BUTENE-1 POLYMER COMPOSITION HAVING HIGH MELT FLOW RATE
Document Type and Number:
WIPO Patent Application WO/2019/025583
Kind Code:
A1
Abstract:
A butene-1 polymer composition having MFR values of from 20 to less than 100 g/10 min., measured according to ISO 1133 at 190°C with a load of 2.16 kg, comprising: A) a butene-1 homopolymer or a copolymer of butene-1 with one or more comonomers selected from ethylene and higher alpha-olefins, having a copolymerized comonomer content of up to 5% by mole; B) a copolymer of butene-1 with one or more comonomers selected from ethylene and higher alpha-olefins, having a copolymerized comonomer content of from 6% to 20% by mole; said composition having a total copolymerized comonomer content from 4% to 15% by mole, referred to the sum of A) and B), and a content of fraction soluble in xylene at 0°C of 75% by weight or less, determined on the total weight of A) and B).

Inventors:
MARCHINI ROBERTA (IT)
SPATARO STEFANO (IT)
PICA ROBERTA (IT)
Application Number:
PCT/EP2018/071110
Publication Date:
February 07, 2019
Filing Date:
August 03, 2018
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
BASELL POLIOLEFINE ITALIA SRL (IT)
International Classes:
C08F2/00; C08F10/08; C08L23/20; C09J123/20; C08F4/6592
Domestic Patent References:
WO2004099269A22004-11-18
WO2009000637A12008-12-31
WO2001047939A12001-07-05
Foreign References:
EP3266825A12018-01-10
EP0314495A21989-05-03
EP0163783A11985-12-11
US4677025A1987-06-30
US4960820A1990-10-02
EP0314495A21989-05-03
Other References:
JOURNAL OF POLYMER SCIENCE PART B: POLYMER LETTERS, vol. 1, no. 11, November 1963 (1963-11-01), pages 587 - 591
MACROMOLECULES, vol. 35, no. 7, 2002
M. KAKUGO; Y. NAITO; K. MIZUNUMA; T. MIYATAKE, MACROMOLECULES, vol. 16, no. 4, 1982, pages 1160
J. C. RANDALL, MACROMOL. CHEM PHYS., vol. C30, 1989, pages 211
Attorney, Agent or Firm:
GAVERINI, Gaetano (IT)
Download PDF:
Claims:
CLAIMS

What is claimed is:

1. A butene-1 polymer composition having a MFR value of from 20 to less than 100 g/10 min., preferably from 25 to 95 g/10 min., more preferably from 30 to 80 g/10 min., measured according to ISO 1133 at 190°C with a load of 2.16 kg, and comprising:

A) a butene-1 homopolymer or a copolymer of butene-1 with one or more

comonomers selected from ethylene and higher alpha-olefins, having a copolymerized comonomer content (CA) of up to 5% by mole, preferably up to 4% by mole;

B) a copolymer of butene-1 with one or more comonomers selected from ethylene and higher alpha-olefins, having a copolymerized comonomer content (CB) of from 6% to 20% by mole, preferably from 8% to 18% by mole; said composition having a total copolymerized comonomer content from 4% to 15% by mole, preferably from 5% to 15% by mole, referred to the sum of A) and B), and a content of fraction soluble in xylene at 0°C of 75% by weight or less, preferably of 70% by weight or less, determined on the total weight of A) and B).

2. The butene-1 polymer composition of claim 1, comprising from 30% to 70% by weight, preferably from 35% to 65% by weight of A) and from 30% to 70% by weight, preferably from 35% to 65% by weight of B), referred to the total weight of A) and B).

3. The butene-1 polymer composition of claim 1, having DH Tmll values of from 4 to 15 J/g, measured with a scanning speed corresponding to 10°C/min.

4. The butene-1 polymer composition of claim 1, having a Mw/Mn value, where Mw is the weight average molar mass and Mn is the number average molar mass, both measured by GPC, equal to or lower than 4.

5. The butene-1 polymer composition of claim 1, having a Mz value, measured by GPC, of 180,000 g/mol or higher.

6. The butene-1 polymer composition of claim 1, having a Mw value equal to or greater than 90,000 g/mol.

7. A process for preparing the butene-1 polymer composition of claim 1, comprising at least two sequential stages, carried out in two or more reactors connected in series, wherein components A) and B) are prepared in separate subsequent stages, operating in each stage, except the first stage, in the presence of the polymer formed and the catalyst used in the preceding stage.

8. The process of claim 9, carried out in the presence of a metallocene catalyst obtainable by contacting:

- a stereorigid metallocene compound;

- an alumoxane or a compound capable of forming an alkyl metallocene cation; and, optionally,

- an organo aluminum compound.

9. Manufactured articles consisting of or comprising the butene-1 polymer composition of claim 1 or 2.

10. The manufactured articles of claim 9, in form of films or fibers.

11. A hot-melt adhesive composition consisting of or comprising the butene-1 polymer

composition of claim 1 or 2.

