Abstract:
A three-dimensional printing kit can include a polymeric build material including from about 80 wt% to 100 wt% polymer particles having an average particle size from about 10 μm to about 150 μm; and a fusing agent including an aqueous liquid vehicle and from about 2 wt% to about 20 wt% radiation absorber. The radiation absorber can include a charged yellow water-soluble dye that can be from about 1 wt% to about 40 wt% soluble in water.

Inventors:
DISCEKICI EMRE HIRO (US)
NAUKA KRZYSZTOF (US)
RUDISILL STEPHEN G (US)
Application Number:
PCT/US2020/021662
Publication Date:
September 16, 2021
Filing Date:
March 09, 2020
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
HEWLETT PACKARD DEVELOPMENT CO (US)
International Classes:
B29C64/264; B29C64/165; B33Y10/00; B33Y30/00; B33Y70/10
Domestic Patent References:
WO2016171724A12016-10-27
WO2019172937A12019-09-12
WO2018022046A12018-02-01
WO2018080456A12018-05-03
Foreign References:
CN108136673A2018-06-08
US6583273B12003-06-24
US20130316081A12013-11-28
Other References:
See also references of EP 4117892A4
Attorney, Agent or Firm:
COSTALES, Shruti et al. (US)
Download PDF:
Claims:
CLAIMS

What is Claimed Is:

1. A three-dimensional printing kit comprising: a polymeric build material including from about 80 wt% to 100 wt% polymer particles having an average particle size from about 10 pm to about 150 pm; and a fusing agent including an aqueous liquid vehicle and from about 2 wt% to about 20 wt% radiation absorber, the radiation absorber including a charged yellow water- soluble dye that is from about 1 wt% to about 40 wt% soluble in water.

2. The three-dimensional printing kit of claim 1 , wherein the polymeric build material includes polyamide, polyethylene, polyethylene terephthalate (PET), polystyrene, polyacrylate, polyacetal, polypropylene, polycarbonate, polyester, acrylonitrile butadiene styrene, thermoplastic polyamide, thermoplastic polyurethane, engineering plastic, polyether ketone, polyetheretherketone (PEEK), polyethylene terephthalate, polybutylene terephthalate, polymer blends thereof, amorphous polymers thereof, core-shell polymers thereof, or a copolymer thereof.

3. The three-dimensional printing kit of claim 1 , wherein the aqueous liquid vehicle includes from about 5 wt% to about 50 wt% organic co-solvent, wherein the organic co-solvent includes ethanol, methanol, propanol, acetone, tetrahydrofuran, hexane, 1 -butanol, 2-butanol, tert-butanol, isopropanol, propylene glycol, methyl ethyl ketone, dimethylformamide, 1,4-dioxone, acetonitrile, 1 ,2-butanediol, 1 -methyl-2, 3- propanediol, 2-pyrrolidone, or a combination thereof.

4. The three-dimensional printing kit of claim 1 , wherein the aqueous liquid vehicle includes from about 0.01 wt% to about 2 wt% surfactant.

5. The three-dimensional printing kit of claim 1 , wherein the radiation absorber exhibits peak absorption at from about 355 nm to about 455 nm.

6. The three-dimensional printing kit of claim 1 , wherein the radiation absorber includes a sulfonated azo yellow dye.

7. The three-dimensional printing kit of claim 1 , wherein the radiation absorber is present in the fusing agent at from about 5 wt% to about 15 wt%.

8. The three-dimensional printing kit of claim 1 , further comprising a detailing agent, wherein the detailing agent includes a detailing compound to reduce a temperature of the polymeric build material onto which the detailing agent is applied.

9. A method for three-dimensional printing comprising: iteratively applying a polymeric build material as individual layers, the polymeric build material including from about 80 wt% to 100 wt% polymeric particles having an average particle size from about 10 pm to about 150 pm to a powder bed; based on a three-dimensional object model, selectively applying a fusing agent including an aqueous liquid vehicle and from about 2 wt% to about 20 wt% radiation absorber, the radiation absorber including a charged yellow water-soluble dye that is from about 1 wt% to about 40 wt% soluble in water; and exposing the powder bed to ultraviolet energy or high-energy visible light having a wavelength in a range from about 355 nm to about 455 nm to selectively fuse portions of the individual layers of the polymeric build material together and form a three- dimensional object.

10. The method of claim 9, wherein the exposing includes exposing with the ultraviolet energy from a UV-LED light array via selectively applying the ultraviolet energy by activating a plurality of individual UV-LED lights of the UV-LED light array.

11. The method of claim 9, wherein a weight ratio of the polymeric build material to the radiation absorber following selectively applying the fusing agent onto the polymeric build material ranges from about 10:1 to about 350:1.

12. The method of claim 9, wherein based on the three-dimensional object model, the method further comprising applying a detailing agent onto individual layers of the polymer build material to selectively cool the polymeric build material.

13. The method of claim 9, wherein the radiation absorber includes a sulfonated azo yellow dye.

14. A three-dimensional printing system comprising: a polymeric build material including from about 80 wt% to 100 wt% polymer particles having an average particle size from about 10 pm to about 150 pm; and a fusing agent including an aqueous liquid vehicle and from about 2 wt% to about 20 wt% radiation absorber, the radiation absorber including a charged yellow water- soluble dye that is from about 1 wt% to about 40 wt% soluble in water; and an ultraviolet energy source that emits ultraviolet energy having a peak wavelength in a range from about 355 nm to about 400 nm, or a high-energy visible light source that emits high-energy visible light having a peak wavelength in a range from about 400 nm to about 455 nm.

15. The system of claim 14, wherein the system includes the ultraviolet energy source and the ultraviolet energy source has a peak emission of ultraviolet energy with a narrow band wavelength of less than about 30 nm, wherein the narrow band wavelength corresponds with a peak absorption of the radiation absorber.

Description:
THREE-DIMENSIONAL PRINTING WITH CHARGED YELLOW WATER-SOLUBLE DYE-BASED FUSING AGENT

BACKGROUND

[0001] Three-dimensional (3D) printing may be an additive printing process used to make three-dimensional solid parts from a digital model. Three-dimensional printing is often used in rapid product prototyping, mold generation, mold master generation, and short run manufacturing. Some three-dimensional printing techniques can be considered additive processes because they involve the application of successive layers of material. This can be unlike other machining processes, which often focus more on removal of material to create the final part.

