FOAM INCLUDING SURFACE-MODIFIED NANOPARTICLES
Document Type and Number:
WIPO Patent Application WO/2002/062881
Kind Code:
A2
Abstract:
A foam composition that includes a vehicle and surface-modified nanoparticles disposed in the vehicle. The individual nanoparticles having a particle diameter of less than about 100 nanometers.

Inventors:
KOLB BRANT U
BARAN JIMMIE R JR
JOHNSON MICHAEL A
JOHNSON GORDON G
LEHMANN MEGAN P
SOKALSKI JOHN S
Application Number:
PCT/US2001/049667
Publication Date:
August 15, 2002
Filing Date:
December 26, 2001
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
3M INNOVATIVE PROPERTIES CO (US)
International Classes:
C09K23/00; C08J9/00; C08J9/06; C08J9/12; C08J9/30; C09J5/08; C09J7/38; C09J11/04; C09J11/06; C09J123/00; C09J133/08; C09J161/00; C09J201/00; C09K3/00; (IPC1-7): C08J9/00
Foreign References:
EP0437068A21991-07-17
Other References:
See also references of EP 1358254A2
Attorney, Agent or Firm:
Bardell, Scott A. (Post Office Box 33427 Saint Paul, MN, US)
Download PDF:
Claims:
What is claimed is:
1. A foam composition comprising: a vehicle; and surfacemodified nanoparticles disposed in said vehicle, said individual nanoparticles having a particle diameter of less than about 100 nanometers.
2. The foam composition of claim 1, wherein said foam is essentially free of surfactant.
3. The foam composition of claim 1, further comprising surfactant.
4. The foam composition of claim 1, wherein said surfacemodified nanoparticles comprise at least about 0.5% by weight of said composition.
5. The foam composition of claim 1, wherein said individual nanoparticles have a particle diameter no greater than about 50 nanometers.
6. The foam composition of claim 1, wherein said nanoparticles are selected from the group consisting of silica, titania, alumina, zirconia, vanadia, ceria, iron oxide, antimony oxide, tin oxide, aluminum/silica and combinations thereof.
7. The foam composition of claim 1, wherein said nanoparticles comprise surface groups selected from the group consisting of hydrophobic groups, hydrophilic groups and combinations thereof.
8. The foam composition of claim 1, wherein said nanoparticles comprise surface groups derived from an agent selected from the group consisting of silane, organic acid, organic base and combinations thereof.
9. The foam composition of claim 1, wherein said nanoparticles comprise organosilyl surface groups derived from an agent selected from the group consisting of alkylsilane, arylsilane, alkoxysilane and combinations thereof.
10. The foam composition of claim 1, wherein said nanoparticles comprise surface groups derived from an agent selected from the group consisting of carboxylic acids, sulfonic acids, phosphonic acids and combinations thereof.
11. The foam composition of claim 1, wherein said vehicle comprises monomer, oligomer or polymer or a combination thereof.
12. The foam composition of claim 1, wherein said vehicle comprises a polymer selected from the group consisting of thermoplastic polymer, thermoset polymer, elastomer and mixtures thereof.
13. The foam composition of claim 1, wherein said vehicle comprises a polymer selected from the group consisting of polyester, polyurethane, amino resin, alkyd resin, phenolic resin, epoxy resin, isocyanate resin, isocyanurate resin, polysiloxane resin and mixtures thereof.
14. The foam composition of claim 1, wherein said vehicle comprises acrylic resin.
15. The foam composition of claim 1, wherein said vehicle is nonpolymerizable.
16. The foam composition of claim 1, wherein said vehicle is essentially free of polymer.
17. The foam composition of claim 1, wherein said vehicle comprises polyolefin.
18. The foam composition of claim 1, wherein said vehicle comprises metallocene polymerized polyolefin.
19. The foam composition of claim 1, wherein said vehicle comprises resin selected from the group consisting of novolac resin, resole resin and polyurea resin and mixtures thereof.
20. The foam composition of claim 1, wherein said vehicle comprises isooctyl acrylate and acrylic acid.
21. The foam composition of claim 1, wherein said vehicle is selected from the group consisting of water, alcohols, aldehydes, ketones, esters, ethers, amines, amides, hydrocarbons, halocarbons and mixtures thereof.
22. The foam composition of claim 1, further comprising a foaming agent.
23. The foam composition of claim 1, wherein said surfacemodified nanoparticles comprise surface groups having a solubility parameter similar to the solubility parameter of said vehicle.
24. The foam composition of claim 1, wherein said surfacemodified nanoparticles appear to be dissolved in said vehicle.
25. The foam composition of claim 1 wherein said vehicle comprises an adhesive composition.
26. The foam composition of claim 1 wherein said vehicle comprises a pressure sensitive adhesive composition.
27. The foam composition of claim 26, wherein said pressure sensitive adhesive composition comprises acrylic resin.
28. The foam composition of claim 1, wherein said vehicle comprises a hot melt adhesive composition.
29. An adhesive tape comprising the foam composition of claim 1.
30. A pressure sensitive adhesive tape comprising the foam composition of claim 1.
31. The pressure sensitive adhesive tape of claim 30, wherein said foam composition comprises acrylic resin.
32. An article comprising the foam composition of claim 1.
33. A method of making a foam composition, said method comprising introducing a foaming agent into a composition of claim 1 in an amount sufficient to form voids in said composition.
34. The method of claim 33, wherein said step of introducing a foaming agent comprises stirring said composition.
35. The method of claim 33, wherein said step of introducing a foaming agent comprises a chemical reaction of at least one component of the composition.
36. The method of claim 33, wherein said foaming agent is selected from the group consisting of liquid, gas and solid foaming agents.
37. The method of claim 33, wherein said foaming agent comprises a gas selected from the group consisting of air, nitrogen, oxygen, carbon dioxide, helium, argon, nitrous oxide, and mixtures thereof.
38. The method of claim 34, wherein said foaming agent comprises a degradation product of a component of the composition.
39. A method of making a tape, said method comprising: substantially simultaneously a) foaming a composition of claim 1; and b) coating said composition on a substrate.
40. A method of determining compatibility of a predetermined vehicle and surface modified nanoparticles, said method comprising: a) selecting surfacemodified nanoparticles; b) combining said surfacemodified nanoparticles and said vehicle to form a composition; and c) introducing a foaming agent into said composition, wherein if said composition forms a persistent foam or appear to dissolve in said vehicle, said surfacemodified nanoparticles are compatible with said vehicle.
41. A method of foaming a composition comprising a) adding surfacemodified nanoparticles identified by the method of claim 40 to the predetermined vehicle of claim 40; and b) foaming the vehicle.
Description:
FOAM INCLUDING SURFACE-MODIFIED NANOPARTICLES The invention relates to foaming compositions that include surface-modified nanoparticles.

Pure liquids generally cannot foam unless a surfactant is present in the liquid. The surfactant functions by lowering the surface tension of the liquid such that a gas bubble introduced below the surface of the liquid can be maintained in the liquid. The surfactants can also stabilize the foam after it is formed. Such surfactants include, for example, ionic, nonionic and polymeric surfactants.

In some applications, surfactant may migrate to the surface of the composition, which may lead to undesirable consequences. In pressure sensitive adhesive compositions, for example, surfactants may affect the adhesive properties of the composition, and in medical applications the presence of surfactants at the surface of an article, for example, a bandage, may lead to deleterious hygiene effects.

Inorganic particles are included in many foam compositions for a variety of reasons. Some of these particles function as nucleating agents. Other particles act as filler to alter the physical properties of the composition including, for example, altering the rheology of the composition. Still other particles, hydrophobic fumed silica for example, have been found to function as defoaming agents. Fumed silica, which is also known as pyrogenic silica, consists of primary particles that are irreversibly bonded together in the form of aggregates, which have an average size of from 200 nm to 300 nm.

In one aspect, the invention features a foam composition that includes a vehicle and surface-modified nanoparticles disposed in the vehicle, the individual nanoparticles having a particle diameter of less than about 100 nanometers. In one embodiment, the foam is essentially free of surfactant. In another embodiment, the foam composition further includes surfactant. In various embodiments, the foam composition includes at least about 0.5% by weight, at least about 1% by weight, at least about 2% by weight, at least about 5% by weight or at least about 10% by weight surface-modified nanoparticles.

In various embodiments, the individual nanoparticles have a particle diameter no greater than about 50 nanometers, from 3 nanometers to 50 nanometers, no greater than about 20 nanometers, from 3 nanometers to 20 nanometers and from 3 nanometers to 10 nanometers.

