Login| Sign Up| Help| Contact|

Patent Searching and Data


Title:
METHODS FOR PURIFYING CARBON MATERIALS
Document Type and Number:
WIPO Patent Application WO/2005/089422
Kind Code:
A2
Abstract:
Methods of purifying samples are provided that are capable of removing carbonaceous and noncarbonaceous impurities from a sample containing a carbon material having a selected structure. Purification methods are provided for removing residual metal catalyst particles enclosed in multilayer carbonaceous impurities in samples generate by catalytic synthesis methods. Purification methods are provided wherein carbonaceous impurities in a sample are at least partially exfoliated, thereby facilitating subsequent removal of carbonaceous and noncarbonaceous impurities from the sample. Methods of purifying carbon nanotube-containing samples are provided wherein an intercalant is added to the sample and subsequently reacted with an exfoliation initiator to achieve exfoliation of carbonaceous impurities.

Inventors:
DAILLY ANNE (US)
AHN CHANNING (US)
RACHID YAZAMI (US)
FULTZ BRENT T (US)
Application Number:
PCT/US2005/008897
Publication Date:
September 29, 2005
Filing Date:
March 16, 2005
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
CALIFORNIA INST OF TECHN (US)
DAILLY ANNE (US)
AHN CHANNING (US)
RACHID YAZAMI (US)
FULTZ BRENT T (US)
International Classes:
C01B31/02; C01B31/04; D01F9/12; D01F11/12; D06M11/83
Foreign References:
US20030224168A12003-12-04
US20020127171A12002-09-12
US20050006623A12005-01-13
US20040131859A12004-07-08
Attorney, Agent or Firm:
Barone, Stephen B. (Winner & Sullivan P.C., 4875 Pearl East Circle, Suite 20, Boulder CO, US)
Download PDF:
Claims:
We claim:
1. A method of purifying a sample containing a carbon material having a selected structure said method comprising the steps of: providing said sample containing said carbon material having a selected structure and impurities comprising carbonaceous Impurities, wherein said carbonaceous impurities comprising one or more carbon layers having a structure different than that of said selected structure; exfoliating at least a portion of the carbon layers of said carbonaceous impurities, thereby generating exfoliated carbonaceous material; and removing said impurities, thereby purifying said sample containing a carbon material having a selected structure.
2. The method of claim 1 wherein said step of removing said impurities comprises oxidizing the exfoliated carbonaceous material.
3. The method of claim 1 wherein said step of removing said impurities comprises preferentially oxidizing said exfoliated carbonaceous material such that the carbon material having a selected structure is not substantially oxidized.
4. The method of claim 1 wherein said step of removing said impurities comprises oxidizing said exfoliated carbonaceous materials in air at a temperature selected from the range of about 250 degrees Celsius to about 450 degrees Celsius.
5. The method of claim 4 wherein said step of removing said impurities comprises oxidizing said exfoliated carbonaceous materials in the presence of air having a relative humidity selected from the range of about 50 percent to about 100 percent.
6. The method of claim 1 wherein said impurities comprise metal particles, wherein said metal particles are at least partially enclosed by a plurality of said carbon layers, wherein said step of exfoliating at least a portion of said multilayer carbonaceous impurities exfoliates at least a portion of said carbon layers enclosing said metal particles, thereby exposing the surface of said metal particles.
7. The method of claim 6 wherein said step of removing said impurities comprises oxidizing said metal particles, thereby generating oxidized metal particles, wherein the volume of said metal particles increases upon oxidation, thereby disrupting said carbon layers enclosing said metal particles further exposing said rnetal surface of said oxidized metal particles.
8. The method of claim 6 wherein said step of removing said impurities comprises dissolving said metal particles.
9. The method of claim 6 wherein said step of removing said impurities comprises dissolving said metal particles into an acidic solution.
10. The method of claim 9 wherein said step of dissolving said metal particles into an acidic solution comprises refluxing said sample in concentrated hydrochloric acid.
11. The method of claim 6 wherein said metal particles comprise one or more transition metals.
12. The method of claim 6 wherein said metal particles comprise one or more metals selected from the group consisting of: nickel; yttrium; iron; molybdenum; palladium copper; molybdenum; and cobalt. To.
13. I he method ot claim 1 wherein said step of exfoliating at least a portion of the carbon layers of said carbonaceous impurities comprises adding an intercalant to said sample.
14. The method of claim 13 wherein said intercalant inserts into interstitial sites in between multiple carbon layers comprising said carbonaceous impurities, interstitial sites between carbon layers comprising said carbonaceous impurities and said carbon material having a selected structure or both, thereby generating intercalated carbon layers.
15. The method of claim 14 wherein said intercalant is electrochemically intercalated into said carbon layers by application of an electric potential or electric current to said sample.
16. The method of claim 14 wherein said carbon layers comprise a material selected from the group consisting of: graphene layers; graphite layers; and amorphous carbon layers.
17. The method of claim 14 wherein said step of exfoliating at least a portion of the carbon layers of said layer carbonaceous impurities comprises adding an exfoliation initiator which reacts with said intercalant in said intercalated carbon layers.
18. The method of claim 17 wherein said intercalant in said intercalated carbon layers and said exfoliation initiator undergo an exothermic reaction.
19. The method of claim 17 wherein said intercalant in said intercalated carbon layers, and said exfoliation initiator undergo a reaction generating a gas phase product.
20. The method of claim 17 wherein said intercalant is potassium and said exfoliation initiator is ethanol.
21. The method of claim 20 further comprising the step of reacting said intercalated carbon layers with ethanol.
22. The method of claim 14 wherein said step of exfoliating at least a portion of the carbon layers of said carbonaceous impurities further comprises increasing the temperature of said sample.
23. The method of claim 13 wherein said intercalant is an electron donor intercalant.
24. The method of claim 23 wherein said electron donor intercalant is an alkali metal.
25. The method of claim 13 wherein said intercalant is an electron acceptor intercalant.
26. The method of claim 25 wherein said electron acceptor intercalant is selected from the group consisting of: a halogen; a metal chloride; nitric acid; perchloric acid; sulfuric acid; and formic acid.
27. The method of claim 13 wherein said step of exfoliating at least a portion of the carbon layers of said carbonaceous impurities comprises adding an additional intercalant to said sample, wherein said add itional intercalant inserts between at least a portion of said carbon layers of said carbonaceous impurities, thereby generating bi intercalated carbon layers.
28. The method of claim 1 wherein said carbon material having a selected structure is a single walled carbon nanotube and said impurities are selected from the group consisting of: graphene layers; 4O graphite; amorphous carbon; multiwalled carbon nanotubes; and metal particles.
29. The method of claim 1 wherein said carbon material having a selected structure is a multiwalled carbon nanotube and said impurities are selected from the group consisting of: graphene layers; graphite; amorphous carbon; and metal particles.
30. The method of claim 1 wherein said carbon material having a selected structure is a fullerene and said impurities are selected from the group consisting of: graphene layers; graphite; amorphous carbon; and metal particles.
31. The method of claim 1 wherein said carbon material having a selected structure is a carbon fiber; and said impurities are selected from the group consisting of: graphene layers; graphite; amorphous carbon; and metal particles.
32. The method of claim 1 wherein said carbon material having a selected structu re is a carbon film; and said impurities are selected from the group consisting of: graphene layers; graphite; amorphous carbon; and metal particles.
33. The method of claim 1 wherein said carbon material having a selected structure is diamond; and said impurities are selected from th& group consisting of: graphene layers; graphite; amorphous carbon; and metal particles.
34. The method of claim 1 wherein said sample is prepared using a synthesis method selected from the group consisting of: arcdischarge methods; chemical vapor deposition methods; plasma enhanced chemical vapor deposition methods; high pressure carbon monoxide disproportionation methods; pyrolytic methods; flame synthesis methods; electrochemical methods; and laser ablation methods.
35. The method claim 1 further comprising the step of annealing said sample after removing said impurities.
36. The method of claim 35 wherein the temperature of said sample is raised to a temperature selected from the range of about 65O degrees Celsius to about 850 degrees Celsius during annealing.
37. A method of exfoliating at least a portion of a plurality of carbon layers at least partially enclosing metal particles in a sample generated in the synthesis of carbon nanotubes; said method comprising the steps of: providing said sample generated in the synthesis of carbon nanotubes containing carbon nanotubes and said metal particles, wherein each metal particle is at least partially enclosed by said ca rbon layers; adding an intercalant to said sample, wherein said intercalant inserts between at least a portion of said carbon layers, thereby generating intercalated carbon layers; and adding an exfoliation initiator to said sample which reacts with intercalant present between said carbon layers, thereby exfoliating at least a portion of said carbon layers at least partially enclosing metal particles.
38. The method of claim 37 wherein said intercalant is potassium and said exfoliation initiator is ethanol.
39. The method of claim 37 wherein said intercalant in said intercalated carbon layers and said exfoliation initiator undergo an exothermic reaction.
40. The method of claim 37 wherein said sample is prepared using a synthesis technique selected from the group consisting of: arcdischarge methods; chemical vapor deposition methods; tube furnace methods; pyrolytic methods; electrochemical methods; and laser ablation methods.
41. A method of removing carbonaceous coatings from the outer surfaces of carbon nanotubes; said method comprising the steps of: providing a sample comprising said carbon nanotubes, wherein at least a portion of the outer surfaces of said nanotubes are partially or completely coated with said carbonaceous coatings, and w/herein said carbonaceous coatings have a structure different from that of said nanotubes; adding an intercalant to said sample, wherein said intercalant inserts into interstitial sites between said nanotubes and said carbonaceous coating, thereby generating intercalated carbon layers; and adding an exfoliation initiator to said sample which reacts with intercalant in said intercalated carbon layers, wherein the reaction between said intercalant present between said carbon nanotubes and said carbonaceous coating and said exfoliation initiator exfoliates said carbonaceous coating, thereby removing said carbonaceous coatings from the outer surfaces of said carbon nanotubes.
42. The method of claim 41 wherein said intercalant is potassium and said exfoliation initiator is ethanol.
43. The method of claim 41 wherein said intercalant in said intercalated carbon layers and said exfoliation initiator undergo an exothermic reaction.
44. The method of claim 41 wherein said sample generated in the synthesis of carbon nanotubes is prepared using a synthesis technique selected from the group consisting of: arcdischarge methods; chemical vapor deposition methods; tube furnace methods; pyrolytic methods; electrochemical methods; and laser ablation methods.
45. A method of purifying a sample containing single walled nanotubes, said method comprising the steps of: providing said sample containing said single walled nanotubes and impurities comprising metal particles, wherein said metal particles are at least partially enclosed by a plurality of carbon layers having a structure different from that of said carbon nanotubes; adding an intercalant to said sample, wherein said intercalant inserts between at least a portion of said carbon layers enclosing said metal particles, thereby generating intercalated carbon layers; and adding an exfoliation initiator which reacts with intercalant in said intercalated carbon layers, thereby exfoliating at least a portion of said carbon layers and exposing the surface of said metal particles; and refluxing said sample in concentrated hydrochloric acid, thereby d issolving said metal particles and purifying said sample containing single walled nanotubes.
46. The method of claim 45 wherein said intercalant is potassium and said exfoliation initiator is ethanol, and wherein potassium present between said carbon layers and ethanol undergo an exothermic reaction generating a gas phase product.
47. The method of claim 45 comprising the step of reacting said intercalated carbon layers with ethanol.
48. A method of purifying a sample containing carbon fibers, said method comprising the steps of: providing said sample containing said carbon fibers and impurities comprising metal particles, wherein said metal particles are at least partially enclosed by a plurality of carbon layers; adding an intercalant to said sample, wherein said intercalant inserts between at least a portion of said carbon layers enclosing said metal particles, thereby generating intercalated carbon layers enclosing said metal particles; and adding an exfoliation initiator which reacts with intercalant in said intercalated carbon layers enclosing said metal particles, thereby exfoliating at least a portion of said carbon layers and exposing the surface of said metal particles; and refluxing said sample in concentrated hydrochloric acid, th&reby dissolving said metal particles and purifying said sample containing carbon fibers.
49. The method of claim 48 wherein said carbon fibers are catalytically grown carbon nanofibers.
50. The method of claim 48 wherein said intercalant is potassium and said exfoliation initiator is ethanol, and wherein potassium present between said carbon layers and ethanol undergo an exothermic reaction generating a gas phase product.
51. The method of claim 48 comprising the step of reacting said intercalated carbon layers with ethanol.
Description:
METHODS FOR PURIFYING CARBON MATERIALS

