POLYMORPHS

This application claims the benefit of U.S. Provisional Application No. 62/190,676, filed July 9, 2015, which is incorporated herein by reference.

BACKGROUND

Metal oxide (M _x O _y ) semiconducting materials have had a profound impact on the market for thin film device applications for numerous years. However, cost-effective mass production of high-purity materials remains challenging for scientists and engineers.

SUMMARY

Disclosed herein is a method comprising:

reacting an aluminum mineral polymorph or a gallium mineral polymorph with an acid at an aluminum metal to acid molar ratio or gallium metal to acid molar ratio sufficient to produce Mi3 nanoscale clusters, M nano-agglomerates, or a M13 slurry, wherein M is Al or Ga.

Also disclosed herein is a method comprising:

mixing an aluminum mineral polymorph or a gallium mineral polymorph with an acid to produce a slurry; and

processing the slurry under conditions sufficient to produce an aqueous solution of Μΐ3(μ3-ΟΗ)6(μ2-ΟΗ) ΐ8 (Η2θ)24(Νθ3)ΐ5 nanoscale clusters, wherein M is Al or Ga.

The foregoing will become more apparent from the following detailed description, which proceeds with reference to the accompanying figures.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a structural representation of various aluminum materials that were converted to flat-Ali3 clusters via acidification according to the methods disclosed herein. FIG. 2 shows overall balanced equations for the reaction of metal bulk materials and

FIGS. 3A and 3B are optical microscope images of AI13 (FIG. 3A) and Gai3 (FIG. 3B) single crystal produced from the acidification process disclosed herein.

FIGS. 4A and 4B show dynamic light scattering of AI13 (FIG. 4A) and Gai ₃ (FIG. 4B) in

0.1 M aqueous solutions.

FIGS. 5A and 5B are solid state Raman spectra of AI13 (FIG. 5A) and Gai ₃ (FIG. 5B). Both spectra are consistent with previous reports of both clusters.

FIG. 6 is a powder x-ray of AI13 experimental compared with literature references. FIG. 7 is a ²⁷ Al NMR spectra of A113 Keggin ions from different synthetic methods.

FIG. 8 is a graph showing dielectric constants for AI2O3 thin- films from precursors disclosed herein with selected ratios of Νθ3 ^~ :Α1 ³⁺ . The Keggin ion (Ratio 0.5 N03 ^~ :l Al ³⁺ ) shows a higher dielectric constant, suggesting that the material makes more continuous (less porous) thin-films with a 350 °C anneal. The inset shows the test structure of the MIS device used for the CV measurement.

DETAILED DESCRIPTION

Methods such as vapor deposition are effective for producing atomically-uniform metal oxide thin films; however the process is expensive, time consuming, and product yields are low. Although solution processing of Μΐ3(μ3-ΟΗ)6(μ2-ΟΗ) ΐ8 (Η2θ)24(Νθ3) ΐ5 (M = Al or Ga) clusters is potentially a viable alternative to traditional deposition methods, product variability, reaction conditions, and long reaction times are deterrents for large-scale production. Advancements in the understanding of cluster reactivity have allowed chemists to develop more efficient and safer methods that utilize reducing agents such as zinc and electrochemical titrations to produce the aforementioned clusters. These methods however have significant drawbacks that include: long crystallization periods, extensive purification requirements, production of toxic byproducts, and the use of non-trivial and often expensive electrochemical apparatuses.

