ growth -2.7cm -2.4 cm -1.5cm -1.2cm

Dimensional

-13.2% -11.7% -23.1% -19.4% Change

After IX wash 19.0cm 20.0cm 5.2cm 5.4cm

After 3X wash 17.7cm 18.1 cm 5.0cm 5.0cm shrinkage/ growth -1.3cm -1.9cm -0.2cm -0.4cm

Dimensional

-6.8% -9.5% -3.8% -7.4% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.4cm 20.5 cm 6.5 cm 6.2cm

After 4X wash 17.7cm 18.2cm 5.0cm 5.1 cm shrinkage/ growth -2.7cm -2.3 cm -1.5cm -1.1 cm

Dimensional

-13.2% -11.2% -23.1% -17.7% Change

After IX wash 19.0cm 20.0cm 5.2cm 5.4cm

After 4X wash 17.7cm 18.2cm 5.0cm 5.1 cm shrinkage/ growth -1.3cm -1.8cm -0.2cm -0.3cm

Dimensional

-6.8% -9.0% -3.8% -5.6% Change

Note: Sample was torqued and wrinkled after wash

Table 20: Reference 132484 / 17060105

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 19.4cm 20.2cm 5.2cm 5.1 cm

After IX wash 17.5cm 17.9cm 5.1 cm 4.9cm shrinkage/ growth -1.9cm -2.3 cm -0.1 cm -0.2cm

Dimensional

-9.8% -11.4% -1.9% -3.9%

Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 19.4cm 20.2cm 5.2cm 5.1 cm

After 2X wash 16.7cm 17.0cm 5.2cm 5.0cm shrinkage/ growth -2.7cm -3.2cm 0.0cm -0.1 cm

Dimensional

-13.9% -15.8% 0.0% -2.0% Change

After IX wash 17.5cm 17.9cm 5.1 cm 4.9cm

After 2X wash 16.7cm 17.0cm 5.2cm 5.0cm shrinkage/ growth -0.8cm -0.9cm 0.1 cm 0.1 cm

Dimensional

-4.6% -5.0% 2.0% 2.0% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 19.4cm 20.2cm 5.2cm 5.1 cm

After 3X wash 16.0cm 16.2cm 4.9cm 5.0cm shrinkage/ growth -3.4cm -4.0 cm -0.3cm -0.1 cm

Dimensional

-17.5% -19.8% -5.8% -2.0% Change

After IX wash 17.5cm 17.9cm 5.1 cm 4.9cm

After 3X wash 16.0cm 16.2cm 4.9cm 5.0cm shrinkage/ growth -1.5cm -1.7cm -0.2cm 0.1 cm

Dimensional

-8.6% -9.5% -3.9% 2.0% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 19.4cm 20.2cm 5.2cm 5.1 cm

After 4X wash 15.4cm 15.5cm 4.8cm 4.8cm shrinkage/ growth -4.0cm -4.7 cm -0.4cm -0.3cm

Dimensional

-20.6% -23.3% -7.7% -5.9% Change

After IX wash 17.5cm 17.9cm 5.1 cm 4.9cm

After 4X wash 15.4cm 15.5cm 4.8cm 4.8cm shrinkage/ growth -2.1 cm -2.4 cm -0.3cm -0.1 cm

Dimensional

-12.0% -13.4% -5.9% -2.0% Change

Table 21 : Reference 132485 / 17060106

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.1 cm 20.5 cm 5.4cm 5.2cm

After IX wash 18.1 cm 17.8cm 4.8cm 4.3 cm shrinkage/ growth -2.0cm -2.7 cm -0.6cm -0.9cm

Dimensional

-10.0% -13.2% -11.1% -17.3% Change

Length Width Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.1 cm 20.5 cm 5.4cm 5.2cm

After 2X wash 16.8cm 16.9cm 4.6cm 4.7cm shrinkage/ growth -3.3cm -3.6cm -0.8cm -0.5cm

Dimensional

-16.4% -17.6% -14.8% -9.6% Change

After IX wash 18.1 cm 17.8cm 4.8cm 4.3 cm

After 2X wash 16.8cm 16.9cm 4.6cm 4.7cm shrinkage/ growth -1.3cm -0.9cm -0.2cm 0.4cm

Dimensional

-7.2% -5.1% -4.2% 9.3% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.1 cm 20.5 cm 5.4cm 5.2cm

After 3X wash 16.2cm 16.3cm 4.4cm 4.2cm shrinkage/ growth -3.9cm -4.2 cm -1.0cm -1.0cm

Dimensional

-19.4% -20.5% -18.5% -19.2% Change

After IX wash 18.1 cm 17.8cm 4.8cm 4.3 cm

After 3X wash 16.2cm 16.3cm 4.4cm 4.2cm shrinkage/ growth -1.9cm -1.5cm -0.4cm -0.1 cm

Dimensional

-10.5% -8.4% -8.3% -2.3% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.1 cm 20.5 cm 5.4cm 5.2cm

After 4X wash 15.4cm 15.7cm 4.5 cm 4.2cm shrinkage/ growth -4.7cm -4.8 cm -0.9cm -1.0cm

Dimensional

-23.4% -23.4% -16.7% -19.2% Change

After IX wash 18.1 cm 17.8cm 4.8cm 4.3 cm

After 4X wash 15.4cm 15.7cm 4.5 cm 4.2cm shrinkage/ growth -2.7cm -2.1 cm -0.3cm -0.1 cm

Dimensional

-14.9% -11.8% -6.3% -2.3% Change

Table 22: Reference 132486 / 17060107

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.8cm 20.7cm 5.5cm 5.2cm

After IX wash 18.8cm 18.6cm 5.2cm 4.8cm shrinkage/ growth -2.0cm -2.1 cm -0.3cm -0.4cm

Dimensional

-9.6% -10.1% -5.5% -7.7% Change Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.8cm 20.7cm 5.5cm 5.2cm

After 2X wash 18.5cm 18.1 cm 5.3cm 4.8cm shrinkage/ growth -2.3 cm -2.6 cm -0.2cm -0.4cm

Dimensional

-11.1% -12.6% -3.6% -7.7% Change

After IX wash 18.8cm 18.6cm 5.2cm 4.8cm

After 2X wash 18.5cm 18.1 cm 5.3cm 4.8cm shrinkage/ growth -0.3 cm -0.5 cm 0.1 cm 0.0cm

Dimensional

-1.6% -2.7% 1.9% 0.0% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.8cm 20.7cm 5.5cm 5.2cm

After 3X wash 17.4cm 18.1 cm 5.4cm 4.9cm shrinkage/ growth -3.4cm -2.6 cm -0.1 cm -0.3cm

Dimensional

-16.3% -12.6% -1.8% -5.8% Change

After IX wash 18.8cm 18.6cm 5.2cm 4.8cm

After 3X wash 17.4cm 18.1 cm 5.4cm 4.9cm shrinkage/ growth -1.4cm -0.5 cm 0.2cm 0.1 cm

Dimensional

-7.4% -2.7% 3.8% 2.1% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.8cm 20.7cm 5.5cm 5.2cm

After 4X wash 17.4cm 17.7cm 5.3cm 4.9cm shrinkage/ growth -3.4cm -3.0cm -0.2cm -0.3cm

Dimensional

-16.3% -14.5% -3.6% -5.8% Change

After IX wash 18.8cm 18.6cm 5.2cm 4.8cm

After 4X wash 17.4cm 17.7cm 5.3cm 4.9cm shrinkage/ growth -1.4cm -0.9cm 0.1 cm 0.1 cm

Dimensional

-7.4% -4.8% 1.9% 2.1% Change

Table 23: Reference 132487 / 17060108

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.5 cm 20.5 cm 5.4cm 5.4cm

After IX wash 18.6cm 18.4cm 4.9cm 4.9cm shrinkage/ growth -1.9cm -2.1 cm -0.5cm -0.5cm

Dimensional

-9.3% -10.2% -9.3% -9.3% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.5 cm 20.5 cm 5.4cm 5.4cm

After 2X wash 18.5cm 18.1 cm 4.9cm 4.8cm shrinkage/ growth -2.0cm -2.4 cm -0.5cm -0.6cm

Dimensional

-9.8% -11.7% -9.3% -11.1% Change

After IX wash 18.6cm 18.4cm 4.9cm 4.9cm

After 2X wash 18.5cm 18.1 cm 4.9cm 4.8cm shrinkage/ growth -0.1 cm -0.3 cm 0.0cm -0.1 cm

Dimensional

-0.5% -1.6% 0.0% -2.0% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.5 cm 20.5 cm 5.4cm 5.4cm

After 3X wash 18.0cm 17.7cm 4.5 cm 5.0cm shrinkage/ growth -2.5 cm -2.8 cm -0.9cm -0.4cm

Dimensional

-12.2% -13.7% -16.7% -7.4% Change

After IX wash 18.6cm 18.4cm 4.9cm 4.9cm

After 3X wash 18.0cm 17.7cm 4.5 cm 5.0cm shrinkage/ growth -0.6cm -0.7 cm -0.4cm 0.1 cm

Dimensional

-3.2% -3.8% -8.2% 2.0% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.5 cm 20.5 cm 5.4cm 5.4cm

After 4X wash 17.5cm 17.7cm 4.6cm 4.9cm shrinkage/ growth -3.0cm -2.8 cm -0.8cm -0.5cm

Dimensional

-14.6% -13.7% -14.8% -9.3% Change

After IX wash 18.6cm 18.4cm 4.9cm 4.9cm

After 4X wash 17.5cm 17.7cm 4.6cm 4.9cm shrinkage/ growth -1.1 cm -0.7 cm -0.3cm 0.0cm

Dimensional

-5.9% -3.8% -6.1% 0.0% Change

Table 24: Reference 132488 / 17060201

Length Width Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.2cm 20.5 cm 5.4cm 5.3cm

After IX wash 18.9cm 18.8cm 5.1 cm 5.1 cm shrinkage/ growth -1.3cm -1.7cm -0.3cm -0.2cm

Dimensional

-6.4% -8.3% -5.6% -3.8% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.2cm 20.5 cm 5.4cm 5.3cm

After 2X wash 18.7cm 19.2cm 5.2cm 5.2cm shrinkage/ growth -1.5cm -1.3cm -0.2cm -0.1 cm

Dimensional

-7.4% -6.3% -3.7% -1.9% Change

After IX wash 18.9cm 18.8cm 5.1 cm 5.1 cm

After 2X wash 18.7cm 19.2cm 5.2cm 5.2cm shrinkage/ growth -0.2cm 0.4cm 0.1 cm 0.1 cm

Dimensional

-1.1% 2.1% 2.0% 2.0% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.2cm 20.5 cm 5.4cm 5.3cm

After 3X wash 18.6cm 19.1 cm 5.0cm 5.1 cm shrinkage/ growth -1.6cm -1.4cm -0.4cm -0.2cm

Dimensional

-7.9% -6.8% -7.4% -3.8% Change

After IX wash 18.9cm 18.8cm 5.1 cm 5.1 cm

After 3X wash 18.6cm 19.1 cm 5.0cm 5.1 cm shrinkage/ growth -0.3 cm 0.3cm -0.1 cm 0.0cm

Dimensional

-1.6% 1.6% -2.0% 0.0% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.2cm 20.5 cm 5.4cm 5.3cm

After 4X wash 18.7cm 18.9cm 5.1 cm 5.1 cm shrinkage/ growth -1.5cm -1.6cm -0.3cm -0.2cm

Dimensional

-7.4% -7.8% -5.6% -3.8% Change

After IX wash 18.9cm 18.8cm 5.1 cm 5.1 cm

After 4X wash 18.7cm 18.9cm 5.1 cm 5.1 cm shrinkage/ growth -0.2cm 0.1 cm 0.0cm 0.0cm

Dimensional

-1.1% 0.5% 0.0% 0.0% Change Table 25: Reference 132489 / 17060202

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.5 cm 20.4cm 5.3cm 5.3cm

After IX wash 19.7cm 19.4cm 5.1 cm 5.0cm shrinkage/ growth -0.8 cm -1.0cm -0.2cm -0.3 cm

Dimensional

-3.9% -4.9% -3.8% -5.7% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.5 cm 20.4cm 5.3cm 5.3cm

After 2X wash 19.5cm 19.7cm 5.1 cm 5.0cm shrinkage/ growth -1.0cm -0.7cm -0.2cm -0.3 cm

Dimensional

-4.9% -3.4% -3.8% -5.7% Change

After IX wash 19.7cm 19.4cm 5.1 cm 5.0cm

After 2X wash 19.5cm 19.7cm 5.1 cm 5.0cm shrinkage/ growth -0.2cm 0.3 cm 0.0cm 0.0cm

Dimensional

-1.0% 1.5% 0.0% 0.0% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.5 cm 20.4cm 5.3cm 5.3cm

After 3X wash 19.4cm 19.3cm 5.0cm 5.0cm shrinkage/ growth -1.1 cm -1.1 cm -0.3 cm -0.3 cm

Dimensional

-5.4% -5.4% -5.7% -5.7% Change

After IX wash 19.7cm 19.4cm 5.1 cm 5.0cm

After 3X wash 19.4cm 19.3cm 5.0cm 5.0cm shrinkage/ growth -0.3 cm -0.1 cm -0.1 cm 0.0cm

Dimensional

-1.5% -0.5% -2.0% 0.0% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.5 cm 20.4cm 5.3cm 5.3cm

After 4X wash 19.4cm 19.4cm 4.9cm 4.9cm shrinkage/ growth -1.1 cm -1.0cm -0.4cm -0.4cm

Dimensional

-5.4% -4.9% -7.5% -7.5% Change After IX wash 19.7cm 19.4cm 5.1 cm 5.0cm

After 4X wash 19.4cm 19.4cm 4.9cm 4.9cm shrinkage/ growth -0.3 cm 0.0cm -0.2cm -0.1 cm

Dimensional

-1.5% 0.0% -3.9% -2.0% Change

Table 26: Reference 132490 / 17060203

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.3 cm 20.1 cm 5.3cm 5.2cm

After IX wash 18.9cm 18.1 cm 5.1 cm 4.9cm shrinkage/ growth -1.4cm -2.0 cm -0.2cm -0.3cm

Dimensional

-6.9% -10.0% -3.8% -5.8% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.3 cm 20.1 cm 5.3cm 5.2cm

After 2X wash 18.7cm 18.2cm 5.2cm 5.0cm shrinkage/ growth -1.6cm -1.9cm -0.1 cm -0.2cm

Dimensional

-7.9% -9.5% -1.9% -3.8% Change

After IX wash 18.9cm 18.1 cm 5.1 cm 4.9cm

After 2X wash 18.7cm 18.2cm 5.2cm 5.0cm shrinkage/ growth -0.2cm 0.1 cm 0.1 cm 0.1 cm

Dimensional

-1.1% 0.6% 2.0% 2.0% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.3 cm 20.1 cm 5.3cm 5.2cm

After 3X wash 18.9cm 18.3cm 5.0cm 5.0cm shrinkage/ growth -1.4cm -1.8cm -0.3cm -0.2cm

Dimensional

-6.9% -9.0% -5.7% -3.8% Change

After IX wash 18.9cm 18.1 cm 5.1 cm 4.9cm

After 3X wash 18.9cm 18.3cm 5.0cm 5.0cm shrinkage/ growth 0.0cm 0.2cm -0.1 cm 0.1 cm

Dimensional

0.0% 1.1% -2.0% 2.0% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.3 cm 20.1 cm 5.3cm 5.2cm After 4X wash 18.7cm 18.1 cm 5.0cm 4.8cm shrinkage/ growth -1.6cm -2.0 cm -0.3cm -0.4cm

Dimensional

-7.9% -10.0% -5.7% -7.7% Change

After IX wash 18.9cm 18.1 cm 5.1 cm 4.9cm

After 4X wash 18.7cm 18.1 cm 5.0cm 4.8cm shrinkage/ growth -0.2cm 0.0cm -0.1 cm -0.1 cm

