A SOUND INSULATING SHEET MATERIAL WITH A CELLULAR STRUCTURE INCLUDING GELATINE AND/OR A PROCESS FOR PRODUCING THE SAME

The present, invention relates to a. sheet material with a cellular structure which also includes sound dampening properties, and in particular to a composition for producing the sheet material that is also environmentally friendly. The present invention also relates to a process for producing the sheet material.

Background

Sound dampenin properties are found in materials with a high sound transmission loss. Th Sound transmission loss of a material is determined by various physical factors such as mass and stiffness. The mass per unit area of a material is the most important factor in controlling the transmission of sound through the material. The so-called mass law is worth repeating here, as it applies to most materials at most, frequencies;

TL = 20 1og ₁₀ (m _s f> - 48. where;. TL= transmission los (dB)

r¾ . = mass per unit area (kg/ni ² )

f = frequency of the sound (H¾)

Stiffness of the material is another factor that influences TL. Stiffer materials exhibit "coincidence dips" which are not explained by the above mass law. The coincidence or critical frequency is shown by: f _c = A/t where: A is a constant for a material

t is the thickness of the material (mm) An example of a composition that is commonly used to produce sheet material with sound dampening properties is what is termed a loaded vinyl. In such a composition, a material with a high density is combined with vinyl at formulation stage, The resultin product has a. high densit whilst still maintaining high flexibility and thereby providing sound dampening properties.

However, vinyl is a product derived from petroleum sources so its cost and production is directly linked to the oil price and dictated by oil supply. Furthermore, vinyl doe not biodegrade easily and in addition produees toxic fumes when burnt. This poses particular problem when a loaded vinyl is used in building applications.

Accordingly, there is a need for an alternative material that may be used to produce a sheet material with sound dampening properties and which overcomes the disadvantages of loaded vinyl .

One attempt at providing such a material is described in WO 2006/053393 which describes a composition for producing a sheet material consisting of water, gelatine, glycerine and a filler material. However, it was found that the sheet material produced from such a composition was not stable at temperatures above 25"C, particularly when packaged immediately after manufacturing and then exposed to the sun. The material was found to melt and lose shape, providing undesirable characteristics when using this material in building applications.

The present invention seeks to provide a composition for producing sheet material wit sound dampening properties which addresses the issues outlined above. The present invention also seeks to provide a. rocess for producing such a sheet material.

Summary In accordance with one aspect the present invention provides a composition for producing a sheet material with a cellular structure, the composition includin the following components:

(a) about 5 to about 25 weigh t% gelatine,

.(b) about 25 to about 60 weigh % filler material,

(c) about 15 t about 40 weight.% water, and

(d) a cellular structure promoting agent.

In one form the cellular structure promoting agent reacts with one or more of components (a), (b) and/or (c) to provide the cellular stmeture of the sheet material. In one form the cellular structure promoting agent reacts with one or more of components (a), (b) and/or (c) to produce a gas which forms a cellular structure in the composition which upon curing provides the cellular structure of the sheet material . According to another aspect the present invention provides a composition for producing sheet material with a cellular slmcture, the composition consisting essentially of the followin components:

(a) about 5 to about: 25 weight% gelatine,

(b) about 25 to about 60 weight^ filler material,

(c) about 15 to about 40 weight% water.

(d) about 0.5 to about 2 weight cellular structure promoting agent, and,

(e) about 10 to about 30 wc.igh% lubricating compound.

In one form in addition to components (a) to (e) the remaining balance of the composition i made up from components selected from one or more of the following: gluten, starch, one or more alkaline earth metals, colourant, fungicide, perfume and deodoriser.

In one form, the cellular structure promoting agent i a composition includin peroxide group. In one form the cellular structure promoting agent is sodium percarbonate. In one form the cellular structure promoting agent reacts with the water in the composition to produce oxygen which provides the cellular structure in the composition. In one form the composition includes about 0.2 to about 5 weight % and preferably 0.5 to about 2 weight of the cellular structure promoting agent. In another form the composition includes about 1 to about 2 weight% of the cellular structuring agent . In one form the composition includes about 20 to about 30 weight water.

In one form the composition further includes a lubricating compound such as for example ethylene glycol and propylene glycol, glycerine (glycerol). In one form, the composition includes about 10 t about 30 weight% of the lubricating compound. In another form the composition includes about 10 to about 15 weight % of the lubricating compound. In one form the lubricating, compound is glycerine.

In one form the composition further includes an alkaline earth metal chloride. In one form the composition includes about 1 to about 5 weight% of the alkaline earth metal chloride. In another form the composition includes about 1 to 2 weigh t% of the alkaline earth metal chloride. In one form the alkaline earth metal chloride is magnesium chloride.

In one form the compositio further includes gluten, hi one form the composition includes about 1 to about 5 weig t% gluten. In another form the composition includes about 2 to about 4 weight.% gluten.

In one form the composition includes starch. In one form the starch is included in the form of tapioca starch. In one. form the composition includes abou 1 to abou 5 weight% starch. In another form the composition includes about 2 to about 4weight% starch.

In one form the gelatine has a bloom of between about 220 and about 260. In one form the gelatine has a bloom of about 250. In one form the gelatine is type-B gelatine. In one form the composition includes about 5 to about 1 weight % of gelatine. In another form the c mposition includes abou 10 to 15 weight% gelatine. In one form the densit of the filler material is greater than 1 g/cm3. in one form the density of the filler material is about. 2,0 to about 5.0 g cm3. In one form the filler material i selected from calcium carbonate and/or barium sulphate. In one form the composition includes about 30 to about 50 weight% of the filler material. In another form the composition includes about 35 to about 45 weight.% filler material. In one form the filler material is chosen from a combination of calcium carbonate and barium sulphate. In one form the filler material is calcium carbonate.

In one form the composition further includes a fungicide,

In one form the composition further includes a deodoriser.

In one form the composition further includes a perfume compound.

In one form the composition further includes a colourant. In another form the colourant is water based.

According to another aspect the present invention provides a process for produeing a sheet material with a cellular structure- the process including the steps of:

a. preparing a composition including the steps of:

i . providing 15 t about 40% water;

ii. dissolving about 5 to about 25 weight% gelatine into the water to provide a first mixture;

ii i. mixing about 20 to about 60 weight% o a filler material into the first mixture to form a second mixture;

iv. introducing a cellular structure promoting agent: to the second mixture to for the composition, the above weight% calculated on the weight of the total composition ,

b. forming the composition into a sheet; and

c. allowing the sheet to cure In one form the cellular structure promoting agent is selected from a composition including a peroxide group. In one form the cellular structure promoting agent is sodium perearhonate. In one form the cellular structure promoting agent reacts with the water in the composition to produce oxygen which provides a cellular structure in the composition which upon curing provides the cellular structure in the sheet material

In one form the preparation of the composition at step a. is conducted at a temperature of about 75"C to about 95°C. In one form ste a. is conducted at a temperature of abou 80°C. In one form the filler material at step in. is calcium carbonate.

In one form about 10 to about 30 weight. glycerine is added t the filler material before ste a.iii. in an alternative form, about 5 to about 15 weight ^< % glycerine is added to the water after step a.i. and the remaining about 5 to about 15 weight glycerine is added after step a .it. and before step a.iii.

In one form about 1 to 5 weight% of magnesium chloride i added to the water after ste a.i. and before step a.ii, In one form the cellular structure promoting agent is introduced to the second mixture about 1 minute to about 15 minutes before ste b. In one form the cellular structure promoting agent is introduced to the second mixture about 2 minutes before step b.

In one form step b. include pouring the composition onto a. substantially horizontal surface to form a sheet.

According to another aspect the present invention provides sheet material prepared from a composition as herein described or from a proces as herein described, In one form, a further planar sheet material may be bonded to one or both planar faces of the sheet material to provide a layered sheet material. In one form the planar sheet material is composed ol ^" thermally bonded polyester sheeting or needle punched polyester sheeting. In one form the planar sheet material is thermally bonded polyester sheeting and the thermally polyester bonded sheeting is bonded to a further sheet material in the form of aluminium foil.

