SYNTHESIS OF AN ACRYLIC POLYMER IN FLOW REACTOR
Document Type and Number:
WIPO Patent Application WO/2016/003978
Kind Code:
A1
Abstract:
An improved process for synthesizing acrylic polymers, which is highly controllable to achieve high molecular weight, high conversion rate, and low polydispersity involves continuously introducing initiator(s), acrylic monomer(s), and optionally other monomers capable of polymerizing with the acrylic monomer(s), into a microchannel of a microreactor having an integral micromixer and an integral heat exchanger.

Inventors:
HE MINGQIAN (US)
HORN CLEMENS RUDOLF (FR)
HU JIEYU (US)
JEAN PATRICK (FR)
NIU WEIJUN (US)
SCHISSEL DAVID NEAL (US)
WINNINGHAM MICHAEL JAMES (US)
Application Number:
PCT/US2015/038445
Publication Date:
January 07, 2016
Filing Date:
June 30, 2015
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
CORNING INC (US)
International Classes:
C08F2/01; B01F13/00; B01J19/00; C08F220/12
Domestic Patent References:
WO2010054347A12010-05-14
Foreign References:
US7939033B22011-05-10
Other References:
PAUL WATTS, CHARLOTTE WILES: "Recent advances in synthetic micro reaction technology", CHEM. COMMUN., vol. 2007, 12 October 2006 (2006-10-12), pages 443 - 467, XP002744194, DOI: 10.1039/b609428g
TAKESHI IWASAKI, JUN-ICHI YOSHIDA: "Free radical polymerization in microreactors. Significant improvement in molecular weight distribution control", MACROMOLECULES, vol. 38, 20 January 2005 (2005-01-20), pages 1159 - 1163, XP002744187, DOI: 10.1021/ma048369m
DANIEL WILMS, JOHANNES KLOS, HOLGER FREY: "Microstructured reactors for polymer synthesis: A renaissance of continuous flow processes for tailor-made macromolecules?", MACROMOL. CHEM. PHYS., vol. 209, 13 February 2000 (2000-02-13), pages 343 - 356, XP002744188, DOI: 10:1002/macp.200700588
NENAD MICIC, ALAN YOUNG, JULIEN ROSSELGONG, CHRISTIAN H. HORNUNG: "Scale-up of the reversible addition-fragmentation chain transfer (RAFT) polymerization using continuous flow processing", PROCESSES, vol. 2, 8 January 2014 (2014-01-08), pages 58 - 70, XP002744189, ISSN: 2227-9717, DOI: 10.3390/pr2010058
CHRISTOPHE A. SERRA, ZHENQI CHANG: "Microfluidic-assisted synthesis of polymer particles", CHEM. ENG. TECHNOL., vol. 31, no. 8, 28 July 2008 (2008-07-28), pages 1099 - 1115, XP002744190, DOI: 10.1002/ceat.200800219
NAIR, K, P; VICTOR BREEDVELD, V.; WECK, M., MACROMOLECULES, vol. 41, 2008, pages 3429 - 3438
ISLAMOVA, R.M. ET AL., POLYMER SCIENCE, vol. 48, no. 3, 2006, pages 130
ISLAMOVA, R. M. ET AL., RUSSIAN JOURNAL OF APPLIED CHEMISTRY, 2006
WATTS, P.; WILES, C., CHEM. COMMUN., 2007, pages 443
VANDENBERGH, J.; JUNKERS, T., POLYMER CHEMISTRY, vol. 3, no. 10, 2012, pages 2739
IWASAKI, T.; YOSHIDA, J., MACROMOLECULES, vol. 38, 2005, pages 1159
See also references of EP 3164422A1
Attorney, Agent or Firm:
CICCARELLI, John (Intellectual Property DepartmentSP-TI-0, Corning New York, US)
Download PDF:
Claims:
WHAT IS CLAIMED IS:

1. A process for synthesizing a polymer, comprising:

continuously introducing a fluid stream including at least one radical initiator and at least one monomer into a channel of a reactor having an integral mixer and an integral heat exchanger to effect simultaneous and substantially continuous mixing of the fluid stream, reaction of the monomers, and heat transfer from the resulting polymer product.

2. The process of Claim 1, in which the fluid stream includes at least one acrylate.

3. The process of any of the preceding claims, in which the fluid stream includes at least one alkyl acrylate and a nitrogen containing monomer copolymerizable with the alkyl acrylate.

