The present invention relates to the use of a component based on 1,3-dioxane compounds, especially 1,3-dioxane alcohols, and derivatives thereof in lubricant and release agents. This invention also relates to a lubricant and release agent based on or containing 1,3-dioxane compounds as above.

Lubricant and release agents are normally used in connec¬ tion with metal cutting, tapping, threading, reaming etc. as well as for concrete casting. Further and frequent application areas include utensils and plants for refri¬ geration, air conditioners, jet and conventional combustion engines, hydraulic fluids and the like.

Above exemplified application areas most often involve lubricant and release agents based on or containing mineral oils and one or more property adjusting additives such as EP-additives (EP = Extreme Pressure). EP-additives are mostly based on chloric, sulphuric and/or phosphatic compounds of the paraffin type.

Products containing mineral oils give rise to oil mist with pendant oil-polluted air and oil coated equipments in and around a working area. Mineral oils and for instance EP- additives are furthermore known to cause skin irritation, eczema and/or allergic reactions. Carcinogenic effects can not be excluded, as most mineral oils contain for example aromatic hydrocarbons of the benzopyrene type, which compounds at high working temperatures most probably form carcinogenic polyaromatics.

Mineral oils as well as chloric, sulphuric and/or phosphatic compounds give also rise to undesirable ecological effects,

such as gradual concentration of undesired compounds like chlorine, sulphur and/or phosphorous in soil and water. Furthermore, mineral oils are not or only to a very low extent biodegradable, while the component according to the invention per se is biodegradable and based on bio¬ degradable substances.

Mineral oils have per se a limited lubricating and releasing power, why a number of additives must be admixed. Besides property adjusting additives must for instance waterborne emulsions of mineral oils and synthetic lubricants comprise compounds such as emulsifiers and biocides, which compounds may irritate the skin and/or the respiratory passage.

According to the present invention, it has surprisingly been possible to solve above discussed problems by a replacement of mineral oils and/or property adjusting additives with a component based on 1,3-dioxane compounds and/or derivatives thereof.

The lubricating properties have furthermore been improved by utilisation of the component as additive in lubricant and release agents. An addition is performed without any gurther alteration of the original composition. A suitable addition level is 0.1-20% by weight, preferably 0.5-10% by weight, calculated on included active substances.

The component is of the general formula

^R 1\ / ^R 2

O O

^N CH

in which formula R- is -H, -OH, -CH ₃ , -C ₂ H ₅ , ~ ^CH 2 ^OR 3\' -CH ₂ 0 ₍ C ₂ H ₄ 0) _n R ₃ , -CH ₂ 0(C ₃ H ₆ 0) _n R3, -C^O^HgO)^, -CH ₂ 0(C ₈ H ₈ 0 _)n R ₃ , -CH ₂ 0 ₍ R ₅ ) _m (R ₆ ) _p R ₃ or -CH ₂ OR _? and R ₂ is -H, -OH, -OR ₄ , -0(C ₂ H ₄ 0) _n R ₄ , -0(C^gO)^, -O^HgO)^, -0(C ₈ H ₈ 0) _n R ₄ , -CH ₂ OR ₄ , -CH ₂ 0(C ₂ H ₄ 0) _n R ₄ , -CH ₂ 0(C ₃ H ₆ 0) _n R ₄ , -CH ₂ 0(C ₄ H ₈ 0) _n R ₄ , -CH ₂ 0(C ₈ H ₈ 0) _n R ₄ , -0(R ₅ > _m 6 ) _p -CH ₂ 0 ₍ R ₅ ) _ra (R ₆ ) _p R ₄ , -OR _? or -CH ₂ OR ₇ .

R_ and/or R. is each independently selected from any of the below groups:

(i) hydrogen;

(ii) an alkyl moiety;

(iii) a substituted alkyl moiety;

(iv) an alkenyl moiety;

(v) a substituted alkenyl moiety;

(vi) a cycloalkyl moiety;

(vii) a substituted cycloalkyl moiety;

(viii) a cycloalkenyl moiety;

(ix) a substituted cycloalkenyl moiety;

(x) an aryl moiety;

(xi) a substituted aryl moiety;

(xii) an aralkyl moiety, an alkaryl moiety, an aralkenyl moiety and/or an alkenaryl moiety.