In one form the aluminium foil is bonded to the thermally bonded polyester sheeting using an adhesive, in the form of a laminate.

Detailed Description of Embodiments

The foregoing describes only some embodiments of the present invention, and modifications and/or changes can be made thereto without departing from the scope and spirit of the invention, the embodiments being illustrative and not restrictive. In the context of this specification,: the word "comprising" means 'Including principally but not necessarily solely" r "having" or "including", and not "consisting only of ^* . Variations of the word "comprising", such as "comprise" and "comprises" have correspondingly varied meanings. In certain embodiments the composition as herein is able to produce an acoustic sheet material with a cellular structure which has significant sound dampening characteristics. The sheet material once formed has a density of about 0.2 g cm ³ (without fillers included in the composition) and density when fillers are included of about 0.8 to 1.2 g/cm' u to a density of about 2.5 g/cm ³ . In addition to the high density, the sheet material is very flexible and has a high elastic memory. The combination of the high density and the flexibility provides thai the sheet material ha excellent sound dampening properties.

As the composition of the present invention is made fro non-petroleum based products, the sheet material produced from the composition is biodegradable and n n toxic, Furtliermore. the cost of the sheet material is independent from the oil price and oil supply. Anotber advantage of the composition is that the resultant sheet material is tire retardant and does not give off toxic fumes when burnt in contrast to the alternative sound dampening sheet material product of loaded vinyl. This provides that the sheet material produced from the composition as herein described ma be used extensively as a building material for various applications to provide a safer and greener alternative to loaded vinyl. The shee material produced from the composition may also be used in areas which are subject to fire hazards such as for example in engine environments on boats and in heavy industry installations, During the process to produce the sheet material with sound dampening properties, the composition may also he coloured by using any suitable colouring technique to produce sheeting in. any colour that may be desired. Furthermore, prior to curing, th composition has excellent adhesion properties and does not therefore require a separate adhesive at the formation stage if is desired to bond the sheet material to another substrate. Alternatively, once the sheeting material has cured, the material is also compatible with most glues and adhesives such that a composite material may also be produced in this fashion.

It was found tha the inclusion of a cellular structure promoting agent together with water, gelatine and a filler material provided a composition that; when formed into a sheet or other structure and allowed to cure, provided a material with cellular structure throughout its composition.

In certain embodiments the cellular structure promoting agent is selected from a compound that reacts with the one ore more of the other constituents of the composition tor producing the sheet material thereby producing gas at the formation stage of the sheet which provides the cellula structure of the resulting composition when in sheet form.

One clas of preferred cellular structure promoting agents is selected from compositions including a peroxide group such as for example the following compounds:

2Na ₂ C0 ₃ - 3H ₂ 0 ₂ .

{NH4) ₂ S04.¾02

In an alternative embodiment, the cellular structure promoting agent may also be selected from compositions includin persulfate group, such as for example sodium persulfate NasSaOs.

In a preferred embodiment the cellular structure promoting agent is selected from sodium percarbonate.

It was also surprisingly found that when the cellular structure promoting agent Is in th form of a composition including a peroxide group (such as sodium percarbonate), the cellular structure promoting agent reacted with the water in the composition to produce a ga which is understood to be oxygen. The production of oxygen within the composition once the cellular structure promoting agent was included formed gas hubbies throughout the composition which were maintained throughout in the form of a cellular structure once the. composition cured, In addition, and without wishing to be bound by theory, it is also thought that the oxygen, made available to the gelatine within the compositio by the reaction of the peroxide group with water as the gelatine begins to gel, provides for stronger cross-linking between the gelatine molecules as the composition i cured. The stronger cross-linking stabilises the "visco-e!astic" properties of the cured sheet material produced from the composition in conditions of high humidity, low humidity and with temperature varialion, such that the sheet, material can perform, without loss of structural integrity in temperatures from about minus 40°C to about 18<fC (was tested in freezing conditions for over 90 days) as well as in dry and wet conditions. This provides that the sheet material is easily about able to withstand temperatures of up to about 9G"C which can often occur if the sheet material is left out exposed to direct sunlight such a for example on a building site or when the sheet material is located within packaging made of plastic and the like. It was also found that the material maintained flexibility and the same visco-elastic properties even at ver cold temperatures below Q°C, With out wishing to be bound by theory it is thought that at least the inclusion of the cellular stmcturo promoting agent and particularly, a celluJar structure promoting agent that includes a peroxide group and/or the addition of a filler chosen from calcium carbonate provides that the structural integrity of the sheet material is maintained as the ambient temperature increases. This is in contrast to the composition described in WO 2006/053393 that tends to melt and become putty like and lose its structural integrity when exposed to temperatures above 25 °C.