4. The process of any of the preceding claims, in which the fluid stream includes butyl acrylate and acrylamide.

5. The process of any of the preceding claims, in which at least one monomer that is introduced into the microchannel is dissolved in a solvent in which the monomer is miscible.

6. The process of any of the preceding claims, in which at least one radical initiator is an azo compound.

7. The process of any of the preceding claims, in which at least one radical initiator is azobisisobutyronitrile.

8. The process of any of the preceding claims, in which at least one radical initiator that is introduced into the microchannel is dispersed in a solvent in which the radical initiator is miscible.

9. The process of any of the preceding claims, in which at least one radical initiator is introduced into the microchannel via a first pump and at least one acrylic monomer is introduced into the microchannel via a second pump.

10. The process of any of the preceding claims, in which the copolymer product is poly (butyl acrylate-co-acrylamide).

11. The process of Claim 10, in which the poly (butyl acrylate-co-acrylamide) product has a polydispersity that is less than 5.

12. The process of Claim 10, in which the poly (butyl acrylate-co-acrylamide) product has a polydispersity that is less than 4.

13. The process of any of Claims 10- 11 , in which the poly (butyl acrylate-co- acrylamide) product has a number average molecular weight greater than 50,000.

14. The process of any of Claims 10- 11 , in which the poly (butyl acrylate-co- acrylamide) product has a weight average molecular weight greater than 150,000.

15. The process of any of the preceding claims, in which the conversion yield is greater than 90%.

16. The process of any of the preceding claims, in which the reaction is exothermic and the heat exchanger is controlled such that the copolymer product leaving the microchannel is at a temperature within 50°C of the temperature at an inlet to the microchannel.

Description:
SYNTHESIS OF AN ACRYLIC POLYMER

IN FLOW REACTOR

[0001] This application claims the benefit of priority under 35 U.S.C. § 1 19 of U.S.

Provisional Application Serial No. 62/020,005 filed on July 02, 2014 the content of which is relied upon and incorporated herein by reference in its entirety.

FIELD

[0002] This disclosure relates to the field of synthesis of acrylate copolymers in a continuous flow reactor.

BACKGROUND

[0003] Hydrogen-bonding group containing materials capable of associating into polymer networks have attracted significant research attention and have been proposed as candidate materials for fiber coating applications due to their good solubility, coating properties and elasticity (Nair, K, P; Victor Breedveld, V.; Week, M. Macromolecules 2008, 41, 3429-3438). Free radical polymerization of acrylic monomers initiated by AIBN serves as an excellent method for synthesis of such materials (Islamova, R.M., et al., Polymer Science 2006, 48(3); 130; Islamova, R. M., et al. Russian Journal of Applied Chemistry 2006). Radical polymerization is a fast and exothermic reaction which can quickly release large amounts of heat. Processing at a very large scale has to be slowed down due to the limited heat removal capacity of a batch reactor. A new device featuring miniaturization of the polymerization unit and greater heat transfer efficiency with no heat accumulation during polymerization is required. The microreactor technology is considered an attractive solution because microreactor has process miniaturization and micro heat exchanger (Watts, P.; Wiles, C. Chem. Commun., 2007, 443). Recently, polymerizations using microreactor technology have been investigated (Vandenbergh, J.; Junkers, T., Polymer Chemistry 2012, 3(10), 2739). However, up to now, such polymerization processes have been performed using tubular reactors without integral mixing. In 2005, the Yoshida group reported the preparation of poly(butyl acrylate) in a microreactor system which consisted of a T-shaped micromixer and tubular flow paths with a heat-conductive reactor (Iwasaki, T.; Yoshida, J., Macromolecules 2005, 38, 1 159). It was found that material with a lower polydispersity index (PDI) of molecular weight than that produced in a batch reactor could be prepared. In this device, the microtube possessed good properties for heat exchange, but didn't play a role in mixing.

[0004] Polymerization of butyl acrylate and acrylamide was used as a model reaction to study polymerization in a microreactor. Our results demonstrated that a microfluidic process strategy with simultaneous micromixing and heat transfer for the scale-up of a free radical co- polymerization process is a promising method.

