APPLICATIONS

RELATED APPLICATIONS

[0001] This application claims the benefits of U.S. Provisional Application No. 61/681 ,272, filed Aug 9, 2012 which is herein incorporated by reference in its entirety for all purposes.

FIELD OF INVENTION

[0002] The present invention relates to providing personal and public protection through enhanced filtration, and more particularly to a medium developed for the irreversible absorption or desorption of targeted gases. The medium is processed to yield a form factor (e.g., particle type, particle size, surface area, pore size, pore size distribution, total pore volume, functionality, etc ..) specific to the capture of a given gas (e.g., through use in chemical respirators).

BACKGROUND OF INVENTION

[0003] Current materials do not provide adequate ventilation protection against select chemical agents, toxic industrial compounds, toxic industrial materials, and other harmful volatile organic compounds. These chemicals have very low physical exposure limits yet are difficult to capture and retain in personal or collective filtration devices. This lack of performance leads to large, heavy respirator mask canisters that impede war fighter and emergency responder performance and field of view. Furthermore, the large mass and volume of current material required leads to a large pressure drop across the bed resulting in labored breathing in order to pull sufficient air through the mask for respiration.

[0004] A need therefore exists for an improved adsorbent material in personal protection equipment to irreversibly adsorb targeted gases from the environment.

SUMMARY OF INVENTION

[0005] The present invention involves the use of nanoporous carbons derived from partially or fully demetaiized metal carbides in personal protection equipment for the irreversible absorption and adsorption of both broad and specific targeted gases. These materials have been specifically processed to provide enhanced effective loadings against specific gases. This parameter corresponds to the amount of target gas the filtering medium is capable of adsorbing: the larger the effective loading, the more target gas is "trapped" into the medium, in particular, the medium has been modified to present a specific particle size disiribuiioii and to provide a high surface area and a high total pore volumes. Specifically, this medium was further designed to be highly porous (commonly 2,250 rrT/g) with tunable nanoscale pores (1-5 nm) of various pore shapes. The functionality that is added for the targeted adsorption / absorption of gases was also tailored to provide high effective loading capabilities in dry and wet atmospheric conditions as tested in relative humidity of 0% and 80% respectively. [0006] One general aspect of the present invention is that it is at least seven times more adsorbent per unit mass than what is currently used. Compared to the prior art filtration material, the present invention has a much higher capacity to filter and retain chemical adsorbents across a broad class of chemical compounds. The invention also utilizes nanoporous carbons which are extremely hydrophobic while still able to capture volatile organic compounds, thus providing practical operation under high relative humidity. Furthermore, once adsorbed, the chemicals can be desorbed to provide analysis of an exposure event.

[0007] Those skilled in the art will appreciate that the present invention will sign ficantly improve the protection offered to the warfighter through the application of such material for personal filtration. For exam le^ the present invention can be implemented as powders and substituted into existing gas masks. Alternatively, fibers of the material can be used and integrated into protective clothing. Finally, the invention can also be integrated into building .filters for collective protection.

BRIEF DESCRIPTION OF DRAWINGS

[0008] The present Invention is further described with reference to the following drawings wherein:

[0009] Figure 1 is a graph displaying the gas ehroroatograph/mass spectrometer detection of 50 volatile organic compounds simultaneously adsorbed onto a nanoporous carbon and a standard sorbent.

[0010] Figure 2 is an image displaying the comparative sizes of the standard filtration mask canister (left) and the nanoporous carbon containing canister (right). [0011] Figure 3 is a graph displaying the performance of several different nanoporous carbons compared to the standard filtration mask.

[0012] Figure 4 is a graphical representation comparing various embodiments of the invention using acid, impregnation, and previous embodiments.

[0013] Figure 5 is a graphical representation comparing various embodiments and prior art under alternating drying conditions,

[0014] Figure 6 is a graph comparing breakthrough curves of one embodiment, with prior art,

DETAILED DESCRIPTION

[0015] Nanoporous carbons outperform other state-of-the-art sorbent materials in both adsorption rate and capacity for various volatile organic compounds, The present invention can adsorb a broad range of volatile organic compounds, including toxic industrial compounds and a limited number of chemical warfare agents, even under conditions of 80% relative humidity.