In addition, it was also found that the addition of a cellular structure promoting agent in the form of a peroxide -group provided that the resulting material had increased resistance to the presence of hydrocarbons, oils and grease as well as water.

In certain embodiments there is provided a composition for producing a sheet material with a cellular structure, the composition consistin of the following components:

(a) about 5 to about 25 weighty? gelatine,

(b) about 25 to about 60 weight% filler material.

(c) about 15 to about 40 weights water,

(d) about 0.5 to about 2 weight% cellular- structure promoting agent, and,

(e) about 10 to about 30 wcigh.% lubricating compound;

wherein the remaining balance of the composition is made up from components selected from one or more of the following: about 1 to about 5 weight gluten, about 1 to about 5 weight % starch, about 1 to about 5 weight.% of one or more alkaline earth metals and optionally minor amounts of any one of the following: colourants, fungicides, perfumes and deodori sers, In certain embodiments the composition including a cellular tructure promoting agent ma be used to produce a sheet with a cellular- structure of various thicknesses. These sheets were found to have increased resilience, low thermal conductivity, increased sound dampening characteristics, as well as a high fire rating. As such, the sheet material produced in this way was found to be suitable for a variety of applications such as for pipe lagging and an underlay for flooring assemblies. In addition, the composition may be used as a component in mattress construction due to its resilience and high fire rating. Accordingly, the thickness of the sheet material including a cellular structure may very from less than 1 mm to 8 mm for applications including acoustic sheeting for building constructions, underlay for flooring assemblies and pipe lagging up to 100mm to 250 mm for mattress con truction.

The cellula structure of the composition also unexpectedly increased the Sound Transmission Loss (STL) for a given weight by about 3 to 4 dB which is a significant advantage over and above the prio art products such as loaded vinyl. The cellular' structure of the composition once cured, was also found to increase the resilience of the sheet material. It was also found that when the sheet material of the present invention wa combined with a further layer bonded thereto (for example: a needle punched polyester sheeting), there was a marked increase in the impact insulation when the sheet material was used as a sound proofing underlay providing a floor acoustic / impact noise treatment. Indeed when tested, it was found to provide up to a 6 STAR impact insulation rating.

Again due to the cellular structure of the composition once the sheet material is formed the sheet material provides a heat resistance ( 0.082 W/rnK) @ 23 De C mean temp, 50-70% R.H) and a good vapour permeability resistance 8.19 X10-15 Kg Pa.m2,

In a further embodiment, the sheet material with a cellular- structure may be bonded to a construction panel such as for example plasterboard panel to produce composite building material. Indeed in a further embodiment the sheet material wit a cellular structure may be sandwiched between two construction panels uch as plasterboard to produce a composite building material. The sheet material with a cellular structure may be situated between the construction panel i one continuous layer, or alternatively in discrete spaced apart sections.

The construction panel may be composed of any common construction panel material such as for example plaster board, plywood and fibre.

Such a composite building material may be used in a variety of applications where a construction panel may be used with the added benefit of providing a construction panel with increased sound insulation properties from conventional construction panels.

In an embodiment where the sheet material with cellular structure is bonded to one side of a constructional panel, the resulting composite building material may be cut to size by first scoring or cutting through the side of they composite material including the sheet material with a cellular structure. The composite building material may then be snapped or folded to break through the construction panel layer along the line of the score/cut thereby providing the composite building material in the desired size for a building application.

