Title:
SOFT BLACKPLATES WITH HARDNESS HR30T OF 51±3 FOR TINNING AND PRODUCTION METHOD FOR THE SAME
Document Type and Number:
WIPO Patent Application WO/2007/000108
Kind Code:
A1
Abstract:
Soft blackplates with hardness HR30T of 51±3 for tinning comprise (wt.%)
up to 0.005 C, 0.20-0.30 Mn, 0.03-0.06 Al, up to 0.03 Si, 0.03-0.06 Ti, up to 0.012
P, up to 0.015 S, up to 0.003 N, up to 0.004 O, and the balance Fe and other inevitable
impurities. The method for producing the soft blackplates involves the following
steps: steelmaking, continuous casting, hot rolling, combination of pickling
and cold tandem rolling, continuous annealing, and temper rolling. The main
process parameters in the method are as follows: slab delivering temperature
is 1190-1250 deg. C, final rolling temperature is 880 - 920 deg. C, coiling temperature
is between 560 deg. C and 620 deg. C, annealing temperature is 730-760 deg. C, holding
time is 25-50 seconds, temper elongation is 1.2-2.2%.
Inventors:
LI JUN (CN)
LIN XIUZHEN (CN)
ZHANG LIYANG (CN)
JIN RENZHONG (CN)
LIN XIUZHEN (CN)
ZHANG LIYANG (CN)
JIN RENZHONG (CN)
Application Number:
PCT/CN2006/001459
Publication Date:
January 04, 2007
Filing Date:
June 26, 2006
Export Citation:
Assignee:
BAOSHAN IRON & STEEL (CN)
LI JUN (CN)
LIN XIUZHEN (CN)
ZHANG LIYANG (CN)
JIN RENZHONG (CN)
LI JUN (CN)
LIN XIUZHEN (CN)
ZHANG LIYANG (CN)
JIN RENZHONG (CN)
International Classes:
C22C38/14; C21D8/04; C21D9/48; C25D3/30
Foreign References:
CN1176667A | 1998-03-18 | |||
CN1273612A | 2000-11-15 | |||
CN1303446A | 2001-07-11 | |||
US4698102A | 1987-10-06 | |||
KR20040057704A | 2004-07-02 | |||
KR20010064849A | 2001-07-11 | |||
KR20010109930A | 2001-12-12 | |||
KR920005614B1 | 1992-07-10 |
Other References:
LI J.: "Principle of the Metallurgical Process Control on Black-Sheet Production", BAOGANG TECHNOLOGY, no. 4, August 1998 (1998-08-01), pages 41 - 44
LI J.: "Review on Application Performances of DI Tinplate at Baosteel", BAOGANG TECHNOLOGY, no. 6, December 2000 (2000-12-01), pages 11
LI J.: "Review on Application Performances of DI Tinplate at Baosteel", BAOGANG TECHNOLOGY, no. 6, December 2000 (2000-12-01), pages 11
Attorney, Agent or Firm:
SHANGHAI PATENT & TRADEMARK LAW OFFICE, LLC. (Shanghai 3, CN)
Download PDF:
Previous Patent: A REFRIGERATOR OR AN AIR CONDITIONER TYPE DART MACHINE
Next Patent: SOFT BLACKPLATES FOR TINNING AND PRODUCTION METHOD FOR THE SAME
Next Patent: SOFT BLACKPLATES FOR TINNING AND PRODUCTION METHOD FOR THE SAME