Disclosed herein is a facile and non-toxic synthesis of M13 clusters. For convenience, "MB clusters" refers to [Μΐ3(μ3-ΟΗ)6(μ2-ΟΗ) ΐ8 (H20)2 ₄ ]a [X] i5a, wherein a is an integer of 1 to 4, [Mi30 ₄ (OH)2 ₄ (H20) i2)]b[X]7b, wherein b is an integer of 1 to 4, or a mixture thereof, wherein M is Al or Ga and X is a counterion derived from a protic acid. In certain embodiments, a M13 cluster is Μι ₃ (μ3-ΟΗ) ₆ (μ2-ΟΗ)ι ₈ (Η ₂ 0) ₂₄ (Ν03) ΐ5. [Μι ₃ (μ3-ΟΗ) ₆ (μ2-ΟΗ)ι ₈ (H ₂ 0) ₂₄ ]a [X] _15a is also known as "flat" M13 and [Mi ₃ 04(OH)24(H ₂ 0)i2)]b[X]7b is also known as "Keggin" M13. "M nano-agglomerates" refers to a composition comprising M _y species, wherein y is 2 to 32. For example, M nano-agglomerates may include M13 clusters and at least one further M-containing component such as, for example, M-containing dimers and/or trimers, and/or larger aggregates such as M26, M30, or M32. This synthesis requires no purification and takes advantage of acid- base chemistry to produce scalable quantities of clusters, nano-agglomerates, and slurries in high quantitative yields.

In one embodiment, a simple, inexpensive, and atom economical method has been developed to synthesize aqueous flat M13 or Keggin M13 nanoclusters via acidification of representative mineral polymorphs of purified aluminum or gallium oxides, oxyhydroxides, and/or hydroxides (M2O3, MO(OH), or M(OH) ₃ where M = Al or Ga).

Under this principle, the acidification can be done directly with the mineral mined directly from the Earth, but would most likely require some form of purification and separation of other agglomerate material that may be present. With this synthetic route, these clusters can be produced on a mass scale and be potentially utilized for solution processing of amorphous metal oxide (M2O3) dielectric thin film devices commercially. Additionally, the slurry mixture can be used as a polishing agent for surface smoothing.

Nanoscale clusters generally refers to discrete, monodispersed architectures of oligomers linked together with defined dimensions that range from 1 nm < x nm < 5 nm, while nano- agglomerate species refer to dimensions ranging from 5 nm < x nm < 200 nm, and slurries are insoluble motifs that are 200 nm and beyond.

Aqueous nanoscale clusters, nano-agglomerates, and slurry mixtures have been synthesized via the acidification of bulk aluminum and gallium minerals/materials. This process can be carried out at wide concentration gradients from, for example, 1 mM to 4 M metal content and requires virtually no post-reaction purification or separation of excess monomer formed or initial reactant material used. The acidification products have a hydrodynamic radii of 1 nm ± 0.1 nm and can then be used directly "as is" as solution precursors for thin film fabrication so long as the original products used are pure (see, e.g., U.S. Patent No. 9,340,678, for a description of the use as precursors for thin film fabrication). This synthetic route represents a facile, economical, and scalable scheme to mass-produce desirable precursor materials for solution processing transparent thin film devices. Identification of these clusters in the solid and solution states with powder x-ray diffraction, optical microscopy, Raman spectroscopy, and dynamic light scattering was consistent with data previously reported in the literature.

More specifically, disclosed herein in certain embodiments are methods for reacting an aluminum containing polymorphs or a gallium containing polymorphs with an acid to produce Mi3 nanoscale clusters (e.g., Μΐ3(μ3-ΟΗ)6(μ2-ΟΗ) ΐ8 (Η2θ)24(Νθ3)ΐ5 nanoscale clusters). Also disclosed herein are methods of mixing an aluminum containing polymorph or a gallium containing polymorph mineral with an acid to produce a slurry, and processing the slurry under high enough acidic conditions (metal to acid ratio > 1:0.7 mol. eq.) sufficient to produce an aqueous solution of M13 nanoscale clusters (e.g., Μΐ3(μ3-ΟΗ)6(μ2-ΟΗ) ΐ8 (Η2θ)2 ₄ (Νθ3)ΐ5 nanoscale clusters).

In principle, any representative mineral polymorph regardless of oxidation state can be made into a slurry or solution nanoscale cluster or nanoagglomerate in solution under the following conditions: the final product of cluster or agglomerate must contain a stabilizing proton accepting ion [ex. NO3 , P0 ₄ ^3" , C10 ₄ ^" , S0 ₄ ^2" , (X ^" where X = F, CI, Br, or I), CO3 ^2" , TsO ^" , Mn0 ₄ ^" , Se0 ₄ ² ] that would be generated via use of their corresponding acids, stable in the solid state and insoluble from a pH gradient of weakly acidic to weakly basic, and exhibits amphoterism. Thus X in [Μΐ3(μ3-ΟΗ)6(μ2-ΟΗ) ΐ8 (H20)2 ₄ ]a [X] i5a or

[Mi30 ₄ (OH)2 ₄ (H20) i2)]b[X]7b may be monovalent counterion (meaning that subscript a or b is 1) or a polyvalent counterion (meaning that subscript a or b is greater than 1).

