Abstract:
The present invention relates to metal-organic framework characterized in that it comprises a polymer coating; further the invention relates to a process for the preparation of said polymer-coated metal-organic framework and a process for recycling after degradation. The polymer coated MOFs of this invention find application in a broad range of technologies and therapeutic areas.

Inventors:
LI TAO (CN)
CHEN LIHAN (CN)
Application Number:
PCT/EP2020/059871
Publication Date:
October 15, 2020
Filing Date:
April 07, 2020
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
SHELL INT RESEARCH (NL)
SHELL OIL CO (US)
UNIV SHANGHAI TECH (CN)
International Classes:
B01J20/22; B01D53/04; B01J20/32; B01J20/34; C02F1/28
Domestic Patent References:
WO2017083467A12017-05-18
Foreign References:
US20080227634A12008-09-18
Other References:
ARNAU CARNÉ-SÁNCHEZ ET AL: "Protecting Metal-Organic Framework Crystals from Hydrolytic Degradation by Spray-Dry Encapsulating Them into Polystyrene Microspheres", ADVANCED MATERIALS, vol. 27, no. 5, 1 February 2015 (2015-02-01), pages 869 - 873, XP055713021, ISSN: 0935-9648, DOI: 10.1002/adma.201403827
WANG ZHANG ET AL: "A Facile and General Coating Approach to Moisture/Water-Resistant Metal-Organic Frameworks with Intact Porosity", JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, vol. 136, no. 49, 20 November 2014 (2014-11-20), US, pages 16978 - 16981, XP055618190, ISSN: 0002-7863, DOI: 10.1021/ja509960n
SHULIANG YANG ET AL: "A new post-synthetic polymerization strategy makes metal-organic frameworks more stable", CHEMICAL SCIENCE, vol. 10, no. 17, 1 January 2019 (2019-01-01), United Kingdom, pages 4542 - 4549, XP055712934, ISSN: 2041-6520, DOI: 10.1039/C9SC00135B
SANFENG HE ET AL: "A generalizable method for the construction of MOF@polymer functional composites through surface-initiated atom transfer radical polymerization", CHEMICAL SCIENCE, vol. 10, no. 6, 1 January 2019 (2019-01-01), United Kingdom, pages 1816 - 1822, XP055712769, ISSN: 2041-6520, DOI: 10.1039/C8SC03520B
Attorney, Agent or Firm:
SHELL LEGAL SERVICES IP (NL)
Download PDF:
Claims:
C L A I M S

1. A metal-organic framework characterized in that it

comprises a polymer coating.

2. The metal-organic framework of claim 1, wherein the metal- organic framework comprises one or more metal ions or metal clusters and one or more organic linkers, the metal ions or metal clusters being of any metal selected from the periodic table, preferably a metal from group IIA, IIIA, first row transition metals, second row transition metals, actinides, and lanthanides.

3. The metal-organic framework of claim 2, wherein the

organic linkers are small organic molecules with two or more coordinating functional groups.

4. The metal-organic framework of any one of claims 1-3,

wherein the BET surface area ranges from 10 m2/g to 7000 m2/g .

5. The metal-organic framework of any one of claims 1-4,

wherein the pore size ranges from 0.3 nm to 10 nm.

6. The metal-organic framework of any one of claims 1-5,

wherein the polymer coating is selected from styrene, acrylate, and methacrylate polymer coatings, and further from polyimide, polysulfone, polyethersulfone, and

polyamide polymer coatings.

7. The metal-organic framework of any one of claims 1-6,

wherein the polymer coating has a thickness of from 1 nm to 1 mm.

8. Use of the metal-organic framework of any one of claims 1-7 in gas storage, gas separation, gas capture,

catalysis, sensing, bioimaging and therapeutics.

9. A process for the preparation of a metal-organic framework comprising a polymer coating, comprising a controlled radical polymerization step.

10. A process for recycling of degraded polymer-coated metal- organic frameworks, comprising vapor or liquid assisted annealing or a solvothermal reaction.

Description:
A POLYMER COATED METAL-ORGANIC FRAMEWORK

FIELD OF THE INVENTION

The present invention relates to a metal-organic framework comprising a polymer coating, a use thereof, a process for preparing such polymer coated metal-organic framework, and a process for recycling the same.

