SPALLATION

CROSS-REFERENCE TO RELATED APPLICATION

[0002] This application claims priority from U.S. Application No, 13/625, 134, tiled 24 September 2012, entitled "Surface Modification to Prevent Oxide Scale Spallation".

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

[0002] The invention was made with Government support under Contract DE-AC05- 76RL01830, awarded by the U.S. Department of Energy. The Government has certain rights in the invention.

TECHNICAL FIELD

[0003] This invention relates to surface morphology. More specifically, this invention relates to a modified surface of a ferritic stainless steel structure exhibiting a periodic morphology on tbe cross-section of the surface.

BACKGROUND OF THE INVENTION

[0004] Under typical solid oxide reel cell (SOFC) operating conditions, an oxide scale layer inevitably forms on the surface of ferritic stainless steels, If tbe resulting scale/metal interface is structurally weak, spallation, peeling, or delamination can occur along the scale/metal interface. This can lead to degradation of interconnect performance and redaction of useful stack life,

[0005] To improve scale adhesion between the oxide scale and the steel alloy, various coating applications have been developed and employed. These coating applications include treating the al loys with oxygen active elements or adding a rare earth element to certain coatings. Although these techniques have been proven io improve seaie adhesion, they eventually result in oxide scale growth and serious cell performance degradation. T herefore, a new approach is needed to prevent delanunation/spallation of the oxide scale on the surface of ferritic stainless steels.

SUMMARY OF THE INVENTION

[0006] The present invention is directed to a surface modification to prevent oxide scale spallation, in one embodiment, the surface comprises a ferritic stainless steel substrate having a modified surface. A cross-section of the modified surface exhibits a periodic morphology.

[0007] In one embodiment, the periodic morphology does not exceed a critical buckling length. The critical buckling length is equivalent to the length of a wave attribute observed in the cross section periodic morphology.

[0008] In one embodiment, the modified surface has been subject to shot peening. In another embodiment, the modified surface has been subject to surface blasting, in another embodiment, the modified surface has been subject to surface grinding.

[0009] in one embodiment, the modified surface further comprises a coating. The coating can comprise, but is not limited to, a rare-earth element containing oxide. The oxide can be, but Is not limited to, a Mn-Co spinel oxide.

[0010] Preferably, the periodic morphology is applied to the steel prior to application of the coating, as the coating tends to compensate for or smooth out some of the texture of the underlying steel. The steel can be, but is not limited to, a solid oxide fuel cell (SOFC) interconnect. [0011] In one embodiment, the cross-section of the modified surface comprises a real or true surface area greater than its original or apparent surface area.

[0012] iN another embodiment of the present invention, a method of surface modification to prevent scale spal lation is disclosed. The method comprises providing a ferritic stainless steel substrate having a surface. The method also comprises forming a periodic morphology an the cross-section ofthe surface of the substrate.

[0013] In one embodiment the method comprises subjecting the surface to shot peening, surface blasting, and/or surface grinding,

[0014] In another embodiment of the present invention, a surface modification to prevent oxide scale spallation is disclosed. The surface modification includes a ferritic stainless steel substrate having a modified surface. A cross section of the modified surface exhibits a periodic morphology. The periodic morphology does not exceed a critical buckling length. The critical buckling length is equivalent to the length of a wave attribute observed in the cross section periodic morphology,

BRIEF DESCRIPTION OF THE D]AWINGS

[0015] Figure 1 illustrates a periodic surface morphology. High, compressive stress regions are indicated on the interface of the oxide scale/substrate.

[0016] Figure 2A shows cross-section images of the periodic surface morphology applied to a stainless-steel substrate, created through shot-peening,

[0017] Figure 2B shows cross-section images of the periodic suriace morphology applied to a stainless-steel substrate, created through shot-blasting,

[0018] Figure 3 shows an image of a coated 441 SS substrate exposed to 850 °C for 2000 hours without surface modification.

[0019] Figure 4A shows an image of a coated 441 SS substrate thai was surface modified, in accordance with one embodiment of the present invention, and then exposed to 850 °C for 2000 hours or one thermal cycle.

[0020] Figure 4B shows an image of a coated 441 SS substrate that was surface modified, in accordance with one embodiment of the present invention, and then exposed to 850 °C for 4000 hours or two thermal cycles.

[0021] Figure 4C shows an image of a coated 441 SS substrate that was surface modified, in accordance with one embodiment of the present invention, and then exposed to 850 °C for 6000 hours or three thermal cycles.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0022] The present invention is directed to a periodic, surface morphology on a ferritic stainless steel substrate, which can be used as part of an Interconnect of a SOFC stack, to prevent oxide scale spallation.