BRIEF DESCRIPTION OF THE DRAWINGS

[0002] FIG. 1 is a schematic illustration of an example three-dimensional printing kit in accordance with the present disclosure;

[0003] FIG. 2 is a flow diagram illustrating an example method of three- dimensional printing in accordance with the present disclosure; and

[0004] FIG. 3 is a schematic illustration of an example three-dimensional printing system in accordance with the present disclosure.

DETAILED DESCRIPTION

[0005] Three-dimensional printing can be an additive process involving the application of successive layers of a polymeric build material with a fusing agent printed thereon to bind the successive layers of the polymeric build material together. More specifically, a fusing agent including a radiation absorber can be selectively applied to a layer of a polymeric build material on a support bed, e.g., a build platform supporting polymeric build material, to pattern a selected region of a layer of the polymeric build material. The layer of the polymeric build material can be exposed to electromagnetic radiation, and due to the presence of the radiation absorber on the printed portions, absorbed light energy at those portions of the layer having the fusing agent printed thereon can be converted to thermal energy, causing that portion to melt or coalesce, while other portions of the polymeric build material do reach temperatures suitable to melt or coalesce. This can then be repeated on a layer-by-layer basis until the three- dimensional object is formed.

[0006] In accordance with this, a three-dimensional printing kit (or “kit”) can include a polymeric build material including from about 80 wt% to 100 wt% polymer particles that can have an average particle size from about 10 pm to about 150 pm and a fusing agent that can include an aqueous liquid vehicle and from about 2 wt% to about 20 wt% radiation absorber. The radiation absorber can include a charged yellow water- soluble dye that can be from about 1 wt% to about 40 wt% soluble in water. In one example, the polymeric build material can include polyamide, polyethylene, polyethylene terephthalate (PET), polystyrene, polyacrylate, polyacetal, polypropylene, polycarbonate, polyester, acrylonitrile butadiene styrene, thermoplastic polyamide, thermoplastic polyurethane, engineering plastic, polyether ketone, polyetheretherketone (PEEK), polyethylene terephthalate, polybutylene terephthalate, polymer blends thereof, amorphous polymers thereof, core-shell polymers thereof, or a copolymer thereof. In another example, the aqueous liquid vehicle can include from about 5 wt% to about 50 wt% organic co-solvent. The organic co-solvent can include ethanol, methanol, propanol, acetone, tetrahydrofuran, hexane, 1 -butanol, 2-butanol, tert-butanol, isopropanol, propylene glycol, methyl ethyl ketone, dimethylformamide, 1 ,4-dioxone, acetonitrile, 1 ,2-butanediol, 1 -methyl-2, 3-propanediol, 2-pyrrolidone, or a combination thereof. In yet another example, the aqueous liquid vehicle can include from about 0.01 wt% to about 2 wt% surfactant. In a further example, the radiation absorber can have a peak absorption at from about 355 nm to about 455 nm. In one example, the radiation absorber can include a sulfonated azo yellow dye. In another example, the radiation absorber can be present in the fusing agent at from about 5 wt% to about 15 wt%. In yet another example, the kit can further include a detailing agent. The detailing agent can include a detailing compound to reduce a temperature of the polymeric build material onto which the detailing agent can be or was applied.

[0007] In another example of the present disclosure, a method of three- dimensional printing (or “method”) can include iteratively applying a polymeric build material as individual layers, the polymeric build material can include from about 80 wt% to 100 wt% polymeric particles that can have an average particle size from about 10 pm to about 150 pm to a powder bed, and based on a three-dimensional object model, selectively applying a fusing agent that can include an aqueous liquid vehicle and from about 2 wt% to about 20 wt% radiation absorber that can include a charged yellow water-soluble dye that can be from about 1 wt% to about 40 wt% soluble in water. The method can also include exposing the powder bed to ultraviolet energy or high-energy visible light having a wavelength in a range from about 355 nm to about 455 nm to selectively fuse portions of the individual layers of the polymeric build material together and form a three-dimensional object. In one example, exposing includes exposing with the ultraviolet energy from a UV-LED light array via selectively applying the ultraviolet energy by activating a plurality of individual UV-LED lights of the UV-LED light array. In another example, a weight ratio of the polymeric build material to the radiation absorber following the selectively applying of the fusing agent onto the polymeric build material can range from about 10:1 to about 350:1. In yet another example, the method can further include, based on the three-dimensional object model, applying a detailing agent onto individual layers of the polymeric build material to selectively cool the polymeric build material. In an example, the radiation absorber can include a sulfonated azo yellow dye.

[0008] In a further example, a three-dimensional printing system (or “system”) can include a polymeric build material including from about 80 wt% to 100 wt% polymer particles that can have an average particle size from about 10 pm to about 150 pm, and a fusing agent that can include an aqueous liquid vehicle and from about 2 wt% to about 20 wt% radiation absorber that can include a charged yellow water-soluble dye that can be from about 1 wt% to about 40 wt% soluble in water. The system can also include an ultraviolet energy source or a high-energy visible light source that can emit an ultraviolet energy having a peak wavelength in a range from about 355 nm to about 455 nm. In another example, the system includes the ultraviolet energy source and the ultraviolet energy source has a peak emission of ultraviolet energy with a narrow band wavelength of less than about 30 nm, wherein the narrow band wavelength corresponds with a peak absorption of the radiation absorber (the narrow band wavelength may span the UV energy and HEV light ranges in some examples).

[0009] When discussing the three-dimensional printing kit, method of three- dimensional printing, and/or the three-dimensional printing system herein, these discussions can be considered applicable to one another whether or not they are explicitly discussed in the context of that example. Thus, for example, when discussing a polymeric build material related to a three-dimensional printing kit, such disclosure is also relevant to and directly supported in the context of the method of three-dimensional printing, the three-dimensional printing system, and vice versa.

[0010] Terms used herein will have the ordinary meaning in their technical field unless specified otherwise. In some instances, there are terms defined more specifically throughout the specification or included at the end of the present specification, and thus, these terms can have a meaning as described herein.

