SYNTHETIC POLYISOPRENE FOLEY CATHETER
Document Type and Number:
WIPO Patent Application WO/2009/088851
Kind Code:
A1
Abstract:
An indwelling urinary drainage catheter (12, 110) includes synthetic polyisoprene rubber (SPIR). Advantageously, the SPIR catheter can meet the tensile and resiliency requirements of Foley applications while avoiding the risk of allergic reactions in sensitive patients. The SPIR comprises an accelerator system that uses a carbamate as the only accelerator, a guanidine as the only accelerator, a combination of guanidine and carbamate accelerators, a combination of carbamate and thiazole acccelerators, or a combination of guanidine, carbamate and thiazole accelerators.

Inventors:
LAWSON KENNETH GLENN (US)
CHEN FUNG BOR (US)
CAPSTICK IAN (US)
TUCK RANDY (US)
Application Number:
PCT/US2008/088526
Publication Date:
July 16, 2009
Filing Date:
December 30, 2008
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
BARD INC C R (US)
LAWSON KENNETH GLENN (US)
CHEN FUNG BOR (US)
CAPSTICK IAN (US)
TUCK RANDY (US)
International Classes:
C08F36/08
Domestic Patent References:
WO2001072158A12001-10-04
Foreign References:
US20020173563A12002-11-21
US20050065249A12005-03-24
Attorney, Agent or Firm:
ALTMAN, Daniel, E. (Martens Olson & Bear, LLP,2040 Main Street, 14th Floo, Irvine CA, US)
Download PDF:
Claims:
WHAT IS CLAIMED IS:

1. A composition comprising synthetic polyisoprene latex and an accelerator system comprising a guanidine, wherein a polyisoprene film formed from heating and curing the composition has a tensile strength of about 3,000 psi to about 5,000 psi.

2. The composition of claim 1 wherein the guanidine is the only accelerator.

3. The composition of claim 1 wherein the guanidine is diphenylguanidine.

4. The composition of claim 3 wherein the amount of diphenylguanidine is between about 0.1 phr and 2 phr.

5. The composition of claim 3 wherein the amount of diphenylguanidine is about 0.5 phr.

6. A composition comprising synthetic polyisoprene latex and an accelerator system comprising a carbamate, wherein a polyisoprene film formed from heating and curing the composition has a tensile strength of about 3,000 psi to about 5,000 psi.

7. The composition of claim 6 wherein the carbamate is sodium dibutyl dithiocarbamate.

8. The composition of claim 7 wherein the amount of sodium dibutyl dithiocarbamate is between about 0.01 phr and 2 phr.

9. The composition of claim 7 wherein the amount of sodium dibutyl dithiocarbamate is about 0.1 phr.

10. The composition of claim 6 wherein the carbamate is the only accelerator.

11. A method for curing synthetic polyisoprene latex comprising the steps of: forming a film from a composition comprising synthetic polyisoprene latex and an accelerator system having a guanidine and a carbamate as the accelerators; and heating the film at a temperature of about 50° C to about 140° C for about 30 to 240 minutes wherein the synthetic polyisoprene latex cured film has a tensile strength of about 3,000 psi to about 5,000 psi.

12. The method of claim 11, wherein the guanidine is diphenylguanidine.

13. The method of claim 12 wherein the amount of diphenylguanidine is between about 0.1 phr and 2 phr

14. The method of claim 11, wherein the carbamate is sodium dibutyl dithiocarbamate.

15. The method of claim 14 wherein the amount of sodium dibutyl dithiocarbamate is between about 0.01 phr and 2 phr

16. A method for curing synthetic polyisoprene latex comprising the steps of: forming a film from a composition comprising synthetic polyisoprene latex and an accelerator system having a carbamate and a thiazole as the accelerators; and heating the film at a temperature of about 50° C to about 140° C for about 30 to 240 minutes wherein the synthetic polyisoprene latex cured film has a tensile strength of about 3,000 psi to about 5,000 psi.