Dimensional

-1.1% 0.0% -2.0% -2.0% Change

Table 27: Reference 132491 / 17060204

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.7cm 20.8 cm 5.4cm 5.3cm

After IX wash 18.4cm 18.9cm 5.1 cm 4.9cm shrinkage/ growth -2.3 cm -1.9cm -0.3cm -0.4cm

Dimensional

-11.1% -9.1% -5.6% -7.5% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.7cm 20.8 cm 5.4cm 5.3cm

After 2X wash 18.2cm 19.3cm 5.1 cm 4.9cm shrinkage/ growth -2.5 cm -1.5cm -0.3cm -0.4cm

Dimensional

-12.1% -7.2% -5.6% -7.5% Change

After IX wash 18.4cm 18.9cm 5.1 cm 4.9cm

After 2X wash 18.2cm 19.3cm 5.1 cm 4.9cm shrinkage/ growth -0.2cm 0.4cm 0.0cm 0.0cm

Dimensional

-1.1% 2.1% 0.0% 0.0% Change

Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.7cm 20.8 cm 5.4cm 5.3cm

After 3X wash 18.4cm 19.2cm 5.0cm 4.9cm shrinkage/ growth -2.3 cm -1.6cm -0.4cm -0.4cm

Dimensional

-11.1% -7.7% -7.4% -7.5% Change

After IX wash 18.4cm 18.9cm 5.1 cm 4.9cm

After 3X wash 18.4cm 19.2cm 5.0cm 4.9cm shrinkage/ growth 0.0cm 0.3cm -0.1 cm 0.0cm

Dimensional

0.0% 1.6% -2.0% 0.0% Change Length Width

Specimen 1 Specimen 2 Specimen 1 Specimen 2

Original State 20.7cm 20.8 cm 5.4cm 5.3cm

After 4X wash 18.3cm 19.4cm 4.9cm 4.8cm shrinkage/ growth -2.4cm -1.4cm -0.5cm -0.5cm

Dimensional

-11.6% -6.7% -9.3% -9.4% Change

After IX wash 18.4cm 18.9cm 5.1 cm 4.9cm

After 4X wash 18.3cm 19.4cm 4.9cm 4.8cm shrinkage/ growth -0.1 cm 0.5cm -0.2cm -0.1 cm

Dimensional

-0.5% 2.6% -3.9% -2.0% Change

Table 28: Summary Chart

superwashed NeW 1/27 with 23.5 micron

Table 29: NeWl-42.8 with 18.9 micron NS (Woolmark Test Method)

Length Width total

Dimensional dimensional

Change Specimen 1 Specimen 2 Specimen 1 Specimen 2 change after IX wash -7% -5% -4% 9%

average -6.1% 2.6% -3.6% after 2X wash -10% -8% -8% -2%

average -9.5% -5.3% -14.8% after 3X wash -15% -12% -6% -2%

average -13.4% -4.3% -17.6%

17060106 NeW 1/42.8 with IS .9 micron, 80% methanol

Table 30: NeWl-30 with 21.0 micron NS (Woolmark Test Method)

Length Width

Dimensional

Change Specimen 1 Specimen 2 Specimen 1 Specimen 2

after IX wash -1.6% -2.7% 1.9% 0.0%

average -2.1 % 1.0% -1.2% after 2X wash -7.4% -2.7% 3.8% 2.1%

average -5.1 % 3.0% -2.1% after 3X wash -7.4% -4.8% 1.9% 2.1%

average -6.1 % 2.0% -4.1%

17060107 NeW 1/30 with 21.0 micron, 0.2% citric acid

total dimensional

Length Width change

Dimensional

Change Specimen 1 Specimen 2 Specimen 1 Specimen 2

after IX wash -0.5% -1.6% 0.0% -2.0%

average -1.1 % -1.0% -2.1% after 2X wash -3.2% -3.8% -8.2% 2.0%

average -3.5% -3.1% -6.6% after 3X wash -5.9% -3.8% -6.1% 0.0%

average -4.9% -3.1% -7.9%

17060108 NeW 1/30 with 21.0 micron, 80% methanol

Table 31 NeW2-60 with l i 1.5 micron SW (Woolmark Test Method)

engt t total

Dimensional dimensional

Change Specimen 1 Specimen 2 Specimen 1 Specimen 2 change after IX wash 0.5% 2.4% -1.7% -3.7%

average 1.4% -2.7% -1.2% after 2X wash 1.0% 0.0% -1.7% -5.6%

average 0.5% -3.6% -3.1% after 3X wash 1.0% 0.0% -1.7% 0.0%

average 0.5% -0.8% -0.4%

17042002 superwashed NeW 2/60 with 18 .5 micron

Length Width

total

Dimensional dimensional

Change Specimen 1 Specimen 2 Specimen 1 Specimen 2 change after IX wash -1.1% 0.6% 2.0% 2.0%

average -0.3% 2.0% 1.7% after 2X wash 0.0% 1.1% -2.0% 2.0%

average 0.6% 0.0% 0.6% after 3X wash -1.1% 0.0% -2.0% -2.0%

average -0.5% -2.0% -2.5%

17060203 superwashed NeW 2/60 with 18 .5 micron, 0.2% citric acid

Length Width

total

Dimensional dimensional

Change Specimen 1 Specimen 2 Specimen 1 Specimen 2 change after IX wash -1.1% 2.1% 0.0% 0.0%

average 0.5% 0.0% 0.5% after 2X wash 0.0% 1.6% -2.0% 0.0%

average 0.8% -1.0% -0.2% after 3X wash -0.5% 2.6% -3.9% -2.0%

average 1.1% -3.0% -1.9%

17060204 superwashed NeW 2/60 with 18 .5 micron, 80% methanol

Table 32: NeWl-27 with 23.5 micron SW (Woolmark Test Method)

Length Width

total

Dimensional dimensional

Change Specimen 1 Specimen 2 Specimen 1 Specimen 2 change after 2X wash -1.5% -0.5% -2.0% 0.0%

average -1.0% -1.0% -2.0% after 3X wash -1.5% 0.0% -3.9% -2.0%

average -0.8% -3.0% -3.7%

17060202 superwashed NeW 1/27 with 23.5 micron, 80% methanol

Table 33 : NeWl -42.8 with 18.9 micron NS (AATCC Test Method)

average -14.9% - 1.0% - 15.9% after 3X wash -17.5% ■19.8% -5.8% -2.0%

average -18.7% -3.9% -22.5% after 4X wash -20.6% -23.3% -7.7% -5.9%

average -6.8% -28.7% 17060105 NeW 1/42.8 with 18.9 micron, 0.2% citric acid

Length Width

total

Dimensional dimensional

ChangeSpecimen 1 Specimen 2 Specimen 1 Specimen 2 change after IX wash -10.0% -13.2% -11.1% -17.3%

average -11.6% -14.2% -25.8% after 2X wash -16.4% -17.6% -14.8% -9.6%

average -17.0% -12.2% -29.2% after 3X wash -19.4% -20.5% -18.5% -19.2%

average -19.9% -18.9% -38.8% after 4X wash -23.4% -23.4% -16.7% -19.2%

average -23.4% -17.9% -41.3%

17060106 NeW 1/42.8 with l i 3.9 micron, 80% methanol

Table 34: NeWl-30 with 21.0 micron NS (AATCC Test Method)

after 2X wash -9.8% -1.5% -18.5% -17.7%

average -5.6% -18.1% -23.7% after 3X wash -13.2% -11.7% -23.1% -19.4%

average -12.5% -21.2% -33.7% after 4X wash -13.2% -11.2% -23.1 % - 17.7%

average -12.2% -20.4% -32.6%

17050902 NeW 1/30 with 21.0 micron

Length Width

total

Dimensional dimensional

ChangeSpecimen 1 Specimen 2 Specimen 1 Specimen 2 change after IX wash -9.6% -10.1 % -5.5% -7.7%

average -9.9% -6.6% -16.5% after 2X wash -11.1 % -12.6% -3.6% -7.7%

average -11.8% -5.7% -17.5% after 3X wash -16.3% - 12.6% -1.8% -5.8%

average - 14.5% -3.8% - 18.2% after 4X wash - 16.3% -14.5% -3.6% -5.8%

average -15.4% -4.7% -20.1%

17060107 NeW 1/30 with 21.0 micron, 0.2 % citric acid

Length Width

total

Dimensional dimensional

ChangeSpecimen 1 Specimen 2 Specimen 1 Specimen 2 change after IX wash -9.3% - 10.2% -9.3% -9.3%

average -9.8% -9.3% - 19.0% after 2X wash -9.8% -11.7% -9.3% -11.1 %

average -10.7% -10.2% -20.9% after 3X wash -12.2% -13.7% -16.7% -7.4%

average -12.9% -12.0% -25.0% after 4X wash -14.6% -13.7% -14.8% -9.3%

average -14.1 % -12.0% -26.2%

17060108 NeW 1/30 with 21.0 micron, 80°/ i methanol

Table 35 : NeW2-60 with 18.5 micron SW (AATCC Test Method)

Length Width

total

Dimensional dimensional

ChangeSpecimen 1 Specimen 2 Specimen 1 Specimen 2 change after IX wash -6.4% -4.5% 0.0% -1.8%

average -5.4% -0.9% -6.3% after 2X wash -12.1% -7.2% -5.6% -7.5%

average -9.6% -6.6% -16.2% after 3X wash -11.1% -7.7% -7.4% -7.5%

average -9.4% -7.5% -16.9% after 4X wash -11.6% -6.7% -9.3% -9.4%

average -9.2% -9.3% -18.5%

17060204 superwashed NeW 2/60 with 1 S .5 micron, 80% methanol

Table 36: NeWl-27 with 23.5 micron SW (AATCC Test Method)

average -7.4% -4.7% -12.0% after 2X wash -7.4% -6.3% -3.7% -1.9%

average -6.9% -2.8% -9.7% after 3X wash -7.9% -6.8% -7.4% -3.8%

average -7.4% -5.6% -13.0% after 4X wash -7.4% -7.8% -5.6% -3.8%

average -7.6% -4.7% -12.3%

17060201 superwashed NeW 1/27 with 23.5 micron, 0.2% citric acid

Length Width

total

Dimensional dimensional

ChangeSpecimen 1 Specimen 2 Specimen 1 Specimen 2 change after IX wash -3.9% -4.9% -3.8% -5.7%

average -4.4% -4.7% -9.1% after 2X wash -4.9% -3.4% -3.8% -5.7%

average -4.2% -4.7% -8.9% after 3X wash -5.4% -5.4% -5.7% -5.7%

average -5.4% -5.7% -11.0% after 4X wash -5.4% -4.9% -7.5% -7.5%

average -5.1% -7.5% -12.7%

17060202 superwashed NeW 1/27 with 23.5 micron, 80% methanol

Example 3: Silk coating wool, including a citric acid pretreatment and methanol post treatment - Addition of a new control; Samples tested for dimensional changes after laundering, perceived hand, and fiber morphology by SEM analysis

This example adds a new control with no silk coating for evaluating the application of silk fibroin solution on fabrics made with wool fabric tube after a pretreatment of citric acid and followed by a methanol bath. The application takes place in a sequence of baths and pads application with multiple drying steps. The samples were tested for dimensional changes after laundering, perceived hand, and fiber morphology with SEM analysis.

Table 37: Coating Experimental Variables

Analysis Samples are conditioned at ambient condition for 24 hrs before a massing post coating. The percentage change is calculated based on the following formula: mass post coating— mass before coating

Mass change % = ;— x 100 mass before coating

The dimensional changes of the samples post laundering are analyzed based on Woolmark Company TM31-May 2000 and AATCC Test Method 135- 2015. Samples are tested after t=l and t=4 laundering cycle for the Woolmark test, and at t=0 and t=3 for the AATCC test.

After the dimensional analysis test, the wool fabric tubes are scored for hand against a non treated control. Scoring are made for softness and any additional perceived difference.

After the hand test is completed the samples are analyzed by SEM (FIGS. 7 to 14).

Table 38: Processing recording and mass percentage change post treatment for samples 17060105 and 17060106 17060105

Table 39: Processing recording and mass percentage change post treatment for samples 17060107 and 17060108 17060107

Table 40: Processing recording and mass percentage change post treatment for samples 17060201 and 17060202

Table 41 : Processing recording and mass percentage change post treatment for samples 17060203 and 17060204

Table 42: Hand score of wool tube

Dimensional Stability to laundering is as described in Tables 12 to 36.

Example 4: Silk coating a cashmere fabric: improving pilling resistance and water repellency

Materials and Methods:

A cashmere fabric was used to test for improvements in pilling resistance and water repellency upon silk treatment. The silk coated cashmere sample was obtained with a four bath process: 1) 0.25% Citric Acid; 2) 0.25% Citric Acid, 0.375% Low MW silk, 0.125% Med MW silk (Total Silk: 0.5% 3L: 1M); 3) 0.25% Citric Acid; 4) 80% Methanol.

Table 43: Control cashmere fabric sample before Pilling Resistance Test

Table 44: Control and Silk coated fabric samples after Pilling Resistance Test

As shown above, the pilling resistance tests demonstrated that a silk treated sample had a 0.5 improvement in pilling over control for both length and width, improving it from moderate to slight pilling class (on width). Table 45: Dimensional Changes of Cashmere Fabrics after Home Laundering - AATCC Test Method 135-2015; Woolmark Test Method: Washing of Wool Textile

Products - The Woolmark Company TM31-May 2000

Length Width

CHA- CHA- CHA-

17101902- 17101902- CHA- 17101902- 17101902-

T001 T002 T001 T002

Original

20.0 cm cm 20.0 cm

State 20.0 20.0 Cm

After IX

19.2 cm cm 19.9 cm

wash 18.5 19.3 Cm shrinkage

-0.8 cm -1.5 cm -0.1 cm -0.7 cm /growth

Dimensio

nal -4.0% -7.5% -0.5% -3.5%

Change

Length Width

CHA- CHA- CHA-

17101902- 17101902- CHA- 17101902- 17101902-

T001 T002 T001 T002

Original

20.0 cm 20.0 cm 20.0 cm 20.0 cm State

After 2X

18.9 cm cm 19.5 cm

wash 18.3 19.3 Cm shrinkage

-1.1 cm -1.7 cm -0.5 cm -0.7 cm /growth

Dimensio

nal -5.5% -8.5% -2.5% -3.5%

Change

After IX

19.2 cm 18.5 cm 19.9 cm 19.3 cm wash

After 2X

18.9 cm 18.3 cm 19.5 cm 19.3 cm wash

shrinkage

-0.3 cm -0.2 cm -0.4 cm 0.0 cm /growth

Dimensio

nal -1.6% -1.1% -2.0% 0.0%

Change

Length Width

CHA- CHA- CHA-

17101902- 17101902- CHA- 17101902- 17101902-

T001 T002 T001 T002 Original

20.0 cm 20.0 cm 20.0 cm 20.0 cm State

After 3X

18.5 cm cm 19.1 cm cm wash 17.8 19.3 shrinkage

-1.5 cm -2.2 cm -0.9 cm -0.7 cm /growth

Dimensio

nal -7.5% -11.0% -4.5% -3.5%

Change

After IX

19.2 cm 18.5 cm 19.9 cm 19.3 cm wash

After 3X

18.5 cm 17.8 cm 19.1 cm 19.3 cm wash

shrinkage

-0.7 cm -0.7 cm -0.8 cm 0.0 cm /growth

Dimensio

nal -3.6% -3.8% -4.0% 0.0%

Change

Length Width

CHA- CHA- CHA-

17101902- 17101902- CHA- 17101902- 17101902-

T001 T002 T001 T002

Original

20.0 cm 20.0 cm 20.0 cm 20.0 cm State

After 4X

18.2 cm cm 19.3 cm cm wash 17.7 19.4 shrinkage

-1.8 cm -2.3 cm -0.7 cm -0.6 cm /growth

Dimensio

nal -9.0% -11.5% -3.5% -3.0%

Change

After IX

19.2 cm 18.5 cm 19.9 cm 19.3 cm wash

After 4X

18.2 cm 17.7 cm 19.3 cm 19.4 cm wash

shrinkage

-1.0 cm -0.8 cm -0.6 cm 0.1 cm /growth

Dimensio

nal -5.2% -4.3% -3.0% 0.5%

Change

Testing Information:

• Home Laundered see above times using AATCC TM 150 Table II

Laundry Test Conditions: load size = 1.8 kg (4 lbs.); Launder Right Side Out; Top Loading Machine Wash; (2) Delicate; (III) 105 ± 5 °F using 66 ± 1 g 1993 AATCC Standard Reference Detergent WOB; (A)Tumble Dry ii Delicate;

Ballast Wash Load Type 3 - 50/50 polyester/cotton bleached plain weave; a (-) indicates shrinkage and (+) indicates growth; fabrics were not hand ironed or restored; evaluation conditions: 21 °C (± 2 °C) and 65% RH (± 5% RH) Not Used

Table 46: Cashmere Fabric Water Repellency: Spray Test (AATCC 22-2014)

Spray Test Rating

CHA- 17101902-T001 CHA- 17101902-T002

Specimen

1 0 70

Specimen

2 0 70

Specimen

3 N/A N/A

Testing Information:

• Rated the Face of the Specimen - No Average Recorded

• Used the Spray Test Rating Chart

• Rating of 100 - No Sticking or Wetting of the Specimen Face

• Rating of 90 - Slight Random Sticking or Wetting of the Specimen Face

• Rating of 80 - Wetting of Specimen Face at Spray Points

• Rating of 70 - Partial Wetting of the Specimen Face Beyond the Spray Points

• Rating of 50 - Complete Wetting of the Entire Specimen Face Beyond the Spray Points

• Rating of 0 - Complete Wetting of the Entire Face of the Specimen

Example 5: Polyester/Lycra and Nylon/Lycra Fabrics Coated with Silk and Silicone: Biocompatibility Evaluation

After silk coating (Table 47), samples are ambientally conditioned for 24 hrs., then shipped to a testing lab for cytotoxicity assessment (Table 48).

