Field

[0001] This invention relates to cyanoacrylate-containing compositions that include (a) a beta-alkoxy cyanoacrylate component, (b) a cyanoacrylate component selected from butyl cyanoacrylates , octyl cyanoacrylates , and combinations thereof; (c) a rubber toughening component; (d) a surface modified component; and (e) an adhesion promoter. Cured products of the inventive cyanoacrylate compositions demonstrate improved toughness without an odor typically found with cyanoacrylate- containing compositions.

Brief Description of Related Technology

[0002] Cyanoacrylate adhesive compositions are well known, and widely used as quick setting, instant adhesives with a wide variety of uses. See H.V. Coover, D.W. Dreifus and J.T.

O'Connor, "Cyanoacrylate Adhesives" in Handbook of Adhesives, 27, 463-77, I. Skeist, ed., Van Nostrand Reinhold, New York, 3rd ed. (1990) . See also G.H. Millet, "Cyanoacrylate Adhesives" in Structural Adhesives: Chemistry and Technology, S.R. Hartshorn, ed., Plenun Press, New York, p. 249-307 (1986).

[0003] U.S. Patent No. 4,440,910 (O'Connor) pioneered rubber toughened cyanoacrylate compositions through the use of certain organic polymers as toughening additives that are elastomeric, i.e., rubbery, in nature. The '910 patent is thus directed to and claims a curable adhesive comprising a substantially solvent-free mixture of: (a) a cyanoacrylate ester, and (b) about 0.5% to about 20% by weight of an elastomeric polymer. The elastomeric polymer is selected from elastomeric copolymers of a lower alkene monomer and (i) acrylic acid esters, (ii) methacrylic acid esters or (iii) vinyl acetate. More

specifically, the ' 910 patent notes that as toughening additives for cyanoacrylates , acrylic rubbers; polyester urethanes;

ethylene-vinyl acetates; fluorinated rubbers; isoprene- acrylonitrile polymers; chlorosulfinated polyethylenes ; and homopolymers of polyvinyl acetate were found to be particularly useful .

[0004] The elastomeric polymers are described in the ' 910 patent as either homopolymers of alkyl esters of acrylic acid; copolymers of another polymerizable monomer, such as lower alkenes, with an alkyl or alkoxy ester of acrylic acid; and copolymers of alkyl or alkoxy esters of acrylic acid. Other unsaturated monomers which may be copolymerized with the alkyl and alkoxy esters of acrylic include dienes, reactive halogen- containing unsaturated compounds and other acrylic monomers such as acrylamides.

[0005] Conventional commercial ethyl cyanoacrylate

compositions have an odor, which some end users find offensive. β-methoxy ethyl cyanoacrylate is known to not have the same odor. Ethyl cyanoacrylate compositions are also known to show blooming when cured, which tends to be absent with β-methoxy ethyl cyanoacrylate.

[0006] Today there are no toughened, low odor/low bloom cyanoacrylate products commercially available in the market. Commercially available toughened cyanoacrylate products are predominately based on ethyl cyanoacrylate monomer and exhibit (1) an odor that some end users find offensive and/or (2) sometimes blooming when cured.

[0007] Commercially available cyanoacrylate products are often toughened with an ethylene : methyl methacrylate terpolymer. This polymer contributes little toughness to cyanoacrylate compositions containing β-methoxy ethyl cyanoacrylate, one reason for which may be that the polymer shows sparing

solubility in β-methoxy ethyl cyanoacrylate.

[0008] Notwithstanding the state of the art and the efforts to date to improve the toughness of β-alkoxyalkyl cyanoacrylate compositions, there remained a long felt, yet unmet, need to provide toughness to cured reaction products of such

cyanoacrylate compositions, and while doing so minimize the odor and/or blooming oftentimes associated with cyanoacrylate

compositions. Until now.