17. The method of claim 16, wherein the thiazole is zinc mercaptobenzothiazole.

18. The method of claim 17 wherein the amount of zinc mercaptobenzothiazole is between about 0.1 phr and 2 phr

19. The method of claim 16, wherein the carbamate is zinc diethyldithiocarbamate.

20. The method of claim 19 wherein the amount of zinc diethyldithiocarbamate between about 0.05 phr and 2 phr

21. A method for curing synthetic polyisoprene latex comprising the steps of: forming a film from a composition comprising synthetic polyisoprene latex and an accelerator system having a carbamate, a thiazole and a guanidine as the accelerators; and heating the film at a temperature of about 50° C to about 140° C for about 30 to 240 minutes, wherein the synthetic polyisoprene latex cured film has a tensile strength of about 3,000 psi to about 5,000 psi.

22. The method of claim 21, wherein the thiazole is zinc mercaptobenzothiazole.

23. The method of claim 22 wherein the amount of zinc mercaptobenzothiazole is between about 0.1 phr and 2 phr

24. The method of claim 21, wherein the carbamate is sodium dibutyl dithiocarbamate.

25. The method of claim 24 wherein the amount of sodium dibutyl dithiocarbamate between about 0.05 phr and 2 phr.

26. The method of claim 21, wherein the guanidine is diphenylguanidine.

27. The method of claim 26, wherein the amount of diphenylguanidine is between about 0.05 phr and 2 phr

28. An indwelling urinary drainage catheter formed by the process of any one of claims 1, 6, 11, 16, and 21.

29. The catheter of claim 28 further comprising a finish layer, a build up layer, and an inner layer, wherein Young's Modulus of the finish layer is lower than the Young's Modulus of at least one of the middle layer and of the inner layer.

Description:

CRBARD.009VPC PATENT

SYNTHETIC POLYISOPRENE FOLEY CATHETER

RELATED APPLICATION

This application claims the benefit of U.S. Provisional Application No. 61/019,213, filed January 4, 2008, the disclosure of which is hereby incorporated by reference in its entirety.

BACKGROUND OF THE INVENTION Field of the Invention

This application relates to indwelling urinary drainage catheters, and relates more specifically to indwelling urinary drainage catheters comprising a hypoallergenic or non- allergenic, synthetic polyisoprene based formulation. Description of the Related Art

Balloon catheters are well known medical devices in which an inflatable member is located adjacent to the distal end medical devices of the catheter shaft and inflated once the catheter is positioned within the body of the patient to anchor the distal end. Such catheters comprise an elongated shaft defining a drainage lumen and an inflation lumen. The drainage lumen comprises a major portion of the cross-section of the catheter shaft and is closed at its distal end by a tip portion. Openings or ports distal to the balloon permit fluid to enter the drainage lumen. The proximal end of the drainage lumen is placed in fluid communication with a method of drainage such as a urinary drainage bag. In some embodiments, the communication is made through a drainage funnel located at the proximal end of the catheter through which the drainage lumen opens.

The inflation lumen is formed within the wall of the catheter shaft and extends from a location inside of the balloon, along the catheter shaft, and through an opening, typically a branch adjacent the proximal end of the shaft. An inflation valve at the end of the branch or other opening permits fluid to be infused into the inflation lumen.

For urinary catheters such as Foley catheters, the catheter is introduced into the patient and is advanced into the urethra until the distal end of the catheter, including the balloon, resides within the bladder. The balloon is then inflated, typically by coupling a syringe to the inflation valve and actuating it to discharge fluid from the syringe, through the inflation lumen, and into the balloon. Foley catheters are typically manufactured from

natural rubber latex, or, in some cases, silicone. Natural rubber latex contains proteins that can cause severe allergic reactions in some individuals. Silicone Foley catheters are sometimes used to avoid allergic reactions in such cases.

SUMMARY OF THE INVENTION

An aspect of the invention is directed to a composition comprising synthetic polyisoprene latex and an accelerator system comprising a guanidine. A polyisoprene film formed from heating and curing the composition has a tensile strength of about 3,000 psi to about 5,000 psi.

