BACKGROUND OF THE INVENTION.

Elastomers, based on the condensation of a major proportion of thiodiethanol with one or more aliphatic diols containing a sulfur-vulcanizable double bond, are described by Aloia, U.S. Patent 3,951,927; Chang et al., U.S. Patent 3,985,708; Chang, U.S. Patent 4,000,213; and Li et al., U.S. Patent 4,028,305, all of which are incor¬ porated herein by reference. Heretofore, application of conventional sulfur vulcanization systems, e.g., sulfur, zinc oxide, benzothiazole sulfenamides, thiuram sulfides, mercaptobenzothiazole, and the like, to the vulcanization of these elastomers has been less than satisfactory. Zinc oxide has heretofore been considered to be essential to the vulcanization of unsaturated elastomers with sulfur. In the vulcanization of thiodiethanol-based elastomers of the invention, conventional sulfur-vulcanization systems containing zinc oxide result in a fast cure, but the vulcanized elastomers exhibit poor heat aging as manifested by high compression set and poor continuous stress-relaxation, However, when zinc oxide is omitted from the cure system, the cure rate is impractically slow. All of these factors indicate that there is a need for a vulcanization system to vulcanize thiodiethanol-based elastomers.

In order for an elastomer to achieve commercial success, it must be vulcanizable to useful products with an efficient, practical vulcanization system. It is an object of the invention to rovide useful vulcanized ---

products from thiodiethanol-based elastomers, and to pro¬ vide elastomers exhibiting significantly improved aged properties, such as compression set.

SUMMARY OF THE INVENTION

5 The present invention provides a novel vulcaniza¬ tion system for thiodiethanol-based elastomers, comprising sulfur and an aliphatic linear, branched chain or cyclic polyethyleneamine, or mixture thereof, or a dissociable organic salt thereof.

10 DESCRIPTION OF THE INVENTION

INCLUDING PREFERRED EMBODIMENTS The aliphatic linear, branched chain or cyclic polyethyleneamines which are useful in the vulcanization system of the present invention range from relatively

15 simple polyethyleneamines, which are represented by the formula:

H-t-HN—(CH2).2--NH2 (-

20 wherein n is an integer from 1 to about 10, to complex re¬ action products of ethylene dichloride and ammonia, which boil above the boiling point of diethylenetriamine (206.7°C to dissociable organic salts of polyethyleneamines produced by reaction thereof with acids having a dissociation consta

^{Δ ~ D~} lleessss tthhan about 10-3, or mixtures of any of the above mat- erials.

Polyethyleneamines representative of the above formula (I) includeΪ eth lenediamine

30 diethylenetriamine triethylenetetramine tetraethylenepentamine pentaethylenehexamine, and the like. The complex polyethyleneamine reaction mixtures 5 contain linear, branched chain and cyclic structures which include, for example, the following: /^ __~B~-~υr- ^' _> *

O'-

H2N-CH2CH2- H-CH2CH2- H-CH2CH2-NH-CH2CH2-NH-CH2CH2-NH2

Pentacthylenehexamine H2N-CH2CH2-NH-CH2CH2-N-CH2CH2- H-CH2CH2- H2

I -

CH2

I

CH2 ^" .

I . .

NH ₂ Symmetrical diaminoethyltriaminoethylamine H2N-CH2CH2-N-CH2CH2-NH-CH2CH2-NH-CH2CH2- H2

^" I ^■

CH ₂

I

CH2

I

NH ₂ Unsymmetrical diaminoethyltriaminoethylamine

Symmetrical diaminoethy1 riethylenetetramine

H2NOCH2CH2- H-CH2CH2-N N-CH2CH2- H-CH2CH2-NH2 Symmetrical diaminoethyldiaminoethyl piperazine

-CH2CH2- H-GH2CH2-NH-CH2CH2-NH2 Unsymmetrical diaminoethyldiaminoethyl piperazine

'SUBSTITUTE SHEET

Pipeτazinoethyl triethylene tetramine H2 -CH2CH2-N-CH2- H-CH2CH2- H2

1

CH2 ^:

I

CH ₂ •

I I

CH ₂ CH ₂

-

H 4-(N-pipeτazinoethyl)triethylene tetramine ^'

Bispiperazinoethylamine

Aminoethyl diperazinoethane In addition to the linear, branched chain and cyclic polyethyleneamines, organic salts thereof, which dissociate under vulcanization conditions to liberate the free amine, may also be used.

Useful organic salts are those which are formed from acids having a dissociation constant less than about lO""*- ¹ , and including salts of aliphatic carboxylic acids, especially those of 2-18 carbon atoms, carbonic.-, acid, carbamic acid and the like. Particularly useful salts are the fatty acid salts, e.g., the stearate. Useful salts also include the condensation products of polyethylene

SUBSTITUTE SHEET

amines and the aforementioned fatty acids, for example stearic acid, such as diethylenetriamine-stearic acid condensate.