In certain embodiments the process for producing a sheet material in accordance with the present invention includes the followin steps:

a. preparing a composition including the steps of:

1 . dissolving about 1 to about 5 weight. magnesium chloride in about 15 to about 40 weight% water at a temperature of about 80°C (this step takes about 5 minutes);

2. dissolving about 5 to about 25 weight% gelatine int the water and magnesium chloride in step 1 , to form a mixture (this step takes about 45 minutes);

3. adding a filler such as calcium ^' carbonate to about half of the 10 to about 30 weigbl ^' % glycerine t form a. first glycerine mixture and heat for about 0.5 hours at about 75 to 80°C; 4. dispersing about 1 to about 5 weights gluten into the second half of the glycerine to form a mixture at a temperature of about 55 °C (this ste takes about 15 minutes);

5. Add the mixture from ste 3 to the mixture from step 4 to produce a mixture.

6. mixing the mixture from step 2 and the mixture from step 5 to form a mixture (this step takes about 15 minutes);

7. adding about 1 to about 5 weight% starch in the form of tapioca to the mixture of step 6 and dissolving the tapioca to form a mixture (this step takes about 15 minutes);

8. adding about 0.5 to about 2 weight % of a cellular structuring agent such as in the form of sodium percarbonate to the mixture of step 7 about 1 t about 15 minutes before step b, b. extruding the composition onto flat surface to form sheet; and c. allowing the sheet to cure.

In an alternative embodiments the process for producing a sheet material in accordance with the present invention includes the following steps:

a, preparing a composition including the steps of;

1. dissolving about 1 to about 5 wei t magnesium chloride in about 15 to about 40 weight% and then adding about 5 to about 15 weight% of a lubricating compound such as glycerine and heat the resulting mixture from about 80°C to about 95 ^6' C;

2. dissolving about 5 to about 25 weight.% gelatine into the mixture of step 1 to form a mixture;

3. dispersin about 1 to about 5 weight gluten into about 5 to about 15 weight% of a lubricating compound such as glycerine to form mixture;

4. adding the mixture of step 2. t the mixture of step 3. to form a mixture; 5 adding about 1 to about 5 weight% starch such as in the form of tapioca and about 25 to about 60% filler material such as calcium carbonate and/or barium sulphate to the mixture of step 4. and agitate to eliminate lumps to form a mixture;

6 adding about 0.5 to about 2 weight% of a cellular structuring agent such as in the form of sodium percarbonate to the mixture of step 5. about 1 to about 15 minutes before step b.

b, extruding the composition onto a flat surface to form a sheet; and allowing the sheet to cure

In a preferred embodiment, the cellular structuring agent, such as sodium percarbonate, is mixed with an amount of glycerine prior to being added before step b. The addition of th glycerine means that the cellular structuring agent is added in the form of a. suspension which provides the delivery of the cellular straelming agent into the mixture prior to step b. does not clump or clog which can sometimes occur if the cellular structuring agent is in the form of a powder.

A further advantage of the composition for forming the sheet material with a cellular structure is that once the cellular structuring agent is included with the remainder of the composition, the composition may be formed into a sheet using any applicable process such as by pouring the composition onto a horizontal surface, extruding the composition or moulding the composition. The composition then cure at ambient temperature, without the addition of any further energy for example by heating the composition. The composition will also cure in conditions with high humidity.

In another embodiment of the present invention, the sheet material produced by the composition, or the process as described herein, is used a tire basis of a multi layered sheet material.. In this embodiment further materials in sheet form are bonded to one or both of the planar faces of the sheet material to produce a multi layered sheet material. In one embodiment thermally bonded polyester sheeting, which has bee laminated on one planar surface with an additional foil layer, is adhered to one, or both, sides of the sheet material prepared from the composition described herein during production. The planar surface of the thermally bonded polyester sheeting that does not include the additional foil layer is bonded prior to the composition curing to form the sheet material. Once the sheet material cures strong adhesion is formed between the sheet, material and the thermally bonded polyester sheeting. The resultant multi layered sheet material was found to have the desirable properties including: increased strength and tear resistance and water resistance,

It was found that the thermally treated polyester bonded strongly to the composition as herein described before curing and there wa no need for any further adhesi ve or glue. The pattern appearing on the foil planar face of the thermally bonded polyester or 'Pimple' look also helps to scatter high frequencies (over 1000 Hz) and also provides heat reflection. The multi layered sheet material provides a flexible noise barrier from that has a foil reflective layer on both sides, which make it water resistant heat resistant (heat transfer) and allows the product t be used in various applications such as for example a an 'acoustic sarking'. The present invention will become better understood from the following examples of preferred but non-limiting embodiments thereof.