BACKGROUND OF THE INVENTION

Metal-organic frameworks (herein after MOFs) are a large class of porous materials constructed from

metal/metal cluster building blocks linked by organic linkers through coordination bonds. Due to the

availability of a wide selection of metals, metal coordination modes, and the power of organic synthesis, their combinations have led to the emergence of tens of thousands of MOF structures in two decades. Their

potential in application fields such as gas storage, gas separation, catalysis, sensing, bioimaging, therapeutics etc. has been widely acknowledged.

With the rapid evolution in this field, now the concept of "tailor-made" porous materials with desired pore sizes, pore geometry, pore chemistry and even mechanical properties, has been made possible. However, a significant drawback of MOF materials is their relatively low stability towards water, acids, bases and other aggressive chemicals compared to conventional porous materials such as zeolites and porous carbons. This drawback severely limits their further deployment in many realistic industrial applications. For example, many MOF materials have shown great potential for post-combustion CO 2 capture. However, due to the huge quantity of materials needed for such application, potential CO 2 sorbent materials are expected to have long term

durability in order to reduce the cost and to limit their environmental impact. Unfortunately, the generally high humidity of flue gas streams has a negative impact not only on the CO 2 uptake capability of most MOF materials but also on their durability. One option to reduce the cost of sorbent materials is to recycle them after use.

A traditional way to recycle a MOF after degradation is to first digest it into a monomer mixture (metal ions and organic linkers) followed by multiple separation and purification processes to obtain metal salts and organic linkers in pure form. Then these monomers are again mixed under appropriate condition to allow the nucleation and growth of the MOF to occur. Finally, the obtained MOF crystals are separated and processed for the second use. Obviously, this is a costly and tedious procedure of recycling. Moreover, typical MOF synthetic conditions require the use of excess amounts of reagent and solvent resulting in a very low efficiency.

There is a need for MOF materials with a higher durability/recoverability, and for a more efficient and less costly way for recycling the materials.

SUMMARY OF THE INVENTION

The present disclosure provides a solution to said problems and needs. Accordingly, the present invention relates to a metal-organic framework comprising a polymer coating. Further, the present invention relates to a process for the preparation of a metal-organic framework comprising a polymer coating, comprising a controlled radical polymerization step. The polymer-coated MOFs of this invention can be broadly applied to replace their neat MOF counterparts to extend their mechanical and chemical durability.

Accordingly, a further aspect of the invention relates to the use of the polymer-coated MOFs in gas storage, gas separation, gas capture, catalysis, sensing, bioimaging and therapeutics, and in particular, the use thereof in direct air capture, post-combustion CO2 capture, and methane storage.

Another aspect of the present invention relates to a process for (in situ) recycling of degraded polymer- coated metal-organic frameworks, comprising vapor or liquid assisted annealing or a solvothermal reaction. The presently claimed recycling process eliminates the tedious procedures needed in a traditional recycling process and replaces them with a one-step

recrystallization process. This process can be used to significantly extend the operation lifespan of MOF-based sorbent materials by repetitive recycling.

DESCRIPTION OF THE DRAWINGS

(Note: the annotation "RE" means recrystallized and "DE" means degraded)

Scheme 1. Synthesis scheme of random copolymer 1 (RCP1) . Figure 1. Schematic illustration of the degradation and recrystallization process of a MOF particle within a polymeric shell.

Figure 2. TEM images of (A) HKUST-1@PS; (B) HKUST-1 @PS- DE; and (C) HKUST-1 @PS-RE .

Figure 3. Powder X-ray diffraction patterns of HKUST- 1@PS, HKUST-1 @PS-DE, and HKUST-1 @PS-RE .

Figure 4. CO2 adsorption isotherms of HKUST-1@PS, HKUST- 1 @PS-DE, and HKUST-1 @PS-RE at 298 K. Solid and hollow symbols represent adsorption and desorption points respectively .

Figure 5. Normalized CO2 uptake capacity of HKUST-1@PS (also referred to as HKUST-1@xPS, "x" meaning

crosslinked) after 5 degradation-recrystallization cycles at 298 K.

Figure 6. Comparative example. TEM images of (A) HKUST-1 and (B) HKUST-l-DE (i.e. MOF particles without polymer coating) .

Figure 7. Comparative example. Powder X-ray diffraction patterns of HKUST-1, HKUST-l-DE, and HKUST-l-RE.