Description:
BUTENE-1 POLYMER COMPOSITION HAVING HIGH MELT FLOW RATE

FIELD OF THE INVENTION

[0001] The present disclosure relates to a butene-1 polymer composition having a melt flow rate of not less than 20 g/min., measured according to norm ISO 1133 with a load of 2.16 kg at 190 °C, thus having a high fluidity in the molten state.

[0002] The butene-1 polymer composition provides high tensile properties, low hardness, low flexural modulus and a low glass transition temperature, while still retaining a measurable crystallinity.

[0003] The present butene-1 polymer composition has many applications. In particular the present butene-1 polymer composition can be used in the production of films and fibers, as a component of hot-melt adhesives, as a polymer additive to enhance rheological, mechanical and optical properties of polymer compositions, or as a fluidizer for lubricants.

BACKGROUND OF THE INVENTION

[0004] Butene- 1 polymers having high melt flow rate are disclosed in the art, in particular in US4677025, US4960820 and EP0314495. These polymers have been used in many application fields, due to their valuable properties (such as chemical inertia, mechanical properties and nontoxicity).

[0005] In particular, due to their high fluidity in the molten state and their physical properties, the butene-1 polymers with high melt flow rate can be used in the production of films and fibers, optionally blended with other poly olefins, and in various kinds of holt-melt formulations.

[0006] As explained in US4677025, the molecular weights and molecular weight distribution of the butene-1 polymer has an effect on the final polymer properties.

[0007] It has now been found that by combining at least two butene-1 polymers with different and specific comomomer contents and by a proper selection of the melt flow rate and optionally of molecular weights and molecular weight distribution, which is made possible by using a metallocene catalyst, an advantageous profile of properties is achieved.

SUMMARY OF THE INVENTION

[0008] Thus the present disclosure provides a butene-1 polymer composition having a Melt

Flow Rate value of from 20 to less than 100 g/10 min., preferably from 25 to 95 g/10 min., more preferably from 30 to 80 g/10 min., measured according to ISO 1133 at 190°C with a load of

2.16 kg (hereinafter called "MFR") and comprising: A) a butene-1 homopolymer or a copolymer of butene-1 with one or more comonomers selected from ethylene and higher alpha-olefins, having a copolymerized comonomer content (CA) of up to 5% by mole, preferably up to 4% by mole;

B) a copolymer of butene-1 with one or more comonomers selected from ethylene and higher alpha-olefins, having a copolymerized comonomer content (CB) of from 6% to 20% by mole, preferably from 8% to 18% by mole; said composition having a total copolymerized comonomer content from 4% to 15% by mole, preferably from 5% to 15% by mole, referred to the sum of A) and B), and a content of fraction soluble in xylene at 0°C of 75% by weight or less, preferably of 70% by weight or less, determined on the total weight of A) and B).

[0009] The butene-1 polymer composition provided herein can be obtained directly in polymerization, without requiring the use of free radical generating agents, like peroxides, to increase the MFR value, thus avoiding the chemical contamination and unpleasant odor which results from the introduction of free radical generating agents.

Such butene-1 polymer composition has a low hardness, low flexural modulus, high values of elongation at break and a low glass transition temperature, which are useful properties in films and fibers, where the present butene-1 polymer composition can be used in blend with other polyolefins, particularly with the propylene polymers conventionally used for producing said articles, and also in hot melt compositions.

DETAILED DESCRIPTION OF THE INVENTION

[0010] Specific amounts of fraction soluble in xylene at 0°C for the butene-1 polymer composition as provided herein, expressed as the weight content of fraction measured by extraction on the total weight of A) and B), are of from 35% to 75% by weight, or from 35% to 70% by weight, in particular from 40% to 70% by weight, or from 40% to 65% by weight.

[0011] When A) is a copolymer, a specific lower limit of comonomer content is of 1% by mole.

[0012] Preferably, when both A) and B) are copolymers, the difference between the percent values of the copolymerized comonomer contents of B) and A) satisfies the following relation: C B ) - C A ) > 5; or

C B ) - C A ) > 6. [0013] The relative amounts of components A) and B) can be easily determined depending upon the desired value of total copolymerized comonomer content, the comonomer contents of the single components and their content of fraction soluble in xylene at 0 °C.

[0014] Preferred amounts are from 30% to 70% by weight, preferably from 35% to 65% by weight of A) and from 30% to 70% by weight, preferably from 35% to 75% by weight of B), all referred to the total weight of A) and B).

[0015] Specific examples of higher alpha-olefins that can be present as comonomers, in addition or in alternative to ethylene, in components A) and B) are the alpha-olefins of formula CH 2 = CHR wherein R is methyl or an alkyl radical containing 3 to 8 or 3 to 6 carbon atoms, such as propylene, hexene-1, octene-1.

[0016] However ethylene is the preferred comonomer, in particular for component B).

