BACI9GROUND ART The morphology of cross-linked multi-vesiculated polyester particles described in prior art consist of largely spherical hollow particles with multiple air voids in the dry state.

These particles re-absorb water in paints and coatings, are difficult to manufacture and their particle size control is limited to processing variables such as temperature, speed of agitation and process time.

It is an object of this invention to provide cross-linked polyester particles whose morphology is largely spherical with multiple air voids that hinder the re-entry and re-absorption of water when the cross-linked particles are dry.

It is a further object of the invention to provide a conversion process of the raw materials composition which permits cross-linked particle size and distribution control through process variables such as temperature, rate of agitation and processing time as well through the concentration of modifying co-monomer in the raw material composition and the optimization of the process stage for adding this co-monomer to the said composition.

It is yet a further object of this invention to provide a vesiculated polymer particle which may be used in paint and coatings formulations for the beneficial replacement of titanium dioxide pigments, expensive extenders, emulsion polymers, open time modifiers such as glycols and humectants with simultaneous achievement of improved opacity, whiteness, scrub resistance, water resistance and special faux finish effects.

DISCLOSURE OF THE INVENTION According to the invention, vesiculated polymer particles include particulate solids and have associated with the surfaces thereof, long chain aliphatic chemical groups and/or sterically hindered, branched chained chemical groups.

In the one form of the invention, the chemical groups are hydrophobic and comprise organic compounds with at least one polymerisable carbon-carbon double bond with linear, branched or cyclic moeities having at least four carbon atoms, including but not limited to: Glycidyl methacrylate; Octadecene; Lauryl methacrylate ; Ethylene glycol di methacrylate (EGDMA); Cyclohexene; Acrylated castor oil; Acrylated ricinoleic acid; Methacrylated ricinoleic acid; Hydroxy-ethyl acrylate; Soya Bean Oil; Unsaturated fatty acids, e. g. Oleic acid, tallow fatty acid; Unsaturated fatty alcohols, e. g. Oleyl alcohol, pentadeca-12-ene-1-ol. ; Oleamide; Triglycerides, e. g. tall oil, ting oil ; 0 Ethylenic unsaturated urethanes; Acrylic unsaturated urethanes; Air drying short oil alkyds; Alkyl and Aryl Esters of maleic anhydride, singly or in combination.

In this description, the term associated may refer to groups included in the polymer particles or applied to the surface or portions of the surface thereof.

According to a second aspect of the invention, a raw material composition for manufacture of vesiculated particles includes a carboxylic acid functional, free-radical polymerizable polyester resin, a co-reactive diluent monomer and a modifying co-monomer, the modifying co-monomer including at least one polymerisable carbon-carbon double bond with linear, branched or cyclic moeities having at least four carbon atoms, including but not limited to: Glycidyl methacrylate; Octadecene; Lauryl methacrylate; Ethylene glycol di methacrylate (EGDMA) ; Cyclohexene; Acrylated castor oil Aorylated riaingleie said; Mathacrylatest ricinoleic acid; Hydroxy-ethyl acrylate; Soya Bean Oil ; Unsaturated fatty acids, e. g. Oleic

acid, tallow fatty acid; Unsaturated fatty alcohols, e. g. Oleyl alcohol, pentadeca-12-ene-1-ol. ; Oleamide ; Triglycerides, e. g. tall oil, ting oil; Ethylenic unsaturated urethanes; Acrylic unsaturated urethanes; Air drying short oil alkyds; Alkyl and Aryl Esters of maleic anhydride, singly or in combination.

The modifying co-monomer may comprise between 3 and 20% by mass of the added or reactive diluent monomer, and preferably comprises between 5 and 9% by mass of the added diluent monomer. This excludes the diluent monomer present in the polyester resin.

Suitable diluent co-monomers comprise ethylenic, acrylic and methacrylic functional monomers for example styrene, butyl acrylate, methyl methacrylate and preferably styrene.

In one form, the polyester resin composition comprises Propylene glycol 30,35% Phthalic anhydride 12.96% Maleic anhydride 25.75% Styrene 30.75% Inhibitor (10% solution) 0. 18% TOTAL 100,00 According to a third aspect of the invention, a method of manufacture of the vesiculated particles includes the steps of - pre-dispersing pigment particles in a polyester; - dissolving the pre-dispersed pigment-polyester in a suitable monomer in the presence of a water-soluble base; - forming a stable emulsion of droplets of solution of the pre-dispersed pigment-polyester and monomer (oil phase) in water; - adding a hydrophobic monomer and polymerising the polyester and co-polymerisable monomer thereby producing granules of opaque, cross-linked vesiculated particles as a

dispersion in water, the particles including hydrophobic groups associated with their surfaces.