Table 47: Coating Experimental Variables

0.187% low MW + 0.025% citric

Domosil 302 (150) 0.063% medium acid (50%) or to

RWAF 70 seconds MW (3: 1 ratio) pH 4-5

0.187% low MW + 0.025% citric

Ultratex 350 (177) 0.063% medium acid (50%) or to

CSP 60 seconds MW (3: 1 ratio) pH 4-5

0.187% low MW + 0.025% citric

Ultratex 350 (177)

6608D2B 0.063% medium acid (50%) or to

SI 60 seconds MW (3: 1 ratio) pH 4-5

0.187% low MW + 0.025% citric

Domosil 350 (177) 0.063% medium acid (50%) or to

RWAF 60 seconds MW (3: 1 ratio) pH 4-5

Table 48: Summary of Cytotoxicity Tests

Test

Shortened Batch

Product Name Article Results

Product Code Lot

Name

Black Nylon Fabric Fabric No reactivity

A2701171

(16120107) 11 (passed)

2 step coating Fabric

Mild reactivity, 6606D2, 0.25% Silk

complete lysis 3L1M*, 3% Ultratex TexNylonSil 17042601 Fabric 1

under the test CSP, 0.025% citric

article (passed) acid

2 step coating Fabric

6606D2, 0.25% Silk No reactivity

TexNylonSil 17042602 Fabric 2

3L1M, 3%Ultratex SI, (passed) 0.025% citric acid

2 step coating Fabric

Mild reactivity, 6606D2, 0.25% Silk

complete lysis 3L1M, 3% Domosil TexNylonSil 17042603 Fabric 3

under the test RWAF, 0.025% citric

article (passed) acid

2 step coating Fabric

Mild reactivity, 6608D2B, 0.25% Silk

Fabric complete lysis 3L1M, 3% Ultratex TexPolySil 17042604

12 under the test CSP, 0.025% citric

article (passed) acid

2 step coating Fabric Slight reactivity, 6608D2B, 0.25% Silk Fabric partial cell lysis

TexPolySil 1 7042605

3L1M, 3%Ultratex SI, 13 under test article 0.025% citric acid (passed)

2 step coating Fabric

Mild reactivity, 6608D2B, 0.25% Silk

Fabric complete lysis

3L1M, 3% Domosil TexPolySil 17042606

14 under the test RWAF, 0.025% citric

article (passed) acid

* 3L1M: 3: 1 low MW si k to medium IV [W silk Example 6: Nylon/Lycra Fabric Coated with Silk and Silicone: Laundering Fastness Evaluation (Hand and Water Drop Absorption) - First Sample Set

Table 49: Coating Experimental Variables

Analysis: Samples coated as described in Table 49, are conditioned at ambient for 24 hrs before delivering them to testing lab for laundering test. The samples are used for:

o N=l control no laundering

o N=l after 10 laundering cycles

o N=l after 25 laundering cycles

o N=l after 50 laundering cycles

o Fabrics are evaluated for hand by two technicians against the control not laundered (Table 50).

Laundering method AATCC Test Method 135-2015 (Table I, "Dimensional Changes of Fabrics after Home Laundering"). Testing Information: Home Laundered 52 times using AATCC TM 150 (Table II); Laundry Test Conditions: load size = 1.8 kg (4 lbs), Launder Right Side Out Wash; Normal/CottonSturdy (III) 105±5 °F using 1993 AATCC Standard Reference Detergent WOB; Top Loading Machine; Tumble Dry (i) Cotton Sturdy; Ballast Wash Load Type 3 - 50/50 polyester/cotton bleached plain weave; Samples removed at 10, 25 and 52 launderings.

After laundering fabrics are evaluated for water drop test (Table 51). The sample fabric is placed on top of a 7 cm diameter positioned on the drapability jig. A RODI water drop is dispensed with an eye dropper from approximately 3 cm above the fabric. A video imaging recording capture the time from the water drop contacting the fabric until its full absorption or up to 60 seconds

Table 50: Hand Score of Fabric Results

Table 51 : Water Drop Test Results

Average water drop

Sample # Description

absorption time

1705030 6606D2 nylon/lycra, first step 0.25% t=0 27.4

7 silk 3L1M, 0.025% citric acid, t=10 60

second step 2% Ultratex CSP, 0.25% t=25 60

citric acid

t=52 17.2

1705030 6606D2 nylon/lycra, first step 0.25% t=0 1

8 silk 3L1M, 0.025% citric acid, t=10 2.6

second step 3% Domosil RWAF, t=25 3.6

0.25% citric acid

t=52 2.6

1705030 t=0 2.6

6608D2B polyester/lycra, 0.25% silk

6

3L1M, 0.025% citric acid, 3% t=10 60

Domosil RWAF t=25 60

t=52 60

1705030 6608D2B polyester/lycra, first step t=0 11.2

9 0.25% silk 3L1M, 0.025% citric acid, t=10 60

second step 2% Ultratex CSP, 0.25% t=25 60

citric acid

t=52 60

1705031 6608D2B polyester/lycra, first step t=0 0.8

0 0.25% silk 3L1M, 0.025% citric acid, t=10 3.2

second step 3% Domosil RWAF, t=25 7

0.25% citric acid

t=52 28.6

* 3L1M: 3: 1 I low MW silk to medium MW silk

Note: end of test 60 seconds

Example 7: Nylon/Lycra Fabric and Polyester/Lycra Fabric Coated with Silk and Silicone: Laundering Fastness Evaluation (Hand and Water Drop Absorption) - Second Sample Set

Table 52: Coating Experimental Variables

Analysis:

Samples coated as described in Table 52, are conditioned at ambient for 24 hrs before delivering them to testing lab for laundering test. The samples will be used for: o N=l control no laundering;

o N=l after 10 laundering cycles;

o N=l after 25 laundering cycles;

o N=l after 50 laundering cycles;

o Fabrics are evaluated for hand by two technicians against the control not laundered (Table 53).

Laundering method AATCC Test Method 135-2015 (Table I, "Dimensional Changes of Fabrics after Home Laundering"). Testing Information: Home Laundered 52 times using AATCC TM 150 (Table II); Laundry Test Conditions: load size = 1.8 kg (4 lbs), Launder Right Side Out Wash; (l)Normal/CottonSturdy (III) 105±5 °F using 1993 AATCC Standard Reference Detergent WOB; Top Loading Machine; Tumble Dry (i) Cotton Sturdy; Ballast Wash Load Type 3 - 50/50 polyester/cotton bleached plain weave; Samples removed at 10, 25 and 52 launderings.

After laundering fabrics are evaluated for water drop test (Table 54, and FIG. 32). The sample fabric is placed on top of a 7 cm diameter positioned on the drapability jig. A RODI water drop is dispensed with an eye dropper from approximately 3 cm above the fabric. A video imaging recording capture the time from the water drop contacting the fabric until its full absorption or up to 60 seconds.

Table 53: Hand Score of Fabric Sample # Description t=0 t=10 t=25 t=52

6606D2 nylon/lycra, 0.25% silk

17050303 3L1M*, 0.025% citric acid, 3% 5 4 1 1

Domosil RWAF

6606D2 nylon/lycra, first step

0.25% silk 3L1M, 0.025% citric

17050308 5 5 3 3 acid, second step 3% Domosil

RWAF, 0.25% citric acid

6606D2 nylon/lycra, 0.25% silk

17060101 5 6 6 6

3L1M, 0.025% citric acid

6606D2 nylon/lycra, 3% Domosil

17060102 5 4 4 3

RWAF, 0.25% citric acid

6608D2B polyester/lycra, 0.25%

17050306 silk 3L1M, 0.025% citric acid, 3% 5 4 3 3

Domosil RWAF

6608D2B polyester/lycra, first step

0.25% silk 3L1M, 0.025% citric

17050310 5 5 4 4 acid, second step 3% Domosil

RWAF, 0.25% citric acid

6608D2B polyester/lycra, 0.25%

17060103 5 6 4 4 silk 3L1M, 0.025% citric acid

6608D2B polyester/lycra, 3%

17060104 5 4 4 4

Domosil RWAF, 0.25% citric acid

* 3L1M: 3: 1 low MW silk to medium MW silk

Sample #17060101 and # 17060103 had some scores higher than 5; without being limited to any one theory, it is theorized that there is affinity between silk and silicone and the silicone shedding from the coated fabric recoated the silk only coated variables

Table 54: Water Drop Test Results

t=25 1 0.000 t=50 1 0.000 t=0 19.8 2.775

6606D2 nylon/lycra, 3% t=10 59.8 0.447

17060102 Domosil, 0.025% citric acid

t=25 9.6 2.608 t=50 9.8 2.950

6608D2B polyester/lycra, t=0 2.6 0.548 0.25% silk 3L1M, 0.025% citric t=10 60 0.000

17050306

acid, 3% Domosil RWAF t=25 60 0.000 t=52 60 0.000

6608D2B polyester/lycra, first t=0 0.8 0.274 step 0.25% silk 3L1M, 0.025% t=10 3.2 0.447 citric acid, second step 3%

17050310 t=25 7 2.345

Domosil RWAF, 0.25% citric

acid t=52 28.6 3.130

6608D2B polyester/lycra t=0 0.5 0.000 0.187% low MW, 0.063% t=10 1.4 0.548

17060103 medium MW, 0.025% citric

t=25 2.8 0.447 acid

t=50 24.6 7.503 t=0 1.4 0.548

6608D2B polyester/lycra, 3% t=10 60 0.000

17060104 Domosil RWAF

t=25 9.4 4.037 t=50 60 0.000

Example 8: Nylon/Lycra and Polyester/Lycra Fabric Coated with Silk and Silicone: Evaluation of Oil Repellency / Hydrocarbon Resistance, and Soil Repellency

Table 55: Coating Experimental Variables

Fabric type Dry/cure

Silk PH Silicone PH

(application temperature solution correction coating correction steps) °F (°C)

0.187%

Fabric low MW + 0.025%

6606D2 0.063% citric acid 302 (150)

N/A N/A

nylon/lycra medium (50%) or to 70 seconds

(1) MW (3: 1 pH 4-5

ratio)

0.187%

Fabric low MW + 0.025%

6608D2B 0.063% citric acid 350 (150)

N/A N/A

polyester/lycra medium (50%) or to 60 seconds

(1) MW (3: 1 pH 4-5

ratio)

Analysis:

Samples coated as described in Table 55, are conditioned at ambient for 24 hrs before lab delivery for testing. The samples tested for (Table 56):

AATCC TM118-2013, Oil Repellency: Hydrocarbon Resistance; the scale ranges from zero to eight, with a rating of eight signifying the most repellent surface; testing conditions: 21 °C (± 2 °C) and 65% RH (± 5% RH);

AATCC TM130-2015, Soil Release: Oily Stain Release Method; AATCC Stain Release Replica version 2013 used for grading; washing procedure III (41 ± 3 °C (105 ± 5 °F)); ballast wash load Type 3 - 92 x 92 cm (36 x 36 in) hemmed pieces of 50/50 Poly/Cotton sheeting; 1993 AATCC Standard Reference Detergent WOB containing no phosphate; washer manufacturer: Kenmore, Model #: 110.23902200, or Whirlpool, Model #: GTS9679PW3; dryer manufacturer: Whirlpool, Model #: LEQ9858PW1; a grade of 5 indicates excellent stain removal; a grade of 1 indicates very poor stain removal; testing conditions: 21 °C (± 2 °C) and 65% RH (± 5% RH).

The sample tested for each method are:

N=l control no laundering

N=l Fabric 6606D2, 0.25% silk 3L1M

N=l Fabric 6606D2, 0.25% silk 3L1M, 3% Domosil RWAF silicone

N=l Fabric 6608D2B, 0.25% silk 3L1M

N=l Fabric 6608D2B, 0.25% silk 3L1M, 3% Domosil RWAF silicone

Table 56: Oil Repellency and Soil Release Average

Soil Average Oil Release: Repellency: Oily Stain Hydrocarbon

Sample # Description

Release Resistance Method - Test AATCC AATCC 118-2013 130-2015

16111801 6606D2 nylon/lycra control 3.8 0

6606D2 nylon/lycra, first step 0.25%

silk 3L1M*, 0.025% citric acid,

17050308 4.3 0

second step 3% Domosil RWAF,

0.25% citric acid

6606D2 nylon/lycra, 0.25% silk

17050301 4.5 0

3L1M, 0.025% citric acid

16122001 6608D2B polyester/lycra control 4.5 0

6608D2B polyester/lycra, first step

0.25% silk 3L1M, 0.025% citric acid,

17050310 3.8 0

second step 3% Domosil RWAF,

0.25% citric acid

6608D2B polyester/lycra, 0.25% silk

17050304 4.3 0

3L1M

3L1M: 3: 1 low MW silk to medium MW silk

Example 9: Nylon/Lycra and Polyester/Lycra Fabric Coated with Silk and Silicone: Evaluation of Textile Abrasion

The experiment includes the determination of the abrasion resistance of textile fabrics using the Martindale abrasion tester. Fabrics of all types may be tested by this method, but difficulties may arise with fabrics with a pile depth greater than 0.08 in (2 mm).

The values stated in inch-pound units are regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

Materials and Equipment: 6606D2 nylon/lycra sample #16120102-M coated with 0.15% low MW, 0.05% medium MW (ratio 3: 1), 0.025% citric acid; silk medium molecular weight solution at 6%; silk low molecular weight solution at 6%; citric acid; unfiltered tap water; fabric sample style 6606D2; Krantz tenter frame; dye machine.