CROSS-REFERENCE TO RELATED APPLICATIONS This application claims the benefit of U.S. provisional Patent Application 60/553,930 filed March 17, 2004, which is hereby incorporated by reference in its entirety to the extent not inconsistent with the disclosure herein.

BACKGROUND OF INVENTION Since their discovery in the early 1990s, carbon nanotubes have been the subject of intense scientific research directed toward developing techniques for synthesizing high quality nanotube materials, and evaluating their physical and chemical properties. Carbon nanotubes are allotropes of carbon comprising one or more cylindrically configured graphene sheets. Carbon nanotubes typically have small diameters (« 1 - 10 nanometers) and large lengths (up to several microns), and therefore may exhibit very large aspect ratios (length to diameter ratio « 103 to about 105). Nanotube materials are often classified on the basis of structure as either single walled carbon nanotubes (SWNTs) or multiwalled carbon nanotubes (MWNTs). Research over the past decade has demonstrated that carbon nanotube materials exhibit extraordinary mechanical, electrical and chemical properties, which has stimulated substantial interest in developing applied technologies exploiting these properties.

Single walled carbon nanotubes (SWNTs) are one class of carbon nanotubes which have been identified as potentially useful materials for a number of applied technologies. SWNTs are made up of a single, contiguous graphene sheet wrapped around and joined with itself to form a hollow, seamless tube having capped ends similar in structure to smaller fullerenes. SWNTs typically have very small diameters (~ 1 nanometer) and are often present in curled and looped configurations. The energy band structure of SWNTs varies considerably, and SWNTs exhibit either metallic or semiconductor electrical behavior depending on their precise molecular structure and diameter. Under some experimental conditions, SWNTs undergo efficient self assembly processes that generate bundles (or ropes) of SWNTs aligned along their lengths and strongly bound together by van der Waals forces. SWNTs are chemically versatile materials which have been demonstrated as capable of functionalization of their exterior surfaces and capable of encapsulation of materials within their hollow cores, such as gases and molten materials.

Research over the last decade has identified a number of unique properties of SWNTs which make these materials particularly promising candidate materials for a variety of device applications ranging from a revolutionary class of new electronic devices to composite materials having enhanced mechanical properties. First, SWNTs are believed to have remarkable mechanical properties suggesting their utility as structural reinforcement additives in high strength, low weight and high performance composite materials. For example, calculations and experimental results suggest that the SWNTs have tensile strengths at least 100 times that of steel or any known other known fiber. In addition, SWNTs are suffer than conventional reinforcement materials, such as carbon fibers, while also exhibiting a very large Young's Modulus (as large as about 1 TPa) when distorted in some directions. Second, SWNTs exhibit useful electrical properties which may serve the basis of a new class of nanotube based electronic devices. For example, the electron transport behavior in carbon nanotubes is predicted to be essentially that of a quantum wire, which has stimulated interest in fabricating ultrafast nanotube based devices. In addition, the electrical properties of SWNTs have been observed to vary significantly upon charge transfer doping and intercalation, which has opened up new avenues for tuning the electrical properties of these materials. Further, due to their nanometer size diameter, mechanical robustness, chemical stability and high electrical conductivity, SWNTs may provide enhanced field emitters in a range of devices, including flat panel displays, AFM tips and electron microscopes. Finally, SWNTs are also believed to possess useful thermal, magnetic and optical properties which make them suitable materials for a range of emerging applied technologies.

The unique chemical and physical characteristics of carbon nanotubes is often severely attenuated or entirely lost when these materials are present with substantial amounts of impurities. Therefore, the successful development of nanotube based technologies taking full advantage of their extraordinary properties depends critically on the availability of sources of substantially pure nanotube materials. Currently available methods for synthesizing SWNTs, however, do not directly result in substantially pure samples containing these materials. Rather, conventional synthesis processes, such as techniques utilizing arc discharge, laser ablation, and chemical vapor deposition, yield a complex reaction product comprising a mixture of SWNTS, carbonaceous impurities and noncarbonaceous impurities. The impurity component of the reaction product generated using many of these techniques is very significant and SWNTs often comprise less than half of the reaction product by weight. Carbonaceous impurities generated in conventional synthesis processes are present in both single layer and multilayer configurations and include amorphous carbon, graphene sheets, graphite, incomplete and complete fullerenes and multiwalled nanotubes. Noncarbonaceous impurities commonly present in SWNT containing samples include residual metal catalyst particles, such as particles comprising nickel, yttrium, iron, molybdenum, palladium, and cobalt, and catalyst support materials, such as ceramic materials.

As a result of associative intermolecular interactions, such as van der Waals interactions, impurities and SWNTs in samples prepared via conventional synthesis techniques are present in highly coupled physical states. For example, the outer surfaces of SWNTs and bundles of SWNTs are typically heavily coated with a variety of single and multilayer carbonaceous impurities. In addition, metal catalyst particles unavoidably generated in catalytic synthesis methods are often entirely or partially encapsulated in high stable multilayers comprising carbonaceous impurities. Associative intermolecular interactions involving these materials present a unique challenge for purifying and isolating SWNTs in samples prepared by conventional synthesis methods. For example, the carbon multilayers surrounding metal catalyst particles severely reduce the effectiveness of purification via dissolution of the particles in acids provided to the sample. In addition, associative interactions between carbonaceous impurities and SWNTs pose significant problems for positioning, aligning and/or integrating SWNTs into desired device configurations.

Significant research has been direct toward developing methods of isolating and purifying SWNTs, due to the inability of conventional synthesis methods to directly produce substantially pure samples of high quality carbon nanotubes. Effective purification methods are capable of removing the wide range of different impurities that exhibit markedly different chemical and physical properties. In addition, effective purification methods are capable of selectively removing a majority of these impurities without causing significant damage to or destruction of the SWNTs. Furthermore, effective purification methods are capable high throughout processing of significant quantities of SWNTs in a relatively small number of efficient purification steps, thereby avoiding unreasonably long processing times.

A number of different approaches have been pursued in recent years for purifying SWNT containing samples. First, several techniques have been developed that are based on chemically modifying impurities to enhance their removal, including selective oxidation processes, such as gas phase oxidation, catalytic oxidation and acid oxidation, and nitric acid and hydrogen peroxide reflux methods. Although chemical modification techniques have been demonstrated as capable of enhancing the purity of SWNT containing samples, these treatments invariably destroy a significant portion of the SWNTs present in the sample, and are not effective at removing metal particulate impurities enclosed in carbon multilayers. Second, purification methods have been pursued based on microfiltration and cross flow filtration techniques. These techniques require a relatively large number of repeated filtration and suspension processing steps, however, making the procedures relatively slow and inefficient. Finally, purification of SWNTs via size exclusion chromatography has also been demonstrated. However, this approach requires use of surfactants for suspension of the SWNTs in the sample undergoing chromatographic separation, which can result in residual surfactant in the purified sample that can deleteriously affect the chemical and physical properties of the purified nanotubes.