In one form, the base may comprise a polyamine, for example diethylenetriamine.

Particles of various sizes may be manufactured using different mixers with different mixing intensity when emulsifying the polyester in water. In one form of the invention, suitably designed equipment controlling pressure, temperature, and residence time, for example homogenisers, may be used. Chemical control of particle size and particle size distribution is also effected by the introduction of long chain aliphats or sterically hindered, branched, chained co-monomers.

As most of these monomers or macro-monomers when incorporated into vesiculated polymer particles coarsen the average particle size, it was found preferable to add it at a later stage during emulsification of the organic phase in the water phase. This minimsed the effect on particle size. The coarser particle size versions can however be used to impart special effects in paint e. g. texture.

The modified vesiculated polymer particles when incorporated into paint systems had the effect of improving water resistance, abrasion resistance, whiteness and opacity.

EXAMPLES The following examples are intended to illustrate the invention, but are not presented as limitations on the scope of the invention.

Example 1 The following vesiculated polymer particles were synthesized as per prior art. Parts by Weight Stage 1 Polyester 14,99 Titanium Dioxide 0,86 Styrene 6,54 Diethylene Triamine 0, 21 Stage 2 Polyvinyl alcohol solution (10%) 13,28 Hydroxy Ethyl cellulose solution (2. 5%) 10,45 Water 52,92 Diethylene Triamene 0,06 Stage 3 Water 0,21 Ferrous Sulphate 0,01 Curnene Hydroperoxide 0,12 Stage 4 Bacteriacide 0, 35 100,00

Procedure 1. The Titanium Dioxide is dispersed in the polyester at high speed in a high shear mixture.

2. Styrene and Diethylene Triamine is added to 1) above at low speed.

3. Stage 2 is prepared in a separate vessel at low speed.

4. Stage 1 (organic phase) is added to Stage 2 at high speed on a high shear mixture and stirred until the desired particle size of the organic phase is obtained.

5. Stage 3 is then added at low shear by firstly pre-mixing the Ferrous Sulphate and water and then added. This is followed by adding the Cumene Hydroperoxide.

6. The stirrer is stopped and the product is left undisturbed to cure overnight.

7. The vesiculated particles are then stirred until homogenous and a suitable bacteriacide is added.

A fluid white dispersion of cross-linked polymer particles is obtained in water which on drying forms non-film forming particles with multiple air voids present.

Average particle size will vary depending on the stirring intensity used when adding Stage 1 to Stage 2.

Example 2 As per Example 1 but 0, 1% of the Styrene was replaced with Lauryl Methacrylate.

Stirring conditions as per Example 1.

Example 3 As per Example 1 but 3% of the Styrene was replaced with Lauryl Methacrylate. Stirring conditions as per Example 1.

Example 4 As per Example 1 but 5% of the Styrene was replaced with Lauryl Methacrylate. Stirring conditions as per Example 1.

Example 5 As per Example 1 but 7% of the Styrene was replaced with Lauryl Methacrylate. Stirring conditions as per Example 1.

Example 6 As per Example 1 but 9% of the Styrene was replaced with Lauryl Methacrylate. Stirring conditions as per Example 1.

Example 7 As per Example 1 but 20% of the Styrene was replaced with Lauryl Methacrylate. Stirring conditions as per Example 1.

Example 8 The vesiculated particles produced in the above examples 1 to 7 were measured for the following properties: 1. Total solids content using a Mettler HR73 halogen moisture analyzer.

2. Viscosity using a Brookfield LVT viscometer.

3. pH using a Metrohm 744 pH meter.

4. Specific gravity using a Sheen 100cc"weight per gallon"cup.

5. Opacity using Leneta form 2A opacity charts and Sheen micropac reflectometer.

6. Whiteness using BYK-Gardner color-view spectrophotometer.

7. Average particle size using a scanning electron microscope (Topcon & Scion image analysis software).

Results as follows: Vesiculated Particles Manufactured on Variable Shear Cowles Mixer LMA Solids, Viscosity, pH S. G. Opacity Whiteness Average % % cps Particle Size, microns 0 23. 50 800 6. 78 1. 043 0. 93 94.0 5.6 0.1 23.80 610 6.66 1.044 0.96 96.7 6.1 3 23. 90 1200 6.50 1.044 0.96 96.1 6.9 5 23. 63 1250 6.55 1.046 0. 95 96. 4 7. 5 7 23. 7 3720 6.74 1.042 0.96 97.0 8.3 9 23.46 3900 6.75 1.044 0.95 95.4 16.0 20 23. 67 14800 6. 73 1.033 0.88 94.5 36.5 The improvement in opacity and whiteness is clearly illustrated as well as the effect of increase particle size.