SUMMARY OF THE DISCLOSURE

[0005] An improved process for synthesizing a polymer via radical chain

polymerization is provided by continuously introducing at least one radical initiator and at least one monomer that is polymerizable via radical chain polymerization, into a channel of a reactor having integral mixing and integral heat exchange to effect simultaneous and continuous mixing of the monomers and reaction products, and heat transfer from the resulting copolymer product to a coolant circulating through the heat exchanger.

[0006] At least one monomer can be an acrylate, such as butyl acrylate.

[0007] At least two acrylic monomers can be used in the process, such as butyl acrylate and acrylamide.

[0008] The monomer(s), radical initiator(s), or both can be introduced to the reactor either with or without a solvent carrier.

[0009] The radical initiator can be an azo compound, such as azobisisobutyronitrile.

[0010] At least one radical initiator can be introduced into the channel by a first pump and at least one monomer can be introduced into the channel by a second pump.

BRIEF DESCRIPTION OF THE DRAWINGS

[0011] Figure 1 is a schematic illustration of a microreactor used in the disclosed polymerization process.

DETAILED DESCRIPTION [0012] The disclosed polymer syntheses differ from conventional free-radical initiated chain reactions by being performed in a continuous flow reactor having a reactor channel with integral heat exchange and substantially continuous mixing induced by mixers integrated into the reactor channel. This arrangement provides very uniform concentrations of reactant(s), products and initiator(s) within a differential volume of the reactor channel defined by a transverse cross-sectional area of the channel having a differential length along the flow direction of the channel. The integral heat exchange allows temperature(s) and temperature gradients within the continuous reactor to be precisely controlled.

[0013] An example of a continuous reactor having an integral heat exchanger and a permanent mixing is schematically illustrated in Figure 1. The reactor 10 includes a channel 12 in which the chemical reactions or polymer syntheses occur. The reactant(s), products and initiator(s) continuously flow through the channel 12, such that the reactor 10 is similar to a plug flow reactor having integral heat exchange and integral mixers. However, the hydraulic diameter of the channel is typically less than 5 millimeters, more typically less than 1 millimeter, and can be less than 500 micrometers. Such reactors are typically referred to as meso-reactors (channel dimensions from about 300 μιη to about 5 mm) or micro-reactors (channel dimensions from about 10 μιη to about 300 μιη).

[0014] An example of a suitable reactor that provides appropriate mixing and thermal control is illustrated and described in U.S. Patent No. 7,939,033, which is incorporated in its entirety herein.

[0015] Reactants are introduced from a tank 14 via a first pump 16; an initiator is introduced from a second tank 18 via a second pump 20. A first section of reactor 10 can include channels 22 and 23 for adjusting the temperature of the reactant(s) and initiator(s) before they are combined at a mixing point 24 (e.g., a T- or Y- shaped convergence of channels 22 and 23 into channel 12).

[0016] Along the flow path of channel 12 is one or a plurality of micromixers 26. In the schematic illustration (Figure 1), a plurality of discrete micromixers 26 are shown.

However, the integral micromixer can extend continuously along the entire length of the microchannel 12. Micromixer(s) 26 can be passive or active. Examples of known passive micromixers that can be incorporated into microreactor 10 include parallel lamination and sequential lamination micromixers in which the flow stream is split into a plurality of sub- streams that are rejoined to form a laminate stream; and chaotic advection micromixers in which, for example, obstacles are incorporated in the microchannel to create transverse flow, or the microchannel walls are provided with a pattern of grooves to induce transverse flow. Examples of known active micromixers that can be used in the disclosed polymer synthesis apparatus include pressure field disturbance micromixers that incorporate an integrated micropump in the microreactor that alternately drives and stops or accelerates and slows flow within the microchannel; electrokinetic instability micromixers that take advantage of a fluctuating electric field to induce mixing in the microchannel; dielectrophoretic disturbance micromixers in which polarization of fluid components is induced by a non-uniform electric field causing movement of the polarized component; magneto-hydrodynamic disturbance micromixers, in which induction of Lorentz body forces in an electrolyte solution creates current flows and mixing; and ultrasound disturbance micromixers in which ultrasonic waves are introduced into the microchannel, such as by integrated piezoelectric ceramic transducers, to cause acoustic stirring of the fluid perpendicular to the main flow direction to cause mixing. Other types of micromixers can also be used. It is also possible to use a combination of micromixers.