Another aspect is directed to a composition comprising synthetic polyisoprene latex and an accelerator system comprising a carbamate. A polyisoprene film formed from heating and curing the composition has a tensile strength of about 3,000 psi to about 5,000 psi.

Another aspect is directed to a method for curing synthetic polyisoprene latex that includes forming a film from a composition comprising synthetic polyisoprene latex and an accelerator system having a guanidine and a carbamate as the accelerators. The method further includes heating the film at a temperature of about 50° C to about 140° C for about 30 to 240 minutes. The synthetic polyisoprene latex cured film has a tensile strength of about 3,000 psi to about 5,000 psi.

Another aspect is directed to a method for curing synthetic polyisoprene latex that includes forming a film from a composition comprising synthetic polyisoprene latex and an accelerator system having a carbamate and a thiazole as the accelerators. The method further includes heating the film at a temperature of about 50° C to about 140° C for about 30 to 240 minutes. The synthetic polyisoprene latex cured film has a tensile strength of about 3,000 psi to about 5,000 psi.

Another aspect is directed to a method for curing synthetic polyisoprene latex that includes forming a film from a composition comprising synthetic polyisoprene latex and an accelerator system having a carbamate, a thiazole and a guanidine as the accelerators. The method further includes heating the film at a temperature of about 50° C to about 140° C for about 30 to 240 minutes. The synthetic polyisoprene latex cured film has a tensile strength of about 3,000 psi to about 5,000 psi.

Another aspect is directed to an indwelling urinary drainage catheter formed by the processes disclosed herein.

BRIEF DESCRIPTION OF THE DRAWINGS

These and other features, aspects and advantages of the present invention will now be described in connection with preferred embodiments of the invention, in reference to the accompanying drawings. The illustrated embodiments, however, are merely examples and are not intended to limit the invention. The following are brief descriptions of the drawings.

FIG. 1 is a perspective view of a Foley catheter according to a preferred embodiment of the present invention in an uninflated state.

FIG. 2 is a plan view of a Foley catheter similar to the catheter from Figure 1 with a balloon portion of the catheter in an inflated state.

FIG. 3 is a side view of a balloon catheter according to an embodiment of the present invention.

FIG. 4 is a cross-sectional view taken along line 4-4 of FIG. 3.

FIG. 5 is a cross-sectional view taken along line 5-5 of FIG. 3 with an expanded finish layer omitted for clarity.

FIG. 6 is an enlarged view of an upper portion of FIG. 5 designated by view 6.

FIG. 7 is a block diagram describing an exemplary process for manufacturing a Foley catheter, according to a preferred embodiment of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The following detailed description is now directed to certain specific embodiments of the invention. In this description, reference is made to the drawings wherein like parts are designated with like numerals throughout the description and the drawings.

Indwelling urinary drainage catheters, or Foley catheters, typically include a soft, thin rubber tube (or body) with a balloon on one end. The catheter is threaded through the urinary duct (urethra) and into the bladder to drain urine from the bladder. A Foley catheter is typically used when normal urination is disrupted by an infection, a swollen prostate gland, bladder stones, or, sometimes, an injury, hi very sick people, a catheter may be used to keep track of urine production.

A typical Foley catheter has a drainage lumen and an inflation lumen for inflating and deflating the balloon. The balloon is normally deflated until properly positioned in a

patient's bladder. Once the catheter is properly positioned, the inflation lumen delivers fluid to inflate the balloon. The inflated balloon holds the catheter in place.

Indwelling catheters are predominantly manufactured from natural rubber latex. Silicone catheters are sometimes used to prevent severe (e.g., Type I) allergic reactions caused by the proteins contained in natural rubber latex. Silicone catheters, however, require costly tooling and a complex manufacturing process, hi addition, they do not have the same feel, physical properties and versatile processing ability as natural rubber latex. For example, silicone does not have the same elastic properties as natural or synthetic polyisoprene rubber, hi addition, the balloon made with silicone rubber does not recover as well as polyisoprene after deflation and can cause discomfort and injury to patients. Furthermore, the stiffness of the silicone catheters required for insertion can increase discomfort to the contact tissues after insertion.