The following references relate generally to methods of synthesizing and purifying carbon nanotubes: (1 ) A. M. Cassell, J. A. Raymakers, J. Kong, H. J. Dai, J. Phys. Chem. B 103(31 ), (1999), pp. 6484-6492; (2) M. Su, B. Zheng, J. Liu, Chem. Phys. Lett. 322(5), (2000), pp. 321-326; (3) B. Kitiyanan, W. E. Alvarez, J. H. Harwell, D. E. Resasco, Chem. Phys. Lett. 317(3-5), (2000), pp. 497-503; (4) J. H. Hafner, M. J. Bronikowski, B. R. Azamian, P. Nicolaev, A. G. Rinzler, D. T. Colbert, K. A. Smith, R. E. Smalley, Chem. Phys. Lett. 296(1-2), (1998) pp. 195-202 (5) H. M. Cheng, F. Li, G. Su, H. P. Pan, L. L. He, X. Sun, M. S. Dresselhaus, Appl. Phys. Lett. 72(25), (1998), pp. 3282-3284; (6) B. Zheng, Y. Li, J. Liu, Applied Physics A 74, 345-348 (2002); (7) C. Journet, W. K. Maser, P. Bernier, A. Loiseau, M. Lamy de Ia Chapelle, S. Lefrant, R. Lee, J. E. Fischer, Nature 388, 756-758 (1997); (8) A. Thess, R. Lee, P. Nikolaev, H. Dai, P. Petit, J. Robert, C. Xu, Y. H. Lee, S. G. Kim, A. G. Rinzler, D. T. Colbert, G. E. Scuseria, D. Tomanek, J. E. Fischer, R. E. Smalley, Science 273, (1996) 483-487; (9) M. Holzinger, A. Hirsch, P. Bernier, G. S. Duesberg, M. Burghard, Applied Physics A 70, (2000) 599-602; (10) G. S. Duesberg, J. Muster, V. Krstic, M. Burghard, S. Roth, Appl. Phys. A 67, (1998), 117-119; (11 ) J. Liu, A. G. Rinzler, H. Dai, J. H. Hafner, R. K. Bradley, P. J. Boul, A. Lu, T. Iverson, K. Shelimov, C. B. Huffman, F. Rodriuez-Macias, Y. S. Shon, T. R. Lee, D. T. Colbert, R. E. Smalley, Science 280, (1998) 1253-1256; (12) A. G. Rinzler, J. Liu, H. Dai, P. Nikolaev, C. B. Huffman, F. J. Rodriguez-Macias, P. J. Boul, A. H. Lu, D. Heymann, D. T. Colbert, R. S. Lee, J. E. Fischer, A. M. Rao, P. C. Eklund, R. E. Smalley, Appl. Phys. A 67, (1998) 29-37; (13) Y. Feng, G. Zhou, G. Wang, M. Qu, Z. Yu, Chem, Phys, Lett, 375, (2003) 645-648; (14) T. Takenobu, M. Shiraishi, A. Yamada, M. Ata, H. Kataura, Y. Iwasa, Synthetic Metals 135-136, (2003) 787-788; (15) I. W. Chiang, B. E. Brinson, A. Y. Huang, P. A. Willis, M. J. Bronikowski, J. L. Margrave, R. E. Smalley, R. H. Hauge, J. Phys. Chem. B 105, (2001 ) 8297-8301.

It will be appreciated from the foregoing that there is currently a need in the art for improved methods for purifying carbon nanotube materials, particularly SWNTs, such that these materials can be effectively integrated into a range of applied technology settings. Specifically, methods are needed for purifying SWNT containing samples generated via conventional SWNT synthesis methods, such as samples comprising mixtures of SWNTS, a range of carbonaceous impurities and metal or metal oxide catalyst particles. In addition, purification methods are needed that provide high yields of high quality nanotube materials, thereby minimizing loss or damage to SWNTs in a sample undergoing purification. Further, low cost and versatile purification methods are needed that are compatible with high throughput processing of large amounts of SWNTs generated by the conventional synthesis techniques.

SUMMARY OF THE INVENTION The present invention provides processes for purifying samples comprising one or more desired forms of carbon by removing impurities from the sample. Purification methods of the present invention are capable of preferentially removing undesired impurities, thereby increasing the purity a desired carbon material having a selected structure in a sample. Methods of the present invention are capable of effectively removing impurities without substantially damaging or destroying the desired carbon material in a sample undergoing processing. In some embodiments, therefore, the present methods provide a means of purifying a selected carbon material such that the purified selected carbon material has a structure and composition that does not different significantly from its structure and composition in the starting material subject to processing or has a structure that is enhanced after processing via the present methods, such as a structure exhibiting enhanced extent of crystallinity. The present purification methods are versatile and, thus capable of generating a range of substantially pure carbon materials, including carbon nanotubes (SWNTS and MWNTs), fullerenes, and other carbon allotropes such as carbon fibers, carbon films and diamond, from samples generated by a range of synthesis methods, including, catalytic and noncatalytic processes. In one embodiment, the methods of the present invention provide a source of substantially pure, high quality carbon nanotubes, are compatible with high throughput processing of samples comprising large quantities of carbon nanotubes, and require substantially less processing steps than conventional methods of purifying carbon nanotubes.

The present purification methods selectively remove carbonaceous impurities, noncarbonaceous impurities and multiphase impurities having both a carbon- containing portion and a noncarbon-containing portion by exfoliating single and multilayer carbonaceous impurities having structures that differ from the structures of selected carbon materials in the sample. Exfoliation processes useful in the present methods disrupt the structure and arrangement of single and multilayer carbon impurities thereby making these materials more susceptible to removal via subsequent processing steps. Exfoliation of carbon impurities comprising a plurality of layers of graphene, graphite and/or amorphous carbon, for example, makes these materials susceptible to removal by gas phase oxidation at temperatures lower than those corresponding to the gas phase oxidation of thee materials in their unexfoliated forms. In embodiments of the present invention providing high yields of selected carbon materials, exfoliation is carried out under conditions wherein undesired carbonaceous impurities are at least partially exfoliated, while the desired, selected forms of carbon do not undergo substantial exfoliation and/or chemical degradation. Any exfoliation process capable of selectively disrupting the structure and arrangement of single and multilayer carbonaceous impurities may be used in the present purification methods, including methods wherein one or more intercalants are added to the sample and insert into interstitial sites between multilayers of carbonaceous impurities and/or into interstitial sites located between a selected carbon material and a carbonaceous impurities coating its outer surface.

The present invention provides methods that are particularly useful for purifying samples prepared by processes that yield a mixture of a desired carbon material, including carbon nanotubes (SWNTS and/or MWNTs), fullerenes, and/or other selected allotropes of carbon, and impurities comprising residual metal catalyst particles or catalyst support materials, such as transition metal or metal oxide particles partially or completely enclosed in multilayer carbonaceous impurities. In one embodiment, the present invention provides methods for at least partially exfoliating carbonaceous multilayers enclosing metal catalyst particles in a sample. This aspect of the present invention enhances subsequent removal of metal particles because exfoliation ruptures the structure of the carbonaceous layers thereby making the particles susceptible to removal via dissolution. Optionally, methods of this aspect of the present invention may further comprise the step of selectively removing the exfoliated carbonaceous multilayers, for example via wet oxidation, which further exposes the outer surfaces of the metal particles and enhances subsequent removal via dissolution. This aspect of the present invention provides versatile purification methods useful for increasing the purity of a desired carbon material in samples generated by virtually any catalytic synthesis techniques employing metal or metal based catalysts such as metal carbonyls.

In one aspect, the present invention provides a method of purifying a sample containing a carbon material having a selected structure wherein at least partial exfoliation of undesired single and multilayer carbonaceous impurities present in the sample allows for effective removal of impurities having a range of chemical compositions and physical states. A sample is provided containing the carbon material having a selected structure and impurities. The impurities present in the sample comprise carbonaceous impurities comprising one or more carbon layers having structures different than that of the selected carbon material undergoing purification. Optionally, the impurities present in the sample comprise noncarbonaceous impurities, such as metal particles and/or metal derivative particles such as metal oxide particles, and multiphase impurities, such as metal particles and/or metal derivative particles such as metal oxide particles partially or completely enclosed in multilayer carbonaceous impurities.

At least a portion of the carbon layers of the carbonaceous impurities are exfoliated, and the impurities are removed thereby purifying the sample . Exfoliation of at least a portion of the carbon layers in this method of the present invention allows for effective removal of carbonaceous impurities, noncarbonaceous impurities and multiphase impurities. In one embodiment, removal of exfoliated carbonaceous materials directly purifies the sample. Any method of removing exfoliated carbonaceous material may be used in the present methods provided that it does not substantially damage or destroy the selected carbon material undergoing purification, including but not limited to chemical transformation methods (e.g. wet oxidation and dissolution), filtration (e.g. cross flow or microfiltration methods) and chromatographic methods (e.g. size exclusion chromatography).

In another embodiment, exfoliation processing steps exfoliate at least a portion of carbon multilayers enclosing metal particles in the sample undergoing processing. In this embodiment, exfoliation at least partially exposes the surface of the metal particles, thereby allowing for their effective removal by a wide variety of removal methods. Removal of the exposed metal particles may be provided by any technique known in the art including, but not limited to, dissolution in a solution added to the sample, for example by refluxing the sample in a concentrated inorganic and/or organic acid, and/or treatment with an appropriate gas, for example by treatment with a halogen gas, such as chlorine at high temperatures (e.g. at or above about 900 degrees Celsius). Optionally, the purification methods of the present invention may further comprise the step of annealing the sample after the impurities have been removed. This optional step is beneficial in some applications as it may repair any damage to the carbon material having a selected structure that occurs during processing. It also removes residual reactant and solvant(s) and/or enhances the crystalline structure of the selected carbon material. Purification methods of the present invention are capable of enriching the purity of a single selected carbon material or plurality of different selected carbon materials. Selectivity in the present invention is provided by processing steps that are capable of exfoliating a selected set of materials corresponding to undesired impurities, while avoiding exfoliating or damaging to the desired carbon material(s) in the sample undergoing purification. In one embodiment, for example, the present invention provides methods for selectively enriching the purity of single walled carbon materials, such as SWNTs and/or single walled fullerenes, by selectively exfoliating carbonaceous materials that comprise a plurality of carbon multilayers, such as graphene multilayer structures, graphite multilayers, amorphous carbon multilayers, multiwalled fullerenes, MWTNs or any combination of these materials. Selective exfoliation in this aspect of the present invention allows for multilayer carbonaceous impurities to be efficiently removed, for example by selective oxidation, without significant loss of or damage to the desired single walled carbon materials. Alternatively, the present invention provides methods for selectively enriching the purity of one or more selected multilayer carbon structures, such as MWNTs, multiwalled fullerenes, diamond, carbon fibers, carbon films or any combination of these materials. In this embodiment, the exfoliation technique employed and experimental conditions of the sample (e.g. temperature, sample composition, composition of exfoliation initiator added to the sample etc.) are chosen such that undesired multilayered carbonaceous impurities are selectively exfoliated and subsequently removed, resulting in enhancement of the purity of the selected multilayer carbon structures in the sample.

Exfoliation of multilayer carbonaceous impurities can be carried out in any manner which promotes effective removal of impurities, while not substantially damaging or destroying the carbon materials having a selected structure in the sample. Exfoliation processes preferred for some application are rapid exothermic chemical reactions or physical changes that exfoliate carbonaceous materials without damaging desired components of a sample. In some embodiments, exfoliation is carried out by addition of one or more intercalants to the sample that insert into interstitial sites between carbon multilayers of multilayer carbonaceous impurities and/or insert into interstitial sites between a selected carbon material, such as SWNTs or MWNTs, and a carbonaceous impurity coating the outside of the selected carbon material.