[00 ί 6] The present inventio is further defined by the following working embodiments:

[0017] Referring to Figure 1, an experiment was performed to demonstrate the capability of one embodiment of the present invention to adsorb multiple compounds simultaneously without significant displacement or pore occlusion. At 7 Umin gas flow over 5 minutes of a 50 component lOOppb hydrocarbon gas mix, 250 rng of nanoporous carbon outperformed 250 mg of a standard sorbent, and showed fairly linear adsorption capacity across molecular weights from 44 g/mol. to 120 g/niol. [0018] One embodiment of the present invention has established the relevance of using nanoporous carbide-derived carbons against difficult to capture toxic industrial compounds, and thus the capability of reducing the size of a filtration mask. In the following working example, baseline folly demetalized material as well as partially demetalized and surface funetiona ized materials were compared to the current widely used personal filtration medium for chemical respirators, Activated carbon impregnated with copper, Silver, Zinc, Molybdenum, and TriEthlyeneBi Amine, (ASZM-TEDA).

[0019] Comparison studies between nanoporous carbons and ASZM-TEDA required that a consistent flow rate through a packed bed of materia! be established. Particle size distribution analysis confirmed that nanoporous carbon particles are about 350 μιη in diameter compared to the about i .0 to 1.5 mm diameter activated charcoal particles of ASZM-TEDA. As a result of the size difference, packed beds of equivalent mass showed a much lower pressure drop across ASZM-TEDA packed beds as compared to the nanoporous carbon bed. Testing revealed that equi valent tlow rates and pressure drops could be obtained if 200 mg of ASZM-TEDA was tested versus 30 rag of nanoporous carbon. Therefore, further testing was conducted using only 30 mg of nanoporous carbon in comparison to 200 mg of ASZM-TEDA.

[0020] The test conditions for detennining the breakthrough point of 40 ppm acetonitriie (ACN) at 5 L/min were devised to yield physiologically relevant data. Given that the average mass of ASZM-TEDA in a personal filtration mask is about 120 grams and that the breathing rate under moderate exercise for an average male is about 30 L/min., our test of 200 mg ASZM-TEDA and 5 L min ACN represents a 1 /600th scale model. In these conditions, one m inute of test gas exposure equates to about 20 minutes of field canister use.

[0021] The present invention was also tested to show that partial dernetalization and surface functionalization of standard nanoporous carbon particles will improve the capture of difficult to trap molecules, such as ammonia.

[0022] Figure 2 shows one embodiment of the present invention a canister 6 of reduced size. Also portrayed in Figure 2 is the difference between this embodiment and the prior art for chemical respirators, the current C2A1 canister 4. The difference in canister size is evident and represents an approximate 85% reduction in material weight and about 80% reduction in overall volume. The smaller sized C2A1 canister 6 still maintains equivalent pressure drop across the bed and improves performance by 100%. This also allows for breathing.

[0023] Additionally, because effective desorption when using nanoporous carbons requires elevated temperatures, for example, about 325 °C over 5 minutes, use of the present invention as a filtration media is highly attractive since no analyte desorption is expected at standard operating temperatures for this embodiment,

[0024] Referring to Figure 3, the data show that for ammonia (NH ₃ ), the ASZM- TEDA material performs slightly better than a standard molybdenum or low percent residual titanium nanoporous carbon. However, it is interesting to note that the overall breakthrough profiles for the nanoporous carbons are much sharper than ASZ - TEDA. This sharper slope indicates improved complete protection until the material is defeated. Hydrogen treated nanoporous carbon (M08HL) with about 5% residual metal performs better than AS ZM-TEDA and the surface oxidized sample outperforms ASZM-TEDA by almost 300%. This long breakthrough time approaches that of the zeolyie ZSM5, which was specifically designed to trap N¾ and does not perform well for other gases of interest.

[0025 j The data in Figure 3 was obtained using a 20 rag packed bed of material while flowing 1000 mg m ^J of N!¾ through the bed at a rate of 20 ml/ m. These working embodiments were conducted in helium as a helium ionization detector was used to determine the breakthrough curves. The displayed axes were normalized as min/g of material and 100% delivered gas for comparative purposes and to correct for test to test variability in the detector,

[0026] Other embodiments focused on improving the functionalization of the medium. Two paths were investigated in parallel: acid treatment and impregnation by a metal salt. The study on the metal salt impregnation did not lead to any significant improvement in the effective loading despite varying several parameters (salt type, salt concentration,, activation of the CDC, etc .). However, unexpected results were obtained from the stud on acid treatment. Daring the optimization of the acid treatment, it was demonstrated that the performance of a functionaiized o ₂ C is comparable (and in some cases better) to the values obtained with the prior art ARC material.