After manufactured, some catheters are dipped in a coating solution so as to be slippery for insertion into the human body. However, conventional coating materials are often not entirely retained on the device surface and can leach out during use, risking toxicity to the patient and decreasing lubricity while in use.

Synthetic polyisoprene latex is a man-made polymer that does not contain natural rubber latex or any other proteins (i.e., allergens), hi embodiments of the invention, synthetic polyisoprene can provide a cost-effective substitute to silicone and a hypoallergenic or non-allergenic alternative to natural rubber latex in forming medical articles, such as indwelling urinary drainage catheters. According to various embodiments, synthetic polyisoprene catheters provide the feel and physical properties of natural rubber latex without the risk of natural rubber latex allergic reactions. Also in various embodiments, the recovery of the balloon after deflation is improved, as compared with silicone rubber catheters.

Conventional processes for making elastomeric articles from natural or synthetic latex typically involve preparing a latex dispersion or emulsion, dipping a former in the shape of the article to be manufactured into the latex and curing the latex while on the former, hi the curing step, cross-linking or vulcanization through sulfur groups occurs between the polymer units. Certain conventional dipping processes and machinery are applicable to the manufacturing of synthetic polyisoprene catheters. However, conventional compounding formulations and curing conditions used to process natural rubber latex articles are not adequate to produce synthetic polyisoprene articles having the

desired properties for certain medical applications, including use in indwelling urinary drainage catheters.

In embodiments of the invention, new compounding formulations and processes are provided to achieve the goal of curing synthetic polyisoprene latex to match the strength of natural rubber latex, while eliminating patient exposure to natural rubber latex protein. Also, in embodiments of the invention, desirable properties of certain elastomeric articles, such as indwelling urinary drainage catheters, can be advantageously influenced or controlled during the cross-linking and curing stages of the manufacturing process. These properties can include, for example, stiffness, tensile strength, and coefficient of friction.

In preferred embodiments of the invention, accelerator systems are provided, including accelerator systems for synthetic polyisoprene latex. The accelerator system is compounded with the synthetic polyisoprene latex and can include one or more accelerators. For example, the accelerator system can include a single accelerator. Exemplary single accelerators include guanidine and carbamate. The accelerator system can include a combination of two accelerators. Exemplary two-accelerator systems can include a combination of guanidine and carbamate or a combination of carbamate and thiazole. An exemplary three-accelerator system can include a combination of guanidine, carbamate and thiazole. The listed accelerator systems are used to produce synthetic polyisoprene having a tensile strength of greater than 3,000 psi to about 5,000 psi. Embodiments of the invention also include methods for curing synthetic polyisoprene latex.

Embodiments of the invention also provide an indwelling urinary drainage catheter having a multi-layered design to render different desired functionalities together. For example, a multilayered article can be produced that has adequate stiffness, along with a low friction coefficient, to enable easy insertion and soft touch in a body to enhance patient comfort. As another example, a first layer of an article can be hydrophobic to facilitate drainage of body fluid and minimize bacterial growth and body fluid residuals retained by the wall of the article. A second layer can be configured to stiffen the article for ease of insertion, and/or can be configured to soften at body temperature so as to reduce pressure on the patient contact tissues. A third layer can comprise tissue repairing nutrients and/or a super absorbent material to reduce drag and

friction force for ease in inserting and removal of the article, so as to reduce pain associated with the article during insertion.

In some embodiments, one or more layers of an indwelling urinary drainage catheter can be configured to have a 500% modulus higher than about 500 psi for easy insertion. In some embodiments, synthetic polyisoprene latex is blended with other synthetic polymers or pigments to obtain a 500% modulus up to 500 psi. For example, the synthetic polyisoprene latex may be blended with polyurethane (PU), clay, and/or a polymer filler to achieve the desired material properties. For example, increasing the amount of PU in a given layer generally increases the 500% modulus for that layer.