SUMMARY

[0009] Cyanoacrylate compositions (a) a β-alkoxyalkyl

cyanoacrylate component, (b) a cyanoacrylate component selected from butyl cyanoacrylates , octyl cyanoacrylates , and

combinations thereof; (c) a rubber toughening component; (d) a surface modified component; and (e) an adhesion promoter, are thus provided.

[0010] The inclusion of the β-alkoxyalkyl cyanoacrylate component provides a cyanoacrylate base for the composition that does not emit an odor commonly found in cyanoacrylate

compositions. The cyanoacrylate component recited above

provides a vehicle by which to introduce a rubber toughening component to the β-alkoxyalkyl cyanoacrylate component. The rubber toughening component provides for improved toughness, as is shown in the Examples. Rubber toughening components are sometimes known to show sparing solubility in cyanoacrylate compositions, particularly cyanoacrylate compositions containing beta-alkoxyalkyl cyanoacrylates . As a result, the toughness observed in prior attempts has been limited at best. The cyanoacrylate component recited above aids in that regard.

[0011] This invention is also directed to a method of bonding together two substrates, which method includes applying to at least one of the substrates a composition as described above, and thereafter mating together the substrates.

[0012] In addition, the present invention is directed to reaction products of the inventive compositions.

[0013] Also, the invention is directed to a method of preparing the inventive compositions, and a method of conferring improved toughness to a cured reaction product of a

cyanoacrylate composition, while minimizing the odor oftentimes associated with cyanoacrylate compositions as well as bloom sometimes observed with cured product thereof.

[0014] The invention will be more fully understood by a reading of the section entitled "Detailed Description", which follows .

DETAILED DESCRIPTION

[0015] As noted above, this invention is directed to a cyanoacrylate composition comprising (a) a β-alkoxyalkyl cyanoacrylate component, (b) a cyanoacrylate component selected from butyl cyanoacrylates, octyl cyanoacrylates, and

combinations thereof; (c) a rubber toughening component; (d) a surface modified component; and (e) an adhesion promoter.

[0016] The β-alkoxyalkyl cyanoacrylate component (a) may be chosen from β-methoxymethyl cyanoacrylate, β-methoxyethyl cyanoacrylate, β-ethoxymethyl cyanoacrylate, β-ethoxyethyl cyanoacrylate and combinations thereof. Particularly desirable among those β-alkoxyalkyl cyanoacrylates is β-methoxyethyl cyanoacrylate .

[0017] The β-alkoxyalkyl cyanoacrylate component (a) should be included in the compositions in an amount within the range of from about 40% to about 90% by weight, such as from about 55% to about 85% by weight, for example from about 55% to about 80% by weight being desirable, with the range of about 55% to about 75% by weight being particularly desirable, and about 60% by weight of the total composition being particularly suitable.

[0018] The cyanoacrylate component (b) may be selected from butyl cyanoacrylates (such as n-butyl cyanoacrylate), octyl cyanoacrylates (such as n-octyl cyanoacrylate), and combinations thereof .

[0019] The cyanoacrylate component (b) should be included in the compositions in an amount within the range of from about 5% to about 50% by weight, such as from about 5% to about 30% by weight, suitably from about 7% to about 27% by weight. About 10% to about 30% by weight may be employed, with the range of about 20% to about 35% by weight being desirable, and about 30% by weight of the total composition being particularly desirable.

[0020] Suitably, the β-alkoxyalkyl cyanoacrylate component (a) and the cyanoacrylate component (b) are present in the composition in a by weight ratio of from about 55 to about

85: about 5 to about 30.

[0021] The rubber toughening component (c) may be selected from (i) reaction products of the combination of ethylene, methyl acrylate and monomers having carboxylic acid cure sites, (ii) dipolymers of ethylene and methyl acrylate, (iii)

vinylidene chloride-acrylonitrile copolymers, (iv) vinyl chloride/vinyl acetate copolymer, (v) copolymers of polyethylene and polyvinyl acetate, and combinations thereof.

