Title:
THERMALLY CURED UNDERCOAT FOR LITHOGRAPHIC APPLICATION
Document Type and Number:
WIPO Patent Application WO/2005/089150
Kind Code:
A2
Abstract:
Thermally curable undercoat composition comprising for producing a bilayer relief image comprising a) a polymer of Structure (I) comprising repeating units of Structure (II), (III), and (IV) wherein each R1 is independently a hydrogen atom or an alkyl group having from 1 to 3 carbon atoms or a halogen atom; L represents a single bond, a -COO- group, or a -CON(R2)- group; R2 represents a hydrogen atom or an alkyl group having from 1 to 3 carbon atoms; M represents a C5-7 cycloalkylene group or an arylene group having from 6 to 18 carbon atoms; W represents a single bond, a -COO- group, -0-, -(C=O)-, or -(SO2)-; R3 represents a hydrogen atom or a linear unsubstituted or substituted alkyl having from 5 to 30 carbon atoms or an unsubstituted or substituted cycloalkyl group having from 5 to 30 carbon atoms, a bridged unsubstituted or substituted alicyclic hydrocarbon group having from 5 to 25 carbon atoms or an unsubstituted or substituted aryl group having from 6 to 18 carbon atoms or an arylalkyl group having from 7 to 18 carbon atoms; n is an integer from 1 to 3, q is an integer from 0 to 3, the sum of n and q being no greater than 5; R4 is a linear or branched or cyclic C1 - C10 alkyl or a halogen group; R5 is an alkyl or branched alkyl or cyclic alkyl or an unsubstituted or substituted alicyclic group, having 5 to 30 carbon atoms or (R60)tR7 group where R6 is a C1-10 linear or branched alkylene group and R7 is linear, branched or cyclic alkyl or an unsubstituted or substituted alicyclic group or an unsubstituted or substituted a romatic or a Ikyl a romatic group having 1 to 30 carbon atoms and t is an integer about 1 to 4; b) a phenolic crosslinker; c) a thermal acid generator (TAG); and d) a solvent.

Inventors:
DE BINOD B
MALIK SANJAY
KOCAB THOMAS J
SARUBBI THOMAS
Application Number:
PCT/US2005/007588
Publication Date:
September 29, 2005
Filing Date:
March 09, 2005
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
FUJIFILM ELECTRONIC MATERIALS
International Classes:
G03C1/492; G03F7/09
Domestic Patent References:
WO2002073307A22002-09-19
Foreign References:
US20030204035A12003-10-30
EP0987600A12000-03-22
Other References:
See also references of EP 1743363A4
Attorney, Agent or Firm:
Greeley, Paul D. (Greeley Ruggiero & Perle LLP, One Landmark Square, 10th Floo, Stamford CT, US)
Download PDF:
Claims:
We claim:
1. A thermally curable undercoat composition comprising a) a polymer of Structure I comprising repeating units of Structure II, III, and IV M W RJ (D (II) (III) (IV) wherein each R1 is independently selected from the group consisting of a hydrogen atom, an alky! group having from 1 to 3 carbon atoms, and a halogen atom; L is selected from the group consisting of a single bond, a COO group, and a CON(R2) group; R2 is selected from the group consisting of a hydrogen atom and an alkyl group having from 1 to 3 carbon atoms; M is selected from the group consisting of a C57 cycloalkylene group and an arylene group having from 6 to 18 carbon atoms; W is selected from the group consisting of a single bond, a COO group, O, (C=O), and (SO2); R3 is selected from the group consisting of a hydrogen atom, a linear unsubstituted or substituted alkyl having from 5 to 30 carbon atoms, an unsubstituted or substituted cycloalkyl group having from 5 to 30 carbon atoms, a bridged unsubstituted or substituted aiicyclic hydrocarbon group having from 5 to 25 carbon atoms, an unsubstituted or substituted aryl group having from 6 to 18 carbon atoms and an arylalkyl group having from 7 to 18 carbon atoms; n is an integer from 1 to 3, q is an integer from 0 to 3, the sum of n and q being no greater than 5; R4 is selected from the group consisting of a linear or branched or cyclic Ci C10 alkyl and a halogen group; R5 is selected from the group consisting of a linear, branched or cyclic alkyl and an unsubstituted or substituted alicyclic group, having 5 to 30 carbon atoms, and a (R6O)tR7 group where R6 is a C∏o linear or branched alkylene group and R7 is selected from the group consisting of a linear, branched or cyclic alkyl, an unsubstituted or substituted alicyclic group and an unsubstituted or substituted aromatic or alkyl aromatic group having 1 to 30 carbon atoms and t is an integer from 1 to 4; b) a phenolic crosslinker having Structure V R 110ϋ\\ R (V) wherein p is an integer of about.
2. to 6; R8 is a CH2OR1.
3. group; R9 is selected from the group consisting of a hydrogen atom, CH2OR1.
4. group, C1C5 alkyl group, and aryl; R10, R11 and R1.
5. are each independently selected from the group consisting of a hydrogen atom, and a C1C5 alkyl group; X is a di tri, tetra, penta or hexa valent alkyl or arylalkyl moiety; c) a thermal acid generator (TAG) of Structure Vl (SO3H)X R20L I B wherein A is selected from the group consisting of a phenyl and a naphthyl group, R20 is selected from the group consisting of an alkyl or a cyclic alkyl and an unsubstituted or substituted alicyclic group having 5 to 30 carbon atoms; when A is phenyl, x is an integer of from 1 to 3, y is an integer of from 0 to 5, the sum of x and y being no greater than 6, and z is 6xy; when A is naphthyl, x is an integer from 1 to 3, y is an integer from 0 to 7, the sum of x and y being no greater than 8, and z is 8 xy; B is a primary, secondary, or tertiary unsubstituted or substituted alkyl or carbocyclic or heterocyclic amine having 4 to 30 carbon atoms; and d) a solvent.
6. 2 A thermally curable undercoat composition according to claim 1 wherein the polymer of structure I is a polymer of Structure VlI R 23 R' R (VII) wherein R1 is selected from the group consisting of a hydrogen atom, an alkyl group having from 1 to 3 carbon atoms and a h alogen atom; R21 i s an unsubstituted or substituted aromatic group having C6C3o carbon atoms; R22 is selected from the group consisting of a hydrogen a nd a C iC4 alkyl g roup, R23 i s selected f rom the group consisting of cyclic alkyl, an unsubstituted or substituted alicyclic group having 5 to 30 carbon atoms, and (R30O)tR7 group where R30 is a C24 linear or branched alkylene group and R7 is selected from the group consisting of linear, branched or cyclic alkyl, an unsubstituted or substituted alicyclic group, an unsubstituted or substituted aromatic or alkyl aromatic group having 1 to 30 carbon atoms; n is an integer of about 1 to 2 and t is an integer about 1 to 4.
7. A thermally curable undercoat composition according to claim 1 wherein the polymer of Structure I is a polymer of Structure VIII CK ^O R26 XOH)n (VIII) wherein R24 is selected from the group consisting of a hydrogen atom and a methyl group; R25 is an unsubstituted or substituted aromatic group having C6C30 carbon atoms; R26 is selected from the group consisting a cyclic alky! or an unsubstituted or substituted alicyclic group having 5 to 30 carbon atoms and a (R30O)tR7 group where R30 is a C24 linear or branched alkylene group and R7 is selected from the group consisting a linear, branched or cyclic alkyl group , an unsubstituted or substituted alicyclic group, an unsubstituted or substituted aromatic or alkyl aromatic group having 1 to 30 carbon atoms and t is an integer of about 1 to 4; and n is an integer of about 1 to 2. 4.
8. A thermally curable undercoat composition according to claim 1 wherein the polymer of Structure I is a polymer of Structure IX R 28 R 27 OH)n (IX) wherein R1 is selected from the group consisting of a hydrogen atom, an alkyl group having from 1 to 3 carbon atoms, and a halogen atom; R22 is selected from the group consisting of a hydrogen atom, and a C1C4 alkyl group; R27 is selected from the group consisting of a hydrogen atom and a substituted or unsubstituted C5C7 cycloalkyl; R28 is selected from the group consisting of a cyclic alkyl, an unsubstituted or substituted alicyclic group having 5 to 30 carbon atoms and (R30O )tR7 group where R30 is a C24 linear or branched alkylene group and R7 is selected from the group consisting of a linear, branched or cyclic alkyl, an unsubstituted or substituted alicyclic group, and an unsubstituted or substituted aromatic or alkyl aromatic group having 1 to 30 carbon atoms and t is an integer of about 1 to 4, and n is an integer of about 1 to 3.
9. A thermally curable undercoat composition according to claim 1 wherein the polymer of Structure I is a polymer of Structure X R 28 S29 (X) wherein R24 is selected from the group consisting of a hydrogen atom and a methyl group; R28 is selected from the group consisting of a cyclic alkyl, an unsubstituted or substituted alicyclic group having 5 to 30 carbon atoms and (R30O)tRτ group where R30 is a C24 linear or branched alkylene group and R7 is selected from the group consisting of a linear, branched or cyclic alkyl, an unsubstituted or substituted alicyclic group, and an unsubstituted or substituted aromatic or alkyl aromatic group having 1 to 30 carbon atoms and t is an integer of about 1 to 4; R29 is a substituted or unsubstituted C5C7 cycloalkyl group; and n is an integer of about 1 to 2.
10. A thermally curable undercoat composition according to claim 1 wherein, in repeating unit of Structure II, R1 is selected from the group consisting of hydrogen and methyl; L is selected from the group consisting of a single bond and a COO group;. M is selected from the group consisting of a C5C7 cycloalkylene group and a C6C10 arylene group; and W is a single bond.
11. A thermally curable undercoat composition according to claim 1 wherein, in repeating unit of Structure II, R3 is selected from the group consisting of a hydrogen atom, cyclopentyl, cyclohexyl, adamantyl, bicycle[2.2.1]heptyl, tricycle[5.2.1.02i6]decyl, phenyl and naphthyl.
12. A thermally curable undercoat composition according to claim 1 wherein, in the repeating unit of Structure III, wherein R1 is selected from the group consisting of hydrogen and methyl; R4 is selected from the group consisting of a hydrogen atom, a halogen group and a C1C4 linear or branched alkyl group.
13. A thermally curable undercoat composition according to claim 1 wherein, in repeating unit of Structure II, R1 is selected from the group consisting of hydrogen and methyl; L is selected from the group consisting of a single bond and a COO group;. M is selected from the group consisting of a C5C7 cycloalkylene group and a CΘCIO arylene group; and W is a single bond, and R3 is selected from the group consisting of a hydrogen atom, cyclopentyl, cyclohexyl, adamantyl, bicycle[2.2.1]heptyl, tricycle[5.2.1.02l6]decyl, phenyl and naphthyl; in the repeating unit of Structure III, wherein R1 is selected from the group consisting of hydrogen and methyl; R4 is selected from the group consisting of a hydrogen atom, a halogen group and a C1C4 linear or branched alkyl group; and, in the repeating unit of Structure IV, wherein R1 is selected from the group consisting of hydrogen and methyl; R5 is selected from the group consisting of a cyclohexyl, bicycle[2.2.1]heptyl, adamantly, adamantylmethyl, tricycIe[5.2.1.02,6]decanemethyl, and ethoxydicyclopentenyl .
14. A polymer of Structure X R 28 (X) wherein R24 is selected from the group consisting of a hydrogen atom and a methyl group; R28 is selected from the group consisting of a cyclic alkyl, an unsubstituted or substituted alicyclic group having 5 to 30 carbon atoms and (R30O)tR7 group where R30 is a C24 linear or branched alkylene group and R7 is selected from the group consisting of a linear, branched or cyclic alkyl, an unsubstituted or substituted alicyclic group, and an unsubstituted or substituted aromatic or alkyl aromatic group having 1 to 30 carbon atoms and t is an integer of about 1 to 4; R29 is a substituted or unsubstituted C5C7 cycloalkyl group; and n is an integer of about 1 to 2.
15. A process for forming a pattern on a substrate comprising the following process steps: a. providing a substrate, b. coating in a first coating step said substrate with a thermally curable undercoat composition of claim 1 , c. curing said undercoat composition, d. coating in a second coating step a photoresist over the undercoat to produce a bilayer photoresist stack, e. exposing the bilayer photoresist stack to provide a photosensitive composition portion of the bilayer photoresist stack, f. developing the photosensitive composition portion of the bilayer photoresist stack making a portion of the underlying undercoat visible, g. rinsing the bilayer photoresist stack, and h. etching the visible undercoat in an oxidizing plasma to produce a bilayer relief image.
16. A process for forming a pattern on a substrate comprising the following process steps: a. providing a substrate, b. coating in a first coating step said substrate with a thermally curable undercoat composition of claim 2, c. curing said undercoat composition, d. coating in a second coating step a photoresist over the undercoat to produce a bilayer photoresist stack, e. exposing the bilayer photoresist stack to provide a photosensitive composition portion of the bilayer photoresist stack, f. developing the photosensitive composition portion of the bilayer photoresist stack making a portion of the underlying undercoat visible, g. rinsing the bilayer photoresist stack, and h. etching the visible undercoat in an oxidizing plasma to produce a bilayer relief image.
17. A process for forming a pattern on a substrate comprising the following process steps: a. providing a substrate, b. coating in a first coating step said substrate with a thermally curable undercoat composition of claim 3, c. curing said undercoat composition, d. coating in a second coating step a photoresist over the undercoat to produce a bilayer photoresist stack, e. exposing the bilayer photoresist stack to provide a photosensitive composition portion of the bilayer photoresist stack, f. developing the photosensitive composition portion of the bilayer photoresist stack making a portion of the underlying undercoat visible, g. rinsing the bilayer photoresist stack, and h. etching the visible undercoat in an oxidizing plasma to produce a bilayer relief image.
18. A process for forming a pattern on a substrate omprising the following process steps: a. providing a substrate, b. coating in a first coating step said substrate with a thermally curable undercoat composition of claim 4, c. curing said undercoat composition, d. coating in a second coating step a photoresist over the undercoat to produce a bilayer photoresist stack, e. exposing the bilayer photoresist stack to provide a photosensitive composition portion of the bilayer photoresist stack, f. developing the photosensitive composition portion of the bilayer photoresist stack making a portion of the underlying undercoat visible, g. rinsing the bilayer photoresist stack, and h. etching the visible undercoat in an oxidizing plasma to produce a bilayer relief image.
19. A process for forming a pattern on a substrate comprising the following process steps: a. providing a substrate, b. coating in a first coating step said substrate with a thermally curable undercoat composition of claim 5, c. curing said undercoat composition, d. coating in a second coating step a photoresist over the undercoat to produce a bilayer photoresist stack, e. exposing the bilayer photoresist stack to provide a photosensitive composition portion of the bilayer photoresist stack, f. developing the photosensitive composition portion of the bilayer photoresist stack making a portion of the underlying undercoat visible, g. rinsing the bilayer photoresist stack, and h. etching the visible undercoat in an oxidizing plasma to produce a bilayer relief image.
20. A process for forming a pattern on a substrate comprising the following process steps: a. providing a substrate, b. coating in a first coating step said substrate with a thermally curable undercoat composition of claim 6, c. curing said undercoat composition, d. coating in a second coating step a photoresist over the undercoat to produce a bilayer photoresist stack, e. exposing the bilayer photoresist stack to provide a photosensitive composition portion of the bilayer photoresist stack, f. developing the photosensitive composition portion of the bilayer photoresist stack making a portion of the underlying undercoat visible, g. rinsing the bilayer photoresist stack, and h. etching the visible undercoat in an oxidizing plasma to produce a bilayer relief image.
21. A process for forming a pattern on a substrate comprising the following process steps: a. providing a substrate, b. coating in a first coating step said substrate with a thermally curable undercoat composition of claim 7, c. curing said undercoat composition, d. coating in a second coating step a photoresist over the undercoat to produce a bilayer photoresist stack, e. exposing the bilayer photoresist stack to provide a photosensitive composition portion of the bilayer photoresist stack, f. developing the photosensitive composition portion of the bilayer photoresist stack making a portion of the underlying undercoat visible, g. rinsing the bilayer photoresist stack, and h. etching the visible undercoat in an oxidizing plasma to produce a bilayer relief image.
22. A process for forming a pattern on a substrate comprisingthe following process steps: a. providing a substrate, b. coating in a first coating step said substrate with a thermally curable undercoat composition of claim 8, c. curing said undercoat composition, d. coating in a second coating step a photoresist over the undercoat to produce a bilayer photoresist stack, e. exposing the bilayer photoresist stack to provide a photosensitive composition portion of the bilayer photoresist stack, f. developing the photosensitive composition portion of the bilayer photoresist stack making a portion of the underlying undercoat visible, g. rinsing the bilayer photoresist stack, and h. etching the visible undercoat in an oxidizing plasma to produce a bilayer relief image.
23. A process for forming a pattern on a substrate comprising the following process steps: a. providing a substrate, b. coating in a first coating step said substrate with a thermally curable undercoat composition of claim 9, c. curing said undercoat composition, d. coating in a second coating step a photoresist over the undercoat to produce a bilayer photoresist stack, e. exposing the bilayer photoresist stack to provide a photosensitive composition portion of the bilayer photoresist stack, f. developing the photosensitive composition portion of the bilayer photoresist stack making a portion of the underlying undercoat visible, g. rinsing the bilayer photoresist stack, and h. etching the visible undercoat in an oxidizing plasma to produce a bilayer relief image.
24. A bilayer relief image produced by the process of claim 11.
25. A coated substrate comprising a semiconductor substrate coated by the composition of claim 1 wherein the composition of claim 1 is further coated with a photoresist.
Description:
THERMALLY CURED UNDERCOAT FOR LITHOGRAPHIC APPLICATION