[0017] Microreactor 10 is also provided with an integral heat exchanger 30 in which a thermal fluid (e.g., a coolant) is introduced from a tank 32 via a pump 34 into fluid passageways in intimate thermal communication with microchannel 12. In the event of a highly exothermic reaction, which is typical for radical initiated chain reaction synthesis of acrylic polymers, the heat of reaction is transferred from the fluid stream to the coolant and exits the microreactor 10 via thermal fluid outlet 36. While the illustrated reactor 10 implies a single flow chamber in microreactor 10 for the thermal fluid, multiple thermal fluid inlets and outlets can be provided.

[0018] The term "polymer" encompasses homopolymers and copolymers comprised of at least one type of monomer unit (i.e., the portion of the monomer that is incorporated into the polymer chain).

[0019] Monomers that are polymerizable via radical chain polymerization include, but are not limited to, ethylene, 1,3-dienes, styrene, halogenated alkenes, vinyl esters, acrylates, methacrylates, acrylonitrile, methacrylonitrile, arylamide, methacrylamide, N- vinylcarbazole, and N-vinyl pyrrolidone. [0020] Acrylic monomers that are polymerizable via radical chain polymerization include, but are not limited to, acrylamides and methacrylamides such as 2-acrylamido-2- methyl-l-propanesulfonate, 3-(acrylamido) phenylborate, 3-acrylamidopropyl- trimethylamine, N-acryloylamido - ethoxyethanol, alkylacrylamides, N-(3-aminopropyl) methacrylamide, N-tert-butylacrylamide, diacetone acrylamide, Ν,Ν-diethylacrylamide, N,N- diethylmethacrylamide, Ν,Ν-dimethylacrylamide, N-[3-(dimethylamino)-propyl]

methacrylamide, N-ethylacrylamide, N-hydroxyethyl acrylamide, N-(hydroxymethyl) acrylamide, N-(isobutoxymethyl)-acrylamide, N-isopropylacrylamide, N- isopropylmethacrylamide, methacrylamide, N-(3-methyoxypropyl)-acrylamide, N- phenylacrylamide, N-(triphenylmethyl) methacrylamide and N-[tris(hydroxymethyl) methyl] acrylamide; acrylates, such as 4-acetoxyphenethyl acrylate, acryloyl chloride, 4- acryloylmorpholine, 2-(4-benzoyl-3-hydroxyphenoxy)ethyl acrylate, benzyl 2-propylacrylate, butyl acrylate, 2-[[(butylamino)carbonyl]oxy]ethyl acrylate, tert-butyl 2-bromoacrylate, 4- tert-butylcyclohexyl acrylate, 3-(dimethylamino)propyl acrylate, ethyl acrylate, ethyl 2- (bromomethyl)acrylate; acrylic acids, such as acrylic acid, 2-bromoacrylic acid, 2- (bromomethyl)acrylic acid, 2-ethylacrylic acid, methacrylic acid, 2-propylacrylic acid, 2- (trifluoromethyl)acrylic acid; acrylonitrile; fluorinated acrylics, such as

2,2,3,3,4,4,5,5,6,6,7,7-dodecafluoroheptyl acrylate, 2,2,3,3,4,4,4-heptafluorobutyl acrylate, 2,2,3,3,4,4,4-heptafluorobutyl methacrylate, 2,2,3, 4,4,4-hexafluorobutyl acrylate, 2,2,3,4,4,4- hexafluorobutyl methacrylate, 1, 1, 1,3,3,3-hexafluoroisopropyl acrylate, 1, 1, 1,3,3,3- hexafluoroisopropyl methacrylate; and methacrylates, such as allyl methacrylate, 2- aminoethyl methacrylate, benzyl methacrylate, glycidyl methacrylate, hydroxybutyl methacrylate, 2 -hydroxy ethyl methacrylate, isobutyl methacrylate, methyl methacrylate, phenyl methacrylate, 3-(trimethoxysilyl)propyl methacrylate, (trimethylsilyl)methacrylate, vinyl methacrylate.

[0021] Other monomers that are polymerizable via radical chain polymerization include vinyl monomers, such as vinyl acetate, vinyl propionate, vinyl butyrates, vinyl benzoates, vinyl isopropyl acetates, vinyl halides, vinyl aromatics (e.g., styrene) allylic monomers, such as allyl acetate; and other ethylenically unsaturated monomers.