Coating Methods: the fabric is dyed in black with a dyeing machine using the following recipe:

o ERIOFAST BLACK M 6%; o Low molecular weight and medium molecular weight silk are diluted using tap water from 6% to the concentration for each of the 3 tests reported in Table 57;

o The solution will be prepared for 104 liter pad liquor, with an estimating wet pick up rate of 65-70% for the processed fabric, and reduced by the end of each of the 3 tests to a minimum level of 60 liter (safety factor of 20% from the 50 liter minimum level of bath processing);

o When medium molecular weight is used in the coating solution, the solution will be prepared with the following steps: mix low molecular weight, water, and citric acid for 2-3 minutes; add medium molecular weight and mix for additional 2-3 minutes;

o When only low molecular weight silk is used, the silk solution is mixed with water and citric acid for 2-5 minutes;

o Citric acid is added to the solution to correct the pH to 4-5, not exceeding a 0.25% liquor concentration;

o The tenter frame is cleaned from any residue that may have built up on the bath or pad rollers from previous runs;

o The approximately 700 yards dyed fabric is split into N=5 sections, N=3 sections of 220 yards each, N=l section of 35 yards, and N=l section of 5 yards;

o The fabric is processed per Table 1, except for the 5 yards sample that is tested unprocessed for control;

o For each test number, a sample of the solution is taken after it is mixed in the mixing tank, at approximately the middle of the fabric processing on the tenter frame and after the fabric is processed on the tenter frame bath; the solution is analyzed to quantify the silk solution concentration and determine any depletion rate at the tenter frame bath for fabric exposure;

o During each trial, the first 5 meters of fabric sample are collected for testing, after approximately 110 meter additional 5 meter sample are collected, and the last 5 meter of processed fabric are collected;

o After the fabric is cut during the middle of the run to collect the 5 meter sample, the fabric can be rolled on the same core;

o All fabric rolls processed are assigned an identification number for traceability.

Table 57: Coating Processing Variables

at

Abrasion Method:

• Fabric is not laundered;

• Abradand: worsted wool;

· Mass of Weight = 9 kPa for apparel fabrics;

• Abrasion cycle for the Martindale Abrasion Tester, 16 rubs required to complete a geometric shape, known as a Lissajous Figure (geometric figure that starts as a straight line, then becomes a widening ellipse, and narrows to again become a straight line; there are 16 rubs in one Lissajous figure); rub = one rotation of the two outer gears of the Martindale Abrasion Tester;

• Testing Conditions: 21 °C (± 2 °C) and 65% RH (± 5% RH);

• End of test confirmed under a microscope for see through hole.

Interim results: the abrasion test is completed on N=3 samples; sample #1 was voluntary stopped at 1,388,251 cycles; sample #2 was voluntary stopped at 585,696 cycles. For comparative purposes, a sock normally wears at 5,000-10,000 cycles;

25,000 cycles typically represent a 95 percentile result.

Example 10. Preparation of Silk Gels

Table 58. Gel Samples - Silk gel formulations including additives, concentration of silk and additive, gelation conditions and gelation times. mL 2% Mass Ratio Amount

Sample Temp/ Days to silk Vit C silk: Additive of

Name Treatment Gelation solution (8) Vit C additive

1 10 0.04 5:01 None None RT 8

2 10 0.08 2.5: 1 None None RT 8

3 10 0.2 1 :01 None None RT 8

4 10 0.4 1 :02 None None RT 14

5 10 0.8 1 :04 None None RT None

6 10 0.04 5:01 None None Fridge -39

7 10 0.08 2.5: 1 None None Fridge -39

8 10 0.2 1 :01 None None Fridge -39

9 10 0.4 1 :02 None None Fridge None

10 10 0.8 1 :04 None None Fridge None

RT/Shake

11 10 0.2 1 :01 None None 8 vigorously

37 °C

0-1 10 0.04 5:01 None None 3

Oven

50 °C

0-2 10 0.04 5:01 None None 2

Oven

37 °C

0-3 10 0.2 1 :01 None None 4

Oven

50 °C

0-4 10 0.2 1 :01 None None 3

Oven

M 40 0.16 5:01 None None RT 5

D 40 0.16 5:01 None None RT 5

El 10 0.04 5:01 Vit E 1 drop RT 7

E2 10 0.04 5:01 Vit E 3 drops RT 7

E3 10 0 None Vit E 1 drop RT None

E4 10 0 None Vit E 3 drops RT None

LI 10 0.04 5:01 Lemon 300 RT 6

L2 10 0.04 5:01 Lemon Juice 300 RT 6

L3 10 0.04 5:01 Lemon Juice 1000 RT 5

L4 10 0 None Lemon 300 μΐ, RT 6

L5 10 0 None Lemon Juice 300 μΐ, RT 7

Jar 1 20 0.08 5:01 Lemon Juice 2000 μΐ, RT 5-7

Lemongrass

Jar 2 5 0.02 5:01 1 drop RT 2-3

Oil

Rosemary

R-l 10 0.04 5:01 1 drop RT 7

Oil

T-l 10 0.04 5:01 None None RT/Tube 7

RO-1 10 0.04 5:01 Rose Oil 1 drop RT 6

RO-2 10 None None Rose Oil 1 drop RT None Ratio of Silk to Vitamin C

Samples 1-10 were used to examine the effect of silk to vitamin C ratio on serum gelation. Samples 1-3 with less vitamin C gelled quicker than samples 4 and 5. All other conditions were kept constant. Samples 6-8 with less vitamin C gelled quicker than samples 9 and 10. All other conditions were kept constant. It is concluded that decreasing the ratio of silk to vitamin C (increasing the amount of vitamin C), will lengthen the time to gel creation. At ratios with small amounts of vitamin C, days to gel creation did not vary greatly.

Physical Stimulation

Samples 3 and 11 were used to examine the effect of physical stimulation on serum gelation. Each sample was prepared under the same conditions. Sample 11 was vigorously shaken for about 3 minutes after addition of vitamin C. Treatment of 3 and 11 was otherwise the same. The shaking resulted in bubbles but did not significantly change gel creation time.

Temperature Treatment

Samples 1, 3, 6, 8, O-l, 0-2, 0-3, and 0-4 were used to examine the effect of temperature treatment on serum gelation time. Samples 1, 6, 0-1, and 0-2 were identical other than temperature treatment. Samples 3, 8, 0-3, and 0-4 were identical other than temperature treatment. The two groups differed in silk to vitamin C ratio. Time to serum gelation was directly related to temperature treatment with a higher temperature resulting in quicker serum gelation.

Solution Volume

Samples 1, M and D were used to examine the effect of solution volume on serum gelation time. Samples M and D varied from sample 1 only by an increased solution volume. Samples M and D gelled in 5 days while sample 1 gelled in 8 days. Samples M and D were definitively noticed to be gelled on the day of gelling while sample 1 gelled over a weekend.

Additives

Samples El, E2, E3, E4, LI, L2, L3, L4, L5, Jar 2, Rl, RO-1 and RO-2 were used to examine the effect of additives on serum gelation time. Samples El -4 contained Vitamin E. Only samples El and E2 contained vitamin C and only these two samples gelled. Vitamin E can be added to a solution to become a gel but it appears that another additive may be needed to create a gel. Samples Ll-5 contained a form of lemon juice. Samples LI and L4 had juice directly from a lemon while samples L2, L3 and L5 contained lemon juice from a plastic lemon container. Samples L4 and L5 did not have vitamin C while all others did. All samples gelled showing that lemon juice can create gel on its own. Amount of lemon juice and type of lemon juice had little effect on gelation time. Sample Jar 2 contained lemon grass oil which formed an albumen like substance when initially added. This sample also had vitamin C but gelation time was significantly quicker than with other vitamin C samples. Sample Rl contained rosemary oil, which seemed to be soluble, as well as vitamin C. The sample gelled in a similar time frame to other samples with only vitamin C. Samples RO-1 and RO-2 contained rose oil while only RO-1 had vitamin C. Only RO-1 gelled showing that rose oil will not create a gel quickly on its own. In both cases the rose oil was immiscible and visible as yellow bubbles.

Aqueous silk fibroin-based fragment solution and essential oils are immiscible liquids. In an embodiment, to increase the fragrance of the silk fibroin-based fragment solution, without entrapping oils within the solution, the solution is mixed with the essential oil with the use of a stir bar. The stir bar is rotated at a speed such that some turbulence is observed in the mixture, thus causing contact between the fragrant essential oil and the molecules in solution, adding a scent to the solution. Before casting of product from the solution, mixing may be stopped and the oil allowed to separate to the top of the solution. Dispensing from the bottom fraction of the solution into the final product allows for fragrance without visible essential oil within the final product.

Alternatively, the silk fibroin-based solution and essential oil can be combined with or without additional ingredients and/or an emulsifier to create a composition containing both ingredients.

In an embodiment, mixing of the solution as described above can reduce gelation time if the solution is used to create a gel formulation.

Vessel

Samples Tl and Jar 1 were used to examine the effect of casting vessel on serum gelation time. Jar 1 was cast in a glass jar while Tl was cast in an aluminum tube. Both samples gelled and did not affect serum gel time.

Summary

All treatments of silk solution for gel solution were in a conical tube at room temperature unless otherwise stated. The ratio of silk to vitamin C did affect the ability of a solution to gel as ratios above 1 :2 did not gel and a 1 :2 ratio took twice as long as other lower ratios (5: 1, 2.5: 1, 1 : 1). Temperature affected gel creation time with higher temperatures resulting in quicker gel times. 50 °C treatment gelled in as quick as 2 days, 37 °C treatment gelled in as quick as 3 days, room temperature treatment gelled in 5-8 days and storage in a refrigerator took at least 39 days to gel. The effects of additives on gel creation were dependent on the additive. Vitamin E, Rosemary Oil and Rose Oil all had no effect on gel creation. Each of these additives did not prevent gelation or affect the time to gelation. Each also required the presence of vitamin C to gel. Lemon juice from a fresh lemon, pre-squeezed lemon juice from a plastic lemon container and lemon grass oil did affect gel creation. Without wishing to be bound by theory, it is believed that the lower pH as a result of these additives is the reason the additives had an impact on decreasing gelation time. Both lemon juice types were able to cause gelation without the presence of vitamin C. This occurred in the same number of days as with vitamin C. The lemongrass oil was able to decrease the number of days to gelation to 2-3 days. All additives appeared soluble other than lemongrass oil and rose oil. Rose oil remained in yellow bubbles while the lemongrass oil was partially soluble and formed an albumen like chunk. In an embodiment, oils that are not fully soluble, can still be suspended within the gel as an additive. Physical stimulation by shaking, vessel the solution was cast into and solution volume did not affect gelation time.

Rosemary 5.1616

672.4 5.1484

(Fridge, Foil 5.1352

Covered 5.1984

616.5 5.201

storage) 5.2036

Lemongrass 5.1871

640.5 5.1824

(Fridge, Foil 5.1776

Covered 5.2098

627.7 5.2126

storage) 5.2154

Example 11. Preparation of Silk Gels

Additional gels may be prepared according to Table 60, Table 61, Table 62, and Table 63.

Gels of the present disclosure can be made with about 0.5% to about 8% silk solutions. Gels of the present disclosure can be made with ascorbyl glucoside at concentrations of about 0.67% to about 15% w/v. Gels of the present disclosure be clear/white in color. Gels of the present disclosure can have a consistency that is easily spread and absorbed by the skin. Gels of the present disclosure can produce no visual residue or oily feel after application. Gels of the present disclosure do not brown over time.

Silk gels with essential oils were prepared by diluting a silk solution of the present disclosure to 2%. Vitamin C was added to the solution and allowed to dissolve. The essential oil was added, stirred and dissolved. The solution was aliquot into jars.

Example 12. Coating Fabrics with Aqueous Silk Solutions

Silk Solution and Silk Gel Application to Fabric and Yarn Samples

Three 50 mm diameter fabric samples from each of three different fabric materials, cotton, polyester, and nylon/LYCRA®, were placed in plastic containers, about 0.3 mL of about 5.8% silk fibroin solution was deposited using a 1 mL syringe and 18-gauge needle on two samples of each material, and allowed to sit for about 1 minute. About 0.3 mL of denatured alcohol (containing methanol and ethanol) was then deposited using a 1 mL syringe and 30-gauge needle on one of the silk-coated samples of each material.

In an additional experiment, silk gel with Rosemary Essential Oil (water, silk, ascorbyl glucoside, rosemary essential oil) was collected on a tip and applied to half the length of 2 pieces of 400 μιτι tencel yarn. One sample was then wetted with about 0.3 mL alcohol.

Silk Solution Dip Test

Polyester fabric samples were dipped in silk fibroin solutions of varying concentration. Samples were placed in incubator with air flow on foil and allowed to dry at about 22.5 °C for about 15.5 hours. Change in mass before and after silk coating was measured.

Silk Solution Spray Test

A spray test was performed to verify the handle impact of silk fibroin solution sprayed on polyester fabric. About 0.5% silk fibroin solution was applied to a 4 inch by 4 inch square of polyester fabric using a spray gun from a distance of about 10 inches. Three passes were completed from left to right and from right to left (six passes total). Samples were placed in a 50 °C oven on aluminum foil over a water bath for about 1.5 hours. Methods were repeated with a second polyester fabric sample with an about 5.8% silk fibroin solution spray application. No change in material hand was observed in samples sprayed with either 0.5% or 5.8% solutions. Perceived increase in materials smoothness was observed for samples sprayed with either the 0.5% and 5.8% solutions.

Example 13. Optimized Fabric Coating Processes

The coating processes described in Table 67 were used to produce multiple fabric samples for performance testing, as described in more detail below.

Table 67. Coating Processes.

1 Spray

1 1 Material for coating

1.1.1 cork board 24" χ 36" Hobby Lobby part 132894

1.1.2 Covered the cork board with polyester interlock fabric

1.1.3 Saw horse for support

1.1.4 Several clamps for holding cork panel to saw horse

1.1.5 Double filter to remove oil residue from compressor and

dehumidificaton salt

1.1.6 Iwata eclipse MP-CS airbrush

1.1.7 Husky 30.3 liter tank compression system

1.1.8 Push pin to hold fabric on cork panel Hobby Lobby part

#523456

1 2 Material for preparation

1.2.1 Scissor

1.2.2 Ruler

1.2.3 Balance AWS model Pnx-203

1 3 Material for drying

1.3.1 Wolf stove set up at 150 °F maintaining 71-78 °C with fan system.

1.3.2 Flat baking sheet

1.3.3 Aluminum foil

1.3.4 SC 307T thermometer with probe

1 4 Execution

1.1.1 lay fabric to be coated on top of cork panel covered with

polyester fabric

1.1.2 secure fabric with pin to the cork panel

1.1.3 set compressor with oil and humidity filters 1.1.4 set air pressure supply to 55 psi

1.1.5 load solution to airbrush gun

1.1.6 position airbrush gun approximately 10 inches from board

1.1.7 pull the airbrush gun trigger and over spray 2 inches side to side the fabric to be coated

1.1.8 remove pin from cork panel and place coated fabric on aluminum foil

1.1.9 place coated fabric in oven for 30-60 min at 150 °C

Stencil/Spray

2.1 Material for coating

2.1.1 cork board 24" χ 36" Hobby Lobby part 132894

2.1.2 Covered the cork board with polyester interlock fabric

2.1.3 Saw horse for support

2.1.4 Several clamps for holding cork panel to saw horse

2.1.5 Double filter to remove oil residue from compressor and dehumidification salt

2.1.6 Iwata eclipse MP-CS airbrush

2.1.7 Husky 30.3 liter tank compression system

2.1.8 Push pin to hold fabric on cork panel Hobby Lobby part

#523456

2.1.9 Stencil pattern SKU#75244 Lincaine 12"x 24"x 0.020"

Hobby Lobby

2.2 Material for preparation

2.2.1 Scissor

2.2.2 Ruler

2.2.3 Balance AWS model Pnx-203

2.3 Material for drying

2.3.1 Wolf stove set up at 150 °F maintaining 71-78 °C with fan system.

2.3.2 Flat baking sheet

2.3.3 Aluminum foil

2.3.4 SC 307T thermometer with probe

2.4 Execution

2.4.1 lay fabric to be coated on top of cork panel covered with polyester fabric

2.4.2 lay stencil pattern on top of fabric

2.4.3 secure stencil with pin to the cork panel

2.4.4 set compressor with oil and humidity filters

2.4.5 set air pressure supply to 55 psi

2.4.6 load solution to airbrush gun

2.4.7 position airbrush gun approximately 10 inches from board

2.4.8 pull the airbrush gun trigger and over spray 2 inches side to side the fabric to be coated