In one embodiment of the present invention, addition of an intercalant generates intercalated carbon materials having intercalants present in interstitial sites between carbon multilayers comprising carbonaceous impurities. The presence of intercalants between the multilayers of carbonaceous impurities makes these materials susceptible to various selective exfoliation processes. For example, some intercalants weaken or disrupt the intermolecular or intramolecular forces between adjacent multilayers resulting in more selective and more complete exfoliation. Insertion of some intercalants of the present invention between multilayers results in an expansion of the interlayer distance separating adjacent multilayers and/or may provide a reactant for chemical reactions that initiate selective exfoliation of multilayer carbonaceous impurities.

Alternatively, addition of intercalants in the present invention generates intercalated carbon materials having intercalants present in interstitial sites between a selected carbon material and an impurity comprising a carbonaceous outer layer coating the selected carbon material. This aspect of the present invention is useful for disrupting associative interactions, such as van der Waals interactions, between impurities and desired carbon materials in a sample. In one embodiment, insertion of intercalants into interstitial sites between a selected carbon material and a layer comprising carbonaceous impurity provides a means of separating the selected carbon material from impurities that associatively interact with it. This aspect of the present invention is particularly useful for separating and removing single or multiple layer carbonaceous impurities coating the outer surfaces of SWNTs and MWNTs. This aspect of the present invention is useful for removing coatings of carbonaceous impurities on carbon nanotubes which affect their physical, electrical and chemical properties and present difficulties in integrating these materials into desired device configurations.

In one embodiment of the present invention, exfoliation is achieved by adding an exfoliation initiator to a sample containing one or more intercalants which reacts with intercalants in intercalated carbon layers, thereby initiating selective exfoliation. Exemplary exfoliation initiators react exothermically with intercalants in intercalated carbon layers and, optionally initiate an expansion of material present between carbon layers, for example by generating a gaseous reaction product. In another embodiment, exfoliation is achieved by subsequently raising the temperature of the intercalated carbon layers, for example by heating the sample or exposing the sample to electromagnetic radiation. Rapidly raising the temperature of intercalated samples provides sufficient energy to selectively exfoliate the carbon layers of carbonaceous impurities.

As many carbonaceous impurities are amphoteric in nature, intercalants useful in this aspect of the present invention include, electron donor intercalant, such as alkali metals (e.g. Li, K, Na, Rb and Cs), and electron acceptor intercalants, such as halogens (e.g. fluorine, bromine and iodine), metal chlorides and acids (e.g. lewis acids such as nitric acid, perchloric acid, sulfuric acid; and formic acid). The present invention includes methods wherein more than one type of intercalant is added to the sample undergoing purification, for example methods in which carbon layers are bi- intercalated. The present invention includes intercalation processing of samples via electrochemical methods, including but not limited to, intercalation initiated via chronoamperometric or chronovoltametric methods. Intercalants may be provided as liquids, gases and in solutions added to samples undergoing purification. Preferred intercalants for applications requiring high yields of high quality carbon materials do not significantly damage or disrupt the desired carbon material undergoing purification.

The present methods are capable of processing samples comprising complex mixtures of materials having a wide range of chemical compositions, structures and physical states. For example, the present methods are useful for purifying sample generated by virtually all catalytic and noncatalytic synthesis methods for making SWNTs, MWNTs, catalytically grown carbon fibers, catalytically grown carbon films and diamond, including but not limited to, arc-discharge methods, chemical vapor deposition methods, plasma enhanced chemical vapor deposition methods, high pressure carbon monoxide disproportionation methods; pyrolytic methods, flame synthesis methods, electrochemical synthesis methods; and laser ablation methods. The versatility with respect to the type of carbon material that is purified in the present methods largely arises from the use of selective exfoliation wherein impurities having structures similar to, but not the same as, a desired carbon material may be exfoliated and removed without substantial loses or damage to the desired carbon material. In addition, this versatility arises from the use of selective exfoliation to render noncarbonaceous impurities in a state susceptible to removal via dissolution.

The present invention provides a method of purifying a sample containing SWNTS by selectively removing graphene layers, graphite, amorphous carbon, incomplete fullerenes, metal particles or any combination of these materials. In one embodiment, methods of this aspect of the present invention are capable of providing purified samples corresponding to a yield of SWNTs selected over the range of about 15 % to about 20% and a purity selected from about 90 to about 98% by weight. In the context of this description, the term yield refers to the weight ratio (in percent) of the achieved purified SWNT to the initial amount of carbon material before purification (e.g. 1 gram of carbon will provide 150 milligram of purified SWNT in a process providing a 15% yield). In another embodiment, the present invention provides a method of purifying a sample containing MWNTS by selectively removing graphene layers, graphite, amorphous carbon, incomplete fullerenes, metal particles or any combination of these materials. Further, the methods of the present invention are applicable to purifying nanotubes made from other materials, such as boron nitride nanotubes. The present methods are not limited to purifying carbon nanotube containing samples, and are capable of isolating and purifying other useful allotropes of carbon, such as single walled fullerenes, multiwalled fullerenes, diamond, carbon fibers, carbon films, and carbon whiskers.

The present methods are also suitable for purification of diamond materials. Conventional diamond synthesis methods, such as high temperature - high pressure processing of molten graphite and chemical vapor deposition methods, generate diamond-containing samples having significant carbonaceous impurities, such as graphite. Methods of the present invention are useful for exfoliating these carbonaceous impurities, thereby allowing for more easy removal of the exfoliated carbonaceous impurities. In another aspect, the present invention provides a method of purifying a sample containing a carbon material having a selected structure comprising the steps of: (1 ) providing the sample containing the carbon material having a selected structure and impurities comprising carbonaceous impurities, wherein the carbonaceous impurities comprising one or more carbon layers having a structure different than that of the selected structure; (2) exfoliating at least a portion of the carbon layers of the carbonaceous impurities, thereby generating exfoliated carbonaceous material; and (3) removing the impurities, thereby purifying the sample containing a carbon material having a selected structure. Optionally, methods of this aspect of the present invention may further comprise the step of annealing the purified sample to repair any damage incurred during purification processing, remove residual exfoliation reactants and solvent and/or enhance the crystal structure of the carbon material having a selected structure.

In another aspect, the present invention provides a method of exfoliating at least a portion of a plurality of carbon multilayers at least partially enclosing metal particles in a sample generated in the synthesis of carbon nanotubes comprising the steps of: (1) providing the sample generated in the synthesis of carbon nanotubes containing the metal particles, wherein each metal particle is at least partially enclosed by the carbon multilayers; (2) adding an intercalant to the sample, wherein the intercalant inserts between at least a portion of the carbon multilayers, thereby generating intercalated carbon multilayers having intercalant present between the carbon multilayers; and (3) adding an exfoliation initiator to the sample which reacts with intercalant present between the carbon multilayers, thereby exfoliating at least a portion of the carbon multilayers.

In another aspect, the present invention provides a method of removing carbonaceous coatings from the outer surfaces of carbon nanotubes comprising the steps of: (1 ) providing a sample comprising the carbon nanotubes, wherein at least a portion of the outer surfaces of the nanotubes are partially or completely coated with the carbonaceous coatings, and wherein the carbonaceous coatings have a structure different from that of the nanotubes; (2) adding an intercalant to the sample, wherein the intercalant inserts into interstitial sites between the nanotubes and the carbonaceous coating; and (3) adding an exfoliation initiator to the sample which reacts with the intercalant, wherein the reaction between the intercalant present between the carbon nanotubes and the carbonaceous coating and the exfoliation initiator exfoliates the carbonaceous coating, thereby removing the carbonaceous coatings from the outer surfaces of the carbon nanotubes. Optionally, methods of this aspect of the present invention may further comprise the step of annealing the purified sample to repair any damage incurred during purification processing, remove residual exfoliation reactants and solvent and/or enhance the crystal structure of the carbon material having a selected structure.

In another aspect, the present invention provides a method of purifying a sample containing single walled nanotubes comprising the steps of: (1 ) providing the sample containing the single walled nanotubes and impurities comprising metal particles, wherein the metal particles are at least partially enclosed by a plurality of carbon multilayers having a structure different from that of the carbon nanotubes; (2) adding an intercalant to the sample, wherein the intercalant inserts between at least a portion of the carbon multilayers enclosing the metal particles, thereby generating intercalated carbon multilayers having intercalant present between the carbon multilayers; and (3) adding an exfoliation initiator which reacts with intercalant present between the carbon multilayers, thereby exfoliating at least a portion of the carbon multilayers and exposing the surface of the metal particles; and (4) refluxi ng the sample in concentrated hydrochloric acid, thereby dissolving the metal particles and purifying the sample containing single walled nanotubes. Optionally, methods of this aspect of the present invention may further comprise the step of annealing the purified sample to repair any damage incurred during purification processing, remove residual exfoliation reactants and solvent and/or enhance the crystal structure of the carbon material having a selected structure.

BRIEF DESCRIPTION OF THE DRAWINGS Fig.1A provides a schematic diagram showing processing steps in a purification method of the present invention useful for removing carbonaceous impurities and metal catalyst particles from a sample containing one or more desired carbon materials having selected structures. Figu re 1 B provides a schematic flow d iagram showing processing steps in a purification method using potassium intercalation for purifying SWNTs generated by catalytic synthesis techniques, such as arc-discharge, gas phase catalysis (e.g. metal carbonyls) and laser ablation synthesis methods.

Figure 2 shows a transmission electron microscope (TEM) image of the as-received sample containing SWNT that was purified using the present methods. The inset in Figure 2 shows a region of the as-received material that comprises of the nanotube rope structure. The metal containing catalyst appears as darker, sphere shaped domains.

Figures 3A and 3B show TGA data recorded in an Ar/O2 flow for the two studies of metal catalyst removal, where Figure 3A shows data for the conventional reflux purification methods. The plots in Figure 3A correspond to: (1 ) As-received Carbolex, (2) after processing in HNO3 and H2O2, (3) after heating at various temperatures i n wet air (3) 35O0C, (4) 425°C, (5) 4800C, (6) 5100C, (7) 52O0C and finally (8) after heat treatment in N2/H2 forming gas at 750°C. The plots in Figure 3B correspond to: (1 ) As-received Carbolex, (2) after doping with K, reacting with EtOH and HCI reflux, (3) after 35O0C wet oxidation, (4) after 425°C wet oxidation and (5) after annealing at 7500C in N2/H2 forming gas. Each oxidation step was followed by HCI reflux.

Figure 4 provides Raman spectra of the sample after the different stages of purification using the present methods and provides reference spectra useful for interpreting the Raman spectra of the sample. The plots in Figure 4 correspond to: (a) as-received Carbolex, (b) after doping with K, (c) after reacting with EtOH, (d) after HCI reflux, 350°C wet oxidation and HCI reflux, (e) after 4250C wet oxidation and HCI reflux (f) after N2/H2 forming gas treatment at 75O0C, (g) graphite powder, (h) graphite powder after K intercalation (KCs).

Figure 5 presents X-ray diffraction (XRD) patterns from samples after different steps of purification using the present methods. The plots in Figure 5 correspond to: (a) SWNT material purified with the HNO3 process, (b) As-received Carbolex material, (c) after doping with K, (d) after reacting in EtOH, HCI reflux, wet oxidation at 3500C, HCI reflux, (e) after wet oxidation at 425°C, HCI reflux, (f) after annealing in N2/H2 forming gas at 7500C. The peak indexing is shown. Figure 6 provides transmission electron microscope (FEM) images of the SWNT- containing sample after purification by the present methods.

Figure 7 provides X-ray diffraction (XRD) patterns o-f the starting carbon fiber- containing sample and the sample after different purification processing steps of the present invention.

Figure 8 shows a transmission electron microscope (TE IvI) image of the as-received sample containing carbon fibers that was purified using trie present methods.

Figures 9A, 9B and 9C provide TEM images of the carbon fiber-containing sample after purification by the present methods.

DETAILED DESCRIPTION OF THE IMVENTION Referring to the drawings, like numerals indicate like elements and the same number appearing in more than one drawing refers to the same element. In addition, hereinafter, the following definitions apply:

"Carbon material" and "carbonaceous materials" are used synonymously in the present description and refer to a class of compounds comprising carbon atoms. Carbon materials include allotropes of carbon such as SWNTs, MWNTs, single walled and multiwalled fullerenes, graphite, graphene, amorprious carbon, carbon fibers, carbon films, carbon whiskers, and diamond, and all derivatives thereof. Carbon materials in the present invention may be entirely comprised of carbon atoms or may include carbon in combination with other elements, such as dopants, intercalants and functional groups conjugated to the carbon structures. D epending on the composition of the sample and intended outcome of the purification method, carbon materials may be classified as desired carbon materials or undesired carbonaceous impurities. Desired carbon materials have a selected structure (which depends on the precise application of the method) and are purified by the present methods. Carbonaceous impurities, in contrast, have a structure different from that of the desired carbon materials and are subject to removal by the present methods. Carbon materials, including both desired carbon materials and carbonaceous impurities, may exist in single or multilayer forms. The term "carbon layer" refers to a structure of wherein certain atoms are held together by directed covalent, ionic or other strong intramolecular forces. Layers may be planar or contoured. Interactions between different ca rbon layers may be via intermolecular forces, such as van der Waals interactions. Examples of carbon layers include, but are not limited to, graphite layers, graphene sheets, walls of a multiwalled or single walled fullerenes, MWNTs, SWNTs, layers comprising carbon fiber and carbon films. Carbon layer may also refer to a carbonaceous impurity coating the outer surface of a particle, such as a residual metal catalyst particle, metal derivative particles such as metal oxide particles or particle comprising catalyst support material, and a carbonaceous impurity coating the outer surface of desired a carbon material, such as a carbon nanotube (SWNT and MWNT), a fullerene, other desired carbon allotrope. The terms "carbon layer" and "carbon layers" does not limit the size, shape or orientation of the layers.

"Exfoliation" refers to a process whereby adjacent layers are separated by a distance such that the strength of associative interactions between adjacent layers is decreased. Exfoliation of a multilayer material, such as a plu rality of graphene sheets or graphite layers, includes separation of a single layer comprising a multilayer structure and includes involve separation of a plurality of layers comprising a multilayer structure. Exfoliation may involve separation of two different materials or separation of different layers of a multilayer material by disruption of associative interactions, such as van der Waals interactions, that hold the materials together. For example, the present invention provides methods of exfoliating carbonaceous impurities that coat a desired carbon material such as a carbon nanotube (SWNT or MWNT), fullerene, carbon fiber, diamond, and carbon film. In addition, the present invention provides methods of exfoliating carbonaceous impurities that coat particles, such as metal catalyst particles, metal derivative particles such as metal oxide particles, and particles comprising catalyst support materials. The present invention provides methods wherein carbon layers comprising carbonaceous impurities are either partially or entirely exfoliated.

"Intercalant" refers to a material that inserts into interstitial sites and/or endohedral sites in a single or multilayer receiving material. Additio n of an intercalant to a receiving material comprising a carbon material (e.g. graphite, graphene, amorphous carbon, MWNTs etc.), generates intercalated carbonaceous material. In some cases, the intercalated carbonaceous material has a well defined stoichiometry with respect to the amount of intercalant associated with the carbon material. In one embodiment of the present invention, intercalant is added to a sample and inserts into interstitial sites between carbon layers in multilayer carbonaceous impurities and/or inserts into interstitial sites between a desired carbon material and a carbonaceous impurity coating its outer surface.

"Exfoliation initiator" refers to a material that reacts with intercalant in intercalated carbonaceous material, thereby causing at least partial exfoliation of the intercalated carbonaceous material. Exfoliation initiators may comprise molecules, ions, atoms or complexes thereof, and may be in solid, gas, liquid or solution phases.

"Metal catalyst particles" refer to metal particles generated by catalytic synthesis methods for generating carbon materials. Metal catalyst particles typically comprise transition metals and mixtures thereof including, but not limited to, nickel, molybdenum, palladium, yttrium, iron, copper, molybdenum; and cobalt.

"Purification" refers to a process whereby the percentage (or fraction) of a desired material in a sample is increased via processing. Purification methods of the present invention may increase the percentage by mass, percentage by weight, percentage by volume and/or mole fraction of one or more selected carbon materials in a sample undergoing processing. Purification methods of the present invention useful for some applications are capable of providing a purified selected carbon material having a structure and composition that does not vary significant from its structure and composition in the starting material subject to processing or has a structure that is enhanced after processing via the present methods, such as a structure exhibiting an enhanced extent of crystallinity. For example, methods of the present invention are capable of purifying a SWNT-containing sample such that the purified SWNTs are not present in derivatized (i.e. oxidized) or functionalized forms.

In the following description, numerous specific details of the devices, device components and methods of the present invention are set forth in order to provide a thorough explanation of the precise nature of the invention. It wil I be apparent, however, to those of skill in the art that the invention can be practiced without these specific details.

This invention provides methods of purifying samples contai ning a carbon material having a selected structure by removing carbonaceous, noncarbonaceous and multiphase impurities from the sample. Particularly, the pr&sent invention provides purification methods for samples containing selected carbon materials, such as carbon nanotubes (SWNTs and MWNTs), wherein carbonaceous impurities comprising carbon layers having a different structure than the selected carbon material are exfoliated, thereby facilitating subsequent removal of impurities via chemical transformation, for example by selective oxidation andΛ>r dissolution processes.

Figure 1A provides a schematic diagram showing processing steps in a purification method of the present invention useful for removing carbonaceous impurities and metal catalyst particles from a sample containing one o r more desired carbon materials having selected structures. As shown in process step 1 of Figure 1A, a sample is provided for processing that comprises a mixture c*f one or more desired carbon materials having selected structures and impurities. Impurities in the sample may have a range of different chemical compositions and physical states, including carbonaceous impurities comprising carbon materials having structures different from that of the desired carbon material, such as impurities comprising single or multilayer forms of graphene, graphite, amorphous carbon, carbon fibers, carbon films, MWNTs and selected combinations of these materials, noncarbonaceous materials such as metal catalysts, metal derivatives including metal oxides, catalyst support materials and aggregates and particles thereof, and multiphase impurities, such as metal catalyst particles partially or completely enclosed in multilayer carbonaceous impurities.

Referring again to Figure 1A, an intercalant is added to the sample in process step 2, thereby generating intercalated carbon layers in the sample. In one embodiment, enough intercalant is added to allow the formation of intercalated carbon layers having the highest possible stoichiometry, and in some embodiments the sample containing intercalant is allowed to react to substantial completion, lntercalants provided to the sample may insert into interstitial sites between adjacent layers in multilayer carbonaceous impurities and/or insert into interstitial sites located between a desired carbon material and a carbonaceous impurity coating its outer surface. In addition, intercalants added to the sample may insert into endohedral sites of carbonaceous impurities. Intercalants may be added to the sample in liquid form, gaseous form or in a carrier solution. In methods of the present invention using highly reactive intercalants, such as alkali metals, the sample is optionally evacuated and heated to remove moisture and oxygen prior to the addition of the intercalants, and the sample containing intercalant is optionally kept in an inert atmosphere for the entire duration of the intercalation reaction. Optionally, the sample containing intercalants is electrochemically intercalated by application of a constant or variable electric potential to the sample during intercalation, as also indicated in process step 2.

As shown in process steps 3, 4 and 5 of Figure 1A, the sample having intercalated carbon layers is selective exfoliated, thereby generating exfoliate carbonaceous material. In the context of this description sel ective exfoliation refers to a process whereby carbon materials comprising impurities undergo at least partial exfoliation, while carbon materials undergoing purification (having a selected structure) do not undergo substantial exfoliation. Figure 1A shows two pathways (process steps 4 & 5) for achieving selective exfoliation. In the embodiment shown in process step 4, an exfoliation initiator is added to the sample that undergoes a chemical reaction with intercalants in the intercalated carbon layers. Preferably for some applications, the reaction between the exfoliation initiator and intercalants in the intercalated carbon layers is very a fast exothermic reaction and, optionally, a reaction that results in an expansion of material between intercalated layers, for example by forming a product in the gas phase. The reaction between the exfoliation initiator and intercalants in the intercalated carbon layers is selective such that desired carbon materials having a selected structure are not lost or damaged during the exfoliation process. An alternative route to selective exfoliation is shown in process step 5. In this embodiment, exfoliation of intercalated carbon layers is initiated by raising the temperature of the sample, preferably for some embodiments raising the temperature very rapidly. Referring to process step 6 of Figure 1A, exfoliated carbonaceous material is selectively removed from the sample. Removal of exfoliated carbonaceous material may be achieved by any method that does not significantly destroy or damage the selected carbon material undergoing purification. In some embodiments, chemical transformation of exfoliated carbonaceous materials is used to direct remove impurities, such as selective oxidation in wet air at successively higher temperatures. In addition, exfoliated carbonaceous material may be removed using separation techniques, such as microfiltration and chromatography. As also shown in process step 6 in Figure 1A, in one embodiment wherein the sample contains multiphase impurities comprising metal, metal derivative or ceramic particles parti ally or completely enclosed in a plurality of carbon impurity layers, exfoliation and subsequent removal of exfoliated carbonaceous material exposes the outer surface of the metal or metal derivative residual catalyst particles. Metal particles ha\-/ing an exposed outer surface are subsequently removed via dissolution, for example dissolution in concentrated inorganic or organic acid added to the sample. As shown in Figure 1A, selective exfoliation steps (process steps 3, 4 and 5) and i mpurity removal steps (process steps 6 and 7) may be repeated until a selected purity of the desired carbon material having a selected structure is achieved.