[0022] The radical initiator(s) can be thermal initiators that undergo thermal, homolytic dissociation to generate radicals. Examples of thermal initiators include peroxides such as benzoyl peroxide, dibenzoyl peroxide, succinic acid peroxide, dilauroyl peroxide, didecanoyl peroxide, dicumyl peroxide, di-t-butyl peroxide, di-t-amyl proxide, a,a'-di(t-butyl peroxy) diisopropyl-benzene, 2,5-dimethyl-2,5-di-(t-butylperoxy) hexane, 2,5-dimethyl-2,5- di-(t-butylperoxy) hexyne-3, t-butyl cumyl peroxide, a-cumyl peroxyneodecanoate, a-cumyl peroxyneopheptanoate, t-amyl peroxyneodecanoate, t-butyl peroxyneodecanoate, di-(2- ethylhexyl) peroxy-dicarbonate, t-amyl peroxypivalate, t-butyl peroxypivalate, 2,5-dimethyl- 2,5 bis (2-ethyl-hexanoylperoxy) hexane, dibenzoyl peroxide, t-amyl peroxy-2- ethylhexanoate, t-butyl peroxy -2 -ethylhexanoate, l, l-di-(t-amylperoxy) cyclohexane, 1, 1-di- (t-butylperoxy) 3,3,5-trimethyl cyclohexane, l, l-di-(t-butylperoxy) cyclohexane, OO-t-amyl- 0(2-ethylhexyl) monoperoxycarbonate, OO-t-butyl O-isopropyl monoperoxycarbonate, 00- t-butyl 0-(2-ethylhexyl) monoperoxycarbonate, t-amyl peroxybenzoate, t-butyl

peroxyacetate, t-butyl peroxybenzoate, ethyl 3,3-di-(t-amylperoxy) butyrate, ethyl 3,3-di-(t- butylperoxy) butyrate, dicumyl peroxide; and azo compounds such as 4,4'-azobis(4- cyanovaleric acid), l, l '-azobis(cyclohexane carbonitnle), azobisisobutyronitrile (AIBN), and 2,2'-azobis(2-methylpropionamidine) dihydrochloride, 2,2'-aziobis[2-imidazolin-2-yl) propane] dihydrochloride, 2,2'-azobis[2-(2-imidazolin-2-yl) propane disulfate dehydrate, 2,2'-azobis(2-methylpropionamidine) dihydrochloride, 2,2'-azobis[N-(2-carboxyethyl)-2- methylpropionamidine] hydrate, 2,2'-azobis {2-[ l-(2-hydroxyethyl)-2-imidazolin-2-yl] propane} dihydrochloride, 2,2'-azobis[2-(2-imidazolin-2-yl) propane], 2,2'-azobis(l-imino- l-pyrrolidino-2-ethylpropane) dihydrochloride, 2,2'-azobis {2-methyl-N-[l,l-bis

(hydroxymethyl)-2-hydroxyethyl] propionamide} and 2,2'-azobis[2-methyl-N-(2- hydroxy ethyl) propionamide].

[0023] The radical initiator(s) can be photochemical initiators that produce radicals when irradiated, typically with ultraviolet or visible light. Examples of photochemical initiators that can be used in the process disclosed herein include benzophenone (e.g., "IRGACURE 500"), methylbenzoyl formate (e.g., "DAROCUR MBF"), 1-hydroxy- cyclohexyl-phenyl-ketone (e.g., "IRGACURE 184"), 2-hydroxy-2-methyl-l -phenyl- 1- propanone (e.g., DAROCUR 1 173"), 2-hydroxy-l-[4-(2-hydroxyethoxy) phenyl] -2 -methyl- 1-propanone (e.g., "IRGACURE 2959"), oxy-phenyl-acetic acid 2-[2 oxo-2 phenyl-acetoxy- ethoxy]-ethylester and oxy-phenyl-acetic 2-[2-hydroxy-ethoxy]-ethyl ester (e.g.,

"IRGACURE 754"), alpha, alpha-dimethoxy-alpha-phenylacetophenone (e.g., "IRGACURE 651"), 2-benzyl-2-(dimethylamino)-l-[4-(4-morpholinyl) phenyl] -1-butanone (e.g.,