2.4.9 remove pin from cork panel and place coated fabric on aluminum foil

2.4.10 place coated fabric in oven for 30-60 min at 150 °C

Screen print

3.1 Material for coating

3.1.1 cork board 24" χ 36" Hobby Lobby part 132894

3.1.2 Covered the cork board with polyester interlock fabric 3.1.3 Saw horse for support

3.1.4 Several clamps for holding cork panel to saw horse

3.1.5 screen print frame 12" χ 18" part# 4710 made by Speed Ball

3.1.6 silicon spatula

3 2 Material for preparation

3.2.1 Scissor

3.2.2 Ruler

3.2.3 Balance AWS model Pnx-203

3 3 Material for drying

3.3.1 Wolf stove set up at 150 °F maintaining 71-78 °C with fan system.

3.3.2 Flat baking sheet

3.3.3 Aluminum foil

3.3.4 SC 307T thermometer with probe

3 4 Execution

3.4.1 lay fabric to be coated on top of cork panel covered with polyester fabric

3.4.2 lay screen print frame on top of fabric

3.4.3 load solution to one edge of the screen print frame

3.4.4 with a silicon spatula move solution across the screen print frame until the entire fabric to be coated surface is covered

3.4.5 remove screen print frame and place coated fabric on

aluminum foil

3.4.6 place coated fabric in oven for 30-60 min at 150 °C

Bath

4 1 Material for coating

4.1.1 cork board 24" χ 36" Hobby Lobby part 132894

4.1.2 Covered the cork board with polyester interlock fabric

4.1.3 Saw horse for support

4.1.4 Several clamps for holding cork panel to saw horse

4.1.5 Paint tray liner Item #: 170418 Model #: LOWES0- PK170418 at Lowes Hardware

4.1.6 Noodle making machine Imperia model #15-4590

4 2 Material for preparation

4.2.1 Scissor

4.2.2 Ruler

4.2.3 Balance AWS model Pnx-203

4 3 Material for drying

4.3.1 Wolf stove set up at 150 °F maintaining 71-78 °C with fan system.

4.3.2 Flat baking sheet

4.3.3 Aluminum foil

4.3.4 SC 307T thermometer with probe

4 4 Execution

4.4.1 load silk solution inside the paint tray liner well

4.4.2 immerse the fabric sample to be coated inside the silk

solution until it is all saturated

4.4.3 pass the saturated fabric between pressure roller (noodle making machine) to remove any excess solution

4.4.4 place coated fabric on aluminum foil I 4.4.5 place coated fabric in oven for 30-60 min at 150 °C |

The products produced using the coating processes described above were tested for accumulative one-way transport capability (or index) and other properties using Association of Textile, Apparel & Materials Professionals (AATCC) test method 195- 2012 for the measurement, evaluation, and classification of liquid moisture management properties of textile fabrics. The details of the test methods are available from AATCC, and a synopsis of the methods and calculations is provided here. The absorption rate (ART) (top surface) and (ARB) (bottom surface) is defined as the average speed of liquid moisture absorption for the top and bottom surfaces of the specimen during the initial change of water content during a test. The accumulative one-way transport capability (R) is defined as the difference between the area of the liquid moisture content curves of the top and bottom surfaces of a specimen with respect to time. The bottom surface (B) is defined for testing purposes as the side of the specimen placed down against the lower electrical sensor which is the side of the fabric that would be the outer exposed surface of a garment when it is worn or product when it is used. The top surface (T) for testing purposes is defined as the side of a specimen that, when the specimen is placed on the lower electrical sensor, is facing the upper sensor. This is the side of the fabric that would come in contact with the skin when a garment is worn or when a product is used. The maximum wetted radius (MWRT) and (MWRB) (mm) is defined as the greatest ring radius measured on the top and bottom surfaces. Moisture management is defined, for liquid moisture management testing, as the engineered or inherent transport of aqueous liquids such as perspiration or water (relates to comfort) and includes both liquid and vapor forms of water. The overall (liquid) moisture management capability (OMMC), an index of the overall capability of a fabric to transport liquid moisture as calculated by combining three measured attributes of performance: the liquid moisture absorption rate on the bottom surface (ARB), the one-way liquid transport capability (R), and the maximum liquid moisture spreading speed on the bottom surface (SSB). The spreading speed (SSi) is defined as the accumulated rate of surface wetting from the center of the specimen where the test solution is dropped to the maximum wetted radius. The total water content (U) (%) is defined as the sum of the percent water content of the top and bottom surfaces. The wetting time (WTT) (top surface) and (WTB) (bottom surface) is defined as the time in seconds when the top and bottom surfaces of the specimen begin to be wetted after the test is started.

A moisture management tester (MMT) is used to perform the test. The accumulative one-way liquid transport capability (R) is calculated as: [Area (UB) - Area (U T )]/total testing time. The OMMC is calculated as: OMMC = Ci* AR B _ndv + Ci Rnvd + C3* SSB ndv, where Ci, C 2 , and C3 are the weighting values * for ARe ndv, Rndv and SSe ndv; (ARB) = absorption rate; (R) = one-way transport capability, and (SSB) = spreading speed. Detailed calculations of these parameters, and other parameters of interest, are provided in AATCC test method 195-2012.

A description of the samples used is given in Table 68.

Table 68. Description of samples.

The results of the tests are depicted in FIG. 33 A through FIG. 62B and illustrate the superior performance of silk coated fabric, including superior performance with respect to accumulative one-way transport capability (index) and overall moisture management capability.

Example 14. Antimicrobial Properties of Silk Coatings on Fabrics

The antimicrobial properties of silk coatings were testing on four materials: a cotton/LYCRA jersey (15051201), a cotton/LYCRA jersey with 1% silk fibroin solution (sfs) bath coating (15070701), a polyester/LYCRA finish after final setting (15042003), and a polyester/LYCRA semi-finished 1% sfs bath coating (15070702) (wherein LYCRA is the trade name of a polyester-polyurethane copolymer). AATCC test method 100-2012 for the assessment of antibacterial finishes on textile materials was used. The details of the test method are available from AATCC. Briefly, the tests were performed using tryptic soy broth as a growth medium, a sample size of 4 layers, autoclave sterilization, 100 mL Letheen broth with Tween for neutralization, a target inoculation level of 1-2 χ 10 5 CFU/mL, 5% nutrient broth as an inoculent carrier and dilution medium, a contact time of 18 to 24 hours, and a temperature of 37 +/- 2 °C.

The results of the tests are summarized in Table 69 and are depicted in FIG. 63 to FIG. 67, and illustrate the superior antimicrobial performance of the silk-coated fabrics.

Table 69. Antimicrobial test results.

150707 Staphylococcus aureus ATCC 1.23E+05 1.03E+04 91.63%

02 6538

Klebsiella pneumoniae ATCC 1.65E+05 2.33E+05 -40.91%

4352

Example 15. Methods of Preparing Fabrics with Silk Coatings

A method for preparing an aqueous solution of pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from about 6 kDa to about 17 kDa includes the steps of: degumming a silk source by adding the silk source to a boiling (100 °C) aqueous solution of sodium carbonate for a treatment time of between about 30 minutes to about 60 minutes; removing sericin from the solution to produce a silk fibroin extract comprising non-detectable levels of sericin; draining the solution from the silk fibroin extract; dissolving the silk fibroin extract in a solution of lithium bromide having a starting temperature upon placement of the silk fibroin extract in the lithium bromide solution that ranges from about 60 °C to about 140 °C; maintaining the solution of silk fibroin-lithium bromide in an oven having a temperature of about 140 °C for a period of at least 1 hour; removing the lithium bromide from the silk fibroin extract; and producing an aqueous solution of silk protein fragments, the aqueous solution comprising: fragments having an average weight average molecular weight ranging from about 6 kDa to about 17 kDa, and wherein the aqueous solution of pure silk fibroin-based protein fragments comprises a polydispersity of between about 1.5 and about 3.0. The method may further comprise drying the silk fibroin extract prior to the dissolving step. The aqueous solution of pure silk fibroin-based protein fragments may comprise lithium bromide residuals of less than 300 ppm as measured using a high-performance liquid chromatography lithium bromide assay. The aqueous solution of pure silk fibroin-based protein fragments may comprise sodium carbonate residuals of less than 100 ppm as measured using a high- performance liquid chromatography sodium carbonate assay. The method may further comprise adding a therapeutic agent to the aqueous solution of pure silk fibroin-based protein fragments. The method may further comprise adding a molecule selected from one of an antioxidant or an enzyme to the aqueous solution of pure silk fibroin-based protein fragments. The method may further comprise adding a vitamin to the aqueous solution of pure silk fibroin-based protein fragments. The vitamin may be vitamin C or a derivative thereof. The method may further comprise adding an alpha hydroxy acid to the aqueous solution of pure silk fibroin-based protein fragments. The alpha hydroxy acid may be selected from the group consisting of gly colic acid, lactic acid, tartaric acid and citric acid. The method may further comprise adding hyaluronic acid or its salt form at a concentration of about 0.5% to about 10.0% to the aqueous solution of pure silk fibroin-based protein fragments. The method may further comprise adding at least one of zinc oxide or titanium dioxide.

A method for preparing an aqueous solution of pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from about 17 kDa to about 39 kDa includes the steps of: adding a silk source to a boiling (100 °C) aqueous solution of sodium carbonate for a treatment time of between about 30 minutes to about 60 minutes so as to result in degumming; removing sericin from the solution to produce a silk fibroin extract comprising non-detectable levels of sericin; draining the solution from the silk fibroin extract; dissolving the silk fibroin extract in a solution of lithium bromide having a starting temperature upon placement of the silk fibroin extract in the lithium bromide solution that ranges from about 80 °C to about 140 °C; maintaining the solution of silk fibroin-lithium bromide in a dry oven having a temperature in the range between about 60 °C to about 100 °C for a period of at least 1 hour; removing the lithium bromide from the silk fibroin extract; and producing an aqueous solution of pure silk fibroin-based protein fragments, wherein the aqueous solution of pure silk fibroin-based protein fragments comprises lithium bromide residuals of between about 10 ppm and about 300 ppm, wherein the aqueous solution of silk protein fragments comprises sodium carbonate residuals of between about 10 ppm and about 100 ppm, wherein the aqueous solution of pure silk fibroin-based protein fragments comprises fragments having an average weight average molecular weight ranging from about 17 kDa to about 39 kDa, and wherein the aqueous solution of pure silk fibroin-based protein fragments comprises a polydispersity of between about 1.5 and about 3.0. The method may further comprise drying the silk fibroin extract prior to the dissolving step. The aqueous solution of pure silk fibroin-based protein fragments may comprise lithium bromide residuals of less than 300 ppm as measured using a hi gh- performance liquid chromatography lithium bromide assay. The aqueous solution of pure silk fibroin-based protein fragments may comprise sodium carbonate residuals of less than 100 ppm as measured using a high-performance liquid chromatography sodium carbonate assay. The method may further comprise adding a therapeutic agent to the aqueous solution of pure silk fibroin-based protein fragments. The method may further comprise adding a molecule selected from one of an antioxidant or an enzyme to the aqueous solution of pure silk fibroin-based protein fragments. The method may further comprise adding a vitamin to the aqueous solution of pure silk fibroin-based protein fragments. The vitamin may be vitamin C or a derivative thereof. The method may further comprise adding an alpha hydroxy acid to the aqueous solution of pure silk fibroin-based protein fragments. The alpha hydroxy acid may be selected from the group consisting of gly colic acid, lactic acid, tartaric acid and citric acid. The method may further comprise adding hyaluronic acid or its salt form at a concentration of about 0.5% to about 10.0% to the aqueous solution of pure silk fibroin-based protein fragments. The method may further comprise adding at least one of zinc oxide or titanium dioxide.

A method for preparing an aqueous solution of pure silk fibroin-based protein fragments having an average weight average molecular weight ranging from about 39 kDa to about 80 kDa, includes the steps of: adding a silk source to a boiling (100 °C) aqueous solution of sodium carbonate for a treatment time of about 30 minutes so as to result in degumming; removing sericin from the solution to produce a silk fibroin extract comprising non-detectable levels of sericin; draining the solution from the silk fibroin extract; dissolving the silk fibroin extract in a solution of lithium bromide having a starting temperature upon placement of the silk fibroin extract in the lithium bromide solution that ranges from about 80 °C to about 140 °C; maintaining the solution of silk fibroin-lithium bromide in a dry oven having a temperature in the range between about 60 °C to about 100 °C for a period of at least 1 hour; removing the lithium bromide from the silk fibroin extract; and producing an aqueous solution of pure silk fibroin- based protein fragments, wherein the aqueous solution of pure silk fibroin-based protein fragments comprises lithium bromide residuals of between about 10 ppm and about 300 ppm, sodium carbonate residuals of between about 10 ppm and about 100 ppm, fragments having an average weight average molecular weight ranging from about 40 kDa to about 65 kDa, and wherein the aqueous solution of pure silk fibroin-based protein fragments comprises a polydispersity of between about 1.5 and about 3.0. The method may further comprise drying the silk fibroin extract prior to the dissolving step. The aqueous solution of pure silk fibroin-based protein fragments may comprise lithium bromide residuals of less than 300 ppm as measured using a high-performance liquid chromatography lithium bromide assay. The aqueous solution of pure silk fibroin-based protein fragments may comprise sodium carbonate residuals of less than 100 ppm as measured using a high-performance liquid chromatography sodium carbonate assay. The method may further comprise adding a therapeutic agent to the aqueous solution of pure silk fibroin-based protein fragments. The method may further comprise adding a molecule selected from one of an antioxidant or an enzyme to the aqueous solution of pure silk fibroin-based protein fragments. The method may further comprise adding a vitamin to the aqueous solution of pure silk fibroin-based protein fragments. The vitamin may be vitamin C or a derivative thereof. The method may further comprise adding an alpha hydroxy acid to the aqueous solution of pure silk fibroin-based protein fragments. The alpha hydroxy acid may be selected from the group consisting of gly colic acid, lactic acid, tartaric acid and citric acid. The method may further comprise adding hyaluronic acid or its salt form at a concentration of about 0.5% to about 10.0% to the aqueous solution of pure silk fibroin-based protein fragments. The method may further comprise adding at least one of zinc oxide or titanium dioxide.

Example 16. Characterization of Silk Coatings on Polyester

A summary of the results from studies of silk coatings on polyester are given in Table 70 and Table 71. The results shown in FIG. 68 and FIG. 69 illustrate that the accumulative one way transport index and OMMC performance is maintained even at 50 wash cycles. Additional test results are shown in FIG. 70 to FIG. 77. The antimicrobial performance of the silk coated polyester fabrics are maintained to 25 to 50 washing cycles, as shown in FIG. 78 and FIG. 79. The results illustrate the surprising improvement in moisture management properties, as well as the surprising result that the improved properties survive many wash cycles.

Attorney Docket No. 032272-5008-WO

Table 70. Test results for semifinished polyester with 1% silk solution coating.

Testing Results: Semifinished polyester with 1% silk solution coating

Number of

Washes

0 Cycles

10 Cycles

25 Cycles

50 Cycles

DBl/ 99944375.1 367

Attorney Docket No. 032272-5008-WO

Table 71. Test results for wicking finished polyester without silk coating.

Testing Results: Wicking Finished Polyester

Number of

Washes

0 Cycies

25 Cycles

50 Cycles

DBl/ 99944375.1 368

Example 17. Characterization of Silk Coatings on Polyester Fabrics

Scanning electron microscopy (SEM) analysis was performed using a Hitachi S- 4800 field-emission SEM (FE-SEM) operated at 2 kV accelerating voltage. Pieces from each sample were sectioned using a razor blade and placed on carbon adhesive tape mounted on aluminum SEM stubs. A coating of iridium approximately 2 nm thick was applied via sputter deposition in order to minimize the buildup of surface charge.

The samples used in the SEM study are described in Table 72. SEM micrographs for fabric samples are shown in FIG. 80 to FIG. 120. Table 72. Fabric samples tested by scanning electron microscopy and optical

profilometry.