In one embodiment, the nanoparticles are selected from the group consisting of silica, titania, alumina, zirconia, vanadia, ceria, iron oxide, antimony oxide, tin oxide, aluminum/silica and combinations thereof.

In some embodiments, the nanoparticles include surface groups selected from the group consisting of hydrophobic groups, hydrophilic groups and combinations thereof. In other embodiments, the nanoparticles include surface groups derived from an agent selected from the group consisting of a silane, organic acid, organic base and combinations thereof. In other embodiments, the nanoparticles include organosilyl surface groups derived from an agent selected from the group consisting of alkylsilane, arylsilane, alkoxysilane, and combinations thereof.

In one embodiment, the nanoparticles include surface groups derived from an agent selected from the group consisting of carboxylic acid, sulfonic acid, phosphonic acid, and combinations thereof.

In some embodiments, the vehicle includes monomer, oligomer, polymer or a combination thereof. In other embodiments, the vehicle includes polymer selected from the group consisting of thermoplastic polymers, thermoset polymers, elastomers and mixtures thereof. In another embodiment, the vehicle includes a polymer selected from the group consisting of natural rubber, synthetic rubber, acrylonitrile-butadiene rubber, polyisoprene rubber, polychloroprene rubber, polybutadiene rubber, butyl rubber, ethylene-propylene-diene monomer rubber, ethylene-propylene rubber, styrene-butadiene copolymer, styrene-isoprene copolymer, styrene-butadiene-styrene rubber, styrene- isoprene-styrene rubber, styrene-ethylene-butylene-styrene rubber, styrene-ethylene- propylene-styrene rubber, polyisobutylene rubber, ethylene vinyl acetate rubber, silicone rubber, polyvinyl ethers and combinations thereof. In one embodiment, the vehicle includes a polymer selected from the group consisting of polyester, polyurethane, amino resin, alkyd resin, phenolic resin, epoxy resin, isocyanate resin, isocyanurate resin polysiloxane resin and mixtures thereof. In other embodiments, the vehicle includes a polymer selected from the group consisting of polyacrylonitrile, acrylonitrile-butadiene- styrene, styrene-acrylonitrile, cellulosic polymers, chlorinated polyether, ethylene vinyl acetate copolymers, polyamides, polyimides, polycarbonates, polyolefins, polyethylene terephthalate, polyphenylene oxides, polystyrene, polyurethanes, polyisocyanurates,

polyvinyl chloride, polyvinyl acetate, polyvinyl alcohols, polyvinyl butyral, polyvinyl pyrrolidone, polyvinylidene chloride and mixtures thereof.

In one embodiment, the vehicle includes acrylic resin. In some embodiments, the acrylic resin includes acrylic or methacrylic acid ester of a monohydric alcohol having from 1 to 20 carbon atoms.

In some embodiments, the vehicle is nonpolymerizable. In other embodiments, the vehicle is essentially free of polymers. In one embodiment, the vehicle includes polyolefin. In some embodiments, the vehicle includes a metallocene polymerized polyolefin.

In other embodiments, the vehicle includes resin selected from the group consisting of novolac, resole and polyurea resins and mixtures thereof.

In one embodiment, the vehicle is selected from the group consisting of water, alcohols, aldehydes, ketones, esters, ethers, amines, amides, hydrocarbons, halocarbons and mixtures thereof.

In another embodiment, the foam composition further includes a foaming agent.

In one embodiment, the surface-modified nanoparticles include statistically averaged randomly surface-modified nanoparticles.

In one embodiment, the surface-modified nanoparticles include surface groups having a solubility parameter similar to the solubility parameter of the vehicle.

In one embodiment, the surface-modified nanoparticles appear to be dissolved in the vehicle.

In another embodiment, the vehicle includes an adhesive composition. In other embodiments, the vehicle includes a pressure sensitive adhesive composition. In one embodiment, the pressure sensitive adhesive composition includes acrylic resin. In some embodiments, the acrylic resin includes an acrylic or methacrylic acid ester of a monohydric alcohol having from 1 to 20 carbon atoms. In one embodiment, the pressure sensitive adhesive composition includes isooctyl acrylate and acrylic acid copolymer.

In another embodiment, the vehicle includes a hot melt adhesive composition.

In another aspect, the invention features an adhesive tape (for example, a pressure sensitive adhesive tape) including an above-described foam composition. In other embodiments, the adhesive tape further includes a substrate and the foam composition is disposed on the substrate. In some embodiments, the foam composition includes an

acrylic resin. In one embodiment, the acrylic resin includes acrylic or methacrylic acid ester of a monohydric alcohol having from 1 to 20 carbon atoms.

In another aspect, the invention features an article that includes an above-described foam composition. In one embodiment, the article is a gasket. In other embodiments, the article is automobile body molding.

In other aspects, the invention features a method of making a foam that includes introducing a foaming agent into a composition in an amount sufficient to form voids in the composition, where the composition includes a vehicle and surface-modified nanoparticles disposed in the vehicle and the surface-modified nanoparticles have a particle diameter of no greater than about 100 nanometers. In some embodiments, the step of introducing a foaming agent includes mechanically stirring the composition. In some embodiments, the step of introducing a foaming agent includes a chemical reaction of at least one component of the composition.

In one embodiment, the foaming agent is selected from the group consisting of liquid, gas, and solid foaming agents. In other embodiments, the foaming agent includes a gas selected from the group consisting of air, nitrogen, oxygen, carbon dioxide, helium, argon, nitrous oxide, and mixtures thereof. In other embodiments, the foaming agent includes the degradation product of a component of the vehicle.

In another aspect, the invention features a method of making a tape where the method includes substantially simultaneously a) foaming a composition that includes a vehicle and a plurality of surface-modified nanoparticles having an particle diameter of less than about 100 nanometers, and b) coating the composition on a substrate.

In one aspect, the invention features a method of determining the compatibility of a predetermined vehicle and surface-modified nanoparticles, where the method includes: a) selecting surface-modified nanoparticles, b) combining the surface-modified nanoparticles and the vehicle to form a composition, and c) introducing a foaming agent into the composition, wherein if the composition forms a persistent foam, the surface-modified nanoparticles are compatible with the vehicle.

In other aspects, the invention features a method of determining compatibility of a predetermined vehicle and surface-modified nanoparticles, where the method includes a) selecting surface-modified nanoparticles; and b) combining the surface-modified nanoparticles and the vehicle to form a composition, wherein, if the surface-modified

nanoparticles appear to dissolve in the vehicle, the surface-modified nanoparticles are compatible with the vehicle.

In some aspects, the invention features a method for selecting compatible surface-modified nanoparticles for a predetermined vehicle, and the method includes selecting surface-modified nanoparticles that have a particle diameter of less than about 100 nanometers and that include attached surface groups that have a solubility parameter substantially similar to the solubility parameter of the predetermined vehicle, dispersing the surface-modified nanoparticles in a vehicle, and foaming the vehicle, wherein the presence of a persistent foam indicates that the surface-modified nanoparticles are compatible with the vehicle.

In another aspect, the invention features a method of foaming a composition that includes a) adding surface-modified nanoparticles identified by an above-described method to a predetermined vehicle, and b) foaming the vehicle.

The term"surface-modified nanoparticle"refers to a particle that includes surface groups attached to the surface of the particle. The surface groups modify the character of the particle.

The term"persistent foam"refers to the presence of gas voids in a composition for a period greater than 1 minute after the composition has been foamed.

The terms"particle diameter"and"particle size"refer to the maximum cross- sectional dimension of a particle. If the particle is present in the form of an aggregate, the terms"particle diameter"and"particle size"refer to the maximum cross-sectional dimension of the aggregate.

The inventors have discovered that compositions that include surface-modified nanoparticles are capable of forming a persistent foam. These compositions surprisingly are capable of forming a persistent foam in the absence of a surfactant. The invention has broad application due to the wide variety of compositions that can be foamed once appropriate surface-modified nanoparticles are dispersed throughout the composition.

The surface-modified nanoparticle containing compositions can also be formulated to provide improved foaming, for example, an increased number of voids, more uniformly dimensioned voids, and combinations thereof, relative to the composition without surface-modified nanoparticles.

The foam compositions can also be formulated to be free of volatile organic compounds and flammable solvents.

Other features of the invention will be apparent from the following description of preferred embodiments thereof, and from the claims.