FIELD OF THE INVENTION

[0002] The present invention relates to deep UV lithography used in semiconductor manufacturing and more particularly to undercoat layers for chemically amplified bilayer resist systems.

BACKGROUND TO THE INVENTION

[0003] Integrated circuit production relies on the use of photolithographic processes to define the active elements and interconnecting structures on microelectronic devices. Until recently, g-line (436 nm) and 1-line (365 nm) wavelengths of light have been used for the bulk of microlithographic applications. However, in order to achieve smaller d imensions of resolution, the wavelength of light u sed for microlithography in semiconductor m anufacturing has been reduced into the deep UV regions of 254 nm and 193 nm. As the patterns and wavelengths become finer, the materials properties of the photoresists used for pattern delineation have become more and more demanding. In particular, requirements of sensitivity, transparency, aesthetics of the image produced, and the selectivity of the resists to etch conditions for pattern transfer become more and more strenuous. The problem with using deep UV wavelengths is that resists used at the higher wavelengths were too absorbent and insensitive. Because of this, the traditional lithographic materials, such as novolaks, diazonaphthoquinones, etc., are unsuitable platforms for ultra large-scale integration (ULSI) manufacture and beyond. Thus, in order to utilize deep UV light wavelengths, new resist materials with low optical absorption and enhanced sensitivities were needed along with additional lithographic techniques.

[0004] Advanced photoresists usually employ a technique called chemical amplification in which an acid generated by photolysis catalyzes a solubility switch from alkali insoluble to alkali soluble by removal of an acid sensitive group protecting an alkali-solubilizing moiety. The principle of chemical amplification as a basis for photoresist operation has been known for some years (see US Patent No. 4,491,628). Most chemically amplified resists have been designed around the use of acid sensitive carboxylic esters or acid sensitive hydroxystyrene derivatives.

[0005] However, chemically amplified resist systems have many shortcomings. One problem is standing wave effects, which occur when monochromatic is reflected off the surface of a reflective substrate during exposure. The formation of standing waves in the resist reduces resolution and causes linewidth variations. For example, standing waves in a positive resist have a tendency to result in a foot at the resist/substrate interface reducing the resolution of the resist

[0006] In addition, chemically amplified resist profiles and resolution may change due to substrate poisoning. Particularly, this effect occurs when the substrate has a nitride layer. It is believed that residual N-H bonds in the nitride film deactivates the acid at the nitride/resist interface. For a positive resist, this results in an insoluble area, and either resist scumming, or a foot at the resist/substrate interface.

[0007] Furthermore, lithographic aspect ratios require the chemically amplified resist layer be thin, e.g., about 0.5 μm or lower, to print sub 0.18 μm features. This in turn requires the resist to have excellent plasma etch resistance such that resist image features can be transferred down into the underlying substrate. However, in order to decrease absorbance of the chemically a mplified resist, a romatic g roups, such as those in novolaks had to be removed, which in turn decreased the etch resistance.

[0008] The most common type of photoresists are called "single layer" photoresists in which the photoresist has both the function of imaging and plasma etch resistance. Single layer resists use anti-reflective coatings to minimize standing wave problems, which also assists in decreasing problems with substrate poisoning. However, there are distinct performance tradeoffs between resist absorbance, image profiles, resolution and substrate plasma etch resistance which are not optimum for all semiconductor processes.

[0009] Utilizing an underlayer or undercoat film that is placed on the substrate before the chemical amplified resist film is applied can reduce the above-mentioned problems and break the performance tradeoffs described above. The undercoat absorbs most of the deep UV light attenuating standing wave effects. In addition, the undercoat prevents deactivation of the acid catalyst at the resist/substrate interface. Furthermore, the undercoat layer can contain some aromatic groups to provide substrate etch resistance.

[001O] In the typical bilayer resist process, the undercoat layer is applied on the substrate. The chemically amplified resist is then applied on the undercoat I ayer, exposed to deep UV light and developed to form images in the chemically amplified resist topcoat. The bilayer resist system is then placed in an oxygen plasma etch environment to etch the undercoat in the areas where the chemically amplified resist has been removed by the development. The chemically amplified resist in a bilayer system typically contains silicon and is thus able to withstand oxygen plasma etching by converting the s ilicon to s ilicon d ioxide, that then withstands the etch process. After the bottom layer is etched, the resist system can be used for subsequent processing such as non-oxygen plasma etch chemistry that removes the underlying substrate.

[0011] Even though the undercoat attenuates standing waves and substrate poisoning, it poses other problems. First, some undercoat layers are soluble to the chemical amplified resist solvent component. If there is intermixing between the top and undercoat layers, the resolution and sensitivity of the top resist layer will be detrimentally affected.

[0012] In addition, if there is a large difference in the index of refraction between the chemical amplified resist and the undercoat layer, light will reflect off the undercoat layer causing standing wave effects in the resist. Thus, the real portion "n" of the index of refraction of the two layers must be made to essentially match or to have their differences m inimized, and the imaginary portion "k" of the index of refraction of the two layers must be optimized to minimize reflectivity effects.

[0013] Another problem with undercoating layers is that they are sometimes too absorbent because of incorporation of aromatic groups. Some semiconductor manufacturing deep UV exposure tools utilize the same wavelength of light to both expose the resist and to align the exposure mask to the layer below the resist. If the undercoat layer is too absorbent, the reflected light needed for alignment is too attenuated to be useful. However, if the undercoat layer is not absorbent enough, standing waves may occur. A formulator must balance these competing objectives.

[0014] In addition, some undercoats have very poor plasma etch resistance to plasma chemistry. The etch resistance of the undercoat should be comparable to the etch rate of novolak resins in order to be commercially viable. [0015] Furthermore, some undercoat layers require UV exposure in order to form cross-links before the radiation sensitive resist topcoat layer can be applied. The problem with UV cross-linking undercoat layers is that they require long exposure times to form sufficient cross-links. The long exposure times severely constrain throughput and add to the cost of producing integrated circuits. The UV tools also do not provide uniform exposure so that some areas of the undercoat layer may be cross-linked more than other areas of the undercoat layer. In addition, UV cross-linking exposure tools are very expensive and are not included in most resist coating tools because of expense and space limitations.

[O016] Some undercoat layers are cross-linked by heating. However, the problem with some of these undercoat layers is that they require high curing temperatures and long curing times before the top layer can be applied. In order to be commercially useful, undercoat layers should be curable at temperatures below 250 0C and for a time less than 180 seconds. After curing, the undercoat should have a high glass transition temperature to withstand subsequent high temperature processing and not intermix with the resist layer.

[O017] Even at temperatures below 250 °C sublimation of small a mounts of the undercoated formulation (e.g. TAGs, oligomers from the polymer, etc.) or products (e.g. acids, alcohols, water) from the thermal curing frequently occur. This can result in contamination of the equipment, which requires more frequent cleaning or replacement of equipment to avoid loss of product yield and other measures. This results in increased costs and is undesirable.

[0018] In certain applications, it is desirable for the undercoat to planarize the surface of the substrate. However, this may be difficult to accomplish with undercoats undergoing thermal crosslinking. As the temperature rises and the number of crosslinks increase, the glass transition temperature of the film increases. This makes it more difficult for the film to flow and planarize the substrate. Thus it is desirable to use as low a molecular weight material as possible to improve the planarization. However, use of lower molecular weight polymers in the undercoat can adversely impact the lithographic performance of the photoresist imaging process.

[0019] In addition to the requirements for no intermixing, no sublimation, good substrate plasma etch resistance, good planarization properties, and optical properties appropriately complementing the photoresist coated over the undercoat, the undercoat must be compatible with at least one edge bead remover acceptable to the semiconductor industry as well as give excellent compatibility with the photoresist coated over the undercoat so that lithographic performance (e.g. photospeed, wall profiles, depth of focus, adhesion, etc.) are not adversely impacted. Solutions for these issues individually frequently adversely impact the performance in other areas. The present invention is directed to thermally curable polymer compositions with decreased sublimation tendencies in which lower molecular weight polymers may be employed without major adverse impacts in other performance areas.

SUMMARY OF THE INVENTION

[0020] The present invention is directed to a novel thermally curable undercoat composition comprising

a) a polymer of Structure I comprising repeating units of Structure II, III, and IV -M- -W- -Rά

O (H) (III) (IV)

wherein each R1 is independently a hydrogen atom or an alkyl group having from 1 to 3 carbon atoms or a halogen atom; L represents a single bond, a -COO- group, or a -CON(R2)- group; R2 represents a hydrogen atom or an alkyl group having from 1 to 3 carbon atoms; M represents a C5-7 cycloalkylene group or an arylene group having from 6 to 18 carbon atoms; W represents a single bond, a -COO- group, -O-, -(C=O)-, or -(SO2)-; R3 represents a hydrogen atom or a linear unsubstituted or substituted alkyl having from 5 to 30 carbon atoms or an unsubstituted or substituted cycloalkyl group having from 5 to 30 carbon atoms, a bridged unsubstituted or substituted alicyclic hydrocarbon group having from 5 to 25 carbon atoms or an unsubstituted or substituted aryl group having from 6 to 18 carbon atoms or an arylalkyl group having from 7 to 18 carbon atoms; n is an integer from 1 to 3, q is an integer from 0 to 3, the sum of n and q being no greater than 5; R4 is a linear or branched or cyclic Ci - C10 alkyl or a halogen group; R5 is an alkyl or branched alkyl or cyclic alkyl or an unsubstituted or substituted alicyclic group, having 5 to 30 carbon atoms or (R6O)tR7 group where R6 is a C∏o linear or branched alkylene group and R7 is linear, branched or cyclic alkyl or an unsubstituted or substituted alicyclic group 0 r a n unsubstituted 0 r s ubstituted a romatic or a lkyl a romatic g roup having 1 to 30 carbon atoms and t is an integer about 1 to 4;

b) a phenolic crosslinker having Structure V R 110ϋx\

K (V)

wherein p is an integer about 2 to 6; R is a -CH2OR group; R is a hydrogen atom, -CH2OR >112 group, CrC5 alkyl group, or aryl; R 10 , R >1111 and R^ are each independently a hydrogen atom, or a C1-C5 alkyl group; X is a di- tri-, tetra-, penta- or hexa- valent aikyl or arylalkyl moiety;

c) a thermal acid generator (TAG) of Structure Vl

(SO3H)X

wherein A is a phenyl or naphthyl group, R20 is an alkyl or a cyclic alkyl or an unsubstituted or substituted alicyclic group having 5 to 30 carbon atoms; when A is phenyl, x is an integer of from 1 to 3, y is an integer of from 0 to 5, the sum of x and y being no greater than 6, and z is 6-x-y; when A is naphthyl, x is an integer from 1 to 3, y is an integer from 0 to 7, the sum of x and y being no greater than 8, and z is 8- x-y; B is a primary, secondary, or tertiary unsubstituted or substituted alkyl or carbocyclic or heterocyclic amine having 4 to 30 carbon atoms; and

d) a solvent. [0021] In addition, the present invention also relates to novel polymers forthe undercoat compositions, and a photolithographic coated substrate comprising: a substrate, a thermally cured undercoat composition on the substrate, and a photoresist coated over the thermally cured undercoat composition. Furthermore, the present invention further relates to a process for using the photolithographic coated substrate for the production of relief structures.

DETAILED DESCRIPTION AND EMBODIMENTS

[0022] The invention provides a thermally curable polymer composition to be used as an undercoat in lithographic processes that has low sublimation tendencies and good planarization capabilities that is compatible with high performance lithographic imaging with high formulation latitude.

The present invention is directed to a novel thermally curable undercoat composition comprising:

a) a polymer of Structure I comprising repeating units of Structure H, III, and IV

L M W- -Rd

(I) (H) (III) (IV)

wherein each R1 is independently a hydrogen atom or an alkyl group having from 1 to 3 carbon atoms or a halogen atom; L represents a single bond, a -COO- group, or a -CON(R2)- group; R2 represents a hydrogen atom or an alkyl group having from 1 to 3 carbon atoms; M represents a C5.7 cycloalkylene group or an arylene group having from 6 to 18 carbon atoms; W represents a single bond, a -COO- group, -O-, -(C=O)-, or -(SO2)-; R3 represents a hydrogen atom or a linear unsubstituted or substituted alkyl having from 5 to 30 carbon atoms or an unsubstituted or substituted cycloalkyl group having from 5 to 30 carbon atoms, a bridged unsubstituted or substituted alicyclic hydrocarbon group having from 5 to 25 carbon atoms or an unsubstituted or substituted aryl group having from 6 to 18 carbon atoms or an arylalkyl group having from 7 to 18 carbon atoms; n is an integer from 1 to 3, q is an integer from 0 to 3, the sum of n and q being no greater than 5; R4 is a linear or branched or cyclic Ci - C10 alkyl or a halogen group; R5 is an alkyl or branched alkyl or cyclic alkyl or an unsubstituted or substituted alicyclic group, having 5 to 30 carbon atoms or (R6O)tR7 group where R6 is a C-∏o linear or branched alkylene group and R7 is linear, branched or cyclic alkyl or an unsubstituted or substituted alicyclic group 0 r a n unsubstituted 0 r s ubstituted a romatic or a lkyl a romatic g roup having 1 to 30 carbon atoms and t is an integer about 1 to 4;

b) a phenolic crosslinker having Structure V

R

wherein p is an integer about 2 to 6; R8 is a -CH2OR12 group; R9 is a hydrogen atom, -CH2OR12 group, CrC5 alkyl group, or aryl; R10, R11 and R12 are each Independently a hydrogen atom, or a C1-C5 alkyl group; X is a di- tri-, tetra-, penta- or hexa- valent alkyl or arylalkyl moiety;

c) a thermal acid generator (TAG) of Structure Vl

.(SO3H)X

(VΓ>

wherein A is a phenyl or naphthyl group, R20 is an alkyl or a cyclic alkyl or an unsubstituted or substituted alicyclic group having 5 to 30 carbon atoms; when A is phenyl, x is an integer of from 1 to 3, y is an integer of from 0 to 5, the sum of x and y being no greater than 6, and z is 6-x-y; when A is naphthyl, x is an integer from 1 to 3, y is an integer from O to 7, the sum of x and y being no greater than 8, and z is 8- x-y; B is a primary, secondary, or tertiary unsubstituted or substituted alkyl or carbocyclic or heterocyclic amine having 4 to 30 carbon atoms; and

d) a solvent.