Illustrative aluminum-containing mineral polymorphs include corundum, gibbsite, boehmite, diaspore, bayerite, and nordstrandite and any combination or mixture thereof.

Illustrative gallium-containing mineral polymorphs include Ga(0)OH, Ga203, Ga(OH)3 (sohngeite), and any combination or mixture thereof. The acid may be any acid that dissolves the mineral. Illustrative acids that have the ability to dissolve the material include nitric acid, sulfuric acid, selenic acid, halide acids (e.g., hydrochloric acid, hydrobromic acid, hydroiodic acid, chloric acid, bromic acid, iodic acid), sulfonic acids (e.g., tosylic acid, sulfanilic acid, benzene sulfonic acid, salicylic acid, Armstrong's acid, triflic acid), carboxylic acids (formic acid, oxalic acid, acetic acid, carbonic acid), and a mixture thereof. Nitric acid is a preferred acid 1:0.3 - 1:0.65 mol. eq. of metal to acid ratio to produce slurries and 1:0.7 - 1:1.15 mol eq. of metal to acid ratio to produce nanoagglomerates, and 1:1.15 - 1: 1.3 mol eq. of metal to acid to produce clusters). All other monovalent acids listed above will follow the same stoichiometry as nitric acid. In certain embodiments, 1: 1.15 - 1:1.3 mol eq. of metal to acid ratio will produce flat [Μΐ3(μ3-ΟΗ)6(μ2-ΟΗ)ι ₈ (Η ₂ 0)24] [X] i5a. Of note, [Μΐ3(μ3-ΟΗ) ₆ (μ2-ΟΗ)ι ₈ (H ₂ 0) ₂ 4]a [X]is clusters wherein X is polyvalent counterion (e.g., a divalent counterion such as SO4 ^2" ) can be produced by the methods disclosed herein.

In certain embodiments, 1:0.3 - 0.65 mol. eq. of metal to acid ratio (more particularly

1:0.45 - 0.65) will produce Keggin [Mi30 ₄ (OH)24(H ₂ 0) i2)]b[X]7b. Of note,

[Mi304(OH)24(H20)i2)]b[X]7b clusters wherein X is a monovalent counterion (e.g., NO3 ^" ) can be produced by the methods disclosed herein.

The mineral polymorph (M) is reacted with the acid, for example, at a M ³⁺ :N03 ^" molar ratio in a range to produce nanoscale clusters. In certain embodiments, the M ³⁺ :N03 ^" molar ratio is tunable over a wide concentration gradient, provided the M ³⁺ :N03 ^" molar ratio is controlled via controlling the mol. eq. of metal to acid so that the reaction does not proceed to formation of the metal nitrate salt (e.g., A1(N03)3 or gallium nitrate Ga(N03)3). Overall balanced equations for the reaction of metal bulk materials and HNO3 are shown in FIG. 1. The reaction parameters and overall balanced equations are also applicable to acids other than nitric acid.

The mixing typically is carried out until complete dissolution occurs, causing a clear solution.

The slurry may be mixed at temperatures ranging from 25 to 100 °C, more particularly 45 to 80 °C, and most particularly 55 to 75 °C.

The methods described herein may have a reaction time of 12 to 72 hours, more particularly 24 to 36 hours.

The methods disclosed herein do not require the use of any secondary reagents to facilitate cluster formation (e.g., zinc powder or di-butyl nitrosamine) or a potentially expensive electrochemical apparatus setup.