[0022] Desirably, the reaction products (c) (i) of the combination of ethylene, methyl acrylate and monomers having carboxylic acid cure sites, where the reaction products are substantially free of release agents, anti-oxidants , stearic acid and polyethylene glycol ether wax, β-alkoxyalkyl

cyanoacrylate are chosen for use. DuPont supplies such a reaction product under the trade name VAMAC VCS 5500.

[0023] The rubber toughening component (c) should be included in the compositions in an amount within the range of from about 3% to about 20% by weight, with the range of about 5% to about 15% by weight being desirable, and about 8% by weight of the total composition being particularly desirable.

[0024] A particularly interesting additive is a surface modified component, which may take many forms. See e.g. U.S. Patent No. 8,609,780 (Misiak) . For instance, Inhance/Fluoro- Seal, Ltd . s ' surface-modification technology is a controlled oxidat which a reactive gas atmosphere modifies the outermost molecular layer of a particle/ fiber/plastic/ film or fabric . The treatment causes the molecular backbone and/or side chains to react, resulting in formation of polar functional groups on tIn6 su.-t fel C6 su.ch. as hydroxyls and carboxylates .

[0025] According to Inhance ' s we ese oxygen- containing chemical functionalitieS Ccl ^" LIse the trea

to have high surface energy . This in turn means that the treated particles are readily wetted and dispersed in polar polymers , such as polyols . The surface modification also results in stronger bonding between the particles (or fibers ) and the matrix resin . The enhanced adhesion is a result of chemical bonding with surface functionalities and hydrogen . See www.inhanceproducts.com/technology.html, Aug. 10, 2006.

[0026] Commercially available surface modified polyolefins from Inhance include those in the family described as INHANCE® UH-1000 and HD-1000 series particles. Specific representatives of that family include those designated as UH-1045 (having an average size of 300 μπι) , UH-1080 (having an average size of 125 μιτι) , UH-1200 (having an average size of 63 μπι) , UH-1250 (having an average size of 53 μπι) , UH-1500 (having an average size of 45 μπι) , UH-1700 (having an average size of 38 μιτι) and HD-1800 (having an average size of 18 μιτι) .

[ 0027 ] INHANCE® UH-1000 series particles are free flowing white particles or powder, derived from virgin UHMWPE resin, and having the following general properties :

Surface Energy : 55+ dynes/cm (water wettable)

Specific Gravity: 0.93-0.94

Bulk Density: 20-31 lb. /ft ³ (0.32-0.50 g/cc)

Molecular Weight: 3,000,000-5,000,000

[ 0028 ] INHANCE® UH-1000 Series Particles are reported to provide composites with superior abrasion resistance, reduced coefficient of friction, enhanced work of fracture and improved moisture barrier .

[ 0029 ] Another particularly interesting additive is an adhesion promoter, such as phosphoric acid and anhydrides, like itaconic anhydride.

[ 0030 ] Suitably, the β-alkoxyalkyl cyanoacrylate component (a) is present in an amount of from about 55% to about 80% by weight, and the cyanoacrylate component is present in an amount of from about 7% to about 27% by weight, based on the total weight of the composition. [0031] The cyanoacrylate component (b) may be present in about a 30:70 by weight ratio with the β-alkoxyalkyl

cyanoacrylate (a) .

[0032] Accelerators may also be included in the inventive cyanoacrylate compositions, such as any one or more selected from calixarenes and oxacalixarenes , silacrowns, crown ethers, cyclodextrins , poly (ethyleneglycol) di (meth) acrylates ,

ethoxylated hydric compounds and combinations thereof.

[0033] Of the calixarenes and oxacalixarenes, many are known, and are reported in the patent literature. See e.g. U.S. Patent Nos. 4,556,700, 4,622,414, 4,636,539, 4,695,615, 4,718,966, and 4,855,461, the disclosures of each of which are hereby expressly incorporated herein by reference.

[0034] For instance, as regards calixarenes, those within the following structure are us

where R ¹ is alkyl, alkoxy, substituted alkyl or substituted alkoxy; R ² is H or alkyl; and n is 4, 6 or 8.