[0023] The polymer employed in the thermally curable polymer composition comprises repeating units of Structures II, III, and IV. In the repeating unit having Structure II, R1 is a hydrogen atom or an alkyl group having from 1 to 3 carbon atoms. Examples of R1 groups include methyl, ethyl, propyl, and iso-propyl. Preferred R1 are hydrogen and methyl. L represents a single bond, a -COO- group, or a -CON(R2)- group, wherein R2 represents a hydrogen atom o r an alkyl g roup h aving f rom 1 to 3 carbon atoms. Preferred L groups are a single bond, or a -COO- group. M represents a C5-C7 cycloalkylene group or a C6-C18 arylene group. Preferred M groups are a C5-C7 cycloalkylene group or a Cβ-C1o arylene group. W represents a single bond, a -COO- group, a -(CO)- group, or an -(SO2)- group. The preferred W is a single bond. [0024] In the repeating unit having Structure Ii, R3 represents a hydrogen atom, or a linear unsubstituted or substituted alkyl having from 5 to 30 carbon atoms or a cycloalkyl group having from 5 to 30 carbon atoms, a bridged alicyclic hydrocarbon group having from 5 to 25 carbon atoms or an aryl group having from 6 to 18 carbon atoms or an aikyl aryl group having from 7 to 18 carbon atoms. Suitable examples of R3 include but are not limited to hydrogen, methyl, ethyl, propyl, butyl, isopropyl, isobutyl, tert-butyl, cyclohexyl, cyclopentyl, cycloheptyl cyclooctyl, cyclononyl, cyclodecanyl, cyclodecanemethyl, cyclododecyl, cyclodecanemethyl, bicyclo[1.1.1]pentyl, bicyclo[2.1.1]hexyl, bicyclo[2.2.1]heptyl, bicyclo[3.1.1]heptyl, bicyclo[2.2.2]octyl, bicyclo[3.2.1 ]octyl, bicyclo[4.1.1]octyl, bicyclo[3.2.2]nonyl, bicyclo[3.3.1]nonyl, bicyclo[4.2.1 ]nonyl, bicyclo[5.1.1]nonyl, bicyclo[3.3.2]decyl, bicyclo[4.2.2]decyl, bicyclo[4.3.1]decyl, bicyclo[5.2.1]decyl, bicyclo[3.3.3jundecyl, bicyclo[4.3.2]undecyl, bicyclo[4.4.1]undecyl, bicyclo[5.3.1]undecyl, bicyclo[4.4.2]dodecyl, bicyclo[5.3.2]dodecyl, bicyclo[5.3.3]tridecyl, bicyclo[5.4.2]tridecyl, bicyclo[5.5.1]tridecyl, adamantyl, adamantylmethyl, tricyclo[5,2,1 ,02l6]decanemethyl, tetracyclo[4,4,0,12'5,17'10]dodecanyl, phenyl, benzyl, phenylethyl, naphthyl, naphthylmethyl and the like. Preferred R3 are a hydrogen atom, cyclopentyl, cyclohexyl, bicyclo[2.2.1]heptyl, adamantyl, adamantylmethyl, tricyclo[5,2,1 ,02>6]decyl, tricyclo[5,2,1 ,02'6]decanemethyl, tetracyclo^AO.I^.I^dodecanyl, phenyl, benzyl, phenylethyl, naphthyl and naphthylmethyl group.

[0025] Suitable examples of monomers generating the repeating unit of Structure (II) include, but are not limited to styrene, 4-methylstyrene, 4-methoxystyrene, 4- cyclohexystyrene, 3-cyclohexystyrene, 1-vinylnaphthalene, 2-vinylnapthanlene, 4- phenylstyrene, 3-phenylstyrene, 4-(4'-phenoxyphenyl)styrene, 4-(4'- methoxyphenyl)styrene, 4-(4'-acetylphenyl)styrene, 4-(4'-benzoylphenyl)styrene, N- methylphenylacrylamide, N-methylphenylmethacrylamide, N,N-dimethylacrylamide, 4- cyclohexylphenylacrylate, 4-cyclohexylphenylmethacryIate, 4-cyclopentylphenylacrylate, 4-cyclopentylphenylmethacrylate, 4-cycloheptylphenylacrylate, 4- cycloheptylphenylmethacrylate, 3-cyclohexylphenylacrylate, 3- cyclohexylphenylmethacrylate, S-cyclopentylphenylacrylate, 3- cyclopentylphenylmethacrylate, S-cycloheptylphenylacrylate, 3- cycloheptylphenylmethacrylate, 2-cyclohexylphenylacrylate, 2- cyclohexylphenylmethacrylate, 2-cyclopentylphenylacrylate, 2- cyclopentylphenylmethacrylate, 2-cycloheptylphenylacrylate, 2- cycloheptylphenylmethacrylate, 4-biphenylacrylate, 4-biphenylmethacrylate, (3- phenyl)phenylacrylate, (3-phenyl)phenylmethacrylate, (2-phenyl)phenylacrylate, (2- phenyl)phenylmethacrylate, (4-benzoyl)phenylacrylate, (4-benzoyl)phenylmethacrylate, 4-(4'-methylcyclohexyl)phenylacrylate, 4-(4'-methylcyclohexyl)phenylmethacrylate, 4- (3'-methylcyclohexyl)phenylacrylate, 4-(3'-methylcyclohexyl)phenylmethacrylate, 4-(4'- tert-butylcyclohexyl)phenylacrylate, 4-(4'-tert-butylcyclohexyl)phenylmethacrylate, 4-(4'- chlorocyclohexyl)phenylacrylate, 4-(4'-chlorocyclohexyl)phenylmethacrylate, 4-(45- bromocyclohexyl)phenylacrylate, 4-(4'-bromocyclohexyl)phenylmethacrylate, 4-(4'- methylcarbonylcyclohexyl)phenylacrylate, 4-(4'- methylcarbonylcyclohexyl)phenyimethacrylate, 4-(4'- methoxycarbonylcyclohexyl)phenylacrylate, 4-(4'- methoxycarbonylcyclohexyl)phenylmethacrylate, 4-(4'-methylpheny!)phenylacrylate, 4- (4'-methylphenyl)phenylmethacrylate, 4-(3'-methylphenyl)phenylacrylate, 4-(3'- methylphenyl)phenylmethacrylate, 4-(4'-tert-butylphenyl)phenylacrylate, 4-(4'-tert- butylρhenyl)phenylmethacrylate, 4-(4'-chlorophenyl)phenylacrylate, 4-(4'- chlorophenyl)phenylmethacrylate, 4-(4'-bromophenyl)phenylacrylate, 4-(4'- bromophenyOphenylmethacrylate, 4-(4'-methylcarbonylphenyl)phenylacrylate, 4-(4'- methylcarbonylphenyl)phenylmethacrylate, 4-(4'- methoxycarbonylphenyl)phenylacrylate, 4-(4'- methoxycarbonylphenyl)phenylmethacrylate, (4-phenylsulfonyl)phenylacrylate, (4- phenylsulfonyl)phenylmethacrylate, (4-methylsulfonyl)phenylacrylate, (4- methylsulfonyl)phenylmethacrylate, (4-benzylsulfonyl)phenylacrylate, (4- benzylsulfonyOphenylmethacrylate, and the like. More preferred examples of monomers generating Structure (II) include styrene, 4-methylstyrene, 4-methoxystyrene, A- cyclohexystyrene, 4-phenylstyrene, 3-phenylstyrene, , 4-(4'-methoxyphenyl)styrene, 4- (4'-acetylphenyl)styrene, 4-cyclohexylphenylacrylate, 4-cyclohexylphenylmethacrylate, 4-cycloheptylphenylacrylate, 4-cycloheptylphenylmethacrylate, 4-biphenylacrylate, 4- biphenylmethacrylate, (4-benzoyl)phenylacrylate, (4-benzoyl)phenylmethacrylate, (4- acetyl)phenylacrylate, 4-(4'-methylcyclohexyl)phenylacrylate, 4-(4'- methylcyclohexyl)phenylmethacrylate, 4-(4'-chlorocyclohexyl)phenylacrylate, 4-(4'- chlorocyclohexyl)phenylmethacrylate, 4-(4'-bromocyclohexyl)phenylacrylate, 4-(4'- bromocyclohexyl)phenylmethacrylate, 4-(4'-methylcarbonylcyclohexyl)phenylacrylate, 4-(4'-methylcarbonylcyclohexyl)phenylmethacrylate, 4-(4'- methoxycarbonylcyclohexyl)phenylacrylate , 4-(4'- methoxycarbonylcyclohexyl)phenylmethacrylate, 4-(4'-methylphenyl)phenylacrylate, 4- (4'-methylphenyI)phenylmethacrylate, 4-(4'-chlorophenyl)phenylacrylate, 4-(4'- chlorophenyl)phenylmethacrylate, (4-phenylsulfonyl)phenylacrylate, (4- phenylsulfonyl)phenylmethacrylate, (4-benzylsulfonyl)phenylmethacrylate, and the like. Most preferred examples of monomers generating Structure (II) include styrene, 4- methylstyrene, 4-methoxystyrene, 4-cyclohexystyrene, 4-phenylstyrene, 1- vinylnaphthalene, 2-vinylnapthanlene, 4-cyclohexylphenylacrylate, 4- cyclohexylphenylmethacrylate, 4-biphenylacrylate, 4-biphenylmethacrylate and the like.

[0026] The polymer of Structure I further includes a repeating unit represented by Structure (III), wherein R1 has the meaning as defined above; n is an integer from 1 to 2, q is an integer from 0 to 3, the sum of n and q being no greater than 5; wherein R4 is a linear or branched or cyclic C1 - Cio alkyl or a halogen group. Suitable examples of R4 groups include but are not limited to methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, pentyl, hexyl, cyclohexyl, cyclopentyl, octyl, cyclooctyl, cyclononyl, chloro, fluoro, bromo and the like. Preferred R4 groups are a halogen group or a C1-C4 linear or branched alkyl group. It is also preferred that q = 0. Suitable examples of monomers generating Structure (III) include but are not limited to 4-hydroxystyrene, 3- hydroxystyrene, 2-hydroxystyrene, 2-methyi-4-hydroxystyrene, 2-tert-butyl-4- hydroxystyrene, 3-methyl-4-hydroxystyrene, 2-fluoro-4-hydroxystyrene, 2-chloro-4- hydroxystyrene, 3,4-dihydroxystyrene, 3,5-dihydoxystyrene, 3,4.5-trihydroxystyrene, 3,5-dimethyl-4-hydroxystyrene, 3,5-tert-butyl-4-hydroxystyrene and the like. Preferred examples of monomers generating Structure (III) include 4-hydroxystyrene, 3- hydroxystyrene, and 3,5-dihydoxystyrene. The most preferred monomer generating Structure III is 4-hydroxystyrene.

[0027] In practice, the monomeric unit described by Structure 111 is provided by using a derivative at the hydroxylic group which is removable. For example, hydroxystyrene (II; R1= H1 n = 1; q - 0) can be provided by 4-acetoxystyrene or 4- trimethylsiloxystyrene. Subsequent to the polymerization, the protecting group is removed.

[0028] The polymer of Structure I further includes a repeating unit represented by Structure (IV), wherein R1 has the meaning as defined above and R5 is a cyclic alkyl or an unsubstituted or substituted alicyclic group having 5 to 30 carbon atoms or (R6O)tR7 group where R6 is a C~rio linear or branched alkylene group and R7 is a linear, branched or cyclic alkyl or an unsubstituted or substituted alicyclic group or an unsubstituted or s ubstituted a romatic or a lkyl aromatic group having 1 to 30 carbon atoms and t is an integer from 1 to about 4.

[0029] Suitable examples of R5 include but are not limited to cyclohexyl, cyclopentyl, cycloheptyl cyclooctyl, cyclononyl, cyclodecanyl, cyclodecanemethyl, cyclododecyl, cyclodecanemethyl, bicyclo[1.1.1]pentyl, bicyclo[2.1.1]hexyl, bicyclo[2.2.1]heptyl, bicyclo[3.1.1]heptyl, bicyclo[2.2.2]octyl, bicyclo[3.2.1]octyl, bicyclo[4.1.1]octyl, bicyclo[3.2.2]nonyl, bicyclo[3.3.1]nonyl, bicyclo[4.2.1]nonyl, bicyclo[5.1.1]nonyl, bicyclo[3.3.2]decyl, bicyclo[4.2.2]decyl, bicyclo[4.3.1]decyl, bicyclo[5.2.1]decyl, bicyclo[3.3.3]undecyl, bicyclo[4.3.2]undecyl, bicyclo[4.4.1]undecyl, bicyclo[5.3.1]undecyl, bicyclo[4.4.2]dodecyl, bicyclo[5.3.2]dodecyl, bicyclo[5.3.3]tridecyl, bicyclo[5.4.2]tridecyl, bicyclo[5.5.1]tridecyl, adamantyl, adamantylmethyl, thcyclo[5,2,1 ,02i6]decanemethyl, tetracyclo[4A0f 12^17i1^dodecanyl and the like. Preferred examples of R5 include cyclohexyl, b icyclo[2.1.1]hexyl, b icyclo[2.2.1]heptyl, bicyclo[3.1.1]heptyl, adamantyl, adamantylmethyl, tricyclo[5,2,1 ,02i6]decanemethyl, tetracyclo[4,4,0,12'5,17l10]dodecanyl, ethoxycyclohexyl, propyloxycyclohexyl, isopropyloxycyclohexyl, tricyclo[5,2,1 ,02i6]decyl, ethoxytricyclρ[5,2,1 ,02l6]decyl , and ethoxydicyclopentenyl.

[0030] Suitable examples of R6 include but are not limited to methylene, ethylene, propylene, butylene, isopropylene, isobutylene and the like. Preferred examples of R6 include ethylene, propylene, and isopropylene.

