BACKGROUND OF THE INVENTION Clothing made from cellulosic fabrics such as cotton, linen, hemp, ramie, cupro, lyocell, newcell, rayon, polynosics, are very popular. Of particular interest are clothing items such as jeans made from indigo-dyed denim fabrics made of cotton or cotton blends. Such clothing items are typically sewn from sized and cut cloth and tend to be stiff due to the presence of sizing compositions.

In other cases the fibers or rolls of fabric are treated with enzymes prior to sewing the final garment. After a period of wear, the clothing items can develop a certain degree of softness, an overall reduction of shade as well as localized areas of color variation. Additionally, after repeated washing the garment continues to provide a more comfortable fit, a softer feel and a worn appearance. In recent years such comfort, feel and appearance have become increasingly popular.

The most widespread methods for producing this comfort, feel and look involve washing of clothing items with cellulases in large washing machines with pumice stones or other abrasives. The pumice helps soften the fabric and helps to provide the faded surface similar to that produced by the extended wear of the fabric. However, the use of pumice has some disadvantages. For example, the pumice must be manually removed from processed clothing items because it tends to accumulate in pockets, on interior surfaces, in creases, and in folds. Also, the pumice stones can cause overload damage to electric motors of stone washing

machines, and clog machine drainage passages and drain lines. These processing and equipment problems can add significantly to the cost of doing business and to the purchase price of the goods.

In view of the problems of using pumice, alternative methods to using pumice or other abrasives in the stone washing process have been sought.

One alternative involves the use of enzyme treatments which break down the cellulose in fabrics (Geller US Patent No. 4,951,366; Olson US Patent's Nos.

4,832,864,4,912,056, Olson et al. Patent Nos. 5,006,126,5,122,159 and 5,213,581, Christner et al. U. S. Patent No. 4,943,530, Boegh et al. U. S. Patent No. 4,788,682). Methods for treating cellulose containing fabrics with hydrolytic enzymes, such as cellulases, are known in the art to improve the softness or feel of such fabrics (Novo Brochure Cellulase SP 227; Novo Brochure Celluzyme; Murata US Patent No. 4,443,355; Parslow US Patent No. 4,661,289; Tai US Patent No.

4,479,881; Barbesgaard US Patent No. 4,435,307; Browning UK Patent No.

1,368,599).

Cellulases are known in the art as enzyme systems that hydrolyze cellulose ( (3-1, 4-glucan linkages), thereby resulting in the formation of glucose, cellobiose, cellooligosaccharides, and the like. Cellulase compositions are comprised of several different enzyme components, including those identified as exocellobiohydrolases, endoglucanases, and ß-glucosidases. Moreover, these classes of enzymes can be further separated into individual isoenzymes.

The complete cellulase system is required to efficiently convert crystalline cellulose to glucose. Generally, if total hydrolysis of a cellulose substrate is needed, the cellulase mixture should contain ß-glucosidases and cellobiohydrolases, as well as endoglucanases. Endoglucanases catalyze random hydrolysis ouf 6-1, 4-glycosidic bonds between glucose units of cellulose polymers.

Such components hydrolyze soluble cellulose derivatives such as carboxymethylcellulose, thereby reducing the viscosity of such solutions. Such enzyme components act on internal regions of the polymer, resulting in a rapid decrease in average polymer chain length together with a slow increase in the

number of reducing ends. The rapid decrease in average chain length of the cellulose polymer is evidenced by the decrease in viscosity of a cellulose solution.

The substrate specificity and mode of action of the different cellulases varies among strains of organisms that produce cellulases. For example, the currently accepted mechanism of cellulase action in cellulase from the fungus Trichodenna reesei is that endoglucanase activity first break internal/3-1, 4- glucosidic bonds in regions of low crystallinity of the cellulose (Ruohnen L., et al.

In:"Proceedings of the Second Tricel Symposium on Trichoderma Reesei Cellulases and Other Hydrolases", (ed. by P. Sudminen and T. Reinkainen.,) Foundation for Biotechnology and Industrial Fermentation Research 8; (1993): 87- 96) The cellobiohydrolase activity binds preferentially to the crystalline regions of the non-reducing end of the cellulose to release cellobiose as the primary product.

ß-Glucosidase or cellobiase activities then act on cellooligosaccharides, e. g., cellobiose, to give glucose as the sole product.

Cellulases are produced in fungi, bacteria, and other microbes.

Fungi typically produce a complete cellulase system capable of degrading crystalline forms of cellulose. For example, Trichoderl11a reesei produces and secreates all of the enzyme activities needed for efficient breakdown of crystalline cellulose, namely endo-1, 4-ß-D-glucanases, cellobiohydrolases (exo-1, 4-ß-D- glucanases), and 1,4-ß-D-glucanases, or ß-glucosidases. Fungal cellulases have an added advantage in that cellulases in fungi can readily be produced in large quantities via fermentation procedures.

Cellulases, or the components thereof, are known in the art to be useful in a variety of industrial textile applications in addition to the stone washing process. For example, cellulases are used in detergent compositions, for the purpose of enhancing the cleaning ability of the composition, as a softening agent, for color brightening, depilling and other uses. When so used, the cellulase will degrade a portion of the cellulosic material, e. g., cotton fabric, in the wash, which facilitates the cleaning and/or softening of the fabric. The endoglucanase components of fungal cellulases have also been used for the purposes of enhancing

the cleaning ability of detergent compositions, for use as a softening agent, and for use in improving the feel of cotton fabrics, and the like. However, there is a problem with using the cellulase derived from Trichoderona spp. and especially Trichodenna longibrachiatum in detergent compositions. Generally, such components have their highest activity at acid pHs whereas most laundry detergent compositions are formulated for use at neutral or alkaline conditions.

Other textile applications in which cellulases have been used include softening (Browning, UK Patent No. 1,368,599, Parslow, U. S. Patent No.

4,661,289, Tai U. S. Patent No. 4,479,881 and Barbesgaard, U. S. Patent No.

4,435,307), defibrillation (Gintis, D. Mead, E. J., Textile Research Journal, 29, 1959; Cooke, W. D., Journal Of The Textile Research Institute, 74,3,1983; Boegh, European Patent Application No. 0 220 016). Cellulases have also been used in combination with a polymer agent in a process for providing localized variation in the color density of fibers. (WO/94/19528 and WP/94/1529).

Cellulases are classified in the garment and textile industry according to their pH range of operation. Acid cellulases typically have their peak activity at pH values of about 4.0 to 5.5 and less, neutral cellulases at about pH 5.5 to 7.5, and alkaline cellulases at about pH 7.5 to 11.0. Some enzyme compositions may have broader ranges of operation. For example, the neutral/alkaline cellulases may operate at acid, neutral and alkaline pH's at between about 40°C to 60°C.

Acid, neutral and alkaline cellulases are typically used in the"stone wash"treatment of denim jeans, with or without surfactants, buffers, detergents, anti-redeposition agents, softening agents, pumice stones or other abrasives, bleaching agents, such as optical bleaching agents, enzymes, or other means.

If the cellulase composition is not formulated and/or pre-buffered then for acid cellulases, the pH is typically adjusted to between pH 4.5-5.5, with for example, a sodium citrate and citric acid buffer, and for neutral or alkaline cellulases between 5.5-7.5 with, for example, a monosodium and disodium phosphate buffer. Neutral and alkaline cellulases are typically used as additives to laundry

detergents where the pH of operation may range from about pH 7.0 to 11.5. In stone wash applications typical acid cellulases generally provide greater backstaining or redeposition of the indigo dye and greater strength loss of the fabric while the typical neutral and alkaline cellulases generally provide less abrasion, lower backstaining or redeposition and less strength loss of the fabric.

The neutral/alkaline cellulases are the most preferred type of cellulases for the stonewash industry because they cause lower levels of backstaining or redeposition and lower strength loss than acid cellulases (ie ; from Trichoderna sp.). Furthermore, neutral/alkaline cellulases, unlike their acid counterparts, operate at a much wider pH range and are able to maintain better relative wash performance within a wider pH range (pH 5.0-pH 8.0) in the stone washing industry. Therefore, neutral/alkaline cellulases provide several advantages. First, the incoming feed water in wet processing facilities is typically within this pH range lessening the need for as precise pH control as compared to acid cellulases. This makes the stonewashing process more tolerant to operator pH error or neglect leaving the overall procedure more forgiving than procedures using acid cellulases. Secondly, it is known that denim fabrics are alkaline in nature owing to the fact that the dyeing process utilities caustic soda. Simply washing denim releases this caustic into the wash water and the pH of the wash water generally rises. The alkalinity may overcome the bath buffers, but the effect of increased pH is less severe on neutral/alkaline cellulases compared to acid cellulases because neutral/alkaline cellulases operate not only at higher pH, but also over a wider pH range.

The wide spectrum of industrial uses for cellulases or the components of cellulases, especially alkaline and/or neutral cellulases, establishes a clear need for cellulases that are operative at neutral and/or alkaline pH. The present invention provides a procedure for producing neutral/alkaline cellulases having enzymatic activity at neutral and/or alkaline pH's and compositions comprising the same.

SUMMARY OF THE INVENTION This invention relates, in general, to neutral and/or alkaline cellulases and novel methods for producing the same. More specifically, the subject invention provides a method for producing cellulase compositions from fungi of the genus Chrysosporium, and particular Chtysosporiun7 lucknowense, wherein the cellulase compositions have enzymatic activity at neutral and/or alkaline pH's. Industrial applications for the cellulase composition are also provided.

One embodiment of this invention relates to isolated and purified cultures of wild type and mutant fungi of the genus Chrysosporiul17 capable of producing neutral and/or alkaline cellulase compositions, in particular to the strain Chrysosporium lucknowense - GARG 27K and mutants thereof.

Yet another embodiment of this invention provides culturing conditions for producing neutral or alkaline cellulases from fungi of the genus Chrysosporium.

In a further embodiment, this invention provides methods to producing a neutral and/or alkaline cellulase composition through recombinant technology from fungi of the genus Chrysosporiun7.

In yet a further embodiment of this invention methods for generating and culturing mutant strains of the fungi Chrysosporium capable of producing neutral and/or alkaline cellulase are provided.

Another embodiment of this invention relates to the nucleic acid sequences encoding the enzymes of the cellulases compositions produced by Chrysosporium or genetically modified strains of Chrysosporium.

Another embodiment relates to the purified and isolated enzymes of the cellulase compositions produced by Chrysosporiu/11 or genetically modified strains of Chrysosporium.

In yet another embodiment of this invention methods of use are provided for alkaline and/or neutral cellulases produced by Chrysosporium in textile applications, such as softening, bleaching and stone washing procedures,

garment dyeing applications, defibrillation, or biopolishing, color brightening and depilling.

Another embodiment of this invention relates to detergent compositions comprising Chrysosporiun7 cellulase in detergent preparations.

Another embodiment of this invention is to provide methods of use for the cellulase compositions in the saccharification of lignocellulose biomass from agriculture, forest products, municipal solid waste, and other sources.

Yet other embodiments of this invention involve the use of the cellulase compositions for production of fuels and other chemicals for the biobleaching of wood pulp, and for de-inking of recycled print paper.

Detailed Disclosure of the Invention As utilized herein, reference to a"neutral-alkaline cellulase"refers to a cellulase composition which retains significant enzymatic activity at pH values of about 5.5 and above. In a preferred embodiment, the neutral and/or alkaline cellulase compositions of the subject invention have peak enzymatic activity between about pH 5.5 to about 7.5 at 40°C to about 60°C. In the event that the peak enzymatic activity is at a pH of less than about 5.5, the neutral-alkaline cellulase composition will have at least about 50% of the optimal enzymatic activity at about pH 6.0 to about 7.0 at about 40oC to about 60oC. By way of example such activities may be measured by RBBCMCase, CMCase, Cellazyme, endoviscometric or filter paper activity (FPA). Thus, the cellulase compositions of the subject invention will have useful enzymatic activity at pHs greater than 5.5 such that the enzyme composition can be used in stone wash, detergent, de-inking or other applications where neutral and/or alkaline cellulase activity is needed.

The subject invention relates to compositions of cellulases having high activity at neutral or alkaline pH's and to unique methods for producing said neutral and alkaline cellulase compositions. The neutral/alkaline cellulase compositions of this invention may be obtained from any species of Chrysosporiul17. In a particularly preferred embodiment, the cellulase

compositions of the present invention are isolated from Chrysosporium lucknowense Garg 27K (designated isolate Cl) deposited under the Budapest Treaty with the International Depository at the All-Russian Collection of Microorganisms of the Russian Academy of Sciences, Bakhrushina St. 8: Moscow, Russia 113184, on August 29,1996, and assigned accession number VKM F- 3500D. The cellulase compositions of the subject invention are highly advantageous because they possess enzymatic activity at neutral and/or alkaline pH thereby providing beneficial performance characteristics in industrial applications.

The cellulase compositions prepared from fungal strains of the subject invention exhibit activity at between about pH 5.0 to about 12.0 at between about 40° to 60°C as determined by a CMCase, RBBCMCase, Cellazyme, endoviscometric or Filter Paper Activity (FPA) assays. In a preferred embodiment for a stone wash procedure, the cellulase composition may have optimal activity at between about pH 5.5 to 7.0 at about 40°C to about 60°C. Good performance activity at neutral and alkaline pH (ie: 6.0,7.0 & 8.0) has been demonstrated for the neutral and/or alkaline cellulases of the instant invention in Stonewash application trials and at pH 10.0 and above for detergent application trials.

The fermentation procedures for culturing cellulolytic microorganisms for production of cellulase are known in the art. For example, cellulase systems can be produced either by solid or submerged culture, including solid state, batch, fed-batch, and continuous-flow processes. The collection and purification of the cellulase systems from the fermentation broth can also be effected by procedures known in the art. The cellulase composition is readily isolated from the fungal culture by, for example, centrifugation or filtration steps and concentration of the filtrate via membrane or hollow fibers ultrafiltration equipment.

The fungal strain Chrysosporiu7n used to produce the cellulase compositions of the subject invention can be cultured according to standard methods and conditions known in the art. In a preferred embodiment, the cellulase composition of the subject invention is obtained from the Cl strain. The Cl

C11rysosporium strain may be grown in a medium containing inorganic salts, organic nitrogen sources, such as peptones, defatted cotton seed flour, corn steep liquor, or yeast extract and carbon source. Examples of carbon source include, but is not limited to, glucose, lactose, sucrose, cellulose or other carbohydrates.