Three-Dimensional Printing Kits

[0011 ] A three-dimensional printing kit 100 is shown by way of example in FIG. 1. The three-dimensional printing kit can include, for example, a polymeric build material 110 and a fusing agent 120. The polymeric build material can include from about 80 wt% to 100 wt% polymer particles 112 having an average particle size from about 10 pm to about 150 pm. The fusing agent can include an aqueous liquid vehicle 122 and from about 2 wt% to about 20 wt% radiation absorber 124 that can include a charged yellow water-soluble dye that can be from about 1 wt% to about 40 wt% soluble in water. The charged yellow water-soluble dye is shown as particles for illustrative purposes, but may typically be dissolved in the liquid vehicle.

[0012] In some examples, the three-dimensional printing kit can further include other fluids, such as coloring agents, detailing agents, or the like. A detailing agent, for example, can include a detailing compound which can be a compound that can reduce a temperature of the polymeric build material when applied thereto. In some examples, the detailing agent can be applied around edges of the application area of the fusing agent. This can prevent caking around the edges due to heat from the area where the fusing agent was applied. The detailing agent can also be applied in the same area where the fusing agent was applied in order to control the temperature and prevent excessively high temperatures when the polymeric build material is fused.

[0013] The polymeric build material may be packaged or co-packaged with the fusing agent, coloring agent, detailing agent, or the like in separate containers, and/or can be combined with the fusing agent, coloring agent, detailing agent, or the like at the time of printing, e.g., loaded together in a three-dimensional printing system.

Methods of Three-dimensional Printing

[0014] A flow diagram of an example method 200 of three-dimensional (3D) printing is shown in FIG. 2. The method can include iteratively 210 applying a polymeric build material as individual layers. The polymeric build material can include from about 80 wt% to 100 wt% polymeric particles that can have an average particle size from about 10 pm to about 150 pm to a powder bed. Based on a three-dimensional object model, the method can include selectively applying 220 a fusing agent that can include an aqueous liquid vehicle and from about 2 wt% to about 20 wt% radiation absorber that can include a charged yellow water-soluble dye that can be from about 1 wt% to about 40 wt% soluble in water. The method can further include, exposing 230 the powder bed to ultraviolet energy or high-energy visible light having a wavelength in a range from about 355 nm to about 455 nm to selectively fuse portions of the individual layers of the polymeric build material together and form a three-dimensional object. [0015] For clarity, the term “ultraviolet energy” or “UV” energy often includes electromagnetic energy wavelengths ranging from about 10 nm to about 400 nm, and visible light often is defined to include light ranging from 400 nm to 700 nm. “High- energy visible” light, or HEV light, is a sub-range of visible light often defined as ranging from about 400 nm to about 450 nm. Because of the disparities in these definitions, for purposes of the present disclosure, the range of UV energy is defined to include energy wavelengths up to about 405 nm, and HEV light is defined herein to include wavelengths up to about 455 nm. Thus, with respect to the energy wavelength ranges herein that can be from about 355 nm to about 455 nm, the range of about 355 nm to about 405 nm is defined herein to be UV energy, and the range of about 405 nm to about 455 nm is defined to be HEV energy, which encompasses violet to blue visible light. In further detail, the terms “energy” and “light” both refer to electromagnetic energy. Light is used in connection with the HEV energy, as it is within the visible light range.

[0016] In printing in a layer-by-layer manner, the polymeric build material can be spread, a fusing agent applied, the layer of the polymeric build material can be exposed to energy, and then a build platform can then be dropped a distance of 5 pm to 1 mm, which can correspond to the thickness of a printed layer of the three-dimensional object, so that another layer of the polymeric build material can be added again thereon to receive another application of the fusing agent, and so forth. During the build, the radiation absorber in the fusing agent can act to convert the ultraviolet energy to thermal energy and promote the transfer of thermal heat to polymer particles of the polymeric build material in contact with the fusing agent including the radiation absorber. In an example, the fusing agent can elevate a temperature of the polymer particles of the polymeric build material above a melting or softening point of the polymer particles, thereby allowing fusing (e.g., sintering, melting, curing, etc.) the polymeric build material (or polymer particles thereof) and allowing the formation of an individual layer of the three-dimensional object. The method can be repeated until all the individual polymeric build material layers have been created and a three-dimensional object is formed. In some examples, the method can further include heating the polymeric build material prior to dispensing or applying the individual layers of the polymeric build material.

[0017] With respect to applying the fusing agent to the polymeric build material, the fusing agent can be applied such that a specified amount of the radiation absorber is in contact with the polymeric build material. Accordingly, in an example, a weight ratio of the polymeric build material to the radiation absorber following the selectively applying of the fusing agent onto the polymeric build material can range from about 10:1 to about 350:1. In yet other examples, a weight ratio of the polymeric build material to the radiation absorber following the selectively applying of the fusing agent onto the polymeric build material can range from about 50:1 to about 250:1, from about 10:1 to about 100: 1 , from about 100: 1 to about 300: 1 , or from about 150: 1 to about 300: 1.

[0018] In some examples, the exposing can include the ultraviolet energy and the ultraviolet energy can be from an ultraviolet (UV) light source. UV light sources can have less energy consumption, longer lifespans, and smaller sizes than infrared or near-infrared light sources. Example UV light sources can include an electric arc, mercury-vapor lamp, incandescent “black light” lamp, short-wave ultraviolet lamp, fluorescent lamp tube, gas-discharge lamp, xenon arc lamp, deuterium arc lamp, mercury-xenon arc lamp, metal-halide arc lamp, excimer lamp, light-emitting diode, gas laser, laser diode, solid-state laser, or a combination thereof. In one example, the ultraviolet energy can be from an ultraviolet light emitting diode (UV-LED) light array. With respect to UV-LED light emitting diode light arrays, individual light bulbs on the array can be turned on and off. This can permit selective application of the ultraviolet energy by activating a plurality of individual UV-LED lights of an UV-LED light array.

This can also reduce energy consumption.

[0019] In yet other examples, the exposing can include the use of high-energy visible light from a high-energy visible light source. Example high-energy visible light sources can include a blue LED light array, tungsten-halogen lamp, mercury-xenon arc lamp, xenon arc lamp, gas laser, laser diode, solid-state laser, or a combination thereof.

[0020] In some examples, the ultraviolet energy source and/or the high-energy visible light source can emit a wavelength of from about 355 nm to about 455 nm. In yet another example, the ultraviolet energy source can be used which can emit ultraviolet energy at a wavelength from about 355 nm to about 405 nm, from about 375 nm to about 400 nm, from about 360 nm to about 390 nm, or from about 380 nm to about 405 nm. Alternatively or additionally, the high-energy visible light source can be used, which can emit HEV light at from about 405 nm to about 455 nm, or from about 405 nm to about 450 nm. In other examples, energy source used can emit electromagnetic energy at a wavelength spanning both the UV energy range and the HEV light range, e.g., from about 360 nm to about 450 nm, from about 390 nm to about 450 nm, from about 375 nm to about 430 nm, etc. In further detail, the peak emission of the UV energy source or HEV light source can fall within the range of about 355 nm to about 455 nm, but the bandwidth, e.g., about 30 nm wide, may overlap both the UV energy range and the HEV light range. Alternatively, the bandwidth may fall solely within the UV range or the HEV range.

[0021] In some examples, the method can further include, iteratively and selectively dispensing or applying a detailing agent onto an individual polymeric build material layer laterally at a border between a first area where the individual polymeric build material layer was contacted by the fusing agent and a second area where the individual polymeric build material layer was not contacted by the fusing agent. This can prevent caking around the edges due to heat from the area where the fusing agent was applied. The detailing agent can also be applied in the same area where the fusing agent was applied in order to control a temperature of the polymeric build material and prevent excessively high temperatures when the polymeric build material is fused.

Three-Dimensional Printing Systems

[0022] A three-dimensional printing system 300 in accordance with the present disclosure is illustrated schematically in FIG. 3. The three-dimensional printing system can include a polymeric build material 110, a fusing agent 120, and an ultraviolet energy source or a high-energy visible light source 310. The polymeric build material can include from about 80 wt% to 100 wt% polymer particles that can have an average particle size from about 10 pm to about 150 pm. The fusing agent can include an aqueous liquid vehicle and from about 2 wt% to about 20 wt% radiation absorber that can include a charged yellow water-soluble dye that can be from about 1 wt% to about 40 wt% soluble in water. The ultraviolet energy source or the high-energy visible light source can emit energy (e) that can have a peak wavelength in a range from about 355 nm to about 455 nm.

[0023] In some examples, a peak absorption of the radiation absorber can be substantially matched to a narrow band wavelength emitted by the energy source. As used herein, “peak absorption” indicates that from about 70% to about 100% of light emitted in the wavelength range of from about 355 nm to about 405 nm is absorbed by the radiation absorber. In yet other examples at least about 75%, at least about 80%, at least about 85%, at least about 90%, at least about 95%, or 100% of the light emitted in the wavelengths emitted by the energy source is absorbed by the radiation absorber. In an example, the energy source can emit energy that can have a full width at half max of less than about 30 nm corresponding with a peak absorption of the radiation absorber.

In yet other examples, the energy source can emit energy that can have a full width at half max of less than about 25 nm, less than about 20 nm, less than about 15 nm, less than about 10 nm, or less than about 5 nm corresponding with a peak absorption of the radiation absorber.

[0024] The energy source can be positioned to expose the individual layers of the polymeric build material to ultraviolet energy or high-energy visible light to selectively fuse polymer particles of the polymeric build material in contact with the radiation absorber (forming fused layers) to iteratively form each layer of a three-dimensional object 320. In some examples, the energy source can be operatively connected to a lamp/laser driver, an input/output temperature controller, and/or temperature sensors.

[0025] In some examples, the fusing agent, the detailing agent, or other fluid agent can be applied via a fluid applicator and the system can further include a fluid applicator 330. The fluid applicator can be a digital fluid ejector, e.g., thermal or piezo jetting architecture. The fluid applicator, in an example, can be fluidly coupled or coupleable to a fluid agent to iteratively apply the fluid agent to the polymeric build material to form individually patterned object layers. The fluid applicator can be any type of apparatus capable of selectively dispensing or applying a fluid agent. For example, the fluid applicator can be a fluid ejector or digital fluid ejector, such as an inkjet printhead, e.g., a piezo-electric printhead, a thermal printhead, a continuous printhead, etc. The fluid applicator could likewise be a sprayer, a dropper, or other similar structure for applying a fluid agent to the polymeric build material. Thus, in some examples, the application can be by jetting or ejecting from a digital fluid jet applicator, similar to an inkjet pen.

[0026] In an example, the fluid applicator, when present, can be located on a carriage track, but could be supported by any of a number of structures. In yet another example, the fluid applicator can include a motor (not shown) and can be operable to move back and forth, and the fluid applicator can also be moved front to back as well, to provide both x-axis and y-axis movement over the polymeric build material when positioned over or adjacent to a polymeric build material on a powder bed of a build platform.

[0027] In an example, the three-dimensional printing system can further include a build platform 340 to support the polymeric build material. The polymeric build material 110 can be deposited onto the build platform by a build material applicator 350 where the particulate build material can be flattened or smoothed, such as by a mechanical roller or other flattening technique. This can form a flat layer of particulate build material. The build platform can be positioned to permit application of the fusing agent onto a layer of the polymeric build material. The build platform can be configured to drop in height, thus allowing for successive layers of the polymeric build material to be applied by a supply and/or a spreader. The polymeric build material can be layered in the build platform at a thickness that can range from about 5 pm to about 1 mm. In some examples, individual layers can have a relatively uniform thickness. In one example, a thickness of a layer of the polymeric build material can range from about 10 pm to about 500 pm, from about 50 pm to about 300 pm, from about 250 pm to about 500 pm, or from about 30 pm to about 200 pm. Furthermore, heat can be applied to the build platform, or from any other direction or time, to bring the polymeric build material to a temperature near its fusing temperature, making it easier to bring up a temperature enough to generate fusion of the polymeric build material. For example, heat may be applied to the polymeric build material in the powder bed from the build platform, from above, or to the polymeric build material prior to being spread on the powder bed to preheat the polymeric build material within about 10 °C to about 70 °C of a fusing temperature of the polymer particles so that less energy may be applied to bring the polymer particles to their fusing temperature.