[0017] The present butene-1 polymer composition has a measurable crystallinity, as demonstrated by the presence, in the Differential Scanning Calorimetry (DSC) pattern, of the melting temperature peaks of crystalline butene-1 polymers.

[0018] In particular, the present butene-1 polymer shows one or more melting peaks in the second DSC heating scan. Such temperature peak or peaks, generally occurring at temperatures equal to or lower than 90 °C, or equal to or lower than 85 °C, in particular from 40 °C to 90 °C, or from 40 °C to 85 °C, are attributed to the melting point of crystalline form II of the butene-1 polymers (Tmll) and the area under the peak (or peaks) is taken as the global melting enthalpy (DH Tmll). However, if more than one peak is present, the highest (most intense) one is taken as Tmll.

[0019] Specific global DH Tmll values for the present butene-1 polymer are of 15 J/g or less, in particular of from 4 to 15 J/g, measured with a scanning speed corresponding to 10°C/min.

[0020] Moreover, the present butene-1 polymer shows one or more melting peaks, generally occurring at temperatures equal to or lower than 100°C, or equal to or lower than 90°C, in particular from 30°C to 100°C, or from 30°C to 90°C, in a DSC heating scan carried out after aging. Such temperature peak or peaks are attributed to the melting point of crystalline form I of the butene-1 polymers (Tml) and the area under the peak (or peaks) is taken as the global melting enthalpy (DH Tml). However, if more than one peak is present, the highest (most intense) one is taken as Tml.

[0021] Specific global DH Tml values for the present butene-1 polymer are of 50 J/g or less, in particular of from 25 to 50 J/g, or from 30 to 50 J/g, measured with a scanning speed corresponding to 10°C/min. [0022] The present butene- 1 polymer can also have a detectable content of crystalline form III. Crystalline form III is detectable via the X-ray diffraction method described in the Journal of Polymer Science Part B: Polymer Letters Volume 1, Issue 11, pages 587-591, November 1963, or Macromolecules, Vol. 35, No. 7, 2002.

[0023] Specific X-ray crystallinity values for the present butene-1 polymer are of from 10% to 50%, in particular from 15% to 45%.

[0024] The specific MFR values for components A) and B) can be broadly selected, provided that the said MFR values of the overall composition are obtained.

[0025] In this respect, it is well known that the logarithm of the MFR value of polyolefin blends in general, thus of blends of butene-1 polymers as well, is given by the sum of the products of the weight fraction and the logarithm of the MFR value of the single components.

[0026] Thus the MFR value of a composition made of a blend of the said components A) and B) is determined by the following relation:

log MFR (A+B) = wA log MFR (A) + wB log MFR (B)

where MFR (A+B) is the MFR value for the blend of A) and B), MFR (A) and MFR (B) are the MFR values of components A) and B) respectively and wA and wB are the respective weight fractions. For instance, wA and wB are both 0.5 when the blend is made of 50% by weight of component A) and 50% by weight of component B).

[0027] It is however preferred, in order to achieve good fluidity in the molten state, to keep the MFR values of the single components A) and B) sufficiently high, in particular in the range of from 10 to 200 g/10 min., or from 15 to 150 g/10 min.

[0028] Moreover, the present butene-1 polymer composition preferably has at least one of the following further features:

- an intrinsic viscosity (IV) measured in tetrahydronaphthalene (THN) at 135°C equal to lower than 0.98 dl/g, or equal to lower than 0.95 dl/g, in particular from 0.75 dl/g to 0.98 dl/g or from 0.75 dl/g to 0.95 dl/g;

- a Mw/Mn value, where Mw is the weight average molar mass and Mn is the number average molar mass, both measured by GPC (Gel Permeation Chromatography), equal to or lower than 4, in particular equal to or lower than 3.5, or equal to or lower than 2.5, the lower limit being of 1.5 in all cases;

- a Mz value of 180,000 g/mol or higher, or of 190,000 g/mol or higher, in particular from 180,000 to 350,000 g/mol or from 190,000 to 300,000 g/mol;

- Mw equal to or greater than 90,000 g/mol, in particular from 90,000 to 200,000 g/mol;

- isotactic pentads (mmmm) measured with 13 C-NMR operating at 150.91 MHz higher than 90%; in particular higher than 93% or higher than 95%; - 4,1 insertions not detectable using a 13 C-NMR operating at 150.91 MHz;

- a yellowness index lower than 0; in particular from 0 to -10 or from -1 to -9 or from -1 to -5;

- a Shore D value equal to or lower than 50, or equal to or lower than 45, in particular from 15 to 50 or from 15 to 45;

- a tensile stress at break, measured according to ISO 527, of from 10 MPa to 40 MPa, in particular from 15 MPa to 35 MPa;

- a tensile elongation at break, measured according to ISO 527, of from 400% to 1000%; in particular from 500% to 900%;

- a glass transition temperature of -22°C or less, in particular of -23°C or less, wherein the lower limit is -30°C.