Example 9 The vesiculated polymer particles from Example 1 to 7 were formulated into the following mixture to produce water based emulsion paint: RAW MATERIAL PARTS BY WEIGHT Vesiculated Particles 77.5 Styrene Acrylic Emulsion Polymer 9.7 Coalescent 1.1 Ammonia (Diluted 1: 1 with water) 1 Titanium Dioxide Aqueous Dispersion 9.7 Thickener 1 The paints obtained by using the vesieulated partieles from Framoles 107 in the parmple were tested for wet scrub (abrasion) resistance and the following results recorded:

1. Paint using Vesiculated Particles from Example 1 = 20 cycles 2. Paint using Vesiculated Particles from Example 2 = 120 cycles 3. Paint using Vesiculated Particles from Example 3 = 500 cycles 4. Paint using Vesiculated Particles from Example 4 = 1100 cycles 5. Paint using Vesiculated Particles from Example 5 = 1500 cycles 6. Paint using Vesiculated Particles from Example 6 = 900 cycles 7. Paint using Vesiculated Particles from Example 7 = 600 cycles The higher wet scrub cycles indicate better scrub and abrasion resistance in the final paint . The results confirm the improvements in water and scrub resistance obtained by using the compositions of this invention in paints and coatings.

Example 10 Repeat of Example 4 but using Octadecene instead of Lauryl Methacrylate. Stirring conditions as per Example 1.

Example 11 Repeat of Example 4 but using Acrylated Methyl Ricinoleate instead of Lauryl Methacrylate. Stirring conditions as per Example 1.

Example 12 Repeat of Example 4 but using Methacrylated Ricinoleate instead of Lauryl Methacrylate.

Stirring conditions as per Example 1.

Example 13 The vesiculated polymer particles from Examples 10,11 and 12 were measured for properties as above in Example 8.

Results as follows: Vesiculated Particles Manufactured on Variable Shear Cowles Mixer Example Solids, Viscosity, pH S. G. Opacity Whiteness Average % cps Particle Size, microns 10 23. 39 10000 6. 56 1. 045 0. 95 95. 0 17 11 23. 48 1800 6.72 1.043 0. 96 95.4 9 12 23. 50 1900 6.47 1.045 0.96 95.2 9

Example 14 The vesiculated polymer particles from Example 10,11 and 12 were formulated into water-based paint as per Example 9 and tested for wet scrub (abrasion) resistance.

1. Paint using vesiculated particles from Example 1 = 20 cycles.

2. Paint using vesiculated particles from Example 10 = 500 cycles.

3. Paint using vesiculated particles from Example 11 = 1000 cycles.

4. Paint using vesiculated particles from Example 12 = 1200 cycles.

The results confirm the improvements in water and scrub resistance obtained by using the compositions of this invention in paints and coatings.

Example 15 The water resistance and whiteness of paint containing: Vesiculated particles synthesized using prior art technology (Example 1).

Vesiculated particles synthesized using the present patent technology (Example 4). were compared. The paint is of medium quality and suitable for both interior and exterior use.

The following are the results obtained. Paint A B Vesiculated Particles from (Example 1) (Example 4) Water resistance Water droplet method (l) 5 min 10 min. Wet abrasion resistance (2) 1280 cycles 2198 cycles Colour D10° (against Std) P) - 0.28 D -0, 51 D A-0. 06 G-0. 10G B 1. 09Y 0.43 Y DE CMC 1. 41 0. 63

(1) Water resistance by this method is done by subjecting a paint film which has been dried at ambient temperature for 24 hours to water droplets on the surface of the paint. The time taken for blistering or softening of the paint in contact with the water droplet is recorded. The longer the time the better the water resistance. The test is stopped after 10 minutes.

(2) Wet abrasion resistance is done by the attached method. The higher the number of cycles, the better the wet abrasion resistance.

(3) Colour is measured on a colour computer and compared to the paint containing vesiculated particles from example 1.

The L value if positive indicates lightness difference and if negative the darkness difference. Paint B is slightly darker than Paint A.

The A value if positive indicates redness difference and if negative, the greenness difference. Paint B is very slightly greener than Paint A.

The B value if positive indicates the yellowness difference and if negative, the blueness difference. Paint B is less yellow than Paint A and thus whiter.

The DE CMC is the overall difference in colour. Paint B has less overall colour change than Paint A.