The vulcanizable thiodiethanol-based elastomers useful in the present invention are preferably those dis¬ closed in the aforementioned patent to Aloia and Chang et al. C708). *

Specifically, the vulcanizable elastomers of thio¬ diethanol is a polymer represented by the formula: 0 (II) H - OGTmOH wherein -tOG}- comprises randomly alternating structural units selected from

(E) structural units (III) and (IV)

5 or (F) structural units (III), (IV) and (V)

(V) -FOR ¹ -} wherein R is one or more radicals remaining on removal of two hydroxyl groups from 0 (a) • Saturated aliphatic, linear, branched chain or cyclic diol ^' s, or (b) aliphatic linear, branched chain or cyclic diols containing external unsatu- ration having an allylic hydrogen atom, 25 wherein R' is one or more radicals which remain on removal of two hydroxyl groups from a diphenolic compound, said poly¬ mers comprising structural units (E) and (F) being characterized in that: ^■ ^- (1) m is an integer sufficient to provide in said polymer an average molecular weight of at least 8000; ^" (2) the molar ratio of (III) to (IV), when said polymer comprises structural ³⁵ units (E) , or the molar ratio of (III) to the total of (IV) and (V) when

polymer comprises structural units (F) , being not less than 1:1 and (3) they contain from about 1 to 10 mole percent of said diol (b) based on the total of all units (III), (IV) and (V) present in said polymer.

The vulcanization system o the invention comprises sulfur in an amount of from about 0.3 to 3.0 parts by weight per hundred parts of elastomer, preferably 0.3 to 2.0 parts, same basis. The polyethylene amine may be used in an amount of from about 1 to 6 parts thereof per 100 parts of elasto¬ mer, preferably from about 2 to 4 parts, same basis.

In addition to sulfur and the polyamine compound, the vulcanizable elastomer composition may contain other conventional rubber compounding ingredients, such as fillers and reinforcing agents, e.g., carbon black, precipitated hydrous silica, titanium dioxide, calcium carbonate, calcium silicate, and the like; calcium oxide or calcium stearate (or other fatty acid salt) to neutralize acid catalyst resi¬ dues in the elastomer; processing aids, such as sorbitan monostearate or stearic acid; sulfur-donating compounds; mercaptobenzothiazole; sulfenamides; thiuram sulfides, and the like, without departing from the scope of the invention.

The vulcanizable compositions may be prepared by conventional rubber compounding techniques, using a two- roll rubber mill or a Banbury mixer, at temperatures of

300°F. The compositions are vulcanized at similar temper¬ atures, preferably about 325-350°F for about 15 to 60 minutes and, optionally, post-cured for periods of time to develop full cures. The following examples are set forth for purposes of illustration only and are not to be construed as limita¬ tions on the present invention. All parts and percentages are by weight unless otherwise specified.

SUB _S TITUTE SHEET

EXAMPLE 1 An elastomeric copolymer of 80% thiodiethanol, 15% isopropylidenebisphenol and 5% trimethylolpropane, mono- allyl ether was compounded as follows:

Parts by Weight Elastomer 100 Carbon Black 60

Calcium oxide 3

Soirbitan monostearate 2

Sulfur 1.5

Tetramethyl thiuram disulfide 1.5 168.0

To separate portions (168 parts) of the above formulation was added:

A B C

Zinc oxide 5.0 Mercaptobenzothiazole 1.5 2.0 2.0 Polyamine D* - - 4.0

*Mixture of aliphatic and cyclic polyethyleneamines boiling above 340°C.

Each of the compositions A thru C was cured for 60 minutes at 330°F and _. then post-cured for 16 hours at 120°C before testing.

Rheology of the compositions was studied using a Monsanto Oscillating Disc Rheometer operating at 330°F.

Rheometer

A B C

Max. cure rate 6.5 0. 1 1.45 '

(inch-lbs./min.) Max. torque (inch-lbs.) 40.5 _ 87 Torque after 15 minutes 40.5 9 35 (inch - lbs.)

Stress-strain properties of the cured compositions using an Instron tester were as follows: Tensile, psi 1100 750 1660

Elongation, % 220 375 300 Hardness, Shore "A" 71 60

SUBSTIT

Continuous stress-relaxation studies were made to measure the thermal' stability of the compositions. The elastomer samples were tested on an autographic stress- relaxometer consisting of load-sensing elements, a means for extending and maintaining the specimens at a constant elongation, and a circulating air oven. The oven tempera¬ ture was maintained at a temperature of 150°C + 0.1°C and the samples extended to 5 + .05%. The decrease in modulus with time is recorded automatically. Data relating to the relative thermal stability are obtained from plots of f(t)/f(0) versus log time, or log f(t)/f(0) versus time, where f(t) and f(0) are the forces at time t and t-0, respectively ^' , required to maintain the sample at a given extension. The data are reported as 'J-' ^~ ~ - which represents the time at 150°C that is required for a sample to degrade to a value equal to 50% of the initial stress, which is a measure of the amount of degradation experienced by the specimen. Continuous Stress-Relaxation A B C .minutes 350 - 2450

The data illustrate that Composition A, which re¬ presents a conventional sulfur vulcanization system,provides ^~ fast cure rate, but exhibits poor thermal stability compared to Composition C which is many times more stable and which exhibits a good cure rate and develops good mechanical properties. Composition B demonstrates that a very poor cure is obtained without zinc oxide in a conven- tional vulcanization system.