Polymeric Build Materials

[0028] The polymeric build material can be used as the bulk material of the three- dimensional printed object. As mentioned, the polymeric build material can include from about 80 wt% to 100 wt% polymer particles. In another example, the polymeric build material can include from about 85 wt% to about 95 wt%, from about 90 wt% to 100 wt%, or 100 wt% polymer particles.

[0029] In an example, the polymeric build material can include polyamide, polyethylene, polyethylene terephthalate (PET), polystyrene, polyacrylate, polyacetal, polypropylene, polycarbonate, polyester, acrylonitrile butadiene styrene, thermoplastic polyamide, thermoplastic polyurethane, engineering plastic, polyether ketone, polyetheretherketone (PEEK), polyethylene terephthalate, polybutylene terephthalate, polymer blends thereof, amorphous polymers thereof, core-shell polymers thereof, or a copolymer thereof. In another example, the polymeric build material can include a polyamide. In yet example, the polymeric build material can include a thermoplastic polyamide.

[0030] The polymeric build material may include similarly sized polymer particles or differently sized polymer particles. The terms "size" or "particle size," as used herein, refers to the diameter of a substantially spherical particle, or the effective diameter of a non-spherical particle, e.g., the diameter of a sphere with the same mass and density as the non-spherical particle as determined by weight. Particle size information can be determined and/or verified using a scanning electron microscope (SEM), or can be measured using a particle analyzer such as a MASTERSIZER™ 3000 available from Malvern Panalytical, for example. The particle analyzer can measure particle size using laser diffraction. A laser beam can pass through a sample of particles and the angular variation in intensity of light scattered by the particles can be measured. Larger particles scatter light at smaller angles, while small particles scatter light at larger angles. The particle analyzer can then analyze the angular scattering data to calculate the size of the particles using the Mie theory of light scattering. Particle size can be reported as a volume equivalent sphere diameter. An average particle size can refer to a mathematical average of the particle sizes. Alternatively, the particle size can be based on a particle size distribution including a D50 particle size, where 50% of the particles are larger than the D50 value and 50% of the particles are smaller than the D50 value. The polymer particles can have an average particle size from about 10 pm to about 150 pm, from about 25 pm to about 125 pm, from about 50 pm to about 150 pm, or from about 20 pm to about 80 pm. In another example, the D50 particle size can independently be from about 10 pm to about 150 pm, from about 25 pm to about 125 pm, from about 50 pm to about 150 pm, or from about 20 pm to about 80 pm. The polymeric build material can, in some examples, further include flow additives, antioxidants, inorganic filler, or any combination thereof. Typically, an amount of any of these or other similar components can be at about 5 wt% or less. An example flow additive can include fumed silica. Example antioxidants can include hindered phenols, phosphites, thioethers, hindered amines, and/or the like. Example inorganic filler can include particles such as alumina, silica, fibers, carbon nanotubes, cellulose, and/or the like. Some additives may be found in multiple categories of additives, e.g., fumed silica can be a flow additive as well as a filler. In some examples, the filler or other type of additive can become embedded or composited with the polymer particles.

[0031] The polymeric build material can be capable of being printed into three- dimensional objects with a resolution of about 10 pm to about 150 pm, about 20 pm to about 100 pm, or about 25 pm to about 80 pm. As used herein, “resolution” refers to the size of the smallest feature that can be formed on a three-dimensional object. The polymeric build material can form layers from about 10 pm to about 150 pm thick, depending on the size of polymer particles present in the polymeric build material, thus allowing the fused layers of the printed object to have about the same thickness or a few to many times (e.g., 2 to 20 times) thicker than the D50 particle size of the polymer particles, for example. This can provide a resolution in the z-axis direction (e.g., the direction of the buildup of layers) of about 10 pm to about 150 pm. In some examples, however, the polymeric build material can also have a sufficiently small particle size and sufficiently uniform particle shape to provide an x-axis and y-axis resolution about the size of the polymer particle size, e.g., about 2 pm to about 150 pm (e.g., the axes parallel to the support surface of the build platform).

Fusing Agents

[0032] The three-dimensional printing kit, three-dimensional printing system, and method of three-dimensional printing can make use of a fusing agent. The fusing agent can include an aqueous liquid vehicle and from about 2 wt% to about 20 wt% radiation absorber to generate heat from absorbed electromagnetic radiation. In an example, the aqueous liquid vehicle can include water at from about 25 wt% to about 98 wt%, from about 80 wt% to about 95 wt%, from about 40 wt% to about 60 wt%, or from about 60 wt% to about 90 wt%. In some examples, the aqueous liquid vehicle can also include from about 2 wt% to about 60 wt%, from about 5 wt% to about 50 wt%, from about 15 wt% to about 45 wt%, or from about 2 wt% to about 20 wt% organic co-solvent. In an example, the aqueous liquid vehicle can include organic-solvent to water at a ratio from about 1:3 to about 19:1, from about 1:3 to about 10:1, from about 1:2 to about 5:1, from about 1 :2 to about 2: 1 , or from about 1 :2 to about 1:1.

[0033] In some examples, there may be other liquid or dispersed additives in the aqueous liquid vehicle. In some examples, the aqueous liquid vehicle can further include from about 0.01 wt% to about 2 wt% or from about 0.01 wt% to about 0.5 wt% surfactant. Regarding other additives, in some examples, the fusing agent can further include a dispersant. Dispersants can help disperse the radiation absorber. In some examples, the dispersant itself can also absorb radiation. Other additives may be present as part of the aqueous liquid vehicle, as described more fully below.