"IRGACURE 369"), 2-methyl-l-[4-(methylthio)phenyl]-2-(4-morpholinyl-l-propano ne (e.g., "IRGACURE 907"), diphenyl(2,4,6-trimethylbenzoyl)-phosphine oxide (e.g., "DAROCUR TPO"), phosphine oxide, phenyl bis (2,4,6-trimethyl benzoyl) (e.g., "IRGACURE 819"), bis(eta 5-2,4-cyclopentadien-l-yl) bis [2,6-difluoro-3-(lH-pyrrol-l-yl) phenyl] titanium (e.g., "IRGACURE 784"), 1-hydroxy-cyclohexyl-phenyl-ketone (e.g., ("IRGACURE 184"), 2- hydroxy-2-methyl-l -phenyl- 1-propanone (e.g., "DAROCUR 1173"), 2-hydroxy-l-{4-[4-(2- hydroxy-2-methyl-propionyl)-benzyl] -phenyl} -2-methyl-propan- 1 -one (e.g., "IRGACURE 127"), 2-hydroxy-l-[4-(2-hydroxyethoxy)phenyl]-2-methyl-l-propanone (e.g., "IRGACURE 2959"), IRGACURE 184 (50%), benzophenone (50%) (e.g., "IRGACURE 500"), phenylglyoxylate, oxy-phenyl-acetic acid 2-[2-oxo-2-phenyl-acetoxy-ethoxy]-ethyl ester and oxy-phenyl-acetic acid 2-[2-hydroxy-ethoxy]-ethyl ester (e.g., "IRGACURE 754"), phenyl glyoxylic acid methyl ester (e.g., "DAROCUR MBF"), 2,4,6-trimethylbenzoyl- diphenylphosphine oxide (e.g., "LUCIRIN TPO"), 2,4,6-trimethylbenzoyl-diphenyl phosphinate (e.g., "LUCIRIN TPO-L"), liquid blend of acylphosphine oxides (e.g.,

"IRGACURE 2100"), bis(2,4,6-trimethylbenzoyl)-phenylphosphineoxide (e.g., "IRGACURE 819"), IRGACURE 819 (45% active) dispersed in water (e.g., "IRGACURE 819 DW"), LUCIRIN TPO (50% by weight) DAROCUR 1173 (50% by weight) (e.g., "DAROCUR 4265"), IRGACURE 819 (20% by weight) DAROCUR 1173 (80% by weight) (e.g., IRGACURE 2022"), titanocene radical initiator titanium, bis (rj5-2,4-cyclopentadien-l-yl) bis [2,6-difluoro-3-(lH-pyrrol-l-yl)phenyl]- (e.g., "IRGACURE 784"), oxime esters, oxime ester radical initiator [l-(4-phenylsulfanylbenzoyl)heptylideneamino]benzoate (e.g.,

"IRGACURE OXE 01"), oxime ester radical initiator [l-[9-ethyl-6-(2- methylbenzoyl)carbazol-3-yl]ethylideneamino] acetate (e.g., "IRGACURE OXE 02"), 2- methyl-l[4-(methylthio)phenyl]-2-morpholinopropan-l-one (e.g., "IRGACURE 907"), 2- benzyl-2-dimethylamino-l-(4-morpholinophenyl)-butanone-l (e.g., "IRGACURE 369"), 2- dimethylamino-2-(4-methyl-benzyl)-l-(4-morpholin-4-yl-phenyl )-butan-l-one (e.g., "IRGACURE 379"), modified a-aminoketone (e.g., "IRGACURE 389"), benzophenone (BP), benzophenone (e.g., "DAROCUR BP"), and benzildimethyl ketal, 2,2-dimethoxy-l,2- diphenylethan-l-one (e.g., "IRGACURE 651"). [0024] The above photoinitiators and thermal initiators are illustrative examples.

These and other radical initiators may be used individually or in combination.

[0025] The monomer(s) and the radical initiator(s) can be introduced to the reactor in the form of a fluid (liquid) stream comprising a solvent into which the monomer(s) and radical initiator(s) are dissolved. In order to facilitate high conversion of monomer(s) to polymer, while maintaining a fluid stream throughout the reactor (i.e., to prevent plugging of the reactor channel), the fluid stream typically comprises a high percentage of solvent, e.g., greater than 20% solvent, greater than 30% solvent, greater than 40% solvent, or greater than 50% solvent. However, the amount of solvent may be adjusted outside these limits depending on the characteristics of the radical polymerization system (e.g., monomer(s)), residence time, temperatures, initiators), etc.).