[0031] Suitable examples of R7 include but are not limited to cyclohexyl, cyclopentyl, cycloheptyl cyclooctyl, cyclononyl, cyclodecanyl, cyclodecanemethyl, cyclododecyl, cyclodecanemethyl, bicyclo[1.1.1]pentyl, bicyclo[2.1.1]hexyl, bicyclo[2.2.1]heptyl, bicyclo[3.1.1]heptyl, bicyclo[2.2.2]octyl, bicyclo[3.2.1]octyl, bicyclo[4.1.1]octyl, bicyclo[3.2.2]nonyl, bicyclo[3.3.1]nonyl, bicyclo[4.2.1]nonyl, bicyclo[5.1.1]nonyl, bicyclo[3.3.2]decyl, bicyclo[4.2.2]decyl, bicycio[4.3.1]decyl, bicyclo[5.2.1]decyl, bicyclo[3.3.3]undecyl, bicyclo[4.3.2]undecyl, bicyclo[4.4.1]undecyl, bicyclo[5.3.1]undecyl, bicyclo[4.4.2]dodecyl, bicyclot5.3.2]dodecyl, bicyc1o[5.3.3]tridecyl, bicyclo[5.4.2]tridecyl, bicyclo[5.5.1]tridecyl, adamantyl, adamantylmethyl, dicyclopentenyl, tricyclo[5,2,1 ,02'δ]decyl, tricyclo[5,2,1 ,02l6]decanemethyl, tetracyclo[4,4,0,12-5,17i10]dodecanyl and the like. Preferred examples of R7 include cyclohexyl, bicycio[2.1.1]hexyl, bicyclo[2.2.1]heptyl, bicyclo[3.1.1jheρtyl, bicyclo[2.2.2]octyl, bicyclo[3.2.2]nonyl, bicyclo[3.3.2]decyl, bicyclo[4.2.2]decyl, bicyclo[3.3.3]undecyl, bicyclo[4.3.2]undecyl, bicyclo[4.4.1]undecyl, bicyclo[5.3.1]undecyl, bicyclo[4.4.2]dodecyl, bicyclo[5.3.2]dodecyl, bicyclo[5.3.3]tridecyl, bicyclo[5.4.2]tridecyl, bicyclo[5.5.1]tridecyl, adamantyl, adamantylmethyl, tricyclo[5,2,1 ,02'6]decanemethyl, tricyclo[5,2,1 ,02'6]decyl, and tetracyclo[4,4,0,12-5,17>10]dodecanyl.

[0032] Suitable examples of monomers generating repeating units of Structure (111) include but are not limited to cyclohexylacrylate, cyclohexylmethacrylate, cyclopentylacrylate, cyclopentylmethacrylate, cycloheptylacrylate, cycloheptylmethacrylate, bicyclo[2.1.Ijhexylacrylate, bicyclo[2.1.1]hexylmethacrylate, bicyclo[2.2.1]heptylacrylate, bicyclo[2.2.1]heptylmethacrylate, bicyclo[3.2.1]octylacrylate, bicyclo[3.2.1]octylmethacrylate, isobornylacrylate, isobornylmethacrylate, adamantylacrylate, adamantylmethacrylate, tricyclo[5,2,1 ,02'6]decylacrylate, tricyclo[5,2,1 ,02l6]decylmethylacrylate, tricyclo[5,2,1 ,02i6]decanemethyImethacrylate, tetracyclo[4 ,4,0,125,17i10]dodecanylacrylate, tetracyclo[4,4,0,12-5,17i10]dodecanylmethacrylate, ethylene glycol methyl ether acrylate, ethylene glycol methyl ether methacrylate, ethylene glycol ethyl ether acrylate, ethylene glycol ethyl ether methacrylate, ethylene glycol dicyclopentenyl ether acrylate, ethylene glycol dicyclopentenyl ether methacrylate, ethylene glycol phenyl ether acrylate, ethylene glycol phenyl ether methacrylate, ethylene glycol benzyl ether acrylate and ethylene glycol benzyl ether methacrylate the like. Preferred example of monomers generating repeating units of Structure (III) Include cyclohexylacrylate, cyclohexylmethacrylate, bicyclo[2.1.1]hexylmethacrylate, isobornylacrylate, isobornylmethacrylate, adamantylacrylate, adamantylmethacrylate, tricyclo[5,2,1 ,02i6]decylacrylate, tricyclo[5,2,1,02i6]decylmethylacrylate, ethylene glycol ethyl ether methacrylate, ethylene glycol dicyclopentenyl ether acrylate, ethylene glycol dicyclopentenyl ether methacrylate, ethylene glycol phenyl ether acrylate, ethylene glycol phenyl ether methacrylate, ethylene glycol benzyl ether acrylate and ethylene glycol benzyl ether methacrylate.

[0033] The polymers of this invention can be prepared from the corresponding monomers by any suitable conventional polymerization process which reacts an ethylenically unsaturated group. Such processes include, but are not limited to, free radical or controlled radical polymerizations. Such processes typically are run in a solvent or solvent mixture using a catalyst or initiator. Initiators should be chosen based on the temperature to be employed in the polymerization, which in turn may be set by the boiling point of the solvent. The temperature employed may depend on the monomer stability, and the catalytic ability of the catalyst at the operating temperature or by the decomposition half-life of the initiator.

[O034] Suitable initiation concentrations are between about 0.001 to about 10.0 % moles of initiator to total moles of monomer. The preferred range of initiator concentration is between about 0.01 to about 8.0 % moles of initiator to total moles of monomer. The most preferred range of initiator concentration is between about .0.5 to about 8.0 % moles of initiator to total moles of monomer.

[O035] Examples of suitable free radical initiators include, but are not limited to, benzoyl peroxide, 2,2'-azobisisobutyronitrile, 2,2'-azobis(methylisobutyronitrile), dimethyl 2,2'-azobisisobutyrate and lauroyl peroxide. Optionally, a chain transfer agent (e.g. carbon tetrabromide or 1-dodecanethiol) may be included.

[0036] Suitable solvents for polymerization include, but are not limited to, dioxane, tetrahydrofuran, 2-methyltetrahydrofuran, acetonitrile, toluene, ethylacetate, propylene glycol monomethyl ether acetate, tetrahydropyran, methyl ethyl ketone, methyl isobutyl ketone, and diglyme or any combination thereof. Polymers may be isolated by precipitation of the polymerization solution into an appropriate amount of solvent in which the polymer is insoluble. The precipitated polymer may be isolated by filtration and dried using conventional techniques known by someone skilled in the art.

[0037] The polymers of Structure I employed in the present invention have a weight average molecular weight (Mw) in terms of polystyrene of from about 5000 to about 45,000. A weight average molecular weight (Mw) in terms of polystyrene of from about 7,000 to about 30,000 is preferred. A weight average molecular weight (Mw) in terms of polystyrene of from about 8,000 to about 20,000 is more preferred. The value of Mw can be determined by such standard methods as gel permeation chromatography as described, for example, in Jan Rabek, Experimental Methods in Polymer Chemistry, John Wiley&Sons, New York, 1983. The polydispersity of the polymer may range from 1 to about 6. A preferred polydispersity of the polymer is from about 1 to about 4.

[0038] Repeating units of Structure II, III, and IV impart absorption, solubility and crosslinking and film forming functions when applied as a TCU material. Each repeating unit is focused on at least one of the three functions listed above, but may have some impact on more than other functions. This impact is dependent on the specific monomer being employed. Changing the amount of monomer represented by Il in the formula can vary plasma etch resistance and absorbance, which will strongly vary the optical parameter k, whose influence is on the reflection control of TCU material. The crosslinking density and rate is determined by the amount of monomer represented by Structure III in the above formula, which also affects the optical parameter k. The solvent solubility, plasma etch resistance, and film forming properties can be optimized by choosing appropriate co-monomers of Structure III and IV. Generally, for 248 and 193 nm microlithography the optimum range of values for refractive index (n) and complex index (k) are about 1.5O to 1.80 and 0.12 to 0.28 respectively.

[0039] The absorbance properties of the polymers at a given wavelength can be altered by adjusting the particular monomers or by the concentration of the individual m onomers. 1 1 s hould be n oted t hat t he absorbance o f a g iven p olymer may be different at different wavelengths requiring optimization of the choice of monomers to o btain not o nly t he required o ptical p roperties for t he wavelength of interest, butthe other required properties as well.

[0040] The concentration of repeating units in the polymer used in 248 application having Structure Il may range from about 20% to about 85 molar %. A preferred concentration of repeating units in the polymer having Structure Il is from about 30 % to about 80 molar %. A more preferred concentration of repeating units in the polymer having Structure Il is from about 40 to about 70 molar %. A most preferred concentration of repeating units in the polymer having Structure Il is from about 50% to about 70 molar %. The concentration of repeating units in the polymer having Structure III may range from about 10% to about 40 molar %. A preferred concentration of repeating units in the polymer having Structure III is from about 10 % to about 35 molar %. A more preferred concentration of repeating units in the polymer having Structure III is from about 15 to about 30 molar %. A most preferred concentration of repeating units in the polymer having Structure (Il is from about 15% to about 25 molar %. The concentration of repeating units in the polymer having Structure IV may range from about 5% to about 40 molar %. A preferred concentration of repeating units in the polymer having Structure IV is from about 10 % to about 35 molar %. A more preferred concentration of repeating units in the polymer having Structure IV is from about 15 to about 30 molar %. A most preferred concentration of repeating units in the polymer having Structure IV is from about 15% to about 25 molar %.

[0041] Preferred polymers for 248 nm application are described by Structures VII

R 23 R

(VII) wherein R1 is a hydrogen atom or an alkyl group having from 1 to 3 carbon atoms or a halogen atom; R21 is an unsubstituted or substituted aromatic group having O6-C30 carbon atoms; R22 is a hydrogen or a CrC4 alkyl group, R23 is cyclic alkyl or an unsubstituted or substituted alicyclic group having 5 to 30 carbon atoms or (R30O)tR7 group where R30 is a C2-4 linear or branched alkylene group and R7 is linear, branched or cyclic alkyl or an unsubstituted or substituted alicyclic group or an unsubstituted or substituted aromatic or alkyl aromatic group having 1 to 30 carbon atoms; n is an integer of about 1 to 2 and t is an integer about 1 to 4.

[0042] Polymers d escribed by Structures VIII are also preferred for 248 nm application

O R: 26

(OH)n

?25

(VIII) wherein R24 is a hydrogen atom or a methyl group; R25 is an unsubstituted or substituted aromatic group having C6-C30 carbon atoms; R26 is a cyclic alkyl or an unsubstituted or substituted alicyclic group having 5 to 30 carbon atoms or (R3OO)tR7 group where R30 is a C2-4 linear or branched alkylene group and R7 is a linear, branched or cyclic alkyl or an unsubstituted or substituted alicyclic group or an unsubstituted or substituted aromatic or alkyl aromatic group having 1 to 30 carbon atoms and t is an integer about 1 to 4,and n is an integer of about 1 to 2.

[0043] The concentration of repeating units in the polymer used in 193 application having Structure Il may range from about 5% to about 40 molar %. A preferred concentration of repeating units in the polymer having Structure Il is from about 10 % to about 35 molar %. A more preferred concentration of repeating units in the polymer having Structure Il is from about 15 to about 30 molar %. A most preferred concentration of repeating units in the polymer having Structure Il is from about 15% to about 25 molar %. The concentration of repeating units in the polymer having Structure III may range from about 10% to about 40 molar %. A preferred concentration of repeating units in the polymer having Structure III is from about 10 % to about 35 molar %. A more preferred concentration of repeating units in the polymer having Structure III is from about 15 to about 30 molar %. A most preferred concentration of repeating units in the polymer having Structure III is from about 15*% to about 25 molar %. The concentration of repeating units in the polymer having Structure IV may range from about 20% to about 85 molar %. A preferred concentration of repeating units in the polymer having Structure IV is from about 30 % to about 80 molar %. A more preferred concentration of repeating units in the polymer having Structure IV is from about 40 to about 70 molar %. A most preferred concentration of repeating units in the polymer having Structure IV is from about 50% to about 70 molar %.

[0044] Preferred polymers for 193 nm applications are described by Structure IX R 28

(IX)

wherein R1 is a hydrogen atom, an alkyl group having from 1 to 3 carbon atoms, and a halogen atom; R22 is a hydrogen atom, and a C1-C4 alkyl group; R27 is a hydrogen or a substituted or unsubstituted C5-C7cycloalkyl; R28 is a cyclic alkyl or an unsubstituted or substituted alicyclic group having 5 to 30 carbon atoms or (R30O)tR7 group where R30 is a C2-4 linear or branched alkylene group and R7 is a linear, branched or cyclic alkyl or an unsubstituted or substituted alicyclic group or an unsubstituted or substituted aromatic or alkyl aromatic group having 1 to 30 carbon atoms and t is an integer about 1 to 4, and n is an integer of about 1 to 3.

[0045] Novel polymers described by Structures X are also preferred for 193 nm applications R 28

S29

(X)

wherein R24 is selected from the group consisting of a hydrogen atom and a methyl group; R28 is selected from the group consisting of a cyclic alkyl, an unsubstituted or substituted alicyclic group having 5 to 30 carbon atoms and (R30O)tR7 group where R30 is a C2-4 linear or branched alkylene group and R7 is selected from the group consisting of a linear, branched or cyclic alkyl, an unsubstituted or substituted alicyclic group, and an unsubstituted or substituted aromatic or alkyl aromatic group having 1 to 30 carbon atoms and t is an integer of about 1 to 4; R29 is a substituted or unsubstituted C5-C7 cycloalkyl group; and n is an integer of about 1 to 2.

[0046] The thermally curable underlayer compositions comprise a phenolic crosslinker having Structure V R (V) wherein p is an integer about 2 to 6; R8 is a -CH2OR12 group; R9 is a hydrogen atom, -CH2OR12 group, C1-C5 alkyl group, or aryl; R10, R11 and R12 are each independently a hydrogen atom, or a C1-C5 alkyl group; X is a di- trh tetra-, penta- or hexa- valent alkyl or arylalkyl moiety. Examples of the di- tri-, tetra-, penta- or hexa- valent alkyl or arylalkyl moiety include, but are not limited to,

R 13 R 15

OH

R 19 R17 wherein R13, R14, R15, R16, are independently a hydrogen atom or a CrC5 alkyl group ; R17, R18 and R19 are each independently a C1-C5 alkyl, a C5-C8 cycloalkyl or a cycloalkylphenyl group and Z is a bond, -O-, -S-, a C5-C8 cycloalkyl or a cycloalkylphenyl group.

[0047] Examples of the phenolic crosslinker having Structure V include but are not limited to,

H3COH2C CH2OCH3 H3COH2C CH2OCH3

H3COH2C

H3COH2C ^Y ^CH2OCH3 OH

V-3 V-4 H3COH2C. .CH2OCH3 H3GOH2C CH2OCH3 HO- »H H3COH2C H3COH2C CH2OCH3 CH2OCH3 H3COH2C CH2OCH3 CH2OCH3 H3COH2C V-6 CH2OCH3 CH2OCH3 OH OH H3COH2Cx ,XH2OCH3H3COH2Cx J55. ,CH2OCH3 H3COH2C' CH2OCH3 H3COH2C^ ^Y' ^CH2OCH3H3COH2C ^γ CH2OCH3 H3CO H2C'' ^f XH2OCH3 OH OH OH V-8 V-9 CH2OCH3 CH2OCH3

H3COH2' .CH2OCH3 H3COH2I CH2OCH3

H3COH2C CH2OCH3 OH V-1 1 .CH2OCH3 H3COH2C. .CH2OCH3

I2OCH3

V-12 V-13 H3CQH2C. .CH2OCH3

H3COH2C

OH CH2OCH3 CH2OCH3 V-16

[0048] Crosslinkers employed in this invention can be purchased commercially, or prepared by hydroxymethylation or alkoxymethylation of the corresponding phenols using standard techniques known to those skilled in the art. [0049] The thermally curable underlayer compositions comprises a thermal acid generator (TAG) of Structure Vl

VI

wherein A is a phenyl or naphthyl group, R20 is an alkyl or a cyclic alkyi or an unsubstituted or substituted alicyclic group having 5 to 30 carbon atoms; wh en A is phenyl, x is an integer of from 1 to 3, y is an integer of from 0 to 5, the sum of _x and y being no greater than 6, and z is 6-x-y; when A is naphthyl, x is an integer from 1 to 3, y is an integer from 0 to 7, the sum of x and y being no greater than 8, and z is 8- x-y; B is a primary, secondary, or tertiary unsubstituted or substituted alkyl or carbocyclic or heterocyclic amine having 4 to 30 carbon atoms.