The foam composition includes surface-modified nanoparticles, for example, inorganic nanoparticles, having a particle diameter of less than 100 nanometers, disposed in a vehicle. The foam composition includes gas voids, that is, bubbles, which may be present at the surface of the composition, dispersed throughout the composition, or a combination thereof. For some applications, the gas voids are dispersed uniformly throughout the composition. The foam is persistent and preferably includes a cellular structure in which the gas voids are in the form of closed cells.

The surface-modified nanoparticles are preferably individual, unassociated (that is, non-aggregated) nanoparticles dispersed throughout the vehicle and preferably do not irreversibly associate with each other. The term"associate with"or"associating with" includes, for example, covalent bonding, hydrogen bonding, electrostatic attraction, London forces, and hydrophobic interactions.

The surface-modified nanoparticles are selected such that the composition formed therewith is free from a degree of particle agglomeration or aggregation that would interfere with the desired properties of the composition including the ability of the composition to foam. The surface-modified nanoparticles are selected to be compatible with the vehicle to be foamed. For vehicles that include a variety of components, the surface-modified nanoparticles may be selected to be compatible with at least one component of the vehicle.

The surface-modified nanoparticles have surface groups that modify the solubility characteristics of the nanoparticles. The surface groups are selected to render the particle compatible with the vehicle including, for example, a component of the vehicle, in which the particle is disposed such that the resulting composition, upon foaming, forms a persistent foam. When the composition is polymerizable, for example, the surface groups can be selected to associate or react with at least one component of the vehicle to become part of the polymer network of the composition.

One method of assessing the compatibility of the surface-modified nanoparticles with the vehicle includes determining whether the resulting composition forms a persistent

foam when a foaming agent is introduced into the composition. For transparent vehicles, one useful method of assessing the compatibility of the surface-modified nanoparticles with the transparent vehicle includes combining the surface-modified nanoparticles and the vehicle and observing whether the surface-modified nanoparticles appear to dissolve in the vehicle such that the resulting composition is transparent. The nature of the inorganic particle component of the surface-modified particle will prevent the surface-modified particle from actually dissolving in the vehicle, that is, the surface-modified nanoparticles will be dispersed in the vehicle, however the compatibility of the surface groups with the vehicle will give the surface-modified nanoparticles the appearance of dissolving in the vehicle. As the size of the surface-modified nanoparticles increases, the haziness of the vehicle generally increases. Preferred surface-modified nanoparticles are selected such that they do not settle out of the vehicle. The further step in assessing the compatibility of the vehicle and the surface-modified nanoparticles includes determining whether, upon subsequent introduction of a foaming agent, the composition foams.

Suitable surface groups can also be selected based upon the solubility parameter of the surface group and the vehicle. Preferably the surface group, or the agent from which the surface group is derived, has a solubility parameter similar to the solubility parameter of the vehicle to be foamed. When the vehicle to be foamed is hydrophobic, for example, one skilled in the art can select from among various hydrophobic surface groups to achieve a surface-modified particle that is compatible with the hydrophobic vehicle.

Similarly, when the vehicle to be foamed is hydrophilic, one skilled in the art can select from hydrophilic surface groups, and, when the vehicle to be foamed is a fluorocarbon, one skilled in the art can select from among various fluorocarbon surface groups. The particle can also include at least two different surface groups that combine to provide a particle having a solubility parameter that is similar to the solubility parameter of the vehicle.

The surface groups may be selected to provide a statistically averaged, randomly surface-modified particle.

The surface groups are present on the surface of the particle in an amount sufficient to provide surface-modified nanoparticles that are capable of being subsequently dispersed in the vehicle without aggregation. The surface groups preferably are present in

an amount sufficient to form a monolayer, preferably a continuous monolayer, on the surface of the particle.

Surface modifying groups may be derived from surface modifying agents.

Schematically, surface modifying agents can be represented by the formula A-B, where the A group is capable of attaching to the surface of the particle and the B group is a compatibilizing group that may be reactive or non-reactive with a component of the composition. Compatibilizing groups can be selected to render the particle relatively more polar, relatively less polar or relatively non-polar.

Suitable classes of surface-modifying agents include, for example, silanes, organic acids organic bases and alcohols.

Particularly useful surface-modifying agents include silanes. Examples of useful silanes include organosilanes including, for example, alkylchlorosilanes, alkoxysilanes, for example, methyltrimethoxysilane, methyltriethoxysilane, ethyltrimethoxysilane, ethyltriethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, i-propyltrimethoxysilane, i-propyltriethoxysilane, butyltrimethoxysilane, butyltriethoxysilane, hexyltrimethoxysilane, octyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, n-octyltriethoxysilane, phenyltriethoxysilane, polytriethoxysilane, vinyltrimethoxysilane, vinyldimethylethoxysilane, vinylmethyldiacetoxysilane, vinylmethyldiethoxysilane, vinyltriacetoxysilane, vinyltriethoxysilane, vinyltriisopropoxysilane, vinyltrimethoxysilane, vinyltriphenoxysilane, vinyltri (t-butoxy) silane, vinyltris (isobutoxy) silane, vinyltris (isopropenoxy) silane and vinyltris (2-methoxyethoxy) silane; trialkoxyarylsilanes; isooctyltrimethoxy-silane; N- (3-triethoxysilylpropyl) methoxyethoxyethoxy ethyl carbamate; N- (3-triethoxysilylpropyl) methoxyethoxyethoxyethyl carbamate; silane functional (meth) acrylates including, for example, 3- (methacryloyloxy) propyltrimethoxysilane, 3-acryloyloxypropyltrimethoxysilane, 3- (methacryloyloxy) propyltriethoxysilane, 3- (methacryloyloxy) propylmethyldimethoxysilane, 3- (acryloyloxypropyl) methyldimethoxysilane, 3- (methacryloyloxy) propyldimethylethoxysilane, 3- (methacryloyloxy) methyltriethoxysilane, 3- (methacryloyloxy) methyltrimethoxysilane, 3- (methacryloyloxy) propyldimethylethoxysilane,

3- (methacryloyloxy) propenyltrimethoxysilane and 3- (methacryloyloxy) propyltrimethoxysilane; polydialkylsiloxanes including, for example, polydimethylsiloxane, arylsilanes including, for example, substituted and unsubstituted arylsilanes, alkylsilanes including, for example, substituted and unsubstituted alkyl silanes including, for example, methoxy and hydroxy substituted alkyl silanes, and combinations thereof.

Methods of surface-modifying silica using silane functional (meth) acrylates are described, for example, in U. S. Patent Nos. 4,491,508 and 4,455,205 (Olsen et al.); U. S.

Patent Nos. 4,478,876 and 4,486,504 (Chung) and U. S. Patent No. 5,258,225 (Katsamberis).

Useful organic acid surface-modifying agents include, for example, oxyacids of carbon (for example, carboxylic acid), sulfur and phosphorus, and combinations thereof.

Representative examples of polar surface-modifying agents having carboxylic acid functionality include CH30 (CH2CH20) 2CH2COOH (hereafter MEEAA) and 2- (2- methoxyethoxy) acetic acid having the chemical structure CH30CH2CH20CH2COOH (hereafter MEAA) and mono (polyethylene glycol) succinate.

Representative examples of non-polar surface-modifying agents having carboxylic acid functionality include octanoic acid, dodecanoic acid and oleic acid.

Examples of suitable phosphorus containing acids include phosphonic acids including, for example, octylphosphonic acid, laurylphosphonic acid, decylphosphonic acid, dodecylphosphonic acid and octadecylphosphonic acid.

Useful organic base surface-modifying agents include, for example, alkylamines including, for example, octylamine, decylamine, dodecylamine and octadecylamine.

Examples of other useful non-silane surface modifying agents include acrylic acid, methacrylic acid, beta-carboxyethyl acrylate, mono-2- (methacryloyloxyethyl) succinate, and combinations thereof. A useful surface modifying agent that imparts both polar character and reactivity to the nanoparticles is mono (methacryloyloxypolyethyleneglycol) succinate.

Examples of suitable surface-modifying alcohols include, for example, aliphatic alcohols including, for example, octadecyl, dodecyl, lauryl and furfuryl alcohol, alicyclic alcohols including, for example, cyclohexanol, and aromatic alcohols including, for example, phenol and benzyl alcohol, and combinations thereof.