DETAILED DESCRIPTION OF THE DISCLOSURE

The present disclosure relates to metal-organic frameworks (MOFs), which are compounds consisting of metal ions or clusters coordinated by organic ligands (linkers) to form one-, two-, or three-dimensional structures. These MOFs are typically crystalline

materials meaning that their exact structures can be obtained through techniques like single crystal X-ray diffraction or powder X-ray diffraction. They possess many properties analogous to traditional porous materials such as zeolites and porous carbons. These include intrinsic microporosity / mesoporosity and high BET surface area from 10 m 2 /g up to 7000 m 2 /g. Additionally, MOFs possess unique properties that traditional porous materials do not have. These include modular synthesis meaning that the pore size, shape and chemical

environment can be systematically designed by judicious selection of organic linkers and metal coordination modes .

The MOFs used for present disclosure can be

synthesized by a wide variety of methods that are commonly known in the art. These include but not limited to hydrothermal synthesis, solvothermal synthesis, mechanosynthesis , microwave assisted synthesis, spray drying synthesis, continuous flow synthesis etc.

The MOFs used for present disclosure comprise one or more metal ions or metal clusters and one or more organic linkers. The metal ions or metal clusters can be any metal selected from the periodic table and preferably metals from group IIA, IIIA, first row transition metals, second row transition metals, actinides, and lanthanides. Preferred metals are selected from Al, Cr, Zr, Sc, Hf,

Ti, Cu, Co, In, Fe, Ni, Zn and V. Preferred metals are Cu and Zn.

The organic linkers used in the MOFs are small organic molecules with two or more coordinating

functional groups and are not particularly limited.

Preferred functional groups are carboxylic acids

( carboxylates ) , nitrogen containing five/six-member rings (pyridine, imidazole, pyrazole, pyrazine, 1,2,3-triazole,

1.2.4-triazole, tetrazole etc.), and phenols, etc. More preferred linking ligands for linking the adjacent metal building units in the MOF structure are carboxylate-based ligands, which include 1 , 3 , 5-benzenetribenzoate (BTB) ,

1.4-benzenedicarboxylate (BDC) , cyclobutyl 1,4- benzenedicarboxylate (CB BDC), 2-amino 1,4 benzene- dicarboxylate (H2N-BDC) , 4,5,9, 10-tetrahydropyrene-2 , 7- dicarboxylate (HPDC) , terphenyl dicarboxylate (TPDC) , 2,6-naphthalene dicarboxylate (NDC) , pyrene 2,7- dicarboxylate (PDC) , biphenyl dicarboxylate (BDC) , and any di-, tri-, or tetracarboxylate containing phenyl rings .

The average MOF particle size is from 10 nm to 1 mm and preferably from 100 nm to 1mm, more preferably from 100 mm to 10 mm, and in particular from 10mm to 1 mm. The particle size is identified by scanning electron

microscopy (SEM) .

The BET surface area of the MOFs used in this

disclosure range from 10 m 2 /g to 7000 m 2 /g and preferably from 100 m 2 /g to 4000 m 2 /g. The BET surface area is identified using N2 adsorption isotherm data.

The pore size of the MOFs used in this disclosure range from 0.3 nm to 10 nm and preferably from 0.3 nm to 1 nm.

According to the present disclosure, it was found that by coating the MOF particle surface with a thin layer of polymer through controlled radical

polymerization, the metal ions and organic ligands are well-confined within the polymeric boundary to give relatively stable MOF@polymer composites (Figure 2A) .

According to the present disclosure, the MOF

particles need to be coated with a layer of polymer in order to confine the metal ions and organic linker molecules within that were used for the construction of the MOF structure and, in addition, to ensure optimal recrystallization efficiency.

The polymer coatings used in this disclosure are conventional polymer coatings and not particularly limited. Suitable examples include styrene, acrylate, methacrylate polymer coatings, etc. which can be

synthesized using radical initiated polymerization techniques; further polyimide, polysulfone, polyether- sulfone, polyamide polymer coatings, etc. Preferred examples of the polymer coating are polystyrenes, polyimides, polysulfone. Figure 2A shows an example of HKUST-1@PS in which HKUST-1 was coated by a layer of polystyrene with good uniformity. The "HKUST" terminology used herein is in accordance with the terminology introduced by the Hong Kong University of Science and Technology which first appeared in

(10.1126/science.283.5405.1148) .

The thickness of the polymer coating preferably ranges from 1 nm to 1 mm and particularly from 2 nm to 100 nm.

Further, the invention relates to a process for preparing a metal-organic framework comprising a polymer coating, comprising a controlled radical polymerization step, preferably using a technique selected from atom transfer radical polymerization (ATRP) , reversible addition-fragmentation chain-transfer polymerization (RAFT) , or nitroxide-mediated radical polymerization (NMP) . Particularly, the process used for coating the polymer comprises controlled radical polymerization techniques using acrylates, methacrylate, styrenic monomers etc.