[0050] A variety of aromatic sulfonic acid amine salts can be employed as the TAG, including those disclosed in U.S. Pat. Nos. 3,474, 054, 4,200,729, 4,251 ,665 and 5,187,019. Preferably the TAG will have a very low volatility at temperatur&s between 170 - 2200C. Suitable examples of R20 include but are not limited to pentyl, c^yclopentyl, hexyl, cyclohexyl, cyclooctyl, nonyl, cyclononyl, decanyl, cyclodecanyl, cyclodecanemethyl, cyclododecyl, cyclodecanemethyl, bicyclo[1. 1.1]pentyl, bicyclo[2.1.1]hexyl, bicyclo[2.2.1]heptyl, bicyclo[3.1.1]heptyl, bicyclo[2.2.2]octyl, bicyclo[3.2.1]octyl and the like. Suitable examples of primary, secondary, tertiary, unsubstituted or substituted alkyl or carbocyclic group containing amines include but are not limited dibutylamine, tributylamine, dioctylamine, didecylamine, triisob»utylamine, dicyclohexylamine, N-ethyldicyclohexylamine, 1-methylpyrrolidine, 1-butylpyrrolidine, piperdine, 1-methylpiperidine, hexamethyleneimine, heptamethyleneimine, tropane, quinuclidine and the like. Suitable examples heterocyclic amines include b υt are not limited to 4-methyl~1-oxa-3-aza-cyclopentane, 4,4-dimethyl-1-oxa-3-aza-cyclopentane, 4,4-diethyl-i -oxa-3-aza-cyclopentane, 4,4-diisopropyl-1 -oxa-3-aza-cyclopentane, 4,4- ditert-butyl-1-oxa-3-aza-cyclopentane, 4,4-dimethyl-1-oxa-3-aza-cyclohexane, 1 -aza- 3,7-dioxa-5-ethylbicyclo[3.3.0]octane, 1-aza-3,7-dioxa-5-methylbicyclo[3.3.0]octane, 1 - aza-3,7-dioxa-5-tertbutylbicyclo[3.3.0]octane and the like. Most preferred TAG is CDX- 2168E, which is a dodecylbenzene sulfonic acid amine salt supplied at 25-30% activity in propylene gycol methyl ether from King Industries, Norwalk, CT 06852, USA.

[0051] TAGs e mployed in this invention can be purchased commercially, or prepared by reaction of the corresponding amine with the desired sulfonic acid.

[0052] The thermal acid generators described above should not be considered photoacid generators. Any sensitivity that the thermal acid generators would have to UV light should be very poor, and they cannot practically be used in photolithography as a photoacid generator.

[0053] Suitable solvents for the undercoat include ketones, ethers and esters, such as 2-heptanone, cyclohexanone, propylene glycol monoethyl ether acetate, propylene glycol methyl ether acetate, methyl lactate, ethyl lactate, methyl 3- methoxypropionate, N-methyl-2-pyrrolidone, ethylene glycol monoisopropyl ether, diethylene glycol monoethyl ether, diethylene glycol dimethyl ether and the like.

[0054] This invention relates to an EBR (edge bead remover) compatible thermally curable polymer composition, which may be used for forming an undercoat layer in deep UV lithography. The thermally curable polymer composition comprises the polymer of Structure I, the crosslinker of Structure V, the TAG of Structure Vl and a solvent. When the composition is cast as a film and is heated, the thermal acid generator generates an acid that catalyzes the reaction of the hydroxymethyl or alkoxymethyl g roups a nd s ubsequent reaction with the polymer crosslink it. After crosslinking, the undercoat is insoluble in the resist coating solvent. [O055] The thermally curable polymer composition contains, on a total solids basis, about 65 to 95 wt. %, preferably about 70 to about 95 wt%, and more preferably about 72 to about 95 wt. % of the polymer of Structure I. The amount of the cross-linking agent in the thermally curable polymer composition is from about 3 to about 30 wt. %, preferably from about 3 to about 27 wt% and more preferably from about 3 to about 25 wt. %. The amount of the thermal acid generator in the thermally curable polymer composition is from about 0.1 to about 5 wt. %, preferably from about 0.2 to about 4 wt %, and more preferably from about 0.2 to about 3 wt. %.

[O056] The undercoat compositions are solubilized in the organic solvents described above to prepare the undercoat formulations. A specific concentration is not mandatory, although the concentration employed must be in the proper range to obtain the desired coating thickness with the specific coating tool being employed. In general the total solids content employed is from about 4.0 to about 35.0 wt%, preferably from about 5.0 to about 30.0 wt%, and more preferably from about 5.0 to about 25.0 wt. %.

[0057] The thermally curable polymer composition of the present invention should not begin significant cross-linking until it reaches a temperature of about 50° C. Significant cross-linking below 50° C may lead to gel formation at room temperature, which will reduce its shelf life. Gel formation results in non-uniform coatings and line width variations across the substrate when the thermally curable polymer composition is used as an undercoat layer in microlithography.

[0058] The present invention also relates to a photolithographic bilayer coated substrate comprising: a substrate, a film of the thermally cured undercoat composition as described above coated on the substrate, and a radiation-sensitive resist coated over the thermally cured undercoat composition. [O059] The substrate may be, for example, semiconductor materials such as a silicon wafer or a ceramic substrate, glass, metal, plastic or other organic film.

[0060] In a first coating step, the undercoat composition may be applied uniformly to a suitable substrate by known coating methods. Coating methods include, but are not limited to spray coating, spin coating, offset printing, roller coating, screen printing, extrusion coating, meniscus coating, curtain coating, dip coating, and immersion coating.

[0061] After the first coating step, the tacky film of undercoat composition is baked in a first bake step. The baking may take place at one temperature or multiple temperatures in one or more steps. Baking may take place on a hot plate or in various types of ovens known to those skilled in the art. Suitable ovens include ovens with thermal heating, vacuum ovens with thermal heating, and infrared ovens or infrared track modules. Typical times e mployed for baking will depend on ihe chosen baking means and the desired time and temperature and will be known to those skilled in the art. A preferred method of baking is on a hot p late. When baking on a hot plate employing a two step process, typical times range from about 0.5 minute to about 5 minutes at temperatures typically between about 80-130 0C, followed by a cure step for about 0.5 minutes to about 5 minutes typically between about 170 0C to about 250 0C. In a one step process, the undercoat film is cured for about 0.5 minutes to about 5 minutes typically between about 170 0C to about 250 0C. The undercoat coated substrate is then allowed to cool. Preferably, the thermally curable polymer composition is cured at temperatures between about 150 to at>out 250° C and more preferably between temperatures of 180 to 220° C. The preferable cure times are from about 30 to 180 seconds and more preferably from about 6O to about 120 seconds. Typical film thickness may range from about 200 nm to about 1 micron. [O062] Jn a second coating step, the undercoat coated substrate is then coated with a photoresist and in a second baking step, baked. Coating and baking equipment described above for the undercoat may be employed. Typical times employed for baking will depend on the chosen baking means, the particular photoresist, the desired time and the desired temperature and will be known to those skilled in the art. A preferred method of baking is on a hot plate. When baking on a hot plate, typical times range from about 0.5 minute to about 5 minutes at temperatures typically between about 80 0C to about 140 0C. Optimum bake parameters may vary depending on the Deep UV photoresist and solvent employed. Typical film thickness may range from about 100 nm to about 1/2 micron.

[0063] The photoresist may be any suitable radiation-sensitive resist. It is typically a chemically amplified resist sensitive to radiation in the deep UV region such as those discussed in U.S. Patent Nos. 5,492,793 and 5,747,622. Preferably, for a bilayer resist system, the radiation-sensitive resist will contain silicon to protect it f rom oxygen plasma etching. Examples of suitable chemically amplified resists contain an alkali solubilizing group blocked by an acid sensitive group. Examples of suitable alkali solubilizing groups include, but are not limited to, carboxylic acids, phenols, hydroxyimides, hydroxymethylimides, fluorinated alcohols and silanols. Examples of suitable blocking groups include, but are not limited to, alkyl groups containing tertiary carbons, and alpha alkoxy alkyls, and arylisopropyl groups. Examples of suitable blocked alkali solubilizing groups include, but are not limited to, t-butyl esters, alpha alkoxy esters, alpha alkoxyalkyl aromatic ethers, t-butoxyphenyl, t-butoxyimido, and t-butoxymethylimido. Examples of blocked alkali solubilizing groups can be found in US Patents US5468589, US4491628, US5679495, US6379861 , US6329125, and US5206317, which are incorporated herein by reference.

[0064] Suitable polymers for the imaging layer are those which contain both silicon and blocked alkali solubilizing groups. Suitable polymers are those with silicon content of about 5 to about 30% silicon by weight. Preferred polymers are those with silicon content from about 8 to about 25% silicon. Examples of suitable photoresist polymers can be found in US Patents US6146793, US6165682, US6340734, US 6028154, US6042989, US5882844, US5691396, US5731126, and US5985524. Other suitable polymers are disclosed in US Patents US6531260, US6590010, US Patent Application, Serial No. 09/576,146 and JP2001114835, which are incorporated herein by reference. The silicon content may be contained in the polymer before coating as in the above references or the polymer may be silylated after coating as in US Patents US6306990 and US6110637, which are incorporated herein by reference.

[0065] The radiation-sensitive resist will also contain a photoacid generating (PAG) compound. The PAG compounds may be of any suitable type such as sulfonium or iodonium salts, nitrobenzyl esters, imidosulfonates esters and the like. Typically, the PAG will be present in an amount of about 1 to 1 0% based o n the weight of the polymer.

[0066] Any suitable photoacid generator compounds may be used in the photoresist composition. The photoacid generator compounds are well known and include, for example, onium salts such as diazonium, sulfonium, sulfoxonium and iodonium salts, nitrobenzylsulfonate esters, oximesulfonates, imidosulfonates and disulfones. Suitable photoacid generator compounds are disclosed, for example, in US-Patent Nos. US5558978 and US 5468589 which are incorporated herein by reference. US-Patent No. US6261738 disclose examples of suitable oximesulfonate PAGs. Other suitable photoacid generators are perfluoroalkyl sulfonyl methides and perfluoroalkyl sulfonyl imides as disclosed in US Patent US 5554664.

[0067] Suitable examples of photoacid generators are phenacyl p- methylbenzenesulfonate, benzoin p-toluenesulfonate, α-(p-toluene- sulfonyloxy)methylbenzoin 3-(p-toluenesulfonyloxy)-2-hydroxy-2-phenyl-1- phenylpropyl ether, N-(p-dodecylbenzenesulfonyloxy)-1,8-naphthalimide and N- (ρhenyl-sulfonyloxy)-1 ,8-napthalimide.

[0068] Examples of suitable onium salts included but are not limited to, triphenyl sulfonium bromide, triphenyl sulfonium chloride, triphenyl sulfonium iodide, triphenyl sulfonium methane sulfonate, triphenyl sulfonium trifluoromethanesulfonate, triphenyl sulfonium hexafluoropropanesulfonate, triphenyl sulfonium nonafluorobutanesulfonate, triphenyl sulfonium perfluorooctanesulfonate, triphenyl sulfonium phenyl sulfonate, triphenyl sulfonium 4-methyl phenyl sulfonate, triphenyl sulfonium 4-methoxyphenyl sulfonate, triphenyl sulfonium 4-chloropheny! sulfonate, triphenyl sulfonium camphorsulfonate, 4-methylphenyl-diphenyl sulfonium trifluoromethanesulfonate, bis(4-methy!phenyl)-phθnyl sulfonium trifluoromethanesulfonate, tris-4-methylphenyl sulfonium trifluoromethanesulfonate, 4-tert-butylphenyl-diphenyl sulfonium trifluoromethanesulfonate, 4-methoxyphenyl- diphenyl sulfonium trifluoromethanesulfonate, mesityl-diphenyl sulfonium trifluoromethanesulfonate, 4-chlorophenyl-diphenyl sulfonium trifluoromethanesulfonate, bis(4-chlorophenyl)-phenyl sulfonium trifluoromethanesulfonate, tris(4-chlrophenyl) sulfonium trifluoromethanesulfonate, 4- methylphenyl-diphenyl sulfonium hexafluoropropanesulfonate, bis(4-methylphenyl)- phenyl sulfonium hexafluoropropanesulfonate, tris-4-methylphenyl sulfonium hexafluoropropanesulfonate, 4-tert-butylphenyl-diphenyl sulfonium hexafluoropropane sulfonate, 4-methoxyphenyl-diphenyl sulfonium hexafluoropropane sulfonate, mesityl-diphenyl sulfonium hexafluoropropane sulfonate, 4-chlorophenyl-diphenyl sulfonium hexafluoropropane sulfonate, bis(4- chlorophenyl)-phenyl sulfonium hexafluoropropane sulfonate, tris(4-chlrophenyl) sulfonium hexafluoropropane sulfonate, 4-methylphenyl-dipheny! sulfonium perfluorooctanesulfonate, bis(4-methylphenyi)-phenyl sulfonium perfluorooctanesulfonate, tris-4-methyiphenyl sulfonium perfluoroocatanesulfonate, 4-tert-butylphenyl-diphenyl sulfonium perfluorooctane sulfonate, 4-methoxyphenyl- diphenyl sulfonium perfluorooctane sulfonate, mesityl-diphenyl sulfonium perfluorooctane sulfonate, 4-chlorophenyl-diphenyl sulfonium perfluorooctane sulfonate, bis(4-chlorophenyl)-phenyl sulfonium perfluorooctane sulfonate, tris(4- chlrophenyl) sulfonium perfluorooctane sulfonate, diphenyl iodonium hexafluoropropane sulfonate, diphenyl iodonium 4-methylphenyl sulfonate, bis(4-tert- butylphenyl)iodonium trifluoromethane sulfonate, bis(4-tert-butylphenyl)iodonium hexafluoromethane sulfonate, and bis(4-cyclohexylphenyl)iodonium trifluoromethane sulfonate.

[0069] Further examples of suitable photoacid generators for use in this invention are bis(p-toluenesulfonyl)diazomethane, methylsulfonyl p- toluenesulfonyldiazomethane, 1-cyclo-hexylsulfonyl-1-(1,1- dimethylethylsulfonyl)diazomethane, bis(1,1-dimethylethylsulfonyl)diazomethane, bis(1 -methylethylsulfonyl)diazomethane, bis(cyclohexylsulfonyl)diazomethane, 1 -p- toluenesulfonyl-1-cyclohexylcarbonyldiazomethane, 2-methyl-2-(p- toluenesulfonyl )propiophenone, 2-methanesulfonyl-2-methyl-(4- methylthiopropiophenone, 2,4-methy1-2-(p-toluenesulfonyl)pent-3-one, 1-diazo-1- methylsulfonyl-4-phenyl-2-butanone, 2-(cyclohexylcarbonyl-2-(p- toluenesulfonyl)propane, 1-cyclohexylsulfonyl-1 cyclohexylcarbonyldiazomethane, 1 - diazo-1-cyclohexylsulfonyl-3,3-dimethyl-2-butanone, 1 -diazo-1 -(1 ,1- dimethylethylsulfonyl)-3,3-dimethyl-2-butanone, 1-acetyl-1-(1 - methylethylsulfonyl)diazomethane, 1 -diazo-1 -(p-toluenesulfonyl)-3,3-dimethyl-2- butanone, 1 -diazo-1 -benzenesulfonyl-3,3-dimethyl-2-butanone, 1 -diazo-1 ~(p- toluenesulfonyl)-3-methyl-2-butanone, cyclohexyl 2-diazo-2-(p- toluenesulfonyl)acetate, tert-butyl 2-diazo-2-benzenesulfonylacetate, isopropyl-2- diazo-2-methanesulfonylacetate, cyclohexyl 2-diazo-2-benzenesulfonylacetate, tert- butyl 2 diazo-2-(p-toluenesulfonyl)acetate, 2-nitrobenzyl p-toluenesulfonate, 2,6- dinitrobenzyl p-toiuenesulfonate, 2,4-dinitrobenzyl p- trifluoromethylbenzenesulfonate. [0070] The photoacid generator compound is typically employed in the amounts of about 0.0001 to 20% by weight of polymer solids and more preferably about 1% to 10% by weight of polymer solids.