Example 16 Vesiculated particles (i. e. Example 1 and Example 4) were formulated into the following waterbased paints: - Medium quality interior/exterior paint.

- High quality interior matt paint - Effects paint The properties of the paints were evaluated.

Listed below are the paint formulations and the test results: Example 17 Vesiculated particles were synthesized as per Example 1 and Example 4.

The vesiculated particles were applied to a black and white opacity chart by means of a 200mm drawdown bar.

The opacity (i. e. obliterating power) was measured over the black and over the white portions of the opacity chart by means of a reflectometer. The resultant reflectance measurement over the white is divided into the reflectance measurement over the black.

Results as follows: Example 1 Example 4 Opacity 0, 93 0, 95 The higher the figure the greater the obliterating power of the vesiculated bead.

High Quality Matt Interior/Exterior Paint Paint A Paint B Water 28. 11 28.11 Dispersant 0.24 0.24 Titanium Dioxide 7.90 7.90 Calcium Carbonate (2 micron) 21.82 21. 82 Calcium Carbonate (5 micron) 8.11 8.11 Propylene Glycol 1.02 1.02 Anionic Surfactant 0.09 0.09 Defoamer 0.31 0.31 Hydroxy Ethyl Cellulose 0.33 0.33 Ammonia 0.11 0.11 Styrene/Acrylic Emulsion (50% solids) 17. 20 17.20 Coalescent 1.66 1.66 Bacteriacide 0.21 0.21 Vesiculated Particles (Example 1) 12. 91 Vesiculated Particles (Example 2)-12. 91 TOTAL. 100. 0 100. 0 RESULTS Paint A Paint B Water resistance * Water droplet method 8 10 Wet abrasion resistance >10,000 >10,000 Opacity 0. 88 0.92 Whiteness (l) 79. 57 81. 06 Note : Paint B is more water resistant, higher opacity and whiter than Paint A. (1) Whiteness is measured on a colour computer. The higher the figure the whiter the paint.

High Quality Matt Interior Paint Paint A Paint B 1. Titanium Dioxide dispersion 21.32 21.32 2. Talc dispersion 19.07 19.07 3. Thickener 0.29 0.29 4. Water 2.02 2.02 5. Ammonia 0.24 0.24 6. Propylene Glycol 0.77 0.77 7. Coalescent 1.345 1.345 8. Defoamer 0.25 0.25 9. Dispersant 0.19 0.19 10. Bacteriacide 0.10 0.10 11. Pure acrylic Emulsion (48% solids) 39.55 39. 55 12. Thickener (for low shear) 0. 15 0. 15 13. Thickener (for high shear) 0.29 0.29 14. Water 2.95 2.95 15. Vesiculated particles (') 11. 51 16. Vesiculated particles (2) 11. 51 TOTAL 100.0 100.0

RESULTS Paint A Paint B Water resistance Water droplet method 8 10 Wet abrasion resistance >10,000 >10,000 Opacity 92.8 95.1 Whiteness 78. 23 82. 14

Note: Paint B is more water resistant, higher opacity and whiter than Paint A.

(1) Vesiculated particles were manufactured to the particle size as per Example 1 and at 25 micron average particle size by adjusting the rate of agitation (2) Vesiculated particles were manufactured to the particle size as per Example 4 and at 25 micron average particle size Effects Paint Parts by Weight Paint A Paint B 1. Water 6.07 6.07 2. Propylene Glycol 1.79 1.79 3. Dispersant 0.11 0.11 4. Surfactant 0.18 0.18 5. Defoamer 0.09 0.09 6. Bacteriacide 0.05 0.05 7. Ammonia 0.10 0.10 8. Hydroxy Ethyl Cellulose 0.05 0.05 9. Pure Acrylic Emulsion (48% solids) 47.04 47.04 10. Coalescent 2.09 2.09 11. Vesiculated particles (') 39. 16 12. Vesiculated particleS (2)-39. 16 13. Thickener 1.23 1.23 14. Water 0.82 0.82 15. Colour tinter (s) 1. 22 1. 22 TOTAL 100. 0 100. 0 RESULTS

Paint A Paint B Suede EffectNoYes (1) Vesiculated particles were manufactured to the particle size as per Example 1 and at 25 micron average particle size by adjusting the rate of agitation (2) Vesiculated particles were manufactured to the particle size as per Example 4 and at 25 micron average particle size (3) The Suede Effect is an effect imparted to a paint to give a colour texture effect.

Paint B has superior Suede Effect than Paint A as vesiculated bead is more prominent on the surface due to low water absorption.