When the vehicle includes aromatic ring containing epoxy resins, useful surface- modifying groups can include an aromatic ring. Examples of surface-modifying groups particularly suitable for epoxy resin compositions are disclosed in U. S. Patent No.

5,648,407 (Goetz et al.).

A variety of methods are available for modifying the surface of nanoparticles including, for example, adding a surface modifying agent to nanoparticles (for example, in the form of a powder or a colloidal dispersion) and allowing the surface modifying agent to react with the nanoparticles. Other useful surface modification processes are described in, for example, U. S. Patent Nos. 2,801,185 (Iler) and 4,522,958 (Das et al.).

Preferably the nanoparticles are inorganic. Examples of suitable inorganic nanoparticles include silica and metal oxide nanoparticles including zirconia, titania, ceria, alumina, iron oxide, vanadia, antimony oxide, tin oxide, alumina/silica, and combinations thereof. The nanoparticles have an average particle diameter less than about 100 nm, preferably no greater than about 50 nm, more preferably from 3 nm to 50 nm, even more preferably from 3 nm to 20 nm, most preferably from 5 nm to 10 nm. If the nanoparticles are aggregated, the maximum cross sectional dimension of the aggregated particle is within any of these preferable ranges.

Useful surface-modified zirconia nanoparticles include a combination of oleic acid and acrylic acid adsorbed onto the surface of the particle.

Useful surface-modified silica nanoparticles include silica nanoparticles surface-modified with silane surface modifying agents including, for example, acryloyloxypropyl trimethoxysilane, 3-methacryloyloxypropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, n-octyltrimethoxysilane, isooctyltrimethoxysilane, and combinations thereof. Silica nanoparticles can be treated with a number of surface modifying agents including, for example, alcohol, organosilane including, for example, alkyltrichlorosilanes, trialkoxyarylsilanes, trialkoxy (alkyl) silanes, and combinations thereof and organotitanates and mixtures thereof.

The nanoparticles may be in the form of a colloidal dispersion. Examples of useful commercially available unmodified silica starting materials include nano-sized colloidal silicas available under the product designations NALCO 1040,1050,1060,2326,2327, and 2329 colloidal silica from Nalco Chemical Co., Naperville, IL.

Useful metal oxide colloidal dispersions include colloidal zirconium oxide, suitable examples of which are described in U. S. Patent No. 5,037,579, and colloidal titanium oxide, useful examples of which are described in PCT Publication No. WO 00/06495 entitled,"Nanosize Metal Oxide Particles for Producing Transparent Metal Oxide Colloids and Ceramers," (Arney et al.) filed July 30,1998.

Various methods may be employed to combine the surface-modified nanoparticles and the vehicle. In one method, a colloidal dispersion of surface-modified nanoparticles and vehicle are combined. Solvent present in the composition is then removed, leaving the surface-modified nanoparticles dispersed in the vehicle. The solvent may be removed by evaporation including, for example, distillation, rotary evaporation or oven drying.

Optionally, for some colloidal dispersions, for example, aqueous colloidal dispersions, prior to addition of the vehicle, a cosolvent (for example, methoxy-2-propanol or N- methylpyrrolidone) may be added to the colloidal dispersion to assist removal of water.

After the vehicle is added, the water and cosolvent are removed.

Another method for incorporating colloidal dispersions of surface-modified nanoparticles into a vehicle includes drying the colloidal dispersion of surface-modified nanoparticles to a powder, followed by addition of the vehicle or at least one component of the vehicle into which the nanoparticles are to be dispersed. The drying step may be accomplished by conventional means such as oven drying or spray drying. The surface- modified nanoparticles preferably have a sufficient amount of surface groups to prevent irreversible agglomeration or irreversible aggregation upon drying. The drying time and the drying temperature is preferably minimized for nanoparticles having less than 100% surface coverage.

Colloidal dispersions of surface-modified nanoparticles can be added to the vehicle in amounts sufficient to provide a composition capable of foaming, preferably in amounts sufficient to provide a composition capable of forming a persistent foam. Surface- modified nanoparticles may be present in the composition in varying amounts including, for example, from 0.1% by dry weight to 70 % by dry weight, preferably from 0.5% by dry weight to 30 % by dry weight, more preferably from 0.8% by dry weight to 30 % by dry weight, more preferably from 1% by dry weight to 10% by dry weight, most preferably from 2% by dry weight to 10% by dry weight, based on the total weight of the

composition. The surface-modified nanoparticles are preferably dispersed throughout the vehicle, more preferably dispersed homogeneously throughout the vehicle.

A cosolvent can be added to the composition to improve the compatibility (for example, solubility or miscibility) of the surface modifying agent and the surface-modified particles with the other components of the composition.

The vehicle of the foam composition can include a variety of components and may be in the form of a solid, liquid and mixtures thereof. Prior to foaming, the vehicle is preferably a liquid including, for example, solution, emulsion, suspension, dispersion, syrup and melt. The vehicle is selected based upon the desired properties of the foam composition including, for example, tack, stiffness, hardness, density, volume, transparency, flexibility, conformability, resilience, creep, strength modulus elongation, chemical resistance, temperature resistance, environmental resistance and compressibility.

Example vehicles include inorganic liquids such as water and organic liquids including, for example, acids, alcohols, ketones, aldehydes, amines, ethers, hydrocarbons, halocarbons, monomers, oligomers, and polymers.

Examples of useful organic vehicles include natural and synthetic rubber resins including thermosettable rubbers as well as thermoplastic rubbers and elastomers including, for example, nitrile rubbers (for example, acrylonitrile-butadiene), polyisoprene rubber, polychloroprene rubber, polybutadiene rubber, butyl rubber, ethylene-propylene- diene monomer rubbers (EPDM), Santoprene (E) polypropylene-EPDM elastomers, ethylene-propylene rubber, styrene-butadiene copolymers, styrene-isoprene copolymers, styrene-butadiene-styrene rubber, styrene-isoprene-styrene rubber, styrene-ethylene- butylene-styrene rubber, styrene-ethylene-propylene-styrene rubber, polyisobutylene rubber, ethylene vinyl acetate rubbers, silicone rubbers including, for example, polysiloxanes, methacrylate rubbers, polyacrylate rubbers including, for example, copolymers of isooctyl acrylate and acrylic acid, polyesters, polyether esters, polyvinyl ethers, polyurethanes and blends and combinations thereof, including for example, linear, radial, star and tapered block copolymers thereof.

Other useful elastomers include, for example, fluoroelastomers including, for example, polytrifluoroethylene, polyvinylidene fluoride, hexafluoropropylene and fluorinated ethylene-propylene copolymers, fluorosilicones and chloroelastomers including, for example, chlorinated polyethylene, and combinations thereof.

Examples of useful thermoplastic resins include polyacrylonitrile, acrylonitrile- butadiene-styrene, styrene-acrylonitrile, cellulose, chlorinated polyether, ethylenevinylacetate, fluorocarbons including, for example, polychlorotrifluoroethylene, polytetrafluoroethylene, fluorinated ethylene-propylene and polyvinylidene fluoride, polyamides including, for example, polycaprolactam, polyhexamethylene adipamide, polyhexamethylene sebacamide, polyundecanoamide, polylauroamide and polyacrylamide, polyimides including, for example, polyetherimide, polycarbonate, polyolefins including, for example, polyethylene, polypropylene, polybutene and poly-4- methyl pentene, polyalkylene terephthalates including for example, polyethyleneterephthalate, polyalkylene oxides including, for example, polyphenylene oxide, polystyrene, polyurethane, polyisocyanurates, vinyl polymers including, for example, polyvinyl chloride, polyvinyl acetate, polyvinyl alcohol, polyvinyl butyral, polyvinylpyrrolidone, polyvinylidene chloride and combinations thereof.

Useful thermosettable resins include for example, polyesters and polyurethanes and hybrids and copolymers thereof including, for example, acylated urethanes and acylated polyesters, amino resins (for example, aminoplast resins) including, for example, alkylated urea-formaldehyde resins, melamine-formaldehyde resin, acrylate resins including, for example, acrylates and methacrylates, vinyl acrylates, acrylated epoxies, acrylated urethanes, acrylated polyesters, acrylated acrylics, acrylated polyethers, vinyl ethers, acrylated oils and acrylated silicones, alkyd resins such as urethane alkyd resins, polyester resins, reactive urethane resins, phenolic resins including, for example, resole resins, novolac resins and phenol-formaldehyde resins, phenolic/latex resins, epoxy resins including, for example, bisphenol epoxy resins, aliphatic and cycloaliphatic epoxy resins, epoxy/urethane resin, epoxy/acrylate resin and epoxy/silicone resin, isocyanate resins, isocyanurate resins, polysiloxane resins including alkylalkoxysilane resins, reactive vinyl resins and mixtures thereof.