Figure 1 B provides a schematic flow diagram showing processing ste ps in a purification method using potassium intercalation for purifying SWNTs generated by catalytic synthesis techniques, such as arc-discharge and laser ablation synthesis methods. As shown in process step 1 of Figure 1 B, a sample is provided for processing that comprises a mixture of (i) SWNTs, (ii) carbonaceous im purities having structures different than that of the SWNTs and (iii) residual metal catalyst particles enclosed in multilayer carbonaceous impurities carbonaceous im purities having structures different than that of the SWNTs. The sample undergoing processing is evacuated and heated, for example to a temperature of 300 degrees Celsius, to remove any trace of water and oxygen, as illustrated in processing step 2 of Figure 1 B. Potassium intercalant is added to the sample and allowed to react to completion in an inert atmosphere (e.g. argon), thereby generating carbon layers intercalated with potassium (see process step 3). In one embodiment where carbonaceous impurities in the sample include graphite and/or graphene layers, the amount of potassium added to the sample is sufficient to form the most potassium rich intercalation material, such as an intercalation material having the stoichiometry of one potassium atom to eight carbon atoms (i.e. KCs).

Referring to process step 4 in Figure 1 B, the intercalated sample is reacted with an exfoliation initiator comprising ethanol, which initiates an exothermic reaction that selectively exfoliates carbon layers intercalated with potassium. In one embodiment, ethanol reacts with potassium present in intercalated carbon layers to generate potassium alkoxide and hydrogen gas:

2C2H5OH + 2K → 2C2H5O- K+ + H2

In one embodiment, the sample is reacted with ethanol until a neutral pH is observed, indicating that substantially all the intercalated potassium has undergoing reaction. Exfoliation generates exfoliated carbonaceous material and also ruptures the multilayer structure of carbonaceous impurities enclosing the residual metal catalyst particles. Exfoliation provided by this processing step can disrupt and/or fracture the shell-like multilayer structure of carbonaceous impurities enclosing the residual metal catalyst particles resulting in at least partial exposure of their outer surfaces.

As shown in process steps 5 and 6 in Figure 1 B, the sample is refluxed in concentrated hydrochloric acid to dissolve metal particles and subjected to low temperature oxidation under wet air to selectively remove exfoliated carbonaceous materials. Removal of the exfoliated carbonaceous materials further exposes the outer surface of the metal particles, thereby enhancing their removal via subsequent additional processing steps refluxing the sample in concentrated hydrochloric acid. Oxidation in wet air may also at least partially convert the metal particles to metal derivative particles such as metal oxide or metal hydroxide particles. This oxidation process results in an expansion of the volume of the particle due to the lower density of the oxide and/or hydroxide product that further disrupts the shell-like multilayer structure of carbonaceous impurities enclosing the residual metal catalyst particles and also increases the efficiency of subsequent removal of metal particles via dissolution. Process steps 5 and 6 are optionally repeated until a desired purity of the SWNTs is achieved. In one embodiment, the sample is subjected to wet air oxidation at successively higher temperatures each time that process steps 5 and 6 are repeated. As indicated in process step 7 of Figure 1B, the purified sample is optionally annealed in nitrogen to repair any damage to the SWNTs which occurs during processing.

The methods of the present invention may be realized using a wide variety of instrumentation and reagents well known in the art. Use of a two bulb glass reactor and a two zone furnace is beneficial for adding gas phase potassium to the sample in a manner which minimizes the likelihood of condensing potassium on the sample undergoing processing. In this embodiment, the sample undergoing processing is held in a first bulb maintained at a slightly larger temperature and in fluid communication with a second bulb containing the potassium intercalant. Manipulation of samples undergoing purification in a glove box filled with any inert gas, such as argon, is helpful for avoiding inadvertent premature oxidation of intercalants comprising highly reactive alkali metals (e.g. K and Na) during intercalation of the sample. A variety of methods and instrumentation well known in the art may be used for electrochemically intercalating samples including voltammetric intercalation and electrolysis. Any intercalants and/or exfoliation initiators can be used in the present methods including electron donor intercalants, electron acceptor intercalants and combinations of both electron donor intercalants and electron acceptor intercalants. Exemplary intercalants useful for preparing intercalated carbon layers include, but are not limited to, Li, Na, K, Rb, Cs, F2, CI2, Br2, I2, chromium oxides such as Crθ3, metal chlorides such as CdCb, YCI3, AICI3, M0CI5, ZnCI2, FeCI3, sulfuric acid, nitric acid, perchloric acid, formic acid.

The terms and expressions which have been employed herein are used as terms of description and not of limitation, and there is no intention in the use of such terms and expressions of excluding any equivalents of the features shown and described or portions thereof, but it is recognized that various modifications are possible within the scope of the invention claimed. Thus, it should be understood that although the present invention has been specifically disclosed by preferred embodiments and optional features, modification and variation of the concepts herein disclosed may be resorted to by those skilled in the art, and that such modifications and variations are considered to be within the scope of this invention as defined by the appended claims. The specific embodiments provided herein are examples of useful embodiments of the present invention and it will be apparent to one skilled in the art that the present invention may be carried out using a large number of variations and additional processing steps including, but not limited to, sample transfer steps, temperature variation steps and cycles, product purity analysis, additional separations including phase separations, chromatographic separation, separation by filtration techniques such as microfiltration, removal of excess reagents such as process steps removing intercalants and/or exfoliation initiators added to the sample undergoing processing, and solution phase oxidation of carbonaceous impurities.

The following references relate generally to methods of exfoliating carbon materials: (1 ) "Exfoliation of carbon fibers", M. Toyoda and M. Inagaki, Journal of Physics and Chemistry of solids, 65 (2004) 109 - 117; (2) Review of the doping of carbon nanotubes (multiwalled and single-walled)", L. Duclaux, Carbon, 40 (2002), 1751-1764; (3) "Exfoliation process of graphite via intercalation compounds with sulfuric acid", M. Inagaki, R. Tashiro, Y. Reactino and M. Toyoda, Journal of Physics and Chemistry of solids, 65 (2004) 133 - 137; (4) "Graphite exfoliated at room temperature and its structural annealing" M. Inagaki and M. Nakashima, Carbon, Vol. 32, No. 7 (1994), 1253 - 1257; (5) "Exfoliation process and elaboration of new carbonaceous materials", Fuel, VoI 77, No. 6, (1998) 479 - 485; and (6) "Electrochemical intercalation of ZnCI2-CrO3-GIC (graphite intercalation compound) with sulphuric acid", J. M. Skowronski and J. Urbaniak, Polish J. Chem. 78 (2004) 1339-1344.

All references cited in this application and all references cited in these references are hereby incorporated in their entireties by reference herein to the extent that they are not inconsistent with the disclosure in this application. It will be apparent to one of ordinary skill in the art that methods, devices, device elements, materials, procedures and techniques other than those specifically described herein can be applied to the practice of the invention as broadly disclosed herein without resort to undue experimentation. All art-known functional equivalents of methods, devices, device elements, materials, procedures and techniques specifically described herein are intended to be encompassed by this invention. Example 1 : Purification of carbon single walled nanotubes produced by arc - discharge methods. The ability of methods of the present invention using potassium intercalation to purify SWNTs was experimentally verified by purifying SWNT containing samples generated using arc discharge synthesis methods. Thermogravimetric analysis (TGA), Raman spectrometry, X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used to characterize the results of each processing step, and to evaluate the effectiveness of the purification treatment. The purified SWNT products generated by the present methods were compared to SWNT samples purified via conventional acid reflux purification methods. This potassium intercalation step was found to be particularly useful for exfoliating the graphitic shell structure that typically surround residual metal catalyst particles present in samples prepared by many catalytic synthesis methods. By exfoliating the shell structure, subsequent treatments are more efficacious for removing the metal catalyst particles.

1.a Introduction There have been many investigations of single-wall carbon nanotubes (SWNTs) since these materials were first reported in the early Nineties. The unique physical, chemical and mechanical properties of SWNTs make them candidate materials for service in electronic devices, energy storage systems and structural composites, for example. To obtain behavior in these applications that can be unambiguously and solely attributed to nanotubes, purification of the SWNTs is an essential step, since raw materials are typically composed of less than half SWNTs. The efficiency of any purification method is strongly dependent on the raw materials, which differ for the three methods typically used for the production of SWNTs: chemical vapor deposition (CVD), electric arc-discharge and laser ablation.

It has proved a serious challenge to remove multiwalled nanotubes and shells, incomplete fullerenes, graphites, and disordered carbon impurities in the raw materials without also destroying the SWNTs, since all these components are similar chemically. In this example, we concentrate on the purification of SWNTs prepared by arc-discharge and laser oven/ablation because these methods produce SWNTs with a narrow distribution of tube diameters. Important impurities in materials prepared by arc-discharge and laser oven/ablation methods also include metal catalyst particles, which are typically surrounded by shells of polyaromatic carbons. The shell structure protects the metal particles from dissolution in inorganic acids.

Many procedures for purifying SWNTs are based on chromatography and filtration methods, or on selective oxidation processes (i.e. acid oxidation and/or gas oxidation), or a combination of these methods. For any method of purification, a compromise is typically made between impurity removal and the final yield of SWNTs. Another concern is that some purification processes can damage the nanotubes. Refluxing in nitric acid, for example, is effective for removing metallic impurities, but also produces defects in the tubes.