According to the present disclosure, it was further found that even after degradation of the polymer coated MOFs (MOF@polymer) under harsh environment, no apparent leaching of components from the MOF structure was

observed due to the barrier effect of the polymer shell (Figure 2B) . Subsequent vapor or liquid assisted

annealing or solvothermal reaction surprisingly led to the recrystallization of the MOF particles within the polymeric shell (Figure 2C) thereby restoring the shape, crystallinity, and sorption properties of the MOF. It was found that such degradation-recrystallization process can be repeated several times. Therefore, the present

disclosure further relates to a process for recycling of degraded polymer-coated metal-organic frameworks, comprising vapor or liquid assisted annealing or a solvothermal reaction.

A typical vapor assisted annealing process is carried out by exposing a polymer-coated metal-organic framework sample to an organic vapor environment under heating conditions, generally above the boiling point of the solvent used. A preferred heating temperature range is from 60 - 200 °C . Common organic solvent selections include methanol, ethanol, propanol, dimethylformamide, N-Methyl-2-pyrrolidone, and dimethylacetamide etc. and their combinations. Preferably methanol, ethanol and dimethylformamide. Additives may be added to assist the dissolution of linkers and metal ions. Examples of additives include trifluoracetic acid, acetic acid, hydrochloric acid, and formic acid etc.

A typical liquid assisted annealing process is carried out by the addition of a small quantity of organic solvent to a polymer-coated metal-organic framework sample followed by heating, suitably in a temperature range from room temperature (25 °C) to 200 °C . The solvent and additive selection is similar to that of vapor assisted annealing process. The quantity of the solvent is typically quite small, with volume comparable to the solid. Specifically, the solid-liquid volumetric ratio is typically in the range between 1:10 and 10:1. This process can be used to regenerate polymer coated MOF-based sorbent materials on-site with high efficiency and low cost in a short amount of time thereby greatly extending the lifespan of said MOF materials.

In contrast to the polymer coated MOF structures of the present disclosure, non-coated MOF structures with similar MOF composition showed severe leaching issues, and further could not be recrystallized according to the procedures of the present disclosure.

Hereinafter the invention will be further illustrated by the following non-limiting examples.

EXAMPLES

Experimental methods

1. Electron Microscopy

Transmission electron microscopy (TEM) was conducted by JEM-140OPlus TEM (120kV) and JEM 2100 plus (200 kV) .

Briefly, 10 mL Sample-Methanol solution was directly deposited on a carbon coated TEM grid for 30 seconds. Then, excessive solution was wicked away with pieces of filter paper. Then the grid was dried for 15 minutes under 70 °C .

2. Powder X-ray diffraction (PXRD)

PXRD patterns were collected in the 2q range of 5 - 30 ° at room temperature on a Bruker D8 X-ray diffractometer with Cu K radiation (l = 1.54184 A) at a scan rate of 2 °/min and a step size of 0.02 °

3.CO2 adsorption-desorption analysis

CO2 adsorption-desorption analysis was performed with a volumetric adsorption analyzer (e.g. BELSORP-max II or Quantachrome iQ or Micromeritics ASAP 2020) . All samples were pre-exchanged with volatile organic solvents (e.g. MeOH) to remove pre-existing high boiling point solvents. Then the samples were activated at 120 °C for 10 h under constant vacuum. EXAMPLE 1

Synthesis of random copolymer (RCP1) P (vbpt-r-ba-r-aa) (wherein ha: butyl acrylate; aa: acrylic acid; and vbpt : S- (4-vinyl) benzyl S ' -propyl trithiocarbonate)_

(see Scheme 1)

MOF preparation HKUST-1

12.2 g of Cu (NO 3 ) 2 · 3H2O and 2.9 g of benzene-1, 3, 5- tricarboxylic acid was dissolved in 25 ml of

dimethylsulfoxide (DMSO) under 65 °C for 30 min. The solution was then injected into 250 ml of methanol containing 2.5 g of polyvinylpyrrolidone under vigorously stirring at 55 °C for 90 min. The products were harvested by centrifuging and washing twice with methanol, and finally dispersed in methanol for further use. Figure 6A shows the TEM image of the as synthesized HKUST-1