[0034] The fusing agent can include a radiation absorber that can include a charged yellow water-soluble dye. The charged yellow water-soluble dye can be a natural dye or a synthetic dye. In some examples, the charged yellow water-soluble dye can be an acid dye. For example, the charged yellow water-soluble dye can be an anionic dye. In some examples, the charged yellow water-soluble dye can be a sulfur- containing dye. In further examples, the charged yellow water-soluble dye can be a sulfonated azo yellow dye. Examples of charged yellow water-soluble dyes can include Cl acid yellow 23, Cl acid yellow 17, Cl acid yellow 4, Cl acid yellow 5, Cl acid yellow 21 , Cl acid yellow 49, Cl acid yellow 42, Cl acid yellow 117, or a combination thereof. In an example, the charged yellow water-soluble dye can include a sulfonated azo yellow dye, such as Cl acid yellow 23, Cl acid yellow 17, or a combination thereof.

[0035] The charged yellow water-soluble dye can absorb radiation of wavelengths in the range of from about 355 nm to about 455 nm. In yet other examples, the charged yellow water-soluble dye can absorb radiation of wavelengths in the range of from about 390 nm to about 405 nm, from about 355 nm to about 375 nm, from about 355 nm to about 405 nm, from about 390 nm to about 455nm, from about 405 nm to about 455 nm, or from about 380 nm to about 400 nm, or any other range recited herein, for example. In some examples, the fusing agent can exclude pigment, metal oxide nanoparticles, or a combination thereof. Thus, in some examples, the radiation absorber in the fusing agent can consist of charged water-soluble yellow dye, and in other examples, the radiation absorber can consist of sulfonated azo yellow dye.

[0036] An amount of radiation absorber in the fusing agent can vary depending on the type of radiation absorber. In some examples, an amount of radiation absorber in the fusing agent can be from about 2 wt% to about 20 wt%. In yet other examples, the amount of radiation absorber in the fusing agent can be from about 5 wt% to about 15 wt%, from about 5 wt% to about 12 wt, from about 10 wt% to about 20 wt%, or from about 2 wt% to about 10 wt%.

Other Fluid Agents

[0037] In some examples, the three-dimensional printing kit, three-dimensional printing system, or method of three-dimensional printing can further include other fluid agents, such as coloring agent(s), detailing agent, or the like. A coloring agent, for example, may include an aqueous liquid vehicle and a colorant, e.g., a dye and/or pigment. A detailing agent, on the other hand, may include a detailing compound capable of cooling the polymeric build material upon application. In some examples, the detailing agent can be printed around the edges of the portion of a polymeric build material that was or can be printed with the fusing agent. The detailing agent can increase selectivity between fused and un-fused portions of the polymeric build material by reducing a temperature of the polymeric build material around an edge of the portion to be fused. In other examples, the detailing agent can be printed in areas where the fusing agent was or can be printed to provide additional cooling when printing a three- dimensional object.

[0038] In further detail regarding the detailing agent, the detailing compound can be or can include a solvent that can evaporate at a temperature of the polymeric build material supported on the powder bed or build platform. For example, in some cases, the polymeric build material in the powder bed can be preheated to a preheat temperature within about 10 °C to about 70 °C of the fusing temperature of the polymeric build material. In other examples, the detailing compound can provide cooling as a temperature is brought above the preheat temperature due to application of electromagnetic energy applied to the fusing agent (applied to the polymeric build material). Thus, the detailing agent can be a solvent that can evaporate upon contact with the polymeric build material at the preheat temperature and/or fusing temperature, thereby cooling the printed portion through evaporative cooling. In certain examples, the detailing agent can be or can include water, organic co-solvent(s), or combinations thereof, as the detailing compound. In further examples, the detailing agent can be substantially devoid of radiation absorbers. That is, in some examples, the detailing agent can be substantially devoid of ingredients that absorb enough energy from the ultraviolet energy source to cause the polymeric build material to fuse. In certain examples, the detailing agent can include colorants such as dyes or pigments that do not cause the polymeric build material printed with the detailing agent to fuse when exposed to the ultraviolet energy source. Aqueous Liquid Vehicles

[0039] As used herein, the term “aqueous liquid vehicle” may refer to the liquid in the fusing agent and/or other fluid agents that may be present, e.g., detailing agent, coloring agent, etc. The aqueous liquid vehicle may include water alone or in combination with a variety of additional components. The aqueous liquid vehicle may be water, or may include water and organic co-solvent, for example. Examples of components that may be included, in addition to water, may include organic co-solvent, surfactant, buffer, antimicrobial agent, anti-kogation agent, chelating agent, buffer, etc.

In an example, the aqueous liquid vehicle can include water and organic co-solvent. In another example, the aqueous liquid vehicle can include water, organic co-solvent, and a surfactant. In yet another example, the aqueous liquid vehicle can include water, organic co-solvent, surfactant, and buffer or buffer and a chelating agent.

[0040] The aqueous liquid vehicle can include water that may be deionized, for example. In one example, water can be present in the fusing agent, the detailing agent, or other fluid agent at a weight percentage that can vary from about 25 wt% to about 94 wt%, from about 60 wt% to about 94 wt%, or from about 30 wt% to about 75 wt%.

[0041] The aqueous liquid vehicle may include organic co-solvent(s). Some examples of co-solvent(s) that may be added to the aqueous liquid vehicle can include 1-(2-hydroxyethyl)-2-pyrollidinone, 2-pyrrolidinone, 2-methyl-1 ,3-propanediol, 1,5- pentanediol, triethylene glycol, tetraethylene glycol, 1,6-hexanediol, tripropylene glycol methyl ether, ethoxylated glycerol-1 (LEG-1), or a combination thereof. In one example, the co-solvent can include 2-pyrrolidonone. Whether a single co-solvent is included or a combination of co-solvents are included, the total amount of co-solvent(s) in the fusing agent, the detailing agent, or other fluid agent can be from about 5 wt% to about 60 wt%, from about 10 wt% to about 50 wt%, from about 15 wt% to about 45 wt%, from about 30 wt% to about 50 wt%, or from about 5 wt% to about 35 wt%, based on a total weight percentage of the fluid agent.