In an embodiment of an inner or rubberized layer, the synthetic polyisoprene latex is blended with 0-15 phr clay and 0-5 phr polymer filler. In another embodiment of the inner or rubberized layer, the synthetic polyisoprene latex is blended with 0-3 phr PU. In an embodiment of a build up layer, the synthetic polyisoprene latex is blended with 0-15 phr clay, 0-5 phr polymer filler, and 0-3 phr PU. In an embodiment of a finish layer, the synthetic polyisoprene latex is not blended with clay, polymer filler, or PU. With or without blending with other synthetic polymers, the compounded synthetic polyisoprene latex includes the accelerator system described above.

In some embodiments, a finish or outer layer of the catheter is dipped in a slippery, super absorbent material to reduce its coefficient of friction (in a wet condition) to below 0.1 and thereby facilitate easy insertion and removal of the catheter from a patient. In some embodiments, the catheter can be configured to soften within minutes after insertion into the body, to improve patient comfort and reduce the risk of trauma.

Certain preferred embodiments of the invention provide an indwelling urinary drainage catheter having a multi-layer design, with different functional layers bonded together. The references to materials herein as being "bonded" to one another refers to such materials being attached to each other by any means, including but not limited to bonds, attractions, or crosslinks formed between the materials themselves as well as binders or adhesives used to form bonds, attractions, or crosslinks to each material. By such a configuration, the risk of chemicals leaching out can be reduced or minimized.

FIG. 1 is a perspective view of a Foley catheter according to a preferred embodiment of the present invention in an uninflated state. The catheter includes a catheter body 12 with a proximal end 14 and a distal end (or tip) 16. The catheter also includes a balloon 18, an inflation lumen 20, and a drainage lumen 22. The balloon 18 is

deflated for insertion into a patient. The balloon 18 is disposed near the distal end 16. The inflation lumen 20 extends within the catheter body 12 from the proximal end 14 to the balloon 18, in fluid communication with the balloon 18, for inflating and deflating the balloon 18. FIG. 2 shows another Foley catheter with an inflated balloon.

The catheter drainage lumen 22 extends from the proximal end 14 to the distal end 16. The distal end 16 includes an opening 26 in fluid communication with the drainage lumen 22 to facilitate drainage of urine from the bladder of a patient.

The Foley catheter illustrated in FIG. 1 comprises synthetic polyisoprene rubber (SPIR). Stereoregular polyisoprene can be synthesized using various catalyst systems to selectively join together monomer units in a well-ordered fashion. The resulting synthetic polyisoprene rubber (SPIR) tends to exceed natural latex rubber in product consistency, cure rate, and purity. SPIR also exhibits superior characteristics in mixing, extrusion, molding, and calendaring processes. SPIR can be manufactured to meet the particular tensile and resiliency requirements of Foley applications, while avoiding the risk of allergic reaction in sensitive patients.

Part or all of the Foley catheter can comprise SPIR. For example, the body 12, the inflation lumen 20, the drainage lumen 22, the balloon 18, and/or the catheter tip 16 can comprise SPIR. These parts can be formed by extrusion and/or by molding processes, such as injection molding. The SPIR can comprise cis-l,4-polyisoprene, trans- 1,4- polyisoprene, or can have a primarily 1,2 or 3,4 structure. The SPIR can also be crosslinked or otherwise treated to produce the desired characteristics for Foley applications.

Referring now to FIG. 3, a catheter 110 comprises an elongated catheter shaft 112. A balloon 114 is located adjacent the forward tip 116 of the catheter shaft 112. A drainage lumen 118 extends longitudinally within the catheter shaft 112 and terminates just short of the tip 116. The drainage lumen 118 is in communication with the ambient surrounding the tip 116 by way of a plurality of radial drainage eyes 120.

FIG. 4 is a cross-sectional view of the catheter shaft 112 as seen along line 4-4 of FIG. 3. Embodiments of the catheter shaft 112 are formed from two or more distinct layers. The catheter shaft 112 illustrated in FIG 3 is formed from three distinct layers: an innermost or rubberize layer 130, an intermediate or build up layer 132, and an outermost or finish layer 134. In an exemplary two layer embodiment, the finish layer is omitted.

