Title:
SYNTHESIS METHOD FOR WIDE-CHROMATOGRAPHIC-BAND IRON OXIDE YELLOW PIGMENT
Document Type and Number:
WIPO Patent Application WO/2023/201973
Kind Code:
A1
Abstract:
A preparation method for a wide-chromatographic-band iron oxide yellow pigment. The preparation method comprises: 1, weighing 0.03-0.08 mol of CTAB (hexadecyl trimethyl ammonium bromide), dispersing in 30-50 mL of deionized water, stirring at room temperature for 30-60 min until a solution becomes transparent, and denoting the solution as a solution A; 2, separately weighing 0.02-0.2 mol of FeCl3 (ferric chloride), dissolving the FeCl3 in the solution A, and stirring for 30-60 min until a homogeneous solution is formed; 3, pouring the solution into a 50 mL Teflon stainless steel high-pressure reaction kettle and carrying out a hydrothermal reaction at 80-120 °C for 6-24 h; 4, after the reaction is completed, cooling the reaction kettle to room temperature; and 5, separately washing with ethanol and distilled water three times and drying at 50-60°. Finally, the wide-chromatographic-band iron oxide yellow with ΔL reaching 5.17 and ΔB reaching 7.18 is obtained.
Inventors:
YAO YIYANG (CN)
AOKI KOSO (JP)
MISHIMA YUJI (JP)
HOMMYO TORAYUKI (JP)
YANG JIANMING (CN)
SHAO YUXIANG (CN)
LI JINHUA (CN)
SHEN HUI (CN)
AOKI KOSO (JP)
MISHIMA YUJI (JP)
HOMMYO TORAYUKI (JP)
YANG JIANMING (CN)
SHAO YUXIANG (CN)
LI JINHUA (CN)
SHEN HUI (CN)
Application Number:
PCT/CN2022/118400
Publication Date:
October 26, 2023
Filing Date:
September 13, 2022
Export Citation:
Assignee:
ZHEJIANG HUAYUAN PIGMENT CO LTD (CN)
International Classes:
C01G49/02; C01G49/06; C09C1/24
Foreign References:
CN114644364A | 2022-06-21 | |||
CN105129862A | 2015-12-09 | |||
CN111180708A | 2020-05-19 |
Other References:
CHENGZHEN WEI ET AL.: "Size-controlled synthesis of Rod-like α-FeOOH nanostructure", MATERIALS SCIENCE AND ENGINEERING C, vol. 32, no. 6, 28 April 2012 (2012-04-28), XP028519623, ISSN: 0928-4931, DOI: 10.1016/j.msec.2012.04.037
HUI ZHANG: "A facile approach to α-FeOOH nanorods with high aspect ratios", ADVANCED MATERIALS RESEARCH (DURNTEN-ZURICH, SWITZERLAND), SCITEC PUBLICATIONS, vol. 239-242, 12 May 2011 (2011-05-12), pages 2327 - 2330, XP009549743, ISSN: 1662-8985, DOI: 10.4028/www.scientific.net/AMR.239-242.2327
HUI ZHANG: "A facile approach to α-FeOOH nanorods with high aspect ratios", ADVANCED MATERIALS RESEARCH (DURNTEN-ZURICH, SWITZERLAND), SCITEC PUBLICATIONS, vol. 239-242, 12 May 2011 (2011-05-12), pages 2327 - 2330, XP009549743, ISSN: 1662-8985, DOI: 10.4028/www.scientific.net/AMR.239-242.2327
Attorney, Agent or Firm:
HANGZHOU FENGHE PATENT ATTORNEYS OFFICE CO., LTD (CN)
Download PDF: