| Claims 1. A system for processing plastic wherein, in use, the system is adapted for the frictional heating of the plastic. 2. A system as claimed in claim 1 , wherein the system comprises a frictional heater. 3. A system as claimed in claim 2, wherein the frictional heater is adapted to bear against the plastic in use, 4. A system as claimed in claim 2, wherein the frictional heater is adapted to rotate. 5. A system as claimed in claim 4, wherein the frictional heater is adapted to rotate at sufficient speed to cause intimate mixing. 6. A system as claimed in claim 2, further comprising a drive operably coupled to the frictional heater. 7. A system as claimed in claim 6, further comprising a gear operably between the drive and the frictional heater. 8. A system as claimed in claim 6, wherein the drive is an electric drive. 9. A system as claimed in claim 6, wherein the drive is an internal combustion engine, 10. A system as claimed in claim 9, wherein the internal combustion engine is a diesel internal combustion engine. 1 1 . A system as claimed in claim 2, wherein the frictional heater has an axis of rotation and wherein the frictional heater is adapted to bear against the plastic substantially along the axis of rotation. 12. A system as claimed in claim 2, wherein the frictional heater has an axis of rotation and wherein the frictional heater is adapted to bear against the plastic substantially perpendicular to the axis of rotation. 13. A system as claimed in claim 2, wherein the frictional heater is adapted to heat the plastic to greater than 80°C. 14. A system as claimed in claim 2, wherein the frictional heater is adapted to heat the plastic to greater than 100°C. 15. A system as claimed in claim 2, wherein the frictional heater is adapted to heat the plastic to greater than I 60°C. 16. A system as claimed in claim 2, wherein the frictional heater comprises at least one molten plastic conduit. 17. A system as claimed in claim 2, wherein the frictional heater is substantially cylindrical, 1.8. A system as claimed in claim 17, wherein the frictional heater comprises at least one molten plastic conduit adapted to allow molten plastic to enter substantially within the cylinder. 19. A system as claimed in claim 2. further comprising an output adapted to allow the molten plastic to flow therefrom in use. 20. A system as claimed in claim 19, wherein , in use, the frictional heater is arranged to allow molten plastic to flow from within the frictional heater unde gravity. 21. A system as claimed in claim 2, further comprising a chamber adapted to confine the plastic in use. 22. A system as claimed in claim 21, wherein the chamber is adapted to direct the plastic towards the frictional heater. 23. A system as claimed in claim 21 , wherein the chamber comprises an input. 24. A system as claimed in claim 21 , further comprising a pusher and wherein the pusher is adapted to bear the plastic against the frictional heater. 25. A system as claimed in claim 24, wherein the pusher is hydrauiicaily driven. 26. A system as claimed in claim 24, wherein the pressure exerted by the pusher is configured in accordance with operational parameters. 27. A system as claimed in claim 26. wherein the operational parameters comprise plastic type, 28. A system as claimed in claim 2 1 , wherein the pusher is located within the chamber and wherein the pusher is shaped in accordance with the inner profile of the chamber. 29. A system as claimed in claim 28, further comprising a further chamber adapted for confining further plastic and a further pusher located within the further chamber and wherein the pusher and the further pusher are adapted to bear the plastic against the frictional heater. 30. A system as claimed in claim 29, wherein the pressure exerted by the pusher and the further pusher are configurable. 31 . A method for processing plastic comprising the frictional heating of the plastic. 32. A method as claimed in claim 31, wherein the frictional heating is carried out by a frictional healer. 33. A method as claimed in claim 32. further comprises pushing the plastic towards the frictional heater, 34. A method as claimed in claim 32, wherein the frictional heater is a rotational frictional heater. 35. A method as claimed in claim 32. wherein the frictional heater is adapted to rotate at sufficient speed to cause intimate mixing. 36. A method as claimed in claim 33, wherein the direction of pushing the plastic towards the frictional heater is substantially parallel to an axis of rotation of the frictional heater. 37. A method as claimed in claim 33. wherein the direction of pushing the plastic towards the frictional heater is substantially perpendicular to an axis of rotation of the frictional heater. 38. A method as claimed in claim 31, comprising heating the plastic to greater than 80°C. 39. A method as claimed in claim 31, comprising heating the plastic to greater than ).00°C. 40. A method as claimed in claim 31 , comprising heating the plastic to greater than 160°C. 4.1 . A method as claimed in claim 33, wherein the plastic is pushed towards the frictional heater with a force that corresponds with the plastic type. 42. A method as claimed in claim 33, wherein pushing the plastic towards the frictional heater comprises pushing the plastic towards the frictional heater from two or more directions. 43. A method as claimed in claim 42. further comprising pushing the plastic towards the frictional heater with a first force and pushing other plastic towards the frictional heater with a second force. 44. Plastic processed by a system according to any one of claims 1 to 30. 45. Plastic processed by a method according to an one of claims 31 to 43. 46. A materia! coated with plastic processed by a system according to any one of claims 1 to 30. 47. A material coated with plastic processed by a method according to any one of claims 31 to 43. 48. A system as claimed in claim 5, wherein the frictional heater is adapted to rotate at 1 10 rpm or more. 49. A method as claimed in 35, wherein the frictional heater is adapted to rotate at i 10 rpm or more. |
PROCESSED THEREFROM
Field of the Invention The present invention relates to plastic processing systems and in particular to a system and a method for processing plastic, and plastic processed therefrom.
Background
According to existing arrangements, the processing of plastic, including the recycling thereof generally comprises the collection of suitable plastic for recycling, the heating thereof so as to pelletise the plastic, and, once pelletised, the subsequent reheating of the pelletised plastic for re-use, such as by way of injection moulding, extrusion or the like.
However, existing arrangements suffer from, several disadvantages including the inability to process all types of plastic. Specifically, certain types of plastics such as film plastic, or contaminated plastic (such as plastic obtained from butchery process or waste heneficiation process or the like which may be contaminated with offal or food and the like) are generally ill suited for recycling and therefore simply sent to landfill.
Furthermore, existing arrangements are energy intensive, requiring the heating of the entire body of plastic for recycling, and in embodiments, the reheating of the recycled pelletised plastic.
Furthermore, existing plastic processing machines are provided with low tolerance requirements and therefore ill-suited for all types of plastics or foreign bodies within the plastic. For example, shredder or scissor type plastic processing machines may be fouled by film plastic. Furthermore, shredder or scissor type plastic processing machines, by comprising blades with low tolerance parameters, may be easily damaged by foreign bodies within the plastic.
Furthermore, existing plastic processing machines were generally adapted for processing a single type of plastic only and are therefore not suited for processing blends of plastic, such as is typical of plastic obtained from, recycling and waste processing.
The present invention seeks to provide a system and a method for processing plastic, and plastic processed therefrom, which will overcome or substantially ameliorate at least some of the deficiencies of the prior art, or to at least provide an alternative. It is to be understood that, if any prior art information is referred to herein, such reference does not constitute an admission that the information forms part of the common general knowledge in the art, in Australia or any other country.
Summary
A system for processing plastic wherein, in use, the system is adapted for the frictional heating of the plastic.
Advantageously, the frictional heating facilitates mixing of the plastic.
Preferably, the system comprises a frictional heater.
Preferably, the frictional heater is adapted to bear against the plastic in use.
Preferably, the frictional heater is adapted to rotate.
Preferably, the frictional heater is adapted to rotate sufficient speed to cause intimate mixing.
Preferably, the frictional heater is adapted to rotate at 110 rpm or more.
Preferably, the system further comprises a drive operably coupled to the frictional heater. Preferably, the system further comprises a gear operably between the drive and the frictional heater.
Preferably, the drive is a electric drive.
Preferably, the drive is an internal combustion engine.
Preferably, the internal combustion engine is a diesel internal combustion engine.
Preferably, the frictional heater is adapted to bear against the plastic substantially along the axis of rotation.
Preferably, the frictional heater is adapted to bear against the plastic substantially perpendicular to the axis of rotation.
Preferably, the frictional heater is adapted to heat the plastic to greater than 80°C.
Preferably, the frictional heater is adapted to heat the plastic to greater than 100°C.
Preferably, the frictional heater is adapted to heat the plastic to greater than 160°C.
Preferably, the frictional heater comprises at least one molten plastic conduit.
Preferably, the frictional heater is substantiall cylindrical. Preferably, the frietional heater comprises at least one molten plastic conduit adapted to allow molten plastic to enter substantially within the cylinder.
Preferably, the system further comprises an output adapted to allow the molten plastic to flow (herefrom in use.
Preferably, in use, the frietional heater is arranged to allow molten plastic to flow from within the frietional heater under gravity.
Preferably, the system further comprises a chamber adapted to confine the plastic in use. Preferably, the chamber is adapted to direct the plastic towards the frietional heater. Preferably, the chamber comprises an input.
Preferably, the pusher is adapted to bear the plastic against the frietional heater.
Preferably, the pusher is hydraulically driven.
Preferably, the pressure exerted by the pusher is configured in accordance with operational parameters .
Preferably, the operational parameters comprise plastic type.
Preferably, the pusher is shaped in accordance with the inner profile of the chamber.
Preferably, the pusher and the further pusher are adapted to bear the plastic against the frietional heater.
Preferably, the pressure exerted by the pusher and the further pusher are configurable.
According to another aspect, there is provided a method for processing plastic comprising the frietional heating of the plastic.
Preferably, the frietional heating is carried out by a frietional heater.
Preferably, the method further comprises pushing the plastic towards the frietional heater.
Preferably, the frietional heater is a rotational frietional heater.
Preferably, the frietional heater is adapted to rotate at sufficient speed to cause intimate mixing.
Preferably, the frietional heater is adapted to rotate at 1 10 rpm or more.
Preferably, the direction of pushing the plastic towards the friciional heater is substantially parallel to an axis of rotation of the frietional heater. Preferably, the direction of pushing the plastic towards the frictional heater is substantially perpendicular to an axis of rotation of the frictional heater.
Preferably, the method comprises heating the plastic to greater than 80°C.
Preferably, the method comprises heating the plastic to greater than 100°C.
Preferably, the method comprises heating the plastic to greater than 160°C.
Preferably, the plastic is pushed towards the frictional heater with a force that corresponds with the plastic type.
Preferably, pushing the plastic towards the frictional heater comprises pushing the plastic towards the trictional heater from two or more directions,
Preferably, the method further comprises pushing the plastic towards the frictional heater with a first force and pushing other plastic towards the frictional heater with a second force..
According to another aspect there is provided plastic processed by a system described herein.
According to another aspect, there is provided plastic processed by a method described herein.
According to another aspect, there is provided a material coated with plastic processed by a system described herein.
According to anothe aspect, there is provided a material coated with plastic processed by a method described herein.
Other aspects of the invention are also disclosed. Brief Description of the Drawings
Notwithstanding any other forms which may fall within the scope of the present invention, a preferred embodiments of the invention will now be described, by way of example only, with reference to the accompanying drawings in which:
Fig. 1 shows a system for processing plastic in accordance with an embodiment of the present invention; and
Fig. 2 shows a system for processing plastic in accordance with embodiment of the present invention. Description of Embodiments
It should be noted in the following description that like or the same reference numerals in different embodiments denote the same or similar features.
Referring to figure 1 , there is shown in an embodiment of a system 100 adapted for processing plastic. As will become apparent from the description below, the system 100 is adapted for processing plastic, including the recycling of plastic. As will also become apparent from the description below, the system 100 provide advantages including advantages in energy efficiency, contaminant tolerance, differing plastic types and the like. Furthermore, the system 100 is adapted for processing plastic which would otherwise be sent for landfill, such as film type plastic which is generally ill suited for transportation and recycling.
Whereas prior art plastic processing systems utilise heaters, such as electric heaters, or the like in order to melt plastic the system 100 is adapted for frictional heating of the plastic.
Specifically, the system i00 is adapted to use friction in order to melt the plastic. Advantages of using friction to melt plastic comprise energy efficiency in only having to melt the plastic at a localised frictional face of the plastic as opposed to the entire body of plastic as with conventional arrangements. Further advantages include system robustness wherein, as will be described in further detail below, the frictional heater is robust when compared to existing plastic processing systems, which existing plastic processing systems include shredder or scissor type plastic processing systems having high tolerance requirements and therefore prone to failure, especially in the event of contaminant such as a foreig body within the plastic, and require frequent servicing, such as i the sharpening of cutters and the like.
As such, the system 100 comprises a frictional heater 145. In a preferred embodiment, the frictional heater 145 is adapted to rotate while bearing against the plastic so as to heat the plastic at the frictional face of the frictional heater 145. As alluded to above, localising the heating of the plastic at the frictional face reduces the energy requirements of the system 100 as compared to conventional arrangements. Generally, the frictional heater 145 is adapted to heat the plastic just to melting point until such time that the plastic can flow through a molten plastic conduit or the like as will be described in further detail below. As molten plastic flows away, unmolten plastic takes its place so as to be melted and so on and so forth. Of course, differing plastics exhibit differing melting points. As such, certain plastics could potentially melt at 160°C but other types of plastics, such as Nylon would melt at up to 240°C prior to melting. However, as alluded to above, the system 100 is self- regulating in that as soon as the plastic becomes molten, the molten plastic flows through the otional heat 145 to be replaced by adjacent non-molten plastic.
As the frictional heater 145 is adapted to rotate while bearing against the plastic so as to heat and melt the plastic, the shearing motion of the rotating viscous plastic mixture fragments and disperses solid and liquid components of the feed stocks ensuring an homogenous mix to produce uniform and coherent products and co-poiomers.
While the frictional heater 145 is adapted to rotate in a preferred embodiment as alluded to above, in other embodiments the frictional heater 145 need not necessarily rotate and may take the form of a laterally travelling surface from the perspective of the plastic such as provided by metal band travelling past the plastic or the like.
However, where the frictional heater 345 is adapted to rotate in the preferred embodiment, as is apparent from figure 1 , the fictional heater 145 comprises a cylindrical type arrangement adapted to rotate about an axis of rotation and wherein the plastic is adapted to bear against the frictional heater 145 in the direction substantially perpendicular to the axis of rotation. In other words, the plastic is driven towards the frictional heater 145 such that the plastic is heated by the outer periphery of the frictional heater 145.
However, in other embodiments the frictional heater 145 may be provided as a rotating plate wherein the plastic bears against the rotating plate in the direction substantially paral iel with the axis of rotation of the rotating plate, in such an embodiment, the rotating plate may be a stationary rotating plate wherein the plastic is driven towards the rotating plate or alternatively, the rotating plate may additionally be driven towards the plastic. In such an embodiment, the plastic heated by the rotating plate may be dispersed towards the edges of the rotating plate and escape around the edges of the rotating plate so as to form a substantially cylindrical type arrangement once cooled.
Now, in a preferred embodiment, the frictional heater is adapted to rotate substantially at 110 rpm and sufficient speed to cause intimate mixing. However, in embodiments, oilier rotational velocity is ma be utilised depending on the application. In one specific embodiments, the rotational velocity of the factional heater 145 may be controllable in accordance with differing operational parameters such as desired throughput and the like.
It should be noted that one advantage of the system 100 is that there is substantially no resilience requirements of the factional heater 145 and in embodiments, the frictional heater 145 may be manufactured from even mild steel.
Referring to figure 1 , the system 100 comprises a drive 105 for driving the frictional heater 145. Between the drive 105 and the frictional heater 145, there may be a gear 155 adapted to attain the correct gearing ratio depending on the drive, operational parameters and the like. In one embodiment, the drive 105 may be an electric drive. For example, where an electric drive is used, a 55 kW electric motor may be used which may attain a throughput of substantially 250 kg of processed plastic per hour. However, and especially for portable type arrangements, the drive 145 may be an internal combustion engine, such as a diesel internal combustion engine.
The system 100 may further comprise a substantially plastic-tight bearing 160 at the interface of the frictional heater 145 and the chamber 1 10 (described below) so as to substantially prevent the escape of molten plastic therefrom in use.
Now, referring specifically to the frictional heater 145, in the embodiment given, the fictional heater 145 comprises at least one molten plastic conduit 140 (provided as small holes within the frictional heater 145 in the embodiments given) adapted to allow molten plastic to flow with therethrough. As such, the non-molten plastic bears against the frictional heater 145 until such time that the plastic becomes substantially molten. At this stage, the molten plastic is able to travel through the molten plastic conduit 140. In the arrangement given in figure 1, the substantially cylindrical frictional heater 145 comprises a plurality of molten plastic conduits 140 arranged radially, and substantially perpendicular the axis of rotation of the frictional heater 145. As such, the plastic melted by the frictional heater 145 travels through one or more of the molten plastic conduits 145 to substantially within the interior of the frictional heater 145.
Now, as the different molten plastics travels through the molten plastic conduit 140 intimate mixing of plastic types occurs and further contaminants (oil, paper, aluminimum foil, soil and the like) are fragmented by the shear forces of the rotating and flowing viscous molten plastic causing these contaminants to be finely dispersed throughout the molten mass. It should be noted that in converse, less preferred embodiments, the plastic may be driven within the interior of the frictional. heater such that once melted, the plastic escapes through the molten plastic conduits 140 to the exterior of the frictional heater 145,
The system 100 further comprises an outlet 135 adapted to allow the molten plastic to flow therefrom. Specifically, in the embodiment given there is shown the molten plastic
130 flowing from the outlet 135. On the embodiment given in figure 1, once the molten plastic has flown through the molten plastic conduits 140, the molten plastic is drawn under the effect of gravity through and out of the output 135.
Once the molten plastic flows out of the output 135, the molten plastic may be processed in many ways. One such way as to pel !etise the molten plastic so as to be adapted for subsequent reheating and injection moulding such as by using a conventional injection moulding machine. However, so as to preferably retain the heat energy of the plastic and to attain energy efficiency, the molten plastic is processed in situ, hi this regard, the molten plastic may be fed directl into a injection moulding machine, extruding device or the like.
In one embodiment, the molten plastic, as opposed to being recycled for further domestic or commercial use may be utilised to provide material handling and co-firing advantages for certain material. For example, for furnace coke, the furnace coke may be coated with molten plastic derived from system 100 so as to provide advantages in the handling, transportation, combustion and the like of the coke and also in the increased calorific index of the coke when burnt in the furnace. Of course, it must be appreciated that the molten plastic derived from the system 100 may be adapted for coating other material types also, especially hazardous material types which may provide advantages through a protective and encapsulating coating of plastic. In coating the material, the material may be introduced into a rotating drum or the like wherein the molten plastic is introduced into the rotating drum also such that the molten plastic adheres to the surface of the material. Such may be done at an elevated temperature so as to enhance the adherence of the molten plastic to the surface of the material. Of course, other technique may be employed for the purposes of coating and encapsulating, such as by dipping the material within a molten plastic bath, the pouring of the molten plastic over the material and the like.
Referring again to figure 1, the system 100 comprises a chamber 110 adapted to confine the plastic in use. Specifically, the chamber 1 10 is adapted to direct the plastic towards the frictional heater 145 in use. The system 100 further comprises art input 1 5 so as to be used in use to insert the plastic to within the chamber 1 10.
In certain applications, the plastic for recycling may comprise water. Therefore, in one embodiment, (he system 100 comprises at least one vent so as to allow steam (and other gases) to escape therefrom without creating a pressure buildup. The at least, one vent may be located at different locations depending on different applications, including through the body of the chamber 110 and through the pusher 125 (described below). The at least one vent may be used to monitor gases and vapours and include the fitting of a scrubber, known by those practiced in the art, to address any gaseous by-product, issues,
Furthermore, the system 100 comprises a pusher 125 adapted to push the plastic against the frictional heater 145. As is apparent from the embodiment, the pusher 125 comprises a pusher face adapted to conform substantially to the interior cross-section of the chamber 110 so as to provide a substantially flush fit to effectively push the plastic towards the frictional heater 145.
In a preferred embodiment, the pusher 125 is pushed by hydraulic ram 120 or the like. In an embodiment, the hydraulic ram is pressurised to 1500 to 2000 psi such that, assuming that the ratio of the pusher face to the hydraulic ram face is a ratio of 1 to 50, the pressure applied against the molten plastic would be substantially 30 to 40 psi.
As is apparent from the embodiment, the pusher 125 is adapted to be drawn backwards so as to allow plastic to be inserted within the input 145 and subsequently bear forwards so as to push the inserted plastic towards the frictional heater 145.
The insertion of plastic may be automated wherein the reloading of the chambe 1 10 may be controlled by computer processor or the like in conjunction with controlling of a conveyor belt or the like so as to allow for the automated batch processing of plastic. Referring now to figure 2, there is shown in an alternative embodiment of the system 100.
As is apparent, the system 100 as substantially given in figure 2 is at least distinguished from the embodiment given in figure I on account of there being more than one chamber 1 0 and respective pushers 135 within each chamber 1 10.
As such, in this embodiment, plastic may be pushed towards the frictional heater 145 in more than one direction. Specifically, the first pusher 125 in the first chamber 1 10 pushes first plastic towards the frictional heater 145 from a first direction and the second pusher 125 in the respective second chamber 110 pushers second plastic towards the frictional heater 145 from a different direction.
Advantages of using a multi-chamber system .1.00 include greater throughput, including not only in the greater capacity for frictional heating, but also in the great capacity for reloading. In one embodiment, each respective pusher 125 may operate asynchronously with each other so as to allow the reloading of one chamber while the contents of the other chamber are being pushed towards the pusher.
A further advantage of using a multichamber system 100 is in the blending of plastic types. In this manner, plasties may be selected in accordance with their qualities such that the resultant melted plastic comprises a blend of the properties of the respective plastic constituents. For example, a rigid plastic may be blended with a softer plastic so as to provide a plastic with semirigid properties. In one embodiment, during the blending process, the. pressure or force exerted by each respective pusher may be controlled according to the desired properties of the resultant plastic. For example, if a softer resultant plastic were desired, the pusher associated with the chamber comprising the softer plastic would be pushed with greater pressure or force as opposed to the chamber comprising the harder plastic.
It should be appreciated that while in the embodiment provided there are shown two chambers 1 15, it should be appreciated that in other embodiments more than two chambers 110 may be utilised, depending on the application.
In accordance with the above embodiments, there is also provided a method for processing plastic comprising the frictional heating of the plastic, and plastic processed by a system or metliod as described herein. There is also provided a material coated with a plastic processed by a syste or method as described herein,
Reference is made to the below Appendix A and Appendix B providing empirical plastic mix data reciting various characteristics of the resultant plastic product produced by a test system 100 utilising differing plastic types as input. Appendices
Appendix A - First Empirical, plastic mix data
Common Plastics Available from Recycling and Waste Processing:
• High density polyethylene (HDP.E) eg. chemical containers, detergent and cleaning product containers, crinkly shopping bags, shampoo containers
• Low density polyethylene (LDPE) eg. Most plastic bags
• Linear low density polyethylene (LLDPE) eg. silage wrap, pallet wrap, glad wrap, most stretch type films.
• Polypropylene (PP) eg. take away food containers, ice cream containers, baling twine, bulka bags, woven bags, tarpaulins
• Polyvinykhloride (PVC) eg. electrical cable insulation, glueable plumbing pipe and fittings, clear cordial and juice containers
» High impact polystyrene (HIPS) eg. food containers such as yoghurt and butter
• Polyethylene terepthalate (PET) eg. carbonated soft drink bottles, detergent bottles, packaging strapping
• Multi-layer laminated packaging comprising LDPE, HDPE, aluminium foil, paper-board eg. liquid food containers
Small test rig experiments to date indicate that the shear and friction of the rotating viscous plastic melt is significant in achieving intimate mixing of feed stocks. Accordingly, appropriate blending, mixing and melting parameters allows the use of many plastics and plastic composites that otherwise could not be effectively recycled, and the range of plastic mixes that comprise possible input and output variants is endless. Some general examples are set out below:
• HDPE, LDPE & LLDPE will all bond together very well when processed in either a mixed arrangetnent or when sorted to type. These plastics are the most widely available and would be best suited for manufacturing products requiring maximum durability.
• HDPE alone produces a rigid product while LDPE and LLDPE produce a flexible product. The most suitable blend can be selected to suit requirements. In the case of products such as drainage pipe and posts a blend of 50% HDPE - 50% LLDPE or LDPE is well suited. The 50-50 HDPE- LLDPE blend produces the most durable product making it best suited for pipe production.
With ageing and each time plastic is heated some plasticizer is lost and this can cause brittleness with repeated recycling. The addition of LDPE & or LLDPE & or mineral oil effectively adds plasticizer eliminating the brittleness in instances where a plastic is recycled multiple times. Plasticizing additives are available but are quite expensive,
To produce a structurally sound product blended plastics must be thoroughly mixed while molten and contaminants finely dispersed throughout the mix.
In the HDPE, LDPE & LLDPE blends, PP is a suitable substitute to HDPE and results in a more rigid product. PP alone tends to be brittle, but a blend may be suitable for products such as posts or pack spacers.
Processing PVC alone in the test rig produced some toxic gases. This was probably clue to hot spots created when the stationary disc makes contact with the spinning barrel. As the system 100 has no metal to metal contact processing PVC is feasible but extreme care would be necessarv to avoid overheating the PVC and generating hazardous and toxic gases. A scrubber, known by those practiced in the art, could be fitted to the at least one vent to deal with gaseous by-product issues. The end product was very soft and flexible. PVC does not appear compatible with other plastics.
Processing PET in the system 100 was successful but the centrifugal moulding technique caused brittleness. Other tests revealed in order to stop the brittleness PET must be moulded while barely molten.
Processing HIPS in the test rig was successful but the product was brittle. Mixed plastics that are not normally compatible could still be acceptable in limited quantities when fragmented by the shearing action of the rotating viscous mixing process and would be considered the same as other contaminates such as paper, aluminium foil and soil, which end up as small particles, evenly distributed throughout the product such that these contaminants would simply act as filler and have minimal effect on the structure of the plastic or the integrity of extruded products. Some plastic products have added filler powder simply because filler is cheaper than resin .
• Although not suitable for products such as pipe and posts, mixed plastics with a high proportion of incompatible plastics and other contaminates such as food residues could still be utilised for fuel pasties (i.e. for co-firing wit other combListible materials in a bonded format). As long as the plastic component of the pastie can still be moulded the durabi lity of the plastic is of little importance. One of the samples is a 50-50 blend of coke and LDPE, essentially 50% contamination, but with this technology a product can still be moulded.
• For white posts a suitable mix is 48% white 203tr containers HDPE - 48% clear film LDPE - 4% white master batch.
• The system 100 has capacity to receive mixed and contaminated plastics from waste beneficiation plants such as material recovery facilities (MRFs), dry commercial and industrial waste sorting facilities (Dirty MRFs) and alternative waste treatment facilities (AWTs). Facilities of the likes of MRFs, Dirty MRFs and AWT produce an off-take waste stream of contaminated mixed plastics of negative commercial value - i.e. the operator of the facility has to pay a third party to take this material for subsequent processing. Typical subsequent processing might include energy from waste, sorting washing and flaking. However, the system 100 allows this off-take stream to be processes as is, melted and blended then extruded onto combustible materials for co-firing in energy from waste facilities, steel making facilities, cement kilns and the like.
• The system 100 has capacity to receive and melt a mixture of plastics, with the composition of the mixture determined either by actual measurement of components as each plastic type is fed into the syste 100, or through the supply and feeding of mixed plastics arising from waste processing activities where the individual plastic types are not separated but left in a mixed state with no control on mix proportions.
in addition to the foregoing general examples, the following specific examples are relevant to demonstrate the flexibility possible in both the plastics that can be recycled and the products that can be produced: Mix | Advantages and Characteristics
Typical Polyethylene Mixes - Mending to suit properties:
40- 90% HOPE Mixes in this range can achieve properties similar to virgin
10-60 % LDPE or HDPE.
LLDPE The percentages depend on variables such as, the age of the raw materials, the original properties of the raw materials and the properties required in the end product.
The more aged the HDPE the more LDPE or LLDPE will be required to effectively re plasticise back to virgin properties.
90-99% HDPE The oil re-plasticises the HDPE (in a similar manner to the
1-10% mineral oil addition of LDPE or LLDPE above).
or vegetable oil The percentages can be varied to suit the rigidity-fle ibility properties required in the end product.
Increasing the HDPE increases the rigidity while increasing the LDPE,LLDPE or oil increases the flexibility.
Typical Polyethylene - Polypropylene mixes - blending to suit colour:
10-90% LDPE or PP woven material and PE film are both considered difficult to LLDPE. recycle and attract a low or negative value.
10-90% PP White PP and clear or white PE film are very common.
Combinations result in a white or opaque colour plastic, which can then be coloured as required, giving a much broader product range, such as roadside white posts, high visibility stock fencing & in genera! more aesthetically pleasing products.
Typical plastic comp osiie - blending to utilise otherwise un-recyclable plastics
1 -50% Laminated Plastic composites considered impossible to recycle can be plastic, Al foil, included
paper composite
50-99% HDPE,
PP, LDPE &
LLDPE
Oil as a plasticiser:
Previously, whereas plastic film contaminated with animal fat (cheese) and the like tended to degrade the plastic causing some brittleness, results show that 50-50 HDPE/LDPE with 10% mineral oil (engine oil) contamination produced a satisfactory plastic product not prone to brittleness. Indeed, mineral oil appears to have acted like a plasticizer.
As such, HDPE containers with both vegetable oil and mineral oil residues are well suited for introduction into the system 100 thereby advantageously providing an abundant source of low cost plastic. The oil does not appear to degrade the plastic and actually acts as a plastieizer in a similar way to LDPE film. 10% oil has a similar effect to 50 % LDPE film.
Oil contaminated HDPE could be extruded into high value products.
Vegetable oil appears to have the same effect as mineral oil.
The oil did reduce the friction between the plastic and the frictional heater 145, but the melt rate could be maintained by simply increasing the load on the frictional heater 145.
Waste oil may prove to be an effective low cost plasticizer for products recycled
Appendix B■■■■ Second Empirical plastic mix da ta
Two classes of product mix are described:
1. Extruded or moulded mixes to manufacture durable products such as pipes, posts, planks, spacers, protective packaging (dunnage), bearing pads (vibration insulation, and other WPCs (wood plastic composites); and
2. Extruded or moulded mixes to manufacture moulded or coated products such as fuel briquettes, coated fuels, encapsulated wastes.
Four classes of materials that comprise the mix constituents are described: 1. Primary plastics materials that comprise the basis of a mix such as HDPE (high- density polyethylene), LDPE (low-density polyethylene), LLDPE (linear low- density polyethylene), PP (polypropylene), HIPS (high impact polystyrene), PET (polyethylene terephthalate); and
2. Additive materials to the primary plastic materials that enhance the physical propeities of a mix (rigidity, flexibility, UV stability, plasticity, thermal expansion rate) such as mineral oil, vegetable oil, carbon black, and other granular powder materials such as crumb rubber and sawdust; additive materials may be added to the mix either before or after the melt phase; and
3. Contaminant materials that may be included with or attached to the primary plastic materials that add no specific value or beneficial attribute to the end product bu can be accommodated within the blend without great detriment to the utility of the manufactured product,
4. Co-product materials that may be coated by a material mix to produce a
composite fuel suitable for firing into combustion devices such as incinerators, cement kilns, steel-making furnaces, coal-fired power stations and the like, and may include conventional solid fuels such as coal, coke, charcoal, timber, sawdust, and/or other combustible materials such as plastics, paper products etc. ; co-product materials may be added to the mix either before or after the melt phase. Typical mixtures are set out in the following table,
Mixes to
Xla iiaclun? Mould** ) t*r Durable Produ t-*
50%-
0% -
100%
100%
50% -
HDPE 0% -
100%
LDPE 3 1 0%
50%- mimi LLDPE 3 0%~
100%
PP 100%
50% -
100%
100%
Mineral Oil 0% - 15%
Vegetable Oil 0% - 15%
Additive 0% - 15%
Carbon Black 0% - 5%
0% - 15% Crumb Rubber 0% - 5%
Sawdust 0% - 50%
Contaminants in
0%- 10% .A. aggregate
Other plastics 4
Associated 0% - 10% 0% -30% materials' ' ' 0% - 5% 0%; -30%
Attached materials 6 0% - 5% 0% - 1 %
Animal fats and 0% - 2% 0% - 10% grease
Notes:
1. In mixes to manufacture durable products, primary plastics may be blended in various ratios to produce mixes with different physical properties such as rigidity, flexibility.
2. In mixes to manufacture moulded or coated products, primary plastics may be blended in any combination.
3. LDPE and LLDPE may be incorporated in additional amounts as an additive
material to increase plasticity and/or to replace plasticLsers lost or destroyed in heating.
4. Other plastics include plastics types other than a primary plastic type, such as PS/EPS (polystyrene/expanded polystyrene), PVC (polyvinyl chloride), ABS/SAN (acrykmitrile butadiene styrene/styrene acrylonitrile), PU ipoiyurethane), polyester, nylon, and other aggregated polymer types.
5. Associated items include materials or products that are associated with the product that is comprises a primary plastic in a mix, such as plastic caps and labels from plastic bottles, adhesives and tales on joins, aluminium foil, and paper products in composites, etc.
6. Attached materials include extraneous matter and substances that are attached to the surface of a primary plastic as a result of its former use, application, treatment or handling prior to incorporation of the primary plastic in a mix, such as soil, vegetation and plant matter, food residues, oils, detergents, soaps and other chemicals, etc., but excluding animal fats and grease. Interpretation
Embodiments:
Reference throughout this specification to "one embodiment" or "an embodiment" means that a particular feature, structure or characteristic described in connection with the embodiment is included in at least one embodiment of the present invention. Thus, appearances of the phrases "in one embodiment" or "in an embodiment" in various places throughout this specification are not necessarily all referring to the same embodiment, but may. Furthermore, the particular features, structures or characteristics may be combined in any suitable manner, as would be apparent to one of ordinary skill in the art from this disclosure, in one or more embodiments.
Similariy it should be appreciated that in the above description of example embodiments of the invention, various features of the invention are sometimes grouped together in a single embodiment, figure, or description thereof for the purpose of streamlining the disclosure and aiding in the understanding of one or more of the various inventive aspects. This method of disclosure, however, is not to be interpreted as reflecting an intention that the claimed invention requires more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive aspects lie in less than all features of a single foregoing disclosed embodiment. Thus, the claims following the Detailed Description of Specific Embodiments are hereby expressly incorporated into this Detailed Description o Specific Embodiments, with each claim standing on its own as a separate embodiment of this invention.
Furthermore, while some embodiments described herein include some but not other features included in other embodiments, combinations of features of different embodiments are meant to be within the scope of the invention, and form different embodiments, as would be understood by those in the art. For example, in the following claims, any of the claimed embodiments can be used in any combination.
Different. Instances of Objects
As used herein, unless otherwise specified the use of the ordinal adjectives "first", ''second", "third", etc., to describe a common object, merely indicate that different instances of like objects are being referred to, and are not intended to imply that the objects so described must be in a given sequence, either temporally, spatially, in ranking, or in any other manner.
Specific Details
In the description provided herein, numerous specific details are set forth. However, it is understood that embodiments of the invention may be practiced without these specific details. In other instances, well-known methods, structures and techniques have not been shown in detail in order not to obscure an understanding of this description.
Terminology
In describing the preferred embodiment of the invention illustrated in the drawings, specific terminology will be resorted to for the sake of clarity. However, the invention is not intended to be limited to the specific terms so selected, and it is to be understood that each specific term includes all technical equivalents which operate in a similar manner to accomplish a similar technical purpose, Terms such as ' ' forward", "rearward", "radially", "peripherally", "upwardly", "downwardly", and the like are used as words of convenience to provide reference points and are not to be construed as limiting terms.
Comprising and Including
In the claims which follow and in the preceding description of the invention, except where the context requires otherwise due to express language or necessary implication, the word "comprise" or variations such as "comprises" or "comprising" are used in an inclusive sense, i.e. to specify the presence of the stated features but not to preclude the presence or addition of further features in various embodiments of the invention.
Any one of the terms: including or which includes or that includes as used herein is also an open term that also means including at least the elements/features that follow the term, but not excluding others. Thus, including is synonymous with and means comprising. Scope of Invention
Thus, while there has been described what are believed to be the preferred embodiments of the invention, those skilled in the art will recognize that other and further modifications may be made thereto without departing from the spirit of the invention, and it is intended to claim all such changes and modifications as fall, within the scope of the invention. For example, any formulas given above are merely representative of procedures that may be used. Functionality may be added or deleted from the block diagrams and operations may be interchanged among functional blocks. Steps may be added or deleted to methods described within the scope of the present invention.
Although the invention has been described with reference to specific examples, it will be appreciated by those skilled in the art that the invention may be embodted in many other forms.
Industrial Applicability
It is apparent from the above, that the arrangements described are applicable to the plastic processing industry.