Example 1 A sample was produced from a composition with the following constitution:

9 % weigh t gelatine

37 % weight calcium carbonate

27 % weight water

2 %weight magnesium chloride

18 % weight. glycerine 2 %-wei.ghi gluten

3% weight tapioca starch

1% weight sodium percarbonate.

With the balance of the composition being made up of other components such as for example colouring agents.

The preparation of the composition involved dissolving the magnesium chloride in water at a temperature of about 80°C for about 5 minutes and then dissolving the gelatine into the mixture al the same temperature whilst mixing for a period of 45 minutes. In the meantime, half of the total amount of glycerine is brought up to a temperature of about 55°C to which the calcium carbonate is added, the mixture of glycerine and calcium carbonate is then heated for a period of about 30 minutes to a temperature of about 75 to 80°C. Gluten is then dispersed throughout the remaining half of the glycerine over a period of 15 minutes at 55°C. The glycerine calcium carbonate mixture and the glycerine gluten mixture are then combined to form a second mixture. The original mixture including the water, magnesium chloride and gelatine was then mixed for a period of 15 minutes with the second mixture until a homogenous composition resulted. The tapioca was then added to the homogenous composition and dissolved therein which typically takes about 15 minutes of stirring. The sodium percarbonate is then added to the composition just before the mixture i poured in the form of a sheet.

Example 2

A sample of a sheet material with a cellular structure was produced from a composition with the following constitution;

13%weight gelaii

41 % weight. calcium carbonate

26 % weight water

1 % w ei g h t magnesium c hloride

13 % weight glycerine

2 % weight gluten 3% weigh I tap i oca s t arch

1 % weight sodium percarbonate

With the balance of the composition bein made u of other minor constituents such as for example colouring agents, deodorisers and fungicides.

The preparation of the composition involved preparing a first mixture by dissolving the magnesium chloride in the water and then adding half of the amount of glycerine required and then healing the resulting mixture to a temperature of greater than 95°C. The gelatine was then added and dissolved in the first mixture,

A second mixture was prepared by taking the remaining glycerine and blending the gluten therein to form the second mixture which was then added to the first mixture to form a combined mixture. The tapioca starch and the filler in the form of calcium carbonate was then added to the combined mixture and stirred aggressively to eliminate lumps after which the resulting mixture was heated to around 76 to 78 °C.

The cellular structurin agent wa then prepared by pulverising sodium percarbonate into a powder. The powdered sodium percarbonate was then blended with glycerine to form a slurry to aid in the addition of the sodium pcfcaribcnate to the combined mixture.

The production of the shee material then involved blending the sodium percarbonate slurry with the combined mixture using a screw mixer/feeder to form the uncured composition just prior to feeding the uncured composition onto a blade coating table which forms the uncured composition into a. continuous sheet with cellular structure.

The continuous sheet is then allowed to cure forming the sheet material with cellular structure which was found to have a weight of 2.5 kg m ² . The acoustic properties of the sheet material were then tested using a standard "Sound Intensity Probe" as accepted under the US Standards and ISO, the results of which are outlined in. the lOllowin table and chart :

≠ These results may be compared to a loaded vinyl sheet material of weight 4kg/m which produced the following results:

From a comparison of the results for the sheet with a cellular structure of weight 2.5 kg/m ^" and the results for the loaded vinyl sheet material of weight 4kg m ^* it can be seen that the sheet with a cellular structure has significantly better STL (Sound Transmission Loss) results for many applications because the sound vibration dissipates at a faster rate than shown with the loaded vinyl sheet. Many modifications will be apparen to those skilled in the art without departing from the scope of the present invention.