- a density of 0.890 g/cm 3 or more, in particular of 0.892 g/cm 3 or more; wherein the upper limit is of 0.899 g/cm 3 .

[0029] The butene-1 polymer components A) and B) can be obtained by polymerizing the monomer(s) in the presence of a metallocene catalyst system obtainable by contacting:

- a stereorigid metallocene compound;

- an alumoxane or a compound capable of forming an alkyl metallocene cation; and, optionally,

- an organo aluminum compound.

[0030] Preferably the stereorigid metallocene compound belongs to the following formula (I):

wherein:

M is an atom of a transition metal selected from those belonging to group 4; preferably M is zirconium;

X, equal to or different from each other, is a hydrogen atom, a halogen atom, a R, OR, OR'O, OSO2CF3, OCOR, SR, NR2 or PR2 group wherein R is a linear or branched, saturated or unsaturated Ci-C2o-alkyl, C3-C2o-cycloalkyl, C6-C2o-aryl, C7-C2o-alkylaryl or C7-C2o-arylalkyl radical, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; and R' is a Ci-C2o-alkylidene, C6-C2o-arylidene, C7-C2o-alkylarylidene, or C7-C2o-arylalkylidene radical; preferably X is a hydrogen atom, a halogen atom, a OR'O or R group; more preferably X is chlorine or a methyl radical;

R\ R 2 , R 5 , R 6 , R 7 , R 8 and R 9 , equal to or different from each other, are hydrogen atoms, or linear or branched, saturated or unsaturated Ci-C2o-alkyl, C3-C2o-cycloalkyl, C6-C2o-aryl, C7-C2o-alkylaryl or C7-C2o-arylalkyl radicals, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; or R 5 and R 6 , and/or R 8 and R 9 can optionally form a saturated or unsaturated, 5 or 6 membered rings, said ring can bear C1-C20 alkyl radicals as substituents; with the proviso that at least one of R 6 or R 7 is a linear or branched, saturated or unsaturated Ci-C2o-alkyl radical, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably a Ci-Cio-alkyl radical;

R 3 and R 4 , equal to or different from each other, are linear or branched, saturated or unsaturated Ci-C2o-alkyl radicals, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably R 3 and R 4 equal to or different from each other are Ci-Cio-alkyl radicals; more preferably R 3 is a methyl, or ethyl radical; and R 4 is a methyl, ethyl or isopropyl radical.

[0031] Preferably the compounds of formula (I) have formula (la):

(Ia)

Wherein:

M, X, R\ R 2 , R 5 , R 6 , R 8 and R 9 have been described above;

R 3 is a linear or branched, saturated or unsaturated Ci-C2o-alkyl radical, optionally containing heteroatoms belonging to groups 13-17 of the Periodic Table of the Elements; preferably R 3 is a Ci-Cio-alkyl radical; more preferably R 3 is a methyl, or ethyl radical.

[0032] Specific examples of metallocene compounds are dimethylsilyl{(2,4,7-trimethyl-l- indenyl)-7-(2,5-dimethyl-cyclopenta[l,2-b:4,3-b']-dithiophen e)} zirconium dichloride; dimethylsilanediyl{(l-(2,4,7-trimethylindenyl)-7-(2,5-dimeth yl-cyclopenta[l,2-b:4,3-b']- dithiophene) } Zirconium dichloride and dimethylsilanediyl{(l-(2,4,7-trimethylindenyl)-7-(2,5- dimethyl-cyclopenta[ 1 ,2-b: 4,3 -b ' ] -dithiophene) } zirconium dimethyl. [0033] Examples of alumoxanes are methylalumoxane (MAO), tetra-(isobutyl)alumoxane (TIBAO), tetra-(2,4,4-trimethyl-pentyl)alumoxane (TIOAO), tetra-(2,3- dimethylbutyl)alumoxane (TDMBAO) and tetra-(2,3,3-trimethylbutyl)alumoxane (TTMBAO).

[0034] Examples of compounds able to form an alkylmetallocene cation are compounds of formula D + E ~ , wherein D + is a Br0nsted acid, able to donate a proton and to react irreversibly with a substituent X of the metallocene of formula (I) and E " is a compatible anion, which is able to stabilize the active catalytic species originating from the reaction of the two compounds, and which is sufficiently labile to be able to be removed by an olefinic monomer. Preferably, the anion E ~ comprises of one or more boron atoms.

[0035] Examples organo aluminum compound are trimethylaluminum (TMA), triisobutylaluminium (TIBA), tris(2,4,4-trimethyl-pentyl)aluminum (TIOA), tris(2,3- dimethylbutyl)aluminium (TDMBA) and tris(2,3,3-trimethylbutyl)aluminum (TTMBA).

[0036] Examples of the said catalyst system and of polymerization processes employing such catalyst system can be found in WO2004099269 and WO2009000637.

[0037] By operating under known polymerization conditions in the presence of the above described catalysts, the two components A) and B) of the present butene-1 polymer composition can be prepared separately and then blended together in the molten state by using known polymer processing apparatuses, such as mono- and twin screw extruders.