Formed within the build up layer 132 and having its lower edge in contact with the rubberize layer 130 is an inflation lumen 140.

FIG. 5 is a cross-sectional view of the catheter shaft 112 as seen along line 5-5 of FIG. 3. Not seen in FIG. 5, the finish layer 134 is expanded away from the build up layer 132 as the balloon 114 is inflated, leaving only the rubberize layer 130 and build up layer 132 visible. FIG. 6 is an enlarged view of an upper portion from FIG. 5 designated by view 6 and shows the inflation lumen 140 and an inflation eye 144. The inflation eye 144 may be arranged in a radial direction. The inflation eye 144 places the inflation lumen in communication with the space between the build up layer 132 and the balloon 114.

The relative stiffnesses of the various layers 130, 132, and 134 of the balloon catheter 110, as expressed by their Young's moduli, can be controlled. The catheters of the present invention can include an inner rubberize layer 130 of material having a Young's Modulus that is higher than the Young's Modulus of the middle layer 132. In some embodiments having both a middle layer 132 and an outer layer 134, the Young's Modulus of the inner layer can be higher than that of both the middle layer 132 and the outer layer 134. As used herein, Young's Modulus refers to the Modulus of Elasticity when determined according to standard procedures such as American Society for Testing and Materials (ASTM) Method E-Il 1-82 using sample preparation procedures set forth in ASTM Method D-412-98a. As used herein, "wet" Young's Modulus shall refer to Young's Modulus measured after immersion of a material in deionized water at a temperature of 60-85° F for a period of 4-5 days. As used herein, "dry" Young's Modulus shall refer to Young's Modulus of a material that has not been immersed.

In some embodiments, a coagulant dipping process is used to produce elastomeric articles from synthetic polyisoprene. An article-shaped mold is first dipped into a coagulant solution which is known to destabilize the latex. The coagulant dipped mold is then dried and dipped in compounded synthetic polyisoprene. Other synthetic materials such as calcium stearate, magnesium stearate, zinc stearate, polyethylene, polybutadiene emulsion, styrene-isoprene-styrene block copolymer emulsion, polyacrylate, polyurethane, polychloroprene, styrene/butadiene copolymer, nitrile latex and the like can be successfully blended as part of the compounded synthetic polyisoprene latex. The coagulant dip and the polyisoprene latex dip can be dipped multiple times to build up appropriate thickness required for serving different functionalities of elastomeric articles (or layers thereof). The coagulated wet gel on the mold is submersed in water to leach out

the residual compounding ingredients and the coagulant. After the leaching process the wet gel on the mold can be placed in an oven at a temperature range from, for example, 50° to 140° C. After staying in the oven for a specific time, the mold is removed and cooled down. Finally, the articles are stripped from the mold. hi one embodiment, an elongated rod or "form" is dipped into a first liquid coating material to form a layer of coating material on the form. The form has the shape and dimensions of the drainage lumen 118 of the catheter. This first coating layer forms the inner or rubberize layer 130 of the catheter. Once the first layer 130 has dried, an elongated wire is attached longitudinally to the outside of the first layer 130. The form with first layer 130 and wire is then dipped into a second coating material to build up an intermediate or build up layer 132. Multiple dips into the second coating material may be necessary to build up an intermediate layer 132 of appropriate thickness. The inflation eye 144 is then formed near the distal end of the second layer 132 to place the inflation lumen 140 in communication with the ambient surrounding the second layer 132. The build up layer 132 is then dried. The finish layer 134 is applied with a subsequent dip and is dried.