The vehicle may be selected to provide an adhesive composition including, for example, pressure sensitive, hot melt, thermoset and thermoplastic adhesive compositions.

The vehicle can include any pressure-sensitive adhesive composition including, for example, solvent-coatable, hot-melt-coatable, radiation-curable (E-beam, actinic including, for example, visible and UV, and thermal), water-based emulsion type adhesives and combinations thereof. Suitable pressure sensitive adhesive compositions

include, for example, tackified rubber adhesives, for example, natural rubber, olefins, silicones, polyisoprenes, polybutadiene, polyurethanes, styrene-isoprene-styrene and styrene-butadiene-styrene block copolymers and other elastomers, and tackified and untackified acrylic adhesive compositions including copolymers of isooctyl acrylate and acrylic acid.

Acrylate pressure sensitive adhesives are well known in the art. Many of these adhesives are copolymers of an alkyl ester of acrylic acid and, optionally, a minor portion of a co-monomer. Useful acrylic acid esters include acrylic or methacrylic acid esters of a monohydric alcohol having from 1 to 20 carbon atoms including, for example, isooctyl acrylate, 2-ethylhexyl acrylate, isononyl acrylate, isodecyl acrylate, decyl acrylate, dodecyl acrylate, lauryl acrylate, hexyl acrylate, butyl acrylate, and octadecyl acrylate and combinations thereof. Other useful monomers for acrylate-based adhesive compositions include ethylenically-unsaturated monomers including, for example, cyclohexyl acrylate, isobornyl acrylate, N-octyl acrylamide, t-butyl acrylate, methyl methacrylate, ethyl methacrylate and propyl methacrylate and combinations thereof. Other useful ethylenically unsaturated monomers include, for example, acrylic acid, methacrylic acid, itaconic acid, substituted acrylamides including, for example, N, N-dimethylacrylamide, N- vinyl-2-pyrrolidone, N-vinyl caprolactam, acrylonitrile, tetrahydrofurfuryl acrylate, glycidyl acrylate, 2-phenoxyethyl acrylate and benzyl acrylate, and combinations thereof.

The vehicle can also include other ingredients including, for example, initiators, curing agents, cure accelerators, catalysts, crosslinking agents, tackifiers, plasticizers, dyes, flame retardants, coupling agents, pigments, impact modifiers, flow control agents, foaming agents, fillers, glass and polymer microspheres and microparticles, other particles including electrically conductive particles, thermally conductive particles, fibers, antistatic agents, antioxidants and UV absorbers.

Where the vehicle includes monomers, polymerization can be achieved by various conventional free radical polymerization methods, which can be chemical or radiation initiated, including, for example, solvent polymerization, emulsion polymerization, suspension polymerization, bulk polymerization and radiation polymerization including, for example, processes using actinic radiation including, for example, visible and ultraviolet light, electron beam radiation and combinations thereof.

Useful free radical initiators include thermal and photoactive initiators. The type of initiator used depends on the polymerization process. Examples of photoinitiators include benzoin ethers such as benzoin methyl ether and benzoin isopropyl ether, substituted benzoin ethers such as anisoin methyl ether, substituted acetophenones such as 2,2- dimethoxy-2-phenylacetophenone, and substituted alpha-ketols such as 2-methyl-2- hydroxypropiophenone.

The vehicle can also include copolymeric photoinitiators including, for example, 2- [4- (2-hydroxy-2-methylpropenoyl) phenoxy] ethyl-2-methyl-2-N-propenoylamino propanoate and the polymerizable photoinitiator available under the trade designation DAROCUR ZLJ 3331 from Ciba-Geigy, and photoacid generated initiators including, for example, diaryliodoniumhexafluoroantimonate available under the trade designation SarCat CD-1012 from Sartomer (Exton, PA) and triarylsulfonium hexafluorophosphate available under the trade designation SarCat CD-1011 (Sartomer).

Examples of suitable thermal initiators include peroxides such as benzoyl peroxide, dibenzoyl peroxide, dilauryl peroxide, cyclohexane peroxide, methyl ethyl ketone peroxide, hydroperoxides including, for example, butyl hydroperoxide and cumene hydroperoxide, dicyclohexyl peroxydicarbonate, t-butyl perbenzoate, and azo compounds, for example, 2,2,-azo-bis (isobutyronitrile) (AIBN) and combinations thereof. Examples of commercially available thermal initiators include initiators available under the"VAZO" trade designation from DuPont Specialty Chemical (Wilmington, DE) including VAZO 64 (2,2'-azobis (isobutyronitrile)), VAZO 52, VAZO 65 and VAZO 68, as well as thermal initiators available under the trade designation"Lucidol"from Elf Atochem North America, (Philadelphia, PA), and initiators available under the Celogen trade designation from Uniroyal Chemical Co. (Middlebury, CT).

An initiator is used in an amount effective to facilitate polymerization of the monomers present in the composition and the amount will vary depending upon, for example, the type of initiator, the molecular weight of the initiator, the intended application of the resulting adhesive composition and the polymerization process including, for example, the temperature of the process.

The composition may be cross-linked to alter the properties of the composition.

Cross-linking can be achieved with or without a cross-linking agent by using high energy radiation such as gamma or electron beam radiation. A cross-linking agent or a

combination of cross-linking agents can be added to the mixture of polymerizable monomers to facilitate cross-linking.

Useful radiation curing cross-linking agents include multifunctional acrylates, such as those disclosed in U. S. Pat. No. 4,379,201 (Heilmann et al.), which include 1,6- hexanediol diacrylate, trimethylolpropane triacrylate, 1,2-ethylene glycol diacrylate, pentaerythritol tetraacrylate, 1,12-dodecanol diacrylate, and combinations thereof, and copolymerizable aromatic ketone co-monomers such as those disclosed in U. S. Pat. No 4,737,559 (Kellen et al.). Suitable ultraviolet light sources include, for example, medium pressure mercury lamps and ultraviolet black light.

A polymerizable monomer composition may also include a chain transfer agent.

The chain transfer agent is preferably soluble in the monomer mixture prior to polymerization. Examples of suitable chain transfer agents include triethyl silane and mercaptans.

The composition is preferably foamed after the surface-modified nanoparticles have become dispersed throughout the vehicle, more preferably after the surface-modified nanoparticles are homogeneously dispersed throughout the vehicle. The composition can be foamed according to a variety of foaming methods including those described in, for example, U. S. Patent Nos. 5,024,880,4,895,745 and 4,748,061 (Vesley et al.).

The composition is foamed by forming gas voids in the composition using a variety of mechanisms including, for example, mechanical mechanisms, chemical mechanisms, and combinations thereof.

Useful mechanical foaming mechanisms include, for example, agitating, for example, shaking, stirring, or whipping the composition and combinations thereof, injecting gas into the composition, for example, inserting a nozzle beneath the surface of the composition and blowing gas into the composition, and combinations thereof.

Useful chemical foaming mechanisms include, for example, producing gas in situ through a chemical reaction, decomposition of a component of the composition including, for example, a component that liberates gas upon thermal decomposition, evaporating a component of the composition including, for example, a liquid gas, volatilizing a gas in the composition by decreasing the pressure on the composition or heating the composition, and combinations thereof.

In principle, any foaming agent may be used to foam the composition including, for example, chemical foaming agents and physical foaming agents including, for example, inorganic and organic foaming agents.

Examples of chemical foaming agents include water and azo-, carbonate-and hydrazide-based molecules including, for example, 4,4'-oxybis (benzenesulfonyl) hydrazide, 4,4'-oxybenzenesulfonyl semicarbazide, azodicarbonamide, p-toluenesulfonyl semicarbazide, barium azodicarboxylate, azodiisobutyronitrile, benzenesulfonhydrazide, trihydrazinotriazine, metal salts of azodicarboxylic acids, oxalic acid hydrazide, hydrazocarboxylates, diphenyloxide-4,4'-disulphohydrazide, tetrazole compounds, sodium bicarbonate, ammonium bicarbonate, preparations of carbonate compounds and polycarbonic acids, and mixtures of citric acid and sodium bicarbonate, N, N'-dimethyl-N, N'-dinitroso-terephthalamide, N, N'-dinitrosopentamethylenetetramine, and combinations thereof.