[0026] Conventional amounts of initiator(s) can be employed as needed to achieve a desired result (e.g., number or weight average molecular weight, molecular weight distribution or polydispersity, conversion, etc.).

[0027] Compared with a batch reactor, a flow reactor provides several significant features for acrylate copolymerization where both solvent and solvent-free polymerization processes can be done with good thermal control. The amount of polymer could be produced by changing the flow rate or residence time. Increasing flow time could lead to large-scale production. Flow rate and conversion rate can be easily controlled. Well managed heat exchange process for radical reactions is possible. Generally speaking, the polymerization process in a flow reactor is faster than that in a batch process. Polymerization was complete in shorter reaction times, as low as 7 min. A much higher average molecular weight (Mn and Mw) and far lower polydispersity index (PDI) than that produced in a batch reactor could be achieved due to better controlled reaction conditions.

[0028] Reduced operation cost is also achieved based on a reduction in equipment- size/production-capacity ratio (reaction took place in 9 modules with the size of most credit cards), labor (due to shorter reaction time and higher yield), waste production (due to high selectivity in flow reactor along with reduction of solvent used), energy consumption (lower amount of solvent requires less energy for solvent evaporation), and research cost (increasing flow time could lead to large-scale production in flow reactor; while in batch reactor, though the reaction conditions can be realized in small glass laboratory equipment with certain effort, the conditions on the pilot plant scale still need to be investigated due to safety issues).

[0029] Reduced risks associated with large scale radical polymerization are also achieved. The microreactor showed a much wider safe process window due to better heat transfer and process miniaturization (processing at a very large scale has to be slowed down to a technically controllable level.)

[0030] Reaction conditions including residence time and temperature were easily controlled. Scale up polymerization in the flow reactor can be realized by simply increasing flow time without compromising safety.

[0031] The disclosed process will be further illustrated with the following specific examples.

[0032] The disclosed processes generally achieve higher number and weight average molecular weights, e.g., greater than 50,000 and 150,000, respectively, and lower

polydispersity, such as less than 5 or less than 4, as compared with batch processes. The processes also achieve relatively high conversion rates, e.g., greater than 90%, greater than 95% or greater than 99%.

EXAMPLE 1

[0033] The conversion of butyl acrylate and acrylamide to copolymer (BA-co-AA) is illustrated in this example. For comparative purposes a conventional batch reaction is performed by dissolving acrylamide (AA, 1 eq) in butyl acrylate (BA, 49 eq), to obtain solution A. Azoisobisbutyronitrile (0.21 eq) is dissolved in a solvent to obtain solution B. Solution B and solvent are added to solution A to obtain solution C, which contained 50 wt % of solvent. Solution C is purged with nitrogen for 5 min. to remove dissolved oxygen. Polymerization was performed at 65°C by immersing the reactor in an oil bath for 18 h. Poly (butyl acrylate-co-acrylic acid) with nearly complete conversion after solvent evaporation was obtained (preliminary data indicating greater than 99% conversion).

[0034] Butyl acrylate and acrylamide were copolymerized in accordance with this disclosure in a microreactor as described in U.S. Patent No. 7,939,033. A solution C was prepared using the same procedure as that in the batch reactor process. Solution C was introduced into an inlet of a flow reactor by pump, and continuously flowed through modules which possessed heat exchangers at an 80-100 C range for a residence time of 7 min. The exiting product was collected. Poly (butyl acrylate-co-acrylic acid) was produced at a rate of 0.5g/min. A 94% conversion yield was obtained after solvent evaporation.