The balloon 114 can be formed in a number of ways, and any method for forming the balloon may be used. In some preferred embodiments, the balloon is formed by the application of a pre- formed balloon component on the second layer 132. hi one of these embodiments, a finish layer 134 is used and is applied over the pre-formed balloon component and thus forms part of the wall of the balloon 114. hi another of these embodiments, no finish layer 134 is used and the pre-formed balloon component forms the entire wall of the balloon 114. hi other embodiments, a masking material is applied to the exterior of the second layer 132 in the balloon formation area such that a bond does not form between the build up layer 132 and the finish layer 134 in the area surrounding the inflation eye 144 of the inflation lumen 140. hi such latter embodiments, the unadhered portion of the finish layer 134 becomes the inflatable balloon 114.

Regardless of the method used to form the balloon 114, the form with first and second layers 130, 132 and the balloon formation is then dipped into a third coating solution to build up the outer or finish layer 134. Once the outer layer 134 has been dried, the catheter 110 is removed from the form. The space formerly occupied by the form and the inflation wire become the drainage and inflation lumens 118 and 140, respectively. Drainage eyes 120 are then formed in the catheter shaft 112 adjacent its distal end 116 to

place the drainage lumen 118 in communication with the ambient surrounding the forward end of the shaft 112. The balloon 114 is inflated by infusing an inflation medium out the inflation eye 144 of the inflation lumen 140 and into the balloon 114.

To introduce an uninflated balloon catheter 110 into a patient, a stylet may be inserted into the proximal end opening of the drainage lumen (for example, the opening of a drainage funnel) of the catheter and advanced until the forward end of the stylet bears against the inside of the forward tip 116 of the catheter. The catheter 110 with the stylet affixed is then advanced through the urethra and into the neck of the bladder. Because all of the force drawing the catheter 110 along into place is being exerted against a single point in the tip 116 of the catheter 110, it has typically been necessary to embed a fabric reinforcement cap within the wall of the catheter tip 116 to spread out the forces exerted by the stylet over a greater area of the catheter tip 116. In some embodiments, the innermost layer 130 of the catheter 110 is stiffened so that it is able to withstand the forces exerted upon it by the stylet tip without the need for reinforcement, thereby eliminating the need for the embedded fabric and thus substantially simplifying construction.

FIG. 7 is a block diagram describing an exemplary process for manufacturing a Foley catheter, according to a preferred embodiment of the present invention. The process begins with a mold being dipped in a coagulant 200. One example of a suitable coagulant is a solution comprising, for example, 40 gram of calcium nitrate, 8 grams of calcium carbonate and 52 grams of water. Next at block 202, the dipped mold is air dried.

Exemplary compounds of synthetic latex for use in block 204, including an accelerator system, are set forth below. To prepare the synthetic latex for use in block 204, the compound is heated to specific temperature for a specified time. Exemplary cook profiles include, from 1 to 4 hours at IOOF with a 4.75 hour cool down. Another exemplary profile includes 1 hr at IOOF. Another exemplary profile includes 1-2 hours at 9OF.

The mold is dwelled in the compounded polyisoprene latex for, for example, 1 - 7 minutes, preferably 2-5 minutes at block 204. Blocks 200, 202, and 204 may be repeated as needed depending on desired geometry and properties of the medical article or layer.

Next, at block 206, the gel film can be leached in water for, for example, 10 minutes. The mold is then dried in one or more steps. For example, the mold may be dried in an air-circulated oven for 30 minutes at 55° C at block 208 and then dried in an

air-circulated oven for 45 minutes at 85° C at block 210. At block 212, the dried mold is removed from the oven and cooled. After cooling, the medical article is striped from the mold at block 214.

The following examples set forth different compounds of synthetic latex which can be compounded for use in block 204 of FIG. 7. Each compound of synthetic latex includes an accelerator system. The accelerator system compositions listed below are exemplary and should not be construed as limiting the claims to the embodiments depicted therein. Further, different accelerator systems may be used for different layers of a multi-layer medical article.

Example 1

Synthetic polyisoprene latex was prepared with the compounding ingredients listed below in Table 1 and then evaluated. The components are reported by weight as parts per hundred. Diphenyl guanidine was the only accelerator used in the range of 0.1 to 2 phr, preferably 0.2 to 1.0 phr.