R5 _c and R6 _c are two different substituents of the formula CxHy0 wherein x is 2, 3, 4 or 8 and y is 4, 6 or 8.

0

II R ₇ is defined by the general formula -C-NH-R _β in which the substituent R _g is selected from any of the groups (ii) through

(xii).

The mean value n for n is 1-60, preferably 1-20, the mean

values m for m and p for p is 1-59, preferably 1-19 and the sum of the mean values m and p is 2-60, preferably 2-20.

According to one embodiment of the invention, R.. and/or R„ is hydroxyl. In such an embodiment of the invention, the used component is a 1,3-dioxane alcohol, such as 1,3-dioxane-5-ol, 5-ethyl-l,3-dioxane-5-methanol, 1,3-dioxane-5,5-dimethanol and/or adducts thereof with for instance ethylene oxide, propylene oxide, butylene oxide and/or styrene oxide. One or more of the carbon atoms in the 1,3-dioxane ring can, furthermore, be methyl, ethyl, butyl, propyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, ethenyl, butenyl, propenyl, pentenyl, hexenyl, heptenyl, octenyl, nonenyl, decenyl, undecenyl and/or dodecenyl substituted.

The component is in above embodiment used as 100% product or in diluted form and is employed as sole constituent or as additive in a lubricant or release agent. The component can as additive suitably comprise 1-80% by weight, preferably 40-80% by weight, calculated on the total formulation.

In a further embodiment, R, and R ₄ are each independently selected from any of the groups (ii) through (xii) preferably derived from one or more carboxylic acids having 1-6 carboxyl groups and 1-24 carbon atoms, such as abietic acid, acetic acid, behenic acid, benzoic acid, p-tert.butylbenzoic acid, butyric acid, castor fatty acid, dehydrated castor fatty acid, capric acid, caproic acid, caprylic acid, coconut fatty acid, cottonseed fatty acid, crotonic acid, 2-ethylhexanoic acid, formic acid, groundnut fatty acid, heptanoic acid, lauric acid, li\'canic acid, linoic acid, linolenic acid, montanoic acid, myristic acid, nonanoic acid, isononanoic acid, oleic acid, palmitic acid, propionic acid, ricinoleic acid, soybean fatty acid, stearic acid, isostearic acid, tall oil fatty acid, tallow fatty acid, valeric acid, adipic acid, azelaic

acid, fumaric acid, maleic acid or its anhydride, phthalic acid or its anhydride, isophthalic acid, tetrahydrophthalic acid or its anhydride, hexahydrophthalic acid or its anhydride, sebacic acid, succinic acid or its anhydride, citric acid, trimelletic acid or its anhydride, pyromelletic acid or its dianhydride and/or a mixture of two or more of these acids or anhydrides.

Embodiments in which R_ is defined by the general formula

the component according to the invention comprises a reaction product and/or a derivative thereof derived from for instance a 1,3-dioxane alcohol as previously exemplified and at least one isocyanate having the general formula 0=C=N-R _g . R„ is in these embodiments preferably defined by having 4-48, most preferably 8-24 carbon atoms.

In yet a further embodiment R ₃ and/or R ₄ is each independently a group of the formula

^-R 9-

- Ϊ- ^R lθ ^(C 4 ^H 8 ⁰ >q ^{and θr} - ^R 9-ϊ- ^R lθ ^(C 8 ^H 8° ⁾ q 0 0

wherein the mean value q for q is 1-60, preferably 1-20 and R _q is selected from any of the groups (ii) through (xii) preferably derived from one or more carboxylic acids having 2-6 carboxyl groups and 4-10 carbon atoms, such as adipic acid, azelaic acid, fumaric acid, maleic acid or its anhydride, phthalic acid or its anhydride, isophthalic acid, tetrahydrophthalic acid or its anhydride, hexahydrophthalic