More preferably, the fungal strain is grown in media containing both lactose and peptone or lactose and yeast extract. By way of example the fermentation media can compose lactose at about 0.3% to about 1.0%, preferably about 0.5% to about 0.6%, peptone at about 0.3% to about 1.0%, preferably about 0.5% to about 0.6%. Other nitrogen sources and carbohydrate sources known in the art may be used in the fungal growth media including, but not limited to, sweet beet pulp, barley malt, wheat bran, and others known in the art. By way of example sweet beet pulp concentrate may be used in a range of about 15 to about 30 grams/liter (g/L), preferably about 20 to about 25 g/L; barley malt may be used in a range about 10 g/L to about 20g/L, preferably about 14 g/L or about 16g/L, wheat bean may be used in a range about 3g/L to about 8g/L, preferably about 5g/L to about 6 g/L. In one embodiment, the Cl strain is cultured in rotated shake flasks in saline medium containing sweet beet pulp, barley malt, and wheat bran. Cellulase compositions may be isolated from fungi cultured about 3 to 7 days in a growth medium by centrifugation and ultrafiltration concentration of the cell culture medium.

Alternatively the Chrysosporium cultures can be cultured on a large scale for commercial use, by using conventional fermentation techniques. In this context fermentation is used broadly to refer to any controlled fungal culturing conditions. Prior to large scale growth an inoculum of said growth culture is generally cultured. The inoculum media may contain conventional ingredients including, but not limited to, carbon sources, organic nitrogen sources, and inorganic salts. Carbon sources may include, but are not limited to, glucose, lactose, glycerol, and/or cellulose at concentrations in the range of about 0.5 to 200 g/L, more preferably in the range of about 5 to 50 g/L. Organic nitrogen sources may include, but are not limited to, yeast extract, peptone, or defatted

cotton seed flour at concentrations in the range of about 0.5 to 30 g/L, more preferably in the range of 5 to 15 g/L. Inorganic salts may include, but are not limited to, potassium phosphate, for example at about 0.01 to about 10 g/L, magnesium sulfate, for example at about 0.01 to 3.0 g/L, ferrous sulfate, for example at about 0.001 to 10 mg/L.

An inoculum or starter culture may be used to initiate the Chrysosporium culture for a fermenter by methods known in the art. The media used for fermentation may comprise conventional ingredients for culturing fungi, including but not limited to, cellulose, organic nitrogen sources, magnesium chloride and calcium chloride. Examples of organic nitrogen sources include, but are not limited to, peptone or defatted cotton seed flour, such as Pharmamedia.

By way of example, the media may comprise about 5g/l to about 20 g/L of peptone or defatted cotton seed flour, about lOg/L to about 30g/L of cellulose, about 0.03 g/L to about 0.06 g/L of magnesium sulfate heptahydrate and about 0.4 g/L to about 0.8 g/L of calcium chloride dihyrate.

One of skill in the art will appreciate that during fermentation the temperature, oxygenation, pH, and nutrient levels of fermentation mixture should be maintained. By way of example, dissolved oxygen levels should be maintained at about 10 to 60% of air saturation, preferably at about 20 to 40% of air saturation. The pH should be maintained between about 5 and 8, preferably between about 6.5 and 7.5, most preferably between 6.9 and 7.1 and the temperature may be maintained at between about 25°C to about 40°C, preferably at about 28°C to 35°C. The feed solution may comprise ingredients similar to the fermentation media but at higher concentrations to minimize dilution when added to the fermentation media.

The cellulase compositions produced according to the methods of the subject invention are useful for a variety of other applications for which cellulase activity, in particular neutral and/or alkaline cellulase activity, is needed. In one embodiment of this invention, the neutral and/or alkaline cellulase compositions can be used in stone washing procedures for denim jeans. By way of example, the

most preferred pH range of stone wash applications is between about 5.5 to 7.5, most preferably at about pH 6 to about 7. The neutral and/or alkaline cellulase composition obtained from Chrysosporiuna isolates advantageously have significant enzymatic activity at or above neutral or alkaline pH. Stone wash procedures conducted with neutral and/or alkaline cellulase run at neutral and/or alkaline pH's are particularly advantageous compared to traditional procedures using acid cellulases (eg: those from Trichoderma reesei) because of lower levels of backstaining on the garments, less strength loss to the garments and the alkalinity of the water that is present naturally during this process. These stone washing procedures result in jeans with highly desirable feel and appearance. By way of example, 0.02 to lOg of cellulase preparation 47.0528 described herein, may be used per 135g of denim. One of skill in the art will know how to regulate the amount or concentration of the cellulase composition produced by this invention based on such factors as the activity of the cellulase, and the wash conditions, including but not limited to temperature and pH.

In yet another embodiment of this invention, the cellulase compositions of this invention can be used to reduce or eliminate the harshness associated with fabrics made from cellulose by addition to detergent compositions.

By way of example, the preferred range for detergent compositions is between about pH 8 to about 12, most preferably pH 10 to about 11. The cellulase compositions of the subject invention can be used in detergent compositions at neutral and or alkaline pH. Detergent ingredients contemplated for use with the cellulase composition of the subject invention include any detergent ingredient known in the art. Examples of such ingredients include, but are not limited to, detergents, buffers, surfactants, bleaching agents, softeners, solvents, solid forming agents, abrasives, alkalis, inorganic electrolytes, cellulase activators, antioxidants, builders, silicates, preservatives, and stabilizers, and are known in the art. The detergent compositions of this invention preferably employ a surface active agent, i. e., surfactant, including anionic, non-ionic, and ampholytic surfactants well known for their use in detergent compositions. In addition to the

cellulase components and the surface active agent, the detergent compositions of this invention can additionally contain one or more of the following components; the enzymes amylases, cellulases, proteinase, lipases, oxido-reductases, peroxidases and other enzymes; cationic surfactants and long-chain fatty acids; builders; antiredeposition agents; bleaching agents; bluing agents and fluorescent dyes; caking inhibitors; masking agents for factors inhibiting the cellulase activity; cellulase activators; antioxidants; and solubilizers. In addition, perfumes, preservatives, dyes, and the like can be used, if desired, with the detergent compositions of this invention. Examples of detergent compositions employing cellulases are exemplified in Patent No's 4,435,307; 4,443,355; 4,661,289; 4,479,881; 5,120,463, which are herein incorporated by reference.

When a detergent base used in the present invention is in the form of a powder, it may be one which is prepared by any known preparation method including a spray-drying method and/or a granulation method. The granulation method are the most preferred because of the non-dusting nature of granules compared to spray dry products. The detergent base obtained by the spray-drying method is hollow granules which are obtained by spraying an aqueous slurry of heat-resistant ingredients, such as surface active agents and builders, into a hot space. The granules have a size of from about 50 to about 2000 micrometers.

After the spray-drying, perfumes, enzymes, bleaching agents, and/or inorganic alkaline builders may be added. With a highly dense, granular detergent base obtained by such as the spray-drying-granulation method, various ingredients may also be added after the preparation of the base. When the detergent base is a liquid, it may be either a homogenous solution or an inhomogeneous solution.

The cellulase compositions of this invention preferably exhibit high levels of activity at alkaline or neutral pH's, but also may exhibit enzymatic activity at acidic pH's. Therefore, the detergent compositions comprising the cellulases of the present invention can be used in a broad pH range of from acidic to alkaline pH.

Other textile applications in which these cellulase compositions may

be used include, but are not limited to, Garment Dyeing applications including but not limited to Enzymatic Mercerizing of viscose, Bio-Polishing applications, Enzymatic Surface Polishing; Biowash (washing or washing down treatment of textile materials), Enzymatic Microfibrillation, Enzymatic"cottonization"of linen, ramie and hemp; and treatment of Lyocel or Newcell (ie;"TENCEL"from Courtauld's), Cupro and other cellulosic fibers or garments, dye removal from dyed cellulosic substrates such as dyed cotton (Leisola & Linko- (1976) Analytical Biochemistry, v. 70, p. 592. Deternaination Of The Solubilizing Activity Of A Cellulase Co) 11plex Wilh Dye (l Substrates ; Blum & Stahl-Enzymic Degradation Of Cellulose Fibers; Reports of the Shizuoka Prefectural Hamamatsu Textile Industrial Research Institute No. 24 (1985)), as a bleaching agent to make new indigo dyed denim look old (Fujikawa-Japanese Patent Application Kokai No.

50-132269), to enhance the bleaching action of bleaching agents (Suzuki-Great Britain Patent No. 2 094 826), and in a process for compositions for enzymatic desizing and bleaching of textiles (Windbichtler et al., U. S. Patent No. 2,974,001.

Another example of enzymatic desizing using cellulases is provided in Bhatawadekar (May 1983) Journal of the Textile Association, pages 83-86.

In other industrial embodiments, the cellulase compositions can be used in the saccharification of lignocellulose biomass from agriculture, forest products, municipal solid waste, and other sources, for the production of fuels and other chemicals through fermentation, for biobleaching of wood pulp, and for de- inking of recycled print paper all by methods known to one skilled in the art.

In yet another embodiment of the subject invention, various components of the neutral and alkaline cellulase compositions can be isolated and used independently of each other. Specific components or cellulase composition enriched by certain cellulase components can be produced or isolated by chemical and physical means from mutants or specifically produced by genetic engineering methods. The cellulase system can be purified into separate components by art- recognized separation techniques including ion exchange chromatography at a suitable pH, affinity chromatography, size exclusion, chromatography and like.

For example, in ion exchange chromatography, it is possible to separate the cellulase components by eluting with a pH gradient, or a salt gradient, or both.

Such separations can be done by those skilled in the art having the benefit of the teachings provided herein.

Once the individual enzymatic components of the cellulase composition are fractionalized and isolated the proteins may be partially sequenced or microsequenced to design synthetic DNA or probes to isolate the gene encoding the enzymatic proteins of interest. Generally the amino terminal sequence of the protein is determined by conventional protein sequencing methods or by automated sequence (Ausubel et al., (1987) in"Current Protocols in Molecular Biology", John Wiley and Sons, New York, New York). Alternatively, other regions of the protein may be sequenced in combination with chemical cleavage or enzymatic cleavage and protein separation techniques. (Ausubel et al., (1987) in"Current Protocols in Molecular Biology", John Wiley and Sons, New York, New York).

One of skill in the art will understand that the synthetic DNA clones or probes can be used in routine cloning techniques to isolate the genes corresponding to the enzymes present in the neutral/alkaline cellulase compositions produced by Chrysosporium.

It will be understood by one skilled in the art that nucleic and sequences obtained by this invention in the art may vary due to the degeneracy of the genetic code variations in the DNA sequence, but will still result in a DNA sequence capable of encoding the enzymatic components of the cellulase compositions. Such DNA sequences are therefore functionally equivalent to the nucleic acid sequences of the instant invention and are intended to be encompassed within the present invention. Also intended to be encompassed within this invention are nucleic acid sequences which are complementary to nucleic acid sequences capable of hybridizing to the disclosed nucleic acid sequence under a variety of conditions.

This invention further includes the protein or peptides or analogs thereof encoding the enzymes of the cellulase compositions of this invention and

those proteins or peptides having substantially the same function as the enzymatic proteins or peptides of this invention. Such proteins or polypeptides include, but are not limited to, a fragment of the protein, or a substitution, addition or deletion mutant. This invention also encompasses proteins or peptides that are substantially homologous to the proteins encoding the enzymes comprising the cellulase composition of this invention. The term"analog"includes any polypeptide having an amino acid residue sequence substantially identical to the sequence specifically in which one or more residues have been conservatively substituted with a functionally similar residue'and which displays the functional aspects of the proteins as described herein. Examples of conservative substitutions include the substitution of one non-polar (hydrophobic) residue such as isoleucine, valine, leucine or alanine for another, the substitution of one polar (hydrophilic) residue for another such as between arginine and lysine, between glutamine and asparagine, between threonine and serine, the substitution of one basic residue such as lysine, arginine or histidine for another, or the substitution of one acidic residue, such as aspartic acid or glutamic acid for another.

Proteins or polypeptides of the present invention also include any polypeptide having one or more additions and/or deletions or residues relative to the sequence of a polypeptide whose sequence is included in the proteins of this invention so long as the requisite activity is maintained.

This invention also provides a recombinant DNA molecule comprising all or part of the nucleic acid sequences isolated by this invention and a vector. Expression vectors suitable for use in the present invention comprise at least one expression control element operationally linked to the nucleic acid sequence. The expression control elements are inserted in the vector to control and regulate the expression of the nucleic acid sequence. Examples of expression control elements include, but are not limited to, lac system, operator and promoter regions of phage lambda, yeast or other fungi promoters. Examples of promoters that may be used include, but are not limited to, glucoamylase. Additional preferred or required operational elements include, but are not limited to, leader

sequence, termination codons, polyadenylation signals and any other sequences necessary or preferred for the appropriate transcription and subsequent translation of the nucleic acid sequence in the host system. It will be understood by one skilled in the art the correct combination of required or preferred expression control elements will depend on the host system chosen. It will further be understood that the expression vector should contain additional elements necessary for the transfer and subsequent replication of the expression vector containing the nucleic acid sequence in the host system. Examples of such elements include, but are not limited to, origins of replication and selectable markers. It will further be understood by one skilled in the art that such vectors are constructed using conventional methods (Ausubel et al., (1987) in"Current Protocols in Molecular Biology", John Wiley and Sons, New York, New York) or may be commercially available.

Another aspect of this invention relates to a host organism into which recombinant expression vector containing all or part of the nucleic acid sequence has been inserted. The host cells transformed with the nucleic acid sequence of this invention includes eukaryotes, such as animal, plants or seeds, insect and yeast cells, fungal cells, and prokaryotes, such as E. coli or other bacteria. Examples of fungal host cells include but are not limited to Aspergillus, Trichoderma, Humicola, Penicillium, or Neurospora. The means by which the vector carrying the gene may be introduced into the cell include, but are not limited to, transformation, microinjection, electroporation, transduction, or transfection using DEAE-dextran, lipofection, calcium phosphate or other procedures known to one skilled in the art (Sambrook et al. (1989) in"Molecular Cloning. A Laboratory Manual", Cold Spring Harbor Press, Plainview, New York). Alternatively, Chrysosporiul71 cells can be transformed with the nucleic acid sequence of this invention to amplify production of cellulases by Chrysosporium.

In a preferred embodiment, expression vectors that function in fungal cells are used. Examples of such vectors include, but are not limited to

plasmids, described in the patents (Ogawa ; Japanese patent JP5095787 A 930420, Ozeki; Japanese patent JP7115976 A 950509, Murakami; Japanese patent JP3094690 A 910419, Ishida; Japanese patent JP3251175 A 911108, Uozumi; Japanese patent JP5268953 A 931019 DW9346 C12N-009/34 Ollpp, Gottschalk; German patent DE3908813 A 900920 DW9039 000 pp, Gysler; European patent EP-683228 A2 951122 DW9551 C12n-015/60 Eng 041 pp). It is preferred that the recombinant protein expression vector is introduced into fungal cells, such to ensure proper processing and modification and modification of the introduced protein.

In a further embodiment, the recombinant protein expressed by the host cells can be obtained as a crude lysate or can be purified by standard protein purification procedures known in the art which may include differential precipitation, molecular sieve chromatography, ion-exchange chromatography, isoelectric focusing, gel electrophoresis, affinity, and immunoaffinity chromatography and the like. (Ausubel et. al., (1987) in"Current Protocols in Molecular Biology"John Wiley and Sons, New York, New York). In the case of immunoaffinity chromatography, the recombinant protein may be purified by passage through a column containing a resin which has bound thereto antibodies specific for the protein of interest (Ausubel et. al., (1987) in"Current Protocols in Molecular Biology"John Wiley and Sons, New York, New York).

All or parts of the nucleic acid sequences of this invention can also be used as probes to isolate other homologs in other genera or strains. In a preferred embodiment the nucleic acid sequences are used to screen a C/trysosporiu7n library; positive clones are selected and sequenced. Examples of sources from which the gene library can be synthesized include, but are not limited to species of Chzysosporium, Aspergillus, Penicillium, Humicola, CepS1alosporium Tricolerma or bacteria such as Bacillus. One skilled in the art will understand the appropriate hybridization conditions to be used to detect the homologs.

Conventional methods for nucleic acid hybridization, construction of libraries and cloning techniques are described in Sambrook et al., (eds) (1989) In"Molecular

Cloning A Laboratory Manual"Cold Spring Harbor Press, Plainview, New York and Ausubel et al., (eds) in"Current Protocols in Molecular Biology" (1987), John Wiley and Sons, New York, New York.

This invention also relates to mutant strains of Chrysosporium, in particular, mutant strains of Chrysosporium lucknowense capable of producing neutral and/or alkaline cellulases. Methods of DNA mutagenesis and screening for mutants are well known to these skilled in the art and include a variety of chemical and enzymatic methods. Examples of such methods include but are not limited to exposure of the fungi to ultraviolet light (UV), nitrous acid, N-methyl-N'-nitro-N- nitrosoguanidine (NG), and 4-nitroquinoline-N-oxide (4NQO). (Leninger (1972) Biochemistry, Worth Publishers Inc., NY; Jeffrey H. Miller (1972)"Experiments in Molecular Genetics. Cold Spring Harbor Laboratory, Cold Springs Harbor, New York). Preferred methods, include UV and NG. By way of example, mutant strains of Ch7ysosporium capable of producing increased levels cellulase compositions exhibiting enzymatic activity at neutral and or alkaline pH's may be generated by UV mutagenesis. By way of examples mutants may be produced by exposure of the fungal spores to UV light for a period of about 10 to about 180 seconds, preferably 45 to about 90 seconds, and most preferably 65 to 75 seconds.

Mutageneses involving NG may involve varying the concentration of the NG and exposure time. By way of example NG, at about 13 milligrams/liter (mg/L) to about 400mg/L of NG may be used for a period of exposure of about 15 minutes to about 120 minutes. Alternative methods for generating mutants include techniques in the field of molecular biology. Examples of such techniques include, but are not limited to, oligonucleotide directed mutagenesis, linker scanning mutations or oligonucleotide directed mutagenesis using polymerase chain reaction (Ausubel (1987) Current Protocols in Molecular Biology).

Screening and selection of mutant Chrysosporium clones exhibiting improved cellulase production can also be performed by conventional methodology. Examples of selection criteria for screening mutants includes, but is not limited, to the ability of the fungal colony to breakdown cellulase as evidenced

by cellulose clearing by the fungi grown on media plates containing cellulose and increased growth rate on media containing cellulose. By way of example, after mutagenesis the fungal sample may be plated on agar plates containing cellulose by conventional methodology. Colonies exhibiting increased growth and cellulose clearing (as is evidenced by clearing of the media surrounding the isolate) may be selected. However, any other assay for cellulose clearing may be used. Once a mutant is isolated the stock or spores derived from the mutant may be maintained by conventional methodology. The mutants isolated by this method may be cultured or fermented under the conditions described herein and above for the wild type strains of Chrysosporiuwn. The individual enzymatic components of the cellulase composition produced by the mutants may be partially sequenced or microsequenced to design synthetic to isolate the genes encoding the enzymatic proteins of interest. Thus, this invention relates to the nucleic acid sequences encoding the cellulase enzymes produced by the Chrysosporiun7 mutants and to the enzymes themselves. In yet another embodiment of this invention, the mutants isolated may be subjected to further mutagenisis and screened by the methods described herein above.

The present invention also relates to the production, isolation and purification of cellulase enzymes, having both endoglucanase and/or cellobiohydrolase activity from Chrysosporium organisms of any species and strain desired and wherein the purification methodology is not limited to the species of organism. Such purified, or partially purified, protein fractions and enzymes prepared therefrom are, in accordance with the present invention, highly useful in applications such as stone washing, color brightening, depilling and fabric softening, as well as other applications well known in the art. Such purified enzyme preparations are readily amenable to use as additives in detergent and other media used for such applications. These and other methods of use will readily suggest themselves to those of skill in the art and need no detailed description herein. However, description of typical methods of employing these preparations is provided in the examples that follow.

All books, patents or articles references herein are incorporated by reference. The following examples illustrate various aspects of the invention but in no way are included to limit the invention. All percentages are by weight and all solvent mixture proportions are by volume unless otherwise noted.

Materials and Methods Enzyme assays. The assay for CMCase, used carboxymethyl cellulose as the enzymatic substrate, measured the initial rate of hydrolysis, and quantified the amount of reducing sugars released according to the method of Somogyi and Nelson. The method is described in Methods in Enzymology, Vol.

160A, pp. 102-104. Endo-1, 4-ß-glucanase activity was assayed viscometrically as a rate of the decrease of viscosity of soluble substrate CMC according to Bioorganicheskaya Khimia, Vol. 6, pp. 1225-1242 (endoviscometric assay). Filter paper activity (FPA) or total cellulase activity used filter paper as the substrate and estimated the activity required to release 2 mg glucose from a 50-mg sample of filter paper. The assay is based on the Commission on Biotechnology (IUPAC) for the measurement for total cellulase activity or true cellulase and is described in Methods in Enzynaology, Vol. 160A, pp. 94-97. Avicelase activity was estimated as initial rate of reducing sugar formation during hydrolysis if Avicell-cellulose (as described in Bioresource Technology, Vol. 52, pp. 119-124). The assay of cellobiase used cellobiose as the substrate and measured the amount of glucose released (described in Methods in Enzymology, Vol. 160A, pp. 111-112). The assay of ß-glucosidase activity used p-nitrophenyl-ß-D-glucoside as the substrate (described in Methods in Enzynology, Vol. 160A, pp. 109-1100). The protein was determined by Lowry method (according to Journal of Biological Chemistry, Vol.

193, pp. 165-175). The assay of RBB-CMCase is based on determination of the dye release from soluble substrate RBB-CMC (CMC, dyed with Remazolbrilliant Blue), reference to assay-see Megazyme (Australia) Ltd., Product Information Bulletin, April, 1995. Endo-cellulase can also be measured using the Cellazyme assay with Azurine-crosslinked HE-cellulose as substrate (see Megazyme Product

Bulletin CEL, January, 1996).

Example 1-Isolation of C1 Strain The strain was isolated from samples of forest alkaline soil from Sola Lake, Far East of Russian Federation (Pacific Coast of Russia, about 5000 miles east from Moscow). A mixed soil sample was collected from 10 different sites. One gram of each sample was transferred into a flask with 100 ml sterile tap water and sonicated with an ultrasonic dispenser for 1 minute (0.44 Amp, 22 KHz). The suspension (diluted 1: 500) was inoculated into petri dishes with Czapek medium (pH 5.5-6.0) containing 100 mg/L streptomycin. The study was conducted in three replicates. Colonies of various color shape and size were identified for a second isolation step. Further isolation of the sample was performed on plates with Czapek media, malt agar, potato dextrose agar, or Getchinson saline medium pH 7.5 (Table 2). Plates were incubated at about 28°C for several days. Selection for cellulase producers was performed on cellulose agar plates which contained the components shown in Table 1. Preparation of amorphous cellulose is described in Methods in Enzyn7ology vol. 160A.

Table 1. Cellulose agar plates Ingredients g/L KH, PO, 1 KCl 0.1 MgSO,-7H, O 0. 3 NaCI 0.1 FeCl3 0.01 NaNO3 2.5 Amorphous cellulose 5 Agar 15 pH 7.5 The plates were incubated for 3-7 days at 28°C. The formation of light clearing halos around the colonies indicated cellulase activity. One strain, designated herein as Cl, that exhibited significant levels of cellulase activity was chosen for additional study. The strain was deposited at the All-Russian Collection of Microorganisms of Russian Academy of Sciences, (VKM), abbreviation in English-RCM), Bakhrushina St. 8: Moscow, Russia, 113184 under the Budapest Treat on August 29,1996, as Chrysosporium lucknowense Garg 27K, VKM-F 3500 D).

Example 2--Characterization of Cl Strain Growth of the Cl strain on potato dextrose agar gives colonies of 55-60 mm diameter after 7 days. Cl colonies exhibit a white-cream color, the surface is velvet-like and has a slightly raised center. The edge of the colonies is a flat, thin and fibereil. The back side of the colonies has a light cream color.

The mycelium has hyaline and is slightly branched and smooth.

The hyphae are thin-walled. Air hyphae are septate and form spores of 2.0-3.0 micrometers width; the substrate hyphae are sterile.

The conidia are terminal and lateral. No intercalary conidia were found. The majority of conidia are connected with hyphae through short stems or short side branches. The conidia are separated but adjacent. Conidia are hyaline, thin-walled, oval or clavate, and single cellular. Their size varies from 4 to 10 micrometers in diameter.

The Cl strain can be maintained on malt extract agar (at 4°C), and transferred each six months. Maintenance in liquid nitrogen and by lyophilization is also possible. The Cl strain is haploid, filamentous, can grow on agar plates with growth restricting agents like bovinebile (1.5 %), and produces spores.

Example 3--Classification of Cl Strain According to Sutton classification (Van Dorschot, C. A. N. [1980] "A revision of Clrysosporiunz and allied genera,"in Studies in Mycology, No. 20, Centraaddbureau voor Schimmelcultures, Baarn, The Netherlands, pp. 1-36), the Cl strain of the subject invention belongs to the order of Hyphomycetales, family of Moniliaceae, genus of Chrysosporium, species of Chrysosporium lucknowense Garg 1966. This classification was based on observation of the following characteristics of the Cl strain: 1. Signs of Hyphon7veetales order. Conidia are produced directly on mycelium, on separate sporogenous cells or on distinct conidiophores.

2. Signs of Moniliaceae family. Both conidia and conidiophores (if present) are hyaline or brightly colored; conidiophores are single or in loose clusters.

3. Signs of Chrsosnorium Corda 1833 genus. Colonies are usually spreading, white, sometimes cream-colored, pale brown or yellow, felty and/or powdery. Hyphae are mostly hyaline and smooth-walled, with irregular, more or less orthotopic branching. Fertile hyphae exhibit little or no differentiation.

Conidia are terminal and lateral, thallic, borne all over the hyphae, sessile or on short protrusions or side branches, subhyaline or pale yellow, thin-or thick- walled, subglobose, clavate, pyriform, orobovoid, 1-celled, rarely 2-celled, truncate. Intercalary conidia are sometimes present, are solitary, occasionally catenate, subhyaline or pale yellow, broader than the supporting hyphae, normally 1-celled, truncate at both ends. Chlamydospores are occasionally present.

4. Signs of Chrvsosporiun7 lucknowense Garg 1966 species.

Colonies attain 55 mm diameter on Sabouraud glucose agar in 14 days, are cream- colored, felty and fluffy; dense and 3-5 mm high; margins are defined, regular, and fimbriate ; reverse pale yellow to cream-colored. Hyphae are hyaline, smooth-and thin-walled, little branched. Aerial hyphae are mostly fertile and closely septate, about 1-3.5 mm wide. Submerged hyphae are infertile, about 1- 4.5 mm wide, with the thinner hyphae often being contorted. Conidia are terminal and lateral, mostly sessile or on short, frequently conical protrusions or short side branches. Conidia are solitary but in close proximity to one another, 1-4 conidia developing on one hyphal cell, subhyaline, fairly thin-and smooth-walled, mostly subglobose, also clavate orobovoid, 1-celled, 2.5-11 x 1.5-6 mm, with broad basal scars (1-2 mm). Intercalary conidia are absent. Chlamydospores are absent.

5. Description of Cl strain. Colonies grow to about 55-60 mm diameter in size on potato-dextrose agar in about 7 days; are white-cream-colored, felty, 2-3 mm high at the center; margins are defined, regular, fimbriate ; reverse pale, cream-colored. Hyphae are hyaline, smooth-and thin-walled, little branched. Aerial hyphae are fertile, septate, 2-3 mm wide. Submerged hyphae are infertile. Conidia are terminal and lateral; sessile or on short side branches; absent; solitary, but in close proximity to one another, hyaline, thin-and smooth- walled, subglobose, clavate or obovoid, 1-celled, 4-10 mm. Chlamydospores are absent. Intercalary conidia are absent.

Conclusion. Cl is a strain of Chrysosporiun lucknoovense Garg 1966. For convenience the cellulase made by this strain is referred to herein as "Cl"or"Cl cellulase."

Example 4--Assay for Cellulase Activity The Cl strain was grown in 800 ml shake flasks rotated at 220 rpm and incubated at 28°C. The Cl strain was grown in saline Getchinson medium (See Table 2) (pH 7.5) containing 5 g/L of various nutrients, and in some cases with 2 g/L microcrystalline cellulose. One hundred ml of media were added to each flask.

Table 2. Getchinson medium for shake flasks g/L KH, PO, 1 KCl 0.1 Mgso,-7H, 0. 3 NaCl 0.1 FeCl3 0.01 NaNO3 2.5 Combinations of glucose and microcrystalline cellulose, dextrose and microcrystalline cellulose, glycerol and microcrystalline cellulose, lactose and microcrystalline cellulose resulted in very low growth, formation of large aggregates of mycelium, and in the absence of cellulase activities (CMCase assay).

The results are presented in Table 3. Additions of nitrogen organic sources, i. e., peptone, corn steep liquor, or yeast extract enhanced growth and cellulase production and did not result in mycelium aggregates.

Lactose and yeast extract gave the highest cellulase production by Cl. Similar results were obtained when the lactose and yeast extract were substituted with 25 g/L sweet beet pulp, 15 g/L barley malt, and 5 g/L wheat bran.

Table 3. Effect of carbon and nitrogen sources on CMCase activity of C 1 (shake flasks results) Substrate CMCase activity (units/ml) at pH 7.0 Days 3 5 7 Glucose+ cellulose 0 0 0 Dextrose+ cellulose 0 0 0 Glycerol +cellulose 0 0 0 Lactose+ cellulose 0 0 0 Lactose+corn steep liquor 0 0 0.9 Lactose+peptone 10.7 7.4 14.8 Lactose+yeast extract 0 18.5 10.0 Cellulose+ peptone 0.3 1.2 1.6 Cellulose+corn steep liquor 1. 9 2.8 5.5 Example 5--Production of Cellulase for Stone Wash Tests 1. Production in shake flasks. Cl strain was grown in 800 ml shake flasks rotated at 220 rpm and incubated at 28°C for seven days. The growth medium 100 ml per flask was saline Getchinson medium (see Table 2) (pH 7.5) containing 25 g/L sweet beet pulp, 15 g/L barley malt, and 5 g/L wheat bran. The cell mass was separated by centrifugation and the cell-free supernatant was lyophilized and stored for further tests. C 1 cellulase preparation #s 47.1.1 to 47.15.1 were produced in this manner. Cl preparation # 47.16.1 was produced by the same manner, but cell-free supernatant after centrifugation was ultrafiltrated using a 10 kDa cutoff membrane before lyophilization. Cl preparation #'s

47.18.1 to 47.22.1 were produced by the same manner in shake flasks with Getchinson medium, but containing lactose (0.5 % w/v) and peptone (0.5 % w/v) instead of sweet beet pulp, barley malt and wheat bran. The cell mass was separated by centrifugation and the cell free supernatant was lyophilized and stored for further tests. Preparation #'s 47.1000,47.1001,47.2000 & 47.2001 were produced in shake flasks by the same manner as preparation #'s 47.1.1-47.15.1 except that they were produced using other Chrysosporiunz strains. Specifically, 47.2001 was produced by Chrysosporium pannorum, preparation 47.2000 was produced by Chrysosporium pruinosun1, preparation 47.1001 was produced by Chrysosporium keratinophilim and preparation 47.1000 was produced by Chtysosporiun1 quenslandicus71 (see Example 8). The protein content and activity fingerprints of these Cl preparations are shown in Table 4.

Table 4. Protein content and activity fingerprints of Cl preparations and preparation #'s 47.1000,47.1001,47.2000 & 47.2001 which were prepared from other species of Chrysosporiun7 sp.

Prepara-Protein, FPA, CMC-Endo Avice-, B-Glu- tion # % FPU/g ase, (visc), lase, U/g cosida- U/g U/g se, U/g 47.1.1 22 13 170 120 23 135 47.2.1 26 14 137 110 22 190 47.3.1 15 19 140 128 18 198 47.4.1 18 23 150 133 55 220 47.5.1 16 20 179 120.71 185 47.6.1 17 22 224 134 82 280 47.7.1 8 4 78 123 10 22 47.8.1 22 14 168 123 19 124 47.9.1 28 15 204 174 23 151 47.10.1 24 11 181 185 16 147 47.11.1 28 16 234 191 25 269 47.12.1 26 14 167 138 20 178 47.13.1 25 9 137 110 13 141 47.14.1 15 6 39 33 9 59 47.15.1 14 6 95 44 10 75 47.16.1 16 10 146 39 15 107 47.17.1 7 3 100 34 5 29 47.18.1 10 30 120 38 10 42 47.19.1 14 4 28 10 4 11 47.20.1 14 6 17 5 1 9 47.21.1 13 3 34 5 3 9 47.22.1 14 5 35 6 3 10 47.1000 18 4 31 35 6 89 47.1001 13 6 103 38 10 66 47.2000 10 3 78 31 7 67 47.2001 13 3 45 39 7 4 47.0325 50 155 4965 964 184 248 47.0528 67 111 13500 1782 232 423 2. Production in fermentors. Cl cellulase was produced in a 10-L "ANKUM-1M"fermentor with Getchinson medium, lactose (0.5% w/v), peptone (0.5% w/v), and chloramphenicol (50 mg/mL). Initial volume of the nutrition

medium was 7.0 L, final volume after fermentation was 7.3 L. The dissolved oxygen concentration (DO), agitation speed, aeration level, temperature, and pH were controlled. Fermentation was carried out as a batch-mode. The temperature of the fermentation was controlled at 28°C. The initial pH was 7.5 and was later maintained at that level by addition of NH40H (12% w/v). The aeration was at 4- 5 L/minute and agitation at 400-500 rpm. The DO was maintained at above 50%.

Samples (30 ml) were taken for analysis every 8 hours. At the end of fermentation, fungal biomass was separated by centrifugation (10, OOOg, room temperature, 20 minutes), and culture filtrate was lyophilized and stored for further tests. The results are shown in Table 5. Cellulase preparation # 47.17.1 was produced in this manner. Protein content and activity fingerprint of this Cl preparation is shown in Table 4.

Table 5. Production of Cl cellulase in 10-L fermentor Time (h) DO (%) Reducing sugars (g/L) CMCase (U/mL) 0 100 4.8 0 8 90 4,7 0 16 54 4.4 0 24 66 1.2 4 32 70 0.4 10 40 73 0.3 11.5 48 70 0.1 5 56 70 0 3. Production of Cl Preparation #'s 47.0325 and 47.0528. Cl cellulase preparation # 47.0325 was produced using the wild type Cl strain, preparation # 47.0528 was produced using an improved mutant obtained from the wild type Cl strain. These preparations were grown up fermentors under the conditions

described in Examples 13 and 15. Preparation 47.0325 was produced using a batch fermentation and 47.0528 was produced using a fed batch fermentation protocol.

4. Preparation of Humicola wild type preparation #'s 14.22.1 & 14.23.1 The wild type Humicola grisea var. thermoidea preparation # 14.22.1 was produced from the ATCC 16453 strain and the wild type Humicola insolens preparation # 14.23.1 was produced from the ATCC 16454 strain. These Humicola wild type preparations were produced in shake flasks using the same method as described above for (Production in shake flasks) of Cl preparation #'s 47.1.1-# 47.15.1.

Example 6--Comparison of Cl to Other Neutral Cellulases The FPA, CMCase and endoglucanase activities of Cl enzyme preparation &num 47. 0528 were compared to commercial Humicola insolens (Denimax XT) and to wild ATCC-type Humicola (preparation #'s 14.22.1 Huenicola grisea var. thermoidea (ATCC 16453) & 14.23.1 Humicola insolen (ATCC 16454) neutral cellulases. The results are given in the Table 6. The total activities of C-1 &num 47.0528 are clearly higher than those of neutral cellulases from wild type Humicola and from commercial Humicola insolen preparation. The specific CMCase and endoglucanase activities (as units per gram of dry preparation or units per gram of protein) of C-1 47.0528 are higher than those of all tested Humicola preparations listed in Table 6. The specific FPA of C-1 # 47.0528 is higher than the specific FPA of Humicola wild type preparations # 14.22.1 & 14.23 and slightly lower than the specific FPA of the Humicola insolen commercial product Denimax XT. The pH and thermal stability of Cl cellulase was similar to Denimax XT.

Table 6. Comparison of Cl and Huznicola cellulases.

Protei FPA CMCase Endo FPA CMCase Endo n % (visc) (visc) unit/1 gram of dry units/1 gram of preparation protein Cl (47.0528) 67 111 13,500 1782 165 20,115 2,655 Humicola sp. (&num 10 2 28 30 20 280 300 14.23.1) Humicola sp. (&num 10 1 11 19 10 110 190 14.23.1) Denimax XT 13 25 450 99 192 3,460 761 (commercial) (*) Activities were measured at pH 5.0 and 50°C Example 7--The effect of pH and temperature on activity and stability of Cl FPA and CMCase activities The FPA and CMCase activities of Cl exhibit optimal stability and activity at about pH 6-7 and about 50-60°C ; the pH optimum for CMCase activity is about 6.5, and the optimum temperature is about 55°C (see Tables 8,9). At pH 8.0 (50°C), CMCase possesses 80% activity, and FPA-78% activity, at pH 9.0 (50°C), CMCase possesses 65% activity, and FPA-52% activity (see Table 7.).

Table 7., the effect of pH on FPA and CMCase activities of Cl cellulase (#47. 19. 1) at 50°C pH (50°C) FPA (%) CMCase (%) 4.0 50 60 4.5 68 70 5.0 75 78 5.5 80 80 6.0 92 90 6.5 100 100 7.0 95 95 7.5 90 92 8.0 78 80 8.5 60 75 9.0 52 65 The incubation time for the FPA assay was 60 minutes, the incubation time for CMCase assay was 5 minutes.

Table 8. The effect of temperature on FPA and CMCase activities of Cl cellulase (&num 47. 19.1), at pH 7.0 Temperature (C) FPA (%) CMCase (%) 40 45 50 45 60 55 50 70 65 55 100 100 60 70 60 65 40 30 70 20 25 The incubation time for the FPA assay was 60 minutes, the incubation time for the CMCase assay was 5 minutes.

Table 9. Stability of CMCase of C1 cellulase (# 47.19.1) at 50 °C CMCase activity remained (%) <BR> <BR> <BR> <BR> Time (h)<BR> <BR> <BR> pH 5.1 pH 7.2 pH 7.7 pH 8.5 0 100 100 100 100 0.5 100 98 95 85 1 100 95 93 55 2 100 82 78 32 3 100 78 65 25 5 100 75 45 15

The CMCase of Cl exhibits high stability at optimal pH and temperature: For Example; at pH 7.2 and 50 °C CMCase possesses 95 % activity after 1 hour and 75 % activity after 5 hours, at pH 7.7 and 50 °C CMCase possesses 93 % activity after 1 hour and 45 % activity after 5 hours (See Table 9.).

Example 8--Neutral and or alkaline Cellulase activity/performance demonstrated in Other Strains of the Same Genera of Clrvsosporium Various strains of the Chrysosporiuna genus were tested for cellulase production. The full names and origins of these strains are described below.

Strains obtained from the American Type Culture Collection (ATCC), Rockville, Maryland, include: 1. ATCC 44006 Chrysosporium lucknoovense 2. ATCC 34151 Chrysosporiuna pannorum 3. ATCC 24782 Chrysosporium pruinosum Strains obtained from the Russian Collection of Microorganisms (VKM) include: 1. VKMF-2119 Chrysosporium keratinophilum 2. VKMF-2875 Chrysosporium keratinophilum 3. VKMF-2120 Chrysosporium lobatun 4. VKMF-2121 Chrysosporium merdarium 5. VKMF-2116 Chrysosporium guenslandicum 6. VKMF-2117 Chrysosporium guenslandicum 7. VKMF-2877 Chrysosporium tropicum Two types of growth media were used in this study: medium A- Getchinson with sugar beet press, barley malt, and wheat bran; and medium B- Getchinson with peptone and lactose. The compositions of the media are described in Table 11.

Table 11. Media for flasks studies Medium A L L Medium B gL K, HPO, 1 K. HPO, 1 KCl 0.1 KCl 0.1 MgSO,-7H, 0 0.3 MgSO4#7H2O 0. 3 NaCl 0.1 NaCI 0.1 FeCl3 0.01 Fed, 0.01 NaNO3 2.5 NaNO3 2.5 Sweet beet pulp 25 Lactose 5 Barley malt 15 Peptone 5 Wheat bran 5 pH 7.5 pH 7.5 The strains were grown in shake flasks at 220 rpm and at 28°C. Samples of each strain grown in Medium A were taken for analysis after 6 and 7 days of culture. Samples of strains grown in Medium B were taken after 5 days in culture. All samples were assayed for CMCase activity at pH 5 and 7. The results of the CMCase assay are shown in Table 12.

Table 12. Cellulase production by different strains of Chrysosporium Strains medium A medium A medium B (6 days) (7 days) (5 days) RS CMCase RS CMCase RS CMCase pH 5 pH 7 pH 5 pH 7 pH 5 pH 7 1 VKMF 2117 2.7 0 0.46 2.6 0.00 0.00 2.3 0.21 0.09 2. VKMF 2116 1.1 0.22 0.04 0.2 0.38 0.61 4.0 0.58 0.59 3. VKMF 2121 1.9 0 0.57 1.1 0.25 0.10 2.5 0.25 0.09 4. ATCC 24782 3.4 0.33 1.40 1.9 1.85 0.11 3.0 1.10 0.06 5. ATCC 34151 1.0 1.54 0.90 0.9 0.17 0.20 4.3 0.81 0.90 6. ATCC 44006 4.4 0.21 0.49 2.0 0.68 0.34 2.5 1.29 0.06 7. VKMF 2119 4.1 0 0.08 2.7 0.29 0.00 3.8 0.95 0.04 8. VKMF 2120 4.5 0 0.17 2.3 0.23 0.00 2.3 0.12 0.00 9. VKMF 2875 1.6 0 1.01 1.7 0.00 0.00 3.8 1.96 0.05 10. VKMF 2877 2.4 0 0.03 0.8 0.22 0.00 5.0 0.43 0.00 11. Cl (VKMF 2.9 1.70 1.65 nt nt nt 0.1 0.89 0.80 3500D) RS = concentration of reducing sugars in the fermentation medium at the end of fermentation, g/L (Nelson-Somogyi method). pH 5, pH 7 = the values of pH under which the CMCase activity of the fermentation broth was assayed.

CMCase activity in U/ml. nt = not tested In the cases of strains ATCC 34151 Chrysosporium pannorum, ATCC 24782 Chrysosporium pruinosum, VKMF-2875 Chrysosporium keratinophilum, VKMF 2116 Clrysosporium guenslandicum the cell mass was separated by centrifugation and cell free supernatant concentrated from 5 liters to 0.5 liter by ultrafiltration using 10 kDa cut-off membrane. Then the ultrafiltrated concentrate was lyophilized and stored for tests.

The following #-s of cellulase dry preparations were used: 47.2001-ATCC 34151 Chrysosporium pannorum, 47.2000-ATCC 24782 Chrysosporium pruinosum, 47.1001-VKMF-2875 Chrysosporium keratinophilum,

47.1000-VKMF 2116 Chrysosporium guenslaandicum.

Protein content and activity fingerprints of these preparations are given in Table 4.

Example 9--Stone Wash Tests A. Tests with 2-L special washing machine. This system assesses the stone wash performance characteristics related to abrasion and backstaining using only small amounts of enzyme.

Desizing. Forty pieces (30 g each, 25 x 20 cm) of denim fabric (roll) (1.2 kg) were desized in a household washer at 60°C for 20 minutes using a fabric: liquor ratio of 1: 6 (7.2 L) and 0.5 g/L (3.6 g) Sandoclean PC liquid (nonionic washing and wetting agent on base of ethyoxylated fatty alcohols with an average of 6 moles of ethylene oxide, 1 g/L (7.2 g) Sirrix 2UD (acidic buffered sequestration) and 1 g/L (7.2 g) Bactosol TK liquid (high temperature stable alpha- amylase) at a pH of about 5 to 6. After 20 minutes, the liquor was drained and the pieces washed for 5 minutes with cold water (14 L) liquid ratio 1: 10. The pieces were dried at 40°C and used as a stock of comparable samples for the determination of cellulase activity The cellulase treatment of the garment pieces was carried out in a washing machine consisting of an inner drum of 29 cm diameter drum-10. 6 1 total volume (drum rotates at 20 rpm-five turns left-five turns right). Each piece of fabric was sewn together with 4 rubber stoppers prior to the cellulase treatment to give a garment package that ensured that the mechanical effect occurred mainly on the darker outer side of the garment. Each drum was filled with one package and 10 additional rubber stoppers.

The general wash conditions were: 30 g desized denim jean fabric, cellulase in 0.02 M citrate buffer, 50°C, 60 minutes, garment: liquor ratio 1: 4.

After the cellulase treatment the package was washed with hot water (50 C) (garment: liquid ratio 1: 20) for 5 minutes and dried for evaluation.

Application trials were conducted using various Cl cellulase preparations

along with other cellulase preparations prepared from different species of Chrysosporium as well as the commercial Novo Nordisk neutral cellulase products, Denimax XT (US Patent # 4,435,307) and Ultra MG (WPO 91/17243). These application trials were set up to evaluate the stone wash performance characteristics of C-1 as well as several other species of Clirysosporiuin cellulases vs Novo's commercial neutral cellulases. The trials were run at neutral and alkaline pH's (6.5,6.7,7.0, and 8.0). The results are presented in Table 13.

Garments treated with various Cl and other Chrysosporiu) 77 cellulase preparations showed similar wash performance characteristics to those of the commercial neutral cellulases Denimax XT and Denimax Ultra MG. The C-1 and other Chrysosporium cellulase preparations showed good softening effect, bleaching/overall shade reduction, abrasion levels as well as low backstaining values when run under neutral and alkaline pH conditions.

Datacolor measurement is based on the degree of lightness of the sample (reflectance). The sample is exposed to white light (2 pulsed Xenon flash lamps) and the remission is detected between 400 and 700 nm with 16 diodes.

Reflectance from the front side, the higher value the more abrasion. Reflectance from the back side, the higher value the more backstaining.

Table 13., Enzyme Wash with Special 2 Liter Machine (135 grams of denim per run) Enzyme Amount %OWG CMCase Endo °C Liquo pH Time Buffe Dataco Dataco g (visc) r (min r lor lor ratio ) Abrasi Backst U/g /ru U/g /ru on ng n n C-1 1.995 1.5 234 474 191 381 50 1:11 7. 60 0.02M 13.1 1.8 47.11.1 Denimax XT 0.133 0.10 450 60 99 13 50 1:11 7. 60 0.02M 13.1 2.4 0 P C-1 2.100 1.5 167 338 138 290 50 1:11 6. 60 0.02M 14.2 1.8 47.12.1 7 P Denimax XT 0.420 0.30 450 182 99 42 50 1:11 6. 60 0.02M 14.0 2.3 6 P C-1 47.9.1 3.29 2.44 204 671 174 572 50 1:11 6. 60 0.02M 17.1 1.8 7 P C-1 2.3 1.7 146 336 39 90 50 1:11 6. 60 0.02M 16.2 2.3 47.16.lU 7 P 47/1000.1 7.0 5.19 48 336 14 98 50 1:11 6. 60 0.02M 12.9 2.1 5 P

Enzyme Amount %OWG CMCase Endo °C Liquo pH Time Buffe Dataco Dataco g (visc) r (min r lor lor ratio ) Abrasi Backst U/g /ru U/g /ru on ng n n 47/2001.1 7.15 5.30 47 336 20 143 50 1:11 6. 60 0.02M 14.7 1.7 5 P Denimax 0.132 0.10 134 18 243 32 50 1:11 7. 60 0.02M 14.1 3.5 UltraMG 3 P C-1 7.14 5.29 28 200 9 64 50 1:11 6. 60 0.02M 14.7 1.9 47.19.1 5 P C-1 0.068 0.05 4965 338 964 66 50 1:11 7. 60 0.02M 15.1 2.3 47.0325 0 P Denimax XT 1.0 0.74 450 450 99 99 50 1:11 6. 60 0.02M 19.1 2.8 5 P C-1 0.08 0.05 4800 384 178 143 50 1:11 6. 60 0.02M 18.5 3.0 47.0528 2 5 P C-1 0.136 0.10 4965 675 964 131 50 1:11 6. 60 0.02M 18.3 3.8 47.0325 0 P C-1 0.136 0.10 4965 675 964 131 50 1:11 7. 60 0.02M 18.9 3.2 47.0325 0 P Enzyme Amount %OWG CMCase Endo °C Liquo pH Time Buffe Dataco Dataco g (visc) r (min r lor lor ratio ) Abrasi Backst U/g /ru U/g /ru on ng n n C-1 0.136 0.10 4965 675 964 131 50 1:11 8. 60 0.02M 16.7 2.5 47.0325 0 P Humicola 9.18 6.8 28 257 30 275 50 1:11 6. 60 0.02M 14.9 1.3 14.22.1 7 P Humicola 9.18 6.80 11 101 19 174 50 1:11 6. 60 0.02M 12.5 1.5 14.23.1 7 P T. reesei 0.30 0.22 9190 273 200 600 50 1:11 4. 60 0.02c 17.5 8.0 cp 7 0 8 a Blank 0.00 0.00 0 0 50 1:11 6. 60 0.02M 9.1 n/a 0 0 5 P 0.02MP = Phosphate Buffer System<BR> 0.01CA = Citric Acid Buffer System<BR> T.reesei CP = Commercial acid cellulase product produced from Trichoderma reesei.<BR> <P>Datacolor Abrasion = reflectance from the front side, the higher the values, the<BR> more abrasion, blank = 9.1<BR> Datacolor Backstng = reflectance from the back side, the lower the values, the<BR> lower the back staining<BR> % 0WG = for example for 1% OWG, 1 lb of enzyme is used on 100 lbs of garment

B. Tests with 35 lb washing machine. Application Trials were run in a 35 lb washing machine (35 lb washing machine brand is Milnor-washer RPM is 30).

Load size is 2400 g (3 garments), garments used are Levi's 505 jeans. Water level for cellulase bath is 15 L for a liquor ratio of 6.25: 1 (low). The water level for all other baths is 24 L for a liquor ratio of 10: 1 (Med). The buffering system used is MAP-monoammonium phosphate and DAP-diammonium phosphate to maintain the pH of 6.7 during the cellulase bath. In Trials 4,5,6 & 7 a nonionic detergent was added to the cellulase bath, it is known that adding a detergent to the cellulase bath will help in reducing the backstaining on the garments. Zeke is a desizing product. SSCE is Superscour, a nonionic detergent (Zeke and Super Scour are commercial specialty textile chemical products offered by CPN International, Ltd., Inc of Jupiter, Florida). One Example of the Wash Formulas used in these trials is Trial 2. below; Wash Formula-Trial 2.

(C-147.0528)

Load (g) 2400 (3 gmts) Fabric: Denim Formula Time: 1 : 30 Machine : 35# Milnor Weight: 14.5 oz Developed by: Step Operation Time (min) Level Temp (F) Chemical Amount %OWG pH 1 Desize 10 Med 150 Zeke 48 g 2 2 Drain Balance 3 Rinse 2 Med 140 4 Drain Balance 5 Rinse 2 Med 130 6 Drain Balance 7 Abrasion 75 Low 125 MAP 29 g buffer 6.7 (15L) DAP log C-1 1.2 g 0.05 8 Drain Balance 9 Wash 10 Med 160 SSCE 24 g 1 10 Drain Balance 11 Rinse 3 Med 120 12 Drain Balance 13 Rinse 3 Med 100 14 Drain Balance 15 Rinse 3 Med 100 16 Drain Balance 17 Extract 2 In the example above, and in commercial use, one skilled in the art will appreciate that the use of pumice stones in the stonewash process will enhance the

overall stonewash effect on the garments.

The results in Table 14. show that the Cl cellulase preparations # 47.0325 and # 47.0528 performed better in terms of the overall level of abrasion achieved on the garments and well within the range of the backstaining level of the other commercial neutral cellulase products tested.

Table 14., Comparison of C-1 Cellulase Preparations 47.0325 & 47.0528 To Commercial Neutral Cellulases Denimax XT & BTU 202-318 (which contains Denimax XT) Trial Cellulase % OWG Wt (g) Detergent T (°F) pH t (min) 1 Denimax XT 0.50 12.0 no 130 6.7 75 2 C-1 47.0528 0.05 1.2 no 125 6.7 75 3 C-l 47. 0325 0.10 2.4 no 125 6.7 75 4 Denimax XT 0.50 12.0 yes 130 6.7 75 5 C-1 47. 0528 0.05 1.2 yes 125 6.7 75 6 C-1 47.0325 0.10 2.4 yes 125 6.7 75 7 BTU 202-318 2.50 60.0 yes 130 SB 75 ABRASION BACKSTAINING (Most to Least) (Least to Most) Trial 5 Trial 4 Trial 6 Trial 5 Trial 2 Trial 6 Trial 3 Trial 3 Trial 4 Trial 1 Trial 1 Trial 2 Trial 7 Trial 7 Figure Legand for Table 14 All of the trials in table 14. were cleaned up with Super Scour (nonionic detergent) at 1.0 % OWG, 160 F for 5 minutes. SB = Self

Buffered-the commercial product"ROCKSOFT"BTU 202-318 contains Denimax XT, detergent and a buffer system as well as other additives to help enhance the stone wash performance of this commercial product.

C. Tests with 60-L special washing machine. Whole denim garments were desized as described for the 2-L washing machine tests. Each wash test was made with 1 pair of jeans (700 g), 2.8 L liquid (fabric: liquid ratio 1: 4). All jeans were from the same dye lot. They were prewashed using an oxidation method for 15 minutes, then dried. Blue jeans washed at neutral pH with formulated Cl cellulase preparations 47.0325 using 2.4 grams per trial and 47.0528 using 1. 5 grams for one trial and using 1.0 gram for a second trial were compared directly against blue jeans washed under neutral pH conditions and similar formulations using Denimax XT at 12 grams per trial and two other commercial neutral cellulases; Bactosol JE using 2.0 % OWG and BTU 202-318 using 2.0 % OWG (Bactosol JE and BTU 202-318 contain Denimax XT, buffer, detergent as well as other additives to enhance their wash performance). Table 15. shows that the blue jeans from all three C-1 trials outperformed the three commercial neutral cellulase products in terms of the level of abrasion achieved as well as the overall color reduction of the garments. The level of backstaining on the blue jeans from all six trials was very good, they were very similar to one another and what one would expect and see when using Novo's neutral cellulase Denimax XT. The backstaining values for all three of these C-1 trials were within the range of the backstaining values as shown in Table 13. The finished garments from these trials and the trials as rated and shown in Table 14 above were rated in a blind study by four independent groups, of three or more people per group. The people that made up each of these groups are considered to be skilled in the art of stonewashing. They were asked to place each of the garments in the following order: (1) Greatest overall abrasion and color reduction to least overall abrasion and color reduction; and (2) Backstaining, lowest level of backstaining to highest level of backstaining (See Table 15).

Table 15 TRIAI, ENZYME DOSAGE BUFFER DETERGEN'IAAI3RASION/BACKSTAINING COLOR REDUCTION Trial A C-1 47.0528 1.5 grams Phosphate Yes ++++++ 5 Trial B C-1 47.0528 1. 0 grams Phosphate Yes..... 2 Trial C C-1 47.0325 2.4 grams Phosphate Yes +++++ 4 Trial D Denimax XT 12.0 grams Phosphate Yes ++++ 3 Trial E BTU 202-318 2.0% OWG Phosphate Yes +++ 6 Trial F Bactosol JE 2.0% OWG Citrate Yes +++ 1 Legend for Table 15: Abrasion/Color Reduction-+ + + + + + (+6) best (= > + + + + (4) is considered good and was comparable to commercial netural cellulases (e. g.- Denimax XT) Backstaining-The lower number the better (all jeans were judged to be within the range of backstaining as found when using Novo's Denimax TX). Neutral cellulase significantly decreased backstaining compared with traditional acid cellulases such as Trichoderma (see Example 13) % OWG-% Of Weight of Garment, for example for 100 lbs of jeans dryweight at 1 % OWG, 1 lb of enzyme is used.

D. Light reflectance. Another test to evaluate backstaining is to measure the light reflectance of a treated fabric. At the end of washing treatment, jeans samples were analyzed using a reflectometer at two different wavelengths: (1) the higher the signal detected at 680 nm (measured at the outside of the jeans), the lower the backstaining; and (2) the higher the signal detected at 420 nm (measured at the inside of the jeans), the lower the backstaining. Table 16. compares the reflectance values of denim jeans after treatment with commercial cellulases from Novo Nordisk and Genencor International to C-1 preparation # 47.6.1.

Table 16.

Enzyme 680 nm 420 nm Denimax L (neutral cellulase, Novo) 23 20 Primafast 100 (acid cellulase, Genencor) 20 13 C1 47. 6.1 (neutral/alkaline cellulase) 22 18 The light reflectance values for the Cl cellulase were similar to those obtained with Novo Nordisk's commercial product Denimax L, a neutral cellulase, at both 680 and 420 nm and the light reflectance values for Cl cellulase were significantly better than those obtained with Genecor's commercial product Primafast 100, a acid cellulase, at both 680 and 420 nm.

E. Tests in semi-industrial washing machine.

Test &num 1.

2 Jeans, weight 1343 gr Water ratio 6: 1 pH 5. 5 Temp. 54°C Enzyme: Cl (preparation &num 47. 6.1) 12 gr (0.9%) Abrasion time 90 minutes Drop bath Rinse 5 minutes with 1 % non-ionic detergent at 66°C Drop bath Rinse cold Drop bath Soften for 5 minutes with cationic softener at 49°C

Extract and dry.

Test #2. The same procedure as Test &num 1, above, except Denimax 700 T (2% OWG 28.9 gr) enzyme was used and wash conditions were conducted at pH 7.0,54°C.

Cl cellulase was compared to Denimax 700 T, a neutral cellulase commercial product made by Novo. All jeans were from the same dye lot. They were prewashed for 15 minutes using an oxidation method then dried.

The jeans treated with Cl cellulase preparation # 47.6.1 showed slightly less abrasion and lower backstaining than the jeans treated with Denimax 700T cellulase.

Example 10-Cl Cellulase as an Additive to Laundry Detergent A. Soil Release from Cotton Wash performance of Cl cellulase preparation # 47. 9.1 was tested using the wash-performance procedure PW 9406 (Solvay). Soil (ink) release from cotton fabric was tested by Delta Reflectance (%). Wash test compared a Cl cellulase preparation (# 47.9.1) to Celluzyme 0.7 T from Novo Nordisk in the presence and absence of alkaline protease Opticlean L500. The results of this test are shown in the Table 17.

Cl cellulase has soil release properties from ink soiled cotton at neutral pH in a color type detergent as the cellulase enzyme from Humicola insolens.

Table 17. Detergent wash test with C1 cellulase (*) Enzyme tested (pH 7.0) CMCase Reflectance Data (%) dosage (U/I) 1 2 Cellulzyme 0. 7 T 200 3.68 4.75 Celluzyme 0.7 T 500 2.68 4.07 Celluzyme 0. 7 T + 5000 DU/1 (**) 200 2.07 3.13 Celluzyme 0.7 T + 5000 DU/1 (**) 500 2.08 3.22 C1 # 47. 9.1 200 2.18 2.88 Cl&num 47. 9.1.500 2.77 3.72 Cl #47. 9.1 + 5000 DU/1 (**) 200 1.15 1.91 Cl #47. 9.1 + 5000 DU/1 (**) 500 2. 81 3.30 None (control) none 0 0 AADU = Du = Delft unit, Du/I = Defft unit per liter (*) 40C°, 45 min, drying at 68°C, 75 min (**) Alkaline protease Opticlean L500 B. The Stability of Cl Cellulase with Serine Proteases As serine proteases, a trypsin (3. 2 µM, from Bovine Pancreas, activity 10,000-13,000 N-benzyl-L-argine ethylester (BAEE)/mg, Sigma T-8253) and an a- chymotrypsin (8 µM, from Bovine Pancreas, 40-60 U/mg, Sigma C-4129) were used.

The proteases were incubated with Cl cellulase at 20°C and pH 7.0.

Chymotrypsin did not decrease Cl activity for 12 hours and trypsin led to a slight decrease (around 20%) of Cl activity, see Table 18.

Trypsin and chymotrypsin did not significantly change the stability of Cl CMCase at pH-s 4.5 and 7.0 at 50° and 57°C, see Table 18.

Table 18. The effect of proteases on CMCase activity of Cl cellulase (# 47.9.1) Protease Temperature pH Incubation CMCase activity (°C) time (h) remaining (%) None (control) 20 7.0 12 70 + Chymotrypsin 20 7.0 12 70 + Trypsin 20 7. 0 12 50 None (control) 50 4.5 3 100 + Chymotrypsin 50 4.5 3 100 + Trypsin 50 4.5 3 100 None (control) 50 7.0 3 78 + Chymotrypsin 50 7.0 3 60 + Trypsin 50 7. 0 3 68 None (control) 57 4.5 3 62 + Chymotrtrypsin 57 4.5 3 60 + Trypsin 57 4.5 3 62 None (control) 57 7.0 3 30 + Chymotrypsin 57 7.0 3 30 + Trypsin 57 7. 0 3 30 C. The Effect of Citrate EDTA. Tween-80 and Persulfate on CMCase activity Changing from acetate to citrate buffer (a chelating agent) did not effect the of Cl CMCase activity (molarity of buffers-0.1 M, pH 4.5,50 and 57°C), see Table 19.

EDTA (Ethylene Diamine Tetraacetic Acid) (5 mM) as a chelating agent at pH 4.5 and 50°C did not change CMCase activity. At pH 4.5 (57°C) and at pH 7.0 (50°C) EDTA caused slight decreases in CMCase activity. At pH 7.0 and 57°C, EDTA caused slight increase in CMCase activity, see Table 19.

Non-ionic detergent Tween-80 (3 g/L, polyoxyethylene sorbitane

monooleate), did not change CMCase activity of Cl (at pH-s 4.5 and 7.0 and at 50 and 57°C, see Table 19.

Oxidizing agent persulfate (3 g/L) did not change CMCase activity of Cl (at pH-s 4.5 and 7.0 and at 50 and 57°C), see Table 19.

Cl CMCase is resistant to serine proteases (trypsin and chymotrypsin), chelating agents (EDTA, citrate), non-ionic detergent (Tween-80) and to oxidizing agent (persulfate).

Table 19. The effect of citrate, EDTA, Tween-80 and persulfate on activity of Cl cellulasese (# 47.9.1). Incubation time-3 hours.

Effector Concentration Temperat pH CMCase activity ure (°C) remaining (%) None (control)---50 4.5 100 Citrate 0.1 M 50 4.5 100 EDTA 5 mM 50 4.5 100 Tween-80 3 g/L 50 4.5 100 Persulfate 3 g/L 50 4. 5 97 None (control)---57 4.5 62 Citrate 0. 1 M 57 4.5 65 EDTA 5 mM 57 4.5 60 Tween-80 3 g/L 57 4.5 68 Persulfate 3 g/L 57 4. 5 65 None (control)---50 7.0 78 EDTA 5 mM 50 7.0 50 Tween-80 3 g/L 50 7.0 52 Persulfate 3 g/L 50 7. 0 50 None (control)---57 7.0 30 EDTA 5 mM 57 7.0 38 Tween-80 3 g/L 57 7.0 25 Persulfate 3 g/L 57 7. 0 30 Example 11--Stone wash tests of cellulase samples produced by different strains of Chrvsosporium Preparations #-s 47.1000,47.1001,47.2000 and 47.2001 produced by different strains of C11rysosporiunl were used for wash test with 2-L special wash machine at pH 6.5,50°C, during 60 min with 135 g of desized denim jean fabric.

Total amount of CMCase activity per trial was constant and equal to 336 U/run.

After drying abrasion and backstaining of garment was evaluated by Datacolor measurement. The results are presented in Table 20. The results show that cellulases produced from different strains of Chrysosporian1 demonstrate similar wash performance at neutral pH in terms of abrasion and backstaining levels to the cellulases produced by the C-1 species Chrysosporiuz1w lucknowense Garg 1966.

Table 20. Stone wash activity of cellulase preparations from different strains of Chrysosporium Preparation # Abrasion (*) Backstaining (**) 47.1000 12.3 1.6 47.1001 12.1 1.6 47.2000 14.2 1.7 47.2001 14.6 1.6 (*)-reflectance from front side, the higher value the more abrasion, blank = 9.1 (**)-reflectance from back side, the higher value the more backstaining Example 12.--Purification of Cellulase Components 1. Selection of the C1 samples for purification. The Cl cellulase preparation #47. 11.1 was chosen for further purification in view of the fact that 47.11.1 possessed (i) high protein content; (ii) high FPA and CMCase activity (see Table 4).

2. Isolation and purification of Cl complex component. The first purification step included ion exchange chromatography on a DEAE-Toyopearl column (TosoHaas, Japan). Dry Cl cellulose preparation (1.5 g) was dissolved in 15 mL of 0.01 M Na-phosphate buffer, pH 7. The solution was centrifuged and the supernatant desalted using an Acrylex P-2 column. The desalted sample was then applied to the DEAE-Toyopearl column (1.5 x 30 cm) in 0.03 M phosphate buffer,

pH 4.7 and adsorbed proteins were eluted in 0-0. 2 M NaCI gradient with flow rate of 1 mL/min. Three pooled fractions were obtained--the non-bound (NB) fraction was eluted in the start buffer, Fractions I and II were eluted across a 0- 0.2 M NaCI gradient. All fractions possessed cellulolytic activities.

3. SDS-PAGE of protein fractions. After sodium dodecyl sulfate polyacrylamide gel electrophoresis (SDS-PAGE), the NB Fraction included proteins with molecular weights from 30 and 70 kD. Fraction I includes proteins with molecular weights from 25 to 100 kD and Fraction II contained proteins with molecular weights from 35 and 100 kD. SDS-PAGE was carried out with a 10% separating gel (100 X 80 X 0.75 mm) under denaturing conditions. Reagents and kits were obtained from Bio-Rad (USA). Coomassie brilliant blue R-250 in 25% trichloracetic acid was used for protein staining.

4. IEF of Protein Fractions. After isoelectric focusing (IEF), the NB Fraction includes proteins with isoelectric points (pI's) of from 4.6 to 8.0. Fraction I contains proteins with pI values from 3.2 to 5.5, and Fraction II conatins proteins with pI from 3.0 to 5.5. Isoelectic focusing was carried out with 7% PAAG in mini-IEF Model 111 (from Bio-Rad). Reagents and kits were obtained from Bio- Rad (USA). Coomassie brilliant blue R-250 in 25% trichloroacetic acid was used for protein staining.

5. pH-dependencies of CMCase activity of protein fractions. Table 21 represents the pH dependencies of CMCase and RBB-CMCase activities of Fractions NB, I and II of Cl cellulase. The following buffer systems were used: acetate buffer (pH 4-5), phosphate buffer (pH 6-8), and carbonate buffer (pH 8.5- 10). In addition, a universal buffer system was used which consisted of acetate, borate, and phosphate (pH 4-10).

Table 21. The effect of pH on CMCase and RBB-CMCase activities of Cl protein fractions CMCase activity, 50°C (%) pH NB Fraction Fraction I Fraction II 4.0 85 70 95 4.5 95 85 100 5.0 100 90 95 5.5 90 100 90 6.0 80 90 80 6.5 70 85 80 7.0 65 85 80 7.5 60 65 75 8.0 50 60 60 8.5 45 50 50 9.0 30 45 40 9.5 10 40 32 RBB-CMCase activity, 50°C (%) pH NB Fraction Fraction I Fraction II 4.5 65 95 100 5.0 100 100 95 5.5 95 100 90 6.0 95 95 90 6.5 80 87 90 7.0 80 85 87 7.5 60 65 85

8.0 50 60 70 8.5 45 60 60 9.0 30 50 40 9.5 10 40 32 CMCase and RBB-CMCase activities of the NB, I and II Fractions following DEAE-Toyopearl ion exchange chromatography had a non-symmetric bell-type pH profile. CMCase activity of the NB Fraction showed a maximum at pH 4.5-5.5 and 50% of maximal activity at pH 8.0. RBB-CMCase activity of the NB Fraction had a maximum at pH 5.0-6.0 and 50% of maximal activity at pH 8.0. CMCase activity of Fraction I had a maximum at pH 5.0-6.0 and 50% of maximal activity at pH 8.5. RBB-CMCase activity of Fraction I had a maximum at pH 4.5-7.0 and 50% of maximal activity at pH 8.5. CMCase activity of Fraction II had a maximum at pH 4.0-5.5 and 50% of maximal activity at pH 8.5. RBB- CMCase activity of Fraction II had a maximum at pH 4.5-7.5 and 50% of maximal activity at about pH 8.5.

6. Stability of CMCase of protein Fraction I (after DEAE-Toyopearl).

Table 22 shows temporal CMCase activity curves of Fraction I after DEAE- Toyopearl ion exchange chromatography at different pH (5.2-8.7) and 50°C.

CMCase activity of Fraction I was most stable at pH 5.2-7.2 (between about 30% and 45% of activity was lost over 3 hours). At pH 7.7,60% of activity was lost after about 1 hour, whereas at pH 8.3 and 8.7,50% of activity was lost after about 0.5 hour. At pH 8.3,100% of CMCase activity was lost after 3 hours, and at pH 8.7,100% of activity was lost after 2 hours.

Table 22. Stability of CMCase of a protein fraction I after DEAE-Toyopearl at 50°C CMCase activity remained (%) Time (h) pH 5.2 pH 7.2 pH 7.7 pH8.3 pH 8.7 0 100 100 100 100 100 0.5 97 75 65 50 50 1 90 55 40 25 15 2 40 50 35 10 0 3 30 45 25 0 0 7. Properties of Fractions after Ion Exchange Chromatography on DEAE- Toyopearl. Adsorption experiments using Avicel (micro crystalline cellulose) as a substrate demonstrated that fractions I and II did not bind to a crystalline substrate and the NB Fraction bound to Avicel with a distribution coefficient of 0.2 L/g.