The fabric SEM results show that the silk solution has very clearly been deposited along and between individual polyester fibers. The use of 0.1% silk solution results in less coating than 1.0% silk solution. The use of a bath for 0.1% silk solution, with an average molecular weight of 41 kDa, results in uniform coating along fibers with large, smooth features. The use of a spray with a 0.1% silk solution, with an average molecular weight of 41 kDa, in coating along fibers as well as connected, webbed coating between fibers. The use of a spray for 0.1% silk solution, with an average molecular weight of 11 kDa, results in uniform coating along fibers with small, spotted/ribbed features. The use of a stencil for 0.1%) silk solution, with an average molecular weight of 11 kDa, results in coating along fibers that has clear edges and delineation between coated and non coated sides. The use of a bath for 1.0% silk solution, with an average molecular weight of 41 kDa, results in thick coating along fibers as well as thick connected, webbed coating between fibers. The use of a bath for 1.0% silk solution, with an average molecular weight of 11 kDa, results in coating along all sides of individual fibers. Coating appears uniform on surface with many single point extrusions. The use of a spray for 1.0% silk solution, with an average molecular weight of 41 kDa, results in coating along fibers as well as connected, webbed coating between fibers, which was thicker than that observed using 0.1% silk solution. The use of a stencil for 1.0% silk solution, with an average molecular weight of 41 kDa, results in coating along fibers and between fibers, and the coating appears well organized.

The SEM results demonstrate that the silk coating has been applied as an even, thin, uniform coating to the fibers of the fabric. This illustrates the surprising result that the silk coating was applied to the fibers without the use of any additives or cross-linking, using a water based delivery system.

Example 18. Characterization of Silk Coatings on Polyester Films

The film samples are described in Table 73.

Table 73. Film samples tested by scanning electron microscopy and optical profilometry.

The results show that the silk coatings are applied uniformly. Little to no variation is observed in the characteristics or topology of the coated polyester films. Surprisingly, the coating is even, uniform, and thin. Furthermore, surprising, the silk coated the fibers without any additives or cross-linking using a water-based system.

Optical profiling was carried out using a Zygo New View 6200 optical profilometer. Two locations on each sample were randomly selected and measured with 10X magnification. The results are shown in FIG. 121 to FIG. 144. The results indicate that the silk-coated samples have a homogeneous deposition of silk fibroin. Surface roughness features observed in the control are visible after silk coating on Mylar films, which is consistent with the presence of a relatively thin silk film that is forming a conformal coating on Mylar. The results substantiate the uniformity of the coating, and demonstrate that silk can be stenciled into discrete locations.

Contact profilometry was performed and the cross-sectioned samples were examined by SEM. Results are shown in FIG. 145 to FIG. 148. For sample FIL-10- SPRAY-B-10MYL, the thickness ranged from approximately 260 nm to 850 nm in 4 locations analyzed. For sample FIL-10-BATH-B-OlMYL, the coating ranged from approximately 140 nm to 400 nm in 4 locations. SEM images from cross-sections show similar trends, with one location on sample FIL-10-SPRAY-B-lOMYL having a cross- section that measures approximately 500 nm and one on FIL-10-BATH-B-OlMYL measuring approximately 180 nm.

Example 19. Preparation of Silk Fibroin Solutions with Higher Molecular Weights

The preparation of silk fibroin solutions with higher molecular weights is given in Table 74.

Table 74. Preparation and properties of silk fibroin solutions.

Group E FIL 15 100 RT 60 °C sol'n 94.8 2.62

Example 20. Silk Coatings on Natural Fabrics

The coating of natural fabric with silk fibroin-based protein fragment solutions and the resulting properties are illustrated in Table 75, Table 76, FIG. 149, and FIG. 150. The results demonstrate that silk fibroin solutions can coat cotton-Lycra natural fabrics including LUON and POWER LUXTREME.

Table 75. Silk fibroin coated fabrics.

Attorney Docket No. 032272-5008-WO

Table 76. Test results for silk fibroin coated fabrics.

DBl/ 99944375.1 373

Example 21. Manufacturing Processes for Silk Coated Textiles and Leathers

Silk coated textiles and leathers may be manufactured on larger scales according to the methods provided herein using standard textile and leather manufacturing equipment with the addition of silk fibroin-based protein fragment coating steps (e.g., via bath, stencil, or spray methods). For example, a tentering and stentering frame, representing a typical process for applying the silk solution in a continuous process, may include the following units:

An unwinding device used to unroll the fabric supply in a roll configuration;

A feeding system used to control the feed rate of fabric;

A material compensator used to maintain consistent the fabric tension;

A coating machine used to apply the silk solution (i.e., silk fibroin-based protein fragments) in different state (liquid or foam) to the fabric;

A measuring system used to control the amount of silk solution applied;

A dryer used to cure or dry the silk solution on the fabric;

A cooling station used to bring the fabric temperature closed to room value;

A steering frame used to guide the fabric to the rewinding device and maintain straight edges; and

A rewinding used to collect the coated fabric in roll.

Frames may also include rollers and sprayers for application of silk fibroin-based protein fragment coating, UV irradiators for curing of silk and/or other fabric additives (e.g., in a chemical cross-linking step), and RF irradiators (e.g., using microwave irradiation) for drying and chemical cross-linking.

Tentering and stentering equipment and other equipment capable of coating silk solutions onto continuous flat fabric or textile material, including leather, according to the above process, is available from the following suppliers: Aigle, Amba Projex, Bombi, Bruckner, Cavitec, Crosta, Dienes Apparatebau, Eastsign, Europlasma, Fermor, Fontanet, Gaston Systems, Hansa Mixer, Harish, Has Group, Icomatex, Idealtech, Interspare, Isotex, Klieverik, KTP, MP, Mageba, Mahr Feinpruef, Matex, Mathis, Menzel LP, Meyer, Monforts, Morrison Textile, Mtex, Muller Frick, Muratex Textile, Reliant Machinery, Rollmac, Salvade, Sandvik Tps, Santex, Chmitt-Machinen, Schott & Meissner, Sellers, Sicam, Siltex, Starlinger, Swatik Group India, Techfull, TMT Manenti, Unitech Textile Machinery, Weko, Willy, Wumag Texroll, Yamuna, Zappa, and Zimmer Austria.

Equipment capable of drying silk solution coatings on fabric or other textile materials, including leather, is available from the following suppliers: Alea, Alkan Makina, Anglada, Atac Makina, Bianco, Bruckner, Campen, CHTC, CTMTC, Dilmenler, Elteksmak, Erbatech, Fontanet, Harish, Icomatex, Ilsung, Inspiron, Interspare, Master, Mathis, Monfongs, Monforts, Salvade, Schmitt-Maschinen, Sellers, Sicam, Siltex, Swastik Group India, Tacome, Tubetex, Turbang, Unitech Textile Machinery, and Yamuna.

Example 22. Flammability Testing for Silk Coated Textiles

Flame resistant testing of textiles and other products of the invention, coated with silk fibroin-based protein fragments prepared using any of the methods disclosed herein may be performed using methods known to those of skill in the art, and may provide results that demonstrate flame resistant property for textiles and other products coated with silk fibroin-based protein fragments relative to uncoated textiles. Flame resistant testing of fabrics coated with silk fibroin-based protein fragments may be determined, for example, using 16 C.F.R. 1615 or 16 C.F.R. 1616 or other suitable versions of flame resistant testing standards known to those of skill in the art. Briefly, a piece of textile coated with silk fibroin-based protein fragments prepared using any of the methods disclosed herein, after 25 washing cycles, is cut into 3.5 inches wide X 10 inches long rectangle specimen. One specimen is suspended in a test chamber through a specimen holder. The test chamber should be a steel chamber and at least with dimensions 32.9 cm. (1215/16 in.) wide, 32.9 cm. (12 15/16 in.) deep, and 76.2 cm. (30 in.) long. The specimen is suspended in the test chamber vertically along the length of the specimen, and is lit up by a burner. Then the char length is measured. The testing is repeated for 5 times and average char length is calculated based on the individual result. The same testing is performed with a textile without a silk coating as a control. The specimen after 5, 10, 15, 20, 30, 35, 40, 45, and 50 washing cycles are also tested. The average char length needs to be less than 7 inches (177.8 mm) to be determined as flame resistant. The char length is the value used to evaluate passing grade for sleepwear flammability.

Two representative fabrics were used in the flammability tests. A cotton interlock fabric coated with 1% silk fibroin solution (16021103) was compared to the same fabric without (16021101) coating. A polyester double knit fabric coated with 1% silk fibroin solution (16021104) was compared to the same fabric without coating (16021102) with 1% silk fibroin solution. The SFS used to coat the fabrics in these experiments had a weight average molecular weight range of about 32-44 kDa.

Results for a cotton interlock fabric are shown in FIG. 151 and FIG. 152. The coating with silk fibroin-based protein fragments does not adversely affect the flammability of the fabric. Similarly, the results for a polyester double-knit fabric, shown in FIG. 153 and FIG. 154, also indicate that coating with silk fibroin-based protein fragments does not adversely affect the flammability of the fabric. No significant differences between samples made from same material (cotton or polyester) were observed. The differences between fabric made with the same material for afterglow and after flame time were not significant. Cotton, as expected, was flammable and none of the samples were left after the test.

Example 23. Abrasion Testing for Silk Coated Textiles

Abrasion testing of textiles and other products coated with silk fibroin-based protein fragments prepared using any of the methods disclosed herein may be performed using methods known to those of skill in the art, and may provide results that demonstrate improved resistance to abrasion for textiles and other products coated with silk fibroin- based protein fragments relative to uncoated textiles. Improved resistance to abrasion is useful in applications such as upholstery, including upholstery designed for home, automotive, aircraft, or other uses. Abrasion testing of fabrics coated with silk fibroin- based protein fragments may be determined, for example, using ASTM Method D4966-12 (Standard Test Method for Abrasion Resistance of Textile Fabrics (Martindale Abrasion Tester Method), ASTM, 2013) or other suitable versions of ASTM Method D4966. Briefly, abrasion resistance is measured by subjecting a textile specimen to a rubbing motion that takes the form of a geometric figure, beginning with a straight line, which becomes a gradually widening ellipse until it forms another straight line in the opposite direction, after which the motion reverses repeatedly. The rubbing occurs under known conditions of pressure and abrasive action. A Martindale Abrasion Tester (commercially available from James H. Heal Co., Ltd.) is used for testing. Resistance to abrasion is evaluated.

Four samples were tested using ASTM Method D4966-12. Sample 16021101 was a 100% cotton interlock fabric. Sample 16021102 was a 100% polyester double knit. Sample 16021501 was the 100% cotton interlock fabric after bath coating (as described herein) with 1% silk fibroin solution (SFS). Sample 16021502 was the 100% polyester double knit fabric after bath coating (as described herein) with 1% SFS. The SFS used to coat the fabrics in these experiments had a weight average molecular weight range of about l l kDa.

Testing Testing Results:

Results: 16021101 16021102

Specimen 1 943 rubs Specimen 1 2,000 rubs

Specimen 2 1,253 rubs Specimen 2 1,862 rubs

Specimen 3 737 rubs Specimen 3 2,637 rubs

Average 978 rubs Average 2, 166 rubs standard standard

deviation 260 deviation 413

Testing Results: 16021501 Testing Results: 16021502

Specimen 1 805 rubs Specimen 1 4,910rubs

Specimen 2 897 rubs Specimen 2 3,090 rubs

Specimen 3 797 rubs Specimen 3 6,000 rubs

Average 833 rubs Average 4,667 rubs standard standard

deviation 56 deviation 1,470

The foregoing results are illustrated in FIG. 155 and FIG. 156, which show the improved abrasion resistance of polyester after coating with a silk fibroin-based solution. Example 24: Surface analysis of coated fabrics to demonstrate the applied coatings

SEM images of the back side of certain coated fabrics disclosed in Table 77 were obtained at various magnifications as shown in FIGS. 157 to 182.

Table 77

Upon examination of the figures, there are some formations visible on top of controls 16041301 and 16041304, they can be identified as cyclic trimer, which may be a polyester byproduct, salt, or excess dye. The low molecular weight coated fibers present broken bridges between fibers. It may be noted that at low concentration the low molecular weight conglomerates in globs; more than at equivalent concentrations with the medium molecular weight. The medium molecular weight fibers have excellent polyester fibers at any concentration and temperature and a network of bridging fibers may be more visible at higher concentrations. Example 25: Examination of the effect of various parameters on SFS coatings

This experiment tested the impact of SFS molecular weight with a 1% concentration at 3 different drying and curing temperature with different drying and curing temperature time. The fabrics were characterized by mass and Liquid Moisture Management Properties of Textile Fabrics (MMT) following AATCC Test Method 195- 2012 (Tables 78-80).

Table 78 Experimental parameters Variables silk solution concentration 1%

silk solution molecular weight medium low

Wet pick up at 50 setting on padder

Temperature @ heat setting (C) 65 150 200

Curing time (min) 10 5 3

This experiment tested the impact of temperature on silk coated fabric.

Material 15042001 - Non-wicking finish - fabric having a composition of 82 % polyester and 18% elastane.

Material TFF-01-0012/TFF-01-0010 - 6% silk solution, medium molecular weight.

Material TFF-01-0013 - 6% silk solution, low molecular weight.

Table 79

The samples mass recording is reported in the following table for each variable Table 80

The collective results are provided in FIG. 193 for each tested material. However, sample 16040102 did not produce acceptable results and 15042001 is provided as a reference, which is not coated.

The results of these analyses are provided in table form in FIG. 194. Specifically, FIG. 194 describes the grading for each tested sample (medium and low molecular weight samples) in terms of wetting (top and bottom), absorption rate (top and bottom), wetted radius (top max and bottom max), spreading speed (top and bottom), accumulative one- way transport, and overall moisture management capability (OMMC).

From the presented results the SFS coated fabric has an impact on the MMT grading of fabric, significantly improving the accumulative one way transport index from the non- coated standard of grade 2 to the SFS coated grades of 4-5 depending on molecular weight and curing time and temperature. While with the OMMC index the non-coated standard has a grade of 1 compared to the SFS coated grades of 3 independent of tested variables.

Example 26: Impact of SFS concentration at low and medium molecular weight samples.

This experiment tested the impact of SFS concentration at 2 molecular weights using the same drying and curing temperature time. The fabrics were characterized by mass and Liquid Moisture Management Properties of Textile Fabrics (MMT) following AATCC Test Method 195-2012.

The experimental parameters are provided in Table 81. Table 81

The samples mass recording is reported in the following table for each variable tested (Table 82).

Table 82

Sample test results for each variable tested are reported in the table set forth in FIG. 195, where sample 15042001 is a non-coated control. Sample test grading for each variable tested are reported in the table provided in FIG. 196. From the presented results the SFS coated fabric has an impact on the MMT grading of fabric, significantly improving the accumulative one-way transport index from the non- coated standard of grade 2 to the SFS coated grades of 5 depending on molecular weight (low vs. medium) and SFS concentration. While with the OMMC index the non-coated standard has a grade of 1 compared to the SFS coated grades of 3 independent of tested variables.

Example 27: Tested impact of curing time on coatings at two molecular weights

This experiment tested the impact of curing time at 150 °C and 200 °C with SFS at

1% concentration at two molecular weights. The fabrics were characterized by mass and

Liquid Moisture Management Properties of Textile Fabrics (MMT) following AATCC

Test Method 195-2012.

The experimental parameters are provided in Table 83.

Table 83

The samples mass recording is reported in the following table for each variable tested (Table 84).

Table 84

Sample test results for each variable tested are reported in the table set forth in FIG. 197, where samples 16041301 and 16041304 are non-coated fabrics for reference. Sample test grading for each variable tested are reported in the table provided in FIG. 198.

From the presented results the curing temperature time may reduce the MMT grading when 1% SFS coated fabric is exposed between 5-10 minutes at 150 °C or 200 °C. At the other curing time tested 3 and 5 minutes at 150 °C or 200 °C there is no apparent impact on accumulative one-way transport or OMMC grades. Example 28:

This experiment tested the impact of temperatures of 65 °C, 150 °C, and 200 °C at the minimum drying and curing time with 1 % SFS at two molecular weights. The fabrics were characterized by mass and Liquid Moisture Management Properties of Textile Fabrics (MMT) following AATCC Test Method 195-2012.