acid or its anhydride, sebacic acid, succinic acid or its anhydride, citric acid, trimelletic acid or its anhydride, pyromelletic acid or its dianhydride and/or a mixture of two or more of these acids and R-, _ is hydroxyl or selected from any of the groups (ii) through (xii) derived from one or more alcohols having 1-8 hydroxyl groups and 1-24 carbon atoms, such as methanol, ethanol, butanol, isobutanol, propanol, isopropanol, pentanol, hexanol, octanol, 2-ethylhexanol, ethoxyethanol, cetyl alcohol, trimethylol- propane diallyl ether, pentaerythritol triallyl ether, glycerol diallyl ether, l,3-dioxane-5-ol, cyclohexane- dimethanol, 5-ethyl-l,3-dioxane-5-methanol, 1,3-butanediol, 1,4-butanediol, 1,6-hexanediol, pentanediol, neopentyl glycol, hexylene glycol, 2-methyl-l,3-propanediol, 2-methyl-2-ethyl- 1,3-propanediol, 2-methyl-2-butyl-l,3-propanediol, 2-ethyl- 2-butyl-l,3-propanediol, trimethylpentanediol, trimethylol- propane monoallyl ether, pentaerythritol diallyl ether, glycerol monoallyl ether, l,3-dioxane-5,5-dimethanol, glycerol, trimethylolethane, trimethylolpropane, penta¬ erythritol monoallyl ether, pentaerythritol, ditrimethylol- propane, dipentaerythritol, tripentaerythritol, sorbitol and/or a mixture of two or more of these alcohols.

In alternative embodiments, R_, R ₄ , R _g and/or R- ~ is each independently selected from any of the groups (ii) through (xii) preferably derived from one or more hydroxycarboxylic acids having 1-3 carboxyl groups, 1-4 hydroxyl groups and 2-24 carbon atoms, such as dimethylolpropionic acid and hydroxypivalic acid. R ₃ and/or R. can also be selected from group (xii) wherein the alkyl moiety derived from one or more glycidyl esters of monofunctional carboxylic acids having 1-24 carbon atoms or each independently be selected from any of the groups (ii) through (xii) derived from one or more α-epoxides having 5-24 carbon atoms.

In embodiments of the component holding one or more unreacted carboxyl groups these groups can, in order to obtain a water dilutability, be neutralised with a suitable basic compound such as ammonia, an amine, a hydroxide or the like. Ammonia or an amine such as monoethanol amine, diethanol amine, tri- ethanol amine, N,N-dimethylethanol amine, N,N-dimethylamino- methylpropanol, aminomethylpropanol, triethyl amine and/or morpholine are preferred neutralising agents.

Advantages obtained by the present invention include improved working conditions, which conditions are improved through a replacement of mineral oils and/or additives, whereby the skin irritating, allergic and/or eczema producing properties of these compounds are eliminated or reduced. Furthermore, problems caused by oil mist and oil coating can be avoided or reduced by selecting the substituents R ₁ - R. _fi in such a way within the scope of the claims that a reduced vola¬ tility, compared to normally used mineral oils, is obtained. The ecological disadvantages of using mineral oils and for instance chloric, sulphuric and/or phosphatic additives and the like are, due to the biodegradability of the component according to the invention as well as due to the fact that the component does not contain chloric, sulphuric and/or phosphatic substances, avoided.

Further advantages obtained by using the component according to the invention include improved and excellent lubricating power, excellent thermal stability and excellent solubility in most organic media.

The component according to the present invention can suitably be utilised as additive to compositions as disclosed in the American patent 4,405,471 and the European patent application 89 913 158.5 or replace components included in said composi¬ tions. Esters forming part of a lubricating fluid as described in for instance Examples 8-14 of above American patent and

Examples 8-12 of above European patent application can be combined with or wholly and/or partly replaced by esters prepared from one or more 1,3-dioxane alcohols and/or deri¬ vatives thereof such as alkoxylated 1,3-dioxane alcohols and one or more suitable acids, ^" as previously disclosed, which esters possibly have been neutralised with a suitable amine or the like.

The invention will be further explained in connection with enclosed examples in which some preferred embodiments of the invention are disclosed as follows:

Example 1: Preparation of 5-ethyl-l,3-dioxane-5-methanol used as final or intermediate product according to the invention.

Examples 2 and 3: Preparations of onoesters of 5-ethyl-l,3- dioxane-5-methanol used as final or inter¬ mediate product according to the invention.

Examples 4-6: Evaluations of lubricant agents, cutting fluids, containing esters prepared according to Examples 2 and 3.