[0071] Suitable solvents for top radiation-sensitive compositions include ketones, ethers and esters, such as methyl ethyl ketone, methyl isobutyl ketone, 2- heptanone, cyclopentanone, cyclohexanone, 2-methoxy-1-propylene acetate, 2- methoxyethanol, 2-ethoxyethanol, 2-ethoxyethyl acetate, l-methoxy-2-propyl acetate, 1 ,2-dimethoxy ethane ethyl acetate, cellosolve acetate, propylene glycol monoethyl ether a cetate, propylene glycol methyl ether acetate, methyl lactate, ethyl lactate, methyl pyruvate, ethyl pyruvate, ethyl 3-methoxypropionate, N-methyl-2-pyrrolidone, 1 ,4-dioxane, ethylene glycol monoisopropyl ether, diethylene glycol monoethyl ether, diethylene glycol monomethyl ether, diethylene glycol dimethyl ether, and the like. The solvents employed in the top photoresist compositions will be chosen with a view toward compatibility with the polymer resin in the undercoat and top photoresist compositions. F or example, the choice of solventfor the photoresist composition and the concentration thereof depends principally on the type of functionalities incorporated in the acid labile polymer, the photoacid generator, and the coating method. The solvent should be inert, should dissolve all the components in the photoresist, should not undergo any chemical reaction with the components and should be re-removable on drying after coating

[0072] In an additional embodiment, base additives may be added to the photoresist composition. The purpose of the base additive is to scavenge protons present in the photoresist prior to being irradiated by the actinic radiation. The base prevents attack and cleavage of the acid labile groups by the undesirable acids, thereby increasing the performance and stability of the resist. In addition, the base can act as a diffusion control agent to prevent the acid from migrating too far and lower resolution. The percentage of base in the composition should be significantly lower t han t he p hotoacid g enerator o r o therwise t he p hotosensitivity becomes too low. T he preferred range of the base compounds, when present, is a bout 3% to 50% by weight of the photoacid generator compound. Nitrogenous bases are preferred. Suitable examples of base additives are 2-methylimidazole, tetramethyl ammonium hydroxide, tetrabutylammonium hydroxide, triisopropylamine, 4- dimethylaminopryidine, 4,4'-diaminodiphenyl ether, 2,4,5-triphenylimidazole, and 1 ,5- diazabicyclo[4.3.0]non-5-ene, and 1 ,8-diazabicyclo[5.4.0]undec-7-ene.

[0073] Dyes may be added to the photoresist to increase the absorption of the composition to the actinic radiation wavelength. The dye must not poison the composition and must be capable of withstanding the process conditions including any thermal treatments. Examples of suitable dyes are fluorenone derivatives, anthracene derivatives or pyrene derivatives. Other specific dyes that are suitable for photoresist compositions are described in U.S. Patent No. 5593812.

[0074] The photoresist composition may further comprise conventional additives such as adhesion promoters and surfactants. A person skilled in the art will be able to choose the appropriate desired additive and its concentration.

[0075] The i nvention further relates to a process for forming a pattern on a substrate which comprises the following process steps:

A. providing a substrate, B. coating in a first coating step said substrate with a thermally curable undercoat composition of this invention, C. curing said undercoat composition, D. coating in a second coating step a photoresist over the undercoat to produce a bilayer photoresist stack, E. exposing the bilayer photoresist stack, F. developing the photosensitive composition portion of the bilayer photoresist stack making a portion of the underlying undercoat visible, G. rinsing the bilayer photoresist stack, and H. etching the visible undercoat in an oxidizing plasma to produce a bilayer relief image.

[0076] For this process, the substrates, coating, and baking steps are as described for the bilayer stack previously.

[0077] For the production of relief structures, the radiation-sensitive resist is imagewise exposed to actinic radiation. The term 'imagewise' exposure includes both exposure through a photomask containing a predetermined pattern, exposure by means of any suitable source of actinic radiation, such as for example, a computer controlled laser beam which is moved over the surface of the coated substrate, exposure by means of computer-controlled electron beams, and exposure by means of X-rays or UV rays, through a corresponding mask. The imagewise exposure generates acid in the exposed regions of the resist which catalyzes the cleavage of the acid labile groups resulting in a polymer which is aqueous soluble.

[0078] The process described above for the production of relief structures preferably includes, as a further process measure, heating of the coating between exposure and treatment with the developer. With the aid of this heat treatment, known as "post-exposure bake", virtually complete reaction of the acid labile groups in the polymer resin with the acid generated by the exposure is achieved. The duration and temperature of this post-exposure bake can vary within broad limits and depend essentially on the functionalities of the polymer resin, the type of acid generator and on the concentration of these two components. The exposed resist is typically subjected to temperatures of about 5O0C to 15O0C for a few seconds to a few minutes. The preferred post exposure bake i s from about 8O0C to 1300C for about 5 seconds to 180 seconds. Any suitable heating means may be employed. The preferred heating means is a hot plate. [0079] After imagewise exposure and any heat treatment of the material, the exposed areas of the photoresist are removed by d issolution i n a n a queous b ase developer to generate a relief structure. Examples of suitable bases include, but are not limited to, inorganic alkalis (e.g., potassium hydroxide, sodium hydroxide, ammonia water), primary amines (e.g., ethylamine, n-propylamine), secondary amines (e.g. diethylamine, di-n-propylamine), tertiary amines (e.g., triethylamine), alcoholamines (e.g. triethanolamine), quaternary ammonium salts (e.g., tetrarnethylammonium hydroxide, tetraethylammonium hydroxide), and mixtures thereof. The concentration of base employed will vary depending on the base solubility of the polymer employed and the specific base employed. The most preferred developers are those containing tetramethylammonium hydroxide (TMAH). Suitable concentrations of TMAH range from about 1% to about 5%. In addition, an appropriate amount of a surfactant can be added to the developer.

[008O] Development can be carried out by means of immersion, spray, puddling, o r other s imilar developing m ethods known to those skilled in the a rt at temperatures from about 10 0C to 40 0C for about 30 seconds to about 5 minutes with or without agitation. After development, the relief pattern may be optionally rinsed with a rinse comprising de-ionized water or de-ionized water containing one or more surfactants and dried by spinning, baking on a hot plate, in an oven, or other suitable means.

[0081] The radiation-sensitive resist used for the bilayer process described above will typically contain silicon or have silicon incorporated into the resist after development. After images are formed in the radiation-sensitive resist, the imaged substrate will be placed in a plasma-etching environment comprising oxygen so that the underlayer coating will be removed in the area unprotected by the resist. The silicon incorporated in the radiation-sensitive resist forms silicon dioxide when exposed to an oxygen plasma and protects the resist from being etched so that relief structures can be formed in the undercoat layer. [0082] After the oxygen plasma step, the substrate carrying the bilayer relief structure is generally subjected to at least one further treatment step, which changes the substrate in areas not covered by the bilayer coating. Typically, this can be implantation of a dopant, deposition of another material on the substrate or an etching of the substrate. This is usually followed by the removal of the resist coating from the substrate typically by a fluorine/oxygen plasma etch.

[0083] The invention is illustrated by, but not limited to, the following examples in which the parts and percentages are by weight unless otherwise specified.

[0084] General Synthetic Procedure for Polymerization in Tetrahydrofuran (THF):

The m ixture of monomers and chain transfer agent were dissolved in THF under N2 in a round bottom flask equipped with a reflux condenser, a temperature probe and a gas inlet. The mixture was heated to 550C while stirring. Solution degassed by bubbling N2 with syringe for 15 minutes. A solution of initiator in THF was added and the solution was heated to 65°C for 20-24 hours under a N2 atmosphere. The reaction mixture was then cooled to 500C. The reaction mixture was diluted by methanol (50 m L) a nd sodium m ethoxide solution (4 g , 1 0 wt% i n methanol) were added for methanolysis. The mixture was refluxed at 640C and the by-product methyl acetate was continuously removed by azeotropic distillation using Dean-Stark trap for 4 h. After cooling to room temperature, Amberlyst 15 resin (15 g) was added to the mixture to ion exchange with sodium and stirred for 1 h, The resin was filtered and the solution was precipitated into a methanol/water mixture (1.6 L, 2:1 methanol/water) by slow addition. The solid polymer was isolated by filtration and washed with water (100 ml_ x 2). After filtration, the solid was dried at 6O0C for 48 h under vacuum. Molecular weights and molecular weight distributions were measured using a Waters Corp. liquid chromatograph (refractive index detection, Millennium (GPC V software), equipped with the following Phenogel-10, 7.8 x 250 mm columns: 10-4A, 500A & 5OA (from Phenomena) and THF eluent. Thermal decomposition measurements (TGA) were performed using a Perkin-Elmer thermal gravimetric analyzer. The glass transition temperature (Tg) of the polymer was measured using a Perkin-Elmer Pyris 1 Differential Scanning Calorimeter at a heating rate of 20°C/minute. The structure and composition of polymer were a nalyzed w ith a 1 H NMR using a Bruker 400 MHz NMR-spectrometer. See Table 1 for analytical data of the polymer examples.

[0085] Synthesis Example 1

The mixture of monomers [4-biphenyl methacrylate (72.37 g, 0.303 mol), acetoxy styrene (10.56 g, 0.065 mol) and ethylene glycol dicyclopentenyl ether methacrylate (17.07 g, 0.065 mol)] and initiator VAZO 67 (6.00 g, 6.0 wt% vs monomers) and chain transfer agent 1-dodecanethiol (1.8O g , 30 wt% vs i nitiator) were polymerized according to the general procedure above. Transesterification employed 4.0 g sodium methoxide solution. Yield: 91.3g, 94%.

[0086] Synthesis Example 2

The mixture of monomers [4-biphenyl methacrylate (62.74 g, 0.263 mol), acetoxy styrene (14.23 g, 0.087 mol) and ethylene glycol dicyclopentenyl ether methacrylate (23.03 g, 0.087 mol)] and initiator VAZO 67 (6.00 g, 6.0 wt% vs monomers) a nd c hain transfer agent 1-dodecanethiol ( 1.8O g , 30 wt% vs i nitiator) were polymerized according to the general procedure above. Tranesterification employed 5.0 g sodium methoxide solution. Yield: 91.5g, 95%.

[0087] Synthesis Example 3

The mixture of monomers [4-biphenyl methacrylate (54.09 g, 0.227 mol), acetoxy styrene (22.09 g, 0.136 mol) and ethylene glycol dicyclopentenyl ether methacrylate (23.82 g, 0.09 mol)] and initiator VAZO 67 (6.00 g, 6.0 wt% vs monomers) a nd c hain transfer agent 1-dodecanethbl ( 1.80 g , 30 wt% vs i nitiator) were polymerized according to the general procedure above. Transesterification employed 6.0 g sodium methoxide solution. Yield: 85.5g, 91%.

[O088] Synthesis Example 4

The mixture of monomers [biphenyl methacrylate [BPMA](37.74g; 0.158 mol), acetoxy styrene (8.54 g; 0.0527 mol) and ethyleneglycol dicyclopentenyl ether methacrylate (13.82 g; 0.0527 mol) and chain transfer agent, 1-dodecanethiol (1.08 g, 30 wt% of initiator) were dissolved in 83.6 g of PGMEA (propylene glycol methyl ether acetate) (40% of solid) under flow of N2 in a 500 rnL, round bottom flask equipped with a reflux condenser and a gas inlet. The mixture was heated to 70 0C. Then, VAZO 67® [free radical initiator, Dupont product, 2,2'-azobis(2- methylbutyronitrile)] (3.6 g, 6 wt% of monomer used) in 6.4g of PGMEA was added slowly for 1 5 minutes to the reaction mixture and stirred for 24 h under N2. T he disappearance of B PMA was monitored by GPC using a UV detector at 254 nm. After 24 h, residual BPMA was <0.1%. The reaction mixture was cooled to room temperature. Then, 2.0 g of sodium methoxide in methanol (10 wt %) and 50 ml methanol were added to the flask. The reaction mixture was refluxed for 3 h and about 25 ml of methanol was removed by azeotropic distillation using a Dean-Stark trap. The solution was then cooled to room temperature and 10.0 g of Amberlyst 15 resin was added to it. The reaction mixture was stirred for 2h and the resin was isolated by filtration. The solution was distilled to half of the volume under vacuum <60°C to remove methanol and by-product, propylene glycol methyl ether. Finally, a 30 wt% of solid solution was made by adding PGMEA to it.

[0089] Synthesis Example 5

The mixture of monomers [biphenyl methacrylate [BPMA](37.74g; 0.158 mol), acetoxy styrene (8.54 g; 0.0527 mol) and ethyleneglycol dicyclopentenyl ether methacrylate (13.82 g; 0.0527 mol) and chain transfer agent, 1-dodecanethiol (1.08 g, 30wt% of initiator) were dissolved in 83.6 g of PGMEA (propylene glycol methyl ether acetate) (40% of solid) under flow of N2 in a 500 mL, round bottom flask equipped with a reflux condenser and a gas inlet. The mixture was heated to 70 0C. Then, VAZO 67® [free radical initiator, Dupont product, 2,2'-azobis(2- methylbutyronitrile)] (3.6 g, 6 wt% of monomer used) in 6.4g of PGMEA was added slowly for 15 minutes to the reaction mixture. Then, the temperature was slowly increased to 8O0C and stirred for 4 h under N2. The disappearance of BPMA was monitored by GPC using a UV detector at 254 nm. After 3 h, residual BPMA was <0.1%. The mixture was cooled to room temperature. Then, 2.0 g of sodium methoxide in methanol (10 wt %) and 50 ml methanol were added to the flask. The reaction mixture was refluxed for 3 h and about 25 ml of methanol was removed by azeotropic distillation using a Dean-Stark trap. The solution was then cooled to room temperature and 10.0 g of Amberlyst 15 resin was added to it. The reaction mixture was stirred for 2h and the resin was separated by filtration. The solution was distilled to half of the volume under vacuum <60°C to remove methanol and by-product, propylene glycol methyl ether. Finally, a 30 wt% of solid solution was made by adding PGMEA to it.