[0038] However, as previously mentioned, the present butene-1 polymer composition can be prepared directly in polymerization.

[0039] The polymerization process for producing the composition thus comprises at least two sequential stages, carried out in two or more reactors connected in series, wherein components A) and B) are prepared in separate subsequent stages, operating in each stage, except for the first stage, in the presence of the polymer formed and the catalyst used in the preceding stage.

[0040] Said polymerization process can be carried out in liquid phase, optionally in the presence of an inert hydrocarbon solvent, or in gas phase, using fluidized bed or mechanically agitated gas phase reactors.

[0041] The catalyst can be added in the first reactor only, or in more than one reactor.

[0042] The hydrocarbon solvent can be either aromatic (such as toluene) or aliphatic (such as propane, hexane, heptane, isobutane, cyclohexane, 2,2,4-trimethylpentane and isododecane).

[0043] Preferably, the polymerization process is carried out by using liquid butene-1 as polymerization medium. The polymerization temperature can be from 20°C to 150°C, in particular between 50°C and 90°C, for example from 65 °C to 82°C. [0044] The concentration of hydrogen in the liquid phase during the polymerization reaction (molar ppm ¾/ butene-1 monomer) is generally from 400 ppm to 950 ppm, in particular from 450 ppm to 900 ppm.

[0045] The amount of comonomer, in particular ethylene, in the liquid phase, when a copolymer is prepared, can be from 0.1% to 8% by weight, in particular from 0.2% to 6% by weight, with respect to the total weigh of comonomer and butene-1 monomer present in the polymerization reactor.

[0046] In particular, for the preparation of component A) the amount of comonomer can be from 0.1% to 0.9% or from 0.2% to 0.8% by weight, while it can be from 1% to 8% by weight or from 1.5% to 6% by weight for the preparation of component B).

[0047] In hot- melt adhesive applications, the present butene-1 polymer composition can be optionally blended with other materials commonly used in the relevant art.

[0048] In particular, a hot-melt adhesive polyolefin composition can comprise one or more of the following optional components, in addition to the present butene-1 polymer composition comprising the components A) and B):

I) at least one additional polymer, selected in particular from the group of amorphous poly- alpha-olefins, thermoplastic polyure thanes, ethylene/(meth)acrylate copolymers, ethylene/vinyl acetate copolymers and mixtures thereof;

II) at least one resin material different from (I) and selected from aliphatic hydrocarbon resins, terpene/phenolic resins, polyterpenes, rosins, rosin esters and derivatives thereof and mixtures thereof;

III) at least one wax or oil, selected in particular from mineral, paraffinic or naphthenic waxes or oils; and

IV) a nucleating agent.

[0049] Examples of nucleating agents are isotactic polypropylene, polyethylene, amides, like stearamides, or talc.

[0050] Preferred amounts by weight of said optional components, with respect to the total weight of the hot-melt adhesive polyolefin composition, when present and independently from each other are:

from 0.1% to 25%, in particular from 1% to 25% by weight of I);

- from 10% to 75%, in particular from 10% to 40% by weight of II);

from 0.1% to 50%, in particular from 1% to 30% by weight of III);

from 0.01% to 1%, in particular from 0.1% to 1% by weight of IV). [0051] The said components can be added and blended in the molten state with the present butene-1 polymer composition by using known polymer processing apparatuses, such as mono- and twin screw extruders.

[0052] The said hot-melt adhesive compositions can be used in several fields such as in paper and packaging industry, in furniture manufacture e.g. for edgebands, particularly square edges, and softforming applications, for paneling in high moisture environments and in the production of nonwoven articles, like disposable diapers.

EXAMPLES

[0053] Various embodiments, compositions and methods as provided herein are disclosed below in the following examples. These examples are illustrative only, and are not intended to limit the scope of the invention.

[0054] The following analytical methods are used to characterize the polymer compositions.

[0055] Thermal properties (melting temperatures and enthalpies)

[0056] Determined by Differential Scanning Calorimetry (D.S.C.) on a Perkin Elmer DSC-7 instrument, as hereinafter described.

- For the determination of Tmll (the melting temperature measured in the second heating run) a weighted sample (5-10 mg) obtained from the polymerization was sealed into aluminum pans and heated at 200 °C with a scanning speed corresponding to 10 °C/minute. The sample was kept at 200 °C for 5 minutes to allow a complete melting of all the crystallites thus cancelling the thermal history of the sample. Successively, after cooling to -20 °C with a scanning speed corresponding to 10 °C/minute, the peak temperature was taken as the crystallization temperature (Tc). After standing for 5 minutes at -20 °C, the sample was heated for the second time at 200 °C with a scanning speed corresponding to 10 °C/min. In this second heating run, the peak temperature measured was taken as (Tmll). If more than one peak was present, the highest (most intense) one was taken as Tmll. The area under the peak (or peaks) was taken as global melting enthalpy (DH Tmll).