EXAMPLE 2 Following the procedure of Example 1 an elastomeric copolymer of 90% thiodiethanol - 5% diethyleneglycol - 5% trimethylolpropane, monoallyl ether was compounded as follows:

SUBSTITUTE SHEET -≤£

Parts by Weight

Elastomer 100

Carbon black 50

Antioxidant* 2

Tetramethyl thiuram disulfide 1.5

Mercaptobenzothiazole 2.0

Sulfur 1.5

Calcium stearate 3.0

160.0 *Di-B-naphthyl-p-phenylenediamine

To separate portions (160 parts) of the above formulation was added:

D E F

Polyamine D (See Example 1) 2 3 4 The compositions were cured for 30 minutes at

330°F and post-cured for 16 hours at 120°C. Properties - were as follows ^~ .

Monsanto Rheometer @ 330°F

D . E F MaX^cure rate 1.4 2.1 2.4 Max. torque 80+ 95+ 95+

Torque after 15 minutes 39 51 51 Instron Stress-Strain Properties

D E F Tensile, psi 1645 1715 1490 Elongation, % 370 300 270 Compression Set, ° 89 62 41

(Method B: 22 hrs. at 120°C) Continuous Stress-Relaxation

using 2 to 4 parts per hundred of Polyamine D and that the higher concentrations tend to provide increased thermal stability, as manifested by improved compression set and stress-relaxation.

C5 ? l ψr- < _-- - ^* •** - t

EXAMPLE 3 An elastomeric copolymer of 90% thiodiethanol - 5% diethyleneglycol - 5% trimethylolpropane, monoallyl ether was compounded as follows:

Parts by Weight Elastomer 100

Carbon black 50

Calcium stearate 5

Sulfur 1.5

Mercaptobenzothiazole 1.5 Tetramethyl thiuram disulfide 1.5

159.5 Separate portions (159.5 parts) were compounded with the following (all at 4 parts per hundred of rubber of active material). G H J K

Triethylenetetramine 4 - - . - Tetraethylenepentamine : 4 -

Polyamine D** (50% on silica) ^' - 8 Polyamine H* - _. - 4 *Complex polyethyleneamine reaction product boiling above

340°C and containing 24-28% by weight of diethylenetriamine **See Example 1.

The compositions were cured for 30 minutes at 330°F and post-cured for 4 hours at 120°C. Torque (inch-pounds) was measured at 330°F after

30 minutes using a Monsanto Oscillating Disc Rheometer. This is an indication of the extent of cure of the compo¬ sition.

G . _ _ Torque after 30 min. ' 61 60 66 66

The stress-strain properties, obtained on an In- stron tester, were as follows: ^■ - ■ —- ^"

Tensile , psi 520 1550 1500 1540

Elongation, % 490 455 470 435

Hardness, Shore "A" 74 76 75 77

Compression Set, % 34 33 37 27 (Method B: 22 hrs. at 120°C)

The data illustrate that good cures are obtained using various polyethyleneamines with sulfur and that the cured compositions exhibit good ageing resistance, as manifested by low compression set. EXAMPLE 4

An elastomer of 90 percent thiodiethanol - 57o diethyleneglycol - 5% trimethylolpropane, monoallyl ether, was compounded as follows:

Parts by Weight

Control K

Elastomer 100 _. 100

Carbon black 50 50

Calcium stearate 5 5

Sulfur 1.5 1.5 Mercaptobenzothiazole 1.5 1.5

Tetramethyl thiuram disulfide 1.5 1.5

Triethylenetetramine stearate - 4

The compositions were cured for 60 minutes at

330°F. Stress-strain properties are as follows: Tensile, psi under 1530

Elongation, % cured 510

Hardness, Shore "A" | 67

EXAMPLE 5 ^ The procedure of Example 1 was again followed except that the elastomer was prepared from thiodiethanol

(95 parts) and the monoallyl ether of trimethylolpropane

(5 parts). Similar results were achieved.

C?" i- >.

€_.

O PI _ WiPO .

EXAMPLE 6 The procedure of Example 4 was again followed except that the monoallyl ether was replaced by 3-cyclo- hexene-1, 1-dimethanol. Similar results were achieved.

EXAMPLE 7 When the procedure of Example 4 was again followed except that the diethylene glycol was replaced by isopropyl- idene bisphenol, similar results were achieved.

EXAMPLE 8 The procedure of Example 1 was again followed except that Polyamine D was replaced by diethylenetriamine carbonate. Excellent results were observed.

EXAMPLE 9 Following the procedure of Example 8 except that the carbonate was replaced by the corresponding carbamate, the results were comparable.