| Document |
Document Title |
|
JPH02232382A |
PURPOSE: To make flow production of high-temp. superconducting components by mounting ceramic materials onto supporting metals by an enamel coating technique. CONSTITUTION: The ceramic materials are mounted as high-temp. superconducting ...
|
|
JPH02228485A |
PURPOSE: To suppress blotting and staining due to cooked food and to prevent scorching by coating a product obtd. by baking ground coat enamel with cover coat enamel consisting of transparent glaze, mat glaze and special glaze in the for...
|
|
JPH0239463B2 |
|
|
JPH0239082B2 |
|
|
JPH02221385A |
PURPOSE: To produce a high quality stainless material with no irregularity in the color by allowing stainless stock to develop a color by heating in an oxygen-rich atmosphere in an electric kiln, coating the color developed surface with ...
|
|
JPH02217482A |
PURPOSE: To form a vitreous surface protective film excellent in adhesive strength at a low cost by thermally spraying a vitreous material on the surface of a metallic formed part, a ceramic formed part, etc. CONSTITUTION: A powder for t...
|
|
JPH02209491A |
PURPOSE: To make it possible to automatically carry in and out plural substrates to be enameled by forming the substrates on both sides or one side of a strip through thin connecting parts like leaves on a branch to obtain a connected bo...
|
|
JPH02194186A |
PURPOSE: To remarkably increase the adhesive strength of enamel glaze to a work and to evenly electrostatically coat the work with powdery enamel by calcining the enamel glaze at a temp. lower than the roasting temp. of the enamel glaze ...
|
|
JPH02187176A |
PURPOSE: To form a film which may be transformed to glass or the like by applying a coating material obtd. by polycondensation of a specific silicon compd. on a substrate, then irradiating the prescribed coated area with heat energy or t...
|
|
JPH02170989A |
PURPOSE: To reduce pinhole defects by allowing specific amounts of Cu to adhere to the surface of a steel sheet after annealing and also controlling acid pickling velocity in an acid pickling stage at the time of treatment prior to porce...
|
|
JPH02156043A |
PURPOSE: To manufacture an Al killed steel sheet for porcelain enameling excellent in press formability by incorporating specific percentages of C, Mn, S, solAl, Cu, B, N, and P to Fe. CONSTITUTION: A steel having a composition which con...
|
|
JPH02153080A |
PURPOSE: To ensure erasability for a marker and to attain nonhalation by glazing a board substrate having ground coat enamel with slip prepd. by blending Ti-contg. white overglaze having a specified compsn. with Ti-contg. mat glaze havin...
|
|
JPH02122083A |
PURPOSE: To form an alkali silicate-based ceramic coating layer having superior adhesion and free from bubbles when Al, Zn or surface-treated steel is coated with alkali silicate-based ceramic, by previously forming a chemical film on th...
|
|
JPH0218562B2 |
|
|
JPH02113587A |
PURPOSE: To reduce the number of times of baking for facilitating the circuit design further enhancing the reliability of an insulating layer by a method wherein the number of metallic cores of enameled substrates is increased more than ...
|
|
JPH0297686A |
PURPOSE: To obtain an enameled substrate having high adhesive strength between the enamel coat and metal core by forming an oxide coating film on a metal core of an Fe-Ni alloy, immersing the core in a slurry contg. dispersed frit having...
|
|
JPH0297687A |
PURPOSE: To obtain an enameled substrate having high adhesive strength between the enamel coat and metal core by forming an oxide coating film on a metal core of an Fe-Ni-Cr alloy, immersing the core in a slurry contg. dispersed frit hav...
|
|
JPH0213951B2 |
|
|
JPH0213946B2 |
|
|
JPH0266182A |
PURPOSE: To make it possible to easily break an enameled substrate by a single bending at the groove part by previously forming opposite grooves of a specified depth in the part of the metal core of the enameled substrate to be broken an...
|
|
JPH029200Y2 |
|
|
JPH029118B2 |
An electrophoretic coating method, including the steps of electrophoretically coating an anodic workpiece with enamel in an enamel slop composed of a watery suspension. At least one substance is added to the enamel slop which is enamel c...
|
|
JPH027367B2 |
|
|
JPH0243379A |
PURPOSE: To produce the insulating enamel substrate having a large enamel film thickness and small surface roughness by elecrtrodepositing 1st fine glass particles on the surface of a metallic substrate and heat treating the same, then f...
|
|
JPH0240989A |
PURPOSE: To form a resistance circuit, a resistance temperature coefficient of which is less than a specified value, without remarkably changing paste even when the glass composition of a substrate is varied by shaping a dielectric thin-...