Examples 7 and 8: Evaluations of the lubricating power of the products obtained according to Examples 1 and 2.

Example 9: Evaluation of release agents in concrete casting. The release agents are based on products obtained according to Examples 1 and 3 and are compared with a commercial release agent.

The present invention is not limited to disclosed embodiments. The component according to invention as well as its properties

can be varied within the scope of the claims by selecting the substituents R. - R- _Q to comply with particular requirements.

EXAMPLE 1

3.0 moles of trimethylolpropane, 3.6 moles of paraformaldehyde (94%) and 0.40 g of paratoluene sulphonic acid were charged and mixed in a 4-necked reaction flask equipped with a nitrogen inlet, a stirrer and a cooler provided with a water-trap (Dean-Stark) . The mixture was under stirring heated to 130°C and kept at this temperature for 60 minutes. Obtained reaction product was neutralised with powdered sodium hydroxide and thereafter vacuum distilled using a short Vigreaux column, which distillation resulted in the following fractions:

Fraction I and II, colourless or slightly yellowish liquids, were mixed and analytically determined to be 5-ethyl-l,3- dioxane-5-methanol having the following properties:

EXAMPLE 2

1.70 mole of 5-ethyl-l,3-dioxane-5-methanol (obtained in Example 1), 1.615 mole of oleic acid (Edinor Ti05, Henkel KGaA, Fed. Rep. of Germany), 3.5 g of trisnonylphenyl phosphite (antioxidant) and 21 g of xylene (azeotropic solvent) were charged and mixed in a 4-necked reaction flask equipped with a nitrogen inlet, a stirrer and a cooler provided with a water-trap (Dean-Stark) . The temperature was raised to 120°C, whereupon 1.4 g of zinc powder (esterifi- cation catalyst) was added. The temperature of the reaction mixture was now raised to 230°C and maintained until an acid value of less than 2 mg KOH/g was obtained, whereupon the remaining xylene was evaporated at a vacuum of 15 mm Hg. The resulting product was cooled to room temperature, a filter aid (Celite) was added in an amount of 2% and the product was filtered to remove organozinc compounds.

Obtained monoester of 5-ethyl-l,3-dioxane-5-methanol and oleic acid, exhibited the following properties:

Acid value: 1.9 mg KOH/g

Hydroxyl value: 7 mg KOH/g

Viscosity at 23°C: 47 mPas

Colour value: 4-5 Gardner

EXAMPLE 3

2.40 moles of 5-ethyl-l,3-dioxane-5-methanol (obtained in Example 1), 2.28 moles of caprylic-capric acid (C ₈ -C. _Q acids, Karlshamns AB, Sweden), 3.5 g of trisnonylphenyl phosphite (antioxidant), 21 g of xylene (azeotropic solvent) and 0.7 g of an esterification catalyst (Fascat 4100, M&T Chemicals B.V., The Netherlands) were charged and mixed in a 4-necked

reaction flask equipped with a nitrogen inlet, a stirrer and a cooler provided with a water-trap (Dean-Stark) . The temperature of the reaction mixture was raised to 230°C and maintained until an acid value of less than 0.5 mg KOH/g was obtained. The remaining xylene was thereafter evaporated at a vacuum of 15 mm Hg and a temperature of 180°C and the resulting product was cooled to room temperature.

Obtained monoester of 5-ethyl-l,3-dioxane-5-methanol and caprylic-capric acid, exhibited the following properties:

Acid value: 0.3 mg KOH/g

Hydroxyl value: 13 mg KOH/g

Viscosity at 23°C: 31 mPas

Colour value: 1-2 Gardner

EXAMPLE 4

1.5% by weight of 5-ethyl-l,3-dioxane-5-methanol (obtained in Example 1) was added to a commercially available mineral oil based cutting fluid (Peralub 6000, Perstorp AB, Sweden) having a mineral oil content of 23% by weight. The two cutting fluids, the commercially available (Sample 1) and the 5-ethyl- l,3-dioxane-5-methanol modified (Sample 2), were diluted with water to an utility concentration of 5% by weight.

The two cutting fluids were evaluated by tapping in aluminium. The amount of aluminium adhering to the tap were visually determined and the result was used as a basis for grading the lubricating properties.