[0042] The aqueous liquid vehicle may also include surfactant. The surfactant can include a non-ionic surfactant, a cationic surfactant, and/or an anionic surfactant. In one example, the fluid agent can include an anionic surfactant. In another example, the fluid agent can include a non-ionic surfactant. In still another example, the fluid agent can include a blend of both anionic and non-ionic surfactant. Example non-ionic surfactant that can be used include self-emulsifiable, nonionic wetting agents based on acetylenic diol chemistry (e.g., SURFYNOL ® SEF from Air Products and Chemicals,

Inc., USA), a fluorosurfactant (e.g., CAPSTONE ® fluorosurfactants from DuPont, USA), or a combination thereof. In other examples, the surfactant can be an ethoxylated low- foam wetting agent (e.g., SURFYNOL ® 440, SURFYNOL ® 465, or SURFYNOL ® CT-111 from Air Products and Chemical Inc., USA) or an ethoxylated wetting agent and molecular defoamer (e.g., SURFYNOL ® 420 from Air Products and Chemical Inc.,

USA). Still other surfactants can include wetting agents and molecular defoamers (e.g., SURFYNOL ® 104E from Air Products and Chemical Inc., USA), alkylphenylethoxylates, solvent-free surfactant blends (e.g., SURFYNOL ® CT-211 from Air Products and Chemicals, Inc., USA), water-soluble surfactant (e.g., TERGITOL ® TMN-6, TERGITOL ® 15S7, and TERGITOL ® 15S9 from The Dow Chemical Company, USA), or a combination thereof. In other examples, the surfactant can include a non-ionic organic surfactant (e.g., TEGO ® Wet 510 from Evonik Industries AG, Germany), a non-ionic secondary alcohol ethoxylate (e.g., TERGITOL® 15-S-5, TERGITOL ® 15-S-7, TERGITOL ® 15-S-9, and TERGITOL ® 15-S-30 all from Dow Chemical Company, USA), or a combination thereof. Example anionic surfactants can include alkyldiphenyloxide disulfonate (e.g., DOWFAX ® 8390 and DOWFAX ® 2A1 from The Dow Chemical Company, USA), and oleth-3 phosphate surfactant (e.g., CRODAFOS™ N3 Acid from Croda, UK). Example cationic surfactant that can be used can include dodecyltrimethylammonium chloride, hexadecyldimethylammonium chloride, or a combination thereof. In some examples, the surfactant (which may be a blend of multiple surfactants) may be present in the fusing agent, the detailing agent, or other fluid agent at an amount ranging from about 0.01 wt% to about 2 wt%, from about 0.05 wt% to about 1 .5 wt%, or from about 0.01 wt% to about 1 wt%.

[0043] In some examples, the aqueous liquid vehicle may further include a chelating agent, an antimicrobial agent, a buffer, or a combination thereof. While the amount of these may vary, if present, these can be present in the fusing agent, the detailing agent, or other fluid agent at a total amount ranging from about 0.001 wt% to about 20 wt%, from about 0.05 wt% to about 10 wt%, or from about 0.1 wt% to about 5 wt%.

[0044] The aqueous liquid vehicle may include a chelating agent. Chelating agent(s) can be used to minimize or to eliminate the deleterious effects of heavy metal impurities. Examples of suitable chelating agents can include disodium ethylene- diaminetetraacetic acid (EDTA-Na), ethylene diamine tetra acetic acid (EDTA), and methyl-glycinediacetic acid (e.g., TRILON ® M from BASF Corp., Germany). If included, whether a single chelating agent is used or a combination of chelating agents is used, the total amount of chelating agent(s) in the fusing agent, the detailing agent, or other fluid agent may range from 0.01 wt% to about 2 wt% or from about 0.01 wt% to about 0.5 wt%.

[0045] The aqueous liquid vehicle may also include antimicrobial agents. Antimicrobial agents can include biocides and fungicides. Example antimicrobial agents can include the NUOSEPT ® , Ashland Inc. (USA), VANCIDE ® (R.T. Vanderbilt Co.,

USA), ACTICIDE ® B20 and ACTICIDE ® M20 (Thor Chemicals, U.K.), PROXEL ® GXL (Arch Chemicals, Inc.. USA), BARDAC ® 2250, 2280, BARQUAT ® 50-65B, and CARBOQUAT ® 250-T, (Lonza Ltd. Corp., Switzerland), KORDEK® MLX (The Dow Chemical Co., USA), and combinations thereof. In an example, if included, a total amount of antimicrobial agents in the fusing agent, the detailing agent, or other fluid agent can range from about 0.01 wt% to about 1 wt%.

[0046] In some examples, an aqueous liquid vehicle may further include buffer solution(s). The buffer solution(s) can withstand small changes (e.g., less than 1 ) in pH when small quantities of a water-soluble acid or a water-soluble base are added to a composition containing the buffer solution(s). The buffer solution(s) can have pH ranges from about 5 to about 9.5, from about 7 to about 9, or from about 7.5 to about 8.5. In some examples, the buffer solution(s) can include a poly-hydroxy functional amine. In other examples, the buffer solution(s) can include potassium hydroxide, 2-[4-(2- hydroxyethyl) piperazin-1-yl] ethane sulfonic acid, 2-amino-2-(hydroxymethyl)-1 ,3- propanediol (TRIZMA ® sold by Sigma-Aldrich, USA), 3-morpholinopropanesulfonic acid, triethanolamine, 2-[bis-(2-hydroxyethyl)-amino]-2-hydroxymethyl propane-1 ,3-diol (bis tris methane), N-methyl-D-glucamine, N,N,N’N’-tetrakis-(2-hydroxyethyl)- ethylenediamine and N,N,N’N’-tetrakis-(2-hydroxypropyl)-ethylenediamine, beta- alanine, betaine, or mixtures thereof. In yet other examples, the buffer solution(s) can include 2-amino-2-(hydroxymethyl)-1 ,3-propanediol (TRIZMA ® sold by Sigma-Aldrich, USA), beta-alanine, betaine, or mixtures thereof. The buffer solution, if included, can be added to the fusing agent, the detailing agent, or other fluid agent at an amount ranging from about 0.01 wt% to about 10 wt%, from about 0.1 wt% to about 7.5 wt%, or from about 0.05 wt% to about 5 wt%.

Definitions

[0047] It is noted that, as used in this specification and the appended claims, the singular forms "a," "an," and "the" include plural referents unless the content clearly dictates otherwise.