[0027] One embodiment of this invention is the process or fun ctionalization protocol which utilizes an acid treatment. In one working example of this

embodiment, 300 mg of M0 ₂ C was measured and put in a 40 mL vial. Then, 10 mL of nitric acid was added to the vial with Mo ₂ C The vial was equipped with a condenser and placed on a pre-heated heating block. After heating, Mo _% C was filtered through a sintered glass funnel and then thoroughly rinsed with distilled water until the rinsing water pH becomes neutral. Mo ₂ C was then dried under vacuum at room temperature. [0028] Figure 4 is a graphical representation of the results of a second

embodiment in which the surface of the carbide was activated with the acid treatment developed previously. The results are compared to acid treatment by itself (0% Fe3Cl sample) and to the impregnation only series (I series). The data indicates that the acid treatment alone enhances the effective loading at a higher rate than by combining it with impregnation. In order to investigate potential synergy between the impregnation and the acid treatment, another series was developed whereby the acid treatment followed the impregnation (I+A) series. The data was compared to the results obtained during the previous experiment (Ϊ series). As can be seen, performing the impregnation on activated carbide does not improve the effective loading capacity (A+I series ^' ). Although performing the acid treatment after the impregnation seems to produce some effects (especially at a concentration of 20% in metal salt), it does not surpass the capabilities of samples solely treated with acid treatment (0% Fe3Cl sample).

[0029] Figure 5 is a graphical representation of the effects of different drying conditions on the acidification treatment, In these embodiments, several drying conditions were investigated. The first parameter investigated was the temperature at which the drying step occurred. Temperatures varying from room temperature to 350°C were tested with a drying duration of 2 hours. There is a significant improvement in the effective loading (30%) when drying the sample at higher temperatures, with a superior capacity at 240°C (WE = 0.093 g ¾/g CDC). Higher temperatures did not further enhance the effective loading.

[0030] Figure 5 also provides a graphical representation comparing one embodiment of this invention with prior art Aramonia Removal Carbon (ARC), This comparison was performed in order to remove variability due to the experimental setup, and therefore establish a baseline number using the current state of the art niateriai in ammonia removal. Upon reception of the ARC, it was indicated that the ARC had an effective loading of about 0.17 NH3/g ARC. The data obtained on the set-up for the ARC samples are reproducible (<1 % in standard deviation) and provided and average of 0.059 g N¾ / g ARC. Based upon oar current testing results, the materials provided effective loading ranging from 0.052 to 0.093 g N3¾ / g CDC,

demonstrating tha t this embodiment of the invention has, at the least comparable, and, at the best, better than capabilities comparable to the state of the art material.

[0031 Although the absolute values of the effective loading are currently in discussion, the ammonia removal capacity of a material is an intrinsic property.

Consequently, if two materials are behaving similarly on one set-up, they should also perform similarly on a second test platform.

[0032] Figure 6 is a graphical representation of a comparison of the breakthrough points of one embodiment of this material with the prior art ARC. The elevated WE for the ARC samples can be attributed to a low slope for the signal rise while the breakthrough point is relatively early {< 1,000 min / g of sorbent). Alternatively, the breakthrough point for the present embodiment is at a greater time (> 1 ,500 min g of sorbent) and corresponds to a sharp increase in signal. This difference is critical in practical terms. As seen in Figure 6, by the time the present embodiment materials goes through breakthrough, the ARC material has already reached a significant portion of its loading capacity, at least 20%-30% when compared to the a first embodiment and up to 80%-90% when compared to a second embodiment.

Consequently, the individuals / soldiers would be breathing an. atmosphere free of ammonia for longer period of times with gas .masks using the second embodiment when compared to gas masks using the prior art ARC.

[0033] In summary, several of the embodiment materials have demonstrated effective loadings comparable to the effective loading of prior art ARC. One embodiment of the invention has demonstrated an effective loading of 0.093 g N¾ / g CDC, Finally, the breakthrough times for the embodiments are significantly greater than the ones measured for prior art, ARC, demonstrating an enhanced perfonnance over prior art materials.

[0034] While the present invention has been described in connection with the preferred embodiments of the various figures, it is to be understood that other similar embodiments may be used or modifications and additions may be made to the described embodiment for performing the same function of the present invention without deviating therefrom. Therefore, the present invention should not be limited to any single embodiment, but rather construed in breadth and scope in accordance with the reci tation of the appended claims.