- The melting enthalpy and the melting temperature were also measured after aging (without cancelling the thermal history) as follows by using Differential Scanning Calorimetry (D.S.C.) on an Perkin Elmer DSC-7 instrument. A weighted sample (5-10 mg) obtained from the polymerization was sealed into aluminum pans and heated at 200°C with a scanning speed corresponding to 10 °C/minute. The sample was kept at 200 °C for 5 minutes to allow a complete melting of all the crystallites. The sample was then stored for 10 days at room temperature. After 10 days the sample was subjected to DSC, cooled to -20 °C, and then it was heated at 200°C with a scanning speed corresponding to 10°C/min. In this heating run, the peak temperature was taken as the melting temperature (Tml). If more than one peak was present, the highest (most intense) peak was taken as Tml. The area under the peak (or peaks) was taken as global melting enthalpy after 10 days (DH Tml).

[0057] MFR

[0058] Determined according to norm ISO 1133 with a load of 2.16 kg at 190 °C (standard die).

[0059] Intrinsic viscosity

[0060] Determined according to norm ASTM D 2857 in tetrahydronaphthalene at 135 °C.

[0061] Density

[0062] The density of samples was measured according to ISO 1183-1 (ISO 1183-1 method A "Methods for determining the density of non-cellular plastics— Part 1: Immersion method, liquid pycnometer method and titration method"; Method A: Immersion method, for solid plastics (except for powders) in void-free form). Test specimens were taken from compression moulded plaques conditioned for 10 days before carrying out the density measure.

[0063] Comonomer contents

[0064] Comonomer contents were determined via FT-IR.

[0065] The spectrum of a pressed film of the polymer was recorded in absorbance vs. wavenumbers (cm 1 ). The following measurements were used to calculate the ethylene content: a) area (A t ) of the combination absorption bands between 4482 and 3950 cm "1 which is used for spectrometric normalization of film thickness.

b) factor of subtraction (FCRc 2 ) of the digital subtraction between the spectrum of the polymer sample and the absorption band due to the sequences BEE and BEB (B: l,butene units, E: ethylene units) of the methylenic groups (CH 2 rocking vibration).

c) Area (Ac 2 ,biock) of the residual band after subtraction of the C 2 PB spectrum. It comes from the sequences EEE of the methylenic groups (CH 2 rocking vibration).

[0066] APPARATUS

[0067] A Fourier Transform Infrared spectrometer (FTIR) was used, which is capable of providing the spectroscopic measurements above reported.

[0068] A hydraulic press with platens heatable to 200 °C (Carver or equivalent) was used.

[0069] METHOD

[0070] Calibration of (BEB + BEE) sequences

[0071] A calibration straight line is obtained by plotting (BEB + BEE)wt vs. FCR C2 /A t . The slope G r and the intercept I r are calculated from a linear regression. [0072] Calibration of EEE sequences

[0073] A calibration straight line is obtained by plotting %(EEE)wt vs. Ac2,biock/A,. The slope GH and the intercept IH are calculated from a linear regression.

[0074] Sample preparation

[0075] Using a hydraulic press, a thick sheet is obtained by pressing about g 1.5 of sample between two aluminum foils. If homogeneity is in question, a minimum of two pressing operations are recommended. A small portion is cut from this sheet to mold a film. Recommended film thickness ranges between 0.1-0.3 mm.

[0076] The pressing temperature is 140 ± 10 °C.

[0077] A crystalline phase modification takes place with time, therefore it is recommended to collect the IR spectrum of the sample film as soon as it is molded.

[0078] Procedure

[0079] The instrument data acquisition parameters are as follows:

Purge time: 30 seconds minimum.

Collect time: 3 minutes minimum.

Apodization: Happ-Genzel.

Resolution: 2 cm 1 .

Collect the IR spectrum of the sample vs. an air background.

[0080] CALCULATION

[0081] Calculate the concentration by weight of the BEE + BEB sequences of ethylene units:

[0082] Calculate the residual area (AC2,block) after the subtraction described above, using a baseline between the shoulders of the residual band.

[0083] Calculate the concentration by weight of the EEE sequences of ethylene units:

[0084] Calculate the total amount of ethylene percent by weight:

%C2wt = [%(BEE+ BEB)wt + %(EEE)wt]

[0085] NMR analysis of chain structure

[0086] 13 C NMR spectra were acquired on a Bruker AV-600 spectrometer equipped with cryo-probe, operating at 150.91 MHz in the Fourier transform mode at 120°C. [0087] The peak of the Τβδ carbon (nomenclature according to C. J. Carman, R. A. Harrington and C. E. Wilkes, Macromolecules, 10, 3, 536 (1977)) was used as internal reference at 37.24 ppm. The samples were dissolved in l,l,2,2-tetrachloroethane-<i2 at 120°C with a 8 % wt/v concentration. Each spectrum was acquired with a 90° pulse, 15 seconds of delay between pulses and CPD to remove ] H- 13 C coupling. About 512 transients were stored in 32K data points using a spectral window of 9000 Hz.