Suitable inorganic physical foaming agents include, for example, nitrogen, argon, oxygen, water, air, helium, sulfur hexafluoride and combinations thereof.

Useful organic physical foaming agents include carbon dioxide, aliphatic hydrocarbons, aliphatic alcohols, fully and partially halogenated aliphatic hydrocarbons including, for example, methylene chloride, and combinations thereof. Examples of suitable aliphatic hydrocarbon foaming agents include members of the alkane series of hydrocarbons including, for example, methane, ethane, propane, n-butane, isobutane, n- pentane, isopentane and blends thereof. Useful aliphatic alcohols include, for example, methanol, ethanol, n-propanol, and isopropanol and combinations thereof. Suitable fully and partially halogenated aliphatic hydrocarbons include, for example, fluorocarbons, chlorocarbons, and chlorofluorocarbons and combinations thereof.

Examples of fluorocarbon foaming agents include methyl fluoride, perfluoromethane, ethyl fluoride,), 1, 1-difluoroethane (HFC-152a), fluoroethane (HFC-161), 1, 1, 1-trifluoroethane (HFC-143a), 1,1,1,2-tetrafluoroethane (HFC-134a), 1,1,2,2 tetrafluoroethane (HFC-134), 1,1,1,3,3-pentafluoropropane, pentafluoroethane (HFC-125), difluoromethane (HFC-32), perfluoroethane, 2,2-difluoropropane, 1,1,1- trifluoropropane, perfluoropropane, dichloropropane, difluoropropane, perfluorobutane, perfluorocyclobutane and combinations thereof.

Useful partially halogenated chlorocarbon and chlorofluorocarbon foaming agents include methyl chloride, methylene chloride, ethyl chloride, 1,1,1-trichloroethane, 1,1- dichloro-1-fluoroethane (HCFC-141b), 1-chloro-1, 1-difluoroethane (HCFC-142b), chlorodifluoromethane (HCFC-22), 1, l-dichloro-2, 2,2-trifluoroethane (HCFC-123) and 1-chloro-1, 2,2,2-tetrafluoroethane (HCFC-124) and combinations thereof.

Examples of useful fully halogenated chlorofluorocarbons include trichloromonofluoromethane (CFC-11), dichlorodifluoromethane (CFC-12), trichloro-trifluoroethane (CFC-113), dichlorotetrafluoroethane (CFC-114), chloroheptafluoropropane and dichlorohexafluoropropane and combinations thereof.

The foaming agents may be used as single components, in mixtures and combinations thereof, as well as in mixtures with other co-foaming agents. The foaming agent is added to the composition in an amount sufficient to achieve a desired foam density.

The vehicle may also include a nucleating agent. A nucleating agent can be any conventional nucleating agent. The amount of nucleating agent to be added depends upon the desired cell size, the selected foaming agent and the density of the vehicle. Examples of inorganic nucleating agents in small particulate form include clay, talc, silica, and diatomaceous earth. Organic nucleating agents can decompose or react at a given temperature.

One example of an organic nucleating agent is a combination of an alkali metal salt of a polycarboxylic acid with a carbonate or bicarbonate. Examples of useful alkali metal salts of a polycarboxylic acid include the monosodium salt of 2,3-dihydroxy-butanedioic acid (that is, sodium hydrogen tartrate), the monopotassium salt of butanedioic acid (that is, potassium hydrogen succinate), the trisodium and tripotassium salts of 2-hydroxy- 1,2,3-propanetricarboxylic acid (that is, sodium and potassium citrate, respectively), and the disodium salt of ethanedioic acid (that is, sodium oxalate) and polycarboxylic acid such as 2-hydroxy-1, 2,3-propanetricarboxylic acid, and combinations thereof. Examples of carbonate and bicarbonate include sodium carbonate, sodium bicarbonate, potassium bicarbonate, potassium carbonate and calcium carbonate and combinations thereof. One contemplated combination is a monoalkali metal salt of a polycarboxylic acid, such as monosodium citrate or monosodium tartrate, with a carbonate or bicarbonate. It is contemplated that mixtures of different nucleating agents may be added to the vehicle.

Other useful nucleating agents include a stoichiometric mixture of citric acid and sodium bicarbonate.

The components of the foam composition can be selected to provide foam compositions suitable for use in a variety of applications. Representative examples of foam applications include adhesives, flotation, applications in the automotive industry including, for example, automotive body moldings, applications related to automotive glazing including, for example, gaskets and sealants, applications in the construction industry including, for example, structural components, for example, sized lumber, shaped trim, posts, beams and shaped structural members, lightweight ceramics including, for example, pre-cast and cast-in-place construction materials including, for example, cementitious and gypsum materials such as blocks, boards, panels, roofdecks and flooring, landfill covers, odor barriers, dust covers, firefighting and fireproofing foams, liquid containment booms (for example, oil spill containment boom), and fillers for voids such as oil wells and tunnels and voids present in soil. Other foam applications include packaging, commercial cleaning products including, for example, cleaners for vertical cleaning applications, inks, de-inking compositions, surface coatings including, for example, foamed coatings for paper and textile treatment.

The foam compositions can also be formulated for use in applications such as foamed personal care products including, for example, hair treatment compositions, shaving compositions and skin treatment compositions; medical applications including, for example, bandages and wound dressings; and household and industrial applications including, for example, cups, plates, earplugs, cushions, pillows, insulation, a damper including, for example, for suppressing sound, absorbing vibration (including, for example, cushioning the vibration of machine covers) and combinations thereof, and baffles.

In another embodiment, the foam composition is formulated to be useful as a gasket or seal to seal an area from dust, moisture, organic vapor and combinations thereof.

Examples of sealing applications include sealing gaps between parts in computer printers, sealing electronic equipment and sealing skylight assemblies.

The foam composition can be formulated to provide foams that are flexible and conformable and suitable for filling gaps and bonding irregular surfaces. When bonding rough or irregular surfaces, the properties and formulation of the foam tape are preferably

further selected to provide a foam tape that distributes stress uniformly over the bonded area. The foam can also be formulated to provide a bond line that seals, cushions vibration, damps vibration, resists impact, withstands a wide temperature range or provides good insulating qualities or provides a combination of these properties.

The foam composition can be in the form of a tape including, for example, a pressure-sensitive adhesive tape. Useful foam tape constructions include foam composition disposed on a substrate, for example, a backing or a release liner, and, optionally, wound in the form of a roll. In some embodiments, the foam tape construction includes an adhesive composition disposed on a surface of a foam tape, which forms a tape having an adhesive layer on one side of the foam tape, that is, a single coated adhesive foam tape. In another embodiment, the foam composition can be in the form of a tape having an adhesive layer on two major surfaces of the foam tape, which is known as double-coated foam tape.

Adhesive foams have a variety of useful applications including, for example, bonding two substrates together, mounting applications using articles including, for example, hooks, hangers, and holders, joining applications including, for example, adhering two or more containers, for example, boxes, together for later separation, bonding articles to surfaces including, for example, walls, floors, ceilings and counters and replacing mechanical fasteners, mastics, or liquid glues. Other adhesive foam applications include, for example, as structural adhesives and foam-in-place adhesives.

In other embodiments, the foam composition includes other components including, for example, scrims, films, tissues and combinations thereof, dispersed in the foam or disposed in a layered construction with the foam composition in the form of, for example, alternating layers, interpenetrating layers and combinations thereof. Other useful foam constructions include multi-layer foam constructions that include layers of foam where the layers differ in at least one property including, for example, density and composition.

The foam composition can also be subjected to post processes including, for example, die cutting, crosslinking and sterilization.

The invention will now be described further by way of the following examples.

All parts, ratios, percents and amounts stated in the Examples are by weight unless otherwise specified.

Examples Test Procedures Test procedures used in the examples include the following.

Determination of L Value The L value of a sample is determined using a Hunter Lab D25A Optical Sensor colorimeter (Hunter Associates Laboratory, Reston, VA). The L value is a measure of the lightness or darkness of a sample on a scale of 1-100 (where a value of 1 is black and a value of 100 is white). The sample is placed in the colorimeter and the black'control panel used to calibrate the colorimeter is placed behind the sample. The L'value is read from the instrument. According to this test method, a relatively higher nitrogen content in the sample will result in relatively more dispersed gas bubbles and correspondingly more light scattering which results in a higher 1.'value.