Method of the present invention using a potassium intercalation processing step was used to purify arc-derived carbon SWNTs, which are generally recognized as the most challenging to purify. The present purification methods procedure comprise the steps of: (a) intercalating the SWNT containing sample with potassium (b) reacting/exfoliating the resulting powder with ethanol and (c) wet air oxidation at successively higher temperatures, with each step followed by a reflux in concentrated hydrochloric acid. Low temperature wet air oxidation has generally been thought to remove the more disordered carbon layer coatings on metal catalyst particles, allowing the dissolution of the metal in an acid. Oxidation treatments at higher temperatures remove the more stable carbon layer graphitic shells surrounding the catalyst metal particles. During these wet air oxidation treatments, the metal is converted to an oxide and/or hydroxide. The expansion of the metal due to the lower density of the oxide (densities for Ni and NiO are respectively 8.90 and 6.67) cracks the carbon shells and the metal oxide, thus is exposed and is subsequently dissolved by the proper acid.

The step of potassium intercalation followed by reacting with ethanol causes more complete exfoliation of the intercalated layers, weakening the carbon shell structure covering the metallic particles. These structures are therefore more easily cracked by wet air oxidation, more completely exposing the metal catalyst. Each of these steps contributes to the purification, and the combination of potassium intercalation, wet air oxidation and hydrochloric acid treatments produces a high-purity SWNT containing purified sample. By using transmission electron microscopy, Raman spectrometry, x-ray diffractometry, and thermogravimetric analysis, we show that the methods of the present invention provide better yields and purities than another process involving a more established purification process involving a combination of refluxing in HNO3, centrifugations, refluxing in H2O2 and wet oxidations in air at different temperatures (350 to 52O0C).

1.b Experimental Single-wall carbon nanotube materials produced by the arc-discharge method with a Ni-Y catalyst (5 at.%) were obtained from Carbolex Inc. According to the manufacturer the as-received sample purity may vary from 70 to 90 vol.%, and it contains residual catalyst impurities. Figure 2 shows a transmission electron microscope (TEM) image of the as-received sample containing SWNT that was purified using the present methods. The as-received Carbolex soot has a large volume of metal catalyst of various sizes, which appear as dark spheroids. X-ray microanalysis showed these particles to be composed of Ni and Y. Also seen are different types of carbon including: carbon shells, amorphous carbon, and free single- wall carbon nanotubes. The inset in Figure 2 shows a region of the as-received material that comprises of the nanotube rope structure. Note the hexagonal packing of the tubes seen end-on at the top of the inset.

The as-received SWNT-containing sample was first evacuated and heated to 3000C to remove any trace of moisture and O2. Using an argon-filled glove box, samples were then loaded into a two-bulb reactor of the type used to synthesize graphitic potassium intercalation compounds. The carbon material and the potassium metal intercalant are put into each bulb of a glass reactor, evacuated, and then placed into a two-zone furnace. The potassium zone temperature was maintained at 250°C, whereas the nanotube zone temperature was adjusted to higher temperature to minimize the possibility that potassium metal might condense on the sample. The masses of potassium and carbon material were chosen to allow the formation of the most potassium-rich intercalation compound, KCs. After reaction for two days, the potassium-doped nanotubes were reacted with ethanoi until a neutral pH was obtained. The sample was then refluxed in concentrated hydrochloric acid (37%) for 24 hours: a typically green acid color was observed due to the dissolved Ni2+. The materials were then subjected to a low temperature oxidation (350°C during 24 hours) under flow of wet air, and again refluxed with HCI to further remove exposed catalyst particles. A final wet air oxidation at 45O0C with a shortened oxidation time of 2.5 hours was subsequently performed, followed by an HCI treatment. As a final step, to repair possible damage to the tube walls, the sample was annealed in nitrogen forming gas at 7500C for 2 hours.

Thermogravimetric analysis (TGA), Raman spectroscopy, X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used to evaluate the effectiveness of the purification treatments and to determine the relative purity of the SWNTs.

For TGA analysis, the nanotube samples were loaded into an alumina crucible, and a flow of argon was maintained at 40 mL/min while heating at 10°C/min from room temperature to 200°C. This temperature was held for 20 minutes under the argon flow and then for another 20 minutes under a 50:50 Ar/O2 mixture. The chamber was then maintained under a continuous Ar/O2 flow while the temperature was incrementally raised at 5°C/min to 7000C or 10000C. The time (t) dependence of the sample mass (m) was recorded.

To investigate possible SWNT damage from the steps of the purification process, Raman spectra were acquired at room temperature with a Renishaw Micro Raman spectrometer using a 514.5 nm argon ion laser with spectral resolution of 1 cm"1. The samples were encapsulated in argon-filled glass ampoules, and to prevent the loss of potassium from the samples or other instabilities, Raman measurements were made with low laser power.

The crystallinity of the nanotube rope structure and the evolution of the impurity phases during purification were studied by x-ray diffractometry (XRD) and transmission electron microscopy (TEM). X-ray powder diffraction was performed with a Cu Ka X-ray source (Philips PW3040, λ Cu=1.54056A, 45kV, 40 mA). Morphological observations of the as-received SWNTs were obtained by TEM measurements using a Philips EM420 operated at 100 kV. 1.c Results and Discussion

1.c.(\) Thermoqravimetric analysis When heated in the presence of oxygen gas, carbon materials undergo oxidation, forming the gases CO or CO2. Any material remaining after all of the carbon has been consumed is the initial metal catalyst in oxide form. Figures 3A and 3B show TGA data recorded in an Ar/O2 flow for the two studies of metal catalyst removal, where Figure 3A shows data for the conventional reflux purification methods [See, e.g. A. G. Rinzler, J. Liu, H. Dai, P. Nikolaev, C. B. Huffman, F. J. Rodriguez- Macias, P. J. Boul, A. H. Lu, D. Heymann, D. T. Colbert, R. S. Lee, J. E. Fischer, A. M. Rao, P. C. Eklund, R. E. Smalley, Appl. Phys. A 67, (1998) 29-37], and Figure 3B shows data for the present methods using an initial potassium intercalation/exfoliation step. Each set of runs was performed with successive wet air oxidations at increasing temperatures, followed by an HCI reflux step after each oxidation.

For the data in Figure 3A, a nitric acid reflux was performed on the as-received raw soot material, followed by an H2O2 reflux. The sample was subsequently oxidized at temperatures of 350, 425, 480, 510 and 5200C. Using a series of temperatures in this way is necessary because amorphous carbon and multi-shell carbon phases in the as-received soot cannot be removed selectively with a single oxidation step. The oxidation temperature range of amorphous carbon and multi-shell carbons (3500C and 4200C respectively) overlap with the oxidation range for SWNTs (400°C). For the data in Figure 3B, the SWNT material was reacted with potassium using a graphite intercalation procedure, and then reacted with ethanol (EtOH). The number of oxidation steps was reduced to two, performed at temperatures of 35O0C and 425°C.

For both sets of procedures, the samples underwent a final anneal at 7500C under flowing forming gas consisting of nitrogen plus hydrogen. In comparing the TGA curves after the first step of purification for each method, Fig. 3A and 3B shows that the potassium reaction followed by EtOH reacting is more effective as a first step in the purification process. The decomposition temperature shifts to a lower temperature, consistent with the formation of amorphous or turbostratic polyaromatic carbon phases by graphite exfoliation. More significantly, a subsequent mild treatment with HCI causes a larger mass loss after this intercalation step, because the carbon shells around the metal particles were more pervious to acid. In the second and third steps the oxidation processes were carried out at 3500C and 425°C respectively, and the samples were reacted again in HCI. With each reacting step, more metal is removed and the onset oxidation temperature is seen to increase. Such oxidation processes burn the carbon shell around the metal catalyst particles, exposing the metal particles to the acid. Because the nanotubes are more stable against oxidation than amorphous carbon, the nanotubes are not affected by oxidation at these temperatures. Starting from the second stage of purification, the TGA curves for both purification processes show the same behavior, but the potassium intercalation allows a smaller number of oxidation steps for the same amount of catalyst removal.

Yields were measured corresponding to the present purification process and the conventional process examined. The SWNT content remaining in the sample at the end of the present purification process involving potassium intercalation/exfoliation is about 18 wt.% whereas the total yield of carbon nanotubes for the more established purification process combining refluxing in nitric acid, refluxing in H2O2 and wet oxidations in air is less than a few weight percent.

Lcfii) Micro Raman Spectroscopy Figure 4 compares the Raman spectra of the sample after the different stages of purification using the present methods. For comparison, typical Raman spectra of pure graphite are shown before, plot (g) in Fig. 4, and after potassium intercalation, plot (h) in Fig. 4. Graphite reacts with potassium to form graphite intercalation compounds KCn. Intercalation compounds are distinguished by their staging, which is defined as the number of graphene layers separating the intercalated potassium layer. For example, the compound KC8 is a stage 1 binary compound in which all van der Waals gaps between the graphene layers are occupied by potassium. In the spectrum of graphite, the sharp feature at 1584 cm"1 is attributed to the E2g first order mode. The symmetry of the E2g mode restricts the motion of the atoms within the plane of the carbon atoms. An additional band at 1355 cm"1 is attributed to finite size effects, resulting from smaller domains that are present among larger ones. This corresponds to a 'breathing mode' with Ai9 symmetry. A different Raman profile is observed for the potassium intercalated graphite compound. A broad asymmetric feature around 1500 cm'1 is observed, characteristic of stage 1 KCs.

The spectrum from as-received AP Carbolex material (plot (a) in Fig. 4) has two main bands at low (100-200 cm'1) and high (1500-1600 cm"1) frequencies, characteristic of SWNTs. The high-frequency bands can be decomposed into two main peaks at 1590 and 1570 cm'1, which are associated with tangential modes related to C-C bond stretching motions. At low wave number, another characteristic tube mode is observed, where the carbon atoms are displaced radially outward in an in-phase, breathing mode. Superimposed on this spectrum is the contribution from amorphous sp2 carbon, or possibly a thin coating on the nanotubes with a peak around 1350 cm"1. Plot (b) in Figure 4 shows the changes in the Raman spectrum after potassium doping, and has features similar to the spectrum from KC8, plot (h) in Fig. 4. There are significant shifts in the frequencies of both radial and tangential modes, are evidence of the complete reaction of the nanotubes with potassium. After reacting in EtOH, clean SWNTs are recovered as shown by the spectrum of plot (c) in Figure 4. Potassium intercalation followed by EtOH reacting leaves the nanotubes intact, while exfoliating the graphitic carbon coating that surrounds the metal catalyst particles. This is consistent with the increased intensity of Raman band from the turbostratic polyaromatic carbon at 1350 cm"1. Further steps such as HCI reflux and wet air oxidation are then more efficacious in removing the catalyst than in removing disordered and graphitic sp2 carbons. Evidence for this is noted by the presence of the residual line at 1350 cm"1. However, the intensity of this peak does progressively diminish with processing. Raman spectra from the samples after wet air oxidation and subsequent HCI reflux and the last forming gas treatment (plots (d), (e) and (f) in Figure 4, respectively) show the peaks characteristic of SWNTs. They are also consistent with at most minor nanotube damage during the purification.