[0090] Synthesis Example 6

The mixture of monomers [cyclohexyl methacrylate (32.73 g, 0.1945 mol), A- acetoxystyrene (10.52 g, 0.0648 mol) and styrene (6.75 g, 0.0648 mol)] and chain transfer agent 1-dodecanethiol (0.9 g, 0.0044 mol) were dissolved in THF (73 g, 40% solid) in a 500 mL three neck round bottom flask. The initiator VAZO-67 (3.0 g, 0.0156 mol) dissolved in THF (2 g) was added to mixture at 55°C and was heated to 650C for 24 h. The polymer was processed as described in the General Synthetic Procedure for Polymerization in Tetrahydrofuran. [0091] Synthesis Example 7

The mixture of monomers [cyclohexy! methacrylate (32.73 g, 0.1945 mol), 4- acetoxystyrene (10.52 g, 0.0648 mol) and styrene (6.75 g, 0.0648 mol)] was dissolved in THF (73 g, 40% solid) in a 500 ml_ three neck round bottom flask. The initiator VAZO-67 (1.5 g, 0.O078 mol) dissolved in THF (2 g) was added to mixture at 550C and was heated to 650C for 24 h. No chain transfer agent was used. The polymer was processed as described in the General Synthetic Procedure for Polymerization in Tetrahydrofuran.

[0092] Synthesis Example 8

The mixture of monomers [cyclohexyl methacrylate (28.16g, 0.1674 mol), 4- acetoxystyrene (9.05 g, 0.0558 mol) and 4-cyclohexylphenyl acrylate (12.79 g, 0.0558 mol)] and chain transfer agent 1-dodecanethiol (0.8 g, 0.0040 mol) were dissolved in THF (73 g, 40% solid) in a 500 ml_ three neck round bottom flask. The initiator VAZO-67 (2.5 g, 0.O130 mol) dissolved in THF (2 g) was added to mixture at 550C and was heated to 65°C for 24 h. The polymer was processed as described in the General Synthetic Procedure for Polymerization in Tetrahydrofuran.

[0093] Synthesis Example 9

The mixture of monomers [cyclohexyl methacrylate (28.16g, 0.1674 mol), 4- acetoxystyrene (9.05 g, 0.0558 mol) and 4-cyclohexylphenyl acrylate (12.79 g, 0.0558 mol)] was dissolved in THF (73 g, 40% solid) in a 500 ml_ three neck round bottom flask. The initiator VAZO-67 (3.0 g, 0.0156 mol) dissolved in THF (2 g) was added to mixture at 550C and was heated to 650C for 24 h. No chain transfer agent was used. The polymer was processed as described in the General Synthetic Procedure for Polymerization in Tetrahydrofuran. [0094] Synthesis Example 10

The mixture of monomers [cyclohexyl methacryiate (27.69 g, 0.1646 mol), 4- acetoxystyrene (8.90 g, 0.O549 mol) and 4-cyclohexylphenyl methacryiate (13.41 g, 0.0549 mol)] and chain transfer agent 1-dodecanethiol (1.2 g, 0.0059 mol) were dissolved in THF (73 g, 40% solid) in a 500 mL three neck round bottom flask. The initiator VAZO-67 (4.0 g, 0.O208 mol) dissolved in THF (2 g) was added to mixture at 55°C and was heated to 65°C for 24 h. The polymer was processed as described in the General Synthetic Procedure for Polymerization in Tetrahydrofuran.

[0095] Synthesis Example 11

he mixture of monomers [cyclohexyl methacryiate (27.69 g, 0.1646 mol), 4- acetoxystyrene (8.90 g, 0.0549 mol) and 4-cyclohexylphenyl methacryiate (13.41 g, 0.0549 mol)] was dissolved in THF (73 g, 40% solid) in a 500 mL three neck round bottom flask. The initiator VAZO-67 (2.5 g, 0.0130 mol) dissolved in THF (2 g) was added to mixture at 550C and was heated to 650C for 24 h. No chain transfer agent was used. The polymer was processed as described in the General Synthetic Procedure for Polymerization in Tetrahydrofuran.

[0096] Synthesis Example 12

The mixture of monomers [cyclohexyl methacryiate (27.69 g, 0.1646 mol), 4- acetoxystyrene (8.90 g, 0.0549 mol) and 4-cyclohexylphenyl methacryiate (13.41 g, 0.0549 mol)] and chain transfer agent 1-dodecanethiol (1.5 g, 0.0074 mol) were dissolved in THF (148 g, 25% solid) in a 500 mL three neck round bottom flask. The initiator VAZO-67 (5.0 g, 0.0260 mol) dissolved in THF (2 g) was added to mixture at 550C and was heated to 65°C for 24 h. The polymer was processed as described in the General Synthetic Procedure for Polymerization in Tetrahydrofuran. [0097] Synthesis Example 13

The mixture of monomers [TCD methacrylate (22.94 g, 0.104 mol), 4- acetoxystyrene (12.51 g, 0.078 mol) and 4-cyclohexylstyrene(14.55 g, 0.078 mol)] and chain transfer agent 1-dodecanethiol (1.5 g, 0.0074 mol) were dissolved in THF (148 g, 25% solid) in a 500 mL three neck round bottom flask. The initiator VAZO-67 (2.5 g, 0.0130 mol) dissolved in THF (2 g) was added to the mixture at 55°C and was heated to 650C for 24 h. The polymer was processed as described in the General Synthetic Procedure for Polymerization in Tetrahydrofuran.

[0098] Synthesis Example 14

The mixture of monomers [4-phenylstyrene (28.01 g, 0.155 mol), 4- acetoxystyrene (8.40 g, 0.O58 mol) and ethyleneglycol dicyclopentenyl ether methacrylate (15.39 g; 0.058 mol) and chain transfer agent 1-dodecanethiol (1.5 g, 0.0074 mol) are dissolved in THF (148 g, 25% solid) in a 500 mL three neck round bottom flask. The initiator VAZO-67 (2.5 g, 0.0130 mol) dissolved in THF (5 g) iss added to the mixture at 55°C and is heated to 65oC for 24 h. The polymer is processed as described in the General Synthetic Procedure for Polymerization in Tetrahydrofuran.

[0099] Table 1 Thermal Syn. NMR Structure il/lil/IV) Stability Ex. Mole MW PDI Tg (5%wt Ratio loss)

o \^y 9 Il 0.69 III 0.16 14666 1.92 128 310 1 IV 0.15 •T I! 0.6O A, X I T ^0NTYi — s Ill 0.19 13175 1.97 124 305 IV 0.21

Il 0.51 III 0.28 11262 1.88 118 300 IV 0.21

Il 0.59 III 0.2O 15700 1.95 IV 0.21

i $ r Il 0.6O III 0.19 11044 2.11 - IV 0.21

Il 0.15 O U ? ° HI 0.19 10088 2.21 90 256 IV 0.66 OH Q

Il 0.29 IH 0.24 22812 2.16 120 312 IV 0.47 OH Q

°=( A )=° Il 0.22 III 0.2O 13216 2.71 98 311 IV 0.58 0.2O 0.22 40189 4.35 113 301 0.58

0.25 10 0.2O 8132 2.05 97 285 0.55

0.24 11 0.20 28966 3.92 122 275 0.56

0.24 12 0.19 6031 2.04 84 268 0.57

0.33 13 0.27 12300 3.0 138 318 0.40

0.59 14 0.21 15400 2.5 140 275 0.20 [0100] Table 2A contains information on polymers obtained from a polymer vendor by custom synthesis.

Table 2A Polymer Mole Ratio of Monomer MW PDl Tg (0C) # by NMR Il III IV P-1 0.63 0.18 0.19 15,174 2.24 106 P-2 0.62 0.18 0.20 14,473 2.24 100 P-3 0.64 0.18 0.18 18,845 2.35 113 P-4 0.63 0.19 0.18 17,897 2.51 104 P-5 0.63 0.19 0.18 12,800 2.21 P-6 0.65 0.18 0.17 12,241 2.36 P-7 0.65 0.18 0.17 13,473 2.41 P-8 0.61 0.19 0.20 13,135 2.35 P-9 0.63 0.19 0.18 16,708 2.11 114 P-10 0.62 0.21 0.17 15,848 2.54 101 P-11 0.57 0.21 0.22 13703 1.69 P-12 0.59 0.20 0.21 12812 1.79

[0101] Table 2B contains information on polymers obtained from a polymer vendor by custom synthesis Table 2B Polymer Mole Ratio of Monomer MW PDI Tg (0C) # by NMR Il III IV

P-13 0.24 0.19 0.57 9900 1.9 -

[0102] Table 3 lists information about TAGs used in examples in this

application.

Table 3: TAGs

TAG TAG Name TAG Type Solvent % active example system A CHTS Cyclohexyl - 100 tosylate B Nacure 5925 Amine neutralized lsopropanol 25 DDBSA C Nacure 1323 Amine neutralized Xylene 21 DNNSA D Nacure XC- Polymeric Xylene 25 3210 DDBSA covalent blocked E Nacure 1953 DDBSA covalent n-butanol / 2- 25 blocked butoxyethanol F Nacure 1557 Amine neutralized n-butanol / 2- 25 DNNSA butoxyethanol G Nacure 1419 Epoxyblocked Xylene / MIBK 30 DNNSA H CDX-2167 Amine neutralized PGMEA 27.5 DDBSA I CDX-2168E Amine neutralized PGME 27.5 DDBSA DDBSA : dodecylbenzenesulfonic acid; DNNSA : dinonylnaphthalenesulfonic acid

[0103] Undercoat Formulation Example 1 (Comparative)

For 5Og of undercoat solution in a 2oz amber bottle, 7.02g of polymer P-1 ,

2.0Og (15% solution) of CYMEL 303 cross linker, 0.19g of TAG A , and 40.8Og of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter. CYMEL 303 is an alkoxymethylmelamine crosslinker from Cytec Industries.

[0104] Undercoat Formulation Example 2 (Comparative) For 5Og of undercoat solution in a 2oz amber bottle, 6.96g of polymer P-2, 2.0Og (15% solution) of CYMEL 303 cross linker, 0.96g of TAG B solution, and 40.08g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0105] Undercoat Formulation Example 3 (Comparative) For 5Og of undercoat solution in a 2oz amber bottle, 6.94g of polymer P-2, 2.00g (15% solution) of CYMEL 303 cross linker, 1.26g of TAG C solution, and 39.8Og of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0106] Undercoat Formulation Example 4 (Comparative) For 5Og of undercoat solution in a 2oz amber bottle, 6.96g of polymer P-2, 2.00g (15% solution) of CYMEL 303 cross linke, 0.96g of TAG D solution, and 40.08g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0107] Undercoat Formulation Example 5 (Comparative) For 5Og of undercoat solution in a 2oz amber bottle, 6.96g of polymer P-2, 2.0Og (15% solution) of CYMEL 303 cross linker, 0.96g of TAG E solution, and 40.08g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0108] Undercoat Formulation Example 6 (Comparative) For 5Og of undercoat solution in a 2oz amber bottle, 6.94g of polymer P-2, 2.00g (15% solution) of CYMEL 303 cross linker,1.06g of TAG F solution, and 40.01g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0109] Undercoat Formulation Example 7 (Comparative) For 5Og of undercoat solution in a 2oz amber bottle, 6.94g of polymer P-2, 2.00g (15% solution) of CYMEL 303 cross linker, 0.88g of TAG G solution, and 40.18g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0110] Example 1 Sublimation Testing Procedure (Comparative) A blank 150mm virgin bare silicon wafer was weighed on an analytical scale to 5 significant figures. This wafer will be known as the collection wafer. Each example formulation was spin coated onto ten 150mm bare silicon wafers. Film thickness after coating was 5300A. The coated wafer was p laced over a 2050C hotplate with a gap distance of about 8.22 cm. A Teflon ring with an inner diameter of 120mm, an outer diameter of130mm, and a thickness of 2mm was then placed on top of the coated wafer. The collection wafer then was placed onto the Teflon ring, polished side down. The two wafers were then lowered directly onto the 205°C hotplate for 5 seconds. After five seconds both wafers were removed from the hotplate. The collection wafer was allowed to cool on a chill plate for 10 seconds. The coated wafer was then discarded. This procedure was repeated for all ten coated wafers. After the tenth wafer, and the weight of the collection wafer was

obtained and the delta between the starting weight and final weight was calculated.

This procedure was repeated for all the example formulations.

[0111] The results for the sublimation testing for each of the examples can be

found in Table 4. All experiments are comparative.

Table < t: Summary of the Formulations and sublimation results of the Undercoat Formulations Undercoat Polymer Cross- Thermal Acid TAG (% in Weight of formula¬ (% in linking Generator formula¬ collected tion Ex. # formula¬ Agent (TAG) tion) sublimate(grams) tion) 1 14.01 CYMEL A 0.38 0.00244 303 2 13.92 CYMEL B 0.48 0.00O21 303 3 13.87 CYMEL C 0.53 0.00O45 303 4 13.92 CYMEL D 0.48 0.00O20 303 5 13.92 CYMEL E 0.48 0.00161 303 6 13.87 CYMEL F 0.53 0.00O25 303 7 13.87 CYMEL G 0.53 0.00O13 303

[0112] Data in Table 4 shows that the type of TAG used greatly influences the

amount of material being sublimed during curing of the undercoat

[0113] Undercoat Formulation Example 8 (Comparative)

For 5Og of undercoat solution in a 2oz ambev bottle, 6.98g of polymer P-9,

2.0Og (15% solution) of CYMEL 303 cross linker, 0.9Og of TAG B solution, and

40.13g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture

was then rolled overnight, and the undercoat solution was filtered through a 0.20μm

filter. [0114] Undercoat Formulation Example 9 (Comparative)

For 5Og of undercoat solution in a 2oz amber bottle, 6.9Og of polymer P-2, 2.5Og (15% solution) of Pcywderlink cross linker, 0.9Og of TAG B solution, and 39.70g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter. Powderiink is an alkoxymethylated glycoluril crosslinker available from Cytec Industries.

[0115] Undercoat Formulation Example 10

For 5Og of undercoat solution in a 2oz amber bottle, 5.03g of polymer P-9, 15.00g (15% solution) of cross linker V-7, 0.9Og of TAG B solution, and 29.08g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter. V-7 can be obtained from Honshu Chemicals.

[0116] Lithographic Examples 1-4

Lithographic performance of 140nm trench 280nm pitch using a silicon containing resist TIS 248IL-01-23 (available from FUJIFILM Electronic Materials, Inc.) over various undercoat formulations was examined. All samples were spun coated to a film thickness of 500nm undercoat and cured at 2000C for 90 seconds proximity bake. T IS 248IL-01-23 was spun o n top of UL coated wafers to a film thickness of 235nm. A softbake of 125°C for 90 seconds was applied. All wafers were exposed with a Canon EX6 stepper 0.65NA annular illumination using 248 nm light. 0.80 / 0.50 sigma. A. post exposure bake of 115°C for 90 seconds was applied and wafers were puddle developed with OPD262 for 60 seconds and rinsed with Dl water. Profiles of 140nm trench 280 pitch were then examined with a Hitachi cross sectional SEM for profile. Results can be found in Table 5. Lithographic

Experiments 1-3 are comparative.

Table 5: Summary of the Formulations and Profile results of TIS 248IL-01-23

with the Undercoat Formulations

Litho Under¬ Polymer Cross- Cross- Thermal TAG (% in Footing . Ex. coat (% in linking linker (% Acid formula¬ - 140nm # formula¬ formula¬ Agent in Genera¬ tion) Trench tion Ex. tion) formula¬ tor 280nm # tion) (TAG) Pitch 1 1 14.01 CYMEL 0.60 A 0.38 0.00244 303 2 8 13.95 CYMEL 0.60 B 0.45 Heavy 303 footing 3 9 13.80 Powder! 0.75 B 0.45 Heavy ink footing 4 10 10.05 V-7 4.50 B 0.45 Heavy footing

Table 5 shows that despite the improvement in sublimation performance, the TAG

change in the undercoat formulation negatively impacts the lithographic performance

of the photoresist by increasing the width of the image at the photoresist-undercoat

interface (footing).