[0088] The assignments of the spectra, the evaluation of triad distribution and the composition were made according to Kakugo [M. Kakugo, Y. Naito, K. Mizunuma and T. Miyatake, Macromolecules, 16, 4, 1160 (1982)] and Randall [J. C. Randall, Macromol. Chem Phys. , C30, 211 (1989)] using the following:

BBB = 100 (Tpp)/S = 15

BBE = ΙΟΟΤβδ/S = 14

EBE = 100 Ρδδ /S = 114

BEB = 100 Spp/S = 113

BEE= 100 Sas/S = 17

EEE = 100(0.25 S Y 5+0.5 S 5 5)/S = 0.25 19+ 0.5110

Area Chemical Shift Assignments Sequence

1 40.40-40.14 Sococ BBBB

39.64 Τδδ EBE

2 39-76-39.52 Sococ BBBE

3 39.09 Sococ EBBE

4 37.27 Τβδ BBE

5 35.20-34.88 Τββ BBB

6 34.88-34.49 Say BBEB+BEBE

7 34.49-34.00 Sa6 EBEE+BBEE

8 30.91 Syr BEEB

9 30.42 SyS BEEE

10 29.90 66 EEE

11 27.73-26.84 8βδ+2Β 2 BBB+BBE

EBEE+BBEE

12 26.70 2B 2 EBE

13 24.54-24.24 spp BEB

14 11.22 Ρδδ EBE

15 11.05 Ρβδ BBE

16 10.81 Ρββ BBB

[0089] To a first approximation, the mmmm was calculated using 2B2 carbons as follows:

mmmm = Bi* 100/(Bi+B 2 -2*A 4 -A 7 -Ai 4 )

[0090] Mw/Mn and Mz determination by GPC

[0091] Measured by way of Gel Permeation Chromatography (GPC) in 1,2,4- trichlorobenzene (TCB). Molecular weight parameters (Mn, Mw, Mz) and molecular weight distributions Mw/Mn for all the samples were measured by using a GPC-IR apparatus by PolymerChar, which was equipped with a column set of four PLgel Olexis mixed-bed (Polymer Laboratories) and an IR5 infrared detector (PolymerChar). The dimensions of the columns were 300 x 7.5 mm and their particle size was 13 μιη. The mobile phase flow rate was kept at 1.0 mL/min. All the measurements were carried out at 150 °C. Solution concentrations were 2.0 mg/mL (at 150 °C) and 0.3 g/L of 2,6-diterbuthyl-/?-chresole were added to prevent degradation. For GPC calculation, a universal calibration curve was obtained using 12 polystyrene (PS) standard samples supplied by PolymerChar (peak molecular weights ranging from 266 to 1220000). A third-order polynomial fit was used for interpolate the experimental data and obtain the relevant calibration curve. Data acquisition and processing was done by using Empower 3 (Waters). The Mark-Houwink relationship was used to determine the molecular weight distribution and the relevant average molecular weights: the K values were Kps = 1.21 x 10 "4 dL/g and KPB = 1.78 x 10 "4 dL/g for PS and polybutene (PB) respectively, while the Mark- Houwink exponents a= 0.706 for PS and a= 0.725 for PB were used.

[0092] For butene/ethylene copolymers, as far as the data evaluation is concerned, it was assumed for each sample that the composition was constant in the whole range of molecular weight and the K value of the Mark-Houwink relationship was calculated using a linear combination as reported below:

^EB ~ Χ βΚρΕ X B^PB where KEB is the constant of the copolymer, K PE (4.06 x 10 "4 , dL/g) and K PB (1.78 x 10 "4 dL/g) are the constants of polyethylene (PE) and PB, XE and XB are the ethylene and the butene weight relative amount with XE + XB = 1. The Mark-Houwink exponents a = 0.725 was used for all the butene/ethylene copolymers independently on their composition. End processing data treatment was fixed for all samples to include fractions up at 1000 in terms of molecular weight equivalent. Fractions below 1000 were investigated via GC.

[0093] Fractions soluble and insoluble in xylene at 0°C (XS-0°C)

[0094] 2.5 g of polymer composition and 250 cm 3 of o-xylene are introduced in a glass flask equipped with a refrigerator and a magnetic stirrer. The temperature is raised in 30 minutes up to the boiling point of the solvent. The so obtained clear solution is then kept under reflux and stirring for further 30 minutes. The closed flask is then cooled to 100°C in air for 10 to 15 minute under stirring and then kept for 30 minutes in thermostatic water bath at 0 °C for 60 minutes as well. The so formed solid is filtered on quick filtering paper at 0°C. 100 cm 3 of the filtered liquid is poured in a previously weighed aluminum container which is heated on a heating plate under nitrogen flow, to remove the solvent by evaporation. Thus, one calculates the percent by weight of polymer soluble (Xylene Solubles at 0°C = XS 0°C) from the average weight of the residues. The insoluble fraction in o-xylene at 0°C (xylene Insolubles at 0°C = XI 0°C) is:

XI 0°C=100-XS 0°C. [0095] Determination of X-ray crystallinity

[0096] The X-ray crystallinity was measured with an X-ray Diffraction Powder Diffractometer (XDPD) that uses the Cu-Kal radiation with fixed slits and able to collect spectra between diffraction angle 2Θ = 5° and 2Θ = 35° with step of 0.1° every 6 seconds.