1.c(iii) X-Rav diffraction Figure 5 presents X-ray diffraction (XRD) patterns from samples after different steps of purification using the present methods. The XRD pattern of the as-received material shown in plot (b) of Figure 5 is dominated by the 111 and 200 diffraction peaks from fee nickel at 44° and 52°, and includes a diffuse background attributed to synthesis byproducts such as amorphous carbon, which coexist with the SWNTs. After reaction with potassium, some metal particles remain and an increase in the intensity of the background is observed in plot (c) in Figure 5. Precise quantitative details that delineate the effect of the alkali metal reaction are difficult to discern from the XRD data because of the inhomogeneity of this material and because of the nano- scale dimensions of the particles constituting the soot. Plot (d) in Figure 5 shows that subsequent EtOH reacting, wet air oxidation at 3500C and HCI reflux remove large amounts of catalyst, as evidenced by the change in relative peak height of the Ni diffractions with respect to remnant graphitic 002 diffraction peak. As a result of the exfoliation of the graphitic shell around the metal particles, the particles are more easily dissolved in acid. The first wet air oxidation at low temperature removes a large amount of amorphous carbon. This causes an increase in the graphitic particle diffraction peak-to-background, seen in the XRD profile as a doublet peak from turbostratic polyaromatic carbon (dOo2*=34O nm) and graphite (dOo2=335 nm). Plot (e) in Figure 5, obtained after the second wet air oxidation at 425°C followed by HCI reflux, shows well-defined diffractions from a hexagonal molecular crystal with a large unit cell, consistent with a close-packed rope structure of SWNTs. The forming gas treatment greatly improves the crystallinity of the rope packing as evidenced by the low-angle diffraction peaks in plot (f) of Figure 5. The 2-dimensional nanotube-to- nanotube spacing is measured to be 1.712 nm. The X-ray diffraction pattern obtained after the first purification and followed by wet air oxidation at 5100C shows diffraction peaks from the SWNT rope structure and a small 111 diffraction peak from the remaining catalyst. This observation again confirms the effectiveness of the purification process using potassium.

1.c(iv) TEM images of sample after purification Figure 6 provides transmission electron microscope (TEM) images of the SWNT-containing sample after purification by the present methods. These figures show that the present purification methods do not substantially degrade or damage the SWNTs in the sample undergoing processing, and indicate that the structure and composition of the purified SWNTs are similar to their structure and composition in the as-received sample. In addition, comparison of Figure 6 and Figure 2 indicates that the abundance of metal particles in the sample is significantly reduced after purification. 1.d Conclusion The present methods are effective for purifying carbon single-wall nanotubes synthesized by the arc-discharge process. The processing step of potassium intercalation and subsequent reacting with EtOH exfoliates the graphite impurities, and exfoliates the graphitic shells around the metal catalyst particles. After intercalation, the metal catalyst particles are more susceptible to removal by subsequent wet oxidation treatments coupled with HCI reflux steps. It is demonstrated that purification methods using this intercalation step decreases the catalyst content to levels that are obtained by a conventional purification process, however, using fewer purification steps. Evidence for the efficacy of this potassium intercalation step was provided by TGA measurements and TEM observations. Raman spectroscopy indicated that the structural integrity of the nanotubes was not compromised by the various stages of purification. XRD showed good crystallinity of the material after purification.

Example 2: Purification of carbon nanofibers synthesized by catalytic methods. The present invention provides versatile methods for purifying a range of carbon materials in samples generated by catalytic synthesis techniques. The ability of methods of the present invention using potassium intercalation to purify carbon materials other than carbon nanotubes was experimentally verified by purifying samples containing carbon nanofibers generated by catalytic synthesis. The synthesis and characteristics of theses fibers has been reviewed by K. P. De Jong and J. W. Geus in Catalysis reviews-Science and Engineering, 42 (2000) pp 481-510. X-ray diffraction (XRD) is used to characterize the composition of the starting carbon fiber-containing sample and the composition of the sample after important processing steps of the present methods. The experimental results provided in this example illustrate that the present methods provide an effective, nondestructive pathway for purifying samples containing carbon nanofibers. Similar to the experimental results obtained for SWNTs (See e.g., Example 1 ), potassium intercalation followed by reacting in ethanol was observed to be particularly useful for enhancing the removal of residual metal catalyst particles by dissolution in an acid solution.

Carbon fiber materials subject to purification were vapor grown via catalytic growth techniques and, therefore, had a significant impurity comprising residual cobalt - iron catalyst particles having a composition of about 50 percent iron by mass and about 50 percent cobalt by mass, (see for example: M. Audier et al. in J. Crystal Growth 55(1981 ) 549-556) The starting carbon fiber-containing sample was first evacuated and heated to 3000C to remove any trace of moisture and O2. Using an argon-filled glove box, samples were then loaded into a two-bulb reactor of the type used to synthesize graphitic potassium intercalation compounds. The carbon material and the potassium metal intercalant are put into each bulb of a glass reactor, evacuated, and then placed into a two-zone furnace. The potassium zone temperature was maintained at 25O0C, whereas the nanotube zone temperature was adjusted to higher temperature to minimize the possibility that potassium metal might condense on the sample. Intercalation of the carbon fiber-containing sample proceeded under these conditions for two days. After intercalation, the potassium-doped nanotubes were reacted with ethanol to initiate exfoliation. The sample was then refluxed in concentrated hydrochloric acid for 24 hours. The materials were then subjected to a low temperature oxidation (35O0C during 24 hours) under a flow of wet air, and again refluxed with HCI for 24 hours to further remove exposed catalyst particles. A final wet air oxidation at 4500C with a shortened oxidation time of 2.5 hours was subsequently performed, followed by another treatment with concentrated HCI for 24 hours. As a final step, the sample was annealed in nitrogen - hydrogen forming gas at 7500C for 2 hours to repair any damage to the carbon fibers and improve crystallinity.

2.a X-Ray diffraction results Figure 7 provides X-ray diffraction (XRD) patterns of the starting carbon fiber- containing sample and the sample after different purification processing steps of the present invention. The XRD pattern of the starting material provided in plot (1 ) of Figure 7 indicates a peak at about 45 degrees corresponding to the cobalt - iron particles. Also shown in plot (1) of Figure 7 are the 002 and 101 graphite peaks at about 26 degrees and 44 degrees, respectively, which correspond to graphite layers comprising the carbon fibers. Plot (2) of Figure 7 shows the diffraction pattern observed after intercalation with potassium. The cobalt - iron peak at about 45 degrees is clearly observable in plot (2). The 002 and 101 graphite peaks at 26 degrees and 44 degrees, however, are entirely missing and replaced with a series of peaks at about 16 degrees, about 23 degrees and about 34 degrees. These peaks corresponding to the 004 (at «16 degrees), hkl (at «23 degrees) and 008 (at «34 degrees) peaks ot intercalated graphite having a stoichiometry of one potassium to eight carbons (i.e. KC8). Plot (3) provides the XRD pattern observed after reacting the intercalated sample with ethanol and refluxing with concentrated HCI for 24 hours. The cobalt - iron peak at about 45 degrees is not present in the diffraction pattern provided in plot (3), which indicates this series of process steps effectively removes most of the metal catalyst particles. The reemergence of 002 and 101 graphite peaks at 26 degrees and 44 degrees may be attributed to the presence of unintercalated carbon fibers and indicates that the carbon fibers in the sample are not lost or significantly damaged during this processing step. The similarity of the shape and position of 002 and 101 graphite peaks in plots (1) and (3) of Figure 7 indicates that the composition and structure of the fibers after the reacting with ethanol and HCI reflux processing step is similar to the composition of the carbon fibers in the as- received sample. Plot (4) of Figure 7 provides the diffraction pattern obtained after wet oxidation for 24 hours at 350 degrees Celsius and refluxing with concentrated HCI for 24 hours. Similar to plot (3), plot (4) of Figure 7 shows that the carbon fibers are maintained in the sample during this processing step. Plot (5) of Figure 7, provides the diffraction pattern obtained after wet oxcidation for 24 hours at 450 degrees Celsius, refluxing with concentrated HCI for 24 hours and annealing at 750 degrees in a nitrogen - hydrogen forming gas for two hours. Comparison of plots (3), (4) and (5) of Figure 7 indicate that further sample processing via wet oxidation at successively higher temperatures and annealing improves the crystallinity of the purified carbon fibers.

The experimental results provided in this example demonstrate the applicability of the present methods for purifying carbon fibers materials generated by catalytic synthesis. The processing step of potassium intercalation and subsequent reacting with ethanol exfoliates carbonaceous impurities that form shells around residual metal catalyst particles. After intercalation, the residual metal catalyst particles are more susceptible to removal by subsequent wet oxidation treatments coupled with HCI reflux steps. XRD patterns obtained before, during and after sample processing, indicate the present methods provide an effective pathway for removing metal catalyst impurities and that the present methods provide a source of purified carbon fibers exhibiting good crystallinity. 2.bTEM images of sample before and after purification Figure 8 shows a transmission electron microscope (TEM) image of the as- received sample containing carbon fibers that was purified using the present methods. As shown in Figure 8, the as-received sample has a significant component comprising cobalt - iron catalyst particles, which appear as dark spheroids. Also seen are different types of carbon including: carbon shells, amorphous carbon, and carbon fibers.

Figures 9A, 9B and 9C provide TEM images of the carbon fiber-containing sample after purification by the present methods. Figure 9A is a lower resolution image than the images shown in Figures 9B and 9C. These figures show that the present purification methods do not substantially degrade or damage the carbon fibers in the sample undergoing processing, and indicate that the structure and composition of the purified carbon fibers are similar to their structure and composition in the as- received sample. In addition, comparison of Figures 9A, 9B and 9C and Figure 8 indicates that the abundance of metal particles in the sample is significantly reduced after purification by the present methods.