Preparation of HKUST-1@PS

Dissolve lg of HKUST-1 and 250mg of P (vbpt-r-ba-r-aa) in 15ml of dichloromethane (DCM) , the mixture is sealed in a small capped vial and sonicated to get well dispersed. After 12 hours of incubation, the particles were washed twice with toluene and then again dispersed in 15 ml of toluene. Then 4.5ml of styrene, 1.125ml of divinylbenzene (DVB) and 15mg of azobisisobutyronitrile (AIBN) were added to the solution. Three freeze-pump-thaw cycles were applied to the solution to remove dissolved O 2 . Then the ampule was sealed under vacuum. The polymerization reaction was carried out at 75 °C for 1.5 h under

constant stirring. Figure 2A shows is the TEM image of HKUST-1 @PS . The PXRD pattern of HKUST-1 @PS is shown in Figure 3.

The CO2 uptake capacity of HKUST-1 @PS at 298 K is 83 cc/g ( Figure 4 ) .

CO2 uptake is measured by using Brunauer-Emmett-Teller (BET) theory. CO 2 uptake isotherms were obtained using a volumetic sorption analyzer. Commonly used commercial modes include Belsorb MAX II, Quantachrome iQ,

Micromeritics ASAP 2020 etc. Typically, ~30-50mg of MOF sample was loaded into a glass sample cell and then activated at 120 °C for lOh under a constant vacuum. The sample cell was then loaded on to the sorption analyzer for subsequent analysis.

EXAMPLE 2

Degradation and recrystallization experiment

To mimic the degradation process in industry, 150 °C water vapor environment was used to facilitate the degradation process of HKUST-1@PS. The degraded product was therefore named HKUST-1@PS-DE .

After degradation, the powder X-ray diffraction pattern shows the disappearance of HKUST-1 characteristic peaks by replaced by a new phase.

The recrystallization process was carried out by exposing HKUST-1@PS-DE to an appropriate solvent vapor under heat. The recrystallized product HKUST-1@PS-RE showed complete regeneration of HKUST-1 crystallinity.

Detailed description

Degradation HKUST-1@PS by H0 at 150 °C

A HKUST-1 @PS powder sample (~15mg) was placed on a glass slide and the slide was loaded into a Teflon-lined stainless-steel hydrothermal reactor containing ~ 1ml of water. The glass slide was suspended above the water without touching. The reactor was placed in a 150 °C oven overnight. After cooling the reactor, the sample was taken out, collected and denoted as HKUST-1 @PS-DE . The PXRD pattern of HKUST-1 @PS-DE is shown in Figure 3. Its CO2 uptake capacity at 298 K is 91% less than that of HKUST-1@PS (Figure 4) . The TEM image shows that the

HKUST-1 particles transformed into another smaller crystalline particles (Figure 2B) .

Recrystallization of HKUST-1@PS-DE

HKUST-1@PS-DE (~15mg) was placed on a glass slide and loaded into a Teflon-lined stainless-steel hydrothermal reactor containing ~ 1ml of an ethanol/trifluoroacetic acid (TFA) mixture (ethanol :TFA = 98:2) . The glass slide was suspended above the solvent layer without touching. The reactor was placed in a 100 °C oven overnight. After cooling, the sample was taken out, collected and denoted as HKUST-1 @PS-RE . The PXRD pattern of HKUST-1 @PS-RE is shown in Figure 3 which indicates a successful

recrystallization of HKUST-1. Its CO2 uptake capacity at 298 K is 73% of that of HKUST-1 @PS (Figure 4) . The TEM image shows that the HKUST-1 particles reformed in single crystal fashion (Figure 2C) .

Degradation-Recrystallization cycling of HKUST-1@PS HKUST-1@PS was degraded and recrystallized using

aforementioned procedures for 5 cycles. Their CO2 uptake capacity at lbar, 298 K was recorded and plotted in

Figure 5.

EXAMPLE 3

Comparative example - non-polymer coated MOF

Degradation HKUST-1 by H2O vapor at 150 °C

A HKUST-1 sample (~15mg) was placed on to a glass slides and the slide was loaded into a Teflon-lined stainless- steel hydrothermal reactor containing ~ 1ml of water. The glass slide was suspended above the water without

touching. The reactor was placed in a 150 °C oven

overnight. After cooling the reactor, the sample was taken out, collected and denoted as HKUST-l-DE. The PXRD pattern of HKUST-l-DE is shown in Figure 7. Thus, the recrystallization process did not lead to the recovery of HKUST-1 as shown from the PXRD pattern. The TEM image shows leaching of monomers (Figure 6B) .