The samples are diskettes of about 1.5-2.5 mm of thickness and 2.5-4.0 cm of diameter made by compression moulding. The diskettes are aged at room temperature (23 °C) for 96 hours.

After this preparation the specimen is inserted in the XDPD sample holder. The XRPD instrument set in order to collect the XRPD spectrum of the sample from diffraction angle 2Θ = 5° to 2Θ = 35° with steps of 0.1° by using counting time of 6 seconds, and at the end the final spectrum is collected.

Defining Ta as the total area between the spectrum profile and the baseline expressed in counts/sec-20 and Aa as the total amorphous area expressed in counts/sec ·2Θ. Ca is total crystalline area expressed in counts/sec-20.

The spectrum or diffraction pattern is analyzed in the following steps:

1) define a suitable linear baseline for the whole spectrum and calculate the total area (Ta) between the spectrum profile and the baseline;

2) define a suitable amorphous profile, along the whole spectrum, that separate , the amorphous regions from the crystalline ones according to the two phase model;

3) calculate the amorphous area (Aa) as the area between the amorphous profile and the baseline;

4) calculate the crystalline area (Ca) as the area between the spectrum profile and the amorphous profile as Ca = Ta- Aa

5) Calculate the degree of crystallinity ( Cr) of the sample using the formula:

Cr = 100 x Ca / Ta

[0097] Flexural Modulus

[0098] According to norm ISO 178, measured 10 days after molding.

[0099] Shore D

[0100] According to norm ISO 868, measured 10 days after molding.

[0101] Tensile stress and elongation at break

[0102] According to norm ISO 527 on compression molded plaques, measured 10 days after molding.

[0103] Glass transition temperature via DMTA (Dynamic Mechanical Thermal Analysis) Molded specimens of 76 mm by 13 mm by 1 mm are fixed to the DMTA machine for tensile stress. The frequency of the tension and relies of the sample is fixed at 1 Hz. The DMTA translates the elastic response of the specimen starting from -100 °C to 130 °C. In this way it is possible to plot the elastic response versus temperature. The elastic modulus for a viscoelastic material is defined as E=E'+iE". The DMTA can split the two components E' and E" by their resonance and plot E' vs temperature and EVE" = tan (δ) vs temperature.

The glass transition temperature Tg is assumed to be the temperature at the maximum of the curve EVE" = tan (δ) vs temperature.

[0104] Yellowness index

[0105] Determined accordingly to ASTM D 1925.

[0106] Example 1 and Comparative Example 1

[0107] Preparation of the metallocene catalyst (A-l)

[0108] Dimethylsilyl{(2,4,7-trimethyl-l-indenyl)-7-(2,5-dimethyl-cy clopenta[l,2-b:4,3-b']- dithiophene)} zirconium dichloride (A-l) was prepared according to Example 32 of WO0147939.

[0109] Preparation of the catalytic solution

[0110] Under nitrogen atmosphere, 8.1 L of a solution of 4.5 wt/v of TIBA in isododecane (1.84 mol of TIBA) and 760 mL of a solution 30 wt/wt of MAO in toluene (3.65 moles of MAO) were loaded in a 20 L jacketed glass reactor equipped with an anchor stirrer and allowed to react at room temperature for about 1 hour under stirring.

[0111] After this time, the metallocene A-l (1.6 g, 2.75 mmol) was added and dissolved under stirring for about 30 minutes.

[0112] The final solution was discharged from the reactor into a cylinder through a filter to remove solid residues (if any).

[0113] The composition of the solution is as follows:

[0114] Polymerization

[0115] The polymerization was carried out continuously in a pilot plant comprising two stirred reactors connected in series in which liquid butene- 1 constituted the liquid medium.

[0116] The catalytic solution was fed in both reactors.

[0117] The polymerization conditions are reported in Table 1. Table 1

Note: C2H4 = ethylene; kg/gMe = kilograms of polymer per gram of metallocene catalyst (A-1); Split = amount of polymer produced in the concerned reactor.

[0118] In Table 2 the properties of the final products are specified.

[0119] Table 2 reports also the properties of the butene-1 polymer taken as comparison (Comparative Example 1), which is a commercial copolymer containing 6.8% by mole of ethylene, prepared with a Ziegler-Natta catalyst and subsequently subjected to a peroxide treatment, to increase the MFR value.

Table 2