Preparation of Pentamethyl (2-tris (2-methoxyethoxy) silyllethyl) disiloxane Coupling Agent Pentamethyl (2- [tris (2-methoxyethoxy) silyl] ethyl) disiloxane Coupling Agent ("Silane Coupling Agent A") was prepared by combining 143.86 g tris (2- methoxyethoxy) vinylsilane (Aldrich Chemical Co., Milwaukee, WI) and 76.14 g pentamethyldisiloxane (Gelest, Inc., Tullytown, PA) with mixing in 145 g heptane. One drop of a platinum (0) divinyltetramethyldisiloxane catalyst (prepared according to the procedures in U. S. Patent Nos. 3,814,730) was added to 0.3 g heptane to form a solution.

0.1 g of this solution was added to the above reaction mixture, which was then allowed to stir in a nitrogen atmosphere, without heating, overnight. The reaction continued until completion as determined by the disappearance of the Si-H peak using infrared spectroscopy (IR). Heptane was removed from the composition by evaporation under reduced pressure to give Silane Coupling Agent A.

Preparation of Silane Coupling Agent A Surface-Modified Silica Nanoparticles Silica nanoparticles surface modified with Silane Coupling Agent A were prepared as follows: 525g NALCO 2326 15% by weight solids ammonia stabilized colloidal silica having an average particle size of 5 nm and a surface area of about 600 meters2/gram (as

reported by the manufacturer, Nalco Chemical Co., Naperville, IL), 83.7 g Silane Coupling Agent A and 1010 g 1-methoxy-2-propanol (Aldrich) were combined with mixing in a 1 gallon glass jar. The jar containing the mixture was sealed, placed in a vented oven, and heated overnight at 80°C. The mixtures was then transferred to an evaporating dish for drying and dried in a flow-through oven at 150°C to produce 118.8 g of a white particulate solid.

Preparation of Silane Coupling Agent A/Gamma-Methacryloyloxypropyltrimethoxysilane Surface-Modified Silica Nanoparticles Silica nanoparticles surface modified with Silane Coupling Agent A and gamma-methacryloyloxypropyltrimethoxysilane were prepared as follows: 106.93 g Silane Coupling Agent A, 3.25 g SILQUEST A-174 gamma- methacryloyloxypropyltrimethoxysilane (OSi Specialties Inc., Endicott, NY), 1940 g l-methoxy-2-propanol and 1000 g NALCO 2326 colloidal silica were combined in a 1 gallon glass jar. The jar containing the mixture was sealed. The mixture was then shaken to ensure mixing, placed in an oven and heated overnight at 80°C. The mixture was then dried in a flow through oven at 150°C to produce a white particulate solid.

Preparation of Isooctvlsilane Surface-Modified Silica Nanoparticles: Silica nanoparticles surface modified with isooctyltrimethoxysilane were prepared as follows: 61.42 g BS1316 isooctyltrimethoxysilane (Wacker Silicones Corp., Adrian, MI), 1940 g 1-methoxy-2-propanol and 1000 g NALCO 2326 colloidal silica were combined in a 1 gallon glass jar. The mixture was shaken to ensure mixing and then placed in an oven at 80°C overnight. The mixture was then dried in a flow through oven at 150°C to produce a white particulate solid.

Preparation of Methoxyethoxyethoxyethoxyureidopropyltriethoxysilane Coupling Agent Methoxyethoxyethoxyethoxyureidopropyltriethoxysilane coupling agent ("Silane Coupling Agent B") was prepared by charging 50.02 g triethyleneglycol monomethyl ether (Aldrich) and 46 g methyl ethyl ketone into a 250 ml round bottom flask equipped with a magnetic stir bar. A majority of the methyl ethyl ketone was removed via rotary evaporation. 76.03 g 3-isocyanatopropyltriethoxysilane (United Chemical Technologies,

Bristol, PA) and approximately 3 mg dibutyltin dilaurate (Aldrich) were added to the flask and the mixture was stirred. The reaction proceeded with a mild exotherm. The reaction was run for approximately 16 hr, after which time infrared spectroscopy showed a small isocyanate peak. An additional 0.1 g triethyleneglycol monomethyl ether was added to the composition and the remainder of the methyl ethyl ketone was removed via rotary evaporation at reduced pressure and 70°C to give Silane Coupling Agent B. No observable isocyanate peak was detected using infrared spectroscopy.

Preparation of Silane Coupling Agent B Surface-Modified Silica Nanoparticles Silane Coupling Agent B surface-modified silica nanoparticles were prepared by charging 200.0 g Nalco 2327 40% by weight solids ammonia stabilized colloidal silica having an average particle size of 20 nm and a surface area of about 150 meters2/gram (as reported by the manufacturer, Nalco Chemical Co.) to a 1 quart glass jar. 226 g deionized water and 8.47 g Silane Coupling Agent B were added to the colloidal dispersion with stirring. The jar was sealed and heated to 80°C for 18 hours to produce a clear blue tinted colloidal dispersion of 18% by weight Silane Coupling Agent B surface-modified silica nanoparticles in water.

Preparation of Silane Coupling Agent A/Silane Coupling Agent B Modified Silica Nanoparticles in Isooctyl Acrylate/Acrylic Acid (81.5/18.5) Silane Coupling Agent A/Silane Coupling Agent B surface-modified silica nanoparticles were prepared by charging 400.43 g Nalco 2326 colloidal silica to a 1 quart glass jar. 452.97g 1-methoxy-2-propanol, 6.43 g Silane Coupling Agent B and 31.40 g Silane Coupling Agent A were mixed together and added to the colloidal silica with stirring. The jar was sealed and heated to 80°C for 18 hours resulting in a slurry of Silane Coupling Agent A/Silane Coupling Agent B surface-modified silica nanoparticles ("Slurry A").

A 1-liter round-bottom flask was charged with 239.07 g Slurry A and 30.03 g isooctyl acrylate. Water and alcohol were removed from the composition via rotary evaporation at reduced pressure. The flask was removed from the rotary evaporator and an additional 266.56 g Slurry A and 30.17 g isooctyl acrylate were added. The remaining alcohol and water were removed via rotary evaporation at reduced pressure. The flask was

again removed from the rotary evaporator and an additional 323.28 g Slurry A and 30.04 g isooctyl acrylate were added. The remaining alcohol and water were removed via rotary evaporation at reduced pressure.

147.03 g of a viscous colloidal dispersion containing approximately 38.4 % silica was obtained. 20.56 g acrylic acid was added to 144 g of the viscous colloidal dispersion and mixed thoroughly.

Example 1 Example 1 was prepared by adding 0.1 g of the colloidal dispersion of 18% by weight Silane Coupling Agent B surface-modified silica nanoparticles in water to 0.9 g deionized water. The sample was then shaken by hand to produce foam. The foam was observed to be stable for greater than 1 minute.

Comparative Example 1 Comparative Example 1 was prepared by shaking 1 g deionized water for the same period of time that Example 1 was shaken. No foam was visible.

Example 2 Example 2 was prepared by adding 0.04 g isooctylsilane surface-modified silica nanoparticles to 1.96 g toluene. The sample was then shaken by hand to produce foam.

The foam was observed to be stable for greater than 1 minute.

Comparative Example 2 Comparative Example 2 was prepared by shaking 2 g toluene for the same period of time that Example 2 was shaken. No foam was visible.

Example 3 Example 3 was prepared by adding 0.04 g Silane Coupling Agent A surface modified silica nanoparticles to 1.96 g ethyl acetate. The sample was then shaken to produce foam. The foam was observed to be stable for greater than 1 minute.

Comparative Example 3 Comparative Example 3 was prepared by shaking 2 g ethyl acetate for the same period of time that Example 3 was shaken. No foam was visible Preparation of Composition A A syrup was prepared by combining 87.5 parts isooctyl acrylate, 12.5 parts acrylic acid and 0.04 parts IRGACURE 651 2,2-dimethoxy-1,2-diphenylethane-1-one photointiator (Ciba Specialty Chemicals, Tarrytown, NY), and then partially polymerizing the mixture using ultraviolet radiation to provide a syrup having a viscosity of about 3000 cPs. Composition A was prepared by adding an additional 0.19 g IRGACURE 651 and 0.55 g 1,6-hexanediol diacrylate to the syrup. Thirty grams of Composition A was used for Controls 1-6 and Examples 4-11.

Controls 1-6 Control 1 was Composition A.

Control 1 was foamed by stirring the composition with a fritted glass tube through which nitrogen passed, under low pressure (that is, less than 2 psi), into the composition.