The methods disclosed herein can produce M13 nanoscale clusters on a mass scale since the methods are very amenable to scaling up. For example, different forms of aluminum and gallium minerals can be used as starting materials under the same reaction conditions while consistently achieving the same M13 end product. Only simple, inexpensive, and readily available reagents are used and can be readily scaled up to at least the kilogram scale. Atom economy for these methods is upwards of 90% yield, with water being the primary byproduct.

The methods disclosed herein may result in the formation of an M13 nano-aggregate solution that has several different uses. For example, the M13 nano-aggregate solution may be used as industrial polishing agent for chemical-mechanical planarization (CMP). In a further example, the M13 nano- aggregate solution may be used as solution precursors for solution processing of metal oxide (M2O3) thin films for electronic device. For instance, transparent conductive oxide materials containing Al ³⁺ and/or Ga ³⁺ species derived from the aqueous precursors disclosed herein may be made.

Certain illustrative embodiments are described in consecutively numbered clauses as shown below:

1. A method comprising:

reacting an aluminum mineral polymorph or a gallium mineral polymorph with an acid at an aluminum metal to acid molar ratio or gallium metal to acid molar ratio sufficient to produce Μΐ3(μ3-ΟΗ)6(μ2-ΟΗ) ΐ8 (Η2θ)24(Νθ3)ΐ5 nanoscale clusters, nano-agglomerates, or a slurry, wherein M is Al or Ga.

2. A method comprising:

mixing an aluminum mineral polymorph or a gallium mineral polymorph with an acid produce a slurry; and

processing the slurry under conditions sufficient to produce an aqueous solution of Μΐ3(μ3-ΟΗ)6(μ2-ΟΗ) ΐ8 (Η2θ)24(Νθ3)ΐ5 nanoscale clusters, wherein M is Al or Ga.

3. The method of clause 1 or 2, wherein the aluminum mineral polymorph is selected from corundum, gibbsite, boehmite, diaspore, bayerite, nordstrandite, or any combination or mixture thereof.

4. The method of clause 1 or 2, wherein the gallium mineral polymorph is selected from Ga(0)OH, Ga203, Ga(OH)3, or any combination or mixture thereof.

5. The method of any one of clauses 1 to 4, wherein the acid is selected from nitric acid, sulfuric acid, selenic acid, a halide acid, a sulfonic acid, a carboxylic acid, or a mixture thereof.

6. The method of any of clauses 1 to 4, wherein the acid is nitric acid. 7. The method of any one of clauses 1 or 3 to 6, wherein the aluminum metal to acid molar ratio or gallium metal to acid molar ratio is 1:0.3 mol eq of metal to acid to 1:1.3 mol. eq. of metal to acid. 8. The method of any of clauses 2 to 6, wherein the aluminum metal to acid molar ratio or gallium metal to acid molar ratio is greater than 1:0.7 mol eq.

9. The method of clause 6, wherein the aluminum metal to acid molar ratio or gallium metal to acid molar ratio is 1:0.3 to 1:0.65 mol eq to produce the slurry.

10. The method of clause 6, wherein the aluminum metal to acid molar ratio or gallium metal to acid molar ratio is 1 :0.7 to 1: 1.0 mol eq to produce the nano-agglomerates.

11. The method of clause 6, wherein the aluminum metal to acid molar ratio or gallium metal to acid molar ratio is 1:1.15 to 1:1.3 mol eq to produce the nanoscale clusters.

12. The method of any one of clauses 1 to 11, wherein the method is controlled to avoid formation of A1(N03)3 or Ga(N03)3- 13. The method of any one of clauses 1 to 12, wherein the nanoscale clusters have a dimension ranging from 1 nm to 5 nm.

14. The method of any one of clauses 1 or 3 to 12, wherein the nano-agglomerates have a dimension ranging from 5 nm to 200 nm.

15. The method of any one of clauses 1 or 3 to 12, wherein the slurry comprises insoluble motifs having a dimension greater than 200 nm.