[0048] The term "about" as used herein, when referring to a numerical value or range, allows for a degree of variability in the value or range, for example, within 10%, or, in one aspect within 5%, of a stated value or of a stated limit of a range. The term “about” when modifying a numerical range is also understood to include as one numerical subrange a range defined by the exact numerical value indicated, e.g., the range of about 1 wt% to about 5 wt% includes 1 wt% to 5 wt% as an explicitly supported sub-range.

[0049] As used herein, “kit” can be synonymous with and understood to include a plurality of multiple components where the different components can be separately contained (though in some instances co-packaged in separate containers) prior to use, but these components can be combined together during use, such as during the three- dimensional object build processes described herein. The containers can be any type of a vessel, box, or receptacle made of any material.

[0050] As used herein, “applying” when referring to fusing agent that may be used, for example, refers to any technology that can be used to put or place the fluid, e.g., fusing agent, on the polymeric build material or into a layer of polymeric build material for forming a three-dimensional object. For example, “applying” may refer to a variety of dispensing technologies, including “jetting,” “ejecting,” “dropping,” “spraying,” or the like.

[0051] As used herein, “jetting” or “ejecting” refers to fluid agents or other compositions that are expelled from ejection or jetting architecture, such as ink-jet architecture. Ink-jet architecture can include thermal or piezoelectric architecture. Additionally, such architecture can be configured to print varying drop sizes such as up to about 20 picoliters, up to about 30 picoliters, or up to about 50 picoliters, etc.

Example ranges may include from about 2 picoliters to about 50 picoliters, or from about 3 picoliters to about 12 picoliters.

[0052] As used herein, a plurality of items, structural elements, compositional elements, and/or materials may be presented in a common list for convenience. However, these lists should be construed as though an individual member of the list is identified as a separate and unique member. Thus, no individual member of such list should be construed as a de facto equivalent of any other member of the same list based on presentation in a common group without indications to the contrary.

[0053] Concentrations, dimensions, amounts, and other numerical data may be presented herein in a range format. It is to be understood that such range format is used merely for convenience and brevity and should be interpreted flexibly to include the numerical values explicitly recited as the limits of the range, as well as to include all the individual numerical values or sub-ranges encompassed within that range as the individual numerical value and/or sub-range is explicitly recited. For example, a weight ratio range of about 1 wt% to about 20 wt% should be interpreted to include the explicitly recited limits of 1 wt% and 20 wt% and to include individual weights such as about 2 wt%, about 11 wt%, about 14 wt%, and sub-ranges such as about 10 wt% to about 20 wt%, about 5 wt% to about 15 wt%, etc. EXAMPLES

[0054] The following illustrates examples of the present disclosure. Numerous modifications and alternative compositions, methods, and systems may be devised without departing from the present disclosure. The appended claims are intended to cover such modifications and arrangements.

Example 1 - Preparation of Fusing Agents

[0055] Two ultraviolet fusing agent formulations were prepared by admixing the respective components in Tables 1 and 2.

Table 1 : Fusing Agent Formulation 1

* Dowfax ® 2A1 is commercia ly available from The Dow Chemical Company, USA

Table 2: Fusing Agent Formulation 2

* Dowfax ® 2A1 is commercia ly available from The Dow Chemical Company, USA

Both of the formulations were tested for jettability by individually dispensing the formulations as bars printed onto a paper medium using an HP ® inkjet printer Motive. Following printing of the fusing agent formulations, the formulations did not exhibit any negative effects on decap or nozzle health of the printhead. Example 2 - Preparation of Three-Dimensional Objects

[0056] In order to test the fusing capability of the fusing agent formulations from Tables 1 and 2 above, rectangular three-dimensional objects (15x40 mm in size) were printed on a single 300 pm thick layer of a polyamide 12 powder spread on a glass substrate. The polyamide 12 powder was held at an elevated temperature of about 100 °C applying heat from beneath the glass substrate. The fusing agents from Tables 1 and 2 were independently printed at an ink density of 18 picoliters per 600 th of an inch (per single pass), which corresponds to a fusing agent to polymeric build material weight ratio of about 1 :300 for Fusing Agent Formulation 1 and 1 :200 for Fusing Agent Formulation 2. Heat was removed from beneath the glass substrate, and the substrate with polyamide 12 powder and the fusing agent printed thereon was placed under a 395 nm UV-LED light array capable of emitting UV radiation at maximum intensity (100% intensity) of 12 W/cm 2 for the set periods of time indicated in Table 3 below. Table 3: Print Conditions

All of the three-dimensional printed objects fused following exposure to the UV-LED light array and were capable of being moved. High selectivity was observed. The polyamide 12 powder surrounding the rectangles did not fuse. Example 3 - Preparation of Three-Dimensional Objects

[0057] In order to test the fusing capability of the fusing agent formulation from Table 1 above, four square three-dimensional objects (800 pm x 800 pm in size) were printed on an 800 pm thick layer of thermoplastic polyamide powder spread on a glass substrate. The thermoplastic polyamide powder was held at an elevated temperature of 100 °C from beneath the glass substrate. The fusing agent was printed thereon, and then heat was removed from beneath the glass substrate. The substrate with thermoplastic polyamide powder with the fusing agent printed thereon was placed under a 395 nm UV-LED light array capable of emitting UV irradiation at maximum intensity (100% intensity) of 12 W/cm 2 for the set periods of time as indicated in Table 4 below.

Table 4: Print Conditions

All four of the three-dimensional objects fused following exposure to the UV-LED light array and were capable of being moved. High selectivity was observed. The thermoplastic polyamide powder surrounding the rectangles did not fuse.

[0058] The examples above indicate that water-soluble acid yellow dyes can be used as fusing agents for ultraviolet radiation. The ability to use water-soluble acid yellow dyes as radiation absorbers in a fusing agent suggests minimal negative impacts and interference with mechanical properties. The examples further demonstrate reliable printability of fusing agents with water-soluble acid yellow dyes as radiation absorbers with respect to both decap and nozzle health. The ability to print without inorganic pigments can enable access to wide-ranging color spaces. The use of water-soluble acid yellow dyes may enable use of elastomeric materials in the polymeric build material of the three-dimensional printing.