The fritted glass tube was approximately 6 inches in length, included a fritted nozzle end nominally 10 mm in diameter and 16 mm in length, and was attached to a source of nitrogen. The composition was stirred for approximately 2 minutes or until there was no visible sign of additional frothing of the sample.

The foamed sample was then coated between 3 mil thick silicone coated transparent polyethylene terephthalate release liners at a thickness of 40 mils using a notched bar coater, and then cured by immediately placing the coated sample directly beneath a single 15 watt Blacklight F15T8-BL bulb (General Electric Co.) in a two-bulb capacity light fixture (Model XX-15L (UVP San Gabriel, CA)) such that the distance from the bulb to the sample was approximately 6.3 mm. The sample was then exposed to the radiation for approximately 3 minutes, which permanently fixed the foam in place.

Control 2 was prepared by combining 98% by weight Composition A and 2% by weight Dow Corning 1250 surfactant (Dow Coming, Midland, MI). The sample composition was then foamed and cured as described in Control 1.

Control 3 was prepared by combining 98% by weight Composition A and 2% by weight dried NALCO 2326 silica nanoparticles. The sample composition was then foamed and cured as described in Control 1.

Control 4 was prepared by combining 98% by weight Composition A and 2% by weight AEROSIL R-972 dimethylsilyl-modified fumed silica (Degussa Corp., Ridgefield Park, NJ). The sample composition was then foamed and cured as described in Control 1.

Control 5 was prepared by combining 98% by weight Composition A and 2% by weight CABOSIL M-5 hydrophobic fumed silica (Cabot Corp., Naperville, IL). The sample composition was then foamed and cured as described in Control 1.

Control 6 was prepared by combining 98% by weight Composition A and 2% by weight AEROSIL R805 n-octylsilyl-modified fumed silica (DeGussa). The sample composition was then foamed and cured as described in Control 1.

Examples 4-11 Example 4 was prepared by combining 98% by weight Composition A and 2% by weight isooctylsilane surface-modified silica nanoparticles.

The composition of Example 4 was then foamed by stirring the composition with a fritted glass tube through which nitrogen passed, under low pressure (that is, less than 2 psi), into the composition. The fritted glass tube was approximately 6 inches in length, included a fritted nozzle end nominally 10 mm in diameter and 16 mm in length, and was attached to a source of nitrogen. The composition was stirred for approximately 2 minutes or until there was no visible sign of additional frothing of the sample.

The foamed sample was then coated between 3 mil thick silicone coated PET release liners at a thickness of 40 mils using a notched bar coater, and then cured by immediately placing the coated sample directly beneath a single 15 watt Blacklight F15T8-BL bulb (General Electric Co.) in a two-bulb capacity light fixture (Model XX-15L (UVP San Gabriel, CA)) such that the distance from the bulb to the sample was approximately 6.3 mm. The sample was then exposed to the radiation for approximately 3 minutes, which permanently fixed the foam in place.

Example 5 was prepared by combining 99.7% by weight Composition A and 0.3% by weight Silane Coupling Agent A/gamma-methacryloyloxypropyltrimethoxysilane

surface-modified silica nanoparticles. The sample composition was then foamed and cured as described in Example 4.

Example 6 was prepared by combining 99.3% by weight Composition A and 0.7% by weight Silane Coupling Agent A/gamma-methacryloyloxypropyltrimethoxysilane surface-modified silica nanoparticles. The sample composition was then foamed and cured as described in Example 4.

Example 7 was prepared by combining 98.5% by weight Composition A and 1.5% by weight percent of Silane Coupling Agent A/gamma- methacryloyloxypropyltrimethoxysilane surface-modified silica nanoparticles. The sample composition was then foamed and cured as described in Example 4.

Example 8 was prepared by combining 98% weight Composition A and 2% by weight Silane Coupling Agent A/gamma-methacryloyloxypropyltrimethoxysilane surface-modified silica nanoparticles. The sample composition was then foamed and cured as described in Example 4.

Example 9 was prepared by combining 98% by weight Composition A and 2% by weight of the Silane Coupling Agent A/Silane Coupling Agent B surface-modified silica nanoparticles/isooctyl acrylate/acrylic acid composition. The sample composition was then foamed and cured as described in Example 4.

Example 10 was prepared by combining 98% by weight Composition A and 2% by weight Silane Coupling Agent A surface-modified silica nanoparticles. The sample composition was then foamed and cured as described in Example 4.

Example 11 was prepared by combining 97% by weight Composition A, 2% by weight Silane Coupling Agent A surface-modified silica nanoparticles and 1 % by weight Dow Coming 1250 surfactant. The sample composition was then foamed and cured as described in Example 4.

The L values of the foamed and cured samples of Controls 1-6 and Examples 4-11 were determined according to the L Value Test Method. The results are shown in Table 1.

Table 1 Sample % by weight Additive Surface-Modifier % by weight L'Value Composition surface-modified Reading A nanoparticles Control 100 None NA 0 33.6 1 Control 98 2% by weight NA 0 53. 2 2 Surfactant Control 98 NALCO 2326 NA 0 31.6 3 silica nanoparticles Control 98 AEROSIL R-972 Dimethydichlorosilane 0 27. 3 4 hydrophobic fumed silica Control 98 CABOSIL M-5 NA 0 33.9 5 hydrophilic fumed silica Control 98 AEROSIL R-805 n-Octyltrimethoxysilane 0 33.5 6 hydrophobic fumed silica Example 98 Surface-modified Isooctylsilane 2 53. 0 4 NALCO 2326 colloidal silica Example 99.7 Surface-modified Silane Coupling Agent 0.3 51.7 5 NALCO 2326 A/A174 colloidal silica Example 99.3 Surface-modified Silane Coupling Agent 0.7 57.8 6 NALCO 2326 A/A174 colloidal silica Example 98.5 Surface-modified Silane Coupling Agent 1.5 61.6 7 NALCO 2326 A/A 174 colloidal silica Example 98 Surface-modified Silane Coupling Agent 2 58.2 8 NALCO 2326 A/A 174 colloidal silica Example 98 Surface-modified Silane Coupling Agent 2 54.2 9 NALCO 2327 A/Silane Coupling colloidal silica Agent B Example 98 Surface-modified Silane Coupling Agent 2 58.8 10 NALCO 2326 A colloidal silica Example 97 Surface-modified Silane Coupling Agent 2 65.9 11 NALCO 2326 A colloidal silica and 1 % surfactant

Foaming Thermoplastic Compositions Control 7-8 and Examples 12-13 Samples were prepared by melting approximately 45 g ENGAGE 8200 thermoplastic polyolefin elastomer having a melting point of 60°C and a melt flow rate of 5 g/10 min, as determined by ASTM D1238 (DuPont Dow Elastomers, Wilmington, DE), in a PLASTI-CORDER dual rotor kneader (C. W. Brabender Instruments, South Hackensack, NJ). Once the samples were melted, 2% by weight CELOGEN 754-A blowing agent (Uniroyal Chemical Co.) was blended into the polymer melt. For compositions that included nanoparticles, 2% by weight nanoparticles (of the type specified in Table 2) was added to the polymer mixture after the blowing agent was fully blended into the polymer. The mixture was then removed from the kneader.

The polymer mixture was then placed between two polyester films and flattened in a hydraulic press (heated on top and bottom to about 135°C) to a thickness between about 0.1 mm and 1.3 mm.

The sample was then cut into approximately 1 in. x 1 in. pieces. The thickness of each sample was measured using a caliper gauge. The samples were then placed in an oven at about 180°C to activate the blowing agent and foam the samples. The foamed samples were then removed from the oven after 2,5,10 or 15 minutes and cooled to room temperature. The sample thickness was again measured using a caliper gauge. The average percent growth in thickness was calculated for each time interval. A higher percent growth indicates more foaming. The results are reported in Table 2.

Table 2 Sample Silica Particles and Surface Treatment Average Percent Increase in Foam Thickness 2 min 5 min 10 min 15 min Control 7 No particles 49. 9 102.3 122.0 159.7 Control 8 Dried NALCO 2326 silica 58.4 148.4 149.4 191.6 nanoparticles Example 12 Isooctyltrimethoxysilane surface- 63.8 160.5 196.4 229.6 modified silica nanoparticles Example 13 Silane Coupling Agent A surface-63.1 156.7 192.5 208.4 modified silica nanoparticles Other embodiments are within the claims.