A grading of 1-5 was used, wherein:

1 = Poor lubricating properties - A large amount of aluminium adheres to the tap. 5 = Excellent lubricating properties - A very small amount or no aluminium adheres to the tap.

The following results were obtained:

Grading Sample 1: 3 Sample 2: 5

Above grading indicates that a small addition of 5-ethyl-l,3- dioxane-5-methanol, without any alteration of other included constituents, results in substantially increased lubricating properties.

EXAMPLE 5

Example 4 was repeated with the difference that 5-ethyl-l,3- dioxane-5-methanol was replaced by the monoester obtained in Example 2.

Sample 1 = Commercially available cutting fluid. Sample 2 = Monoester modified cutting fluid.

The following results were obtained:

Grading Sample 1: 3 Sample 2: 4

Above grading indicates that a small addition of the mono¬ ester of oleic acid and 5-ethyl-l,3-dioxane-5-methanol, without any alteration of other included constituents, results in increased lubricating properties.

EXAMPLE 6

Example 4 was repeated with the difference that 5-ethyl-l,3- dioxane-5-methanol was replaced by the monoester obtained in Example 3.

Sample 1 = Commercially available cutting fluid. Sample 2 = Monoester modified cutting fluid.

The following results were obtained:

Grading Sample 1: 3 Sample 2: 4

Above grading indicates that a small addition of the monoester of caprylic-capric acid and 5-ethyl-l,3-dioxane-5-methanol, without any alteration of other included constituents, results in increased lubricating properties.

EXAMPLE 7

1.5% by weight of 5-ethyl-l,3-dioxane-5-methanol (obtained in Example 1) was added to a commercially available mineral oil (Nyflex 810, Nynas Petroleum AB, Sweden). The specific surface pressure was, for the two samples, determined according to the German V K I S Arbeitsblatt 6 of June 1975. A high specific surface pressure indicates a high lubricating

power with pendant reduced abrasion of equipment such as taps, drills, cutters and the like.

Sample 1: Commercially available mineral oil.

Sample 2: 5-ethyl-l,3-dioxane-5-methanol modified mineral oil.

The following results were obtained:

Specific Surface Pressure

Sample 1: 10 N/mm 2

Sample 2: 20 N/mm ²

Above results give at hand that a small addition of 5-ethyl- 1,3-dioxane-5-methanol to a mineral oil highly increases its lubricating power.

EXAMPLE 8

Example 7 was repeated with the difference that 5-ethyl-l,3- dioxane-5-methanol was replaced by the monoester obtained in Example 2.

Sample 1: Commercially available mineral oil. Sample 2: Monoester modified mineral oil.

The following results were obtained:

Specific Surface Pressure Sample 1: 10 N/mm ²

Sample 2: 25 N/mm . ^: 2

Above results give at hand that a small addition of the mono¬ ester of oleic acid and 5-ethyl-l,3-dioxane-5-methanol to a mineral oil highly increases its lubricating power.

EXAMPLE 9

A commercially available release agent (Lasol MlOO, Byggekemi i Nol AB, Sweden) based on mineral oil was evaluated in com¬ parison with two embodiments of the invention

Sample 1: A mixture of 40 g of 5-ethyl-l,3-dioxane-5-methanol (obtained in Example 1) and 60 g of water.

and

Sample 2: The monoester (obtained in Example 3) of caprylic- capric acid and 5-ethyl-l,3-dioxane-5-methanol

according to the following method:

- A release agent is sprayed onto the inner side of a cubic steel cast, in which a cube of ordinary concrete, containing Standard Portland cement, is casted. The cube is after 24 hours released from the cast and a visual inspection with regard to adhering concrete is performed on the interior of the cast. The concrete cube is visually inspected with regard to surface roughness, hardness and blistering.

The amount of adhering concrete and the appearance of the surface of the concrete cube are bases for grading the release agent. The surface should be free from blisters, even and hard, while the interior of the cast should be free from adhering concrete.

A grading of 1-3 is used, wherein:

1 = Not approved 3 = Approved

The following results were obtained:

Grading Commercial release agent: 3 Sample 1: 3

Sample 2: 3

Above results show that the environmentally more suitable component according to the invention, can replace a mineral oil based release agent without deterioration of the technical properties.