|
|
JPH0240988A |
PURPOSE: To improve the adhesion of a conductor circuit layer by forming the conductor circuit layer 4 onto a required enameled substrate and dielectric thin-layers just under the layer 4 or just under and near the layer 4. CONSTITUTION:...
|
|
JPH0240990A |
PURPOSE: To obtain a circuit board excellent in surface smoothness, heat resistance, acid resistance, fine printing accuracy and the stability of a gold electrode by forming the gold electrode onto an enamel layer composed of a metallic ...
|
|
JPH0238586A |
PURPOSE: To provide a coated member having a significant oxidation preventing effect and fine black appearance by dissolving iron oxide of lower order on the surface of a metal member and forming a solidified dense potash glass layer. CO...
|
|
JPH0238370A |
PURPOSE: To obtain a composite powder for ceramic coating capable of adhering to the inside of a tube and forming uniform coating layer and further providing structure having excellent thermal shock resistance only by feeding a coating m...
|
|
JPH0234795A |
PURPOSE: To increase energy efficiency and time efficiency and to enable painting on a base material without damaging the material by forming a printed pattern on the surface of the base material and irradiating the pattern with infrared...
|
|
JPH024677B2 |
The invention is concerned with providing substrates with coatings obtainable from sols, for example to protect the substrate (such as in nuclear reactors or hydrocarbon cracking plant) or to provide a carrier for catalytically active ma...
|
|
JPH0211749A |
PURPOSE: To form a glass coating free from cracks and having stable acid resistance, corrosion resistance, and heat resistance by thermally spraying frit glaze having specific viscosity characteristic on the surface of a metallic workpie...
|
|
JPH01316470A |
PURPOSE: To simply produce an enameled product having satisfactory adhesion and free from fish scale and bubbles by removing an iron oxide layer on the surface of a hot or cold rolled steel sheet, roughening the surface of the steel shee...
|
|
JPH0143400Y2 |
|
|
JPH01312083A |
PURPOSE: To improve the adhesion and corrosion resistance of a repaired part when repair is carried out with resin for repair and a curing agent in combination with an inorg. filler and a coupling agent, by adding glass powder as the fil...
|
|
JPH01173158U |
|
|
JPH01294876A |
PURPOSE: To form a repaired part having excellent adhesion to a glass lining and corrosion resistance by using a repairing material consisting of a mixture of transparent repairing resin, a filler obtained by treating glass powder with a...
|
|
JPH01161263U |
|
|
JPH01275781A |
PURPOSE: To prevent the occurrence of defects such as cracks in a glass tube on the inside of a steel tube even when external force is applied to the steel tube, by interposing a specified metal layer between the inner wall of the steel ...
|
|
JPH01272783A |
PURPOSE: To produce an enameled base plate having an enamel layer controlled in heat conductivity by coating a metallic base plate with both an inner layer high in porosity having large blister diameter and an outer layer low in porosity...
|
|
JPH0148867B2 |
|
|
JPH0148868B2 |
|
|
JPH01263282A |
PURPOSE: To shorten the time required to grind an edged tool during cutting work by vitrifying borax and glaze by heating to a high temp. to coat the edged tool with a vitreous coat. CONSTITUTION: An edged tool is heated to about 1,000°...
|
|
JPH0134079Y2 |
|
|
JPH01240674A |
PURPOSE: To form a silicate film excellent in whitening resistance by means of a short-time treatment by treating an Al material with specific alkali silicate, baking the above under specific conditions, and then applying dealkalization ...
|
|
JPH01226327A |
PURPOSE: To enable a far infrared ray radiating member itself to generate heat by a method in which the layer of far infrared ray material is formed on one surface of a metallic plate or the member formed by using the metallic plate, and...
|
|
JPH0140058B2 |
PURPOSE:A lining material, prepared by incorporating a thermosetting resin with specific ceramics, having improved durability in slippery abrasion and impact abrasion, rich in corrosion resistance, heat resistance and working properties,...
|
|
JPH01208342A |
PURPOSE: To obtain the title enamel improved in resistance to wear and scratch, by limiting refractory substances to be applied on the original enamel and by using their specified combination. CONSTITUTION: The objective enamel can be ob...
|
|
JPH0137353B2 |
|
|
JPH01188657A |
PURPOSE:To repair the subject device with a perfectly reproduced railing property without deteriorating the strength of the base metal by removing the glass- lining layer around the broken part on the base metal, and thermally spraying a...
|