The typical curing conditions were 30 minutes at 55° C and then 45 minutes at 85° C. The physical properties were evaluated using an Instron 5564 and measured according to ASTM D-412. The products prepared in this manner exhibited physical properties as follows: 3541 psi for tensile strength, 1075% elongation at break and 237 psi for 500% modulus. This example illustrates that articles prepared with only a guanidine accelerator can exhibit tensile strength greater than 3000 psi.

Example 2

Synthetic polyisoprene latex was prepared with the compounding ingredients listed below in Table 2 and then evaluated. A combination of diphenyl guanidine (DPG) and sodium dibutyl dithiocarbamate (SBC) accelerators was used. DPG ranged from about 0.1 to 2 phr, preferably 0.2 to 1 phr. SBC ranged from about 0.01 to 2 phr, preferably 0.025 to 1.0 phr. The typical curing conditions were 30 minutes at 55° C and then 45 minutes at 85° C. The products prepared in this manner exhibited physical properties as follows: tensile strength of 3356 psi, 983% elongation at break, and 500% modulus of 337 psi. This example illustrates that articles prepared with guanidine and carbamate accelerators can exhibit tensile strength greater than 3000 psi.

Example 3

Synthetic polyisoprene latex was prepared with the compounding ingredients listed below in Table 3 and then evaluated. Sodium dibutyl dithiocarbamate was the only accelerator used in the range of 0.01 to 2 phr, preferably 0.025 to 0.5 phr. The typical curing conditions were 30 minutes at 55° C and then 45 minutes at 105° C. The products prepared in this manner exhibited physical properties as follows: tensile strength of 3898 psi, 960% elongation at break, and 500% modulus of 328 psi. This example illustrates that articles prepared with only a carbamate accelerator can exhibit tensile strength greater than 3000 psi.

Example 4

Synthetic polyisoprene latex was prepared with the compounding ingredients listed below in Table 4 and then evaluated. About 0.1 to 2 phr of zinc mercaptobenzothiazole (ZMBT) and about 0.05 to 2 phr of zinc diethyl dithiocarbamate (ZEC) are the accelerators used. The preferable range for ZMBT is 0.25 to 1.5 phr and for ZEC 0.05 to 1 phr. The typical curing conditions were 30 minutes at 120° C. The products prepared in this manner exhibited physical properties as follows: tensile strength of 3266 psi, 1098% elongation at break, and 500% modulus of 288 psi. This example illustrates that articles prepared with a combination of thiazole and carbamate accelerators can exhibit tensile strength greater than 3000 psi.

Example 5

Synthetic polyisoprene latex was prepared with the compounding ingredients listed below in Table 5 and then evaluated. About 0.1 to 2 phr of zinc mercaptobenzothiazole (ZMBT), about 0.05 to 2 phr of diphenylguanidine (DPG), and

about 0.05 to 2 phr of sodium dibutyl dithiocarbamate (SBC) are the accelerators used. The typical curing conditions were 45 minutes at 115° C. The products prepared in this manner exhibited physical properties as follows: tensile strength of 3161 psi, 863% elongation at break, and 500% modulus of 387 psi. This example illustrates that articles prepared with a combination of thiaole, carbamate and guanidine accelerators can exhibit tensile strength greater than 3000 psi.

The various embodiments of SPIR Foley catheters described above thus provide a number of advantages over known Foley catheters. Of course, it is to be understood that not necessarily all such objectives or advantages may be achieved in accordance with any particular embodiment of the SPIR Foley catheter described herein. Thus, for example, those skilled in the art will recognize that the SPIR Foley catheter may be developed in a manner that achieves or optimizes one advantage or group of advantages as taught herein without necessarily achieving other objectives or advantages as may be taught or suggested herein.

It is contemplated that various aspects and features of the invention described can be practiced separately, combined together, or substituted for one another, and that a variety of combination and subcombinations of the features and aspects can be made and still fall within the scope of the invention. Thus, it is intended that the scope of the present invention herein disclosed should not be limited by the particular disclosed embodiments described above, but should be determined only by a fair reading of the claims.