Examples

Solution preparation and synthesis

All reagents were purchased from Sigma Aldrich and used without further modification. Varying M ³⁺ : N0 ₃ ^" molar ratios from 1:0.7-1.154 of M(OH) ₃ , MO(OH), or M2O3 powder to nitric acid (or other acids) are mixed under external ambient pressure forming slurry mixtures that range from 1 mM to 1 M metal content consistent throughout the reaction. The slurry is magnetically stirred at 60 °C until clear, resulting in complete solution dissolution. No further modification to the solution is done for solution phase spectroscopic measurements. For solid- state measurements aliquots of the solution were deposited on glass slides and allowed to crystallize for solid-state characterizations via Raman spectroscopy and single x-ray

crystallography.

Solid state and solution characterization

Prior to analysis, each sample was filtered into the cuvette with a 0.1 PTFE μιη syringe filter to remove any particulate matter. The following dynamic light scattering (DLS) and phase analysis light scattering (PALS) measured using the ΜοΜυζ from Wyatt technologies. DLS was used to measure the hydrodynamic radius (¾) of the alumina species in solution. The Dynamics software uses the Einstein- Stokes equation (Rh = where Kb = the Boltzmann constant, T = temperature in kelvin, η ~ viscosity, and D _t = translational diffusion coefficient to solve for the ¾ value.

Raman spectra were collected using an Alpha 300S SNOM confocal Raman microscope in a 180° backscattering configuration. A continuous wave pump laser provided -50 mW of power with an excitation wavelength of 532 nm. A 0.3 m spectrometer equipped with 600 grooves/mm grating was used to detect stokes Raman scattering and provided a resolution of 1 cm ¹ . The spectra from each sample were averaged over 100 accumulations at 1 second exposure times. The 520.5 cm ¹ peak of Si was used as an internal standard. FIG. 2 is a structural representation of various aluminum materials that were converted to flat-Ali3 clusters via acidification according to the methods disclosed herein.

FIGS. 3A and 3B are optical microscope images of AI13 (FIG. 3A) and Gai3 (FIG. 3B) single crystal produced from the acidification process disclosed herein.

FIGS. 4A and 4B show dynamic light scattering of AI13 (FIG. 4A) and Gai ₃ (FIG. 4B) in 0.1 M aqueous solutions. FIGS. 5A and 5B are solid state Raman spectra of Ah ₃ (FIG. 5A) and Gai ₃ (FIG. 5B). Both spectra are consistent with previous reports of both clusters.

FIG. 6 is a powder x-ray of AI13 experimental compared with literature references.

Synthesis of aluminum AI13 Keggin ion by controlled dissolution of Al(OH)3 in an aqueous monoprotic acid

The aluminum AI13 Keggin cluster [(Α1ΐ3θ4(ΟΗ)24(Η2θ)ΐ2) ⁷⁺ ] is widely used in applications such as water treatment and flocculation. The current synthetic procedure to produce the cluster is addition of an aqueous base, e.g. NaOH, KOH, NH3, or Ca(OH)2 to an aqueous solution of A1(N03)3 or AICI3. By adding 0.54 parts of a monoprotic strong acid to 1 part Al(OH)3 under mild heating conditions (60 - 90 °C), the Keggin ion forms in high yield. The product of this synthesis has been scaled to liter quantities at concentrations as high as 1 M with respect to Al. This approach yields a material free of alkali, alkaline-earth, and transition- metal ions, leading to a protonated version of the material for water remediation and flocculation. FIG. 7 shows the NMR spectrum of the material synthesized using the traditional NaOH titration of A1(N03)3 compared to this claimed dissolution method. Clearly, the spectra from acid addition match the characteristic spectrum for the Na- Keggin

[(NaAli30 ₄ (OH)24(H ₂ 0)i2) ⁷⁺ ].

Additional work shows that the AI13 Keggin cluster [(Α1ΐ3θ ₄ (ΟΗ)2 ₄ (Η2θ)ΐ2) ⁷⁺ ] can be used as a precursor for solution processed amorphous thin-film dielectric materials. Initial data from an MIS test structure suggests an improved quality of film properties using alumina precursors with decreased counterion concentration after annealing at 350 °C (FIG. 8).

In view of the many possible embodiments to which the principles of the disclosed compositions and methods may be applied, it should be recognized that the illustrated embodiments are only preferred examples of the invention and should not be taken as limiting the scope of the invention.