Specific activities of the NB, I and II Fractions toward different substrates are presented in Table 23. All three fractions possessed CMCase, endoglucanase, avicelase, ß-glucanase and xylanase activities, but the NB Fraction had no B- glucosidase activity, contrary to Fractions I and II. The Micro Denim Wash test for Fractions NB, I and II showed that Fractions I and II possessed approximately equal activity on denim at pH 7 while the NB Fraction showed lower activity (according to the Micro Denim Wash test).

Table 23. Specific Activities of Fractions After Ion Exchange Chromatography on DEAE-Toyopearl Specific Activities, U/mg Protein Fractions CMCase Endoglu Avicelase B-gluco ß-gluc Xylan Micro Denim -canase-sidase-anase-ase Wash Test NB 9.9 6.2 0.18 0.0 11.0 5.3 + I 3.7 2.3 0.02 3.6 1.9 0.7 + + II 0.8 0.2 0.02 0.02 1.2 0.04 + + 8. Micro Denim Wash Test. This test was carried out using 20 mL of buffered enzyme solution having a preset level of CMCase activity. Real Indigo- denim stained swatches were treated at 50°C for 60 minutes in the conditions of excessive mechanical stress (abrasion). The level of cellulase performance was evaluated by panel score according to the color reduction after the samples were dried. Color measuring instruments and software could also be used. More"+" values indicate better abrasion.

9. Further Purification of Proteins from Fraction I After Ion Exchange Chromatography on DEAE-Toyopearl. Desalted Fraction I (25 mL, 0.8 g/1 of protein) was subjected to Macro Prep Q ion exchange chromatography. The MacroPrep Q column (1.5xlO cm) was equilibrated with 0.03 M acetate buffer, pH 4.7, and the adsorbed proteins eluted in 0-0. 1 M NaCI concentration gradient.

Three fractions, 1. 1,1.2, and 1. 3, were collected. Fraction 1. 2 showed the highest Micro Denim Washing activity at pH 7 and fraction 1. 3 showed the lowest. SDS- PAGE results showed that Fractions 1. 1 and 1. 2 differed by the presence of a low molecular weight protein (25 kD) in Fraction 1. 2, which might have accounted for the stonewashing activity. Fraction 1. 1 had a pI of 4.2 as shown by IEF

measurements. Fractions 1. 1 and 1. 3 had too low a protein content to permit further study. Therefore, Fraction 1. 2 was used in further purification.

The next purification step involved chromatofocusing on a Mono P column.

Fraction 1. 2 was equilibrated with 0.03 M imidazole buffer, pH 6.8, and applied to the column. Adsorbed proteins were eluted with Polybuffer 74 (1: 8), pH 4.0, whereupon 2 major peaks in protein and activity profiles were observed. The first peak, designated Peak A, showed lower specific CMCase activity (2.5 Units/mg) compared to Peak B (3.6 Units/mg). Native polyacrylamide gel electrophoresis showed the presence of 2 protein bands in Peak A, with the higher molecular weight protein band being active toward CMC stained with Congo Red. One active protein band under native conditions was observed in Peak B. SDS-PAGE data showed that Peak A included 2 major proteins (60 kD and 70 kD) and Peak B contained one major protein (25 kD) and one minor protein (27 kD). The fraction collected within Peak B was designated as 25 kD-endoC1 and was used in further studies. Table 24 shows the specific activities of 25 kD-endoCl toward different substrates. The 25 kD-endoC1 had CMCase, RBB-CMCase, endo-glucanase, FPA, avicelase, ß-glucanase, and xylanase activities but did not show B-glucosidase activity. This combination of different activities shows that 25 kD-endoC1 is an endoglucanase. The pH optimum of CMCase and RBB-CMCase activities is approximately 6.0 (Table 24). The 25 kD-endoC1 possessed high stonewashing activity (according to a Micro Denim Wash test using cotton swatches) (see Table 24).

During elution of Peak A from the Mono P column a number of fractions were recovered that differed in the ratio of 60 kD to 70 kD proteins, especially a fraction designated 70 (60) kD-C1 that included predominantly a 60 kD protein and a fraction designated 70 kD-endoCl with predominantly a 70 kD protein. Specific activities of these fractions toward different substrates are presented in Table 24.

As is seen therein, the 70 (60) kD-C1 fraction possessed low specific endoglucanase (0.5 U/mg) and a high specific avicelase (0.31 U/mg) activities compared to the 70 kD-endoC1 fraction (2.8 U/mg endoglucanase and 0.18 U/mg avicelase) and had

very low B-glucosidase activity. Specific activities toward FP, B-glucan, and xylan of the 70 (60) kD-C1 fraction were low (see Table 24) and only cellobiose was formed as a product of avicel hydrolysis. Stonewashing activity (according to a Micro Denim Wash test using cotton swatches) of the 70 (60) kD-C1 fraction was low (see Table 24). These data show that the 60 kD protein from Fraction I after ion exchange chromatography on DEAE-Toyopearl can be designated as a cellobiohydrolase. The pH optimum of 70 (60) kD-Cl (toward CMC and RBB- CMC) was approximately 5.0 (Table 24).

The 70kD-endoCl had high specific CMCase, RBB-CMCase, endoglucanase, FPA, B-glucanase and xylanase activities and possessed some avicelase and ß-glucosidase activity (Table 24). The 70kD-endoCl also possessed relatively high stonewashing activity (according to the Micro Denim Wash test using cotton swatches) (see Table 24). The 70kD-endoCl from fraction I after ion exchange chromatography on DEAE-Toyopearl appears to be an endoglucanase. As seen from Table 24, the pH optimum for 70 kD-endoC1 is approximately 6.0 for both the CMCase and RBB-CMCase activities.

10. Further Purification of Proteins from Fraction II after Ion Exchange Chromatography on DEAE-Toyopearl. Fraction II, obtained as a result of DEAE chromatography, was divided into 3 fractions (Fraction 11. 1,11.2, and 11. 3, respectively) using a longer 0-0.2 M NaCI gradient (over a period of 8 hr) on a DEAE-Toyopearl column. Results of SDS-PAGE showed that Fraction 11. 1 included 2 major proteins of molecular weight 60 kD and 100 kD, Fraction 11. 2 included 3 major proteins of 35 kD, 60 kD, and 100 kD, and Fraction 11. 3 included 2 major proteins of 43 kD and 60 kD. Fraction 11. 3 demonstrated the highest CMCase activity (10 units/mg of protein) but showed low washing activity (using a sub-Micro Denim Wash test) and specific CMCase activity of 1 unit/mg.

Fraction 11. 2 did not show any of the washing activity (but CMCase activity was 0.7 U/mg). Thus, Fractions 11. 1 and 11. 3 were purified further.

Table 24. Properties of Cl Enzymes pH 25 kD 70 (60) kD 70 kD 60 kD endo lOOkD 43kD endo 60kD endo endo endo (II. 1) (II. 1) (II. 3) (II. 3) CMCase Activity (U/mg) 5.0 4.6 1.10 3.5 0.70 0.03 1.02 1.32 6.0 5.0 0.83 3.8 0.52 0 1.01 1.07 7.0 3.9 0.65 3.0 0.45 0 0.90 1.03 RBB-CMCase (U/mg) 5.0 8.2 0.12 1.5 0.90 0 0.82 1.21 6.0 8.8 0.10 2.7 0.84 0 0.75 1.14 7.0 6.6 0.07 2.4 0.68 0 0.73 1.12 FPA (U/mg) 5.0 1.0 0.17 0.61 0.31 0 0.45 0.52 Endoglucanase (viscometric) (U/mg) 5.0 2.26 0.50 2.8 0.21 0 0.15 0.27 Avicelase (U/mg) 5.0 0.16 0.31 0.18 0.03 0 0.01 0.01 ß-Glucosidase (U/mg) 5.0 0 0.02 0.16 0.02 0 0.02 0

Table 24-cont'd B-Glucanase (U/mg) 5.0 0.66 0.07 2.4 1.3 0 3.9 4.4 Xylanase (U/mg) 5.0 0.40 0.16 0.50 0.06 0.01 0.07 0.01 Micro Denim Wash Activity 5.0 +++-++ n. d. n. d. n. d. n. d.

7.0 +++-++ n. d. n. d. n. d. n. d.

Sub-Micro Denim Wash Activity 5.0 n. d. n. d. n. d. +++-+ + 7.0 n. d. n. d. n. d. +++-+++ ++ n. d. = not determined 11. Sub-Micro Denim Wash Test. This test was performed on fragments of real Indigo-stained denim in 2 mL of buffered enzyme solution (2 units CMCase activity) at 50°C for 2 hours in the conditions of excessive mechanical stress. The level of cellulase performance was evaluated by panel score according to the color reduction after the samples were dried.

12. Purification of Fraction 11. 1. Fraction 11. 1 was applied to a Macro prep Q column equilibrated with 0.03 M acetate buffer, pH 4.75, and the adsorbed proteins were eluted in a NaCl gradient (0-0. 3 M). Two protein peaks were obtained but only the first one showed CMCase activity. SDS-PAGE of the material from the first peak showed that proteins with 60 kD and 100 kD were isolated in a homogeneous state. According to IEF data, the 60 kD and 100 kD

proteins possessed an acidic pI of about 3. The activities of the 60 kD and 100 kD proteins toward different substrates are shown in Table 24. The 60 kD protein designated as 60 kD (II. 1)-endo was found to possess endoglucanase, CMCase, RBB-CMCase, FPA and 8-glucanase activities at pH 5 (0.2,0.7,0.9,0.3, and 1.3 units/mg of protein, respectively, as shown in Table 24). Avicelase, B-glucosidase, and xylanase activities were rather low. This combination of activities shows that the 60kD (II. l)-endoCl is an endoglucanase. The 60kD (II. 1)-endoCl also possesses high washing activity (by the Sub-Micro Denim Wash test) both at pH 5 and at pH 7 (per Table 24). The pH dependence of CMCase and RBB-CMCase activities for this protein showed maxima at pH 4.0-4.5, with 50% of maximal activity toward CMC and 85% of maximal activity toward RBB-CMC retained at pH 6, and 15- 20% of both activities retained at pH 9 and 10 (see Table 25).

The 100 kD protein from Fraction 11. 1 was designated as lOOkD (II. 1) protein and almost did not have cellulase activity (Table 24). This protein possessed only very low CMCase (0.03 U/mg) and xylanase (0.008 U/mg) activities and could not be determined to be a cellulytic enzyme. According to the Sub-Micro Denim Wash test, the 100 kD (II. 1) protein did not demonstrate any stonewashing activity (Table 24) and also failed to show any protease activity at either pH 5 or pH 7.

13. Purification of Fraction 11. 3. Fraction 11. 3 was also purified by Macro Prep Q chromatography. The adsorbed proteins were eluted in 0.2-0.6 M NaCI gradient (the start buffer was 0.03 M acetate, pH 4.75). SDS-PAGE of the obtained fractions after the Macro Prep Q chromatography showed that the 43 kD and 60 kD proteins were obtained in homogeneous form. Isoelectrofocusing of these fractions showed that both the 43 kD and 60 kD proteins had pI values of about 3. The 43 kD and 60 kD proteins were designated 43kD (II. 3)-endo and 60kD (II. 3)-endo, respectively. The activities of these enzymes toward different substrates (see Table 24) showed that they had similar specific CMCase, FPA, avicelase, and xylanase activities. The 60kD (II. 3)-endo possessed higher specific

RBB-CMCase, endoglucanase and FPA activities (Table 24). At the same time it should be stressed that the 43kD (II. 3)-endo and 60kD (II. 3)-endo possessed very little stonewashing activities at pH 5 (using the Sub-Micro Denim Wash test).

However, both 43kD (II. 3)-endo and 60kD (II. 3)-endo demonstrated remarkable stonewashing activity at pH 7, and at the same time the 43kD (II. 3)- endoCl had higher stonewashing activity compared to the 60kD (II. 3)-endo. As seen from the pH dependencies in Table 25,43kD (II. 3)-endo showed a broad pH optimum (from pH 4.5 to 8) in the case of both CMCase and RBB-CMCase activities. The 43kD (II. 3)-endo possessed 50% CMCase and 70% RBB-CMCase activities from a maximum at pH 9 and 20% of both CMCase and RBB-CMCase at pH 10. In contrast, 60kD (II. 3)-endo had a narrow pH optimum at pH 4-4.5 toward CMC and a broad pH optimum (from pH 4 to 8) toward RBB-CMC and 30% RBB-CMCase activity being retained at pH 9.

It should be noted that in all cases of purified proteins disclosed herein, molecular weights were determined using gel electrophoresis (especially SDS- PAGE) and reference proteins of known molecular weight as standards. As with all analyses using such methods, the results are only approximate and some variation in molecular weight may be observed as different gels are run by different workers using different sets of molecular weight standards as references.

Such purified, and partially purified, enzyme preparations are highly useful as components of detergent, fabric softening, depilling, color brightening and stone washing compositions. Thus, the above isolated and purified enzyme preparations find utility in such applications according to the present invention. Thus, methods for stone washing, fabric softening, depilling, color brightening and cleansing as heretofore recited herein, as well as typical methods for accomplishing such applications as already disclosed in the literature will readily employ such purified, or partially purified, enzyme preparations, and compositions containing such, as main or additive agents in effecting the goals of such procedures. The use of other and different purified, or partially purified, enzyme preparations in such applications is known in the literature with many enzymes in commercial use.