[0035] The chemical structures of the obtained polymers were characterized by 1H

NMR and FT-IR as follows:

1H NMR (CD2C12, 300 MHz, 300 K):

δ (ppm) 4.05-4.01 (m, 2H, OCH2CH2CH2CH3); 2.28-2.26 (m, 1H, CHCO); 2.28- 2.26, 1.91-1.88, 1.62-1.56 (m, 1H, CHCHCO); 1.62-1.56 (m, 2H, OCH2CH2CH2CH3); 1.41-1.34 (m, 2H, , OCH2CH2CH2CH3); 0.94 (t, J=7.5 Hz, 3H, , OCH2CH2CH2CH3);

FT-IR (neat, cm-1) 1724 (C=0 stretching); 1637 and 1621 (C=C stretching, disappeared); 1 185

(O-C stretching)

[0036] GPC data of poly (butyl acrylate-co-acrylic acid):

The polymers were characterized by gel permeation chromatography (GPC). The samples are diluted using a tetrahydrofuran + 0.05% toluene solution to a concentration of -5000 μg/g (0.5 wt. %). The toluene is used as a flow rate marker to ensure the GPC system is consistent throughout the entire analysis. The instrument used is a Waters Alliance 2695 with Millennium software. The mobile phase is tetrahydrofuran and the column set used is a three set series of Polymer Labs columns: 2-PLgel Mixed D, 5 μιη, 300 x 7.5 mm (polystyrene divinyl benzene copolymer) and 1- PLgel ΙΟθΑ, 5 μιη, 300 x 7.5 mm which are optimum for the molecular weight range of interest. The columns are calibrated using polystyrene standards ranging from 160-6,980,000 using EasiCal PS-1&2 kits. The instrument parameters include using a flow rate @ 1.0 mL/min with a column temp @ 40°C. The injection volume is 100 μϊ ^ using a 100 μϊ ^ sample loop with a run time of 35 minutes at isocratic conditions. The detector was a Waters Alliance 2410 differential refractometer operated at 40°C and sensitivity level 4. The samples were injected twice along with a THF + 0.05% toluene blank. Reported polydispersity (PDI) is the ratio of weight average (M w ) to number average (M n ) molecular weight values. Molecular weights and polydispersities disclosed throughout this description and the appending claims are determined using this procedure.

[0037] A much higher average molecular weight (Mn and Mw) (e.g., Mw greater than 135,000; 140,000; 150,000; 160,000; or 170,000) and far lower polydispersity index (PDI) (e.g., less than 7, less than 6, less than 5, or less than 4), than that produced in a batch reactor were achieved. Reaction in the microreactor showed better selectivity than that in the batch reactor.

EXAMPLE 2

[0038] In 2005, the Yoshida group reported the polymerization of butyl acrylate in a microreactor at 80 or 100°C. (Iwasaki, T.; Yoshida, J. Macromolecules 2005, 38, 1159). To further demonstrate the feasibility to carry out self-polymerization in a Corning flow reactor and compare the process of two flow reactors, butyl acrylate was subjected to radical polymerization in a Corning flow reactor.

[0039] Following the above polymerization processes for both the batch reactor and flow reactor using 50 wt % butyl acrylate solution in toluene in the presence of an effective amount of AIBN, poly(butyl acrylate) was prepared.

[0040] The results of both Corning and Yoshida groups are summarized in the Table below.

[0041] The polydispersity index (PDI) for the polymerization of butyl acrylate in the microreactor was smaller than that obtained in a batch reactor in both groups. However, polymerization in the Corning flow reactor afforded the poly(butyl acrylate) with a higher conversion yield and higher polymer molecular weight than that obtained in the microreactor from the Yoshida group. Entry Reactor Polymerization Conversion Mn Mw PDI condition yield

1 Batch reactor 65°C b /18h 98% 20100 128000 6.37 (Corning)

2 Flow reactor 76-102°C/8min c 99% 20900 97000 4.64 ( Corning)

3 Microreactor 80 or 100°C /5.0 min d 89% 19200 60700 3.16 (Yoshida group)

4 Batch reactor 80 or 100°C/4.0 min 88% 9300 95800 10.3 (Yoshida group) Stainless tube ( i.d. 500 μιη x 1 m, thickness of wall = 540 μιη).

b Temperature of oil bath in which batch reactor was immersed

c The temperature of the top module in flow reactor is 76°C; while the temperature of the bottom module in the flow reactor is 102°C.

d Stainless tube was dipped in an oil bath (80 or 100°C).

[0042] The use of a continuous flow micro- or meso-reactor having integral mixers that provide substantially continuous mixing during the residence time in the reactor, coupled with integral heat transfer for controlling temperatures and temperature gradients in the reactor is believed to provide a combination of high conversion yield, high molecular weight and low polydispersity.

[0043] The described embodiments are preferred and/or illustrated, but are not limiting. Various modifications are considered within the purview and scope of the appended claims.