[0035] One particularly desirable calixarene is tetrabutyl tetra [2-ethoxy-2-oxoethoxy] calix-4-arene .

[0036] A host of crown ethers are known. For instance, any one or more of 15-crown-5, 18-crown-6, dibenzo-18-crown- 6 , benzo-15-crown-5-dibenzo-24-crown-8 , dibenzo-30-crown-10 , tribenzo-18-crown-6, asym-dibenzo-22-crown-6, dibenzo-14-crown- 4, dicyclohexyl-18-crown-6, dicyclohexyl-24-crown-8, cyclohexyl- 12-crown-4, 1 , 2-decalyl-15-crown-5 , 1 , 2-naphtho-15-crown-5 , 3 , 4 , 5-naphtyl-l 6-crown-5 , 1 , 2-methyl-benzo-18-crown-6, 1,2- methylbenzo-5 , 6-methylbenzo-18-crown-6, 1, 2-t-butyl-18-crown-6, 1, 2-vinylbenzo-15-crown-5, 1, 2-vinylbenzo-18-crown-6, 1,2-t- butyl-cyclohexyl-18-crown- 6 , asym-dibenzo-22-crown-6 and 1,2- benzo-1 , 4-benzo-5-oxygen-20-crown-7 may be used. See U.S.

Patent No. 4,837,260 (Sato), the disclosure of which is hereby expressly incorporated herein by reference. Of the silacrowns, again many are known, and are reported in the literature.

[0037] Specific examples of silacrown compounds useful in the inventive compositions include:

dimethylsila-ll-crown-4 ;

imethylsila-14-crown

and dimethylsila-17-crown-6.

See e.g. U.S. Patent No. 4,906,317 (Liu), the disclosure of which is hereby expressly incorporated herein by reference.

[0038] Many cyclodextrins may be used in connection with the present invention. For instance, those described and claimed in U.S. Patent No. 5,312,864 (Wenz), the disclosure of which is hereby expressly incorporated herein by reference, as hydroxyl group derivatives of an α, β or γ-cyclodextrin which is at least partly soluble in the cyanoacrylate would be appropriate choices for use herein as the first accelerator component. [0039] For instance, poly (ethylene glycol) di (meth) acrylates suitable for use herein include those within the following structure :

where n is greater than 3, such as within the range of 3 to 12, with n being 9 as particularly desirable. More specific

examples include PEG 200 DMA, (where n is about 4) PEG 400 DMA (where n is about 9), PEG 600 DMA (where n is about 14), and PEG 800 DMA (where n is about 19), where the number (e.g. , 400) represents the average molecular weight of the glycol portion of the molecule, excluding the two methacrylate groups, expressed as grams/mole (i.e., 400 g/mol) . A particularly desirable PEG DMA is PEG 400 DMA.

[0040] And of the ethoxylated hydric compounds (or ethoxylated fatty alcohols that may be employed) , appropriate ones may be chosen from those within the following structure: c— rex -ctri

where C _m can be a linear or branched alkyl or alkenyl chain, m is an integer between 1 to 30, such as from 5 to 20, n is an integer between 2 to 30, such as from 5 to 15, and R may be H or alkyl, such as Ci-6 alkyl.

[0041] When used, the accelerator should be included in the compositions in an amount within the range of from about 0.01% to about 10% by weight, with the range of about 0.1 to about 0.5% by weight being desirable, and about 0.4% by weight of the total composition being particularly desirable.

[0042] A stabilizer package is also ordinarily found in cyanoacrylate compositions. The stabilizer package may include one or more free radical stabilizers and anionic stabilizers, each of the identity and amount of which are well known to those of ordinary skill in the art. See e.g. U.S. Patent Nos .

5,530,037 and 6,607,632, the disclosures of each of which are hereby incorporated herein by reference.

[0043] Other additives may be included in the inventive cyanoacrylate compositions, such as certain acidic materials (like citric acid), thixotropy or gelling agents, thickeners, dyes, and combinations thereof.