[0023] Hutchinson and Sno (Hutchinson, J.W. and Z, Suo "Mixed mode cracking in layered materials." Advances in Applied Mechanics 29 ; 1991 ):63-19 1.) describe the critical buckling stress for a circular disk crack under compression as the following:

[0025] where the critical buckling stress, σ _cr , is inversely proportional to a ² for a given oxide thickness, H, in which a is the radius of the free standing crack along the

oxide/substrate interface, E is the oxide scale elastic modulus, and y is the oxide scale Poissork s ratio. From this relationship, we deduced that creating a global, periodic surface morphology, as illustrated in Figure 1 , may play an effective role in reducing the length of o. thus Increasing the critical stress level required for the oxide scale to buckle. In Figure 1 , high, compressive stress regions 100 are observed on the interface of the oxide

scale/substrate.

[0026] The value of the free standing crack radius, a, is system dependent for it depends on the mechanical properties of the oxide scale and the thickness of the oxide scale for a given substrate. For spallation not to occur, the spallation .resistance must be greater than the buckling driving force ( σ _cr ), i.e., cooling induced compressive stress in the scale. Hence, we define the following relation for a from Equation i : [0027] (2)

[0028] And once a is determined, 2a (the critical buckling length) may then be determined. The oxide thickness, H. can be extrapolated from oxide growth kinetic curves and the physical properties of the oxide scale (i.e. σ _cr, E, v) may be measured through varying experimental techniques,

[0029] Applying this relationship to our embodiment of Ce-spinel coated 441SS substrates where a chromia scale, Cr ₂ O ₃ , forms on the substrate surface, we can determine a for an oxide thickness at 40,000 hoars of iC life (the IC matenai life requirement) and then determine 2a. the critical length that should not be exceeded. This critical buckling length is equivalent to the length of the wave attribute observed in the cross-section periodic morphology.

[0030] We have determined that a should not exceed 94 μm, therefore, the critical buckling length (2a) should not exceed 188 μm for our Ce-spinel coated SS441, embodiment to meet the designed life of 40,000h.

[0031 ] Surface modification of a metallic substrate with a periodic surface morphology may be achieved by various processing techniques. These techniques include, but are not limited to, shot peeniug, surface blasting and surface grinding.

[0032] Figure 2A and 28 are cross-section images of the periodic surface morphology applied to 441 stainless-steel substrates prior to coating, In accordance with one embodiment of the Present Invention. Magnified images of a section of the profile are also included. A "waviness" attribute of the periodic morphology on the surface of the substrate is observed with Figure 2A illustrating a more regular, periodic surface morphology and Figure 2B illustrating a less regular, periodic surface morphology.

[0033] In Figure 2A, the periodic surface morphology was created through shot-peeniag. In Figure 2B, the periodic surface morphology was created through surface blasting.

[0034] An extension of IC life is observed when the surface of 441 SS substrates is modified with a periodic surface morphology before coating. When coated 44! SB substrates are exposed to either 800°C or 850°C for an extended length of time (i.e. 2000h) without the periodic surface morphology, the oxide scale spalls when, the specimen is cooled to room temperature as shown In Fig. 3. However, when the surface of 441 SS substrates are modified with a periodic surface morphology before coating, then exposed to the same elevated temperatures for the same duration or longer, no spallation is observed upon cooling (Fig. 4A),

[0035] The "no apallation" result has been observed In many coated 441 SS specimens where the surface of each specimen was modified with the periodic morphology of the Present invention and then exposed to SOFC operating temperatures. No spallation was observed in surface modified specimens that were exposed to 800 "'€ up to ten 2000 hour thermal cycles - total of 20,000 hours exposed at temperature - and also in surface modified specimens that were exposed to 850 °C up to six 2000 hour thermal cycles (total of 12,000 hours exposed at temperature). At the end of each 2000 hour thermal cycle, specimens were cooled to room temperature.

[0036] Figures 4 A - 4C show images of surface modified 441 SS coated specimens at the end of each thermal cycle where the specimen was exposed at 850 ^° C and no spallation was observed. In Figure 4A, the substrate was surface modified and then exposed to 850 °C for 2000 hours (or one thermal cycle). In Figure 4.8, the substrate was surface modified and then exposed to 850 °C for 4000 hours (or two thermal cycles), in Figure 4C, the substrate was surface modified and then exposed to 850 °C for 6000 hours (or three thermal cycles). From these results, li Is _. evident that toe surface modification of rise Present invention is delaying or mitigating oxide scale spallation.

[0037] As mentioned, an optional coating can be applied to the stainless steel substrate after modification of the surface. The coating can include a rare-earth element, such as cerium, as part of the oxide coating material In one embodiment the oxide is a Mo-Co spinel oxide.

[0038] The present invention has been described in terms of specific embodiments incorporating details to facilitate the understanding of the principles of construction and operation of the invention. As such, references herein to specific embodiments and details thereof are not Intended to limit the scope of the claims appended hereto, it will be apparent to those skilled in the art that modifications can be made in the embodiments chosen for illustration without departing from the spirit and scope of the Invention.