Table 25. The Effect of pH on CMCase and RBB-CMCase activities of Cl Cellulase Enzymes CMCase Activity, 50°C (%) pH 60kD (II. 1)-endo 43kD (II. 3)-endo 60kD (II. 3)-endo 3.5 85 80 85 4.0 100 100 100 5.0 65 100 85 6.0 50 100 70 7.0 45 90 65 8.0 25 70 45 9.0 17 30 30 10.0 15 20 10 11.0 15 5 5 RBB-CMCase activity, 40°C (%) pH 60kD (II. 1)-endo 43kD (II. 3)-endo 60kD (II. 3)-endo 3.5 85 85 80 4.0 100 100 100 5.0 90 100 100 6.0 85 95 95 7.0 70 90 90 8.0 50 80 85 9.0 20 70 70 10.0 15 20 30 11.0 15 15 15

It should be understood that the neutral and/or alkaline cellulases heretofore described can have different enzymatic activities depending on the chemical structure of the substrate used in measuring the activity and the particular assay method employed to measure activity. Thus, the purified, or partially purified, neutral and/or alkaline cellulases will show different pH/activity profiles depending on the assay method and substrates employed. To resolve any confusion as to the nature of the activities and properties of the substantially purified cellulase enzymes prepared by the methods of this example, the following is a description of the activities and properties measured for the cellulases of the purified fractions.

The purified, or partially purified, cellulases prepared herein showed both endoglucanase and/or cellobiohydrolase activity when the appropriate substrate was employed. Thus, the cellulase preparations that showed endoglucanase activities all had pI values between about 3 and about 4.5. More specifically, these fractions included cellulases (endoglucanases) having molecular weights and pI values as follows: MW about 25 kD (pI about 4.0), MW about 70 kD (pI about 4.2), MW about 60 kD (pI about 3.0) and MW about 43 kD (pI about 3.1). These cellulase fractions also contained proteins showing a cellobiohydrolase activity. More specifically, the latter had a MW of about 60 kD and pI about 4.2.

Methods of using the compositions and purified enzymes according to the present invention have been well disclosed in the literature, including many patents, whose disclosures are hereby incorporated by reference. These would include Clarkson (U. S. Patent 5,290,474), which discloses use of cellulase enzymes and cellulase enzyme-containing compositions, including surfactants and other additives, for use in aqueous wash media, detergent compositions, media designed to enhance color retention and/or restoration, as well as imparting improved softening and feel properties, especially to cotton-containing fabrics. The cellulase enzymes and cellulase-containing compositions according to the present invention are also intended for use in the same applications, specific descriptions of which are described in many, if not all, of the references cited. In addition, the utility of cellulase enzymes and compositions for applications such as harshness reduction, or

fabric softening, is also taught in Barbesgaard et al (U. S. Patent 4,435,307), specifically disclosing the use of fungal cellulases, but not those of the genus Chrysosporium, at alkaline pH ranges and including various additive agents, such as those employed in conjunction with the novel cellulase and cellulase compositions of the present invention, for harshness reduction, or fabric softening, and washing as a single operation. The cellulases and cellulase compositions of the present invention are similarly useful and the teachings of Barbesgaard with respect to such applications is specifically incorporated herein. In addition, the use of cellulase enzymes and cellulase compositions, other than the novel cellulases and cellulase compositions of the present invention, for applications to color brightening are specifically disclosed in Boegh (European Patent EP 0 220 016), which teaching is specifically incorporated herein.

Of course, the novel cellulase enzymes and cellulase compositions of the present invention will be understood by those of skill in the art to be highly useful for the same applications as disclosed in in the foregoing references, thus rendering the elucidation of any further details of such applications unnecessary. However, such purified, or partially purified, enzymes and enzyme-containing compositions are also useful in such applications as deinking and biobleaching of paper or pulp materials and method of doing so will readily suggest themselves to those of skill in the art, especially after they review the teachings herein.

Example 13--C-1 Cellulase Production in 60 Liter Batch Fermentor 1. Inoculum Preparation Inoculum preparations or starter cultures for the batch fermentation were prepared as follows. One milliliter (1 ml) of C-1 spore culture was used to inoculate each of two flasks to generate a total of 2.0 liters of inoculum. The starter culture was incubated at 150 rpm, at 300C for 56 hours.

Medium for Inoculum Preparation* K, HPO, 0. 5 g/L MgSO4#7H2O 0. 15 <BR> <BR> Cl 0-05<BR> <BR> <BR> <BR> FeSO4#7H2O 0.007 yeast extract (ohly KAT) 1.0 peptone (Hormel PSR 5) 10.0 lactose 10.0 glucose 10. 0 *The pH of the inoculum medium was adjusted to pH 7.0 with NaOH, the media was then autoclaved for 35 minutes at 121°C in two six liter baffled flasks each containing one liter of medium.

2. Cellulase Production in 60 Liter Batch Fermenter (Preparation of 47. 0325) The two liter shaker flask inoculum culture prepared above, was used inoculate 40 liters of medium contained in a 60 liter fermenter. The medium for fermentation was as follows: Fermentation Medium* K, HPO, 0.22 g/L KH, PO, 0.08 g/L (NH4) SO, 4.0 g/L Na3citrate#2H2O 4. 0 g/L MgSO4 7Hz0 0. 03 g/L CaCl2 2H20 0. 4 g/L FeSO4 7H20 mg/L MnSO4 #7H2O 0.5 mg/L ZnS04 7H20 0.2 mg/L Cocu, #6H2O 0.24 mg/L lactose 5.0 g/L yeast extract (ohly KAT) 0.05 g/L defatted cotton seed flour 5.0 g/L (Pharmamedia) cellulose (Signmacell 50) 20.0 g/L pH 7.0 *The 40 liters medium was in deionized water, and was sterilized for 45 minutes at 121oC.

After inoculation of the fermentation medium, pH was maintained above 6.9 by addition of NH, and below 7.1 by addition of H. SO,. The fermenter was incubated for 64 hours with agitation and aeration as necessary to maintain dissolved oxygen greater than 30% of saturation.

3. Recovery of Cellulase Activity Suspended solids from the fermented culture were removed by filtration on large Buchner funnel using Whatman 54 filter paper and 10 g/L Celite 503 as filter aid. The filtrate was collected, and the cellulase concentrated by ultrafiltration using 10,000 MW cutoff hollow fiber filter. The concentrate was freeze dried.

The dried concentrate was designated cellulase preparation 47.0325. The activity of this preperation is given in Table 4.

Example 14--Mutation procedure used to generate mutant stain of C-1 A spore suspension was prepared using a Pridham agar plate (4 g/L yeast extract, 10 g/L malt extract, 10 g/L glucose, 15 g/L agar) containing a sporulated culture of strain C 1. The plate was flooded with 10 ml of 0.05 % Tween 80. The suspension was transferred to a sterile screw cap tube and vortexed on high for 1 minute. The suspension was then filtered through a column to remove mycelium.

Spores were counted and diluted to 7 x 105 spores per ml in water. Ten mls of the spore suspension were transferred to a standard glass petri dish. The spores were irradiated for 75 seconds at 720Watts/cnr using a Pen-Ray UV bulb. The spore suspension was gently stirred throughout the irradiation using a sterile paper clip as a magnetic stir bar. Following irradiation, the spore suspension was taken to a foil wrapped tube, diluted in water and plated in dim light to NH4 minimal medium as defined below. After incubating 20 days at 30 degrees C, a colony was identified as a large colony with a large zone of cellulose clearing around the colony.

NH4 Minimal Medium pH 7.5 1 g/L K2HPO44 O.1g/L KCl 0.3g/L MgSO4#7H2O 0.1 g/L NaCI 16mg/L FeCl3#6H2O 1.92g/L (NH4) SO, 15g/L Difco Noble agar 2.5g/L acid swollen cellulose (added as a 1.25% stock after autoclaving) 0. 5g/L sodium deoxycholate (added after autoclaving) Example 15--C-1 Mutant Cellulase Production in 60 Liter Batch Fermentation Flasks (Preparation Of 47.0528) 1. Inoculum Preparation Preparations of starter cultures for the fed batch fermentation were prepared as described in Example 13 (section 1).

2. Cellulase Production In 60 Liter Batch Fermentation The two liter inoculum was used to inoculate 40 liters of fermentation medium as described below.

Fermentation Medium*- K2HPO4 0.44 g/L KH2PO4 0.16 g/L (NH4)2SO4 3.0 g/L Na. citrate 2H20 4.0 g/L MgSO4 *7H, 0 0.06 g/L CaCl2 *2H20 0.8 g/L FeSO,'7H, 0 0. 1 mg/L MnSO, *7H, 0 0. 04 mg/L ZnS04 *7H, 0 0. 04 mg/L CoSO4 #6H2O 0. 048 mg/L lactose 5.0 g/L yeast extract (ohly KAT) 0.1 g/L

defatted cotton seed flour 10.0 g/L (Pharmamedia) cellulose (Sigmacell 50) 20.0 g/L *The 40 liters medium was in deionized water, and sterilized by autoclaving for 45 minutes at 121oC.

3. Fermentation Conditions The pH was maintained at around 7.0 and controlled by addition of NH3 at pH above 6.9, and addition of H2SO4 at pH below 7.1. Incubation time was 87 hours, agitation and aeration were as necessary to maintain dissolved oxygen greater than 30% of saturation. At 40 hours, 3.0 liters of feed solution as described below, was added at a rate of 5.0 ml each 5 minutes.

Feed Solution for Fermenter K. HPO, 0.88 g/L KH, PO, 0.32 g/L (NH4) 2SO4 4.0 g/L Na2citrate 2H20 4.0 g/L MgSO4 *7H, 0 0.12 g/L CaCl2#2H2O 0. 16 g/L FeSO, #7H2O 0.2 mg/L MnSO4 7H20 0.08 mg/L ZnSO, 7H20 0.08 mg/L CoCL #6H2O 0. 096 mg/L lactose 20.0 g/L yeast extract (ohly KAT) 0.2 g/L Pharmamedia 20.0 g/L cellulose (Sigmacell 50) 20.0 g/L 4. Recovery of Cellulase Activity Suspended solids were removed by filtration on large Buchner funnel using Whatman 54 filter paper and 10 g/L Celite 503 as filter aid. The filtrate was collected and cellulase concentrated by ultrafiltration using 10,000 MW cutoff hollow fiber filter. The concentrate was dried by freeze-drying. The concentrate was designated cellulase preparation 47.0528 (activity is given in Table 4).

Example 16-Assay of Cellulase Activity Using Cellazyme Assay This assay was carried out using Cellazyme C tablets and the assay kit obtained from Megazyme (Aust) Pty. Ltd., Sydney, NSW 2101, Australia. The substrate used is Azurine-crosslinked HE-celulose (AZCL-Cellulose) supplied commercially as cellazyme C tablets, ready for use. Briefly, 0.5 mL aliquots of enzyme preparation (diluted if necessary) in 0.025 M acetate buffer (pH 4.5) are equilibrated to 40°C for 5 minutes in glass test tubes (16 X 122 mm). The test reaction is then initiated by addition of a Cellazyme C tablet (without stirring).

After exactly 10 minutes at 40°C, the reaction is terminated by addition of Trizma Base solution (10.0 mL, 2% w/v, from Sigma Chemical Co., St. Louis, MO) and then vortexing. The tubes are then allowed to stand for about 5 minutes at room temperature whereupon the slurry is stirred again, filtered through a Whatman No.

1 (9 cm) filter circle and absorbance of the filtrate measured at 590 nm. The absorbance measurements are read against a blank containing both substrate and enzyme but prepared by adding the Trizma Base to the enzyme solution prior to addition of the cellazyme C tablet. This slurry is left at room temperature rather than 40°C. A single blank is used for each set of determinations and was used to zero the spectrophotometer.

In this assay, one unit of enzyme activity is defined as the amount of enzyme required to release one micromole of glucose reducing sugar equivalents per minute under the defined assay conditions. Endo-cellulase activity was then determined by reference to a standard curve (a sample curve was supplied with the kit but could be readily generated in the laboratory, if different particular enzyme, enzyme dilution and conditions are to be employed for a given set of experiments).

Using this assay for our own neutral/alkaline enzyme activity, we found endo-Cellulase activity (taking the activity at pH 7 as 100%) to be 92.4% (at pH 6), 75.6% (at pH 5.0) and 69.7% (at pH 4.0).

Example 17-Detergent Wash Test for De-piling and Color Brightening (Anti- fading) Tests were carried out according to the AATCC monograph, "Standardization of Home Laundry Test Conditions"in the AATCC Technical Manual, 1997 (revised 1995), using a regular Kenmore home top-loading washer, using a Kenmore home tumble-dryer. Three different styles of red adult-size socks (88% cotton, 10% polyester, 2% lycra) were used as test garments (plain ribbed knit, heavy ribbed knit and waffle weave). The socks were divided into 3 groups with an equal number of each style in each group, with a non-washed garment of each style used as a reference. The approximate weight of each group was 1 kg.

The samples of detergent were prepared prior to each wash as follows: a) Cheer Triple Guard (as purchased in the U. S. A. and commonly at alkaline pH) as is (to demonstrate the de-pilling and color care properties of cellulases originally present in Cheer, b) thermally treating the sample of Cheer to inactivate all of the enzymes originally present in the detergent (to limit the performance of Cheer to its components other than enzymes. For thermal inactivation, a 40 g sample of Cheer was suspended in 200 mL of water and heated on high (1000 W) in a home microwave for 5 minutes, the final temperature reached being 95°C. Then, repeating the same steps (a) and (b) above, but adding 5 g of Cl to the preparation.

The wash/dry cycles were performed 25 times for each group. Each group was washed throughout the 25 wash cycles using 1 kg of garments to 20 liters of wash liquor (water level in the washer was low) and 40 g of only one of the above mentioned detergent preparations. The temperature was set on hot-hot, the wash duration was 30 minutes, followed by regular, high speed centrifugation. The dryer temperature was set on high and the drying cycle lasted 45 minutes. The testing was complete after 25 washes, when the garments were evaluated, by several different groups/panels skilled in the art, for de-pilling and color brightening.

A summary of the procedure is as follows: Preparation (s) Inactivation of original Addition of Enzymes Cheer enzymes from AARL a. Cheer (complete) No No b. Cheer (no enzymes) Yes No c. Cheer + Cl Yes Yes (5 g of C1) The results of the rating for each wash group were as follows (where all 3 styles of socks were rated the same): Cheer Cheer Cheer + C 1 (complete) (enzymes inactivated) De-pilling ++++ - +++ Color Brightening + +-+ + + + It should be understood that the examples and embodiments described herein are intended for illustrative purposes only and that various modifications or changes in light thereof will readily suggest themselves to persons skilled in the art and are to be included within the spirit and purview of this application and the scope of the appended claims.