[0117] Undercoat Formulation Example 11 (Comparative)

For 5Og of undercoat solution in a 2oz amber bottle, 7.38g of polymer P-6,

0.77g (15% solution) of CYMEL 303 cross linker, 0.05g of TAG H solution, 0.5Og of

a 1% solution of the surfactant Troysol, and 41.31g of propylene glycol methyl ether

acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the

undercoat solution was filtered through a 0.20μm filter. [0118] Undercoat Formulation Example 12 (Comparative)

For 5Og of undercoat solution in a 2oz amber bottle, 7.38g of polymer P-5, O.77g (15% solution) of CYMEL 303 cross linker, 0.05g of TAG H solution, 0.5Og of a 1 % solution of the surfactant Troysol, and 41.31g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0119] Undercoat Formulation Example 13 (Comparative)

For 5Og of undercoat solution in a 2oz amber bottle, 7.38g of polymer P-8, O.77g (15% solution) of CYMEL 303 cross linker, 0.05g of TAG H solution, 0.5Og of a 1% solution of the surfactant Troysol, and 41.31g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0120] Undercoat Formulation Example 14 (Comparative)

For 5Og of undercoat solution in a 2oz amber bottle, 7.38g of polymer P-7, O.77g (15% solution) of CYMEL 303 cross linker, 0.05g of TAG H solution, 0.5Og of a 1% solution of the surfactant Troysol, and 41.31g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0121] Undercoat Formulation Example 15 (Comparative)

For 5Og of undercoat solution in a 2oz amber bottle, 7.38g of polymer P-2, 0.77g (15% solution) of CYMEL 303 cross linker, 0.05g of TAG H solution, 0.5Og of a 1% solution of the surfactant Troysol, and 41.31g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0122] Undercoat Formulation Example 16 (Comparative)

For 5Og of undercoat solution in a 2oz amber bottle, 7.38g of polymer P-2, O.77g (15% solution) of CYMEL 303 cross linker, 0.05g of TAG H solution, 0.5Og of a 1% solution of the surfactant Troysol, and 41.31g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0123] Undercoat Formulation Example 17 (Comparative)

For 5Og of undercoat solution in a 2oz amber bottle, 7.38g of polymer P-3, 0.77g (15% solution) of CYMEL 303 cross linker, 0.05g of TAG H solution, 0,5Og of a 1 % solution of the surfactant Troysol, and 41.31g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0124] Undercoat Formulation Example 18

For 5Og of undercoat solution in a 2oz amber bottle, 6.36g of polymer P-5, 7.5Og (15% solution) of cross linker V-7, 0.05g of TAG H solution, 0.5Og of a 1% solution of the surfactant Troysol, and 35.59g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0125] Undercoat Formulation Example 19 For 5Og of undercoat solution in a 2oz amber bottle, 6.36g of polymer P-2, 7.5Og (15% solution) of cross linker V-7, 0.05g of TAG H solution, 0.50g of a 1% solution of the surfactant Troysol, and 35.59g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0126] Undercoat Formulation Example 20

For 5Og of undercoat solution in a 2oz amber bottle, 6.36g of polymer P-3, 7.5Og (15% solution) of cross linker V-7, 0.05g of TAG H solution, 0.5Og of a 1% solution of the surfactant Troysol, and 35.59g of propylene glycol methyl ether acetate (PGMEA) were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0127] Lithographic Examples 5-14

Lithographic performance of 140nm trench 280nm pitch using TIS 248IL-01- 23 over various undercoat formulations was examined. All samples were spun coated to a film thickness of 500nm undercoat and cured at 2000C for 90 seconds proximity bake. TIS 248IL-01-23 was spun on top of UL coated wafers to a film thickness of 235nm. A softbake of 125°C for 90 seconds was applied. All wafers were exposed with a Canon EX6 stepper 0.65NA annular illumination using 248 nm light. 0.80 / 0.50 sigma. A post exposure bake of 115°C for 90 seconds was applied and wafers were puddle developed with OPD262 for 60 seconds and rinsed with Dl water. Adhesion failure of 130 and 140nm trench 1 :1 pitch were then examined with a Hitachi cross sectional SEM for profile. Results can be found in Table 6. Lithographic examples 5-11 are comparative. Table 6: Summary of the Formulations and Profile results of TIS 248 IL- 1-23 with the Undercoat Formulations

Lith. Under Polymer Cross Cross TAG (% PGMEA Adhesion Ex. coat Mw linking -linker in (% in Failure 130 # formu¬ Agent (% in formula¬ formula¬ and/or lation formu tion) tion) 140nm iation) trench 5 11 12,241 CYMEL 0.23 0.03 85.00 Yes 303 6 12 12,800 CYMEL 0.23 0.03 85.00 Yes 303 7 13 13,135 CYMEL 0.23 0.03 85.00 Yes 303 8 14 13,473 CYMEL 0.23 0.03 85.00 Yes 303 9 15 14.473 CYMEL 0.23 0.03 85.00 Yes 303 10 16 15,848 CYMEL 0.23 0.03 85.00 No 303 11 17 18,845 CYMEL 0.23 0.03 85.00 No 303 12 18 12,800 V-7 2.25 0.03 85.00 No 13 19 14,473 V-7 2.25 0.03 85.00 No 14 20 18,845 V-7 2.25 0.03 85.00 No

Results in Table 6 show that the undercoat formulations using the cross linker

CYMEL 303 require higher polymer Mw to obtain adequate lithographic

performance. Use of the V-7 crosslinker in combination with an amine sulfonate

TAG provides an undercoat which has low sublimation and allows the use of low

molecular weight polymers for better planarization. In addition, the wider molecular

weight range in which it provides good performance gives more formulation latitude

to account for batch to batch polymer variations.

[0128] Undercoat Formulation Example 21 (Comparative}

For 2Og of undercoat solution, to a 1oz amber bottle were added, 8 .97g of

polymer solution (P-13) (31.9 % wt% in PGMEA), 2.0Og (15% solution) of CYMEL

303 cross linker, 0.055g of TAG H solution, 0.21g of 1 % Troysol solution in PGMEA, and 9.96g of propylene glycol methyl ether acetate (PGMEA). The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0129] Undercoat Formulation Example 22 (Comparative)

For 2Og of undercoat solution, to a 1oz amber bottle were added, 8.97g of polymer solution (P-13) (31.9 wt% in PGMEA), 0.12g of Powderlink cross linker, O.055g of TAG H solution, 0.21g of 1% Troysol solution in PGMEA, and 9.96g of propylene glycol methyl ether acetate (PGMEA). The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0130] Undercoat Formulation Example 23

For 2Og of undercoat solution, to a 1oz amber bottle were added, 8.61g of polymer solution (P-13) (31.9 wt% in PGMEA), 1.6g of V-7 cross linker (15% wt % in PGMEA), 0.054g of TAG H solution, 0.21g of 1% Troysol solution in PGMEA, and 9.53g of propylene glycol methyl ether acetate (PGMEA). The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0131] Undercoat Formulation Example 24

For 2Og of undercoat solution, to a 1oz amber bottle were added, 8.42g of polymer solution (P-13) (31.9 wt% in PGMEA), 2.Og of V-7 cross linker (15% wt % in PGMEA), 0.054g of TAG H solution, 0.21g of 1% Troysol solution in PGMEA, and 9.32g of propylene glycol methyl ether acetate (PGMEA). The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0132] Undercoat Formulation Example 25 For 2Og of undercoat solution, to a 1oz amber bottle were added, 8.23g of polymer solution (P-13) (31.9 wt% in PGMEA), 2.4g of V-7 cross linker (15% wt % in PGMEA), 0.054g of TAG H solution, 0.21g of 1% Troysol solution in PGMEA, and 9.11g of propylene glycol methyl ether acetate (PGMEA). The mixture was then rolled overnight, and the undercoat solution was filtered througri a 0.20μm filter.

[0133] Undercoat Formulation Example 26

For 2Og of undercoat solution, to a 1oz amber bottle were added, 8.61g of polymer solution (P-13) (31.9 wt% in PGMEA), 1.6g of V-7 cross linker (15% wt % in PGMEA), 0.044g of TAG H solution, 0.21g of 1% Troysol solution in PGMEA, and 9.53g of propylene glycol methyl ether acetate (PGMEA). The mixture was then rolled overnight, and the undercoat solution was filtered througri a 0.20μm filter.

[0134] Undercoat Formulation Example 27

For 2Og of undercoat solution, to a 1oz amber bottle were added, 8.43g of polymer solution (P-13) (31.9 wt% in PGMEA), 2.Og of V-7 cross linker (15% wt % in PGMEA), 0.044g of TAG H solution, 0.21g of 1% Troysol solution in PGMEA, and 9.32g of propylene glycol methyl ether acetate (PGMEA). The mixture was then rolled overnight, and the undercoat solution was filtered througri a 0.20μm filter.

[0135] Undercoat Formulation Example 28

For 2Og of undercoat solution, to a 1oz amber bottle were added, 8.24g of polymer solution (P-13) (31.9 wt% in PGMEA), 2.4g of V-7 cross linker (15% wt % in PGMEA), 0.044g of TAG H solution, 0.21g of 1% Troysol solution in PGMEA, and 9.11g of propylene glycol methyl ether acetate (PGMEA). The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter. [0136] Undercoat Formulation Example 29

For 2Og of undercoat solution, to a 1oz amber bottle were added, 8.41g of polymer solution (P-13) (31.9 wt% in PGMEA), 2.Og of V-7 cross linker (15% wt % in PGMEA), 0.066g of TAG H solution, 0.21g of 1% Troysol solution in PGMEA, and 9.32g of propylene glycol methyl ether acetate (PGMEA). The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0137] Undercoat Formulation Example 30

For 2Og of undercoat solution, to a 1oz amber bottle were added, 8.22g of polymer solution (P-13) (31.9 wt% in PGMEA), 2.4g of V-7 cross linker (15% wt % in PGMEA), 0.066g of TAG H solution, 0.21g of 1% Troysol solution in PGMEA, and 9.11g of propylene glycol methyl ether acetate (PGMEA). The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0138] Lithographic Examples 15-24

Lithographic performance of 120nm trench (240nm pitch) using a silicon containing resist TlS 193IL-54-20 (available from FUJIFILM Electronic Materials, Inc.) over various undercoat formulations was examined. All samples were spun coated to a film thickness of 500nm undercoat and cured at 2000C for 60 seconds contact bake. TIS 193IL-54-20 was spun on top of UL coated wafers to a film thickness of 235nm. A softbake of 1250C for 60 seconds was applied. All wafers were exposed with an Ultratech Microstepper using 0.60NA annular illumination; 0.80/0.70 sigma with 193 nm light. A post exposure bake of 115°C for 60 seconds was applied and wafers were puddle developed with OPD262 for 60 seconds and rinsed with Dl water. Pattern fidelity of the 120 nm trenches at 1 :1 pitch was then examined with a Hitachi cross sectional SEM for profile. The results can be found in Table 7. Lithographic Examples 15 and 16 are comparative. Table 7: Summary of the Formulations and Profile results of TIS 193IL-54-20 with the Undercoat Formulations

Litho Under Cross- Cross- TAG H PGMEA Pattern Fidelity linking Ex. # -coat Agent linker (% (% in (% in of 120nm trench formu in formula¬ formula¬ -lation formula¬ tion) tion) tion) 15 21 CYMEL 0.23 0.075 85.00 Severe footing 303 16 22 Powderii 0.23 0.075 85.00 Adhesion failure nk 17 23 V-7 1.2 0.075 85.00 Vertical, clean profiles 18 24 V-7 1.5 0.075 85.00 Vertical, clean profiles 19 25 V-7 1.8 0.075 85.00 Vertical, clean profiles 20 26 V-7 1.2 0.060 85.00 Vertical, clean profiles 21 27 V-7 1.5 0.060 85.00 Vertical, clean profiles 22 28 V-7 1.8 0.060 85.00 Vertical, clean profiles 23 29 V-7 1.5 0.090 85.00 Vertical, clean profiles 24 30 V-7 1.8 0.090 85.00 Vertical, clean profiles

Results in Table 7 show that the undercoat formulations using the cross linker V-7 in

combination with TAG H, promote robust lithographic patterning of the imaging layer

across a range of TAG and cross linker loadings in the undercoat. In contrast, use of

CYMEL 303 crossϋnker p romotes unacceptable severe footing at the base of the

patterned imaging layer profiles. The use of Powderlink crosslinker results in

unacceptable adhesion failure of the imaging layer patterns.

[0139] Undercoat Formulation Example 31

For 5Og of undercoat solution in a 2oz amber bottle, 17.09g of polymer P-11

solution (35% in PGMEA), 10.0g (15% solution in PGMEA) of cross linker V-7, O.05g of TAG I solution, and 22.86g of PGMEA were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0140] Undercoat Formulation Example 32

For 5Og of undercoat solution in a 2oz amber bottle, 17.09g of polymer P-12 solution (35% in PGMEA) , 10.0g (15% solution in PGMEA) of cross linker V-7, O.05g of TAG I solution, and 22.86g of PGMEA were mixed. The mixture was then rolled overnight, and the undercoat solution was filtered through a 0.20μm filter.

[0141] EXAMPLE 2

Undercoat Formulation Examples 31 and 32 were tested according to the procedure described in Example 1. Table 8 contains the results.

Table 8 Undercoat Polymer Cross- Thermal Acid TAG (% in Weight of collected formulation (% in link¬ Generator formula¬ sublimate(grams) Ex. # formula¬ ing (TAG) tion) tion) Agent 31 11.96 V-7 I 0.03 0.00003 32 11.96 V-7 I 0.03 0.00005

The data in Table 8 shows that the combination of the amine n eutralized s ulfonic acid TAG and the alkoxymethylated phenolic crosslinker had only trace amounts of sublimate, lower even than those in Table 4.

[0142] Undercoat Formulation Example 33

For 20Og of undercoat solution in a 8 oz amber bottle, 121.55 of the polymer prepared in Synthesis Example 6 (13% solution in PGMEA), 5.2 g (20% solution in PGMEA) of c rosslinker V-1 , 3.25 of TAG C solution and 70.Og of PGMEA are mixed. The mixture is then rolled overnight, and the undercoat solution is filtered through a 0.20μm filter.

[0143] Lithographic Example 25

The undercoat from Undercoat Formulation Example 33 is lithographically tested using the procedure employed in Lithographic Examples 1-4. The resultant 140 nm features have good resolution with excellent adhesion.

[0144] Undercoat Formulation Example 34

For 5Og of undercoat solution in a 2 oz amber bottle, 30.39 of the polymer prepared in Synthesis Example 14 (13% solution in PGMEA), 1.3 g (20% solution in PGMEA) of crosslinker V-10, 0.82 of TAG F solution, and 17.5 of PGMEA .The mixture is then rolled overnight, and the undercoat solution is filtered through a 0.20μm filter.

[0145] Lithographic Example 26

The undercoat from Undercoat Formulation Example 34 is lithographically tested using the procedure employed in Lithographic Examples 15-24. The resultant 120 nm features have good resolution with excellent adhesion.

[0146] While the invention h as b een described herein with reference to the specific embodiments thereof, it will be appreciated that changes, modification and variations can be made without departing from the spirit and scope of the inventive concept disclosed herein. Accordingly, it is intended to embrace all such changes, modification and variations that fall with the spirit and scope of the appended claims.