[0044] Of the accelerators and these additives, those listed in the table below are desirable examples, particularly in the amounts noted.

[0045] In addition, the cyanoacrylate component may include further cyanoacrylate monomers which may be chosen with a raft of substituents , such as those represented by H2C=C (CN) -COOR, where R is selected from Ci-15 alkyl, alkoxyalkyl, cycloalkyl, alkenyl, aralkyl, aryl, allyl and haloalkyl groups. Desirably, the cyanoacrylate monomer is selected from methyl cyanoacrylate, ethyl-2-cyanoacrylate , propyl cyanoacrylates , allyl

cyanoacrylate, and combinations thereof. [0046] In another aspect of the invention, there is provided a method of bonding together two substrates, which method includes applying to at least one of the substrates a

composition as described above, and thereafter mating together the substrates for a time sufficient to permit the adhesive to fixture .

[0047] In yet another aspect of the invention, there is provided reaction products of the so-described compositions.

[0048] In still another aspect of the invention, there is provided a method of preparing the so-described compositions. The method includes providing (a) a β-akloxyalkyl cyanoacrylate component, and combining therewith with mixing (b) a

cyanoacrylate component selected from butyl cyanoacrylates, octyl cyanoacrylates, and combinations thereof; (c) a rubber toughening component, where desirably the rubber toughening component is dissolved in the cyanoacrylate component in an amount of up to about 20% by weight; (d) a surface modified component; and (e) an adhesion promoter.

[0049] The invention will be further illustrated by the examples which follow.

EXAMPLES

[0050] Sample A was prepared from the constituents in the by weight percentages as set forth in Table A below. Sample A contained n-butyl cyanoacrylate.

Table A

β-Methoxyethyl cyanoacrylate 59.36

n-Butyl cyanoacrylate 25.44

Itaconic anhydride 1.25

Phosphoric acid 0.25 MMBP 0.05

Sulfur dioxide 0.70

Methane sulfonic acid 1.20

Crown Ether 0.25

VAMAC MR 10.00

Silica 1.00

INHANCE® microparticles UH-1045 0.50

[0051] Samples B-D were prepared in a similar fashion and are set forth in Table B below. Samples B-D contained octyl cyanoacrylate .

Table B

B

β-Methoxyethyl cyanoacrylate 76. .32 67. .84 59. .36 n-Octyl cyanoacrylate 8. .48 16. .96 25. .44

Itaconic anhydride 1. .25 1. .25 1. .25

Phosphoric acid 0. .25 0. .25 0. .25

MMBP 0. .05 0. .05 0. .05

Sulfur dioxide 0. .70 0. .70 0. .70

Methane sulfonic acid 1. .20 1. .20 1. .20

Crown Ether 0. .25 0. .25 0. .25

VAMAC MR 10. .00 10. .00 10. .00

Silica 1. .00 1. .00 1. .00

INHANCE® microparticles UH-1250 0. .50 0. .50 0. .50

[0052] To each of Samples A-D MMBP was added in an amount of 0.05 by weight percent as a free radical stabilizer. MMBP is 2 , 2 -Methylenebis- ( 4-methyl-6-tert-butylphenol) .

[0053] The samples were then evaluated on mild steel substrates and aluminum substrates at room temperature and/or a temperature of 80°C over the time period noted in days for T Peel strength performance (measured in N/mm) . The results are captured below in Tables C and D.

Table C

Table D

[0054] These results seem to indicate that the data for room temperature ageing on mild steel substrates show little or substantially no change. In other words on mild steel

substrates the samples show a maintenance of T Peel performance on mild steel substrates. However, data for room temperature ageing on aluminum substrates show a decrease in

performance. No substantial difference in performance is seen between samples having butyl cyanoacrylate and those having octyl cyanoacrylate.

[0055] At elevated temperature conditions over time, Sample A shows an increase in performance over time on mild steel substrates and maintenance of performance over time on aluminium substrates .