The experimental parameters are provided in Table 85.

Table 85

Padder speed (m/min) 3 3

The samples mass recording is reported in the following table for each variable tested (Table 86).

Table 86

Sample test results for each variable tested are reported in the table set forth in FIG. 199, where samples 16041301, 16041304, and 15042001 are non-coated fabrics for reference. Sample test grading for each variable tested is reported in the table provided in FIG. 200.

From the presented results the curing temperature of 65 °C, 150 °C, and 200 °C has limited to no impact on the MMT grading when 1% SFS coated fabric is exposed for respectively 3, 5, and 10 minutes. Medium molecular weight coated fabrics have faster wetting time than low molecular weight coated fabrics or non-coated control fabrics. Low molecular weight coated fabrics exhibit a faster spreading time than medium molecular weight coated fabrics or non-coated control fabrics. Medium molecular weight coated fabrics or low molecular weight coated fabrics perform equal to or better than non-coated control fabrics in terms of Accumulative One Way Transport and OMMC.

Example 29: Listing of Specific Fabrics

Table 87 includes a listing of coated and non-coated fabrics tested in the present

Examples and their associated coating process variables.

Table 87

16041305 1% SFS, medium mw silk, 200 °C, 3 min

16041306 1% SFS, medium mw silk, 150 °C, 5 min

16042501 0.075% SFS, medium mw silk skin side up

16042502 0.075%) SFS, medium mw silk skin side down

16042503 0.1%) SFS, low mw silk skin side up

16042504 0.01%) SFS, low mw silk skin side down

16050301 1% SFS, low mw silk, 200 °C 3min

16050302 0.1% SFS, low mw silk, 200 °C, 3 min

16050303 1% SFS, medium mw silk, 200 °C 3min

16050304 1% SFS, medium mw silk, 200 °C 3min

16050305 1% SFS, medium mw silk, 200 °C 3min

16050306 0.1% SFS, medium mw silk, 200 °C, 3 min

16050307 / non wicking finished, 200 °C, 3 min

15042001

16050308 / non wicking finished, 200 °C, 3 min

15042001

16050309 / non wicking finished, 200 °C, 3 min

15042001

16050310 / non wicking finished, 150 °C, 5 min

15042001

16050311 / non wicking finished, 150 °C, 5 min

15042001

16050312 / non wicking finished, 150 °C, 5 min

15042001

16050401 0.1% SFS, medium mw silk, 65 °C 10 min

16050402 0.1% SFS, medium mw silk, 150 °C 5 min

16050403 0.1% SFS, medium mw silk, 200 °C 3 min

16050404 0.25% SFS, medium mw silk, 65 °C 10 min

16050405 0.25% SFS, medium mw silk, 150 °C 5 min

16050406 0.25% SFS, medium mw silk, 200 °C 3 min 16050407 0.1% SFS, low mw silk, 65 °C 10 min

16050408 0.1% SFS, low mw silk, 150 °C 5 min

16050409 0.1% SFS, low mw silk, 200 °C 3 min

16050410 0.25% SFS, low mw silk, 65 °C 10 min

16050411 0.25% SFS, low mw silk, 150 °C 5 min

16050412 0.25% SFS, low mw silk, 200 °C 3 min

Example 30: A map of the fabric samples tested

A number of the coated and non-coated fabrics described herein were tested for anti-microbial activity. Those fabrics, and their identities and process variables, are set forth in Table 88.

Table 88

0.001

low 1.000 16040106 16040105 16041201 16040104 16041202

16041302 16041303

16040105 16050301

0.750

0.500 16040805

0.250 16050410 16050411 16050412

0.100 16050407 16040806 16050409

16042501 16050302

16042502

16040806

16050408

0.075

0.050 16040807

0.025

0.001 16040808

control

non- 15042001 16041301 16041304 antimicro finished 16050310 16050307 bial

16050311 16050308

16050312 16050309

semi15042002

finished 15042002

finished 15042003

16042003

Example 31 : Results of Liquid Moisture Management Tests

FIG. 201 provides a map of Liquid Moisture Management Test results for various coated fabrics described herein.

Example 32: Silk Fibroin Solution with Silicone Softener

The objective of this study will be to evaluate the impact to the hand of the fabric of two types of silicon softeners in conjunction with silk fibroin solution. In addition, Liquid Moisture Management testing (MMT) according to AATCC 195-2012 will be completed on the samples, and a drapability test according to the drape elevator method modified to accommodate samples dimension.

This study will be performed to evaluate the changes in hand characteristics of a fabric when commercially available silicon softeners are mixed with different percentage and molecular weight of silk fibroin solution followed by a drying and curing process. The fabrics will be characterized for Moisture Management properties and drapability.

Materials and equipment for the study include Silk Therapeutics medium molecular weight solution at 6%, Silk Therapeutics low molecular weight solution at 6%, Huntsman Ultratex CSP, Huntsman Ultratex SI, Acetic acid, Citric acid, RODI water, Fabric sample 15042001 non-wi eking finish, a permanent marker, Werner Mathis MA0881 padder/coater, curing frame, Across International Oven FO-19140, Balance Veritas M314- AI, Universal plastic pH test strip, Drape elevator test fixture, and an LG Nexus 5X phone camera.

Silk coated fabric will be prepared following SOP-TEMP-001. Silk solution concentration will be prepared at the desired concentration as reported in the table below and is mixed to the desired concentration of silicon softener as reported in Table 89. The coating solution is applied to the fabric with bath immersion and pad roller pressure setting at 50. After coating the fabric is dry/cure in the oven at 200 °C for 3 minutes.

Table 89

Experiment Variables

Post curing the fabric is left to condition at room temperature for 24 hrs. Samples are cut to 8 cm by 8 cm square and delivered to MSC lab for MMT testing. After conditioning the fabric is tested for drapability using the drape elevator test modified to accommodate the MMT sample size dimension. After placing the sample on the testing jig an image is recorded with a camera; the elevator is lowered until no more contact is made with the fabric by the elevator table and a second image is recorded. Image analysis of the fabric area is performed through Photoshop. A drape coefficient is calculated with the following formula:

Drape Coefficient = ^-si * ^ '

where Ad is the vertical projection of the draping sample, S I the area of the round sample holder, and S2 is the area of the sample.

Example 33 : Antibacterial Study

An experiment is devised for evaluating the antibacterial proliferation on SFS coated fabrics through multiple washing cycles. Specifically, the study will examine whether bacteria will adhere to silk-coated fabric following wash.

The study will mimic the bacterial deposition on textile material during regular exercise and home laundering.

The antibacterial testing will be at 0, 1, 10, and 25 minute cycles using a front loading washer with water at less than 30 °C. The fabrics will be air or tumble dried at less than 50 °C.

A 13.5 x 13.5 inch fabric swatch will spotted with eight (8) inoculation sites and tested following washing at the disclosed intervals to determine the presence and quantity of bacteria. Example 34: Drapability of Exemplary Silk Coated Fabrics.

The following coated fabrics were prepared according to the processes described herein and tested for drapability according to the method described in Mizutani, et al., "A New Apparatus for the Study of Fabric Drape." Textile Research Journal (2005) 75 : 81- 87.

The materials in the method include a sample and camera holding fixture, sample holding fixture of 5 cm in diameter, an elevator plane, and a camera. The fabric specimens were 8x8 cm 2 . The procedure included: (1) cutting the sample to 8x8 cm square (8 cm diameter may be used); (2) placing the specimen at the center of a fixture; (3) elevating the fixture to examine the draping of the specimen; and (4) capture an image of the specimen.

The images were opened in Adobe Photoshop CS5.1 and the lazo function was used to delmit the perimeter of the specimen. The measurement function was then used to count all the pixels within the selected area and such data was saved. This process was repeated for each specimen. A drape coefficient was calculated based on the following formula:

Drape Coefficient = ^-si * ^ '

where Ad is the vertical projection of the draping sample, S 1 is the area of the round sample holder, and S2 is the area of the sample. The data for such analysis is set forth in Table 90 and associated FIG. 202.

Table 90

16051 109 0.25%, medium mw silk solution, 200 °C 3 85.7 1.7 min

16051 1 15 0.25%, low mw silk solution, 200 °C 3 min 89.9 2.4

16052501 2.2% SI 69.1 4.4

16052502 2.2% SI + acetic acid 0.5% 61.7 1.9

16052503 5% CSP 61.6 4.8

16052504 5% CSP + acetic acid 1% 59.5 3.5

the foregoing study, silk solution, drying parameters, and silicone compositions were used to adjust the drapability for a variety of coated fabrics.

Example 35 : Effect of Mechanical and Steam Finishing on a Silk Coated Fabric

A sample was prepared as described herein, wherein the sample was a polyester/LYCRA non-finished fabric coated with a 1% SFS (medium molecular weight) that was dried at 200 °C for 3 minutes. In addition, the same fabric was subjected to a 41 minutes dryer cycle at normal setting on medium temperature (mechanical finishing) and to steaming on a steam table for 5 seconds (steam finishing). The resulting samples, after finishing, were examined for drapability as shown in Table 91 and in FIG. 203.

Table 91

While the mechanical finishing with the dryer reduced the drapability coefficient (i.e., less stiff fabric), the steam finishing increased the drapability coefficient (i.e., stiffer fabric). Results of experiments measuring solution depletion calculation during coating are shown in FIG. 204, and illustrate the amount of silk fibroin deposited on fabrics.

Additional results of moisture management testing of coated fabrics are given in FIG. 205 to FIG. 210.

Additional results from antimicrobial testing of coated fabrics are given in FIG.

Example 36: Effectiveness of Diluting Silk with Tap Water.

The silk compositions described herein are stable and effective when prepared with tap water.

A 1 : 1 ratio between the silicone and silk gave a softer hand to a resulting fabric with a 20: 1 ratio between silk/silicone and citric acid.

The parameters for the study between tap water and reverse-osmosis/deionized

(RODI) water are set forth in Table 92.

Table 92

The parameters for a second study are set forth in Tables 93 and 94. The results of this study are illustrated in FIG. 215. The second study relates to a water drop test on polyester/lycra knitted fabric treated with RODI water and tap water. Table 93

Table 94

The results of the foregoing study indicated that there was no difference in the resulting properties of those silk solutions prepared in RODI water as compared to unfiltered tap water. Moreover, the silk solutions did not precipitate with the use of tap water.

Example 37: A Study of Silk Solution as a Wicking Agent

Silk solutions as disclosed herein can be adopted as a wicking agent in common finishing recipes to balance the water repellency of silicone softeners.

The present test is a modification to AATCC-79-2014 that was prepared to accommodate the dimensions of the tested samples (8 x 8 cm samples), where the AATCC test is designed for a sample of 150 cm in diameter. Here, the samples are cut in 8 cm by 8 cm and placed in a drapability jig suspended on a 7 cm diameter round metal hoop so the back of the fabric has no surface contact. An RODI water drop is dispensed with an eye dropper from approximately 3 cm above the fabric. A video imaging recording captures the time from the water drop contacting the fabric until its full absorption or up to 30 seconds.

Without silk, the water drop stays on the fabric surface up to the test end of 30 seconds; while in the presence of silk the water drop is absorbed in as long as 4 seconds or as fast as 1 second depending on the tested variables.

The parameters for this study are set forth in Table 95 with the results set forth in FIGS. 212 and 213.

Table 95

16062107 0.5% low mw silk, 2.2 gr/liter Ultratex SI, 0.025 gr/liter 1 citric acid

16062108 0.5% medium mw silk, 5 gr/liter Ultratex CSP, 0.025 gr/liter 4

citric acid

Example 38: A Study of Dyeing Polyester and Nylon Fabrics Followed by the Application of Silicone and Silk Solution through Exhaust.

The objective of this study is to evaluate the application of silk fibroin solution on fabrics made with polyester/spandex and nylon/spandex. The application will take place after dyeing the fabrics at exhaust. In addition, silicon softeners will be added to the silk solution to improve the hand of the fabrics. Liquid Moisture Management testing (MMT) according to AATCC 195-2012, a drapability test according to the drape elevator method modified to accommodate samples dimension, and a water drop test will be used to characterize the fabrics.

This study was performed for research and development purposes to evaluate the feasibility to apply silk fibroin solution at exhaust post dyeing. In addition, commercially available silicon softeners were mixed with different percentage and molecular weight of silk fibroin solution to improve hand and drapability of the fabric.

Materials:

Silk Therapeutics medium molecular weight solution at 6%;

Silk Therapeutics low molecular weight solution at 6%;

Huntsman Ultratex CSP;

Huntsman Ultratex SI;

Acetic acid;

Fabric sample polyester/spandex; and

Fabric sample nylon/spandex.

Equipment: 5 pounds paddle dyer by Rome Machine Foundry Co. SN# 640115; 5 pounds pressure dyer by Optidye RS Basic Plus;

Hydroextractor;

Balance Veritas M314-AI;

Universal plastic PH test strip;

Drape elevator test fixture; and

5X phone camera.

Methods:

Nylon

The fabric sample is placed in the 5-pound paddle dryer along with enough dunnage to total 3-pound load. The tub is filled with water. The following wetting and scouring agent are added:

1.0% wetter D.75 OWG;

1.0% scour SKB OWG;

4.0% black 2RSLD OWG;

acetic acid 56% to reach PH 5.5;

2.0% softener RWS Hydrophilic OWG; and

3% fix agent ED 73% OWG.

The dyer is run at 100 F for 5 minutes. Dye is added and run for 10 minutes. The sample is heated at a rate of 4 F/minute up to 200 F. Acetic acid is added to a pH of 5.5. The sample is allowed to run for 45 more minutes.

A sample color shade is prepared and, if acceptable, the sample is allowed to cool to 160 F.

The solution is dropped and refilled than refilled and run for 5 times, with the entire process repeated 4 times.

Softener is then added (i.e., silicon and silk solution at the concentration reported in Table 96) heat to 160 °F and run for 10 minutes. Drop solution and remove fabric from the machine. Table 96

Polyester

The fabric sample is placed in the 5-pound pressure dryer along with enough dunnage to total 3-pound load. The tub is filled with water. The following wetting and scouring agent are added for pre-scouring process: 1.0% wetter and 2.0% scour.

The solution was heated to 180 °F for 20 minutes. The solution was dropped and rinsed. To the solution was added 1% wetter, acetic acid to pH 5.0, with a level er used as desired, and heated to 110 °F. Dissolved dyes were added and heated to 180 °F, with the temperature held for 10 minutes. The solution was then heated to 265 °F at 3 °F/minute and held at 265 °F for 90 minutes.

The solution was then cooled to 180 °F and the color shade was sampled. Upon acceptance, the solution was dropped and rinsed three times. The solution was further cooled to 140 °F and hydro was added for 15 minutes. The solution was again dropped and rinsed 2-3 times until clean. The solution was then cooled to 110 °F and softener was added (silicone and silk solution at the concentration reported in Table 96) for 10 minutes. The solution was dropped and the fabric was removed from the machine.

The fabric is dried by first removing excess fluid with Hydroextractor followed by a dryer cycle at normal setting with low temperature. Samples are cut to 8 cm by 8 cm square and delivered to MSC lab for MMT testing. Samples cut in 8 cm by 8 cm that are not tested for MMT are placed in the drapability jig suspended on a 7 cm diameter round metal hoop. A RODI water drop is dispensed with an eye dropper from approximately 3 cm above the fabric. A video image recording captured the time from the water drop contacting the fabric until its full absorption or up to 60 seconds.

After conditioning, the fabric is tested for drapability using the drape elevator test modified to accommodate the MMT sample size dimension. After placing the sample on the testing jig an image is recorded with a camera; the elevator is lowered until no more contact is made with the fabric by the elevator table and a second image is recorded. Image analysis of the fabric area is performed through Photoshop. A drape coefficient is calculated with the following formula:

Ad - SI

Drape Coefficient =——— * 100 where Ad is the vertical projection of the draping sample, SI the area of the round sample holder, and S2 is the area of the sample. The fabrics with a water drop test < 3 seconds and a drapability of < 90 were submitted for MMT testing.

Example 39: Bacterial Wash Adherence Study through Washing Machine Cycle

The objective of this study was to evaluate the bacterial proliferation through multiple washing cycles in the laboratory while duplicating the bacterial deposition on textile materials that take place during regular exercise.

Materials. The following list of materials were used for fabric sample preparation and study execution:

Polyester/lycra fabric 15042201;

Deionized water;

6% Mid-MW silk provided by Silk Therapeutics, Inc.;

6% Low-MW Silk provided by Silk Therapeutics, Inc.;

Launtry Permanent Marker;

Front loader washing machine LG model WM3370HWA;

AATCC detergent without optical brightener liquid H/E;

Satphylococcus aureus subsp. aureus RosenbachATCC® 6538; Inoculum carrier to be 5% Nu-broth;

Letheen broth with tween as neutralizer for enumeration;

BD Difco Leethen broth #268110; and

Concentrated Clorox regular bleach.

Equipment. The following is a list of equipment used from the fabric sample preparation and study execution:

Werner Mathis MA-881 padder/coater;

Curing frame;

Across International Oven FO-19140;

Balance Veritas M314-AI;

Universal plastic PH test strip; and

Tempo Filler and Reader from BioMerieux for enumeration. Methods.

Fabric Sample Preparation. Silk coated fabric is prepared following SOP-TEMP- 001. Silk solution concentration at 0.05% is applied to the fabric with bath immersion with the padder's roller pressure setting at 50 and 200 C curing time for 3 minutes. Fabric sample with 13.5 inches by 13.5 inches are divided with a permanent marker to delimit 8 equivalent areas.

Bacteria Inoculation. At the center for each of the 8 areas 2xl0 7 cfu of bacteria solution was inoculated. The total load per washing cycle was expected to be 1-2 xlO 8 CFU. The inoculated fabric was allowed to air dry for 60 minutes.

Washing Cycle. The inoculated fabric was placed in the washing machine with 1.8 kg of cotton towel as dunnage with 50 mL of detergent. A washing machine cycle at gentle setting with warm water at less than 30 C was completed. The inoculated fabric was removed from the washing machine and allowed to air dry for 120 minutes. After each washing cycle the dunnage was bleached with 120 mL concentrated Clorox regular bleach to eliminate any bacteria transfers from the tested specimen to the dunnage. Bacteria Enumeration. At preset intervals, from the dried inoculated fabric 2 square samples were cut out and the bacteria count was enumerated following, as a guideline, the enumeration method of AATCC 100.

Study Execution. For the fabric to be inoculated, multiple bacteria inoculation washing cycles and testing for bacteria enumeration at different intervals were executed on each tested fabric. For the fabric with no inoculation, the same washing cycle and testing for bacteria enumeration at the same intervals were used. Since at enumeration swatches of fabric were removed from the fabric, to maintain the total bacteria load per washing cycle, an additional piece of control fabric was added to the dunnage. The additional fabric was inoculated with the balance of bacteria load. For example, after 1 washing cycle the additional fabric received 4xl0 7 of bacteria load.

Methods of Analysis. Analysis was performed to determine antibacterial properties of the fabric following, as guidelines, the enumeration method of AATCC 100: Antibacterial Finishes. The fabric sample is placed in a polypropylene container with 100 mL of Letheem broth and shaken for 60 seconds. The bacteria count as then enumerated with Tempo filler reader. At each tested interval two side by side tested samples are cut out from the fabric and tested with duplicates. After each enumeration the fabric was tested for any odor intensity and for any changes between T=0 and the enumerated tested sample. Odor is evaluated on the following scale: 0 = no odor; 1 = very weak (odor threshold); 2 = weak; 3 = distinct; 4 = strong; 5 = very strong; and 6 = intolerable. After each enumeration, high resolution image recording was taken for each sample so enumerated.

The fabric surfaces were also examined during the study for both the coated and non-coated fabrics by taking microscopic images of the coated and non-coated samples prior to washing, after one washing, and after 10 washings. A qualitative analysis of the microscopic images was performed to observe the % foreign matter coverage area on the observable fibers. The coated inoculated fibers displayed little or no foreign matter on their observable surfaces as compared to the non-coated inoculated fibers. The presence of silk does not contribute to increased bacteria adherence on the fabric surface, while any bacteria that may be deposited on the surface it can be removed through a standard home laundering cycle. As described herein, bacteria did not appear to adhere to the coated materials after washing. Example 40. A Water Drop Study with Silk and Silicone Coated Fabrics.

A study was performed to determine the effect of water wicking on fabrics coated with silk and silicone that have been treated with citric acid.

As shown herein, citric acid does not function as a wicking agent. However, with a 1 : 1 ratio of silk/silicone at 0.25%, the water took a longer time to absorb than that observed with previously described water drop studies.

The parameters for a first study are set forth in Table 97 and 98. The results of this study are illustrated in FIGS. 215 and 216.

Table 97

Table 98

16062108 0.5% medium mw silk, 5 gr/liter Ultratex CSP, 0.025 gr/liter 4 citric acid

16051103 no coating, 200C, 3 min 1

16070701 0.025% citric acid 1

Example 41. Coating Cotton, Cashmere, and Cashmere/Silk Blends

Example 41a: A knitted and scoured cashmere panel (14" x 20") is soaked for 15 minutes in a 0.25 wt% solution of liquid silk (5 L), then spun dry for 10 seconds. The panel is then soaked for 5 minutes in water (5 L) and spun dry for 10 seconds. The panel is then soaked again in water (5 L) for 5 minutes and spun dry for 10 seconds. The panel is dried at 60 °C for 30 minutes. Panels are tested for hand and pilling.

Example 41b: A knitted and scoured cashmere/silk blend panel (4" x 4") is soaked for 15 minutes in a solution (500 mL) of silk (0.25 wt%) and glutaraldehy de-sodium bisulfite complex (0.1 wt%), then padded at 20 psi. The panel is then soaked for 5 minutes in water or alcohol solution (500 mL) and padded at 20 psi. The panel is then soaked again in water or alcohol solution (500 mL) for 5 minutes and spun dry for 10 seconds. The panel is dried at 60 °C for 5 minutes. Panels are tested for hand and water absorbency.

FIG. 217A illustrates a silk-coated cotton SEM image; scalebar represents 2 μπι. FIG. 217B illustrates a silk-coated cotton SEM image; scalebar represents 10 μπι. FIG. 218 illustrates manipulating water absorbency of liquid silk coated fabric. The time needed for a standard water drop to fully absorb into the fabric is recorded, and varies according to the silk treatment. FIG. 219 illustrates various process parameters for coating fabrics. FIG. 220 illustrates that liquid silk application significantly reduces pilling on cashmere; the pilling score of each cashmere panel, as measured according to ISO 12945-1 : Score 5 = No change; Score 4 = Slight surface fuzzing and/or partially formed pills; Score 3 = Moderate surface fuzzing and/or moderate pilling, pills of varying size and density partially covering the specimen surface; Score 2 = Distinct surface fuzzing and/or severe pilling, pills of varying size and density covering a large proportion of the specimen; Score 1 = Dense surface fuzzing and/or severe pilling, pills of varying size and density covering the whole of the specimen surface. Silk Formulation A: 0.05% M Silk; pH unadjusted, STI- 18050801-T004. Silk Formulation B: 0.25% M Silk; pH 9.25, STI-18050801-T009. Silk Formulation C: 0.25% 3L1M Silk, pH unadjusted, STI-18050801-T005. FIG. 221A (control) and FIG. 22 IB (cashmere treated with silk) illustrate cashmere coating coverage by scanning electron microscopy (SEM); as liquid silk and cashmere bond naturally, SEM demonstrates that liquid silk smooths and refines cashmere fibers. FIG. 222A (microscopic image) and FIG. 222B (dye intensity chart) illustrate deposition of FITC labeled silk fragments preferentially on cashmere cuticles; cuticle edges are 15-20 microns apart, and exhibit more fluorescence than the cuticle faces. (20x objective; laser power: 12%; gain: 600; gamma: 0.45). FIG. 223 illustrate silk protein binding and smoothing the "scales" of wool to the core fiber, preventing the "Velcro-like" effect that is responsible for wool's shrinkage and inability to withstand washing; additional data shows wool + liquid silk is water resistant, stable and shrink-resistant following washing while matching or improving pilling. FIG. 224 illustrates improved washability of wool by area dimensional change on wool tubes finished with liquid silk compared to untreated wool tubes. Liquid silk improves area dimensional change about twofold. FIG. 225A - 225D illustrates SEM images of silk coated wool. Example 42. Coating Synthetic Materials

Example 42a: Polyester Coating - Polyester fabric panels (13" X 13") were coated with a 0.1 wt% liquid silk solution using a pad-dry-cure method. The liquid silk solution is comprised of 3 parts Liquid Silk Formulation A and 1 part Liquid Silk Formulation B. The pH is adjusted to the desired range using pH adjusters commonly used in the field. The panels are soaked for 3 seconds and passed through a padder, after which they are transferred to an oven and dried for 90 seconds at 130 °C. The samples are allowed to rest overnight, after which they are tested for silk deposition, hand, and performance (moisture management, abrasion resistance, pilling resistance, stain release, odor release, SEM, fluorescence microscopy).

FIG. 226 illustrates the coating coverage of silk fragments on polyester as shown by scanning electron microscopy (SEM); SEM confirms that after application of liquid silk, coating coverage is similar or greater than other commercial coatings for polyester. FIG. 226 A illustrates polyester unfinished control sample, showing fibers with no coating. FIG. 226B illustrates polyester finished with silk, showing coated layers on the polyester fibers. FIG. 227 illustrates EDS Data on Polyester Related Experiments; polyester fabric was coated in 6% silk (FIG. 227C) and energy-dispersive X-ray spectroscopy (EDS) was used to determine chemical content (FIG. 227 A and FIG. 227B); EDS suggests regions between fibers (FIG. 227B) show nitrogen content due to silk depositions regions. FIG. 228 illustrates liquid silk coated polyester absorbency; the results indicate that the coated material exceeds commonly accepted industry criteria for absorbency, and outperformed commercial counterparts after 50 laundering cycles. FIG. 229 illustrates dry rate in polyester samples; in general liquid silk coated polyester dried faster than commercial control before laundering and after multiple laundering cycles; AATCC Test Method 201- 1013 Heated Plate Method; higher values indicate faster dry rate (silk + mechanical denotes a second water pass and drying process). FIG. 230 illustrates vertical wicking and abrasion resistance in polyester samples. FIG. 230A: liquid silk coated polyester demonstrated improved wicking at 5 minutes vs. unfinished fabric after 3 laundering cycles. FIG. 230B: liquid silk improves abrasion resistance of polyester fabrics, and outperformed the commercial standard. FIG. 231 illustrates pilling resistance in polyester liquid silk coated fabric which outperforms the commercial standard. FIG. 232A and FIG. 232B illustrates silk-coated Nylon SEM images. FIG. 233 illustrates fluorescence microscopy images for silk-coated vs. control; FIG. 233A: FITC-Silk Coated Nylon; scale bars represent 107 μπι. FIG. 233B: Uncoated Nylon Control; scale bars represent 53 μπι. Nylon coated in FITC- Silk showed increased fluorescence due to the FITC-silk coating; 5% enhancement. FIG. 234 illustrates coating coverage on Nylon: scanning electron microscopy (SEM) confirms application of liquid silk. FIG. 234A: Nylon unfinished control. FIG. 234B: Nylon with silk finish - coated silk layers also adopt clear surface features. FIG. 235 A illustrates absorbency performance of coated Nylon; liquid silk coated nylon exceeded commonly accepted industry criteria for absorbency, and outperformed commercial counterparts after 50 laundering cycles (AATCC Test Method 79-2013; smaller values indicate faster absorbency, silk + mechanical denotes a second water pass and drying process). FIG. 235B illustrates dry rate performance in coated nylon; liquid silk coated nylon dried faster than commercial control before laundering and after multiple laundering cycles (AATCC Test Method 201-1013 Heated Plate Method; higher values indicate faster dry rate; silk + mechanical denotes a second water pass and drying process). FIG. 236A illustrates vertical wicking performance; Nylon liquid silk coated nylon demonstrated improved wicking at 5 minutes vs. commercial finish after 3 laundering cycles (AATCC Test Method 197 (modified); higher values indicate better wicking; silk + mechanical denotes a second water pass and drying process). FIG. 236B illustrates abrasion resistance performance; Nylon liquid silk coated improves abrasion resistance of nylon; liquid silk coated nylon matched the commercial standard Abrasion Resistance - ASTM Standard D4966-12Esl (accelerated); testing ended when fabric first demonstrated abrasion or broke, whichever happened first; instead of wool, Trizact was used.

Example 42b: Odor release - Sour milk test (Odor Properties of Textiles Assessment from Pasteurized Cows' Milk). This test method follows IAC Biofouling of Textiles from Pasteurized Cow's Milk, and includes modifications. The general procedure involves souring the milk using citric acid, placing the milk solution on the fabric, and allowing it to sit open for 3 days. Afterwards, the samples were sent out for washing and drying. Following the washing and drying process, the samples were resealed in clean jars. The samples were stored at room temperature for 24 hours. Odor presence was assessed after 24 hours by opening the jars and wafting the samples for presence of odor. The strength of the odor was rated from 1-5, where little to no odor present was rated (1) and pungent odor present was rated (5).

FIG. 237 illustrates the Sour Milk Test Experimental Results; liquid silk coated fabrics reduced odor more than both finished and unfinished fabrics. FIG. 238 A and FIG. 238B illustrates Sour Milk Test Experimental Results; liquid silk coated fabrics reduced odor more than both finished and unfinished fabrics. FIG. 239 illustrates biocompatibility of liquid silk coated fabrics (by the FDA standard test to show compatibility for contact with human skin); liquid silk coated fabrics demonstrated no reactivity; multiple commercial performance fabrics failed biocompatibility testing (0 = No reactivity around or under specimen (passed); 1 = Slight reactivity, some degenerated cell under test article (passed); 2 = Mild reactivity, zone limited to area under the test article (passed); 3 = Moderate reactivity, zone of lysis extending specimen size up to 1 cm (failed); 4 = Severe, zone of lysis extending farther than 1 cm beyond specimen (failed)).

Example 43. Nebulizer Coating

Materials: Omron model NE-U22V vibrating mesh nebulizer; pipette 1 ml; glassware; tap water; silk low MW 6%; silk medium MW 6%; GAP-17120505-L007-02 Powervita. Procedure: cut N=5 fabric samples to 12 cm x 12 cm square; mark fabric samples with a 2 cm diameter circle to delimit the area of application and label with the abbreviation of the experiment Table 99; prepare solution per Table 99; fill nebulizer reservoir with prepare solution and turn on the nebulizer; allow the nebulizer to begin the production of water drops; place the fabric application area on top of the nebulizer nozzle and wait for 5 seconds; place the tested fabric samples in the oven at 300 °C for 1 minute; repeat procedure for all Table 99 experiments.

Table 99

Water drop test: place the tested fabric on the drapability jig, turn on a video recording and drop a water sample with the dropper. Stop recording as the water is fully absorbed by the fabric.

Table 100

control water only 9 low mw 3 medium mw 4 low MW : medium mw 3

3 : 1

FIGS. 240 A - 240D illustrate samples of fabric coated with silk formulations using a nebulizer applicator. FIG. 240 A: low MW silk; FIG. 240B: medium MW silk; FIG. 240C: low MW to medium MW 3 : 1; FIG. 240D: control. FIGS. 240 A - 240D illustrate nebulizers and the silk solutions, and control, respectively.

All patents, patent applications, and published references cited herein are hereby incorporated by reference in their entirety. While the methods of the present disclosure have been described in connection with the specific embodiments thereof, it will be understood that it is capable of further modification. Further, this application is intended to cover any variations, uses, or adaptations of the methods of the present disclosure, including such departures from the present disclosure as come within known or customary practice in the art to which the methods of the present disclosure pertain.